JP2018096887A - 管材の応力腐食割れ試験方法 - Google Patents
管材の応力腐食割れ試験方法 Download PDFInfo
- Publication number
- JP2018096887A JP2018096887A JP2016242892A JP2016242892A JP2018096887A JP 2018096887 A JP2018096887 A JP 2018096887A JP 2016242892 A JP2016242892 A JP 2016242892A JP 2016242892 A JP2016242892 A JP 2016242892A JP 2018096887 A JP2018096887 A JP 2018096887A
- Authority
- JP
- Japan
- Prior art keywords
- test
- test piece
- stress
- width direction
- stress corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
[1]被試験材である管材から採取した試験片を扁平させて前記試験片の外内表面に所定の試験応力を与えた後、前記試験片を試験溶液中に浸漬して保持し、前記試験片の耐硫化物応力腐食割れ性を評価する管材の応力腐食割れ試験方法であって、扁平により前記試験片の外表面に与える、試験に要求される引張応力がA1、前記管材の降伏応力がB、扁平させた結果前記試験片外表面に発生する、現実の引張応力がA2であるときに、前記試験片の幅方向に対して、A2/Bの比が、A1/B以上1.0以下となる条件で、前記試験応力を与えることを特徴とする管材の応力腐食割れ試験方法。
[2]前記試験応力として、前記A1/Bに対して5%以内の範囲も含むことを特徴とする[1]に記載の管材の応力腐食割れ試験方法。
[3]前記試験片に与える前記試験応力の最大応力が、試験片の幅方向端部以外の部分に与えられることを特徴とする[1]または[2]に記載の管材の応力腐食割れ試験方法。
[4]前記試験片の板厚について、試験片の幅方向中央部より試験片の幅方向両端部を薄くしたことを特徴とする[1]〜[3]のいずれかに記載の管材の応力腐食割れ試験方法。
[5]前記試験片の板厚について、試験片の幅方向中央部から試験片の幅方向端部にかけて漸減的に減ることを特徴とする[1]〜[4]のいずれかに記載の管材の応力腐食割れ試験方法。
[6]前記試験片の板厚について、試験片の幅方向中央部から試験片の幅方向端部にかけてステップ状に減ることを特徴とする[1]〜[4]のいずれかに記載の管材の応力腐食割れ試験方法。
腐食状況は、評価面全体の範囲を目視により評価した。下記基準に照らし、評価した。
合格:ルーペ観察(20倍)でもピット、割れの発生が認められない。
不合格:ピット、割れの発生を目視で観察できる。
2 切り抜き部
3 ネジ
4 テーパ部
5 切り欠き部
10 Cリング試験片
Claims (6)
- 被試験材である管材から採取した試験片を扁平させて前記試験片の外内表面に所定の試験応力を与えた後、前記試験片を試験溶液中に浸漬して保持し、前記試験片の耐硫化物応力腐食割れ性を評価する管材の応力腐食割れ試験方法であって、
扁平により前記試験片の外表面に与える、試験に要求される引張応力がA1、前記管材の降伏応力がB、扁平させた結果前記試験片外表面に発生する、現実の引張応力がA2であるときに、
前記試験片の幅方向に対して、A2/Bの比が、A1/B以上1.0以下となる条件で、前記試験応力を与えることを特徴とする管材の応力腐食割れ試験方法。 - 前記試験応力として、前記A1/Bに対して5%以内の範囲も含むことを特徴とする請求項1に記載の管材の応力腐食割れ試験方法。
- 前記試験片に与える前記試験応力の最大応力が、試験片の幅方向端部以外の部分に与えられることを特徴とする請求項1または2に記載の管材の応力腐食割れ試験方法。
- 前記試験片の板厚について、試験片の幅方向中央部より試験片の幅方向端部を薄くしたことを特徴とする請求項1〜3のいずれか1項に記載の管材の応力腐食割れ試験方法。
- 前記試験片の板厚について、試験片の幅方向中央部から試験片の幅方向端部にかけて漸減的に減ることを特徴とする請求項1〜4のいずれか1項に記載の管材の応力腐食割れ試験方法。
- 前記試験片の板厚について、試験片の幅方向中央部から試験片の幅方向端部にかけてステップ状に減ることを特徴とする請求項1〜4のいずれか1項に記載の管材の応力腐食割れ試験方法。