JP2017155556A - Incombustible decorative plate - Google Patents
Incombustible decorative plate Download PDFInfo
- Publication number
- JP2017155556A JP2017155556A JP2016042295A JP2016042295A JP2017155556A JP 2017155556 A JP2017155556 A JP 2017155556A JP 2016042295 A JP2016042295 A JP 2016042295A JP 2016042295 A JP2016042295 A JP 2016042295A JP 2017155556 A JP2017155556 A JP 2017155556A
- Authority
- JP
- Japan
- Prior art keywords
- sealer
- sealer layer
- layer
- decorative sheet
- plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は不燃化粧板に関する。 The present invention relates to a non-combustible decorative board.
化粧シートと不燃性の板材とを貼り合わせた化粧板は、床面、壁面等の内装や家具などの様々な用途に不燃材料として使用されている。不燃性建築材料として一般的に使用されている火山性ガラス質複層板は、化粧シートを貼り合わせる不燃性の板材として使用可能であるが、化粧シートとの接着性が不十分であるため、化粧シートとの接着性を確保するために、火山性ガラス質複層板の２つの板面のうち化粧シートが接着される側の板面にはシーラー層が設けられている。しかしながら、シーラー層が設けられていることにより、加熱時の総発熱量が大きくなるので、不燃性が低下するという問題があった。 A decorative plate obtained by bonding a decorative sheet and a non-combustible plate material is used as a non-combustible material for various uses such as interiors and furniture such as floor surfaces and wall surfaces. The volcanic glassy multilayer board generally used as a non-combustible building material can be used as a non-combustible board material to which a decorative sheet is bonded, but because the adhesiveness with the decorative sheet is insufficient, In order to ensure adhesion with the decorative sheet, a sealer layer is provided on the plate surface on the side to which the decorative sheet is bonded, out of the two plate surfaces of the volcanic vitreous multilayered plate. However, since the sealer layer is provided, the total calorific value at the time of heating increases, so that there is a problem that nonflammability is lowered.
そこで、本発明は上記のような従来技術が有する問題点を解決し、優れた不燃性を有する不燃化粧板を提供することを課題とする。 Then, this invention makes it a subject to solve the trouble which the above prior arts have, and to provide the nonflammable decorative board which has the outstanding nonflammability.
前記課題を解決するため、本発明の一態様に係る不燃化粧板は、板状の不燃性基材の板面に化粧シートを設けた不燃化粧板であって、不燃性基材の２つの板面にそれぞれシーラー層を設け、化粧シートと相対する側の板面に設けられたシーラー層よりも、化粧シートと相対する側とは反対側の板面に設けられたシーラー層の方が塗布量が多いことを要旨とする。 In order to solve the above-mentioned problems, a non-combustible decorative board according to an aspect of the present invention is a non-combustible decorative board in which a decorative sheet is provided on the plate surface of a plate-like non-combustible base material, and two plates of the non-combustible base material A sealer layer is provided on each side, and the sealer layer provided on the plate surface opposite to the side facing the decorative sheet is applied more than the sealer layer provided on the side opposite the decorative sheet. The gist is that there are many.
本発明によれば、優れた不燃性を有する不燃化粧板を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the nonflammable decorative board which has the outstanding nonflammability can be provided.
本発明の一実施形態について、図面を参照しながら以下に説明する。図１に示す本実施形態の不燃化粧板は、板状の不燃性基材１の板面に化粧シート２を設けて形成したものである。詳述すると、不燃性基材１と化粧シート２は、粘着剤を含有する粘着剤層４を介して接着されているが、不燃性基材１と化粧シート２との接着性を高めるために、不燃性基材１の２つの板面のうち化粧シート２と相対する側の板面にはシーラー剤を含有するシーラー層３Ａが設けられていて、不燃性基材１とシーラー層３Ａが粘着剤層４を介して接着されている。
An embodiment of the present invention will be described below with reference to the drawings. The incombustible decorative board of this embodiment shown in FIG. 1 is formed by providing a
一方、不燃性基材１の２つの板面のうち化粧シート２と相対する側とは反対側の板面にも、シーラー剤を含有するシーラー層３Ｂが設けられている。そして、化粧シート２と相対する側の板面に設けられたシーラー層３Ａよりも、化粧シート２と相対する側とは反対側の板面に設けられたシーラー層３Ｂの方が塗布量が多く形成されている。
On the other hand, a
このような本実施形態の不燃化粧板は、不燃性基材１の両板面にシーラー層３Ａ、３Ｂが設けられており、しかも、化粧シート２と相対する側の板面に設けられたシーラー層３Ａよりも、化粧シート２と相対する側とは反対側の板面に設けられたシーラー層３Ｂの方が塗布量が多く形成されているため、不燃性基材の２つの板面のうち化粧シートと相対する側の板面のみにシーラー層が設けられている不燃化粧板と比べて、加熱時の総発熱量が小さく、優れた不燃性を有している。
In such a non-combustible decorative board according to this embodiment, the
また、不燃性基材１の２つの板面のうち化粧シート２と相対する側とは反対側の板面にもシーラー層３Ｂが設けられているので、本実施形態の不燃化粧板を他の部材へ装着する際の接着性、施工性が優れている。
よって、本実施形態の不燃化粧板は、床面、壁面等の内装や家具などの様々な用途に、不燃材料として好適に使用することができる。
Moreover, since the
Therefore, the incombustible decorative board of this embodiment can be suitably used as an incombustible material for various uses such as interiors and furniture such as floor surfaces and wall surfaces.
不燃性基材１の種類は、優れた不燃性を有しているならば特に限定されるものではないが、例えば、火山性ガラス質堆積物粉体、鉱物繊維等から製造される火山性ガラス質複層板があげられる。
また、化粧シート２の種類は特に限定されるものではないが、優れた不燃性を有していることが好ましく、例えば、ポリエチレンテレフタレート、ポリブチレンテレフタレート等のポリエステル樹脂を含有するフィルム又はシートを基材とする化粧シートや、チタン紙を基材とする化粧シートがあげられる。
The type of nonflammable substrate 1 is not particularly limited as long as it has excellent nonflammability. For example, volcanic glass manufactured from volcanic glassy sediment powder, mineral fibers, etc. Quality multilayer board.
The type of the
さらに、シーラー層３Ａ、３Ｂに含有されるシーラー剤の種類は特に限定されるものではないが、例えば、クロロプレンゴム系シーラー剤、ウレタン系シーラー剤、イソシアネート系シーラー剤、エポキシ系シーラー剤があげられる。シーラー層３Ａとシーラー層３Ｂには、同種のシーラー剤を用いてもよいし、異種のシーラー剤を用いてもよい。
Furthermore, the type of the sealer agent contained in the
シーラー層３Ａ、３Ｂの塗布量（厚さ）の比率は、シーラー層３Ａの塗布量よりもシーラー層３Ｂの塗布量の方が多いならば特に限定されるものではない。ただし、不燃化粧板の加熱時の総発熱量を小さくするためには、化粧シート２と相対する側とは反対側の板面に設けられたシーラー層３Ｂの塗布量が、化粧シート２と相対する側の板面に設けられたシーラー層３Ａの塗布量の１倍以上４倍以下であることが好ましい。
The ratio of the coating amount (thickness) of the
また、不燃化粧板の加熱時の総発熱量を小さくするためには、化粧シート２と相対する側とは反対側の板面に設けられたシーラー層３Ｂの塗布量は、６ｇ／ｍ２以上２０ｇ／ｍ２以下であることが好ましい。
不燃性基材１にシーラー層３Ａ、３Ｂを設ける方法は特に限定されるものではないが、例えば、スポンジロールを用いたロールコーターによりシーラー剤を塗布する方法があげられる。
Moreover, in order to reduce the total calorific value at the time of heating the non-combustible decorative board, the application amount of the
Although the method of providing the
さらに、粘着剤層４に含有される粘着剤の種類は特に限定されるものではないが、例えば、アクリル系粘着剤、酢酸ビニル系粘着剤、エチレン酢酸ビニル系粘着剤、ウレタン系粘着剤、イソシアネート系粘着剤、メラミン樹脂系粘着剤があげられる。
なお、本実施形態は本発明の一例を示したものであって、本発明は本実施形態に限定されるものではない。また、本実施形態には種々の変更又は改良を加えることが可能であり、その様な変更又は改良を加えた形態も本発明に含まれ得る。
Furthermore, although the kind of adhesive contained in the
In addition, this embodiment shows an example of this invention and this invention is not limited to this embodiment. In addition, various changes or improvements can be added to the present embodiment, and forms to which such changes or improvements are added can also be included in the present invention.
〔実施例〕
以下に実施例及び比較例を示して、本発明をさらに具体的に説明する。
（実施例１）
厚さ６ｍｍの火山性ガラス質複層板（大建工業株式会社製の商品名ダイライト）の２つの板面のうち一方の板面に、スポンジロールを用いて、クロロプレンゴム系粘着剤をシーラー剤として塗布して、シーラー層（以下「表側シーラー層」と記す）を設けた。乾燥後の表側シーラー層の質量は６ｇ／ｍ２とした。
〔Example〕
The present invention will be described more specifically with reference to the following examples and comparative examples.
Example 1
A sponge roll is used on one of the two plate surfaces of a 6 mm thick volcanic glassy multilayer plate (trade name Dylite manufactured by Daiken Kogyo Co., Ltd.), and a chloroprene rubber adhesive is used as a sealer agent. And a sealer layer (hereinafter referred to as “front side sealer layer”) was provided. The mass of the front sealer layer after drying was 6 g / m 2 .
また、表側シーラー層を設けた火山性ガラス質複層板の２つの板面のうち他方の板面に、クロロプレンゴム系粘着剤をシーラー剤として塗布して、シーラー層（以下「裏側シーラー層」と記す）を設けた。乾燥後の裏側シーラー層の質量は２０ｇ／ｍ２とした。
次に、表側シーラー層の上にアクリル系粘着剤を厚さ５５μｍとなるように塗布し、粘着剤層を形成した。そして、粘着剤層の上に、ポリブチレンテレフタレート製フィルムを基材とする化粧シートを貼り合わせ、実施例１の不燃化粧板を製造した。
In addition, a chloroprene rubber-based adhesive is applied as a sealer agent to the other of the two volcanic glassy multilayer plates provided with a front side sealer layer, and a sealer layer (hereinafter referred to as “back side sealer layer”). ). The mass of the back side sealer layer after drying was 20 g / m 2 .
Next, an acrylic pressure-sensitive adhesive was applied on the front side sealer layer to a thickness of 55 μm to form a pressure-sensitive adhesive layer. And the decorative sheet which makes a base material the film made from a polybutylene terephthalate was bonded together on the adhesive layer, and the nonflammable decorative board of Example 1 was manufactured.
（比較例１）
表側シーラー層及び裏側シーラー層を備えていない点を除いて実施例１の不燃化粧板と同様の構成の不燃化粧板を製造した。すなわち、厚さ６ｍｍの火山性ガラス質複層板（大建工業株式会社製の商品名ダイライト）の２つの板面のうち一方の板面に、アクリル系粘着剤を厚さ５５μｍとなるように塗布し、粘着剤層を形成した。そして、粘着剤層の上に、ポリブチレンテレフタレート製フィルムを基材とする化粧シートを貼り合わせ、比較例１の不燃化粧板を製造した。
(Comparative Example 1)
A non-combustible decorative board having the same configuration as the non-combustible decorative board of Example 1 was produced except that the front-side sealer layer and the back-side sealer layer were not provided. That is, acrylic adhesive is 55 μm thick on one of the two plate surfaces of a 6 mm thick volcanic glassy multilayer plate (trade name Dylite manufactured by Daiken Kogyo Co., Ltd.). This was applied to form an adhesive layer. And the decorative sheet which uses a polybutylene terephthalate film as a base material was bonded together on the adhesive layer, and the nonflammable decorative board of the comparative example 1 was manufactured.
（比較例２）
裏側シーラー層を備えていない点を除いて実施例１の不燃化粧板と同様の構成の不燃化粧板を製造した。すなわち、厚さ６ｍｍの火山性ガラス質複層板（大建工業株式会社製の商品名ダイライト）の２つの板面のうち一方の板面に、スポンジロールを用いて、クロロプレンゴム系粘着剤をシーラー剤として塗布して、表側シーラー層を設けた。乾燥後の表側シーラー層の質量は６ｇ／ｍ２とした。
次に、表側シーラー層の上にアクリル系粘着剤を厚さ５５μｍとなるように塗布し、粘着剤層を形成した。そして、粘着剤層の上に、ポリブチレンテレフタレート製フィルムを基材とする化粧シートを貼り合わせ、比較例２の不燃化粧板を製造した。
(Comparative Example 2)
A non-combustible decorative board having the same configuration as the non-combustible decorative board of Example 1 was produced except that the back-side sealer layer was not provided. That is, a chloroprene rubber adhesive is applied to one of the two plate surfaces of a 6 mm thick volcanic glassy multilayer plate (trade name Dylite manufactured by Daiken Kogyo Co., Ltd.) using a sponge roll. It applied as a sealer agent and provided the front side sealer layer. The mass of the front sealer layer after drying was 6 g / m 2 .
Next, an acrylic pressure-sensitive adhesive was applied on the front side sealer layer to a thickness of 55 μm to form a pressure-sensitive adhesive layer. And the decorative sheet which makes the base material the film made from a polybutylene terephthalate was bonded together on the adhesive layer, and the nonflammable decorative board of the comparative example 2 was manufactured.
（比較例３）
表側シーラー層の厚さと裏側シーラー層の厚さが同一である点を除いて実施例１の不燃化粧板と同様の構成の不燃化粧板を製造した。すなわち、厚さ６ｍｍの火山性ガラス質複層板（大建工業株式会社製の商品名ダイライト）の２つの板面のうち一方の板面に、スポンジロールを用いて、クロロプレンゴム系粘着剤をシーラー剤として塗布して、表側シーラー層を設けた。乾燥後の表側シーラー層の質量は６ｇ／ｍ２とした。
(Comparative Example 3)
A non-combustible decorative board having the same configuration as the non-combustible decorative board of Example 1 was manufactured except that the thickness of the front sealer layer and the thickness of the back sealer layer were the same. That is, a chloroprene rubber adhesive is applied to one of the two plate surfaces of a 6 mm thick volcanic glassy multilayer plate (trade name Dylite manufactured by Daiken Kogyo Co., Ltd.) using a sponge roll. It applied as a sealer agent and provided the front side sealer layer. The mass of the front sealer layer after drying was 6 g / m 2 .
また、表側シーラー層を設けた火山性ガラス質複層板の２つの板面のうち他方の板面に、クロロプレンゴム系粘着剤をシーラー剤として塗布して、裏側シーラー層を設けた。乾燥後の裏側シーラー層の質量は６ｇ／ｍ２とした。
次に、表側シーラー層の上にアクリル系粘着剤を厚さ５５μｍとなるように塗布し、粘着剤層を形成した。そして、粘着剤層の上に、ポリブチレンテレフタレート製フィルムを基材とする化粧シートを貼り合わせ、比較例３の不燃化粧板を製造した。
Moreover, the chloroprene rubber-type adhesive was apply | coated as a sealer agent to the other board surface among the two board surfaces of the volcanic glassy multilayer board which provided the front side sealer layer, and the back side sealer layer was provided. The mass of the back side sealer layer after drying was 6 g / m 2 .
Next, an acrylic pressure-sensitive adhesive was applied on the front side sealer layer to a thickness of 55 μm to form a pressure-sensitive adhesive layer. And the decorative sheet which makes the base material the film made from a polybutylene terephthalate was bonded together on the adhesive layer, and the nonflammable decorative board of the comparative example 3 was manufactured.
このようにして製造した実施例１及び比較例１〜３の不燃化粧板の不燃性を、ＩＳＯ５６６０に規定されたコーンカロリーメーターによる発熱性試験により評価した。評価項目は、２０分間の加熱による総発熱量、最高発熱速度、及び最高発熱速度が連続して２００ｋＷ／ｍ２を超えた時間（表１には「２００ｋＷ／ｍ２超時間」と記す）である。なお、建築基準法が不燃材料に要求する基準は、総発熱量については８ＭＪ／ｍ２以下、最高発熱速度が連続して２００ｋＷ／ｍ２を超えた時間については１０秒以下である。 The incombustibility of the incombustible decorative plates of Example 1 and Comparative Examples 1 to 3 thus produced was evaluated by a heat generation test using a cone calorimeter specified in ISO5660. The evaluation item is the total calorific value by heating for 20 minutes, the maximum heat generation rate, and the time when the maximum heat generation rate has continuously exceeded 200 kW / m 2 (shown as “over 200 kW / m 2 in Table 1”). is there. The standards required by the Building Standards Act for non-combustible materials are 8 MJ / m 2 or less for the total calorific value, and 10 seconds or less for the time when the maximum heat generation rate continuously exceeds 200 kW / m 2 .
また、実施例１及び比較例１〜３の不燃化粧板については、化粧シートを貼り合わせる際の化粧シートと粘着剤層との接着性（化粧シートの接着性）と、不燃化粧板を他の部材へ粘着剤を介して接着する際の裏側シーラー層と他の部材との接着性（不燃化粧板の施工性）とを評価した。 Moreover, about the incombustible decorative board of Example 1 and Comparative Examples 1-3, the adhesiveness (adhesiveness of a decorative sheet) of a decorative sheet and an adhesive layer at the time of bonding a decorative sheet, and an incombustible decorative board other than The adhesion between the back side sealer layer and other members (workability of non-combustible decorative board) when adhering to the members via an adhesive was evaluated.
これらの評価結果を表１にまとめて示す。比較例１の不燃化粧板は、表側シーラー層及び裏側シーラー層をいずれも備えていないので、総発熱量が低く優れた不燃性を有していた。ただし、化粧シートの接着性と不燃化粧板の施工性は劣っていた。
比較例２の不燃化粧板は、表側シーラー層のみを備えているので、比較例１と比べると総発熱量が高く不燃性が低かった。また、表側シーラー層を備えているため化粧シートの接着性は優れているものの、裏側シーラー層を備えていないので不燃化粧板の施工性は劣っていた。
These evaluation results are summarized in Table 1. Since the nonflammable decorative board of Comparative Example 1 was not provided with either the front side sealer layer or the back side sealer layer, the total calorific value was low and it had excellent nonflammability. However, the adhesiveness of the decorative sheet and the workability of the incombustible decorative board were inferior.
Since the incombustible decorative board of Comparative Example 2 was provided with only the front side sealer layer, the total calorific value was higher than that of Comparative Example 1, and the incombustibility was low. Moreover, since the adhesive property of the decorative sheet is excellent because the front side sealer layer is provided, the workability of the non-combustible decorative board is inferior because the back side sealer layer is not provided.
比較例３の不燃化粧板は、表側シーラー層及び裏側シーラー層を備えているものの、その厚さが同一であるため、比較例１と比べると総発熱量が高く不燃性が低かった。比較例３の不燃化粧板の不燃性は、比較例２と同レベルであった。ただし、表側シーラー層及び裏側シーラー層を備えているので、化粧シートの接着性と不燃化粧板の施工性が優れていた。 Although the incombustible decorative board of Comparative Example 3 was provided with a front side sealer layer and a back side sealer layer, the thickness was the same, so that the total calorific value was higher and the incombustibility was lower than that of Comparative Example 1. The incombustibility of the incombustible decorative board of Comparative Example 3 was the same level as that of Comparative Example 2. However, since the front side sealer layer and the back side sealer layer were provided, the adhesiveness of the decorative sheet and the workability of the incombustible decorative board were excellent.
これに対して実施例１の不燃化粧板は、表側シーラー層及び裏側シーラー層を備えているので、化粧シートの接着性と不燃化粧板の施工性が優れていた。また、表側シーラー層の厚さよりも裏側シーラー層の厚さの方が大きいので、総発熱量は比較例１には及ばないものの、比較例２、３と比べると低く優れた不燃性を有していた。そして、最高発熱速度と、最高発熱速度が連続して２００ｋＷ／ｍ２を超えた時間については、いずれの比較例よりも良好な結果であった。 On the other hand, since the incombustible decorative board of Example 1 was provided with the front side sealer layer and the back side sealer layer, the adhesiveness of the decorative sheet and the workability of the incombustible decorative board were excellent. In addition, since the thickness of the back side sealer layer is larger than the thickness of the front side sealer layer, the total calorific value is not comparable to that of Comparative Example 1, but it is low compared with Comparative Examples 2 and 3 and has excellent nonflammability. It was. And it was a result better than any comparative example about the maximum exothermic rate and the time when the maximum exothermic rate exceeded 200 kW / m < 2 > continuously.
１ 不燃性基材
２ 化粧シート
３Ａ、３Ｂ シーラー層
４ 粘着剤層
DESCRIPTION OF SYMBOLS 1
Claims (1)