JP2017066423A - 透明かつ強靭なゴム組成物およびその製造方法 - Google Patents
透明かつ強靭なゴム組成物およびその製造方法 Download PDFInfo
- Publication number
- JP2017066423A JP2017066423A JP2017006433A JP2017006433A JP2017066423A JP 2017066423 A JP2017066423 A JP 2017066423A JP 2017006433 A JP2017006433 A JP 2017006433A JP 2017006433 A JP2017006433 A JP 2017006433A JP 2017066423 A JP2017066423 A JP 2017066423A
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- composition
- olefin polymer
- jis
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
23℃における屈折率が1.500〜1.525の範囲である第一のオレフィン重合体と、
前記第一のオレフィン重合体とは異なる、第二のオレフィン重合体と
を含み、
前記組成物の2mm厚のシートでJIS K7136に従って測定したヘーズ値が、20%未満であり、
前記組成物のJIS K6253に従って測定したタイプAデュロメータ硬さ(0 sec)が、35以上である組成物が提供される。
低cisイソプレンゴム(IR)成分と、
ブタジエンゴム(BR)、1,2-ポリブタジエンゴム、スチレンブタジエンゴム(SBR)、アクリロニトリルブタジエンゴム(NBR)、水素化ニトリルゴム(HNBR)、ウレタンゴム(U)、エチレンプロピレンゴム(EPM)、エチレンプロピレンジエンゴム(EPDM)、クロロプレンゴム(CR)、および天然ゴム(NR)からなる群から選択される、ゴム重合体成分と
を含み、
前記低cisイソプレンゴム成分と前記ゴム重合体成分の質量の合計を100質量部としたときに、前記低cisイソプレンゴム成分の量が45〜95質量部の範囲であり、
シリカを実質的に含まない組成物が提供される。
リチウム触媒により得られた、23℃における屈折率が1.500〜1.525の範囲である第一のオレフィン重合体を用意するステップと、
リチウム触媒により得られた、前記第一のオレフィン重合体とは異なる第二のオレフィン重合体を用意するステップと、
前記第一のオレフィン重合体と、前記第二のオレフィン重合体とを混合して、混合物を得るステップと、
前記混合物に架橋剤を添加するステップと、
前記混合物を均一に混練するステップと
を含む方法が提供される。
本願明細書において物が「透明」(transparent)であるとは、透過光が主に正透過からなり、可視光線の正透過率が高いことをいう。透明性の程度は、本願においてはヘーズ値または全光線透過率によって規定できる。その程度に及ばない透明性を有する物のことは、本願においては「不透明」(opaque)または「半透明」(semi-transparent)であると称する。
オレフィン重合体とは、オレフィンを重合させたものをいい、ジエン重合体および非ジエン重合体を含む。また、オレフィン重合体には、熱可塑性エラストマー(TPE)も含まれうる。本願の実施形態にかかる組成物は、少なくとも二種以上のオレフィン重合体を含むことができる。
「非ジエン重合体」とは、重合体のユニットにおいて二重結合を二つ有しないものをいう。非ジエン重合体としては例えば、ブチルゴム(IIR)、フッ素ゴム(FKM)、エチレンプロピレンゴム(EPM)、エチレンプロピレンジエンゴム(EPDM)、およびウレタンゴム(U)が含まれるが、これらに限定はされず、当該技術分野において知られる炭化水素から製造できる任意の重合体も含めることができる。
本願の実施形態にかかる組成物の最終的な調製(製品として用いるための仕上げの処理)にあたっては、少なくとも二種のオレフィン重合体の混合物を、架橋剤(加硫剤)により架橋することが好ましい。架橋剤としては例えば、硫黄、硫黄含有化合物、ラジカル架橋剤、および過酸化物といったものが挙げられる。
本願の実施形態にかかる組成物には、その透明性を著しく損わないかぎりにおいて、他の成分を含めることもまた可能である。そうした他の成分としては例えば、着色剤、変性剤、加工剤(ラウリン酸亜鉛など)、抗酸化剤(モノフェノール系、ビスフェノール系、ポリフェノール系、硫黄系、リン系の化合物など;例えばイルガノックス1010(BASF製)、イルガフォス168(BASF製)、イルガノックスPS800(BASF製)など)、還元剤、脱酸素剤、光安定剤、制酸剤、pH安定剤、表面処理剤、熱安定剤、着色剤、充填剤(タルク、炭酸カルシウム、カーボンブラックなど)、界面活性剤、ゲル化剤、殺生物剤、UV吸収剤(サリチル酸、ベンゾフェノン、ベンゾトリアゾール、シアノアクリラート、ヒンダードアミンなど)、ダスティング剤(ポリエチレン等のポリオレフィン、シリカ、タルク、または炭酸カルシウム粉末など)、難燃剤、またはポリリン酸が含まれるが、これらに限定はされない。
本願の実施形態にかかる透明組成物においては、透明性の観点から、ヘーズの値が20%未満であることが好ましく、より好ましくは15%以下、さらに好ましくは10%以下である。ヘーズが20%以上となると、組成物の透明性が低くなってしまい、実用的・審美的な観点から市場の要請に応えられない問題が生ずる。
或る実施形態においては、組成物を、以下の工程を含んだ方法により調製することができる。すなわち、リチウム触媒により得られた23℃における屈折率が1.500〜1.525の範囲である第一のオレフィン重合体を用意する工程と、リチウム触媒により得られた第二のオレフィン重合体を用意する工程と、第一のオレフィン重合体と第二のオレフィン重合体とを混合して混合物を得る工程と、混合物に架橋剤を添加する工程と、混合物を均一に混練する工程とを含む方法により調製可能である。
[工程1]
低シスポリイソプレンゴム(クレイトンポリマー社製、Cariflex IR0307KU)95gの塊を、5インチオープンロール(安田精機株式会社製、ロール温度70℃、回転比1:1.25)にかけて押し潰した。
5インチオープンロールの温度を100℃に上げて、1,2-ポリブタジエン(JSR社製、RB-820)5.0gをロールにかけて、潰しながらロールに巻きつけた。
1,2-ポリブタジエンを巻きつけたロールに、工程1で先に潰しておいたポリイソプレンゴムを加え、同時にラウリン酸亜鉛(0.25g)を加えながら均一に練り上げた。
均一に練られたゴムをロールから外し、ロール温度を70℃に下げた。
70℃になったロールに、工程4で外しておいたゴムを巻きつけて、架橋剤として2,5-ジメチル-2,5-ジ(t-ブチルペルオキシ)ヘキサン(日本油脂製、商品名パーヘキサ(R)25B)を2.0g、およびエチレングリコールメタアクリラート(EGDMA)を4.0g添加して、均一に練った。
次に練りあがったゴムをロールより厚さ3〜4mmのシート状に切りだし、室温で一昼夜放置して熟成させた。
一昼夜熟成させたゴムを、プレス機(関西ロール株式会社製、36t・2段加熱冷却プレス)を用いて、150℃、13分(加圧15MPa)のプレス条件で架橋(cure)させ、ゴム組成物の実施例1を得た。上述した手法により物性の測定も行った。
工程1においてCariflex IR0307KUを80g、工程2においてRB-820を20g用い、工程7において架橋時間を7分間とした他は、実施例1と同様にして、ゴム組成物の実施例2を得た。
工程1においてCariflex IR0307KUを90g、工程2においてRB-820を10g、工程3においてラウリン酸亜鉛を0.5g用い、工程7において架橋温度を160℃、架橋時間を10分間とした他は、実施例1と同様にして、ゴム組成物の実施例3を得た。
工程1においてCariflex IR0307KUを50g、工程2においてRB-820を50g用い、工程5においてEGDMAを添加せずパーヘキサ25Bの量を1.0gとし、工程7において架橋温度を160℃、架橋時間を5分間とした他は、実施例1と同様にして、ゴム組成物の実施例4を得た。
工程1においてCariflex IR0307KUを50g、工程2においてRB-820の代わりにジエン35NR(Firestone Polymers社製)を50g用い、工程5においてEGDMAを添加せずパーヘキサ25Bの量を1.0gとし、工程7において架橋温度を160℃、架橋時間を10分間とした他は、実施例1と同様にして、ゴム組成物の実施例5を得た。
工程1においてCariflex IR0307KUを50g、工程2においてRB-820を50g用い、工程5においてEGDMAを添加せずパーヘキサ25Bの量を1.5gとし、工程7において架橋温度を160℃、架橋時間を6分間とした他は、実施例1と同様にして、ゴム組成物の実施例6を得た。
工程1においてCariflex IR0307KUを50g、工程2においてRB-820を50g用い、工程5においてEGDMAを添加せずパーヘキサ25Bの量を2.0gとし、工程7において架橋温度を160℃、架橋時間を6分間とした他は、実施例1と同様にして、ゴム組成物の実施例7を得た。
工程1においてCariflex IR0307KUを50g、工程2においてRB-820を50g用い、工程5においてパーヘキサ25Bの量を1.0g、EGDMAの量を2.0gとし、工程7において架橋時間を5分間とした他は、実施例1と同様にして、ゴム組成物の実施例8を得た。
工程1においてCariflex IR0307KUを50g、工程2においてRB-820を50g用い、工程5においてパーヘキサ25Bの量を1.0gとし、工程7において架橋時間を4分間とした他は、実施例1と同様にして、ゴム組成物の実施例9を得た。
工程1においてCariflex IR0307KUを60g、工程2においてRB-820を40g用い、工程5においてパーヘキサ25Bの量を1.0gとし、EGDMAを添加せず、工程7において架橋温度を160℃、架橋時間を7分間とした他は、実施例1と同様にして、ゴム組成物の実施例10を得た。
工程1においてCariflex IR0307KUを70g、工程2においてRB-820を30g用い、工程5においてパーヘキサ25Bの量を1.0gとし、EGDMAを添加せず、工程7において架橋温度を160℃、架橋時間を11分間とした他は、実施例1と同様にして、ゴム組成物の実施例11を得た。
工程1においてCariflex IR0307KUを70g、工程2においてRB-820を30g用い、工程5においてEGDMAを添加せず、工程7において架橋温度を160℃、架橋時間を6分間とした他は、実施例1と同様にして、ゴム組成物の実施例12を得た。
工程1においてCariflex IR0307KUを70g、工程2においてRB-820を30g用い、工程5においてパーヘキサ25Bの量を1.0gとし、工程7において架橋時間を6分間とした他は、実施例1と同様にして、ゴム組成物の実施例13を得た。
工程1においてCariflex IR0307KUを70g、工程2においてRB-820を30g用い、工程7において架橋時間を6分間とした他は、実施例1と同様にして、ゴム組成物の実施例14を得た。
[工程c1]
低シスポリイソプレンゴム(クレイトンポリマー社製、Cariflex IR0307KU)100gの塊を、5インチオープンロール(安田精機株式会社製、ロール温度55℃、回転比1:1.25)にかけて押し潰しながらロールに巻きつけた。
巻きついたゴムにラウリン酸亜鉛0.5gを加えた。
次に架橋剤(日本油脂製、2,5-ジメチル-2,5-ジ(t-ブチルペルオキシ)ヘキサン、商品名パーヘキサ(R)25B)を2.0g、およびEGDMAを4.0gを添加して、均一に練った。
練りあがったゴムをロールより厚さ3〜4mmのシート状に切りだし、室温で一昼夜放置して熟成させた。
熟成したゴムを、プレス機(関西ロール株式会社製、36t・2段加熱冷却プレス)を用いて、160℃、15分(加圧15MPa)のプレス条件で架橋させ、ゴム組成物の比較例c1を得た。実施例1と同様に、上述した基準に従い物性を測定した。
工程c2を省略し、工程c3においてEGDMAを添加しなかった他は、比較例c1と同様にして、ゴム組成物の比較例c2を得た。
工程c2においてさらにイルガノックス1010を1.0g添加し、工程c3においてEGDMAを添加しなかった他は、比較例c1と同様にして、ゴム組成物の比較例c3を得た。
工程1においてCariflex IR0307KUに代えて天然ゴム(NR#1; タイ産のRibbed Smoked Sheet #1)50gを用い、工程2においてRB-820を50g用い、工程5においてパーヘキサ25Bの量を1.0gとし、工程7において架橋温度を160℃、架橋時間を7分間とした他は、実施例1と同様にして、ゴム組成物の比較例c4を得た。
工程c1においてCariflex IR0307KUに代えて高シスイソプレンゴム(日本ゼオン社製、IR 2200GA)100gを用い、工程c2を省略し、工程c3においてEGDMAを添加しなかった他は、比較例c1と同様にして、ゴム組成物の比較例c5を得た。
工程1においてCariflex IR0307KUを50g、工程2においてRB-820を50g用い、工程5においてEGDMAを添加せずパーヘキサ25Bの量を1.0gとし、工程7において架橋温度を160℃、架橋時間を7分間とした他は、実施例1と同様にして、ゴム組成物の実施例15を得た。Taber耐摩耗性についてJIS K7204(ASTM D1044)に従って測定し、またDIN耐摩耗性についてJIS K6264-2に従って測定した。
工程5においてEGDMAを2.0g添加し、工程7において架橋温度を150℃、架橋時間を6分間とした他は実施例15と同様にして、ゴム組成物の実施例16を得た。(ヘーズなどの測定は省略した。)
工程5においてEGDMAを4.0g添加し、工程7において架橋温度を150℃、架橋時間を6分間とした他は実施例15と同様にして、ゴム組成物の実施例17を得た。(ヘーズなどの測定は省略した。)
工程7において架橋時間を6分間とした他は実施例15と同様にして、ゴム組成物の実施例18を得た。
工程c2を省略し、工程c3においてEGDMAを添加しなかった他は、比較例c1と同様にして、ゴム組成物の比較例c6を得た。(ヘーズなどの測定は省略した。)
工程1においてCariflex IR0307KUに代えて高シスイソプレンゴム(日本ゼオン社製、IR 2200GA)50gを用い、工程2においてRB-820を50g用い、工程5においてEGDMAを添加せずパーヘキサ25Bの量を1.0gとし、工程7において架橋温度を160℃、架橋時間を7分間とした他は、実施例1と同様にして、ゴム組成物の比較例c7を得た。
本願の実施形態にかかる組成物には、その透明性を著しく損わないかぎりにおいて、他の成分を含めることもまた可能である。そうした他の成分としては例えば、着色剤、変性剤、加工剤(ラウリン酸など)、抗酸化剤(モノフェノール系、ビスフェノール系、ポリフェノール系、硫黄系、リン系の化合物など;例えばイルガノックス1010(BASF製)、イルガフォス168(BASF製)、イルガノックスPS800(BASF製)など)、還元剤、脱酸素剤、光安定剤、制酸剤、pH安定剤、表面処理剤、熱安定剤、着色剤、充填剤(タルク、炭酸カルシウム、カーボンブラックなど)、界面活性剤、ゲル化剤、殺生物剤、UV吸収剤(サリチル酸、ベンゾフェノン、ベンゾトリアゾール、シアノアクリラート、ヒンダードアミンなど)、ダスティング剤(ポリエチレン等のポリオレフィン、シリカ、タルク、または炭酸カルシウム粉末など)、難燃剤、またはポリリン酸が含まれるが、これらに限定はされない。
1,2−ポリブタジエンを巻きつけたロールに、工程1で先に潰しておいたポリイソプレンゴムを加え、同時にラウリン酸(0.25g)を加えながら均一に練り上げた。
工程1においてCariflex IR0307KUを90g、工程2においてRB−820を10g、工程3においてラウリン酸を0.5g用い、工程7において架橋温度を160℃、架橋時間を10分間とした他は、実施例1と同様にして、ゴム組成物の実施例3を得た。
巻きついたゴムにラウリン酸0.5gを加えた。
Claims (12)
- シリカを実質的に含まない、架橋ゴム組成物であって、
23℃における屈折率が1.500〜1.525の範囲である第一のオレフィン重合体と、
前記第一のオレフィン重合体とは異なる、第二のオレフィン重合体と
を含み、
前記組成物の2mm厚のシートでJIS K7136に従って測定したヘーズ値が、20%未満であり、
前記組成物のJIS K6253に従って測定したタイプAデュロメータ硬さ(0 sec)が、35以上である
ことを特徴とする、組成物。 - 前記第二のオレフィン重合体の23℃における屈折率と、前記第一のオレフィン重合体の23℃における屈折率との差の絶対値が、0.100以下であることを特徴とする、請求項1に記載の組成物。
- 透明な架橋ゴム組成物であって、
低cisイソプレンゴム(IR)成分と、
ブタジエンゴム(BR)、1,2-ポリブタジエンゴム、スチレンブタジエンゴム(SBR)、アクリロニトリルブタジエンゴム(NBR)、水素化ニトリルゴム(HNBR)、ウレタンゴム(U)、エチレンプロピレンゴム(EPM)、エチレンプロピレンジエンゴム(EPDM)、クロロプレンゴム(CR)、および天然ゴム(NR)からなる群から選択される、ゴム重合体成分と
を含み、
前記低cisイソプレンゴム成分と前記ゴム重合体成分の質量の合計を100質量部としたときに、前記低cisイソプレンゴム成分の量が45〜95質量部の範囲であり、
シリカを実質的に含まない
ことを特徴とする、組成物。 - 前記低cisイソプレンゴム成分のcis含量が90〜94%の範囲であることを特徴とする、請求項3に記載の組成物。
- 軟化剤としてのオイルを実質的に含まないことを特徴とする、請求項1から4のいずれか一項に記載の組成物。
- JIS K6253に従って測定したタイプAデュロメータ硬さ(30 sec)が、35以上であることを特徴とする、請求項1から5のいずれか一項に記載の組成物。
- JIS K6252に従って2mmシートで測定した引裂強度が、10N/mm以上であることを特徴とする、請求項1から6のいずれか一項に記載の組成物。
- JIS K7361-1に従って測定した全光線透過率が、88%以上であることを特徴とする、請求項1から7のいずれか一項に記載の組成物。
- シリカを実質的に含まない、透明な架橋ゴム組成物の製造方法であって、
リチウム触媒により得られた、23℃における屈折率が1.500〜1.525の範囲である第一のオレフィン重合体を用意するステップと、
リチウム触媒により得られた、前記第一のオレフィン重合体とは異なる第二のオレフィン重合体を用意するステップと、
前記第一のオレフィン重合体と、前記第二のオレフィン重合体とを混合して、混合物を得るステップと、
前記混合物に架橋剤を添加するステップと、
前記混合物を均一に混練するステップと
を含む、方法。 - 前記架橋剤は、過酸化物であることを特徴とする、請求項9に記載の方法。
- 請求項1から8のいずれか一項に記載の組成物または請求項9もしくは10に記載の方法により製造された組成物を含んだ、物品。
- 靴製品、タイヤ、衣服、雨具、アイウェア、マスク、玩具、制振材、建築部材、配線用被覆材、梱包材、コンピュータ用保護部材、コンピュータ用周辺機器、避妊用品、性具、人工乳首、紙おむつ、文房具、容器、食品用トレイ、球技用ボール、ボールチェア、および保護フィルムからなる群から選択されることを特徴とする、請求項11に記載の物品。