JP2016068970A - Sealing label - Google Patents
Sealing label Download PDFInfo
- Publication number
- JP2016068970A JP2016068970A JP2014197870A JP2014197870A JP2016068970A JP 2016068970 A JP2016068970 A JP 2016068970A JP 2014197870 A JP2014197870 A JP 2014197870A JP 2014197870 A JP2014197870 A JP 2014197870A JP 2016068970 A JP2016068970 A JP 2016068970A
- Authority
- JP
- Japan
- Prior art keywords
- label
- vertical
- perforation line
- line
- pair
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
この発明は、容器を封緘する封緘ラベル、特に、開封作業性に優れた封緘ラベルに関する。 The present invention relates to a sealing label for sealing a container, and particularly to a sealing label excellent in opening workability.
この種の封緘ラベルとしては、例えば、図9に示すようなものがある。この封緘ラベル50は、同図に示すように、熱収縮性フィルムによって形成された筒状のラベル本体51と、このラベル本体51の周方向に延びる横ミシン目線52と、ラベル本体51の上端部から下方側に延びる、横ミシン目線52にまで至らない一対の縦ミシン目線53、53とを備えており、この封緘ラベル50が装着された包装体を開封する際には、封緘ラベル50の上端部における一対の縦ミシン目線53、53間を摘んで引き下げた後、周方向に引き回すことによって、理論的には、一対の縦ミシン目線53、53間の部分が縦方向に切除され、続いて、横ミシン目線52に沿って周方向に破断されることで、封緘ラベル50の上方領域が1アクションで除去されるようになっている。
An example of this type of sealing label is shown in FIG. As shown in the figure, the
しかしながら、使用者によっては、封緘ラベル50の上端部における一対の縦ミシン目線53、53間を初めから斜め下向きに引き下げることがあり、そのようにすると、縦ミシン目線53、53に沿って破断した後、ミシン目線のない領域、即ち、縦ミシン目線53、53の下端と横ミシン目線52との間で周方向に破断してしまい、封緘ラベル50の上部を横ミシン目線52に沿って綺麗に切除することができないことがある。
However, depending on the user, the space between the pair of
従って、そのような場合は、再度、横ミシン目線52の上側の残余部分を横ミシン目線52に沿って慎重に切除するといった面倒な作業を行わなければならず、開封に手間がかかるといった問題がある。
Therefore, in such a case, it is necessary to again perform a troublesome operation of carefully cutting the remaining portion above the
そこで、この発明の課題は、1アクションで簡単かつ確実に開封することができる封緘ラベルを提供することにある。 Then, the subject of this invention is providing the sealing label which can be opened simply and reliably by one action.
上記の課題を解決するため、請求項1に係る発明は、上下端が開放された、熱収縮性を有する筒状のラベル本体と、前記ラベル本体における所定の高さ位置で周方向に延びる横ミシン目線と、前記ラベル本体の上端から下方側に延びる、前記横ミシン目線にまで至らない一対の縦ミシン目線と、前記ラベル本体の周方向における前記一対の縦ミシン目線の間に配置された補助破断線とを備え、前記補助破断線は、前記ラベル本体の縦方向の途中位置から前記横ミシン目線またはその近傍まで延びていることを特徴とする封緘ラベルを提供するものである。ここで、「前記一対の縦ミシン目線の間」とは一対の縦ミシン目線と、その上端同士、下端同士を結んで形成される略矩形領域のみを指すのではなく、一対のミシン目線の両下端、及び縦ミシン線の仮想延長線と横ミシン目線の交点、とを結んだ略矩形領域も含むものである。 また、「途中位置」 とは、縦ミシン目線の上端と横ミシン目線に囲まれた領域における途中の位置を意味する。
In order to solve the above-mentioned problems, the invention according to
また、請求項2に係る発明は、請求項1に係る発明の封緘ラベルにおいて、前記ラベル本体は、周方向の引き裂き強度が縦方向の引き裂き強度より小さいことを特徴としている。 According to a second aspect of the present invention, in the sealed label according to the first aspect of the invention, the label main body has a circumferential tear strength smaller than a longitudinal tear strength.
また、請求項3に係る発明は、請求項2に係る発明の封緘ラベルにおいて、前記ラベル本体は、JIS K 7128−1991のA法(トラウザー法)準じて測定された周方向の引き裂き強度が5N /mm以下であることを特徴としている。
The invention according to
また、請求項4に係る発明は、請求項2に係る発明の封緘ラベルにおいて、前記ラベル本体は、JIS K 7128−1991のA法(トラウザー法)準じて測定された縦方向の引き裂き強度が20N/mm以上であることを特徴としている。 According to a fourth aspect of the present invention, there is provided a sealed label according to the second aspect of the invention, wherein the label main body has a longitudinal tear strength of 20 N measured according to method A (trouser method) of JIS K 7128-1991. / Mm or more.
また、請求項5に係る発明は、請求項1、2、3または4に係る発明の封緘ラベルにおいて、前記補助破断手段は、その上端が前記縦ミシン目線の下端より上側に位置していることを特徴としている。
The invention according to claim 5 is the sealing label according to
また、請求項6に係る発明は、請求項1、2、3、4または5に係る発明の封緘ラベルにおいて、前記ラベル本体の周方向における前記一対の縦ミシン目線の外側に、前記ラベル本体の縦方向の途中位置から下方側に延びる破断防止線が形成されていることを特徴としている。
Further, the invention according to claim 6 is the sealing label according to
また、請求項7に係る発明は、請求項1、2、3、4、5または6に係る発明の封緘ラベルにおいて、前記ラベル本体の周方向における前記一対の縦ミシン目線の間に対応する部分には、前記横ミシン目線に繋がる一または複数の切目が形成されていることを特徴としている。
The invention according to claim 7 is the sealing label of the invention according to
また、請求項8に係る発明は、請求項6または7に係る発明の封緘ラベルにおいて、前記破断防止線は、前記横ミシン目線から離間していることを特徴としている。 The invention according to claim 8 is characterized in that, in the sealed label according to claim 6 or 7, the break prevention line is separated from the horizontal perforation line.
また、請求項9に係る発明は、請求項1、2、3、4、5、6、7または8に係る発明の封緘ラベルにおいて、前記ラベル本体には、開封動作を示す表示が施されていることを特徴としている。
The invention according to claim 9 is the sealing label of the invention according to
以上のように、請求項1に係る発明の封緘ラベルは、ラベル本体の周方向における一対の縦ミシン目線の間に配置された補助破断線を備え、その補助破断線は、ラベル本体の縦方向の途中位置から横ミシン目線またはその近傍まで延びているので、一対の縦ミシン目線に沿って破断した後、一方の縦ミシン目線の下端と横ミシン目線との間で周方向に破断し始めたとしても、その破断経路が補助破断線に繋がり、その後は、補助破断線に沿って横ミシン目線またはその近傍まで破断した後、その破断経路が横ミシン目線に繋がって、横ミシン目線に沿って破断していくことになる。従って、1アクションで、封緘ラベルの上部が横ミシン目線に沿って確実に切除される。
As described above, the sealing label of the invention according to
特に、請求項2に係る発明の封緘ラベルのように、周方向の引き裂き強度が縦方向の引き裂き強度より小さい場合、即ち、ラベル本体が周方向に破断しやすい場合に有効であり、請求項3に係る発明の封緘ラベルのように、ラベル本体は、JIS K 7128−1991のA法(トラウザー法)準じて測定された周方向の引き裂き強度が2.5N/mm以下であることが望ましく、請求項4に係る発明の封緘ラベルのように、ラベル本体は、JIS K 7128−1991のA法(トラウザー法)準じて測定された縦方向の引き裂き強度が39N/mm以上であることが望ましい。 In particular, as in the case of the sealed label of the invention according to claim 2, it is effective when the tearing strength in the circumferential direction is smaller than the tearing strength in the longitudinal direction, that is, when the label main body is easily broken in the circumferential direction. Like the sealed label according to the invention, the label body preferably has a tearing strength in the circumferential direction measured according to JIS K 7128-1991 Method A (trouser method) of 2.5 N / mm or less. Like the sealed label of the invention according to Item 4, the label body preferably has a tear strength in the longitudinal direction measured in accordance with A method (trouser method) of JIS K 7128-1991 of 39 N / mm or more.
また、請求項5に係る発明の封緘ラベルのように、補助破断線は、その上端が縦ミシン目線の下端より上側に位置しているものにあっては、一対の縦ミシン目線に沿って破断した後、一方の縦ミシン目線の下端から周方向に破断し始めた破断経路が補助破断線に確実に繋がるので、補助破断線を介して、一方の縦ミシン目線から横ミシン目線を確実に破断することができる。 Further, as in the case of the sealed label of the invention according to claim 5, the auxiliary breaking line is broken along a pair of vertical perforations when the upper end is located above the lower end of the vertical perforation. After that, the break path that started to break in the circumferential direction from the lower end of one vertical perforation line is securely connected to the auxiliary break line, so the horizontal perforation line is surely broken from one vertical perforation line via the auxiliary break line. can do.
また、請求項6に係る発明の封緘ラベルは、ラベル本体の周方向における一対の縦ミシン目線の外側に、ラベル本体の縦方向の途中位置から下方側に延びる破断防止線が形成されているので、一対の縦ミシン目線に沿って破断した後、一方の縦ミシン目線の下端から補助破断線に破断が伝播するのに対し、他方の縦ミシン目線の下端から周方向に破断が伝播し始めた破断経路が破断防止線に到達することで、他方の縦ミシン目線の下端から周方向への破断が防止され、一方の破断のみを横ミシン目線に伝播させ確実に破断することができる。従って、封緘ラベルの上部が、複数に分割されることなく、一体的に切除されるので、煩わしさもない。 Moreover, since the sealing label of the invention according to claim 6 is formed with a break prevention line extending downward from a midway position in the longitudinal direction of the label body on the outside of the pair of vertical perforations in the circumferential direction of the label body. After breaking along a pair of vertical perforations, the break propagates from the lower end of one vertical perforation to the auxiliary break line, whereas the break begins to propagate in the circumferential direction from the lower end of the other vertical perforation When the break path reaches the break prevention line, breakage in the circumferential direction from the lower end of the other vertical perforation line is prevented, and only one of the breaks can be propagated to the horizontal perforation line and reliably broken. Therefore, since the upper part of the sealing label is cut out integrally without being divided into a plurality of parts, there is no troublesomeness.
また、請求項7に係る発明の封緘ラベルのように、ラベル本体の周方向における一対の縦ミシン目線の間に対応する部分に、横ミシン目線に繋がる一または複数の切目が形成されているものにあっては、一対の縦ミシン目線間を、当該発明に不慣れなユーザが途中で周方向に方向転換することなく、真下に引き下げた場合であっても、横ミシン目線の高さ位置を越えて下側に破断していくことがなく、封緘ラベルの上部だけを綺麗に切除することができる。 Further, as in the sealed label of the invention according to claim 7, one or a plurality of cuts connected to the horizontal perforation line are formed in a portion corresponding to between the pair of vertical perforation lines in the circumferential direction of the label main body. In this case, even when a user unfamiliar with the present invention pulls down directly between the pair of vertical perforations without changing the direction in the circumferential direction, the horizontal perforation exceeds the height position. Therefore, only the upper part of the sealing label can be cut cleanly without breaking down.
また、請求項8に係る発明の封緘ラベルは、破断防止線が横ミシン目線から離間しているので、破断防止線で横ミシン目線の破断が停止されるおそれがなく、横ミシン目線を確実に破断することができる。 Further, in the sealing label of the invention according to claim 8, since the break prevention line is separated from the horizontal perforation line, there is no fear that the break of the horizontal perforation line is stopped by the break prevention line, and the horizontal perforation line is surely secured. Can break.
また、請求項9に係る発明の封緘ラベルは、ラベル本体には、開封動作を示す表示が施されているので、1アクションでの開封が可能であることをユーザに認識させることができる。 In the sealed label according to the ninth aspect of the invention, since the label main body is provided with a display indicating the opening operation, the user can recognize that the opening can be performed with one action.
以下、実施の形態について図面を参照して説明する。図1は、本発明の封緘ラベルの一実施形態を示している。同図に示すように、この封緘ラベル1は、点眼薬等の蓋付容器における蓋の封緘を行うために、蓋付容器全体に装着されるものであり、上下端が開放された、主として周方向に熱収縮性を有する筒状のラベル本体10と、このラベル本体10における所定の高さ位置で周方向に延びる横ミシン目線21と、ラベル本体10の上端から下方側に延びる、横ミシン目線21にまで至らない一対の縦ミシン目線22、22と、ラベル本体10の周方向における一対の縦ミシン目線22、22の間で、ラベル本体10の縦方向の途中位置から横ミシン目線21まで延びる、補助破断線としての一対の補助破断用縦ミシン目線31、31と、ラベル本体10の周方向における一対の縦ミシン目線22、22の外側で、ラベル本体10の縦方向の途中位置から横ミシン目線21まで延びる、破断防止線としての破断防止用縦ミシン目線32、32とを備えている。なお、封緘ラベル1の下方領域を容器等に接着するために、ラベル本体10の内面に感熱接着剤等からなる接着層を部分的に形成したり、封緘ラベル1の容器等に対する滑り性を向上させるために、ラベル本体10の内面に滑り層などを形成してもよい。
Hereinafter, embodiments will be described with reference to the drawings. FIG. 1 shows an embodiment of the sealing label of the present invention. As shown in the figure, this
前記ラベル本体10は、熱収縮性フィルムの両側端部を重ね合わせ、この重ね合わせ部分を溶剤又は接着剤などを用いて接着することによって筒状に形成されている。熱収縮性フィルムは、ポリスチレン系、ポリオレフィン系、ポリスチレン系、塩化ビニル等であってもよい。
The label
また、前記積層フィルムは、全体として熱収縮性を有していていればよく、例えば、熱収縮性を有さないフィルムを含んでいてもよい。前記熱収縮性フィルムは、成膜後に少なくとも一軸延伸し、所要の温度で熱エージングすることにより得ることができる。
前記熱収縮性フィルムは、所要温度(例えば80℃〜100℃)で少なくとも一方向(主たる熱収縮方向)に熱収縮可能であり、この熱収縮性フィルムの一方向が周方向となるように熱収縮性フィルムを筒状に形成することにより、主として周方向に熱収縮性を有するラベル本体10が構成されている。
前記熱収縮性フィルムの厚みは、特に限定されないが、例えば20〜120μmであり、好ましくは、30〜80μmである。
Moreover, the said laminated | multilayer film should just have heat-shrink property as a whole, for example, may contain the film which does not have heat-shrink property. The heat-shrinkable film can be obtained by at least uniaxial stretching after film formation and heat aging at a required temperature.
The heat-shrinkable film can be thermally shrunk in at least one direction (main heat-shrinking direction) at a required temperature (for example, 80 ° C. to 100 ° C.), and heat is applied so that one direction of the heat-shrinkable film is a circumferential direction. By forming the shrinkable film into a cylindrical shape, the
Although the thickness of the said heat-shrinkable film is not specifically limited, For example, it is 20-120 micrometers, Preferably, it is 30-80 micrometers.
前記熱収縮性フィルムは、JIS K 7128−1991(プラスチック及びシートの引裂試験方法)のA法(トラウザー法)に準じて測定した引裂き強度が、縦方向については20N/mm以上、好ましくは30N/mm以上、さらに好ましくは35N/mm以上、特に、好ましくは、35N/mm〜200N/mmであり、周方向については5N/mm以下、好ましくは3N/mm以下、さらに好ましくは2.5N/mm以下、特に、好ましくは、2.5N/mm〜1N/mmである。縦方向の引裂き強度が20N/mmを下回ると、縦方向に引き裂きやすくなるので、一対の縦ミシン目線22、22の下端以降の破断経路が、補助破断用縦ミシン目線31に繋がることなく、そのまま横ミシン目21まで延びてしまい、1アクションで開封できなくなるからである。また、縦方向の引裂き強度が200N/mmを超えると、縦方向に引き裂きにくくなるので、縦方向の破断性を向上させるために、一対の縦ミシン目線22、22を構成している貫通孔を大きくしなければならない等、設計上の制約を被るためである。具体的には、貫通孔の縦方向の長さ:非貫通部の縦方向の長さが、通常、0.7:0.7や0.5:0.8であったものを、1.5:0.5に変更しなければならない。また、周方向の引裂き強度が5N/mmを上回ると、一対の縦ミシン目線22、22の下端以降の破断経路が、補助破断用縦ミシン目線31に繋がりにくくなるからである。なお、デザイン印刷層などは引裂き強度に殆ど影響しないことから、前記熱収縮性フィルムの縦方向の引裂き強度は、ラベル本体10の縦方向の引裂き強度に略等しい。こういった引裂き強度を満足する熱収縮性フィルムの材料としては、ポリエステル系フィルムを含んでいれば、特に限定されるものではなく、ポリエステル系フィルムの単層フィルムまたはポリエステル系フィルムを含む積層フィルムであってもよい。
The heat-shrinkable film has a tear strength measured in accordance with A method (trouser method) of JIS K 7128-1991 (plastic and sheet tear test method) in the longitudinal direction of 20 N / mm or more, preferably 30 N / mm or more, more preferably 35 N / mm or more, particularly preferably 35 N / mm to 200 N / mm, and 5 N / mm or less in the circumferential direction, preferably 3 N / mm or less, more preferably 2.5 N / mm. Hereinafter, it is particularly preferably 2.5 N / mm to 1 N / mm. If the tear strength in the vertical direction is less than 20 N / mm, it becomes easy to tear in the vertical direction, so that the break path after the lower ends of the pair of
前記ポリエステル系フィルムとしては、芳香族ポリエステル系フィルム、脂肪族ポリエステル系フィルムなどが挙げられる。
芳香族ポリエステル系フィルムとしては、ジカルボン酸成分としてテレフタル酸を主成分とし且つジオール成分としてエチレングリコールを主成分としたポリエチレンテレフタレート系フィルムなどが挙げられ、脂肪族ポリエステル系フィルムとしては、ポリ乳酸を主成分とするポリ乳酸系フィルムなどが挙げられる。
Examples of the polyester film include aromatic polyester films and aliphatic polyester films.
Examples of the aromatic polyester film include a polyethylene terephthalate film containing terephthalic acid as a main component as a dicarboxylic acid component and ethylene glycol as a main component as a diol component. A polylactic acid is mainly used as an aliphatic polyester film. Examples include polylactic acid film as a component.
前記積層フィルムは、ポリエステル系フィルムを2層以上積層した積層フィルム、又は、ポリエステル系フィルムの1層又は2層以上と他の層の1層又は2層以上とを積層した積層フィルムであり、好ましくは、積層フィルムは、ポリエステル系フィルム/他の層/ポリエステル系フィルムの3層構造である。
なお、前記他の層は特に限定されず、例えば、ポリスチレン、スチレン−ブタジエン共重合体などのポリスチレン系樹脂、ポリプロピレン、環状ポリオレフィンなどのポリオレフィン系樹脂、ポリカーボネート、ポリ塩化ビニル系樹脂などの熱可塑性樹脂からから選ばれる1種単独、又は2種以上の混合物を含む樹脂フィルム;金属蒸着層;不織布などの断熱層などが挙げられる。
The laminated film is a laminated film obtained by laminating two or more layers of a polyester film, or a laminated film obtained by laminating one layer or two layers or more of a polyester film and one layer or two or more layers of other layers, The laminated film has a three-layer structure of polyester film / other layers / polyester film.
The other layers are not particularly limited. For example, polystyrene resins such as polystyrene and styrene-butadiene copolymers, polyolefin resins such as polypropylene and cyclic polyolefin, thermoplastic resins such as polycarbonate and polyvinyl chloride resins, and the like. A resin film containing one kind selected from the above or a mixture of two or more kinds; a metal vapor-deposited layer; and a heat insulating layer such as a nonwoven fabric.
前記熱収縮性フィルムには、必要に応じてデザイン印刷層が設けられていてもよい。デザイン印刷層は、熱収縮性フィルムの表面又は裏面に設けることができる。また、前記熱収縮性フィルムは、例えば、乳白色のような非透明なフィルムまたは透明性に優れたフィルムを用いてもよいが、デザイン印刷層を裏面側に設ける場合には透明性に優れたものが用いられる。 The heat-shrinkable film may be provided with a design printing layer as necessary. The design print layer can be provided on the front surface or the back surface of the heat-shrinkable film. The heat-shrinkable film may be, for example, a non-transparent film such as milky white or a film having excellent transparency. However, when the design print layer is provided on the back side, the film has excellent transparency. Is used.
前記横ミシン目線21は、ラベル本体10の縦方向の中間位置に配置されており、ラベル本体10の全周にわたって形成されている。なお、ラベル本体10の周方向に延びる横ミシン目線21は、縦方向に所要間隔を開けて2本以上形成されていてもよい。1本の横ミシン目線21は、厳密にミシン目線が1本だけ形成されている場合の他、2本隣接して形成されている場合を含む意味であり、本明細書において、「ミシン目線が2本隣接して形成」とは、2本のミシン目線が1mm以内の間隔を有して平行に形成されていることをいう。
The
蓋付容器を封緘する目的で用いられる封緘ラベル1は、胴部と蓋部の境界部分またはその近傍部分に横ミシン目線21が一致するように、容器に装着される。このため、横ミシン目線21の形成位置は、容器の種類に応じて適宜設計される。封緘ラベル1は、横ミシン目線21を境にして、上部領域と下部領域に区画されており、このうち、上部領域が開封時に切除される。
The
ここで、本明細書において、「ミシン目線」とは、ミシン針の縫い跡の如くフィルムの表面から裏面に貫通する複数の貫通孔が所要間隔を開けて形成された、方向性を有する複数の貫通孔の集合をいう。かかるミシン目線は、方向性を有して並んだ各貫通孔の間に、非貫通部(貫通処理の成されていないフィルム部分)が存在する。1つの貫通孔の正面視形状は、細長い直線状、針穴状(打ち抜き略円形状又は略楕円形状)などが挙げられる。ミシン目線に沿ってフィルムが切れ易くなることから、ミシン目線の貫通孔の形状は、細長い直線状が好ましい。また、本明細書において、「切目」とは、フィルムに設けられた切り口をいい、ミシン目との相違点として、単独でもその切離機能を果たせることがある。 切目の長さは、例えば3mm〜10mmであり、好ましくは、5mm〜8mmである。 Here, in the present specification, the “perforation line” means a plurality of directional holes in which a plurality of through holes penetrating from the front surface of the film to the back surface thereof are formed at predetermined intervals like a sewing mark of a sewing needle. A collection of through holes. The perforation line has a non-penetrating part (a film part not subjected to a penetrating treatment) between the through holes arranged with directivity. Examples of the front view shape of one through hole include an elongated linear shape, a needle hole shape (a punched substantially circular shape or a substantially elliptical shape), and the like. Since the film is easily cut along the perforation line, the shape of the through hole of the perforation line is preferably an elongated straight line. In the present specification, the “cut” means a cut provided in the film, and as a difference from the perforation, the cut function may be achieved by itself. The length of the cut is, for example, 3 mm to 10 mm, preferably 5 mm to 8 mm.
前記横ミシン目線21の1つの貫通孔の周方向における長さは、特に限定されないが、例えば、0.3mm〜3mmであり、好ましくは、0.5mm〜2mmである。また、横ミシン目線21の1つの非貫通部の周方向における長さは、特に限定されないが、例えば、0.3mm〜3mmであり、好ましくは、0.3mm〜1mmである。
The length in the circumferential direction of one through hole of the
前記一対の縦ミシン目線22、22は、両者の間隔が徐々に狭まるように、ラベル本体10の上端から斜め下方側に向かって直線状に延びているが、横ミシン目線21にまで至っておらず、縦ミシン目線22の下端(縦ミシン目線22の複数の貫通孔のうちで、最も下側に位置する貫通孔の下端)と横ミシン目線21との間には、所要のミシン目線の非形成領域が存在している。それぞれの縦ミシン目線22の下端と横ミシン目線21との間の長さL1は、例えば、2.5mm〜20mmであり、好ましくは、3mm〜10mmであり、より好ましくは、4mm〜6mmである。この実施形態では、L1=3mmに設置されている。この間の長さL1が余りに小さいと、縦ミシン目線22の非貫通部の長さと殆ど異ならず、縦ミシン目線22が実質的に横ミシン目線21と繋がり、他方、この間の長さL1が余りに大きいと相対的に縦ミシン目線22の長さが短くなり、ユーザが縦ミシン目線を把持して開封しづらくなる。なお、一対の縦ミシン目線22、22は、両者の間隔が徐々に狭まるように、ラベル本体10の上端から斜め下方側に向かって直線状に延びているが、これに限定されるものではなく、一対の縦ミシン目線は、平行に形成されていてもよく、曲線状であってもよい。
The pair of
一対の縦ミシン目線22、22の間隔は、ラベル本体10の周長の半分未満であり、好ましくは、ラベル本体10の周長の0.1倍〜0.3倍である。具体的には、一対の縦ミシン目線22、22の間隔は、ラベル本体10の周長にもよるが、例えば、3mm〜20mmである。この実施形態では、ラベル本体10の周長が67mmであり、一対の縦ミシン目線22、22の上端の間隔L2が18mm、下端の間隔L3が14mmである。縦ミシン目線22を構成している1つの貫通孔の縦方向の長さは、特に限定されないが、例えば、0.3mm〜3mmであり、好ましくは、0.5mm〜2mmである。縦ミシン目線22の1つの非貫通部の縦方向の長さは、特に限定されないが、例えば、0.3mm〜2mmであり、好ましくは、0.5mm〜1.5mmである。
The distance between the pair of
前記ラベル本体10の上端には、一対の縦ミシン目線22、22間に略台形状の摘み部11が延出されており、この封緘ラベル1では、摘み部11の両側縁の基端部に、縦ミシン目線22を構成している最上位の貫通孔が、ラベル本体10の上端と交差して配置されている。従って、摘み部11の両側縁の基端部に対応するラベル本体10の上端には、貫通孔に起因した切込みが形成されることになる。
A substantially
前記一対の補助破断用縦ミシン目線31、31は、所定の間隔を開けた状態で平行に配設されており、それぞれの上端部と縦ミシン目線22の下端部とが上下方向に重なるように、ラベル本体10の上部領域における縦方向の中間位置から横ミシン目線21まで延びている。補助破断用縦ミシン目線31の上端の高さ位置は、特に限定されないが、補助破断用縦ミシン目線31の上端は、縦ミシン目線22の下端よりも上側に位置していることが望ましい。また、補助破断用縦ミシン目線31と縦ミシン目線22の下端との間隔も、特に限定されないが、2mm〜4mmの間に設定しておくことが望ましい。なお、この封緘ラベル1では、各補助破断用縦ミシン目線31の長さL4が5mm、一対の補助破断用縦ミシン目線31、31の間隔L5が8mm、各補助破断用縦ミシン目線31と隣り合う縦ミシン目線22の下端との間隔L6が3mm、補助破断用縦ミシン目線31の上端部と縦ミシン目線22の下端部との上下方向の重なり長さが2mmに設定されている。
The pair of auxiliary perforating
前記補助破断用縦ミシン目線31を構成している1つの貫通孔の縦方向の長さは、特に限定されないが、例えば、0.3mm〜3mmであり、好ましくは、0.5mm〜2mmである。補助破断用縦ミシン目線31の1つの非貫通部の縦方向の長さは、特に限定されないが、例えば、0.3mm〜2mmであり、好ましくは、0.5mm〜1.5mmである。
The length in the vertical direction of one through hole constituting the auxiliary perforation
前記破断防止用縦ミシン目線32は、補助破断用縦ミシン目線31と同様に、それぞれの上端部と縦ミシン目線22の下端部とが上下方向に重なるように、ラベル本体10の上部領域における縦方向の中間位置から横ミシン目線21まで延びている。また、本実施例では、補助破断用縦ミシン目線31と平行で同一長さとなっているが、これに限定されるわけではなく、平行でなくてもよいし、同一の長さでなくてもよい。破断防止用縦ミシン目線32の上端の高さ位置は、特に限定されないが、破断防止用縦ミシン目線32の上端は、縦ミシン目線22の下端よりも上側に位置していることが望ましい。また、破断防止用縦ミシン目線32と縦ミシン目線22の下端との間隔も、特に限定されないが、2mm〜4mmの間に設定しておくことが望ましい。なお、この封緘ラベル1では、各破断防止用縦ミシン目線32の長さL7が5mm、破断防止用縦ミシン目線32と隣り合う補助破断用縦ミシン目線31との間隔L8が6mm、各破断防止用縦ミシン目線32と隣り合う縦ミシン目線22の下端との間隔L9が3mm、破断防止用縦ミシン目線32の上端部と縦ミシン目線22の下端部との上下方向の重なり長さが2mmに設定されている。
Similar to the auxiliary perforation
また、ラベル本体10には、図3に示すように、一対の縦ミシン目線22、22間の領域に開封動作を示す矢印が印刷されており、摘み部11を摘んで、斜め下方に引き下げ、そのまま周方向に引き回すことによって、1アクションで開封可能であることを開封者に知らしめるようになっている。
In addition, as shown in FIG. 3, the label
上述した封緘ラベル1は、例えば、次のようにして製造できる。従来公知の方法で、ラベル本体10が連続的に繋がった、シート状に折り畳まれた長尺帯状のラベル基材を準備する。この長尺帯状のラベル基材は、例えば、長尺状の熱収縮性フィルムを筒状にしながらその両側端部を接着した後、それをシート状に折り畳むことによって得られる。図5において、この長尺帯状のラベル基材LMの一方側から扁平体全体の厚み方向に貫通するように、横ミシン目線21、縦ミシン目線22、補助破断用縦ミシン目線31及び破断防止用縦ミシン目線32をそれぞれ形成すると共に、ラベル基材LMを一点鎖線で示す切断予定線clにて幅方向に切断することにより、個別のラベル本体10が得られる。なお、ミシン目線の形成手段は、特に限定されず、針、刃、レーザー光線などが挙げられる。
The
図6(a)、(b)は、封緘ラベル1が蓋付容器CVに装着されたラベル付き容器LVを示している。蓋付容器CVとしては、胴部Bと胴部Bの上端部に開閉可能に取り付けられた蓋部Cとを有し、目薬などの医薬品、栄養飲料などの飲料、化粧品、調味料、食品などが収納された容器などが挙げられる。
まず、蓋部Cの下端付近に横ミシン目線21が位置するように、封緘ラベル1を蓋付容器CVに外嵌した後、その封緘ラベル1の全体を所定温度(例えば、80℃〜100℃)に加熱すると、封緘ラベル1が周方向に収縮し、蓋付容器CVの外面に密着する。なお、上方領域を蓋付容器CVの天面よりも上方に出た状態で封緘ラベル1を外嵌した場合には、同図(b)に示すように、熱収縮により、封緘ラベル1の上部領域の一部(この上部領域の一部には、摘み部11が含まれている)が、蓋部Cの天面の周縁部に回り込むように折れ曲がり、蓋部Cにおける天面の周端部に密着する。
FIGS. 6A and 6B show a labeled container LV in which the
First, after the
このようにして得られたラベル付き容器LVを開封する際、右利きの人は、左手でラベル付き容器LVの胴部を持ち、右手で摘み部11を摘んで、例えば、斜め右下方に引き下げると、図7(a)に示すように、一対の縦ミシン目線22,22に沿ってラベル本体10が帯状に切除されていき、一方の縦ミシン目22(この場合は、右側の縦ミシン目22)が先に下端まで破断される。
When opening the labeled container LV obtained in this way, a right-handed person holds the body of the labeled container LV with his left hand, picks the
その後、破断した一方の縦ミシン目22(右側の縦ミシン目22)の下端から引裂強度の小さい周方向に破断していき、その破断経路が左隣りの補助破断用縦ミシン目線31に到達する。そして、その補助破断用縦ミシン目線31に沿ってさらに下方側に破断していき、その破断経路が横ミシン目21に到達する。
Thereafter, the fracture occurs in the circumferential direction with a small tear strength from the lower end of one broken vertical perforation 22 (right vertical perforation 22), and the fracture path reaches the auxiliary fracture
このとき、他方の縦ミシン目22(左側の縦ミシン目22)も、その下端まで破断され、そこから引裂強度の小さい周方向に破断していき、その破断経路が左隣りの破断防止用縦ミシン目線32に到達するが、左側の破断経路は、右側の破断経路に比べて、急激に屈曲することになるので、破断防止用縦ミシン目線32に沿って下方側に破断することなく、破断防止用縦ミシン目線32に到達した時点で、周方向への破断が停止される。
At this time, the other vertical perforation 22 (the left vertical perforation 22) is also broken to the lower end thereof, and then is broken in the circumferential direction with a small tear strength, and the fracture path is the left adjacent break prevention vertical. Although it reaches the
従って、切除された帯状部分をそのまま周方向に引き回すと、同図(b)に示すように、右側の破断経路が到達した横ミシン目21に沿って破断していき、最終的に、切除された帯状部分が切り離されることなく、封緘ラベル1の上部領域が切除される。
Therefore, when the cut strip-like portion is drawn around in the circumferential direction as it is, as shown in FIG. 5B, the right side breaking path is broken along the
以上のように、この封緘ラベル1は、ラベル本体10の周方向における一対の縦ミシン目線22、22の間に、ラベル本体10の縦方向の途中位置から横ミシン目線21まで延びる補助破断用縦ミシン目線31が形成されているので、周方向に引き裂きやすいラベル本体10であっても、一方の縦ミシン目線22に沿って破断した破断経路が、補助破断用縦ミシン目線31を介して、横ミシン目21に確実に到達するので、1アクションで、封緘ラベルの上部を横ミシン目線22に沿って確実に切除することができる。
As described above, the
また、この封緘ラベル1は、ラベル本体10の周方向における一対の縦ミシン目線22、22の外側に、ラベル本体10の縦方向の途中位置から下方側に延びる破断防止用縦ミシン目線32が形成されているので、周方向に引き裂きやすいラベル本体10であっても、一対の縦ミシン目線22、22に沿って破断した後、他方の縦ミシン目線22の下端から周方向に破断し始めた破断経路が破断防止用縦ミシン目線32に到達することで、他方の縦ミシン目線22の下端から周方向への破断が阻止され、横ミシン目線21だけを確実に破断することができる。従って、封緘ラベルの上部領域が、複数に分割されることなく、一体的に切除されるので、煩わしさもない。
Further, the
なお、上述した実施形態では、補助破断用縦ミシン目線31の上端部と縦ミシン目線22の下端部とが上下方向に重なっているが、これに限定されるものではなく、例えば、ラベル本体10が縦方向にある程度の破断性を有していれば、補助破断用縦ミシン目線31の上端と縦ミシン目線22の下端とが同一高さであってもよく、補助破断用縦ミシン目線31の上端と縦ミシン目線22の下端とが高さ方向に僅かに離間していてもよい。
In the above-described embodiment, the upper end portion of the auxiliary perforation
また、上述した実施形態では、一対の補助破断用縦ミシン目線31、31を一対の縦ミシン目線22、22の間に配設しているが、これに限定されるものではなく、1本の補助破断用縦ミシン目線を一対の縦ミシン目線22、22の間の中央位置に配設してもよく、3本以上の補助破断用縦ミシン目線を一対の縦ミシン目線22、22の間に配置してもよい。
In the embodiment described above, the pair of auxiliary perforation
また、上述した実施形態では、補助破断線として、ミシン目線を採用しているが、これに限定されるものではなく、一または複数の切目線やハーフカット線を採用することも可能である。 In the above-described embodiment, the perforation line is adopted as the auxiliary break line, but the invention is not limited to this, and one or a plurality of cut lines and half cut lines can also be adopted.
また、上述した実施形態では、破断防止用縦ミシン目線32がそれぞれの上端部と縦ミシン目線22の下端部とが上下方向に重なるように、これに限定されるものではなく、例えば、ラベル本体10が縦方向にある程度の破断性を有していれば、破断防止用縦ミシン目線32の上端と縦ミシン目線22の下端とが同一高さであってもよく、破断防止用縦ミシン目線32の上端と縦ミシン目線22の下端とが高さ方向に僅かに離間していてもよい。
Further, in the above-described embodiment, the
また、上述した実施形態では、破断防止線としてとして、ミシン目線を採用しているが、これに限定されるものではなく、ハーフカット線を採用することも可能である。 In the above-described embodiment, a perforation line is employed as the break prevention line, but the present invention is not limited to this, and a half-cut line can also be employed.
また、上述した実施形態では、破断防止用縦ミシン目線32がラベル本体10の上部領域における縦方向の中間位置から横ミシン目線21まで延びているが、このように、破断防止用縦ミシン目線32と横ミシン目線21とが繋がっていると、横ミシン目線21に沿って破断する際、破断防止用縦ミシン目線32の接続部分で横ミシン目線21の破断が止まってしまうおそれがあるので、例えば、破断防止用縦ミシン目線32の下端と横ミシン目線21との間に僅かな隙間(例えば、2mm程度)を形成するようにしてもよい。
Further, in the above-described embodiment, the
また、上述した実施形態では、ラベル本体10の全周にわたって横ミシン目線21が形成されているが、ラベル付き容器10を開封する際、摘まんだ摘み部11を、途中で方向を変更することなく、真下に引き下げてしまうと、横ミシン目線21を越えて破断してしまうおそれがあるので、例えば、ラベル本体10の全周にわたって横ミシン目線21を形成するのではなく、一対の縦ミシン目線22、22の間に対応する部分については、一または複数の切目を形成するようにしてもよい。
In the above-described embodiment, the
また、上述した実施形態では、一対の縦ミシン目線22、22における対応する左右の貫通孔が平行になるように配置されているが、これに限定されるものではなく、例えば、図8に示すように、一対の縦ミシン目線22、22における対応する左右の貫通孔がハの字形状になるように配置することで、縦ミシン目線22、22に加わる破断力が外方向に逃げていくようにしてもよい。摘み部11を摘んで破断を開始しても、破断が縦ミシン目線22、22より内側に向かっていく傾向がみられる場合に有効である。
Further, in the above-described embodiment, the corresponding left and right through holes in the pair of
また、上述した実施形態では、一対の縦ミシン目線22、22の外側に破断防止線としての破断防止用縦ミシン目線32、32を形成しているが、破断防止線は必ずしも必要ではなく、ラベル本体10の周方向における一対の縦ミシン目線22、22の間に補助破断線が少なくとも1本形成されていればよい。
In the above-described embodiment, the break prevention
以下、実施例を示して、本発明を詳細に説明する。ただし、本発明は、下記実施例に限定されるものではない。 Hereinafter, the present invention will be described in detail with reference to examples. However, the present invention is not limited to the following examples.
[実施例]
熱収縮性フィルムとして、一方向に熱収縮性を有する厚み50μmのポリエチレンテレフタレートフィルム(三菱樹脂(株)製の商品名「LX18S」)を用いた。この熱収縮性フィルムを、熱収縮方向を周方向にして筒状に形成することにより、周長約70mm、軸方向長さ55mm の筒状フィルムを形成した。この筒状フィルム(ポリエチレンテレフタレートフィルム)の縦方向及び周方向の引裂き強度をそれぞれ、JIS K 7128−1991のA法(トラウザー法)に従って測定した。その結果を、表1に示す。
この筒状フィルムに、図1乃至図4に示すような、縦ミシン線22、横ミシン線21、補助破断線31並びに破断防止線32を形成することにより、実施例の封緘ラベルを作製した。
なお、縦ミシン線22、横ミシン線21、補助破断線31並びに破断防止線32の貫通孔の長さは全て共通で0.7mm、非貫通部の長さは全て共通で0.7mmとした。また、縦ミシン線22の下端と補助破断線31の間隔、及び、縦ミシン線22の下端と破断防止線32の間隔は、3mmとし、縦ミシン線22の下端と横ミシン線21との間の長さは、5mmとした(図1参照)。
得られた熱収縮性筒状ラベルを、周長約63mm、軸方向の長さ約52mm の蓋付点眼容器に熱収縮装着することにより、筒状ラベル付き容器を作製した。
[Example]
A 50 μm thick polyethylene terephthalate film (trade name “LX18S” manufactured by Mitsubishi Plastics, Inc.) having heat shrinkability in one direction was used as the heat shrinkable film. By forming this heat-shrinkable film into a cylindrical shape with the heat-shrink direction being the circumferential direction, a cylindrical film having a circumferential length of about 70 mm and an axial length of 55 mm was formed. The tear strength in the longitudinal direction and circumferential direction of this tubular film (polyethylene terephthalate film) was measured in accordance with method A (trouser method) of JIS K 7128-1991. The results are shown in Table 1.
By forming the
Note that the lengths of the through holes of the
The obtained heat-shrinkable cylindrical label was heat-shrink mounted on a lidded eye drop container having a circumferential length of about 63 mm and an axial length of about 52 mm to produce a container with a cylindrical label.
[比較例]
熱収縮性フィルムとして、一方向に熱収縮性を有する厚み50μmのポリスチレンフィルム(シーアイ化成(株)製の商品名「BS55S)を用いたこと以外は、実施例と同様にして、引裂き強度を測定し、筒状ラベル付き容器を作製した。
[Comparative example]
The tear strength was measured in the same manner as in Example except that a 50 μm thick polystyrene film (trade name “BS55S” manufactured by C-I Kasei Co., Ltd.) having heat shrinkability in one direction was used as the heat shrinkable film. And the container with a cylindrical label was produced.
[開封試験]
実施例及び比較例の筒状ラベル付き容器のそれぞれについて、十人の試験者が、縦ミシン線22の間における熱収縮性筒状ラベルの上端部を摘み、それを下方に引き出した後、周方向に引き出して評価した。その結果、1アクションで封緘ラベルの上部を横ミシン目線22に沿って確実に切除することができた人数を、表1に示す。
[Opening test]
For each of the cylindrically labeled containers of the examples and comparative examples, ten testers picked the upper end portion of the heat-shrinkable cylindrical label between the vertical
実施例の熱収縮性筒状ラベルは、熱収縮性筒状ラベルの上方領域をほぼ誰でも簡易に且つ確実に除去できた。
一方、比較例の熱収縮性筒状ラベルは、誰でもが簡易に且つ確実に除去できるものではなかった。
In the heat-shrinkable cylindrical label of the example, almost anyone could easily and reliably remove the upper region of the heat-shrinkable cylindrical label.
On the other hand, the heat-shrinkable cylindrical label of the comparative example could not be removed easily and reliably by anyone.
本発明は、蓋付容器を封緘する場合に利用することができる。 The present invention can be used when sealing a container with a lid.
1 封緘ラベル
10 ラベル本体
11 摘み部
21 横ミシン目線
22 縦ミシン目線
31 補助破断用縦ミシン目線(補助破断線)
32 破断防止用縦ミシン目線(破断防止線)
LM ラベル基材
B 胴部
C 蓋部
CV 蓋付容器
LV ラベル付き容器
DESCRIPTION OF
32 Vertical perforation line for preventing breakage (breakage prevention line)
LM Label base material B Body C Lid CV Container with lid LV Container with label
Claims (9)
前記ラベル本体における所定の高さ位置で周方向に延びる横ミシン目線と、
前記ラベル本体の上端から下方側に延びる、前記横ミシン目線にまで至らない一対の縦ミシン目線と、
前記ラベル本体の周方向における前記一対の縦ミシン目線の間に配置された補助破断線とを備え、
前記補助破断線は、前記ラベル本体の縦方向の途中位置から前記横ミシン目線またはその近傍まで延びていることを特徴とする封緘ラベル。 A cylindrical label body having heat shrinkability, with upper and lower ends opened,
A horizontal perforation line extending in the circumferential direction at a predetermined height position in the label body;
A pair of vertical perforations extending from the upper end of the label body to the lower side and not reaching the horizontal perforations;
An auxiliary breaking line arranged between the pair of vertical perforations in the circumferential direction of the label body,
The sealing label, wherein the auxiliary breaking line extends from a midway position in the longitudinal direction of the label main body to the horizontal perforation line or the vicinity thereof.