JP2015229905A - Repair method for waterproof sheet - Google Patents

Repair method for waterproof sheet Download PDF

Info

Publication number
JP2015229905A
JP2015229905A JP2014117738A JP2014117738A JP2015229905A JP 2015229905 A JP2015229905 A JP 2015229905A JP 2014117738 A JP2014117738 A JP 2014117738A JP 2014117738 A JP2014117738 A JP 2014117738A JP 2015229905 A JP2015229905 A JP 2015229905A
Authority
JP
Japan
Prior art keywords
waterproof
waterproof sheet
coating
base
sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2014117738A
Other languages
Japanese (ja)
Other versions
JP2015229905A5 (en
Inventor
杉山　明宏
Akihiro Sugiyama
明宏 杉山
健二 熊谷
Kenji Kumagai
健二 熊谷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dyflex Corp
Original Assignee
Dyflex Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dyflex Corp filed Critical Dyflex Corp
Priority to JP2014117738A priority Critical patent/JP2015229905A/en
Publication of JP2015229905A publication Critical patent/JP2015229905A/en
Publication of JP2015229905A5 publication Critical patent/JP2015229905A5/ja
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a repair method for a waterproof sheet that generates only a small amount of industrial wastes, inhibits water leakage, offers an efficient connecting structure for rising and internal corner parts, and maintains excellent workability.SOLUTION: A repair method for a waterproof sheet is for repairing a waterproof sheet 2 laid on a substrate 1 with an adhesive or mechanical means in between, and comprises the steps for: partially cutting out the waterproof sheet 2 laid on the substrate 1, for partially exposing the substrate 1; applying a primer 3 on the exposed substrate 1 and a part of the waterproof sheet 2 around the exposed substrate 1; and applying a first waterproof coating material 4 on the exposed substrate 1 and the part of the waterproof sheet 2 around the exposed substrate 1, over the primer 3.

Description

本発明は、防水シートの改修方法に関する。  The present invention relates to a method for repairing a waterproof sheet.

従来、ビル、マンション、学校などの屋上、ベランダ、開放廊下などの防水には、塩ビシート防水工法が広く用いられている。塩ビシート防水工法としては、塩化ビニル樹脂に、可塑剤、充填剤などを添加し補強繊維を積層して成型した塩ビシートを、接着剤などで下地に貼り付ける密着工法と、前記の塩ビシートをディスク板などで固定する機械固定工法とが挙げられる（例えば、特許文献１参照）。
塩ビシート防水工法の特徴としては、下記のような特徴が挙げられる。
（１）露出防水仕様で軽量のため、構造体への負担を軽減し、防水層のメンテナンスを目視で確認できる。
（２）定期的にトップコートを塗り替える必要がないため、メンテナンスを簡略化できる。
（３）防水保証がトップコートの塗替えなしで１０年間である。
（４）トータルコストを削減できる。
（５）耐候性、耐薬品性、耐摩耗性に優れる。 Conventionally, a PVC sheet waterproofing method has been widely used for waterproofing roofs of buildings, condominiums, schools, etc., verandas, and open corridors. As a PVC sheet waterproofing method, a PVC sheet formed by adding a plasticizer, a filler and the like to a vinyl chloride resin and laminating reinforcing fibers, and sticking it to the base with an adhesive, etc., and the above PVC sheet And a machine fixing method for fixing with a disk plate or the like (see, for example, Patent Document 1).
The following characteristics are mentioned as the characteristics of the PVC sheet waterproofing method.
(1) Since it is lightweight with an exposed waterproof specification, the burden on the structure can be reduced and the maintenance of the waterproof layer can be visually confirmed.
(2) Since it is not necessary to repaint the top coat regularly, maintenance can be simplified.
(3) The waterproof guarantee is 10 years without repainting the top coat.
(4) The total cost can be reduced.
(5) Excellent weather resistance, chemical resistance, and wear resistance.

特開２００５−１４６７７４号公報JP 2005-146774 A

従来、塩ビシート防水を、塩ビシート防水工法で改修する場合、以下のような課題があった。
密着工法で改修する場合、既設の塩ビシートを撤去して、下地を修正する必要がある。そのため、工期が長い上に、産業廃棄物（塩ビシート等）が発生する。よって、密着工法による改修は現実的ではない。
一方、機械固定工法で改修する場合、既設の塩ビシートの上に、新規の塩ビシートを設置した後、両方の塩ビシートの厚み方向に対して、ドリルで穿孔し、円盤状または帯状の板を介してリベットにより、下地に対して塩ビシートを点状に固定する。しかしながら、機械固定工法では、（１）穿孔時に騒音や振動が発生するため、建物の居住者（特に最上階）に悪影響を及ぼすことがある、（２）既設の防水層を穿孔するため、作業途中の急な降雨により漏水が発生するおそれがある、（３）機械固定工法で設置された塩ビシート防水を、再度、機械固定工法で改修した場合、塩ビシートの立ち上がりおよび入り隅周辺の納まりが困難である、という課題があった。 Conventionally, when PVC sheet waterproofing is repaired by the PVC sheet waterproofing method, there are the following problems.
When refurbishing with the close-in construction method, it is necessary to remove the existing PVC sheet and modify the groundwork. Therefore, the construction period is long and industrial waste (such as PVC sheet) is generated. Therefore, refurbishment by the close contact method is not realistic.
On the other hand, when refurbishing with the machine fixing method, after installing a new PVC sheet on the existing PVC sheet, drill in the thickness direction of both PVC sheets with a drill to form a disk-shaped or strip-shaped plate. The PVC sheet is fixed to the base with a rivet. However, in the machine fixing method, (1) noise and vibration are generated when drilling, which may adversely affect the residents of the building (especially the top floor). (2) There is a risk of water leakage due to sudden rain on the way. (3) If the waterproof PVC sheet installed by the machine fixing method is repaired again by the machine fixing method, the PVC sheet will rise and fit around the corner. There was a problem that it was difficult.

本発明は、上記事情に鑑みてなされたものであって、産業廃棄物の発生量が少なく、漏水が発生し難く、立ち上がりおよび入り隅周辺の納まりがよく、施工性に優れる防水シートの改修方法を提供することを目的とする。  The present invention has been made in view of the circumstances described above, and is a method for repairing a waterproof sheet that generates less industrial waste, hardly leaks water, has a good fit around the rising and entering corners, and has excellent workability. The purpose is to provide.

本発明の防水シートの改修方法は、接着剤または機械的手段を介して、下地上に設置された防水シートを改修する防水シートの改修方法であって、前記下地上に設置された防水シートを部分的に切り取り、前記下地を部分的に露出させる工程と、前記露出させた下地上および前記露出させた下地の周辺の前記防水シート上に、プライマーを塗布する工程と、前記プライマーを介して、前記露出させた下地上および前記露出させた下地の周辺の前記防水シート上に、第１の塗膜防水材を塗布する工程と、を有することを特徴とする。  The waterproof sheet repair method of the present invention is a waterproof sheet repair method for repairing a waterproof sheet placed on a base via an adhesive or mechanical means, wherein the waterproof sheet installed on the base is Partially cutting, partially exposing the base, applying a primer on the exposed base and the waterproof sheet around the exposed base, and via the primer Applying a first waterproof coating material on the exposed base and the waterproof sheet around the exposed base.

本発明の防水シートの改修方法において、前記第１の塗膜防水材を塗布する前に、前記露出させた下地および前記露出させた下地の周辺の前記防水シートを覆うように、前記第１の塗膜防水材が浸透可能な補強材を配置する工程を有していてもよい。  In the waterproof sheet refurbishing method of the present invention, before applying the first coating waterproofing material, the first base is formed so as to cover the exposed base and the waterproof sheet around the exposed base. You may have the process of arrange | positioning the reinforcing material which a coating-film waterproof material can osmose | permeate.

本発明の防水シートの改修方法において、前記プライマーを塗布した後、前記露出させた下地上に粘着部材を配置する工程を有していてもよい。  The waterproof sheet repairing method of the present invention may include a step of placing an adhesive member on the exposed base after the primer is applied.

本発明の防水シートの改修方法において、前記防水シートの全面上および前記第１の塗膜防水材からなる塗膜の全面上に、第２の塗膜防水材を塗布する工程を有していてもよい。  The method for repairing a waterproof sheet according to the present invention includes a step of applying a second waterproof coating material on the entire surface of the waterproof sheet and on the entire coating film made of the first waterproof coating material. Also good.

本発明によれば、産業廃棄物の発生量が少なく、漏水が発生し難く、立ち上がりおよび入り隅周辺の納まりがよく、施工性に優れる防水シートの改修方法を提供することができる。  ADVANTAGE OF THE INVENTION According to this invention, the amount of industrial waste generated is small, it is hard to generate | occur | produce a water leak, the accommodation of the standup | rising and entering corner periphery is good, and the repair method of the waterproof sheet excellent in workability can be provided.

本発明の防水シートの改修方法の第１の実施形態を示す概略断面図である。It is a schematic sectional drawing which shows 1st Embodiment of the repair method of the waterproof sheet of this invention. 本発明の防水シートの改修方法の第２の実施形態を示す概略断面図である。It is a schematic sectional drawing which shows 2nd Embodiment of the repair method of the waterproof sheet of this invention.

本発明の防水シートの改修方法の実施の形態について説明する。
なお、本実施の形態は、発明の趣旨をより良く理解させるために具体的に説明するものであり、特に指定のない限り、本発明を限定するものではない。 An embodiment of the waterproof sheet repair method of the present invention will be described.
Note that this embodiment is specifically described in order to better understand the gist of the invention, and does not limit the present invention unless otherwise specified.

（１）第１の実施形態
図１は、本実施形態の防水シートの改修方法を示す概略断面図である。
本実施形態の防水シートの改修方法は、接着剤または機械的手段を介して、下地上に設置された防水シートを改修する方法である。すなわち、本実施形態の防水シートの改修方法は、上述の密着工法または機械固定工法により、下地上に設置された防水シートを改修する方法である。 (1) 1st Embodiment FIG. 1: is a schematic sectional drawing which shows the repair method of the waterproof sheet of this embodiment.
The waterproof sheet repair method of this embodiment is a method of repairing a waterproof sheet installed on a base via an adhesive or mechanical means. In other words, the waterproof sheet repair method of the present embodiment is a method of repairing the waterproof sheet installed on the base by the above-described adhesion method or machine fixing method.

本実施形態の防水シートの改修方法では、まず、下地１の上面１ａ上に設置された防水シート２を部分的に、複数箇所において切り取り、下地１を部分的に露出させる（下地を露出させる工程）。
防水シート２を切り取る大きさ（面積）や、下地１を露出させる間隔は、特に限定されないが、防水シート２の改修が必要な部分の大きさ（面積）などに応じて適宜調整される。 In the waterproof sheet refurbishing method of the present embodiment, first, the waterproof sheet 2 installed on the upper surface 1a of the base 1 is partially cut out at a plurality of locations, and the base 1 is partially exposed (step of exposing the base). ).
The size (area) for cutting off the waterproof sheet 2 and the interval at which the base 1 is exposed are not particularly limited, but may be appropriately adjusted according to the size (area) of the portion that needs to be repaired.

防水シート２を切り取る方法としては、特に限定されないが、各種カッターを用いる方法が挙げられる。  Although it does not specifically limit as a method of cutting off the waterproof sheet 2, The method of using various cutters is mentioned.

下地１としては、コンクリート、モルタル、アスファルトなどからなるものが挙げられる。
防水シート２としては、一般的な塩ビシート防水工法で用いられる防水用の塩ビシートや、防水用のゴムシートなどが挙げられる。 Examples of the base 1 include those made of concrete, mortar, asphalt and the like.
Examples of the waterproof sheet 2 include a waterproof PVC sheet used in a general PVC sheet waterproofing method, a waterproof rubber sheet, and the like.

次いで、露出させた下地１の上面１ａ上、および、露出させた下地１の周辺の防水シート２の上面２ａ上にプライマー３を塗布する（プライマーを塗布する工程）。
プライマー３を塗布する方法は、特に限定されないが、例えば、一般的な塗布法、スプレー法などが用いられる。 Next, the primer 3 is applied on the exposed upper surface 1a of the base 1 and the upper surface 2a of the waterproof sheet 2 around the exposed base 1 (step of applying a primer).
The method for applying the primer 3 is not particularly limited. For example, a general application method, a spray method, or the like is used.

プライマー３は、下地１および防水シート２と、後述する第１の塗膜防水材４との接着性を改善（向上）するためのものである。
プライマー３としては、特に限定されないが、例えば、ウレタン系樹脂などが挙げられる。 The primer 3 is for improving (improving) the adhesion between the base 1 and the waterproof sheet 2 and a first coating waterproofing material 4 described later.
Although it does not specifically limit as the primer 3, For example, urethane type resin etc. are mentioned.

露出させた下地１の周辺の防水シート２において、プライマー３を塗布する面積は、特に限定されないが、防水シート２の改修が必要な部分の大きさ（面積）、第１の塗膜防水材４によって形成される防水塗膜に必要とされる接着強度などに応じて適宜調整される。  In the waterproof sheet 2 around the exposed base 1, the area to which the primer 3 is applied is not particularly limited, but the size (area) of the waterproof sheet 2 that needs to be repaired, the first waterproof film 4 It adjusts suitably according to the adhesive strength etc. which are required for the waterproof coating film formed by.

次いで、露出させた下地１の上面１ａおよび露出させた下地１の周辺の防水シート２の上面２ａを覆うように、第１の塗膜防水材４が浸透可能（透過可能）な補強材５を配置する（補強材を配置する工程）。  Next, a reinforcing material 5 through which the first coating waterproof material 4 can penetrate (permeate) so as to cover the upper surface 1a of the exposed base 1 and the upper surface 2a of the waterproof sheet 2 around the exposed base 1 is provided. Arrangement (step of arranging the reinforcing material).

補強材５は、下地１を露出させることにより、防水シート２に形成された凹みを覆い、その部分の機械的強度を補強するためのものである。
補強材５としては、メッシュ、クロス、不織布、織布などが挙げられる。
補強材５の材料としては、ガラス、炭素、金属などからなる無機繊維、ビニロン、ポリエステル、ナイロンなどからなる合成繊維などが挙げられる。
補強材５の形状（平面視した場合の形状）や大きさ（面積）は、特に限定されないが、露出させた下地１の形状や大きさ（面積）、防水シート２の改修が必要な部分の大きさ（面積）、第１の塗膜防水材４によって形成される防水塗膜に必要とされる接着強度などに応じて適宜調整される。 The reinforcing material 5 is for covering the dent formed in the waterproof sheet 2 by exposing the base 1, and reinforcing the mechanical strength of the portion.
Examples of the reinforcing material 5 include mesh, cloth, non-woven fabric, woven fabric, and the like.
Examples of the material of the reinforcing material 5 include inorganic fibers made of glass, carbon, metal, and the like, and synthetic fibers made of vinylon, polyester, nylon, and the like.
The shape (shape in plan view) and size (area) of the reinforcing material 5 are not particularly limited, but the shape and size (area) of the exposed base 1 and the portion of the waterproof sheet 2 that needs to be repaired are not limited. The size (area) is appropriately adjusted according to the adhesive strength required for the waterproof coating formed by the first coating waterproof material 4.

補強材５の厚さは、特に限定されないが、第１の塗膜防水材４によって形成される防水塗膜に必要とされる接着強度などに応じて適宜調整される。  The thickness of the reinforcing material 5 is not particularly limited, but is appropriately adjusted according to the adhesive strength required for the waterproof coating formed by the first coating waterproof material 4.

次いで、プライマー３および補強材５を介して、露出させた下地１の上面１ａ上および露出させた下地１の周辺の防水シート２の上面２ａ上に、第１の塗膜防水材４を塗布する（第１の塗膜防水材を塗布する工程）。
第１の塗膜防水材４を塗布する方法は、特に限定されないが、例えば、一般的な塗布法、スプレー法などが用いられる。 Next, the first waterproof coating material 4 is applied to the exposed upper surface 1 a of the base 1 and the upper surface 2 a of the waterproof sheet 2 around the exposed base 1 through the primer 3 and the reinforcing material 5. (The process of apply | coating a 1st coating-film waterproof material).
Although the method of apply | coating the 1st film waterproofing material 4 is not specifically limited, For example, a general apply | coating method, a spray method, etc. are used.

第１の塗膜防水材４としては、硬化して防水塗膜を形成し、その防水塗膜が、ビル、マンション、学校などの屋根や屋上の防水に要求される防水性能を発揮するものであれば、特に限定されないが、ウレタン塗膜防水材などが挙げられる。  The first coating waterproofing material 4 is cured to form a waterproof coating, and the waterproof coating exhibits the waterproof performance required for waterproofing roofs and roofs of buildings, condominiums, schools, etc. If there is, it is not particularly limited, and examples thereof include a urethane coating waterproof material.

第１の塗膜防水材４によって形成される防水塗膜の厚さは、特に限定されないが、その防水塗膜に必要とされる接着強度などに応じて適宜調整される。  The thickness of the waterproof coating formed by the first waterproof coating 4 is not particularly limited, but is appropriately adjusted according to the adhesive strength required for the waterproof coating.

次いで、防水シート２の全面上および第１の塗膜防水材４からなる防水塗膜の全面上に、第２の塗膜防水材６を塗布する（第２の塗膜防水材を塗布する工程）。
この工程により、防水シート２の改修が完了する。
第２の塗膜防水材６を塗布する方法は、特に限定されないが、例えば、一般的な塗布法、スプレー法などが用いられる。 Next, the second waterproof coating 6 is applied on the entire surface of the waterproof sheet 2 and the entire waterproof coating composed of the first waterproof coating 4 (step of applying the second waterproof coating) ).
Through this process, the repair of the waterproof sheet 2 is completed.
Although the method of apply | coating the 2nd coating film waterproofing material 6 is not specifically limited, For example, a general apply | coating method, a spray method, etc. are used.

なお、防水シート２の全面とは、防水シート２の上面２ａのうち第１の塗膜防水材４からなる防水塗膜が形成されていない部分の全てのことである。また、第１の塗膜防水材４からなる防水塗膜の全面とは、第１の塗膜防水材４からなる防水塗膜における防水シート２と接していない側の面の全てのことである。  In addition, the whole surface of the waterproof sheet 2 is all parts of the upper surface 2a of the waterproof sheet 2 where the waterproof coating film made of the first coating film waterproof material 4 is not formed. Moreover, the whole surface of the waterproof coating film made of the first coating film waterproof material 4 is all the surface of the waterproof coating film made of the first coating film waterproof material 4 that is not in contact with the waterproof sheet 2. .

第２の塗膜防水材６としては、第１の塗膜防水材４と同様のものが用いられる。  As the second waterproof membrane 6, the same waterproof membrane as the first waterproof membrane 4 is used.

本実施形態の防水シートの改修方法によれば、防水シート２を全面的に撤去することなく、少なくとも改修が必要な部分の周辺の防水シート２を除去すればよいので、防水シート２などの産業廃棄物の発生量を少なくすることができる。
また、防水シートとは異なり、改修後の防水シート２の接続部（ジョイント）がシームレスになるため、漏水の原因となる部位を減らすことができる。
また、塗膜防水材を用いるので、塗膜防水材からなる防水塗膜の立ち上がりおよび入り隅周辺の納まりがよく、施工性を改善（向上）することができる。
さらに、次回の防水シート２の改修においても、同じ方法で塗膜防水材を塗り重ねることができる。 According to the waterproof sheet repair method of the present embodiment, at least the waterproof sheet 2 around the portion that needs to be repaired is removed without removing the waterproof sheet 2 entirely. The amount of waste generated can be reduced.
Moreover, since the connection part (joint) of the waterproof sheet 2 after a repair becomes seamless unlike a waterproof sheet, the site | part which causes water leakage can be reduced.
Moreover, since the waterproof coating material is used, the waterproof coating film made of the waterproof coating material has a good rise and fits around the corners, and the workability can be improved (improved).
Furthermore, in the next renovation of the waterproof sheet 2, the waterproof coating material can be applied repeatedly by the same method.

なお、本実施形態では、補強材を配置する工程と、第２の塗膜防水材を塗布する工程とを、必須の工程としたが、本発明はこれに限定されない。本発明にあっては、補強材を配置する工程を省略してもよい。また、防水シートの改修が部分的で十分である場合、第２の塗膜防水材を塗布する工程を省略してもよい。  In addition, in this embodiment, although the process of arrange | positioning a reinforcing material and the process of apply | coating a 2nd coating-film waterproof material were made into an essential process, this invention is not limited to this. In the present invention, the step of arranging the reinforcing material may be omitted. Further, when the waterproof sheet is partially and sufficiently repaired, the step of applying the second waterproofing film may be omitted.

（２）第２の実施形態
図２は、本実施形態の防水シートの改修方法を示す概略断面図である。
本実施形態の防水シートの改修方法は、接着剤または機械的手段を介して、下地上に設置された防水シートを改修する方法である。すなわち、本実施形態の防水シートの改修方法は、上述の密着工法または機械固定工法により、下地上に設置された防水シートを改修する方法である。 (2) 2nd Embodiment FIG. 2: is a schematic sectional drawing which shows the repair method of the waterproof sheet of this embodiment.
The waterproof sheet repair method of this embodiment is a method of repairing a waterproof sheet installed on a base via an adhesive or mechanical means. In other words, the waterproof sheet repair method of the present embodiment is a method of repairing the waterproof sheet installed on the base by the above-described adhesion method or machine fixing method.

本実施形態の防水シートの改修方法では、まず、第１の下地１１の上面１１ａ上に積層された第２の下地１２の上面１２ａ上に設置された防水シート１３を部分的に、複数箇所において切り取り、第２の下地１２を部分的に露出させる（下地を露出させる工程）。
防水シート１３を切り取る大きさ（面積）や、第２の下地１２を露出させる間隔は、特に限定されないが、防水シート１３の改修が必要な部分の大きさ（面積）などに応じて適宜調整される。 In the repair method of the waterproof sheet of the present embodiment, first, the waterproof sheet 13 installed on the upper surface 12a of the second base 12 laminated on the upper surface 11a of the first base 11 is partially and at a plurality of locations. Cutting out and partially exposing the second base 12 (step of exposing the base).
The size (area) to cut off the waterproof sheet 13 and the interval at which the second base 12 is exposed are not particularly limited, but are appropriately adjusted according to the size (area) of the portion that needs to be repaired. The

防水シート１３を切り取る方法としては、特に限定されないが、各種カッターを用いる方法が挙げられる。  A method for cutting off the waterproof sheet 13 is not particularly limited, and examples thereof include a method using various cutters.

第１の下地１１としては、コンクリート、モルタルなどからなるものが挙げられる。
第２の下地１２としては、アスファルトなどからなるものが挙げられる。
防水シート１３としては、一般的な塩ビシート防水工法で用いられる防水用の塩ビシートや、防水用のゴムシートなどが挙げられる。 Examples of the first base 11 include those made of concrete, mortar, and the like.
Examples of the second base 12 include those made of asphalt.
Examples of the waterproof sheet 13 include a waterproof PVC sheet used in a general PVC sheet waterproofing method, a waterproof rubber sheet, and the like.

次いで、露出させた第２の下地１２の上面１２ａ上、および、露出させた第２の下地１２の周辺の防水シート１３の上面１３ａ上にプライマー１４を塗布する（プライマーを塗布する工程）。
プライマー１４を塗布する方法は、特に限定されないが、例えば、一般的な塗布法、スプレー法などが用いられる。 Next, the primer 14 is applied onto the exposed upper surface 12a of the second base 12 and the upper surface 13a of the waterproof sheet 13 around the exposed second base 12 (step of applying a primer).
Although the method of apply | coating the primer 14 is not specifically limited, For example, a general apply | coating method, a spray method, etc. are used.

プライマー１４は、第２の下地１２、防水シート１３および後述する粘着部材１５と、後述する第１の塗膜防水材１６との接着性を改善（向上）するためのものである。
プライマー１４としては、特に限定されないが、例えば、ウレタン系樹脂などが挙げられる。 The primer 14 is for improving (improving) the adhesion between the second base 12, the waterproof sheet 13, the adhesive member 15 to be described later, and the first waterproofing film 16 to be described later.
Although it does not specifically limit as the primer 14, For example, urethane type resin etc. are mentioned.

露出させた第２の下地１２の周辺の防水シート１３において、プライマー１４を塗布する面積は、特に限定されないが、防水シート１３の改修が必要な部分の大きさ（面積）、第１の塗膜防水材１６によって形成される防水塗膜に必要とされる接着強度などに応じて適宜調整される。  In the waterproof sheet 13 around the exposed second base 12, the area to which the primer 14 is applied is not particularly limited, but the size (area) of the portion that needs to be repaired of the waterproof sheet 13, the first coating film It adjusts suitably according to the adhesive strength etc. which are required for the waterproof coating film formed of the waterproof material 16.

次いで、プライマー１４を介して、露出させた第２の下地１２の上面１２ａ上に、粘着部材１５を配置する（粘着部材を配置する工程）。
すなわち、第２の下地１２を露出させることにより、防水シート１３に形成された凹み内に、粘着部材１５を配置する。 Next, the adhesive member 15 is arranged on the exposed upper surface 12a of the second base 12 via the primer 14 (step of arranging the adhesive member).
That is, the adhesive member 15 is disposed in the recess formed in the waterproof sheet 13 by exposing the second base 12.

粘着部材１５は、第２の下地１２と、第１の塗膜防水材１６によって形成される防水塗膜との接着性を向上するためのものである。
粘着部材１５としては、露出させた第２の下地１２側と対向する側に粘着層が設けられ、第１の塗膜防水材１６が塗布される側に、第１の塗膜防水材１６との接着性が高い基材が設けられたものが用いられる。
粘着部材１５の粘着層を構成する材料としては、ブチルゴム、改質アスファルトなどが挙げられる。
粘着部材１５の基材を構成する材料としては、ポリエステル、ポリエチレン、ポリプロピレンなどが挙げられる。 The adhesive member 15 is for improving the adhesion between the second base 12 and the waterproof coating formed by the first coating waterproofing material 16.
As the adhesive member 15, an adhesive layer is provided on the side facing the exposed second base 12 side, and on the side where the first coating waterproof material 16 is applied, Those provided with a base material having high adhesiveness are used.
Examples of the material constituting the adhesive layer of the adhesive member 15 include butyl rubber and modified asphalt.
Examples of the material constituting the base material of the adhesive member 15 include polyester, polyethylene, and polypropylene.

粘着部材１５の厚さは、特に限定されないが、防水シート１３の厚さ、すなわち、第２の下地１２を露出させることにより、防水シート１３に形成された凹みの深さに応じて適宜調整される。  The thickness of the adhesive member 15 is not particularly limited, but is appropriately adjusted according to the thickness of the waterproof sheet 13, that is, the depth of the recess formed in the waterproof sheet 13 by exposing the second base 12. The

次いで、露出させた第２の下地１２の上面１２ａ上に配置した粘着部材１５および露出させた第２の下地１２の周辺の防水シート１３の上面１３ａを覆うように、第１の塗膜防水材１６が浸透可能（透過可能）な補強材１７を配置する（補強材を配置する工程）。  Next, the first coating film waterproofing material is provided so as to cover the adhesive member 15 disposed on the upper surface 12a of the exposed second base 12 and the upper surface 13a of the waterproof sheet 13 around the exposed second base 12. A reinforcing material 17 that can penetrate (permeate) 16 is arranged (step of arranging a reinforcing material).

補強材１７は、第２の下地１２を露出させることにより、防水シート１３に形成された凹みを覆い、その部分の機械的強度を補強するためのものである。
補強材１７としては、メッシュ、クロス、不織布、織布などが挙げられる。
補強材１７の材料としては、ガラス、炭素、金属などからなる無機繊維、ビニロン、ポリエステル、ナイロンなどからなる合成繊維などが挙げられる。
補強材１７の形状（平面視した場合の形状）や大きさ（面積）は、特に限定されないが、露出させた下地１の形状や大きさ（面積）、防水シート１３の改修が必要な部分の大きさ（面積）、第１の塗膜防水材１６によって形成される防水塗膜に必要とされる接着強度などに応じて適宜調整される。 The reinforcing member 17 covers the dent formed in the waterproof sheet 13 by exposing the second base 12, and reinforces the mechanical strength of the portion.
Examples of the reinforcing material 17 include a mesh, a cloth, a nonwoven fabric, and a woven fabric.
Examples of the material of the reinforcing material 17 include inorganic fibers made of glass, carbon, metal, and the like, and synthetic fibers made of vinylon, polyester, nylon, and the like.
The shape (shape in plan view) and size (area) of the reinforcing member 17 are not particularly limited, but the shape and size (area) of the exposed base 1 and the portion of the waterproof sheet 13 that needs to be repaired are not limited. The size (area) is appropriately adjusted according to the adhesive strength required for the waterproof coating formed by the first coating waterproof material 16.

補強材１７の厚さは、特に限定されないが、第１の塗膜防水材１６によって形成される防水塗膜に必要とされる接着強度などに応じて適宜調整される。  The thickness of the reinforcing material 17 is not particularly limited, but is appropriately adjusted according to the adhesive strength required for the waterproof coating formed by the first coating waterproof material 16.

次いで、プライマー３、粘着部材１５および補強材１７を介して、露出させた第２の下地１２の上面１２ａ上および露出させた第２の下地１２の周辺の防水シート１３の上面１３ａ上に、第１の塗膜防水材１６を塗布する（第１の塗膜防水材を塗布する工程）。
第１の塗膜防水材１６を塗布する方法は、特に限定されないが、例えば、一般的な塗布法、スプレー法などが用いられる。 Next, on the upper surface 12a of the exposed second base 12 and the upper surface 13a of the waterproof sheet 13 around the exposed second base 12 through the primer 3, the adhesive member 15 and the reinforcing member 17, the first 1 coating film waterproofing material 16 is applied (step of applying the first coating waterproofing material).
Although the method of apply | coating the 1st film waterproofing material 16 is not specifically limited, For example, a general apply | coating method, a spray method, etc. are used.

第１の塗膜防水材１６としては、硬化して防水塗膜を形成し、その防水塗膜が、ビル、マンション、学校などの屋根や屋上の防水に要求される防水性能を発揮するものであれば、特に限定されないが、ウレタン塗膜防水材などが挙げられる。  The first coating waterproofing material 16 is cured to form a waterproof coating, and the waterproof coating exhibits the waterproof performance required for waterproofing roofs and roofs of buildings, condominiums, schools, etc. If there is, it is not particularly limited, and examples thereof include a urethane coating waterproof material.

第１の塗膜防水材１６によって形成される防水塗膜の厚さは、特に限定されないが、その防水塗膜に必要とされる接着強度などに応じて適宜調整される。  The thickness of the waterproof coating formed by the first waterproof coating 16 is not particularly limited, but may be appropriately adjusted according to the adhesive strength required for the waterproof coating.

次いで、防水シート１３の全面上および第１の塗膜防水材１６からなる防水塗膜の全面上に、第２の塗膜防水材１８を塗布する（第２の塗膜防水材を塗布する工程）。
この工程により、防水シート１３の改修が完了する。
第２の塗膜防水材１８を塗布する方法は、特に限定されないが、例えば、一般的な塗布法、スプレー法などが用いられる。 Next, the second waterproof coating 18 is applied on the entire surface of the waterproof sheet 13 and the entire waterproof coating composed of the first waterproof coating 16 (the step of applying the second waterproof coating). ).
By this process, the repair of the waterproof sheet 13 is completed.
Although the method of apply | coating the 2nd coating film waterproofing material 18 is not specifically limited, For example, a general apply | coating method, a spray method, etc. are used.

なお、防水シート１３の全面とは、防水シート１３の上面１３ａのうち第１の塗膜防水材１６からなる防水塗膜が形成されていない部分の全てのことである。また、第１の塗膜防水材１６からなる防水塗膜の全面とは、第１の塗膜防水材１６からなる防水塗膜における防水シート１３と接していない側の面の全てのことである。  Note that the entire surface of the waterproof sheet 13 refers to all of the upper surface 13a of the waterproof sheet 13 where the waterproof coating film made of the first coating waterproof material 16 is not formed. Moreover, the whole surface of the waterproof coating film made of the first coating film waterproof material 16 means all surfaces on the side not in contact with the waterproof sheet 13 in the waterproof coating film made of the first coating film waterproof material 16. .

第２の塗膜防水材１８としては、第１の塗膜防水材１６と同様のものが用いられる。  As the second waterproof coating material 18, the same one as the first waterproof coating material 16 is used.

本実施形態の防水シートの改修方法によれば、防水シート１３を全面的に撤去することなく、少なくとも改修が必要な部分の周辺の防水シート１３を除去すればよいので、防水シート１３などの産業廃棄物の発生量を少なくすることができる。
また、防水シートとは異なり、改修後の防水シート１３の接続部（ジョイント）がシームレスになるため、漏水の原因となる部位を減らすことができる。
また、塗膜防水材を用いるので、塗膜防水材からなる防水塗膜の立ち上がりおよび入り隅周辺の納まりがよく、施工性を改善（向上）することができる。
さらに、次回の防水シート１３の改修においても、同じ方法で塗膜防水材を塗り重ねることができる。 According to the waterproof sheet repairing method of the present embodiment, at least the waterproof sheet 13 around the portion that needs to be repaired should be removed without removing the waterproof sheet 13 entirely. The amount of waste generated can be reduced.
Moreover, since the connection part (joint) of the waterproof sheet 13 after a repair becomes seamless unlike a waterproof sheet, the site | part which causes water leakage can be reduced.
Moreover, since the waterproof coating material is used, the waterproof coating film made of the waterproof coating material has a good rise and fits around the corners, and the workability can be improved (improved).
Further, in the next renovation of the waterproof sheet 13, the waterproof coating material can be applied repeatedly by the same method.

なお、本実施形態では、補強材を配置する工程と、第２の塗膜防水材を塗布する工程とを、必須の工程としたが、本発明はこれに限定されない。本発明にあっては、補強材を配置する工程を省略してもよい。また、防水シートの改修が部分的で十分である場合、第２の塗膜防水材を塗布する工程を省略してもよい。  In addition, in this embodiment, although the process of arrange | positioning a reinforcing material and the process of apply | coating a 2nd coating-film waterproof material were made into an essential process, this invention is not limited to this. In the present invention, the step of arranging the reinforcing material may be omitted. Further, when the waterproof sheet is partially and sufficiently repaired, the step of applying the second waterproofing film may be omitted.

１・・・下地、２・・・防水シート、３・・・プライマー、４・・・第１の塗膜防水材、５・・・補強材、６・・・第２の塗膜防水材、１１・・・第１の下地、１２・・・第２の下地、１３・・・防水シート、１４・・・プライマー、１５・・・粘着部材、１６・・・第１の塗膜防水材、１７・・・補強材、１８・・・第２の塗膜防水材。 DESCRIPTION OF SYMBOLS 1 ... Base | substrate, 2 ... Waterproof sheet, 3 ... Primer, 4 ... 1st film waterproofing material, 5 ... Reinforcement material, 6 ... 2nd film waterproofing material, DESCRIPTION OF SYMBOLS 11 ... 1st foundation | substrate, 12 ... 2nd foundation | substrate, 13 ... Waterproof sheet, 14 ... Primer, 15 ... Adhesive member, 16 ... 1st coating film waterproofing material, 17 ... Reinforcing material, 18 ... 2nd coating film waterproofing material.

Claims (4)

接着剤または機械的手段を介して、下地上に設置された防水シートを改修する防水シートの改修方法であって、
前記下地上に設置された防水シートを部分的に切り取り、前記下地を部分的に露出させる工程と、
前記露出させた下地上および前記露出させた下地の周辺の前記防水シート上に、プライマーを塗布する工程と、
前記プライマーを介して、前記露出させた下地上および前記露出させた下地の周辺の前記防水シート上に、第１の塗膜防水材を塗布する工程と、
を有することを特徴とする防水シートの改修方法。 A method of repairing a waterproof sheet that repairs a waterproof sheet installed on a base via an adhesive or mechanical means,
Partially cutting off the waterproof sheet placed on the base, partially exposing the base;
Applying a primer on the exposed base and on the waterproof sheet around the exposed base; and
Applying a first waterproof coating material on the exposed base and the waterproof sheet around the exposed base via the primer;
A method of repairing a waterproof sheet, comprising: 前記第１の塗膜防水材を塗布する前に、前記露出させた下地および前記露出させた下地の周辺の前記防水シートを覆うように、前記第１の塗膜防水材が浸透可能な補強材を配置する工程を有することを特徴とする請求項１に記載の防水シートの改修方法。  Reinforcing material that can be penetrated by the first waterproof coating material so as to cover the exposed base and the waterproof sheet around the exposed base before applying the first waterproof waterproof coating The method for repairing a waterproof sheet according to claim 1, further comprising a step of arranging 前記プライマーを塗布した後、前記露出させた下地上に粘着部材を配置する工程を有することを特徴とする請求項１または２に記載の防水シートの改修方法。  The method for repairing a waterproof sheet according to claim 1, further comprising a step of arranging an adhesive member on the exposed base after applying the primer. 前記防水シートの全面上および前記第１の塗膜防水材からなる塗膜の全面上に、第２の塗膜防水材を塗布する工程を有することを特徴とする請求項１〜３のいずれか１項に記載の防水シートの改修方法。  4. The method according to claim 1, further comprising a step of applying a second waterproof coating material on the entire surface of the waterproof sheet and on the entire surface of the coating film made of the first waterproof coating material. The method for repairing the waterproof sheet according to item 1.
JP2014117738A 2014-06-06 2014-06-06 Repair method for waterproof sheet Pending JP2015229905A (en)