JP2015076221A - Aluminum alloy for negative electrode material of aluminum air battery, and aluminum air battery - Google Patents
Aluminum alloy for negative electrode material of aluminum air battery, and aluminum air battery Download PDFInfo
- Publication number
- JP2015076221A JP2015076221A JP2013210810A JP2013210810A JP2015076221A JP 2015076221 A JP2015076221 A JP 2015076221A JP 2013210810 A JP2013210810 A JP 2013210810A JP 2013210810 A JP2013210810 A JP 2013210810A JP 2015076221 A JP2015076221 A JP 2015076221A
- Authority
- JP
- Japan
- Prior art keywords
- aluminum
- negative electrode
- aluminum alloy
- air battery
- electrode material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、アルミニウム空気電池の負極材として用いられるアルミニウム合金及び該アルミニウム合金からなる負極材を有するアルミニウム空気電池に関する。 The present invention relates to an aluminum alloy used as a negative electrode material of an aluminum air battery and an aluminum air battery having a negative electrode material made of the aluminum alloy.
アルミニウム空気電池は、アルミニウム溶解反応を負極とした反応（１）及び空気中の酸素を活物質とした反応（２）によって表される一次電池である。負極材に用いられる金属としては、アルミニウムの他、亜鉛、マグネシウム、リチウムなどが知られているが、加工性が良好であること、軽量であること、３価の軽金属元素であることから単位重量当たりの電流効率が高いことから、アルミニウム材が注目されている。
（１）負極（アノード）反応：Ａｌ＋２Ｈ２Ｏ→ＡｌＯ２ −＋４Ｈ＋＋３ｅ−
（２）正極（カソード）反応：Ｏ２＋Ｈ２Ｏ＋４ｅ−→４ＯＨ−
The aluminum-air battery is a primary battery represented by a reaction (1) using an aluminum dissolution reaction as a negative electrode and a reaction (2) using oxygen in the air as an active material. As the metal used for the negative electrode material, zinc, magnesium, lithium and the like are known in addition to aluminum, but unit weight because of good workability, light weight, and trivalent light metal element. Aluminum material has attracted attention because of its high current efficiency.
(1) Negative electrode (anode) reaction: Al + 2H 2 O → AlO 2 − + 4H + + 3e −
(2) Positive electrode (cathode) reaction: O 2 + H 2 O + 4e − → 4OH −
アルミニウム空気電池では、負極活物質にアルミニウム又はアルミニウム合金を用い、正極活物質には空気中の酸素を用い、電解液としてはＮａＣｌ水溶液やＮａＯＨ水溶液又はＫＯＨ水溶液が用いられる。 In an aluminum air battery, aluminum or an aluminum alloy is used for the negative electrode active material, oxygen in the air is used for the positive electrode active material, and an aqueous NaCl solution, an aqueous NaOH solution, or an aqueous KOH solution is used as the electrolyte.
このようなアルミニウム空気電池は、軽量且つ電気容量が高いことが求められる。 Such an aluminum air battery is required to be lightweight and have a high electric capacity.
アルミニウム空気電池用の負極材として、これまでに種々のアルミニウム合金が開発されており、例えば、Ｚｎ０．５〜１０％、Ｓｎ０．０４〜１．０％、Ｇａ０．００３〜１．０％を含有するアルミニウム合金（特許文献１、特許文献２）、Ｓｎ０．０４〜０．５％を含有し、０．０５％以下のＳｉ、０．１％以下のＦｅを含有するアルミニウム合金を鋳造し、均質化熱処理によりアルミニウムとＳｎとの固溶体を急冷したアルミニウム合金（特許文献３）、Ｍｇ０．１〜２．０％、Ｓｎ０．０３〜１．０％、Ｍｎ０．０１〜０．５％を含有するアルミニウム合金（特許文献４）、Ｍｇ０．０００１〜８％を含有し、Ｓｉ、Ｆｅを規制したアルミニウム合金（特許文献５）が開示されている。 Various aluminum alloys have been developed so far as negative electrode materials for aluminum air batteries, including, for example, Zn 0.5 to 10%, Sn 0.04 to 1.0%, Ga 0.003 to 1.0% Cast aluminum alloy containing 0.04 to 0.5% Sn, 0.05% or less Si, 0.1% or less Fe, and homogeneous Aluminum alloy obtained by quenching a solid solution of aluminum and Sn by hydrothermal treatment (Patent Document 3), aluminum containing Mg 0.1 to 2.0%, Sn 0.03 to 1.0%, Mn 0.01 to 0.5% An alloy (Patent Document 4), an aluminum alloy containing 0.0001 to 8% Mg and regulating Si and Fe (Patent Document 5) is disclosed.
上記の材料は、いずれも、常温での通電時の電流密度が１０〜１００ｍＡ／ｃｍ２程度であり、電池としての出力が小さいという問題があった。これらの材料で大きい出力を得る場合には、電池の使用温度を６０℃以上と高温にしたり、電池セルを大きくする必要があった。しかし、近年の輸送機向けなどの空気電池では、小型且つ常温でも使用可能な空気電池の要求が多い。そのため、常温において高い電流密度が得られることが課題である。 Each of the above materials has a problem that the current density when energized at room temperature is about 10 to 100 mA / cm 2 and the output as a battery is small. In order to obtain a large output with these materials, it was necessary to increase the use temperature of the battery to a high temperature of 60 ° C. or higher or to enlarge the battery cell. However, in recent air batteries for transportation equipment and the like, there are many demands for air batteries that are small and can be used at room temperature. Therefore, it is a problem that a high current density can be obtained at room temperature.
また、電池の電圧（起電力）とは正極と負極との電位差であり、この電位差が大きいほど、電池の性能としては高くなる。通常、負極の電位は、電流を流さない状態で最も卑であり、電流を流すと、電位が貴に変化する分極という現象が生じる。そのため、アルミニウム空気電池には、電流を流しても、負極の電位が卑のままの状態が維持されること、すなわち、分極し難いことが要求される。 The battery voltage (electromotive force) is a potential difference between the positive electrode and the negative electrode, and the larger the potential difference, the higher the performance of the battery. Usually, the potential of the negative electrode is the lowest when no current is passed, and when a current is passed, a phenomenon called polarization in which the potential changes preciously occurs. Therefore, the aluminum air battery is required to maintain a state in which the potential of the negative electrode remains low even when a current is passed, that is, it is difficult to be polarized.
また、アルミニウム合金負極材にアルカリ電解液が接触すると、両性金属であるアルミニウムでは自己腐食が発生するが、自己腐食によるアルミニウム合金の消耗は、電流を得ることには寄与しないため、自己腐食量が多いと、負極材の単位重量当たりに得られる電流、すなわち電流効率が低下してしまう。 In addition, when an alkaline electrolyte comes into contact with an aluminum alloy negative electrode material, self-corrosion occurs in aluminum, which is an amphoteric metal, but consumption of the aluminum alloy due to self-corrosion does not contribute to obtaining current, so the amount of self-corrosion is small. If the amount is large, the current obtained per unit weight of the negative electrode material, that is, the current efficiency is lowered.
また、電解液のアルカリ濃度を高くすると、アルミニウム合金のアノード反応速度が増大することや、電解液の抵抗が低下することから、電流密度を高くすることができる。しかし、アルカリ濃度が高くなると、自己腐食量も増大するため、電流効率が低くなる可能性がある。そのため、電解液のアルカリ濃度が高くても、自己腐食量が小さいことが要求される。 Further, when the alkaline concentration of the electrolytic solution is increased, the anode reaction rate of the aluminum alloy is increased and the resistance of the electrolytic solution is decreased, so that the current density can be increased. However, as the alkali concentration increases, the amount of self-corrosion also increases, which may reduce current efficiency. Therefore, even if the alkaline concentration of the electrolytic solution is high, the amount of self-corrosion is required to be small.
なお、電流効率とは、通電により消耗したアルミニウム合金の質量に対する、得られた電気量から計算されるアルミニウム合金の電気化学当量の質量の割合である。電流効率が高いほど、同じ質量のアルミニウム合金から取り出される電流が多いことを示す。 The current efficiency is a ratio of the mass of the electrochemical equivalent of the aluminum alloy calculated from the obtained electric quantity to the mass of the aluminum alloy consumed by energization. Higher current efficiency indicates more current drawn from the same mass of aluminum alloy.
従って、本発明の目的は、常温でも電流密度が高く、通電を続けても負極の電位が卑のままの状態が維持され、自己腐食が少なく、且つ、アルカリ濃度が高い電解液を用いても電流効率が高いアルミニウム空気電池の負極材用アルミニウム合金を提供することにある。 Therefore, the object of the present invention is to use an electrolytic solution that has a high current density even at room temperature, maintains a negative electrode potential even when energization is continued, reduces self-corrosion, and has a high alkali concentration. An object of the present invention is to provide an aluminum alloy for a negative electrode material of an aluminum air battery having high current efficiency.
発明者らは、上記従来技術における課題を解決すべく、鋭意研究を重ねた結果、アルミニウム合金材のＳｎ、Ｆｅ及びＳｉの含有量と、合金マトリックス中の金属Ｓｎ析出物粒子の大きさ及びその存在量と、を調節することにより、上記課題を解決することができることを見出し、本発明を完成させるに至った。 As a result of intensive studies to solve the problems in the prior art, the inventors have studied the contents of Sn, Fe, and Si in the aluminum alloy material, the size of the metal Sn precipitate particles in the alloy matrix, and the content thereof. The inventors have found that the above problem can be solved by adjusting the abundance and have completed the present invention.
すなわち、本発明（１）は、０．１質量％以上１０．０質量％以下のＳｎと、０．０００１質量％以上０．０１００質量％以下のＦｅと、０．０００１質量％以上０．００５０質量％以下のＳｉと、を含有し、残部がＡｌ及び不可避不純物からなるアルミニウム合金であり、
アルミニウム合金マトリクス中に金属Ｓｎ析出物粒子を含有し、合金断面に観察される金属Ｓｎ析出物粒子のうち、０．１〜１００μｍの大きさの金属Ｓｎ析出物粒子の個数密度が、４００個／ｍｍ２以上であること、
を特徴とするアルミニウム空気電池の負極材用アルミニウム合金を提供するものである。
That is, the present invention (1) includes 0.1 mass% or more and 10.0 mass% or less of Sn, 0.0001 mass% or more and 0.0100 mass% or less of Fe, 0.0001 mass% or more and 0.0050 mass% or more. An aluminum alloy containing less than or equal to mass% Si, the balance being Al and inevitable impurities,
The metal Sn precipitate particles are contained in the aluminum alloy matrix, and among the metal Sn precipitate particles observed in the cross section of the alloy, the number density of the metal Sn precipitate particles having a size of 0.1 to 100 μm is 400 / mm 2 or more,
An aluminum alloy for a negative electrode material of an aluminum-air battery is provided.
また、本発明（２）は、正極材と、電解液と、負極材と、を有する空気電池であって、
該電解液が、２〜１０ＭのＫＯＨ又はＮａＯＨを含有する水溶液であり、
該負極材が、請求項１記載の空気電池の負極材用アルミニウム合金からなること、
を特徴とするアルミニウム空気電池を提供するものである。
The present invention (2) is an air battery comprising a positive electrode material, an electrolytic solution, and a negative electrode material,
The electrolyte is an aqueous solution containing 2 to 10 M KOH or NaOH;
The negative electrode material is made of an aluminum alloy for a negative electrode material of an air battery according to claim 1,
An aluminum air battery characterized by the above is provided.
本発明によれば、常温でも電流密度が高く、通電を続けても負極の電位が卑のままの状態が維持され、自己腐食が少なく、且つ、アルカリ濃度が高い電解液を用いても電流効率が高いアルミニウム空気電池の負極材用アルミニウム合金を提供することができる。 According to the present invention, the current density is high even at room temperature, the negative electrode potential is maintained even when energization is continued, the self-corrosion is small, and the current efficiency is high even when using an electrolyte with a high alkali concentration. Can provide an aluminum alloy for a negative electrode material of an aluminum-air battery having a high value.
本発明のアルミニウム空気電池の負極材用アルミニウム合金は、０．１質量％以上１０．０質量％以下のＳｎと、０．０００１質量％以上０．０１００質量％以下のＦｅと、０．０００１質量％以上０．００５０質量％以下のＳｉと、を含有し、残部がＡｌ及び不可避不純物からなるアルミニウム合金であり、
アルミニウム合金マトリクス中に金属Ｓｎ析出物粒子を含有し、合金断面に観察される金属Ｓｎ析出物粒子のうち、０．１〜１００μｍの大きさの金属Ｓｎ析出物粒子の個数密度が、４００個／ｍｍ２以上であること、
を特徴とするアルミニウム空気電池の負極材用アルミニウム合金である。
The aluminum alloy for the negative electrode material of the aluminum-air battery of the present invention comprises 0.1 mass% or more and 10.0 mass% or less of Sn, 0.0001 mass% or more and 0.0100 mass% or less of Fe, and 0.0001 mass%. % And 0.0050% by mass or less of Si, and the balance is an aluminum alloy composed of Al and inevitable impurities,
The metal Sn precipitate particles are contained in the aluminum alloy matrix, and among the metal Sn precipitate particles observed in the cross section of the alloy, the number density of the metal Sn precipitate particles having a size of 0.1 to 100 μm is 400 / mm 2 or more,
An aluminum alloy for a negative electrode material of an aluminum-air battery.
本発明のアルミニウム空気電池の負極材用アルミニウム合金は、アルミニウム空気電池の負極材に用いられるアルミニウム合金である。 The aluminum alloy for the negative electrode material of the aluminum air battery of the present invention is an aluminum alloy used for the negative electrode material of the aluminum air battery.
本発明のアルミニウム空気電池の負極材用アルミニウム合金は、Ｓｎと、Ｆｅと、Ｓｉと、を含有し、残部Ａｌ及び不可避不純物からなるアルミニウム合金である。 The aluminum alloy for the negative electrode material of the aluminum-air battery of the present invention is an aluminum alloy containing Sn, Fe, and Si, the balance being Al and inevitable impurities.
本発明のアルミニウム空気電池の負極材用アルミニウム合金は、Ｓｎを含有する。アルミニウム合金マトリクスから析出したＳｎは、アルカリ濃度が高い電解液中において、アルミニウム合金に酸化被膜が形成されるのを阻害するので、通電時のアルミニウム合金の電位を卑にさせる効果がある。そして、本発明のアルミニウム空気電池の負極材用アルミニウム合金のＳｎ含有量は、０．１質量％以上１０．０質量％以下、好ましくは０．２質量％以上５．０質量％以下である。Ｓｎ含有量が、上記範囲未満だと、通電時の電位が十分に卑にならず、また、上記範囲を超えると、自己腐食量が多くなってしまう。 The aluminum alloy for the negative electrode material of the aluminum-air battery of the present invention contains Sn. Sn deposited from the aluminum alloy matrix inhibits the formation of an oxide film on the aluminum alloy in an electrolyte solution having a high alkali concentration, and therefore has the effect of lowering the potential of the aluminum alloy during energization. And Sn content of the aluminum alloy for negative electrode materials of the aluminum air battery of this invention is 0.1 to 10.0 mass%, Preferably it is 0.2 to 5.0 mass%. If the Sn content is less than the above range, the potential during energization is not sufficiently low, and if it exceeds the above range, the amount of self-corrosion increases.
本発明のアルミニウム空気電池の負極材用アルミニウム合金は、アルミニウム合金マトリクス中に金属Ｓｎ析出物粒子を含有する。そして、アルミニウム合金断面に観察される金属Ｓｎ析出物粒子のうち、０．１〜１００μｍの大きさの金属Ｓｎ析出物粒子の個数密度は、４００個／ｍｍ２以上、好ましくは４５０個／ｍｍ２以上２０００個／ｍｍ２以下である。０．１μｍ未満の金属Ｓｎ析出物粒子は、酸化被膜の形成を阻害する効果が低く、また、１００μｍを超える金属Ｓｎ析出物粒子の存在は、０．１〜１００μｍの大きさの金属Ｓｎ析出物粒子の個数密度を低くする要因となる。 The aluminum alloy for negative electrode material of the aluminum air battery of the present invention contains metal Sn precipitate particles in an aluminum alloy matrix. Of the metal Sn precipitate particles observed on the cross section of the aluminum alloy, the number density of the metal Sn precipitate particles having a size of 0.1 to 100 μm is 400 / mm 2 or more, preferably 450 / mm 2. The above is 2000 pieces / mm 2 or less. Metal Sn precipitate particles less than 0.1 μm have a low effect of inhibiting the formation of an oxide film, and the presence of metal Sn precipitate particles exceeding 100 μm is a metal Sn precipitate having a size of 0.1 to 100 μm. It becomes a factor to lower the number density of particles.
なお、本発明において、金属Ｓｎ析出物粒子の個数密度は、以下のようにして求められる。先ず、測定対象となるアルミニウム合金を切断して、その切断面を樹脂埋めして研磨し、研磨した表面を、ＥＰＭＡ面分析して、Ｓｎの分布を測定する。次いで、得られる分析結果から、一定の広さの範囲に存在する円相当径が０．１〜１００μｍの大きさの金属Ｓｎ析出物粒子を数え、１ｍｍ２当たりに換算することにより、金属Ｓｎ析出物粒子の個数密度を求める。 In the present invention, the number density of the metal Sn precipitate particles is determined as follows. First, an aluminum alloy to be measured is cut, the cut surface is filled with resin and polished, and the polished surface is subjected to EPMA surface analysis to measure Sn distribution. Next, from the analysis results obtained, the number of metal Sn precipitate particles having an equivalent circle diameter of 0.1 to 100 μm existing in a certain range is counted and converted per 1 mm 2 , thereby obtaining metal Sn precipitation. The number density of the product particles is obtained.
本発明のアルミニウム空気電池の負極材用アルミニウム合金は、Ｆｅ及びＳｉを含有する。Ｆｅ及びＳｉは、アルミニウム合金マトリクス中に、Ａｌ−Ｆｅ系、Ａｌ−Ｆｅ−Ｓｉ系、金属Ｓｉ等のＦｅ又はＳｉを含有する粒子として析出する。そして、アルカリ濃度が高い電解液中においては、これらのＦｅ又はＳｉを含有する析出物粒子の電位は、Ｓｎを含有するアルミニウム合金マトリクスより貴となる。すると、Ｆｅ又はＳｉを含有する析出物粒子とＳｎを含有するアルミニウム合金マトリクスとの間で、局部電池が形成されるため、自己腐食による負極材の消耗が生じ、その結果、電流効率が低くなる。自己腐食により消耗したアルミニウム合金が放出した電子は、Ｆｅ又はＳｉを含有する析出物粒子でのカソード反応で使われるため、このような電子を電流として取り出せないためである。これらのことから、Ｆｅ及びＳｉの含有量は、少ないほど好ましく、本発明のアルミニウム空気電池の負極材用アルミニウム合金のＦｅの含有量は、０．０００１質量％以上０．０１００質量％以下であり、且つ、Ｓｉの含有量は、０．０００１質量％以上０．００５０質量％以下である。 The aluminum alloy for negative electrode material of the aluminum air battery of the present invention contains Fe and Si. Fe and Si are precipitated in the aluminum alloy matrix as particles containing Fe or Si such as Al—Fe, Al—Fe—Si, and metal Si. And in the electrolyte solution with a high alkali concentration, the electric potential of the deposit particle | grains containing these Fe or Si becomes nobler than the aluminum alloy matrix containing Sn. Then, since the local battery is formed between the precipitate particles containing Fe or Si and the aluminum alloy matrix containing Sn, the negative electrode material is consumed due to self-corrosion, and as a result, the current efficiency is lowered. . This is because the electrons emitted from the aluminum alloy consumed by self-corrosion are used in the cathode reaction with the precipitate particles containing Fe or Si, so that such electrons cannot be taken out as current. For these reasons, the Fe and Si contents are preferably as low as possible, and the Fe content in the aluminum alloy for negative electrode materials of the aluminum-air battery of the present invention is 0.0001 mass% or more and 0.0100 mass% or less. And content of Si is 0.0001 mass% or more and 0.0050 mass% or less.
本発明のアルミニウム空気電池の負極材用アルミニウム合金は、例えば、所定の含有量となるようにアルミニウム合金中のＳｎ、Ｆｅ及びＳｉの含有量を調整して鋳造し、このときの鋳造物の冷却条件等を適宜選択することにより、アルミニウム合金中のＳｎ、Ｆｅ及びＳｉの含有量と、アルミニウム合金マトリクス中に析出する金属Ｓｎ析出物粒子の大きさ及び数を調節して、製造される。なお、上記は、本発明のアルミニウム空気電池の負極材用アルミニウム合金の製造方法の一例であり、これに限定されるものではない。 The aluminum alloy for the negative electrode material of the aluminum air battery of the present invention is cast, for example, by adjusting the contents of Sn, Fe and Si in the aluminum alloy so as to have a predetermined content, and cooling of the cast at this time By appropriately selecting conditions and the like, the content of Sn, Fe and Si in the aluminum alloy and the size and number of metal Sn precipitate particles precipitated in the aluminum alloy matrix are adjusted. In addition, the above is an example of the manufacturing method of the aluminum alloy for negative electrode materials of the aluminum air battery of this invention, It is not limited to this.
本発明のアルミニウム空気電池の負極材用アルミニウム合金は、アルミニウム空気電池の負極材に加工されて、アルミニウム空気電池の負極材として、好適に用いられる。そして、アルミニウム空気電池の負極材として、本発明のアルミニウム空気電池の負極材用アルミニウム合金からなる負極材を用いることにより、２〜１０Ｍ、好ましくは４〜８ＭのＫＯＨ又はＮａＯＨを含有する水溶液を、空気電池の電解液として用いる場合に、常温、例えば２０〜３０℃で、高い電流密度が得られ、通電を続けても負極の電位が卑のままの状態が維持され、すなわち、分極し難く、自己腐食が少なく、且つ、アルカリ濃度が高い電解液を用いても電流効率が高くなる。つまり、本発明のアルミニウム空気電池の負極材用アルミニウム合金は、高濃度アルカリ水溶液、すなわち、２〜１０Ｍ、好ましくは４〜８ＭのＫＯＨ又はＮａＯＨを含有する水溶液を電解液として用いるアルミニウム空気電池用の負極材として、優れた性能を発揮する。 The aluminum alloy for a negative electrode material of an aluminum air battery of the present invention is processed into a negative electrode material of an aluminum air battery and is suitably used as a negative electrode material of an aluminum air battery. And as a negative electrode material of an aluminum air battery, by using a negative electrode material made of an aluminum alloy for a negative electrode material of the present invention, an aqueous solution containing 2 to 10 M, preferably 4 to 8 M KOH or NaOH, When used as an electrolytic solution for an air battery, a high current density is obtained at room temperature, for example, 20 to 30 ° C., and the negative electrode potential is maintained even when energization is continued, that is, it is difficult to polarize, Even when an electrolytic solution having a low self-corrosion and a high alkali concentration is used, the current efficiency is increased. That is, the aluminum alloy for the negative electrode material of the aluminum-air battery of the present invention is a high-concentration alkaline aqueous solution, that is, an aluminum-air battery using an aqueous solution containing 2 to 10 M, preferably 4 to 8 M KOH or NaOH as an electrolyte. Excellent performance as a negative electrode material.
例えば、本発明のアルミニウム空気電池の負極材用アルミニウム合金は、８Ｍと高アルカリ濃度のＫＯＨ水溶液中、温度２５℃で、負極表面における電流密度が３００ｍＡ／ｃｍ２の定電流電解試験において、電極電位が−１．０Ｖ ｖｓ Ｈｇ／ＨｇＯ以下であり、−１．０Ｖ ｖｓ Ｈｇ／ＨｇＯ以下の電位を１時間以上維持でき、電流効率が９０〜９５％と高くなる。 For example, the aluminum alloy for the negative electrode material of the aluminum-air battery of the present invention has an electrode potential in a constant current electrolysis test at a temperature of 25 ° C. and a current density of 300 mA / cm 2 in a KOH aqueous solution with a high alkali concentration of 8M. Is −1.0 V vs Hg / HgO or less, a potential of −1.0 V vs Hg / HgO or less can be maintained for 1 hour or more, and the current efficiency is as high as 90 to 95%.
本発明のアルミニウム空気電池は、正極材と、電解液と、負極材と、を有するアルミニウム空気電池であって、
該電解液が、２〜１０ＭのＫＯＨ又はＮａＯＨを含有する水溶液であり、
該負極材が、本発明のアルミニウム空気電池の負極材用アルミニウム合金からなること、
を特徴とするアルミニウム空気電池である。
The aluminum air battery of the present invention is an aluminum air battery having a positive electrode material, an electrolytic solution, and a negative electrode material,
The electrolyte is an aqueous solution containing 2 to 10 M KOH or NaOH;
The negative electrode material is made of an aluminum alloy for the negative electrode material of the aluminum-air battery of the present invention;
It is the aluminum air battery characterized by this.
本発明のアルミニウム空気電池に係る正極材は、特に制限されず、例えば、白金や二酸化マンガンなどの正極触媒を含むニッケル、ステンレス、チタンの多孔質板等が挙げられる。 The positive electrode material according to the aluminum air battery of the present invention is not particularly limited, and examples thereof include a nickel, stainless steel, titanium porous plate containing a positive electrode catalyst such as platinum or manganese dioxide.
本発明のアルミニウム空気電池に係る電解液は、２〜１０Ｍ、好ましくは４〜８Ｍの濃度のＫＯＨ又はＮａＯＨを含有する水溶液である。電解液のＫＯＨ又はＮａＯＨの濃度が、上記範囲にあることにより、２０〜３０℃で、高い電流密度が得られる。一方、電解液のＫＯＨ又はＮａＯＨの濃度が、上記範囲未満だと、電流密度が低くなり、また、上記範囲を超えると、自己腐食量が著しく増大する。 The electrolytic solution according to the aluminum air battery of the present invention is an aqueous solution containing KOH or NaOH having a concentration of 2 to 10M, preferably 4 to 8M. When the concentration of KOH or NaOH in the electrolytic solution is in the above range, a high current density can be obtained at 20 to 30 ° C. On the other hand, when the concentration of KOH or NaOH in the electrolytic solution is less than the above range, the current density becomes low, and when it exceeds the above range, the amount of self-corrosion increases remarkably.
本発明のアルミニウム空気電池に係る負極材は、本発明のアルミニウム空気電池の負極材用アルミニウム合金が、負極材の形状に加工されたものである。 The negative electrode material according to the aluminum air battery of the present invention is obtained by processing the aluminum alloy for the negative electrode material of the aluminum air battery of the present invention into the shape of the negative electrode material.
本発明のアルミニウム空気電池は、正極材、電解液及び負極材の他に、必要に応じて、集電板、樹脂容器、電解液への添加剤などを有してもよい。 In addition to the positive electrode material, the electrolytic solution, and the negative electrode material, the aluminum-air battery of the present invention may have a current collector plate, a resin container, an additive to the electrolytic solution, and the like as necessary.
（実施例及び比較例）
表１に示す化学成分含有量となるようにアルミニウム合金中の化学成分量を調整してブックモールドを用いて鋳造し、１７５ｍｍ長さ、１７５ｍｍ幅、３０ｍｍ厚さの鋳塊を得た。次いで、得られた鋳塊を切断した後、切削加工して、厚さ１ｍｍの負極材用アルミニウム合金を得た。
(Examples and Comparative Examples)
The amount of the chemical component in the aluminum alloy was adjusted so as to have the chemical component content shown in Table 1, and cast using a book mold to obtain an ingot having a length of 175 mm, a width of 175 mm, and a thickness of 30 mm. Next, the obtained ingot was cut and then cut to obtain an aluminum alloy for negative electrode material having a thickness of 1 mm.
＜分析＞
（金属Ｓｎ析出物粒子の分析）
測定対象となるアルミニウム合金を切断して、その切断面を樹脂埋めして研磨し、研磨した表面を、ＥＰＭＡ面分析して、Ｓｎの分布を測定した。次いで、得られる分析結果から、一定の広さの範囲に存在する円相当径が０．１〜１００μｍの大きさの金属Ｓｎ析出物粒子を数え、１ｍｍ２当たりに換算することにより、金属Ｓｎ析出物粒子の個数密度を求めた。その結果を表１に示す。
<Analysis>
(Analysis of metal Sn precipitate particles)
The aluminum alloy to be measured was cut, the cut surface was filled with resin and polished, and the polished surface was subjected to EPMA surface analysis to measure Sn distribution. Next, from the analysis results obtained, the number of metal Sn precipitate particles having an equivalent circle diameter of 0.1 to 100 μm existing in a certain range is counted and converted per 1 mm 2 , thereby obtaining metal Sn precipitation. The number density of physical particles was determined. The results are shown in Table 1.
＜性能評価＞
上記で得た負極材用アルミニウム合金を、１５ｍｍ×５０ｍｍに切断し、試験片を得た。次いで、試験面として１０ｍｍ×１０ｍｍを露出させ、試験面以外をシリコン系の樹脂で被覆し、樹脂被覆試験片を得た。
（平均電圧）
２５℃に保たれた８Ｍ水酸化カリウム水溶液中において、Ｐｔを正極に用い、上記で得た樹脂被覆試験片を負極に用い、３００ｍＡ／ｃｍ２のアノード電流を５分間流した。このときの電位を、１Ｍ ＮａＯＨ中のＨｇ／ＨｇＯ電極を基準として測定し、５分間の平均電圧を求めた。その結果を表１に示す。なお、５分間の平均電圧が−１．０００Ｖ ｖｓ Ｈｇ／ＨｇＯ以下のものを、電流密度が高く且つ分極し難い負極材と判断した。
<Performance evaluation>
The aluminum alloy for negative electrode materials obtained above was cut into 15 mm × 50 mm to obtain test pieces. Next, 10 mm × 10 mm was exposed as a test surface, and the other surfaces were covered with a silicon-based resin to obtain a resin-coated test piece.
(Average voltage)
In an 8M aqueous potassium hydroxide solution maintained at 25 ° C., Pt was used as the positive electrode, the resin-coated test piece obtained above was used as the negative electrode, and an anode current of 300 mA / cm 2 was passed for 5 minutes. The potential at this time was measured with reference to an Hg / HgO electrode in 1M NaOH, and an average voltage for 5 minutes was obtained. The results are shown in Table 1. In addition, the thing whose average voltage for 5 minutes is -1.000V vs Hg / HgO or less was judged to be a negative electrode material with a high current density and being hard to polarize.
（腐食試験）
上記と同様にして得た樹脂被覆負極材用アルミニウム合金試験片を、８ＭＫＯＨ水溶液中に、電流を流さずに２０分浸漬した。２０分間浸漬前後の質量変化を測定し、試験面の面積で除して、腐食量を求めた。その結果を表１に示す。なお、腐食量が０．０１５ｇ／ｃｍ２以下のものを、腐食量が少ない負極材と判断する。
(Corrosion test)
An aluminum alloy test piece for a resin-coated negative electrode material obtained in the same manner as described above was immersed in an 8M KOH aqueous solution for 20 minutes without passing an electric current. The change in mass before and after immersion for 20 minutes was measured and divided by the area of the test surface to determine the amount of corrosion. The results are shown in Table 1. In addition, the corrosion amount of 0.015 g / cm 2 or less is determined as a negative electrode material with a small amount of corrosion.
２）３００ｍＡ／ｃｍ２のアノード電流を５分間流したときの平均電位
Claims (2)
アルミニウム合金マトリクス中に金属Ｓｎ析出物粒子を含有し、合金断面に観察される金属Ｓｎ析出物粒子のうち、０．１〜１００μｍの大きさの金属Ｓｎ析出物粒子の個数密度が、４００個／ｍｍ２以上であること、
を特徴とするアルミニウム空気電池の負極材用アルミニウム合金。 0.1 mass% or more and 10.0 mass% or less of Sn, 0.0001 mass% or more and 0.0100 mass% or less of Fe, and 0.0001 mass% or more and 0.0050 mass% or less of Si are contained. And the balance is an aluminum alloy composed of Al and inevitable impurities,
The metal Sn precipitate particles are contained in the aluminum alloy matrix, and among the metal Sn precipitate particles observed in the cross section of the alloy, the number density of the metal Sn precipitate particles having a size of 0.1 to 100 μm is 400 / mm 2 or more,
An aluminum alloy for a negative electrode material of an aluminum air battery.
該電解液が、２〜１０ＭのＫＯＨ又はＮａＯＨを含有する水溶液であり、
該負極材が、請求項１記載の空気電池の負極材用アルミニウム合金からなること、
を特徴とするアルミニウム空気電池。 An air battery having a positive electrode material, an electrolytic solution, and a negative electrode material,
The electrolyte is an aqueous solution containing 2 to 10 M KOH or NaOH;
The negative electrode material is made of an aluminum alloy for a negative electrode material of an air battery according to claim 1,
Aluminum air battery characterized by.