JP2015048571A - 炭素繊維及び天然繊維を備えた成形品、その製造方法及び使用 - Google Patents
炭素繊維及び天然繊維を備えた成形品、その製造方法及び使用 Download PDFInfo
- Publication number
- JP2015048571A JP2015048571A JP2014173650A JP2014173650A JP2015048571A JP 2015048571 A JP2015048571 A JP 2015048571A JP 2014173650 A JP2014173650 A JP 2014173650A JP 2014173650 A JP2014173650 A JP 2014173650A JP 2015048571 A JP2015048571 A JP 2015048571A
- Authority
- JP
- Japan
- Prior art keywords
- fiber
- mass
- layer
- mat
- range
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【課題】繊維マット並びに成形品を提供する。
【解決手段】繊維マットは第一の繊維層を備え、その第一の繊維層は、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維を組み合わせることによって形成されている。また、成形品は、繊維マットから成形された成形基体を備え、その繊維マットは、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維を組み合わせることによって形成された第一の繊維層を備える。
【選択図】図１
【解決手段】繊維マットは第一の繊維層を備え、その第一の繊維層は、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維を組み合わせることによって形成されている。また、成形品は、繊維マットから成形された成形基体を備え、その繊維マットは、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維を組み合わせることによって形成された第一の繊維層を備える。
【選択図】図１
Description
本開示は、炭素繊維及び天然繊維を備えた軽量成形品の製造、それに関連する処理及び製造の方法に関する。
環境を意識した製造業者は、再利用／再生材料、並びに再生可能資源からの材料を使用することによって、製品の二酸化炭素排出量を減らそうとしている。
運送業においては、多くの製品が、繊維が硬化樹脂に埋め込まれている繊維強化複合材で形成されている。特に、航空業界では、こうした材料の高い強度対重量比に起因して、多くの構造部品に対して炭素繊維強化複合品が使用されている。
炭素繊維強化複合品の製造プロセスでは、必然的にプロセススクラップが生じる。炭素繊維強化複合品の製造による製造プロセススクラップは、未使用の炭素繊維、並びに、多様な表面処理（例えば、結合剤）及び樹脂含浸された炭素繊維を含み得る。こうしたスクラップは、一般的に、トリム廃棄物や拒絶された（欠陥のある）成形品の形状であり得る。
更に、炭素繊維強化複合品自体が、同様に、その寿命の終わりにはスクラップになる。寿命末期（ＥＯＬ，ｅｎｄ‐ｏｆ‐ｌｉｆｅ）スクラップは、製造ストラップとは対照的に、環境に晒された強化樹脂に埋め込まれた炭素繊維を含み得る。ＥＯＬスクラップは、製造後に炭素繊維強化複合品に加えられた追加の構成要素（例えば、コーティングや、締結具）、並びに汚染物質も含み得る。
製造の多様な段階及び製品の寿命の終わりにおいて繊維強化複合品から炭素繊維を再生するプロセスが開発されている。しかしながら、再生炭素繊維の特性が、未使用の炭素繊維よりも劣る可能性を考慮して、航空業界では、このような再生炭素繊維を航空機の部品に戻して組み込むことに抵抗がある。
一方、自動車業界においては、自動車製造業者は、未使用の炭素繊維を広く使用することはない。未使用の炭素繊維は、炭素繊維強化複合品の強度対重量比を必要とする限られた応用を除いて、経済的な使用には一般的に高価過ぎると考えられる。むしろ、自動車製造業者は、長年にわたってガラス繊維を使用しており、最近では、特に軽量化のために特定の天然繊維を使用するようになってきている。しかしながら、天然繊維は、ガラス繊維のような物理特性及び寸法安定性を提供しないことが多い。
自動車の特定の応用において必要とされているのは、顕著に悪い影響をコストに与えずに、重量を更に減らし、物理特性及び寸法を上昇させる改良型の繊維強化材である。
本開示の一実施形態では、第一の繊維層を備えた繊維マットが提供され、その第一の繊維層は、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維を組み合わせることによって形成される。
本開示の他の実施形態では、第一の繊維層と第二の繊維層との間に挟まれたコア層を備えた繊維マットが提供され、その第一の繊維層は、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維を組み合わせることによって形成され、また、その第二の繊維層は、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維を組み合わせることによって形成される。
本開示の他の実施形態では、繊維マットから成形された成形基体を備えた成形品が提供され、その繊維マットは、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維を組み合わせることによって形成された第一の繊維層を備える。
本開示の上述の及び他の特徴、並びにそのような特徴を得るための手法は、添付図面と共に説明される以下の実施形態の説明を参照することによって、より明らかになり、より良く理解されるものである。
本開示は、以下の説明に与えられていたり、図面に示されていたりする構成要素の構成及び配置の詳細にその応用を限定するものではないことを理解されたい。本発明は、他の実施形態においても多様な方法で実現可能なものである。また、当業者には理解されるように、本願で用いられている用語は、説明を目的とするものであり、限定を目的とするものではない。
図面を参照すると、図１は、本開示に係る平坦な繊維マット１０の第一の例示的な実施形態を示す。図示されているように、繊維マット１０は第一の繊維層１２を備える。特に、繊維層１２は、以下のように、異なる材料組成の繊維を備え得る：
・ 繊維層１２の４５〜５５質量％は、ポリマー繊維、特に合成ポリマー繊維から形成され得る。例示的な合成ポリマー繊維として、ポリプロピレン繊維が挙げられ、更に、そのポリプロピレン繊維は、ポリプロピレンホモポリマー及び／又はポリプロピレンコポリマー（例えば、ポリプロピレン‐無水マレイン酸コポリマー）の繊維を含み得る。ポリマー繊維は、８ｍｍから４０ｍｍ、特に１２ｍｍから２５ｍｍの長さを有し得る。特に、ポリマー繊維は、２．１６ｋｇの負荷における２３０℃でのＡＳＴＭ Ｄ１２３８‐１３に従って決定された０．１〜１０ｇ／１０分、特に２．１６ｋｇの負荷における２３０℃でのＡＳＴＭ Ｄ１２３８‐１３に従って決定された０．６〜６ｇ／１０分のメルトフローインデックスを有し得る；
・ 繊維層１２の３５〜４５質量％は、天然繊維から形成され得る。例示的な天然繊維は、ケナフ麻、亜麻、黄麻、サイザル麻、及びセルロースのうち一つ以上を含み得る。天然繊維は、８ｍｍから４０ｍｍ、特に１２ｍｍから２５ｍｍの長さを有し得る；そして、
・ 繊維層１２の５〜１５質量％は、炭素繊維から形成され得る。更に、炭素繊維は、未使用及び／又は再生された炭素繊維を含み得る。炭素繊維は、８ｍｍから４０ｍｍ、特に１２ｍｍから２５ｍｍの長さを有し得る。
・ 繊維層１２の４５〜５５質量％は、ポリマー繊維、特に合成ポリマー繊維から形成され得る。例示的な合成ポリマー繊維として、ポリプロピレン繊維が挙げられ、更に、そのポリプロピレン繊維は、ポリプロピレンホモポリマー及び／又はポリプロピレンコポリマー（例えば、ポリプロピレン‐無水マレイン酸コポリマー）の繊維を含み得る。ポリマー繊維は、８ｍｍから４０ｍｍ、特に１２ｍｍから２５ｍｍの長さを有し得る。特に、ポリマー繊維は、２．１６ｋｇの負荷における２３０℃でのＡＳＴＭ Ｄ１２３８‐１３に従って決定された０．１〜１０ｇ／１０分、特に２．１６ｋｇの負荷における２３０℃でのＡＳＴＭ Ｄ１２３８‐１３に従って決定された０．６〜６ｇ／１０分のメルトフローインデックスを有し得る；
・ 繊維層１２の３５〜４５質量％は、天然繊維から形成され得る。例示的な天然繊維は、ケナフ麻、亜麻、黄麻、サイザル麻、及びセルロースのうち一つ以上を含み得る。天然繊維は、８ｍｍから４０ｍｍ、特に１２ｍｍから２５ｍｍの長さを有し得る；そして、
・ 繊維層１２の５〜１５質量％は、炭素繊維から形成され得る。更に、炭素繊維は、未使用及び／又は再生された炭素繊維を含み得る。炭素繊維は、８ｍｍから４０ｍｍ、特に１２ｍｍから２５ｍｍの長さを有し得る。
特に、繊維層１２は、参照としてその全体が本願に組み込まれるＵｔｉｌｉｚａｔｉｏｎ ｏｆ Ｒｅｃｙｃｌｅｄ ＣａｒｂｏｎＦｉｂｅｒとの名称の特許文献１に開示されているプロセスによって、平坦なシートとして形成され得る。また、繊維層１２は、エアレイ（ａｉｒｌａｙ）プロセス等の乾式レイド方式の不織布製造プロセス等によっても、平坦なシートに形成され得る。特に、繊維層１２は、５００〜１０００ｇ／ｍ２（ｇｓｍ，ｇｒａｍｓ／ｓｑｕａｒｅ ｍｅｔｅｒ）の面積質量を有し得る。
特許文献１に開示されているプロセスを用いて製造される例示的な一実施形態では、
８４０ｇｓｍの質量を有する繊維層１２が、以下のものから形成され得る：
・ ５０％のポリプロピレン‐無水マレイン酸コポリマー繊維であって、９５〜９９質量％のポリプロピレンと、ポリプロピレンに対するコモノマーとして１〜５質量％の無水マレイン酸とを備えるもの；
・ ４０％の天然繊維であって、そのうちの３８％がケナフ麻、黄麻、及び亜麻の組み合わせであって、２％がセルロース繊維であるもの；及び、
・ １０％の再生炭素繊維。
８４０ｇｓｍの質量を有する繊維層１２が、以下のものから形成され得る：
・ ５０％のポリプロピレン‐無水マレイン酸コポリマー繊維であって、９５〜９９質量％のポリプロピレンと、ポリプロピレンに対するコモノマーとして１〜５質量％の無水マレイン酸とを備えるもの；
・ ４０％の天然繊維であって、そのうちの３８％がケナフ麻、黄麻、及び亜麻の組み合わせであって、２％がセルロース繊維であるもの；及び、
・ １０％の再生炭素繊維。
繊維層１２に加えて、繊維マット１０は、第二の繊維層１４及び第三の繊維層１６を更に備え得て、特に、それらの層１４及び１６は、３０〜１００ｇｓｍ、特に５０〜７５ｇｓｍの面積質量を有する不織スクリムで構成され、それぞれ第一の繊維層１２の対向する前面及び裏面に配置される。不織スクリムは、ポリエチレンテレフタレートで特に形成され得て、これは、以下で詳細に説明するように、装飾カバーに対する繊維マット１０の結合を促進し、また、後に形成されるリブ及び締結部に対する結合も促進する。
炭素繊維を含有する繊維層１２を使用しない繊維マットと比較して、本開示に係る繊維マット１０は、以下のような、引張強度及び熱変形温度の物理特性の向上を示し得る。
図２に示されるような繊維マット１０’の第二の実施形態では、繊維マット１０’は、対向する二つの繊維層１２ａ、１２ｂの間に挟まれたコア１８を備え得る。コア１８は、３００〜１０００ｇｓｍの面積質量と、０．５から１．５ｍｍの厚さとを有し得る。コア１８は、再生羊毛、ボール紙、ハニカム、ポリウレタン発泡体で形成され得る。第一の実施形態と比較して、繊維層１２ａ、１２ｂの各々は、１００〜６００ｇｓｍの面積質量を有し得る。
図３に示されるように、繊維マット１０は、成形品７０を製造するのに用いられ得る。製品７０は、まず、４５〜６０秒間の期間で３７５〜４２５℃の温度に、又は、繊維マット１０が４００℃の温度に達するまで、対向する二枚の加熱プレート２０、２２の間で繊維マット１０を加熱することによって、形成され得る。繊維マット１０が十分に加熱されると、繊維マット１０を、第一の加熱圧縮モールド３０の対向する二つの半分の部分３２、３４の間に配置し得る。圧縮モールドは、６０〜１２０℃の温度に加熱され得る。モールド３０を閉じて、合成ポリマー樹脂が基体４０を形成するような圧縮下において流れて、繊維マット１０が基体４０に成形され得る。次に、基体４０を冷却して、圧縮モールド３０から取り外し得る。基体４０は、０．５〜２ｍｍの厚さを有し得て、特に１〜１．５ｍｍの厚さを有し得る。
次に、基体４０を、装飾カバー層６０（シート状であり得る）と共に、第二の圧縮モールド５０の対向する二つの半分の部分５２、５４の間に配置し得る。次に、第二の圧縮モールド５０を閉じて、圧縮成形を行い、装飾カバー層６０を基体４０に積層して、装飾カバー層６０が基体４０の外側スクリム層１４に結合した成形品７０を形成し得る。
装飾カバー層６０は、ポリ塩化ビニル（ＰＶＣ，ｐｏｌｙｖｉｎｙｌ ｃｈｌｏｒｉｄｅ）、熱可塑性ウレタン（ＴＰＵ，ｔｈｅｒｍｏｐｌａｓｔｉｃ ｕｒｅｔｈａｎｅ）、熱可塑性オレフィン（ＴＰＯ，ｔｈｅｒｍｏｐｌａｓｔｉｃ ｏｌｅｆｉｎ）で形成され得る。装飾カバー層は、０．５〜２．５ｍｍの範囲内の厚さを有し得て、また、ポリ塩化ビニル（ＰＶＣ）又はポリオレフィン発泡体のクッション層に重なる塩化ポリビニル（ＰＶＣ）、熱硬化性ウレタン（ＴＰＵ）、熱硬化性オレフィン（ＴＰＯ）の外側スキンで形成され得る。
代替実施形態では、装飾カバー層６０は、繊維マット１０と共に、第一の圧縮モールド３０に導入されて、１ステップで成形品７０が形成され得て、この場合、単一のモールド３０が用いられる。
更なる代替実施形態では、装飾層６０が必ずしも要求されず、成形品７０が基体４０のみを備え得る。繊維マット１０’が図３のプロセスに示される繊維マット１０’となり得ることは理解されたい。
図４に示されるような図３のプロセスの代替実施形態では、圧縮モールド３０が、射出圧縮モールド３０’として構成され得て、射出圧縮成形で使用される射出圧縮成形機のスクリュー可塑化ユニット等のポリマー送達ユニット３６から樹脂を受け取るように構成される。この場合、繊維マット１０の圧縮成形の後で、ポリマー送達ユニット３８から、モールドの半分の部分の中の適切なランナ３８を介して、ポリマー材料が、圧縮成形された基体の裏面に送達されて、基体４０’の裏面に対して、基体４０’の長さ方向に延伸する複数の細長の強化（補強）リブ４２と、締結部（例えば、ネジ山、ドッグハウス等）が成形され得る。
成形品７０は、サイドトリムパネル（例えば、ドアトリムパネル）等の内装又は外装トリムパネル等の自動車用トリム部品、パッケージトレイ、天井、インストルメントパネル、上部又は下部インストルメントパネルクローズアウトパネル、コンソール、トランクのライナ、ドアボルスタ、ニーボルスタ、シートバックであり得る。
本発明の好ましい実施形態について説明してきたが、多様な変更、調整、及び修正を本発明の精神及び添付の特許請求の範囲から逸脱することなく行うことができることを理解されたい。従って、本発明の範囲は、上記の説明で定められるものではなく、添付の特許請求の範囲をその等価物の完全な範囲と共に参照することによって定められるものである。更に、添付の特許請求の範囲は、出願人が特許請求する権利を有する最大の範囲、本発明を特許請求することができる唯一のものを必ずしも備えるものではなく、記載された全ての特徴が必要という訳でもないことを理解されたい。
１０ 繊維マット
１２、１４、１６ 繊維層
１８ コア
１２、１４、１６ 繊維層
１８ コア
Claims (27)
- 第一の繊維層を備えた繊維マットであって、
前記第一の繊維層が、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維とを組み合わせることによって形成されている、繊維マット。 - 前記第一の繊維層が、５００〜１０００ｇ／ｍ２の範囲内の面積質量を有する、請求項１に記載の繊維マット。
- 前記炭素繊維が、未使用の炭素繊維及び再生炭素繊維のうち少なくとも一方を備える、請求項１に記載の繊維マット。
- 前記炭素繊維が、８〜４０ミリメートルの範囲内の長さを有する、請求項１に記載の繊維マット。
- 前記天然繊維が、ケナフ麻、黄麻、亜麻、及びセルロース繊維のうち少なくとも一つを備える、請求項１に記載の繊維マット。
- 前記天然繊維が、８〜４０ミリメートルの範囲内の長さを有する、請求項１に記載の繊維マット。
- 前記合成ポリマー繊維が、熱可塑性繊維を備える、請求項１に記載の繊維マット。
- 前記合成ポリマー繊維が、ポリプロピレン繊維を備える、請求項１に記載の繊維マット。
- 前記ポリプロピレン繊維が、ポリプロピレン‐無水マレイン酸コポリマーを備える、請求項８に記載の繊維マット。
- 前記合成ポリマー繊維が、８〜４０ミリメートルの範囲内の長さを有する、請求項１に記載の繊維マット。
- 前記第一の繊維層の前面に第二の繊維層を更に備え、前記第二の繊維層が、３０〜１００ｇ／ｍ２の範囲内の面積質量を有するスクリム層を備える、請求項１に記載の繊維マット。
- 前記第二の繊維層の繊維が、ポリエチレンテレフタレート繊維を備える、請求項１１に記載の繊維マット。
- 前記第一の繊維層の裏面に第三の繊維層を更に備え、前記第三の繊維層が、３０〜１００ｇ／ｍ２の範囲内の面積質量を有するスクリム層を備える、請求項１１に記載の繊維マット。
- 前記第三の繊維層の繊維が、ポリエチレンテレフタレート繊維を備える、請求項１３に記載の繊維マット。
- 第一の繊維層と第二の繊維層との間に挟まれたコア層を備えた繊維マットであって、
前記第一の繊維層が、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維とを組み合わせることによって形成されていて、
前記第二の繊維層が、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維とを組み合わせることによって形成されている、繊維マット。 - 前記第一の繊維層が、１００〜６００ｇ／ｍ２の範囲内の面積質量を有し、且つ、
前記第二の繊維層が、１００〜６００ｇ／ｍ２の範囲内の面積質量を有する、請求項１５に記載の繊維マット。 - 前記コア層が、３００〜１０００ｇ／ｍ２の範囲内の面積質量を有する、請求項１５に記載の繊維マット。
- 前記コア層が、ポリマー発泡体、ハニカム、ボール紙、金属メッシュのうち少なくとも一つで形成されている、請求項１５に記載の繊維マット。
- 繊維マットから成形された成形基体を備えた成形品であって、
前記繊維マットが、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維とを組み合わせることによって形成された第一の繊維層を備える、成形品。 - 前記第一の繊維層が、５００〜１０００ｇ／ｍ２の範囲内の面積質量を有する、請求項１９に記載の成形品。
- 前記繊維マットが、４５〜５５質量％の合成ポリマー繊維と、３５〜４５質量％の天然繊維と、５〜１５質量％の炭素繊維とを組み合わせることによって形成された第二の繊維層を備える、請求項１９に記載の成形品。
- 前記第一の繊維層が、１００〜６００ｇ／ｍ２の範囲内の面積質量を有し、且つ、
前記第二の繊維層が、１００〜６００ｇ／ｍ２の範囲内の面積質量を有する、請求項２１に記載の成形品。 - 前記第一の繊維層と前記第二の繊維層との間に挟まれたコア層を更に備える請求項２１に記載の成形品。
- 前記コア層が、３００〜１０００ｇ／ｍ２の範囲内の面積質量を有する、請求項２３に記載の成形品。
- 前記コア層が、ポリマー発泡体、ハニカム、ボール紙、金属メッシュのうち少なくとも一つで形成されている、請求項２３に記載の成形品。
- 前記成形基体に重なった装飾カバーを更に備えた請求項１９に記載の成形品。
- 前記装飾カバーがシートから形成されている、請求項２６に記載の成形品。