JP2015013966A - Chain lubricant composition and chain - Google Patents

Chain lubricant composition and chain Download PDF

Info

Publication number
JP2015013966A
JP2015013966A JP2013142096A JP2013142096A JP2015013966A JP 2015013966 A JP2015013966 A JP 2015013966A JP 2013142096 A JP2013142096 A JP 2013142096A JP 2013142096 A JP2013142096 A JP 2013142096A JP 2015013966 A JP2015013966 A JP 2015013966A
Authority
JP
Japan
Prior art keywords
chain
lubricant composition
less
mass
fatty acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2013142096A
Other languages
Japanese (ja)
Other versions
JP2015013966A5 (en
JP5808775B2 (en
Inventor
邦仁 吉井
Kunihito Yoshii
邦仁 吉井
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tsubakimoto Chain Co
Original Assignee
Tsubakimoto Chain Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tsubakimoto Chain Co filed Critical Tsubakimoto Chain Co
Priority to JP2013142096A priority Critical patent/JP5808775B2/en
Priority to PCT/JP2014/066325 priority patent/WO2015001978A1/en
Priority to US14/898,887 priority patent/US20160137948A1/en
Priority to CN201480036734.3A priority patent/CN105339478A/en
Priority to DE112014003161.5T priority patent/DE112014003161T5/en
Publication of JP2015013966A publication Critical patent/JP2015013966A/en
Publication of JP2015013966A5 publication Critical patent/JP2015013966A5/ja
Application granted granted Critical
Publication of JP5808775B2 publication Critical patent/JP5808775B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a chain lubricant composition that can easily suppress the blackening of chain, and a chain with said composition applied thereon.SOLUTION: The chain lubricant composition contains a base oil, a viscosity improver, and a rust inhibitor. The chain lubricant composition is composed so as sulfur to be 100 mass ppm or less, phosphorus to be 1 mass% or less, and aromatic content to be 1 mass% or less. The chain lubricant composition preferably further contains an oily agent, and the oily agent preferably is composed of a compound having sulfur of 100 mass ppm or less, phosphorus of 1 mass% or less, and aromatic content of 1 mass% or less. The oily agent preferably comprises at least one selected from fatty acid esters and lanolin fatty acid alcohol esters. The chain lubricant composition preferably is used in a bath for chain immersion.

Description

本発明は、チェーン用潤滑剤組成物及びそれを適用したチェーンに関する。   The present invention relates to a chain lubricant composition and a chain to which the same is applied.

従来、チェーンの潤滑に用いられるチェーン用潤滑剤組成物としては、基油と増粘剤とを含有する構成が知られている。例えば、特許文献１には、増粘剤の一種であるワックスを含有し、ちょう度が６０以上４７５以下であり、滴点が６０℃以上、１２０℃以下であるチェーン用潤滑剤組成物が開示されている。   Conventionally, a structure containing a base oil and a thickener is known as a chain lubricant composition used for chain lubrication. For example, Patent Document 1 discloses a chain lubricant composition containing a wax which is a kind of thickener, having a consistency of 60 to 475, and a dropping point of 60 ° C to 120 ° C. Has been.

特開２００９−１４４００５号公報JP 2009-144005 A

ところで、チェーンの外観は、チェーン用潤滑剤組成物の黒色化によって損なわれることがある。また、黒色化したチェーン用潤滑剤組成物が、チェーンの使用時に周囲に飛散した場合、その周囲における汚れが目立ち易くなる。なお、上述した特許文献１は、チェーンの黒色化の改善について何ら教示していない。   By the way, the external appearance of a chain may be impaired by blackening of the lubricant composition for chains. Further, when the blackened lubricant composition for the chain is scattered around the chain when it is used, the dirt around the chain is easily noticeable. Note that Patent Document 1 described above does not teach any improvement in blackening of the chain.

本発明は、こうした実情に鑑みてなされたものであり、その目的は、チェーンの黒色化を抑制することの容易なチェーン用潤滑剤組成物及びそれを適用したチェーンを提供することにある。   The present invention has been made in view of such circumstances, and an object thereof is to provide a lubricant composition for a chain that can easily suppress the blackening of the chain and a chain to which the same is applied.

上記課題を解決するチェーン用潤滑剤組成物は、基油、増粘剤、及び防錆剤を含有するチェーン用潤滑剤組成物であって、前記組成物は、硫黄が１００質量ｐｐｍ以下、リンが１質量％以下、アロマ分が１質量％以下となるように構成されている。   A lubricant composition for a chain that solves the above problems is a lubricant composition for a chain containing a base oil, a thickener, and a rust preventive agent, wherein the composition contains 100 mass ppm or less of sulfur, phosphorus Is 1% by mass or less, and the aroma content is 1% by mass or less.

本発明者は、チェーン用潤滑剤組成物に硫黄、リン及びアロマ分の少なくとも一種が含有されると、加熱による黒色化が促進されることを見いだした。すなわち、硫黄が１００質量ｐｐｍ以下、リンが１質量％以下、アロマ分が１質量％以下となるようにチェーン用潤滑剤組成物を構成することで、硫黄、リン及びアロマ分を要因とした黒色化が抑制される。   The present inventor has found that blackening by heating is promoted when at least one of sulfur, phosphorus and aroma is contained in the chain lubricant composition. That is, by configuring the chain lubricant composition so that sulfur is 100 mass ppm or less, phosphorus is 1 mass% or less, and the aroma content is 1 mass% or less, black due to sulfur, phosphorus, and aroma content. Is suppressed.

上記チェーン用潤滑剤組成物は、さらに、油性剤を含有し、前記油性剤は、硫黄が１００質量ｐｐｍ以下、リンが１質量％以下、アロマ分が１質量％以下の化合物からなることが好ましい。   The chain lubricant composition further contains an oily agent, and the oily agent is preferably composed of a compound having sulfur of 100 mass ppm or less, phosphorus of 1 mass% or less, and an aromatic content of 1 mass% or less. .

上記チェーン用潤滑剤組成物について、前記油性剤は、脂肪酸エステル及びラノリン脂肪酸アルコールエステルから選ばれる少なくとも一種を含むことが好ましい。
上記チェーン用潤滑剤組成物は、チェーン浸漬用の槽内で用いられることが好ましい。 About the said lubricant composition for chains, it is preferable that the said oil-based agent contains at least 1 type chosen from fatty acid ester and lanolin fatty-acid alcohol ester.
The chain lubricant composition is preferably used in a chain immersion bath.

上記課題を解決するチェーンは、前記チェーン用潤滑剤組成物を適用したチェーンである。   The chain that solves the above problem is a chain to which the chain lubricant composition is applied.

本発明によれば、チェーンの黒色化を抑制することが容易となる。   According to the present invention, it is easy to suppress the blackening of the chain.

実施形態のチェーンの一部を概略的に示す分解斜視図。The disassembled perspective view which shows a part of chain of embodiment schematically. チェーンを概略的に示す部分断面図。The fragmentary sectional view which shows a chain roughly.

以下、チェーン用潤滑剤組成物及びチェーンの実施形態について説明する。
チェーン用潤滑剤組成物は、基油、増粘剤、及び防錆剤を含有する。チェーン用潤滑剤組成物は、硫黄が１００質量ｐｐｍ以下、リンが１質量％以下、アロマ分が１質量％以下となるように構成されている。 Hereinafter, embodiments of the lubricant composition for chains and the chain will be described.
The lubricant composition for a chain contains a base oil, a thickener, and a rust inhibitor. The chain lubricant composition is configured such that sulfur is 100 mass ppm or less, phosphorus is 1 mass% or less, and the aroma content is 1 mass% or less.

＜基油＞
基油は、硫黄が１００質量ｐｐｍ以下、リンが１質量％以下、アロマ分が１質量％以下の基油からなることが好ましい。基油としては、鉱油及び合成油から選ばれる少なくとも一種が好適に用いられる。鉱油としては、硫黄の含有量が少なく、リン及びアロマ分を実質的に含有しないものが好適である。こうした鉱油は、プロセス油として市販されるものから選択して用いることができる。鉱油の成分としては、流動パラフィン等のパラフィン系炭化水素が挙げられる。パラフィン系炭化水素は、ｎ−ｄ−Ｍ法の環分析において、パラフィン炭素数（％ＣＰ）が５０以上のものを示す。 <Base oil>
The base oil is preferably composed of a base oil having a sulfur content of 100 mass ppm or less, a phosphorus content of 1 mass% or less, and an aroma content of 1 mass% or less. As the base oil, at least one selected from mineral oil and synthetic oil is preferably used. As the mineral oil, those having a low sulfur content and substantially not containing phosphorus and aroma are preferred. Such mineral oils can be selected from those commercially available as process oils. Examples of mineral oil components include paraffinic hydrocarbons such as liquid paraffin. Paraffinic hydrocarbons have a paraffin carbon number (% CP) of 50 or more in the ring analysis of the ndM method.

合成油としては、例えば、合成炭化水素（ポリ−α−オレフィン：ＰＡＯ、エチレンとα−オレフィンとのコオリゴマー、ポリブテン等）、エステル、ポリフェニルエーテル、ポリアルキレングリコール、シリコーン、及びフルオロカーボンが挙げられる。エステルとしては、例えば、ヒンダードエステル（二塩基酸エステル、ポリオールエステル等）、ジエステル、及びケイ酸エステルが挙げられる。   Synthetic oils include, for example, synthetic hydrocarbons (poly-α-olefins: PAO, ethylene and α-olefin co-oligomers, polybutenes, etc.), esters, polyphenyl ethers, polyalkylene glycols, silicones, and fluorocarbons. . Examples of the ester include hindered esters (dibasic acid esters, polyol esters, etc.), diesters, and silicate esters.

基油は、一種又は二種以上を用いることができる。
チェーン用潤滑剤組成物中における基油の含有量は、好ましくは７０質量％以上である。 1 type, or 2 or more types can be used for a base oil.
The content of the base oil in the chain lubricant composition is preferably 70% by mass or more.

＜増粘剤＞
増粘剤は、常温（２５℃）で固体状であり、基油に分散又は溶解することで基油を増粘する働きを有する。増粘剤は、硫黄が１００質量ｐｐｍ以下であり、リンが１質量％以下であり、アロマ分が１質量％以下の化合物からなることが好ましい。増粘剤としては、重合型ポリエチレンワックス、及びポリマーから選ばれる少なくとも一種が好適に用いられる。ポリマーとしては、例えば、ポリメタクリレート、及びポリイソブチレンが挙げられる。 <Thickener>
The thickener is solid at normal temperature (25 ° C.) and has a function of thickening the base oil by being dispersed or dissolved in the base oil. The thickener is preferably composed of a compound having sulfur of 100 mass ppm or less, phosphorus of 1 mass% or less, and an aroma content of 1 mass% or less. As the thickener, at least one selected from polymerized polyethylene wax and polymer is preferably used. Examples of the polymer include polymethacrylate and polyisobutylene.

増粘剤は、一種又は二種以上を用いることができる。
チェーン用潤滑剤組成物中における増粘剤の含有量は、好ましくは１質量％以上である。チェーン用潤滑剤組成物中の増粘剤の含有量は、好ましくは２５質量％以下である。 One or more thickeners can be used.
The content of the thickener in the chain lubricant composition is preferably 1% by mass or more. The content of the thickener in the chain lubricant composition is preferably 25% by mass or less.

＜防錆剤＞
防錆剤は、硫黄が１００質量ｐｐｍ以下、リンが１質量％以下、アロマ分が１質量％以下の化合物からなることが好ましい。防錆剤としては、例えば、ソルビタン系防錆剤、ラノリン系防錆剤、コハク酸系防錆剤、アミン系防錆剤、及び金属石けんが好適に用いられる。 <Rust preventive>
The rust preventive agent is preferably composed of a compound having sulfur of 100 mass ppm or less, phosphorus of 1 mass% or less, and an aroma content of 1 mass% or less. As the rust preventive agent, for example, sorbitan rust preventive agent, lanolin rust preventive agent, succinic acid rust preventive agent, amine rust preventive agent, and metal soap are preferably used.

ソルビタン系防錆剤としては、例えば、ソルビタン脂肪酸エステル（ソルビタンモノオレエート、ソルビタントリステアレート等）が挙げられる。
ラノリン系防錆剤としては、例えば、ラノリン脂肪酸アルコール、及びラノリン脂肪酸アルコールエステルが挙げられる。 Examples of the sorbitan rust preventive include sorbitan fatty acid esters (sorbitan monooleate, sorbitan tristearate, etc.).
Examples of the lanolin-based rust preventive include lanolin fatty acid alcohol and lanolin fatty acid alcohol ester.

コハク酸系防錆剤としては、例えば、無水アルキルコハク酸等のアルキルコハク酸誘導体が挙げられる。
アミン系防錆剤としては、例えば、有機酸アミン塩、及び脂肪酸アミン塩が挙げられる。 Examples of the succinic acid-based rust preventive include alkyl succinic acid derivatives such as alkyl succinic anhydride.
Examples of the amine-based rust preventive include organic acid amine salts and fatty acid amine salts.

金属石けんとしては、例えば、ラノリン脂肪酸石けんが挙げられる。
防錆剤は、一種又は二種以上を用いることができる。防錆剤は、ソルビタン脂肪酸エステルを含むことが好ましい。 Examples of the metal soap include lanolin fatty acid soap.
One or more rust inhibitors can be used. It is preferable that a rust preventive agent contains sorbitan fatty acid ester.

チェーン用潤滑剤組成物中における防錆剤の含有量は、好ましくは１質量％以上である。チェーン用潤滑剤組成物中の防錆剤の含有量は、好ましくは１０質量％以下である。
＜その他の成分＞
チェーン用潤滑剤組成物には、油性剤を含有させることができる。 The content of the rust inhibitor in the chain lubricant composition is preferably 1% by mass or more. The content of the rust inhibitor in the chain lubricant composition is preferably 10% by mass or less.
<Other ingredients>
The chain lubricant composition may contain an oily agent.

油性剤は、硫黄が１００質量ｐｐｍ以下、リンが１質量％以下、アロマ分が１質量％以下の化合物からなることが好ましい。
油性剤としては、例えば、脂肪酸エステル、ラノリン脂肪酸アルコールエステル、長鎖脂肪酸、長鎖脂肪酸塩、有機アルコール、及びアルキルアミンが挙げられる。脂肪酸エステルは、例えば、下記一般式（１）で表される。 The oily agent is preferably composed of a compound having sulfur of 100 mass ppm or less, phosphorus of 1 mass% or less, and an aroma content of 1 mass% or less.
Examples of the oily agent include fatty acid esters, lanolin fatty acid alcohol esters, long chain fatty acids, long chain fatty acid salts, organic alcohols, and alkylamines. The fatty acid ester is represented, for example, by the following general formula (1).

Ｒ１ＣＯＯＲ２ ・・・（１）
一般式（１）中、Ｒ１は炭素数７〜１８の飽和又は不飽和アルキル基であり、Ｒ２は炭素数１〜４のアルキル基を示す。 R 1 COOR 2 (1)
In general formula (1), R 1 is a saturated or unsaturated alkyl group having 7 to 18 carbon atoms, and R 2 represents an alkyl group having 1 to 4 carbon atoms.

ラノリン脂肪酸アルコールエステルとしては、例えば、ラノリン脂肪酸ラノリンアルコールエステル（商品名：Ｅｃｏｌａｎｏ ＬＹ，ＬＣ、日本精化株式会社製）、及びラノリン脂肪酸ペンタエリスリトールエステル（商品名：ネオコートＥＰＳ−２，ＥＰＳ−２４、日本精化株式会社製）が挙げられる。なお、ラノリン脂肪酸アルコールエステルは、防錆効果も得られ易い。   Examples of the lanolin fatty acid alcohol ester include lanolin fatty acid lanolin alcohol ester (trade name: Ecolano LY, LC, manufactured by Nippon Seika Co., Ltd.), and lanolin fatty acid pentaerythritol ester (trade name: Neocoat EPS-2, EPS-24, Nippon Seika Co., Ltd.). In addition, lanolin fatty acid alcohol ester is easy to obtain a rust prevention effect.

長鎖脂肪酸としては、炭素数７〜１７の飽和又は不飽和脂肪酸が挙げられる。長鎖脂肪酸としては、例えば、ステアリン酸、及びオレイン酸が挙げられる。有機アルコールとしては、例えば、ラウリルアルコールが挙げられる。アルキルアミンとしては、例えばステアリルアミンが挙げられる。   Examples of the long chain fatty acid include saturated or unsaturated fatty acids having 7 to 17 carbon atoms. Examples of the long chain fatty acid include stearic acid and oleic acid. Examples of the organic alcohol include lauryl alcohol. Examples of the alkylamine include stearylamine.

油性剤は、一種又は二種以上を用いることができる。
チェーン用潤滑剤組成物は、油性剤を含有することが好ましく、その油性剤は脂肪酸エステル及びラノリン脂肪酸アルコールエステルから選ばれる少なくとも一種を含むことがより好ましい。 One or two or more oily agents can be used.
The chain lubricant composition preferably contains an oily agent, and the oily agent more preferably contains at least one selected from fatty acid esters and lanolin fatty acid alcohol esters.

チェーン用潤滑剤組成物中の油性剤の含有量は、好ましくは１質量％以上、１０質量％以下の範囲である。チェーン用潤滑剤組成物は、脂肪酸エステルを１質量％以上、１０質量％以下の範囲で含有することがより好ましい。   The content of the oil-based agent in the chain lubricant composition is preferably in the range of 1 to 10% by mass. The chain lubricant composition more preferably contains a fatty acid ester in a range of 1% by mass to 10% by mass.

チェーン用潤滑剤組成物には、必要に応じて、極圧剤、酸化防止剤、及び消泡剤を含有させることもできる。
＜チェーン用潤滑剤組成物中の硫黄、リン及びアロマ分＞
チェーン用潤滑剤組成物中に含まれる硫黄は、例えば、ＪＩＳ Ｋ２５４１に規定される方法で定量することができる。チェーン用潤滑剤組成物中に含まれるリンは、例えば、プラズマ発光分光分析で定量することができる。チェーン用潤滑剤組成物中に含まれるアロマ分は、例えば、ｎ−ｄ−Ｍ法の環分析で定量することができる。 If necessary, the chain lubricant composition may contain an extreme pressure agent, an antioxidant, and an antifoaming agent.
<Sulfur, phosphorus and aroma content in the lubricant composition for chains>
The sulfur contained in the chain lubricant composition can be quantified by, for example, a method defined in JIS K2541. The phosphorus contained in the chain lubricant composition can be quantified by, for example, plasma emission spectrometry. The aroma contained in the chain lubricant composition can be quantified, for example, by ring analysis of the ndM method.

＜チェーン用潤滑剤組成物の調製方法＞
チェーン用潤滑剤組成物は、基油、増粘剤及び防錆剤を周知の撹拌機で撹拌することで調製される。このとき、必要に応じて油性剤等を含有させる。チェーン用潤滑剤組成物の調製の際には、増粘剤の溶融温度以上に加熱されることが好ましい。 <Method for preparing lubricant composition for chain>
The chain lubricant composition is prepared by stirring the base oil, the thickener, and the rust inhibitor with a well-known stirrer. At this time, if necessary, an oily agent or the like is contained. In the preparation of the chain lubricant composition, it is preferably heated to a temperature higher than the melting temperature of the thickener.

＜チェーンの構成＞
図１に示すように、本実施形態のチェーン１１は、ローラチェーンであり、隣り合って配置される内リンク２１と外リンク３１が回動自在に連結された構成を有する。 <Chain structure>
As shown in FIG. 1, the chain 11 of this embodiment is a roller chain, and has a configuration in which an inner link 21 and an outer link 31 arranged adjacent to each other are rotatably connected.

内リンク２１は、対向して配置される２つの内プレート２２，２３と、内プレート２２，２３を支持する円筒状のブシュ２４，２５と、ブシュ２４，２５に回転自在に支持される円筒状のローラ２６，２７とを備えている。   The inner link 21 has two inner plates 22, 23 arranged opposite to each other, cylindrical bushes 24, 25 that support the inner plates 22, 23, and a cylindrical shape that is rotatably supported by the bushes 24, 25. The rollers 26 and 27 are provided.

内プレート２２，２３は、ブシュ２４，２５により連結されることで、互いに離間した状態で保持されている。
内プレート２２において、チェーン１１の連なる方向に沿って位置する一端部及び他端部は、貫通孔２２ａ，２２ｂを有している。内プレート２３においても、一端部及び他端部は、貫通孔２３ａ，２３ｂを有している。ブシュ２４の有する孔は、貫通孔２２ａ，２３ａを通じて内プレート２２，２３の対向する面とは反対側となる外面に開口している。ブシュ２５の有する孔についても、貫通孔２２ｂ，２３ｂを通じて内プレート２２，２３の対向する面とは反対側となる外面に開口している。 The inner plates 22 and 23 are held by the bushes 24 and 25 so as to be separated from each other.
In the inner plate 22, one end and the other end located along the direction in which the chain 11 is continuous have through holes 22 a and 22 b. Also in the inner plate 23, one end and the other end have through holes 23a and 23b. The holes of the bush 24 are opened through the through holes 22a and 23a on the outer surface opposite to the surfaces facing the inner plates 22 and 23. Also about the hole which the bush 25 has, it opens to the outer surface on the opposite side to the surface which the inner plates 22 and 23 oppose through the through-holes 22b and 23b.

外リンク３１は、対向して配置される２つの外プレート３２，３３と、外プレート３２，３３を連結する２つの円柱状のピン３４，３５を有している。外プレート３２，３３は、ピン３４，３５により連結されることで、互いに離間した状態で保持されている。   The outer link 31 has two outer plates 32 and 33 arranged opposite to each other, and two columnar pins 34 and 35 connecting the outer plates 32 and 33. The outer plates 32 and 33 are held apart from each other by being connected by pins 34 and 35.

ピン３４，３５は、内リンク２１の有するブシュ２５と、その内リンク２１に隣り合って配置される内リンク２１の有するブシュ２４とにそれぞれ挿入されている。これにより、隣り合う内リンク２１，２１は、外リンク３１を介して連結される。   The pins 34 and 35 are inserted into the bushing 25 of the inner link 21 and the bushing 24 of the inner link 21 arranged adjacent to the inner link 21, respectively. Thereby, the adjacent inner links 21 and 21 are connected via the outer link 31.

図２に示すように、ピン３４，３５の外周面とブシュ２４，２５の内周面との間には隙間が形成されている。チェーン１１は、例えば、鋼材から形成することができる。
＜チェーン用潤滑剤組成物の使用方法及び作用＞
チェーン用潤滑剤組成物のチェーン１１への適用は、例えば、チェーン用潤滑剤組成物にチェーン１１を浸漬することで、ピン３４，３５の外周面とブシュ２４，２５の内周面との間にチェーン用潤滑剤組成物を供給する。この浸漬において、チェーン用潤滑剤組成物は、増粘剤の融点以上の温度で維持されることが好ましい。チェーン用潤滑剤組成物は、例えば１００℃以上の温度に加熱されることで、ピン３４，３５の外周面とブシュ２４，２５の内周面との間に流入し易くなる。 As shown in FIG. 2, a gap is formed between the outer peripheral surface of the pins 34 and 35 and the inner peripheral surface of the bushes 24 and 25. The chain 11 can be formed from a steel material, for example.
<Use and action of lubricant composition for chain>
Application of the chain lubricant composition to the chain 11 is performed, for example, by immersing the chain 11 in the chain lubricant composition, so that the outer peripheral surface of the pins 34 and 35 and the inner peripheral surface of the bushes 24 and 25 are Supply the chain lubricant composition. In this immersion, the chain lubricant composition is preferably maintained at a temperature equal to or higher than the melting point of the thickener. The chain lubricant composition is likely to flow between the outer peripheral surfaces of the pins 34 and 35 and the inner peripheral surfaces of the bushes 24 and 25 by being heated to, for example, a temperature of 100 ° C. or higher.

上述した浸漬では、チェーン浸漬用の槽が用いられる。チェーン浸漬用の槽内では、チェーン用潤滑剤組成物が加熱された状態で維持される。この槽内では、チェーン１１が所定時間浸漬された後に、そのチェーン１１は槽内から搬出され、新たなチェーン１１が浸漬される。このようにチェーン浸漬用の槽では、チェーン用潤滑剤組成物のチェーン１１への適用、すなわち給油が繰り返される。なお、槽内には、チェーン１１に給油された組成物の量に応じて、新たなチェーン用潤滑剤組成物が補給される。   In the immersion described above, a tank for chain immersion is used. In the chain immersion tank, the chain lubricant composition is maintained in a heated state. In this tank, after the chain 11 is immersed for a predetermined time, the chain 11 is carried out of the tank and a new chain 11 is immersed. In this manner, in the chain immersion tank, application of the chain lubricant composition to the chain 11, that is, lubrication, is repeated. A new chain lubricant composition is replenished in the tank according to the amount of the composition supplied to the chain 11.

こうしたチェーン浸漬用の槽内では、チェーン用潤滑剤組成物が長時間加熱された状態で維持されることがある。このとき、本実施形態のチェーン用潤滑剤組成物は、黒色化の要因となる成分、すなわち硫黄、リン、及びアロマ分が実質的に含有されないか、又は、極めて低濃度で含有される構成であるため、槽内のチェーン用潤滑剤組成物の黒色化を抑制することが容易となる。このように構成されたチェーン用潤滑剤組成物は、加熱された状態においても、例えば、褐色又は淡褐色に維持され易くなる。   In such a chain immersion bath, the chain lubricant composition may be kept heated for a long time. At this time, the chain lubricant composition of the present embodiment is substantially free of components that cause blackening, that is, sulfur, phosphorus, and aroma, or is contained at a very low concentration. Therefore, it becomes easy to suppress blackening of the lubricant composition for chains in the tank. The chain lubricant composition thus configured is easily maintained, for example, brown or light brown even in a heated state.

チェーン１１は、例えば、物品の搬送又は動力の伝達に用いられる。チェーン１１は、例えば、複数のスプロケットに巻回されて用いられる。このとき、ピン３４，３５の外周面とブシュ２４，２５の内周面との間などがチェーン用潤滑剤組成物によって潤滑される。   The chain 11 is used for conveying articles or transmitting power, for example. For example, the chain 11 is wound around a plurality of sprockets. At this time, the space between the outer peripheral surface of the pins 34 and 35 and the inner peripheral surface of the bushes 24 and 25 is lubricated by the chain lubricant composition.

以上詳述した本実施形態によれば、次のような効果が発揮される。
（１）基油、増粘剤、及び防錆剤を含有するチェーン用潤滑剤組成物は、硫黄が１００質量ｐｐｍ以下であり、リンが１質量％以下であり、アロマ分が１質量％以下となるように構成されているため、硫黄、リン、及びアロマ分を要因としたチェーン用潤滑剤組成物の黒色化を抑制することができる。これにより、チェーン１１の黒色化を抑制することが容易となる。従って、外観の良好なチェーン１１が得られ易い。 According to the embodiment described in detail above, the following effects are exhibited.
(1) The chain lubricant composition containing a base oil, a thickener, and a rust inhibitor has a sulfur content of 100 mass ppm or less, a phosphorus content of 1 mass% or less, and an aroma content of 1 mass% or less. Therefore, the blackening of the lubricant composition for chains caused by sulfur, phosphorus, and aroma can be suppressed. Thereby, it becomes easy to suppress blackening of the chain 11. Therefore, it is easy to obtain the chain 11 having a good appearance.

（２）チェーン用潤滑剤組成物は、さらに油性剤を含有し、この油性剤は硫黄が１００質量ｐｐｍ以下であり、リンが１質量％以下であり、アロマ分が１質量％以下の化合物からなることが好ましい。この構成によれば、油性剤の含有によって、例えばチェーン摩耗寿命を改善する場合であっても、チェーン１１の黒色化を抑制することが容易となる。こうした油性剤としては、例えば、脂肪酸エステル及びラノリン脂肪酸アルコールエステルから選ばれる少なくとも一種を含むことが好適である。   (2) The lubricant composition for a chain further contains an oily agent. The oily agent is a compound having sulfur of 100 mass ppm or less, phosphorus of 1 mass% or less, and an aroma content of 1 mass% or less. It is preferable to become. According to this configuration, it becomes easy to suppress the blackening of the chain 11 even when, for example, the chain wear life is improved by containing the oily agent. As such an oily agent, for example, it is preferable to contain at least one selected from fatty acid esters and lanolin fatty acid alcohol esters.

（３）チェーン用潤滑剤組成物に含有させる防錆剤は、ソルビタン脂肪酸エステルを含むことが好ましい。防錆剤の中でも、ソルビタン脂肪酸エステルは、チェーン用潤滑剤組成物中の含有量を比較的低減しても、防錆効果が得られ易い。ソルビタン脂肪酸エステルは、硫黄、リン及びアロマ分を実質的に含有しないため、硫黄、リン、及びアロマ分を要因としたチェーン用潤滑剤組成物の黒色化を抑制することができる。   (3) It is preferable that the rust preventive agent contained in the chain lubricant composition contains a sorbitan fatty acid ester. Among the rust preventives, sorbitan fatty acid esters are likely to have a rust preventive effect even if the content in the chain lubricant composition is relatively reduced. Since sorbitan fatty acid ester does not substantially contain sulfur, phosphorus, and aroma, it can suppress blackening of the lubricant composition for chains caused by sulfur, phosphorus, and aroma.

（４）ソルビタン脂肪酸エステル又はラノリン脂肪酸アルコールエステルは、チェーン用潤滑剤組成物中に含まれる増粘剤の結晶化を妨げる働きを有する。このため、チェーン用潤滑剤組成物中で増粘剤の一部が固化したとしても、その状態が視認され難くなることで、チェーン１１の外観が改善される。   (4) The sorbitan fatty acid ester or lanolin fatty acid alcohol ester has a function of hindering the crystallization of the thickener contained in the chain lubricant composition. For this reason, even if a part of thickener solidifies in the lubricant composition for chains, the appearance of the chain 11 is improved by making the state difficult to be visually recognized.

（５）チェーン浸漬用の槽内では、チェーン用潤滑剤組成物が加熱された状態で維持されることがある。すなわち、チェーン浸漬用の槽内は、チェーン用潤滑剤組成物の黒色化が進行し易い環境下である。このようなチェーン浸漬用の槽内において黒色化を抑制することが容易となる点で、本実施形態のチェーン用潤滑剤組成物は特に有利である。例えば、チェーン浸漬用の槽内でチェーン用潤滑剤組成物が黒色化した場合、その組成物と新たに調製したチェーン用潤滑剤組成物とを交換する対策が考えられる。ところが、その交換の頻度が高い場合、交換作業の手間が増すとともに経済的にも不利となる。この点、上述したチェーン用潤滑剤組成物では、槽内のチェーン用潤滑剤組成物において、黒色化を要因とした交換の頻度を低減することができる。   (5) In the chain immersion tank, the chain lubricant composition may be maintained in a heated state. That is, the inside of the chain immersion bath is in an environment where the blackening of the chain lubricant composition is likely to proceed. The lubricant composition for a chain according to this embodiment is particularly advantageous in that it is easy to suppress blackening in such a chain immersion bath. For example, when the chain lubricant composition is blackened in a chain immersion bath, a countermeasure for exchanging the composition with a newly prepared chain lubricant composition can be considered. However, when the frequency of the replacement is high, the labor of the replacement work increases and it is economically disadvantageous. In this regard, in the above-described chain lubricant composition, the frequency of replacement due to blackening in the chain lubricant composition in the tank can be reduced.

（変更例）
なお、前記実施形態を次のように変更して構成することもできる。
・チェーン用潤滑剤組成物に配合する基油中には、硫黄が１００質量ｐｐｍを超えて含有されていてもよい。この場合であっても、例えば硫黄を実質的に含有しない増粘剤及び防錆剤を用いて、配合比を調整することで、チェーン用潤滑剤組成物中における硫黄の含有量を１００質量ｐｐｍ以下にすることもできる。すなわち、硫黄、リン、及びアロマ分の少なくとも一種の濃度が、上述したチェーン用潤滑剤組成物中の濃度を超える原料を用いることもできる。 (Example of change)
In addition, the said embodiment can also be changed and comprised as follows.
-The base oil mix | blended with the lubricant composition for chains may contain sulfur exceeding 100 mass ppm. Even in this case, for example, by using a thickener and a rust preventive agent substantially not containing sulfur, adjusting the blending ratio, the sulfur content in the chain lubricant composition is 100 mass ppm. It can also be: That is, a raw material in which at least one concentration of sulfur, phosphorus, and aroma components exceeds the concentration in the above-described chain lubricant composition can also be used.

・前記チェーン用潤滑剤組成物を適用するチェーンは、特に限定されず、前記チェーン用潤滑剤組成物は、例えば、ローラ２６，２７を省略したブシュチェーンに適用されてもよい。   The chain to which the chain lubricant composition is applied is not particularly limited, and the chain lubricant composition may be applied to, for example, a bush chain in which the rollers 26 and 27 are omitted.

・前記チェーン用潤滑剤組成物は、所謂プレ給油用としてチェーン１１に適用しているが、チェーン１１の使用途中に給油するメンテナンス用としてチェーン１１に適用することもできる。すなわち、チェーン浸漬用の槽内以外で前記チェーン用潤滑剤組成物を使用する場合であっても、例えばチェーン１１の使用時の発熱や使用環境による加熱に基づく黒色化を抑制することができる。   The chain lubricant composition is applied to the chain 11 for so-called pre-lubrication, but can also be applied to the chain 11 for maintenance that lubricates the chain 11 during use. That is, even when the chain lubricant composition is used outside the chain immersion bath, for example, blackening due to heat generation during use of the chain 11 or heating due to the use environment can be suppressed.

次に、試験例を説明する。
（基油の試験例）
表１に示される基油について、１５０℃で維持する黒色化試験を行った。黒色化について以下の基準で評価した。 Next, test examples will be described.
(Base oil test example)
About the base oil shown in Table 1, the blackening test maintained at 150 degreeC was done. Blackening was evaluated according to the following criteria.

２０００時間経過しても黒色化しない：最適（◎）
１０００時間を超え、２０００時間以内に黒色化したもの：好適（○）
１００時間を超え１０００時間以内に黒色化したもの：やや不適（△）
１００時間以内に黒色化したもの：不適（×）
黒色化試験の評価結果を表１に示す。 No blackening after 2000 hours: Optimal (◎)
Blackened for more than 1000 hours and within 2000 hours: preferred (◯)
Blackened within 1000 hours over 100 hours: Slightly unsuitable (△)
Blackened within 100 hours: unsuitable (x)
The evaluation results of the blackening test are shown in Table 1.

高精製鉱油は、リン及びアロマ分を実質的に含有しない。高精製鉱油中の硫黄の含有量は、数１０質量ｐｐｍ以下である。合成炭化水素は、硫黄、リン、及びアロマ分のいずれも実質的に含有しない。 Highly refined mineral oil is substantially free of phosphorus and aroma. The content of sulfur in the highly refined mineral oil is several tens of mass ppm or less. Synthetic hydrocarbons are substantially free of sulfur, phosphorus, and aroma.

（増粘剤の試験例）
表２に示される増粘剤について上記の基油と同様に黒色化試験、及びその評価を行った。黒色化試験の評価結果を表２に示す。 (Thickener test example)
About the thickener shown in Table 2, the blackening test and its evaluation were performed similarly to the above base oil. Table 2 shows the evaluation results of the blackening test.

（防錆剤の試験例）
表３に示される防錆剤について上記の基油と同様に黒色化試験、及びその評価を行った。黒色化試験の評価結果を表３に示す。 (Test example of rust inhibitor)
About the rust preventive agent shown in Table 3, the blackening test and the evaluation were performed similarly to the above base oil. The evaluation results of the blackening test are shown in Table 3.

（その他の成分の試験例）
表４に示される油性剤及び極圧剤について上記の基油と同様に黒色化試験、及びその評価を行った。黒色化試験の評価結果を表４に示す。 (Test example of other ingredients)
About the oiliness agent and extreme pressure agent which are shown in Table 4, the blackening test and its evaluation were performed similarly to said base oil. Table 4 shows the evaluation results of the blackening test.

次に、実施例を説明する。 Next, examples will be described.

（実施例１及び２）
表５に示される各成分を混合することで、各実施例のチェーン用潤滑剤組成物を調製した。表５中の基油は、高精製鉱油（商品名：サンピュアＰ１００、日本サン石油株式会社製）であり、増粘剤は、ポリエチレンワックス（三井ハイワックス２００Ｐ、三井化学株式会社製）である。表５中の防錆剤は、ソルビタン脂肪酸エステルであり、油性剤は脂肪酸エステルである。各実施例のチェーン用潤滑剤組成物は、硫黄が１００質量ｐｐｍ以下、リンが１質量％以下、アロマ分が１質量％以下となるように構成されている。 (Examples 1 and 2)
Each component shown in Table 5 was mixed to prepare a chain lubricant composition of each example. The base oil in Table 5 is a highly refined mineral oil (trade name: Sunpure P100, manufactured by Nippon Sun Oil Co., Ltd.), and the thickener is polyethylene wax (Mitsui High Wax 200P, manufactured by Mitsui Chemicals, Inc.). The rust preventive agent in Table 5 is sorbitan fatty acid ester, and the oily agent is fatty acid ester. The lubricant composition for a chain of each example is configured such that sulfur is 100 mass ppm or less, phosphorus is 1 mass% or less, and the aroma content is 1 mass% or less.

（比較例１及び２）
表５に示される各成分を混合することで、各比較例のチェーン用潤滑剤組成物を調製した。表５中の極圧剤として、比較例１では硫化オレフィンを用い、比較例２ではジアルキルジチオフォスフェートを用いた。各比較例のチェーン用潤滑剤組成物に含まれる硫黄の含有量は、
１００質量ｐｐｍを超えている。 (Comparative Examples 1 and 2)
Each component shown in Table 5 was mixed to prepare a chain lubricant composition of each comparative example. As extreme pressure agents in Table 5, Comparative Example 1 used sulfurized olefins and Comparative Example 2 used dialkyldithiophosphates. The sulfur content contained in the chain lubricant composition of each comparative example is:
It exceeds 100 mass ppm.

得られた各例のチェーン用潤滑剤組成物をそれぞれチェーン浸漬用の槽に供給し、その組成物を１５０℃で１０００時間維持した。その結果、各実施例のチェーン用潤滑剤組成物では黒色化は確認されなかった。各比較例のチェーン用潤滑剤組成物では１００時間以内に黒色化が確認された。 The obtained chain lubricant composition of each example was supplied to a chain immersion tank, and the composition was maintained at 150 ° C. for 1000 hours. As a result, blackening was not confirmed in the lubricant composition for chains of each Example. Blackening was confirmed within 100 hours in the chain lubricant compositions of the comparative examples.

次に、チェーン浸漬用の槽内で図１及び図２に示されるチェーン１１を各例のチェーン用潤滑剤組成物に浸漬し、１０分経過後、槽内からチェーン１１を取り出した。各実施例のチェーン用潤滑剤組成物が適用されたチェーン１１では、黒色化が抑制された良好な外観を有していた。各比較例のチェーン用潤滑剤組成物が適用されたチェーン１１では、黒色化が抑制されず、外観が不良であった。   Next, the chain 11 shown in FIGS. 1 and 2 was immersed in the chain lubricant composition of each example in a chain immersion tank, and after 10 minutes, the chain 11 was taken out from the tank. The chain 11 to which the chain lubricant composition of each example was applied had a good appearance with suppressed blackening. In the chain 11 to which the chain lubricant composition of each comparative example was applied, blackening was not suppressed and the appearance was poor.

１１…チェーン、２１…内リンク、２２，２３…内プレート、２２ａ，２２ｂ，２３ａ，２３ｂ…貫通孔、２４，２５…ブシュ、２６，２７…ローラ、３１…外リンク、３２，３３…外プレート、３４，３５…ピン。   DESCRIPTION OF SYMBOLS 11 ... Chain, 21 ... Inner link, 22, 23 ... Inner plate, 22a, 22b, 23a, 23b ... Through-hole, 24, 25 ... Bush, 26, 27 ... Roller, 31 ... Outer link, 32, 33 ... Outer plate , 34, 35 ... pins.

Claims (5)

基油、増粘剤、及び防錆剤を含有するチェーン用潤滑剤組成物であって、
前記組成物は、硫黄が１００質量ｐｐｍ以下、リンが１質量％以下、アロマ分が１質量％以下となるように構成されていることを特徴とするチェーン用潤滑剤組成物。 A lubricant composition for a chain containing a base oil, a thickener, and a rust inhibitor,
The said composition is comprised so that sulfur may be 100 mass ppm or less, phosphorus is 1 mass% or less, and an aroma content is 1 mass% or less, The chain lubricant composition characterized by the above-mentioned. さらに、油性剤を含有し、前記油性剤は、硫黄が１００質量ｐｐｍ以下、リンが１質量％以下、アロマ分が１質量％以下の化合物からなる請求項１に記載のチェーン用潤滑剤組成物。   2. The chain lubricant composition according to claim 1, further comprising an oily agent, wherein the oily agent comprises a compound having a sulfur content of 100 mass ppm or less, a phosphorus content of 1 mass% or less, and an aroma content of 1 mass% or less. . 前記油性剤は、脂肪酸エステル及びラノリン脂肪酸アルコールエステルから選ばれる少なくとも一種を含む請求項２に記載のチェーン用潤滑剤組成物。   The lubricant composition for a chain according to claim 2, wherein the oily agent contains at least one selected from fatty acid esters and lanolin fatty acid alcohol esters. チェーン浸漬用の槽内で用いられる請求項１から請求項３のいずれか一項に記載のチェーン用潤滑剤組成物。   The lubricant composition for a chain according to any one of claims 1 to 3, which is used in a chain immersion bath. 請求項１から請求項４のいずれか一項に記載のチェーン用潤滑剤組成物を適用したことを特徴とするチェーン。   A chain, wherein the chain lubricant composition according to any one of claims 1 to 4 is applied.
JP2013142096A 2013-07-05 2013-07-05 Lubricant composition for chain and chain Active JP5808775B2 (en)