JP2014051326A - Method of manufacturing cap - Google Patents
Method of manufacturing cap Download PDFInfo
- Publication number
- JP2014051326A JP2014051326A JP2013233628A JP2013233628A JP2014051326A JP 2014051326 A JP2014051326 A JP 2014051326A JP 2013233628 A JP2013233628 A JP 2013233628A JP 2013233628 A JP2013233628 A JP 2013233628A JP 2014051326 A JP2014051326 A JP 2014051326A
- Authority
- JP
- Japan
- Prior art keywords
- liner
- cap
- tip
- metal cap
- top plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、飲料用等のボトルにおける口部を密栓する金属キャップ及びこれを被着したキャップ付きボトルに関する。 The present invention relates to a metal cap for sealing a mouth of a bottle for beverages and the like, and a bottle with a cap to which the cap is attached.
従来、スチールやアルミニウム合金等の金属製ボトルにおける口金部に被着されるキャップにおいて、キャップが回転操作されて開栓される際に、内圧を開放してボトル本体内のガスを外部に放出するためのベントホール（ナールスリットまたはベントスリットとも称される）がキャップ上端部近傍に形成されたものが知られている。
例えば、特許文献１では、天面壁近傍のスカート壁内面に複数の突起を突設したキャップ本体と、上記突起に周縁の複数箇所を係止されて天面壁内側に非接合状態で配置されたライナーと、を備え、キャップ本体の周囲に切り込みを入れて切り込んだ部分をキャップ内側に押し込んで折曲させて上記突起を形成したキャップが記載されている。このキャップでは、上記突起を形成した切り込みがベントホールとして機能する。
Conventionally, when a cap is attached to a cap portion of a metal bottle such as steel or aluminum alloy, when the cap is rotated and opened, the internal pressure is released and the gas in the bottle body is released to the outside. A vent hole (also referred to as a knurl slit or a vent slit) is formed near the upper end of the cap.
For example, in Patent Document 1, a cap main body in which a plurality of protrusions are provided on the inner surface of a skirt wall near the top wall, and a liner disposed in a non-joined state on the inner side of the top wall with a plurality of peripheral edges locked to the protrusions. And a cap in which a notch is formed around the cap body and the cut portion is pushed into the cap and bent to form the protrusion. In this cap, the notch formed with the protrusion functions as a vent hole.
また、特許文献２には、天板部、および該天板部の周縁部から略垂下してなる周壁部を備えるキャップ本体と、該キャップ本体の内側に天板部の内面を覆うように配設されたライナーと、を備え、ボトル缶の口金部に螺着されるキャップであって、周壁部の上部に、天板部の周縁部から連続してキャップ本体の径方向内方へ向って延びるライナー支持部が周方向に間隔をあけて複数形成され、該ライナー支持部の軸方向上端部にライナーが配置されているキャップが記載されている。このキャップでは、周壁部の周方向に複数形成されたナール部の凹部の下端部にベントホールとしてスリットを形成し、凹部をライナー支持部としている。また、このキャップでは、予めライナーを天板部内面に配置した後に、ベントホールとなるスリットおよびライナー支持部を形成している。 Patent Document 2 discloses a cap body having a top plate portion and a peripheral wall portion substantially hanging from the peripheral edge portion of the top plate portion, and an inner surface of the cap body so as to cover the inner surface of the top plate portion. A cap that is screwed to the cap portion of the bottle can, and is continuously inward from the peripheral portion of the top plate portion and radially inward of the cap body. There is described a cap in which a plurality of extending liner support portions are formed at intervals in the circumferential direction, and a liner is disposed at an upper end portion in the axial direction of the liner support portion. In this cap, a slit is formed as a vent hole in the lower end portion of the recess of the knurled portion formed in the circumferential direction of the peripheral wall portion, and the recess serves as a liner support portion. Further, in this cap, after a liner is disposed in advance on the inner surface of the top plate portion, a slit that becomes a vent hole and a liner support portion are formed.
このように上記従来のキャップでは、ベントホールとして形成したスリットの突起部を内側に押し込んで突起またはライナー支持部とし、これらを、ライナーを係止して脱落を防止するフックとしている。 As described above, in the conventional cap, the protrusions of the slits formed as vent holes are pushed inward to form protrusions or liner support parts, which are hooks that lock the liner and prevent it from falling off.
上記従来の技術には、以下の課題が残されている。
すなわち、ボトル口部に密着したライナーを開栓の際にボトル口部から剥がしきれず、密着されたままライナーがキャップに対して下方に引っ張られたときに、上記特許文献１の技術のように、ベントホールの下部突起部でライナーを係止する場合、破断部である下部突起部の先端にライナーの外周縁が引っ掛かってライナー全体が撓み、ライナーの引っ掛かっていない外周縁から外れてライナーが脱落してしまうおそれがあった。また、脱落しない場合でも、ライナーの外周部がベントホールの下部突起部のエッジに擦れて開栓時にスムーズな官能が得られず、ときにはライナーが僅かに削れる場合があった。
さらに、上記特許文献２の技術では、ベントホールとなるスリットおよび凹部を形成した後にライナーを挿入しようとすると、破断部であるスリットの上部突起部の先端にライナーが引っ掛かってスムーズに挿入できなかったり、擦れによってライナーが傷ついたりするおそれがあった。このため、予めライナーを天板部内面に配置した後に、ベントホールとなるスリットおよび凹部を形成する必要があり、キャップの加工工程上、手間であった。
The following problems remain in the conventional technology.
That is, when the liner that is in close contact with the bottle mouth portion cannot be peeled off from the bottle mouth portion when opening, the liner is pulled downward with respect to the cap while being in close contact, as in the technique of Patent Document 1 above. When the liner is locked by the lower protrusion of the vent hole, the outer peripheral edge of the liner is caught at the tip of the lower protrusion, which is a fractured part, and the entire liner is bent, and the liner falls off from the outer peripheral edge where the liner is not caught. There was a risk of doing so. Even when the liner does not fall off, the outer periphery of the liner rubs against the edge of the lower protrusion of the vent hole, and a smooth sensation cannot be obtained when the plug is opened, and sometimes the liner is slightly scraped.
Further, in the technique of Patent Document 2, when a liner is inserted after forming slits and recesses to be vent holes, the liner is caught at the tip of the upper protrusion of the slit, which is a fracture portion, and the insertion cannot be performed smoothly. The liner could be damaged by rubbing. For this reason, it is necessary to form slits and recesses to be vent holes after arranging the liner on the inner surface of the top plate in advance, which is troublesome in the cap processing process.
本発明は、前述の課題に鑑みてなされたもので、開栓時にライナーの脱落を防止すると共に、スムーズな開栓およびライナーの挿入が可能な金属キャップおよびキャップ付きボトルを提供することを目的とする。 The present invention has been made in view of the above-described problems, and an object thereof is to provide a metal cap and a bottle with a cap that can prevent the liner from falling off during opening and that allows smooth opening and insertion of the liner. To do.
本発明は、前記課題を解決するために以下の構成を採用した。すなわち、本発明の金属キャップは、上方に配された天板部と、該天板部の周縁から略垂下されてなる円筒部とを備え、前記天板部の内面にライナーが非接着状態で挿入された後にボトルの口部を密栓する金属キャップであって、前記円筒部が、前記天板部近傍であって周方向にスリット状に開口形成され開栓時に内圧を開放するベントホールと、該ベントホールの上部開口端部および下部開口端部を前記円筒部の半径方向内方に向けて曲げて形成した上部突起部および下部突起部と、を有し、前記上部突起部の先端が、挿入された際の前記ライナーの外周縁よりも半径方向内方に位置されていると共に、前記下部突起部の先端と半径方向で同位置または該先端よりも半径方向外方に位置していることを特徴とする。 The present invention employs the following configuration in order to solve the above problems. That is, the metal cap according to the present invention includes a top plate portion disposed above and a cylindrical portion substantially suspended from the periphery of the top plate portion, and a liner is not bonded to the inner surface of the top plate portion. A metal cap that seals the mouth of the bottle after being inserted, wherein the cylindrical portion is formed in a slit shape in the vicinity of the top plate portion in the circumferential direction, and a vent hole that opens the internal pressure at the time of opening, An upper protrusion and a lower protrusion formed by bending the upper opening end and the lower opening end of the vent hole toward the radially inner side of the cylindrical portion, and the tip of the upper protrusion is It is located radially inward from the outer peripheral edge of the liner when inserted, and is located at the same position in the radial direction as the tip of the lower protrusion or radially outward from the tip. It is characterized by.
この金属キャップでは、ベントホールの上部突起部の先端が、挿入された際のライナーの外周縁よりも半径方向内方に位置されていると共に、下部突起部の先端と半径方向で同位置または該先端よりも半径方向外方に位置しているので、挿入されたライナーの外周部が開栓時に上部突起部の上面に係止されるが、破断部である先端にライナーが引っ掛からず、撓みによる脱落を防止することができる。また、ベントホールの上部突起部の先端が、下部突起部よりも半径方向外方に位置しているので、ライナーを挿入する際に、下部突起部がガイドになると共にライナーと上部突起部の先端との接触を防いで上部突起部の先端にライナーが引っ掛かることを抑制することができる。 In this metal cap, the tip of the upper protrusion of the vent hole is positioned radially inward from the outer peripheral edge of the liner when inserted, and is the same position or the same as the tip of the lower protrusion in the radial direction. Since it is located radially outward from the tip, the outer periphery of the inserted liner is locked to the upper surface of the upper protrusion when it is opened, but the liner does not catch on the tip, which is a break, and is bent. Dropout can be prevented. In addition, since the tip of the upper projection of the vent hole is located radially outward from the lower projection, when inserting the liner, the lower projection serves as a guide and the tip of the liner and upper projection It is possible to prevent the liner from being caught on the tip of the upper projection portion by preventing contact with the upper projection portion.
また、本発明の金属キャップは、前記ライナーが、前記天板部の内面側に配された摺動層と、前記挿入後にモールド成形によって前記摺動層に積層され前記摺動層よりも柔軟で外径の小さい密封層と、を備え、前記上部突起部の先端が、挿入された際の前記ライナーの前記摺動層の外周縁よりも半径方向内方に位置し、前記下部突起部の先端が、前記密封層の外周縁よりも半径方向外方に位置していることを特徴とする。
すなわち、この金属キャップでは、上部突起部の先端が、挿入された際のライナーの摺動層の外周縁よりも半径方向内方に位置し、下部突起部の先端が、密封層の外周縁よりも半径方向外方に位置しているので、挿入時にライナーの摺動層とベントホールの上部突起部の先端との接触を下部突起部によって防ぐことができると共に、挿入後の密封層のモールド成形時に内部に挿入される金型を、下部突起部によってセンタリングして位置決めすることができる。
In the metal cap of the present invention, the liner is laminated to the sliding layer by molding after the sliding layer disposed on the inner surface side of the top plate portion, and is more flexible than the sliding layer. A sealing layer having a small outer diameter, and the tip of the upper projection is positioned radially inward from the outer periphery of the sliding layer of the liner when inserted, and the tip of the lower projection Is located radially outward from the outer peripheral edge of the sealing layer.
That is, in this metal cap, the tip of the upper projection is positioned radially inward from the outer periphery of the sliding layer of the liner when inserted, and the tip of the lower projection is from the outer periphery of the sealing layer. Is also located radially outward, so that contact between the sliding layer of the liner and the tip of the upper protrusion of the vent hole can be prevented by the lower protrusion during insertion, and the sealing layer is molded after insertion. Sometimes the mold inserted inside can be centered and positioned by the lower projection.
また、本発明の金属キャップは、前記上部突起部の先端部が、さらに下方に折り曲げられて先端面が下方に向けられていることを特徴とする。
すなわち、この金属キャップでは、上部突起部の先端部が、さらに下方に折り曲げられて先端が下方に向けられているので、挿入時に弾性によって下部突起部を越えたライナーの外周縁が上部突起部の先端に接触し難くなり、引っ掛かることをさらに抑制することができる。
Further, the metal cap of the present invention is characterized in that a tip portion of the upper protrusion is further bent downward and a tip surface is directed downward.
That is, in this metal cap, since the tip of the upper protrusion is further bent downward and the tip is directed downward, the outer peripheral edge of the liner that exceeds the lower protrusion by elasticity during insertion is the upper protrusion. It becomes difficult to come into contact with the tip and can be further suppressed from being caught.
本発明のキャップ付きボトルは、ボトル本体と、該ボトル本体の口部に被着される金属キャップと、を備え、前記金属キャップが、上記本発明の金属キャップであることを特徴とする。
すなわち、このキャップ付きボトルでは、金属キャップが、上記本発明の金属キャップであるので、開栓時においてライナーの脱落を防止することができると共にスムーズなグリップ官能を得ることができる。
The bottle with a cap according to the present invention includes a bottle main body and a metal cap that is attached to the mouth of the bottle main body, and the metal cap is the metal cap according to the present invention.
That is, in this bottle with a cap, since the metal cap is the metal cap of the present invention, it is possible to prevent the liner from falling off when opening the plug and to obtain a smooth gripping sensation.
本発明によれば、以下の効果を奏する。
すなわち、本発明に係る金属キャップによれば、ベントホールの上部突起部の先端が、挿入された際のライナーの外周縁よりも半径方向内方に位置されていると共に、下部突起部の先端と半径方向で同位置または該先端よりも半径方向外方に位置しているので、開栓時にライナーの脱落を防止することができると共に、スムーズな開栓およびライナーの挿入が可能になる。
したがって、本発明の金属キャップを採用したキャップ付きボトルでは、開栓時においてライナーの脱落を防止することができると共にスムーズなグリップ官能を得ることができる。
The present invention has the following effects.
That is, according to the metal cap according to the present invention, the tip of the upper projection of the vent hole is positioned radially inward from the outer peripheral edge of the liner when inserted, and the tip of the lower projection Since it is located at the same position in the radial direction or radially outward from the tip, it is possible to prevent the liner from dropping off at the time of opening, and to smoothly open and insert the liner.
Therefore, in the bottle with a cap that employs the metal cap of the present invention, it is possible to prevent the liner from falling off when opening, and to obtain a smooth gripping sensation.
以下、本発明に係る金属キャップ及びキャップ付きボトルの一実施形態を、図１から図５を参照しながら説明する。 Hereinafter, an embodiment of a metal cap and a bottle with a cap according to the present invention will be described with reference to FIGS. 1 to 5.
本実施形態の金属キャップ１は、図１及び図２に示すように、例えば直径３８ｍｍ口径のアルミニウム又はアルミニウム合金製（金属製）ボトル本体の口金部（口部）に被着されて密栓するピルファープルーフキャップ（以下、ＰＰキャップとも称す）となるものである。この金属キャップ１は、アルミニウム又はアルミニウム合金板材をカップ状に成形したもので、上方に配された天板部２と、該天板部２の周縁から略垂下されてなる円筒部３と、を備えている。 As shown in FIGS. 1 and 2, the metal cap 1 of the present embodiment is a pill that is attached to a base part (mouth part) of a bottle body made of aluminum or aluminum alloy (metal) having a diameter of 38 mm, for example, and tightly plugs. It becomes a proof cap (hereinafter also referred to as PP cap). This metal cap 1 is formed by molding an aluminum or aluminum alloy plate material into a cup shape, and includes a top plate portion 2 disposed above and a cylindrical portion 3 substantially suspended from the periphery of the top plate portion 2. I have.
この金属キャップ１は、天板部２の内面にライナー９が非接着状態で挿入された後にボトル本体の口部を密栓するものである。
上記円筒部３は、周方向に断続的に形成されたスリット４を介して上下に分割された筒上部５と筒下部６とを有し、隣接するスリット４間に形成される複数のブリッジ４ａによって筒上部５と筒下部６とを連結した形状としたものである。
The metal cap 1 seals the mouth of the bottle body after the liner 9 is inserted into the inner surface of the top plate 2 in a non-adhered state.
The cylindrical portion 3 has a cylindrical upper portion 5 and a cylindrical lower portion 6 that are divided vertically through slits 4 that are intermittently formed in the circumferential direction, and a plurality of bridges 4 a formed between adjacent slits 4. Thus, the cylinder upper part 5 and the cylinder lower part 6 are connected to each other.
また、上記円筒部３は、天板部２近傍であって周方向に複数並べて形成されたナール凹部７と、ナール凹部７に周方向にスリット状に開口形成され開栓時に内圧を開放するベントホールであるナールスリット８と、該ナールスリット８の上部開口端部および下部開口端部を円筒部３の半径方向内方に向けて曲げて形成した上部突起部８ａおよび下部突起部８ｂと、を有している。
上記ナール凹部７は、開栓時にＰＰキャップと把持する指との間の摩擦抵抗を増大させるものであり、これにより手を滑らせることなく容易に開栓可能とするものである。
The cylindrical portion 3 includes a knurled recess 7 formed in the vicinity of the top plate 2 and arranged in the circumferential direction, and a vent that opens to the knurled recess 7 in a slit shape in the circumferential direction and releases the internal pressure when the cap is opened. A knurl slit 8 that is a hole, and an upper protrusion 8a and a lower protrusion 8b that are formed by bending the upper opening end and the lower opening end of the knurl slit 8 inward in the radial direction of the cylindrical portion 3. Have.
The knurled recess 7 increases the frictional resistance between the PP cap and the finger to be gripped when opening, thereby enabling easy opening without sliding the hand.
上記ナールスリット８は、ナール凹部７の上端部にナール凹部７の幅と同じ長さに周方向にせん断されて形成されている。このナールスリット８は、ボトル本体に装着されたキャップ１（ＰＰキャップ）がブリッジ４ａを破断しつつ上方に回転操作された際、ボトル本体内のガスを外部に放出するためのベントホールである。 The knurl slit 8 is formed in the upper end of the knurl recess 7 by being sheared in the circumferential direction to the same length as the width of the knurl recess 7. The knurl slit 8 is a vent hole for releasing the gas in the bottle body to the outside when the cap 1 (PP cap) attached to the bottle body is rotated upward while breaking the bridge 4a.
また、ナールスリット８の上部突起部８ａの先端は、挿入された際のライナー９の外周縁よりも半径方向内方に位置されていると共に、下部突起部８ｂの先端と半径方向で同位置または該先端よりも半径方向外方に位置している。
さらに、上部突起部８ａの先端部は、さらに下方に折り曲げられて先端面が下方に向けられている。
The tip of the upper protrusion 8a of the knurl slit 8 is located radially inward from the outer peripheral edge of the liner 9 when inserted, and is the same position as the tip of the lower protrusion 8b in the radial direction or It is located radially outward from the tip.
Further, the tip of the upper protrusion 8a is further bent downward so that the tip surface is directed downward.
また、ナールスリット８の上部突起部８ａは、図２の（ｂ）に示すように、上部の外側凸部となる屈曲部を起点にして円筒部３の内方に向けて所定の角度θ（円筒部３の軸線に平行な仮想線３ａに対する角度）で屈曲されている。この角度θとしては、２８〜８２°に範囲内に設定することが好ましい。 Further, as shown in FIG. 2B, the upper protrusion 8a of the knurl slit 8 has a predetermined angle θ (inward) toward the inside of the cylindrical portion 3 with a bent portion serving as an upper outer convex portion as a starting point. It is bent at an angle) to an imaginary line 3a parallel to the axis of the cylindrical portion 3. This angle θ is preferably set within a range of 28 to 82 °.
この金属キャップ１に挿入されるライナー９は、天板部２の内面側に配された摺動層９ａと、挿入後にモールド成形によって摺動層９ａに直接またはバリアー層等の中間層を介して積層され摺動層９ａよりも柔軟で外径の小さい密封層９ｂと、を備えている。上記摺動層９ａは、ポリプロピレン等で形成された円盤状の硬質シートで構成され、上記密封層９ｂは、硬質シート上にモールド成形で積層状態にエラストマー樹脂等で形成される。
また、ナールスリット８の上部突起部８ａの先端は、挿入された際のライナー９の摺動層９ａの外周縁よりも半径方向内方に位置し、下部突起部８ｂの先端は、密封層９ｂの外周縁よりも半径方向外方に位置している。
The liner 9 to be inserted into the metal cap 1 includes a sliding layer 9a disposed on the inner surface side of the top plate portion 2, and after insertion, directly on the sliding layer 9a by molding or through an intermediate layer such as a barrier layer. A sealing layer 9b that is laminated and is softer than the sliding layer 9a and has a smaller outer diameter. The sliding layer 9a is formed of a disk-shaped hard sheet formed of polypropylene or the like, and the sealing layer 9b is formed of an elastomer resin or the like in a laminated state by molding on the hard sheet.
The tip of the upper protrusion 8a of the knurl slit 8 is positioned radially inward from the outer peripheral edge of the sliding layer 9a of the liner 9 when inserted, and the tip of the lower protrusion 8b is the sealing layer 9b. It is located radially outward from the outer peripheral edge.
このライナー９は、図２の（ｂ）に示すように、金属キャップ１内に挿入して硬質シートの摺動層９ａを天板部２の内面に接して配置した状態で、モールド成形用の金型Ｍを金属キャップ１内に挿入し、該金型Ｍを用いてエラストマー樹脂等を樹脂成形することで、密封層９ｂを形成する。このモールド成形用の金型Ｍを挿入する際に、ナールスリット８の下部突起部８ｂが金型Ｍのガイドの役割を果たし、金型Ｍのセンタリング（位置決め）が行われる。 As shown in FIG. 2 (b), the liner 9 is inserted into the metal cap 1 and is placed in contact with the inner surface of the top plate portion 2 with a hard sheet sliding layer 9a disposed therein. The mold M is inserted into the metal cap 1, and an elastomer resin or the like is molded using the mold M to form the sealing layer 9b. When the mold M for molding is inserted, the lower protrusion 8b of the knurl slit 8 serves as a guide for the mold M, and the centering (positioning) of the mold M is performed.
なお、この密封層９ｂは、ボトルの口部に密着する外周部が中心部よりも厚く形成されている。
また、上部突起部８ａに接触するライナー９の厚みは、０．１〜２．０ｍｍの範囲内に設定することが好ましい。また、ライナー９の外径（摺動層９ａの外径）は、金属キャップ１の寸法に応じて決定されるが、直径１５〜６５ｍｍの範囲内に設定される。
In addition, this sealing layer 9b is formed so that the outer peripheral part closely_contact | adhering to the opening part of a bottle is thicker than a center part.
Moreover, it is preferable to set the thickness of the liner 9 which contacts the upper protrusion part 8a in the range of 0.1-2.0 mm. Moreover, although the outer diameter of the liner 9 (the outer diameter of the sliding layer 9a) is determined according to the dimension of the metal cap 1, it is set within a range of 15 to 65 mm in diameter.
次に、口金部に上記金属キャップ１を被着させてなるＰＰキャップ及び該ＰＰキャップにより密閉されたキャップ付きボトル１００を、図３を参照しながら説明する。 Next, a PP cap in which the metal cap 1 is attached to the base and a bottle 100 with a cap sealed by the PP cap will be described with reference to FIG.
本実施形態のキャップ付きボトル１００は、図３に示すように、飲料等の液体が充填されアルミニウム又はアルミニウム合金からなるボトル本体１１と、該ボトル本体１１の口金部１２に被着されたＰＰキャップ１０（金属キャップ１）と、を備えている。このＰＰキャップ１０は、天板部２が肩絞り加工されている。また、ＰＰキャップ１０は、ねじ山１３の外形に沿うねじ部１４を筒上部５に形成すると共に、膨出部１５の下部に沿うピルファープルーフ部１６を筒下部６に形成することにより、ボトル本体１１の口金部１２に被着したものである。 As shown in FIG. 3, a bottle 100 with a cap according to the present embodiment includes a bottle main body 11 made of aluminum or an aluminum alloy and filled with a liquid such as a beverage, and a PP cap attached to a base portion 12 of the bottle main body 11. 10 (metal cap 1). As for this PP cap 10, the top-plate part 2 is shoulder-drawn. In addition, the PP cap 10 forms a screw portion 14 along the outer shape of the thread 13 on the upper portion 5 of the cylinder, and forms a pill fur proof portion 16 along the lower portion of the bulging portion 15 on the lower portion 6 of the bottle. It is attached to the base part 12 of the main body 11.
このＰＰキャップ１０のキャッピング加工は、プレッシャーブロック、ネジローラー、スカートローラー等からなるキャッピング装置を用いて行われる。
すなわち、口金部１２に被せた金属キャップ１の天板部２を、プレッシャーブロックでボトル底部の方向に押圧し、この状態でプレッシャーブロックによる絞り加工により、金属キャップ１の肩部に段差部を形成する。
The capping process of the PP cap 10 is performed using a capping device including a pressure block, a screw roller, a skirt roller, and the like.
That is, the top plate portion 2 of the metal cap 1 placed on the base portion 12 is pressed toward the bottom of the bottle with a pressure block, and in this state, a stepped portion is formed on the shoulder portion of the metal cap 1 by drawing with the pressure block. To do.
さらに、この状態でネジローラーによりネジ部１４を形成し、スカートローラーで口金部１２のカブラ部である膨出部１５にスカート部であるピルファープルーフ部１６を巻きつけることで、キャッピング加工が行われる。すなわち、金属キャップ１が被着されるボトル本体１１の口金部１２には、ねじ山１３及び膨出部１５が形成されており、ここに被せられた金属キャップ１はねじ山１３、膨出部１５等の形状に沿うように塑性変形される。
これによって、金属キャップ１がＰＰキャップ１０として口金部１２に被着され、ボトル本体１１を密封状態とすることで、ボトル１００が得られる。
Further, in this state, the screw portion 14 is formed by the screw roller, and the pill roller proof portion 16 that is the skirt portion is wound around the bulging portion 15 that is the turntable portion of the base portion 12 by the skirt roller, so that the capping process is performed. Is called. That is, a screw thread 13 and a bulging part 15 are formed on the cap part 12 of the bottle main body 11 to which the metal cap 1 is attached, and the metal cap 1 covered here has the screw thread 13 and the bulging part. It is plastically deformed along the shape of 15 etc.
As a result, the metal cap 1 is attached to the base portion 12 as the PP cap 10 and the bottle body 11 is sealed, whereby the bottle 100 is obtained.
なお、ＰＰキャップ１０の天板部２の内側には、上述したようにライナー９が挿入配置されており、該ライナー９によってボトル本体１１の開口部がシールされている。
また、キャッピング後におけるライナー９の摺動層９ａの外周縁からナールスリット８の上部突起部８ａの先端までの半径方向におけるオーバーラップ寸法ａは、０．１０〜１．５２ｍｍの範囲内に設定することが好ましい。
The liner 9 is inserted and arranged inside the top plate portion 2 of the PP cap 10 as described above, and the opening of the bottle body 11 is sealed by the liner 9.
Further, the overlap dimension a in the radial direction from the outer peripheral edge of the sliding layer 9a of the liner 9 to the tip of the upper protrusion 8a of the knurl slit 8 after capping is set within a range of 0.10 to 1.52 mm. It is preferable.
以上、説明したように本実施形態の金属キャップ１では、ベントホールであるナールスリット８の上部突起部８ａの先端が、挿入された際のライナー９の外周縁よりも半径方向内方に位置されていると共に、下部突起部８ｂの先端と半径方向で同位置または該先端よりも半径方向外方に位置しているので、挿入されたライナー９の外周部が開栓時に上部突起部８ａの上面に係止されるが、破断部である先端にライナー９が引っ掛からず、撓みによる脱落を防止することができる。 As described above, in the metal cap 1 of the present embodiment, the tip of the upper protrusion 8a of the nar slit 8 that is a vent hole is positioned radially inward from the outer peripheral edge of the liner 9 when inserted. And the same position in the radial direction as the tip of the lower projection 8b or radially outward from the tip, so that the outer periphery of the inserted liner 9 is the upper surface of the upper projection 8a when opened. However, the liner 9 does not get caught at the tip which is a broken part, and can be prevented from falling off due to bending.
また、ナールスリット８の上部突起部８ａの先端が、下部突起部８ｂよりも半径方向外方に位置しているので、ライナー９を挿入する際に、下部突起部８ｂがガイドになると共にライナー９と上部突起部８ａの先端との接触を防いで上部突起部８ａの先端にライナー９が引っ掛かることを抑制することができる。 Since the tip of the upper protrusion 8a of the knurl slit 8 is located radially outward from the lower protrusion 8b, the lower protrusion 8b serves as a guide and the liner 9 when the liner 9 is inserted. It is possible to prevent the liner 9 from being caught on the tip of the upper protrusion 8a by preventing contact between the upper protrusion 8a and the tip of the upper protrusion 8a.
さらに、上部突起部８ａの先端が、挿入された際のライナー９の摺動層９ａの外周縁よりも半径方向内方に位置し、下部突起部８ｂの先端が、密封層９ｂの外周縁よりも半径方向外方に位置しているので、挿入時にライナー９の摺動層９ａとナールスリット８の上部突起部８ａの先端との接触を下部突起部８ｂによって防ぐことができると共に、挿入後の密封層９ｂのモールド成形時に内部に挿入される金型Ｍを、下部突起部８ｂによってセンタリングして位置決めすることができる。 Furthermore, the tip of the upper projection 8a is positioned radially inward from the outer periphery of the sliding layer 9a of the liner 9 when inserted, and the tip of the lower projection 8b is from the outer periphery of the sealing layer 9b. Is also located radially outward, so that contact between the sliding layer 9a of the liner 9 and the tip of the upper projection 8a of the knurl slit 8 during insertion can be prevented by the lower projection 8b and after insertion. The mold M inserted inside when the sealing layer 9b is molded can be centered and positioned by the lower protrusion 8b.
また、上部突起部８ａの先端部が、さらに下方に折り曲げられて先端が下方に向けられているので、挿入時に弾性によって下部突起部８ｂを越えたライナー９の外周縁が上部突起部８ａの先端に接触し難くなり、引っ掛かることをさらに抑制することができる。
したがって、本発明の金属キャップ１を採用したキャップ付きボトルでは、開栓時においてライナー９の脱落を防止することができると共に、スムーズなグリップ官能を得ることができる。
Further, since the tip of the upper projection 8a is further bent downward and the tip is directed downward, the outer peripheral edge of the liner 9 that has elastically exceeded the lower projection 8b during insertion is the tip of the upper projection 8a. It becomes difficult to come into contact with and can be further suppressed from being caught.
Therefore, in the bottle with a cap that employs the metal cap 1 of the present invention, the liner 9 can be prevented from falling off during opening, and a smooth gripping sensation can be obtained.
次に、本実施形態の金属キャップ及びキャップ付きボトルを実際に作製し、開栓時におけるライナーの脱落について評価した。 Next, the metal cap and the bottle with the cap according to the present embodiment were actually produced, and the dropping of the liner at the time of opening was evaluated.
＜評価１＞
まず、ナールスリットの上部突起部の角度θを、０〜８７°の間で変化させて作製した際、開栓した金属キャップを目視評価して、ライナーが外れた上部突起部および下部突起部（以下、フックと称す）の数とボトルの数（以下、缶数と称す）とからフック外れ度数を調べ、良否判定を行った。
<Evaluation 1>
First, when the angle θ of the upper protrusion of the knurled slit was changed between 0 and 87 °, the opened metal cap was visually evaluated, and the upper protrusion and the lower protrusion with the liner removed ( Hereinafter, the hook removal frequency was examined from the number of hooks and the number of bottles (hereinafter referred to as the number of cans), and the quality was judged.
なお、上記フック外れ度数は、以下の数式により算出した。
フック外れ度数＝（外れたフックの数×缶数）÷評価缶数
例えば、評価した缶数が３０缶であり、２つの缶で２つのフックが外れ、３つの缶で３つのフックが外れ、さらに３つの缶で４つのフックが外れた場合、以下のように算出される。
（（２フック×２缶）＋（３フック×３缶）＋（４フック×３缶））÷評価缶数３０缶＝０．８３（フック外れ度数）
In addition, the said hook removal frequency was computed with the following numerical formula.
Hook removal frequency = (number of hooks removed × number of cans) ÷ number of cans For example, the number of cans evaluated is 30 cans, 2 hooks come off with 2 cans, 3 hooks come off with 3 cans, Further, when four hooks come off with three cans, the calculation is performed as follows.
((2 hooks x 2 cans) + (3 hooks x 3 cans) + (4 hooks x 3 cans)) / Evaluation cans 30 cans = 0.83 (hook removal frequency)
また、良否判定は、フック外れ度数が１．０以上の場合、ライナー脱落のリスクが有るとして「×」とし、フック外れ度数が０．４以上１．０未満の場合、ライナー脱落までに至らないが外観的不良となるおそれがあるとして「△」とし、フック外れ度数が０．４未満の場合、ライナー脱落の問題はないとして「○」とした。
なお、本実施例では、５℃の低温で各条件１００缶を評価した。その結果を表１に示す。
また、角度θは、Ｘ線によるフック断面を複数測定した平均値で求めた。
In addition, the pass / fail judgment is “X” because there is a risk of liner dropping when the hook removal frequency is 1.0 or more, and when the hook removal frequency is 0.4 or more and less than 1.0, the liner does not come off. “△” because there is a risk of appearance failure, and “◯” because there is no problem of liner dropping when the hook disengagement frequency is less than 0.4.
In this example, 100 cans were evaluated at a low temperature of 5 ° C. The results are shown in Table 1.
Further, the angle θ was determined by an average value obtained by measuring a plurality of hook cross sections by X-rays.
表１に示すように、ナールスリットの上部突起部の角度θが２８〜８２°の範囲ではフック外れ度数の良否判定で良好な結果が得られている。なお、角度θが８７°では、フック割れが生じたため、成型不良として評価していない。 As shown in Table 1, when the angle θ of the upper protrusion of the knurl slit is in the range of 28 to 82 °, good results are obtained in the determination of the hook removal frequency. Note that when the angle θ is 87 °, hook cracks have occurred, so that the molding failure is not evaluated.
＜評価２＞
次に、ライナーとナールスリットの上部突起部とのオーバーラップ寸法ａを、−０．５〜１．５２ｍｍの間で変化させた際、上記と同様にフック外れ度数を調べ、良否判定を行った結果を、表２に示す。
なお、ライナーとナールスリットの上部突起部とのオーバーラップ寸法ａがマイナスになる場合、すなわち、ナールスリット８の上部突起部８ａの先端が、ライナー９の外周縁よりも半径方向外方に位置している比較例について、図４および図５に示す。
また、オーバーラップ寸法ａは、Ｘ線によるフック断面を複数測定した平均値で求めた。
<Evaluation 2>
Next, when the overlap dimension a between the liner and the upper protrusion of the knurled slit was changed between -0.5 and 1.52 mm, the hook removal frequency was examined in the same manner as described above to determine whether or not it was good. The results are shown in Table 2.
When the overlap dimension a between the liner and the upper protrusion of the nar slit is negative, that is, the tip of the upper protrusion 8a of the nar slit 8 is positioned radially outward from the outer peripheral edge of the liner 9. The comparative example is shown in FIG. 4 and FIG.
In addition, the overlap dimension “a” was obtained as an average value obtained by measuring a plurality of hook cross sections by X-rays.
表２に示すように、オーバーラップ寸法ａが０．１０〜１．５２ｍｍまでフック外れ度数の良否判定で良好な結果が得られている。 As shown in Table 2, good results have been obtained in the quality determination of the hook removal frequency until the overlap dimension a is 0.10 to 1.52 mm.
なお、本発明の技術範囲は上記実施形態および実施例に限定されるものではなく、本発明の趣旨を逸脱しない範囲において種々の変更を加えることが可能である。
例えば、本発明は、上述したように少なくとも摺動層および密封層からなる多層構造のライナーを挿入する金属キャップに好適であるが、単層のライナーを挿入するキャップに適用しても構わない。
The technical scope of the present invention is not limited to the above-described embodiments and examples, and various modifications can be made without departing from the spirit of the present invention.
For example, the present invention is suitable for a metal cap into which a liner having a multilayer structure including at least a sliding layer and a sealing layer is inserted as described above, but may be applied to a cap into which a single-layer liner is inserted.
１…金属キャップ、２…天板部、３…円筒部、７…ナール凹部、８…ナールスリット（ベントホール）、８ａ…上部突起部、８ｂ…下部突起部、９…ライナー、９ａ…摺動層、９ｂ…密封層、１０…ＰＰキャップ、１１…ボトル本体、１２…口金部（口部）、１００…ボトル（キャップ付きボトル） DESCRIPTION OF SYMBOLS 1 ... Metal cap, 2 ... Top plate part, 3 ... Cylindrical part, 7 ... Knurl recess, 8 ... Knurl slit (vent hole), 8a ... Upper protrusion, 8b ... Lower protrusion, 9 ... Liner, 9a ... Sliding Layer, 9b ... sealing layer, 10 ... PP cap, 11 ... bottle body, 12 ... base part (mouth part), 100 ... bottle (bottle with cap)
本発明は、飲料用等のボトルにおける口部を密栓する金属キャップにライナーを配置したキャップの製造方法に関する。 The present invention relates to a method of manufacturing a cap in which a liner is disposed on a metal cap that tightly closes a mouth portion of a beverage bottle or the like.
従来、スチールやアルミニウム合金等の金属製ボトルにおける口金部に被着されるキャップにおいて、キャップが回転操作されて開栓される際に、内圧を開放してボトル本体内のガスを外部に放出するためのベントホール（ナールスリットまたはベントスリットとも称される）がキャップ上端部近傍に形成されたものが知られている。
例えば、特許文献１では、天面壁近傍のスカート壁内面に複数の突起を突設したキャップ本体と、上記突起に周縁の複数箇所を係止されて天面壁内側に非接合状態で配置されたライナーと、を備え、キャップ本体の周囲に切り込みを入れて切り込んだ部分をキャップ内側に押し込んで折曲させて上記突起を形成したキャップが記載されている。このキャップでは、上記突起を形成した切り込みがベントホールとして機能する。
Conventionally, when a cap is attached to a cap portion of a metal bottle such as steel or aluminum alloy, when the cap is rotated and opened, the internal pressure is released and the gas in the bottle body is released to the outside. A vent hole (also referred to as a knurl slit or a vent slit) is formed near the upper end of the cap.
For example, in Patent Document 1, a cap main body in which a plurality of protrusions are provided on the inner surface of a skirt wall near the top wall, and a liner disposed in a non-joined state on the inner side of the top wall with a plurality of peripheral edges locked to the protrusions. And a cap in which a notch is formed around the cap body and the cut portion is pushed into the cap and bent to form the protrusion. In this cap, the notch formed with the protrusion functions as a vent hole.
また、特許文献２には、天板部、および該天板部の周縁部から略垂下してなる周壁部を備えるキャップ本体と、該キャップ本体の内側に天板部の内面を覆うように配設されたライナーと、を備え、ボトル缶の口金部に螺着されるキャップであって、周壁部の上部に、天板部の周縁部から連続してキャップ本体の径方向内方へ向って延びるライナー支持部が周方向に間隔をあけて複数形成され、該ライナー支持部の軸方向上端部にライナーが配置されているキャップが記載されている。このキャップでは、周壁部の周方向に複数形成されたナール部の凹部の下端部にベントホールとしてスリットを形成し、凹部をライナー支持部としている。また、このキャップでは、予めライナーを天板部内面に配置した後に、ベントホールとなるスリットおよびライナー支持部を形成している。 Patent Document 2 discloses a cap body having a top plate portion and a peripheral wall portion substantially hanging from the peripheral edge portion of the top plate portion, and an inner surface of the cap body so as to cover the inner surface of the top plate portion. A cap that is screwed to the cap portion of the bottle can, and is continuously inward from the peripheral portion of the top plate portion and radially inward of the cap body. There is described a cap in which a plurality of extending liner support portions are formed at intervals in the circumferential direction, and a liner is disposed at an upper end portion in the axial direction of the liner support portion. In this cap, a slit is formed as a vent hole in the lower end portion of the recess of the knurled portion formed in the circumferential direction of the peripheral wall portion, and the recess serves as a liner support portion. Further, in this cap, after a liner is disposed in advance on the inner surface of the top plate portion, a slit that becomes a vent hole and a liner support portion are formed.
このように上記従来のキャップでは、ベントホールとして形成したスリットの突起部を内側に押し込んで突起またはライナー支持部とし、これらを、ライナーを係止して脱落を防止するフックとしている。 As described above, in the conventional cap, the protrusions of the slits formed as vent holes are pushed inward to form protrusions or liner support parts, which are hooks that lock the liner and prevent it from falling off.
上記従来の技術には、以下の課題が残されている。
すなわち、ボトル口部に密着したライナーを開栓の際にボトル口部から剥がしきれず、密着されたままライナーがキャップに対して下方に引っ張られたときに、上記特許文献１の技術のように、ベントホールの下部突起部でライナーを係止する場合、破断部である下部突起部の先端にライナーの外周縁が引っ掛かってライナー全体が撓み、ライナーの引っ掛かっていない外周縁から外れてライナーが脱落してしまうおそれがあった。また、脱落しない場合でも、ライナーの外周部がベントホールの下部突起部のエッジに擦れて開栓時にスムーズな官能が得られず、ときにはライナーが僅かに削れる場合があった。
さらに、上記特許文献２の技術では、ベントホールとなるスリットおよび凹部を形成した後にライナーを挿入しようとすると、破断部であるスリットの上部突起部の先端にライナーが引っ掛かってスムーズに挿入できなかったり、擦れによってライナーが傷ついたりするおそれがあった。このため、予めライナーを天板部内面に配置した後に、ベントホールとなるスリットおよび凹部を形成する必要があり、キャップの加工工程上、手間であった。
The following problems remain in the conventional technology.
That is, when the liner that is in close contact with the bottle mouth portion cannot be peeled off from the bottle mouth portion when opening, the liner is pulled downward with respect to the cap while being in close contact, as in the technique of Patent Document 1 above. When the liner is locked by the lower protrusion of the vent hole, the outer peripheral edge of the liner is caught at the tip of the lower protrusion, which is a fractured part, and the entire liner is bent, and the liner falls off from the outer peripheral edge where the liner is not caught. There was a risk of doing so. Even when the liner does not fall off, the outer periphery of the liner rubs against the edge of the lower protrusion of the vent hole, and a smooth sensation cannot be obtained when the plug is opened, and sometimes the liner is slightly scraped.
Further, in the technique of Patent Document 2, when a liner is inserted after forming slits and recesses to be vent holes, the liner is caught at the tip of the upper protrusion of the slit, which is a fracture portion, and the insertion cannot be performed smoothly. The liner could be damaged by rubbing. For this reason, it is necessary to form slits and recesses to be vent holes after arranging the liner on the inner surface of the top plate in advance, which is troublesome in the cap processing process.
本発明は、前述の課題に鑑みてなされたもので、開栓時にライナーの脱落を防止すると共に、スムーズな開栓およびライナーの挿入が可能な金属キャップにライナーを配置したキャップの製造方法を提供することを目的とする。 The present invention has been made in view of the above-described problems, and provides a method for manufacturing a cap in which a liner is disposed on a metal cap that can prevent the liner from dropping off when opening and can be smoothly opened and inserted. The purpose is to do.
本発明は、前記課題を解決するために以下の構成を採用した。すなわち、本発明のキャップの製造方法は、金属キャップにライナーを配置する工程を有し、前記金属キャップが、上方に配された天板部と、該天板部の周縁から略垂下されてなる円筒部とを備え、前記天板部の内面にライナーが非接着状態で挿入された後にボトルの口部を密栓する金属キャップであって、前記円筒部が、前記天板部近傍であって周方向にスリット状に開口形成され開栓時に内圧を開放するベントホールと、該ベントホールの上部開口端部および下部開口端部を前記円筒部の半径方向内方に向けて曲げて形成した上部突起部および下部突起部と、を有し、前記上部突起部の先端が、挿入された際の前記ライナーの外周縁よりも半径方向内方に位置されていると共に、前記下部突起部の先端と半径方向で同位置または該先端よりも半径方向外方に位置し、前記ライナーが、前記天板部の内面側に配されたシートである摺動層と、前記挿入後にモールド成形によって前記摺動層に積層され前記摺動層よりも柔軟で外径の小さい密封層と、を備え、前記上部突起部の先端が、挿入された際の前記ライナーの前記摺動層の外周縁よりも半径方向内方に位置し、前記下部突起部の先端が、前記密封層の外周縁よりも半径方向外方に位置し、前記ライナーを配置する工程が、前記摺動層を前記金属キャップ内に挿入して前記天板部の内面に接して配置する工程と、前記摺動層の挿入後に前記摺動層に直接または中間層を介して前記密封層をモールド成形する工程とを有し、前記密封層をモールド成形する工程において、モールド成形時に前記金属キャップ内部に挿入される金型を、前記下部突起部によってガイドし、センタリングして位置決めすることを特徴とする。 The present invention employs the following configuration in order to solve the above problems. That is, the cap manufacturing method of the present invention includes a step of arranging a liner on the metal cap, and the metal cap is substantially suspended from the top plate portion disposed above and the periphery of the top plate portion. A metal cap that seals the mouth of the bottle after the liner is inserted in an unbonded state on the inner surface of the top plate portion, and the cylindrical portion is in the vicinity of the top plate portion. A vent hole that is formed in a slit shape in the direction to release the internal pressure when the cap is opened, and an upper protrusion formed by bending the upper opening end and the lower opening end of the vent hole inward in the radial direction of the cylindrical portion And the tip of the upper projection is positioned radially inward from the outer peripheral edge of the liner when inserted, and the tip and radius of the lower projection In the same position or at the tip Also located radially outward, said liner, and the sliding layer is a sheet which is disposed on the inner side of the top plate portion, from the sliding layer is laminated on said sliding layer by molding after the insertion A flexible sealing layer having a small outer diameter, and the tip of the upper protrusion is located radially inward from the outer peripheral edge of the sliding layer of the liner when inserted, and the lower protrusion And the step of disposing the liner includes inserting the sliding layer into the metal cap and contacting the inner surface of the top plate portion. A step of molding the sealing layer directly or via an intermediate layer after the insertion of the sliding layer, and in the step of molding the sealing layer, A mold sometimes inserted inside the metal cap , Guided by the lower projecting portion, and wherein the positioning and centering.
上記金属キャップでは、ベントホールの上部突起部の先端が、挿入された際のライナーの外周縁よりも半径方向内方に位置されていると共に、下部突起部の先端と半径方向で同位置または該先端よりも半径方向外方に位置しているので、挿入されたライナーの外周部が開栓時に上部突起部の上面に係止されるが、破断部である先端にライナーが引っ掛からず、撓みによる脱落を防止することができる。また、ベントホールの上部突起部の先端が、下部突起部よりも半径方向外方に位置しているので、ライナーを挿入する際に、下部突起部がガイドになると共にライナーと上部突起部の先端との接触を防いで上部突起部の先端にライナーが引っ掛かることを抑制することができる。
また、この金属キャップでは、上部突起部の先端が、挿入された際のライナーの摺動層の外周縁よりも半径方向内方に位置し、下部突起部の先端が、密封層の外周縁よりも半径方向外方に位置しているので、挿入時にライナーの摺動層とベントホールの上部突起部の先端との接触を下部突起部によって防ぐことができると共に、挿入後の密封層のモールド成形時に内部に挿入される金型を、下部突起部によってセンタリングして位置決めすることができる。
したがって、上記キャップの製造方法では、モールド成形用の金型を挿入する際に、下部突起部が金型のガイドの役割を果たし、金型のセンタリング（位置決め）が行われる。
In the metal cap, the tip of the upper protrusion of the vent hole is positioned radially inward from the outer peripheral edge of the liner when inserted, and the tip of the lower protrusion is at the same position or in the radial direction. Since it is located radially outward from the tip, the outer periphery of the inserted liner is locked to the upper surface of the upper protrusion when it is opened, but the liner does not catch on the tip, which is a break, and is bent. Dropout can be prevented. In addition, since the tip of the upper projection of the vent hole is located radially outward from the lower projection, when inserting the liner, the lower projection serves as a guide and the tip of the liner and upper projection It is possible to prevent the liner from being caught on the tip of the upper projection portion by preventing contact with the upper projection portion.
In this metal cap, the tip of the upper projection is positioned radially inward from the outer periphery of the sliding layer of the liner when inserted, and the tip of the lower projection is from the outer periphery of the sealing layer. Is also located radially outward, so that contact between the sliding layer of the liner and the tip of the upper protrusion of the vent hole can be prevented by the lower protrusion during insertion, and the sealing layer is molded after insertion. Sometimes the mold inserted inside can be centered and positioned by the lower projection.
Therefore, in the above-described cap manufacturing method, when the mold for molding is inserted, the lower projection serves as a guide for the mold, and the centering (positioning) of the mold is performed.
また、本発明のキャップの製造方法は、前記上部突起部の先端部が、さらに下方に折り曲げられて先端面が下方に向けられていることを特徴とする。
すなわち、このキャップの製造方法では、上部突起部の先端部が、さらに下方に折り曲げられて先端が下方に向けられているので、挿入時に弾性によって下部突起部を越えたライナーの外周縁が上部突起部の先端に接触し難くなり、引っ掛かることをさらに抑制することができる。
Further, the cap manufacturing method of the present invention is characterized in that the tip portion of the upper protrusion is further bent downward and the tip surface is directed downward.
That is, in this cap manufacturing method , since the tip of the upper projection is further bent downward and the tip is directed downward, the outer peripheral edge of the liner beyond the lower projection due to elasticity when inserted is the upper projection. It becomes difficult to come into contact with the tip of the part, and it can be further suppressed from being caught.
本発明によれば、以下の効果を奏する。
すなわち、本発明に係るキャップの製造方法によれば、挿入時にライナーの摺動層と上部突起部の先端との接触を下部突起部によって防ぐことができると共に、挿入後の密封層のモールド成形時に内部に挿入される金型を、下部突起部によってセンタリングして位置決めすることができる。
The present invention has the following effects.
That is, according to the method for manufacturing a cap according to the present invention, contact between the sliding layer of the liner and the tip of the upper protrusion can be prevented by the lower protrusion at the time of insertion, and at the time of molding the sealing layer after insertion. The mold inserted inside can be centered and positioned by the lower protrusion.
以下、本発明に係るキャップの製造方法の一実施形態を、図１から図５を参照しながら説明する。 Hereinafter, an embodiment of a method for producing a cap according to the present invention will be described with reference to FIGS. 1 to 5.
本実施形態のキャップの製造方法に用いる金属キャップ１は、図１及び図２に示すように、例えば直径３８ｍｍ口径のアルミニウム又はアルミニウム合金製（金属製）ボトル本体の口金部（口部）に被着されて密栓するピルファープルーフキャップ（以下、ＰＰキャップとも称す）となるものである。この金属キャップ１は、アルミニウム又はアルミニウム合金板材をカップ状に成形したもので、上方に配された天板部２と、該天板部２の周縁から略垂下されてなる円筒部３と、を備えている。 As shown in FIGS. 1 and 2, the metal cap 1 used in the cap manufacturing method of the present embodiment is covered on the base (mouth) of a bottle body made of aluminum or aluminum alloy (metal) having a diameter of 38 mm, for example. It becomes a pilfer-proof cap (hereinafter also referred to as PP cap) that is worn and tightly plugged. This metal cap 1 is formed by molding an aluminum or aluminum alloy plate material into a cup shape, and includes a top plate portion 2 disposed above and a cylindrical portion 3 substantially suspended from the periphery of the top plate portion 2. I have.
この金属キャップ１は、天板部２の内面にライナー９が非接着状態で挿入された後にボトル本体の口部を密栓するものである。
上記円筒部３は、周方向に断続的に形成されたスリット４を介して上下に分割された筒上部５と筒下部６とを有し、隣接するスリット４間に形成される複数のブリッジ４ａによって筒上部５と筒下部６とを連結した形状としたものである。
The metal cap 1 seals the mouth of the bottle body after the liner 9 is inserted into the inner surface of the top plate 2 in a non-adhered state.
The cylindrical portion 3 has a cylindrical upper portion 5 and a cylindrical lower portion 6 that are divided vertically through slits 4 that are intermittently formed in the circumferential direction, and a plurality of bridges 4 a formed between adjacent slits 4. Thus, the cylinder upper part 5 and the cylinder lower part 6 are connected to each other.
また、上記円筒部３は、天板部２近傍であって周方向に複数並べて形成されたナール凹部７と、ナール凹部７に周方向にスリット状に開口形成され開栓時に内圧を開放するベントホールであるナールスリット８と、該ナールスリット８の上部開口端部および下部開口端部を円筒部３の半径方向内方に向けて曲げて形成した上部突起部８ａおよび下部突起部８ｂと、を有している。
上記ナール凹部７は、開栓時にＰＰキャップと把持する指との間の摩擦抵抗を増大させるものであり、これにより手を滑らせることなく容易に開栓可能とするものである。
The cylindrical portion 3 includes a knurled recess 7 formed in the vicinity of the top plate 2 and arranged in the circumferential direction, and a vent that opens to the knurled recess 7 in a slit shape in the circumferential direction and releases the internal pressure when the cap is opened. A knurl slit 8 that is a hole, and an upper protrusion 8a and a lower protrusion 8b that are formed by bending the upper opening end and the lower opening end of the knurl slit 8 inward in the radial direction of the cylindrical portion 3. Have.
The knurled recess 7 increases the frictional resistance between the PP cap and the finger to be gripped when opening, thereby enabling easy opening without sliding the hand.
上記ナールスリット８は、ナール凹部７の上端部にナール凹部７の幅と同じ長さに周方向にせん断されて形成されている。このナールスリット８は、ボトル本体に装着されたキャップ１（ＰＰキャップ）がブリッジ４ａを破断しつつ上方に回転操作された際、ボトル本体内のガスを外部に放出するためのベントホールである。 The knurl slit 8 is formed in the upper end of the knurl recess 7 by being sheared in the circumferential direction to the same length as the width of the knurl recess 7. The knurl slit 8 is a vent hole for releasing the gas in the bottle body to the outside when the cap 1 (PP cap) attached to the bottle body is rotated upward while breaking the bridge 4a.
また、ナールスリット８の上部突起部８ａの先端は、挿入された際のライナー９の外周縁よりも半径方向内方に位置されていると共に、下部突起部８ｂの先端と半径方向で同位置または該先端よりも半径方向外方に位置している。
さらに、上部突起部８ａの先端部は、さらに下方に折り曲げられて先端面が下方に向けられている。
The tip of the upper protrusion 8a of the knurl slit 8 is located radially inward from the outer peripheral edge of the liner 9 when inserted, and is the same position as the tip of the lower protrusion 8b in the radial direction or It is located radially outward from the tip.
Further, the tip of the upper protrusion 8a is further bent downward so that the tip surface is directed downward.
また、ナールスリット８の上部突起部８ａは、図２の（ｂ）に示すように、上部の外側凸部となる屈曲部を起点にして円筒部３の内方に向けて所定の角度θ（円筒部３の軸線に平行な仮想線３ａに対する角度）で屈曲されている。この角度θとしては、２８〜８２°に範囲内に設定することが好ましい。 Further, as shown in FIG. 2B, the upper protrusion 8a of the knurl slit 8 has a predetermined angle θ (inward) toward the inside of the cylindrical portion 3 with a bent portion serving as an upper outer convex portion as a starting point. It is bent at an angle) to an imaginary line 3a parallel to the axis of the cylindrical portion 3. This angle θ is preferably set within a range of 28 to 82 °.
この金属キャップ１に挿入されるライナー９は、天板部２の内面側に配された摺動層９ａと、挿入後にモールド成形によって摺動層９ａに直接またはバリアー層等の中間層を介して積層され摺動層９ａよりも柔軟で外径の小さい密封層９ｂと、を備えている。上記摺動層９ａは、ポリプロピレン等で形成された円盤状の硬質シートで構成され、上記密封層９ｂは、硬質シート上にモールド成形で積層状態にエラストマー樹脂等で形成される。
また、ナールスリット８の上部突起部８ａの先端は、挿入された際のライナー９の摺動層９ａの外周縁よりも半径方向内方に位置し、下部突起部８ｂの先端は、密封層９ｂの外周縁よりも半径方向外方に位置している。
The liner 9 to be inserted into the metal cap 1 includes a sliding layer 9a disposed on the inner surface side of the top plate portion 2, and after insertion, directly on the sliding layer 9a by molding or through an intermediate layer such as a barrier layer. A sealing layer 9b that is laminated and is softer than the sliding layer 9a and has a smaller outer diameter. The sliding layer 9a is formed of a disk-shaped hard sheet formed of polypropylene or the like, and the sealing layer 9b is formed of an elastomer resin or the like in a laminated state by molding on the hard sheet.
The tip of the upper protrusion 8a of the knurl slit 8 is positioned radially inward from the outer peripheral edge of the sliding layer 9a of the liner 9 when inserted, and the tip of the lower protrusion 8b is the sealing layer 9b. It is located radially outward from the outer peripheral edge.
このライナー９は、図２の（ｂ）に示すように、金属キャップ１内に挿入して硬質シートの摺動層９ａを天板部２の内面に接して配置した状態で、モールド成形用の金型Ｍを金属キャップ１内に挿入し、該金型Ｍを用いてエラストマー樹脂等を樹脂成形することで、密封層９ｂを形成する。このモールド成形用の金型Ｍを挿入する際に、ナールスリット８の下部突起部８ｂが金型Ｍのガイドの役割を果たし、金型Ｍのセンタリング（位置決め）が行われる。 As shown in FIG. 2 (b), the liner 9 is inserted into the metal cap 1 and is placed in contact with the inner surface of the top plate portion 2 with a hard sheet sliding layer 9a disposed therein. The mold M is inserted into the metal cap 1, and an elastomer resin or the like is molded using the mold M to form the sealing layer 9b. When the mold M for molding is inserted, the lower protrusion 8b of the knurl slit 8 serves as a guide for the mold M, and the centering (positioning) of the mold M is performed.
なお、この密封層９ｂは、ボトルの口部に密着する外周部が中心部よりも厚く形成されている。
また、上部突起部８ａに接触するライナー９の厚みは、０．１〜２．０ｍｍの範囲内に設定することが好ましい。また、ライナー９の外径（摺動層９ａの外径）は、金属キャップ１の寸法に応じて決定されるが、直径１５〜６５ｍｍの範囲内に設定される。
In addition, this sealing layer 9b is formed so that the outer peripheral part closely_contact | adhering to the opening part of a bottle is thicker than a center part.
Moreover, it is preferable to set the thickness of the liner 9 which contacts the upper protrusion part 8a in the range of 0.1-2.0 mm. Moreover, although the outer diameter of the liner 9 (the outer diameter of the sliding layer 9a) is determined according to the dimension of the metal cap 1, it is set within a range of 15 to 65 mm in diameter.
次に、口金部に上記金属キャップ１を被着させてなるＰＰキャップ及び該ＰＰキャップにより密閉されたキャップ付きボトル１００を、図３を参照しながら説明する。 Next, a PP cap in which the metal cap 1 is attached to the base and a bottle 100 with a cap sealed by the PP cap will be described with reference to FIG.
本実施形態のキャップ付きボトル１００は、図３に示すように、飲料等の液体が充填されアルミニウム又はアルミニウム合金からなるボトル本体１１と、該ボトル本体１１の口金部１２に被着されたＰＰキャップ１０（金属キャップ１）と、を備えている。このＰＰキャップ１０は、天板部２が肩絞り加工されている。また、ＰＰキャップ１０は、ねじ山１３の外形に沿うねじ部１４を筒上部５に形成すると共に、膨出部１５の下部に沿うピルファープルーフ部１６を筒下部６に形成することにより、ボトル本体１１の口金部１２に被着したものである。 As shown in FIG. 3, a bottle 100 with a cap according to the present embodiment includes a bottle main body 11 made of aluminum or an aluminum alloy and filled with a liquid such as a beverage, and a PP cap attached to a base portion 12 of the bottle main body 11. 10 (metal cap 1). As for this PP cap 10, the top-plate part 2 is shoulder-drawn. In addition, the PP cap 10 forms a screw portion 14 along the outer shape of the thread 13 on the upper portion 5 of the cylinder, and forms a pill fur proof portion 16 along the lower portion of the bulging portion 15 on the lower portion 6 of the bottle. It is attached to the base part 12 of the main body 11.
このＰＰキャップ１０のキャッピング加工は、プレッシャーブロック、ネジローラー、スカートローラー等からなるキャッピング装置を用いて行われる。
すなわち、口金部１２に被せた金属キャップ１の天板部２を、プレッシャーブロックでボトル底部の方向に押圧し、この状態でプレッシャーブロックによる絞り加工により、金属キャップ１の肩部に段差部を形成する。
The capping process of the PP cap 10 is performed using a capping device including a pressure block, a screw roller, a skirt roller, and the like.
That is, the top plate portion 2 of the metal cap 1 placed on the base portion 12 is pressed toward the bottom of the bottle with a pressure block, and in this state, a stepped portion is formed on the shoulder portion of the metal cap 1 by drawing with the pressure block. To do.
さらに、この状態でネジローラーによりネジ部１４を形成し、スカートローラーで口金部１２のカブラ部である膨出部１５にスカート部であるピルファープルーフ部１６を巻きつけることで、キャッピング加工が行われる。すなわち、金属キャップ１が被着されるボトル本体１１の口金部１２には、ねじ山１３及び膨出部１５が形成されており、ここに被せられた金属キャップ１はねじ山１３、膨出部１５等の形状に沿うように塑性変形される。
これによって、金属キャップ１がＰＰキャップ１０として口金部１２に被着され、ボトル本体１１を密封状態とすることで、ボトル１００が得られる。
Further, in this state, the screw portion 14 is formed by the screw roller, and the pill roller proof portion 16 that is the skirt portion is wound around the bulging portion 15 that is the turntable portion of the base portion 12 by the skirt roller, so that the capping process is performed. Is called. That is, a screw thread 13 and a bulging part 15 are formed on the cap part 12 of the bottle main body 11 to which the metal cap 1 is attached, and the metal cap 1 covered here has the screw thread 13 and the bulging part. It is plastically deformed along the shape of 15 etc.
As a result, the metal cap 1 is attached to the base portion 12 as the PP cap 10 and the bottle body 11 is sealed, whereby the bottle 100 is obtained.
なお、ＰＰキャップ１０の天板部２の内側には、上述したようにライナー９が挿入配置されており、該ライナー９によってボトル本体１１の開口部がシールされている。
また、キャッピング後におけるライナー９の摺動層９ａの外周縁からナールスリット８の上部突起部８ａの先端までの半径方向におけるオーバーラップ寸法ａは、０．１０〜１．５２ｍｍの範囲内に設定することが好ましい。
The liner 9 is inserted and arranged inside the top plate portion 2 of the PP cap 10 as described above, and the opening of the bottle body 11 is sealed by the liner 9.
Further, the overlap dimension a in the radial direction from the outer peripheral edge of the sliding layer 9a of the liner 9 to the tip of the upper protrusion 8a of the knurl slit 8 after capping is set within a range of 0.10 to 1.52 mm. It is preferable.
以上、説明したように金属キャップ１では、ベントホールであるナールスリット８の上部突起部８ａの先端が、挿入された際のライナー９の外周縁よりも半径方向内方に位置されていると共に、下部突起部８ｂの先端と半径方向で同位置または該先端よりも半径方向外方に位置しているので、挿入されたライナー９の外周部が開栓時に上部突起部８ａの上面に係止されるが、破断部である先端にライナー９が引っ掛からず、撓みによる脱落を防止することができる。 As described above, in the metal cap 1, the tip of the upper protrusion 8a of the nar slit 8 that is a vent hole is positioned radially inward from the outer peripheral edge of the liner 9 when inserted, Since it is located at the same position in the radial direction as the tip of the lower projection 8b or radially outward from the tip, the outer periphery of the inserted liner 9 is locked to the upper surface of the upper projection 8a when opened. However, the liner 9 is not caught at the tip, which is a broken portion, and can be prevented from falling off due to bending.
また、ナールスリット８の上部突起部８ａの先端が、下部突起部８ｂよりも半径方向外方に位置しているので、ライナー９を挿入する際に、下部突起部８ｂがガイドになると共にライナー９と上部突起部８ａの先端との接触を防いで上部突起部８ａの先端にライナー９が引っ掛かることを抑制することができる。 Since the tip of the upper protrusion 8a of the knurl slit 8 is located radially outward from the lower protrusion 8b, the lower protrusion 8b serves as a guide and the liner 9 when the liner 9 is inserted. It is possible to prevent the liner 9 from being caught on the tip of the upper protrusion 8a by preventing contact between the upper protrusion 8a and the tip of the upper protrusion 8a.
さらに、上部突起部８ａの先端が、挿入された際のライナー９の摺動層９ａの外周縁よりも半径方向内方に位置し、下部突起部８ｂの先端が、密封層９ｂの外周縁よりも半径方向外方に位置しているので、挿入時にライナー９の摺動層９ａとナールスリット８の上部突起部８ａの先端との接触を下部突起部８ｂによって防ぐことができると共に、挿入後の密封層９ｂのモールド成形時に内部に挿入される金型Ｍを、下部突起部８ｂによってセンタリングして位置決めすることができる。
したがって、本実施形態のキャップの製造方法では、モールド成形用の金型を挿入する際に、下部突起部が金型のガイドの役割を果たし、金型のセンタリング（位置決め）が行われる。
Furthermore, the tip of the upper projection 8a is positioned radially inward from the outer periphery of the sliding layer 9a of the liner 9 when inserted, and the tip of the lower projection 8b is from the outer periphery of the sealing layer 9b. Is also located radially outward, so that contact between the sliding layer 9a of the liner 9 and the tip of the upper projection 8a of the knurl slit 8 during insertion can be prevented by the lower projection 8b and after insertion. The mold M inserted inside when the sealing layer 9b is molded can be centered and positioned by the lower protrusion 8b.
Therefore, in the cap manufacturing method of the present embodiment, when the mold for molding is inserted, the lower protrusion serves as a guide for the mold, and the centering (positioning) of the mold is performed.
また、上部突起部８ａの先端部が、さらに下方に折り曲げられて先端が下方に向けられているので、挿入時に弾性によって下部突起部８ｂを越えたライナー９の外周縁が上部突起部８ａの先端に接触し難くなり、引っ掛かることをさらに抑制することができる。
したがって、本発明の金属キャップ１を採用したキャップ付きボトルでは、開栓時においてライナー９の脱落を防止することができると共に、スムーズなグリップ官能を得ることができる。
Further, since the tip of the upper projection 8a is further bent downward and the tip is directed downward, the outer peripheral edge of the liner 9 that has elastically exceeded the lower projection 8b during insertion is the tip of the upper projection 8a. It becomes difficult to come into contact with and can be further suppressed from being caught.
Therefore, in the bottle with a cap that employs the metal cap 1 of the present invention, the liner 9 can be prevented from falling off during opening, and a smooth gripping sensation can be obtained.
次に、本実施形態のキャップ及びキャップ付きボトルを実際に作製し、開栓時におけるライナーの脱落について評価した。 Next, the cap of this embodiment and the bottle with the cap were actually produced, and the dropping of the liner at the time of opening was evaluated.
＜評価１＞
まず、ナールスリットの上部突起部の角度θを、０〜８７°の間で変化させて作製した際、開栓した金属キャップを目視評価して、ライナーが外れた上部突起部および下部突起部（以下、フックと称す）の数とボトルの数（以下、缶数と称す）とからフック外れ度数を調べ、良否判定を行った。
<Evaluation 1>
First, when the angle θ of the upper protrusion of the knurled slit was changed between 0 and 87 °, the opened metal cap was visually evaluated, and the upper protrusion and the lower protrusion with the liner removed ( Hereinafter, the hook removal frequency was examined from the number of hooks and the number of bottles (hereinafter referred to as the number of cans), and the quality was judged.
なお、上記フック外れ度数は、以下の数式により算出した。
フック外れ度数＝（外れたフックの数×缶数）÷評価缶数
例えば、評価した缶数が３０缶であり、２つの缶で２つのフックが外れ、３つの缶で３つのフックが外れ、さらに３つの缶で４つのフックが外れた場合、以下のように算出される。
（（２フック×２缶）＋（３フック×３缶）＋（４フック×３缶））÷評価缶数３０缶＝０．８３（フック外れ度数）
In addition, the said hook removal frequency was computed with the following numerical formula.
Hook removal frequency = (number of hooks removed × number of cans) ÷ number of cans For example, the number of cans evaluated is 30 cans, 2 hooks come off with 2 cans, 3 hooks come off with 3 cans, Further, when four hooks come off with three cans, the calculation is performed as follows.
((2 hooks x 2 cans) + (3 hooks x 3 cans) + (4 hooks x 3 cans)) / Evaluation cans 30 cans = 0.83 (hook removal frequency)
また、良否判定は、フック外れ度数が１．０以上の場合、ライナー脱落のリスクが有るとして「×」とし、フック外れ度数が０．４以上１．０未満の場合、ライナー脱落までに至らないが外観的不良となるおそれがあるとして「△」とし、フック外れ度数が０．４未満の場合、ライナー脱落の問題はないとして「○」とした。
なお、本実施例では、５℃の低温で各条件１００缶を評価した。その結果を表１に示す。
また、角度θは、Ｘ線によるフック断面を複数測定した平均値で求めた。
In addition, the pass / fail judgment is “X” because there is a risk of liner dropping when the hook removal frequency is 1.0 or more, and when the hook removal frequency is 0.4 or more and less than 1.0, the liner does not come off. “△” because there is a risk of appearance failure, and “◯” because there is no problem of liner dropping when the hook disengagement frequency is less than 0.4.
In this example, 100 cans were evaluated at a low temperature of 5 ° C. The results are shown in Table 1.
Further, the angle θ was determined by an average value obtained by measuring a plurality of hook cross sections by X-rays.
表１に示すように、ナールスリットの上部突起部の角度θが２８〜８２°の範囲ではフック外れ度数の良否判定で良好な結果が得られている。なお、角度θが８７°では、フック割れが生じたため、成型不良として評価していない。 As shown in Table 1, when the angle θ of the upper protrusion of the knurl slit is in the range of 28 to 82 °, good results are obtained in the determination of the hook removal frequency. Note that when the angle θ is 87 °, hook cracks have occurred, so that the molding failure is not evaluated.
＜評価２＞
次に、ライナーとナールスリットの上部突起部とのオーバーラップ寸法ａを、−０．５〜１．５２ｍｍの間で変化させた際、上記と同様にフック外れ度数を調べ、良否判定を行った結果を、表２に示す。
なお、ライナーとナールスリットの上部突起部とのオーバーラップ寸法ａがマイナスになる場合、すなわち、ナールスリット８の上部突起部８ａの先端が、ライナー９の外周縁よりも半径方向外方に位置している比較例について、図４および図５に示す。
また、オーバーラップ寸法ａは、Ｘ線によるフック断面を複数測定した平均値で求めた。
<Evaluation 2>
Next, when the overlap dimension a between the liner and the upper protrusion of the knurled slit was changed between -0.5 and 1.52 mm, the hook removal frequency was examined in the same manner as described above to determine whether or not it was good. The results are shown in Table 2.
When the overlap dimension a between the liner and the upper protrusion of the nar slit is negative, that is, the tip of the upper protrusion 8a of the nar slit 8 is positioned radially outward from the outer peripheral edge of the liner 9. The comparative example is shown in FIG. 4 and FIG.
In addition, the overlap dimension “a” was obtained as an average value obtained by measuring a plurality of hook cross sections by X-rays.
表２に示すように、オーバーラップ寸法ａが０．１０〜１．５２ｍｍまでフック外れ度数の良否判定で良好な結果が得られている。 As shown in Table 2, good results have been obtained in the quality determination of the hook removal frequency until the overlap dimension a is 0.10 to 1.52 mm.
なお、本発明の技術範囲は上記実施形態および実施例に限定されるものではなく、本発明の趣旨を逸脱しない範囲において種々の変更を加えることが可能である。 The technical scope of the present invention is not limited to the above-described embodiments and examples, and various modifications can be made without departing from the spirit of the present invention .
１…金属キャップ、２…天板部、３…円筒部、７…ナール凹部、８…ナールスリット（ベントホール）、８ａ…上部突起部、８ｂ…下部突起部、９…ライナー、９ａ…摺動層、９ｂ…密封層、１０…ＰＰキャップ、１１…ボトル本体、１２…口金部（口部）、１００…ボトル（キャップ付きボトル） DESCRIPTION OF SYMBOLS 1 ... Metal cap, 2 ... Top plate part, 3 ... Cylindrical part, 7 ... Knurl recess, 8 ... Knurl slit (vent hole), 8a ... Upper protrusion, 8b ... Lower protrusion, 9 ... Liner, 9a ... Sliding Layer, 9b ... sealing layer, 10 ... PP cap, 11 ... bottle body, 12 ... base part (mouth part), 100 ... bottle (bottle with cap)
Claims (4)
前記円筒部が、前記天板部近傍であって周方向にスリット状に開口形成され開栓時に内圧を開放するベントホールと、
該ベントホールの上部開口端部および下部開口端部を前記円筒部の半径方向内方に向けて曲げて形成した上部突起部および下部突起部と、を有し、
前記上部突起部の先端が、挿入された際の前記ライナーの外周縁よりも半径方向内方に位置されていると共に、前記下部突起部の先端と半径方向で同位置または該先端よりも半径方向外方に位置していることを特徴とする金属キャップ。 A top plate portion disposed above and a cylindrical portion substantially suspended from the periphery of the top plate portion, and after the liner is inserted into the inner surface of the top plate portion in a non-adhered state, the mouth portion of the bottle is A metal cap for sealing,
A vent hole that is formed in a slit shape in the circumferential direction in the vicinity of the top plate portion and opens the internal pressure when the cylindrical portion is opened;
An upper protrusion and a lower protrusion formed by bending the upper opening end and the lower opening end of the vent hole inward in the radial direction of the cylindrical portion;
The tip of the upper projection is positioned radially inward from the outer peripheral edge of the liner when inserted, and is the same position as the tip of the lower projection or in the radial direction, or more radially than the tip. A metal cap characterized by being located outward.
前記ライナーが、前記天板部の内面側に配された摺動層と、
前記挿入後にモールド成形によって前記摺動層に積層され前記摺動層よりも柔軟で外径の小さい密封層と、を備え、
前記上部突起部の先端が、挿入された際の前記ライナーの前記摺動層の外周縁よりも半径方向内方に位置し、
前記下部突起部の先端が、前記密封層の外周縁よりも半径方向外方に位置していることを特徴とする金属キャップ。 The metal cap according to claim 1,
The liner is a sliding layer disposed on the inner surface side of the top plate portion,
A sealing layer that is laminated to the sliding layer by molding after the insertion and is softer than the sliding layer and has a smaller outer diameter, and
The tip of the upper protrusion is located radially inward from the outer peripheral edge of the sliding layer of the liner when inserted.
The metal cap, wherein a tip of the lower protrusion is positioned radially outward from an outer peripheral edge of the sealing layer.
前記上部突起部の先端部が、さらに下方に折り曲げられて先端面が下方に向けられていることを特徴とする金属キャップ。 The metal cap according to claim 1 or 2,
A metal cap, wherein a tip portion of the upper protrusion is further bent downward and a tip surface is directed downward.
前記金属キャップが、請求項１から３のいずれか一項に記載の金属キャップであることを特徴とするキャップ付きボトル。 A bottle body, and a metal cap attached to the mouth of the bottle body,
The said metal cap is a metal cap as described in any one of Claim 1 to 3, The bottle with a cap characterized by the above-mentioned.