JP2014000106A - Hygienic mask and base material for the same - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a hygienic mask in which fuzz is prevented, coarse feeling is eliminated in wearing the hygienic mask, and which gives soft and smooth feeling, and provide a base material for the hygienic mask.SOLUTION: A nonwoven base material for a hygienic mask includes a laminate in which a plurality of nonwoven fabric sheets are laminated. A hygienic mask uses the nonwoven base material. The nonwoven fabric sheet of the laminate, which forms the most inner layer touching to skin, has the friction coefficient of 0.05-0.12 and a bending resistance of 45-60 mm, the bending resistance being prescribed in JIS L1096 (45° cantilever method).

Description

  The present invention relates to a sanitary mask using a nonwoven fabric as a material and a base material thereof.

  Hygiene masks used for hay fever prevention, cold prevention, etc., use various materials such as cotton, paper, and non-woven fabrics, but they can be manufactured at low cost and prevent invasion of splashes containing pollen and viruses. Sanitary masks using non-woven fabric as a raw material are widely used because they are excellent in air permeability.

  Such a sanitary mask using a nonwoven fabric as a raw material rubs the skin and the mask at the time of wearing, and the surface of the nonwoven fabric becomes fluffy when worn for a long time, and the texture due to the fluffing becomes worse.

  Then, as a thing which prevents the deterioration of the touch by fluffing, the sanitary mask which formed the inner surface of the nonwoven fabric sheet which contacts skin, for example in the smooth surface which prevented fluffing is provided (for example, refer patent document 1). .

JP 2004-41504 A

  The above-described sanitary mask described in Patent Document 1 is a method of smoothing the surface of the nonwoven fabric sheet, and the surface of the nonwoven fabric sheet is hardened by embossing or the like to form a smooth surface. In this case, the surface of the nonwoven fabric sheet is smoothed. Although it is possible, if the surface of the nonwoven fabric sheet is hardened too much by embossing or the like, the bulk of the nonwoven fabric sheet will be reduced and hardened. For this reason, there is a problem that the feeling of being worn out at the time of wearing becomes stronger and the feeling of wearing becomes worse. Thus, simply smoothing the surface of the nonwoven sheet in contact with the skin is not sufficient to obtain a good wearing feeling.

  SUMMARY OF THE INVENTION An object of the present invention is to provide a sanitary mask and a base material thereof that suppress fuzz, have no wrinkle feeling at the time of wearing, have a soft touch, and are smooth.

  As a result of intensive studies to solve the above-mentioned problems, the inventors have made the above-mentioned problems by making the nonwoven fabric sheet forming the innermost layer in contact with the skin of the sanitary mask a specific coefficient of friction and bending resistance. The present inventors have found that the problem can be solved and have completed the present invention.

  In order to achieve the above object, the nonwoven fabric substrate for sanitary mask according to claim 1 is a nonwoven fabric substrate for sanitary mask comprising a laminate in which a plurality of nonwoven fabric sheets are overlaid. The nonwoven fabric sheet forming the innermost layer on the side in contact with the skin has a friction coefficient of 0.05 to 0.12, and the bending resistance (45 ° cantilever method) specified in JIS L1096 is 45 to 60 mm. It is characterized by.

  The nonwoven fabric base material for sanitary masks according to claim 2 is characterized in that the nonwoven fabric sheet of the innermost layer according to claim 1 has a single fiber fineness of 1-10 decitex of nonwoven fabric fibers.

  The nonwoven fabric substrate for sanitary mask according to claim 3, wherein the nonwoven fabric sheet of the innermost layer according to claim 1 or 2 is a thermal bond nonwoven fabric comprising a core-sheath composite fiber having a core part made of polypropylene and a sheath part made of polyethylene. The fiber length of the nonwoven fabric fiber is 15 to 100 mm.

  The sanitary mask according to claim 4 is composed of a mask main body that covers the nose part and the mouth part, and ear hook parts provided on both side edges of the mask main body, and according to any one of claims 1 to 3. The sanitary mask nonwoven fabric base material is used for the mask body.

  The nonwoven fabric base material for sanitary masks of the present invention has a smooth surface of the nonwoven fabric sheet in contact with the skin by setting the friction coefficient of the nonwoven fabric sheet forming the innermost layer on the side in contact with the skin to 0.05 to 0.12. For this reason, the friction generated between the skin and the nonwoven fabric sheet is reduced, the fuzz caused by the friction between the skin and the nonwoven fabric sheet can be suppressed, and a smooth touch can be obtained. Further, by setting the bending resistance (45 ° cantilever method) specified in JIS L1096 within a range of 45 to 60 mm, there is no feeling of stiffness at the time of wearing, and a soft touch can be obtained.

  According to the sanitary mask of the present invention using such a sanitary mask nonwoven fabric substrate, the nonwoven fabric sheet forming the innermost layer on the side in contact with the skin is made to have a specific coefficient of friction and bending resistance, thereby fuzzing. In addition to being able to suppress, an excellent touch can be obtained, and an unprecedented good wearing feeling can be obtained.

  The nonwoven fabric base material for sanitary masks of the present invention comprises a laminate in which a plurality of nonwoven fabric sheets are superimposed. This embodiment demonstrates the case where the laminated body is formed with the nonwoven fabric sheet of 3 layers, an outermost layer, an intermediate | middle layer, and an innermost layer.

[Outermost layer]
The nonwoven fabric sheet of the outermost layer is made of a nonwoven fabric composed of polyolefin fibers or polyester fibers. As the polyolefin fiber or polyester fiber, the core part / sheath part is polypropylene (PP) / polyethylene (PE), polyethylene terephthalate (PET) / polyethylene (PE), polyethylene terephthalate (PET) / low melting point polyethylene terephthalate (PET). ), Or a core-sheath composite fiber such as polypropylene (PP) / polypropylene (PP), or regular fiber composed of PP alone or PET alone.

  As the nonwoven fabric sheet of the outermost layer, a spunbond nonwoven fabric, a thermal bond nonwoven fabric, a spunlace nonwoven fabric, an air-through nonwoven fabric, a melt blown nonwoven fabric, and a needle punched nonwoven fabric can be used. Preferably used.

The single yarn fineness of the nonwoven fabric fiber forming the outermost nonwoven fabric sheet is 1 to 10 dtex, more preferably 2 to 6 dtex. Outermost nonwoven sheet basis weight, production stability, in view of handling properties, 15~45g / ^{m 2,} more preferably from 20 to 40 g / ^{m 2.}

[Middle layer]
The non-woven fabric sheet of the intermediate layer is made of a non-woven fabric composed of polyolefin fibers or polyester fibers, like the non-woven fabric sheet of the outermost layer. As the polyolefin fiber or polyester fiber, the core part / sheath part is polypropylene (PP) / polyethylene (PE), polyethylene terephthalate (PET) / polyethylene (PE), polyethylene terephthalate (PET) / low melting point polyethylene terephthalate (PET). ), Or a core-sheath composite fiber such as polypropylene (PP) / polypropylene (PP), or regular fiber composed of PP alone or PET alone.

  As the intermediate layer nonwoven fabric sheet, a spunbond nonwoven fabric, a thermal bond nonwoven fabric, a spunlace nonwoven fabric, an air-through nonwoven fabric, a melt blown nonwoven fabric, or a needle punched nonwoven fabric can be used. Used for.

  Moreover, in order to improve the function which collects pollen and dust, it is preferable to use what was electret-ized as the nonwoven fabric sheet of an intermediate | middle layer. By using a non-woven sheet that has been electretized in the intermediate layer, fine pollen and dust can be efficiently collected. This electretization is achieved by running a non-woven fabric over a grounded electrode and applying a high voltage to the needle electrode or wire electrode from above to perform corona discharge.

When the melt blown nonwoven fabric is used for the nonwoven fabric sheet of the intermediate layer, the average fiber diameter of the nonwoven fabric fibers is 3 to 15 μm, more preferably 4 to 8 μm. Nonwoven sheet basis weight of the intermediate layer, production stability, in view of handling properties, 15~45g / ^{m 2,} more preferably from 20 to 40 g / ^{m 2.}

[Innermost layer]
The innermost nonwoven fabric sheet on the side in contact with the skin is made of a nonwoven fabric composed of polyolefin fibers or polyester fibers, similarly to the outermost layer and intermediate layer nonwoven fabric sheets. As the polyolefin fiber or polyester fiber, the core part / sheath part is polypropylene (PP) / polyethylene (PE), polyethylene terephthalate (PET) / polyethylene (PE), polyethylene terephthalate (PET) / low melting point polyethylene terephthalate (PET). ), Or a core-sheath composite fiber such as polypropylene (PP) / polypropylene (PP), or regular fiber composed of PP alone or PET alone.

  As the innermost layer nonwoven fabric sheet, a spunbond nonwoven fabric, a thermal bond nonwoven fabric, a spunlace nonwoven fabric, an air-through nonwoven fabric, a melt blown nonwoven fabric, and a needle punched nonwoven fabric can be used. .

  When the thermal bond nonwoven fabric is used for the innermost nonwoven fabric sheet, the fiber length of the nonwoven fabric fiber is 15 to 100 mm, more preferably 38 to 64 mm. If the fiber length of the nonwoven fabric fiber is less than 15 mm, it will be difficult to open the raw material fibers, and the productivity will deteriorate. On the other hand, when it exceeds 100 mm, it becomes difficult to produce a nonwoven fabric having a uniform fiber density.

  The single yarn fineness of the nonwoven fabric fiber forming the innermost nonwoven fabric sheet is 1 to 10 dtex, more preferably 1.5 to 3 dtex. When the single yarn fineness of the nonwoven fabric fiber is less than 1 dtex, the production becomes difficult. On the other hand, if it exceeds 10 dtex, the texture becomes hard and the touch becomes poor.

The basis weight of the innermost nonwoven fabric sheet is 15 to 100 g / m ² , more preferably 20 to 40 g / m ² . When the basis weight of the innermost nonwoven fabric sheet is less than 15 g / m ² , the shape retention becomes low, and the breathing during wearing deforms and causes discomfort. On the other hand, when it exceeds 100 g / m 2, the texture becomes hard and the touch becomes poor.

  The innermost nonwoven fabric sheet has a coefficient of friction (MIU) on the surface in contact with the skin of 0.05 to 0.12, more preferably 0.10 to 0.15. When the coefficient of friction (MIU) is less than 0.05, slipping occurs during production, the defect occurrence rate increases, and the yield decreases. On the other hand, when it exceeds 0.12, the smoothness is deteriorated and fuzzing is likely to occur. Moreover, a smooth touch cannot be obtained and a good wearing feeling cannot be obtained. The friction coefficient (MIU) in the present invention was measured using a surface friction test apparatus (KES-FB4) manufactured by Kato Tech Co., Ltd., and an average friction coefficient was obtained. The measuring method will be described in detail in Examples.

  The innermost nonwoven fabric sheet has a bending resistance (45 ° cantilever method) specified in JIS L1096 of 35 to 60 mm, more preferably 40 to 55 mm. When the bending resistance exceeds 60 mm, the flexibility is lost, the feeling of being irritated at the time of wearing becomes stronger, and the touch becomes worse. On the other hand, if the bending resistance is less than 35 mm, the shape retaining property is low, and the breathing during wearing deforms and causes discomfort. The bending resistance in the present invention was measured in the vertical (MD) direction (conveying direction of the nonwoven fabric sheet) by JIS L1096 8.21.1A method (45 ° cantilever method).

  The sanitary mask of the present invention is composed of a mask main body that covers the nose and mouth and ear hooks provided on both side edges of the mask main body, and the above-mentioned sanitary mask nonwoven fabric substrate is used for the mask main body. It is characterized by.

  The shape of the sanitary mask is not particularly limited. For example, the mask main body may be provided with pleats extending in the vertical direction, and when worn, the pleats may be expanded in the vertical direction so that the mask main body has a mountain-shaped three-dimensional shape. Alternatively, the mask main body may be a three-dimensional shape that has a flat shape that is folded in two from the center in the state before use, and a three-dimensional shape that swells forward in the use state.

  Hereinafter, the present invention will be described with reference to examples, but the present invention is not limited to the following examples. The test methods commonly used in the examples and comparative examples are as follows.

(1) Basis weight A test piece of 100 × 100 mm was taken from the sample length direction, the weight in a horizontal equilibrium state was measured, and calculated per 1 m ² .

(2) Coefficient of friction The sample is cut into a vertical (MD direction) 20 cm x horizontal (CD direction) 20 cm, and the sample is attached to a KES surface test apparatus (KES-FB4: manufactured by Kato Tech Co., Ltd.) with a predetermined load, and friction is applied. The sample was set on the child so that the friction direction was vertical, and MIU (friction coefficient) was measured under standard measurement conditions (sample tension: 400 g, surface measurement sample moving speed: 1 mm / sec, initial load: 50 g). The vertical (MD) direction is measured three times, and the average is shown. A smaller value means less frictional resistance.

(3) Bending softness The bending softness in the vertical (MD) direction was measured by JIS L1096 8.21.1A method (45 ° cantilever method).

(4) Sensory evaluation While feeling (feel) when wearing a sanitary mask was subjected to sensory evaluation from the viewpoint of smoothness and softness, sensory evaluation was also performed on the overall wearing feeling. The evaluation was performed by 10 panelists and judged according to the following criteria. The most popular opinion is taken as the evaluation result, and the result is shown in Table 1.
1. About “smoothness” ◎: There is a very smooth feeling.
○: There is a smooth feeling.
(Triangle | delta): There is little smooth feeling and there exists a rough feeling.
X: There is no smooth feeling and the feeling of roughness is strong.
2. About “softness” ◎: There is a very soft feeling.
○: There is a soft feeling.
Δ: Little soft feeling and stiff feeling.
X: There is no soft feeling and a strong feeling of stickiness.
3. About “wearing feeling” ◎: Very good.
○: Good.
Δ: Neither can be said.
X: Bad.

[Example 1]
A pleated sanitary mask was prepared using a sanitary mask nonwoven fabric base material in which the following nonwoven fabric sheet was laminated on three layers of an outermost layer, an intermediate layer, and an innermost layer.
As the outermost layer, a nonwoven fabric sheet having a basis weight of 28 g / m ² produced by a spunbond method using polypropylene (PP) single fiber was used.
As the intermediate layer, a polypropylene (PP) single fiber was used, and a nonwoven fabric sheet having a basis weight of 25 g / m ² produced by a melt blow method was used.
The innermost layer uses a polypropylene (PP) / polyethylene (PE) core-sheath composite fiber having a single yarn fineness of 2.2 dtex and a fiber length of 51 mm, and a basis weight of 25 g / m ² produced by a thermal bond method. Non-woven fabric sheet (friction coefficient of surface contact surface 0.107, bending resistance 50 mm) was used.

[Comparative Example 1]
As the innermost layer, a polypropylene (PP) / polyethylene (PE) core-sheath composite fiber having a single yarn fineness of 6.6 dtex and a fiber length of 64 mm was used, and the basis weight produced by the thermal bond method was 27 g / m ^2. Non-woven fabric sheet (the coefficient of friction of the surface in contact with the skin is 0.125, the bending resistance is 84 mm).
Other than that was carried out similarly to Example 1, and produced the sanitary mask.

[Comparative Example 2]
The innermost layer has a single yarn fineness of 6.6 dtex, a fiber (polypropylene (PP) / polyethylene (PE) core-sheath composite fiber having a fiber length of 64 mm) and a single yarn fineness of 20 dtex, and a fiber. A non-woven fabric sheet having a basis weight of 27 g / m ² prepared by a thermal bond method mixed with 50% by weight of a polypropylene (PP) / polyethylene (PE) core-sheath composite fiber having a length of 64 mm (friction of the surface in contact with the skin) A coefficient of 0.133 and a bending resistance of 71 mm) were used.
Other than that was carried out similarly to Example 1, and produced the sanitary mask.

[Comparative Example 3]
As the innermost layer, a nonwoven fabric sheet (smooth roll / 130 ° C.) pressed on the surface of the innermost nonwoven fabric sheet used in Example 1 with a heat calender roll (coefficient of friction of the surface in contact with the skin 0.087, bending resistance 70 mm) Was used.
Other than that was carried out similarly to Example 1, and produced the sanitary mask.

[Comparative Example 4]
As the innermost layer, a basis weight produced by a thermal bond method using a polypropylene (PP) / polyethylene (PE) core-sheath composite fiber having a single yarn fineness of 2.2 dtex and a fiber length of 51 mm is 50 g / m ^2. Non-woven fabric sheet (friction coefficient of surface contact surface 0.107, bending resistance 50 mm) was used.
Other than that was carried out similarly to Example 1, and produced the sanitary mask.

  As is apparent from the results shown in Table 1, it can be seen that the sanitary mask of Example 1 has good smoothness and softness, and is also good in wearing feeling. Although not shown in the table, it was confirmed that the sanitary mask of Example 1 after wearing had almost no fuzz on the innermost nonwoven fabric sheet surface.

  In contrast, the sanitary masks of Comparative Examples 1 and 2 are not smooth and soft, and a good wearing feeling cannot be obtained. Moreover, although the sanitary masks of Comparative Examples 3 and 4 have smoothness, they do not have softness and are stiff, so that a good wearing feeling cannot be obtained.

The innermost layer of non-woven fabric sheet of basis weight, 15~100g / ^{m 2,} is good RiYoshimi Mashiku is 20~40g / ^{m 2.} When the basis weight of the innermost nonwoven fabric sheet is less than 15 g / m ² , the shape retention becomes low, and the breathing during wearing deforms and causes discomfort. On the other hand, when it exceeds 100 g / m 2, the texture becomes hard and the touch becomes poor.

The innermost nonwoven fabric sheet has a coefficient of friction (MIU) on the surface in contact with the skin of 0.05 to 0.12, more preferably 0.8. 08 to 0.1 is preferably a 2. When the coefficient of friction (MIU) is less than 0.05, slipping occurs during production, the defect occurrence rate increases, and the yield decreases. On the other hand, when it exceeds 0.12, the smoothness is deteriorated and fuzzing is likely to occur. Moreover, a smooth touch cannot be obtained and a good wearing feeling cannot be obtained. The friction coefficient (MIU) in the present invention was measured using a surface friction test apparatus (KES-FB4) manufactured by Kato Tech Co., Ltd., and an average friction coefficient was obtained. The measuring method will be described in detail in Examples.

Claims (4)

A sanitary mask nonwoven fabric substrate comprising a laminate in which a plurality of nonwoven fabric sheets are overlaid,
The nonwoven fabric sheet forming the innermost layer on the side in contact with the skin of the laminate has a friction coefficient of 0.05 to 0.12 and a bending resistance (45 ° cantilever method) defined in JIS L1096 is 45. A nonwoven fabric base material for sanitary mask, characterized in that it is -60 mm.   2. The sanitary mask nonwoven fabric substrate according to claim 1, wherein the innermost nonwoven fabric sheet has a single fiber fineness of 1 to 10 dtex.   The innermost nonwoven fabric sheet is a thermal bond nonwoven fabric composed of a core-sheath composite fiber having a core part made of polypropylene and a sheath part made of polyethylene, and the fiber length of the nonwoven fabric fiber is 15 to 100 mm. The nonwoven fabric base material for sanitary masks of 2. In a sanitary mask composed of a mask body covering the nose and mouth and ear hooks provided on both side edges of the mask body,
A sanitary mask, wherein the sanitary mask nonwoven fabric substrate according to any one of claims 1 to 3 is used for the mask body.