JP6143972B2 - mask - Google Patents

Description

  The present invention relates to a mask that can be worn comfortably for a long time with greatly improved wearing comfort.

  Opportunities to wear masks are increasing to prevent hay fever, prevent viruses, and prevent colds. In addition to this situation, masks having various functions have been proposed.

For example, as a three-dimensional mask having comfort, a mask has been proposed in which a non-woven fabric containing a specific amount of regenerated cellulose fiber is used in the inner layer portion, thereby eliminating the stuffiness of the space in the mask (see Patent Document 1). .
Further, as a mask having a function of inactivating allergens and viruses, a mask that is easy to breathe when worn by providing a filtration layer and an enzyme layer having a specific basis weight has been proposed (see Patent Document 2).
Furthermore, as a mask that can improve the feeling of wearing, a mask is proposed in which the surface on the side in contact with the wearer's face is made of a specific moisture-permeable material (see Patent Document 3).

JP 2007-000276 A JP 2011-103924 A JP 2011-072479 A

The above-mentioned patent document discloses a mask that can easily breathe when worn and does not feel stuffy, that is, can improve the wearing feeling.
On the other hand, the functions required of masks are diversified because of increasing opportunities for wearing masks. It is an object of the present invention to provide a mask having a significantly improved wearing comfort by focusing on “wearing comfort” as one of the functions required for the mask.

  The present inventors diligently studied to solve the above-mentioned problems, and obtained the knowledge that the compression characteristic of the mask body is important as a factor necessary for improving the wearing comfort. And in order to provide a specific compression characteristic to a mask main body, it discovered that the said subject could be solved by providing a buffer layer in the intermediate | middle layer of a mask, and completed this invention.

The present invention is a non-woven mask having a mask body covering at least a part of the user's face, and a pair of ear hooks provided on both sides of the mask body,
The mask body has a multilayer structure having at least an outermost layer, an intermediate layer, and a mouthpiece layer,
The intermediate layer is at least selected from polyester fibers, polypropylene fibers, rayon fibers, acrylate fibers, nylon fibers, acetate fibers, wool fibers, cotton fibers, urethane fibers, and polyethylene fibers. Including a buffer layer made of a nonwoven fabric containing one or more kinds,
The mask body is a non-woven mask having a compression property WC measured by a KES system of 0.5 to 2.0 gf · cm / cm ² .

The buffer layer is preferably made of a nonwoven fabric having a basis weight of 30 g / m ² or more, and is preferably a needle punched nonwoven fabric.
The mask body preferably has a thickness of 1.0 mm or more, and the mouthpiece layer is preferably made of a nonwoven fabric using fibers having an official moisture content of 1% or more.
Moreover, it is preferable that the intermediate layer further includes one or more collection filters, and the mouthpiece layer and the buffer layer are arranged adjacent to each other.

  According to the present invention, a nonwoven fabric mask is provided in which the feeling of wearing is greatly improved without reducing the feeling of wearing such as breathlessness and stuffiness.

It is a front view of the mask concerning one embodiment. It is a schematic diagram which shows the layer structure of the mask main body in the AA cross section of FIG. It is a graph explaining the compression characteristic in a KES test.

  Hereinafter, the present invention will be described in detail by exemplifying specific embodiments. In addition, this invention is not limited to the content demonstrated below, In the range which does not change the summary, it can change arbitrarily and can implement. In addition, the drawings used for the description all schematically show the nonwoven fabric mask according to the present invention, and may not accurately represent the scale and shape of each component.

The mask according to the present invention is a non-woven mask having a mask main body that covers at least a part of the user's face, and a pair of ear hooks provided on both sides of the mask main body. One embodiment of a mask according to the present invention is shown in FIG.
A mask 10 shown in FIG. 1 has a mask body 1 and a pair of ear hooks 2 provided on both sides of the mask body 1. The mask 10 is a pleated mask and has pleats formed from a plurality of lateral folds in the drawing. In FIG. 1, a box fold (box pleat) is provided in the center of the mask body 1 along the left-right direction, two upward car folds (one-way pleats) above the center box fold, and a downward direction. Two downward car folds are provided. Therefore, when the mask 10 is not worn, the mask body 1 is folded into a substantially planar shape so as not to be bulky, and is configured to have a three-dimensional shape that bulges outward when the mask body 1 is unfolded when worn. .
In FIG. 1, one box fold, two upward car folds, and two downward car folds are formed. In the present invention, however, the pleated shape is 0-3 independently of the box fold in the center of the mask. One wheel fold may be formed, and preferably one or two vehicle folds are formed. In addition, the mask according to the present invention may be composed of vehicle folds, and in that case, 1 to 6 vehicle folds may be formed in the left-right direction of the mask body 1.

Further, a nose fitter may be provided on the upper side portion of the mask body 1, and for example, a metal thin plate, a polyethylene thin plate, or a polypropylene thin plate can be used as the nose fitter.
Furthermore, a mouse bar may be provided in the central portion of the mask body 1 to maintain the mask shape when worn, and the same material as that usable for the nose fitter can be applied.
The mask according to the present invention may be a flat mask that is not pleated.

The mask body is a multilayer structure having at least an outermost layer, an intermediate layer, and a mouthpiece layer.
As an intermediate | middle layer, a buffer layer is included at least and you may have a collection filter, an antibacterial filter, etc. besides this. An example of the layer structure is shown in FIG.
FIG. 2 is a schematic diagram showing the layer structure of the mask body in the cross section taken along the line AA in FIG. 1. From the right face side in the figure, the mouthpiece layer 6, the buffer layer 5, the two filter layers 4, and the outermost layer. It has a configuration in which the outer layer 3 is laminated in order. In the present invention, other layers may be included, the filter layer may be omitted, or the number of layers may be changed.

The mask body has a compression characteristic WC (gf · cm / cm ² ) measured by the KES system of 0.5 or more. The inventors of the present invention have reached that the mask main body can have such a compression characteristic to achieve a mask that is comfortable to wear. The compression property WC (gf · cm / cm ² ) is preferably 0.6 or more, more preferably 0.7 or more, still more preferably 0.8 or more, and 0.85 or more. It is particularly preferred. On the other hand, if the compression property WC is too high, it tends to cause stuffiness and breathlessness in the mouth, and the feeling of use tends to decrease, so it is usually 2.0 or less, preferably 1.8 or less. It is more preferably 6 or less, and further preferably 1.5 or less.

Further, the initial thickness T ₀ (mm) for calculating the compression characteristic WC, also measured by the KES system, is preferably 1.0 or more, more preferably 1.2 or more, and 1.4 More preferably, it is more preferably 1.6 or more. On the other hand, the upper limit is not particularly limited, but is usually 4.0 or less, preferably 3.5 or less, more preferably 3.0 or less, still more preferably 2.8 or less. Particularly preferred is 5 or less.
In addition, the thickness T _M (mm) at the time of maximum compression for calculating the compression characteristic WC, which is also measured by the KES system, is preferably 0.4 or more, and more preferably 0.5 or more. And more preferably 0.6 or more. On the other hand, the upper limit is usually 1.2 or less, preferably 1.0 or less, more preferably 0.8 or less, still more preferably 0.75 or less, and 0.7 or less. Is particularly preferred.
When T ₀ and T _M when calculating the compression characteristic WC are in the above range, it is easy to adjust the compression characteristic WC, which is a means for achieving the wearing comfort realized by the mask according to the present invention, to the above range. Become. Note that T ₀ represents the thickness of the mask body.

In the present invention, the compression characteristics WC, T ₀ , and T _M can be measured by the following method. For example, the compression characteristics can be measured by “Kamio Kawabata, Textile Engineering Journal (Textile Engineering) Vol. 33 No. 2 (1980) (hereinafter also referred to as Reference Document 1) ”.
For example, KESFB3-AUTO-A automated compression tester manufactured by Kato Tech Co., Ltd. can be used as the measuring instrument used for the measurement. However, the measuring instrument is other than this, and the measuring method described in the above Reference 1 is realized. A measuring instrument that can be used may be used. When KESFB3-AUTO-A is used, the area of the pressure plate to the nonwoven fabric is 2.0 cm ² , the compression deformation rate is 0.02 mm / sec, and the maximum compression load is 50 gf / cm ² .
Note that when measuring the compression of the mask body, if the mask is a pleated mask, measurement is performed in a state where the mask is expanded, that is, in a state where each layer is laminated one by one.

FIG. 3 shows a graph for measuring and calculating the compression characteristic WC.
In FIG. 3, the y-axis direction (vertical axis direction) indicates the pressure P (gf / cm ² ) applied to the nonwoven fabric, and the x-axis direction (horizontal axis direction) in the drawing indicates the thickness T (mm) of the nonwoven fabric.
In FIG. 3, B on the x-axis shows the thickness T ₀ of the nonwoven fabric when the pressure P is 0, and C on the x-axis in the figure is the nonwoven fabric when the pressure P is 50 gf / cm ² which is the maximum compressive load. The thickness _TM is shown. WC is calculated as an integral value of P when T is T ₀ to T _M , that is, an area of a + b in the figure.

On the other hand, of the two curves in FIG. 3, the curve with the larger P value (the curve located in the upper part in the figure) shows the movement of the thickness T when a compressive load is applied to the nonwoven fabric. The curve with the smaller value (the curve located in the lower part of the figure) shows the movement of the thickness T when releasing the compressive load from the nonwoven fabric. In addition to the WC, the compression characteristics include LC indicating compression strength and RC indicating compression recovery, and are defined as follows.
LC: (a + b area) / ΔABC area RC: b area / (a + b area)
In the present invention, it has been found that, among these compression characteristics, when the compression characteristic WC satisfies a specific range, the wearing comfort of the mask is dramatically improved.

In order for the mask body to satisfy the compression characteristics, it is necessary to include at least a buffer layer in the intermediate layer of the mask.
The buffer layer is at least one selected from polyester fibers, polypropylene fibers, rayon fibers, acrylate fibers, nylon fibers, acetate fibers, wool fibers, cotton fibers, urethane fibers, and polyethylene fibers. It may be a non-woven fabric comprising one or more species, and may be a non-woven fabric comprising one type of fiber or a mixed non-woven fabric comprising two or more types of fibers.
As a mixed nonwoven fabric composed of two or more kinds of fibers, for example, a mixed nonwoven fabric of acrylate fibers and polypropylene fibers, a mixed nonwoven fabric of acrylate fibers and polyester fibers, a mixed nonwoven fabric of rayon fibers and polypropylene fibers, etc. From the viewpoint of improving the hygroscopic performance, it is preferable to include an acrylate fiber.
The acrylate fiber used in the present invention is preferably a fiber obtained by introducing a metal salt carboxyl group into the acrylate fiber by introduction and hydrolysis of a hydrazine compound and by neutralization if necessary. . Examples of such cross-linked polyacrylate fibers are “Ex (registered trademark)”, “Moiscare (registered trademark)”, “Dismel (registered trademark)”, “Etiquette” manufactured by Toyobo Co., Ltd. (Registered trademark) "," mois fine (registered trademark) "and the like.

In the present invention, it is preferable to use a nonwoven fabric with a large basis weight as the nonwoven fabric constituting the buffer layer, preferably 30 g / m ² or more, more preferably 40 g / m ² or more, and 45 g / m ² or more. It is more preferable that it is 50 g / m ² or more. The upper limit is usually 80 g / m ² or less, and preferably 70 g / m ² or less. By using a non-woven fabric having a large basis weight as described above, a mask main body with greatly improved wearing comfort can be obtained.
In general, a non-woven fabric having a basis weight of about 20 g / m ² is used in order to prevent stuffiness and breathlessness in consideration of wearing feeling. In the present invention, it has been found that the wearing comfort is greatly improved by employing a non-woven fabric having a basis weight which is not normally used for a mask.

  Moreover, it is preferable that the thickness of a buffer layer is 0.3 mm or more, and it is more preferable that it is 0.6 mm or more. Moreover, it is 1.5 mm or less normally, More preferably, it is 1.0 mm or less. Here, the measuring method of thickness shall follow the JIS L 1913A method (constant pressure of 0.5 kPa).

The buffer layer has a compression characteristic WC (gf · cm / cm ² ) measured by the KES system of usually 0.4 or more, preferably 0.5 or more, and preferably 0.6 or more. Is more preferably 0.7 or more, and particularly preferably 0.8 or more. Moreover, it is 2.0 or less normally, it is preferable that it is 1.8 or less, it is more preferable that it is 1.6 or less, and it is still more preferable that it is 1.5 or less. By setting the compression characteristic WC of the buffer layer within the above range, the compression characteristic WC of the mask body can be easily set within a desired range.
In order to set the compression characteristic WC of the buffer layer in the above range, it can be achieved by increasing the basis weight of the nonwoven fabric constituting the buffer layer or increasing the thickness of the buffer layer.

  The nonwoven fabric which comprises a buffer layer can be manufactured by a known manufacturing method. Specifically, spun bond, thermal bond, spun lace, air through, melt blow, needle punch, etc. are applied. In the present invention, a nonwoven fabric produced by needle punching or air-through is preferably applied. By adopting a nonwoven fabric manufactured by needle punching or air-through for the buffer layer, it becomes easy to adjust the thickness to a preferable value while suppressing an excessive increase in the compression characteristic WC. Moreover, since the nonwoven fabric manufactured with a needle punch is bulky and fluffy, it is easy to make it soft and soft, and it is most preferable to use a nonwoven fabric manufactured with a needle punch for the buffer layer of the present invention. In addition, the buffer layer may be a single layer or two or more layers of non-woven fabric manufactured by a single manufacturing method, and further laminated or bonded each non-woven fabric manufactured by a plurality of manufacturing methods May be used. Furthermore, the buffer layer of the present invention may be formed integrally with the mouthpiece layer and / or the outermost layer.

  In the present invention, the nonwoven fabric of the outermost layer is not particularly limited, and generally known fibers can be used as a mask material. Specific examples include polyester fibers, polypropylene fibers, rayon fibers, nylon fibers, acrylate fibers, acetate fibers, wool fibers, cotton fibers, urethane fibers, and polyethylene fibers. The nonwoven fabric which consists of these 1 type of fibers may be sufficient, and the mixed nonwoven fabric which consists of 2 or more types of fibers may be sufficient.

Among these, it is preferable to use a fiber having an official moisture content of 1% or more. Examples of fibers having an official moisture content of 1% or more include rayon fibers, nylon fibers, acrylate fibers, acetate fibers, wool fibers, and cotton fibers, and nylon fibers are particularly preferable. The official moisture content means the moisture content of the fiber in an environment of 20 ° C. and 60% RH.
The basis weight of the outermost nonwoven fabric is preferably 40 g / m ² or less, more preferably 35 g / m ² or less, and further preferably 30 g / m ² or less. On the other hand, it is preferably 10 g / m ² or more, and more preferably 15 g / m ² or more.

  In the present invention, the nonwoven fabric of the mouthpiece layer is not particularly limited, and generally known fibers can be used as a mask material. Specific examples include polyester fibers, polypropylene fibers, rayon fibers, nylon fibers, acrylate fibers, acetate fibers, wool fibers, cotton fibers, urethane fibers, and polyethylene fibers. The nonwoven fabric which consists of these 1 type of fibers may be sufficient, and the mixed nonwoven fabric which consists of 2 or more types of fibers may be sufficient.

Among these, it is preferable to use a fiber having an official moisture content of 1% or more. Examples of fibers having an official moisture content of 1% or more include rayon fibers, nylon fibers, acrylate fibers, acetate fibers, wool fibers, and cotton fibers, and nylon fibers are particularly preferable. By adopting non-woven fabrics using fibers with an official moisture content of 1% or higher, such as nylon fibers, the moisture content is higher than the materials such as polypropylene and polyethylene used for the mask layer of general masks. Since the fibers become softer and the fibers are softer, the wearing comfort tends to be improved.
The basis weight of the nonwoven fabric of the mouthpiece layer is preferably 40 g / m ² or less, more preferably 30 g / m ² or less, and still more preferably 20 g / m ² or less. On the other hand, it is preferably 5 g / m ² or more, and more preferably 10 g / m ² or more.
Moreover, it is preferable to use a thin fiber as the nonwoven fabric constituting the mouthpiece layer. Specifically, the average fiber diameter is preferably 18 μm or less, and more preferably 15 μm or less. By using a non-woven fabric with fine fibers in this way, it is possible to obtain a mask body that is softer and has much improved comfort.
Further, the nonwoven fabric of the mouthpiece layer is preferably thin, and the specific thickness is preferably 0.2 mm or less, and more preferably 0.15 mm or less.

In the present invention, a filter layer may be provided as an intermediate layer. The filter layer is a non-woven fabric made of fine fibers so as to collect fine particles such as pollen, dust and viruses. Examples of the fibers used include polyester fibers, polypropylene fibers, and polyethylene fibers.
Although a known method is used as a method for producing the filter layer, it is preferably produced by a melt blown method.
The basis weight of the nonwoven fabric used for the filter layer is preferably 40 g / m ² or less, more preferably 30 g / m ² or less, still more preferably 20 g / m ² or less, and 15 g / m ² or less. Most preferably it is. On the other hand, the lower limit is preferably 5 g / m ² or more, and more preferably 10 g / m ² or more.
The filter layer may have only one layer or two or more layers, but preferably has two or more layers from the viewpoint of stabilizing the collection efficiency of the fine particles.

  In the present invention, the mask body has a multilayer structure having an intermediate layer between the outermost layer and the mouthpiece layer. Any layer structure may be used as long as it has a buffer layer as an intermediate layer, but it is preferable that the mouthpiece layer and the buffer layer are adjacent to each other in order to improve the wearing comfort of the mask.

The total basis weight of the nonwoven fabric used for the mask body of the present invention is preferably 150 g / m ² or less, more preferably 140 g / m ² or less, and further preferably 130 g / m ² or more. On the other hand, it is preferably 85 g / m ² or more, more preferably 90 g / m ² or more, and further preferably 100 g / m ² or more.

  The mask manufacturing method according to the present invention is not particularly limited, and can be manufactured according to a known method. For example, a mask body is manufactured by overlaying nonwoven fabrics constituting the outermost layer, the filter layer, the buffer layer, and the mouthpiece layer, and subjected to pleating as necessary, so that an ear strap, a nose fitter, and / or a mouse bar It is completed through known and common processes such as installation.

  EXAMPLES Hereinafter, although an Example demonstrates this invention further in detail, it cannot be overemphasized that this invention is not limited only to embodiment of these Examples.

<Example 1>
Nylon nonwoven fabric (thickness: 0.18 mm) having a basis weight of 30 g / m ² as the outermost layer,
Two layers of polypropylene nonwoven fabric having a basis weight of 10 g / m ² as a filter layer (each thickness: 0.18 mm),
Mixed nonwoven fabric having a basis weight of 55 g / m ² and a thickness of 0.70 mm as a buffer layer (nonwoven fabric having a surface layer of a spunbond nonwoven fabric made of polyester and a back layer of a needle punched nonwoven fabric made of acrylate fibers and polyester fibers),
Nylon nonwoven fabric having a basis weight of 20 g / m ² , a thickness of 0.14 mm, and an average fiber diameter of 14.4 μm,
And a mask having a five-layer structure (thickness: 1.1 mm, total weight: 125 g / m ² ) laminated in this order according to a conventional method was produced.
In addition, the thickness of a nonwoven fabric and a mask is the value measured according to JISL1913A method (constant pressure of 0.5 kPa). Moreover, an average fiber diameter is an average value of the value (n = 50) which measured the diameter from the side of the fiber under the optical microscope using the digital microscope (VHX-1000 / VH-Z75) by Keyence Corporation. .

<Comparative Example 1>
Polypropylene nonwoven fabric (thickness: 0.23 mm) having a basis weight of 25 g / m ² as the outermost layer,
As an intermediate layer, a polypropylene nonwoven fabric having a basis weight of 18 g / m ² ,
Two layers of polypropylene nonwoven fabric having a basis weight of 10 g / m ² as a filter layer (each thickness: 0.18 mm),
A polypropylene nonwoven fabric having a basis weight of 18 g / m ² , a thickness of 0.2 mm, and an average fiber diameter of 19.3 μm was prepared as a mouthpiece layer, and a mask having a five-layer structure (thickness: 0.85 mm, total) The basis weight was 81 g / m ² ). The measurement conditions for the thickness of the nonwoven fabric and the average fiber diameter are the same as in Example 1.

<Comparative example 2>
A commercially available mask (A company mask, purchased in April 2015) was used. The nonwoven fabric used in this mask was divided into layers, and the basis weight of each layer and the thickness of the mouthpiece layer were measured,
Outer layer: basis weight 31 g / m ² and thickness 0.3 mm,
Filter layer: basis weight 27 g / m ² and thickness 0.17 mm,
Mouth layer: 25 g / m ² per unit area and 0.25 mm thickness,
The total basis weight of this three-layer structure mask was 83 g / m ² .
The thickness of the nonwoven fabric was measured under the same conditions as in Example 1.

<Comparative Example 3>
A commercially available mask (B company mask, obtained in April 2015) was used. The nonwoven fabric used in this mask was divided into layers, and the basis weight of each layer and the thickness and average fiber diameter of the mouthpiece layer were measured,
Outer layer: basis weight 29 g / m ² and thickness 0.29 mm,
Filter layer: basis weight 19 g / m ² and thickness 0.18 mm,
Mouth layer: basis weight 33 g / m ² , thickness 0.30 mm, average fiber diameter 16.6 μm,
The total basis weight of this three-layer structure mask was 81 g / m ² .
The thickness and average fiber diameter of the nonwoven fabric were measured under the same conditions as in Example 1.

<Comparative example 4>
A mask having a four-layer structure according to Comparative Example 4 (thickness: 1.1 mm, total basis weight: 70 g / m ² ) obtained by removing the buffer layer from the mask of Example 1 was used. The measurement conditions for the thickness of the nonwoven fabric and the average fiber diameter are the same as in Example 1.

<Example 2>
In the mask of Example 1, the buffer layer has a basis weight of 55 g / m ² and a mixed nonwoven fabric having a thickness of 0.93 mm (a surface layer of a spunbond nonwoven fabric made of polyester and a backing layer of a needle punched nonwoven fabric made of rayon fiber and polyester fiber) A mask (thickness: 1.5 mm, total basis weight: 125 g / m ² ) having a five-layer structure according to Example 2 was manufactured. The measurement conditions for the thickness of the nonwoven fabric and the average fiber diameter are the same as in Example 1.

<Example 3>
In the mask of Example 1, the buffer layer has a basis weight of 55 g / m ² and a mixed nonwoven fabric having a thickness of 1.4 mm (a surface layer of a spunbond nonwoven fabric made of polyester and a back layer of a needle punched nonwoven fabric made of acrylic fiber and polyester fiber) The mask (thickness: 1.9 mm, total basis weight: 125 g / m ² ) having a five-layer structure according to Example 3 was manufactured. The measurement conditions for the thickness of the nonwoven fabric and the average fiber diameter are the same as in Example 1.

<Example 4>
The mask of Example 1 has a five-layer structure according to Example 4 using a mixed nonwoven fabric (air-through polyester, polyethylene and polypropylene mixed nonwoven fabric) having a buffer layer weight of 35 g / m ² and a thickness of 0.81 mm. A mask (thickness: 1.3 mm, total weight: 105 g / m ² ) was manufactured. The measurement conditions for the thickness of the nonwoven fabric and the average fiber diameter are the same as in Example 1.

<Example 5>
In the mask of Example 1, a buffer layer is disposed at a position adjacent to the outermost layer (outermost layer → buffer layer → filter layer 2 layer → mouth layer), and a mask having a five-layer structure according to Example 5 ( Thickness: 1.1 mm, total weight: 125 g / m ² ) was manufactured. The measurement conditions for the thickness of the nonwoven fabric and the average fiber diameter are the same as in Example 1.

<Example 6>
A mask having a three-layer structure according to Example 6 (thickness: 0.95 mm, total basis weight: 105 g / m ² ) obtained by removing the two filter layers from the mask of Example 1 was used. The measurement conditions for the thickness of the nonwoven fabric and the average fiber diameter are the same as in Example 1.

<Evaluation of buffer layer, mouthpiece layer and mask compression characteristics>
The compression characteristics of the masks according to Examples and Comparative Examples were evaluated. In addition, the compression characteristics of the buffer layers of Examples 1 to 6 and the compression characteristics of the mouthpiece layers of Comparative Examples 2 and 3 were evaluated. The compression property evaluation was performed using a KESFB3-AUTO-A automated compression tester manufactured by Kato Tech Co., Ltd. The area of the pressure plate to the nonwoven fabric was 2.0 cm ² , the compression deformation rate was 0.02 mm / sec, and the maximum compression load was evaluated at 50 gf / cm ² .
Compression characteristics _WC, LC, RC, the measurement results of the T 0, _{T M} shown in Table 1.

<Mask sensory test evaluation 1>
Sensory test evaluation of the masks according to the manufactured Example 1, Comparative Example 1, and Comparative Example 3 was performed. Specifically, the masks according to Example 1, Comparative Example 1, and Comparative Example 3 were applied to a total of 18 women, 10 women in their 20s to 40s and 8 men in their 20s to 40s, 5 times a day. They were worn for about hours and evaluated based on the evaluation items and evaluation criteria shown in Table 2. Table 2 shows the number of people who selected the relevant evaluation criteria for each evaluation item.

<Mask sensory test evaluation 2>
Similarly to the mask sensory test evaluation 1, the masks according to Example 2 and Example 4 and Comparative Example 1 and Comparative Example 4 were evaluated. The results are shown in Table 3.

  From the above, the mask according to the present invention has been evaluated very well on the feeling of wearing, such as per-skin at the time of wearing the mask, the softness of the mask, and the smooth feeling, while being used such as breathlessness and stuffiness in the mask. There was no problem with the feeling. In addition to this, the odor of the mask is also suppressed, and the nylon nonwoven fabric adopted as the mouthpiece layer and the buffer layer that sets the compression characteristic WC value of the mask body to a specific value to improve the wearing comfort can reduce some odor It is thought that also worked. The mask according to the present invention also has such an unpredictable effect.

10 Mask 1 Mask body 2 Ear hook 3 Outermost layer 4 Filter layer 5 Buffer layer 6 Mouth layer

Claims (6)

A non-woven mask having a mask body covering at least a part of the user's face, and a pair of ear hooks provided on both sides of the mask body,
The mask body has a multilayer structure having at least an outermost layer, an intermediate layer, and a mouthpiece layer,
The intermediate layer is at least selected from polyester fibers, polypropylene fibers, rayon fibers, acrylate fibers, nylon fibers, acetate fibers, wool fibers, cotton fibers, urethane fibers, and polyethylene fibers. Including a buffer layer made of a nonwoven fabric containing one or more kinds,
The mask body, Ri compression characteristics WC is 0.5~2.0gf · cm / cm ² der measured by KES system,
The buffer layer, Ru compression characteristics WC is 0.4~2.0gf · cm / cm ² der measured by KES system, nonwoven mask. The nonwoven fabric mask according to claim 1, wherein the buffer layer is made of a nonwoven fabric having a basis weight of 30 g / m ² or more.   The said buffer layer is a nonwoven fabric mask of Claim 1 or 2 which uses a needle punch nonwoven fabric.   The said mask main body is a nonwoven fabric mask of any one of Claims 1-3 whose thickness is 1.0 mm or more.   The said mouthpiece layer is a nonwoven fabric mask of any one of Claim 1 to 4 which consists of a nonwoven fabric using the fiber of official moisture content 1% or more.   The nonwoven fabric mask according to any one of claims 1 to 5, further comprising one or more collection filters as the intermediate layer, wherein the mouthpiece layer and the buffer layer are disposed adjacent to each other.

Images