JP2013129728A - Rubber composition - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a rubber composition for improving the sustention of an antioxidant effect in a cured rubber composition.SOLUTION: The rubber composition includes a rubber component and an antioxidant for rubber obtained by carrying an antioxidant material for rubber on a mesoporous silica having a mesopore volume exceeding 0.81 cm/g. Preferably, the composition includes the rubber component and the antioxidant obtained by carrying the antioxidant material on the mesoporous silica having the mesopore volume of ≥0.84 to ≤5.0 cm/g. In a solid NMR measurement of the antioxidant for rubber, it is preferable that the chemical shift of a peak based onC included in the antioxidant material carried on the silica is different by comparison from that of a peak based onC included in the antioxidant material which is not carried on the silica.

Description

  The present invention relates to a rubber composition and the like.

  Patent Document 1 describes a vulcanized rubber composition containing N- (1,3-dimethylbutyl) -N′-phenyl-p-phenylenediamine and silica as an antiaging substance for rubber. .

JP 2011-132471 A

  The conventional vulcanized rubber composition contains the rubber anti-aging substance itself as it is, and its anti-aging effect may not always be sufficiently satisfactory in terms of sustainability.

The present invention includes the following inventions.
1. A rubber composition comprising a rubber anti-aging agent obtained by supporting a rubber anti-aging substance on mesoporous silica having a mesoporous pore volume exceeding 0.81 cm ³ / g, and a rubber component.

2. That the anti-aging agent for rubber pore volume of mesopores and a 0.84 cm 3 / ^g or more 5.0 cm 3 / ^g or less is rubber anti-aging agent obtained by supporting the mesoporous silica and the rubber component Features 1 The rubber composition as described.

3. In the solid state NMR measurement, the rubber anti-aging agent contains a peak chemical shift based on ¹³ C contained in the rubber anti-aging substance supported on silica contained in the rubber anti-aging substance not supported on silica ^13. 1. A rubber anti-aging agent different from the chemical shift of the peak based on C. Or 2. The rubber composition as described.

4). The mesoporous silica has a mesopore diameter of 6 nm or more and 50 nm or less. ~ 3. The rubber composition according to any one of the above.

（式（Ｉ）中、Ｒ^１は、水素原子又は炭素数１〜１３のアルキル基を表す。） 5. 1. The rubber anti-aging substance is a compound represented by the formula (I): ~ 4. The rubber composition according to any one of the above.

(In formula (I), R ¹ represents a hydrogen atom or an alkyl group having 1 to 13 carbon atoms.)

6). 1. 1 part by mass to 100 parts by mass of mesoporous silica is contained with respect to 10 parts by mass of the anti-aging substance for rubber. ~ 5. The rubber composition according to any one of the above.

7). 1. An anti-aging agent for rubber obtained by supporting an anti-aging agent for rubber on mesoporous silica having a pore volume of mesopores exceeding 0.81 cm ³ / g, a rubber component, and a crosslinking agent. ~ 6. The rubber composition according to any one of the above.

8). 7). A vulcanized rubber composition comprising the rubber composition described above.

9. 7). A tire produced by processing the described rubber composition.

10. 8). A tire belt comprising a steel cord coated with the vulcanized rubber composition described above.

11. 8). A carcass for tires comprising a carcass fiber cord coated with the vulcanized rubber composition described above.

12 8). A tire sidewall, a tire inner liner, a tire cap tread, or a tire undertread comprising the vulcanized rubber composition described above.

  In the vulcanized rubber composition containing the rubber composition of the present invention, the durability of the anti-aging effect is improved.

It is a figure which shows the result of the solid-state NMR measurement of the antiaging substance for rubber | gum. It is a figure which shows the result of the solid-state NMR measurement of this anti-aging agent for rubber | gum (1). It is a figure explaining the method for measuring the transfer amount of the antiaging substance for rubber | gum in a vulcanized rubber composition.

<Rubber aging prevention substances>
The “anti-aging agent for rubber” in the present invention is an organic substance blended for the purpose of preventing the aging of the rubber product and extending its life. The “anti-aging agent for rubber” in the present invention is not particularly limited, and examples thereof include those described in pages 436 to 443 of “Rubber Industry Handbook <Fourth Edition>” edited by the Japan Rubber Association. be able to. Specifically, for example, N-phenyl-N′-1,3-dimethylbutyl-p-phenylenediamine (6PPD), reaction product of aniline and acetone (TMDQ), poly (2,2,4-trimethyl-1) , 2-) Dihydroquinoline) (“Antioxidant FR” manufactured by Matsubara Sangyo Co., Ltd.), synthetic wax (paraffin wax, etc.), vegetable wax, compound represented by formula (I), or compound represented by formula (II) Etc.
Preferable examples include substances having a relatively low molecular weight (specifically, for example, a molecular weight of about 150 to 400).
More preferable examples include a compound represented by the formula (I) or a compound represented by the formula (II).

（式（Ｉ）中、Ｒ^１は、水素原子又は炭素数１〜１３のアルキル基を表す。）

(In formula (I), R ¹ represents a hydrogen atom or an alkyl group having 1 to 13 carbon atoms.)

（式（ＩＩ）中、Ｒ^２は、水素原子又は、炭素数１〜１３のアルキル基を表す。Ｒ^３は、水素原子又は、炭素数１〜１３のアルコキシ基を表す）

(In formula (II), R ² represents a hydrogen atom or an alkyl group having 1 to 13 carbon atoms. R ³ represents a hydrogen atom or an alkoxy group having 1 to 13 carbon atoms)

  More specifically, for example, N-isopropyl-N′-phenyl-p-phenylenediamine (IPPD), N- (1,3-dimethylbutyl) -N′-phenyl-p-phenylenediamine (6PPD), ETMDQ ( 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline) and 2,2,4-trimethyl-1,2-dihydroquinoline.

<Mesoporous silica with a mesopore volume exceeding 0.81 cm ³ / g (hereinafter sometimes referred to as “mesoporous silica”)>
Mesoporous silica has a composition formula of SiO ₂ · nH ₂ O and a CAS registration number of 7631-86-9.
As the mesoporous silica, those having relatively large mesopores on the surface are preferable.
Pore volume of mesopores having a mesoporous silica surfaces are silica exceeding 0.81 cm ³ / g, preferably not more than 0.84 cm ³ / g or more 5.0 cm ³ / g, more preferably 1. 0 cm ³ / g or more 5.0cm and a ³ / g or less, particularly preferably not more than 1.3 cm ³ / g or more 5.0cm ³ / g.
The mesopore means a pore having a diameter of 2 nm or more and 50 nm or less in the catalyst field in IUPAC. The mesopore diameter is preferably 6 nm or more and 50 nm or less.

  Specific examples of mesoporous silica include silicia 310P, 420, 530, 550, 710, and 730 manufactured by Fuji Silysia, and silo-hovic 100, 507, and 702 manufactured by Fuji Silysia.

The rubber anti-aging agent is obtained by supporting a rubber anti-aging substance on mesoporous silica. The rubber anti-aging agent is preferably obtained by supporting an anti-aging agent for rubber in the mesopores of mesoporous silica.
As content of the mesoporous silica in this anti-aging agent for rubber | gum, it is good to contain 0.1-100 mass parts of mesoporous silica with respect to 10 mass parts of anti-aging substances for rubber | gum, for example. More preferably, it is good to contain 0.1 mass part-50 mass parts with respect to 10 mass parts of antiaging substances for rubber | gum, for example. Particularly preferably, for example, 0.1 part by mass to 30 parts by mass with respect to 10 parts by mass of the rubber anti-aging substance may be contained.

  The method for producing the anti-aging agent for rubber is not particularly limited as long as the anti-aging agent for rubber can be supported on mesoporous silica. Can be mentioned.

<Method for producing anti-aging agent for rubber>
(1): A rubber anti-aging substance is dissolved in a solvent, and the resulting solution is mixed with mesoporous silica to obtain a mixture. Mesoporous silica may be used as a slurry liquid mixed with a dispersion medium. The solvent is then removed from the mixture and the solid is dried (and crushed). Here, the “solvent” and “dispersion medium” are not particularly limited as long as they can dissolve the anti-aging material for rubber and can be removed by distillation. For example, toluene, xylene, hexane, heptane, etc. And hydrocarbon solvents such as acetone, methyl ethyl ketone, and methyl isobutyl ketone, and alcohol solvents such as methanol, ethanol, and isopropanol.

(2): After the rubber anti-aging substance is melted, mesoporous silica is added to the resulting melt to obtain a mixture. Next, a method of drying (and crushing) the mixture.

  In the method (1) and the method (2), the amount of mesoporous silica added is, for example, from 0.1 parts by mass to 100 parts by mass with respect to 10 parts by mass of the antiaging substance for rubber. it can. Preferably, 0.1 mass part-50 mass parts are mentioned with respect to 10 mass parts of antiaging substances for rubber | gum, for example. More preferably, for example, 0.1 mass part-30 mass parts can be mentioned with respect to 10 mass parts of anti-aging substances for rubber | gum.

Incidentally, it can be easily confirmed, for example, by solid-state NMR measurement that the antiaging substance for rubber is supported on mesoporous silica. Specifically, for example, the presence or absence of a change in the chemical shift of the peak based on ¹³ C contained in the rubber anti-aging substance may be observed before and after the rubber anti-aging substance is supported on mesoporous silica.
By supporting the rubber anti-aging substance on the mesoporous silica, the interaction between the functional group of the rubber anti-aging substance and the functional group of the mesoporous silica and the rubber anti-aging substance are supported on the mesopores. A change occurs in the three-dimensional structure, and as a result, a change in the chemical shift of the peak based on ¹³ C contained in the anti-aging material for rubber occurs. And what is necessary is just to confirm by the solid state NMR measurement that the said change exists. On the other hand, if the rubber anti-aging substance is not supported on the mesoporous silica, the interaction between the functional group of the rubber anti-aging substance and the functional group of the mesoporous silica does not occur, and as a result, it is included in the rubber anti-aging substance. ^No change in peak chemical shift based on ¹³ C occurs. And what is necessary is just to confirm by the solid state NMR measurement that the said change does not exist.

<Use of anti-aging agent for rubber>
The rubber composition containing the rubber anti-aging agent (hereinafter sometimes referred to as “the rubber composition of the present invention”) contains the rubber anti-aging agent and a rubber component. The rubber composition of the present invention is preferably obtained by kneading the rubber anti-aging agent and a rubber component. Kneading can be performed by a known method. The rubber composition of the present invention is, for example, a masterbatch that is used to produce a more uniform vulcanized rubber composition having a more uniform quality (usually, the rubber before the vulcanized rubber composition is produced). And a rubber composition containing a high-concentration anti-aging material for rubber, which is a granular material in which a component and a large amount of the anti-aging agent for rubber are pre-kneaded. The rubber composition of the present invention may be a kneaded rubber composition further containing a filler, zinc oxide, stearic acid, a crosslinking agent, a vulcanization accelerator component, and the like.

As content of the anti-aging agent for rubber | gum in this invention rubber composition, 0.1 mass part-990 mass parts can be mentioned with respect to 100 mass parts of rubber components, for example.
When the rubber composition of the present invention is a kneaded rubber composition further containing a filler, zinc oxide, stearic acid, a crosslinking agent, a vulcanization accelerator component, etc., the antiaging agent for the rubber in the rubber composition of the present invention The content of can be 0.1 to 50 parts by weight, preferably 0.5 to 30 parts by weight, for example, with respect to 100 parts by weight of the rubber component. it can. More preferably, 1 mass part-20 mass parts can be mention | raise | lifted, for example.
When the rubber composition of the present invention is a masterbatch used for producing a vulcanized rubber composition, the content of the rubber anti-aging agent in the rubber composition of the present invention is, for example, 100 parts by mass of a rubber component. Part by mass to 1 part by mass to 990 parts by mass, preferably 1 part by mass to 900 parts by mass, for example, more preferably 1 part by mass to 700 parts by mass. Particularly preferred examples include 1 part by mass to 500 parts by mass.

  Examples of rubber components include natural rubber, epoxidized natural rubber, deproteinized natural rubber and other modified natural rubber, polyisoprene rubber (IR), styrene / butadiene copolymer rubber (SBR), polybutadiene rubber (BR), acrylonitrile. Examples include various synthetic rubbers such as butadiene copolymer rubber (NBR), isoprene / isobutylene copolymer rubber (IIR), ethylene / propylene-diene copolymer rubber (EPDM), and halogenated butyl rubber (HR). Preferable examples include natural rubber, highly unsaturated rubber such as styrene / butadiene copolymer rubber and polybutadiene rubber. More preferably, natural rubber etc. can be mentioned. It is also effective to combine several rubber components such as a combination of natural rubber and styrene / butadiene copolymer rubber, a combination of natural rubber and polybutadiene rubber.

Examples of the natural rubber include grades of natural rubber such as RSS # 1, RSS # 3, TSR20, and SIR20.
Examples of the epoxidized natural rubber include those having a degree of epoxidation of 10 mol% to 60 mol% (specifically, for example, ENR25, ENR50, etc., manufactured by Kumpoulan Guthrie).
Examples of the deproteinized natural rubber include a deproteinized natural rubber having a total nitrogen content of 0.3% by mass or less.
As the modified natural rubber, for example, 4-vinylpyridine, N, N-dialkylaminoethyl acrylate (specifically, N, N-diethylaminoethyl acrylate, etc.), 2-hydroxy acrylate, etc. are reacted in advance with natural rubber. And modified natural rubber containing a polar group.

Examples of the styrene-butadiene copolymer rubber (SBR) include emulsion polymerization SBR and solution polymerization SBR described in pages 210 to 211 of the “Rubber Industry Handbook <Fourth Edition>” edited by the Japan Rubber Association. Can be mentioned. As the rubber composition for tread, for example, solution polymerization SBR can be preferably mentioned. Further, for example, solution polymerization SBR in which molecular ends are modified using 4,4′-bis- (dialkylamino) benzophenone such as “Nippol (registered trademark) NS116” manufactured by Nippon Zeon Co., Ltd., “SL574” manufactured by JSR, etc. Solution-polymerized SBR having a molecular end modified with a tin halide compound of No. 1, commercially available products of silane-modified solution-polymerized SBR such as “E10” and “E15” manufactured by Asahi Kasei Corporation, lactam compounds, amide compounds, urea compounds, N, An N-dialkylacrylamide compound, an isocyanate compound, an imide compound, a silane compound having an alkoxy group (trialkoxysilane compound, etc.) and an aminosilane compound alone, or a silane compound having a tin compound and an alkoxy group, Alkylacrylamide compounds and silane compounds having alkoxy groups A solution polymerization SBR having a plurality of different compounds such as nitrogen, tin, silicon, or a plurality of elements at the molecular ends obtained by modifying the molecular ends, respectively. More preferred can be mentioned.
Further, an oil-added SBR obtained by adding an oil such as process oil or aroma oil after polymerization into emulsion polymerization SBR and solution polymerization SBR can be preferably exemplified as the rubber composition for tread.

Examples of the polybutadiene rubber (BR) include solution polymerization BR such as a high cis BR having 90% or more of cis 1,4 bond and a low cis BR having a cis bond of around 35%. Preferably, for example, low cis BR having a high vinyl content can be used. Furthermore, for example, “Nipol (registered trademark) BR 1250H” manufactured by Nippon Zeon, tin-modified BR, 4,4′-bis- (dialkylamino) benzophenone, tin halide compound, lactam compound, amide compound, urea compound, etc. , N, N-dialkylacrylamide compound, isocyanate compound, imide compound, silane compound having alkoxy group (trialkoxysilane compound, etc.), aminosilane compound alone, or silane having tin compound and alkoxy group A compound, a plurality of different compounds such as an alkylacrylamide compound and an alkoxy group-containing silane compound, or the like, and each of the molecular ends obtained by modifying the molecular ends is nitrogen, tin, or silicon, or , Solution polymerization BR having a plurality of these elements It can be cited more preferably.
These BR can be preferably mentioned as a rubber composition for a tread or a rubber composition for a sidewall. Usually, it is used in a blend of SBR and / or natural rubber. As the blend ratio, in the case of the rubber composition for tread, SBR and / or natural rubber is 60% by mass to 100% by mass, BR is 40% by mass to 0% by mass, etc. with respect to the total rubber mass. Can do. Moreover, in the case of the rubber composition for sidewalls, SBR and / or natural rubber may be 10% by mass to 70% by mass, BR may be 90% by mass to 30% by mass, etc. with respect to the total rubber mass. . Preferably, a blend of natural rubber 40% by mass to 60% by mass and BR 60% by mass to 40% by mass with respect to the total rubber mass. In this case, a blend of modified SBR and non-modified SBR and a blend of modified BR and non-modified BR are also preferable.

Examples of the filler include carbon black, silica, talc, clay, titanium oxide and the like that are usually used in the rubber field. Preferably, carbon black, silica, etc. are mentioned, for example. More preferably, carbon black etc. can be mentioned, for example.
Examples of the carbon black include those described on page 494 of “Rubber Industry Handbook <Fourth Edition>” edited by the Japan Rubber Association. Preferably, for example, HAF (High Abrasion Furnace), SAF (Super Abrasion Furnace), ISAF (Intermediate SAF), FEF (Fast Extrusion Furnace), MAF, GPF (General Purpose Furnace), SRF (Semi-Reinforcing Furnace), etc. Carbon black is mentioned.
In the case of tire tread rubber composition, CTAB (Cetyl Tri-methyl Ammonium Bromide) surface area 40m ² / g~250m ² / g, nitrogen adsorption specific surface area 20m ² / g~200m ² / g, particle size 10nm~50nm Preferably, carbon black can be mentioned. More preferably, for example, carbon black and the like is CTAB surface 70m ² / g~180m ² / g. Specifically, for example, in the ASTM standard, N110, N220, N234, N299, N326, N330, N330T, N339, N343, N351 and the like can be mentioned. Moreover, the surface treatment carbon black which made 0.1 mass%-50 mass% adhere the silica to the surface of carbon black can also be mentioned preferably. More preferably, for example, a combination of several fillers such as a combination of carbon black and silica is used.
In the case of the tire tread rubber composition, for example, carbon black alone or both carbon black and silica can be preferably mentioned.
In the case of the carcass rubber composition, the rubber composition for a side wall is, CTAB surface area of 20m ² / g~60m ² / g, it can be preferably exemplified a carbon black particle size 40 nm to 100 nm. Specifically, for example, in the ASTM standard, N330, N339, N343, N351, N550, N568, N582, N630, N642, N660, N662, N754, N762 and the like can be mentioned.

  Although the usage-amount of this filler is not specifically limited, For example, 5 mass parts-100 mass parts can be mentioned with respect to 100 mass parts of rubber components. In the case of using only carbon black as a filler, for example, 30 to 80 parts by mass is preferably cited with respect to 100 parts by mass of the rubber component. Moreover, when using together carbon black and a silica as a filler in a tread member use, 5-60 mass parts of carbon black is mentioned preferably with respect to 100 mass parts of rubber components, for example.

The silica used as a filler, for example, a CTAB specific surface area 50m ² / g~180m ² / g of silica, silica nitrogen adsorption specific surface area 50m ² / g~300m ² / g or the like. Specifically, for example, “AQ” and “AQ-N” manufactured by Tosoh Silica Co., Ltd., “Ultra Gil (registered trademark) VN3”, “Ultra Gil (registered trademark) 360”, and “Ultra Gil (registered trademark)” manufactured by Degussa. 7000 ”,“ Zeosil (registered trademark) 115GR ”,“ Zeosil (registered trademark) 1115MP ”,“ Zeosil (registered trademark) 1205MP ”,“ Zeosil (registered trademark) Z85MP ”manufactured by Rhodia, (Registered trademark) AQ "and the like. Further, for example, silica having a pH of 6 to 8, silica containing 0.2% by mass to 1.5% by mass of sodium, true spherical silica having a roundness of 1 to 1.3, silicone oil such as dimethyl silicone oil It is also preferable to blend an organosilicon compound containing an ethoxysilyl group, silica surface-treated with an alcohol such as ethanol or polyethylene glycol, silica having two or more different nitrogen adsorption specific surface areas, and the like.

Although the usage-amount of this filler is not specifically limited, For example, 10 mass parts-120 mass parts can be mentioned with respect to 100 mass parts of rubber components.
Moreover, when mix | blending a silica, it is good to mix | blend 5-50 mass parts of carbon black with respect to 100 mass parts of rubber components, for example. As a compounding ratio of silica / carbon black, the range of 0.7 / 1-1 / 0.1 can be mentioned, for example.
When silica is used as the filler, bis (3-triethoxysilylpropyl) tetrasulfide (“Si-69” manufactured by Degussa), bis (3-triethoxysilylpropyl) disulfide (“Si-Si” manufactured by Degussa) -75 "), bis (3-diethoxymethylsilylpropyl) tetrasulfide, bis (3-diethoxymethylsilylpropyl) disulfide, octanethioic acid S- [3- (triethoxysilyl) propyl] ester (General Electronic Silicones) "NXT silane"), octanethioic acid S- [3-{(2-methyl-1,3-propanedialkoxy) ethoxysilyl} propyl] ester and octanethioic acid S- [3-{(2-methyl-1) , 3-propanedialkoxy) methylsilyl} propyl] ester Rutriethoxysilane, methyltrimethoxysilane, methyltriethoxysilane, methyltriacetoxysilane, methyltributoxysilane, ethyltrimethoxysilane, ethyltriethoxysilane, isobutyltrimethoxysilane, isobutyltriethoxysilane, n-octyltrimethoxysilane , N-octyltriethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, vinyltri (methoxyethoxy) silane, phenyltrimethoxysilane, phenyltriethoxysilane, phenyltriacetoxysilane, 3-methacryloxypropyltrimethoxysilane, 3 -Methacryloxypropyltriethoxysilane, 3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, N- (2-aminoethyl) ) -3-aminopropyltrimethoxysilane, N- (2-aminoethyl) -3-aminopropyltriethoxysilane, (3-glycidoxypropyl) trimethoxysilane, (3-glycidoxypropyl) triethoxy Silane, 2- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, 2- (3,4-epoxycyclohexyl) ethyltriethoxysilane, 3-isocyanatopropyltrimethoxysilane and 3-isocyanatopropyl It is preferable to add a compound having a functional group such as an element such as silicon or alkoxysilane capable of binding to silica, such as one or more silane coupling agents selected from the group consisting of triethoxysilane. Specifically, for example, bis (3-triethoxysilylpropyl) tetrasulfide (“Si-69” manufactured by Degussa), bis (3-triethoxysilylpropyl) disulfide (“Si-75” manufactured by Degussa), 3 -Octanoylthiopropyltriethoxysilane ("NXT silane" manufactured by General Electronic Silicones) and the like can be mentioned.
Although the addition time of these compounds is not particularly limited, it is preferable to add to the rubber at the same time as the silica. As a compounding quantity, 2 mass%-10 mass% can be mentioned with respect to the mass of a silica, for example. Preferably, 7 mass%-9 mass% are mentioned, for example.
As compounding temperature at the time of compounding the above-mentioned compound with rubber, 80 ° C-200 ° C can be mentioned, for example. Preferably, 110 degreeC-180 degreeC is mentioned, for example.
When silica is used as the filler, for example, in addition to silica, an element such as silicon that can be bonded to silica, or a compound having a functional group such as alkoxysilane, a monohydric alcohol such as ethanol, butanol, or octanol, Divalent or higher alcohols such as ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, polypropylene glycol, pentaerythritol, polyether polyol, N-alkylamines, amino acids, liquid polybutadienes whose molecular ends are carboxyl-modified or amine-modified, etc. May be blended.

  As usage-amount of a zinc oxide, 1 mass part-15 mass parts can be mentioned with respect to 100 mass parts of rubber components, for example. Preferably, 1 mass part-8 mass parts are mentioned, for example.

  As a usage-amount of a stearic acid, 0.5 mass part-10 mass parts can be mentioned with respect to 100 mass parts of rubber components, for example. Preferably, 1 mass part-5 mass parts are mentioned, for example.

  As a crosslinking agent, sulfur etc. can be mentioned, for example. Examples of sulfur include powdered sulfur, precipitated sulfur, colloidal sulfur, insoluble sulfur, and highly dispersible sulfur. Preferably, powder sulfur etc. are mentioned. Moreover, when using for tire members with many sulfur amounts, such as a member for belts, an insoluble sulfur etc. can be mentioned preferably, for example. Note that the sulfur does not contain a vulcanization accelerator. As usage-amount of sulfur, 0.3 mass part-5 mass parts can be mentioned with respect to 100 mass parts of rubber components, for example. Preferably, 0.5 mass part-3 mass parts are mentioned, for example.

  Examples of the vulcanization accelerator include thiazole vulcanization accelerators and sulfenamide vulcanization accelerators described on pages 412 to 413 of “Rubber Industry Handbook <Fourth Edition>” edited by Japan Rubber Association. And guanidine vulcanization accelerators.

Specifically, for example, N-cyclohexyl-2-benzothiazolylsulfenamide (CBS), N-tert-butyl-2-benzothiazolylsulfenamide (BBS), N, N-dicyclohexyl-2- Examples include benzothiazolylsulfenamide (DCBS), 2-mercaptobenzothiazole (MBT), dibenzothiazyl disulfide (MBTS), and diphenylguanidine (DPG). Also, morpholine disulfide, which is a known vulcanizing agent, can be used.
When carbon black is used as the filler, for example, N-cyclohexyl-2-benzothiazolylsulfenamide (CBS), N-tert-butyl-2-benzothiazolylsulfenamide (BBS), N, N It is preferable to use either dicyclohexyl-2-benzothiazolylsulfenamide (DCBS) or dibenzothiazyl disulfide (MBTS) and diphenylguanidine (DPG).
When silica and carbon black are used in combination as fillers, for example, N-cyclohexyl-2-benzothiazolylsulfenamide (CBS), N-tert-butyl-2-benzothiazolylsulfenamide (BBS) , N, N-dicyclohexyl-2-benzothiazolylsulfenamide (DCBS) or dibenzothiazyl disulfide (MBTS) and diphenylguanidine (DPG) are preferably used in combination.

Although it does not restrict | limit especially as a ratio of sulfur and a vulcanization accelerator, For example, sulfur / vulcanization accelerator = 2 / 1-1 / 2 can be mentioned by mass ratio.
EV vulcanization in which the mass ratio of sulfur / vulcanization accelerator, which is a method for improving heat resistance in a rubber member mainly composed of natural rubber, is 1 or less is preferably used in applications requiring improvement in heat resistance.

  In addition, you may mix | blend various compounding agents normally used in the rubber | gum field | area. Examples of such compounding agents include oils; fatty acids such as stearic acid; Coumarone resin G-90 (softening point: 80 ° C. to 100 ° C.) manufactured by Nikkaku Chemical, and process resin AC8 (softened) manufactured by Kobe Oil Chemical Co., Ltd. Coumarone-indene resin such as terpene resin, terpene / phenol resin, aromatic modified terpene resin, etc .; “Nikanol (registered trademark) HP-100” (softening point 105-105) manufactured by Mitsubishi Gas Chemical Co., Ltd. 125 ° C.) xylene / formaldehyde resin; rosin derivatives such as “Ester gum” series and “neotol” series manufactured by Arakawa Chemical Co .; hydrogenated rosin derivatives; novolac alkylphenol resins; resol alkylphenol resins; Resin; liquid polybutadiene;

  Examples of the oil include process oil and vegetable oil. Examples of the process oil include paraffinic process oil, naphthenic process oil, and aromatic process oil.

<Vulcanized rubber composition containing anti-aging agent for rubber>
The vulcanized rubber composition containing the rubber anti-aging agent is usually obtained by heat-treating a rubber composition obtained by kneading the rubber anti-aging agent, a rubber component and a crosslinking agent. As temperature conditions in heat processing, 120 degreeC-180 degreeC can be mentioned, for example. The heat treatment may be usually performed at normal pressure or under pressure.

The vulcanized rubber composition containing the present antiaging agent for rubber is suitably used for tires. Examples of the tire include a pneumatic tire and a solid tire.
Further, the vulcanized rubber composition containing the present anti-aging agent for rubber is a tire belt comprising a steel cord coated with each member constituting the tire, that is, a vulcanized rubber composition containing the present anti-aging agent for rubber. , A tire carcass including a carcass fiber cord coated with a vulcanized rubber composition containing the rubber anti-aging agent, a tire sidewall including a vulcanized rubber composition containing the rubber anti-aging agent, and a tire inner It is also preferably used as a liner, a tire tread or a tire undertread.

  The vulcanized rubber composition containing the present antiaging agent for rubber can extend the life of rubber materials such as tires. Further, the vulcanized rubber composition can be used not only for the above-mentioned tire use, but also as an anti-vibration rubber for automobiles such as engine mounts, strut mounts, bushes, and exhaust hangers.

EXAMPLES Hereinafter, although an Example, a reference example, a comparative example, etc. are given and this invention is demonstrated concretely, this invention is not limited to these.
<Rubber aging prevention substances>
A1: Antigen 6C (N- (1,3-dimethylbutyl) -N′-phenyl-p-phenylenediamine) manufactured by Sumitomo Chemical Co., Ltd.
<Mesoporous silica>
B1: Silicia 310P manufactured by Fuji Silysia
B2: Silicia 420 manufactured by Fuji Silysia
B3: Silicia 530 manufactured by Fuji Silysia
X1: God ball B-6C made by Suzuki Yushi Co., Ltd.
X2: Silicia 710 manufactured by Fuji Silysia
X3: Silicia 730 manufactured by Fuji Silysia

Production Example 1 (Production example of anti-aging agent for rubber)
A 500 ml beaker is charged with 20 g of mesoporous silica (B1), and 200 ml of methanol is added thereto to form a slurry liquid. On the other hand, 20 g of rubber anti-aging substance (A1) was charged into a 100 mL Erlenmeyer flask, and 50 mL of methanol was added thereto to obtain a methanol solution. Add a methanol solution of the rubber anti-aging substance (A1) to the silica gel slurry beaker prepared previously, and then wash the 100 mL Erlenmeyer flask containing the methanol solution with 20 ml of methanol. The resulting washing solution was also added to obtain a mixture. The resulting mixture was stirred at 25 ° C. under air for 1 day. After the stirring was completed, the obtained mixture was dried by an evaporator to obtain the rubber anti-aging agent (1) as a gray solid.

Production Example 2 (Production Example of Anti-aging Agent for Rubber)
The rubber anti-aging agent (2) was obtained in the same manner as in Production Example 1 except that the mesoporous silica (B1) was changed to the mesoporous silica (B2).

Production Example 3 (Production Example of Anti-aging Agent for Rubber)
The rubber anti-aging agent (3) was obtained in the same manner as in Production Example 1 except that the mesoporous silica (B1) was changed to the mesoporous silica (B3).

Production Example 4 (Production Example of Anti-aging Agent for Mesoporous Silica (X1) -Supported Rubber)
An anti-aging agent for silica (X1) -supported rubber was obtained in the same manner as in Production Example 1 except that the mesoporous silica (B1) was changed to mesoporous silica (X1).

Production Example 5 (Production Example of Anti-aging Agent for Mesoporous Silica (X2) -Supported Rubber)
An anti-aging agent for silica (X2) -supported rubber was obtained in the same manner as in Production Example 1 except that the mesoporous silica (B1) was changed to mesoporous silica (X2).

Production Example 6 (Production Example of Anti-Aging Agent for Mesoporous Silica (X3) -Supported Rubber)
An anti-aging agent for silica (X3) -supported rubber was obtained in the same manner as in Production Example 1 except that the mesoporous silica (B1) was changed to mesoporous silica (X3).

  The mesoporous diameters and pore volumes of mesoporous silica in Table 1 are measured values. The measurement was performed under the following measurement conditions.

[Mesopore diameter and pore volume measurement conditions]
Measuring device: BELSORP-mini (manufactured by Nippon BEL Co., Ltd.)
Pretreatment device: BELPREP-vacII (manufactured by Nippon BEL Co., Ltd.)
Test method: Nitrogen adsorption method Pretreatment method: Vacuum degassing at 120 ° C for 8 hours Measurement method: Measurement of adsorption / desorption isotherm by nitrogen using constant volume method Adsorption temperature: 77K
Adsorbent: Nitrogen pore volume: Calculated by BJH method

<Confirmation of loading of rubber anti-aging agent on mesoporous silica by solid state NMR measurement>
The rubber anti-aging agent (1) obtained in Production Example 1 was subjected to solid state NMR measurement under the following conditions. The results are shown in FIGS.
Comparison of before and after loading of rubber anti-aging material on mesoporous silica showed a change in the chemical shift of the peak based on ¹³ C contained in rubber anti-aging material, so that rubber anti-aging material on mesoporous silica was observed. Was confirmed.

[Solid state NMR measurement conditions]
Device: ECA400 [manufactured by JEOL Ltd.]
MAS: 6kHz
Measurement: ¹³ C CPMAS
contact time: 2ms
Integration: 10,000 times

Reference Example 1 (Production example of basic rubber composition)
Into a 10 L kneader, 50 parts by mass of both natural rubber (product name: SMR-CV60) and butadiene rubber (product name: JSR BR01, manufactured by JSR Corporation) were added and kneaded for 2 minutes. The remaining materials shown in Table 2 were added to the obtained kneaded material, and the mixture was further kneaded for 10 minutes to obtain a rubber composition as a basic rubber composition. The discharge temperature of the rubber composition from the kneader was 95 ° C.

Comparative Example 1 (Production Example of Vulcanized Rubber Composition not Containing Anti-aging Agent for Rubber)
163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)) 0.8 A rubber composition was obtained by kneading parts by mass and 1.5 parts by mass of sulfur with an open roll machine having a roll set temperature of 60 ° C. The obtained rubber composition was hot press molded at 145 ° C. Thus, a vulcanized rubber composition having a width of 15.5 cm, a length of 16.0 cm and a thickness of 2 mm and containing no anti-aging agent for rubber (however, both an anti-aging agent for rubber and mesoporous silica) was obtained the exclusive). Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c (90)) than the extended 5 minutes time and vulcanization time .
Next, 163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)) A rubber composition was obtained by kneading 0.8 parts by mass, 1.5 parts by mass of sulfur, and 3 parts by mass of an anti-aging agent for rubber (A1) with an open roll machine having a roll set temperature of 60 ° C. . The obtained rubber composition is heated and press-molded at 145 ° C. to form a vulcanized rubber composition containing no anti-aging agent for rubber in the form of a sheet having a width of 15.5 cm, a length of 16.0 cm, and a thickness of 2 mm. (However, an anti-aging material for rubber was included, and mesoporous silica was not included). Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c ₍₉₀₎₎ than the extended 5 minutes time and the vulcanization time.

Reference Example 2 (Method for measuring the migration amount of anti-aging substances for rubber)
Vulcanized rubber composition containing no anti-aging agent for rubber (however, it does not contain both anti-aging agent for rubber and mesoporous silica) and vulcanized rubber composition containing no anti-aging agent for rubber (however, The amount of migration of the rubber anti-aging substance was measured using a rubber anti-aging substance and no mesoporous silica).
Three sheets manufactured from a vulcanized rubber composition that does not contain the rubber anti-aging agent (but does not contain both the rubber anti-aging substance and mesoporous silica), and does not contain the rubber anti-aging agent The initial weight of each sheet was measured for three sheets produced from a vulcanized rubber composition (however, containing an antiaging substance for rubber and not containing mesoporous silica).
FIG. 3 is a diagram for explaining a method for measuring the amount of migration of the rubber anti-aging substance in the vulcanized rubber composition. Six sheets after weight measurement (sheets 1 to 3 produced from a vulcanized rubber composition containing an antioxidant for rubber, sheets 4 to 4 produced from a vulcanized rubber composition not containing an antioxidant for rubber) After laminating 6), the entire laminate was wrapped with aluminum foil 7, and further wrapped with aluminum laminate 8 from above. About 3 kg of weights 9 were placed on the aluminum foil and aluminum laminate package thus obtained.
The package on which the weight was placed was left in a thermostatic chamber at 25 ° C. for 6 days, then the aluminum foil and the aluminum laminate package were opened, each sheet was taken out, and the weight of each sheet was measured.
The amount of migration of the anti-aging agent for rubber was defined as a change in weight from the initial weight of the sheet produced from the vulcanized rubber composition not containing the anti-aging agent for rubber. Separately, as a result of extracting and quantifying the anti-aging agent for rubber from the vulcanized rubber composition of each sheet, it was confirmed that the weight change was caused by the migration of the anti-aging agent for rubber.

Example 1 (Production Example of Vulcanized Rubber Composition Containing Anti-aging Agent for Rubber)
163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)) 0.8 By kneading the mass part, 1.5 parts by mass of sulfur, and 6 parts by mass of the anti-aging agent for rubber (1) obtained in Production Example 1 with an open roll machine having a roll set temperature of 60 ° C., An inventive rubber composition was obtained. The resulting rubber composition is heated and press-molded at 145 ° C. to form a vulcanized rubber composition containing the present antioxidant for rubber in the form of a sheet having a width of 15.5 cm, a length of 16.0 cm, and a thickness of 2 mm. Got. Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c ₍₉₀₎₎ than the extended 5 minutes time and the vulcanization time.

(Production example of vulcanized rubber composition not containing anti-aging agent for rubber)
On the other hand, 163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)] 0 A rubber composition was obtained by kneading 0.8 parts by mass and 1.5 parts by mass of sulfur with an open roll machine having a roll set temperature of 60 ° C. The obtained rubber composition was heated and pressed at 145 ° C. By molding, a vulcanized rubber composition not containing the rubber anti-aging agent in the form of a sheet having a width of 15.5 cm, a length of 16.0 cm, and a thickness of 2 mm (however, it does not contain an anti-aging agent for rubber) was obtained. Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c ₍₉₀₎₎ than the extended 5 minutes time and the vulcanization time.
Using the vulcanized rubber composition containing the present anti-aging agent for rubber and the vulcanized rubber composition not containing the anti-aging agent for rubber (excluding the anti-aging agent for rubber), the same as in Reference Example 2 The amount of migration of the rubber anti-aging substance was measured.

Example 2 (Production Example of Vulcanized Rubber Composition Containing Anti-aging Agent for Rubber)
163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)) 0.8 By mixing 6 parts by mass of 1.5 parts by mass of sulfur, 1.5 parts by mass of sulfur, and 6 parts by mass of the anti-aging agent for rubber (2) obtained in Production Example 2 with a roll setting temperature of 60 ° C., An inventive rubber composition was obtained. The resulting rubber composition is heated and press-molded at 145 ° C. to form a vulcanized rubber composition containing the present antioxidant for rubber in the form of a sheet having a width of 15.5 cm, a length of 16.0 cm, and a thickness of 2 mm. Got. Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c ₍₉₀₎₎ than the extended 5 minutes time and the vulcanization time.

(Production example of vulcanized rubber composition not containing anti-aging agent for rubber)
On the other hand, 163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)] 0 A rubber composition was obtained by kneading 0.8 parts by mass and 1.5 parts by mass of sulfur with an open roll machine having a roll set temperature of 60 ° C. The obtained rubber composition was heated and pressed at 145 ° C. By molding, a vulcanized rubber composition not containing the rubber anti-aging agent in the form of a sheet having a width of 15.5 cm, a length of 16.0 cm, and a thickness of 2 mm (however, it does not contain an anti-aging agent for rubber) was obtained. Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c ₍₉₀₎₎ than the extended 5 minutes time and the vulcanization time.
Using the vulcanized rubber composition containing the present anti-aging agent for rubber and the vulcanized rubber composition not containing the anti-aging agent for rubber (excluding the anti-aging agent for rubber), the same as in Reference Example 2 The amount of migration of the rubber anti-aging substance was measured.

Example 3 (Production Example of Vulcanized Rubber Composition Containing Anti-aging Agent for Rubber)
163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)) 0.8 By kneading the mass part, 1.5 parts by mass of sulfur, and 6 parts by mass of the anti-aging agent for rubber (3) obtained in Production Example 3 with an open roll machine having a roll set temperature of 60 ° C., An inventive rubber composition was obtained. The resulting rubber composition is heated and press-molded at 145 ° C. to form a vulcanized rubber composition containing the present antioxidant for rubber in the form of a sheet having a width of 15.5 cm, a length of 16.0 cm, and a thickness of 2 mm. Got. Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c ₍₉₀₎₎ than the extended 5 minutes time and the vulcanization time.

(Production example of vulcanized rubber composition not containing anti-aging agent for rubber)
On the other hand, 163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)] 0 A rubber composition was obtained by kneading 0.8 parts by mass and 1.5 parts by mass of sulfur with an open roll machine having a roll set temperature of 60 ° C. The obtained rubber composition was heated and pressed at 145 ° C. By molding, a vulcanized rubber composition not containing the rubber anti-aging agent in the form of a sheet having a width of 15.5 cm, a length of 16.0 cm, and a thickness of 2 mm (however, it does not contain an anti-aging agent for rubber) was obtained. Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c ₍₉₀₎₎ than the extended 5 minutes time and the vulcanization time.
Using the vulcanized rubber composition containing the present anti-aging agent for rubber and the vulcanized rubber composition not containing the anti-aging agent for rubber (excluding the anti-aging agent for rubber), the same as in Reference Example 2 The amount of migration of the rubber anti-aging substance was measured.

Comparative Example 2 ((X1) Production Example of Vulcanized Rubber Composition Containing Anti-aging Agent for Supported Rubber)
163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)) 0.8 By kneading the mass part, 1.5 parts by mass of sulfur, and 6 parts by mass of the anti-aging agent for supported rubber (X1) obtained in Production Example 4 with an open roll machine having a roll set temperature of 60 ° C., rubber is obtained. A composition was obtained. The resulting rubber composition is heated and press-molded at 145 ° C. to form a vulcanized rubber composition containing the present antioxidant for rubber in the form of a sheet having a width of 15.5 cm, a length of 16.0 cm, and a thickness of 2 mm. Got. Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c ₍₉₀₎₎ than the extended 5 minutes time and the vulcanization time.

((X1) Production Example of Vulcanized Rubber Composition Not Containing Anti-aging Agent for Supported Rubber)
On the other hand, 163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)] 0 A rubber composition was obtained by kneading 0.8 parts by mass and 1.5 parts by mass of sulfur with an open roll machine having a roll set temperature of 60 ° C. The obtained rubber composition was heated and pressed at 145 ° C. By molding, a vulcanized rubber composition not containing the rubber anti-aging agent in the form of a sheet having a width of 15.5 cm, a length of 16.0 cm, and a thickness of 2 mm (however, it does not contain an anti-aging agent for rubber) was obtained. Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c ₍₉₀₎₎ than the extended 5 minutes time and the vulcanization time.
(X1) Reference Example 2 using a vulcanized rubber composition containing an anti-aging agent for a supported rubber and a vulcanized rubber composition not containing the anti-aging agent for rubber (but not containing an anti-aging agent for rubber) In the same manner as above, the amount of migration of the anti-aging agent for rubber was measured.

Reference Example 3 ((X2) Production Example of Vulcanized Rubber Composition Containing Anti-aging Agent for Supported Rubber)
163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)) 0.8 By kneading the mass part, 1.5 parts by mass of sulfur, and 6 parts by mass of the anti-aging agent for supported rubber (X2) obtained in Production Example 5 with an open roll machine having a roll set temperature of 60 ° C., rubber is obtained. A composition was obtained. The resulting rubber composition is heated and press-molded at 145 ° C. to form a sheet shape having a width of 15.5 cm, a length of 16.0 cm, and a thickness of 2 mm, and containing (X2) an anti-aging agent for a supported rubber. A rubber composition was obtained. Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c ₍₉₀₎₎ than the extended 5 minutes time and the vulcanization time.

((X2) Production example of vulcanized rubber composition not containing anti-aging agent for supported rubber)
On the other hand, 163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)] 0 A rubber composition was obtained by kneading 0.8 parts by mass and 1.5 parts by mass of sulfur with an open roll machine having a roll set temperature of 60 ° C. The obtained rubber composition was heated and pressed at 145 ° C. By molding, a vulcanized rubber composition not containing an anti-aging agent for supported rubber (X2) in the form of a sheet having a width of 15.5 cm, a length of 16.0 cm and a thickness of 2 mm (however, an anti-aging agent for rubber is added) includes not) was obtained. Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c (90)) than the extended 5 minutes time and the vulcanization time.
(X2) Using a vulcanized rubber composition containing an anti-aging agent for a supported rubber and (X2) a vulcanized rubber composition not containing an anti-aging agent for a supporting rubber (however, not containing an anti-aging agent for rubber) In the same manner as in Reference Example 2, the amount of migration of the rubber anti-aging substance was measured.

Reference Example 4 ((X3) Production Example of Vulcanized Rubber Composition Containing Anti-aging Agent for Supported Rubber)
163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)) 0.8 By kneading the mass part, 1.5 parts by mass of sulfur, and 6 parts by mass of the anti-aging agent for supported rubber (X3) obtained in Production Example 6 with an open roll machine having a roll set temperature of 60 ° C., rubber is obtained. A composition was obtained. The resulting rubber composition is heated and press-molded at 145 ° C. to form a sheet shape having a width of 15.5 cm, a length of 16.0 cm, and a thickness of 2 mm, and containing (X3) an anti-aging agent for a supported rubber. A rubber composition was obtained. Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c ₍₉₀₎₎ than the extended 5 minutes time and the vulcanization time.

((X3) Production example of vulcanized rubber composition not containing anti-aging agent for supported rubber)
On the other hand, 163.5 parts by mass of the basic rubber composition obtained in Reference Example 1, 2 parts by mass of zinc oxide, and a vulcanization accelerator (N-tert-butyl-2-benzothiazolesulfenamide (TBBS)] 0 A rubber composition was obtained by kneading 0.8 parts by mass and 1.5 parts by mass of sulfur with an open roll machine having a roll set temperature of 60 ° C. The obtained rubber composition was heated and pressed at 145 ° C. By molding, a vulcanized rubber composition containing 15.5 cm in width, 16.0 cm in length and 2 mm in thickness and containing no anti-aging agent for supported rubber (X3) includes not) was obtained. Incidentally, between 90% vulcanization of the measured rubber composition in conformity with JIS K 6300-2 to _(t c (90)) than the extended 5 minutes time and the vulcanization time.
(X3) Using a vulcanized rubber composition containing an anti-aging agent for a supported rubber and (X3) a vulcanized rubber composition not containing an anti-aging agent for a supporting rubber (but not including an anti-aging agent for rubber), In the same manner as in Reference Example 2, the amount of migration of the rubber anti-aging substance was measured.

The results obtained are summarized in Table 4.
“Transition rate of anti-aging agent for rubber” described in Table 4 is a vulcanized rubber composition not containing the anti-aging agent for rubber obtained in Comparative Example 1 (however, an anti-aging agent for rubber is added). It is a relative amount of migration when the amount of migration of the anti-aging agent for rubber is 100). The smaller the value, the slower the migration rate of the anti-aging material for rubber, which means that the durability of the anti-aging effect in the vulcanized rubber composition is improved.

Reference Example 5 (Production Example of Vulcanized Rubber Composition)
The vulcanized rubber composition obtained by the following first step and second step is suitable for undertread.
<First step>
(Procedure 1)
Using a Banbury mixer (600 ml Labo Plast Mill manufactured by Toyo Seiki Co., Ltd.), 100 parts by mass of styrene / butadiene copolymer rubber SBR # 1502 (manufactured by Sumitomo Chemical Co., Ltd.), ISAF-HM (manufactured by Asahi Carbon Co., Ltd., trade name “Asahi # 80”) ) 35 parts by mass, 2 parts by mass of stearic acid, 3 parts by mass of zinc oxide, 8 parts by mass of the anti-aging agent for rubber (1) obtained in Production Example 1, and wax (“OZOACE-0355” manufactured by Nippon Seiwa) ) A rubber composition is obtained by kneading 2 parts by mass within a range of 160 ° C. to 175 ° C. for 5 minutes at a rotation speed of a mixer of 50 rpm.
(Procedure 2)
The rubber composition obtained in step 1 and 2 parts by mass of N-cyclohexyl-2-benzothiazolesulfenamide (CBS) as a vulcanization accelerator within the range of 60 ° C. to 80 ° C. in an open roll machine. By kneading 0.5 parts by mass of diphenylguanidine (DPG) as a vulcanization accelerator, 0.8 parts by mass of dibenzothiazyl disulfide (MBTS) as a vulcanization accelerator and 1 part by mass of sulfur, rubber was obtained. A kneaded product is obtained.
<Second step>
The rubber kneaded material obtained in the first step (procedure 2) is heat-treated at 145 ° C. to obtain a vulcanized rubber composition.

Reference Example 6 (Production Example of Vulcanized Rubber Composition)
The vulcanized rubber composition obtained by the following first step and second step is suitable for a belt.
<First step>
(Procedure 1)
Using a Banbury mixer (600 ml Lab Plast Mill manufactured by Toyo Seiki Co., Ltd.), 100 parts by mass of commercially available natural rubber (RSS # 1), 45 parts by mass of HAF (Asahi Carbon Co., Ltd., trade name “Asahi # 70”), stearic acid 3 Parts by mass, zinc oxide 5 parts by mass, hydrous silica (“Nipsil (registered trademark) AQ” manufactured by Tosoh Silica Co., Ltd.) 10 parts by mass, anti-aging agent for rubber (1) obtained in Production Example 1, 16 parts by mass, resorcin A rubber composition is obtained by kneading 2 parts by mass and 2 parts by mass of cobalt naphthenate within a range of 160 ° C. to 175 ° C. for 5 minutes at a rotation speed of a mixer of 50 rpm.
(Procedure 2)
The rubber composition obtained in Procedure 1 and N, N-dicyclohexyl-2-benzothiazolesulfenamide (DCBS) 1 as a vulcanization accelerator within the range of 60 ° C. to 80 ° C. in an open roll machine. A rubber kneaded material is obtained by kneading 3 parts by mass of 6 parts by mass of sulfur, 6 parts by mass of sulfur, and 3 parts by mass of a methoxylated methylol melamine resin (“SUMIKANOL 507AP” manufactured by Sumitomo Chemical Co., Ltd.).
<Second step>
The rubber kneaded material obtained in the first step (procedure 2) is heat-treated at 145 ° C. to obtain a vulcanized rubber composition.

Reference Example 7 (Production Example of Vulcanized Rubber Composition)
The vulcanized rubber composition obtained by the following first step and second step is suitable for an inner liner.
<First step>
(Procedure 1)
Using a Banbury mixer (600 ml Lab Plast Mill manufactured by Toyo Seiki Co., Ltd.), 100 parts by mass of halogenated butyl rubber (“Br-IIR2255” manufactured by ExxonMobil), 60 parts by mass of GPF, 1 part by mass of stearic acid, 3 parts by mass of zinc oxide, And 10 parts by mass of paraffin oil (“Diana Process Oil” manufactured by Idemitsu Kosan Co., Ltd.) is kneaded within a range of 160 ° C. to 175 ° C. for 5 minutes at a rotation speed of a mixer of 50 rpm to obtain a rubber composition.
(Procedure 2)
In the range of 60 ° C. to 80 ° C. with an open roll machine, the rubber composition obtained in Procedure 1, the anti-aging agent for rubber obtained in Production Example 1 (1), 2 parts by mass, and a vulcanization accelerator A rubber kneaded product is obtained by kneading 1 part by mass of a certain dibenzothiazyl disulfide (MBTS) and 2 parts by mass of sulfur.
<Second step>
A vulcanized rubber composition is obtained by heat-treating the kneaded product obtained in the first step (procedure 2) at 145 ° C.

Reference Example 8 (Production Example of Vulcanized Rubber Composition)
The vulcanized rubber composition obtained by the following first step and second step is suitable for side walls.
<First step>
(Procedure 1)
Using a Banbury mixer (600 ml Labo Plast Mill manufactured by Toyo Seiki Co., Ltd.), 40 parts by mass of commercially available natural rubber (RSS # 3), 60 parts by mass of polybutadiene rubber (“BR150B” manufactured by Ube Industries), 50 parts by mass of FEF, and stearic acid 2 0.5 parts by mass, 3 parts by mass of zinc oxide, 16 parts by mass of the anti-aging agent for rubber (1) obtained in Production Example 1, 10 parts by mass of aromatic oil (“NC-140” manufactured by Cosmo Oil Co., Ltd.) and wax A rubber composition was obtained by kneading 2 parts by mass (“Sannok (registered trademark) wax” manufactured by Ouchi Shinsei Chemical Industry Co., Ltd.) within the range of 160 ° C. to 175 ° C. for 5 minutes at a rotation speed of a mixer of 50 rpm. Get things.
(Procedure 2)
The rubber composition obtained in Procedure 1 and N-tert-butyl-2-benzothiazolylsulfenamide (BBS) 0. A rubber kneaded material is obtained by kneading 75 parts by mass and 1.5 parts by mass of sulfur.
<Second step>
The rubber kneaded material obtained in the first step (procedure 2) is heat-treated at 145 ° C. to obtain a vulcanized rubber composition.

Reference Example 9 (Production Example of Vulcanized Rubber Composition)
The vulcanized rubber composition obtained by the following first step and second step is suitable for carcass.
<First step>
(Procedure 1)
Using a Banbury mixer (600 ml Labo Plast Mill manufactured by Toyo Seiki Co., Ltd.), 70 parts by mass of commercially available natural rubber (TSR20), 30 parts by mass of styrene / butadiene copolymer rubber SBR # 1502 (manufactured by Sumitomo Chemical), N339 (Mitsubishi Chemical Corporation) 60 parts by mass, 2 parts by mass of stearic acid, 5 parts by mass of zinc oxide, 7 parts by mass of process oil (“Diana Process PS32” manufactured by Idemitsu Kosan Co., Ltd.) within a range of 160 ° C. to 175 ° C. for 5 minutes, 50 rpm A rubber composition is obtained by kneading at a rotational speed of the mixer.
(Procedure 2)
The rubber composition obtained in Procedure 1 and N-tert-butyl-2-benzothiazolylsulfenamide (BBS) 1 mass as a vulcanization accelerator within the range of 60 ° C. to 80 ° C. in an open roll machine. A rubber kneaded product is obtained by kneading 8 parts by mass of 3 parts by mass of sulfur, 3 parts by mass of sulfur and the anti-aging agent for rubber (1) obtained in Production Example 1.
<Second step>
The rubber kneaded product obtained in the first step (procedure 2) is heat-treated at 145 ° C. to obtain a vulcanized rubber.

Reference Example 10 (Production Example of Vulcanized Rubber Composition)
The vulcanized rubber composition obtained by the following first step and second step is suitable for cap treads.
<First step>
(Procedure 1)
Using a Banbury mixer (600 ml Laboplast Mill manufactured by Toyo Seiki Co., Ltd.), 100 parts by mass of styrene / butadiene copolymer rubber SBR # 1500 (manufactured by JSR), silica (trade name: “Ultrasil (registered trademark) VN3-G” Degussa 78.4 parts by mass, carbon black (trade name “N-339” manufactured by Mitsubishi Chemical Corporation), 6.4 parts by mass, silane coupling agent (bis (3-triethoxysilylpropyl) tetrasulfide: trade name “ 6.4 parts by mass of Si-69 “manufactured by Degussa), 47.6 parts by mass of process oil (trade name“ NC-140 ”manufactured by Cosmo Oil Co., Ltd.), anti-aging agent for rubber obtained in Production Example 1 (1 ) 12 parts by mass, 2 parts by mass of zinc oxide and 2 parts by mass of stearic acid were kneaded in the range of 70 ° C. to 120 ° C. for 5 minutes at a rotation speed of a mixer of 80 rpm, and subsequently 0 ℃ in the range of to 120 ° C., 5 min, by kneading at a rotation speed of 100rpm of mixer to obtain a rubber composition.
(Procedure 2)
The rubber composition obtained in step 1 and 1 part by mass of N-cyclohexyl-2-benzothiazolesulfenamide (CBS) as a vulcanization accelerator within the range of 30 ° C. to 80 ° C. in an open roll machine 1 part by weight of diphenylguanidine (DPG) as a vulcanization accelerator, 1.5 parts by weight of wax (trade name “Sannok (registered trademark) N” manufactured by Ouchi Shinsei Chemical Co., Ltd.) and 1.4 parts by weight of sulfur By kneading, a rubber kneaded product is obtained.
<Second step>
The rubber kneaded material obtained in the first step (procedure 2) is heat-treated at 160 ° C. to obtain a vulcanized rubber composition.

Reference Example 11 (Production Example of Vulcanized Rubber Composition)
In Reference Example 10, the same procedure as in Reference Example 10 was used except that solution-polymerized SBR (“ASAPREN (registered trademark)” manufactured by Asahi Kasei Chemicals) was used instead of styrene-butadiene copolymer rubber SBR # 1500 (manufactured by JSR). Thus, a vulcanized rubber composition is obtained. The obtained vulcanized rubber composition is suitable as a cap tread.

Reference Example 12 (Production Example of Vulcanized Rubber Composition)
In Reference Example 10, SBR # 1712 (manufactured by JSR) was used instead of styrene-butadiene copolymer rubber SBR # 1500 (manufactured by JSR), the amount of process oil used was changed to 21 parts by mass, and zinc oxide was charged. A vulcanized rubber composition is obtained in the same manner as in Reference Example 10 except that the timing is changed to Procedure 2. The obtained vulcanized rubber composition is suitable as a cap tread.

  Even if the anti-aging agent for rubber (1) is replaced with the anti-aging agent for rubber (2) or the anti-aging agent for rubber (3), the same results as in Reference Examples 5 to 12 are obtained.

  In the vulcanized rubber composition containing the rubber composition of the present invention, the durability of the anti-aging effect is improved.

1,2,3 Sheets manufactured from a vulcanized rubber composition containing an antioxidant for rubber 4,5,6 Sheets 7 manufactured from a vulcanized rubber composition not containing an antioxidant for rubber 7 Aluminum foil 8 Aluminum laminate 9 weight

Claims (12)

A rubber composition comprising a rubber anti-aging agent obtained by supporting a rubber anti-aging substance on mesoporous silica having a mesoporous pore volume exceeding 0.81 cm ³ / g, and a rubber component. That the anti-aging agent for rubber pore volume of mesopores and a 0.84 cm 3 / ^g or more 5.0 cm 3 / ^g or less is rubber anti-aging agent obtained by supporting the mesoporous silica and the rubber component The rubber composition according to claim 1, wherein In the solid state NMR measurement, the rubber anti-aging agent contains a peak chemical shift based on ¹³ C contained in the rubber anti-aging substance supported on silica contained in the rubber anti-aging substance not supported on silica ^13. The rubber composition according to claim 1 or 2, wherein the rubber composition is an anti-aging agent for rubber which is different from the chemical shift of the peak based on C.   The rubber composition according to any one of claims 1 to 3, wherein the mesoporous silica has a mesopore diameter of 6 nm to 50 nm. The rubber composition according to any one of claims 1 to 4, wherein the rubber anti-aging substance is a compound represented by the formula (I).

(In formula (I), R ¹ represents a hydrogen atom or an alkyl group having 1 to 13 carbon atoms.)   The rubber composition according to any one of claims 1 to 5, wherein the rubber composition contains 1 to 100 parts by mass of mesoporous silica with respect to 10 parts by mass of the anti-aging substance for rubber. A rubber anti-aging agent obtained by supporting a rubber anti-aging substance on mesoporous silica having a mesoporous pore volume exceeding 0.81 cm ³ / g, a rubber component, and a crosslinking agent. The rubber composition according to any one of claims 1 to 6.   A vulcanized rubber composition comprising the rubber composition according to claim 7.   A tire manufactured by processing the rubber composition according to claim 7.   A tire belt comprising a steel cord coated with the vulcanized rubber composition according to claim 8.   A carcass for a tire comprising a carcass fiber cord coated with the vulcanized rubber composition according to claim 8.   A tire sidewall, a tire inner liner, a tire cap tread, or a tire undertread comprising the vulcanized rubber composition according to claim 8.