JP2013063462A - Press forming method of longitudinally curving hat-shaped member - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a press forming method of a longitudinally curving hat-shaped member, which hardly causes a defective shape due to the spring back of a curve section provided so that a hat head has a protruding shape when viewed from a longitudinal wall direction (side).SOLUTION: In a press forming method of a longitudinally curving hat-shaped member, a metal plate is press-formed into the hat-shaped member that has a hat-shaped cross section with a height h and a curve section provided so that the hat head has a protruding shape when viewed from the longitudinal wall direction (side), so that a curvature radius R1 outside of the hat head of the curve section and a curvature radius R2 inside of a flange section of the curve section satisfy the relationship R1-R2>h.

Description

  The present invention relates to a press-forming method for a hat-shaped member using a metal plate, and more particularly to a press-forming method for a hat-shaped member curved in a longitudinal direction such that the hat head is convex when viewed from the vertical wall direction (side surface). .

  When a metal plate is press-molded using a mold in which punches and dies are arranged to face each other, the molded product after mold release will spring back or twist due to elastic recovery, and the specified dimensional accuracy cannot be obtained. It is well known that so-called shape defects occur.

  2. Description of the Related Art In recent years, in car body structural members of automobiles, in order to reduce the weight as a raw material, application of a high-tensile steel plate having a thin plate thickness or an aluminum alloy plate having a small specific gravity has been increasing. However, in the case of high-tensile steel plates and aluminum alloy plates, the problem of shape failure is highlighted, and several press forming methods that do not easily cause shape failure have been proposed. In particular, as a countermeasure against the slant of the vertical wall 2 and the angle defect of the corner of the hat head 1 that occur when press-molding a hat-shaped member having a hat-shaped cross section as shown in FIG. 1 restricts the inflow of the material flowing into the vertical wall portion 2 in the longitudinal direction of the flange portion 3 when the hat-shaped metal press part including the hat head 1, the vertical wall portion 2 and the flange portion 3 is drawn. A method of forming by forming a restraining portion (bead portion) is disclosed. Further, in Patent Document 2, when forming a metal member having a shape curved in the longitudinal direction with a hat-shaped cross section, the line length LW1 in the width direction in the intermediate product shape formed in the first forming step, and the product shape A press molding method is disclosed in which the relationship with the line length LW in the width direction is set to 0.9 <LW / LW1 <1.0, and the shape freezing property of the product shape is excellent.

JP 2006-281312 A JP 2010-064139

  However, as seen from the vertical wall direction (side view) as shown in Fig. 2 (a) perspective view, (b) top view, (c) side view, etc. For a hat-shaped member curved in the longitudinal direction having a curved portion 4 in which the hat head 1 becomes convex, the method described in Patent Document 1 and Patent Document 2 also results from springback in the curved portion 4 It is not possible to suppress the occurrence of defective shapes.

  The shape after press molding in Patent Document 2 is a convex shape when viewed from the hat head direction (upper surface), and the flange is on the same plane, and the shape is different from the present application.

  The present invention relates to a press molding method of a hat-shaped member curved in a longitudinal direction in which a shape defect caused by a spring back of a curved portion provided so that a hat head is convex when viewed from the vertical wall direction (side surface) hardly occurs. The purpose is to provide.

  As a result of intensive studies to achieve the above object, the present inventors have found that the curvature radius R1 on the hat head side of the convex curved portion and the curvature radius R2 on the flange portion side of the curved portion are R1-R2 > It has been found that it is effective to perform press molding so as to satisfy the relationship of h (hat height).

  The present invention was made based on such knowledge, the metal plate has a hat-shaped cross-sectional shape of height h, and the hat head is convex when viewed from the vertical wall direction (side surface). When press-molding into a hat-shaped member having a curved portion, the curvature radius R1 on the hat head side of the curved portion and the curvature radius R2 on the flange portion side of the curved portion satisfy the relationship of R1-R2> h. A press-molding method for a hat-shaped member curved in the longitudinal direction is provided.

  By the press molding method of the present invention, a hat-shaped member curved in the longitudinal direction is less likely to cause shape failure due to the spring back of the curved portion provided so that the hat head is convex when viewed from the vertical wall direction (side surface). Can be molded.

It is a figure which shows an example of a normal hat-shaped member. It is a diagram showing an example of a convex hat-shaped member as viewed from the vertical wall direction (side surface) targeted by the present invention, (a) is a perspective view, (b) is a top view, (c) is a side view. is there. FIG. 3 is a view showing a side surface of the hat-shaped member of FIG. It is a figure which shows typically the surplus part which arises in the hat head side of a curved part at the time of press molding by this invention. It is a figure which shows the definition of the springback amount (Sb) measured in the Example. It is a figure which shows the springback amount in the position along the longitudinal direction from an edge part.

  FIG. 3 shows a longitudinal section (side view) of the hat-shaped member corresponding to (c) of FIG. The hat-shaped member targeted by the present invention is convex when viewed from the vertical wall direction (side surface).

  Hereinafter, R1 is a radius of curvature outside the hat head 1, and R2 is a radius of curvature inside the flange portion 3.

  Usually, when press-molding a hat-shaped member having a height h curved in this way, the center of the curvature radius R1 on the outer side of the hat head 1 of the curved portion 4 and the radius of curvature on the inner side of the flange portion 3 of the curved portion 4 The centers of R2 are coincident, and the molding is performed under the condition satisfying the relationship of R1 = R2 + h. However, under such conditions, as described above, even if the method described in Patent Document 1 or Patent Document 2, tension in the longitudinal direction of the hat-type member acts on the curved portion 4 of the hat head 1, so that after molding, It is impossible to avoid the occurrence of a shape defect due to the springback that releases the residual stress and tries to restore it.

  However, if the blank material (steel plate) on the flat plate is pressed by the blank holder when it is molded under the condition satisfying the relationship of R1-R2> h as in the present invention, it is sandwiched between the punch head, the die and the blank holder. Since the gap formed between the steel plate and the steel plate is larger than that under the condition satisfying the relationship of R1 = R2 + h, the excess portion of the steel plate as shown in FIG. A gap is generated due to lack of familiarity. Then, the surplus portion is crushed in the direction toward the center of the curved portion by the punch and die near the bottom dead center of the molding, and is compressed in the longitudinal direction of the hat-shaped member. Since the residual stress is reduced and the spring back at the curved portion is reduced, the occurrence of shape defects is suppressed.

  The hat-shaped member targeted by the present invention is convex when viewed from the vertical wall direction (side surface), and the hat-shaped member shown in the conventional Patent Document 2 is viewed from the hat head direction (upper surface). Since it is a convex shape and the target shape is different, both springback control means are also different.

  Further, the curvature radius R1 on the outer side of the hat head 1 of the curved portion 4 is determined by the curvature radius of the punch head, and the curvature radius R2 on the inner side of the flange portion 3 of the curved portion 4 is determined by the curvature radius of the die. Can be changed independently.

  Actually, using a high strength steel plate with a tensile strength of 980 MPa and a thickness of 1.2 mm, R1 and R2 were changed, and a hat-shaped member with a height h of 50 mm curved in the longitudinal direction was press-formed with a wrinkle holding load of 30 tons. . Then, a spring back amount Sb (mm) at a position along the longitudinal direction from the end portion was measured. Here, as shown in FIG. 5, Sb is a displacement amount after spring back measured on the basis of a position (mold shape position) where it is assumed that no spring back occurs in the longitudinal section. It is.

  The results are shown in FIG.

  In CASE1, CASE4, and CASE5 that satisfy R1-R2> h, it is understood that Sb becomes smaller and shape defects are less likely to occur than in BASE that satisfies normal R1 = R2 + h.

  On the other hand, in CASE2 and CASE3 satisfying R1-R2 <h, Sb is larger than BASE and shape defects are likely to occur.

1 Hat head
2 Vertical wall
3 Flange
4 Curved part

Claims (1)

  When a metal plate is press-molded into a hat-shaped member having a hat-shaped cross-sectional shape having a height h and having a curved portion in which the hat head is convex along the longitudinal direction, the hat of the curved portion A longitudinally-curved hat-shaped member characterized in that the curvature radius R1 on the head side and the curvature radius R2 on the flange side of the curved portion are formed so as to satisfy the relationship of R1-R2> h. Press molding method.