JP2013059864A - Rustproof multilayer film - Google Patents
Rustproof multilayer film Download PDFInfo
- Publication number
- JP2013059864A JP2013059864A JP2011197955A JP2011197955A JP2013059864A JP 2013059864 A JP2013059864 A JP 2013059864A JP 2011197955 A JP2011197955 A JP 2011197955A JP 2011197955 A JP2011197955 A JP 2011197955A JP 2013059864 A JP2013059864 A JP 2013059864A
- Authority
- JP
- Japan
- Prior art keywords
- film
- rust
- pvdc
- rustproof
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、金属の防錆に関するものであり、更に詳しくは、金属製の機械や部品の保管中や輸送中における発錆を抑えるために使用する包装用の防錆積層フイルムに関するものである。 The present invention relates to rust prevention of metals, and more particularly, to a rust prevention laminated film for packaging used to suppress rusting during storage or transportation of metal machines and parts.
一般に、金属製の機械や部品の保管中や輸送中において、機械や部品の表面が酸化されて錆が発生するのを防ぐために、防錆包装が行われている。ＪＩＳ Ｚ−０３０３（さび止め包装方法通則）にはさび止め包装方法が規定され、防錆管理に幅広く利用されている。この通則には５．５．１さび止め処理材料として、さび止め油やさび止め剤（気化性、水溶性、気化性水溶性）が規定されており、更にはさび止め紙やさび止めフイルム、その他が規定されている。 In general, rust-proof packaging is performed in order to prevent the surfaces of machines and parts from being oxidized and rusting during storage and transportation of metal machines and parts. JIS Z-0303 (General Rules for Rust Prevention Packaging Method) defines a rust prevention packaging method and is widely used for rust prevention management. These general rules stipulate rust-preventing oil and rust-preventing agents (vaporizable, water-soluble, water-soluble water-soluble) as rust-proofing materials. Others are prescribed.
さび止め油は、金属製品をさび止め油に浸漬することにより行なうので、金属製品の細部までさび止め油が入り込み、防錆効果が高いものである。しかしながら、さび止め油から金属製品を取り出した後、２４時間程度油切りを施さなければならず、また、保管や輸送後、使用する前にさび止め油を洗浄する必要があり、多大の労力が掛かるとともに、コストが高くなるものであった。さらに、浄剤にフロン系の洗浄剤が用いられるので地球環境保全の問題があり、また、洗浄されたさび止め油の処理の問題があった。 Since rust prevention oil is performed by immersing a metal product in rust prevention oil, the rust prevention oil penetrates into the details of the metal product and has a high rust prevention effect. However, after removing the metal product from the rust-preventing oil, it must be drained for about 24 hours, and after storage and transportation, the rust-preventing oil must be washed before use. It took a lot of time and cost. In addition, since a fluorocarbon-based cleaning agent is used as a cleaning agent, there are problems in global environmental conservation, and there is a problem in the processing of the washed rust prevention oil.
そこで、近年、上述した問題点が無く、金属製品の細部まで入り込む利点がある気化性さび止め剤（以下、「気化性防錆剤」と言う）が多く使用されるようになって来た。気化性防錆剤は、常温で気化（昇華）して金属製品の細部まで入り込んで防錆効果を発揮するものであり、このような気化性防錆剤としては、鉄鋼用として亜硝酸塩を主体としたもの（特許文献１等参照）やアミン類を主体としたもの（特許文献２等参照）があり、銅用としてトリアゾール環等の複素環式化合物があり、これらの気化性防錆剤は各社から販売されている。
Therefore, in recent years, a vaporizable rust preventive agent (hereinafter referred to as “vaporizable rust preventive agent”) that does not have the above-described problems and has an advantage of entering even the details of metal products has been used. Vaporizable rust preventives are those that vaporize (sublimate) at room temperature to enter the details of metal products and exhibit rust prevention effects. As such vaporizable rust preventives, nitrite is mainly used for steel. (Refer to
このような気化性防錆剤の使用方法としては、気化性防錆剤を包装体内に直接散布したり、ガス透過性のある袋に詰めて包装体内に収納したり、気化性防錆剤を紙に塗布又は含浸させて防錆紙を製作し、この防錆紙で金属製品をラッピングしたり、気化性防錆剤を含有させた防錆フイルムを板紙に貼着させて防錆板紙を製作し、この防錆板紙で梱包箱を作り金属製品を梱包・密封したり（特許文献３等参照）、気化性防錆剤と低融点樹脂（エチレン−酢酸ビニル共重合樹脂）との２成分からなる均一混合組成物を高融点樹脂の基材フイルム上に積層したフイルムで袋を製作し、この防錆袋に金属製品を収納する方法が提案されている（特許文献４等参照）。
Such vaporizable rust preventives can be used by spraying the vaporizable rust preventive agent directly into the package, packing it in a gas-permeable bag and storing it in the package, or using a vaporizable rust preventive agent. Applying or impregnating paper to produce rust-proof paper, wrapping metal products with this rust-proof paper, or attaching rust-proof film containing vaporizable rust-proofing agent to paperboard to produce rust-proof paperboard And make a packing box with this rust-proof paperboard, and pack and seal metal products (see
しかしながら、気化性防錆剤を包装体内に直接散布したり、ガス透過性のある袋に詰めて包装体内に収納したり、気化性防錆剤を塗布又は含浸させた防錆紙でラッピングしたりする方法は、気化性防錆剤の気化したガスが包装体外に逃げ易く、気化性防錆剤が全て気化すると効果がなくなるので、防錆効果の持続性が短いものであった。また、防錆板紙からなる梱包箱を用いる方法は、板紙はポーラスであるので、気化した防錆剤が梱包箱から逃げ易く効果の持続性が短いものであった。 However, the vaporizable rust preventive agent can be sprayed directly into the package, packed in a gas permeable bag and stored in the package, or wrapped with rust preventive paper coated or impregnated with the vaporizable rust preventive agent In the method, the vaporized gas of the vaporizable rust preventive agent can easily escape to the outside of the package, and since the effect is lost when all of the vaporizable rust preventive agent is vaporized, the durability of the rust preventive effect is short. Further, in the method using a packaging box made of rustproof paperboard, since the paperboard is porous, the vaporized rustproofing agent easily escapes from the packaging box and has a short duration of effect.
さらに、気化性防錆剤と低融点樹脂との均一混合組成物を、高融点樹脂の基材フイルムに積層したフイルムからなる防錆袋で金属製品を収納する方法においては、基材フイルムとしてポリエチレンフイルム、ポリプロピレンフイルム、ポリエステルフイルム、ナイロンフイルム等を単独で用いていたので、気化した防錆剤を透過し易く、防錆効果の持続性が短いものであった。 Furthermore, in a method of storing metal products in a rust-proof bag made of a film in which a uniform mixture composition of a vaporizable rust inhibitor and a low-melting resin is laminated on a base film of a high-melting resin, polyethylene is used as the base film. Since a film, a polypropylene film, a polyester film, a nylon film, or the like was used alone, the vaporized rust preventive agent was easily transmitted, and the durability of the rust preventive effect was short.
特に、近年、金属製品に要求される防錆期間は、常温で数年間、海外へ輸送する際の赤道直下での船倉の条件（５０℃内外、高湿度）下で１ヶ月の防錆期間が望まれており、このような要求を満足することが出来なかった。 In particular, in recent years, the rust-prevention period required for metal products is as long as several months at room temperature and one month under the conditions of the hold (50 ° C inside and outside, high humidity) just below the equator when transporting overseas. It was desired and could not satisfy such a request.
本願発明は、以上の問題点を解決し、防錆効果を長期間維持出来るようにした防錆積層フイルムを提供することを目的とする。 An object of the present invention is to provide a rust-proof laminated film that solves the above-described problems and can maintain a rust-proofing effect for a long period of time.
本発明者らは、鋭意研究した結果、ピンホール発生がない二軸延伸ナイロンフイルム（以下、「Ｏ−ＮＹフイルム」と言う）に、ガスバリヤー性の優れたポリ塩化ビニリデン（以下、「ＰＶＤＣ」と言う）をコートしたＰＶＤＣコートＯ−ＮＹフイルムと、気化性防錆剤を混練したＬＤＰＥ樹脂又はＬＬＤＰＥ樹脂の防錆フイルムを貼り合せ、防錆フイルムを内側にして金属製品を収納すれば、防錆フイルムから気化した気化性防錆剤の気体がＰＶＤＣコート層により遮断され、外部に逃げることなく袋内に滞留して防錆効果を長期間に亘って発揮できることを見出し、本発明を完成するに至った。 As a result of diligent research, the present inventors have found that a biaxially stretched nylon film (hereinafter referred to as “O-NY film”) that does not generate pinholes and a polyvinylidene chloride (hereinafter referred to as “PVDC”) having excellent gas barrier properties. PVDC coated O-NY film coated with a rust preventive film of LDPE resin or LLDPE resin kneaded with a vaporizable rust preventive agent, and the metal product is stored with the rust preventive film inside. It is found that the gas of the vaporizable rust inhibitor vaporized from the rust film is blocked by the PVDC coat layer, stays in the bag without escaping to the outside, and can exhibit the rust preventive effect over a long period of time, thereby completing the present invention. It came to.
請求項１に係る防錆積層フイルムは、Ｏ−ＮＹフイルムにＰＶＤＣをコートしたＰＶＤＣコートＯ−ＮＹフイルムと、気化性防錆剤を混練した防錆フイルムとを有し、該防錆フイルムをＰＶＤＣコートＯ−ＮＹのＰＶＤＣコート面にドライラミネートで積層したことを特徴として構成されている。
The rust-proof laminated film according to
請求項２に係る防錆積層フイルムは、防錆フイルムが、ＬＤＰＥ樹脂又はＬＬＤＰＥ樹脂に防錆剤を混練し、インフレーション法で製膜されたことを特徴として構成されている。
The rust-proof laminated film according to
請求項３に係る防錆積層フイルムは、ドライラミネートの接着剤がポリエーテル系の主剤とイソシアネートの硬化剤とからなる二液硬化型の接着剤であることを特徴として構成されている。
The rust-proof laminated film according to
請求項１に係る防錆積層フイルムにおいて、Ｏ−ＮＹフイルムは揉みに強くピンホールが発生し難いものであり、ＰＶＤＣコート層はバスバリヤー性に優れているとともに、揉みに強くピンホールが発生し難いものであり、さらに、Ｏ−ＮＹフイルムとＰＶＤＣコート層とは接着強度が大きいので、ＰＶＤＣコート層がＯ−ＮＹフイルムから剥がれることが無い。防錆フイルムは混練された気化性防錆剤が気化して防錆フイルムの外部へ拡散していくものである。
In the rust-proof laminated film according to
したがって、防錆フイルムを内面に配置して袋を作製して密封包装した際、袋内部において気化した防錆剤を長期間に亘って保持することが出来る。すなわち、防錆フイルムに混練された気化性防錆剤は、時間の経過と共に気化し、防錆フイルムを透過して行くので、防錆フイルムの内面側（袋の内面側）においては、気化性防錆剤は袋内部に拡散して満たして行くが、防錆フイルムの外面側（袋の外面側）においては、ＰＶＤＣコート層が積層されているので、気化した気化性防錆剤はＰＶＤＣコート層により遮断される。したがって、気化した気化性防錆剤は、袋の内部にのみ蓄積されることとなり、防錆フイルムに混練した気化性防錆剤の固体と、袋内部の気化性防錆剤の気体との間が平衡状態になると、気化性防錆剤の固体は気化しないこととなる。その結果、この平衡状態が破れない限り、混練した気化性防錆剤の気化が抑制され、長期に亘って防錆効果を発揮することが出来る。 Therefore, when the rust preventive film is disposed on the inner surface and the bag is produced and hermetically packaged, the rust preventive agent vaporized inside the bag can be retained for a long period of time. That is, the vaporizable rust preventive agent kneaded in the rust preventive film evaporates over time and permeates the rust preventive film, so that it is vaporizable on the inner surface side of the rust preventive film (the inner surface side of the bag). The rust preventive agent diffuses and fills the inside of the bag, but on the outer surface side of the rust film (the outer surface side of the bag), since the PVDC coat layer is laminated, the vaporized rust preventive agent is the PVDC coat. Blocked by layers. Therefore, the vaporized rust preventive agent accumulates only inside the bag, and the gap between the vaporizable rust preventive agent kneaded in the rust preventive film and the gas inside the bag. When the is in an equilibrium state, the vaporizable rust preventive solid does not vaporize. As a result, as long as this equilibrium state is not broken, vaporization of the kneaded vaporizable rust inhibitor is suppressed, and a rust preventive effect can be exhibited over a long period of time.
また、物流過程において袋が揉まれたり、包装工程（真空包装等）において折り曲げられたりしても、Ｏ−ＮＹフイルム及びＰＶＤＣコート層にピンホールが発生することが無く、また、ＰＶＤＣコート層がＯ−ＮＹフイルムから剥離することも無い。したがって、外圧等により過酷な状態に晒されても、袋内に満たされた気化性防錆剤を安定して保持することが出来る。 Also, even if bags are squeezed in the distribution process or bent in the packaging process (vacuum packaging, etc.), no pinholes are generated in the O-NY film and the PVDC coating layer. There is no peeling from the O-NY film. Therefore, the vaporizable rust preventive agent filled in the bag can be stably held even when exposed to a severe state by external pressure or the like.
さらに、防錆フイルムとＰＶＤＣコートＯ−ＮＹフイルムとはドライラミネートで積層されているので、最も一般的に行われているフイルムの積層方法であり、簡単にコストも安く積層することが出来る。 Further, since the rust-proof film and the PVDC-coated O-NY film are laminated by dry lamination, it is the most commonly used film lamination method, and can be easily and inexpensively laminated.
請求項２に係る防錆積層フイルムにおいては、防錆フイルムは、ＬＤＰＥ樹脂又はＬＬＤＰＥ樹脂を用い、インフレーション法で製膜されているので、低温で製膜することが出来る。したがって、製膜時に、混練された気化性防錆剤の気化が小さく、大部分の気化性防錆剤を防錆フイルム中に残存させることが出来る。 In the rust-proof laminated film according to the second aspect, the rust-proof film is formed by an inflation method using an LDPE resin or an LLDPE resin, and thus can be formed at a low temperature. Therefore, the vaporization of the kneaded vaporizable rust inhibitor is small during film formation, and most of the vaporizable rust inhibitor can remain in the rust film.
請求項３に係る防錆積層フイルムにおいては、ドライラミネートの接着剤として、ポリエーテル系の主剤とイソシアネートの硬化剤とからなる二液硬化型の接着剤を用いているので、接着剤から錆を発生させる物質が発生することが無い。したがって、防錆剤の防錆硬化を十分に発揮させることが出来る。
In the rust-proof laminated film according to
本発明の防錆積層フイルムは、Ｏ−ＮＹフイルムにＰＶＤＣをコートしたＰＶＤＣコートＯ−ＮＹフイルムと、気化性防錆剤を混練した防錆フイルムとを積層したものであり、気化性防錆剤により金属製品の防錆を行なうものである。 The rust-proof laminated film of the present invention is a laminate of a PVDC-coated O-NY film obtained by coating PVDC on an O-NY film and a rust-proof film obtained by kneading a vaporizable rust preventive agent. This prevents rust of metal products.
金属は、金を除いて殆どの金属が何らかの化合物として存在している。例えば、鉄は磁鉄鉱、褐鉄鉱等の鉄鉱石として産出され、溶鉱炉等により精錬され鉄として得ている。この鉄の状態は準安定な状態であり、元の酸化された安定な状態に向かい進んでいく。空気中における酸化は化１に示すような反応式で進むと考えられている。 Most metals exist as a compound except gold. For example, iron is produced as iron ores such as magnetite and limonite, and is refined by a blast furnace or the like to obtain iron. This iron state is a metastable state and proceeds towards the original oxidized stable state. It is believed that oxidation in air proceeds according to the reaction formula shown in Chemical Formula 1.
この反応式から明らかなように、空気中に於いて鉄を酸化から守るには水及び酸素を排除すれば良いこととなる。したがって、金属製品をさび止め油に浸漬する防錆方法は、さび止め油の皮膜によって金属の表面を覆い、空気中の水分や酸素を遮断して酸化を防ぐ防錆方法である。 As is apparent from this reaction equation, water and oxygen can be excluded to protect iron from oxidation in the air. Therefore, the rust prevention method of immersing a metal product in rust prevention oil is a rust prevention method in which the surface of the metal is covered with a coating of rust prevention oil and moisture and oxygen in the air are blocked to prevent oxidation.
一方、防錆剤として気化性の防錆剤があり、鉄用としては、アミン類の亜硝酸塩類、アミン類のカルボン酸塩類、アミン類のクロム酸塩類、カルボン酸のエステル類、これらの混合物等がある。銅及び銅合金用としては、複素環状化合物であるトリアゾール環、ピロール環、ピラゾール環、チアゾール環、イミダゾール環やチオ尿素類、メルカプト基を有するもの等がある。これらの気化性防錆剤の防錆メカニズムは、鉄用のアミン類の亜硝酸塩類の場合、例えば気化したジシクロヘキシルアンモニウムナイトライトが鉄表面上に吸着された水分に溶解し、鉄と反応して安定的な皮膜を作ることにより防錆するものである（化２参照）。 On the other hand, there are vaporizable rust preventives as rust preventives. For iron, nitrites of amines, carboxylates of amines, chromates of amines, esters of carboxylic acids, and mixtures thereof Etc. For copper and copper alloys, there are a heterocyclic compound such as a triazole ring, a pyrrole ring, a pyrazole ring, a thiazole ring, an imidazole ring, a thiourea, or a mercapto group. In the case of nitrites of amines for iron, the rust prevention mechanism of these vaporizable rust preventives is, for example, that vaporized dicyclohexylammonium nitrite dissolves in moisture adsorbed on the iron surface and reacts with iron. Rust prevention is achieved by creating a stable film (see Chemical Formula 2).
また、アミンのカルボン酸塩類の場合、金属表面に吸着した水分に気化したガスが溶解し、水の中でアミンとカルボン酸に解離し、更に金属表面で再結合し、安定的なアミンのカルボン酸塩の皮膜を作って防錆すると考えられている（化３参照）。 In the case of amine carboxylates, the gas vaporized in the water adsorbed on the metal surface dissolves, dissociates into amine and carboxylic acid in the water, and recombines on the metal surface to form a stable amine carboxylate. It is thought to create an acid film and prevent rusting (see Chemical Formula 3).
さらに、銅用のベンゾトリアゾールの場合、金属表面に吸着した水分に気化したガスが溶解し、銅と反応して安定的なベンゾトリアゾール銅塩の皮膜を作って防錆すると考えられている（化４参照）。 Furthermore, in the case of benzotriazole for copper, it is thought that gas vaporized by moisture adsorbed on the metal surface dissolves and reacts with copper to form a stable benzotriazole copper salt film to prevent rusting. 4).
防錆フイルムに混練する気化性防錆剤は、防錆する金属製品が鉄製品であれば鉄用の気化防錆剤を主体に、銅又は銅合金製品であれば銅用の気化防錆剤を主体にし、必要によりこれらを混合して練り込むことが出来る。 Vaporizable rust preventives to be kneaded into rust preventive films are mainly vaporized rust preventives for iron if the metal product to be rusted is iron products, and vaporized rust preventive for copper if it is a copper or copper alloy product. Can be mixed and kneaded if necessary.
気化性防錆剤の混練量は、気化性防錆剤の持つ特質（気化速度、防錆効果）、要求される防錆期間、製膜方法、包装形態等により適宜最適に設定する。例えば、気化速度が速い場合は、防錆フイルムの製膜時に気化消失する量が多くなるので多く混練する必要があり、防錆効果が小さい場合は、所定の防錆効果を得るために多く混練する必要があり、また、製膜時の温度が高い製膜方法の場合は、損失を補填するために多く混練する必要がある。以上のように、各種条件を検討して適宜適切な混練量とする。 The kneading amount of the vaporizable rust inhibitor is appropriately set optimally depending on the characteristics (vaporization rate, rust prevention effect) of the vaporizable rust inhibitor, the required rust prevention period, the film forming method, the packaging form, and the like. For example, if the vaporization rate is high, the amount of vaporization disappears during film formation of the anticorrosive film, so it is necessary to knead a lot. In the case of a film forming method having a high temperature during film formation, it is necessary to knead a lot in order to compensate for the loss. As described above, various conditions are examined and an appropriate kneading amount is appropriately set.
気化性防錆剤の混練量は、上記条件を勘案すると、金属製品を２０℃−６０％ＲＨで３年間保管する場合、０．５〜５重量％が好ましく、１．０〜３．０重量％がより好ましい。混練量が０．５重量％未満であれば、気化速度の速い場合は製膜時の気化消失で不足となり、防錆効果の小さい場合は充分な防錆効果を期待することが出来ない。また、５重量％を超えると、充分な防錆効果は得られるがコストが高くなる。 In consideration of the above conditions, the kneading amount of the vaporizable rust preventive agent is preferably 0.5 to 5% by weight, preferably 1.0 to 3.0% when the metal product is stored at 20 ° C.-60% RH for 3 years. % Is more preferable. If the kneading amount is less than 0.5% by weight, if the vaporization rate is high, the vaporization disappears during film formation, and if the rust prevention effect is small, a sufficient rust prevention effect cannot be expected. On the other hand, if it exceeds 5% by weight, a sufficient rust prevention effect can be obtained, but the cost becomes high.
以上のような気化性防錆剤は、常温で固体から液体を経ずに直接気化（昇華）するものであり、温度が高くなればその気化速度も速くなる。したがって樹脂に混練して防錆フイルムを製膜する場合、出来るだけ低温で製膜する必要がある。したがって、製膜にはＴダイ法とインフレーション法とがあるが、インフレーション法が低温で製膜できるので好ましい。 The vaporizable rust preventive as described above is directly vaporized (sublimated) from a solid at room temperature without passing through a liquid, and its vaporization rate increases as the temperature increases. Therefore, when a rust-preventive film is formed by kneading with a resin, it is necessary to form the film at a temperature as low as possible. Therefore, although there are a T-die method and an inflation method for film formation, the inflation method is preferable because it can be formed at a low temperature.
また、低温で製膜できるので融点の低い樹脂が好ましく、例えば、ＬＤＰＥ樹脂、ＬＬＤＰＥ樹脂が好ましい。ＬＤＰＥ樹脂やＬＬＤＰＥ樹脂のインフレーション法による製膜においては、樹脂温度１５０〜２００℃の低温で製膜することができる。さらに、これらの樹脂は溶融張力が大きい方が好ましく、例えば、ＭＦＲは、０．１〜５ｇ／ｍｉｎの範囲が好ましく、０．５〜３ｇ／ｍｉｎの範囲がより好ましい。ＭＦＲは、０．１ｇ／ｍｉｎ未満であると、押出機のスクリーンに負荷がかかって押出しが難しくなり、また、５ｇ／ｍｉｎを超えると、溶融張力が小さく吹き上げたバブルが不安定となって均一な厚みが得られなくなる。 Moreover, since it can form into a film at low temperature, resin with low melting | fusing point is preferable, for example, LDPE resin and LLDPE resin are preferable. In the film formation by the inflation method of LDPE resin or LLDPE resin, the film can be formed at a low temperature of 150 to 200 ° C. Further, these resins preferably have a higher melt tension. For example, the MFR is preferably in the range of 0.1 to 5 g / min, and more preferably in the range of 0.5 to 3 g / min. When the MFR is less than 0.1 g / min, the extruder screen is loaded and it becomes difficult to extrude. When the MFR exceeds 5 g / min, the melt tension is small and the blown-up bubbles are unstable and uniform. Thickness cannot be obtained.
防錆フイルムの厚みは、２０〜１５０μｍが好ましく、３０〜１２０μｍがより好ましい。２０μｍ未満であるとインフレーション法で製膜することが難しくなり、１５０μｍを超えるとコストが高くなる。 20-150 micrometers is preferable and, as for the thickness of a rust prevention film, 30-120 micrometers is more preferable. When the thickness is less than 20 μm, it is difficult to form a film by the inflation method, and when it exceeds 150 μm, the cost increases.
ＰＶＤＣコートＯ−ＮＹフイルムは、揉みに極めて強いものであり、物流課程や真空包装工程におけるフイルムの折り曲げや揉まれでピンホールが発生することが無い。ＰＶＤＣコートＯ−ＮＹフイルムとＳｉＯｘの蒸着フイルムとの揉みに対する耐性に関し比較した試験について説明する。各フイルムのゲルボフレックステストの前後における酸素ガスバリヤー性及び水蒸気バリヤー性の変化により評価した。試験したフイルムは、以下の通りである。 The PVDC-coated O-NY film is extremely resistant to stagnation, and pinholes do not occur when the film is bent or entrapped in a physical distribution process or a vacuum packaging process. A test comparing the resistance against stagnation between the PVDC-coated O-NY film and the deposited film of SiOx will be described. Each film was evaluated by changes in oxygen gas barrier properties and water vapor barrier properties before and after the gelboflex test. The tested films are as follows.
Ｏ−ＮＹ／ＰＶＤＣ（コート）／ドライ／ＬＬＤＰＥ（５０μｍ）
Ｏ−ＮＹ／ＳｉＯｘ（蒸着）／ドライ／ＬＬＤＰＥ（５０μｍ）
ＰＥＴ／ＳｉＯｘ（蒸着）／ドライ／ＬＬＤＰＥ（５０μｍ）
結果を図１に示す。図１の結果より、Ｏ−ＮＹ／ＰＶＤＣ（コート）／ドライ／ＬＬＤＰＥ（５０μｍ）は、１００回のゲルボテスト後も酸素ガスバリヤー性及び水蒸気バリヤー性とも殆んど低下しないのが分かる。これに対し、ＰＥＴ／ＳｉＯｘ（蒸着）／ドライ／ＬＬＤＰＥ（５０μｍ）及びＯ−ＮＹ／ＳｉＯｘ（蒸着）／ドライ／ＬＬＤＰＥ（５０μｍ）は、１００回のゲルボフレックステスト後、酸素ガスバリヤー性及び水蒸気バリヤー性とも大幅に低下していることが分かる。これは、揉みにより蒸着ＳｉＯｘ層にクラックが入り、酸素ガスや、水蒸気が通り易くなったためである。したがって、蒸着ＳｉＯｘ層を有する積層フイルムは、防錆積層フイルムには使用できないことが分かる。
O-NY / PVDC (coat) / dry / LLDPE (50 μm)
O-NY / SiOx (deposition) / dry / LLDPE (50 μm)
PET / SiOx (deposition) / dry / LLDPE (50 μm)
The results are shown in FIG. From the results of FIG. 1, it can be seen that O-NY / PVDC (coat) / dry / LLDPE (50 μm) hardly deteriorates in oxygen gas barrier property and water vapor barrier property even after 100 gelbo tests. On the other hand, PET / SiOx (deposition) / dry / LLDPE (50 μm) and O-NY / SiOx (deposition) / dry / LLDPE (50 μm) have oxygen gas barrier properties and water vapor after 100 gelbo flex tests. It can be seen that the barrier properties are also greatly reduced. This is because the deposited SiOx layer is cracked by stagnation, and oxygen gas and water vapor easily pass through. Therefore, it turns out that the laminated | multilayer film which has a vapor deposition SiOx layer cannot be used for a rust prevention laminated | multilayer film.
酸素ガスバリヤー性に関しては、酸素透過度測定器（ＭＯＣＯＮ社製「ＯＸ−ＴＲＡＮ（登録商標）ＭＯＤＥＬ２／２１」）を用い、温度２０℃、湿度７０％ＲＨの条件で測定し、水蒸気バリヤー性に関しては、水蒸気透過度測定器（ＭＯＣＯＮ社製「ＯＸ−ＴＲＡＮ（登録商標）ＭＯＤＥＬ３／３３」）を用い、温度４０℃、湿度９０％ＲＨの条件で測定した。
Regarding the oxygen gas barrier property, the oxygen permeability measuring device (“OX-TRAN (registered trademark)
また、優れた酸素ガスバリヤー性を有するフイルムとしてＥＶＯＨフイルムが知られているが、その酸素ガスバリヤー性は湿度依存性があり、湿度６０％を超えると図２に示すように急激にその性能が低下し、高湿度下ではガスバリヤー性の機能を失っている。また、水蒸気バリヤー性はプラスチックフイルムの中で最も悪く、水蒸気の遮断性能はない。したがって、ＥＶＯＨフイルムは、本発明の防錆積層フイルムには使用できないものである。これに対し、ＰＶＤＣコート層は、ガスバリヤー性に湿度依存性はなく、高湿度下に於いても酸素ガスバリヤー性、水蒸気バリヤー性とも低下することなく安定的なガスバリヤー性を保つものである。 In addition, EVOH film is known as a film having excellent oxygen gas barrier properties. However, the oxygen gas barrier property is dependent on humidity, and when the humidity exceeds 60%, the performance rapidly increases as shown in FIG. The gas barrier function is lost under high humidity. Further, the water vapor barrier property is the worst among plastic films, and there is no water vapor blocking performance. Therefore, the EVOH film cannot be used for the rust-proof laminated film of the present invention. On the other hand, the PVDC coating layer does not depend on humidity in the gas barrier property, and maintains a stable gas barrier property without decreasing both the oxygen gas barrier property and the water vapor barrier property even under high humidity. .
本発明の防錆積層フイルムは、上述した防錆フイルムをＰＶＤＣコートＯ−ＮＹフイルムのＰＶＤＣコート面にドライラミネートにより積層したものである。ドライラミネートに使われる接着剤としては、ポリエーテル系の主剤とイソシアネートの硬化剤とからなる２液硬化型接着剤、ポリエステル系の主剤とイシシアネートの硬化剤とからなる２液硬化型接着剤がある。 The rust-proof laminated film of the present invention is obtained by laminating the above-mentioned rust-proof film on the PVDC-coated surface of the PVDC-coated O-NY film by dry lamination. Adhesives used for dry lamination include two-part curable adhesives composed of a polyether-based main component and an isocyanate curing agent, and two-part curable adhesives composed of a polyester-based main component and an isocyanate curing agent. is there.
代表的なポリエーテルとしては、エチレンオキシドやプロピレンオキシドの開環重合で作られるポエチレングリコールやポリプロピレングリコールがある。また、代表的なポリエステルとしては、多価アルコールのエチレングリコールや１．６ヘキサンジオールと、多価カルボン酸であるテレフタル酸やイソフタル酸やアジピン酸とから脱水縮合反応して作られるものがあり、特に代表的なのはエチレングリコールとテレフタル酸から作られるポリエチレンテレフタレートである。これら２種類の主剤の硬化剤としては、いずれもイソホロンジイソシアネート（ＩＰＤＩ）、ヘキサメチレンジイソシアネート（ＨＤＩ）、トルエンジイソシアネート（ＴＤＩ）がある。 Typical polyethers include polyethylene glycol and polypropylene glycol made by ring-opening polymerization of ethylene oxide and propylene oxide. Typical polyesters include those made by dehydration condensation reaction from polyhydric alcohols such as ethylene glycol and 1.6 hexanediol and polycarboxylic acids such as terephthalic acid, isophthalic acid and adipic acid, Particularly representative is polyethylene terephthalate made from ethylene glycol and terephthalic acid. As these two types of main curing agents, there are isophorone diisocyanate (IPDI), hexamethylene diisocyanate (HDI), and toluene diisocyanate (TDI).
このうちポリエステル系の主剤とイソシアネートの硬化剤からなる２液硬化型接着剤は、防錆効果を損ない、錆の発生を引き起こすものであった。すなわち、多価アルコールと多価カルボン酸から脱水縮合反応して作られるポリエステルの製造工程において脱水縮合反応の未反応物の多価カルボン酸が残留し、この残留した多価カルボン酸が接着剤層から防錆フイルムを透過して袋内面に移行するからだと考えられる。したがって、ポリエステル系の主剤とイソシアネートの硬化剤からなる２液硬化型接着剤は、本発明の防錆積層フイルムには使用できないものであった（表４参照）。 Of these, a two-component curable adhesive comprising a polyester-based main agent and an isocyanate curing agent impairs the rust prevention effect and causes rusting. That is, unreacted polyvalent carboxylic acid in the dehydration condensation reaction remains in the production process of the polyester produced by the dehydration condensation reaction from the polyhydric alcohol and the polyvalent carboxylic acid. It is thought that this is because it passes through the rust-proof film and moves to the inner surface of the bag. Therefore, the two-component curable adhesive comprising a polyester-based main agent and an isocyanate curing agent cannot be used for the rust-proof laminated film of the present invention (see Table 4).
これに対し、ポリエーテル系主剤とイソシアネートの硬化剤とからなる２液硬化型接着剤は、上述したような弊害はないものであり、本発明の防錆積層フイルムに好適なものであった。 On the other hand, a two-component curable adhesive comprising a polyether-based main component and an isocyanate curing agent does not have the above-described adverse effects, and is suitable for the rust-proof laminated film of the present invention.
本発明の防錆積層フイルムは、防錆フイルム面を内面側に、ＰＶＤＣコートＯ−ＮＹフイルムを外側に配置して袋状に形成し、この袋に金属製品を収納密封することにより使用する。このように使用することにより、防錆フイルムから気化した気化性防錆剤の気体は、袋内部に満たされるので、金属製品に防錆効果を発揮することが出来る。また、袋状の他、防錆効果を求められている分野に広く用いることが出来る。 The rust-proof laminated film of the present invention is used by forming a rust-proof film surface on the inner surface side and a PVDC-coated O-NY film on the outer side to form a bag, and housing and sealing the metal product in this bag. By using in this way, the gas of the vaporizable rust inhibitor evaporated from the rust preventive film is filled in the bag, so that the metal product can exhibit a rust preventive effect. Moreover, it can be widely used in the field | area where the antirust effect is calculated | required besides a bag shape.
［実施例１］
〔気化性防錆剤マスターバッチの作製〕
セバシン酸（豊国製油（株）製「ＨＯＫＯＫＵ−ＳＡ」）１モルに対して２モルのＫＯＨを、水存在下で混合反応させた後、スプレードライ方式で水分を蒸発・乾燥させて水分量０．５％以下にしたセバシン酸カリウムの結晶を得た。このセバシン酸カリウムと、ベンゾトリアゾール（キレスト（株）製「Ｃ．Ｖ．Ｉ．ＴＴ」）とを８０重量部：２０重量部の割合で混合し後、粉砕機で１００μｍ以下に粉砕して気化性防錆剤の混合組成物を得た。この混合組成物と、ＬＬＤＰＥ樹脂（（株）プライムポリマー製「ＳＰ２０２０」）とを３０重量部：７０重量部の割合でペレタイザー付の押出機に投入し、押出温度１５０℃で押出し、ペレタイズして気化性防錆剤を３０重量％含有した気化性防錆剤マスターバッチ（以下、「気化性防錆剤ＭＢ」と言う）を作製した。
[Example 1]
[Production of vaporizable rust inhibitor masterbatch]
After mixing and reacting 2 mol of KOH in the presence of water with respect to 1 mol of sebacic acid (“HOKOKU-SA” manufactured by Toyokuni Oil Co., Ltd.), the moisture content is evaporated and dried by a spray drying method. A crystal of potassium sebacate having a concentration of 5% or less was obtained. After mixing this potassium sebacate and benzotriazole ("CV I.TT" manufactured by Kyrest Co., Ltd.) at a ratio of 80 parts by weight: 20 parts by weight, the mixture is pulverized to 100 μm or less by a pulverizer and vaporized. A mixed composition of an anticorrosive agent was obtained. This mixed composition and LLDPE resin (“SP2020” manufactured by Prime Polymer Co., Ltd.) are charged into an extruder equipped with a pelletizer at a ratio of 30 parts by weight to 70 parts by weight, extruded at an extrusion temperature of 150 ° C., and pelletized. A vaporizable rust preventive masterbatch (hereinafter referred to as “vaporizable rust preventive MB”) containing 30% by weight of a vaporizable rust preventive was prepared.
〔防錆フイルムの作製〕
前記気化性防錆剤ＭＢと、ＬＬＤＰＥ樹脂（（株）プライムポリマー製「ＳＰ２０２０」（ＭＦＲ：２．３ｇ／１０ｍｉｎ、密度：０．９１５ｇ／ｃｍ３））とを５重量部：９５重量部の割合でドライブレンドして混合した。この混合した樹脂を空冷式のインフレーション成膜機に投入し、下記の条件でインフレーション成膜を行なった。得られたインフレーションフイルム（防錆フイルム）は、気化性防錆剤の含有率が１．５重量％、厚さ７０μｍであった。
[Production of rust-proof film]
5 parts by weight: 95 parts by weight of the vaporizable rust preventive MB and LLDPE resin (“SP2020” (MFR: 2.3 g / 10 min, density: 0.915 g / cm 3 ) manufactured by Prime Polymer Co., Ltd.) Dry blended at a ratio and mixed. This mixed resin was put into an air-cooled inflation film forming machine, and inflation film formation was performed under the following conditions. The obtained inflation film (rust preventive film) had a vaporizable rust preventive agent content of 1.5% by weight and a thickness of 70 μm.
シリンダー径： ６５ｍｍΦ、Ｌ／Ｄ；２５
丸ダイス径： ２００ｍｍΦ
リップキャップ： ０．８ｍｍ
押出温度： １６０℃
ブロー比： ２．５
冷却エアー： １５℃、流量；２０ｍ３／ｍｉｎ
製膜速度： １０ｍ／ｍｉｎ
Cylinder diameter: 65mmΦ, L / D; 25
Round die diameter: 200mmΦ
Lip cap: 0.8mm
Extrusion temperature: 160 ° C
Blow ratio: 2.5
Cooling air: 15 ° C., flow rate: 20 m 3 / min
Film forming speed: 10 m / min
〔防錆積層フイルムの作製〕
ＰＶＤＣコートＯ−ＮＹフイルム（ユニチカ（株）製「エンブレムＤＣＷＵ」（厚み：１５μｍ））を用意し、このＰＶＤＣコートＯ−ＮＹフイルムのＰＶＤＣコート面に５０Ｗ・分／ｍ２のコロナ処理を行った。次いで、ドライラミネート機（中島精機エンヂニアリング（株）製「ＬＸ−３」）にヘリオ彫刻によるスクリーン線数９５線のグラビアロールをセットし、ポリエーテル系接着剤（ロックペイント（株）製接着剤（主剤：ＲＵ−３６００、硬化剤：Ｈ−６８９、溶剤：酢酸エチルエステル））を、加工速度１００ｍ／ｍｉｎでＰＶＤＣコート面に塗布し、熱風温度６０℃、８０℃、７５℃の３ゾーンで乾燥させた。
[Preparation of rust-proof laminated film]
A PVDC-coated O-NY film (“Emblem DCWU” (thickness: 15 μm) manufactured by Unitika Ltd.) was prepared, and the PVDC-coated surface of this PVDC-coated O-NY film was subjected to a corona treatment of 50 W · min / m 2 . . Next, a gravure roll with 95 screen lines by helio engraving was set on a dry laminating machine (“LX-3” manufactured by Nakajima Seiki Engineering Co., Ltd.), and a polyether-based adhesive (adhesive manufactured by Rock Paint Co., Ltd.) Main agent: RU-3600, curing agent: H-689, solvent: ethyl acetate)) was applied to the PVDC coated surface at a processing speed of 100 m / min and dried in three zones of
次に、前記防錆フイルムを５０Ｗ・分／ｍ２でコロナ処理を行い、このコロナ処理面を、ＰＶＤＣコートＯ−ＮＹフイルムの接着剤塗布面と合わせ、ニップ圧１８ｋｇ−ｃｍの線圧で貼合・積層し、その後５０℃のエージング室で３日間エージングを行って防錆積層フイルムを作製した。 Next, the rust-proof film is subjected to corona treatment at 50 W · min / m 2 , the corona-treated surface is aligned with the adhesive-coated surface of the PVDC-coated O-NY film, and a nip pressure of 18 kg-cm is applied. Then, aging was performed in an aging chamber at 50 ° C. for 3 days to produce a rust-proof laminated film.
〔ラミネート強度試験〕
防錆積層フイルムを１５ｍｍ幅に切断した後、接着部分を手で剥離し、剥離した部分の双方（ＰＶＤＣコートＯ−ＮＹフイルムと防錆フイルム）を定速引張試験機のチャックに固定する。そして、初期チャック間を５０ｍｍとし、３００ｍｍ／ｍｉｎ．の引張速度で未剥離部分を水平に保ちながらＴ型剥離を行い、ＰＶＤＣコートＯ−ＮＹフイルムのＰＶＤＣコート層と防錆フイルム層との間のラミネート強度を測定した。結果を表１に示す。
[Lamination strength test]
After cutting the rust-proof laminated film to a width of 15 mm, the bonded part is peeled off by hand, and both peeled parts (PVDC-coated O-NY film and rust-proof film) are fixed to the chuck of a constant-speed tensile tester. Then, the gap between the initial chucks is set to 50 mm, and 300 mm / min. T-type peeling was carried out while keeping the unpeeled portion horizontal at a tensile speed of 1, and the laminate strength between the PVDC coat layer and the rust preventive film layer of the PVDC coat O-NY film was measured. The results are shown in Table 1.
ラミネート強度は包装材料としては充分な強度であった。 The laminate strength was sufficient as a packaging material.
〔ガスバリヤー性試験〕
防錆フイルムのガスバリヤー性を、酸素ガスバリヤー性に関しては、酸素透過度測定器（ＭＯＣＯＮ社製「ＯＸ−ＴＲＡＮ（登録商標）ＭＯＤＥＬ２／２１」）を用い、温度３０℃、湿度８０％ＲＨの条件で測定し、水蒸気バリヤー性に関しては、水蒸気透過度測定器（ＭＯＣＯＮ社製「ＯＸ−ＴＲＡＮ（登録商標）ＭＯＤＥＬ３／３３」）を用い、温度４０℃、湿度９０％ＲＨの条件で測定した。結果を表２に示す。
[Gas barrier property test]
Regarding the gas barrier property of the rust-proof film and the oxygen gas barrier property, an oxygen permeability measuring device (“OX-TRAN (registered trademark)
酸素ガスバリヤー性、水蒸気バリヤー性とも包装材料として充分な性能であり、特に水蒸気バリヤー性は、輸出における赤道直下での船倉の中の高温、高湿度下においても、水蒸気が透過して侵入することはないと考えられる。 Both oxygen gas barrier properties and water vapor barrier properties are sufficient as packaging materials, and in particular, water vapor barrier properties allow water vapor to permeate and penetrate even at high temperatures and high humidity in the hold just below the equator during export. It is not considered.
[比較例１]
実施例１の防錆積層フイルムに用いた防錆フイルムのみからなるものである。
[Comparative Example 1]
It consists only of the rust-proof film used for the rust-proof laminated film of Example 1.
[比較例２]
気化性防錆剤を混練していない他は、実施例１の防錆フイルムと同一条件で作製したＬＬＤＰＥフイルムのみからなるものである。
[Comparative Example 2]
Except not knead | mixing a vaporizable rust preventive agent, it consists only of the LLDPE film produced on the same conditions as the rust preventive film of Example 1. FIG.
〔防錆試験〕
ＳＰＣＣ（冷間圧延鋼板：６０×８０×１．２ｍｍ）、Ｃ１１００Ｐ（タフピッチ銅板：４０×６０×１．２ｍｍ）及び亜鉛板（旧２種：４０×６０×１．２ｍｍ）を＃２４０研磨紙で研磨した後、脱脂処理を行って試験片を用意した。また、実施例１、比較例１及び比較例２のフイルムを矩形にカットし、実施例１においては防錆フイルム面が内面になるようにして三方をヒートシールし、内寸９０×１１０ｍｍ及び内寸７０×９０ｍｍの２種類の大きさの袋をそれぞれ用意した。
[Rust prevention test]
SP240 (cold rolled steel plate: 60 × 80 × 1.2 mm), C1100P (tough pitch copper plate: 40 × 60 × 1.2 mm) and zinc plate (formerly 2 types: 40 × 60 × 1.2 mm) # 240 polished paper After polishing, the sample was prepared by degreasing. Further, the films of Example 1, Comparative Example 1 and Comparative Example 2 were cut into rectangles, and in Example 1, the three sides were heat-sealed so that the rust-proof film surface was the inner surface, and the inner dimension was 90 × 110 mm and the inner Two types of bags each having a size of 70 × 90 mm were prepared.
前記ＳＰＣＣの試験片は、内寸９０×１１０ｍｍの袋に収納し、前記Ｃ１１００Ｐ及び亜鉛板の試験片は、内寸７０×９０ｍｍの袋に収納し、含気包装（試験片が袋の内面に接触しないように空気を残す）と真空包装（試験片が袋の内面に接触するように空気を吸引する）との２種類の包装を行った。 The test piece of SPCC is housed in a bag with an inner dimension of 90 × 110 mm, the test piece of C1100P and the zinc plate is housed in a bag with an inner dimension of 70 × 90 mm, and the aerated packaging (the test piece is placed on the inner surface of the bag). Two types of packaging were performed: air was left so as not to contact) and vacuum packaging (air was sucked so that the test piece was in contact with the inner surface of the bag).
これら包装を行った試験片の防錆試験を、環境試験機（ＫＡＴＯ社製 「シルバリーエンペラー」）を用いて行った。環境試験機の温湿度条件は（５℃・９５％ＲＨ−６時間→５０℃・９５％ＲＨ−１６時間）を１サイクルとして、このサイクルを繰返しながら試験片表面を目視観察し、錆、腐食、変色状態を評価した。結果を表３に示す。 The rust prevention test of the test piece which carried out these packaging was performed using the environmental testing machine ("Silbury Emperor" made by KATO). The temperature and humidity conditions of the environmental tester are (5 ° C / 95% RH-6 hours → 50 ° C / 95% RH-16 hours) as one cycle, and the surface of the test piece is visually observed while repeating this cycle. The discoloration state was evaluated. The results are shown in Table 3.
評価は下記の通りである。
◎：腐食、錆、変色なし
○：極僅かな腐食（点錆１〜３個、変色面積１０％未満）
△：軽度の腐食（点錆４〜９個、変色面積１０〜３０％未満）
×：明確な腐食（点錆１０個以上、変色面積３０〜５０％未満）
××：激しい腐食（変色面積５０％以上）
Evaluation is as follows.
◎: Corrosion, rust, no discoloration ○: Slight corrosion (1 to 3 spot rust, discoloration area less than 10%)
Δ: Mild corrosion (4-9 spot rust, discoloration area less than 10-30%)
X: Clear corrosion (10 or more spot rust, discoloration area 30 to less than 50%)
XX: Severe corrosion (discolored area 50% or more)
表３の結果から判るように、実施例１は、防錆フイルムのみの比較例１に比べ、防錆効果がはるかに長く持続し、２０℃−６０％ＲＨ下で３年以上の保管が可能である。 As can be seen from the results in Table 3, Example 1 has a much longer antirust effect than Comparative Example 1 with only an anticorrosive film, and can be stored for 3 years or more at 20 ° C.-60% RH. It is.
これは防錆フイルムのみでは、袋内に気化した防錆剤がＬＬＤＰＥ層を透過して外部へ逃げて行くので、ＬＬＤＰＥ層に混練された気化性防錆剤が早く消失するのに対し、本発明品では、袋内に気化した防錆剤がＰＶＤＣコート層により遮断され、袋内に気化した防錆剤とＬＬＤＰＥ層に練り込まれた固体の防錆剤との間に平衡を保ち、混練された防錆剤（固体）の気化が抑制されるためである。 This is because the rust preventive agent vaporized in the bag passes through the LLDPE layer and escapes to the outside with the rust preventive film alone, whereas the vaporizable rust preventive agent kneaded in the LLDPE layer disappears quickly. In the invention, the rust preventive agent vaporized in the bag is blocked by the PVDC coating layer, and the rust preventive agent vaporized in the bag and the solid rust preventive agent kneaded in the LLDPE layer are balanced and kneaded. This is because vaporization of the applied antirust agent (solid) is suppressed.
［比較例３］
ＰＶＤＣコートＯ−ＮＹフイルムと防錆フイルムとをドライラミネートで貼合する際に使用する接着剤として、ポリエステル系接着剤（ロックペイント（株）製接着剤（主剤：ＲＵ−８０、硬化剤：Ｈ−５、溶剤：酢酸エチルエステル））を用いた他は、実施例１と全く同じ材料を用い、全く同様の工程で積層フイルムを作製した。
[Comparative Example 3]
As an adhesive used when bonding a PVDC coat O-NY film and a rust preventive film with a dry laminate, a polyester-based adhesive (an adhesive manufactured by Rock Paint Co., Ltd. (main agent: RU-80, curing agent: H -5, Solvent: Acetic acid ethyl ester)) was used, and a laminated film was prepared in exactly the same process using the same material as in Example 1.
[比較例４]
気化性防錆剤を混練していない他は、実施例１の防錆フイルムと同一条件で作製したＬＬＤＰＥフイルムのみからなるものである。
[Comparative Example 4]
Except not knead | mixing a vaporizable rust preventive agent, it consists only of the LLDPE film produced on the same conditions as the rust preventive film of Example 1. FIG.
〔防錆試験〕
実施例１の場合と同様に、ＳＰＣＣとＣ１１００Ｐの試験片を用意するとともに、２種類の大きさの袋用意し、含気包装及び真空包装を行い、環境試験機（ＫＡＴＯ社製 「シルバリーエンペラー」）により同一の条件で試験し、試験片の表面の錆、腐食、変色状態を評価した。評価基準は同一である。防錆試験の結果を表４に示す。
[Rust prevention test]
As in the case of Example 1, SPCC and C1100P test pieces were prepared, bags of two sizes were prepared, aerated packaging and vacuum packaging were performed, and an environmental tester (“Silverly Emperor” manufactured by KATO) was used. )) Under the same conditions, and the rust, corrosion, and discoloration of the surface of the test piece were evaluated. The evaluation criteria are the same. Table 4 shows the results of the rust prevention test.
ＳＰＣＣの項の結果より、比較例３は防錆フイルムを積層しているにもかかわらず、比較例４よりも錆の発生が早く、しかも含気包装と真空包装を比べると、フイルムが試験片に接触する真空包装の方が錆の発生が早いことが確認された。この結果より、比較例３は錆の発生を促す要因があると考えられる。実施例１のポリエーテル系接着剤ではこのような現象が起こらないので、ポリエステル系接着剤に由来すると考えられる。すなわちポリエステル系接着剤の主剤の作製工程において、多価アルコールと多価カルボン酸との脱水縮合反応の未反応物である多価カルボン酸が残留し、ドライラミネートで貼合した接着剤層から多価カルボン酸が防錆フイルムを透過して袋内に移行し、試験片の表面に付着して錆の発生を促すものと考えられる。 From the results of the SPCC section, although Comparative Example 3 is laminated with a rust-proof film, rust is generated faster than Comparative Example 4, and the film is a test piece when compared with aerated packaging and vacuum packaging. It was confirmed that the rust was generated earlier in the vacuum packaging in contact with From this result, it is considered that Comparative Example 3 has a factor that promotes the generation of rust. Since such a phenomenon does not occur in the polyether-based adhesive of Example 1, it is considered that it is derived from the polyester-based adhesive. That is, in the production process of the main component of the polyester-based adhesive, the polyvalent carboxylic acid, which is an unreacted product of the dehydration condensation reaction between the polyhydric alcohol and the polyvalent carboxylic acid, remains, and a large amount is obtained from the adhesive layer bonded by dry lamination. It is considered that the monovalent carboxylic acid passes through the rust-proof film and moves into the bag, adheres to the surface of the test piece, and promotes the generation of rust.
Claims (3)