JP2012255214A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2012255214A5 JP2012255214A5 JP2012167264A JP2012167264A JP2012255214A5 JP 2012255214 A5 JP2012255214 A5 JP 2012255214A5 JP 2012167264 A JP2012167264 A JP 2012167264A JP 2012167264 A JP2012167264 A JP 2012167264A JP 2012255214 A5 JP2012255214 A5 JP 2012255214A5
- Authority
- JP
- Japan
- Prior art keywords
- mass
- aluminum alloy
- alloy plate
- less
- rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
Claims (13)
Fe:0.05〜0.60質量%,
Cu:0.70超〜1.0質量%未満,
Mn:0.10〜1.80質量%,
Mg:0.70超〜1.50質量%,
Zr:0.10超〜0.20質量%未満,
Ti:0.03〜0.25質量%であって、
残部Alおよび不可避的不純物からなり、ケース成形前に人工時効処理されていないことを特徴とする電池ケース用アルミニウム合金板。 Si: 0.10 to 0.60 mass%,
Fe: 0.05-0.60 mass%,
Cu: more than 0.70 to less than 1.0% by mass,
Mn: 0.10 to 1.80% by mass,
Mg: more than 0.70 to 1.50% by mass,
Zr: more than 0.10 to less than 0.20% by mass,
Ti: 0.03 to 0.25% by mass,
An aluminum alloy plate for a battery case, comprising the balance Al and unavoidable impurities and not subjected to artificial aging treatment before the case is formed.
該鋳塊に500〜600℃で1時間以上保持する均質化処理を施した後、
430〜560℃の温度で熱間圧延を開始して熱延板とし、
圧延率50%以上で冷間圧延を施した後、
中間焼鈍を施し、
さらに圧延率10〜60%の最終冷間圧延を施す、
ことを特徴とする電池ケース用アルミニウム合金板の製造方法。 An ingot is produced by casting a molten aluminum alloy having the composition according to claim 1 by a semi-continuous casting method,
After subjecting the ingot to a homogenization treatment of holding at 500 to 600 ° C. for 1 hour or longer,
Hot rolling is started at a temperature of 430 to 560 ° C. to form a hot rolled sheet,
After cold rolling at a rolling rate of 50% or more,
Intermediate annealing,
Furthermore, the final cold rolling with a rolling rate of 10 to 60% is performed.
The manufacturing method of the aluminum alloy plate for battery cases characterized by the above-mentioned.
該鋳塊に500〜600℃で1時間以上保持する均質化処理を施した後、
430〜560℃の温度で熱間圧延を開始して熱延板とし、
圧延率50%以上で冷間圧延を施した後、
中間焼鈍を施し、
さらに圧延率10〜60%の最終冷間圧延を施す、
ことを特徴とする電池ケース用アルミニウム合金板の製造方法。 An ingot is produced by casting a molten aluminum alloy having the composition according to claim 2 by a semi-continuous casting method,
After subjecting the ingot to a homogenization treatment of holding at 500 to 600 ° C. for 1 hour or longer,
Hot rolling is started at a temperature of 430 to 560 ° C. to form a hot rolled sheet,
After cold rolling at a rolling rate of 50% or more,
Intermediate annealing,
Furthermore, the final cold rolling with a rolling rate of 10 to 60% is performed.
The manufacturing method of the aluminum alloy plate for battery cases characterized by the above-mentioned.
該鋳塊に500〜600℃で1時間以上保持する均質化処理を施した後、
430〜560℃の温度で熱間圧延を開始して熱延板とし、
圧延率50%以上で冷間圧延を施した後、
中間焼鈍を施し、
さらに圧延率10〜60%の最終冷間圧延を施す、
ことを特徴とする電池ケース用アルミニウム合金板の製造方法。 An ingot is produced by casting a molten aluminum alloy having the composition according to claim 3 by a semi-continuous casting method,
After subjecting the ingot to a homogenization treatment of holding at 500 to 600 ° C. for 1 hour or longer,
Hot rolling is started at a temperature of 430 to 560 ° C. to form a hot rolled sheet,
After cold rolling at a rolling rate of 50% or more,
Intermediate annealing,
Furthermore, the final cold rolling with a rolling rate of 10 to 60% is performed.
The manufacturing method of the aluminum alloy plate for battery cases characterized by the above-mentioned.
Fe:0.05〜0.60質量%,Fe: 0.05-0.60 mass%,
Cu:0.70超〜1.0質量%未満,Cu: more than 0.70 to less than 1.0% by mass,
Mn:0.10〜1.80質量%,Mn: 0.10 to 1.80% by mass,
Mg:0.70超〜1.50質量%,Mg: more than 0.70 to 1.50% by mass,
Zr:0.10超〜0.20質量%未満,Zr: more than 0.10 to less than 0.20% by mass,
Ti:0.03〜0.25質量%であって、Ti: 0.03 to 0.25% by mass,
残部Alおよび不可避的不純物からなるアルミニウム合金板であって、An aluminum alloy plate comprising the balance Al and inevitable impurities,
ケース成形後、人工時効処理されてT8材となっていることを特徴とする電池ケース用アルミニウム合金板。An aluminum alloy plate for a battery case, which has been subjected to artificial aging treatment after forming the case to become a T8 material.
Fe:0.05〜0.60質量%,Fe: 0.05-0.60 mass%,
Cu:0.70超〜1.0質量%未満,Cu: more than 0.70 to less than 1.0% by mass,
Mn:0.10〜1.80質量%,Mn: 0.10 to 1.80% by mass,
Mg:0.70超〜1.50質量%,Mg: more than 0.70 to 1.50% by mass,
Zr:0.10超〜0.20質量%未満,Zr: more than 0.10 to less than 0.20% by mass,
Ti:0.03〜0.25質量%であって、Ti: 0.03 to 0.25% by mass,
残部Alおよび不可避的不純物からなるアルミニウム合金板であって、An aluminum alloy plate comprising the balance Al and inevitable impurities,
複数段で深絞り成形し、最終過程でしごき成形するD1成形によるケース成形後、人工時効処理されていることを特徴とする電池ケース用アルミニウム合金板。An aluminum alloy plate for a battery case, which is subjected to artificial aging treatment after case forming by D1 forming, which is deep-drawn in a plurality of stages and ironed in the final process.
Fe:0.05〜0.60質量%,Fe: 0.05-0.60 mass%,
Cu:0.70超〜1.0質量%未満,Cu: more than 0.70 to less than 1.0% by mass,
Mn:0.10〜1.80質量%,Mn: 0.10 to 1.80% by mass,
Mg:0.70超〜1.50質量%,Mg: more than 0.70 to 1.50% by mass,
Zr:0.10超〜0.20質量%未満,Zr: more than 0.10 to less than 0.20% by mass,
Ti:0.03〜0.25質量%であって、Ti: 0.03 to 0.25% by mass,
残部Alおよび不可避的不純物からなるアルミニウム合金板であって、An aluminum alloy plate comprising the balance Al and inevitable impurities,
最終冷延率10〜60%で最終冷間圧延された冷延まま材をケース成形した後、人工時効処理されていることを特徴とする電池ケース用アルミニウム合金板。An aluminum alloy plate for a battery case, which is subjected to artificial aging treatment after forming a case of a cold-rolled material that has been finally cold-rolled at a final cold rolling rate of 10 to 60%.