Abstract

PROBLEM TO BE SOLVED: To create the layer configuration which is excellent in productivity of a label itself, and superior in productivity and sticking properties of an in-mold molding in an in-mold label for a polypropylene resin container.SOLUTION: In an in-mold label, the layer configuration is formed by laminating a printing layer and an anchor coat layer in this order on the surface of an adhesion layer made of a synthetic resin film, and further laminating a protective layer made of a low-density polyethylene resin thereon by an extrusion lamination method, and a polyethylene resin-based film is excluded from the synthetic resin film.

Description

The present invention relates to an in-mold label and a labeled container.

As a means to achieve the display of decorations, product names, and explanations on the surface of synthetic resin molded products such as synthetic resin blow molded containers Is frequently used.
In addition, as one of the methods for attaching the label, a so-called in-mold label is set in the mold in advance as an insert material, and the in-mold is attached to the surface of the molded product in-mold at the same time as the molded product is molded. There is a molding method.

With this in-mold molding method, label sticking is achieved simultaneously with molding of the molded product, and there is no need for a separate separate sticking operation, and there is a step between the surface of the molded product and the in-mold label. Therefore, there is absolutely no risk of deterioration of the appearance or tactile sensation of the molded product due to this level difference, and for example, ensuring a strong and stable sticking of the in-mold label to the container body regardless of the thinning of the blow molded container It has an excellent effect that it can be obtained.
For example, Patent Document 1 describes an invention relating to an in-mold label, a blow-molded article with a label, and a method for manufacturing the same.

FIG. 7 is a cross-sectional view showing an example of a layer structure of an in-mold label that has been generally used conventionally (hereinafter, sometimes simply referred to as a label).
The label 111 is a back side of a transparent base layer 113 made of an unstretched cast film made of polypropylene (hereinafter may be abbreviated as PP) (hereinafter also abbreviated as CPP film). A printing layer 114 by gravure printing is laminated, an anchor coat (hereinafter sometimes abbreviated as “AC”) agent is applied, an AC layer 115 is laminated, and a low density polyethylene (hereinafter abbreviated as “LDPE”). There is a layer structure in which a resin adhesive layer 112 is laminated by an extrusion laminating method, and is affixed to a peripheral wall of a polyethylene container body (hereinafter abbreviated as PE) by an in-mold molding method. Is done.
In addition, this type of label can make the adhesive surface uneven by embossing or provide many small holes that penetrate the entire label, suppressing the occurrence of air accumulation during in-mold molding, and sufficient adhesion Property can be obtained, and a good appearance can be obtained.

JP 2004-136486 A

Here, according to the label layer structure as shown in FIG. 7 or the manufacturing method, there is no problem in the case of a label for a container made of PE resin, but for a container made of PP resin other than PE resin, for example. In this case, the resin of the adhesive layer 112 must be a PP resin and laminated by an extrusion laminating method.
However, compared to the use of extrusion lamination of PE resin, there is almost no use of extrusion lamination of resins different from PE, such as PP, and productivity will be improved if extrusion lamination of resins other than PE is attempted. Ignoring it, it was necessary to change the resin to be extruded and laminated from PE resin to another resin, or to install a dedicated machine at a high cost.

On the other hand, as a method for laminating the adhesive layer, there are a method of laminating an adhesive film on the base film layer by a dry laminating method, and a method of applying a heat-sensitive adhesive to the base layer in addition to the extrusion laminating method.
However, when laminating an adhesive film to be an adhesive layer on a base material layer by the dry laminating method, it is difficult to adjust the tension at the time of dry laminating unless the film to be the base material layer has a certain thickness, and the label is curled. Will occur.
On the other hand, when the total thickness of the label is increased by increasing the thickness of the base material layer and the adhesive film, the shrinkage of the peripheral wall of the body part is different in the label attaching region compared to other regions, In particular, when the peripheral wall of the container is thin, there is a problem that the peripheral wall is significantly deformed near the end of the label.
For this reason, in the label in which the adhesive layer is laminated by the dry laminating method, it is difficult to prevent both the label curling and the deformation of the container due to the sticking due to restrictions derived from the label manufacturing method, and it has been put into practical use. However, there is a problem that the productivity is low and the cost is high.
In addition, according to the method of applying the heat-sensitive adhesive, the adhesive layer cannot be thickened, so that the adhesive force is insufficient, and the depth of the emboss cannot be increased sufficiently, so that air accumulation occurs.

Accordingly, the present invention relates to an in-mold label for a resin container other than a PE-based one having the above-mentioned problems, and creates a layer structure excellent in productivity of the label itself, productivity of in-mold molding, and stickability. This is a problem.

The present invention relates to an in-mold label and a labeled container,
The main structure of the in-mold label of the present invention according to the means for solving the above problems is as follows:
It has a layer structure in which a printed layer and an anchor coat layer are laminated in this order on the surface side of an adhesive layer made of a synthetic resin film, and further a protective layer made of a low density polyethylene resin by an extrusion lamination method is laminated,
That is, the synthetic resin film is a film other than polyethylene resin.

Here, the film that forms the adhesive layer of the label having the above-described configuration is the same system as the surface to be bonded of the synthetic resin molded product to be bonded, and other than the PE system that can be directly heat-sealed to this bonding surface. Selected from
The label is made of LDPE resin by forming a printed layer on the surface side of the film other than the PE system by gravure printing or the like, and then laminating an AC layer on the printed layer, and then extruding and laminating the AC layer on the AC layer. It is manufactured by laminating a protective layer.
Here, when printing on the film which forms an adhesive layer, it is preferable to corona-treat the printing surface.
Usually, application of the AC agent and extrusion lamination are carried out in a continuous process, and the AC layer is formed immediately before the protective layer is extrusion laminated.
In order to prevent dust and the like from adhering to the surface of the label attached to the container body, and to prevent the surface of the label aligned in the holder and the back of the label from adhering due to static electricity, An antistatic agent may be kneaded into the LDPE resin that forms, or an antistatic agent may be applied to the surface of the protective layer.

  Another configuration of the in-mold label of the present invention is that the synthetic resin film is a polypropylene resin cast film in the above main configuration, and is a label for a PP resin molded product.

  Moreover, in the label of this invention, it is preferable to have the unevenness | corrugation by embossing in the back surface side of an contact bonding layer.

Moreover, the main structure of the labeled container of the present invention is:
In a container in which an in-mold label is pasted simultaneously with blow molding by the in-mold molding method on the peripheral wall of the body portion of the synthetic resin container body,
The container body is made of synthetic resin other than polyethylene resin,
The in-mold label is laminated in the order of the printed layer and the anchor coat layer on the surface side of the adhesive layer made of a synthetic resin film that is the same as the container body and can be directly heat-sealed to the peripheral wall of the body of the container body. It has a layer structure in which a protective layer made of a low-density polyethylene resin by a method is laminated.

The other configuration of the labeled container of the present invention is the main configuration described above,
The container body is made of polypropylene resin, and the adhesive layer of the in-mold label is made of polypropylene resin cast film.

  The labeled container of the present invention is a thin container with an average wall thickness of the peripheral wall of the container body of 0.8 mm or less, and its effects are effectively exhibited.

Here, in the configuration of the present invention, the PE resin is an ethylene homopolymer or a copolymer containing ethylene as a main component, and the copolymer component includes an α-olefin having 3 to 20 carbon atoms (for example, Propylene, 1-butene, 1-pentene, 1-hexene, 4-methylpentene-1, 1-octene, etc.), vinyl acetate, and the like, and include categories ranging from high density polyethylene to low density polyethylene.
Examples of the synthetic resin that forms the container body other than the PE resin include the above-described PP resin, polyester resin typified by polyethylene terephthalate resin, polystyrene resin, and polyamide resin.
Moreover, as a film which forms a contact bonding layer, the film which consists of resin of the same series etc. can be selected according to the synthetic resin which forms the above-mentioned container main body.

Regarding labels used for containers with in-mold labels, considering the elements and problems described in 1) to 8) below, the structure of the label such as the laminated structure, the material of each layer, the layer thickness, etc. It is necessary to select a manufacturing method and a processing method.
1) Productivity of label manufacturing process or processing process 2) Curl property of label 3) In in-mold molding, labels are aligned in a predetermined holder and are fed into a mold continuously and reliably. 4) Generation of wrinkles on the label due to contact of the molten resin at high temperature with fluid deformation and generation of air accumulation 5) Cooling and solidification of the resin in the mold and after molding Deformation of container accompanying shrinkage 6) Adhesiveness of label to container surface 7) Container due to drop impact caused by notch-shaped groove having V-shaped cross section formed at boundary between label end and container body 8) Label appearance (gloss, transparency, etc.)

  In particular, in the case of a thin-walled container having an average wall thickness of the body wall of the container body of 0.8 mm or less, the problem of wrinkles and air accumulation described in 4), deformation of the container described in 5), and 7) Since the problem of the cracking of the container due to the drop impact described remarkably appears, it is necessary to design the layer structure of the label from a viewpoint different from the case where the peripheral wall is thick.

Therefore, for the laminated structure of the label of the present invention described above,
A printed layer is formed on the surface side of a commercially available synthetic resin film having an appropriate thickness by printing such as gravure printing, and then an AC layer is laminated on the printed layer. By laminating a PE-based resin extrusion laminating device and an LDPE resin layer that serves as a protective layer using the manufacturing process, a dedicated machine can be used with high productivity and at a high cost. There is no need for installation, and it can be manufactured at low cost.

Further, in the configuration related to the label, the protective layer made of LDPE resin is laminated by the extrusion laminating method, so that there is no concern about the decrease in productivity related to curling or the like in the laminating process as in the case of the dry laminating method. It can be formed thin as long as it exhibits the function of protecting the printing layer, called a protective layer.
For this reason, within the range in which the total thickness of the label is not excessively increased, the adhesive layer made of CPP film can be thickened to exhibit the function as a base material layer for maintaining the strength and rigidity of the entire label. it can.

  And since the thickness of the whole label is almost determined by the adhesive layer that also functions as the base material layer as described above, the problem is that if the thickness is too thin, the supply of the label in in-mold molding cannot be performed properly and accurately. On the other hand, if the container is too thick, the peripheral wall may be deformed, particularly if the container is thin, or the peripheral wall becomes a V-shaped notch-shaped groove at the end of the label and the drop impact strength is reduced. In consideration of such problems, it is possible to provide a label having an optimum laminated structure by selecting a film having an appropriate thickness from commercially available CPP films.

In addition, since the thickness of the adhesive layer can be made relatively thick as described above, it becomes possible to secure a sufficient depth of unevenness by embossing, and air pools and wrinkles are generated during in-mold molding. Can be effectively suppressed.
For example, an adhesive layer made of a CPP film is firmly bonded and fixed to the peripheral wall made of PP resin under a pressure acting during in-mold molding.
In addition to embossing, there are methods for forming a large number of small holes in the label and letting the air escape from these holes as means for suppressing the occurrence of the above-mentioned air accumulation.

In addition, in the said structure or the following description, in order to clarify the relative positional relationship of each layer which a label laminates, the term of the surface side or a back surface side is used, but the back surface side sticks to a molded article. It corresponds to the surface side, and the surface side corresponds to the opposite side.
In the above configuration, the AC layer is a layer having a function of sufficiently exerting the adhesiveness between the printed layer and the protective layer, or the adhesive layer and the protective layer, and is bonded with organic titanate, organic isocyanate, polyethyleneimine, or the like. It is formed by applying an anchor coating agent mainly composed of an agent.

Since the label and the container with a label according to the present invention have the above-described configuration, the following effects can be obtained.
In the label of the present invention, a printed layer is formed on the surface side of a commercially available synthetic resin film having an appropriate thickness by printing such as gravure printing, and then an AC layer is laminated on the printed layer. From the top, by laminating a PEPE resin extrusion laminating apparatus that has been generally used from the top and the LDPE resin layer that serves as a protective layer using its manufacturing process, high productivity and a large amount of cost are newly added. Therefore, it is not necessary to install a dedicated machine and it can be manufactured at a low cost.

In addition, since the thickness of the entire label is almost determined by the adhesive layer, the depth of unevenness due to embossing associated with air stagnation and wrinkles, label supply in in-mold molding, as well as container deformation problems and label Considering the problem that the peripheral wall becomes notched at the end, etc., by selecting a film with an appropriate thickness from commercially available synthetic resin films, it is possible to provide a label with an optimal laminated structure,
As a result, it is possible to provide a thin-label container with a good appearance that adheres firmly to the surface of the container body other than the PE-based resin and does not deform, while taking advantage of the characteristics of the in-mold molding method. .

It is a front view which shows one Example of the container with a label of this invention. It is a plane sectional view shown along the AA line in FIG. It is sectional drawing which shows the layer structure of one Example of the label of this invention used for the container of FIG. 1, (a) is layer structure before laminating | stacking AC layer and a protective layer, (b) is AC structure. The layer structure after laminating | stacking a layer and a protective layer and giving an embossing to an adhesive surface is shown. It is a schematic explanatory drawing which shows an example of the deformation | transformation aspect of a container in a plane cross section. It is a schematic explanatory drawing which shows an example of the process for shape | molding the container of this invention. It is the table | surface which put together the evaluation results, such as the layer structure of the various labels of an Example and a comparative example, the presence or absence of embossing of a label, the presence or absence of curl, and the adhesiveness to a container main body. It is sectional drawing which shows the laminated constitution of the prior art example of a label.

DESCRIPTION OF THE PREFERRED EMBODIMENTS Embodiments of a label and a labeled container according to the present invention will be described below with reference to the drawings.
1 and 2 show one embodiment of the container of the present invention, FIG. 1 is a front view, and FIG. 2 is a plan sectional view taken along line AA in FIG.
FIG. 3 is an example of the label of the present invention, and is a cross-sectional view showing the layer structure of the label 11 used in the labeled container of FIG. 1, wherein (a) is a laminate of an AC layer and a protective layer. The previous layer configuration, (b) shows the layer configuration after laminating the AC layer 15 and the protective layer 16 and then embossing the adhesive surface of the adhesive layer 12.

The container body 1 is a casing having an elliptical cylindrical body portion 2 made of PP resin by direct blow molding, having a height of 200 mm and a capacity of 600 ml, and an average thickness of the peripheral wall 2 w of the body portion 2 is 0.45 mm. It is.
A rectangular label 11 is attached to the front and back of the body portion 2 simultaneously with the blow molding of the container body 1 by an in-mold molding method.
The label 11 has a layer structure of a protective layer 16 / AC layer 15 / gravure printed layer 14 / adhesive layer 12 in order from the surface side (see FIG. 3B).
The adhesive layer 12 is made of a CPP film, the layer thickness is 0.05 mm, the AC layer 15 is formed by applying an anchor coating agent mainly composed of an organic titanate-based adhesive, and the protective layer 16 is formed by extruding an LDPE resin. The layers are laminated by the laminating method, the layer thickness is 0.01 mm, and the average thickness of the entire label 11 is 0.065 mm.
Moreover, the unevenness | corrugation by embossing is formed in the back surface side which contact | connects the surrounding wall 2w of the container main body 1 of the contact bonding layer 12. FIG.
In the label 11 in which the adhesive layer 12 is embossed, the dimension indicated by t in FIG. 3B is the thickness of the label 11.

The manufacturing method of this label 11 is as follows.
1) A CPP film having an appropriately selected thickness to be the adhesive layer 12 is prepared.
2) One side of the CPP film is corona-treated, this corona-treated surface is set as the surface side, and the printing layer 14 is laminated on the surface side by gravure printing.
3) From the top of the printed layer 14, the anchor coating agent is applied in a continuous process to laminate the AC layer 15, and then the LDPE resin is laminated on the AC layer by extrusion lamination to form the protective layer 16.
4) The back surface side of the laminated film, that is, the back surface side of the adhesive layer 12 is embossed to form irregularities.
5) A label 11 is produced by punching out each sheet with a die-cut roll into a predetermined shape.

Next, FIG. 5 is a schematic explanatory view of the process of the in-mold molding method for directly blow-molding the labeled container of FIG. 1. A cylindrical PP resin parison 22 is extruded from a die 21, and the upper and lower parts thereof are blow-molded. A state sandwiched between the split molds 23 is shown.
When blown air is blown in this state, the parison 22 expands (see the arrow direction in FIG. 5) and is shaped into the shape of the cavity (see the state of the two-dot chain line in FIG. 5), and the container body 1 is molded. At the same time as the molding, the label 11 fixed and arranged in advance on the mold surface by the reduced pressure intake passage 24 is adhered to the peripheral wall 2w of the trunk portion.

Here, the unevenness formed on the back surface side of the adhesive layer 12 by embossing exhibits a function as an air escape path at the time of in-mold molding, and the label 11 does not generate a float (blister) due to air accumulation. I am doing so.
Further, the unevenness can alleviate the shrinkage behavior of the label due to the contact of the high temperature parison, which is the main cause of wrinkles, and can effectively suppress wrinkles.
Furthermore, in order to reduce the contact area between the label surface and the label back surface, where the irregularities overlap and align in the holder, the labels are removed from the holder securely one by one in the automatic feeding of the label, Can be supplied into the mold.

  Since the adhesive layer 12 is made of a CPP film and is of the same system as the PP resin that forms the container body 1, the label 11 is firmly attached to the peripheral wall 2 w of the body portion 2 of the container body 1. Also, combined with the effects of in-mold molding, the average thickness of the peripheral wall 2w is 0.45 mm, regardless of whether it is a thin-walled container, no blisters or wrinkles, and the surface of the molded product and the in-mold label There is no level difference between them, and the label 11 is attached with high quality. (See Figure 2)

  Next, in order to compare with the label 11 of the embodiment described above (hereinafter referred to as label L), four types of labels of comparative examples (hereinafter referred to as label Lc1 to label Lc4) having a layer structure different from the label L. The four types of labels are adhered to the same container body as the PP resin container body 1 used in the examples by the same in-mold molding method, and the presence or absence of curl in the label, the container body Adhesion to the container, deformation of the container body after labeling, and drop impact resistance of the container were evaluated.

6 shows the layer structure of the label L and the labels Lc1 to Lc4, the presence or absence of embossing, the presence or absence of curling, the adhesion to the container body, the presence or absence of deformation of the container after the label is attached to the container body, It is the table | surface which put together the evaluation result of drop impact resistance.
In the table of FIG. 6, the layer configuration of label L is (protective layer / AC layer / printing layer / adhesive layer), and the layer configuration of labels Lc1 to Lc4 is (base material layer / printing layer / AC layer or DL layer). / Adhesive layer) is shown.
In this table, the abbreviations used in the description of the layer structure of the label are as follows.
・ CPP: PP resin cast film ・ Extruded LDPE: Low density polyethylene resin layer laminated by extrusion laminating method ・ AC: Anchor coat layer ・ DL: Dry laminate layer In the layer structure, the values in parentheses are in micrometer units The layer thickness shown.
The synthetic paper used for the label Lc4 is YUPO IDS80 manufactured by YUPO Corporation.
Moreover, the test method of the drop impact test is that the container is filled with a specified amount of water, left in a thermostatic chamber adjusted to 5 ° C. for 24 hours, then taken out and immediately taken upright from 1 m in height and lying down. Drop in order. This is one cycle, dropped 10 cycles, and if there is no damage to the container, no abnormality is assumed.

Next, the label L of the example and the labels Lc1 to Lc4 of the comparative example will be described below along the table of FIG.
As shown in the table, the label L and the labels Lc1 to Lc4 are all obtained by embossing the adhesive layer.
(1) Example label L
1) The layer structure of the label L is as described above, the layer thickness before embossing of the adhesive layer 12 is 0.05 mm, printed, coated with an anchor coating agent, and laminated with an LDPE resin by an extrusion laminating method, The thickness of the label L in the embossed state is 0.065 mm, and the adhesive layer 12 has a layer configuration that also functions as a base material layer.
2) Curling was not generated in the label L, and the effect of the uneven shape by embossing was combined, so that it could be smoothly supplied into the mold.
3) The thickness of the label L is not too thick, the deformation of the peripheral wall 2w of the container body 1 is not seen as seen in FIG. 2, and the end 11e (see FIG. 2) of the label and the peripheral wall 2w The depth of the V-shaped notch-shaped groove formed in the boundary portion of the container can be reduced, and the container was not cracked due to a drop impact caused by the groove.
4) The thickness of the adhesive layer 12 before embossing is 0.05 mm, the depth of the unevenness by the embossing can be taken sufficiently, there is no occurrence of air accumulation, and the adhesive layer 12 is of the same type as the container body 1 Strong adhesiveness is achieved by being made of a synthetic resin and combined with the effects of the in-mold molding method.

(2) Comparative example label Lc1
1) The label Lc1 has a layer structure in which a printing layer and an AC layer are laminated on the back side of a CPP film substrate, and further an LDPE resin adhesive layer is laminated by an extrusion laminating method.
2) Since the adhesive layer 12 was made of a synthetic resin different from the container body 1, the label 11 could not be adhered even by the in-mold molding method. For this reason, the deformation of the container and the drop impact could not be evaluated.

(3) Label Lc2 of the comparative example
1) The label Lc2 has a layer structure in which a printing layer is laminated on the back side of a base layer made of CPP film, and an adhesive layer made of CPP film is laminated by a dry laminating method.
2) Since the CPP film to be the base material layer was as thin as about 0.03 mm, it was difficult to adjust the tension during dry lamination of the adhesive layer, and the label was curled. For this reason, at the time of in-mold molding, the label could not be put in an aligned state in the hopper, and the label could not be automatically supplied to the mold by the apparatus.

(4) Comparative Example Label Lc3
1) The label Lc3 has a layer structure in which the thickness of the base material layer is increased to 0.05 mm so that the tension during dry lamination can be stably adjusted as compared with the label Lc2.
2) The thickening of the base material layer enabled stable adjustment of the tension during dry lamination, and no curling occurred. On the other hand, the total thickness of the label was 0.08 mm or more. As shown in FIG. 4, the peripheral wall 2 w of the container body 1 is deformed and becomes V-shaped in a sectional view formed at the boundary between the end of the label and the container body 1 in the drop impact test. Cracks caused by the notch-shaped grooves occurred.
As can be seen from the examination results of the above-described labels Lc2 and Lc3, in the case of a label in which the adhesive layer is laminated by the dry laminating method, the deformation of the container due to the sticking of the label and the curling of the label due to the restrictions derived from the label manufacturing method. It can be said that it is difficult to prevent both together effectively.

(5) Comparative Example Label Lc4
1) The label Lc4 uses synthetic paper whose main constituent material is a PP-based resin. A heat-sealable resin layer is formed in advance as an adhesive layer and is embossed.
2) The thickness of the label was as large as 0.08 mm. In this case as well, as shown in FIG. 4, deformation occurred in the peripheral wall 2w of the container body 1, and cracking occurred in the drop impact test.

As mentioned above, although embodiment of the in-mold label of this invention and the container with a label, and its effect were demonstrated along the Example, embodiment of this invention is not limited to the said Example.
In the above embodiment, an example of combining a container body made of PP resin and a label having an adhesive layer made of CPP film was explained, but the container body was made of a copolymer resin mainly composed of propylene in addition to PP resin, It can be made of a resin appropriately selected from PP resins, such as a blend resin mainly composed of PP resin, and the container body may be of a laminated type having an outer layer made of PP resin. it can.

Moreover, the container main body can be combined with a label having a film-made adhesive layer made of a resin of the same type or the like using a polyester resin, a polystyrene resin, a polyamide resin, or the like.
Moreover, in the said Example, although the container main body was based on the direct blow molding method, it can also be based on the biaxial stretch blow molding method.
Furthermore, the label of the present invention is not limited to the blow molding method, but can be applied to other in-mold molding methods such as an injection molding method and a thermoforming method.

As described above, the in-mold label of the present invention is free from deformation of the container due to label sticking and no air accumulation even if the peripheral wall of the container main body to be stuck is thin, and the label It is possible to suppress cracking due to a drop impact starting from the end face, and to provide a particularly thin container with a label that is packaged in high quality with an in-mold label, and is expected to be used in various applications.

DESCRIPTION OF SYMBOLS 1; Container body 2; Body 2w; Body wall 11; Label 11e; End 12 (of label); Adhesive layer 14; Print layer 15; Anchor coat (AC) layer 16; Protective layer 21; Blow split mold 24; vacuum intake passage 111; label 112; adhesive layer 113; substrate layer 114; printed layer 115; anchor coat (AC) layer

Claims (6)

The printed layer (14) and the anchor coat layer (15) were laminated in this order on the surface side of the adhesive layer (12) made of a synthetic resin film, and further a protective layer (16) made of low-density polyethylene resin was laminated by an extrusion lamination method. An in-mold label having a layer structure, wherein the synthetic resin film is a film other than polyethylene resin. The in-mold label according to claim 1, wherein the synthetic resin film is a polypropylene resin cast film. The in-mold label according to claim 1 or 2, wherein the back surface side of the adhesive layer (12) has unevenness by embossing. A container in which an in-mold label (11) is attached to a peripheral wall (2w) of a body portion (2) of a container body (1) made of a synthetic resin simultaneously with blow molding by an in-mold molding method, the container body (1 ) Is made of a synthetic resin other than polyethylene resin, and the in-mold label (11) is the same system as the container body (1) and directly on the peripheral wall (2w) of the body (2) of the container body (1). A printed layer (14) and an anchor coat layer (15) are laminated in this order on the surface side of the adhesive layer (12) made of heat-synthetic synthetic resin film, and further a protective layer made of low-density polyethylene resin by extrusion lamination ( A container with an in-mold label having a layer structure in which 16) is laminated. The container with an in-mold label according to claim 4, wherein the container body (1) is made of polypropylene resin, and the adhesive layer (12) of the in-mold label (11) is made of polypropylene resin cast film. The thin-walled container with an in-mold label according to claim 4 or 5, wherein the average wall thickness (2w) of the container body (1) is 0.8 mm or less.