JP2012224744A - Polysiloxane modified compound with polyhedral structure, composition containing the same, cured product, and optical device using the composition - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a liquid polysiloxane-based compound with a polyhedral structure excellent in molding processability and transparency, and a composition using the compound.SOLUTION: This polysiloxane modified compound with a polyhedral structure is obtained by hydrosilylating a polysiloxane-based compound (a) with a polyhedral structure having an alkenyl group, a compound (b) having a hydrosilyl group, and an organosilicon compound (c) having one alkenyl group in one molecule, wherein the addition amount of component (b) is within such a range that not less than 1.0 and less than 2.5 hydrogen atoms directly bonded to Si atoms of the constituent (b) to one alkenyl group of the constituent (a).

Description

  The present invention has a high heat resistance and light resistance, is excellent in gas barrier properties and thermal shock resistance, and has good handling properties when sealing an optical semiconductor element, a polysiloxane composition, a cured product, and The present invention relates to an optical device using the composition.

  Polysiloxane composition is excellent in heat resistance, cold resistance, weather resistance, light resistance, chemical stability, electrical properties, flame resistance, water resistance, transparency, colorability, non-adhesiveness, non-corrosion It is used in various industries. Among them, a composition composed of polysiloxane having a polyhedral structure is known to exhibit further excellent heat resistance, light resistance, chemical stability, low dielectric property, etc. from its specific chemical structure. .

  As an application example using a polysiloxane having a polyhedral structure, there is one intended to be used for an optical semiconductor element sealant. For example, in Patent Document 1, a polysiloxane having a polyhedral structure having two or more oxetanyl groups A polysiloxane-based composition having a polyhedral structure containing a resin, an aliphatic hydrocarbon containing one or more epoxy groups, and a cationic polymerization initiator is disclosed. This material has high refraction and light extraction efficiency. high. However, since it has an oxetanyl group or an epoxy group, there is a problem that heat resistance and light resistance are low.

  In addition, the polysiloxane composition has excellent characteristics, but generally has a problem of low gas barrier properties. Therefore, when used in an optical semiconductor element sealant application, there is a problem that the reflector is blackened by sulfide. For example, in Patent Document 2, a metal member is previously made of an acrylic resin having a high gas barrier property. The coating process is performed. However, after performing the coating treatment with an acrylic resin, it takes time and labor, such as sealing with a silicone resin separately, and there is a problem in productivity.

  In the optical semiconductor element sealant application, in order to obtain white light, a sealant containing a yellow phosphor with respect to a blue light emitting element is used, or in order to further enhance color rendering, A means such as using a sealant containing a green phosphor and a red phosphor for a blue light emitting element is used, but when the sealant has a low viscosity, There was a problem that the phosphors settled and the emission colors varied. To solve this problem, for example, Patent Document 4 discloses a method of modifying polysiloxane having a polyhedral structure with styrene, and the viscosity of the modified product can be adjusted by changing the amount of styrene used. Therefore, the viscosity of the composition can be adjusted, and the phosphor can be prevented from settling. A cured product using the modified product is excellent in molding processability, transparency, heat resistance / light resistance, and crack resistance. However, this method proves that it is difficult to achieve both gas barrier properties and high heat resistance and light resistance, leaving room for further improvement.

  As described above, it has been desired to develop a material having high heat resistance and light resistance, excellent thermal shock resistance and gas barrier properties, and good handling properties when sealing an optical semiconductor element.

JP2008-163260 JP 2009-206124 A JP2009-149976

  A polysiloxane composition, a cured product, and a composition having high heat resistance and light resistance, excellent gas barrier properties and thermal shock resistance, and good handling properties when sealing an optical semiconductor element An object is to provide an optical device used.

  As a result of intensive studies to solve the above problems, the present inventors have the following configurations.

  1) Hydrosilylation reaction of a polyhedral polysiloxane compound (a) having an alkenyl group, a compound (b) having a hydrosilyl group, and an organosilicon compound (c) having one alkenyl group in one molecule In the polyhedral polysiloxane modified product obtained, the number of hydrogen atoms directly connected to the Si atom of the component (b) is 1.0 or more and less than 2.5 per alkenyl group of the component (a) A modified polyhedral polysiloxane characterized by being added.

  2) The modified polyhedral polysiloxane according to 1), wherein the component (c) is an organosilicon compound having one or more aryl groups.

  3) The modified polyhedral polysiloxane according to 1) or 2), which is liquid at a temperature of 20 ° C.

  4) The modified polyhedral polysiloxane according to any one of 1) to 3), which has a viscosity of 10 Pa · s or more at a temperature of 20 ° C.

  5) The polyhedral polysiloxane according to any one of 1) to 4), wherein the compound (b) having a hydrosilyl group is a cyclic siloxane having a hydrosilyl group and / or a linear siloxane. Denatured body.

6) A polyhedral polysiloxane compound (a) having an alkenyl group has the formula
[AR ¹ ₂ SiO—SiO _3/2 ] _a [R ² ₃ SiO—SiO _3/2 ] _b
(A + b is an integer of 6 to 24, a is an integer of 1 or more, b is 0 or an integer of 1 or more; A is an alkenyl group; R ¹ is an alkyl group or an aryl group; R ² is an alkyl group or an aryl group Or a polysiloxane modified with a polyhedral polysiloxane according to any one of 1) to 5), characterized in that it is composed of a siloxane unit represented by a group linked to other polyhedral skeleton polysiloxane) body.

7) Formula [XR ³ ₂ SiO—SiO _3/2 ] _a [R ⁴ ₃ SiO—SiO _3/2 ] _b
[A + b is an integer of 6 to 24, a is an integer of 1 or more, b is 0 or an integer of 1 or more; R ³ is an alkyl group or an aryl group; R ⁴ is an alkenyl group, a hydrogen atom, an alkyl group, an aryl group Or a group linked to another polyhedral skeleton polysiloxane, X has a structure represented by the following general formula (1) or general formula (2), and when there are a plurality of X, the general formula (1 ) Or the structure of the general formula (2) may be different, or the structure of the general formula (1) or the general formula (2) may be mixed. X has at least one of general formula (1) and / or general formula (2).

{L is an integer of 2 or more; m is an integer of 0 or more; n is an integer of 2 or more; Y and Z are a polyhedral polysiloxane via a hydrogen atom, an alkenyl group, an alkyl group, an aryl group, or an alkylene chain. The bonded site or the structure of the following general formula (3) may be the same or different. However, at least one of Y or Z is a hydrogen atom, and at least one has a structure of the following general formula (3). }

(Q is an integer of 0 or more; R ⁵ is a group containing an organosilicon compound) R is an alkyl group or an aryl group. A modified polyhedral polysiloxane, comprising a siloxane unit represented by the formula:

8) The modified polyhedral polysiloxane according to 7), wherein R ⁵ contains one or more aryl groups.

  9) A polysiloxane composition containing the modified polyhedral siloxane according to any one of 1) to 8).

  10) A polysiloxane composition comprising the modified polyhedral polysiloxane according to any one of 1) to 9) and a polysiloxane having two or more alkenyl groups in one molecule.

  11) The polysiloxane composition according to 10), wherein the polysiloxane having two or more alkenyl groups in one molecule has one or more aryl groups.

  12) The polysiloxane composition according to any one of 9) to 11), comprising a hydrosilylation catalyst.

  13) The polysiloxane composition according to any one of 9) to 12), comprising a curing retarder.

  14) A cured product obtained by curing the polysiloxane composition according to any one of 9) to 13).

  15) An optical device using the polysiloxane composition according to any one of 9) to 13) as a sealing layer.

  A polysiloxane composition, a cured product, and a composition having high heat resistance and light resistance, excellent gas barrier properties and thermal shock resistance, and good handling properties when sealing an optical semiconductor element The used optical device can be provided.

Hereinafter, the present invention will be described in detail.

<Polyhedral polysiloxane compound (a) having an alkenyl group>
The polyhedral polysiloxane compound (a) having an alkenyl group in the present invention is not particularly limited as long as it is a polysiloxane having an alkenyl group in the molecule and having a polyhedral skeleton. Specifically, for example, the following formula [R ⁶ SiO _3/2 ] _x [R ⁷ SiO _3/2 ] _y
(X + y is an integer of 6 to 24; x is an integer of 1 or more, y is 0 or an integer of 1 or more; R ⁶ is an alkenyl group or a group having an alkenyl group; R ⁷ is any organic group, or Groups linked to other polyhedral skeleton polysiloxanes)
A polyhedral polysiloxane compound having an alkenyl group composed of a siloxane unit represented by formula (I) can be suitably used.
[AR ¹ ₂ SiO—SiO _3/2 ] _a [R ² ₃ SiO—SiO _3/2 ] _b
(A + b is an integer of 6 to 24, a is an integer of 1 or more, b is 0 or an integer of 1 or more; A is an alkenyl group; R ¹ is an alkyl group or an aryl group; R ² is a hydrogen atom or an alkyl group And a polyhedral polysiloxane compound having an alkenyl group composed of a siloxane unit represented by an aryl group or a group linked to another polyhedral skeleton polysiloxane).

  Examples of the alkenyl group include a vinyl group, an allyl group, a butenyl group, and a hexenyl group, and a vinyl group is preferable from the viewpoint of heat resistance and light resistance.

R ¹ is an alkyl group or an aryl group. Specific examples of the alkyl group include a methyl group, an ethyl group, a propyl group, a butyl group, a cyclohexyl group, and a cyclopentyl group. Examples of the aryl group include aryl groups such as a phenyl group and a tolyl group. Is done. R ¹ in the present invention is preferably a methyl group from the viewpoint of heat resistance and light resistance.

R ² is a hydrogen atom, an alkyl group, an aryl group, or a group linked to another polyhedral skeleton polysiloxane. Specific examples of the alkyl group include a methyl group, an ethyl group, a propyl group, a butyl group, a cyclohexyl group, and a cyclopentyl group. Examples of the aryl group include aryl groups such as a phenyl group and a tolyl group. Is done. R ² in the present invention is preferably a methyl group from the viewpoint of heat resistance and light resistance.

  a is not particularly limited as long as it is an integer of 1 or more, but is preferably 2 or more, and more preferably 3 or more, from the handleability of the compound and the physical properties of the resulting cured product. Further, b is not particularly limited as long as it is 0 or an integer of 1 or more.

  The sum of a and b (= a + b) is an integer from 6 to 24, but from the viewpoint of the stability of the compound and the stability of the resulting cured product, it should be 6 to 12, and more preferably 6 to 10. preferable.

The method for synthesizing the component (a) is not particularly limited, and the component can be synthesized using a known method. As a synthesis method, for example, a silane of R ⁸ SiX ^a ₃ (wherein R ⁸ represents R ⁶ or R ⁷ described above, and X ^a represents a hydrolyzable functional group such as a halogen atom or an alkoxy group). It is obtained by the hydrolysis condensation reaction of the compound. Alternatively, after synthesizing a trisilanol compound having three silanol groups in the molecule by hydrolytic condensation reaction of R ⁸ SiX ^a _3, the ring is closed by reacting the same or different trifunctional silane compounds, and polyhedral Methods for synthesizing structural polysiloxanes are also known.

  In addition, for example, there is a method of hydrolytic condensation of tetraalkoxysilane such as tetraethoxysilane in the presence of a base such as quaternary ammonium hydroxide. In this synthesis method, a silicate having a polyhedral structure is obtained by a hydrolytic condensation reaction of tetraalkoxysilane, and the obtained silicate is further reacted with a silylating agent such as an alkenyl group-containing silyl chloride. It is possible to obtain a polyhedral polysiloxane in which Si atoms and alkenyl groups forming a polyhedral structure are bonded through a siloxane bond. In the present invention, the same polyhedral polysiloxane can be obtained from a substance containing silica such as silica or rice husk instead of tetraalkoxylane.

<Compound (b) having hydrosilyl group>
From the viewpoint of gas barrier properties, the amount of the compound (b) having a hydrosilyl group is such that hydrogen bonded directly to the Si atom of the component (b) per alkenyl group of the polyhedral polysiloxane compound (a) having an alkenyl group The number of atoms may be 1.0 or more and less than 2.5. By adding the component (b) within this range, for example, in the reaction with the component (a), synthesis in one pot is possible without leaving the unreacted component (b). When the addition amount of the component (b) is small, gelation occurs due to a cross-linking reaction, resulting in a modified polyhedral polysiloxane having poor handling properties. When it is excessive, a gas barrier of a cured product obtained using the modified polyhedral polysiloxane. May adversely affect sex.

  The compound (b) having a hydrosilyl group used in the present invention is not particularly limited as long as it has one or more hydrosilyl groups in the molecule, but the obtained polyhedral polysiloxane modified product has transparency, heat resistance, From the viewpoint of light resistance, it is preferably a siloxane compound having a hydrosilyl group, and more preferably a cyclic siloxane having a hydrosilyl group or a linear polysiloxane. In particular, from the viewpoint of gas barrier properties and blue laser resistance, a cyclic siloxane is preferable.

  The linear polysiloxane having a hydrosilyl group includes a copolymer of a dimethylsiloxane unit, a methylhydrogensiloxane unit and a terminal trimethylsiloxy unit, and a copolymer of a diphenylsiloxane unit, a methylhydrogensiloxane unit and a terminal trimethylsiloxy unit. Copolymers, copolymers of methylphenylsiloxane units and methylhydrogensiloxane units and terminal trimethylsiloxy units, polydimethylsiloxane blocked at the end with dimethylhydrogensilyl groups, polyblocked at the ends with dimethylhydrogensilyl groups Examples thereof include diphenylsiloxane and polymethylphenylsiloxane blocked at the end with a dimethylhydrogensilyl group.

  In particular, as a linear polysiloxane having a hydrosilyl group, a polysiloxane having a molecular end blocked with a dimethylhydrogensilyl group from the viewpoints of reactivity during modification, heat resistance of the resulting cured product, light resistance, etc. Furthermore, polydimethylsiloxane having a molecular end blocked with a dimethylhydrogensilyl group can be suitably used. Specific examples thereof include tetramethyldisiloxane and hexamethyltrisiloxane.

  Examples of the cyclic siloxane having a hydrosilyl group include 1,3,5,7-tetrahydrogen-1,3,5,7-tetramethylcyclotetrasiloxane, 1-propyl-3,5,7-trihydrogen-1. , 3,5,7-tetramethylcyclotetrasiloxane, 1,5-dihydrogen-3,7-dihexyl-1,3,5,7-tetramethylcyclotetrasiloxane, 1,3,5-trihydrogen -1,3,5-trimethylcyclotrisiloxane, 1,3,5,7,9-pentahydrogen-1,3,5,7,9-pentamethylcyclopentasiloxane, 1,3,5,7, Examples include 9,11-hexahydrogen-1,3,5,7,9,11-hexamethylcyclohexasiloxane. Specific examples of the cyclic siloxane in the present invention include, for example, 1,3,5,7-tetrahydro, from the viewpoints of industrial availability and reactivity, or heat resistance, light resistance, strength, and the like of the resulting cured product. Gen-1,3,5,7-tetramethylcyclotetrasiloxane can be preferably used.

  These compounds (b) having a hydrosilyl group may be used alone or in combination of two or more.

<Organic silicon compound (c) having one alkenyl group in one molecule>
In the present invention, the organosilicon compound (c) having one alkenyl group in one molecule undergoes a hydrosilylation reaction with the hydrosilyl group of the compound (b) having a hydrosilyl group.

  By using the component (c), the elastic modulus of the obtained cured product can be reduced, and further, the thermal shock resistance, fracture strength, gas barrier properties, and the like can be improved. Further, by using the component (c), it is possible to take out the polyhedral polysiloxane-modified product in liquid form.

  The component (c) in the present invention is not particularly limited as long as it is an organosilicon compound having one alkenyl group in one molecule, but it is a gas barrier that at least one aryl group is contained in one molecule. From the viewpoint of heat resistance and refractive index, it is more preferable that the aryl group is directly bonded to the silicon atom from the viewpoint of heat resistance and light resistance.

  The component (c) in the present invention is preferably silane or polysiloxane from the viewpoints of heat resistance and light resistance. Specific examples of such component (c) include vinyltrimethylsilane, vinyldimethylphenylsilane, vinyldiphenylmethylsilane, vinyltriphenylsilane, vinyltriethylsilane, vinyldiethylphenylsilane, vinyldiphenylethylsilane, and allyldimethylphenyl. Examples include silane, allyldiphenylmethylsilane, allyltriphenylsilane, allyldiethylphenylsilane, and allyldiphenylethylsilane. Among these, vinyltrimethylsilane, vinyldimethylphenylsilane, vinyldiphenylmethylsilane, and vinyltriphenylsilane are preferable examples from the viewpoint of heat resistance and light resistance.

  When the component (c) is a polysiloxane, examples thereof include a polysiloxane having a linear structure having one alkenyl group, a polysiloxane having one alkenyl group at the molecular end, and a cyclic siloxane having one alkenyl group.

In addition, when the component (c) is a polysiloxane having a straight chain structure having one alkenyl group, specifically, for example, polydimethylsiloxane having a dimethylvinylsilyl group and a trimethylsilyl group each blocked at one end, dimethyl Polymethylphenylsiloxane blocked with a vinylsilyl group and a trimethylsilyl group each at one end, polydiphenylsiloxane blocked with a dimethylvinylsilyl group and a trimethylsilyl group respectively, and a dimethylvinylsilyl group and a trimethylsilyl group. A copolymer of a dimethylsiloxane unit and a methylphenylsiloxane unit each having one end blocked, and a dimethylsiloxane unit and a diphenylsiloxane unit each having one end blocked with a dimethylvinylsilyl group and a trimethylsilyl group. A copolymer of a methylphenylsiloxane unit and a diphenylsiloxane unit each having one end blocked with a dimethylvinylsilyl group and one trimethylsilyl group, and one terminal each with a diethylvinylsilyl group and a triethylsilyl group Polydimethylsiloxane blocked one by one, polymethylphenylsiloxane blocked one by one with diethylvinylsilyl group and triethylsilyl group, one end each blocked with diethylvinylsilyl group and triethylsilyl group Polydiphenylsiloxane, a copolymer of dimethylsiloxane units and methylphenylsiloxane units each blocked with a diethylvinylsilyl group and a triethylsilyl group, and a terminal with diethylvinylsilyl group and triethylsilyl group, respectively. Copolymers of one by one sequestered dimethylsiloxane units and diphenylsiloxane units and the like. Among them, from the viewpoint of heat resistance and light resistance, polydimethylsiloxane having one end each blocked with a dimethylvinylsilyl group and one trimethylsilyl group, and polymethylsiloxane having one end blocked with a dimethylvinylsilyl group and one trimethylsilyl group. Phenylsiloxane, polydiphenylsiloxane blocked with dimethylvinylsilyl group and trimethylsilyl group each at one end, dimethylsiloxane unit and methylphenylsiloxane unit blocked with dimethylvinylsilyl group and trimethylsilyl group at one end respectively A preferred example is a copolymer of a dimethylsiloxane unit and a diphenylsiloxane unit each having one end blocked with a dimethylvinylsilyl group and a trimethylsilyl group.
In addition, when the component (c) is a polysiloxane having one alkenyl group at the molecular end, specifically, for example, a polysiloxane whose ends are blocked one by one with the dimethylvinylsilyl group and the trimethylsilyl group exemplified above, Polysiloxane composed of at least one siloxane unit and one dimethylvinylsiloxane unit selected from the group consisting of SiO ₂ units, SiO _3/2 units, SiO units, SiO _1/2 units, one terminal with diethylvinylsilyl group Examples of the blocked polysiloxane include polysiloxanes comprising at least one siloxane unit selected from the group consisting of SiO ₂ units, SiO _3/2 units, and SiO units. Among them, from the viewpoint of heat resistance and light resistance, at least 1 selected from the group consisting of a polysiloxane having one end blocked with a dimethylvinylsilyl group, the polysiloxane being composed of SiO ₂ units, SiO _3/2 units, and SiO units. A preferred example is polysiloxane comprising two siloxane units.

  In addition, when the component (c) is a cyclic siloxane having one alkenyl group, specifically, for example, 1-vinyl-1,3,3,5,5,7,7-heptamethylcyclotetrasiloxane, 1-vinyl Vinyl-3-phenyl-1,3,5,5,7,7-hexamethylcyclotetrasiloxane, 1-vinyl-3,5-diphenyl-1,3,5,7,7-pentamethylcyclotetrasiloxane, 1-vinyl-3,5,7-triphenyl-1,3,5,7-tetramethylcyclotetrasiloxane, 1-vinyl-1,3,3,5,5,7,7-heptaethylcyclotetrasiloxane 1-vinyl-3-phenyl-1,3,5,5,7,7-hexamethylethylcyclotetrasiloxane, 1-vinyl-3,5-diphenyl-1,3,5,7,7-pentaethyl Cyclotetrasi Hexane, 1-vinyl-3,5,7-triphenyl-1,3,5,7-tetraethyl cyclotetrasiloxane and the like. Among them, from the viewpoint of heat resistance and light resistance, 1-vinyl-1,3,3,5,5,7,7-heptamethylcyclotetrasiloxane, 1-vinyl-3-phenyl-1,3,5,5, 7,7-hexamethylcyclotetrasiloxane, 1-vinyl-3,5-diphenyl-1,3,5,7,7-pentamethylcyclotetrasiloxane, 1-vinyl-3,5,7-triphenyl-1 3,5,7-tetramethylcyclotetrasiloxane is a preferred example.

  These (c) component organosilicon compounds having one alkenyl group per molecule may be used alone or in combination of two or more.

  The amount of the organosilicon compound (c) having one alkenyl group in one molecule is such that the amount of the alkenyl group directly bonded to the Si atom of the component (c) is one hydrosilyl group of the component (b) having the hydrosilyl group. It is preferable that the number is 0.01 to 0.5. When the addition amount is small, the thermal shock resistance of the resulting cured product may be lowered, and when the addition amount is large, a curing failure may occur in the resulting cured product.

<Modified polyhedral polysiloxane>
The modified polyhedral polysiloxane of the present invention comprises a polyhedral polysiloxane compound (a) having an alkenyl group (a) and an organosilicon compound (c) having one alkenyl group in one molecule in the presence of a hydrosilylation catalyst described later. Is hydrosilylated with a compound (b) having a hydrosilyl group.

  The method for obtaining the modified polyhedral polysiloxane of the present invention is not particularly limited and can be variously set. For example, after reacting the component (a) and the component (b) in advance, the method reacting with the component (c) Or a method of reacting the component (c) with the component (b) and then reacting with the component (a), a method of reacting the component (b) with the component (a) and the component (c), etc. Is mentioned. After completion of each reaction, for example, volatile unreacted components may be distilled off under reduced pressure and heating conditions, and used as a target product or an intermediate for the next step.

  Among them, in order to suppress the product obtained only from the component (b) and the component (c), after reacting the component (a) and the component (b) in advance and distilling off the unreacted component (b), A method of reacting with component (c) is preferred. Moreover, in order to improve the convenience of reaction and crack resistance, the method of making (b) component react by coexisting (a) component and (c) component is preferable.

  In the polyhedral polysiloxane modified product thus obtained, a part of the hydrosilyl group of the component (b) used in the reaction may remain.

Polyhedral polysiloxane is not particularly limited as amount of a hydrosilylation catalyst used in the synthesis of the modified product, used for the reaction (a) component and the component (c) alkenyl groups 1 mol per 10 ^-1 to 10 ^{- It} is good to use in the range of ¹⁰ mol. Preferably it is used in the range of 10 ⁻⁴ to 10 ⁻⁸ mol. If there are many hydrosilylation catalysts, depending on the type of hydrosilylation catalyst, it absorbs light with a short wavelength, which may cause coloration or decrease the light resistance of the resulting cured product. There is also a risk of foaming. Moreover, when there are few hydrosilylation catalysts, reaction may not progress and there exists a possibility that a target object may not be obtained.

  As reaction temperature of hydrosilylation reaction, it is 30-400 degreeC, More preferably, it is preferable that it is 40-250 degreeC, More preferably, it is 45-140 degreeC. If the temperature is too low, the reaction does not proceed sufficiently, and if the temperature is too high, gelation may occur and handling properties may deteriorate.

  The polyhedral polysiloxane modified product thus obtained can ensure compatibility with various compounds, particularly siloxane compounds, and further, since hydrosilyl groups are introduced into the molecule, It becomes possible to make it react with the compound which has. Specifically, a cured product can be obtained by reacting with a polysiloxane having two or more alkenyl groups in one molecule described later.

  The modified polyhedral polysiloxane in the present invention can be liquid at a temperature of 20 ° C. It is preferable that the polyhedral polysiloxane modified is in a liquid form because of excellent handling properties.

The modified polyhedral polysiloxane in the present invention has the formula
[XR ³ ₂ SiO—SiO _3/2 ] _a [R ⁴ ₃ SiO—SiO _3/2 ] _b
[A + b is an integer of 6 to 24, a is an integer of 1 or more, b is 0 or an integer of 1 or more; R ³ is an alkyl group or an aryl group; R ⁴ is an alkenyl group, a hydrogen atom, an alkyl group, an aryl group Or a group linked to another polyhedral skeleton polysiloxane, X has a structure represented by the following general formula (1) or general formula (2), and when there are a plurality of X, the general formula (1 ) Or the structure of the general formula (2) may be different, or the structure of the general formula (1) or the general formula (2) may be mixed. X has at least one of general formula (1) and / or general formula (2).

{L is an integer of 2 or more; m is an integer of 0 or more; n is an integer of 2 or more; Y and Z are a polyhedral polysiloxane via a hydrogen atom, an alkenyl group, an alkyl group, an aryl group, or an alkylene chain. The bonded site or the structure of the following general formula (3) may be the same or different. However, at least one of Y or Z is a hydrogen atom, and at least one has a structure of the following general formula (3). }

(Q is an integer of 0 or more; R ⁵ is a group containing an organosilicon compound) R is an alkyl group or an aryl group. ]
It is a polyhedral polysiloxane compound composed of siloxane units represented by the formula: Among these, R ⁶ preferably has one or more aryl groups from the viewpoint of gas barrier properties.

  The polyhedral polysiloxane modified product thus obtained has a polyhedral structure by controlling the amount of component (a), component (b), component (c) added, reaction sequence, reaction time, reaction temperature, and the like. The viscosity of the modified polysiloxane can be controlled. It is also possible to adjust the viscosity of the polysiloxane composition described later by controlling the viscosity of the modified polyhedral polysiloxane. The viscosity of the modified polyhedral polysiloxane is not particularly limited, but when the modified polyhedral polysiloxane is liquid at a temperature of 20 ° C., the viscosity at a temperature of 20 ° C. may be 10 Pa · s to 300 Pa · s. Preferably, it is 1 Pa · s to 100 Pa · s. If the modified polyhedral polysiloxane is too low in viscosity, the polysiloxane composition described later will have low viscosity, and additives such as phosphors may settle without being dispersed. If the viscosity is too high, the handling property may be deteriorated.

<Polysiloxane having two or more alkenyl groups in one molecule>
In the present invention, the number of polysiloxane siloxane units having two or more alkenyl groups in one molecule is not particularly limited, but is preferably 2 or more, and more preferably 2 to 10. When the number of siloxane units in one molecule is small, the composition tends to volatilize, and desired physical properties may not be obtained after curing. Moreover, when there are many siloxane units, the gas barrier property of the obtained hardened | cured material may fall.

  In the present invention, the polysiloxane having two or more alkenyl groups in one molecule preferably has an aryl group from the viewpoint of gas barrier properties. In addition, in the polysiloxane having two or more alkenyl groups in one molecule having an aryl group, the aryl group is preferably bonded directly to the Si atom from the viewpoint of heat resistance and light resistance. In addition, the aryl group may be present at either the side chain or the terminal of the molecule, and the molecular structure of such an aryl group-containing polysiloxane is not limited. In addition to the chain shape, it may have a cyclic structure.

  Examples of such aryl groups include phenyl, naphthyl, 2-methylphenyl, 3-methylphenyl, 4-methylphenyl, 2-ethylphenyl, 3-ethylphenyl, and 4-ethylphenyl. Group, 2-propylphenyl group, 3-propylphenyl group, 4-propylphenyl group, 3-isopropylphenyl group, 4-isopropylphenyl group, 2-butylphenyl group, 3-butylphenyl group, 4-butylphenyl group, 3-isobutylphenyl group, 4-isobutylphenyl group, 3-tbutylphenyl group, 4-tbutylphenyl group, 3-pentylphenyl group, 4-pentylphenyl group, 3-hexylphenyl group, 4-hexylphenyl group, 3-cyclohexylphenyl group, 4-cyclohexylphenyl group, 2,3-dimethylphenyl Group, 2,4-dimethylphenyl group, 2,5-dimethylphenyl group, 2,6-dimethylphenyl group, 3,4-dimethylphenyl group, 3,5-dimethylphenyl group, 2,3-diethylphenyl group, 2,4-diethylphenyl group, 2,5-diethylphenyl group, 2,6-diethylphenyl group, 3,4-diethylphenyl group, 3,5-diethylphenyl group, biphenyl group, 2,3,4-trimethyl Examples include phenyl group, 2,3,5-trimethylphenyl group, 2,4,5-trimethylphenyl group, 3-epoxyphenyl group, 4-epoxyphenyl group, 3-glycidylphenyl group, 4-glycidylphenyl group and the like. . Among these, a phenyl group is a preferred example from the viewpoint of heat resistance and light resistance. These may be used alone or in combination of two or more.

  The polysiloxane having two or more alkenyl groups in one molecule in the present invention is a linear polysiloxane having two or more alkenyl groups from the viewpoint of heat resistance and light resistance, and two or more alkenyl groups at the molecular ends. Preferred examples include polysiloxanes having a cyclic structure and cyclic siloxanes having two or more alkenyl groups.

  Specific examples of the linear polysiloxane having two or more alkenyl groups include copolymers of dimethylsiloxane units, methylvinylsiloxane units and terminal trimethylsiloxy units, diphenylsiloxane units, methylvinylsiloxane units and terminal trimethylsiloxy units. Copolymer, methylphenylsiloxane unit, copolymer of methylvinylsiloxane unit and terminal trimethylsiloxy unit, polydimethylsiloxane blocked with dimethylvinylsilyl group, endblocked with dimethylvinylsilyl group Examples thereof include polydiphenylsiloxane and polymethylphenylsiloxane whose ends are blocked with dimethylvinylsilyl groups.

Specific examples of the polysiloxane having two or more alkenyl groups at the molecular terminals include polysiloxanes whose ends are blocked with the dimethylvinylsilyl group exemplified above, two or more dimethylvinylsiloxane units and SiO ₂ units, SiO _{3 /} Examples thereof include polysiloxane composed of at least one siloxane unit selected from the group consisting of ₂ units and SiO units.

Examples of the cyclic siloxane compound having two or more alkenyl groups include 1,3,5,7-tetravinyl-1,3,5,7-tetramethylcyclotetrasiloxane, 1,3,5,7-tetravinyl-1 -Phenyl-3,5,7-trimethylcyclotetrasiloxane, 1,3,5,7-tetravinyl-1,3-diphenyl-5,7-dimethylcyclotetrasiloxane, 1,3,5,7-tetravinyl -1,5-diphenyl-3,7-dimethylcyclotetrasiloxane, 1,3,5,7-tetravinyl-1,3,5-triphenyl-7-methylcyclotetrasiloxane, 1-phenyl-3,5 , 7-trivinyl-1,3,5,7-tetramethylcyclotetrasiloxane, 1,3-diphenyl-5,7-divinyl-1,3,5,7-tetramethylcycloteto Siloxane, 1,3,5-trivinyl-1,3,5-trimethylcyclosiloxane, 1,3,5,7,9-pentavinyl-1,3,5,7,9-pentamethylcyclosiloxane, 1,3 5,7,9,11-hexavinyl-1,3,5,7,9,11-hexamethylcyclosiloxane and the like.
These polysiloxanes having two or more alkenyl groups in one molecule may be used alone or in combination of two or more.

  The amount of polysiloxane having two or more alkenyl groups per molecule can be variously set, but per alkenyl group is directly linked to Si atoms contained in the polyhedral polysiloxane-based modified polyhedral polysiloxane. It is desirable that the added hydrogen atoms be added at a rate of 0.3 to 5, preferably 0.5 to 3. When the proportion of alkenyl groups is small, appearance defects due to foaming or the like are likely to occur, and when the proportion of alkenyl groups is large, physical properties after curing may be adversely affected.

  A cured product can be prepared by hydrosilylating the hydrosilyl group of the modified polyhedral polysiloxane of the present invention and the alkenyl group of a polysiloxane having two or more alkenyl groups in one molecule. In the hydrosilylation reaction, it is preferable to use a hydrosilylation catalyst. As the hydrosilylation catalyst that can be used in this reaction, those described below can be used. In the hydrosilylation reaction between a polyhedral polysiloxane modified and a polysiloxane having two or more alkenyl groups in one molecule, the hydrosilylation catalyst used in the synthesis of the polyhedral polysiloxane modified is the polyhedral polysiloxane. Since it is brought together with the modified body, it is not necessary to use a hydrosilylation catalyst separately.

<Hydrosilylation catalyst>
In the present invention, a hydrosilylation catalyst is used in synthesizing a polyhedral polysiloxane modified product and curing the composition containing the modified product.

  As the hydrosilylation catalyst used in the present invention, a known hydrosilylation catalyst can be used, and there is no particular limitation.

Specifically, a platinum-olefin complex, chloroplatinic acid, platinum alone, a carrier (alumina, silica, carbon black, etc.) supported by solid platinum, a platinum-vinylsiloxane complex, such as Pt _n (ViMe ₂ SiOSiMe ₂ Vi) _n , Pt [(MeViSiO) ₄ ] _m ; platinum-phosphine complex, such as Pt (PPh ₃ ) ₄ , Pt (PBu ₃ ) ₄ ; platinum-phosphite complex, such as Pt [P (OPh) ₃ ] ₄ , Pt [P (OBu) ₃ ] ₄ (wherein Me represents a methyl group, Bu represents a butyl group, Vi represents a vinyl group, Ph represents a phenyl group, and n and m represent an integer) , Pt (acac) _2, also platinum described in U.S. Patent 3,159,601 and in Pat 3159662 of Ashby et al - hydrocarbon complex, and Lamoreaux et al U.S. Patent Platinum is described in the 3220972 Pat Arcola - DOO catalysts may be mentioned.

Examples of catalysts other than platinum compounds include RhCl (PPh ₃ ) ₃ , RhCl ₃ , Rh / Al ₂ O ₃ , RuCl ₃ , IrCl ₃ , FeCl ₃ , AlCl ₃ , PdCl ₂ .2H ₂ O, NiCl _2. , TiCl ₄ , and the like. These catalysts may be used alone or in combination of two or more. From the viewpoint of catalytic activity, chloroplatinic acid, platinum-olefin complex, platinum-vinylsiloxane complex, Pt (acac) _{2 and the} like are preferable.

<Curing retarder>
The curing retarder is a component for improving the storage stability of the polysiloxane composition of the present invention or adjusting the reactivity of the hydrosilylation reaction during the curing process. In the present invention, as the retarder, known compounds used in addition-type curable compositions with hydrosilylation catalysts can be used. Specifically, compounds containing aliphatic unsaturated bonds, organophosphorus compounds , Organic sulfur compounds, nitrogen-containing compounds, tin compounds, organic peroxides, and the like. These may be used alone or in combination of two or more.

  Specific examples of the compound containing an aliphatic unsaturated bond include 3-hydroxy-3-methyl-1-butyne, 3-hydroxy-3-phenyl-1-butyne, and 3,5-dimethyl-1- Examples thereof include propargyl alcohols such as hexyn-3-ol and 1-ethynyl-1-cyclohexanol, ene-yne compounds, maleic acid esters such as maleic anhydride and dimethyl maleate, and the like.

  Specific examples of the organophosphorus compound include triorganophosphine, diorganophosphine, organophosphon, and triorganophosphite.

  Specific examples of the organic sulfur compound include organomercaptans, diorganosulfides, hydrogen sulfide, benzothiazole, thiazole, benzothiazole disulfide, and the like.

  Specific examples of nitrogen-containing compounds include N, N, N ′, N′-tetramethylethylenediamine, N, N-dimethylethylenediamine, N, N-diethylethylenediamine, N, N-dibutylethylenediamine, and N, N-dibutyl. -1,3-propanediamine, N, N-dimethyl-1,3-propanediamine, N, N, N ′, N′-tetraethylethylenediamine, N, N-dibutyl-1,4-butanediamine, 2,2 Examples include '-bipyridine.

  Specific examples of tin compounds include stannous halide dihydrate, stannous carboxylate, and the like.

  Specific examples of the organic peroxide include di-t-butyl peroxide, dicumyl peroxide, benzoyl peroxide, and t-butyl perbenzoate. Of these, dimethyl maleate, 3,5-dimethyl-1-hexyn-3-ol, and 1-ethynyl-1-cyclohexanol can be exemplified as particularly preferred curing retarders.

The addition amount of the curing retarder is not particularly limited, but is preferably used in the range of 10 ⁻¹ to 10 ³ mol, more preferably in the range of 1 to 100 mol, per 1 mol of the hydrosilylation catalyst. preferable. Moreover, these hardening retarders may be used independently and may be used in combination of 2 or more types.

<Polysiloxane composition and cured product>
The polysiloxane composition of the present invention can be obtained by adding polysiloxane having two or more alkenyl groups in one molecule, a hydrosilylation catalyst, and a curing retarder to the modified polyhedral polysiloxane as necessary. Can do. The polysiloxane composition of the present invention can be handled as a liquid resin composition. By using a liquid resin composition, it is possible to easily obtain a molded body according to the application by injecting or applying to a mold, package, substrate or the like and curing.

  When adding temperature when making it harden | cure, Preferably it is 30-400 degreeC, More preferably, it is 50-250 degreeC. If the curing temperature is too high, the resulting cured product tends to have poor appearance, and if it is too low, curing is insufficient. Moreover, you may make it harden | cure combining the temperature conditions of two or more steps. Specifically, for example, by raising the curing temperature stepwise such as 70 ° C., 120 ° C., and 150 ° C., a preferable cured product can be obtained, which is preferable.

  The curing time can be appropriately selected depending on the curing temperature, the amount of the hydrosilylation catalyst to be used and the amount of the reactive group, and other combinations of the composition of the present application. Preferably, a cured product can be obtained by performing the treatment for 10 minutes to 8 hours.

  The viscosity of the polysiloxane composition of the present invention is not particularly limited, but the viscosity at a temperature of 23 ° C. is preferably 1 Pa · s to 300 Pa · s, more preferably 2 Pa · s to 100 Pa · s. . If the viscosity of the polysiloxane composition is too low, additives such as phosphors may settle without being dispersed. Further, when the viscosity of the polysiloxane composition is too high, the handling property may be deteriorated.

  An adhesiveness imparting agent can be added to the polysiloxane composition of the present invention as necessary.

  The adhesion-imparting agent is used for the purpose of improving the adhesion between the polysiloxane-based composition and the substrate in the present invention, and is not particularly limited as long as it has such an effect, but the silane coupling agent Can be illustrated as a preferred example.

  The silane coupling agent is not particularly limited as long as it is a compound having at least one functional group reactive with an organic group and one hydrolyzable silicon group in the molecule. The group reactive with the organic group is preferably at least one functional group selected from an epoxy group, a methacryl group, an acrylic group, an isocyanate group, an isocyanurate group, a vinyl group, and a carbamate group from the viewpoint of handling. From the viewpoints of adhesiveness and adhesiveness, an epoxy group, a methacryl group, and an acrylic group are particularly preferable. As the hydrolyzable silicon group, an alkoxysilyl group is preferable from the viewpoint of handleability, and a methoxysilyl group and an ethoxysilyl group are particularly preferable from the viewpoint of reactivity.

  Specific preferred silane coupling agents include 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropylmethyldimethoxysilane, 3-glycidoxypropyltriethoxysilane, and 3-glycidoxypropylmethyldisilane. Ethoxysilane, 2- (3,4-epoxycyclohexyl) ethyltrimethoxysilane, 2- (3,4-epoxycyclohexyl) ethylmethyldimethoxysilane, 2- (3,4-epoxycyclohexyl) ethyltriethoxysilane, 2- Alkoxysilanes having an epoxy functional group such as (3,4-epoxycyclohexyl) ethylmethyldiethoxysilane: 3-methacryloxypropyltrimethoxysilane, 3-methacryloxypropyltriethoxysilane, 3-acryloxypropyltrimethoxysila Alkoxysilanes having a methacrylic group or an acrylic group such as 3-acryloxypropyltriethoxysilane, methacryloxymethyltrimethoxysilane, methacryloxymethyltriethoxysilane, acryloxymethyltrimethoxysilane, acryloxymethyltriethoxysilane Is mentioned. These may be used alone or in combination of two or more.

  The addition amount of the silane coupling agent is 0.05 to 30 parts by weight with respect to 100 parts by weight of a mixture of the polyhedral polysiloxane modified product and a polysiloxane having two or more alkenyl groups in one molecule. Preferably, it is 0.1 to 10 parts by weight. If the addition amount is small, the effect of improving the adhesiveness does not appear, and if the addition amount is large, the physical properties of the cured product may be adversely affected.

  In the present invention, a known adhesion promoter can be used to enhance the effect of the adhesion promoter. Adhesion promoters include, but are not limited to, epoxy-containing compounds, epoxy resins, boronic ester compounds, organoaluminum compounds, and organotitanium compounds.

An inorganic filler can be added to the polysiloxane composition of the present invention as necessary.
By using an inorganic filler as the composition of the polysiloxane composition of the present invention, the strength, hardness, elastic modulus, thermal expansion coefficient, thermal conductivity, heat dissipation, electrical characteristics, light reflectance of the molded product obtained Various physical properties such as flame retardancy, fire resistance, and gas barrier properties can be improved.
The inorganic filler is not particularly limited as long as it is an inorganic substance or a compound containing an inorganic substance. Specifically, for example, quartz, fumed silica, precipitated silica, silicic anhydride, fused silica, crystalline silica, ultrafine powder amorphous silica, etc. Silica-based inorganic filler, alumina, zircon, iron oxide, zinc oxide, titanium oxide, silicon nitride, boron nitride, aluminum nitride, silicon carbide, glass fiber, glass flake, alumina fiber, carbon fiber, mica, graphite, carbon black, Examples thereof include ferrite, graphite, diatomaceous earth, white clay, clay, talc, aluminum hydroxide, calcium carbonate, manganese carbonate, magnesium carbonate, barium sulfate, potassium titanate, calcium silicate, inorganic balloon, and silver powder. These may be used alone or in combination of two or more.

  The inorganic filler may be appropriately subjected to a surface treatment. Examples of the surface treatment include alkylation treatment, trimethylsilylation treatment, silicone treatment, treatment with a silane coupling agent, and the like, but are not particularly limited.

As the shape of the inorganic filler, various types such as a crushed shape, a piece shape, a spherical shape, and a rod shape can be used. The average particle size and particle size distribution of the inorganic filler are not particularly limited, but from the viewpoint of gas barrier properties, the average particle size is preferably 0.005 to 50 μm, more preferably 0.01 to 20 μm. More preferably. Similarly, the BET specific surface area, although not particularly limited, from the viewpoint of gas barrier properties, it is preferably ^70m 2 / g or more, more preferably 100 m ² / g or more, further 200 meters ² / It is especially preferable that it is g or more.

  The addition amount of the inorganic filler is not particularly limited, but it is preferably 1 to 1000 parts by weight, more preferably 100 parts by weight, based on 100 parts by weight of the polyhedral polysiloxane modified body and polysiloxane having two or more alkenyl groups in one molecule. 3 to 500 parts by weight, more preferably 5 to 300 parts by weight. When the amount of the inorganic filler added is large, the fluidity may be deteriorated, and when the amount of the inorganic filler added is small, desired physical properties may not be obtained.

  The order of mixing the inorganic fillers is not particularly limited, but in terms that storage stability tends to be good, the polyhedral polysiloxane modification is performed after mixing with polysiloxane having two or more alkenyl groups in one molecule. A method of mixing the body is desirable. In addition, a polyhedral polysiloxane modified body that is a reaction component, and a polysiloxane having two or more alkenyl groups in one molecule are well mixed and a stable molded product is easily obtained. It is preferable to mix an inorganic filler with a mixture of polysiloxane having two or more alkenyl groups in one molecule.

  The means for mixing these inorganic fillers is not particularly limited, but specifically, for example, a stirrer such as a two-roll or three-roll, a planetary stirring deaerator, a homogenizer, a dissolver, a planetary mixer, etc. And melt kneaders such as a plast mill. The mixing of the inorganic filler may be performed at normal temperature, may be performed by heating, may be performed under normal pressure, or may be performed under reduced pressure. If the temperature during mixing is high, the composition may be cured before molding.

  The polysiloxane composition of the present invention may optionally contain various additives such as phosphors, colorants, heat resistance improvers, reaction control agents, mold release agents, and dispersants for fillers. Can be added. Examples of the filler dispersant include diphenylsilane diol, various alkoxysilanes, carbon functional silane, silanol group-containing low molecular weight siloxane, and the like. In addition, it is preferable to stop these arbitrary components to the minimum addition amount so that the effect of this invention may not be impaired.

  In the polysiloxane composition of the present invention, the above-described components are uniformly mixed using a kneader such as a roll, a Banbury mixer, a kneader, or a planetary stirring deaerator, and heat-treated as necessary. Or you may.

The polysiloxane composition of the present invention can be used as a molded article. As a molding method, any method such as extrusion molding, compression molding, blow molding, calender molding, vacuum molding, foam molding, injection molding, liquid injection molding, and cast molding can be used.
Specific uses of the molded product obtained in the present invention include, for example, substrate materials in the field of liquid crystal displays, light guide plates, prism sheets, deflection plates, retardation plates, viewing angle correction films, adhesives, color filters, polarizers. Examples of the peripheral material of the liquid crystal display device such as a protective film and a film for liquid crystal such as a passivation film are exemplified. It is also used in PDP (plasma display) sealants, antireflection films, optical correction films, housing materials, front glass protective films, front glass substitute materials, adhesives, color filters, passivation films, and LED display devices. LED element mold material, front glass protective film, front glass substitute material, adhesive, color filter, passivation film, substrate material for plasma addressed liquid crystal display, light guide plate, prism sheet, deflector plate, retardation plate, field of view Corner correction film, adhesive, color filter, polarizer protective film, passivation film, front glass protective film, front glass substitute material, color filter, adhesive, passivation film, and field emission in organic EL displays Various film substrate in Isupurei (FED), front glass protective films, front glass substitute material, adhesive, a color filter, a passivation film is exemplified.

  In the optical recording field, VD (video disc), CD / CD-ROM, CD-R / RW, DVD-R / DVD-RAM, MO / MD, PD (phase change disc), disc substrate material for optical cards, Examples include pickup lenses, protective films, sealants, and adhesives. More specifically, optical pickup members such as next-generation DVDs, such as pickup lenses, collimator lenses, objective lenses, sensor lenses, protective films, element sealants, sensor sealants, gratings, adhesives, prisms And a wave plate, a correction plate, a splitter, a hologram, a mirror, and the like.

  In the field of optical equipment, examples include still camera lens materials, viewfinder prisms, target prisms, viewfinder covers, and light receiving sensor sections. In addition, a photographing lens and a viewfinder of a video camera are exemplified. Moreover, the projection lens of a projection television, a protective film, a sealing agent, an adhesive agent, etc. are illustrated. Examples are materials for lenses of optical sensing devices, sealants, adhesives, and films.

  In the field of optical components, fiber materials, lenses, waveguides, element sealants, adhesives and the like around optical switches in optical communication systems are exemplified. Examples include optical fiber materials, ferrules, sealants, adhesives and the like around the optical connector. Examples of optical passive components and optical circuit components include lenses, waveguides, LED element sealants, adhesives, and the like. Examples include substrate materials, fiber materials, element sealants, adhesives, and the like around an optoelectronic integrated circuit (OEIC).

  In the field of optical fibers, examples include sensors for industrial use such as lighting and light guides for decorative displays, displays and signs, and optical fibers for communication infrastructure and for connecting digital devices in the home.

  Examples of the semiconductor integrated circuit peripheral material include an interlayer insulating film, a passivation film, an LSI, and a resist material for microlithography for an LSI material.

  In the field of automobiles and transport equipment, automotive lamp reflectors, bearing retainers, gear parts, anti-corrosion coatings, switch parts, headlamps, engine internal parts, electrical parts, various interior and exterior parts, drive engines, brake oil tanks, automobile protection Examples include rusted steel plates, interior panels, interior materials, protective / bundling wireness, fuel hoses, automobile lamps, and glass substitutes. Moreover, the multilayer glass for rail vehicles is illustrated. Further, examples thereof include a toughness imparting agent for aircraft structural materials, engine peripheral members, wireness for protection and binding, and corrosion-resistant coating.

  In the construction field, interior / processing materials, electrical covers, sheets, glass interlayers, glass substitutes, and solar cell peripheral materials are exemplified. In agriculture, a house covering film is exemplified.

  Next-generation DVDs, organic EL element peripheral materials, organic photorefractive elements, light-amplifying elements that are light-to-light conversion devices, optical arithmetic elements, substrate materials around organic solar cells, etc. Examples thereof include fiber materials, element sealants, and adhesives.

  Next, although the composition of this invention is demonstrated in detail based on an Example, this invention is not limited only to these Examples.

(viscosity)
An E-type viscometer manufactured by Tokyo Keiki was used. Measurement was performed at a measurement temperature of 23.0 ° C. and an EHD type 48φ 1-fold cone.

(SiH value)
400 MHz NMR manufactured by Varian Technologies Japan Limited was used. The SiH value of the modified polyhedral polysiloxane is obtained by calculating the following formula (1) by making a mixture of the modified polyhedral polysiloxane and dibromoethane and measuring the NMR.
SiH value (mol / kg) = [integral value of peak attributed to SiH group of polyhedral polysiloxane modified product] / [integral value of peak attributed to methyl group of dibromoethane] × 4 × [in the mixture Dibromoethane weight] / [Molecular weight of dibromoethane] / [Modified polyhedral polysiloxane weight in mixture] (1)
Calculated using

(Preparation of samples for heat resistance test and light resistance test)
A polysiloxane-based composition was filled into a mold and thermally cured in a convection oven at 80 ° C. × 2 hours, 100 ° C. × 1 hour, 150 ° C. × 5 hours to prepare a sample having a thickness of 2 mm.

(Heat resistance test)
The sample prepared as described above was cured for 200 hours in a convection oven (in air) set at a temperature of 150 ° C. and visually observed. The case where no change in color due to coloring or the like was observed was evaluated as ◯, and the case where it was observed was evaluated as ×.

(Light resistance test)
A metering weather meter (model M6T) manufactured by Suga Test Instruments Co., Ltd. was used. The sample prepared as described above was irradiated with a black panel temperature of 120 ° C. and an irradiance of 0.53 kW / m ² to an integrated irradiance of 50 MJ / m ² and observed visually. The case where no change in color due to coloring or the like was observed was evaluated as ◯, and the case where it was observed was evaluated as ×.

(Creation of sample for cold thermal shock test)
In an LED package manufactured by Enomoto Co., Ltd. (product name: TOP LED 1-IN-1, external dimensions 3528, 3.5 mm × 2.8 mm × 1.9 mm, inner diameter 2.4 mm), 0.4 mm × 0.4 mm × 0. Two 2 mm single crystal silicon chips were bonded with an epoxy adhesive (product name: LOCTITE 348) manufactured by Henkel Japan, and fixed by heating for 30 minutes in a convection oven set at 150 ° C. A polysiloxane-based composition was injected here, and a sample was prepared by thermosetting in a convection oven at 80 ° C. × 2 hours, 100 ° C. × 1 hour, 150 ° C. × 5 hours.

(Cold thermal shock resistance test)
The sample prepared as described above was subjected to 200 cycles of high temperature holding 100 ° C., 30 minutes, low temperature holding −40 ° C., 30 minutes using a thermal shock tester (TSA-71H-W manufactured by ESPEC), A sample was observed. After the test, if there was no change visually, it was rated as “C”, and if it cracked or peeled off or colored with the package, it was marked “X”.

(Making samples for moisture permeability test)
(In the present invention, the moisture permeability of the cured product was used as an index of the gas barrier property of the obtained cured product. That is, a low moisture permeability is synonymous with a high gas barrier property.) Polysiloxane composition Was filled in a mold and thermally cured in a convection oven at 80 ° C. × 2 hours, 100 ° C. × 1 hour, 150 ° C. × 5 hours to prepare a sample of 5 cm square and 2 mm thickness. This sample was cured for 24 hours in an environment of room temperature 25 ° C. and humidity 55% RH.

(Moisture permeability test)
A jig is prepared by fixing a 5 cm square polyisobutylene rubber sheet (3 mm thick, 3 cm square inside so as to be a square shape) on top of a 5 cm square plate glass (0.5 mm thick), 1 g of calcium chloride (for moisture measurement) manufactured by Wako Pure Chemical Industries, Ltd. is filled into a square shape. Furthermore, the above 5 cm square sample with a thickness of 2 mm is fixed to the upper part, and this is used as a test specimen. The test specimen is cured for 24 hours at a temperature of 40 ° C. and a humidity of 90% RH in a thermo-hygrostat (PR-2KP manufactured by ESPEC).
Moisture permeability (g / m ² / day) = {(total weight of specimen after moisture permeability test (g)) − (total weight of specimen before moisture permeability test (g))} × 10000/9 (2)
The moisture permeability (water vapor transmission rate) was calculated according to

(Hydrogen sulfide test: H ₂ S test)
A polysiloxane-based composition is injected into an LED package (product name: TOP LED 1-IN-1) manufactured by Enomoto Co., Ltd., and heat-cured in a convection oven at 80 ° C. × 2 hours, 100 ° C. × 1 hour, 150 ° C. × 5 hours. To make a sample. This sample was put in a flow type gas corrosion tester (Factkey KG130S), and a hydrogen sulfide exposure test was conducted for 96 hours under the conditions of 40 ° C., 80% RH, and hydrogen sulfide 3 ppm. After the test, if the package reflector was not discolored, it was rated as ◯, if slightly discolored, Δ, and if discolored, ×.

(Phosphor sedimentation test)
To 5 g of the polysiloxane composition, 0.05 g of a phosphor (Y3957 manufactured by Intematics) was added, and the mixture was thoroughly stirred and allowed to stand. The observation was made after 1 hour, and when the phosphor remained dispersed, it was marked as ◯, and when sedimentation was observed, it was marked as x.

(Production Example 1)
To 1262 g of a 48% choline aqueous solution (trimethyl-2hydroxyethylammonium hydroxide aqueous solution), 1083 g of tetraethoxysilane was added and stirred vigorously at room temperature for 2 hours. When the reaction system generated heat and became a homogeneous solution, the stirring was loosened and the reaction was further continued for 12 hours. Next, 1000 mL of methanol was added to the solid produced in the reaction system to obtain a uniform solution.

  While vigorously stirring a solution of 537 g of dimethylvinylchlorosilane, 645 g of trimethylsilyl chloride and 1942 mL of hexane, the methanol solution was slowly added dropwise. After completion of the dropwise addition, the mixture was reacted for 1 hour, and then the organic layer was extracted and concentrated to obtain a solid. Next, the produced solid is washed by vigorously stirring in methanol and filtered to obtain a trihedral polysiloxane compound having a polyhedral structure having 16 Si atoms and an alkenyl group having 3 vinyl groups. 592 g of (vinyldimethylsiloxy) pentakis (trimethylsiloxy) octasilsesquioxane (Fw = 1166.2) was obtained as a white solid.

Example 1
10 g of the polyhedral polysiloxane compound having an alkenyl group obtained in Production Example 1 is dissolved in 20 g of toluene, and further a xylene solution of a platinum vinylsiloxane complex (a platinum vinylsiloxane complex containing 3 wt% as platinum, Umicore Precious Metals Japan). Manufactured, Pt-VTSC-3X) 0.9 μL was dissolved. The solution thus obtained was converted to 3.6 g of 1,3,5,7-tetrahydrogen-1,3,5,7-tetramethylcyclotetrasiloxane (polyhedral polysiloxane having an alkenyl group used). An amount of 2.3 hydrosilyl groups with respect to one alkenyl group of the compound) and 7.2 g of toluene were added dropwise and heated at 105 ° C. for 2 hours. When this solution was subjected to ¹ H-NMR measurement, it was confirmed that alkenyl groups derived from polyhedral polysiloxane compounds having alkenyl groups had disappeared. In addition to this solution, 2.9 g of vinyldiphenylmethylsilane prepared separately (to one hydrosilyl group of 1,3,5,7-tetrahydrogen-1,3,5,7-tetramethylcyclotetrasiloxane used) On the other hand, a solution of 5 g of toluene in an amount of 0.21 alkenyl groups) was added dropwise and heated at 105 ° C. for 2 hours. When this solution was subjected to ¹ H-NMR measurement, it was confirmed that a vinyl group derived from vinyldiphenylmethylsilane had disappeared. After dissolution and cooling to room temperature, toluene was distilled off to obtain 16.2 g (SiH value: 1.16 mol / kg) of a modified liquid polyhedral polysiloxane. 0.93 g of 1,5-divinyl-3,3-diphenyl-1,1,5,5-tetramethyltrisiloxane was added to 5.0 g of the resulting modified product and stirred to obtain a polysiloxane composition. . Various evaluations described above were performed using the composition thus obtained, and the results are shown in Table 1.

(Example 2)
10 g of the polyhedral polysiloxane compound having an alkenyl group obtained in Production Example 1 is dissolved in 20 g of toluene, and further a xylene solution of a platinum vinylsiloxane complex (a platinum vinylsiloxane complex containing 3 wt% as platinum, Umicore Precious Metals Japan). Manufactured, Pt-VTSC-3X) 0.9 μL was dissolved. The solution thus obtained was treated with 3.1 g of 1,3,5,7-tetrahydrogen-1,3,5,7-tetramethylcyclotetrasiloxane (polyhedral polysiloxane having an alkenyl group used). An amount of 2.0 hydrosilyl groups per alkenyl group of the compound) and 6.2 g of toluene were added dropwise and heated at 105 ° C. for 2 hours. When this solution was subjected to ¹ H-NMR measurement, it was confirmed that alkenyl groups derived from polyhedral polysiloxane compounds having alkenyl groups had disappeared. Further, 2.4 g of vinyldiphenylmethylsilane prepared separately (to one hydrosilyl group of 1,3,5,7-tetrahydrogen-1,3,5,7-tetramethylcyclotetrasiloxane used) was added to this solution. On the other hand, a solution of 5 g of toluene in an amount of 0.21 vinyl groups) was added dropwise and heated at 105 ° C. for 2 hours. When this solution was subjected to ¹ H-NMR measurement, it was confirmed that the vinyl group derived from diphenylmethylvinylsilane had disappeared. After dissolution and cooling to room temperature, toluene was distilled off to obtain 15.3 g (SiH value 1.04 mol / kg) of a liquid polyhedral polysiloxane modified. 0.83 g of 1,5-divinyl-3,3-diphenyl-1,1,5,5-tetramethyltrisiloxane was added to 5.0 g of the resulting modified product and stirred to obtain a polysiloxane composition. . Various evaluations described above were performed using the composition thus obtained, and the results are shown in Table 1.

(Example 3)
10 g of the polyhedral polysiloxane compound having an alkenyl group obtained in Production Example 1 is dissolved in 20 g of toluene, and further a xylene solution of a platinum vinylsiloxane complex (a platinum vinylsiloxane complex containing 3 wt% as platinum, Umicore Precious Metals Japan). Manufactured, Pt-VTSC-3X) 0.9 μL was dissolved. 1.9 g of 1,3,5,7-tetrahydrogen-1,3,5,7-tetramethylcyclotetrasiloxane (polyhedral polysiloxane system having an alkenyl group used) was obtained. Of the polyhedral polysiloxane compound having an alkenyl group used, and 0.85 g of 1,1,3,3-tetramethyldisiloxane The solution was added dropwise to a mixed solution of 5.5 g of toluene in an amount of 0.5 hydrosilyl group per alkenyl group, and heated at 105 ° C. for 2 hours. When this solution was subjected to ¹ H-NMR measurement, it was confirmed that alkenyl groups derived from polyhedral polysiloxane compounds having alkenyl groups had disappeared. Further, 2.4 g of vinyldiphenylmethylsilane prepared separately (to one hydrosilyl group of 1,3,5,7-tetrahydrogen-1,3,5,7-tetramethylcyclotetrasiloxane used) was added to this solution. On the other hand, a solution of 5 g of toluene in an amount of 0.21 vinyl groups) was added dropwise and heated at 105 ° C. for 2 hours. When this solution was subjected to ¹ H-NMR measurement, it was confirmed that the vinyl group derived from diphenylmethylvinylsilane had disappeared. After dissolution and cooling to room temperature, 12.4 g of a liquid polyhedral polysiloxane modified product (SiH value 0.92 mol / kg) was obtained by distilling off toluene. 0.75 g of 1,5-divinyl-3,3-diphenyl-1,1,5,5-tetramethyltrisiloxane was added to 5.0 g of the resulting modified product and stirred to obtain a polysiloxane composition. . Various evaluations described above were performed using the composition thus obtained, and the results are shown in Table 1.

(Comparative Example 1)
A solution of 10 g of the polyhedral polysiloxane compound having an alkenyl group obtained in Production Example 1 and 20 g of toluene was added to a xylene solution of a platinum vinylsiloxane complex (a platinum vinylsiloxane complex containing 3 wt% as platinum, Umicore Precious Metals Japan). Manufactured, Pt-VTSC-3X) 0.8 μL was dissolved. The solution thus obtained was added to 20 g of 1,3,5,7-tetrahydrogen-1,3,5,7-tetramethylcyclotetrasiloxane (polyhedral polysiloxane compound having an alkenyl group used). An amount of 12.7 hydrosilyl groups relative to one alkenyl group) was slowly added dropwise to a solution of 10 g of toluene and reacted at 105 ° C. for 2 hours. When this solution was subjected to ¹ H-NMR measurement, it was confirmed that alkenyl groups derived from polyhedral polysiloxane compounds having alkenyl groups had disappeared. Ethinylcyclohexanol 1.06 μl and dimethyl maleate 0.25 μl were added, and toluene and unreacted components were distilled off to obtain 16.5 g of a liquid modified product (SiH value 4.72 mol / kg). 3.1 g of 1,5-divinyl-3,3-diphenyl-1,1,5,5-tetramethyltrisiloxane was added to 5,0 g of the resulting modified product and stirred to obtain a composition. Various evaluations described above were performed using the composition thus obtained, and the results are shown in Table 1.

(Comparative Example 2)
A solution of 10 g of the polyhedral polysiloxane compound having an alkenyl group obtained in Production Example 1 and 20 g of toluene was added to a xylene solution of a platinum vinylsiloxane complex (platinum vinylsiloxane complex containing 3 wt% as platinum, Umicore Precious Metals Japan). Manufactured, Pt-VTSC-3X) 0.8 μL was dissolved. The solution thus obtained was added to 20 g of 1,3,5,7-tetrahydrogen-1,3,5,7-tetramethylcyclotetrasiloxane (polyhedral polysiloxane compound having an alkenyl group used). An amount of 12.7 hydrosilyl groups relative to one alkenyl group) was slowly added dropwise to a solution of 10 g of toluene and reacted at 105 ° C. for 2 hours. When this solution was subjected to ¹ H-NMR measurement, it was confirmed that alkenyl groups derived from polyhedral polysiloxane compounds having alkenyl groups had disappeared. Ethinylcyclohexanol 1.06 μl and dimethyl maleate 0.25 μl were added, and toluene and unreacted components were distilled off to obtain 16.5 g of a liquid modified product (SiH value 4.72 mol / kg). To 5,0 g of the obtained modified product, 3.1 g of 1,5-divinyl-3,3-diphenyl-1,1,5,5-tetramethyltrisiloxane and 1.3 g of vinyldiphenylmethylsilane were added and stirred. A composition was obtained. Various evaluations described above were performed using the composition thus obtained, and the results are shown in Table 1.

As described above, the polyhedral polysiloxane compound of the present invention can be made into a transparent liquid and is easy to handle with the transparent liquid, and the molded body obtained from the composition using the corresponding compound has a heat resistance, Excellent light resistance and little decrease in light transmittance.

Claims (15)

Obtained by hydrosilylating a polyhedral polysiloxane compound (a) having an alkenyl group, a compound (b) having a hydrosilyl group, and an organosilicon compound (c) having one alkenyl group in one molecule. A modified polyhedral polysiloxane,
Modified polyhedral polysiloxane, wherein hydrogen atom directly connected to Si atom of component (b) is added within a range of 1.0 to less than 2.5 per alkenyl group of component (a) . The modified polyhedral polysiloxane according to claim 1, wherein the component (c) is an organosilicon compound having one or more aryl groups.   The modified polyhedral polysiloxane according to claim 1 or 2, which is liquid at a temperature of 20 ° C.   The modified polyhedral polysiloxane according to any one of claims 1 to 3, which has a viscosity of 10 Pa · s or more at a temperature of 20 ° C. The modified polyhedral polysiloxane according to any one of claims 1 to 4, wherein the compound (b) having a hydrosilyl group is a cyclic siloxane having a hydrosilyl group and / or a linear siloxane. . The polyhedral polysiloxane compound (a) having an alkenyl group has the formula
[AR ¹ ₂ SiO—SiO _3/2 ] _a [R ² ₃ SiO—SiO _3/2 ] _b
(A + b is an integer of 6 to 24, a is an integer of 1 or more, b is 0 or an integer of 1 or more; A is an alkenyl group; R ¹ is an alkyl group or an aryl group; R ² is an alkyl group or an aryl group Or a group linked to other polyhedral skeleton polysiloxane)
The modified polyhedral polysiloxane according to any one of claims 1 to 5, wherein the modified polyhedral polysiloxane is composed of a siloxane unit represented by formula (1). Formula [XR ³ ₂ SiO—SiO _3/2 ] _a [R ⁴ ₃ SiO—SiO _3/2 ] _b
[A + b is an integer of 6 to 24, a is an integer of 1 or more, b is 0 or an integer of 1 or more; R ³ is an alkyl group or an aryl group; R ⁴ is an alkenyl group, a hydrogen atom, an alkyl group, an aryl group Or a group linked to another polyhedral skeleton polysiloxane, X has a structure represented by the following general formula (1) or general formula (2), and when there are a plurality of X, the general formula (1 ) Or the structure of the general formula (2) may be different, or the structure of the general formula (1) or the general formula (2) may be mixed. X has at least one of general formula (1) and / or general formula (2).

{L is an integer of 2 or more; m is an integer of 0 or more; n is an integer of 2 or more; Y and Z are a polyhedral polysiloxane via a hydrogen atom, an alkenyl group, an alkyl group, an aryl group, or an alkylene chain. The bonded site or the structure of the following general formula (3) may be the same or different. However, at least one of Y or Z is a hydrogen atom, and at least one has a structure of the following general formula (3). }

(Q is an integer of 0 or more; R ⁵ is a group containing an organosilicon compound) R is an alkyl group or an aryl group. ]
A polyhedral polysiloxane modified product comprising a siloxane unit represented by the formula: The modified polyhedral polysiloxane according to claim 7, wherein R ⁵ contains one or more aryl groups.   The polysiloxane type composition containing the polyhedral structure siloxane modified body of any one of Claims 1-8.   A polysiloxane composition comprising the modified polyhedral siloxane according to any one of claims 1 to 9 and a polysiloxane having two or more alkenyl groups in one molecule. The polysiloxane composition according to claim 10, wherein the polysiloxane having two or more alkenyl groups in one molecule has one or more aryl groups.   The polysiloxane composition according to claim 9, comprising a hydrosilylation catalyst.   The polysiloxane composition according to any one of claims 9 to 12, comprising a curing retarder. Hardened | cured material formed by hardening | curing the polysiloxane type composition of any one of Claims 9-13. An optical device comprising the polysiloxane composition according to any one of claims 9 to 13 as a sealing layer.