JP2012201778A - Resin composition for water-based coating and coating provided by compounding the resin composition for water-based coating - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a resin composition for water-based coating, which drastically improves weatherability without decreasing contamination resistance and film appearances such as glossiness and without using a complex production method.SOLUTION: There is provided a resin composition for water-based coating comprising (A) a water-soluble and/or water-dispersible resin, (B) an organosilane represented by general formula (1): Si(R)(OR)and/or a hydrolytic condensate thereof [wherein, Ris the same or different and 1-4C alkyl; Ris the same or different and a 2-8C (substituted) organic group; and n=1 or 2], and (C) a curing catalyst promoting hydrolysis/condensation reaction of alkoxysilyl.

Description

  The present invention is suitable for various coatings such as buildings, structures, building materials, ships, metal products, road vehicles, electrical machinery, machinery, woodwork products, etc., forming a hydrophilic surface and having excellent weather resistance. The present invention relates to a paint resin composition and a paint obtained by blending the aqueous paint resin composition.

  In recent years, in the field of paints, from the viewpoint of pollution control or resource saving, attempts have been made to switch from using organic solvents to water-soluble or water-dispersed resins. However, water-based paints tended to be inferior in coating film performance compared to solvent-based paints. Under such circumstances, water-based paints are also required to have the same coating film properties as solvent-based paints, and in particular, are required to have high performance such as stain resistance.

  In response to these requirements, a method of blending an organosilicate in a paint is known (for example, see Table 4 in Patent Document 1). By this method, the hydrophilicity of the formed coating film is improved, and it is effective in preventing the adhesion of oily contaminants, and the adhered contaminants can be washed away with water droplets such as rain. However, when the above method is applied to an aqueous paint, there is a problem that the miscibility of the organosilicate into the aqueous paint is poor and the surface gloss is lowered.

  On the other hand, as a method for improving the miscibility of organosilicates in water-based paints, water-soluble and / or water-dispersible curing agents having a functional group and a hydrophilic group in the organosilicate molecule, alkoxysilane compounds There is disclosed a method of mixing and adding a compound that promotes hydrolysis / condensation (see, for example, Patent Document 2). By this method, the miscibility with the water-based paint was improved, and the extreme decrease in surface gloss and water resistance was solved.

  On the other hand, weather resistance is raised as an important function along with contamination resistance. As one means for improving the weather resistance, an organic-inorganic composite aqueous resin in which an organosilane is reacted with an acrylic resin has been proposed (see, for example, Patent Document 3). Although the weather resistance is improved by this method, the production method thereof is very complicated, and cannot be applied to general emulsions for paints.

  Further, since the organosilane used exhibits water repellency, there is also a problem that the stain resistance is not sufficient.

WO94 / 06870 Publication JP 2005-015676 A Japanese Patent Laid-Open No. 11-349815

  The problem to be solved by the present invention is to improve weather resistance and stain resistance by adding to a general coating resin without requiring a complicated production method.

The inventors have (A) a water-soluble and / or water-dispersible resin, (B) an organosilane represented by the general formula (1) and / or a hydrolysis condensate thereof Si (R ² ) _n (OR ¹ ). _4-n (1)
(Wherein R ¹ is the same or different and the alkyl group has 1 to 4 carbon atoms, R ² is the same or different substituted and unsubstituted organic group having 2 to 8 carbon atoms, n = 1 or 2), ( C) A resin composition for water-based paints containing a curing catalyst that promotes hydrolysis / condensation reaction of alkoxysilyl groups. (Claim 1)
The resin composition for water-based paint according to claim 1, further comprising (D) an organosilicate and / or a modified product thereof. (Claim 2)
The resin composition for water-based paints according to any one of claims 1 to 2, further comprising (E) a hindered amine light stabilizer (HALS) having a logarithmic value (pKa) of the reciprocal of the acid dissociation constant of 7 or less. . (Claim 3)
The resin composition for water-based paints according to any one of claims 1 to 3, wherein the water-soluble and / or water-dispersible resin (A) is a resin having a polyoxyalkylene chain. (Claim 4)
The curing catalyst for promoting the hydrolysis / condensation reaction of the alkoxysilyl group (C) is one or more selected from organic tin compounds, acidic phosphate esters, and reaction products of acidic phosphate esters and amines. The resin composition for water-based paints according to any one of claims 1 to 4, wherein the resin composition is for water-based paints. (Claim 5)
The resin composition for water-based paints according to any one of claims 1 to 5, wherein all or part of the (A) water-soluble and / or water-dispersible resin is an alkoxysilyl group-containing acrylic resin. (Claim 6)
The resin composition for water-based paints according to any one of claims 1 to 6, wherein the component (B) is vinylsilane and / or a hydrolysis condensate thereof. (Claim 7)
(A) a base material (I) containing a water-soluble and / or water-dispersible resin, (B) an organosilane represented by the general formula (1) and / or a hydrolysis condensate thereof,
Si (R ² ) _n (OR ¹ ) _4-n (1)
(Wherein R ¹ is the same or different and the alkyl group has 1 to 4 carbon atoms, R ² is the same or different substituted and unsubstituted organic group having 2 to 8 carbon atoms, n = 1 or 2), ( C) Curing catalyst for promoting hydrolysis and condensation reaction of alkoxysilyl group, (D) Organosilicate and / or modified product thereof, and (F) Water-soluble and / or water having a reactive functional group and a hydrophilic group in the molecule The resin composition for a two-component or multicomponent water-based paint according to any one of claims 1 to 7, which is a two-component or multicomponent type used by mixing the auxiliary agent (II) containing a dispersible curing agent before use. object. (Claim 8)
The coating composition formed by mix | blending the resin composition for water-based coatings in any one of Claims 1-8. (Claim 9)
Claims obtained by blending the base material (I) with (A) water-soluble and / or water-dispersible resin and (G) titanium dioxide subjected to at least three kinds of surface treatments of silicon dioxide, aluminum oxide and zirconium dioxide. Item 10. The coating composition according to Item 9. (Claim 10)

  By using the resin composition for water-based paints of the present invention, a paint having excellent weather resistance and stain resistance can be produced without using a paint resin produced by a complicated production method.

  Hereinafter, the present invention will be described in detail based on an embodiment thereof.

[(A) Water-soluble and / or water-dispersible resin]
As the water-soluble and / or water-dispersible resin, any conventionally known one can be used without particular limitation as long as it has a film-forming ability. Specific examples thereof include an acrylic resin emulsion and an acrylic silicon resin emulsion. , Urethane resin emulsion, fluororesin emulsion, epoxy resin emulsion, polyester resin emulsion, alkyd resin emulsion, melamine resin emulsion, and the like, but are not limited thereto. These may be used alone or in combination of two or more. Among these, from the viewpoint of weather resistance of the formed coating film, it is preferably at least one selected from the group consisting of an acrylic resin emulsion, an acrylic silicon resin emulsion, a fluororesin emulsion, and a urethane resin emulsion.

  As the acrylic resin emulsion, those obtained by radical copolymerization of an acrylic monomer and a monomer copolymerizable with the acrylic monomer can be used.

  Although there is no limitation in particular as the said monomer which can be used, As a specific example, methyl (meth) acrylate, ethyl (meth) acrylate, n-butyl (meth) acrylate, iso-butyl (meth) acrylate, tert -Butyl (meth) acrylate, benzyl (meth) acrylate, cyclohexyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, isodecyl (meth) acrylate, lauryl (meth) acrylate, tridecyl (meth) acrylate, stearyl (meth) acrylate (Meth) acrylate monomers such as isobornyl (meth) acrylate; aromatic hydrocarbon vinyl monomers such as styrene, α-methylstyrene, chlorostyrene, 4-hydroxystyrene, vinyltoluene; vinyl acetate, propion Vinyl esters and allyl compounds such as vinyl, vinyl versatate and diallyl phthalate; Nitrile group-containing vinyl monomers such as (meth) acrylonitrile; Epoxy group-containing vinyl monomers such as glycidyl (meth) acrylate; 2-hydroxy Ethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 2-hydroxyethyl vinyl ether, hydroxystyrene, Aronics 5700 (manufactured by Toagosei Co., Ltd.), placelFA-1, placelFA-4, placelFM-1, placelFM-4 (Above, manufactured by Daicel Chemical Industries, Ltd.), HE-10, HE-20, HP-10, HP-20 (above made by Nippon Shokubai Co., Ltd.), Blemmer PEP series, Blemmer NKH-5050, Blemmer GLM (above (Manufactured by NOF Corporation), hydroxyl group-containing vinyl monomers such as hydroxyl group-containing vinyl modified hydroxyalkyl vinyl monomers; AS-6, AN-6, AA- which are macromonomers manufactured by Toagosei Co., Ltd. 6, compounds such as AB-6, AK-5, vinyl methyl ether, propylene, butadiene and the like.

  Furthermore, a hydrophilic vinyl monomer capable of improving the stability of the emulsion can also be used. Examples of the vinyl monomer having a hydrophilic group that can be used include sodium styrenesulfonate, sodium 2-sulfoethyl methacrylate, 2-sulfoethyl methacrylate ammonium, and vinyl monomers having a polyoxyalkylene chain.

  In particular, when a vinyl monomer having a polyoxyalkylene chain is used, the stain resistance is greatly improved due to a synergistic effect with the later-described (B) organosilicate and / or a modified product thereof.

Although there is no limitation in the vinyl-type monomer which has a polyoxyalkylene chain, the acrylic acid ester or methacrylic acid ester which has a polyoxyalkylene chain is preferable.
Specific examples include commercial products manufactured by NOF Corporation, Blemmer PE-90, Blemmer PE-200, Blemmer PE-350, Blemmer AE-90, Blemmer AE-200, Blemmer AE-350, Blemmer PP-500. , Blemmer PP-800, Blemmer PP-1000, Blemmer AP-400, Blemmer AP-550, Blemmer AP-800, Blemmer 700 PEP-350B, Blemmer 10 PEP-550B, Blemmer 55 PET-400, Blemmer 30 PET-800, Blemmer 55 PET-800 , Blemmer 30PPT-800, Blemmer 50PPT-800, Blemmer 70PPT-800, Blemmer PME-100, Blemmer PME-200, Blemmer PME-400, Blemmer PM -1000, Blemmer PME-4000, Blemmer AME-400, Blemmer 50POEP-800B, Blemmer 50AOEP-800B, Blemmer AEP, Blemmer AET, Blemmer APT, Blemmer PLE, Blemmer ALE, Blemmer PSE, Blemmer ASE, Blemmer PKE, Blemmer AKE, Blemmer PNE, Blemmer ANE, Blemmer PNP, Blemmer ANP, Blemmer PNEP-600; commercial products manufactured by Kyoeisha Chemical Co., Ltd., light ester 130MA, light ester 041MA, light ester MTG, light acrylate EC-A, light acrylate MTG -A, light acrylate 130A, light acrylate DPM-A, light acrylate P-200A, light acrylic NP-4EA, light acrylate NP-8EA, light acrylate EHDG-A; commercial products manufactured by Nippon Emulsifier Co., Ltd., MA-30, MA-50, MA-100, MA-150, RMA-1120, RMA-564, RMA-568, RMA-506, MPG130-MA, Antox MS-60, MPG-130MA, RMA-150M, RMA-300M, RMA-450M, RA-1020, RA-1120, RA-1820; new NK-ESTER M-20G, M-40G, M-90G, M-230G, AMP-10G, AMP-20G, AMP-60G, AM-90G, LA, which are commercially available products from Nakamura Chemical Co., Ltd .; Examples include commercial products manufactured by Sanyo Chemical Co., Ltd., such as Eleminol RS-30 and RS-3000.

  It is also possible to use a monomer having two or more polymerizable unsaturated bonds such as polyethylene glycol di (meth) acrylate, ethylene glycol di (meth) acrylate, triallyl cyanurate, allyl (meth) acrylate and divinylbenzene. Is possible.

  In addition, trifluoro (meth) acrylate, pentafluoro (meth) acrylate, perfluorocyclohexyl (meth) acrylate, 2,2,3,3-tetrafluoropropyl (meth) acrylate, β- (perfluorooctyl) ethyl (meth) ) By using a fluorine-containing vinyl monomer such as acrylate, a fluorine-containing acrylic resin emulsion having high water / oil repellency can be produced.

  Moreover, a crosslinked acrylic resin emulsion in which a carbonyl group-containing vinyl monomer is copolymerized with the above monomer and a compound containing a hydrazine and / or hydrazide group is blended can also be produced.

The acrylic silicone resin emulsion is obtained by modifying the acrylic resin emulsion with a silicon-containing compound, and has improved weather resistance compared to the acrylic resin emulsion. The modification may be performed at the emulsion synthesis stage or separately after the synthesis is completed.
Among the acrylic silicon resin emulsions, the alkoxysilyl group-containing acrylic resin emulsion is particularly excellent in terms of stain resistance and weather resistance.

Furthermore, by using a multi-stage polymerization of an alkoxysilyl group-containing acrylic resin emulsion to form a core / shell structure, flexibility can be imparted without deteriorating stain resistance and weather resistance, such as elastic paints, etc. It can be applied to flexible bases.
The alkoxysilyl group-containing acrylic resin emulsion is obtained by radical copolymerization of (a) an acrylic monomer, (b) an alkoxysilyl group-containing monomer, and (c) a monomer copolymerizable therewith. Can be used.

  Specific examples of the (a) acrylic monomer include methyl (meth) acrylate, ethyl (meth) acrylate, iso-propyl (meth) acrylate, n-butyl (meth) acrylate, iso-butyl (meth) acrylate, tert-butyl (meth) acrylate, benzyl (meth) acrylate, cyclohexyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, isodecyl (meth) methacrylate, lauryl (meth) acrylate, tridecyl (meth) acrylate, stearyl (meth) Examples include acrylate and isobornyl (meth) acrylate.

In particular, when 60% by weight or more of a methacrylic acid ester having an alkyl group having 4 or more carbon atoms and / or a cycloalkyl group is used, the storage stability of the emulsion is greatly improved.
(B) The alkoxysilyl group-containing monomer is not particularly limited, but the alkoxysilyl group-containing monomer (b1) represented by the general formula (2) is used for polymerization of the shell portion, and the alkoxy represented by the general formula (3). It is preferable to use the silyl group-containing monomer (b2) for the polymerization of the core part.
The alkoxysilyl group-containing monomer (b1) has the general formula (2)
R ³ R ⁴ _(3-a) SiX _a (2)
(Wherein R ³ is a monovalent organic group having a polymerizable double bond, R ⁴ is an alkyl group having 1 to 4 carbon atoms, X is an alkoxy group having 1 to 4 carbon atoms, a is 2 or 3) An organosilicon compound having 2 or 3 alkoxy groups and having a reactive double bond. Specific examples thereof include vinyltrimethoxysilane, γ- (meth) acryloxypropyltrimethoxysilane, vinyltriethoxysilane, γ- (meth) acryloxypropyltriethoxysilane, γ- (meth) acryloxypropyltripropoxy. Silane, γ- (meth) acryloxypropyltributoxysilane, vinylmethyldimethoxysilane, γ- (meth) acryloxypropylmethyldimethoxysilane, vinylmethyldiethoxysilane, γ- (meth) acryloxypropylmethyldiethoxysilane, γ- (Meth) acryloxypropylmethyldipropoxysilane, γ- (meth) acryloxypropylmethyldibutoxysilane, and the like can be used, and these can be used alone or in combination of two or more. Among these, X has particularly preferably 2 to 4 carbon atoms from the viewpoint of the storage stability of the emulsion.

By using 0.5 to 20 parts by weight, preferably 1 to 15 parts by weight, based on 100 parts by weight of the shell part in the core / shell type emulsion, the shell part is highly crosslinked, weather resistance, coating film hardness, Blocking resistance can be improved.
Further, the alkoxysilyl group-containing monomer (b2) has the general formula (3)
R ⁵ R ⁶ _(3-b) SiY _b (3)
(In the formula, R ⁵ is a monovalent organic group having a polymerizable double bond, R ⁶ is an alkyl group having 1 to 4 carbon atoms, Y is an alkoxy group having 1 to 4 carbon atoms, and b is a relation of b <a. And an organic silicon compound having 1 or 2 alkoxy groups and a reactive double bond. Specific examples thereof include vinylmethyldimethoxysilane, vinylmethyldiethoxysilane, γ- (meth) acryloxypropylmethyldimethoxysilane, γ- (meth) acryloxypropylmethyldiethoxysilane, γ- (meth) acryloxypropyl. Methyldipropoxysilane, γ- (meth) acryloxypropylmethyldibutoxysilane, vinyldimethylmethoxysilane, vinyldimethylethoxysilane, γ- (meth) acryloxypropyldimethylethoxysilane, γ- (meth) acryloxypropyldimethylmethoxy Silane, γ- (meth) acryloxypropyldimethylpropoxysilane, γ- (meth) acryloxypropyldimethylbutoxysilane, and the like can be used, and these can be used alone or in combination of two or more.

  By using these in an amount of 0 to 20 parts by weight, preferably 0.5 to 10 parts by weight, based on 100 parts by weight of the core part in the core / shell type emulsion, a mild cross-linked structure is introduced into the core part and the flexibility is impaired. The water resistance and weather resistance can be improved without any problems.

  It is preferable in terms of adhesion, tackiness, flexibility, and storage stability that the carbon numbers X and Y of the alkoxy groups (b1) and (b2) have a relationship of X> Y.

  The component (c) is not particularly limited as long as it is copolymerizable with the component (a) and (b). Specific examples thereof include aromatic hydrocarbon vinyl monomers such as styrene, α-methylstyrene, chlorostyrene, 4-hydroxystyrene, and vinyl toluene; vinyl acetate, vinyl propionate, vinyl versatate, diallyl phthalate, and the like. Vinyl esters and allyl compounds; Nitrile group-containing vinyl monomers such as (meth) acrylonitrile; Epoxy group-containing vinyl monomers such as glycidyl (meth) acrylate; 2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (Meth) acrylate, 2-hydroxyethyl vinyl ether, hydroxystyrene, Aronics 5700 (manufactured by Toagosei Co., Ltd.), packageFA-1, packageFA-4, packageFM-1, and packageFM-4 (above, Daicel) Gaku Co., Ltd.), HE-10, HE-20, HP-10, HP-20 (manufactured by Nippon Shokubai Co., Ltd.), Blemmer PEP series, Blemmer NKH-5050, Blemmer GLM (Nippon Oil Co., Ltd.) ), Hydroxyl group-containing vinyl monomers such as hydroxyl group-containing vinyl-modified hydroxyalkyl vinyl monomers; AS-6, AN-6, AA-6, AB-6 which are macromonomers manufactured by Toagosei Co., Ltd. Examples thereof include compounds such as AK-5, vinyl methyl ether, propylene, butadiene and the like.

  Furthermore, hydrophilic vinyl monomers can also be used. Examples of the vinyl monomer having a hydrophilic group that can be used include sodium styrenesulfonate, sodium 2-sulfoethyl methacrylate, 2-sulfoethyl methacrylate ammonium, and vinyl monomers having a polyoxyalkylene chain. Although there is no limitation in the vinyl-type monomer which has a polyoxyalkylene chain, the acrylic acid ester or methacrylic acid ester which has a polyoxyalkylene chain is preferable, As a specific example, Blenmer PE-90, PE- by NOF Corporation is mentioned. 200, PE-350, AE-90, AE-200, AE-350, PP-500, PP-800, PP-1000, AP-400, AP-550, AP-800, 700PEP-350B, 10PEP-550B, 55PET-400, 30PET-800, 55PET-800, 30PPT-800, 50PPT-800, 70PPT-800, PME-100, PME-200, PME-400, PME-1000, PME-4000, AME-400, 50POEP- 800B, 50AOEP-800B, AEP, ET, APT, PLE, ALE, PSE, ASE, PKE, AKE, PNE, ANE, PNP, ANP, PNEP-600, Kyoeisha Chemical Co., Ltd. light ester 130MA, 041MA, MTG, light acrylate EC-A, MTG- A, 130A, DPM-A, P-200A, NP-4EA, NP-8EA, EHDG-A, MA-30 manufactured by Nippon Emulsifier Co., Ltd., MA-50, MA-100, MA-150, RMA-1120, RMA-564, RMA-568, RMA-506, MPG130-MA, Antox MS-60, MPG-130MA, RMA-150M, RMA-300M, RMA-450M, RA-1020, RA-1120, RA-1820, new Nakamura Chemical Co., Ltd. NK-ESTER M-20G, M-40G, M-9 G, M-230G, AMP-10G, AMP-20G, AMP-60G, AM-90G, LA, and the like.

  In addition, a monomer having two or more polymerizable unsaturated bonds such as polyethylene glycol di (meth) acrylate, ethylene glycol di (meth) acrylate, triallyl cyanurate, allyl (meth) acrylate, divinylbenzene or the like is used. It is also possible. In this case, the generated particles have a structure having cross-linking, and the water resistance of the formed coating film is improved.

  Further, trifluoro (meth) acrylate, pentafluoro (meth) acrylate, perfluorocyclohexyl (meth) acrylate, 2,2,3,3-tetrafluoropropyl methacrylate, β- (perfluorooctyl) ethyl (meth) acrylate, etc. It is also possible to impart high water and oil repellency by using a fluorine-containing vinyl monomer.

  It is also possible to impart crosslinkability by using a carbonyl group-containing vinyl monomer such as diacetone acrylamide or methyl vinyl ketone and blending a compound containing hydrazine and / or hydrazide group. The water resistance of the coated film is improved.

  In particular, the use of a hydroxyl group-containing vinyl monomer and / or a vinyl monomer having a polyoxyalkylene chain in an amount corresponding to 0.5 to 20% by weight of the emulsion particles impairs the stability of the alkoxysilyl group. It is possible to improve the mechanical stability and chemical stability of the emulsion. Of these, vinyl monomers having a polyoxyalkylene chain having a hydroxyl group at the terminal are particularly effective.

  If the amount used is less than 0.5% by weight, the mechanical stability and chemical stability are poor, and if it exceeds 20% by weight, the water resistance is lowered. Especially preferably, it is 1 to 5 weight%.

  Next, the manufacturing method of an emulsion is demonstrated.

  It is obtained by emulsion polymerization of a mixture comprising the components (a), (b), and (c) by a known emulsion polymerization method.

  In the production of the core / shell type emulsion, first, a mixture comprising the components (a), (b2) and (c) is subjected to emulsion polymerization by a known emulsion polymerization method as a first stage, and the obtained core component is obtained. In the presence, the mixture comprising (a), (b1) and (c) is emulsion polymerized to introduce the shell component. In addition, you may divide | segment several times and superpose | polymerize in each component of a core part and a shell part.

  When the core component is sufficiently hydrophobic with respect to the shell component, the target composition can be obtained even if the shell component is polymerized first.

  In emulsion polymerization, commonly used ionic or nonionic surfactants can be used.

  Examples of the ionic surfactant include an anionic surfactant having a polyoxyethylene chain such as polyoxyethylene nonylphenyl ether sulfate, polyoxyethylene allyl ether sulfate, octylphenoxyethoxyethyl sulfonate, polyoxyethylene tridecyl ether sulfate, and the like. Sulfonic acid salts such as sodium lauryl sulfonate, sodium dodecylbenzene sulfonate and sodium isooctylbenzene sulfonate; ammonium salts such as imidazoline laurate and ammonium hydroxide are typical examples. An anionic surfactant having an oxyethylene chain is preferred.

  Examples of the nonionic surfactant include polyethylene glycol nonylphenyl ether; polyoxyethylenes such as polyoxyethylene nonylphenyl ether and polyoxyethylene lauryl ether.

  In the present invention, it is preferable to use a reactive surfactant having a polymerizable double bond in one molecule as the surfactant in terms of water resistance and weather resistance. In particular, when a reactive surfactant having a polyoxyalkylene group in the molecule is used, the mechanical stability can be improved.

  Specific examples of such reactive surfactants include, for example, Adeka Soap ER-10, ER-20, ER-30, ER-40, SR-05, SR-10, SR-20 manufactured by ADEKA Corporation, SR-30, SR-1025, SR-10S, NE-10, NE-20, NE-30, NE-40, SE-10N), Nippon Emulsifier Co., Ltd. Antox-MS-60, RMA-1120, RMA 564, RMA-568, RMA-506, Aqualon KH-05, KH-10, KH-0530, KH-1025, RN-20, RN-30, RN-50, RN- from Daiichi Kogyo Seiyaku Co., Ltd. 2025, HS-10, HS-20, HS-1025, BC-05, BC-10, BC-0515, BC-1025, Elyonol JS-2, JS-20 manufactured by Sanyo Chemical Industries, Ltd. RS-30, RS-300, manufactured by Kao Corp. LATEMUL S-180, S-180A, PD-104, PD-420, such as PD-430, PD-450 and the like.

  Of these, non-alkylphenol-based ones are preferred in consideration of the environment.

  The surfactants can be used alone or in admixture of two or more, and the amount used is 10 parts by weight or less, preferably 0.5 to 8 parts by weight based on 100 parts by weight of the total amount of monomers. is there.

  Although there is no limitation in particular as a polymerization initiator, In order to perform superposition | polymerization more stably, it is preferable to use a redox type | system | group as a polymerization initiator. Further, in order to maintain the stability of the mixed solution during the polymerization and perform the polymerization stably, the temperature is 70 ° C. or lower, preferably 40 to 65 ° C., and the pH is preferably adjusted to 5 to 9.

  Examples of the initiator used in the redox system include potassium persulfate, ammonium persulfate, hydrogen peroxide, t-butyl hydroperoxide, benzoyl peroxide, cumene hydroperoxide, and the like. Examples thereof include acidic sodium sulfite, Rongalite, Bruggolite FF-6 (manufactured by Bruggamann Chemical US), thiourea dioxide, L-ascorbic acid and the like. In particular, a combination of an organic peroxide such as t-butyl hydroperoxide, benzoyl peroxide, cumene hydroperoxide and the like and Rongalite, Bruggolite FF-6 or thiourea dioxide is preferable.

  Note that the reducing agent is particularly preferably Bruggolite FF-6 or thiourea dioxide which does not generate formaldehyde in consideration of the environment.

  The amount of the polymerization initiator used is 0.01 to 10 parts, preferably 0.05 to 5 parts by weight based on 100 parts by weight of the total amount of monomers. When the amount of the polymerization initiator used is less than 0.01 parts by weight, the polymerization may be difficult to proceed. When the amount exceeds 10 parts by weight, the molecular weight of the produced polymer tends to decrease. is there.

  In order to stably impart the catalytic activity of the polymerization initiator, a compound containing a divalent iron ion such as iron sulfate and a chelating agent such as disodium ethylenediaminetetraacetate may be used. The amount of the chelating agent used is 0.0001 to 1 part by weight, preferably 0.001 to 0.5 part by weight, based on 100 parts by weight of the total amount of monomers.

  Chain transfer agents can be added to control the molecular weight of the polymer. Known chain transfer agents such as n-dodecyl mercaptan, tert-dodecyl mercaptan, n-butyl mercaptan, γ-mercaptopropyltrimethoxysilane, γ-mercaptopropyltriethoxysilane, γ-mercaptopropylmethyldimethoxysilane, Examples include mercaptan compounds such as γ-mercaptopropylmethyldiethoxysilane, organic halides such as chloroform and carbon tetrachloride, sulfide benzene, isopropylbenzene, and ferric chloride.

  In order to maintain the stability of the emulsion, it is preferable to maintain the pH at 6 to 10 with a base and / or a buffer after completion of the polymerization. The adjustment and maintenance are not particularly limited as long as the base and / or buffering agent are generally used. Examples of the base include alkali metal hydroxides such as sodium hydroxide and potassium hydroxide; ammonia and organic amines. Examples of buffering agents include carbonates such as sodium hydrogen carbonate and disodium hydrogen phosphate, phosphates, and carboxylates. Among these pH adjusters and buffering agents, those containing an alkali metal are preferred, and the use of sodium bicarbonate is more preferred.

  The resin solid content concentration of the acrylic resin emulsion and the acrylic silicone resin emulsion is preferably 20 to 70% by weight, and more preferably 30 to 60% by weight. When the resin solid content concentration exceeds 70% by weight, the viscosity of the system is remarkably increased, so that it becomes difficult to remove heat generated by the polymerization reaction, or it takes a long time to take out from the polymerization vessel. There is a tendency to become necessary. Further, when the resin solid content concentration is less than 20% by weight, there is no problem in the aspect of the polymerization operation, but the amount of resin generated by one polymerization operation is small, which is disadvantageous in terms of economy. This is disadvantageous in terms of coating workability and coating film performance degradation, such as a reduced coating film thickness.

  The acrylic resin emulsion and the acrylic silicon resin emulsion preferably have an average particle size of about 0.02 to 1.0 μm. The average particle diameter can be adjusted by the amount of surfactant charged at the initial stage of polymerization.

These acrylic resin emulsions and acrylic silicon resin emulsions are commercially available from various companies, for example, bon coat and water sol, which are commercial products manufactured by DIC Corporation; Acryset, which is a commercial product manufactured by Nippon Shokubai Co., Ltd. Polyzole, Polydurex, a commercial product manufactured by Showa Polymer Co., Ltd .; Yodzole, Kanebinol, a commercial product manufactured by Henkel Technologies Japan Co., Ltd., and a commercial product manufactured by Asahi Kasei Chemicals Co., Ltd. Rikabond, a commercial product manufactured by Chuo Rika Kogyo Co., Ltd .; Primal, a commercial product manufactured by Rohm and Haas Japan Co., Ltd .; Acronal, a commercial product manufactured by BASF Japan Co., Ltd .; Nichigo Mobile ( Movinyl which is a commercial product of Kaneka; Kane which is a commercial product of Kaneka Co., Ltd. Zemurakku, Kanebirakku, and the like.
Urethane resin emulsions are those in which urethane resin is dispersed in water, and there are those in which a hydrophilic group is added to the urethane resin to make it self-dispersible, and in which a hydrophobic urethane resin is forcibly emulsified with an emulsifier. Any of them can be used.

  These are, for example, commercial products manufactured by Daiichi Kogyo Seiyaku Co., Ltd., Superflex 90, Superflex 107M, Superflex 110, Superflex 126, Superflex 130, Superflex 150, Superflex 150HS, Superflex 160. , Superflex 300, Superflex 361, Superflex 370, Superflex 410, Superflex 420, Superflex 460, Superflex 460S, Superflex 500, Superflex 600, Superflex E-2000, Superflex E-2500, Super Flex E-4000, Superflex E-4500, Superflex E-4700, Sue Over Flex R-5000, Elastron BN-08, ELASTRON BN-11, ELASTRON BN-50D; DSM. N. NeoRez R-960, NeoRez R-972, NeoRez R-9637, NeoRez R-9679, NeoRez AX-311, NeoRez R-966, NeoRez R-967, NeoRez R-9603, NeoRez R -600, NeoRez R-9320, NeoRez R-9617, NeoRez R-9621, NeoPac R-9000, NeoPac R-9699; commercial products manufactured by Mitsui Chemicals, Takelac W-615, Takelac W-6010, Bamboo rack W-6020, Bamboo rack W-6061, Bamboo rack W-511, Bamboo rack W-405, Bamboo rack W-7004, Bamboo rack W-605, Bamboo rack W-512A6, Bamboo rack W-635, Bamboo rack W-63 C, Takerak WS-7000, Takerak WS-5000, Takerak WS-5070X, Takerak WS-4000, Takerak XW-75-X35; Adekabon titer HUX-290H, which is a commercial product manufactured by ADEKA Corporation (Adekabon) Titer HUX-290K, Adekabon titer HUK-290N, Adekabon titer HUX-395D, Adekabon titer HUX-394, Adekabon titer HUX-232, Adekabon titer HUX-240, Adekabon titer HUX-320, Adekabon titer HUX-350, Adekabon titer HUX-380, Adekabon titer HUX-381, Adekabon titer HUX-388, Adekabon titer HUX-380A, Adekabon titer HUX-386, Ade Examples thereof include Caboon titer HUX-401, Adekabon titer HUX-750, Adekabon titer HUX-670, Adekabon titer HUX-680, Adekabon titer HUX-575, Adekabon titer HUX-580, and the like.

  The urethane resin emulsion can be used alone or in a mixed system with other resin emulsions. In particular, a mixed system with an acrylic resin emulsion is useful in terms of ease of coating design and cost.

As the fluororesin emulsion, a dispersion of a fluoroolefin polymer and / or a copolymer of a monomer copolymerizable with the fluoroolefin in water can be used.
Examples of the fluoroolefin include vinylidene fluoride, trifluoroethylene, chlorotrifluoroethylene, tetrafluoroethylene, pentafluoropropylene, hexafluoropropylene and the like.

  Monomers copolymerizable with fluoroolefin include olefins such as ethylene and propylene; vinyl ethers such as ethyl vinyl ether, propyl vinyl ether, butyl vinyl ether and cyclohexyl vinyl ether; butyl vinyl ester, octyl vinyl ester, vinyl acetate, versatic acid Vinyl esters such as vinyl (Veova 10, Veova 9 and Veova 11 manufactured by Hexion Specialty Chemicals Japan); aromatic vinyl compounds such as styrene and vinyl toluene; allyl ethers such as ethyl allyl ether and butyl allyl esters And (meth) acrylic acid esters.

  These are commercially available from various companies. For example, Lumiflon, which is a commercial product manufactured by Asahi Glass Co., Ltd .; Zeffle, which is a commercial product manufactured by Daikin Industries, Ltd .; Cefral coat, which is a commercial product manufactured by Central Glass Co., Ltd .; Fluoronate, which is a commercial product manufactured by DIC Corporation; Zaflon, which is a commercial product manufactured by Toa Gosei Co., Ltd., and Kyner manufactured by Arkema, France.

[(B) Organosilane and / or hydrolysis condensate thereof]
(B) The organosilane and / or its hydrolysis condensate is a compound represented by the general formula (1) and / or its hydrolysis condensate, and contains (A) a water-soluble and / or water-dispersible resin. The weather resistance can be improved by adding to the paint.
Si (R ² ) _n (OR ¹ ) _4-n (1)
(Wherein R ¹ is the same or different and the alkyl group has 1 to 4 carbon atoms, R ² is the same or different, a substituted or unsubstituted organic group having 2 to 8 carbon atoms, n = 1 or 2)
Further, since it does not have a methyl group directly bonded to a silicon atom, the obtained coating film does not exhibit water repellency, does not deteriorate the stain resistance, and can be improved.

R ¹ in the organosilane in the general formula is an alkyl group having 1 to 4 carbon atoms, and it is generally known that the reactivity improves as the carbon number decreases. When added to a water-based paint, a methyl group having a small number of carbon atoms is highly reactive, and the time until the paint gels, that is, the pot life is shortened. On the other hand, when a butyl group having a large number of carbon atoms is used, the stain resistance imparting rate decreases and the pot life becomes longer. Considering the balance between the contamination resistance and the pot life, when the alkyl part has 1 carbon number and 2, 3 or 4 carbon atoms, 2 carbon atoms and 3 or 4 carbon atoms are mixed. It is preferable. On average, the carbon number is preferably 1.5 to 2.8, particularly preferably 1.8 to 2.5, and more preferably 2 to 2.2. A silicate having the same number of methyl groups and ethyl groups can be said to be the alkyl moiety 1.5.

R ² is a substituted or unsubstituted organic group having 2 to 8 carbon atoms, such as an alkyl group having 2 to 8 carbon atoms such as an ethyl group, an n-propyl group, an i-propyl group, a vinyl group, Alkenyl groups such as allyl groups and methallyl groups; halogenated alkyl groups such as γ-chloropropyl groups and 3,3,3-trifluoropropyl groups; γ-glycidoxypropyl groups, 3,4-epoxycyclohexylethyl groups and the like An epoxyalkyl group; a (meth) acryloxyalkyl group such as γ-methacryloxypropyl group; a mercaptoalkyl group such as γ-mercaptopropyl group; an aryl group such as phenyl group; an amino group such as γ-aminopropyl group And an organic group having a substituent having 2 to 8 carbon atoms such as an alkyl group.

  Specific examples of these organosilanes include ethyltrimethoxysilane, ethyltriethoxysilane, n-propyltrimethoxysilane, n-propyltriethoxysilane, i-propyltrimethoxysilane, i-propyltriethoxysilane, γ- Chloropropyltrimethoxysilane, γ-chloropropyltriethoxysilane, vinyltrimethoxysilane, vinyltriethoxysilane, 3,3,3-trifluoropropyltrimethoxysilane, 3,3,3-trifluoropropyltriethoxysilane, γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropyltriethoxysilane, γ-methacryloxypropyltrimethoxysilane, γ-methacryloxypropyltriethoxysilane, γ-mercaptopropyltrimethoxy Lan, γ-mercaptopropyltriethoxysilane, phenyltrimethoxysilane, phenyltriethoxysilane, γ-aminopropyltrimethoxysilane, 3,4-epoxycyclohexylethyltrimethoxysilane, 3,4-epoxycyclohexylethyltriethoxysilane, Examples include diethyldimethoxysilane, diethyldiethoxysilane, diphenyldimethoxysilane, diphenyldiethoxysilane, and / or a hydrolysis condensate thereof.

Of these, hydrolysis condensates are preferable, and the degree of condensation is preferably about 1 to 20. A more preferable range of the condensation degree is 3-15.
Specific examples of the hydrolysis condensate include a hydrolysis condensate of vinyl silane, Dynasylan 6490 manufactured by Evonik Degussa Japan Co., Ltd., Dynasylan 6498, a product of Evonik Degussa Japan Co., Ltd. which is a hydrolysis condensate of vinylsilane and alkylsilane. Dynasylan 6598, Ebonic Degussa Japan Co., Ltd., Dynasylan 1146, Hydrolyzed Condensate of Aminosilane and Alkylsilane, Edynic Degussa Japan Co., Ltd., Dynasylan 9896, Hydrolyzed Condensate of Alkylsilane, Hydroxy Condensate of Phenylsilane Shin-Etsu Chemical Co., Ltd. KR-217, epoxy silane hydrolysis condensate Shin-Etsu Chemical Co., Ltd. X-41-1053, mercapto silane hydrolysis condensate Shin-Etsu Chemical Co., Ltd.) X-41-1805, and the like.

Among these, Dynasylan 6490, Dynasylan 6598, X-41-1053, and X-41-1805 in which R ¹ is an ethyl group or a mixture of a methyl group and an ethyl group are preferable.

Further, Dynasylan 6490 and Dynasylan 6598, which are condensates containing vinylsilane, are more preferable.
The said compound may be single 1 type, and may use 2 or more types together.

  The addition amount of these (B) organosilane and / or its condensate is (D) organosilicate and / or its later described with respect to 100 parts by weight of the solid content of (A) water-soluble and / or water-dispersible resin. It is preferable to add 2 to 40 parts by weight in total with the modified product. If it is less than 2 parts by weight, the weather resistance and stain resistance are not sufficient, and if it exceeds 40 parts by weight, the gloss of the coating tends to decrease. A more preferable addition amount is 5 to 20 parts by weight.

  The addition amount of (D) organosilane and / or its condensate alone is not (D) the total of organosilicate and / or its modified product. (A) Water-soluble and / or water-dispersible resin 1 to 40 parts by weight is preferable, 2 to 30 parts by weight is more preferable, and 5 to 20 parts by weight is particularly preferable with respect to 100 parts by weight of the solid content.

[(C) Curing catalyst for promoting hydrolysis / decomposition condensation reaction of alkoxysilyl group]
When the aqueous resin composition of the present invention is applied, the crosslinking reaction is promoted by adding a curing catalyst that accelerates the hydrolytic condensation reaction of alkoxysilyl groups. As the curing catalyst, an organometallic compound, an acidic catalyst, or a basic catalyst is used. In addition, latent catalysts such as photoacid generators and photobase generators can also be used.

  In particular, an organic tin compound, an acidic phosphate ester, and a reaction product of an acidic phosphate ester and an amine are preferable in terms of activity.

Examples of organic tin compounds include dibutyltin dilaurate, dibutyltin dimaleate, dibutyltin dioleylmalate, dioctyltin dilaurate, dibutyltin diacetate, dibutyltin dimethoxide, dibutyltin thioglycolate, dibutyltin bisisononyl 3-mercaptopropionate, Examples include dibutyltin bisisooctyl thioglycolate, dibutyltin bis 2-ethylhexyl thioglycolate, dimethyltin bisdodecyl mercaptide, dimethyltin bis (octylthioglycolate) salt, and tin octylate.
Among them, dibutyltin thioglycolate, dibutyltin bisisononyl 3-mercaptopropionate, dibutyltin bisisooctylthioglycolate, dibutyltin bis2-ethylhexylthioglycolate, dimethyltin bisdodecyl from the viewpoint of stability in water Mercaptides such as mercaptides, dibutyltin bisdodecyl mercaptides, dioctyltin bisdodecyl mercaptides, and dimethyltin bis (octylthioglycolate) salts are preferred.

  The addition method is not particularly limited, but a method of adding after mixing with a surface active substance in advance is preferable from the viewpoint of miscibility in the emulsion and expression of gloss of the coating film.

  Examples of the acidic phosphate compound include propyl acid phosphate, dibutyl phosphate, 2-ethylhexyl acid phosphate, di-2-ethylhexyl phosphate, monoisodecyl acid phosphate, diisodecyl phosphate, lauryl acid phosphate, stearyl acid phosphate and the like. Examples of amine compounds to be reacted with these acidic phosphate compounds include N-ethylmorpholine, N-methyldiethanolamine, N-ethyldiethanolamine, Nn-butyldiethanolamine, Nt-butyldiethanolamine, triethylamine, n-butylamine, Examples include hexylamine, triethanolamine, diazabicycloundecene, and ammonia.

  The addition method is not particularly limited, but those having self-emulsifying properties can be added as they are. Moreover, it is preferable to add the thing which shows emulsification by carrying out (partial) neutralization with an amine compound after previously emulsifying in water. Further, it can be added by being carried on an emulsion of an amino group-containing resin.

  The photoacid generator is a compound that generates an acid upon exposure to light. For example, a strong acid such as toluenesulfonic acid or a sulfonium salt such as boron tetrafluoride, an onium salt such as an ammonium salt, a phosphonium salt, an iodonium salt, or a selenium salt; Iron-allene complexes; silanol-metal chelate complexes; sulfonic acid derivatives such as disulfones, disulfonyldiazomethanes, disulfonylmethanes, sulfonylbenzoylmethanes, imidosulfonates, benzoinsulfonates; organic halogen compounds, etc. Examples thereof include compounds that generate an acid upon irradiation with radiation, as disclosed in JP-A-5-34412.

  Although it does not specifically limit as a photobase generator, For example, a cobalt amine complex, O-acyl oxime, a carbamic acid derivative, a formamide derivative, a quaternary ammonium salt, a tosyl amine, a carbamate, an amine imide compound etc. can be mentioned. Specific examples include 2-nitrobenzyl carbamate, 2,5-dinitrobenzyl cyclohexyl carbamate, N-cyclohexyl-4-methylphenylsulfonamide, 1,1-dimethyl-2-phenylethyl-N-isopropylcarbamate, and the like. . A photobase generator may be used independently and 2 or more types may be used together.

  The addition amount of the curing catalyst is preferably 0.01 to 10 parts by weight, particularly preferably 0.05 to 5 parts by weight, based on 100 parts by weight of the solid content of the water-soluble and / or water-dispersible resin (A). . If it is less than 0.01 parts by weight, the curing activity is low, and if it exceeds 10 parts by weight, the pot life is shortened, and the water resistance and weather resistance of the coating film are lowered.

[(D) Organosilicate and / or modified product thereof]
Organosilicate is a compound containing a hydrolyzable silicon group, and is a compound represented by the general formula (4). (B) When used in combination with organosilane and / or its hydrolysis condensate, stain resistance Can be further improved.

Si- (OR) ₄ (4)
(Wherein R is the same or different and has 1 to 4 carbon atoms)

  Specific examples of the compound include tetramethoxysilane, tetraethoxysilane, tetra-n-propoxysilane, tetra-i-propoxysilane, tetra-n-butoxysilane, tetra-i-butoxysilane, tetra-t-butoxysilane, and These partial hydrolysis and condensates can be exemplified. Of these, ethyl silicate 40 and ethyl silicate 48 are preferred. The said compound may be single 1 type, and may use 2 or more types together. Organosilicates containing different alkoxysilyl groups in the same molecule can also be used. For example, methyl ethyl silicate, methyl propyl silicate, methyl butyl silicate, ethyl propyl silicate, propyl butyl silicate and the like. The ratio of these substituents can be arbitrarily changed between 0 to 100%. Moreover, although it described that the partial hydrolysis and condensate of these silicates can also be used, about 1-20 are preferable for a condensation degree. A more preferable range of the condensation degree is 3-15.

  In the organosilicate compound, compounds having 1 to 4 carbon atoms in the alkoxy moiety of the functional group of the alkoxysilyl group are exemplified, but it is generally known that the reactivity decreases as the carbon number decreases. When added to a water-based paint, an organosilicate having a small number of carbon atoms, such as methyl silicate, is highly reactive, and the time until gelation of the paint, that is, the pot life is shortened. On the other hand, when butyl silicate having a large number of carbon atoms is used, the stain resistance imparting rate is lowered and the pot life is lengthened. Considering the balance between the contamination resistance and the pot life, when the alkyl part of the alkoxysilyl group has 1 carbon and 2, 3 or 4 carbons, the carbon number is 2 and the carbon number is 3 or 4 is preferably mixed, and the average carbon number is preferably 1.5 to 2.8. That is, an equimolar mixture of methyl silicate and ethyl silicate or a silicate having the same number of methyl groups and ethyl groups in the same molecule can be said to be the alkyl part 1.5.

  (D) The organosilicate and the (B) organosilane and / or the condensate thereof have low miscibility with water, and therefore may reduce the gloss of the coating film. In order to prevent a decrease in gloss, a method of emulsifying in water with a surface active substance in advance or adding it as a mixture with a surface active substance is preferable. A surface active substance is a substance having a hydrophilic group and a hydrophobic group in the molecule, and (B) an organosilane and / or its condensate and (D) an organosilicate can be emulsified and dispersed in water. is there. Specific examples include anionic surfactants, nonionic surfactants, cationic surfactants, and amphoteric surfactants.

  Examples of the anionic surfactants include higher alcohol sulfates, alkyl (benzene) sulfonates, alkyl sulfate salts, polyoxyethylene alkylphenyl sulfonates, alkyl diphenyl ether sulfonates, and polyoxyethylene alkylphenol sulfate salts. , Selected from the group consisting of styrene sulfonate or vinyl sulfate, alkyl sulfosuccinate, alkyl naphthalene sulfonate, alkyl phosphate, polyoxyethylene alkyl phosphate, polyacrylic acid (salt) and sulfonate These are various water-soluble oligomers, and various compounds such as water-soluble acrylic resins or derivatives thereof. These may be used alone or in combination of two or more. .

  Further, only typical examples of the above-mentioned nonionic surfactants will be exemplified. Polyoxyethylene alkyl ether, polyoxyethylene alkyl phenyl ether, polyoxyethylene higher fatty acid ester, sorbitan fatty acid ester, polyoxyethylene With various water-soluble polymer nonionic activators such as ethylene sorbitan fatty acid ester, polyoxyethylene-polyoxypropylene block copolymer, acetylene glycol surfactant, polyvinyl alcohol or hydroxyethyl cellulose. Yes, these may be used alone or in combination of two or more.

  Furthermore, only typical examples of the above-mentioned cationic surfactants include quaternary ammonium salts such as alkylamine salts and alkyltrialkylammonium chlorides, alkylbetaines, and amine oxides. These may be used alone or in combination of two or more.

  Each of the anionic surfactants, nonionic surfactants or cationic surfactants as listed above may be used singly or in combination of two or more, and among these, it can be particularly preferably used. As the surfactant, it is more preferable to use a nonionic surfactant having no ionic group.

  The amount of these surfactants used is 0.05 to 50 parts by weight as an active ingredient, preferably 100 parts by weight in total of (B) organosilane and / or its condensate and (D) organosilicate, 0.1 to 30 parts by weight. If it is less than 0.05 part by weight, a stable emulsion cannot be obtained, and the storage stability is also lowered. If it exceeds 50 parts by weight, problems such as the appearance of the resulting coating film and a decrease in water resistance occur.

  Furthermore, only typical examples of the above-mentioned cationic surfactants include quaternary ammonium salts such as alkylamine salts and alkyltrialkylammonium chlorides, alkylbetaines, and amine oxides. These may be used alone or in combination of two or more.

  Each of the anionic surfactants, nonionic surfactants or cationic surfactants as listed above may be used singly or in combination of two or more, and among these, it can be particularly preferably used. As the surfactant, it is more preferable to use a nonionic surfactant having no ionic group.

  As another method for improving miscibility, hydrophilic groups such as polyoxyalkylene chains and amino groups can be introduced and modified so that the organosilicate becomes water-soluble or self-water dispersible.

  The addition amount of these (D) organosilicate and / or modified product thereof is (B) organosilane and / or condensate thereof with respect to 100 parts by weight of the solid content of (A) water-soluble and / or water-dispersible resin. It is preferable to add 2 to 40 parts by weight in total. If it is less than 2 parts by weight, the weather resistance and stain resistance are not sufficient, and if it exceeds 40 parts by weight, the gloss of the coating tends to decrease. A more preferable addition amount is 5 to 20 parts by weight.

  The addition amount of (B) the organosilicate and / or its modified product alone is not the sum of (B) the organosilane and / or its condensate. (A) Water-soluble and / or water-dispersible resin 0 to 30 parts by weight is preferable, 1 to 20 parts by weight is more preferable, and 5 to 15 parts by weight is particularly preferable with respect to 100 parts by weight of the solid content.

  The mixing ratio of (B) the organosilane and / or its condensate and (D) the organosilicate and / or its modified product is preferably 10/0 to 1/9, and 9/1 to 3 / 7 is more preferable, and 7/3 to 4/6 is particularly preferable.

[(E) Hindered amine light stabilizer (HALS) having a logarithm of reciprocal of acid dissociation constant (pKa) of 7 or less]
A hindered amine light stabilizer (HALS) is a compound that improves the weather resistance of a coating film by capturing and detoxifying radicals generated when the coating film deteriorates, and is generally used.

  However, generally used HALS has a high logarithmic value (pKa) of the reciprocal of the acid dissociation constant, that is, many of them exhibit basicity, and these highly basic HALS are converted to organosilicates or modified products thereof. When added to a water-based paint imparted with anti-staining properties, the anti-staining performance is often reduced. However, even when HALS having a pKa of 7 or less is added to an aqueous paint imparted with stain resistance using an organosilicate or a modified product thereof, the stain resistance is not lowered. The preferred pKa is 6.5 or less and 1.5 or more, and the particularly preferred pKa is 6 or less and 2.0 or more.

  pKa measurements are obtained by non-aqueous titration. An organic reference material having a known pKa value in water is added dropwise to non-aqueous media (1: 1 acetonitrile: chloroform and 0.1N perchloric acid / dioxane titration system), and non-aqueous semi-neutralization to pKa Create a plot of the position (HNP) calibration curve. The “unknown” HALS is then titrated to determine the HNP and the corresponding pKa inferred from this calibration plot.

  Specific commercial products with a pKa of 7 or less include, for example, TINUVIN 123, TINUVIN 152, TINUVIN NOR 371 FF, TINUVIN XT855 FF, TINUVIN XT850 FF, TINUVIN 5100, TINUVIN 622, manufactured by BASF Japan K.K. ADEKA ADK STAB LA-81, Clariant Japan Co., Ltd. Hostavin 3058 Liq. , Hostavin 3068 Liq. Etc.

  In addition, many commercially available HALS are poorly miscible with water, and when added to water-based paints, many of them deteriorate the appearance such as gloss.

  As a solution to this problem, a product dispersed in water in advance is commercially available. For example, TINUVIN 123-DW manufactured by BASF Japan Co., Ltd. in which TINUVIN 123 is dispersed in water, SDX-2987, which is a prototype of ADEKA Co., Ltd. in which Adeka Stub LA-81 is dispersed in water, and the like can be mentioned.

  As another solution, auxiliary agent (II) previously mixed with a water-soluble and / or water-dispersible curing agent having a reactive functional group and a hydrophilic group in the molecule (F) described later is used, and (A) water-soluble The base material (I) containing a water-soluble and / or water-dispersible resin is mixed before use and used as a two-component or multi-component resin composition for water-based paints.

  By adding to the substrate (I) together with a water-soluble and / or water-dispersible curing agent having a reactive functional group and a hydrophilic group in the molecule (F) which has surface active ability and high compatibility with HALS , The miscibility is greatly improved.

  Further, when this addition method is used, it is possible to use high molecular weight type HALS and solid type HALS which have been difficult to apply to water-based paints due to miscibility.

Furthermore, by using HALS (e1) having a molecular weight of less than 600 and HALS (e2) having a molecular weight of 600 or more in combination, the appearance such as gloss can be further improved.
These (E) hindered amine light stabilizers (HALS) whose logarithmic value (pKa) of the reciprocal of the acid dissociation constant is 7 or less are (A) 100 parts by weight of the solid content of the water-soluble and / or water-dispersible resin. The amount is preferably 0.1 to 10 parts by weight, more preferably 0.3 to 7 parts by weight, and particularly preferably 1 to 4 parts. If it is less than 0.1 part by weight, a sufficient weather resistance improving effect cannot be obtained, and if it exceeds 10 parts by weight, the stain resistance and the coating film hardness are lowered.

[(F) Water-soluble and / or water-dispersible curing agent having a reactive functional group and a hydrophilic group in the molecule]
The water-soluble and / or water-dispersible curing agent having a reactive functional group and a hydrophilic group in the molecule is a substance having a reactive functional group in addition to a hydrophilic group and a hydrophobic group.
The reactive functional group reacts with the resin component and / or other compounding agent mixed in the water-based paint, and further with the reactive functional group itself, without reducing the water resistance of the obtained coating film. (Rather improved), (B) organosilane and / or its hydrolysis condensate, (D) organosilicate and (E) HALS can be emulsified and dispersed in water. The reactive functional group may be the same as the hydrophilic group or the hydrophobic group. Specific reactive functional groups include (block) isocyanate groups, epoxy groups, carbodiimide groups, alkoxysilyl groups, oxazoline groups, hydrazide groups, allyl groups, propenyl groups, (meth) acryloyl groups, vinyl groups, and the like.

  Examples of the (block) isocyanate group-containing compound include 2,4-tolylene diisocyanate (2,4-TDI), 2,6-tolylene diisocyanate (2,6-TDI), 4,4′-diphenylmethane diisocyanate ( MDI), xylylene diisocyanate (XDI), isophorone diisocyanate (IPDI), methylcyclohexyl diisocyanate (H6TDI), 4,4′-dicyclohexylmethane diisocyanate (H12MDI), 1,3-bis (isocyanatomethyl) cyclohexane (H6XDI), Tetramethylxylylene diisocyanate (TMXDI), 2,2,4-trimethylhexamethylene diisocyanate (TMHDI), hexamethylene diisocyanate (HDI), norbornene diisocyanate ( NBDI), 2,4,6-triisopropylphenyl diisocyanate (TIDI), 1,12-diisocyanatododecane (DDI), 2,4, -bis- (8-isocyanate octyl) -1,3-dioctylcyclobutane (OCDI) N-pentane-1,4-diisocyanate and their isocyanurate-modified products, adduct-modified products, burette-modified products, allophanate-modified products, those having one or more isocyanate groups in these polymers, polyalkylene oxide groups, It is modified with a carboxyl group to make it water-soluble and / or water-dispersible. Further, these isocyanate groups may be masked with a blocking agent (phenol, ε-caprolactam, etc.). Among these, those using a non-yellowing or hardly yellowing isocyanate are preferable from the viewpoint of weather resistance.

These are generally commercially available as cross-linking agents. For example, bihydur 3100, bihydur 2336, bihydur LS2150 / 1, manufactured by Sumika Bayer Urethane Co., Ltd., bihydur BL116, bihydur BL5140, bihydur BL5235, bihydur TPLS2186, bihydrol TPLS2153, Mitsui Chemicals Takenate WD-220, Takenate WD-240, Takenate WD-720, Takenate WD-725, Takenate WD-726, Takenate WD-730, Takenate WB-700, Takenate WB-720, Takenate WB-730, Takenate WB-920, Nippon Polyurethane Industry Co., Ltd. Aquanate 100, Aquanate 110, Aquanate 200, Aqua Over DOO 210, Aquanate 120, Asahi Kasei Chemicals Corp. DURANATE WB40-100, Duranate WB40-80D, Duranate WT20-100, such as Duranate WT30-100 the like.
Further, it may be a copolymer with a vinyl monomer having a (block) isocyanate group, a hydrophilic group-containing vinyl monomer and other vinyl monomers.

  Examples of the vinyl monomer having a (block) isocyanate group include 2-methacryloyloxyethyl isocyanate, methacrylic acid-2- (O- [1′-methylpropylideneamino] carboxyamino) ethyl, and m-iso. And propenyl-α, α-dimethylbenzyl isocyanate.

  Examples of the hydrophilic group-containing vinyl monomer include α, β-ethylenically unsaturated carboxylic acid, styrene sulfonic acid, vinyl sulfonic acid, sodium styrene sulfonate, sodium 2-sulfoethyl (meth) acrylate, (meth) acrylamide, N-methylol (meth) acrylamide, dialkylaminoalkyl (meth) acrylate, dialkylaminoalkyl (meth) acrylate hydrochloride, 2-aminoethyl (meth) acrylate hydrochloride, vinyl monomer having a polyoxyalkylene chain, etc. can give.

  Examples of the α, β-ethylenically unsaturated carboxylic acid include (meth) acrylic acid, itaconic acid, maleic acid, crotonic acid, phthalic acid, citraconic acid and the like.

  Examples of the dialkylaminoalkyl (meth) acrylate and dialkylaminoalkyl (meth) acrylate hydrochloride include dimethylaminoethyl (meth) acrylate, diethylamineethyl (meth) acrylate, dimethylaminopropyl (meth) acrylate, and hydrochloride thereof.

  Although there is no particular limitation on the vinyl monomer having a polyoxyalkylene chain, an acrylic acid ester or a methacrylic acid ester having a polyoxyalkylene chain is preferred, and specific examples include Bremer PE-90 manufactured by NOF Corporation, PE-200, PE-350, AE-90, AE-200, AE-350, PP-500, PP-800, PP-1000, AP-400, AP-550, AP-800, 700PEP-350B, 10PEP- 550B, 55PET-400, 30PET-800, 55PET-800, 30PPT-800, 50PPT-800, 70PPT-800, PME-100, PME-200, PME-400, PME-1000, PME-4000, AME-400, 50POEP-800B, 50AOEP-800B AEP, AET, APT, PLE, ALE, PSE, ASE, PKE, AKE, PNE, ANE, PNP, ANP, PNEP-600, Kyoeisha Chemical Co., Ltd. light ester 130MA, 041MA, MTG, light acrylate EC-A, MTG-A, 130A, DPM-A, P-200A, NP-4EA, NP-8EA, EHDG-A, MA-30, MA-50, MA-100, MA-150, RMA- manufactured by Nippon Emulsifier Co., Ltd. 1120, RMA-564, RMA-568, RMA-506, MPG130-MA, Antox MS-60, MPG-130MA, RMA-150M, RMA-300M, RMA-450M, RA-1020, RA-1120, RA-1820 , Shin-Nakamura Chemical Co., Ltd. NK-ESTER M-20G, M-40 , M-90G, M-230G, AMP-10G, AMP-20G, AMP-60G, AM-90G, LA, and Sanyo Kasei Co., Ltd. ELEMINOL RS-30, RS-300, and the like.

As an epoxy group containing compound, many things are marketed, for example, Nagase Chemtech Co., Ltd. Denacol EX-611, EX-612, EX-614, EX-614B, EX-622, EX-512, EX-521, EX-411, EX-421, EX-301, EX-313, EX-314, EX-321, EX-211, EX-810, EX-811, EX-851, EX-821, EX- 830, EX-832, EX-841, EX-861, EX-911, EX-941, EX-920, EX-921, EX-931, EX-145, EX-171, EX-701, Kyoeisha Chemical Co., Ltd. ) Epolite 40E, Epolite 100E, Epolite 200E, Epolite 400E, Epolite 70P, Epolite 200P, Epolite 00P, Epolite 1500NP, Epolite 80MF, Epolite 100MF, Sakamoto Pharmaceutical Co., Ltd. SR-NPG, SR-16H, SR-TMP, SR-TPG, SR-4PG, SR-2EG, SR-8EG, SR-8EGS, SR-GLG, SR-DGE, SR-4GL, SR-4GLS, NOF Corporation Epiol BE-200, G-100, E-100, E-400, E-1000, P-200, NPG-100 , TMP-100, epiol OH and the like.
Moreover, the copolymer with the vinyl monomer which has an epoxy group, a hydrophilic group containing vinyl monomer, and another vinyl monomer may be sufficient.

  Examples of the vinyl monomer having an epoxy group include glycidyl (meth) acrylate, glycidyl vinyl ether, 3,4, -epoxycyclohexyl (meth) acrylate manufactured by Daicel Chemical Industries, Ltd., M-GMA, Cycler M-100, Cycler A-200, Cycler M-101, Celoxide 2000 and the like.

  Examples of the carbodiimide group-containing compound include water-soluble or self-emulsifying carbodiimide compounds described in JP-A-8-59303.

  This includes 2,4-tolylene diisocyanate (2,4-TDI), 2,6-tolylene diisocyanate (2,6-TDI), 4,4'-diphenylmethane diisocyanate (MDI), xylylene diisocyanate (XDI) , Isophorone diisocyanate (IPDI), methylcyclohexyl diisocyanate (H6TDI), 4,4′-dicyclohexylmethane diisocyanate (H12MDI), 1,3-bis (isocyanatomethyl) cyclohexane (H6XDI), tetramethylxylylene diisocyanate (TMXDI), 2,2,4-trimethylhexamethylene diisocyanate (TMHDI), hexamethylene diisocyanate (HDI), norbornene diisocyanate (NBDI), 2,4,6-triisopropylphenyl Diisocyanate (TIDI), 1,12-diisocyanate dodecane (DDI), 2,4, -bis- (8-isocyanate octyl) -1,3-dioctylcyclobutane (OCDI), n-pentane-1,4-diisocyanate, etc. One type or two or more types of polyfunctional isocyanates are subjected to a carbon dioxide decondensation reaction to form a carbodiimide, and the terminal residual isocyanate group is sealed with a hydrophilic group.

  Examples of the hydrophilic group to be sealed include a residue of an alkyl sulfonate, a quaternary salt of a residue of a dialkylamino alcohol, a residue of a polyoxyalkylene whose end is blocked with an alkoxy group.

  These are commercially available as aqueous resin crosslinking agents. For example, Nisshinbo Carbodilite V-02, V-04, V-06, V-02-L2, E-01, E-02, E-03, E-04, E-05, and the like.

  Examples of water-free materials include V-02B, V-04B, V-04K, and Elastostab H01.

  Examples of the alkoxysilyl group-containing compound include A-1230, MAC-2101, MAC-2301, and the like manufactured by Momentive Performance Materials Japan.

  It can also be obtained by reacting an isocyanate-based silane coupling agent with the terminal hydroxy group of polyoxyalkylene.

  The polyoxyalkylene is not particularly limited as long as it has one or more hydroxy groups at the terminal.

  Examples of the isocyanate-based silane coupling agent include A-1310, Y-5187 manufactured by Momentive Performance Materials Japan, and KBE-9007 manufactured by Shin-Etsu Chemical Co., Ltd.

  It can also be obtained by reacting the compound having an epoxy group with an amino silane coupling agent.

  Examples of the amino silane coupling agent include γ-aminopropyltriethoxysilane, γ-aminopropyltrimethoxysilane, N- (β-aminoethyl) -γ-aminopropyltrimethoxysilane, N- (β-amino). Ethyl) -γ-aminopropyltriethoxysilane, N- (β-aminoethyl) -γ-aminopropylmethyldimethoxysilane, γ-phenylaminopropyltrimethoxysilane, Shin-Etsu Chemical Co., Ltd. KBE-9103, KBM- 575, KBM-6123, A1102, A-1122, A-1170, etc. manufactured by Momentive Performance Materials Japan (go).

  Furthermore, it may be a copolymer with an alkoxysilyl group-containing vinyl monomer, a hydrophilic group-containing vinyl monomer, and other vinyl monomers.

  Specific examples of vinyl monomers containing alkoxysilyl groups include vinyltrimethoxysilane, vinylmethyldimethoxysilane, vinyltriethoxysilane, vinylmethyldiethoxysilane, vinyltris (2-methoxyethoxy) silane, vinyltrimethyl. Isopropoxysilane, γ- (meth) acryloyloxypropyltrimethoxysilane, γ- (meth) acryloyloxypropylmethyldimethoxysilane, γ- (meth) acryloyloxypropyltriethoxysilane, γ- (meth) acryloyloxypropylmethyldi Ethoxysilane, γ- (meth) acryloyloxypropyltri-n-propoxysilane, γ- (meth) acryloyloxypropyltriisopropoxysilane, vinyltriacetoxysilane, β- (meth) acryl Yl oxy ethyltrimethoxysilane, and the like.

  The oxazoline group-containing compound is commercially available as an aqueous crosslinking agent. For example, Nippon Shokubai Co., Ltd. Epocross WS-500, K-2010E, K-2020E, K-2030E, K-1010E, K-1020E, K- 1030E.

  Examples of the hydrazide group-containing compound include carbohydrazide, adipic acid dihydrazide, sebacic acid dihydrazide, dodecanediohydrazide, aminopolyacrylamide, and the like.

  (F) a water-soluble and / or water-dispersible curing agent having a reactive functional group and a hydrophilic group in the molecule, (B) an organosilane and / or a hydrolysis condensate thereof, (C) an alkoxysilyl group A curing catalyst for promoting hydrolysis / condensation reaction, (D) an organosilicate and / or a modified product thereof, and (E) a hindered amine light stabilizer (HALS) having a logarithm of the reciprocal of acid dissociation constant (pKa) of 7 or less. Mixing in advance, leaving as auxiliary (II), and mixing with substrate (I) containing water-soluble and / or water-dispersed resin (A) just before coating, very good coating appearance and excellent weather resistance A coating film showing stain resistance is obtained.

  The amount of the water-soluble and / or water-dispersible curing agent having (F) a reactive functional group and a hydrophilic group is as follows: (B) an organosilane and / or its hydrolysis condensate and (D) an organosilicate and The amount is 5 to 300 parts, preferably 10 to 200 parts, more preferably 20 to 100 parts, based on 100 parts by weight in total with the modified product. If it is less than 5 parts by weight, (B) organosilane and / or its hydrolysis condensate, (D) organosilicate and / or its modified product, (E) HALS and (C) curing catalyst are uniformly dispersed in the paint. Therefore, the gloss value of the formed coating film decreases. Moreover, when 300 weight part or more is used, the hardness of the formed coating film falls.

  Further, when an acetylene glycol surfactant and / or a similar structure thereof is used in combination, the gloss can be improved and the surface tack can be reduced. Specific examples of the acetylene glycol surfactant and / or a similar structure thereof include Surfinol 104, 104E, 104H, 104A, 104BC, 104DPM, 104PA, 104PG-50, 104S, 420, manufactured by Nissin Chemical Industry Co., Ltd. 440, 465, 485, SE, SE-F, 504, 61, 2502, 82, DF110D, DF37, CT111, CT121, CT131, CT136, TG, GA, FS-85, Dynol 604, Envirogem AD-01, Olphin STG, SPC, E1004, E1010, AK-02, PD-001, PD-002W, PD-004, PD-301, WE-001, WE-002, WE-003, AF-103, AF-104, etc. It is done. Of these, Surfynol 104 series, Surfynol 2502, and Envigem AD-01, to which ethylene oxide is not added, are particularly preferable for reducing surface tack.

[(G) Titanium dioxide subjected to at least three types of surface treatment of silicon dioxide, aluminum oxide, and zirconium dioxide]
As a white pigment used for coloring, titanium dioxide is usually used. The titanium dioxide has photocatalytic reactivity and causes deterioration of the coating film. Titanium dioxide commercially available for coatings is subjected to various surface treatments in order to suppress the photocatalytic reaction and to impart dispersion stability. Examples of the surface treatment material include silicon dioxide, aluminum oxide, zirconium dioxide, phosphate ester, polyol and the like.

  Among these, when titanium dioxide having been subjected to at least three kinds of surface treatments of silicon dioxide, aluminum oxide, and zirconium dioxide is used for an aqueous paint imparted with stain resistance using an organosilicate and a modified product thereof, A coating film excellent in appearance such as stain resistance, weather resistance and gloss can be obtained.

These titanium dioxides subjected to at least three kinds of surface treatments of silicon dioxide, aluminum oxide, and zirconium dioxide are commercially available from various companies. For example, D-918, D-2667 manufactured by Sakai Chemical Industry Co., Ltd., Ishihara Sangyo Examples thereof include PFC-105 manufactured by KRONOS 2315 and KRONOS 2310 manufactured by Kronos, Germany.

  These (F) addition amounts of titanium dioxide subjected to at least three kinds of surface treatments of silicon dioxide, aluminum oxide, and zirconium dioxide may be added in an amount necessary for adjusting the target color.

  However, since addition of a large amount leads to a decrease in gloss, weather resistance, and toning properties, preferably (A) 200 parts by weight with respect to 100 parts by weight of the solid content of the water-soluble and / or water-dispersible resin. Hereinafter, it is more preferable that the amount be 150 parts by weight or less, and still more preferably 100 parts by weight or less.

  If necessary, the obtained resin composition for water-based paints contains pigments usually used in paints such as titanium dioxide, calcium carbonate, kaolin clay, talc, barium sulfate, white carbon, carbon, petal, ocher, cyanine. Blue and other film forming aids such as alcohols such as benzyl alcohol; glycols such as ethylene glycol monobutyl ether, propylene glycol monomethyl ether, propylene glycol monobutyl ether, dipropylene glycol monomethyl ether, dipropylene glycol monobutyl ether, ethylene glycol mono Glycol esters such as butyl ether acetate and 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate, colloidal silica, plasticizer, solvent, dispersion Additives commonly used in paints such as humectants, wetting agents, thickeners, antiseptics, fungicides, anti-algae agents, anti-freezing agents, light stabilizers, UV absorbers and antifoaming agents can be added. .

  The resin composition for water-based paints obtained by the present invention and the paint comprising the resin composition for water-based paints are used for buildings, detached houses, apartment houses, factory houses, hospitals, schools, gas stations, etc., bridges・ Structure such as civil engineering, plant, offshore structure, sluice, steel tower, large pipe, pool, sash, joinery, various boards, inorganic building materials, ship, PCM, metal furniture, container, guardrail, bicycle member, etc. Metal products such as fences, food cans, drums, cylinders, gas appliances, oil stoves, road vehicles such as passenger cars, trucks, buses, motorcycles, home electrics, heavy electrical machinery, electronic machines, office machines, communication machines, measuring machines, Electric machinery such as refrigerators, lighting fixtures, vending machines, computer-related equipment, industrial machinery, agricultural machinery, construction machinery, railway vehicles, aircraft machinery, plywood, furniture, musical instruments, etc. It can be used in any variety of painting.

  Hereinafter, the present invention will be described based on examples, but the present invention is not limited thereto.

[(A) Synthesis of water-soluble and / or water-dispersible resin (Synthesis Examples 1 to 3)]
In a reaction vessel equipped with a stirrer, a reflux condenser, a nitrogen gas inlet tube and a dropping funnel, 192 parts by weight of deionized water, 0.46 parts by weight of Newcol-707SN (manufactured by Nippon Emulsifier Co., Ltd .: active ingredient 30%), 1.0 part by weight of 5% aqueous sodium hydrogen carbonate solution was charged, and the temperature was raised to 50 ° C. while introducing nitrogen gas. After heating, 2.0 parts by weight of 7% t-butyl hydroperoxide aqueous solution, 1.4 parts by weight of 10% Bruggolite FF-6 aqueous solution, ferrous sulfate heptahydrate (0.10%) / ethylenediamine tetra 2.8 parts of disodium acetate (0.40%) mixed aqueous solution was added, and Adeka Soap SR-1025 (manufactured by ADEKA Corporation: effective) was added to the monomer mixture described in Table 1 (A-1 to 3) core part. Component emulsion 25%) 9.6 parts by weight, Adeka Soap ER-20 (manufactured by ADEKA Co., Ltd .: active ingredient 75%) 1.5 parts by weight and deionized water 50 parts by weight emulsified monomer emulsion for 160 minutes Added constant speed over time. Meanwhile, 1.6 parts by weight of 7% t-butyl hydroperoxide aqueous solution and 3.2 parts by weight of 2.5% Bruggolite FF-6 aqueous solution were added in two portions. Polymerization was performed after 1 hour after the addition of the monomer emulsion was completed.

  Further, 1.3 parts by weight of 7% t-butyl hydroperoxide aqueous solution and 3.6 parts by weight of 2.5% Bruggolite FF-6 aqueous solution were added, and then added to the monomer and chain transfer agent mixture described in Table 1 Shell part. Rear soap SR-1025 (manufactured by ADEKA Corporation: active ingredient 25%) 14.4 parts by weight, ADEKA rear soap ER-20 (manufactured by ADEKA Corporation: 75% active ingredient) 2.3 parts by weight and deionized water A monomer emulsion added with 71 parts by weight and emulsified was added at a constant rate over 240 minutes. Meanwhile, 2.3 parts by weight of 7% t-butyl hydroperoxide aqueous solution and 3.4 parts by weight of 2.5% Bruggolite FF-6 aqueous solution were added in three portions. After completion of the addition, polymerization was carried out 1.5 hours later. After adding 22 parts of 5% aqueous sodium hydrogen carbonate solution to the obtained emulsion, the solid content was adjusted to 50% with deionized water (A-1 to 3).

[Production Example of Substrate (I)]
Using the synthesized resin composition (A-1 to 3) and a commercially available aqueous resin composition, a paint was prepared with the formulation shown in Table 3 using the pigment paste of Table 2.

D-918: Sakai Chemical Industry Co., Ltd. (surface treatment: silicon dioxide, aluminum oxide, zirconium dioxide)
Ti-Pure R-706: manufactured by DuPont Co., Ltd. (surface treatment: silicon dioxide, aluminum oxide, polyol)

Superflex 410: Urethane resin emulsion Zeffle SE-310 manufactured by Daiichi Kogyo Seiyaku Co., Ltd .: Fluororesin emulsion manufactured by Daikin Industries

[Production example of auxiliary agent (II)]
The raw materials listed in Table 4 were put into a container equipped with a stirrer, a reflux condenser, and a nitrogen gas introduction pipe in order from the top. After completion of the addition, the temperature was raised to 40 ° C. and the mixture was stirred for 60 minutes to obtain a stain resistance imparting composition (QA-1 to 8, QB-1).

CS-12: manufactured by Chisso Corporation 2,2,4-trimethylpentanediol 1,3-monoisobutyrate pro-glide DMM: manufactured by Dow Chemical Japan Co., Ltd. dipropylene glycol dimethyl ether carbodilite V-04B: Nisshinbo Chemical Co., Ltd. Polycarbodiimide Dynasylan 6498: Hydrolysis condensate of vinylsilane manufactured by Evonik Degussa Japan Co., Ltd. Dynasylan 6598: Hydrolysis condensate of vinylsilane and alkylsilane manufactured by Evonik Degussa Japan Co., Ltd. X-41-1053: Shin-Etsu Chemical Co., Ltd. Hydrolysis condensate of epoxy silane DC3074 manufactured by Toray Dow Corning Co., Ltd. Hydrolyzed condensate silicate 45 of organosilane having a phenyl group and organosilane having a methyl group: Tetra Chemical Industries, Ltd. Tetra Part of ethoxysilane Hydrolyzed condensate (silica residual ratio 45%)
ENVIROGEM AD-01: Nissin Chemical Industry Co., Ltd. acetylene glycol surfactant-like product Unilube 70MO-10SB: NOF Corporation nonionic surfactant TINUVIN 123: BASF Japan K.K. Light stabilizer Hostavin 3058 Liq. : Hindered amine light stabilizer manufactured by Clariant Japan

(Examples 1-12, Comparative Examples 1-7)
The base material (I) and auxiliary agent (II) prepared according to the formulation in Tables 3 and 4 were added and stirred and mixed in the number of parts shown in Table 5, and the glass plate gloss test, weather resistance evaluation, and stain resistance evaluation were performed. It was. The results are shown in Table 5.

○ Glass Plate Gloss After adding the auxiliary agent (II) to the prepared substrate (I) as necessary and stirring and mixing, it was applied to a glass plate using a 6 mil applicator and dried at room temperature for 7 days. Using a gloss meter Multi-Gloss 268 manufactured by Konica Minolta, the gloss value at an incident angle of 60 ° of this specimen was measured.

○ Weather resistance evaluation SK # 1000 primer (manufactured by SK Kaken Co., Ltd., solvent-based two-component epoxy resin primer) is applied on a flexible plate, cured at room temperature for 1 day, and then water-based serratic F intermediate coating (SK Chemical) Co., Ltd., an intermediate coating for water-based fluorine paint) was applied once with a spray and then cured at room temperature for 1 day to be used as a base for evaluation. The auxiliary material (II) was added to the base material (I) prepared on the base as necessary, stirred and mixed, then applied once by spraying, and dried at room temperature for 7 days. This test plate was placed in a xenon arc lamp type accelerated weathering tester (Hybrid exposure system manufactured by Toyo Seiki Seisakusho: Atlas Weatherometer Ci4000 + HE system) added with a hydrogen peroxide spray function for 345 hours. Using a gloss meter Multi-Gloss 268 manufactured by Konica Minolta Co., Ltd., the gloss retention was calculated from the previously measured gloss value at an incident angle of 60 ° before the test and the measured value after the test.

○ Evaluation of contamination resistance SK # 1000 primer (manufactured by SK Kaken Co., Ltd., solvent-based two-component epoxy resin primer) is applied on a flexible plate, cured at room temperature for 1 day, and then water-based serratic F intermediate coating (SK) Kaken Co., Ltd., water-based fluorine paint intermediate coating) was applied once by spraying, and was cured at room temperature for 1 day to be used as a base for evaluation. The auxiliary material (II) was added to the base material (I) prepared on the base as necessary, stirred and mixed, then applied once by spraying, and dried at room temperature for 7 days. The test plate was exposed for 3 months at 45 degrees south in Settsu City, Osaka. Contamination is measured by a color difference meter (manufactured by Konica Minolta Co., Ltd .: CR-300) with the brightness represented by the L * a * b * color system at the beginning of exposure, and the absolute value of the brightness difference before and after exposure ( (ΔL value) was used as a measure of contamination. The exposed coating film was lightly washed with water and dried for 3 hours or more, and then the static contact angle of water was measured with a contact angle measuring device (Kyowa Interface Science Co., Ltd .: S-150).

  Examples 1 to 6 and Example 12 are significantly improved in weather resistance and contamination resistance as compared to Comparative Example 1. Those containing a hindered amine light stabilizer (HALS) having a logarithmic value (pKa) of the reciprocal of the acid dissociation constant of 7 or less are further improved in weather resistance. Further, even in comparison with Comparative Example 2 which is the prior art, no significant reduction in gloss and stain resistance is seen, and an improvement in weather resistance is seen.

  In Examples 8 to 11, (A) the type of water-soluble and / or water-dispersible resin was changed, but the weather resistance and contamination resistance were significantly higher than those of Comparative Examples 4 to 7 which correspond to each other. Has improved.

  In Comparative Example 3, although the weather resistance is improved as compared with Comparative Example 2, the organosilane hydrolysis condensate having a methyl group that exhibits water repellency is used. Yes.

Claims (10)

(A) Water-soluble and / or water-dispersible resin, (B) Organosilane represented by general formula (1) and / or its hydrolysis condensate Si (R ² ) _n (OR ¹ ) _4-n (1)
(Wherein R ¹ is the same or different and the alkyl group has 1 to 4 carbon atoms, R ² is the same or different substituted and unsubstituted organic group having 2 to 8 carbon atoms, n = 1 or 2), ( C) A resin composition for water-based paints containing a curing catalyst that promotes hydrolysis / condensation reaction of alkoxysilyl groups. The resin composition for water-based paint according to claim 1, further comprising (D) an organosilicate and / or a modified product thereof. The resin composition for water-based paints according to any one of claims 1 to 2, further comprising (E) a hindered amine light stabilizer (HALS) having a logarithmic value (pKa) of the reciprocal of the acid dissociation constant of 7 or less. . The resin composition for water-based paints according to any one of claims 1 to 3, wherein the water-soluble and / or water-dispersible resin (A) is a resin having a polyoxyalkylene chain. The curing catalyst for promoting the hydrolysis / condensation reaction of the alkoxysilyl group (C) is one or more selected from organic tin compounds, acidic phosphate esters, and reaction products of acidic phosphate esters and amines. The resin composition for water-based paints according to any one of claims 1 to 4, wherein the resin composition is for water-based paints. The resin composition for water-based paints according to any one of claims 1 to 5, wherein all or part of the (A) water-soluble and / or water-dispersible resin is an alkoxysilyl group-containing acrylic resin. The resin composition for water-based paints according to any one of claims 1 to 6, wherein the component (B) is vinylsilane and / or a hydrolysis condensate thereof. (A) a base material (I) containing a water-soluble and / or water-dispersible resin, (B) an organosilane represented by the general formula (1) and / or a hydrolysis condensate thereof,
Si (R ² ) _n (OR ¹ ) _4-n (1)
(Wherein R ¹ is the same or different and the alkyl group having 1 to 4 carbon atoms, R ² is the same or different, a substituted and unsubstituted organic group having 2 to 8 carbon atoms, n = 1 or 2), (C) a curing catalyst for promoting the hydrolysis-condensation reaction of an alkoxysilyl group, (D) an organosilicate and / or a modified product thereof, and (F) a water-soluble compound having a reactive functional group and a hydrophilic group in the molecule and / or The two-component or multicomponent aqueous coating resin according to any one of claims 1 to 7, wherein the auxiliary (II) containing a water-dispersible curing agent is a two-component or multicomponent type used by mixing before use. Composition. The coating composition formed by mix | blending the resin composition for water-based coatings in any one of Claims 1-8. Claims obtained by blending the base material (I) with (A) water-soluble and / or water-dispersible resin and (G) titanium dioxide subjected to at least three kinds of surface treatments of silicon dioxide, aluminum oxide and zirconium dioxide. Item 10. The coating composition according to Item 9.