JP2011246672A

JP2011246672A - Pressure-sensitive adhesive sheet to be stuck to the skin

Info

Publication number: JP2011246672A
Application number: JP2010123901A
Authority: JP
Inventors: Tomio Hatanaka; 富男畠中
Original assignee: Lintec Corp
Current assignee: Lintec Corp
Priority date: 2010-05-31
Filing date: 2010-05-31
Publication date: 2011-12-08

Abstract

PROBLEM TO BE SOLVED: To provide a pressure-sensitive adhesive sheet to be stuck to the skin, capable of suppressing remaining of moisture evaporated through the skin on an adhesive sheet/skin interface or in the adhesive sheet and alleviating irritation caused by a hydration reaction.SOLUTION: The pressure-sensitive adhesive sheet to be stuck to the skin is used for adhering on the skin and includes fine pores with a diameter of 10 μm or less on the inside thereof and has a base film with a water-vapor transmission ratio of 10000 g/m/24h or more and an adhesive layer arranged on one surface of the base film. A water-vapor transmission ratio of the entire pressure-sensitive adhesive sheet to be stuck to the skin is 1000 g/m/24h or more.

Description

本発明は、皮膚貼付用粘着シートに関するものである。 The present invention relates to an adhesive sheet for skin application.

従来より、絆創膏、パップ剤を固定するためのテーピング材、爪の保護シート、点滴針の固定テープ、シワ伸ばし用シート等の皮膚に貼付する粘着シートが知られている（例えば、特許文献１参照）。
皮膚に貼着する粘着シートには、皮膚に対する刺激が少ないことが要求される。 Conventionally, adhesive sheets to be applied to the skin such as adhesive bandages, taping materials for fixing cataplasms, nail protection sheets, drip needle fixing tapes, and wrinkle-stretching sheets are known (see, for example, Patent Document 1). ).
The pressure-sensitive adhesive sheet adhered to the skin is required to have less irritation to the skin.

ところで、皮膚に対する刺激の原因の一つとして、水和反応がある。この水和反応は、粘着シートの貼着時に、皮膚から蒸散される水分がシート／皮膚界面またはシート内に滞留し、角層の水和、細菌の増殖等が生じることを言い、この水和反応が皮膚刺激の原因の一つとなっている。 By the way, one of the causes of skin irritation is a hydration reaction. This hydration reaction means that when the adhesive sheet is applied, moisture evaporated from the skin stays in the sheet / skin interface or in the sheet, resulting in hydration of the stratum corneum, bacterial growth, etc. Reaction is one of the causes of skin irritation.

しかしながら、従来の粘着シートでは、水分の透過性が低いため、皮膚から蒸散される水分がシート／皮膚界面またはシート内に滞留するのを十分に防止することができず、水和反応による刺激を防止することができなかった。 However, in the conventional adhesive sheet, the moisture permeability is low, so it is not possible to sufficiently prevent the moisture evaporated from the skin from staying in the sheet / skin interface or in the sheet, and irritation caused by the hydration reaction. Could not be prevented.

特開２００７−２５４５１５号公報JP 2007-254515 A

本発明の目的は、皮膚から蒸散される水分が粘着シート／皮膚界面または粘着シート内に滞留するのを抑制し、水和反応による刺激を緩和することが可能な皮膚貼付用粘着シートを提供することにある。また、そのような皮膚貼付用粘着シートの特性を生かしたまま、印刷層を設けることを課題とする。 An object of the present invention is to provide a pressure-sensitive adhesive sheet for skin application, which can suppress the moisture evaporated from the skin from staying in the pressure-sensitive adhesive sheet / skin interface or the pressure-sensitive adhesive sheet, and can reduce irritation caused by a hydration reaction. There is. It is another object of the present invention to provide a printed layer while taking advantage of the characteristics of such an adhesive sheet for skin application.

このような目的は、下記（１）〜（６）の本発明により達成される。
（１）皮膚に貼着して用いられる皮膚貼付用粘着シートであって、
内部に直径１０μｍ以下の細孔を有し、かつ、透湿度が１００００ｇ／ｍ^２／２４ｈ以上である基材フィルムと、
当該基材フィルムの一方の面上に設けられた粘着剤層と、を有し、
皮膚貼付用粘着シート全体の透湿度が１０００ｇ／ｍ^２／２４ｈ以上であることを特徴とする皮膚貼付用粘着シート。 Such an object is achieved by the present inventions (1) to (6) below.
(1) A pressure-sensitive adhesive sheet for skin application that is used by being attached to the skin,
Inside it has the following pore diameters 10 [mu] m, and a substrate film is moisture permeability 10000g ^/ m 2 ^/ 24h or more,
An adhesive layer provided on one surface of the base film, and
For application to the skin adhesive sheet, wherein the moisture permeability of the entire skin sticking the adhesive sheet is 1000g / m 2 / ^24h or more.

（２）前記基材フィルムは、ポリウレタンフィルムである上記（１）に記載の皮膚貼付用粘着シート。 (2) The adhesive sheet for skin application according to (1), wherein the base film is a polyurethane film.

（３）２０％伸長時の引張力が、３Ｎ／２５ｍｍ以下である上記（１）または（２）に記載の皮膚貼付用粘着シート。 (3) The adhesive sheet for skin application according to the above (1) or (2), wherein the tensile force at 20% elongation is 3 N / 25 mm or less.

（４）２００％伸長後の伸長率が、２０％以下である上記（１）ないし（３）のいずれかに記載の皮膚貼付用粘着シート。 (4) The adhesive sheet for skin application according to any one of the above (1) to (3), wherein the elongation rate after 200% elongation is 20% or less.

（５）ＪＩＳＺ０２３７：２０００の試験板に対する180度引き剥がし粘着力試験法に準拠して測定される粘着力が、７Ｎ／２５ｍｍ以下である上記（１）ないし（４）のいずれかに記載の皮膚貼付用粘着シート。 (5) The adhesive strength measured in accordance with the 180 degree peeling adhesive strength test method for the test plate of JIS Z0237: 2000 is 7 N / 25 mm or less, according to any one of (1) to (4) above. Adhesive sheet for skin application.

（６）前記基材フィルムの前記粘着剤層が設けられた面とは反対側の面に、ドット印刷により形成された印刷層を有する上記（１）ないし（５）のいずれかに記載の皮膚貼付用粘着シート。 (6) The skin according to any one of the above (1) to (5), which has a printed layer formed by dot printing on a surface opposite to the surface on which the pressure-sensitive adhesive layer of the base film is provided. Adhesive sheet for sticking.

本発明によれば、皮膚から蒸散される水分が粘着シート／皮膚界面または粘着シート内に滞留するのを抑制し、水和反応による刺激を緩和することが可能な皮膚貼付用粘着シートを提供することができ、また、そのような皮膚貼付用粘着シートの特性を生かしたまま、印刷層を設けることができる。 ADVANTAGE OF THE INVENTION According to this invention, the adhesive sheet for skin sticking which suppresses the water | moisture content transpiration | evaporated from skin staying in an adhesive sheet / skin interface or an adhesive sheet, and can ease the irritation | stimulation by a hydration reaction is provided. In addition, a printed layer can be provided while taking advantage of the properties of the adhesive sheet for skin application.

本発明の皮膚貼付用粘着シートの第１実施形態を示す縦断面図である。It is a longitudinal cross-sectional view which shows 1st Embodiment of the adhesive sheet for skin sticking of this invention. 本発明の皮膚貼付用粘着シートの第２実施形態を示す縦断面図である。It is a longitudinal cross-sectional view which shows 2nd Embodiment of the adhesive sheet for skin sticking of this invention.

以下、本発明の皮膚貼付用粘着シートを好適実施形態に基づいて詳細に説明する。
《第１実施形態》
まず、本発明の皮膚貼付用粘着シートの第１実施形態について説明する。 Hereinafter, the adhesive sheet for skin application of the present invention will be described in detail based on preferred embodiments.
<< First Embodiment >>
First, 1st Embodiment of the adhesive sheet for skin sticking of this invention is described.

図１は、本発明の皮膚貼付用粘着シートの第１実施形態を示す縦断面図である。
皮膚貼付用粘着シート１０は、皮膚に貼着して用いられる粘着シートであって、例えば、絆創膏、パップ剤を固定するためのテーピング材、爪の保護シート、ささくれ（さかむけ）の保護テープ、点滴針の固定テープ、シワ伸ばし用シート、筋肉の固定用のテープ、ランニング時の乳首の保護テープ、香りシート等の用途で用いることができる。 FIG. 1 is a longitudinal sectional view showing a first embodiment of the adhesive sheet for skin application of the present invention.
The adhesive sheet 10 for skin application is an adhesive sheet that is used by being adhered to the skin, and includes, for example, an adhesive bandage, a taping material for fixing a poultice, a protective sheet for nails, and a protective tape for cresting. It can be used in applications such as a drip needle fixing tape, a wrinkle-stretching sheet, a muscle fixing tape, a nipple protective tape during running, and a scent sheet.

皮膚貼付用粘着シート１０は、図１に示すように、基材フィルム１と、基材フィルム１の一方の面に設けられた粘着剤層２とを備えている。 As shown in FIG. 1, the adhesive sheet 10 for skin application includes a base film 1 and an adhesive layer 2 provided on one surface of the base film 1.

これに対して、本発明の皮膚貼付用粘着シートは、基材フィルムとして、内部に直径１０μｍ以下の細孔を有し、かつ、透湿度が１００００ｇ／ｍ^２／２４ｈ以上であるものを用い、かつ、皮膚貼付用粘着シート全体としての透湿度が１０００ｇ／ｍ^２／２４ｈ以上である点に特徴を有している。このような特徴を有することにより、皮膚から蒸散される水分がシート／皮膚界面またはシート内に滞留するのを抑制することができ、角層の水和、細菌の増殖等が生じるのを効果的に防止することができる。その結果、皮膚への刺激が緩和された皮膚貼付用粘着シートを提供することができる。 In contrast, the pressure-sensitive adhesive sheet for skin adhesion of the present invention, the substrate film is internally has the following pore diameters 10 [mu] m, and moisture permeability used as is 10000g ^/ m 2 ^/ 24h or more, And it has the characteristics in the water vapor permeability as the whole adhesive sheet for skin sticking being 1000 g / m < ² > / 24h or more. By having such characteristics, it is possible to suppress moisture transpiration from the skin from staying in the sheet / skin interface or in the sheet, and effective in causing hydration of the stratum corneum, bacterial growth, etc. Can be prevented. As a result, it is possible to provide a pressure-sensitive adhesive sheet for skin application with reduced irritation to the skin.

基材フィルム１は、粘着剤層２を支持する機能を有する層である。
基材フィルム１としては、内部に直径１０μｍ以下の細孔を有し、かつ、透湿度が１００００ｇ／ｍ^２／２４ｈ以上であるものであれば、いかなる材質のものを用いてもよいが、多孔質のポリウレタンフィルム、多孔質のポリオレフィンフィルム、多孔質のポリエステルフィルム等が挙げられる。特に、多孔質のポリウレタンフィルムを用いるのが好ましい。多孔質のポリウレタンフィルムを用いることにより、他の材料を用いた多孔質のフィルムを用いるよりも、高い透湿度のフィルムが得られやすい。なおかつ、ポリウレタンフィルムは柔軟性に富むため、得られる皮膚貼付用粘着シート１０は、皮膚への刺激が緩和されるとともに、曲面追従性に特に優れたものとなる。 The base film 1 is a layer having a function of supporting the pressure-sensitive adhesive layer 2.
The substrate film 1, which incorporates a following pore diameters 10 [mu] m, and, as long as moisture permeability is 10000g / m 2 / ^24h or more, may be used as any material, but porous Quality polyurethane film, porous polyolefin film, porous polyester film and the like. In particular, it is preferable to use a porous polyurethane film. By using a porous polyurethane film, it is easier to obtain a film with a high moisture permeability than using a porous film using other materials. In addition, since the polyurethane film is rich in flexibility, the obtained pressure-sensitive adhesive sheet 10 for skin application is particularly excellent in curved surface followability while mitigating irritation to the skin.

上述したように、基材フィルム１は、透湿度が１００００ｇ／ｍ^２／２４ｈ以上であるものであるが、透湿度は、１２０００ｇ／ｍ^２／２４ｈ以上であるのがより好ましい。これにより、皮膚から蒸散される水分がシート／皮膚界面またはシート内に滞留するのをより効果的に抑制することができ、角層の水和、細菌の増殖等が生じるのをさらに効果的に防止することができる。その結果、皮膚への刺激をより好適に緩和することができる。 As described above, the substrate film 1 is moisture permeability is not more 10000g ^/ m 2 ^/ 24h or more, moisture permeability, and more preferably 12000g ^/ m 2 ^/ 24h or more. As a result, it is possible to more effectively suppress moisture transpiration from the skin from staying in the sheet / skin interface or in the sheet, and more effectively preventing hydration of the stratum corneum, bacterial growth, etc. Can be prevented. As a result, irritation to the skin can be mitigated more suitably.

また、上述したように、基材フィルム１は、内部に直径１０μｍ以下の細孔を有しているが、当該細孔は、基材フィルム１の厚み方向において連通する細孔であるのが好ましい。これにより、皮膚貼付用粘着シート１０の水分の透過性をより好適なものとすることができ、皮膚への刺激をより好適に緩和することができる。 Moreover, as described above, the base film 1 has pores having a diameter of 10 μm or less inside, and the pores are preferably pores communicating in the thickness direction of the base film 1. . Thereby, the water permeability of the adhesive sheet for skin application 10 can be made more suitable, and the irritation to the skin can be more suitably mitigated.

基材フィルム１の平均厚さは、１５〜７０μｍであるのが好ましく、２０〜６０μｍであるのがより好ましい。これにより、皮膚貼付用粘着シート１０の水分の透過性をより好適なものとすることができ、皮膚への刺激をより好適に緩和することができる上、皮膚貼付用粘着シート１０の十分な強度と取り扱い性を保つことができる。 The average thickness of the base film 1 is preferably 15 to 70 μm, and more preferably 20 to 60 μm. As a result, the moisture permeability of the adhesive sheet for skin application 10 can be made more suitable, irritation to the skin can be more suitably mitigated, and sufficient strength of the adhesive sheet for skin application 10 can be achieved. And maintain the handleability.

粘着剤層２は、皮膚貼付用粘着シート１０を皮膚に貼付する機能を備えた層である。
粘着剤層２を構成する材料としては、特に限定されず、例えば、アクリル系粘着剤、シリコーン系粘着剤、ウレタン系粘着剤、ゴム系粘着剤等が挙げられるが、皮膚貼付用粘着シート１０の透湿度を１０００ｇ／ｍ^２／２４ｈとするためには、アクリル系粘着剤、シリコーン系粘着剤、ウレタン系粘着剤が好ましく、製造コストの面から、アクリル系粘着剤が好ましい。 The pressure-sensitive adhesive layer 2 is a layer having a function of sticking the adhesive sheet for skin application 10 to the skin.
The material constituting the pressure-sensitive adhesive layer 2 is not particularly limited, and examples thereof include an acrylic pressure-sensitive adhesive, a silicone-based pressure-sensitive adhesive, a urethane-based pressure-sensitive adhesive, and a rubber-based pressure-sensitive adhesive. moisture permeability in order to 1000g / m 2 / ^24h, the acrylic pressure-sensitive adhesives, silicone pressure-sensitive adhesives, urethane-based adhesives are preferred, from the viewpoint of manufacturing cost, an acrylic adhesive is preferable.

アクリル系粘着剤を構成するアクリル系重合体としては、１種又は２種以上の単量体を重合してなる公知の重合体を用いることができる。単量体として用いることができるアクリル系単量体としては、（メタ）アクリル酸メチル、（メタ）アクリル酸エチル、（メタ）アクリル酸ブチル、（メタ）アクリル酸２−エチルヘキシル、（メタ）アクリル酸ドデシル等の（メタ）アクリル酸アルキルエステル；（メタ）アクリル酸シクロヘキシル等の（メタ）アクリル酸シクロアルキルエステル；（メタ）アクリル酸２−ヒドロキシエチル、（メタ）アクリル酸２−ヒドロキシブチル等の水酸基含有（メタ）アクリル酸エステル；（メタ）アクリル酸；（メタ）アクリルアミド、Ｎ−イソプロピルアクリルアミド等の（メタ）アクリルアミド誘導体等が挙げられる。単量体として用いることができる非アクリル系単量体としては、スチレン、酢酸ビニル、Ｎ−ビニルピロリドン、オレフィン系単量体等が挙げられる。 As an acrylic polymer which comprises an acrylic adhesive, the well-known polymer formed by superposing | polymerizing 1 type, or 2 or more types of monomers can be used. Examples of acrylic monomers that can be used as monomers include methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, and (meth) acrylic. (Meth) acrylic acid alkyl esters such as dodecyl acid; (meth) acrylic acid cycloalkyl esters such as (meth) acrylic acid cyclohexyl; (meth) acrylic acid 2-hydroxyethyl, (meth) acrylic acid 2-hydroxybutyl, etc. Examples include hydroxyl group-containing (meth) acrylic acid esters; (meth) acrylic acid; (meth) acrylamide derivatives such as (meth) acrylamide and N-isopropylacrylamide. Non-acrylic monomers that can be used as the monomer include styrene, vinyl acetate, N-vinylpyrrolidone, olefinic monomers, and the like.

粘着剤の透湿性を高いものとするために、単量体として、たとえば、アルキレンオキサイド基の繰り返し単位を３〜２０単位有するマクロモノマーを単量体として用いることで、アクリル系重合体を水蒸気の通りやすいものとするという方法が知られており、このような単量体を用いることで、皮膚貼付用粘着シート１０の透湿度を、より高いものとすることができる。 In order to increase the moisture permeability of the pressure-sensitive adhesive, for example, a macromonomer having 3 to 20 repeating units of an alkylene oxide group is used as a monomer, so that the acrylic polymer is made of water vapor. The method of making it easy to pass through is known, and by using such a monomer, the moisture permeability of the adhesive sheet for skin application 10 can be made higher.

アクリル系粘着剤には、所望の凝集力と粘着力を達成するために、架橋剤を添加してもよい。架橋剤として一般的に用いられるものは、単量体として水酸基含有（メタ）アクリル酸エステルや、（メタ）アクリル酸を用いた場合に水酸基又はカルボキシル基と、結合を生じるエポキシ系架橋剤、イソシアナート系架橋剤、アジリジン系架橋剤、金属キレート系架橋剤等である。 A crosslinking agent may be added to the acrylic pressure-sensitive adhesive in order to achieve desired cohesive strength and adhesive strength. Generally used as a crosslinking agent is a hydroxyl group-containing (meth) acrylic acid ester or an epoxy-based crosslinking agent that forms a bond with a hydroxyl group or a carboxyl group when (meth) acrylic acid is used as a monomer. Examples thereof include nate-based crosslinking agents, aziridine-based crosslinking agents, and metal chelate-based crosslinking agents.

アクリル系粘着剤には、凝集力の制御や、皮膚への追従性を高めるために、可塑剤を含有していてもよい。可塑剤としては、低分子成分、オリゴマー等を用いることができる。可塑剤として、室温で液体である低分子成分が、可塑作用が高く、また調製の容易性から好ましい。室温で液体である低分子成分としては、ミリスチン酸イソプロピル、ミリスチン酸ブチル、ステアリン酸ブチル等の脂肪酸エステル；ホホバ油、オリーブスクワラン等の植物油；流動パラフィン等の炭化水素等の油状成分が、本来的に疎水性であるアクリル系粘着剤との相溶性の面から好ましい。 The acrylic pressure-sensitive adhesive may contain a plasticizer in order to control the cohesive force and enhance the followability to the skin. As the plasticizer, low molecular components, oligomers, and the like can be used. As the plasticizer, a low molecular component that is liquid at room temperature is preferable because of its high plasticity and ease of preparation. Low molecular components that are liquid at room temperature include fatty acid esters such as isopropyl myristate, butyl myristate, and butyl stearate; vegetable oils such as jojoba oil and olive squalane; and oily components such as hydrocarbons such as liquid paraffin. In view of compatibility with an acrylic pressure-sensitive adhesive which is hydrophobic.

このほか、アクリル系粘着剤には、粘着付与剤、充填剤、美容成分、薬効成分、着色剤、顔料等を所望の効果を付与するために添加することができる。 In addition, tackifiers, fillers, cosmetic ingredients, medicinal ingredients, colorants, pigments, and the like can be added to the acrylic adhesive in order to impart desired effects.

充填剤として、親水性の充填剤を添加することによって、水蒸気が通過する経路とし、粘着剤層の透湿性を高める方法が知られている。このような親水性の充填剤の添加によっても、皮膚貼付用粘着シート１０の透湿度を高いものとすることができる。 As a filler, a method of increasing the moisture permeability of the pressure-sensitive adhesive layer by adding a hydrophilic filler to form a path through which water vapor passes is known. Addition of such a hydrophilic filler can also increase the moisture permeability of the adhesive sheet 10 for skin application.

ところで、上述のとおり本発明における基材フィルム１の透湿度は１００００ｇ／ｍ^２／２４ｈ以上と高いものであるので、粘着剤は上述のような、アルキレンオキサイド基の繰り返し単位を３〜２０単位有するマクロモノマーを単量体として用いたり、親水性を添加したりする方法によって透湿性の高めたものを選択する必要がなく、皮膚貼付用として一般的に用いられているアクリル系粘着剤をも用いることができる。 By the way, as above-mentioned, since the water vapor transmission rate of the base film 1 in this invention is as high as 10,000 g / m < ² > / 24h or more, an adhesive has 3-20 units of repeating units of an alkylene oxide group as mentioned above. There is no need to use a macromonomer as a monomer or to select a material with increased moisture permeability by adding hydrophilicity, and acrylic adhesives commonly used for skin application are also used. be able to.

また、透湿性が高くなるよう設計された粘着剤を用いた場合には、透湿度のより高い皮膚貼付用粘着シート１０の提供が可能である。 Moreover, when the adhesive designed so that moisture permeability becomes high can be provided, the adhesive sheet 10 for skin sticking with higher moisture permeability can be provided.

粘着剤層２の平均厚さは、５〜４０μｍであるのが好ましく、７〜３０μｍであるのがより好ましい。これにより、皮膚貼付用粘着シート１０の水分の透過性をより好適なものとすることができ、皮膚への刺激をより好適に緩和することができる上、皮膚上に固定するのに十分な粘着特性が得られる。 The average thickness of the pressure-sensitive adhesive layer 2 is preferably 5 to 40 μm, and more preferably 7 to 30 μm. As a result, the moisture permeability of the adhesive sheet for skin application 10 can be made more suitable, irritation to the skin can be mitigated more suitably, and sufficient adhesion to fix on the skin can be achieved. Characteristics are obtained.

上述したような基材フィルム１および粘着剤層２を備えた皮膚貼付用粘着シート１０は、上記のように皮膚貼付用粘着シート１０全体の透湿度が１０００ｇ／ｍ^２／２４ｈ以上であるが、皮膚貼付用粘着シート１０全体の透湿度は、１２００ｇ／ｍ^２／２４ｈ以上であるのがより好ましく、１５００ｇ／ｍ^２／２４ｈ以上であるのがより好ましい。これにより、皮膚から蒸散される水分がシート／皮膚界面またはシート内に滞留するのをより効果的に抑制することができ、角層の水和、細菌の増殖等が生じるのをより確実に防止することができる。その結果、皮膚への刺激をさらに緩和することができる。 The adhesive sheet 10 for skin application provided with the base film 1 and the adhesive layer 2 as described above has a moisture permeability of 1000 g / m ² / 24h or more as described above, as described above. moisture permeability of the entire skin adhesion pressure-sensitive adhesive sheet 10, more preferably at 1200g ^/ m 2 ^/ 24h or more, more preferably 1500g ^/ m 2 ^/ 24h or more. As a result, it is possible to more effectively prevent moisture transpiration from the skin from staying in the sheet / skin interface or in the sheet, and more reliably prevent hydration of the stratum corneum, bacterial growth, etc. can do. As a result, the skin irritation can be further alleviated.

なお、皮膚貼付用粘着シート１０全体の透湿度を上記のような範囲とするには、粘着剤層２に透湿度を高めるための特殊な方法を用いることなく、たとえば上述のアクリル系粘着剤の単量体として挙げたものを任意に選択して調製した重合体と、適宜の成分を用いたアクリル系粘着剤によって、粘着剤層２を上述の好ましい厚さで設けることによって可能である。 In addition, in order to make the moisture permeability of the adhesive sheet 10 for skin sticking whole into the above ranges, without using the special method for raising moisture permeability to the adhesive layer 2, for example of the above-mentioned acrylic adhesive It is possible to provide the pressure-sensitive adhesive layer 2 with the above-mentioned preferable thickness by using a polymer prepared by arbitrarily selecting those listed as monomers and an acrylic pressure-sensitive adhesive using appropriate components.

また、皮膚貼付用粘着シート１０の２０％伸長時の引張力は、３Ｎ／２５ｍｍ以下であるのが好ましく、１．０〜２．８Ｎ／２５ｍｍであるのがより好ましく、１．０〜１．５Ｎ／２５ｍｍであるのがより好ましい。上記引張力が上記範囲であると、皮膚貼付用粘着シート１０を皮膚に貼付中に、皮膚貼付用粘着シート１０と皮膚の伸縮が異なることによるひずみによって生じる皮膚刺激を効果的に緩和することができる。 Moreover, it is preferable that the tensile force at the time of 20% expansion | extension of the adhesive sheet 10 for skin sticking is 3N / 25mm or less, It is more preferable that it is 1.0-2.8N / 25mm, 1.0-1. More preferably, it is 5 N / 25 mm. When the tensile force is within the above range, skin irritation caused by strain caused by the expansion and contraction of the skin adhesive pressure-sensitive adhesive sheet 10 and the skin can be effectively alleviated while the skin adhesive pressure-sensitive adhesive sheet 10 is applied to the skin. it can.

なお、２０％伸長時の引張力は、２５ｍｍ×１５０ｍｍに切り取った皮膚貼付用粘着シート１０の長手方向の両端部から２５ｍｍを固定し、長手方向に１００ｍｍの皮膚貼付用粘着シート１０が１２０ｍｍとなるまで速度３００ｍｍ／分で引っ張った直後に測定される力である。 The tensile force at 20% elongation is fixed to 25 mm from both ends in the longitudinal direction of the adhesive sheet 10 for skin application cut to 25 mm × 150 mm, and the adhesive sheet 10 for skin application of 100 mm is 120 mm in the longitudinal direction. The force measured immediately after pulling at a speed of 300 mm / min.

また、皮膚貼付用粘着シート１０の２００％伸長後の伸長率は、２０％以下であるのが好ましく、１５％以下であるのがより好ましい。伸長率がこのような範囲であると、皮膚貼付用粘着シート１０を皮膚に貼付中に、皮膚の伸長に追従した皮膚貼付用粘着シート１０が元の長さに回復し、皮膚貼付用粘着シート１０が変形によって、貼られていた皮膚の形状と異なるものとなることによって生じる皮膚刺激を効果的に緩和することができる。 Moreover, it is preferable that the elongation rate after 200% expansion | extension of the adhesive sheet 10 for skin sticking is 20% or less, and it is more preferable that it is 15% or less. When the elongation rate is within such a range, the adhesive sheet 10 for skin application following the elongation of the skin is restored to the original length while the adhesive sheet 10 for application to the skin is applied to the skin, and the adhesive sheet for application to the skin Skin irritation caused by 10 becoming different from the shape of the pasted skin due to deformation can be effectively mitigated.

なお、上記伸長率は、２５ｍｍ×１５０ｍｍに切り取った皮膚貼付用粘着シート１０を長手方向に２００％伸長させ、応力を解除した直後における皮膚貼付用粘着シート１０の長さを、伸長後の長さとして、下記式により得られる割合であり、伸長率が低いほど伸長による変形が少ないことを示す。
伸長率＝｛伸長後の長さ−伸長前の長さ｝×１００／伸長前の長さ In addition, the said elongation rate is the length after extending | stretching the length of the adhesive sheet 10 for skin affixing immediately after extending | stretching the adhesive sheet 10 for skin sticking cut out to 25 mm x 150 mm 200% in a longitudinal direction, and releasing stress. As the ratio is obtained by the following formula, the lower the elongation ratio, the less the deformation due to elongation.
Elongation rate = {length after extension−length before extension} × 100 / length before extension

また、皮膚貼付用粘着シート１０のＪＩＳＺ０２３７：２０００の試験板に対する１８０度引き剥がし粘着力試験法に準拠して測定される粘着力は、７Ｎ／２５ｍｍ以下であるのが好ましく、１．０〜６．５Ｎ／ｍｍであるのがより好ましい。これにより、皮膚貼付用粘着シート１０を剥がす際の皮膚の角層剥離による刺激を効果的に緩和することができる。 Moreover, it is preferable that the adhesive force measured based on the 180 degree | times peeling adhesive force test method with respect to the test board of JIS Z0237: 2000 of the adhesive sheet 10 for skin sticking is 7 N / 25mm or less, and 1.0- More preferably, it is 6.5 N / mm. Thereby, the irritation | stimulation by the stratum corneum peeling of the skin at the time of peeling the adhesive sheet 10 for skin sticking can be relieve | moderated effectively.

なお、上記粘着力は、ＪＩＳＺ０２３７：２０００の試験板に対する１８０度引き剥がし粘着力試験法に準拠して測定される応力であり、具体的には、以下のようにして測定される。 In addition, the said adhesive force is the stress measured based on the 180 degree peeling adhesive force test method with respect to the test board of JISZ0237: 2000, and is specifically measured as follows.

皮膚貼付用粘着シート１０の基材フィルム１の上面に固定材（５０μｍのポリエステルフィルムと２５μｍの粘着剤О２０４とからなる粘着シート）を貼り合わせ、２５ｍｍ×２００ｍｍに切り取る。皮膚貼付用粘着シート１０の粘着剤層２をＳＵＳ板に貼り付け、圧着し、３０分後に皮膚貼付用粘着シート１０の端を１８０度方向に３００ｍｍ／ｍｉｎの速度で引っ張った際の応力を測定する。 A fixing material (adhesive sheet made of 50 μm polyester film and 25 μm adhesive O204) is bonded to the upper surface of the base film 1 of the adhesive sheet 10 for skin application, and cut into 25 mm × 200 mm. The pressure-sensitive adhesive layer 2 of the adhesive sheet for skin application 10 is attached to a SUS board and pressed, and after 30 minutes, the stress is measured when the end of the adhesive sheet 10 for skin application is pulled in the direction of 180 degrees at a speed of 300 mm / min. To do.

《第２実施形態》
次に、本発明の皮膚貼付用粘着シートの第２実施形態について説明する。 << Second Embodiment >>
Next, 2nd Embodiment of the adhesive sheet for skin sticking of this invention is described.

本実施形態では、前述した第１実施形態と異なる点について説明し、同様な構成についてはその説明を省略する。 In the present embodiment, differences from the first embodiment described above will be described, and descriptions of similar configurations will be omitted.

図２は、本発明の皮膚貼付用粘着シートの第２実施形態を示す縦断面図である。
皮膚貼付用粘着シート１０’は、基材フィルム１と、基材フィルム１の一方の面に設けられた粘着剤層２とを備えている点で、前述した実施形態と共通しており、図２に示すように、基材フィルム１上に印刷層３を設けた点で前述した実施形態と異なっている。 FIG. 2 is a longitudinal sectional view showing a second embodiment of the adhesive sheet for skin application of the present invention.
The adhesive sheet 10 'for skin application is common to the above-described embodiment in that it includes a base film 1 and an adhesive layer 2 provided on one surface of the base film 1. As shown in FIG. 2, the embodiment differs from the above-described embodiment in that the printing layer 3 is provided on the base film 1.

基材フィルム１および粘着剤層２については、前述した実施形態と同じであるので、その説明を省略する。 About the base film 1 and the adhesive layer 2, since it is the same as embodiment mentioned above, the description is abbreviate | omitted.

本実施形態では、基材フィルム１の粘着剤層２が設けられた面とは反対側の面に印刷層３が設けられている。特に、本実施形態では、印刷層３がドット印刷によって形成されている点に特徴を有している。 In this embodiment, the printing layer 3 is provided on the surface opposite to the surface on which the pressure-sensitive adhesive layer 2 of the base film 1 is provided. In particular, the present embodiment is characterized in that the printing layer 3 is formed by dot printing.

ところで、通常、基材フィルム上に印刷層を設けた場合、皮膚貼付用粘着シート全体としての透湿性は低下し、皮膚から蒸散される水分がシート／皮膚界面またはシート内に滞留するのを十分に防止することができなくなり、水和反応による刺激を防止することができなくなるという問題が生じる。 By the way, normally, when a printing layer is provided on a base film, the moisture permeability of the entire adhesive sheet for skin application is lowered, and it is sufficient that the moisture evaporated from the skin stays in the sheet / skin interface or in the sheet. The problem that it becomes impossible to prevent the irritation caused by the hydration reaction occurs.

しかしながら、本実施形態では、上記のような特性を有する基材フィルム１上に、ドット印刷によって印刷層３が設けられているので、基材フィルム１の表面を完全に覆うことがないので、基材フィルム１の透湿性の低下を防止することができる。そのため、皮膚貼付用粘着シート１０全体としての透湿性が損なわれることがないので、皮膚から蒸散される水分がシート／皮膚界面またはシート内に滞留するのを抑制することができ、角層の水和、細菌の増殖等が生じるのを効果的に防止することができる。その結果、皮膚への刺激が緩和された皮膚貼付用粘着シート１０’を提供することができる。 However, in this embodiment, since the printing layer 3 is provided by dot printing on the base film 1 having the above characteristics, the surface of the base film 1 is not completely covered. A decrease in moisture permeability of the material film 1 can be prevented. Therefore, the moisture permeability of the adhesive sheet for skin application 10 as a whole is not impaired, so that moisture evaporated from the skin can be prevented from staying in the sheet / skin interface or in the sheet. It is possible to effectively prevent the sum and the growth of bacteria. As a result, it is possible to provide a pressure-sensitive adhesive sheet for skin application 10 ′ in which irritation to the skin is alleviated.

印刷は、公知の印刷方法を用いることができ、フレキソ印刷、オフセット印刷、グラビア印刷、レタープレス印刷等が挙げられる。 For printing, a known printing method can be used, and examples thereof include flexographic printing, offset printing, gravure printing, and letter press printing.

印刷に用いるインクは、ドット印刷で用いる公知のものを用いることができる。インクは、顔料、染料等を含有しており、これらが水蒸気の透過を妨げ、ベタ印刷により印刷層３を設けた場合には、皮膚貼付粘着シート１０の透湿度を著しく下げてしまう。しかし、上述のとおりドット印刷とすることによって、これを防止できる。 As the ink used for printing, a known ink used for dot printing can be used. The ink contains pigments, dyes, and the like, which impede the permeation of water vapor, and when the printing layer 3 is provided by solid printing, the moisture permeability of the skin adhesive pressure-sensitive adhesive sheet 10 is significantly reduced. However, this can be prevented by dot printing as described above.

ドット印刷は通常、基材フィルム１の粘着剤層２が設けられた面とは反対側の面の表面積の１０〜８０％を覆い、２０〜７０％を覆うことが好ましく、３０〜６０％を覆うことがより好ましい。ドット印刷が基材フィルム１の粘着剤層２が設けられた面とは反対側の面の表面積を覆う比率が大きすぎると、水蒸気の透過を妨げ、当該比率が小さすぎると、非印刷部が多くなりすぎ、所望の表示を得られない可能性がある。 The dot printing usually covers 10 to 80% of the surface area of the surface opposite to the surface on which the adhesive layer 2 of the base film 1 is provided, preferably 20 to 70%, preferably 30 to 60%. It is more preferable to cover. If the ratio of the dot printing covering the surface area of the surface opposite to the surface on which the pressure-sensitive adhesive layer 2 of the base film 1 is provided is too large, the permeation of water vapor is impeded. There is a possibility that a desired display cannot be obtained due to excessive increase.

以上、本発明の皮膚貼付用粘着シートの好適な実施形態について説明したが、本発明は、これらに限定されるものではない。 As mentioned above, although preferred embodiment of the adhesive sheet for skin sticking of this invention was described, this invention is not limited to these.

次に、本発明の具体的実施例について説明する。
［１］皮膚貼付用粘着シートの作製
（実施例１）
［基材フィルム］
基材フィルムとして、TECHNOBRANE AIR TAF-40（ポリウレタンフィルム、セーレン株式会社製、平均厚さ：４０μｍ、直径１０μｍ以下の細孔有り）を用いた。 Next, specific examples of the present invention will be described.
[1] Preparation of adhesive sheet for skin application (Example 1)
[Base film]
As the base film, TECHNOBRANE AIR TAF-40 (polyurethane film, manufactured by Seiren Co., Ltd., average thickness: 40 μm, with pores having a diameter of 10 μm or less) was used.

このフィルムをデジタル顕微鏡（株式会社ハイロックス製、KH-7700、倍率1,000倍）で観察すると、フィルムの両面には直径１０μｍ以下の微細孔が均一に存在し、また、フィルムの断面ではフィルムを連通する細孔が確認された。また、このフィルムの透湿度は１１７００ｇ／ｍ^２／２４ｈであった。 When this film is observed with a digital microscope (Hilox Co., Ltd., KH-7700, magnification 1000 times), fine pores with a diameter of 10 μm or less are uniformly present on both sides of the film, and the film is communicated in the cross section of the film. Pores were confirmed. Moreover, the water vapor transmission rate of this film was 11700 g / m < ² > / 24h.

［粘着剤層の形成］
アクリル系粘着剤（リンテック株式会社製、商品名「Ｏ２２０」、固形分：５０％）および、剥離紙（リンテック株式会社製、商品名「ＳＰ−ＫＰ−８シロ」）を用意した。 [Formation of adhesive layer]
An acrylic adhesive (trade name “O220” manufactured by Lintec Corporation, solid content: 50%) and release paper (trade name “SP-KP-8 Shiro” manufactured by Lintec Corporation) were prepared.

次に、アクリル系粘着剤をロールナイフコーターを用いて、前記剥離紙の剥離処理が施された剥離紙面に乾燥後の厚さが１５μｍとなるように塗布した後、１００℃で２分間乾燥し、剥離紙上に粘着剤層を形成した。 Next, an acrylic pressure-sensitive adhesive was applied to the release paper surface on which the release paper had been peeled off using a roll knife coater so that the thickness after drying was 15 μm, and then dried at 100 ° C. for 2 minutes. An adhesive layer was formed on the release paper.

［皮膚貼付用粘着シートの形成］
上記のようにして得られた剥離紙上の粘着剤層と、上記のようにして得られた基材フィルムとを貼り合わせることにより、皮膚貼付用粘着シートを得た。 [Formation of adhesive sheet for skin application]
A pressure-sensitive adhesive sheet for skin application was obtained by bonding the pressure-sensitive adhesive layer on the release paper obtained as described above and the base film obtained as described above.

（実施例２）
粘着剤層の厚みが２０μｍとなるように調整した以外は、前記実施例１と同様にして皮膚貼付用粘着シートを作製した。 (Example 2)
A pressure-sensitive adhesive sheet for skin application was prepared in the same manner as in Example 1 except that the thickness of the pressure-sensitive adhesive layer was adjusted to 20 μm.

（実施例３）
粘着剤層の厚みが３０μｍとなるように調整した以外は、前記実施例１と同様にして皮膚貼付用粘着シートを作製した。 (Example 3)
A pressure-sensitive adhesive sheet for skin application was prepared in the same manner as in Example 1 except that the thickness of the pressure-sensitive adhesive layer was adjusted to 30 μm.

（実施例４）
粘着剤層を以下のようにして形成した以外は、前記実施例１と同様にして皮膚貼付用粘着シートを作製した。 Example 4
A pressure-sensitive adhesive sheet for skin application was prepared in the same manner as in Example 1 except that the pressure-sensitive adhesive layer was formed as follows.

［粘着剤層の形成］
アクリル系粘着剤（リンテック株式会社製、商品名「О２０４」、固形分：５０％）に対して、ミリスチン酸イソプロピルを２００：５の割合で混合し、粘着剤溶液を得た。また、剥離紙（リンテック株式会社製、商品名「ＳＰ−ＫＰ−８シロ」）を用意した。 [Formation of adhesive layer]
Isopropyl myristate was mixed in a ratio of 200: 5 to an acrylic pressure-sensitive adhesive (trade name “O204”, manufactured by Lintec Corporation, solid content: 50%) to obtain a pressure-sensitive adhesive solution. Also, release paper (trade name “SP-KP-8 Shiro” manufactured by Lintec Corporation) was prepared.

次に、アクリル系粘着剤をロールナイフコーターを用いて、前記剥離紙の剥離処理が施された剥離紙面に乾燥後の厚さが２０μｍとなるように塗布した後、１００℃で２分間乾燥し、剥離紙上に粘着剤層を形成した。 Next, an acrylic pressure-sensitive adhesive was applied to the release paper surface on which the release paper was subjected to a release treatment using a roll knife coater so that the thickness after drying was 20 μm, and then dried at 100 ° C. for 2 minutes. An adhesive layer was formed on the release paper.

（実施例５）
粘着剤層を以下のようにして形成した以外は、前記実施例１と同様にして皮膚貼付用粘着シートを作製した。 (Example 5)
A pressure-sensitive adhesive sheet for skin application was prepared in the same manner as in Example 1 except that the pressure-sensitive adhesive layer was formed as follows.

［粘着剤層の形成］
アクリル系粘着剤（リンテック株式会社製、商品名「О２０４」、固形分：５０％）を、ロールナイフコーターを用いて、剥離紙（リンテック株式会社製、商品名「ＳＰ−ＫＰ−８シロ」）の剥離処理が施された面に乾燥後の厚さが２０μｍとなるように塗布した後、１００℃で２分間乾燥し、剥離紙上に粘着剤層を形成した。 [Formation of adhesive layer]
Acrylic adhesive (trade name “О204”, manufactured by Lintec Corporation, solid content: 50%) is released using a roll knife coater (trade name “SP-KP-8 Shiro” manufactured by Lintec Corporation). After applying to the surface on which the release treatment was performed so that the thickness after drying was 20 μm, it was dried at 100 ° C. for 2 minutes to form an adhesive layer on the release paper.

（実施例６）
実施例１のポリウレタンフィルムの代わりに、ポリウレタンフィルム（セーレン株式会社製、TECHNOBRANE AIR TAF-30平均厚さ：３０μｍ、１０μｍ以下の細孔有り、透湿度：１２５００ｇ／ｍ^２／２４ｈ）を用いた以外は、実施例１と同様にして皮膚貼付用粘着シートを作製した。 (Example 6)
Instead of the polyurethane film of Example 1, a polyurethane film (manufactured by Seiren Co., TECHNOBRANE AIR TAF-30 Average thickness: 30 [mu] m, there following pores 10 [mu] m, moisture permeability: 12500g ^/ m 2 ^/ 24h) except for using Produced a pressure-sensitive adhesive sheet for skin application in the same manner as in Example 1.

（実施例７）
実施例１の皮膚貼付用シートの、粘着剤層が設けられた面とは反対側の面に、表面積の４０％がインクで被覆されるように、レタープレス方式により、UV161(T&K TOKA製)をインクとして用いて厚さ３μmのドット印刷を設け、皮膚貼付用シートを作製した。 (Example 7)
UV161 (manufactured by T & K TOKA) by letter press so that 40% of the surface area is covered with ink on the surface opposite to the surface on which the adhesive layer is provided of the sheet for skin application of Example 1. Was used as an ink to provide dot printing with a thickness of 3 μm to prepare a sheet for skin application.

（比較例１）
［粘着剤層の形成］
アクリル系粘着剤（リンテック株式会社製、商品名「Ｏ２２０」、固形分：５０％）および、剥離紙（リンテック株式会社製、商品名「ＳＰ−ＫＰ−８シロ」）を用意した。 (Comparative Example 1)
[Formation of adhesive layer]
An acrylic adhesive (trade name “O220” manufactured by Lintec Corporation, solid content: 50%) and release paper (trade name “SP-KP-8 Shiro” manufactured by Lintec Corporation) were prepared.

［皮膚貼付用粘着シートの形成］
上記のようにして得られた剥離紙上の粘着剤層と、基材フィルム（低密度ポリエチレンフィルム、日本マタイ社製、平均厚さ：２０μｍ、１０μｍ以下の細孔無し、透湿度：１２００／ｍ^２／２４ｈ）とを貼り合わせることにより、皮膚貼付用粘着シートを得た。 [Formation of adhesive sheet for skin application]
The pressure-sensitive adhesive layer on the release paper obtained as described above and a base film (low density polyethylene film, manufactured by Nippon Matai Co., Ltd., average thickness: 20 μm, no pores of 10 μm or less, moisture permeability: 1200 / m ² / 24h) to obtain an adhesive sheet for skin application.

（比較例２）
基材フィルムとして、ポリウレタンフィルム（日本マタイ社製、平均厚さ：２０μｍ、１０μｍ以下の細孔無し、透湿度：２３００ｇ／ｍ^２／２４ｈ）を用いた以外は、前記比較例１と同様にして皮膚貼付用粘着シートを作製した。 (Comparative Example 2)
As the substrate film, a polyurethane film (Nihon Matai Co., average thickness: 20 [mu] m, the pores without following 10 [mu] m, moisture permeability: 2300g ^/ m 2 ^/ 24h) except for using, in the same manner as in Comparative Example 1 A pressure-sensitive adhesive sheet for skin application was prepared.

（比較例３）
基材フィルムとして、ポリ塩化ビニルフィルム（バンドー化学社製、平均厚さ：２０μｍ、１０μｍ以下の細孔無し、透湿度：９００ｇ／ｍ^２／２４ｈ）を用いた以外は、前記比較例１と同様にして皮膚貼付用粘着シートを作製した。 (Comparative Example 3)
As the base film, polyvinyl chloride film (Bando Chemical Co., Ltd., average thickness: 20 [mu] m, the pores without following 10 [mu] m, moisture permeability: 900g ^/ m 2 ^/ 24h) except for using, as in the Comparative Example 1 Thus, an adhesive sheet for skin application was prepared.

（比較例４）
基材フィルムの表面にレタープレス方式でべた印刷を施し、厚さ３μｍの印刷層を形成した以外は、前記実施例１と同様にして皮膚貼付用粘着シートを製造した。 (Comparative Example 4)
A pressure-sensitive adhesive sheet for skin application was produced in the same manner as in Example 1 except that the surface of the base film was solid-printed by the letter press method to form a 3 μm thick printed layer.

［２］透湿度の測定
各実施例および各比較例で得られた皮膚貼付用粘着シートの透湿度は、ＪＩＳＺ０２０８（防湿包装材料の透過湿度試験方法）に準じて測定した。 [2] Measurement of moisture permeability The moisture permeability of the adhesive sheet for skin application obtained in each Example and each Comparative Example was measured according to JIS Z0208 (Testing method for moisture permeability of moisture-proof packaging material).

透湿度測定用カップに、水分測定用塩化カルシウム約１０ｇを入れ、直径７０ｍｍの円状に切り取った皮膚貼付用粘着シートを適用した（透過面積：６０ｍｍφの円の面積）。４０℃、９０％ＲＨの環境下に５分間放置した後、取り出し、速やかに全体の重量（ｍｇ）を計量し、これを初期の重量とした。その後、さらに、４０℃、９０％ＲＨの環境下に入れ、１時間後に取り出し、速やかに全体の重量を計量し、１時間後の重量とした。次の式により、透湿度を算出した。
透湿度＝｛（１時間後の重量−初期の重量）／１０００｝／
／（１×０．００２８２６）×２４ About 10 g of calcium chloride for moisture measurement was put into a moisture permeability measurement cup, and an adhesive sheet for skin application cut into a circle with a diameter of 70 mm was applied (permeation area: area of a circle of 60 mmφ). After leaving it in an environment of 40 ° C. and 90% RH for 5 minutes, it was taken out, and the entire weight (mg) was immediately measured, and this was taken as the initial weight. Thereafter, the sample was further placed in an environment of 40 ° C. and 90% RH, taken out after 1 hour, and immediately weighed to obtain the weight after 1 hour. The moisture permeability was calculated by the following formula.
Moisture permeability = {(weight after 1 hour-initial weight) / 1000} /
/(1×0.002826)×24

なお、上式における１０００は、ｍｇ単位をｇ単位に変換するための係数であり、１は測定時間（時間）、０．００２８２６は透過面積（ｍ^２）である。ここで、ＪＩＳＺ０２０８の規定する測定時間である２４時間よりも測定時間を短くしているのは、本発明に用いる皮膚貼付用粘着シートの透湿性があまりにも高く、２４時間の測定では途中で吸湿剤である塩化カルシウムの吸湿量が飽和量に達するためである。
この結果を表１に示す。 Note that 1000 in the above equation is a coefficient for converting mg units to g units, 1 is a measurement time (hour), and 0.002826 is a transmission area (m ² ). Here, the measurement time is shorter than 24 hours, which is the measurement time defined by JIS Z0208, because the adhesive sheet for skin application used in the present invention has a very high moisture permeability, and the measurement for 24 hours is halfway. This is because the moisture absorption amount of calcium chloride as the moisture absorbent reaches the saturation amount.
The results are shown in Table 1.

［３］評価
［３−１］２４時間貼着後の皮膚の状態
５０ｍｍ×５０ｍｍに切り取った各実施例および各比較例の皮膚貼付用粘着シートの剥離紙を剥がし、粘着剤層を上腕内側に貼り付け、２４時間後にゆっくりと剥がした（速度：１６７ｍｍ／ｓ以下）。１０分後の皮膚の状態を目視で確認し、以下の３段階で官能評価を行った。 [3] Evaluation [3-1] Skin condition after 24 hours sticking The release paper of the adhesive sheet for skin application of each Example and each Comparative Example cut to 50 mm × 50 mm was peeled off, and the adhesive layer was placed on the inner side of the upper arm Pasting and peeling off slowly after 24 hours (speed: 167 mm / s or less). The condition of the skin after 10 minutes was visually confirmed, and sensory evaluation was performed in the following three stages.

Ａ：貼付周囲の皮膚と変化がない。
Ｂ：皮膚の貼付した部分が若干白くなっているが、実用上問題ない範囲である。
Ｃ：皮膚の貼付した部分が白くなっており、皮膚がふやけている。 A: There is no change with the surrounding skin.
B: Although the part where the skin is affixed is slightly white, it is in a range where there is no practical problem.
C: The part where the skin is affixed is white, and the skin is bright.

［３−２］２０％伸長時の引張力
各実施例および各比較例の皮膚貼付用粘着シートの２０％伸長時の引張力を、上述した実施形態で述べたのと同様にして測定した。 [3-2] Tensile force at 20% elongation The tensile force at 20% elongation of the adhesive sheet for skin application of each Example and each Comparative Example was measured in the same manner as described in the above-described embodiment.

［３−３］貼付時の刺激評価
５０ｍｍ×５０ｍｍに切り取った各実施例および各比較例の皮膚貼付用粘着シートの剥離紙を剥がし、粘着剤層を上腕内側に貼り付け、貼付時の違和感、痛みを以下の３段階で官能評価した。 [3-3] Evaluation of stimulation at the time of application Peel off the release paper of the adhesive sheet for skin application of each Example and each Comparative Example cut to 50 mm × 50 mm, and apply the adhesive layer to the inner side of the upper arm. Pain was sensory evaluated in the following three stages.

Ａ：違和感および痛みはなく、貼付している感覚が極めて低い。
Ｂ：痛みはないが、貼付している違和感が若干ある。
Ｃ：皮膚が引っ張られる若干の痛みを感じ、貼付している違和感が強く感じる。 A: There is no sense of incongruity and pain, and the pasting sensation is extremely low.
B: Although there is no pain, there is a little uncomfortable feeling affixed.
C: Feels a slight pain that the skin is pulled, and strongly feels a sense of discomfort.

［３−４］ＪＩＳＺ０２３７：２０００の試験板に対する180度引き剥がし粘着力試験法に準拠して測定される粘着力
各実施例および各比較例の皮膚貼付用粘着シートのＪＩＳＺ０２３７：２０００の試験板に対する１８０度引き剥がし粘着力試験法
に準拠して測定される粘着力を、上述した実施形態で述べたのと同様にして測定した。 [3-4] Adhesive strength measured according to JIS Z0237: 2000 test plate peel-off adhesion test method JIS Z0237: 2000 test of adhesive sheet for skin application of each example and each comparative example The adhesive strength measured in accordance with the 180 degree peel adhesion test method for the plate was measured in the same manner as described in the above-described embodiment.

［３−５］剥離時の痛み
５０ｍｍ×５０ｍｍに切り取った各実施例および各比較例の皮膚貼付用粘着シートの剥離紙を剥がし、粘着剤層を上腕内側に貼り付け、２４時間後に勢いよく剥がした（速度：１７ｍｍ／ｓ以上）ときの痛みを以下の３段階で官能評価した。 [3-5] Pain at the time of peeling The release paper of the adhesive sheet for skin application of each Example and each Comparative Example cut out to 50 mm × 50 mm is peeled off, the adhesive layer is attached to the inner side of the upper arm, and peeled off vigorously after 24 hours. The pain at the time of (speed: 17 mm / s or more) was sensory evaluated in the following three stages.

Ａ：ほとんど痛みは感じず、皮膚に発赤はない。
Ｂ：剥離時に不快な痛みを若干感じるが、皮膚に顕著な発赤はない。
Ｃ：剥離時に不快な痛みを感じ、皮膚に発赤を確認する。 A: There is almost no pain and there is no redness on the skin.
B: Some unpleasant pain is felt at the time of peeling, but there is no noticeable redness on the skin.
C: Unpleasant pain is felt at the time of peeling, and redness is confirmed on the skin.

［３−６］２００％伸長後の伸長率
各実施例および各比較例の皮膚貼付用粘着シートの２００％伸長後の伸長率を、上述した実施形態で述べたのと同様にして測定した。 [3-6] Elongation rate after 200% elongation The elongation rate after 200% elongation of the adhesive sheet for skin application of each Example and each Comparative Example was measured in the same manner as described in the above-described embodiment.

［３−７］関節への貼付性
５０ｍｍ×５０ｍｍに切り取った各実施例および各比較例の皮膚貼付用粘着シートの剥離紙を剥がし、粘着剤層を手首外側に貼り付け、皮膚貼付用粘着シートの皮膚への追従性を以下の３段階で官能評価した。 [3-7] Adhesiveness to joints The release paper of the adhesive sheets for skin application of each Example and each Comparative Example cut to 50 mm x 50 mm is peeled off, and the adhesive layer is applied to the outside of the wrist, and the adhesive sheet for application to the skin Sensory evaluation of the following ability to the skin was carried out in the following three stages.

Ａ：皮膚貼付用粘着シートは手首の動きに追従し、浮きはなかった。
Ｂ：皮膚貼付用粘着シートは手首の動きに追従し、浮きが端部にわずかにあった。
Ｃ：皮膚貼付用粘着シートは手首の動きに追従できず、端部から、いずれの端部からも１０ｍｍ以上離れた部分に到るまで浮きが発生した。 A: The adhesive sheet for skin application followed the movement of the wrist and did not float.
B: The adhesive sheet for affixing the skin followed the movement of the wrist, and there was a slight lift at the end.
C: The pressure-sensitive adhesive sheet for skin application could not follow the movement of the wrist, and floating occurred from the end part to a part separated by 10 mm or more from any end part.

［３−８］皮膚からの剥離性
５０ｍｍ×５０ｍｍに切り取った各実施例および各比較例の皮膚貼付用粘着シートの剥離紙を剥がし、粘着剤層を上腕内側に貼り付け、２４時間後にゆっくりと剥がした（速度：５ｍｍ／ｓ以下）。この時の剥離性を以下の２段階で官能評価した。 [3-8] Peelability from skin Peel off the release paper of the adhesive sheet for skin application of each Example and each Comparative Example cut to 50 mm x 50 mm, and apply the adhesive layer to the inner side of the upper arm, and slowly after 24 hours Peeled off (speed: 5 mm / s or less). The peelability at this time was subjected to sensory evaluation in the following two stages.

○：基材フィルムが破壊されることなく、容易に剥がすことができた。
×：基材フィルムが破壊され、容易に剥がすことができなかった。 ○: The base film could be easily peeled off without being destroyed.
X: The base film was destroyed and could not be easily peeled off.

これらの結果を表１に合わせて示す。
表１から明らかなように、本発明の皮膚貼付用粘着シートでは、水和反応による刺激を緩和することができるものであった。また、貼付時の違和感や剥がす際の痛みも少ないものであった。また、曲面追従性にも優れていた。これに対して、比較例では満足な結果が得られなかった。 These results are also shown in Table 1.
As is clear from Table 1, the pressure-sensitive adhesive sheet for skin application of the present invention can alleviate irritation caused by a hydration reaction. Moreover, there was little discomfort at the time of sticking and pain at the time of peeling. Moreover, it was excellent also in curved surface followability. On the other hand, satisfactory results were not obtained in the comparative example.

１基材フィルム
２粘着剤層
３印刷層
１０、１０’ 皮膚貼付用粘着シート DESCRIPTION OF SYMBOLS 1 Base film 2 Adhesive layer 3 Print layer 10, 10 'Adhesive sheet for skin sticking

Claims

It is a pressure-sensitive adhesive sheet for skin application used by being attached to the skin,
Inside it has the following pore diameters 10 [mu] m, and a substrate film is moisture permeability 10000g ^/ m 2 ^/ 24h or more,
An adhesive layer provided on one surface of the base film, and
For application to the skin adhesive sheet, wherein the moisture permeability of the entire skin sticking the adhesive sheet is 1000g / m 2 / ^24h or more.

The pressure-sensitive adhesive sheet for skin application according to claim 1, wherein the base film is a polyurethane film.

The adhesive sheet for skin application according to claim 1 or 2, wherein the tensile force at 20% elongation is 3 N / 25 mm or less.

The pressure-sensitive adhesive sheet for skin application according to any one of claims 1 to 3, wherein the elongation rate after elongation at 200% is 20% or less.

The pressure-sensitive adhesive sheet for skin application according to any one of claims 1 to 4, wherein the pressure-sensitive adhesive strength measured in accordance with a 180-degree peel strength test method for a JIS Z0237: 2000 test plate is 7 N / 25 mm or less.