JP2011208257A - High-strength steel for reinforcing bar and method for producing the same - Google Patents
High-strength steel for reinforcing bar and method for producing the same Download PDFInfo
- Publication number
- JP2011208257A JP2011208257A JP2010079130A JP2010079130A JP2011208257A JP 2011208257 A JP2011208257 A JP 2011208257A JP 2010079130 A JP2010079130 A JP 2010079130A JP 2010079130 A JP2010079130 A JP 2010079130A JP 2011208257 A JP2011208257 A JP 2011208257A
- Authority
- JP
- Japan
- Prior art keywords
- node
- less
- steel
- wire
- ribs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、例えば、鉄筋コンクリート構造物に使用される剪断補強筋の素材として用いて好適な高強度鉄筋用鋼材およびその製造方法に関するものである。 The present invention relates to a steel material for high-strength rebar suitable for use as a material for a shear reinforcing bar used in a reinforced concrete structure, for example, and a method for manufacturing the same.
鉄筋コンクリート構造物を補強し、その崩壊を防ぐための補強材として、剪断補強筋が使用される。剪断補強筋を使用した鉄筋コンクリート構造物では、鉄筋コンクリート構造物が剪断変形する際に、剪断補強筋が伸びて塑性変形することにより、鉄筋コンクリート構造物の変形エネルギーが剪断補強筋に吸収されて、鉄筋コンクリート構造物の崩壊が防止される。
しかし、これまでの剪断補強筋は、伸び特性という点からは必ずしも十分とは言えなかった。剪断補強筋は、曲げ加工により円形や角形等に成形されて製造されるものであり、伸び特性が良好であると、曲げ加工が容易となり、加工性の面からも大きなメリットとなる。
Shear reinforcement is used as a reinforcement for reinforcing a reinforced concrete structure and preventing its collapse. In a reinforced concrete structure using shear reinforcement, when the reinforced concrete structure undergoes shear deformation, the shear reinforcement is stretched and plastically deformed, so that the deformation energy of the reinforced concrete structure is absorbed by the shear reinforcement and the reinforced concrete structure Collapse of things is prevented.
However, conventional shear reinforcements have not always been sufficient in terms of elongation characteristics. The shear reinforcing bar is manufactured by being bent into a circular shape or a square shape, and if the elongation property is good, the bending processing becomes easy, which is a great merit in terms of workability.
また、近年では、剪断補強筋を溶接して施工することで鉄筋コンクリート構造物の補強が可能な、施工性のよい溶接閉鎖型の需要が高まっている。この溶接閉鎖型の剪断補強筋では、溶接後の強度・延性を低下させないことが大切であり、溶接部の継手伸びも重要な特性となる。通常、剪断補強筋の溶接では、フラッシュバット溶接やアプセットバット溶接と呼ばれる高能力、高生産性の抵抗溶接が利用される。
フラッシュバット溶接とは、２本の棒鋼の端面どうしを接触させ２つの端面の間に大電圧をかけ、アークの接触と短絡を繰り返して端部に溶融部を形成し、最後にこの溶融部をアプセット（据え込み変形）により排出し、２本の棒鋼の端部に接合部を形成する溶接法である。また、アプセットバット溶接とは、完全に突き合わせられた２本の棒鋼の端面の間に大電圧をかけ、抵抗発熱により端部をアプセットし２本の棒鋼の端部に接合部を形成する溶接法である。
In recent years, there has been an increasing demand for a welded closed type with good workability, which can reinforce a reinforced concrete structure by welding shear reinforcement bars. In this welded-type shear reinforcement, it is important not to lower the strength and ductility after welding, and the joint elongation of the welded portion is also an important characteristic. Usually, in the welding of shear reinforcement, high-capacity, high-productivity resistance welding called flash butt welding or upset butt welding is used.
With flash butt welding, the end faces of two steel bars are brought into contact with each other, a large voltage is applied between the two end faces, arc contact and short-circuit are repeated to form a melted part at the end, and finally this melted part is It is a welding method that discharges by upset (upsetting deformation) and forms a joint at the ends of two steel bars. Upset butt welding is a welding method in which a large voltage is applied between the end faces of two steel bars that are completely butted, the ends are upset by resistance heat generation, and a joint is formed at the ends of the two steel bars. It is.
このような剪断補強筋に用いる鉄筋用鋼材として、圧延後に焼入れや焼き戻し等の熱処理を施さなくとも強度と延性に優れ、溶接しても母材と同等レベルの引張強度や延性を有する非調質鉄筋用鋼材が知られている（例えば、特許文献１、特許文献２、特許文献３参照。）。
As a steel material for reinforcing bars used for such a shear reinforcement, it is excellent in strength and ductility without being subjected to heat treatment such as quenching and tempering after rolling, and has a tensile strength and ductility equivalent to that of the base material even if it is welded. Steel materials for quality reinforcing steel are known (see, for example, Patent Document 1,
特許文献１に記載の非調質鉄筋用鋼材は、Mo添加を必須とするため、コストが高いという問題がある。
また、特許文献２に記載の高強度鉄筋用非調質鋼材は、Tiを0.003％以上含有するため、TiＮの生成により靭性が低下する場合がある。
しかも、これらの鋼材は、低温靭性について考慮されていないため、寒冷地での使用に際して割れが発生するおそれもある。
また、これらの鋼材は圧延ままでの高い強度−延性バランスの達成を目的としているが、熱間圧延後の線材冷却履歴等のばらつきに起因した特性のばらつきが大きく、優れた特性を安定的に得ることが困難であるのが実情である。
The steel material for non-tempered rebar described in Patent Document 1 has a problem of high cost because it requires the addition of Mo.
Moreover, since the non-tempered steel material for high-strength reinforcing bars described in
Moreover, since these steel materials are not considered for low temperature toughness, there is a risk of cracking when used in cold regions.
In addition, these steel materials are intended to achieve a high strength-ductility balance as rolled, but there are large variations in properties due to variations in wire cooling history after hot rolling, etc. The reality is that it is difficult to obtain.
特許文献３に記載の非調質鉄筋用鋼材は、上記したコストや低温靭性の問題を解決できる優れた鋼材であるが、特許文献１，２に記載の鋼材と同様、延性のばらつきが大きく、曲げ加工を行う際に折れが発生する場合があるという問題がある。
The steel material for non-tempered rebar described in
一方、鉄筋コンクリート構造物における補強材として用いられる異形棒鋼には、高い引張り強度や延性だけでなく、コンクリートとの付着力が要求される。
JIS G 3112に、ＹＳ：490MPa級(SD490)までの比較的低強度の鉄筋コンクリート用棒鋼に関する規定があり、同規定では、成分組成や強度に加えて、節の平均間隔、節の高さなどが規定されている。しかしながら、当該JIS規定は、主にコンクリートとの付着力の観点からなされたものであり、一方で曲げ加工時の折損を促進する要因となる。
On the other hand, deformed steel bars used as reinforcing materials in reinforced concrete structures are required to have not only high tensile strength and ductility, but also adhesion to concrete.
JIS G 3112 has provisions for steel bars for reinforced concrete with relatively low strength up to YS: 490MPa class (SD490). In this provision, in addition to the composition and strength, the average spacing of nodes, the height of nodes, etc. It is prescribed. However, the JIS regulations are mainly made from the viewpoint of adhesion to concrete, and on the other hand, it is a factor that promotes breakage during bending.
当該JIS規定を満足する形状として、例えば図６に示すような、節２およびリブ３を有する形状の異形鉄筋１が主にSD490級以下の比較的低強度の異形鉄筋に用いられているが、このような形状の場合、曲げ加工の方向とリブ位置の関係によって、延性が大きく異なる。すなわち、図７（ａ）に示すように、鉄筋の周方向でリブ３のある位置を最内側として曲げる場合と、図７（ｂ）に示すように、鉄筋の周方向でリブ３とリブ３の間の位置を最内側として曲げる場合とでは、延性が大きく異なる。特に鋼材の高強度化に伴って、リブ３とリブ３の間の位置を最内側として曲げる場合に曲げ延性に問題が生じ、ＹＳ：785MPaを超える高強度鉄筋コンクリート用棒鋼においては、曲げ延性とコンクリート付着力の両立は困難とされてきた。
As a shape satisfying the JIS regulations, for example, a deformed reinforcing bar 1 having a
本発明は、上記の問題を有利に解決するもので、ＹＳ：785MPa以上の高強度鉄筋用鋼材であっても、延性のばらつきが小さく、しかも低温靭性に優れ、溶接しても母材と同等レベルの引張強度や延性を有し、さらにはコンクリートとの付着力にも優れた高強度鉄筋用鋼材を、その有利な製造方法と共に提案することを目的とする。 The present invention advantageously solves the above-mentioned problems, and even if it is a steel material for high-strength reinforcing steel of YS: 785 MPa or more, there is little variation in ductility, and it is excellent in low-temperature toughness and is equivalent to the base material even when welded The purpose of the present invention is to propose a high-strength steel material for reinforcing bars having a level of tensile strength and ductility, and also having excellent adhesion to concrete, together with its advantageous manufacturing method.
すなわち、本発明の要旨構成は次のとおりである。
１．質量％で、
Ｃ：0.15〜0.30％、
Si：0.05〜1.0％、
Mn：0.2〜2.5％、
Al：0.01〜1.0％、
Nb：0.001〜0.3％、
Ti：0.003％未満、
Ｐ：0.03％以下、
Ｓ：0.03％以下および
Ｎ：0.0060％未満
を含有し、さらに、
Cr：0.1〜2.0％、
Mo：0.01〜1.0％、
Ｖ：0.01〜1.0％、
Ｗ：0.01〜1.0％、
Ni：0.01〜1.0％、
Cu：0.01〜1.0％、
Co：0.01〜1.0％および
Sb：0.0010〜0.0050％
のうちから選ばれる１種または２種以上を含有する鋼組成からなり、
鋼組織が、80％以上がベイナイトで、残部がフェライト、パーライトまたはマルテンサイトの組織からなり、
円周方向に90°間隔で、線材の長手方向に連続する４本のリブを有し、該４本のリブ幅の和が該線材の公称周長の15％以上25％以下で、
該リブを接続する形の節を該線材の公称直径の40％以上70％以下の間隔で有し、該節の高さが該線材の公称直径の4.0％以上8.0％以下で、
該節の頭頂部から節底にかけての節側面傾斜部と母材表面との成す角が100°以上135°未満で、節根元部の角部のＲが（節高さ×10％）以上（節高さ×25％）未満で、該節側面傾斜部の表面粗度Ｒmaxが0.2mm以内であり、
ＹＳ：785MPa以上、ＴＳ：930MPa以上
であることを特徴とする、曲げ特性およびコンクリート密着性のバランスに優れる高強度鉄筋用鋼材。
That is, the gist configuration of the present invention is as follows.
1. % By mass
C: 0.15-0.30%
Si: 0.05-1.0%
Mn: 0.2-2.5%
Al: 0.01 to 1.0%
Nb: 0.001 to 0.3%,
Ti: less than 0.003%,
P: 0.03% or less,
S: not more than 0.03% and N: less than 0.0060%,
Cr: 0.1-2.0%
Mo: 0.01-1.0%,
V: 0.01 to 1.0%
W: 0.01-1.0%
Ni: 0.01-1.0%,
Cu: 0.01 to 1.0%,
Co: 0.01-1.0% and
Sb: 0.0010 to 0.0050%
Consisting of a steel composition containing one or more selected from
More than 80% of the steel structure is bainite, and the balance consists of ferrite, pearlite, or martensite.
It has four ribs continuous in the longitudinal direction of the wire at 90 ° intervals in the circumferential direction, and the sum of the four rib widths is 15% or more and 25% or less of the nominal circumference of the wire,
Nodes having a shape connecting the ribs at intervals of 40% to 70% of the nominal diameter of the wire, and the height of the nodes is 4.0% to 8.0% of the nominal diameter of the wire;
The angle formed by the slope of the side surface of the node from the top to the bottom of the node and the surface of the base material is 100 ° or more and less than 135 °, and the corner R of the node root is (node height × 10%) or more ( Less than 25 mm), and the surface roughness Rmax of the inclined side surface of the node is within 0.2 mm,
YS: 785 MPa or more, TS: 930 MPa or more, a high-strength steel material for rebar excellent in the balance of bending characteristics and concrete adhesion.
２．前記鋼材が、質量％で、さらに、
Ｂ：0.0005〜0.0100％
を含有し、かつ鋼中のＢ量、Ｎ量およびTi量が、次式（１）の関係を満足することを特徴とする前記１に記載の高強度鉄筋用鋼材。
Ｂ（％）≧｛Ｎ（％）／14−Ti（％）／27｝×11＋0.0005 ・・・（１）
ただし、Ｍ（％）は、Ｍ元素の含有量（質量％）を表わす。
2. The steel material is in mass%, and
B: 0.0005-0.0100%
2. The steel material for high-strength reinforcing bars as described in 1 above, wherein the B content, the N content and the Ti content in the steel satisfy the relationship of the following formula (1).
B (%) ≧ {N (%) / 14−Ti (%) / 27} × 11 + 0.0005 (1)
However, M (%) represents content (mass%) of M element.
３．質量％で、
Ｃ：0.15〜0.30％、
Si：0.05〜1.0％、
Mn：0.2〜2.5％、
Al：0.01〜1.0％、
Nb：0.001〜0.3％、
Ti：0.003％未満、
Ｐ：0.03％以下、
Ｓ：0.03％以下および
Ｎ：0.0060％未満
を含有し、さらに、
Cr：0.1〜2.0％、
Mo：0.01〜1.0％、
Ｖ：0.01〜1.0％、
Ｗ：0.01〜1.0％、
Ni：0.01〜1.0％、
Cu：0.01〜1.0％、
Co：0.01〜1.0％および
Sb：0.0010〜0.0050％
のうちから選ばれる１種または２種以上を含有する組成からなる鋼素材を、加熱温度：Ａc3点〜1350℃、圧延終了温度：Ａr3点以上の条件で熱間圧延し、該熱間圧延の最終仕上圧延時に下記を満足するリブおよび節を形成し、その後500〜800℃の温度範囲を0.3℃/ｓ以上、25℃/ｓ以下の冷却速度で冷却することを特徴とする高強度鉄筋用鋼材の製造方法。
記
リブ：円周方向に90°間隔で線材の長手方向に連続する４本のリブを有し、該４本のリブ幅の和は該線材の公称周長の15％以上25％以下。
節：円周方向に隣り合うリブを接続する形の節であり、線材の長さ方向に該線材の公称直径の40％以上70％以下の間隔で配置、節の高さは該線材の公称直径の4.0％以上8.0％以下、節の頭頂部から節底にかけての節側面傾斜部と母材表面との成す角は100°以上135°未満、節根元部の角部のＲは（節高さ×10％）以上（節高さ×25％）未満、該節側面傾斜部の表面粗度Ｒmaxは0.2mm以内。
3. % By mass
C: 0.15-0.30%
Si: 0.05-1.0%
Mn: 0.2-2.5%
Al: 0.01 to 1.0%
Nb: 0.001 to 0.3%,
Ti: less than 0.003%,
P: 0.03% or less,
S: not more than 0.03% and N: less than 0.0060%,
Cr: 0.1-2.0%
Mo: 0.01-1.0%,
V: 0.01 to 1.0%
W: 0.01-1.0%
Ni: 0.01-1.0%,
Cu: 0.01 to 1.0%,
Co: 0.01-1.0% and
Sb: 0.0010 to 0.0050%
A steel material having a composition containing one or more selected from the above is hot-rolled under conditions of heating temperature: Ac 3 points to 1350 ° C., rolling end temperature: Ar 3 points or more, High strength, characterized in that ribs and nodes satisfying the following conditions are formed during the final finish rolling of the rolling, and then the temperature range of 500 to 800 ° C. is cooled at a cooling rate of 0.3 ° C./s or more and 25 ° C./s or less. A method for manufacturing steel for reinforcing bars.
Rib: Four ribs continuous in the longitudinal direction of the wire at 90 ° intervals in the circumferential direction, and the sum of the widths of the four ribs is 15% or more and 25% or less of the nominal circumference of the wire.
Knots: Knots in the form of connecting ribs adjacent in the circumferential direction, arranged in the length direction of the wire at intervals of 40% to 70% of the nominal diameter of the wire, and the height of the knot is the nominal height of the wire 4.0 to 8.0% of the diameter, the angle between the node side slope from the top of the node to the node bottom and the surface of the base material is 100 ° to less than 135 °, and R at the corner of the node root is Thickness x 10%) or more (node height x 25%) and the surface roughness Rmax of the node side inclined portion is within 0.2 mm.
４．前記鋼素材が、質量％で、さらに、
Ｂ：0.0005〜0.0100％
を含有し、かつ鋼中のＢ量、Ｎ量およびTi量が、次式（１）の関係を満足することを特徴とする前記３に記載の高強度鉄筋用鋼材の製造方法。
Ｂ（％）≧｛Ｎ（％）／14−Ti（％）／27｝×11＋0.0005・・・（１）
ただし、Ｍ（％）は、Ｍ元素の含有量（質量％）を表わす。
4). The steel material is in mass%, and
B: 0.0005-0.0100%
And the amount of B, N and Ti in the steel satisfy the relationship of the following formula (1):
B (%) ≧ {N (%) / 14−Ti (%) / 27} × 11 + 0.0005 (1)
However, M (%) represents content (mass%) of M element.
５．前記３または４に記載の製造方法で製造された鉄筋用鋼材に対し、鉄筋コンクリート施工に使用するための曲げ加工前に、次式（２）を満たす保持温度Ｔ（Ｋ）、保持時間ｔ（秒）での保持を行うことを特徴とする高強度鉄筋用鋼材の製造方法。
Ｔ×logｔ≧1500 ・・・（２）
5. The holding temperature T (K) and the holding time t (seconds) satisfying the following formula (2) before bending for use in reinforced concrete construction on the steel for reinforcing bars manufactured by the manufacturing method described in 3 or 4 above. The method of manufacturing a steel material for high-strength reinforcing steel,
T × logt ≧ 1500 (2)
本発明によれば、強度、延性が高く、延性のばらつきが小さく、曲げ加工特性の異方性が小さく、低温靭性に優れ、溶接した場合の母材伸びや溶接継手伸びに優れ、さらにはコンクリートとの付着力にも優れた鋼材を、必ずしも高価な合金元素を添加することなく低コストで得ることができる。 According to the present invention, the strength and ductility are high, the variation in ductility is small, the anisotropy of bending properties is small, the low temperature toughness is excellent, the base material elongation and weld joint elongation are excellent when welded, and the concrete The steel material having excellent adhesion can be obtained at a low cost without necessarily adding an expensive alloy element.
以下、本発明を具体的に説明する。
まず、本発明において鋼材の成分組成を前記の範囲に限定した理由について説明する。以下の説明において％で示す単位は、特に記載がある場合以外は全て質量％である。
Ｃ：0.15〜0.30％
Ｃは、目的とする強度を確保するために0.15％以上の添加を必要とする。しかし、0.30％を超えて添加すると溶接性や延性が劣化するので、0.30％以下とする。
Hereinafter, the present invention will be specifically described.
First, the reason why the component composition of the steel material is limited to the above range in the present invention will be described. In the following description, all units shown in% are% by mass unless otherwise specified.
C: 0.15-0.30%
C needs to be added in an amount of 0.15% or more in order to ensure the intended strength. However, if added over 0.30%, weldability and ductility deteriorate, so 0.30% or less.
Si：0.05〜1.0％
Siは、鋼の脱酸および強化を図るために添加するが、0.05％未満ではその添加効果に乏しく、一方1.0％を超えて添加すると継手曲げ性を低下させるので、Si含有量は0.05〜1.0％の範囲とする。
Si: 0.05-1.0%
Si is added to deoxidize and strengthen the steel, but if less than 0.05%, the effect of addition is poor, while if added over 1.0%, the joint bendability is lowered, so the Si content is 0.05 to 1.0. % Range.
Mn：0.2〜2.5％
Mnは、焼入性を確保し目標の強度を得るために、少なくとも0.2％の添加が必要である。しかし、2.5％を超えて添加すると延性や溶接性の劣化を招くため、2.5％以下とする。
Mn: 0.2-2.5%
Mn needs to be added in an amount of at least 0.2% in order to ensure hardenability and obtain the target strength. However, adding over 2.5% causes deterioration of ductility and weldability, so 2.5% or less.
Al：0.01〜1.0％
Alは、鋼の脱酸のために添加するが、0.01％以下ではその効果が少なく、一方1.0％を超えて添加すると継手曲げ性を低下させるため、Al含有量は0.01〜1.0％の範囲とする。
Al: 0.01 to 1.0%
Al is added for deoxidation of steel, but its effect is small at 0.01% or less, while adding over 1.0% lowers joint bendability, so the Al content is in the range of 0.01 to 1.0%. To do.
Nb：0.001〜0.3％
Nbは、鋼中に微細な炭窒化物を形成し、母材の強度上昇のみならず、溶接熱影響部の軟化抑制に有効な元素である。また、析出炭窒化物がTiＮと比較してもさらに微細であるため、靭性への悪影響も小さい。しかし、添加量が0.001％に満たないと十分な添加効果が得られず、一方0.3％を超えるとNb炭窒化物であっても溶接熱影響部の靭性劣化が著しくなるため、Nb含有量は0.001〜0.3％の範囲とする。
Nb: 0.001 to 0.3%
Nb is an element that forms fine carbonitrides in steel and is effective not only in increasing the strength of the base material but also in suppressing softening of the weld heat affected zone. Further, since the precipitated carbonitride is finer than TiN, the adverse effect on toughness is small. However, if the addition amount is less than 0.001%, a sufficient addition effect cannot be obtained. On the other hand, if it exceeds 0.3%, the toughness deterioration of the weld heat-affected zone becomes remarkable even with Nb carbonitride, so the Nb content is The range is 0.001 to 0.3%.
Ti：0.003％未満
Tiは、Ｎを固定し粗大な窒化物（TiＮ）を生成し、靭性低下を促進するので、基本的には添加しないことが望ましいが、0.003％未満であれば許容される。
Ti: Less than 0.003%
Ti fixes N and generates coarse nitrides (TiN) and promotes toughness reduction. Therefore, it is basically desirable not to add Ti, but it is acceptable if it is less than 0.003%.
Ｐ：0.03％以下
Ｐは、鋼材を脆化させ、母材と溶接後の延性および低温靭性を劣化させるので、基本的には含有させないことが望ましいが、不可避的不純物として0.03％以下であれば許容し得る。
P: 0.03% or less P is brittle steel material and deteriorates ductility and low-temperature toughness after welding with the base metal. Therefore, it is basically preferable not to include P, but if it is 0.03% or less as an unavoidable impurity Acceptable.
Ｓ：0.03％以下
Ｓは、鋼中でMnなどの金属と結合して粗大な硫化物を形成し、母材と溶接後の延性および低温靭性を劣化させるので、基本的には含有させないことが望ましいが、不可避的不純物として0.03％以下であれば許容し得る。
S: 0.03% or less S is combined with metals such as Mn in steel to form coarse sulfides, which deteriorates ductility and low-temperature toughness after welding with the base metal. Although desirable, 0.03% or less as an inevitable impurity is acceptable.
Ｎ：0.0060％未満
Ｎは、不可避的不純物であり、0.0060％以上含有された場合、溶接時にTiＮ、ＶＮ等の粗大な析出物を形成し、溶接継手の引張強度および曲げ性を低下させるため、0.0060％未満とする。
N: Less than 0.0060% N is an unavoidable impurity. When 0.0060% or more is contained, coarse precipitates such as TiN and VN are formed during welding, and the tensile strength and bendability of the welded joint are reduced. Less than 0.0060%.
Cr：0.1〜2.0％、Mo：0.01〜1.0％、Ｖ：0.01〜1.0％、Ｗ：0.01〜1.0％、Ni：0.01〜1.0％、Cu：0.01〜1.0％、Co：0.01〜1.0％およびSb：0.0010〜0.0050％のうちから選ばれる１種または２種以上
これらの元素は、鋼材の強度−延性のバランスの向上に有効であり、必要に応じて１種または２種以上を選択して添加することができる。
Cr: 0.1-2.0%, Mo: 0.01-1.0%, V: 0.01-1.0%, W: 0.01-1.0%, Ni: 0.01-1.0%, Cu: 0.01-1.0%, Co: 0.01-1.0% and Sb : One or more elements selected from 0.0010 to 0.0050% These elements are effective in improving the balance between strength and ductility of steel materials, and one or more elements are selected and added as necessary. can do.
Cr：0.1〜2.0％
Crは、焼入性を高める元素であり、強度を上昇させるために添加することができ、その際の添加量は0.1％以上とすることが好ましい。しかし、2.0％を超えて添加すると焼入性が過大となり延性や溶接性を劣化させるので、添加する場合は2.0％以下とする。
Cr: 0.1-2.0%
Cr is an element that enhances hardenability and can be added to increase the strength, and the amount added is preferably 0.1% or more. However, if added over 2.0%, the hardenability becomes excessive and the ductility and weldability are deteriorated.
Mo：0.01〜1.0％
Moは、焼入性を高めるとともに、組織を改善して延性を向上させるために有用な元素であり、0.01％以上添加することが好ましい。しかし、1.0％を超えて添加するとコストが上昇し、また溶接性が劣化する原因となるため、添加する場合は1.0％以下とする。
Mo: 0.01-1.0%
Mo is an element useful for enhancing the hardenability and improving the structure to improve the ductility, and is preferably added in an amount of 0.01% or more. However, if added over 1.0%, the cost will increase and weldability will be deteriorated.
Ｖ：0.01〜1.0％
Ｖは、鋼材の焼入性を向上させると共に、炭窒化物の形成により母材の強度を上昇させ、さらに溶接熱影響部の軟化抑制にも有効な元素である。しかし、添加量が0.01％未満では十分な効果が得られず、一方1.0％を超えると著しく溶接熱影響部の靭性を劣化させるので、、Ｖを添加する場合は0.01％以上、1.0％以下とする。
V: 0.01 to 1.0%
V is an element that improves the hardenability of the steel material, increases the strength of the base material by forming carbonitrides, and is also effective in suppressing softening of the weld heat affected zone. However, if the addition amount is less than 0.01%, a sufficient effect cannot be obtained. On the other hand, if it exceeds 1.0%, the toughness of the weld heat affected zone is remarkably deteriorated. Therefore, when V is added, it is 0.01% or more and 1.0% or less. To do.
Ｗ：0.01〜1.0％
Ｗは、焼入性を向上させる元素である。強度の確保が必要な場合に0.01％以上添加することができるが、高価であることに加えて、過剰に添加すると溶接性を劣化させるので、添加する場合は0.01〜1.0％の範囲とする。
W: 0.01-1.0%
W is an element that improves hardenability. Although it is possible to add 0.01% or more when it is necessary to ensure strength, in addition to being expensive, weldability deteriorates if added excessively, so when added, the content is made 0.01 to 1.0%.
Ni：0.01〜1.0％
Niは、焼入性を向上させる元素である。強度の確保が必要な場合に0.01％以上添加することができるが、高価であることに加えて、過剰に添加すると溶接性を劣化させるので、添加する場合は0.01〜1.0％の範囲とする。
Ni: 0.01-1.0%
Ni is an element that improves hardenability. Although it is possible to add 0.01% or more when it is necessary to ensure strength, in addition to being expensive, weldability deteriorates if added excessively, so when added, the content is made 0.01 to 1.0%.
Cu：0.01〜1.0％
Cuは、焼入性を高め、フェライト相を析出強化することにより強度を向上させる元素である。強度を確保する必要のある場合に添加することができるが、0.01％未満では効果が不十分であり、一方1.0％を超えると熱間加工性や溶接性を阻害するため、添加する場合は0.01〜1.0％の範囲とする。
Cu: 0.01-1.0%
Cu is an element that improves hardenability and improves strength by precipitation strengthening of the ferrite phase. It can be added when it is necessary to ensure strength, but if it is less than 0.01%, the effect is insufficient, while if it exceeds 1.0%, hot workability and weldability are hindered. The range is -1.0%.
Co：0.01〜1.0％
Coは、焼入性を向上させ強度の向上に有効な元素である。強度の確保が必要な場合に0.01％以上添加することができるが、過剰に添加しても効果が飽和するため、添加する場合は1.0％以下とする。
Co: 0.01-1.0%
Co is an element that improves hardenability and is effective in improving strength. When it is necessary to ensure strength, it can be added in an amount of 0.01% or more. However, the effect is saturated even if it is added excessively.
Sb：0.0010〜0.0050％
Sbは、熱間圧延前の加熱時のオーステナイト粒径粗大化を抑制すると共に、加熱時の表層脱炭を抑制する作用を有しており、熱間圧延時の加熱温度の上昇が必要な場合に添加することができる。しかし、添加量が0.0010％未満では十分な効果が得られず、一方0.0050％を超えると効果が飽和すると共に熱間加工性および低温靭性の低下を招くため、添加する場合は0.0010〜0.0050％の範囲とする。
Sb: 0.0010 to 0.0050%
Sb has the effect of suppressing the austenite grain size coarsening during heating before hot rolling and suppressing surface layer decarburization during heating, and it is necessary to increase the heating temperature during hot rolling Can be added. However, if the addition amount is less than 0.0010%, a sufficient effect cannot be obtained. On the other hand, if it exceeds 0.0050%, the effect is saturated and hot workability and low temperature toughness are reduced. Range.
上記以外の残部は、Feおよび上記以外の不可避的不純物である。 The balance other than the above is Fe and inevitable impurities other than the above.
以上、必須成分および抑制成分について説明したが、本発明では、さらに高い強度を得るためにＢを添加することができる。
Ｂ：0.0005〜0.0100％
Ｂは、焼入性を向上させる元素であり、母材の強度上昇を特に必要とする場合に、添加が有効である。強度上昇効果を得るためには0.0005％以上の添加を必要とするが、0.0100％を超えて添加しても焼入性向上効果は飽和し、溶接性が劣化する原因にもなるため、Ｂを添加する場合には0.0005〜0.0100％の範囲とする。また、強度上昇効果を得るためには、Ｂを鋼中に固溶させる必要がある。
As described above, the essential component and the suppressing component have been described. In the present invention, B can be added to obtain higher strength.
B: 0.0005-0.0100%
B is an element that improves hardenability, and addition is effective when it is particularly necessary to increase the strength of the base material. Addition of 0.0005% or more is required to obtain the strength increase effect, but even if added over 0.0100%, the hardenability improving effect is saturated and the weldability is deteriorated. When adding, it is made into the range of 0.0005-0.0100%. Further, in order to obtain the strength increasing effect, it is necessary to dissolve B in the steel.
しかし、鋼中に固溶Ｎが存在する場合には鋼中のＢはＢＮの形成に消費され、ＢＮとしてＢが鋼中に存在する場合には、焼入性の向上に寄与しない。しかし、Tiが存在すると、その存在量に応じて鋼中のＮをTiＮとして固定し、TiＮとなったＮはＢＮの形成に寄与しなくなる。したがって、Ｂを添加する場合にはＢＮの形成に消費される以上の量を添加する必要があり、鋼中のＢ量とＮ量とTi量との間て、次式（１）で示される関係を満足させることが必要である。
Ｂ（％）≧｛Ｎ（％）／14−Ti（％）／27｝×11＋0.0005・・・（１）
なお、上記（１）式の各元素記号は質量％での各元素の含有量である。
However, when solid solution N is present in the steel, B in the steel is consumed for the formation of BN, and when B is present in the steel as BN, it does not contribute to the improvement of hardenability. However, if Ti is present, N in the steel is fixed as TiN according to the amount of Ti present, and N that has become TiN does not contribute to the formation of BN. Therefore, when adding B, it is necessary to add more than is consumed for the formation of BN, and the following formula (1) shows between the B content, the N content and the Ti content in the steel. It is necessary to satisfy the relationship.
B (%) ≧ {N (%) / 14−Ti (%) / 27} × 11 + 0.0005 (1)
In addition, each element symbol of the said (1) Formula is content of each element in the mass%.
次に、本発明の鋼材の金属組織について説明する。
本発明の鋼材の金属組織は、実質的にベイナイト組織からなる。実質的にベイナイト組織からなるとは、本発明の作用効果をなくさない限り、ベイナイト以外の組織を含有していても、本発明の範囲に含まれることを意味する。とはいえ、ベイナイト以外の組織を含有すると、強度と延性のバランスが低下するため、ベイナイト以外の組織は少ないほど望ましい。しかし、ベイナイト以外の組織の割合が低い場合は影響を無視できるため、ベイナイトの体積比率は80％以上であればよい。ベイナイト以外の組織とは、フェライト、パーライトおよび／またはマルテンサイト等であるが、かようなマルテンサイトやフェライト、パーライトを含有する場合には、これらの体積比率はそれぞれ10％未満とすることが望ましい。
Next, the metal structure of the steel material of the present invention will be described.
The metal structure of the steel material of the present invention substantially consists of a bainite structure. The expression “substantially consisting of a bainite structure” means that the composition is included in the scope of the present invention even if it contains a structure other than bainite unless the effects of the present invention are lost. However, the inclusion of a structure other than bainite lowers the balance between strength and ductility, so the smaller the structure other than bainite, the better. However, since the influence can be ignored when the ratio of the structure other than bainite is low, the volume ratio of bainite may be 80% or more. The structure other than bainite is ferrite, pearlite and / or martensite, etc., but when such martensite, ferrite and pearlite are contained, these volume ratios are preferably less than 10% respectively. .
また、本発明の鋼材においては、TiＮは析出させないことが望ましいが、TiＮが析出する場合は、その粒径の最大径を10μm 以下とすることが望ましい。 Further, in the steel material of the present invention, it is desirable not to precipitate TiN, but when TiN is precipitated, it is desirable that the maximum particle size is 10 μm or less.
さらに、発明者は、以下の規定を満たす異形形状を有する鋼材が、鋼材強度、曲げ延性、さらにはコンクリート付着力のバランスに優れることを知見した。
以下、図１、図２を参照して、本発明の鉄筋の異形形状を特定した理由について説明する。なお、図１は、本発明の鉄筋用鋼材の形状を示す斜視図であり、図２は本発明の鉄筋用鋼材の長さ方向断面を示す断面図である。また、図中、符号１で鉄筋を示し、２は節、３はリブ、４は母材表面である。
Furthermore, the inventor has found that a steel material having an irregular shape that satisfies the following regulations is excellent in balance of steel material strength, bending ductility, and concrete adhesion force.
Hereinafter, with reference to FIG. 1, FIG. 2, the reason which specified the deformed shape of the reinforcing bar of this invention is demonstrated. FIG. 1 is a perspective view showing the shape of a steel material for reinforcing bars of the present invention, and FIG. 2 is a cross-sectional view showing a longitudinal section of the steel material for reinforcing bars of the present invention. In the figure, reference numeral 1 denotes a reinforcing bar, 2 is a node, 3 is a rib, and 4 is a base material surface.
円周方向に90°間隔で、線材の長手方向に連続する４本のリブ
図１に示すように、鉄筋１の長手方向に連続するリブ３の本数を90°間隔の４本とすることにより、曲げ加工時における延性の曲げ方向異方性を大幅に低減することが可能になる。
また、リブ３の本数を増やすことにより、応力集中源を大きく増大させることなく鋼材体積比表面積を増大することが可能となる。比表面積の増大に伴い、表層部からの鋼中水素の放出が容易となる。特に再加熱によって脱水素を行う際には、加熱速度を促進する効果も加わり、脱水素に極めて有利な作用を有する。
ここに、リブ本数が３本以下では上記効果が十分に得られず、他方５本以上のリブを設けることは熱間圧延による形状形成が困難となることに加え、リブ間へのコンクリート流入を阻害してコンクリート付着力を低下させるため、リブ本数は90°間隔で４本とすることが必要である。
Four ribs continuous in the longitudinal direction of the wire at 90 ° intervals in the circumferential direction As shown in FIG. 1, the number of
Further, by increasing the number of
Here, if the number of ribs is 3 or less, the above effect cannot be obtained sufficiently. On the other hand, providing 5 or more ribs makes it difficult to form a shape by hot rolling, and also causes the inflow of concrete between the ribs. In order to inhibit and reduce the adhesion of concrete, the number of ribs must be 4 at 90 ° intervals.
４本のリブ幅の和：線材の公称周長の15％以上25％以下
リブ３の幅ｗの和（＝４ｗ）が線材の公称周長（＝母材径Ｄ×π）の15％に満たないと、リブの曲げ延性の改善効果が十分に得られず、一方25％を超えるとコンクリート付着力が大幅に低下するため、４本のリブ幅の和は公称周長の15％以上25％以下の範囲とした。
The sum of the widths of the four ribs: 15% to 25% of the nominal circumference of the wire rod The sum of the widths w of the ribs 3 (= 4w) is 15% of the nominal circumference of the wire rod (= base material diameter D × π) Otherwise, the effect of improving the rib ductility will not be obtained sufficiently, while if it exceeds 25%, the adhesive strength of the concrete will be greatly reduced, so the sum of the four rib widths will be 15% or more of the nominal circumference 25 % Or less.
リブを接続する形の節の間隔：線材の公称直径の40％以上70％以下
本発明の鉄筋用鋼材は、図１に示すように、隣合うリブ３、３を接続する節２を鉄筋用鋼材の長手方向に沿って間隔を置いて複数配置する。節２の存在は、コンクリート付着力を大きく増大させる一方、曲げ加工の際にはその根元部分２ｂが応力集中源として作用し、折損を促進する弊害がある。図２は、本発明の鉄筋用鋼材の長手方向断面を示す図である。節２の間隔Ｌが線材の公称直径Ｄの40％未満の場合、節の根元部分２ｂが応力集中源として作用し、一方70％を超えるとコンクリート付着力が大きく低下する。
Interval between nodes in the form of connecting ribs: 40% or more and 70% or less of the nominal diameter of the wire material As shown in FIG. A plurality are arranged at intervals along the longitudinal direction of the steel material. The presence of the
節の高さ：線材の公称直径の4.0％以上、8.0％以下
節高さｔ（図２参照）が、公称直径Ｄの4.0％未満ではコンクリート付着力が大きく低下し、一方8.0％を超えると、曲げ加工の際節の根元部分２ｂに発生する曲げ応力が大きくなり、当該根元部２ｂに亀裂を生じ、折損を発生しやすくなるため、節の高さは公称直径の4.0％以上、8.0％以下とする。
Node height: 4.0% or more and 8.0% or less of the nominal diameter of the wire If the node height t (see Fig. 2) is less than 4.0% of the nominal diameter D, the concrete adhesion will be greatly reduced, while if it exceeds 8.0% The bending stress generated at the
節の頭頂部から節底にかけて節側面傾斜部と母材表面との成す角θ：100°以上135°未満
節の頂部から節底に節側面傾斜部２ａ（図２参照）と母材表面４との成す角θが100°未満の場合、曲げ加工の際節の根元部２ｂに発生する曲げ応力が大きくなり、当該根元部２ｂに亀裂を生じ、折損を発生しやすくなる。一方、135°を超えるとコンクリート付着力が大きく低下するため、節側面傾斜部と母材表面との成す角θは100°以上135°未満とした。
Angle θ between the node side inclined portion and the base material surface from the top of the node to the node bottom: 100 ° or more and less than 135 ° Nodal side inclined portion 2a (see FIG. 2) and base material surface 4 from the top of the node to the node bottom Is less than 100 °, the bending stress generated at the
節根元部の角部のＲ：（節高さ×10％）以上（節高さ×25％）未満
節根元部２ｂの角部のＲを（節高さ×10％）以上とすると、10％未満の場合と比較して節根元部の応力集中が大幅に緩和され、特にリブ45°方向への曲げ（図５（ｂ）参照）の際の延性が向上し、曲げ延性の異方性が大幅に低減される。一方、角部のＲが（節高さ×25％）を超えるとコンクリート付着力の低下を招くため、角部のＲは（節高さ×10％）以上（節高さ×25％ ）未満の範囲とした。
R at the corner of the node root: (node height x 10%) or more and less than (node height x 25%) When the corner R of the
節側面傾斜部の表面粗度Ｒmax：0.2mm以内
節２の頭頂部から節底にかけての傾斜部２ａ（図２参照）の表面粗度がＲmaxで0.2mmを超えると、曲げ加工の際に新たな応力集中源を導入することとなり、曲げ延性を大幅に低下させるので、節側面傾斜部の表面粗度はＲmaxで0.2mm以内とした。
Surface roughness Rmax of the node side inclined part: within 0.2mm If the surface roughness of the inclined part 2a (see Fig. 2) from the top of the
次に、本発明の鉄筋用鋼材を得るのに好適な鉄筋用鋼材の製造方法について説明する。
本発明の鋼材は、前述した成分組成を有する素材を用い、加熱温度：Ａc3点〜1350℃、圧延終了温度：Ａr3点以上の条件で熱間圧延を行い、該熱間圧延の最終仕上圧延時に下記を満足するリブおよび節を形成し、その後500〜800℃の温度範囲を0.3℃/ｓ以上、25℃/ｓ以下の冷却速度で冷却することにより得ることができる。
記
リブ：円周方向に90°間隔で線材の長手方向に連続する４本のリブを有し、該４本のリブ幅の和は該線材の公称周長の15％以上25％以下。
節：円周方向に隣り合うリブを接続する形の節であり、線材の長さ方向に該線材の公称直径の40％以上70％以下の間隔で配置、節の高さは該線材の公称直径の4.0％以上8.0％以下、節の頭頂部から節底にかけての節側面傾斜部と母材表面との成す角は100°以上135°未満、節根元部の角部のＲは（節高さ×10％）以上（節高さ×25％）未満、該節側面傾斜部の表面粗度Ｒmaxは0.2mm以内。
Next, the manufacturing method of the steel material for rebar suitable for obtaining the steel material for rebar of this invention is demonstrated.
The steel material of the present invention uses the material having the above-described component composition, is subjected to hot rolling under conditions of heating temperature: Ac 3 points to 1350 ° C., rolling end temperature: Ar 3 points or more, and final finish of the hot rolling Ribs and joints that satisfy the following conditions are formed during rolling, and thereafter, a temperature range of 500 to 800 ° C. is cooled at a cooling rate of 0.3 ° C./s or more and 25 ° C./s or less.
Rib: Four ribs continuous in the longitudinal direction of the wire at 90 ° intervals in the circumferential direction, and the sum of the widths of the four ribs is 15% or more and 25% or less of the nominal circumference of the wire.
Knots: Knots in the form of connecting ribs adjacent in the circumferential direction, arranged in the length direction of the wire at intervals of 40% to 70% of the nominal diameter of the wire, and the height of the knot is the nominal height of the wire 4.0 to 8.0% of the diameter, the angle between the node side slope from the top of the node to the node bottom and the surface of the base material is 100 ° to less than 135 °, and R at the corner of the node root is Thickness x 10%) or more (node height x 25%) and the surface roughness Rmax of the node side inclined portion is within 0.2 mm.
以下、各製造工程における限定理由について説明する。
加熱温度：Ａc3点〜1350℃
熱間圧延における加熱温度がＡc3点未満では、加熱後に引き続いて行われる圧延において加工性が悪化するだけでなく、鋼のミクロ組織中に伸長したフェライトが残留して伸びが低下する。一方、加熱温度が1350℃超になると、オーステナイト粒の粗大化に伴って延性が低下し、また燃料原単位の上昇にもつながる。
Hereinafter, the reason for limitation in each manufacturing process will be described.
Heating temperature: Ac 3 points to 1350 ° C
When the heating temperature in the hot rolling is less than Ac 3 point, not only the workability is deteriorated in the subsequent rolling after the heating, but also the elongated ferrite remains in the microstructure of the steel and the elongation is lowered. On the other hand, when the heating temperature exceeds 1350 ° C., the ductility decreases as the austenite grains become coarser, and the fuel consumption rate increases.
圧延終了温度：Ａr3点以上
熱間圧延における圧延終了温度がＡr3点未満では、変形抵抗の増大と変形能低下により圧延が困難になるだけでなく、圧延直後のフェライト生成が促進され、十分なベイナイト分率を得ることが困難になるという問題が生じる。従って、熱間圧延における圧延終了温度はＡr3点以上とした。
Rolling end temperature: Ar 3 point or higher If the rolling end temperature in hot rolling is less than Ar 3 point, not only rolling becomes difficult due to an increase in deformation resistance and a decrease in deformability, but also ferrite formation immediately after rolling is promoted and sufficient. This causes a problem that it is difficult to obtain a high bainite fraction. Therefore, the rolling end temperature in the hot rolling is set to Ar 3 points or more.
熱間圧延の最終仕上圧延時に所望のリブおよび節を形成する。
本発明に従うリブや節を形成するには、できるだけ温度が高い方が好ましいので、本発明では、熱間圧延の最終仕上圧延時にリブおよび節を形成するものとした。
Desired ribs and nodes are formed during the final finish rolling of the hot rolling.
In order to form ribs and nodes according to the present invention, it is preferable that the temperature is as high as possible. Therefore, in the present invention, the ribs and nodes are formed during the final finish rolling of hot rolling.
500〜800℃の温度範囲を0.3℃/ｓ以上、25℃/ｓ以下の冷却速度で冷却する
熱間圧延後、500〜800℃の温度範囲における冷却速度が0.3℃/ｓ未満では、フェライトの組織分率が増加し、一方25℃/ｓ超の冷却速度では島状マルテンサイトの組織分率が増加し、いずれも強度−伸びのバランスが低下する。
なお、上記した制御冷却を行うべき温度範囲を500〜800℃の範囲としたのは、この温度範囲がフェライトの生成抑制とベイナイトの生成促進を目的とする変態制御にとって有効だからである。
Cool at a temperature range of 500-800 ° C at a cooling rate of 0.3 ° C / s to 25 ° C / s. After hot rolling, if the cooling rate in the temperature range of 500-800 ° C is less than 0.3 ° C / s, On the other hand, at a cooling rate of more than 25 ° C./s, the tissue fraction of island martensite increases and the balance between strength and elongation decreases.
The reason why the temperature range for the controlled cooling described above is set to a range of 500 to 800 ° C. is that this temperature range is effective for transformation control for the purpose of suppressing the formation of ferrite and promoting the formation of bainite.
かくして、本発明で所期した、強度、延性が高く、延性のばらつきが小さく、曲げ加工特性の異方性が小さく、低温靭性に優れ、溶接した場合の母材伸びや溶接継手伸びに優れ、さらにはコンクリートとの付着強度にも優れた鋼材を得ることができる。 Thus, as expected in the present invention, the strength and ductility are high, the variation in ductility is small, the anisotropy of bending properties is low, the low temperature toughness is excellent, and the base metal elongation and weld joint elongation are excellent when welded. Furthermore, a steel material having excellent adhesion strength with concrete can be obtained.
また、本発明では、上記のようにして得た鉄筋用鋼材に対し、鉄筋コンクリート施工に使用するための曲げ加工を行う前に、次式（２）を満たす保持温度Ｔ（Ｋ）、保持時間ｔ（秒）での保持を行うことにより、ベイナイトの体積比率が80％以上の組織を有し、残留水素濃度が0.3ppm以下であって、強度−延性バランスや特性のばらつきをより一層改善することができる。
Ｔ×logｔ≧1500 ・・・（２）
Moreover, in this invention, before performing the bending process for using for a reinforced concrete construction with respect to the steel material for reinforcing bars obtained by the above, holding temperature T (K) and holding time t which satisfy | fill following Formula (2). (Seconds) to maintain the structure with a bainite volume ratio of 80% or more and a residual hydrogen concentration of 0.3 ppm or less to further improve the strength-ductility balance and variation in properties. Can do.
T × logt ≧ 1500 (2)
鋼中の残留水素の放出挙動は、温度と時間の関数で表すことが可能であり、保持温度に応じて必要な保持時間は異なっている。上記（２）式を満足する保持温度（Ｋ）−保持時間（秒）の履歴を経ることで、目標とする鋼中の残留水素濃度を0.3ppm以下まで低減することが可能となる。
上記（２）式を満足させるためには、例えば150℃で５時間の熱処理（423×log18000≒1800＞1500）をすることや、あるいは平均気温20℃で20日間保持する（293×log1728000≒1828＞1500）など、種々の方法が可能である。50〜450℃の温度域で30分以上保持することが、一つの目安である。ただし、保持温度が450℃超になると、ベイナイトおよびマルテンサイトの焼戻しが進行しすぎて、強度が低下するため、上記（２）式における保持温度Ｔは450℃以下とすることが好ましい。より好ましくは400℃以下である。なお、気温の高い場所で鋼材を保管する場合は、かような加熱工程は不要であり、鋼材製造後の保管期間の管理のみで所望の効果を得ることが可能である。
The release behavior of residual hydrogen in the steel can be expressed as a function of temperature and time, and the required holding time differs depending on the holding temperature. By passing through the history of holding temperature (K) −holding time (seconds) that satisfies the above formula (2), it is possible to reduce the target residual hydrogen concentration in the steel to 0.3 ppm or less.
In order to satisfy the above formula (2), for example, heat treatment is performed at 150 ° C. for 5 hours (423 × log18000≈1800> 1500) or held at an average temperature of 20 ° C. for 20 days (293 × log1728000≈1828) Various methods are possible, such as> 1500). One guideline is to maintain the temperature in the temperature range of 50 to 450 ° C. for 30 minutes or more. However, when the holding temperature exceeds 450 ° C., tempering of bainite and martensite proceeds excessively and the strength decreases, so the holding temperature T in the above formula (2) is preferably set to 450 ° C. or less. More preferably, it is 400 ° C. or lower. Note that when the steel material is stored in a place where the temperature is high, such a heating step is not necessary, and it is possible to obtain a desired effect only by managing the storage period after manufacturing the steel material.
上記以外の製造工程は特に限定されず、通常の鉄筋の製造工程を用いることができる。
ここで、前述したように、鉄筋用鋼材にリブおよび節を形成させるのに好適な製造法について説明する。リブおよび節は、上述した熱間圧延の最終仕上圧延時に形成させる。この方法は、圧延に使用するロールの圧下面となるロール周面に節およびリブを形成するための溝を設けておくことで、該溝への素材の噛み出しにより節およびリブを形成する、あるいは、４ロール圧延機を用いて、節はロールの圧下面となるロール周面に設けた溝により、一方リブは隣り合うロール間の間隙への噛み出しにより形成することができる。
The manufacturing process other than the above is not particularly limited, and a normal manufacturing process for reinforcing bars can be used.
Here, as described above, a manufacturing method suitable for forming ribs and nodes in the steel material for reinforcing bars will be described. The ribs and nodes are formed during the final finish rolling of the hot rolling described above. In this method, by providing grooves for forming nodes and ribs on the roll peripheral surface, which is the rolling surface of the roll used for rolling, the nodes and ribs are formed by biting the material into the grooves. Alternatively, using a four-roll rolling mill, the nodes can be formed by grooves provided on the peripheral surface of the roll serving as the rolling surface of the roll, and the ribs can be formed by biting into the gap between adjacent rolls.
以下、最終仕上圧延を、各ロールに節を形成させるための節溝を設けた４ロール圧延機により行い、この最終仕上圧延により節およびリブを素材に形成させる方法をについて説明する。
図３に、前述した鉄筋用鋼材を圧延により製造するのに好適な、節およびリブを成形するための最終仕上圧延機を示す。図中、符号10で最終仕上圧延機を、11で各ロールを示す。また、12は周溝、13は節溝、14はラウンド孔型、15はロール隙間、16は周溝の外縁部、17はロール側面である。
さて、最終仕上圧延機10は、節２、リブ３および母材表面４を形成するためのカリバーが設けられた４つのロール11を有する４ロール圧延機で構成される。すなわち、最終仕上圧延機10は、二個一対のロール11ａ，11ｂと、11ｃ，11ｄとをライン方向から見て直交させて配置した４ロール圧延機であり、各ロール11ａ，11ｂ，11ｃ，11ｄには、断面円弧状の周溝12をロール周方向に形成してあり、さらに周方向に沿って所定間隔の節溝13が形成されている。これらロール11のロール隙き間によるラウンド孔型14に、上流側の圧延機列によって断面円形に圧延された素材を通して圧下し、その周面に節２を形成する。同時に、隣接する各ロールの間隙15への噛み出しによりリブ３が形成される。すなわち、リブ３は、ロールに形成した周溝12の両外縁部16側に位置するロール側面17への噛み出しにより形成される。
Hereinafter, a method in which the final finish rolling is performed by a four-roll rolling mill provided with a groove for forming a node in each roll, and a method of forming the node and the rib on the material by the final finish rolling will be described.
FIG. 3 shows a final finish rolling mill for forming nodes and ribs suitable for producing the above-described steel for reinforcing bars by rolling. In the figure,
The final
図４は、ロール11の、周溝12および節溝13の部分を詳細に示した斜視図である。各ロールの、周溝12と節溝13とが交わる角部分にはＲが設けられており、この角部分のＲが素材に転写されて上述の節根元部の角部のＲが形成される。節溝13の側面13ａ（以下、節溝側面13ａという）と周溝12を形成するロール周面とが交わる部分の角度θ’を調整することにより、前述した節傾斜部と母材表面との成す角θを調整することができる。また、節溝側面13ａが転写されて節傾斜部２ａが形成されるため、節溝側面13ａの表面性状を調整することによって、節傾斜部２ａの表面粗度Ｒmaxを調整することができる。また、隣合う節溝13の間隔Ｌ’をラウンド孔型の径Ｄ’（図３参照）に応じて調整することにより、前述した節間隔Ｌと公称直径Ｄとの関係を調整することが可能である。さらに、隣接する各ロール11の間隙15をラウンド孔型の径Ｄ’に応じて調整することで調整することで、前述したリブ２の幅ｗを調整することができる。節２の高さは節溝13の深さおよび圧延時の減面率の調整により、調節することが可能である。
FIG. 4 is a perspective view showing the details of the
なお、本発明において、鋼材の母材径（公称直径）Ｄは6.35mm（Ｄ6）〜19.1mm（Ｄ19）程度とするのが好適である。 In the present invention, the base material diameter (nominal diameter) D of the steel material is preferably about 6.35 mm (D6) to 19.1 mm (D19).
表１に示す成分組成になる鋼（鋼種Ａ〜Ｈ）を溶製鋳造してビレットとしたのち、表２に示す種々異形形状の線材に熱間圧延し、ついで必要に応じて種々の温度で種々の時間保持して、公称直径Ｄ：12.7mm（Ｄ13）の異形棒鋼を製造した（No.１〜20）。なお、最終仕上圧延機として、図３および図４に示した４ロール圧延機を用い、各ロールに形成する節溝13の形状を変化させることで、異形形状の調整を行った。
After steel (steel types A to H) having the composition shown in Table 1 is melt cast and made into billets, it is hot-rolled into various deformed wires shown in Table 2, and then at various temperatures as necessary. By holding for various times, deformed steel bars having a nominal diameter D of 12.7 mm (D13) were produced (Nos. 1 to 20). As the final finishing mill, the four-roll mill shown in FIGS. 3 and 4 was used, and the shape of the
製造した各棒鋼について、顕微鏡観察により組織と各組織の体積比率を調査すると共に、鋼材中の残留水素濃度を測定した。
また、母材の特性を調べるために引張試験を行い、降伏強度（ＹＳ）、引張強度（ＴＳ）および母材伸び（ＥＬ）を測定した。
上記の引張試験において絞り値も測定した。なお絞り値は、各棒鋼について20箇所ずつ測定して絞り値の標準偏差を求めた。
About each manufactured steel bar, while examining the volume ratio of a structure | tissue and each structure | tissue by microscope observation, the residual hydrogen concentration in steel materials was measured.
In addition, a tensile test was performed to examine the characteristics of the base material, and the yield strength (YS), tensile strength (TS), and base material elongation (EL) were measured.
The drawing value was also measured in the above tensile test. The drawing value was measured at 20 points for each bar and the standard deviation of the drawing value was obtained.
さらに、母材の曲げ特性を調べるために、異形棒鋼を長さ：500mmに切断した後、公称直径Ｄの２倍の曲げ直径で180°曲げを行った後、これを90°曲げ戻す曲げ−曲げ戻し試験を０℃で行い、異形棒鋼20本中の折損本数の割合（破断率）を算出することにより曲げ加工性を評価した。曲げ試験は、図５（ａ）あるいはリブ本数が２本のものは図７（ａ）に示すように、リブ３のある位置を最内側として（リブを内径に押しつける方向（リブ方向））曲げる場合と、図５（ｂ）あるいはリブ本数が２本のものは図７（ｂ）に示すようにリブとリブの中間を最内側として（リブとリブの中間を内径に押しつける方向（リブ間方向））曲げる場合のそれぞれについて実施した。
Furthermore, in order to investigate the bending characteristics of the base metal, the deformed steel bar is cut to a length of 500 mm, bent 180 ° with a bending diameter twice the nominal diameter D, and then bent back 90 ° − The bending workability was evaluated by conducting a bending back test at 0 ° C. and calculating the ratio (breakage ratio) of the number of breaks in 20 deformed bars. In the bending test, as shown in FIG. 5 (a) or two ribs, as shown in FIG. 7 (a), the position where the
また、コンクリート付着力を測定する目的で、異形棒鋼を、100×100×100mmのコンクリート中心部を貫通する形で配筋埋込を実施し、片端から15mm、もう片端からは300mm以上を突出させる形態のものを供試材として作製した。該供試材から300mm以上突出した異形棒鋼を500kN引張試験機を用いて引っ張る形で引き抜き試験を実施し、
（最大引抜応力kN/mm2）＝（最大荷重kN）／{（公称直径mm）×（埋込長さmm）×（円周率）}
を測定した。なおコンクリート強度は51.5N/mm2の自然養生のものを使用した。
調査結果を表２に併せて示す。
なお、降伏強度が785MPa以上、引張強度が930MPa以上、方向を問わず曲げ加工時破断率が０％、そしてコンクリート付着力が15kN/mm2以上を本発明の鋼材に必要な特性とした。
In addition, for the purpose of measuring the concrete adhesion force, reinforcing bars are embedded in a shape that penetrates the center of the concrete of 100 x 100 x 100 mm, and protrudes 15 mm from one end and more than 300 mm from the other end. The thing of the form was produced as a test material. A pull-out test was carried out by pulling a deformed steel bar protruding from the specimen by 300 mm or more using a 500 kN tensile tester,
(Maximum pulling stress kN / mm 2 ) = (maximum load kN) / {(nominal diameter mm) × (embedding length mm) × (circumference ratio)}
Was measured. The concrete strength was 51.5N / mm 2 natural curing.
The survey results are also shown in Table 2.
The yield strength was 785 MPa or more, the tensile strength was 930 MPa or more, the breaking rate during bending was 0% regardless of the direction, and the concrete adhesion force was 15 kN / mm 2 or more.
表２に示したとおり、本発明の規定よりもリブ本数が少ないNo.６、リブ幅の和が小さいNo.７、節高さが高いNo.10、節間隔が短いNo.11、側面傾斜部と母材部の成す角が小さいNo.13、角部Ｒが小さいNo.15、側面傾斜部の表面粗度が大きいNo.17はいずれも、少なくともリブ間方向の曲げ時に折損を生じた。
また、本発明の規定よりもリブ幅の和が大きいNo.８、節高さの低いNo.９、節間隔が広いNo.12、側面傾斜部と母材部の成す角が大きいNo.14、角部Ｒが大きいNo.16は、いずれもコンクリート付着力が15kN/mm2に達しなかった。
本発明で１種以上の添加を規定したCr、Mo、Ｖ、Ｗ、Ni、Cu、Co、Sbのいずれをも含有しない鋼Ｇを用いたNo.19は、鋼中ミクロ組織のフェライト含有率が高く、本発明で規定した、体積比率で80％以上のベイナイトを満足しない。そのため、表２に示すように、降伏強度（ＹＳ）、引張強度（ＴＳ）がそれぞれ目標値に達していない。
一方、本発明の規定よりもTi量が高い鋼Ｆを用いたNo.18、および本発明の規定よりもＣ量が多い鋼Ｈを用いたNo.20はそれぞれ、強度目標は達成したものの、延性不足で曲げ加工時に大量の折損を生じた。
これに対し、本発明の要件を満足するNo.１〜５はいずれも、ＹＳ、ＴＳ、曲げ加工時破断率、さらにはコンクリート付着力とも、それぞれ目標とする値を得ることができた。
As shown in Table 2, No. 6 with a smaller number of ribs than specified in the present invention, No. 7 with a small sum of rib widths, No. 10 with a high node height, No. 11 with a short node interval, Side slope No. 13 with a small angle between the base and the base metal part, No. 15 with a small corner R, and No. 17 with a large surface roughness on the side inclined part, caused breakage at least when bending between the ribs. .
Further, No. 8 having a larger sum of rib widths than the provisions of the present invention, No. 9 having a low node height, No. 12 having a wide node interval, and No. 14 having a large angle formed by the side inclined portion and the base material portion. No. 16 having a large corner R did not reach a concrete adhesion of 15 kN / mm 2 .
No. 19 using steel G that does not contain any of Cr, Mo, V, W, Ni, Cu, Co, and Sb, in which one or more additions are specified in the present invention, is the ferrite content of the microstructure in the steel. Therefore, the bainite having a volume ratio of 80% or more as defined in the present invention is not satisfied. Therefore, as shown in Table 2, the yield strength (YS) and the tensile strength (TS) do not reach the target values, respectively.
On the other hand, although No. 18 using steel F having a higher Ti content than the provisions of the present invention and No. 20 using steel H having a higher C amount than the provisions of the present invention, the strength target was achieved. A large amount of breakage occurred during bending due to insufficient ductility.
On the other hand, Nos. 1 to 5 satisfying the requirements of the present invention were able to obtain target values for YS, TS, bending fracture rate, and concrete adhesion, respectively.
１ 鉄筋（異形鉄筋）
２ 節
２ａ 節側面傾斜部
２ｂ 節根元部の角部
３ リブ
４ 母材表面
10 最終仕上圧延機
11 ロール
12 周溝
13 節溝
13ａ 節溝側面
14 ラウンド孔型
15 ロール隙間
16 周溝の外縁部
17 ロール側面
1 Rebar (Deformed bar)
2 node 2a node side inclined
10 Final finishing mill
11 rolls
12 Circumferential groove
13 groove
13a Side groove side
14 round holes
15 Roll gap
16 Outer edge of circumferential groove
17 Roll side
Claims (5)
Ｃ：0.15〜0.30％、
Si：0.05〜1.0％、
Mn：0.2〜2.5％、
Al：0.01〜1.0％、
Nb：0.001〜0.3％、
Ti：0.003％未満、
Ｐ：0.03％以下、
Ｓ：0.03％以下および
Ｎ：0.0060％未満
を含有し、さらに、
Cr：0.1〜2.0％、
Mo：0.01〜1.0％、
Ｖ：0.01〜1.0％、
Ｗ：0.01〜1.0％、
Ni：0.01〜1.0％、
Cu：0.01〜1.0％、
Co：0.01〜1.0％および
Sb：0.0010〜0.0050％
のうちから選ばれる１種または２種以上を含有する鋼組成からなり、
鋼組織が、80％以上がベイナイトで、残部がフェライト、パーライトまたはマルテンサイトの組織からなり、
円周方向に90°間隔で、線材の長手方向に連続する４本のリブを有し、該４本のリブ幅の和が該線材の公称周長の15％以上25％以下で、
該リブを接続する形の節を該線材の公称直径の40％以上70％以下の間隔で有し、該節の高さが該線材の公称直径の4.0％以上8.0％以下で、
該節の頭頂部から節底にかけての節側面傾斜部と母材表面との成す角が100°以上135°未満で、節根元部の角部のＲが（節高さ×10％）以上（節高さ×25％）未満で、該節側面傾斜部の表面粗度Ｒmaxが0.2mm以内であり、
ＹＳ：785MPa以上、ＴＳ：930MPa以上
であることを特徴とする、曲げ特性およびコンクリート密着性のバランスに優れる高強度鉄筋用鋼材。 % By mass
C: 0.15-0.30%
Si: 0.05-1.0%
Mn: 0.2-2.5%
Al: 0.01 to 1.0%
Nb: 0.001 to 0.3%,
Ti: less than 0.003%,
P: 0.03% or less,
S: not more than 0.03% and N: less than 0.0060%,
Cr: 0.1-2.0%
Mo: 0.01-1.0%,
V: 0.01 to 1.0%
W: 0.01-1.0%
Ni: 0.01-1.0%,
Cu: 0.01 to 1.0%,
Co: 0.01-1.0% and
Sb: 0.0010 to 0.0050%
Consisting of a steel composition containing one or more selected from
More than 80% of the steel structure is bainite, and the balance consists of ferrite, pearlite, or martensite.
It has four ribs continuous in the longitudinal direction of the wire at 90 ° intervals in the circumferential direction, and the sum of the four rib widths is 15% or more and 25% or less of the nominal circumference of the wire,
Nodes having a shape connecting the ribs at intervals of 40% to 70% of the nominal diameter of the wire, and the height of the nodes is 4.0% to 8.0% of the nominal diameter of the wire;
The angle formed by the slope of the side surface of the node from the top to the bottom of the node and the surface of the base material is 100 ° or more and less than 135 °, and the corner R of the node root is (node height × 10%) or more ( Less than 25 mm), and the surface roughness Rmax of the inclined side surface of the node is within 0.2 mm,
YS: 785 MPa or more, TS: 930 MPa or more, a high-strength steel material for rebar excellent in the balance of bending characteristics and concrete adhesion.
Ｂ：0.0005〜0.0100％
を含有し、かつ鋼中のＢ量、Ｎ量およびTi量が、次式（１）の関係を満足することを特徴とする請求項１に記載の高強度鉄筋用鋼材。
Ｂ（％）≧｛Ｎ（％）／14−Ti（％）／27｝×11＋0.0005 ・・・（１）
ただし、Ｍ（％）は、Ｍ元素の含有量（質量％）を表わす。 The steel material is in mass%, and
B: 0.0005-0.0100%
The steel material for high-strength reinforcing bars according to claim 1, wherein the B content, the N content, and the Ti content in the steel satisfy the relationship of the following formula (1).
B (%) ≧ {N (%) / 14−Ti (%) / 27} × 11 + 0.0005 (1)
However, M (%) represents content (mass%) of M element.
Ｃ：0.15〜0.30％、
Si：0.05〜1.0％、
Mn：0.2〜2.5％、
Al：0.01〜1.0％、
Nb：0.001〜0.3％、
Ti：0.003％未満、
Ｐ：0.03％以下、
Ｓ：0.03％以下および
Ｎ：0.0060％未満
を含有し、さらに、
Cr：0.1〜2.0％、
Mo：0.01〜1.0％、
Ｖ：0.01〜1.0％、
Ｗ：0.01〜1.0％、
Ni：0.01〜1.0％、
Cu：0.01〜1.0％、
Co：0.01〜1.0％および
Sb：0.0010〜0.0050％
のうちから選ばれる１種または２種以上を含有する組成からなる鋼素材を、加熱温度：Ａc3点〜1350℃、圧延終了温度：Ａr3点以上の条件で熱間圧延し、該熱間圧延の最終仕上圧延時に下記を満足するリブおよび節を形成し、その後500〜800℃の温度範囲を0.3℃/ｓ以上、25℃/ｓ以下の冷却速度で冷却することを特徴とする高強度鉄筋用鋼材の製造方法。
記
リブ：円周方向に90°間隔で線材の長手方向に連続する４本のリブを有し、該４本のリブ幅の和は該線材の公称周長の15％以上25％以下。
節：円周方向に隣り合うリブを接続する形の節であり、線材の長さ方向に該線材の公称直径の40％以上70％以下の間隔で配置、節の高さは該線材の公称直径の4.0％以上8.0％以下、節の頭頂部から節底にかけての節側面傾斜部と母材表面との成す角は100°以上135°未満、節根元部の角部のＲは（節高さ×10％）以上（節高さ×25％）未満、該節側面傾斜部の表面粗度Ｒmaxは0.2mm以内。 % By mass
C: 0.15-0.30%
Si: 0.05-1.0%
Mn: 0.2-2.5%
Al: 0.01 to 1.0%
Nb: 0.001 to 0.3%,
Ti: less than 0.003%,
P: 0.03% or less,
S: not more than 0.03% and N: less than 0.0060%,
Cr: 0.1-2.0%
Mo: 0.01-1.0%,
V: 0.01 to 1.0%
W: 0.01-1.0%
Ni: 0.01-1.0%,
Cu: 0.01 to 1.0%,
Co: 0.01-1.0% and
Sb: 0.0010 to 0.0050%
A steel material having a composition containing one or more selected from the above is hot-rolled under conditions of heating temperature: Ac 3 points to 1350 ° C., rolling end temperature: Ar 3 points or more, High strength, characterized in that ribs and nodes satisfying the following conditions are formed during the final finish rolling of the rolling, and then the temperature range of 500 to 800 ° C. is cooled at a cooling rate of 0.3 ° C./s or more and 25 ° C./s or less. A method for manufacturing steel for reinforcing bars.
Rib: Four ribs continuous in the longitudinal direction of the wire at 90 ° intervals in the circumferential direction, and the sum of the widths of the four ribs is 15% or more and 25% or less of the nominal circumference of the wire.
Knots: Knots in the form of connecting ribs adjacent in the circumferential direction, arranged in the length direction of the wire at intervals of 40% to 70% of the nominal diameter of the wire, and the height of the knot is the nominal height of the wire 4.0 to 8.0% of the diameter, the angle between the node side slope from the top of the node to the node bottom and the surface of the base material is 100 ° to less than 135 °, and R at the corner of the node root is Thickness x 10%) or more (node height x 25%) and the surface roughness Rmax of the node side inclined portion is within 0.2 mm.
Ｂ：0.0005〜0.0100％
を含有し、かつ鋼中のＢ量、Ｎ量およびTi量が、次式（１）の関係を満足することを特徴とする請求項３に記載の高強度鉄筋用鋼材の製造方法。
Ｂ（％）≧｛Ｎ（％）／14−Ti（％）／27｝×11＋0.0005・・・（１）
ただし、Ｍ（％）は、Ｍ元素の含有量（質量％）を表わす。 The steel material is in mass%, and
B: 0.0005-0.0100%
4. The method for producing a steel material for high-strength reinforcing bars according to claim 3, wherein the B content, the N content, and the Ti content in the steel satisfy the relationship of the following formula (1):
B (%) ≧ {N (%) / 14−Ti (%) / 27} × 11 + 0.0005 (1)
However, M (%) represents content (mass%) of M element.
Ｔ×logｔ≧1500 ・・・（２） The holding temperature T (K) and the holding time t () satisfying the following expression (2) are applied to the steel for reinforcing bars manufactured by the manufacturing method according to claim 3 or 4 before bending for use in reinforced concrete construction. A method for producing a steel material for high-strength reinforcing steel, characterized in that holding is performed in seconds).
T × logt ≧ 1500 (2)