JP2011178137A - Lipophilic surface layer material and lipophilic decorative sheet - Google Patents
Lipophilic surface layer material and lipophilic decorative sheet Download PDFInfo
- Publication number
- JP2011178137A JP2011178137A JP2010047232A JP2010047232A JP2011178137A JP 2011178137 A JP2011178137 A JP 2011178137A JP 2010047232 A JP2010047232 A JP 2010047232A JP 2010047232 A JP2010047232 A JP 2010047232A JP 2011178137 A JP2011178137 A JP 2011178137A
- Authority
- JP
- Japan
- Prior art keywords
- lipophilic
- resin
- layer material
- oil
- surface layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、親油性表面層材料、及び、親油性化粧板に関するものである。 The present invention relates to a lipophilic surface layer material and a lipophilic decorative board.
メラミン樹脂化粧板は、表面硬度、耐摩耗性、耐熱性、耐水性などに優れ、意匠性においても美しい外観を有することから、住宅、公共施設、各種事業所などにおいて、家具、扉、間仕切り材用途などに幅広く使用されている。
近年ではユーザーニーズが多様化し、単なる装飾材としてだけではなく、汚れが目立ちにくい（汚れが付着しにくい、もしくは、付着しても目立ちにくい）化粧板、あるいは、付着した汚れを容易に払拭できる化粧板など、意匠性に加えて高度の防汚性能が求められるようになってきた。
Melamine resin decorative boards are excellent in surface hardness, wear resistance, heat resistance, water resistance, etc., and have a beautiful appearance in terms of design, so they are used in furniture, doors, partition materials in houses, public facilities, various offices, etc. Widely used for applications.
In recent years, user needs have diversified, not only as a decorative material, but also as a decorative board that makes stains less noticeable (dirt is less likely to adhere or is less noticeable), or makeup that can easily wipe off the attached dirt High antifouling performance has come to be demanded in addition to design properties such as plates.
従来、例えば、シリコーンのような低表面張力材料を使用し、化粧板表面を撥水・撥油性にして汚れをはじくことにより、汚れの付着を抑えたり、払拭性を向上させたりすることが行われてきた（例えば、特許文献１参照。）。
しかしながら、化学的な手法のみで化粧板表面を撥水・撥油性にするには理論的な限度があり、汚れ（特に、表面張力の低い油性成分）の付着を完全に防ぐことも困難である。
上記のような手法では、化粧板表面に汚れが付着した場合、化粧板表面に対する汚れ付着部分の接触角が大きくなり、その部分に入射した光が乱反射し、付着部分が白く見えるようになる。このため、表面が平滑な鏡面仕上げタイプの化粧板（特に濃色柄）では有効ではなく、通常のメラミン樹脂化粧板と比較しても、かえって汚れが目立ちやすくなる。
また、付着した汚れを払拭しても、撥水・撥油性が不十分で、容易に全て払拭することはできないため、化粧板表面に汚れが残る。この汚れは、払拭作業によって小さく分裂しているが、可視光の波長よりは十分に大きいサイズであり、かつ、はじかれて接触角が大きくなっているため、入射光が乱反射して、払拭後も目立ちやすくなる。
Conventionally, for example, by using a low surface tension material such as silicone and making the surface of the decorative board water and oil repellent and repelling dirt, it is possible to suppress adhesion of dirt and improve wiping performance. (For example, refer to Patent Document 1).
However, there is a theoretical limit to making the decorative board surface water and oil repellent only by chemical methods, and it is difficult to completely prevent the adhesion of dirt (especially oily components with low surface tension). .
In the above method, when dirt adheres to the decorative board surface, the contact angle of the dirt adhesion part with respect to the decorative board surface becomes large, the light incident on the part is irregularly reflected, and the attached part appears white. For this reason, it is not effective for a mirror-finished decorative board (especially a dark colored pattern) with a smooth surface, and dirt is more conspicuous even when compared with a normal melamine resin decorative board.
Further, even if the adhered dirt is wiped off, the water and oil repellency is insufficient and cannot be wiped off easily, so that the dirt remains on the surface of the decorative board. Although this dirt is divided into small pieces by the wiping operation, the size is sufficiently larger than the wavelength of visible light, and it is repelled to increase the contact angle. Will also stand out.
本発明は、従来のメラミン樹脂化粧板の優れた特性を有しながら、汚れ（特に、油性成分による汚れ）が付着しても目立ちにくく、かつ、払拭作業によって容易に汚れが見えなくなる化粧板に用いることができる親油性表面層材料、及び、これを用いてなる親油性化粧板を提供するものである。 The present invention provides a decorative board that has the excellent characteristics of a conventional melamine resin decorative board, is hardly noticeable even when dirt (especially, dirt due to an oily component) adheres, and in which dirt is not easily visible by wiping work. The present invention provides a lipophilic surface layer material that can be used and a lipophilic decorative board using the same.
このような目的は、下記の本発明［１］〜［５］により達成される。
［１］化粧板表面に用いられる親油性表面層材料であって、
上記親油性表面層材料は、第一の面と、第二の面とを有し、少なくとも上記第一の面の最表面に親油性樹脂層が形成されており、
上記親油性樹脂層は、メラミン樹脂と、油変性アルキド樹脂とを含有する親油性樹脂組成物により形成されていることを特徴とする親油性表面層材料。
［２］上記親油性樹脂組成物は、メラミン樹脂に対して、油変性アルキド樹脂０．１〜１０重量％を含有するものである、上記［１］に記載の親油性表面層材料。
［３］上記親油性樹脂組成物は、界面活性剤を含有するものである、上記［１］又は［２
］に記載の親油性表面層材料。
［４］上記親油性樹脂組成物は、エポキシ基含有化合物を含有するものである、上記［１］ないし［３］のいずれかに記載の親油性表面層材料。
［５］上記［１］ないし［４］のいずれかに記載の親油性表面層材料を用いてなる親油性化粧板であって、
上記親油性表面層材料の第一の面側を最表面としたものであることを特徴とする親油性化粧板。
Such an object is achieved by the following present inventions [1] to [5].
[1] A lipophilic surface layer material used for a decorative board surface,
The lipophilic surface layer material has a first surface and a second surface, and at least the outermost surface of the first surface has a lipophilic resin layer formed thereon,
The lipophilic surface layer material, wherein the lipophilic resin layer is formed of a lipophilic resin composition containing a melamine resin and an oil-modified alkyd resin.
[2] The lipophilic surface layer material according to [1], wherein the lipophilic resin composition contains 0.1 to 10% by weight of an oil-modified alkyd resin with respect to the melamine resin.
[3] The lipophilic resin composition described above [1] or [2] containing a surfactant.
] The lipophilic surface layer material of description.
[4] The lipophilic surface layer material according to any one of [1] to [3], wherein the lipophilic resin composition contains an epoxy group-containing compound.
[5] A lipophilic decorative board comprising the lipophilic surface layer material according to any one of [1] to [4] above,
A lipophilic decorative board characterized in that the first surface side of the lipophilic surface layer material is the outermost surface.
本発明によれば、従来のメラミン樹脂化粧板の優れた特性を有しながら、汚れ（特に、油性成分による汚れ）が付着しても目立ちにくく、かつ、払拭作業によって容易に汚れが見えなくなる化粧板に用いることができる親油性表面層材料、及び、これを用いてなる親油性化粧板を得ることができる。 According to the present invention, while having the excellent characteristics of a conventional decorative melamine resin decorative board, even if dirt (especially dirt due to an oil component) adheres, it is not noticeable and the dirt is not easily visible by wiping work. A lipophilic surface layer material that can be used for a plate and a lipophilic decorative plate using the same can be obtained.
以下に、本発明の親油性表面層材料、及び、親油性化粧板について説明する。
本発明の親油性表面層材料は、化粧板表面に用いられる親油性表面層材料であって、第一の面と、第二の面とを有し、少なくとも上記第一の面の最表面に親油性樹脂層が形成されており、上記親油性樹脂層は、メラミン樹脂と、油変性アルキド樹脂とを含有する親油性樹脂組成物により形成されていることを特徴とする。
また、本発明の親油性化粧板は、上記本発明の親油性表面層材料を用いてなる化粧板であって、上記親油性表面層材料の第一の面側を最表面としたものであることを特徴とする。
Hereinafter, the lipophilic surface layer material and the lipophilic decorative board of the present invention will be described.
The lipophilic surface layer material of the present invention is a lipophilic surface layer material used for a decorative board surface, and has a first surface and a second surface, and at least the outermost surface of the first surface. A lipophilic resin layer is formed, and the lipophilic resin layer is formed of a lipophilic resin composition containing a melamine resin and an oil-modified alkyd resin.
The lipophilic decorative board of the present invention is a decorative board using the lipophilic surface layer material of the present invention, wherein the first surface side of the lipophilic surface layer material is the outermost surface. It is characterized by that.
まず、本発明の親油性表面層材料において、親油性樹脂層の形成に用いられる親油性樹脂組成物について説明する。
上記親油性樹脂組成物は、メラミン樹脂と、油変性アルキド樹脂とを含有する。
First, the lipophilic resin composition used for forming the lipophilic resin layer in the lipophilic surface layer material of the present invention will be described.
The lipophilic resin composition contains a melamine resin and an oil-modified alkyd resin.
ここで用いられるメラミン樹脂としては、メラミン（Ｍ）に対するホルムアルデヒド（Ｆ）の反応モル比（F／M比）を１．０〜４．０、好ましくは１．０〜２．０として反応させて得られたものを好適に用いることができる。 As the melamine resin used here, the reaction molar ratio (F / M ratio) of formaldehyde (F) to melamine (M) is 1.0 to 4.0, preferably 1.0 to 2.0. What was obtained can be used conveniently.
ここで用いられる油変性アルキド樹脂において、アルキド樹脂とは、アルコールと酸とを反応させて得られるポリエステル樹脂のことであり、油変性アルキド樹脂とは、油成分で変性されたポリエステル樹脂である。
アルキド樹脂の変性に用いられる油成分とは、具体的には、脂肪酸や油脂（グリセリンに脂肪酸がエステル結合したもので、通常はトリグリセライドの形態をとるもの）などが挙げられる。
In the oil-modified alkyd resin used herein, the alkyd resin is a polyester resin obtained by reacting an alcohol and an acid, and the oil-modified alkyd resin is a polyester resin modified with an oil component.
Specific examples of the oil component used for the modification of the alkyd resin include fatty acids and fats and oils (things in which fatty acids are ester-bonded to glycerin and usually take the form of triglycerides).
油変性アルキド樹脂は、大別して脂肪酸法とモノグリセライド法の２つの方法により合成することができる。
脂肪酸法は、脂肪酸、多塩基酸、多価アルコールを反応させて、脂肪酸で変性させたポリエステル樹脂を合成する方法である。一方、モノグリセライド法は、油脂と多価アルコールとをエステル交換反応させてグリセライド化合物をつくり、さらに多塩基酸あるいは必要に応じ、多価アルコールを加えて反応させエステル化し、油脂で変性させたポリエステル樹脂を合成する方法である。
Oil-modified alkyd resins can be roughly classified by two methods, the fatty acid method and the monoglyceride method.
The fatty acid method is a method of synthesizing a polyester resin modified with a fatty acid by reacting a fatty acid, a polybasic acid and a polyhydric alcohol. On the other hand, the monoglyceride method is a polyester resin in which fats and fats and polyhydric alcohols are transesterified to produce glyceride compounds, and polybasic acid or, if necessary, polyhydric alcohols are added and reacted to be esterified and modified with fats and oils. Is a method of synthesizing.
油変性アルキド樹脂の合成に用いられる脂肪酸としては、例えば、ラウリン酸（ドデカン酸）、ミリスチン酸（テトラデカン酸）、ペンタデシル酸（ペンタデカン酸）、パルミチン酸（ヘキサデカン酸）、パルミトレイン酸（ヘキサデセン酸）、マルガリン酸（ヘプ
タデカン酸）、ステアリン酸（オクタデカン酸）、オレイン酸、バクセン酸、リノール酸（オクタデカジエン酸）、リノレン酸、エレオステアリン酸、ツベルクロステアリン酸（ノナデカン酸）、アラキジン酸（イコサン酸）、イコサジエン酸、イコサトリエン酸、アラキドン酸（イコサテトラエン酸）、ベヘン酸（ドコサン酸）、リグノセリン酸（テトラドコサン酸）、ネルボン酸、セロチン酸（ヘキサドコサン酸）、モンタン酸（オクタドコサン酸）、メリシン酸などが挙げられる。
油変性アルキド樹脂の合成に用いられる油脂としては、例えば、サラダ油、コーン油、大豆油、ゴマ油、菜種油、ベニバナ油、椿油、パーム油、ヤシ油、ヒマワリ油、オリーブ油、魚油、ヒマシ油、パーム油、ラード、牛脂などが挙げられる。
Examples of fatty acids used in the synthesis of the oil-modified alkyd resin include lauric acid (dodecanoic acid), myristic acid (tetradecanoic acid), pentadecylic acid (pentadecanoic acid), palmitic acid (hexadecanoic acid), palmitoleic acid (hexadecenoic acid), Margaric acid (heptadecanoic acid), stearic acid (octadecanoic acid), oleic acid, vaccenic acid, linoleic acid (octadecadienoic acid), linolenic acid, eleostearic acid, tuberculostearic acid (nonadecanoic acid), arachidic acid (icosanoic acid) Acid), icosadienoic acid, icosatrienoic acid, arachidonic acid (icosatetraenoic acid), behenic acid (docosanoic acid), lignoceric acid (tetradocosanoic acid), nervonic acid, cerotic acid (hexadocosanoic acid), montanic acid (octadocosanoic acid), melicic acid, etc. Is It is.
Examples of the oils and fats used in the synthesis of the oil-modified alkyd resin include salad oil, corn oil, soybean oil, sesame oil, rapeseed oil, safflower oil, coconut oil, palm oil, coconut oil, sunflower oil, olive oil, fish oil, castor oil, and palm oil. , Lard, beef tallow and the like.
油変性アルキド樹脂の合成に用いられる多塩基酸としては、例えば、無水フタル酸、テレフタル酸、コハク酸、アジピン酸、セバシン酸などの飽和多塩基酸、マレイン酸、無水マレイン酸、フマル酸、イタコン酸、無水シトラコン酸、イソフタル酸、無水トリメリト酸などの不飽和多塩基酸、シクロペンタジエン−無水マレイン酸付加物、テルペン−無水マレイン酸付加物、ロジン−無水マレイン酸付加物などのディールズ−アルダー反応による多塩基酸などが挙げられる。 Examples of polybasic acids used in the synthesis of oil-modified alkyd resins include saturated polybasic acids such as phthalic anhydride, terephthalic acid, succinic acid, adipic acid, and sebacic acid, maleic acid, maleic anhydride, fumaric acid, and itacone. Diels-Alder reactions such as acid, citraconic anhydride, isophthalic acid, trimellitic anhydride and other unsaturated polybasic acids, cyclopentadiene-maleic anhydride adduct, terpene-maleic anhydride adduct, rosin-maleic anhydride adduct And polybasic acid.
油変性アルキド樹脂の合成に用いられる多価アルコールとしては、例えば、エチレングリコール、ジエチレングリコール、トリエチレングリコール、プロピレングリコール、トリメチレングリコール、テトラメチレングリコール、ネオペンチルグリコールなどの二価アルコール、グリセリン、トリメチロールエタン、トリメチロールプロパンなどの三価アルコール、ジグリセリン、トリグリセリン、ペンタエリスリトール、ペンタエリトリット、ジペンタエリトリット、マンニット、ソルビットなどが挙げられる。 Examples of the polyhydric alcohol used in the synthesis of the oil-modified alkyd resin include dihydric alcohols such as ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, trimethylene glycol, tetramethylene glycol, and neopentyl glycol, glycerin, and trimethylol. Examples thereof include trihydric alcohols such as ethane and trimethylolpropane, diglycerin, triglycerin, pentaerythritol, pentaerythritol, dipentaerythritol, mannitol, and sorbit.
また、上記のようにして得られる油変性アルキド樹脂は、極性溶媒への溶解性を付与することを目的として、必要に応じて極性の高い官能基を導入したものでも良いし、所望の物理的・化学的特性を付与することを目的として、必要に応じて他の変性物質、例えば、ロジン、フェノール、エポキシなどを導入したものでも良い。
本発明に用いられる油変性アルキド樹脂は、上記のようにして合成された市販品を用いることもできる。
In addition, the oil-modified alkyd resin obtained as described above may have a functional group having a high polarity introduced as necessary for the purpose of imparting solubility in a polar solvent, and may have a desired physical property. -For the purpose of imparting chemical characteristics, other modified substances such as rosin, phenol, epoxy and the like may be introduced as necessary.
As the oil-modified alkyd resin used in the present invention, a commercially available product synthesized as described above can be used.
本発明に用いられる油変性アルキド樹脂は、変性に用いられる油のヨウ素価が１００〜１３０である半乾性油、もしくは、ヨウ素価が１００以下である不乾性油であることが好ましい。これにより、経時による油変性アルキド樹脂の化学的な性質変化が少なくなり、油変性アルキド樹脂や親油性表面層材料の保存安定性を高めることができる。
また、油変性アルキド樹脂の油長（樹脂の中に含まれる脂肪酸もしくは油脂の量）が４５〜５８重量％である中油タイプ、もしくは、油長が４５重量％以下である短油タイプであることが好ましい。これにより、化粧板表面の光沢性や耐変色性、硬度を高めることができる。
The oil-modified alkyd resin used in the present invention is preferably a semi-drying oil having an iodine value of 100 to 130, or a non-drying oil having an iodine value of 100 or less. Thereby, the chemical property change of the oil-modified alkyd resin with time is reduced, and the storage stability of the oil-modified alkyd resin and the lipophilic surface layer material can be improved.
The oil length of the oil-modified alkyd resin (the amount of fatty acid or fat contained in the resin) is 45 to 58% by weight, or the short oil type is 45% by weight or less. Is preferred. Thereby, the glossiness, discoloration resistance, and hardness of the decorative board surface can be improved.
上記メラミン樹脂と、上記油変性アルキド樹脂とを含有する親油性樹脂組成物を用いて、本発明の親油性表面層材料に親油性樹脂層を形成することができ、本発明の親油性表面層材料を用いた化粧板表面を親油性とすることができる。
これにより、メラミン樹脂の優れた表面硬度、耐摩耗性、耐熱性、耐水性などの優れた特性を有しながら、防汚性（特に、油性成分による汚れが付着しても目立ちにくく、かつ、払拭作業によって容易に汚れが見えなくなる）を付与することができる。
A lipophilic resin layer can be formed on the lipophilic surface layer material of the present invention using the lipophilic resin composition containing the melamine resin and the oil-modified alkyd resin, and the lipophilic surface layer of the present invention. The decorative board surface using the material can be made oleophilic.
Thereby, while having excellent properties such as excellent surface hardness, abrasion resistance, heat resistance, water resistance of melamine resin, antifouling property (particularly, even if dirt due to oily components adheres, The wiping operation can easily impart dirt).
上記親油性樹脂組成物としては、上記メラミン樹脂に対して、上記油変性アルキド樹脂０．１〜１０重量％を含有するものであることが好ましい。さらに好ましくは０．５〜５重量％である。
メラミン樹脂に対する油変性アルキド樹脂の含有量を上記下限値以上とすることにより、優れた防汚性を付与することができる。また、上記上限値以下とすることにより、メラミン樹脂の優れた物性を維持し、かつ、白化や光沢性の低下のない外観の良好な化粧板を得ることができる。
The lipophilic resin composition preferably contains 0.1 to 10% by weight of the oil-modified alkyd resin with respect to the melamine resin. More preferably, it is 0.5 to 5% by weight.
By setting the content of the oil-modified alkyd resin relative to the melamine resin to be equal to or higher than the above lower limit value, excellent antifouling properties can be imparted. Moreover, by making it into the said upper limit or less, the decorative sheet with the favorable external appearance which maintains the outstanding physical property of a melamine resin and does not have whitening and a glossiness fall can be obtained.
上記親油性樹脂組成物は、メラミン樹脂と、油変性アルキド樹脂とともに、界面活性剤を含有することができる。
これにより、化粧板の製造プロセスにおいて、油変性アルキド樹脂の凝集を防止し、分散性を向上させることができる。製造プロセスにおける油変性アルキド樹脂の分散性を向上させることによって、本発明の親油性化粧板の外観を向上させ、化粧板表面の親油性の均一性を高めることができる。
The lipophilic resin composition can contain a surfactant together with the melamine resin and the oil-modified alkyd resin.
Thereby, in the manufacturing process of a decorative board, aggregation of oil-modified alkyd resin can be prevented and dispersibility can be improved. By improving the dispersibility of the oil-modified alkyd resin in the production process, the appearance of the lipophilic decorative board of the present invention can be improved and the uniformity of the lipophilicity on the surface of the decorative board can be improved.
本発明において親油性樹脂組成物は、溶媒などを添加したワニスの形態で用いられるが、ここで使用されるメラミン樹脂は極性が高く、また、ワニスの溶媒としては通常、極性の高い水が使用される。極性の低い油変性アルキド樹脂を用いる場合、上記のように極性の高いワニス組成物中で、油変性アルキド樹脂の凝集を防ぎ、均一かつ安定に分散させるには、界面活性剤を添加することが効果的である。また、上記と同様の理由で、親油性樹脂組成物を含むワニスを塗布して親油性表面層材料を得るプロセス、これを用いて親油性化粧板を加熱加圧成形するプロセスにおいても、界面活性剤を含むことは、油変性アルキド樹脂の凝集を防ぐのに効果的である。 In the present invention, the oleophilic resin composition is used in the form of a varnish to which a solvent or the like is added, but the melamine resin used here has a high polarity, and usually a highly polar water is used as a solvent for the varnish. Is done. When using a low polarity oil-modified alkyd resin, a surfactant may be added to prevent aggregation of the oil-modified alkyd resin in the highly polar varnish composition as described above, and to disperse uniformly and stably. It is effective. In addition, for the same reason as described above, even in the process of applying a varnish containing a lipophilic resin composition to obtain a lipophilic surface layer material, and using this to heat and pressure-mold a lipophilic decorative board, surface activity Including an agent is effective in preventing aggregation of the oil-modified alkyd resin.
本発明において用いられる界面活性剤としては、上記のように、親油性表面層材料及び親油性化粧板の製造プロセスにおいては、極性の高いメラミン樹脂や水を使用するため、極性の高い界面活性剤であることが好ましい。
極性の高い界面活性剤としては、例えば、ＨＬＢ（Ｈｙｄｒｏｐｈｉｌｅ−Ｌｉｐｏｐｈｉｌｅ Ｂａｌａｎｃｅ／親水親油バランス）が７以上、好ましくは１０以上である非イオン性界面活性剤、陰イオン性界面活性剤、陽イオン性界面活性剤、両性界面活性剤などを挙げることができる。
As described above, the surfactant used in the present invention is a highly polar surfactant because a highly polar melamine resin or water is used in the manufacturing process of the lipophilic surface layer material and the lipophilic decorative board. It is preferable that
Examples of the highly polar surfactant include nonionic surfactants, anionic surfactants, and cationic surfactants having an HLB (Hydrophile-Lipophile Balance / hydrophilic lipophilic balance) of 7 or more, preferably 10 or more. Surfactant, amphoteric surfactant, etc. can be mentioned.
上記親油性樹脂組成物が、界面活性剤を含有する場合、この成分の含有量としては、上記メラミン樹脂に対して、０．０１〜１０重量％とすることが好ましい。さらに好ましくは０．０５〜５重量％である。
これにより、上記作用を効果的に発現させることができる。
When the lipophilic resin composition contains a surfactant, the content of this component is preferably 0.01 to 10% by weight with respect to the melamine resin. More preferably, it is 0.05 to 5% by weight.
Thereby, the said effect | action can be expressed effectively.
また、上記親油性樹脂組成物は、メラミン樹脂と、油変性アルキド樹脂とともに、エポキシ基含有化合物を含有することができる。
これにより、親油性樹脂組成物中のメラミン樹脂と油変性アルキド樹脂との化学的結合を進めることができるので、本発明の親油性化粧板において、油変性アルキド樹脂がブリードアウトするのを防止することができ、親油性化粧板表面の親油性の耐久性を高めることができる。
メラミン樹脂と油変性アルキド樹脂は、加熱により反応して化学結合を生成するが、比較的高温かつ長時間の加熱が必要となる。メラミン樹脂と油変性アルキド樹脂の反応が十分に進行しない場合、本発明の親油性表面層材料を用いて作製した親油性化粧板には、未反応の油変性アルキド樹脂が残ることとなる。未反応の油変性アルキド樹脂が残存した場合、経時でブリードアウトして、親油性化粧板表面の親油性が低下し、防汚性が低下する可能性が考えられる。
Moreover, the said lipophilic resin composition can contain an epoxy group containing compound with a melamine resin and an oil modified alkyd resin.
As a result, chemical bonding between the melamine resin and the oil-modified alkyd resin in the lipophilic resin composition can be promoted, so that the oil-modified alkyd resin is prevented from bleeding out in the lipophilic decorative board of the present invention. It is possible to enhance the lipophilic durability of the surface of the lipophilic decorative board.
The melamine resin and the oil-modified alkyd resin react by heating to produce a chemical bond, but heating at a relatively high temperature for a long time is required. When the reaction between the melamine resin and the oil-modified alkyd resin does not proceed sufficiently, an unreacted oil-modified alkyd resin remains on the lipophilic decorative board produced using the lipophilic surface layer material of the present invention. When the unreacted oil-modified alkyd resin remains, it may bleed out with time, and the lipophilicity of the surface of the lipophilic decorative board may be reduced, and the antifouling property may be reduced.
本発明において用いられるエポキシ基含有化合物としては、上記のように、親油性表面層材料及び親油性化粧板の製造プロセスにおいては、極性の高いメラミン樹脂や水を使用するため、極性の高いエポキシ基含有化合物であることが好ましい。
極性の高いエポキシ基含有化合物としては、例えば、エチレングリコール系、グリセリン系、ソルビトール系などの水溶性エポキシ樹脂や、エポキシ系シランカップリング剤（溶媒が水の場合）などを挙げることができる。
As the epoxy group-containing compound used in the present invention, as described above, in the manufacturing process of the lipophilic surface layer material and the lipophilic decorative board, a highly polar melamine resin or water is used. It is preferable that it is a containing compound.
Examples of highly polar epoxy group-containing compounds include water-soluble epoxy resins such as ethylene glycol, glycerin, and sorbitol, and epoxy silane coupling agents (when the solvent is water).
上記親油性樹脂組成物が、エポキシ基含有化合物を含有する場合、この成分の含有量としては、上記メラミン樹脂に対して、０．０１〜１０重量％とすることが好ましい。さらに好ましくは０．０５〜５重量％である。
これにより、上記作用を効果的に発現させることができる。
When the lipophilic resin composition contains an epoxy group-containing compound, the content of this component is preferably 0.01 to 10% by weight with respect to the melamine resin. More preferably, it is 0.05 to 5% by weight.
Thereby, the said effect | action can be expressed effectively.
また、上記親油性樹脂組成物は、メラミン樹脂と、油変性アルキド樹脂とともに、界面活性剤と、エポキシ基含有化合物とを併せて用いることができる。
これにより、親油性化粧板の外観を向上させ、表面の親油性の均一性及び耐久性を高めることができる。
界面活性剤と、エポキシ基含有化合物とを併せて用いる場合、その含有量としては、それぞれ、メラミン樹脂に対して、界面活性剤０．０１〜１０重量％、好ましくは０．０５〜５重量％、エポキシ基含有化合物０．０１〜１０重量％、好ましくは０．０５〜５重量％とすることができる。これにより、上記作用を効果的に発現させることができる。
Moreover, the said lipophilic resin composition can use together surfactant and an epoxy-group containing compound with a melamine resin and an oil modified alkyd resin.
Thereby, the external appearance of a lipophilic decorative board can be improved and the uniformity and durability of surface lipophilicity can be improved.
When the surfactant and the epoxy group-containing compound are used in combination, the content thereof is 0.01 to 10% by weight, preferably 0.05 to 5% by weight, based on the melamine resin. The epoxy group-containing compound may be 0.01 to 10% by weight, preferably 0.05 to 5% by weight. Thereby, the said effect | action can be expressed effectively.
上記親油性樹脂組成物は、メラミン樹脂、油変性アルキド樹脂、必要に応じて上記各成分のほか、触媒、添加剤、溶媒などを加えた親油性樹脂組成物含有ワニスの形態で用いることができる。
親油性樹脂組成物含有ワニス中の、メラミン樹脂、油変性アルキド樹脂の固形分量は、合計で例えば２０〜８０重量％とすることができる。
The lipophilic resin composition can be used in the form of a melamine resin, an oil-modified alkyd resin, a varnish containing an oleophilic resin composition containing a catalyst, an additive, a solvent, etc. in addition to the above-described components as necessary. .
The total solid content of the melamine resin and oil-modified alkyd resin in the oleophilic resin composition-containing varnish can be, for example, 20 to 80% by weight.
本発明の親油性表面層材料は、親油性化粧板表面に用いられ、第一の面と、第二の面とを有し、少なくとも上記第一の面の最表面に、上記親油性樹脂組成物からなる親油性樹脂層が形成されているものである。
本発明の親油性表面層材料としては、例えば、下記の二つの形態を挙げることができる。
The lipophilic surface layer material of the present invention is used on the surface of a lipophilic decorative board, and has a first surface and a second surface, and at least the outermost surface of the first surface has the lipophilic resin composition. The lipophilic resin layer which consists of a thing is formed.
Examples of the lipophilic surface layer material of the present invention include the following two forms.
第一の形態の親油性表面層材料は、化粧板表面に用いられ、意匠性を有する第一の面と、第二の面とを有し、少なくとも上記第一の面の最表面に親油性樹脂層が形成されているものである。 The lipophilic surface layer material of the first form is used for a decorative board surface, and has a first surface having design properties and a second surface, and at least the outermost surface of the first surface is lipophilic. A resin layer is formed.
第一の形態の親油性表面層材料に用いられる基材は、第一の面側に意匠面が形成されたシート状の基材であり、その材質としては特に限定されないが、好ましくは、パルプ、リンター、合成繊維などを用いることができ、例えば、カーボンブラックなどの顔料を含有するカーボンブラック含有化粧紙などを用いることができる。
この基材の単位面積あたりの重量としては特に限定されないが、８０〜１５０ｇ／ｍ２のものを好適に用いることができる。
The base material used for the lipophilic surface layer material of the first form is a sheet-like base material having a design surface formed on the first surface side, and the material is not particularly limited, but preferably pulp. , Linters, synthetic fibers and the like can be used. For example, carbon black-containing decorative paper containing a pigment such as carbon black can be used.
Although it does not specifically limit as a weight per unit area of this base material, The thing of 80-150 g / m < 2 > can be used conveniently.
第一の形態の親油性表面層材料の少なくとも第一の面側の最表面に親油性樹脂層を形成する方法としては、例えば、上記シート基材を親油性樹脂組成物含有ワニスに含浸させ、これを加熱乾燥する方法、あるいは、上記シート基材をメラミン樹脂ワニスに含浸させ、加熱乾燥した後、第一の面側に親油性樹脂組成物含有ワニスを塗工し、これを加熱乾燥する方法、などにより実施することができる。 As a method of forming the lipophilic resin layer on the outermost surface on at least the first surface side of the lipophilic surface layer material of the first form, for example, the above-mentioned sheet base material is impregnated in the oleophilic resin composition-containing varnish, A method of heating and drying this, or a method of impregnating the above-mentioned sheet base material into a melamine resin varnish and drying by heating, and then applying a lipophilic resin composition-containing varnish to the first surface side and heating and drying the varnish , Etc.
第二の形態の親油性表面層材料は、親油性化粧板表面に用いられ、第一の面と、第二の面とを有し、少なくとも上記第一の面の最表面に親油性樹脂層が形成されているものである。 The lipophilic surface layer material of the second form is used for a lipophilic decorative board surface, and has a first surface and a second surface, and at least the outermost surface of the first surface has a lipophilic resin layer. Is formed.
第二の形態の表面層材料に用いられる基材は、シート状の基材であり、その材質としては特に限定されないが、好ましくは、晒しパルプなどを用いることができる。
この基材の単位面積あたりの重量としては特に限定されないが、２０〜６０ｇ／ｍ２のものを好適に用いることができる。
The base material used for the surface layer material of the second form is a sheet-like base material, and the material thereof is not particularly limited, but preferably bleached pulp or the like can be used.
Although it does not specifically limit as a weight per unit area of this base material, The thing of 20-60 g / m < 2 > can be used conveniently.
第二の形態の親油性表面層材料の少なくとも第一の面側の最表面に親油性樹脂層を形成する方法としては、例えば、上記シート基材を親油性樹脂組成物含有ワニスに含浸させ、これを加熱乾燥する方法、あるいは、上記シート基材をメラミン樹脂ワニスに含浸させ、加熱乾燥した後、第一の面側に親油性樹脂組成物含有ワニスを塗工し、これを加熱乾燥する方法、などにより実施することができる。 As a method for forming the lipophilic resin layer on the outermost surface on at least the first surface side of the lipophilic surface layer material of the second form, for example, impregnating the above-mentioned sheet base material into the oleophilic resin composition-containing varnish, A method of heating and drying this, or a method of impregnating the above-mentioned sheet base material into a melamine resin varnish and drying by heating, and then applying a lipophilic resin composition-containing varnish to the first surface side and heating and drying the varnish , Etc.
本発明において、第二の形態の親油性表面層材料を適用する場合は、これと併せて、化粧層材料を用いる。
ここで化粧層材料としては、第一の形態の親油性表面層材料に用いたのと同様の、意匠面が形成されたシート基材に、メラミン樹脂ワニスを含浸させ、これを加熱乾燥することにより製造することができる。
In the present invention, when applying the lipophilic surface layer material of the second form, a decorative layer material is used in combination with this.
Here, the decorative layer material is impregnated with a melamine resin varnish on a sheet base material on which a design surface is formed, similar to that used for the lipophilic surface layer material of the first form, and is heated and dried. Can be manufactured.
なお、第一の形態の親油性表面層材料、及び、第二の形態の親油性表面層材料の製造に際してメラミン樹脂ワニスを用いる場合は、メラミンに対するホルムアルデヒドの反応モル比（Ｆ／Ｍ比）を１．０〜４．０、好ましくは１．０〜２．０として反応させて得られたメラミン樹脂に、必要に応じて、触媒、添加剤、溶媒などを加えて調製することができる。
また、第二の形態の親油性表面層材料を適用する際に併用する化粧層材料の製造に際しても、同様にして調製したメラミン樹脂ワニスを用いることができる。
In addition, when using a melamine resin varnish in the production of the lipophilic surface layer material of the first form and the lipophilic surface layer material of the second form, the reaction molar ratio (F / M ratio) of formaldehyde to melamine is A catalyst, an additive, a solvent, etc. can be added to the melamine resin obtained by making it react as 1.0-4.0, preferably 1.0-2.0 as needed.
Moreover, the melamine resin varnish prepared similarly can be used also in the production of the decorative layer material used in combination with the application of the lipophilic surface layer material of the second form.
次に、本発明の親油性化粧板について説明する。
本発明の親油性化粧板は、以上に説明した本発明の親油性表面層材料を用いてなるものであり、上記親油性表面層材料の第一の面側を最表層としたものであることを特徴とする。
Next, the lipophilic decorative board of the present invention will be described.
The lipophilic decorative board of the present invention is formed using the lipophilic surface layer material of the present invention described above, and the first surface side of the lipophilic surface layer material is the outermost layer. It is characterized by.
本発明の親油性化粧板は、上記第一の形態の親油性表面層材料を用いた場合は、この親油性表面層材料の第二の面側に、芯材層材料を積層して製造することができる。 When the lipophilic surface layer material of the first aspect is used, the lipophilic decorative board of the present invention is manufactured by laminating the core material layer material on the second surface side of the lipophilic surface layer material. be able to.
芯材層材料は、芯材層基材に熱硬化性樹脂を含浸させてなるものである。
芯材層基材としては特に限定されないが、例えば、クラフト紙などを好適に用いることができる。
芯材層基材の単位面積あたりの重量としては特に限定されないが、例えば、１５０〜２５０ｇ／ｍ２のものを好適に用いることができる。
この芯材層材料に用いられる熱硬化性樹脂としては、例えば、フェノール樹脂、メラミン樹脂、エポキシ樹脂などが挙げられる。これらの中でも、フェノール樹脂を好適に用いることができる。
芯材層基材への熱硬化性樹脂の含浸量としては、芯材層材料に対して、熱硬化性樹脂を例えば３０〜７０重量％とすることができる。
芯材層材料は、熱硬化性樹脂のほか、必要に応じて、触媒、添加剤、溶媒などを加えた熱硬化性樹脂ワニスを調製し、これを芯材層基材に含浸させ、加熱乾燥する方法などにより製造することができる。
The core material layer material is obtained by impregnating a core material base material with a thermosetting resin.
Although it does not specifically limit as a core material layer base material, For example, a craft paper etc. can be used suitably.
Although it does not specifically limit as a weight per unit area of a core material layer base material, For example, the thing of 150-250 g / m < 2 > can be used conveniently.
Examples of the thermosetting resin used for the core material layer material include phenol resin, melamine resin, and epoxy resin. Among these, a phenol resin can be suitably used.
The amount of the thermosetting resin impregnated into the core material layer base material may be, for example, 30 to 70% by weight of the thermosetting resin with respect to the core material material.
For the core layer material, in addition to the thermosetting resin, if necessary, prepare a thermosetting resin varnish to which a catalyst, additive, solvent, etc. are added, impregnate the core layer base material, and heat dry It can manufacture by the method to do.
上記第一の形態の親油性表面層材料を用いた化粧板は、第一の形態の親油性表面層材料の第二の面側に、上記芯材層材料を一枚もしくは複数枚重ね合わせ、これを１２０〜１５
０℃、７〜１０ＭＰａで加熱加圧成形することにより製造することができる。
The decorative board using the lipophilic surface layer material of the first form is superposed on the second surface side of the lipophilic surface layer material of the first form one or more of the core material layer materials, 120 ~ 15
It can be produced by heating and pressing at 0 ° C. and 7 to 10 MPa.
本発明の化粧板は、上記第二の形態の親油性表面層材料を用いた場合は、この親油性表面層材料に、上記化粧層材料、上記芯材層材料を積層して製造することができる。
具体的には、第二の形態の親油性表面層材料の第二の面側に、上記化粧層材料の意匠面側を重ね、さらに、上記芯材層材料を一枚もしくは複数枚重ね合わせ、これを１２０〜１５０℃、７〜１０ＭＰａで加熱加圧成形することにより製造することができる。
When using the lipophilic surface layer material of the second form, the decorative board of the present invention can be manufactured by laminating the decorative layer material and the core layer material on the lipophilic surface layer material. it can.
Specifically, the design surface side of the decorative layer material is superimposed on the second surface side of the lipophilic surface layer material of the second form, and further, one or a plurality of the core material layer materials are superimposed, This can be produced by heating and pressing at 120 to 150 ° C. and 7 to 10 MPa.
以上に説明したように、本発明の親油性化粧板は、本発明の親油性表面層材料を用いたものであり、化粧板の最表面に親油性樹脂組成物からなる親油性樹脂層が形成されている。
これにより、本発明の親油性化粧板は、表面が平滑な鏡面仕上げタイプ（特に濃色柄）において、油性成分による汚れが付着しても目立ちにくく、かつ、払拭作業によって容易に汚れが見えなくなるというものである。
本発明の親油性化粧板は表面が親油性であるため、油性成分による汚れが付着した場合、油性成分による汚れは、表面にぬれ拡がることとなり（化粧板表面と油性成分による汚れとの接触角は小さくなり）、平滑に近い状態となる。そのため、汚れの付着部分へ光が入射しても乱反射が起こりにくくなり、汚れは目立ちにくくなる。また、付着した汚れを払拭した場合、化粧板表面に汚れが残ったとしても、付着した汚れははじかれることなく、平滑にぬれ拡がっているため、視認できなくなる。
本発明の親油性化粧板は、このような特性を有することにより、油汚れや指紋汚れが目立ちやすくなるキッチン廻り、テーブル、家具などに特に好適に用いることができるものである。
As described above, the lipophilic decorative board of the present invention uses the lipophilic surface layer material of the present invention, and the lipophilic resin layer comprising the lipophilic resin composition is formed on the outermost surface of the decorative board. Has been.
As a result, the lipophilic decorative board of the present invention is not noticeable even if dirt due to oily components adheres to a mirror-finished type (particularly dark color pattern) with a smooth surface, and the dirt cannot be easily seen by wiping work. That's it.
Since the surface of the lipophilic decorative board of the present invention is lipophilic, when dirt due to the oil component adheres, the dirt due to the oil component spreads on the surface (the contact angle between the decorative board surface and the dirt due to the oil component). Becomes smaller) and becomes almost smooth. For this reason, even if light is incident on the dirt adhering portion, irregular reflection hardly occurs and the dirt becomes inconspicuous. Further, when the attached dirt is wiped off, even if dirt remains on the surface of the decorative board, the attached dirt is not repelled and spreads smoothly and becomes invisible.
Since the lipophilic decorative board of the present invention has such characteristics, it can be used particularly suitably for kitchens, tables, furniture and the like where oil stains and fingerprint stains are easily noticeable.
以下、実施例により本発明を具体的に説明する。
実施例、比較例で示される「％」は「重量％」を表す。
Hereinafter, the present invention will be described specifically by way of examples.
“%” Shown in Examples and Comparative Examples represents “% by weight”.
＜実施例１＞
（１）親油性表面層材料
（１．１）表面層材料
表面層用のシート基材として、坪量８０ｇ／ｍ２のカーボンブラック含有化粧紙を用いた。
上記シート基材を、メラミン樹脂（Ｆ／Ｍ比１．７）の樹脂固形分に対して、触媒（ＭＲＣユニテック社製「キャタニット」）２．０％を添加したメラミン樹脂ワニス（メラミン樹脂固形分５０％）に含浸させ、これを加熱乾燥して、表面層材料に対するメラミン樹脂分５０％、揮発分６％の表面層材料を得た。
（１．２）親油性表面層材料
メラミン樹脂（Ｆ／Ｍ比１．７）の樹脂固形分に対して、触媒（ＭＲＣユニテック社製「キャタニット」）を２．０％、油変性アルキド樹脂（ＤＩＣ社製「ＷＡＴＥＲＳＯＬ ＢＣ−３０１０」、有効成分５９．２％、半乾性油変性、短油タイプ）を有効成分として５％添加した親油性樹脂組成物含有ワニス（メラミン樹脂固形分５０％）を得た。
上記で得られた表面層材料の第一の面側に、スプレーコート法で上記親油性樹脂組成物含有ワニスを塗布し、これを加熱乾燥して、固形分量で１０ｇ／ｍ２の親油性樹脂層が形成された親油性表面層材料を得た。
<Example 1>
(1) Lipophilic surface layer material (1.1) Surface layer material A carbon black-containing decorative paper having a basis weight of 80 g / m 2 was used as a sheet base material for the surface layer.
Melamine resin varnish (melamine resin solid) in which 2.0% of catalyst (“Catanit” manufactured by MRC Unitech Co., Ltd.) is added to the above-mentioned sheet base material with respect to the resin solid content of melamine resin (F / M ratio 1.7). 50%), and this was heated and dried to obtain a surface layer material having a melamine resin content of 50% and a volatile content of 6% with respect to the surface layer material.
(1.2) Lipophilic surface layer material 2.0% of catalyst (“Catanit” manufactured by MRC Unitech Co., Ltd.) and oil-modified alkyd resin based on resin solids of melamine resin (F / M ratio 1.7) (Variant resin composition-containing varnish (melamine resin solid content 50%) to which 5% is added as an active ingredient (“WATERSOL BC-3010” manufactured by DIC Corporation, active ingredient 59.2%, semi-drying oil modified, short oil type)) Got.
The above-mentioned lipophilic resin composition-containing varnish is applied to the first surface side of the surface layer material obtained above by a spray coating method, and this is heated and dried to obtain a lipophilic resin having a solid content of 10 g / m 2. A lipophilic surface layer material having a layer formed thereon was obtained.
（２）芯材層材料
芯材層基材として、坪量１９０ｇ／ｍ２の未晒しクラフト紙を用いた。
上記基材を、フェノール（Ｐ）とホルムアルデヒド（Ｆ）とを反応モル比（Ｆ／Ｐ比）＝１．３として反応させて得られたレゾール型フェノール樹脂ワニス（フェノール樹脂固
形分５０％）に含浸させ、これを加熱乾燥し、芯材層材料に対するフェノール樹脂分３５％、揮発分６％の芯材層材料を得た。
(2) Core material layer material Unbleached kraft paper having a basis weight of 190 g / m 2 was used as the core material layer base material.
A resol type phenol resin varnish (phenol resin solid content 50%) obtained by reacting the base material with a reaction molar ratio (F / P ratio) = 1.3 of phenol (P) and formaldehyde (F). This was impregnated and dried by heating to obtain a core layer material having a phenol resin content of 35% and a volatile content of 6% with respect to the core layer material.
（３）親油性化粧板
上記（１）で得られた親油性表面層材料の第二の面側に、上記（２）で得られた芯材層材料５枚を重ね合わせ、さらに、外側に鏡面仕上げのプレスプレートを配して、圧力８ＭＰａ、化粧板最高温度１４０℃となるようにプレス装置で加熱加圧成形して、厚みが１．２ｍｍの親油性化粧板を得た。
(3) Lipophilic decorative board On the second surface side of the lipophilic surface layer material obtained in (1) above, 5 core material layer materials obtained in (2) above are superimposed, and further on the outside A mirror-finished press plate was arranged, and heat press molding was performed with a press device so that the pressure was 8 MPa and the decorative plate maximum temperature was 140 ° C., to obtain a lipophilic decorative plate having a thickness of 1.2 mm.
＜実施例２＞
実施例１の（１．２）において、さらに、メラミン樹脂固形分に対してエポキシ樹脂（阪本薬品工業社製「ＳＲ−２ＥＧ」、有効成分１００％、エチレングリコール系エポキシ樹脂、水溶性）を２％添加して親油性樹脂組成物含有ワニスを得た以外は、実施例１と同様にして親油性表面層材料及び親油性化粧板を得た。
<Example 2>
In Example 1, (1.2), epoxy resin ("SR-2EG" manufactured by Sakamoto Yakuhin Kogyo Co., Ltd., active ingredient 100%, ethylene glycol-based epoxy resin, water-soluble) is further added to the melamine resin solid content. An oleophilic surface layer material and an oleophilic decorative board were obtained in the same manner as in Example 1, except that the varnish was added to obtain an oleophilic resin composition-containing varnish.
＜実施例３＞
実施例１の（１．２）において、メラミン樹脂（Ｆ／Ｍ比１．７）の樹脂固形分に対して、触媒（ＭＲＣユニテック社製「キャタニット」）を２．０％、油変性アルキド樹脂（ＤＩＣ社製「ＢＥＣＫＯＳＯＬ １３０８」、有効成分５０．０％、不乾性油変性、短油タイプ）を有効成分として０．５％添加し、さらに、界面活性剤（日本エマルジョン社製「ＥＭＡＬＥＸ ＨＣ−８０」、非イオン性界面活性剤、ＨＬＢ＝１４．６、水溶性）を０．１％添加して親油性樹脂組成物含有ワニス（メラミン樹脂固形分５０％）を得た以外は、実施例１と同様にして親油性表面層材料及び親油性化粧板を得た。
<Example 3>
In (1.2) of Example 1, 2.0% of catalyst (“Catanit” manufactured by MRC Unitech Co., Ltd.) and oil-modified alkyd with respect to the resin solid content of melamine resin (F / M ratio 1.7) Resin (“BECKOSOL 1308” manufactured by DIC, 50.0% active ingredient, non-drying oil modified, short oil type) is added as an active ingredient in an amount of 0.5%, and a surfactant (“EMALEX HC manufactured by Nippon Emulsion Co., Ltd.) is added. -80 ", nonionic surfactant, HLB = 14.6, water-soluble) 0.1% was added to obtain a lipophilic resin composition-containing varnish (melamine resin solid content 50%). In the same manner as in Example 1, a lipophilic surface layer material and a lipophilic decorative board were obtained.
＜実施例４＞
実施例１の（１．２）において、メラミン樹脂（Ｆ／Ｍ比１．７）の樹脂固形分に対して、触媒（ＭＲＣユニテック社製「キャタニット」）を２．０％、油変性アルキド樹脂（ＤＩＣ社製「ＢＥＣＫＯＳＯＬ １３０８」、有効成分５０．０％、不乾性油変性、短油タイプ）を有効成分として０．５％添加し、さらに、界面活性剤（日本エマルジョン社製「ＥＭＡＬＥＸ ＨＣ−８０」、非イオン性界面活性剤、ＨＬＢ＝１４．６、水溶性）を０．１％、エポキシ樹脂（阪本薬品工業社製「ＳＲ−２ＥＧ」、有効成分１００％、エチレングリコール系エポキシ樹脂、水溶性）を０．２％添加して親油性樹脂組成物含有ワニス（メラミン樹脂固形分５０％）を得た以外は、実施例１と同様にして親油性表面層材料及び親油性化粧板を得た。
<Example 4>
In (1.2) of Example 1, 2.0% of catalyst (“Catanit” manufactured by MRC Unitech Co., Ltd.) and oil-modified alkyd with respect to the resin solid content of melamine resin (F / M ratio 1.7) Resin (“BECKOSOL 1308” manufactured by DIC, 50.0% active ingredient, non-drying oil modified, short oil type) is added as an active ingredient in an amount of 0.5%, and a surfactant (“EMALEX HC manufactured by Nippon Emulsion Co., Ltd.) is added. -80 ", nonionic surfactant, HLB = 14.6, water-soluble) 0.1%, epoxy resin (" SR-2EG "manufactured by Sakamoto Yakuhin Kogyo Co., Ltd., active ingredient 100%, ethylene glycol epoxy resin) And water-soluble) 0.2% was added to obtain a lipophilic resin composition-containing varnish (melamine resin solid content 50%), in the same manner as in Example 1, the lipophilic surface layer material and the lipophilic decorative board. Got.
＜比較例１＞
実施例１の（１．２）において、油変性アルキド樹脂を添加せずに樹脂組成物含有ワニス（メラミン樹脂固形分５０％）を得た以外は、実施例１と同様にして表面層材料及び化粧板を得た。
<Comparative Example 1>
In (1.2) of Example 1, the surface layer material and the varnish were obtained in the same manner as in Example 1 except that the resin composition-containing varnish (melamine resin solid content 50%) was obtained without adding the oil-modified alkyd resin. A decorative board was obtained.
実施例で得られた親油性化粧板及び比較例で得られた化粧板について、評価を実施した。結果を表１に示す。
評価項目ならびに評価方法は以下の通りである。
Evaluation was performed about the lipophilic decorative board obtained in the Example and the decorative board obtained in the comparative example. The results are shown in Table 1.
Evaluation items and evaluation methods are as follows.
（１）化粧板の外観
化粧板の外観を目視で確認し、以下の基準により判定した。
Ａ：白濁ムラや光沢低下がなく、良好である
Ｂ：白濁ムラや光沢低下があり、不良である。
（２）皮脂汚れの目立ちにくさ
皮脂膜の量が最も多い部分の１つである鼻に、人差し指を押し当てて皮脂膜を転写させ、その指を化粧板の表面に、一定荷重（１ｋｇ）で押し当てて再転写させた。皮脂膜を転写させた化粧板表面を目視及び拡大観察（４００倍）し、以下の基準により評価した。
Ａ：目視観察の場合、皮脂膜の付着汚れが目立ちにくい（白く見えにくい）。拡大観察の場合、皮脂膜がはじかれておらず、なじんで付着している。
Ｂ：目視観察の場合、皮脂膜の付着汚れが目立ちやすい（白く見える）。拡大観察の場合、皮脂膜がはじかれて付着している。
（３）皮脂汚れの払拭性
上記（２）と同様の方法で化粧板表面に皮脂膜を付着させ、これをティッシュペーパーを用いて、一定荷重（１ｋｇ）で払拭作業を行った後、目視観察及び拡大観察（３０００倍）し、以下の基準により評価した。
Ａ：目視観察の場合、皮脂膜の付着汚れが目立たない（白く見えない）。拡大観察の場合、皮脂膜がはじかれておらず、なじんで付着している。
Ｂ：目視観察の場合、皮脂膜の付着汚れが目立ちやすい（白く見える）。拡大観察の場合、皮脂膜がはじかれて付着している。
（４）油汚れの払拭性
油（トリオレイン）を染み込ませたティッシュペーパーに、人差し指を押し当ててトリオレインを転写させ、その指を化粧板の表面に、一定荷重（１ｋｇ）で押し当てて再転写させた。化粧板表面に付着させたトリオレインを、ティッシュペーパーを用いて、一定荷重（１ｋｇ）で払拭作業を行った後、目視観察及び拡大観察（３０００倍）し、以下の基準により評価した。
Ａ：目視観察の場合、トリオレインの付着汚れが目立たない（白く見えない）。拡大観察の場合、トリオレインがはじかれておらず、なじんで付着している。
Ｂ：目視観察の場合、トリオレインの付着汚れが目立ちやすい（白く見える）。拡大観察の場合、トリオレインがはじかれて付着している。
(1) Appearance of decorative plate The external appearance of the decorative plate was visually confirmed and judged according to the following criteria.
A: There is no white turbidity unevenness and gloss reduction, and it is good.
(2) Hard to notice sebum dirt The index finger is pressed against the nose, which is one of the parts where the amount of sebum film is the largest, to transfer the sebum film, and the finger is applied to the surface of the decorative board at a constant load (1 kg) And re-transferred. The decorative board surface to which the sebum film was transferred was visually and magnified (400 times) and evaluated according to the following criteria.
A: In the case of visual observation, the adhered dirt of the sebum film is not noticeable (it is difficult to look white). In the case of magnified observation, the sebum film is not repelled but is adhered.
B: In the case of visual observation, the adhered dirt of the sebum film is easily noticeable (appears white). In the case of magnified observation, the sebum film is repelled and adhered.
(3) Sebum dirt wiping property A sebum film is adhered to the surface of the decorative board in the same manner as in (2) above, and this is visually observed after performing a wiping operation with a constant load (1 kg) using tissue paper. And the magnified observation (3000 times) was evaluated according to the following criteria.
A: In the case of visual observation, the adhered dirt of the sebum film is not noticeable (not white). In the case of magnified observation, the sebum film is not repelled but is adhered.
B: In the case of visual observation, the adhered dirt of the sebum film is easily noticeable (appears white). In the case of magnified observation, the sebum film is repelled and adhered.
(4) Oil dirt wiping property Press the index finger on the tissue paper soaked with oil (triolein) to transfer the triolein, and press the finger against the surface of the decorative board with a constant load (1 kg). Re-transferred. The triolein adhered to the decorative plate surface was wiped off with a tissue paper at a constant load (1 kg), then visually observed and magnified (3000 times), and evaluated according to the following criteria.
A: In the case of visual observation, triolein adhering dirt is not noticeable (does not appear white). In the case of magnified observation, the triolein is not repelled but adheres.
B: In the case of visual observation, the adhesion stain of triolein is easily noticeable (appears white). In the case of magnified observation, triolein is repelled and adhered.
実施例１〜４は、メラミン樹脂と、油変性アルキド樹脂を含有する親油性樹脂組成物に
より形成されている親油性樹脂層を表面に有する本発明の親油性化粧板であり、外観、皮脂汚れの目立ちにくさ、皮脂汚れ及び油汚れの払拭性において良好なものであった。
比較例１は、油変性アルキド樹脂を含有しない樹脂層を表面に有する化粧板であるが、皮脂汚れの目立ちにくさ、皮脂汚れ及び油汚れの払拭性において実施例と比較して低下が見られた。
Examples 1-4 are the lipophilic decorative boards of this invention which have the lipophilic resin layer formed on the surface by the lipophilic resin composition containing a melamine resin and an oil-modified alkyd resin. It was good in the conspicuousness of the oil, and the wiping property of sebum stains and oil stains.
Comparative Example 1 is a decorative board having a resin layer that does not contain an oil-modified alkyd resin on its surface. However, it is difficult to notice sebum dirt, and the wiping property of sebum dirt and oil dirt is lower than that of the example. It was.
本発明の親油性化粧板は、メラミン樹脂化粧板としての表面性能を損なうことなく、従来のメラミン樹脂化粧板と比較して、油性成分による汚れが付着しても目立ちにくく、付着した汚れを払拭した場合、化粧板表面に汚れが残ったとしても、付着した汚れははじかれることなく、平滑にぬれ拡がっているため、視認できなくなる。
本発明の親油性化粧板は、このような特性を有することにより、油汚れや指紋汚れが目立ちやすくなるキッチン廻り、テーブル、家具などに特に好適に用いることができるものである。
The lipophilic decorative board of the present invention is less noticeable even if dirt due to oily components adheres to it, and does not impair the surface performance as a melamine resin decorative board. In this case, even if dirt remains on the surface of the decorative board, the attached dirt is not repelled and spreads smoothly and is not visible.
Since the lipophilic decorative board of the present invention has such characteristics, it can be used particularly suitably for kitchens, tables, furniture and the like where oil stains and fingerprint stains are easily noticeable.
Claims (5)
前記親油性表面層材料は、第一の面と、第二の面とを有し、少なくとも前記第一の面の最表面に親油性樹脂層が形成されており、
前記親油性樹脂層は、メラミン樹脂と、油変性アルキド樹脂とを含有する親油性樹脂組成物により形成されていることを特徴とする親油性表面層材料。 A lipophilic surface layer material used for a decorative board surface,
The lipophilic surface layer material has a first surface and a second surface, and at least the outermost surface of the first surface has a lipophilic resin layer formed thereon,
The lipophilic surface layer material, wherein the lipophilic resin layer is formed of a lipophilic resin composition containing a melamine resin and an oil-modified alkyd resin.
前記親油性表面層材料の第一の面側を最表面としたものであることを特徴とする親油性化粧板。 A lipophilic decorative board using the lipophilic surface layer material according to any one of claims 1 to 4,
A lipophilic decorative board, wherein the first surface side of the lipophilic surface layer material is the outermost surface.