JP2011025173A - Method of forming pattern face - Google Patents
Method of forming pattern face Download PDFInfo
- Publication number
- JP2011025173A JP2011025173A JP2009174477A JP2009174477A JP2011025173A JP 2011025173 A JP2011025173 A JP 2011025173A JP 2009174477 A JP2009174477 A JP 2009174477A JP 2009174477 A JP2009174477 A JP 2009174477A JP 2011025173 A JP2011025173 A JP 2011025173A
- Authority
- JP
- Japan
- Prior art keywords
- colored
- paint
- transparent
- undercoat
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、新規な模様面の形成方法に関するものである。本発明は、主に建築物や土木構造物等に対して適用することができる。 The present invention relates to a novel pattern surface forming method. The present invention can be applied mainly to buildings, civil engineering structures, and the like.
従来、建築物の内外装等における壁材の一つとして、大理石等の天然石材が使用されている。このような天然石材は、多彩な色柄模様を有しており、美観性に優れたものである。但し、天然石材を加工して得られる壁材は、一般に重く、厚いため、基材への負荷が大きくなりやすい。また、このような壁材は、価格が高いという短所もある。
そこで、大理石等の天然石材に類似した模様を形成させる方法が、種々提案されている。具体的には、塗装方法の工夫により、ランダムなぼかし模様を形成して、天然石材調の模様を表現しようとする方法等が知られている。
Conventionally, natural stone materials such as marble have been used as one of the wall materials in the interior and exterior of buildings. Such natural stone materials have various color patterns and are excellent in aesthetics. However, since the wall material obtained by processing natural stone is generally heavy and thick, the load on the base material tends to increase. In addition, such a wall material has a disadvantage that it is expensive.
Therefore, various methods for forming a pattern similar to natural stone such as marble have been proposed. Specifically, a method of expressing a natural stone-like pattern by forming a random blur pattern by a device of the painting method is known.
例えば、特開平１０−１８３０３０号公報（特許文献１）には、複数の顔料成分を含む塗料組成物を塗装した後、溶剤を含む混合液体を吹き付けることによって、大理石調の模様を形成することが記載されている。
特開平１０−２１６６２６号公報（特許文献２）には、下層塗料を塗装後、下層塗料が乾燥する前に、上層塗料を水滴状に散布する方法が記載されている。
しかしながら、このような方法では、いずれも、塗装に供する材料や装置について、工場内で諸条件を管理しつつ塗装する必要がある。すなわち、実際の建築物等に対して適用できるものではない。
For example, Japanese Patent Laid-Open No. 10-183030 (Patent Document 1) discloses that a marble-like pattern is formed by spraying a mixed liquid containing a solvent after coating a coating composition containing a plurality of pigment components. Are listed.
Japanese Patent Application Laid-Open No. 10-216626 (Patent Document 2) describes a method of spraying the upper layer paint in the form of water droplets after the lower layer paint is applied and before the lower layer paint is dried.
However, in any of these methods, it is necessary to coat materials and equipment used for painting while managing various conditions in the factory. That is, it cannot be applied to an actual building or the like.
本発明は、上述のような問題点に鑑みなされたものであり、建築物等において、美観性の高いランダムなぼかし模様を形成することができる簡便な塗装方法を提供することを目的とするものである。 The present invention has been made in view of the above-described problems, and an object thereof is to provide a simple coating method capable of forming a random blur pattern with high aesthetics in a building or the like. It is.
本発明者は、上記目的を達成するため鋭意検討を行った結果、着色粒状物を含む下塗材を塗付した後、当該下塗材における着色粒状物よりも透明性が高い透明着色粒状物を含む上塗材を塗付する方法に想到し、本発明を完成させるに到った。 As a result of intensive studies to achieve the above object, the present inventor, after applying an undercoat material containing a colored granular material, includes a transparent colored granular material having higher transparency than the colored granular material in the undercoat material. The inventors have conceived a method of applying a top coat material and have completed the present invention.
すなわち、本発明は以下の特徴を有するものである。 That is, the present invention has the following characteristics.
１．基材に対し、
（１）少なくとも１種以上の着色粒状物が分散媒中に分散した下塗材を塗付して、
下塗面を形成する工程、
（２）当該下塗面に対し、
前記着色粒状物よりも透明性が高い透明着色粒状物が、少なくとも１種以上分散媒中に分散した上塗材
を塗付する工程、
を行うことを特徴とする模様面の形成方法。
２．基材に対し、
（１）着色顔料濃度が５重量％を超える着色塗料より得られる着色粒状物が、少なくとも１種以上分散媒中に分散した下塗材を塗付して、下塗面を形成する工程、
（２）当該下塗面に対し、
着色顔料濃度が５重量％以下である透明着色塗料より得られる透明着色粒状物が、少なくとも１種以上分散媒中に分散した上塗材を塗付する工程、
を行うことを特徴とする模様面の形成方法。
３．前記上塗材は、
少なくとも２種以上の透明着色粒状物を含むものであり、
当該透明着色粒状物として、
着色顔料濃度が異なる２種以上の同色の透明着色粒状物
を含む１．または２．記載の模様面の形成方法。
1. For substrate
(1) Applying an undercoat material in which at least one colored granular material is dispersed in a dispersion medium,
Forming an undercoat surface,
(2) For the primer surface
A step of applying a transparent coating material in which at least one or more transparent colored particles having higher transparency than the colored particles are dispersed in a dispersion medium;
A method for forming a pattern surface, comprising:
2. For substrate
(1) A step in which a colored granular material obtained from a colored paint having a color pigment concentration exceeding 5% by weight is coated with at least one undercoat material dispersed in a dispersion medium to form an undercoat surface;
(2) For the primer surface
A step of applying a transparent coating material in which at least one transparent colored granular material obtained from a transparent colored paint having a color pigment concentration of 5% by weight or less is dispersed in a dispersion medium;
A method for forming a pattern surface, comprising:
3. The top coat material is
Including at least two or more transparent colored particulates,
As the transparent colored particulate matter,
Including two or more kinds of transparent colored particulates of the same color having different color pigment concentrations Or 2. The formation method of the described pattern surface.
本発明によれば、ランダムなぼかし模様を、簡便な方法によって形成することができる。この方法によって、天然石材に類似した模様等を得ることが可能となる。本発明は、建築物、土木構造物の壁面等に対し、美観性を付与する塗装方法として、好ましく適用することができる。 According to the present invention, a random blur pattern can be formed by a simple method. This method makes it possible to obtain a pattern similar to natural stone. INDUSTRIAL APPLICABILITY The present invention can be preferably applied as a coating method for imparting aesthetics to a wall of a building or a civil engineering structure.
以下、本発明を実施するための形態について説明する。 Hereinafter, modes for carrying out the present invention will be described.
本発明は、基材に対し、
（１）少なくとも１種以上の着色粒状物が分散媒中に分散した下塗材を塗付して、
下塗面を形成する工程（以下「工程（１）」ともいう）、
（２）当該下塗面に対し、
前記着色粒状物よりも透明性が高い透明着色粒状物が、少なくとも１種以上分散媒中に分散した上塗材を塗付する工程（以下「工程（２）」ともいう）、
を行うものである。
The present invention relates to a substrate,
(1) Applying an undercoat material in which at least one colored granular material is dispersed in a dispersion medium,
A step of forming an undercoat surface (hereinafter also referred to as “step (1)”),
(2) For the primer surface
A step of applying a coating material in which at least one or more transparent colored particles having higher transparency than the colored particles are dispersed in a dispersion medium (hereinafter also referred to as “step (2)”),
Is to do.
本発明では、このような方法を用いることにより、美観性の高いランダムなぼかし模様を形成することができ、自然感の高い仕上りを得ることが可能となる。
このような効果は、上塗材における着色粒状物が透明性を有するため、その散在状態、重なり状態等によって、下層の色柄模様の見え方に変化が生じることに起因するものである。
なお、本発明における「透明」とは、可視光透過性を有し、下層が視認できる性質のことである。
In the present invention, by using such a method, a random blur pattern with high aesthetics can be formed, and a finish with a high natural feeling can be obtained.
Such an effect is attributed to the change in the appearance of the colored pattern in the lower layer due to the scattered state, the overlapping state, etc., because the colored granular material in the top coating material has transparency.
In the present invention, “transparent” means a property having visible light transparency and allowing the lower layer to be visually recognized.
本発明は、主に、建築物、土木構造物等に適用することができる。このような部位を構成する基材としては、例えば、コンクリート、モルタル、サイディングボード、押出成形板、石膏ボード、パーライト板、合板、プラスチック板、金属板、木工板、ガラス、煉瓦、陶磁器タイル等の各種基材が挙げられる。
これら基材は、何らかの表面処理（フィラー処理、サーフェーサー処理、シーラー処理等）が施されたものや、予め着色塗料等で着色されたものでもよく、既に塗膜が形成されたものや、壁紙が貼り付けられたものであってもよい。
The present invention is mainly applicable to buildings, civil engineering structures, and the like. As a base material constituting such a part, for example, concrete, mortar, siding board, extrusion board, gypsum board, pearlite board, plywood board, plastic board, metal board, wood board, glass, brick, ceramic tile, etc. Various base materials are mentioned.
These base materials may have been subjected to some surface treatment (filler treatment, surfacer treatment, sealer treatment, etc.), or may be pre-colored with a colored paint or the like. It may be affixed.
本発明の工程（１）では、上記基材に対し、下塗材を塗付して、下塗面を形成する。この工程（１）における下塗材としては、少なくとも１種以上の着色粒状物が分散媒中に分散した形態の塗料を用いる。分散媒は、着色粒状物の色調を著しく阻害しないものであればよい。
この工程（１）により、基材の上に、着色粒状物が散在した模様面を得ることができる。
In step (1) of the present invention, a primer is applied to the substrate to form a primer surface. As the undercoat material in this step (1), a paint in a form in which at least one or more colored particles are dispersed in a dispersion medium is used. The dispersion medium may be any medium that does not significantly impair the color tone of the colored granular material.
By this step (1), it is possible to obtain a patterned surface in which colored granular materials are scattered on the substrate.
この工程（１）における下塗材としては、少なくとも１種以上の着色粒状物が含まれるものであればよいが、２種以上の異色の着色粒状物が含まれるもの、すなわち２色以上（より好ましくは３〜８色）の着色粒状物が含まれるものが好適である。このような下塗材を用いることにより、一層豊かな美観性を有する模様面を形成することができる。
着色粒状物の色調は、最終的に形成される模様に応じて適宜設定すればよい。
The undercoat material in this step (1) may be any material that contains at least one kind of colored granular material, but it contains two or more kinds of different colored particles, that is, two or more colors (more preferably 3 to 8) are preferable. By using such a primer, a pattern surface having a richer aesthetics can be formed.
What is necessary is just to set suitably the color tone of a colored granular material according to the pattern finally formed.
下塗材における着色粒状物の粒径は、通常０．１〜１０ｍｍ（好ましくは０．５〜５ｍｍ）程度である。本発明では、粒子径が異なる着色粒状物を種々組み合せることによって、意匠性の幅を広げることもできる。 The particle size of the colored granular material in the undercoat material is usually about 0.1 to 10 mm (preferably 0.5 to 5 mm). In the present invention, the range of designability can be expanded by combining various colored granular materials having different particle diameters.
下塗材における着色粒状物の比率は、通常２０〜８０重量％、好ましくは３０〜７０重量％である。 The ratio of the colored granular material in the undercoat material is usually 20 to 80% by weight, preferably 30 to 70% by weight.
下塗材における着色粒状物としては、着色塗料より得られるもの、すなわち着色塗料が粒状化されたものが好適である。着色粒状物が着色塗料に由来するものであれば、色の調製が容易となり、所望の色調が得られやすくなる。また、平坦な面が形成されやすくなる。さらに、下塗材を吹き付けた場合、着色粒状物の跳ね返りが抑制され、塗着効率が向上するという利点もある。
このような着色粒状物は、液状の着色塗料が内包された形態、着色塗料がゲル化した状態、のいずれであってもよい。
As the colored particles in the undercoat material, those obtained from the colored paint, that is, those obtained by granulating the colored paint are suitable. If the colored granular material is derived from a colored paint, the color can be easily prepared and a desired color tone can be easily obtained. In addition, a flat surface is easily formed. Further, when the undercoat material is sprayed, there is an advantage that the rebound of the colored granular material is suppressed and the coating efficiency is improved.
Such a colored granular material may be in a form in which a liquid colored paint is included or a state in which the colored paint is gelled.
このような下塗材としては、一般に多彩模様塗料として知られている形態のものが使用できる。多彩模様塗料は、ＪＩＳ Ｋ５６６７（２００２）「多彩模様塗料」に規定されており、塗料を構成する分散媒と着色粒子の組み合わせによって、水中油型（Ｏ／Ｗ型）、油中水型（Ｗ／Ｏ型）、油中油型（Ｏ／Ｏ型）及び水中水型（Ｗ／Ｗ型）の４種類に分類される。本発明における上塗材としては、特に、水中油型（Ｏ／Ｗ型）または水中水型（Ｗ／Ｗ型）の塗料が好適である。 As such a primer, a material generally known as a multicolor paint can be used. The multicolored paint is defined in JIS K5667 (2002) “Multicolored paint”. Oil-in-water type (O / W type), water-in-oil type (W / O type), oil-in-oil type (O / O type), and water-in-water type (W / W type). As the top coating material in the present invention, an oil-in-water type (O / W type) or a water-in-water type (W / W type) paint is particularly suitable.
下塗材において、着色粒状物を生成する着色塗料としては、結合材、及び顔料を含むものが使用できる。 In the undercoat material, as the colored paint for producing the colored granular material, a material containing a binder and a pigment can be used.
着色塗料における結合材としては、各種の樹脂成分が使用できる。樹脂成分としては、例えば、溶剤可溶型樹脂、非水分散型樹脂、無溶剤型樹脂、水分散型樹脂、水溶性樹脂等が挙げられる。樹脂の種類としては、例えば、アクリル樹脂、ウレタン樹脂、エポキシ樹脂、塩化ビニル樹脂、酢酸ビニル樹脂、アクリルシリコン樹脂、フッ素樹脂、ポリビニルアルコール、セルロース誘導体等、あるいはこれらの複合物等が挙げられる。このような樹脂成分は、塗膜形成後に架橋反応を生じる性質を有するものであってもよい。 Various resin components can be used as the binder in the colored paint. Examples of the resin component include solvent-soluble resins, non-water-dispersed resins, solvent-free resins, water-dispersed resins, and water-soluble resins. Examples of the resin include acrylic resin, urethane resin, epoxy resin, vinyl chloride resin, vinyl acetate resin, acrylic silicon resin, fluororesin, polyvinyl alcohol, cellulose derivative, or a composite thereof. Such a resin component may have a property of causing a crosslinking reaction after the coating film is formed.
顔料としては、着色顔料が使用できる。具体的に、着色顔料としては、例えば、酸化チタン、酸化亜鉛、アルミナ、カーボンブラック、酸化第二鉄（弁柄）、黄色酸化鉄、酸化鉄、群青、コバルトグリーン等の無機着色顔料、アゾ系、ナフトール系、ピラゾロン系、アントラキノン系、ペリレン系、キナクリドン系、ジスアゾ系、イソインドリノン系、ベンゾイミダゾール系、フタロシアニン系、キノフタロン系等の有機着色顔料、パール顔料、アルミニウム顔料、蛍光顔料等が挙げられる。このような着色顔料の１種または２種以上を組み合わせることにより、着色塗料を所望の色調に調製することができる。
着色塗料においては、このような着色顔料に加え、体質顔料を使用することもできる。体質顔料としては、例えば、炭酸カルシウム、硫酸バリウム、クレー、カオリン、陶土、タルク、珪石粉、珪藻土等が挙げられる。
Color pigments can be used as the pigment. Specifically, examples of the color pigment include titanium oxide, zinc oxide, alumina, carbon black, ferric oxide (valve), yellow iron oxide, iron oxide, ultramarine, cobalt green, and other inorganic color pigments, azo series Organic pigments such as naphthol, pyrazolone, anthraquinone, perylene, quinacridone, disazo, isoindolinone, benzimidazole, phthalocyanine, quinophthalone, pearl pigment, aluminum pigment, fluorescent pigment, etc. It is done. By combining one or more of these color pigments, a colored paint can be prepared in a desired color tone.
In the colored paint, an extender can be used in addition to such a colored pigment. Examples of extender pigments include calcium carbonate, barium sulfate, clay, kaolin, porcelain clay, talc, quartzite powder, and diatomaceous earth.
この着色塗料における着色顔料の濃度は、５重量％を超える範囲内（好ましくは５重量％を超え４０重量部以下、より好ましくは６重量％以上３０重量％以下）で設定する。着色粒状物中の着色顔料濃度をこのような範囲内に設定すれば、着色粒状物の隠ぺい性を高めることができ、上塗材中の透明着色粒状物よりも、相対的に透明性の低い着色粒状物を得ることができる。 The concentration of the color pigment in this colored paint is set within a range exceeding 5% by weight (preferably exceeding 5% by weight and not more than 40 parts by weight, more preferably not less than 6% by weight and not more than 30% by weight). If the concentration of the colored pigment in the colored granular material is set within such a range, the concealment of the colored granular material can be improved, and coloring is relatively less transparent than the transparent colored granular material in the top coating material. Granules can be obtained.
下塗材の塗装方法については、本発明の効果が奏される限り、種々の方法を採用することができるが、本発明では吹き付け塗装が好適である。
下塗材の塗付け量は、最終的な模様の種類によって異なるが、通常０．１〜１ｋｇ／ｍ２程度である。下塗材の乾燥は、通常、常温（０〜４０℃程度）で行えばよい。本発明では、下塗材が乾燥した後に、工程（２）を行えばよい。
Various methods can be employed for the coating method of the undercoat material as long as the effect of the present invention is exhibited, but spray coating is preferred in the present invention.
The application amount of the undercoat material varies depending on the final pattern type, but is usually about 0.1 to 1 kg / m 2 . The undercoat material may be usually dried at room temperature (about 0 to 40 ° C.). In the present invention, the step (2) may be performed after the primer is dried.
本発明の工程（２）では、上記下塗面に対し、下塗材中の着色粒状物よりも透明性が高い透明着色粒状物が、少なくとも１種以上分散媒中に分散した上塗材を塗付する。本発明では、このような上塗材を用いることにより、下層の色柄模様に視覚的変化を生じさせ、ランダムなぼかし模様を得ることができる。
透明着色粒状物の粒径は、通常０．１〜１０ｍｍ（好ましくは０．５〜５ｍｍ）程度である。本発明では、粒子径が異なる粒状物を種々組み合せることによって、意匠性の幅を広げることもできる。
In the step (2) of the present invention, at least one or more types of transparent colored particles having higher transparency than the colored particles in the undercoat material are applied to the undercoat surface. . In the present invention, by using such an overcoating material, it is possible to cause a visual change in the lower color pattern and obtain a random blur pattern.
The particle size of the transparent colored granular material is usually about 0.1 to 10 mm (preferably 0.5 to 5 mm). In the present invention, the range of design properties can be expanded by combining various granular materials having different particle diameters.
上塗材における透明着色粒状物としては、透明着色塗料より得られるもの、すなわち透明着色塗料が粒状化されたものが好適である。透明着色粒状物が透明着色塗料に由来するものであれば、色の調製が容易となり、所望の色調が得られやすくなる。また、平坦な面が形成されやすくなる。さらに、上塗材を吹き付けた場合、透明着色粒状物の跳ね返りが抑制され、塗着効率が向上するという利点もある。
このような透明着色粒状物は、液状の透明着色塗料が内包された形態、透明着色塗料がゲル化した状態、のいずれであってもよい。
As the transparent colored granular material in the top coating material, those obtained from the transparent colored paint, that is, those obtained by granulating the transparent colored paint are suitable. If the transparent colored granular material is derived from the transparent colored paint, the color can be easily prepared and a desired color tone can be easily obtained. In addition, a flat surface is easily formed. Further, when the top coating material is sprayed, there is an advantage that the rebound of the transparent colored particulate matter is suppressed and the coating efficiency is improved.
Such a transparent colored granular material may be in a form in which a liquid transparent colored paint is included or in a state in which the transparent colored paint is gelled.
このような上塗材は、分散媒中に、透明着色塗料の粒状物が分散したものである。分散媒は、透明着色粒状物の色調を著しく阻害しないものであればよい。
このような上塗材は、前記下塗材と同様に、一般に多彩模様塗料として知られている塗料の技術に基づき、製造することができる。本発明における上塗材としては、特に、水中油型（Ｏ／Ｗ型）または水中水型（Ｗ／Ｗ型）の塗料が好適である。
Such an overcoating material is a dispersion medium in which particles of transparent colored paint are dispersed. The dispersion medium may be any medium that does not significantly impair the color tone of the transparent colored granular material.
Such a top coating material can be produced based on a coating technique generally known as a multicolored paint, like the undercoat material. As the top coating material in the present invention, an oil-in-water type (O / W type) or a water-in-water type (W / W type) paint is particularly suitable.
上塗材における透明着色塗料としては、結合材、及び顔料を含むものが使用できる。透明着色塗料の色調は、所望の仕上げ外観に応じて、適宜設定すればよい。
透明着色塗料における結合材、顔料としては、工程（１）で説明したものと同様のものが使用できる。
透明着色塗料における着色顔料の濃度は、下塗材における着色粒状物よりも透明性が高くなる範囲内で適宜設定すればよいが、通常は５重量％以下（好ましくは０．００１重量％以上３重量％以下、より好ましくは０．０１重量％以上２重量％以下）である。透明着色塗料の色調は、最終的に形成される模様に応じて適宜設定すればよい。
As the transparent coloring paint in the top coating material, those containing a binder and a pigment can be used. What is necessary is just to set the color tone of a transparent coloring paint suitably according to a desired finishing external appearance.
As the binder and the pigment in the transparent coloring paint, the same materials as described in the step (1) can be used.
The concentration of the color pigment in the transparent coloring paint may be appropriately set within a range in which the transparency is higher than that of the colored granular material in the undercoat material, but is usually 5% by weight or less (preferably 0.001% by weight or more and 3% by weight). % Or less, more preferably 0.01 wt% or more and 2 wt% or less). What is necessary is just to set suitably the color tone of a transparent coloring paint according to the pattern finally formed.
上塗材における透明着色粒状物は、１種であってもよい。すなわち、本発明では、透明着色粒子が１種（１色）のみである上塗材が使用できる。本発明における上塗材は、透明着色粒子の散在状態、重なり状態等の差異によって、視覚的効果を奏するものである。そのため、多種多色の着色粒子が含まれる一般的な多彩模様塗料とは異なり、１種の着色粒子のみでも構成できるのである。 The transparent coloring granular material in the top coating material may be one kind. That is, in the present invention, a top coating material having only one type (one color) of transparent colored particles can be used. The top coating material in the present invention has a visual effect due to the difference in the dispersed state and the overlapping state of the transparent colored particles. For this reason, unlike a general multicolored paint that includes a variety of multicolored colored particles, it can be configured with only one type of colored particles.
本発明の上塗材は、２種以上の透明着色粒子が含まれるものであってもよい。この場合、上塗材としては、着色顔料濃度が異なる２種以上の同色の透明着色粒状物を含むものが好適である。このように、同色であるが、着色顔料濃度が異なる２種以上の透明着色粒子が含まれることにより、全体的な仕上り外観における視覚的変化が豊かとなり、美観性を高めることができる。 The topcoat material of the present invention may contain two or more types of transparent colored particles. In this case, as the top coating material, one containing two or more types of transparent colored particulates having the same color and different color pigment concentrations is suitable. Thus, by including two or more kinds of transparent colored particles having the same color but different color pigment concentrations, the visual change in the overall finished appearance can be enriched and the aesthetics can be enhanced.
なお、本発明における「同色」とは、視覚的に略同じ色として認識できることを意味する。具体的には、相互の色差が、通常５以下（好ましくは４以下、より好ましくは３以下）であればよい。この色差（△Ｅ）は、白紙を背景として用い、対象物の色データ（Ｌ＊、ａ＊、ｂ＊）を測定することにより、算出することができる。色差は、色差計を用いて測定することができる。測定時の対象物の膜厚は、５０μｍ程度とすればよい。 The “same color” in the present invention means that it can be visually recognized as substantially the same color. Specifically, the color difference between them is usually 5 or less (preferably 4 or less, more preferably 3 or less). This color difference (ΔE) can be calculated by measuring the color data (L * , a * , b * ) of the object using white paper as the background. The color difference can be measured using a color difference meter. What is necessary is just to let the film thickness of the target object at the time of a measurement be about 50 micrometers.
上塗材における透明着色粒状物の比率は、通常２０〜８０重量％、好ましくは３０〜７０重量％である。 The ratio of the transparent colored granular material in the top coating material is usually 20 to 80% by weight, preferably 30 to 70% by weight.
上塗材の塗装方法については、本発明の効果が奏される限り、種々の方法を採用することができるが、本発明では吹き付け塗装が好適である。
上塗材の塗付け量は、最終的な模様の種類によって異なるが、通常０．１〜１ｋｇ／ｍ２程度である。上塗材の乾燥は、通常、常温で行えばよい。
Various methods can be employed for the coating method of the top coating material as long as the effects of the present invention are achieved, but spray coating is preferred in the present invention.
The amount of the top coat applied varies depending on the final pattern type, but is usually about 0.1 to 1 kg / m 2 . The top coat material may be usually dried at room temperature.
本発明では、上塗材の塗膜が乾燥した後、必要に応じクリヤー塗料を塗付することもできる。特に耐候性が要求される構造物外部の部位に施工する際には、保護の目的でクリヤー塗料を塗付するのが好ましい。
また、本発明では、目地棒や目地型枠等の目地材の使用によって、格子状、幾何学模様状等の目地部を形成することもできる。この場合は、目地色となる色調で塗装を施した基材に、目地材を貼り付けた後、必要に応じ中塗材等を塗付した後、上記工程を行い、その後に目地材を除去すればよい。
In the present invention, after the coating film of the top coat material is dried, a clear paint can be applied as necessary. It is preferable to apply a clear paint for the purpose of protection, particularly when the construction is performed on a part outside the structure where weather resistance is required.
Moreover, in this invention, joint parts, such as a grid | lattice shape and a geometric pattern shape, can also be formed by using joint materials, such as a joint rod and a joint form. In this case, after applying the joint material to the base material that has been painted in the color tone that becomes the joint color, apply the intermediate coating material, etc., if necessary, and then perform the above steps, and then remove the joint material. That's fine.
以下に実施例を示し、本発明の特徴をより明確にする。 Examples are given below to clarify the features of the present invention.
（下塗材）
下塗材としては、以下に示すものを用意した。
(Priming material)
As the primer, the following materials were prepared.
・下塗材１
白色粒子（アクリル樹脂、二酸化チタン、脂肪族炭化水素系溶剤を主成分とする着色塗料の粒状物、着色顔料濃度１４重量％、粒子径約４ｍｍ）と、淡黄色粒子（アクリル樹脂、黄色酸化鉄、二酸化チタン、脂肪族炭化水素系溶剤を主成分とする着色塗料の粒状物、着色顔料濃度１３重量％、粒子径約２ｍｍ）と、淡灰色粒子（アクリル樹脂、二酸化チタン、黒色酸化鉄、脂肪族炭化水素系溶剤を主成分とする着色塗料の粒状物、着色顔料濃度１４重量％、粒子径約１ｍｍ）が水性媒体中に分散した水中油型の多彩模様塗料。白色粒子：淡黄色粒子：淡灰色粒子＝４０：３０：３０（重量比率）。
・ Prime material 1
White particles (colored paint particles mainly composed of acrylic resin, titanium dioxide, aliphatic hydrocarbon solvent, color pigment concentration 14% by weight, particle diameter of about 4 mm) and light yellow particles (acrylic resin, yellow iron oxide) , Titanium dioxide, granules of colored paint mainly composed of aliphatic hydrocarbon solvent, color pigment concentration 13% by weight, particle diameter about 2 mm) and light gray particles (acrylic resin, titanium dioxide, black iron oxide, fat An oil-in-water multicolor pattern paint in which particles of a colored paint mainly composed of an aromatic hydrocarbon solvent, a color pigment concentration of 14% by weight, and a particle diameter of about 1 mm are dispersed in an aqueous medium. White particles: light yellow particles: light gray particles = 40: 30: 30 (weight ratio).
・下塗材２
黒色粒子（アクリル樹脂、黒色酸化鉄、黄色酸化鉄、弁柄、酸化チタン、脂肪族炭化水素系溶剤を主成分とする着色塗料の粒状物、着色顔料濃度１６重量％、粒子径約３ｍｍ）と、灰色粒子（アクリル樹脂、黒色酸化鉄、二酸化チタン、脂肪族炭化水素系溶剤を主成分とする着色塗料の粒状物、着色顔料濃度１３重量％、粒子径約１ｍｍ）と、灰紫色粒子（アクリル樹脂、弁柄、フタロシアニンブルー、二酸化チタン、脂肪族炭化水素系溶剤を主成分とする着色塗料の粒状物、着色顔料濃度１７重量％、粒子径約２ｍｍ）が水性媒体中に分散した水中油型の多彩模様塗料。黒色粒子：灰色粒子：灰紫色粒子＝３０：３５：３５（重量比率）。
・ Prime material 2
Black particles (acrylic resin, black iron oxide, yellow iron oxide, petal, titanium oxide, colored paint granules mainly composed of aliphatic hydrocarbon solvent, color pigment concentration of 16% by weight, particle diameter of about 3 mm) and , Gray particles (acrylic resin, black iron oxide, titanium dioxide, colored paint granules mainly composed of aliphatic hydrocarbon solvent, color pigment concentration 13% by weight, particle diameter of about 1 mm) and gray purple particles (acrylic) Resin, petal, phthalocyanine blue, titanium dioxide, colored paint granules mainly composed of aliphatic hydrocarbon solvent, color pigment concentration 17% by weight, particle diameter of about 2 mm) dispersed in an aqueous medium Colorful pattern paint. Black particles: gray particles: gray purple particles = 30: 35: 35 (weight ratio).
（上塗材）
上塗材としては、以下に示すものを用意した。
(Coating material)
As the top coating material, the following materials were prepared.
・上塗材１
容器内に水５００重量部を仕込み、攪拌を行いながらポリビニルアルコール１０重量部と、消泡剤１重量部とを均一に混合することにより、分散媒Ａを製造した。
次に、別の容器内にアクリル樹脂液（固形分５０重量％）２００重量部を仕込み、攪拌を行いながら白色顔料液（酸化チタン６０重量％分散液）５重量部と、体質顔料１３０重量部と、粘性調整剤４重量部と、溶剤１５６重量部と、消泡剤５重量部とを均一に混合することにより透明着色塗料Ａ（着色顔料濃度０．６重量％）を製造した。
上述の分散媒Ａに対し、チタン系架橋剤を３重量部加えて均一に混合した後、さらに攪拌を継続しながら透明着色塗料Ａを徐々に添加・分散することにより、約１ｍｍの透明白色粒子が分散した分散液Ａを得た。
上塗材１としては、この分散液Ａをそのまま使用した。
・ Coating material 1
Dispersion medium A was produced by charging 500 parts by weight of water into a container and uniformly mixing 10 parts by weight of polyvinyl alcohol and 1 part by weight of an antifoaming agent while stirring.
Next, 200 parts by weight of an acrylic resin liquid (solid content 50% by weight) is charged in another container, and 5 parts by weight of a white pigment liquid (60% by weight of titanium oxide dispersion) and 130 parts by weight of an extender pigment are stirred. Then, 4 parts by weight of a viscosity modifier, 156 parts by weight of a solvent, and 5 parts by weight of an antifoaming agent were uniformly mixed to produce a transparent colored paint A (colored pigment concentration 0.6% by weight).
After adding 3 parts by weight of a titanium-based cross-linking agent to the above-mentioned dispersion medium A and mixing it uniformly, the transparent colored paint A is gradually added and dispersed while continuing to stir. A dispersion A in which was dispersed was obtained.
As the top coating material 1, this dispersion A was used as it was.
・上塗材２
透明着色塗料Ａに代えて、下記透明着色塗料Ｂを使用した以外は、分散液Ａと同様の製造方法で分散液Ｂを得た。この分散液Ｂは、約２ｍｍの透明白色粒子が分散したものであった。
透明着色塗料Ｂ：アクリル樹脂液２００重量部、白色顔料液（酸化チタン６０重量％分散液）１０重量部、体質顔料１３０重量部、粘性調整剤５重量部、溶剤１５０重量部、消泡剤５重量部からなる塗料（着色顔料濃度１．２重量％）。
・ Coating material 2
A dispersion B was obtained by the same production method as the dispersion A except that the transparent coloring paint B described below was used instead of the transparent coloring paint A. This dispersion B was a dispersion of transparent white particles of about 2 mm.
Transparent coloring paint B: 200 parts by weight of acrylic resin liquid, 10 parts by weight of white pigment liquid (titanium oxide 60% by weight dispersion), 130 parts by weight of extender pigment, 5 parts by weight of viscosity adjusting agent, 150 parts by weight of solvent, defoaming agent 5 Paint consisting of parts by weight (color pigment concentration 1.2% by weight).
以上の方法で得られた分散液Ａと分散液Ｂを、６０：４０の重量比率で混合することにより、上塗材２を製造した。 The topcoat material 2 was manufactured by mixing the dispersion A and the dispersion B obtained by the above method in a weight ratio of 60:40.
・上塗材３
透明着色塗料Ａに代えて、下記透明着色塗料Ｃを使用した以外は、分散液Ａと同様の製造方法で分散液Ｃを得た。この分散液Ｃは、約１ｍｍの透明黒色粒子が分散したものであった。
透明着色塗料Ｃ：アクリル樹脂液２００重量部、黒色顔料液（黒色酸化鉄１０重量％分散液）１重量部、体質顔料１３０重量部、粘性調整剤４重量部、溶剤１６０重量部、消泡剤５重量部からなる塗料（着色顔料濃度０．０２重量％）。
上塗材３としては、この分散液Ｃをそのまま使用した。
・ Coating material 3
A dispersion C was obtained by the same production method as the dispersion A except that the transparent coloring paint C described below was used instead of the transparent coloring paint A. This dispersion C was a dispersion of transparent black particles of about 1 mm.
Transparent coloring paint C: 200 parts by weight of acrylic resin liquid, 1 part by weight of black pigment liquid (black iron oxide 10% dispersion), 130 parts by weight of extender pigment, 4 parts by weight of viscosity modifier, 160 parts by weight of solvent, defoaming agent Paint consisting of 5 parts by weight (color pigment concentration 0.02% by weight).
As the top coating material 3, this dispersion C was used as it was.
（実施例１）
予めシーラー（白色）が塗装されたスレート板に対し、下塗材１を塗付け量０．５ｋｇ／ｍ２にて吹き付け塗装し、４時間乾燥した。
次に、この下塗面の上に、上塗材１を塗付け量０．５ｋｇ／ｍ２にて吹き付け塗装し、２４時間乾燥した。なお、塗装及び乾燥は、すべて標準状態（気温２３℃、相対湿度５０％）にて行った。
以上の方法により得られた模様面は、ランダムなぼかし模様の仕上りとなり、大理石調の美観性を有するものであった。
Example 1
Undercoat material 1 was spray-coated at a coating amount of 0.5 kg / m 2 on a slate plate previously coated with a sealer (white), and dried for 4 hours.
Next, the top coating material 1 was sprayed onto the undercoat surface at a coating amount of 0.5 kg / m 2 and dried for 24 hours. The coating and drying were all performed in standard conditions (temperature 23 ° C., relative humidity 50%).
The pattern surface obtained by the above method has a random blurred pattern finish and has a marble-like aesthetics.
（実施例２）
予めシーラー（白色）が塗装されたスレート板に対し、下塗材１を塗付け量０．５ｋｇ／ｍ２にて吹き付け塗装し、４時間乾燥した。
次に、この下塗面の上に、上塗材２を塗付け量０．５ｋｇ／ｍ２にて吹き付け塗装し、２４時間乾燥した。なお、塗装及び乾燥は、すべて標準状態にて行った。上塗材２の着色粒子を構成する透明着色塗料Ａと、透明着色塗料Ｂとの色差は０．８であった。
以上の方法により得られた模様面は、ランダムなぼかし模様の仕上りとなり、大理石調の美観性を有するものであった。全体的な仕上り性は、実施例１よりも一層良好であった。
(Example 2)
Undercoat material 1 was spray-coated at a coating amount of 0.5 kg / m 2 on a slate plate previously coated with a sealer (white), and dried for 4 hours.
Next, the top coat material 2 was sprayed onto the undercoat surface at a coating amount of 0.5 kg / m 2 and dried for 24 hours. In addition, all painting and drying were performed in the standard state. The color difference between the transparent colored paint A constituting the colored particles of the top coat 2 and the transparent colored paint B was 0.8.
The pattern surface obtained by the above method has a random blurred pattern finish and has a marble-like aesthetics. The overall finish was even better than Example 1.
（実施例３）
予めシーラー（白色）が塗装されたスレート板に対し、下塗材２を塗付け量０．５ｋｇ／ｍ２にて吹き付け塗装し、４時間乾燥した。
次に、この下塗面の上に、上塗材３を塗付け量０．５ｋｇ／ｍ２にて吹き付け塗装し、２４時間乾燥した。なお、塗装及び乾燥は、すべて標準状態にて行った。
以上の方法により得られた模様面は、ランダムなぼかし模様の仕上りとなり、大理石調の美観性を有するものであった。
(Example 3)
The undercoat material 2 was sprayed onto the slate plate previously coated with a sealer (white) at a coating amount of 0.5 kg / m 2 and dried for 4 hours.
Next, the top coat material 3 was sprayed onto the undercoat surface at a coating amount of 0.5 kg / m 2 and dried for 24 hours. In addition, all painting and drying were performed in the standard state.
The pattern surface obtained by the above method has a random blurred pattern finish and has a marble-like aesthetics.
（比較例１）
予めシーラー（白色）が塗装されたスレート板に対し、下塗材１を塗付け量０．５ｋｇ／ｍ２にて吹き付け塗装し、２４時間乾燥した。
以上の方法により得られた模様面は、個々の着色粒子が明瞭に視認されるものであった。
(Comparative Example 1)
Undercoat material 1 was spray-coated at a coating amount of 0.5 kg / m 2 on a slate plate previously coated with a sealer (white) and dried for 24 hours.
In the pattern surface obtained by the above method, individual colored particles were clearly visible.
Claims (3)
（１）少なくとも１種以上の着色粒状物が分散媒中に分散した下塗材を塗付して、
下塗面を形成する工程、
（２）当該下塗面に対し、
前記着色粒状物よりも透明性が高い透明着色粒状物が、少なくとも１種以上分散媒中に分散した上塗材
を塗付する工程、
を行うことを特徴とする模様面の形成方法。 For substrate
(1) Applying an undercoat material in which at least one colored granular material is dispersed in a dispersion medium,
Forming an undercoat surface,
(2) For the primer surface
A step of applying a transparent coating material in which at least one or more transparent colored particles having higher transparency than the colored particles are dispersed in a dispersion medium;
A method for forming a pattern surface, comprising:
（１）着色顔料濃度が５重量％を超える着色塗料より得られる着色粒状物が、少なくとも１種以上分散媒中に分散した下塗材を塗付して、下塗面を形成する工程、
（２）当該下塗面に対し、
着色顔料濃度が５重量％以下である透明着色塗料より得られる透明着色粒状物が、少なくとも１種以上分散媒中に分散した上塗材を塗付する工程、
を行うことを特徴とする模様面の形成方法。 For substrate
(1) A step in which a colored granular material obtained from a colored paint having a color pigment concentration exceeding 5% by weight is coated with at least one undercoat material dispersed in a dispersion medium to form an undercoat surface;
(2) For the primer surface
A step of applying a transparent coating material in which at least one transparent colored granular material obtained from a transparent colored paint having a color pigment concentration of 5% by weight or less is dispersed in a dispersion medium;
A method for forming a pattern surface, comprising:
少なくとも２種以上の透明着色粒状物を含むものであり、
当該透明着色粒状物として、
着色顔料濃度が異なる２種以上の同色の透明着色粒状物
を含む請求項１または２記載の模様面の形成方法。 The top coat material is
Including at least two or more transparent colored particulates,
As the transparent colored particulate matter,
The method for forming a pattern surface according to claim 1 or 2, comprising two or more transparent colored particulates of the same color having different color pigment concentrations.