JP2010142449A - Medical tape or sheet, and method of manufacturing the same - Google Patents
Medical tape or sheet, and method of manufacturing the same Download PDFInfo
- Publication number
- JP2010142449A JP2010142449A JP2008323528A JP2008323528A JP2010142449A JP 2010142449 A JP2010142449 A JP 2010142449A JP 2008323528 A JP2008323528 A JP 2008323528A JP 2008323528 A JP2008323528 A JP 2008323528A JP 2010142449 A JP2010142449 A JP 2010142449A
- Authority
- JP
- Japan
- Prior art keywords
- solution
- pressure
- medical
- sensitive adhesive
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
本発明は、皮膚患部の保護、皮膚へのガーゼ又はチューブなどの医療用部材の固定、更に、整体等における体形補強や補正、あるいはスポーツのテーピング等を目的として皮膚に貼着して用いられる医療・健康用粘着テープ又はシートに関する。 The present invention provides a medical device that is applied to the skin for the purpose of protecting the affected area of the skin, fixing a medical member such as a gauze or tube to the skin, and reinforcing or correcting the body shape of the body, taping for sports, etc. -It relates to a health adhesive tape or sheet.
皮膚患部の保護、皮膚へのガーゼ又はチューブなどの医療用部材の固定、更に、整体等における体形補強や補正、あるいはスポーツのテーピング等を目的として皮膚に貼着して用いられる医療・健康用粘着テープ又はシート（以下この医療・健康用粘着テープ又はシートを医療用粘着シートと称す）としては、フィルムや布地や紙からなる基材の片面に粘着剤層が設けられた医療用粘着テープが知られている(例えば、特許文献１参照)。 Medical / health adhesive used to protect the affected skin area, fix gauze or tubes and other medical components to the skin, and reinforce and correct body shape in body trimming, or taping sports As a tape or sheet (hereinafter, this medical / health pressure-sensitive adhesive tape or sheet is referred to as a medical pressure-sensitive adhesive sheet), a medical pressure-sensitive adhesive tape having a pressure-sensitive adhesive layer provided on one side of a substrate made of a film, fabric or paper is known. (For example, see Patent Document 1).
医療用粘着テープは皮膚に直接貼付して用いられるため、使用後に剥がされると、皮膚の角質層をいっしょに引き剥がしてしまい、皮膚のバリア機能が損なわれ、これが、かぶれや炎症の因となるという問題があった。
本発明の目的は、皮膚のバリア機能を損なうことの少ない医療用粘着シートを提供することである。 An object of the present invention is to provide a medical pressure-sensitive adhesive sheet that does not impair the barrier function of the skin.
本発明の要旨とするところは、基材に粘着剤層が積層されてなり、前記粘着剤層に合成リン脂質ポリマーを含む保湿剤が含有された医療・健康用テープまたはシートであることにある。 The gist of the present invention lies in a medical / health tape or sheet in which a pressure-sensitive adhesive layer is laminated on a base material and a moisturizing agent containing a synthetic phospholipid polymer is contained in the pressure-sensitive adhesive layer. .
前記医療・健康用テープまたはシートにおいては、前記合成リン脂質ポリマーが下記一般式（１）
で表されるポリマー、
下記一般式（２）
で表されるポリマーから選択される１種以上のポリマーであり得る。
In the medical / health tape or sheet, the synthetic phospholipid polymer is represented by the following general formula (1):
A polymer represented by
The following general formula (2)
It may be one or more kinds of polymers selected from the polymers represented by:
また、本発明の要旨とするところは、下記一般式（１）
で表されるポリマー、
下記一般式（２）
で表されるポリマーから選択される１種以上のポリマーを、０．８〜１０重量％の低級アルコールを含有するトルエンに溶解して溶液を得る工程、
該溶液を粘着剤の有機溶剤溶液と混合して混合液を得る工程、
該混合液、または該混合液を有機溶剤で希釈した希釈液、からなる塗布液を基材に塗布し乾燥する工程
を含む医療・健康用テープまたはシートの製造方法であることにある。
The gist of the present invention is the following general formula (1).
A polymer represented by
The following general formula (2)
A step of obtaining a solution by dissolving one or more polymers selected from the polymers represented by formula (1) in toluene containing 0.8 to 10% by weight of a lower alcohol;
Mixing the solution with an organic solvent solution of an adhesive to obtain a mixed solution;
It is a method for producing a medical / health tape or sheet comprising a step of applying a coating solution comprising the mixed solution or a diluted solution obtained by diluting the mixed solution with an organic solvent to a substrate and drying.
前記医療・健康用テープまたはシートの製造方法においては、前記粘着剤がシリコーン系の粘着剤であり得る。 In the manufacturing method of the medical / health tape or sheet, the adhesive may be a silicone-based adhesive.
本発明によると、皮膚のバリア機能を損なうことの少ない医療用粘着シートが提供される。 ADVANTAGE OF THE INVENTION According to this invention, the medical adhesive sheet with little impairing the barrier function of skin is provided.
本発明の医療用粘着シートは、基材に粘着剤層が積層されてなる医療用シートであって、前記粘着剤層に合成リン脂質ポリマーが含有されてなる。 The medical pressure-sensitive adhesive sheet of the present invention is a medical sheet in which a pressure-sensitive adhesive layer is laminated on a base material, and the pressure-sensitive adhesive layer contains a synthetic phospholipid polymer.
粘着剤層は、皮膚と粘着する層であって、粘着性のポリマーを主成分としてなる。 The pressure-sensitive adhesive layer is a layer that adheres to the skin, and is mainly composed of an adhesive polymer.
粘着剤層を構成する粘着剤としては、例えば、スチレン−イソブチレン−スチレン共重合体を主成分とする合成ゴム系粘着剤、ポリウレタン系粘着剤、ポリシロキサン系粘着剤、天然ゴム系粘着剤、ポリエーテル系粘着剤、アクリル系粘着剤等が挙げられ、これらを単独で又は２種以上混合して使用することができる。 Examples of the pressure-sensitive adhesive constituting the pressure-sensitive adhesive layer include a synthetic rubber-based pressure-sensitive adhesive mainly composed of a styrene-isobutylene-styrene copolymer, a polyurethane-based pressure-sensitive adhesive, a polysiloxane-based pressure-sensitive adhesive, a natural rubber-based pressure-sensitive adhesive, Examples include ether-based pressure-sensitive adhesives and acrylic pressure-sensitive adhesives, and these can be used alone or in admixture of two or more.
基材としては、フィルム、編織物、不織布などが挙げられる。 Examples of the substrate include films, knitted fabrics, and nonwoven fabrics.
合成リン脂質ポリマーは、ヒトの細胞を構成する細胞膜のホスファチジルコリンの極性基をもつポリマーであり下記一般式（３）で示される基を有する重合体である。 The synthetic phospholipid polymer is a polymer having a polar group of phosphatidylcholine of a cell membrane constituting a human cell, and a polymer having a group represented by the following general formula (3).
また、この合成リン脂質ポリマーは、再公表特許（Ａ１）：国際公開番号ＷＯ００／０１４２４号公報に記載されているものである。 The synthetic phospholipid polymer is described in Republished Patent (A1): International Publication No. WO00 / 01424.
この合成リン脂質ポリマーとしては２−メタアクリロイルオキシエチルホスホリルコリンを構成単位にもつポリマーが例示される。例えば、その化学構造は下記一般式（４）で示される。このポリマーは分子量が通常５〜２００万のものが用いられる。 Examples of the synthetic phospholipid polymer include polymers having 2-methacryloyloxyethyl phosphorylcholine as a structural unit. For example, the chemical structure is represented by the following general formula (4). This polymer has a molecular weight of usually 5 to 2 million.
合成リン脂質ポリマーの他の一例は、下記一般式（５）で示されるコポリマーである。 Another example of the synthetic phospholipid polymer is a copolymer represented by the following general formula (5).
合成リン脂質ポリマーのさらに他の一例は、下記一般式（６）で示されるコポリマーである。 Yet another example of the synthetic phospholipid polymer is a copolymer represented by the following general formula (6).
一般式（５）で示されるコポリマーと一般式（６）で示されるコポリマーは混合されて用いられてもよい。その他の合成リン脂質ポリマーも含めて合成リン脂質ポリマーは１種が単独で用いられてもよい。２種以上が混合されて用いられてもよい。 The copolymer represented by the general formula (5) and the copolymer represented by the general formula (6) may be mixed and used. One type of synthetic phospholipid polymer including other synthetic phospholipid polymers may be used alone. Two or more kinds may be mixed and used.
本発明において、粘着剤層は、例えば、粘着剤を構成するポリマーを有機溶剤に溶かした溶液または粘着剤を構成するポリマーのエマルジョンに合成リン脂質ポリマーを混合して混合液としたのち、この混合液を必要ならば希釈して塗布液となし、基材に塗布し乾燥して得ることができる。このようにして本発明の医療用粘着シートが得られる。基材表面に積層形成された粘着剤層の厚さは０．０１〜０．５ｍｍ程度である。 In the present invention, the pressure-sensitive adhesive layer is prepared, for example, by mixing a synthetic phospholipid polymer with a solution obtained by dissolving a polymer constituting the pressure-sensitive adhesive in an organic solvent or a polymer emulsion constituting the pressure-sensitive adhesive, and then mixing the mixture. If necessary, the solution can be diluted to form a coating solution, which can be applied to a substrate and dried. Thus, the medical pressure-sensitive adhesive sheet of the present invention is obtained. The thickness of the pressure-sensitive adhesive layer formed on the substrate surface is about 0.01 to 0.5 mm.
従来、医療用粘着シートを皮膚に貼着したのち剥がすと、剥がすときに皮膚から角層が医療用粘着シートに付着して剥がされるという現象があった。角層が剥がされた皮膚は、表面から水分が蒸発しやすくなり乾燥状態となる。乾燥状態となった皮膚は外部からの刺激物に対する保護機能が低下して、かぶれやただれを起しやすくなる。 Conventionally, when a medical pressure-sensitive adhesive sheet is attached to the skin and then peeled off, there has been a phenomenon in which the stratum corneum adheres to the medical pressure-sensitive adhesive sheet when peeled off. The skin from which the stratum corneum has been peeled is easily dried by moisture evaporating from the surface. The dried skin has a reduced protective function against external irritants and tends to cause rashes and sores.
本発明の医療用粘着シートは、粘着剤層に合成リン脂質ポリマーが含有されているので、皮膚に貼着したときにその合成リン脂質ポリマーが皮膚表面に付着し、医療用粘着シートが剥がされた後もその合成リン脂質ポリマーが皮膚表面に残留する。残留した合成リン脂質ポリマーは皮膚の水分の蒸発を抑制して皮膚を保湿するはたらきをする。これにより、医療用粘着シートが剥がされたのちも皮膚が保湿されて乾燥状態になることが抑制され、外部からの刺激物に対する保護機能が保たれて、かぶれやただれを起しにくい。 Since the medical adhesive sheet of the present invention contains a synthetic phospholipid polymer in the adhesive layer, the synthetic phospholipid polymer adheres to the skin surface when attached to the skin, and the medical adhesive sheet is peeled off. After that, the synthetic phospholipid polymer remains on the skin surface. The remaining synthetic phospholipid polymer serves to suppress the evaporation of moisture from the skin and moisturize the skin. This prevents the skin from being moisturized and dried after the medical pressure-sensitive adhesive sheet is peeled off, maintains a protective function against external stimuli, and is unlikely to cause rashes and sores.
また、一般に医療用粘着シートは粘着剤層に添加物が含有されると粘着力が低下する傾向にあるが、本発明の医療用粘着シートは粘着力の低下をともなわずに合成リン脂質ポリマーを添加されているものである。 In general, a medical adhesive sheet tends to have a reduced adhesive strength when an additive is contained in the adhesive layer. However, the medical adhesive sheet of the present invention has a synthetic phospholipid polymer without decreasing the adhesive strength. It is what has been added.
粘着剤層を構成する粘着剤は一般には疎水性で、有機溶剤には可溶であるが水には不溶であるので、合成リン脂質ポリマーが親水性であると、合成リン脂質ポリマーの水溶液がその有機溶剤に不溶なため、粘着剤溶液と合成リン脂質ポリマーの水溶液とを混合して得た混合液を塗布液として基材に塗布・乾燥して得られた粘着剤層においては、粘着剤と合成リン脂質ポリマーとが均一に混合されておらず、粘着剤中に合成リン脂質ポリマーが島状に分散した状態となることが多い。かかる状態では、上述の保護機能や粘着力に製品ごとのバラツキを生ずるおそれがある。また粘着剤層の表面に合成リン脂質ポリマーが筋状あるいは点状に分布して外観にむらがある。従って、合成リン脂質ポリマーと粘着剤とは塗布液中で均一に混合もしくは溶解されていることが好ましく、そのためには本発明において用いられる合成リン脂質ポリマーとしては疎水性のポリマーであることが好ましい。 The pressure-sensitive adhesive constituting the pressure-sensitive adhesive layer is generally hydrophobic and soluble in organic solvents but insoluble in water. Therefore, if the synthetic phospholipid polymer is hydrophilic, an aqueous solution of the synthetic phospholipid polymer Because it is insoluble in the organic solvent, in the pressure-sensitive adhesive layer obtained by applying and drying a mixed solution obtained by mixing a pressure-sensitive adhesive solution and an aqueous solution of a synthetic phospholipid polymer onto a substrate, the pressure-sensitive adhesive And the synthetic phospholipid polymer are not uniformly mixed, and the synthetic phospholipid polymer is often dispersed in islands in the adhesive. In such a state, there is a possibility that the above-described protection function and adhesive force may vary from product to product. In addition, the synthetic phospholipid polymer is distributed in the form of streaks or dots on the surface of the pressure-sensitive adhesive layer, and the appearance is uneven. Therefore, it is preferable that the synthetic phospholipid polymer and the pressure-sensitive adhesive are uniformly mixed or dissolved in the coating solution. For that purpose, the synthetic phospholipid polymer used in the present invention is preferably a hydrophobic polymer. .
疎水性の合成リン脂質ポリマーとしては上記一般式５で表されるポリマーが挙げられる。一般式５で表されるポリマーで市場から入手できるものとしては、日油株式会社製：商品名Ｌｉｐｉｄｕｒｅ（リピジュア）−Ｓが挙げられる。
Examples of the hydrophobic synthetic phospholipid polymer include a polymer represented by the above
一般式５で表されるポリマーを用いた本発明の医療用粘着シートは、一般式５で表されるポリマーを、０．８〜１０重量％の低級アルコールを含有するトルエンに溶解して溶液（トルエン１００重量部に対して０．８〜１０重量部の低級アルコールを含有）を得て、その溶液を粘着剤の有機溶剤溶液と混合して混合液をなし、その混合液を塗布液として基材に塗布し乾燥して得ることができる。あるいはその混合液を有機溶剤で希釈した希釈液を塗布液として基材に塗布し乾燥して得ることができる。
The medical pressure-sensitive adhesive sheet of the present invention using the polymer represented by the
この低級アルコールは、炭素数６以下の低級アルコールであり、メタノール、エタノール、イソプロパノール、ｎ−プロパノール、ｎ−ブタノールなどが例示される。低級アルコールは単品であってもよく、異種のものの混合品であってもよい。人体への適用性のうえでは、エタノールが好ましい。 This lower alcohol is a lower alcohol having 6 or less carbon atoms, and examples thereof include methanol, ethanol, isopropanol, n-propanol, and n-butanol. The lower alcohol may be a single item or a mixture of different types. In view of applicability to the human body, ethanol is preferable.
このようにして得られた医療用粘着シートにおいては、粘着剤層を構成する粘着剤中に極めて均一に合成リン脂質ポリマーがほぼ相溶状態で混在しており、上述の保護機能や粘着力に製品ごとのバラツキがなく、粘着剤層の外観も美麗である。 In the medical pressure-sensitive adhesive sheet obtained in this way, the synthetic phospholipid polymer is mixed in a substantially uniform state in the pressure-sensitive adhesive constituting the pressure-sensitive adhesive layer. There is no variation between products, and the appearance of the adhesive layer is also beautiful.
一般式２で表されるポリマーから溶液を得る場合、トルエンに対する低級アルコールの含有比率が０．８重量％を下回ると、溶剤中へのポリマーの完全な溶解状態が得られず、また、この溶液と粘着剤溶液とを混合した混合液からなる塗布液は均一な溶解状態が得られず、従って、この塗布液を用いて得られる医療用粘着シートの粘着剤層中に合成リン脂質ポリマーが島状に不均一に分散した状態となる。トルエンに対する低級アルコールの含有比率が１０重量％を超えて多くなると、溶剤中へのポリマーの溶解状態は良好であるものの、この溶液と粘着剤溶液とを混合した塗布液は均一な溶解状態が得られず、従って、この塗布液を用いて得られる医療用粘着シートの粘着剤層中に合成リン脂質ポリマーが島状に不均一に分散した状態となる。 In the case of obtaining a solution from the polymer represented by the general formula 2, if the content ratio of the lower alcohol to toluene is less than 0.8% by weight, the polymer cannot be completely dissolved in the solvent. A coating solution composed of a mixture of a liquid and a pressure-sensitive adhesive solution cannot obtain a uniform dissolved state. Therefore, a synthetic phospholipid polymer is not islanded in the pressure-sensitive adhesive layer of a medical pressure-sensitive adhesive sheet obtained using this coating solution. In a non-uniformly distributed state. When the content ratio of the lower alcohol to toluene exceeds 10% by weight, the polymer is dissolved well in the solvent, but the coating solution obtained by mixing this solution and the adhesive solution has a uniform dissolved state. Therefore, the synthetic phospholipid polymer is dispersed in an island-like manner in the pressure-sensitive adhesive layer of the medical pressure-sensitive adhesive sheet obtained by using this coating solution.
本発明の医療用粘着シートの構成と効果は以下の実験例で示される。
実験１
The configuration and effects of the medical pressure-sensitive adhesive sheet of the present invention are shown in the following experimental examples.
粘着剤の調整と粘着シートの作成
合成リン脂質ポリマーとして、日油株式会社製の合成リン脂質ポリマー（タイプ：リピジュアＳ）を用い、粘着剤としてメチルフェニル系ポリシロキサンを用いた。
１重量％のエタノールを含有するトルエン１００重量部に合成リン脂質ポリマー１．５重量部を溶解して溶液−１を作成した。
粘着剤はトルエン、キシレンの重量比８：２の混合溶剤に溶解させて溶液−２を得た。溶液−２中の粘着剤の濃度は６０重量％である。
溶液−２と溶液−１とを、粘着剤と合成リン脂質ポリマーとの重量比が９９：１になるように混合し、均一に混合された混合液を得て塗布液−１とした。
溶液−２と溶液−１とを、粘着剤と合成リン脂質ポリマーとの重量比が９９．５：０．５になるように混合し、均一に混合された混合溶液を得て塗布液−２とした。
溶液−２と溶液−１とを、粘着剤と合成リン脂質ポリマーとの重量比が９９．９：０．１になるように混合し、均一に混合された混合溶液を得て塗布液−３とした。
基材として、フィルム（ＰＥＴ系、岡田紙業社製、厚さ２５μｍ）を用い、塗布液−１を基材に塗布し乾燥して粘着シート−１を得た。粘着剤層の面積当たりの塗布量は３０ｇ／ｍ２）であった。粘着剤層内には合成リン脂質ポリマーが存在を目視できないほどに均一に分散していた。
また、塗布液−２を塗布液として用いたほかは塗布液−１の場合と同様にして、粘着シート−２を得た。粘着剤層内には合成リン脂質ポリマーが存在を目視できないほどに均一に分散していた。
また、塗布液−３を塗布液として用いたほかは塗布液−１の場合と同様にして、粘着シート−３を得た。粘着剤層内には合成リン脂質ポリマーが存在を目視できないほどに均一に分散していた。
さらに、溶液−２を塗布液として用いたほかは粘着シート−１の場合と同様にして粘着シート−４を得た。
Preparation of Adhesive and Preparation of Adhesive Sheet As a synthetic phospholipid polymer, a synthetic phospholipid polymer (Type: Lipidure S) manufactured by NOF Corporation was used, and methylphenyl polysiloxane was used as an adhesive.
Solution-1 was prepared by dissolving 1.5 parts by weight of a synthetic phospholipid polymer in 100 parts by weight of toluene containing 1% by weight of ethanol.
The pressure-sensitive adhesive was dissolved in a mixed solvent of toluene and xylene in a weight ratio of 8: 2 to obtain a solution-2. The concentration of the adhesive in Solution-2 is 60% by weight.
Solution-2 and solution-1 were mixed so that the weight ratio of the pressure-sensitive adhesive and the synthetic phospholipid polymer was 99: 1, and a uniformly mixed solution was obtained to obtain coating solution-1.
Solution-2 and solution-1 are mixed so that the weight ratio of the pressure-sensitive adhesive and the synthetic phospholipid polymer is 99.5: 0.5, and a uniformly mixed solution is obtained to obtain coating solution-2. It was.
Solution-2 and Solution-1 are mixed so that the weight ratio of the pressure-sensitive adhesive and the synthetic phospholipid polymer is 99.9: 0.1, and a uniformly mixed solution is obtained to obtain a coating solution-3. It was.
A film (PET system, manufactured by Okada Paper Industries Co., Ltd., thickness: 25 μm) was used as the base material, and the coating liquid-1 was applied to the base material and dried to obtain an adhesive sheet-1. The coating amount per area of the pressure-sensitive adhesive layer was 30 g / m 2 ). The synthetic phospholipid polymer was uniformly dispersed in the pressure-sensitive adhesive layer so that the presence of the polymer could not be visually observed.
Moreover, except having used the coating liquid-2 as a coating liquid, it carried out similarly to the case of the coating liquid-1, and obtained the adhesive sheet-2. The synthetic phospholipid polymer was uniformly dispersed in the pressure-sensitive adhesive layer so that the presence of the polymer could not be visually observed.
Moreover, except having used the coating liquid-3 as a coating liquid, it carried out similarly to the case of the coating liquid-1, and obtained the adhesive sheet-3. The synthetic phospholipid polymer was uniformly dispersed in the pressure-sensitive adhesive layer so that the presence of the polymer could not be visually observed.
Furthermore, except having used the solution-2 as a coating liquid, the adhesive sheet-4 was obtained like the case of the adhesive sheet-1.
角層保護効果の確認
（１）水分蒸散量
下記の３ケースについて皮膚表面の経皮水分蒸散量を水分蒸散計（Tewameter TM210:Courage+Khazaka社製）によって測定した。
Confirmation of stratum corneum protection effect (1) Moisture transpiration The transdermal moisture transpiration on the skin surface of the following three cases was measured with a moisture transpiration meter (Tewameter TM210: Courage + Khazaka).
ケース１（合成リン脂質ポリマー１％）：粘着シート−１（サイズ：３ｃｍ角）を腕の皮膚に貼着し１分間放置後引き剥がした。引き剥がし後１分間放置して粘着シート−１を貼着した部位の皮膚の水分蒸散量を測定した。この操作を腕の同一部位で３０回繰り返した。
Case 1 (
ケース２（粘着剤のみ）：粘着シート−１に代えて粘着シート−４を用いたほかはケース１と同様にして皮膚表面の水分率の経時変化を測定した。
Case 2 (adhesive only): The moisture content of the skin surface over time was measured in the same manner as in
ケース３（貼着なし）：粘着シートを貼着せずに腕の同一部位で水分蒸散量の経時変化をケース１、２の場合と同様の時間間隔で測定した。
測定結果を図１に示す。
Case 3 (no sticking): The time-dependent change of moisture transpiration was measured at the same time interval as in
The measurement results are shown in FIG.
図１に示すように、ケース３（正常皮膚）において、水分蒸散量は測定期間中ほぼ一定であった。
ケース２（合成リン脂質ポリマー不使用）においては、粘着シート剥離回数が１７回を超えると回数を経るごとに水分蒸散量が増加する。
ケース１（合成リン脂質ポリマー使用）においては、粘着シート剥離回数が２０回を超えると回数を経るごとに水分蒸散量が増加傾向にあるが、増加の程度（グラフの勾配）はケース２に比べて約３分の１ほどでありきわめて小さいといえる。
As shown in FIG. 1, in case 3 (normal skin), the amount of water transpiration was substantially constant during the measurement period.
In Case 2 (without using a synthetic phospholipid polymer), when the number of times the pressure-sensitive adhesive sheet is peeled exceeds 17, the amount of moisture transpiration increases with each passage.
In case 1 (use of synthetic phospholipid polymer), the amount of moisture transpiration tends to increase every time the adhesive sheet peels over 20 times, but the degree of increase (gradient in the graph) is higher than in case 2 It is about one-third, and can be said to be extremely small.
（２）皮膚の赤み
ケース４：粘着シート−１に代えて粘着シート−２を用いたほかはケース１と同様にして皮膚への貼着、引き剥がしの操作を３０回繰り返した。
ケース１、２、４につき、貼着、引き剥がしの操作を３０回繰り返した後の粘着シートを貼着した部位の皮膚の赤みを観察した。この赤みは、最後の剥離直後では、いずれのケースについても同程度であったが、最後の剥離後３日間経過後では、ケース１、２がケース４に比べて赤みの程度が軽減されていた。最後の剥離後３日間経過後の赤みの程度の観察結果を表１に示す。
(2) Skin redness case 4: The procedure of sticking to the skin and peeling was repeated 30 times in the same manner as in
About
保湿効果
粘着シート１、２、３、４のそれぞれにつき皮膚に３時間貼着して除去した後、剥離部位の皮膚水分量を経時的に測定した。結果を図２に示す。粘着シート４（粘着剤のみ）の剥離部位に比べて粘着シート１、２、３（合成リン脂質ポリマー含有）の剥離部位は、皮膚水分量を高い水準で維持していることがわかった。水分率の測定には、（有）アサヒバイオメッド社製の角層膜厚・水分計を用いた。
Each of the moisturizing effect
粘着シートの粘着力
粘着シートの粘着力と、粘着剤への合成リン脂質ポリマーの添加比率との関係を図３に示す。合成リン脂質ポリマーの含有比率の異なる粘着シートは、粘着シート１、２、３などの作成方法に準じて作成した。粘着力はＪＩＳ
Ｚ ０２３７に準拠し、被着体：ＳＵＳ３０４鋼板、引張速度：３００ｍｍ／分、剥離角度：１８０°、２３℃、６５％ＲＨにて測定した。
FIG. 3 shows the relationship between the adhesive strength of the adhesive sheet and the ratio of the synthetic phospholipid polymer added to the adhesive. The pressure-sensitive adhesive sheet having a different content ratio of the synthetic phospholipid polymer was prepared according to the method for preparing the pressure-
In accordance with Z 0237, measurement was performed at adherend: SUS304 steel plate, tensile speed: 300 mm / min, peeling angle: 180 °, 23 ° C., 65% RH.
図３より、合成リン脂質ポリマーを含有する粘着剤を用いた粘着シートは、合成リン脂質ポリマーを含有しない粘着剤を用いた粘着シートと同等の粘着力を有することがわかる。
このような実験例からわかるように、本発明の医療用粘着シートは、粘着テープ（シート）を繰り返し貼付する場合の皮膚バリアの機能の低下を防ぐことができる。また、粘着テープ（シート）貼付後の皮膚への色素沈着を軽減させることができる。さらに、添付部位に保湿性を付与することができる。
FIG. 3 shows that the pressure-sensitive adhesive sheet using the pressure-sensitive adhesive containing the synthetic phospholipid polymer has the same adhesive strength as the pressure-sensitive adhesive sheet using the pressure-sensitive adhesive not containing the synthetic phospholipid polymer.
As can be seen from these experimental examples, the medical pressure-sensitive adhesive sheet of the present invention can prevent a decrease in the function of the skin barrier when the pressure-sensitive adhesive tape (sheet) is repeatedly applied. Moreover, the pigmentation to the skin after sticking an adhesive tape (sheet) can be reduced. Furthermore, moisture retention can be imparted to the attached site.
また、本発明の医療用粘着シートは、粘着力を低下させることなく皮膚バリアの機能の低下を防ぐことができる。 Moreover, the medical adhesive sheet of this invention can prevent the fall of the function of a skin barrier, without reducing adhesive force.
本発明の医療用粘着シートにおいては、粘着剤に合成リン脂質ポリマーに加えてさらにオリーブオイルを添加することにより、皮膚の保護効果が増強される。これは、合成リン脂質ポリマーが一部オリーブオイルに溶解することで合成リン脂質ポリマーの移行性が向上したことによるものと推察される。オリーブオイルは粘着剤に対して０．５〜２重量％添加されることが好ましい。オリーブオイル以外でも、合成高分子ポリマーが溶解あるいは部分溶解するオイル成分であれば、同様の効果が期待できるものと考えられる。例えば、エルカ酸オクチルドデシル、ミスチリン酸オクチルドデシル、オレイン酸、セバシン酸ジオクチルなどが挙げられる。 In the medical pressure-sensitive adhesive sheet of the present invention, the skin protective effect is enhanced by adding olive oil to the pressure-sensitive adhesive in addition to the synthetic phospholipid polymer. This is presumably because the migration of the synthetic phospholipid polymer was improved by partially dissolving the synthetic phospholipid polymer in olive oil. Olive oil is preferably added in an amount of 0.5 to 2% by weight based on the adhesive. In addition to olive oil, it is considered that the same effect can be expected if it is an oil component in which the synthetic polymer is dissolved or partially dissolved. For example, octyl dodecyl erucate, octyl dodecyl myristylate, oleic acid, dioctyl sebacate and the like can be mentioned.
また、本発明の医療用粘着シートにおいては、粘着剤にさらに一般的な保湿剤を添加してもよい。 In the medical pressure-sensitive adhesive sheet of the present invention, a more general moisturizing agent may be added to the pressure-sensitive adhesive.
この一般的な保湿剤としては、例えば、グリセリン、ジグリセリン、エチレングリコール、プロピレングリコール、ジエチレングリコール、ジプロピレングリコール、ブチレングリコール、ジプロピレングリコール、１，３−ブチレングリコール、ポリエチレングリコール、ソルビトール、キシリトール、マルビトール、ピロリドンカルボン酸ナトリウム、Ｎ−（３，４，５，６−テトラヒドロキシ−２−オキソヘキシル）ピログルタミン酸等があり、さらにトレハロース等の糖類、ムコ多糖類（例えば、ヒアルロン酸及びその誘導体、コンドロイチン及びその誘導体、ヘパリン及びその誘導体など）、エラスチン及びその誘導体、コラーゲン、エラスチン、ケラチン及びこれらの誘導体並びにその塩類、加水分解シルク蛋白質、乳酸ナトリウム、尿素、高級脂肪酸オクチルドデシル、イソステアリン酸コレステリル、海藻抽出物、魚介類由来コラーゲン及びその誘導体、各種アミノ酸及びそれらの誘導体、を挙げることができる。 Examples of this general moisturizing agent include glycerin, diglycerin, ethylene glycol, propylene glycol, diethylene glycol, dipropylene glycol, butylene glycol, dipropylene glycol, 1,3-butylene glycol, polyethylene glycol, sorbitol, xylitol, and malbitol. , Sodium pyrrolidonecarboxylate, N- (3,4,5,6-tetrahydroxy-2-oxohexyl) pyroglutamic acid and the like, and sugars such as trehalose, mucopolysaccharides (eg, hyaluronic acid and its derivatives, chondroitin) And derivatives thereof, heparin and derivatives thereof, etc., elastin and derivatives thereof, collagen, elastin, keratin and derivatives thereof and salts thereof, hydrolyzed silk protein, sodium lactate Arm, urea, higher fatty acid octyldodecyl, cholesteryl isostearate, seaweed extract, fish-derived collagen and derivatives thereof, various amino acids and derivatives thereof, can be mentioned.
また、本発明の医療用粘着シートにおいては、粘着剤に必要に応じて通常使用される添加剤等を本発明の効果を阻害しない範囲内で含有させることができる。添加剤としては、タルク等の充填剤、顔料、着色剤、老化防止剤、難燃剤、紫外線吸収剤、帯電防止剤、酸化防止剤、抗菌剤、防カビ剤、滑剤、安定化剤、可塑剤等が挙げられる。 Moreover, in the medical adhesive sheet of this invention, the additive etc. which are normally used as needed to an adhesive can be contained in the range which does not inhibit the effect of this invention. Additives include fillers such as talc, pigments, colorants, anti-aging agents, flame retardants, UV absorbers, antistatic agents, antioxidants, antibacterial agents, antifungal agents, lubricants, stabilizers, plasticizers Etc.
さらに、本発明で使用する粘着剤には、所望により、経皮吸収可能な薬物を配合してもよい。薬物としては、例えば、鎮痛消炎剤、抗炎症剤、抗アレルギー剤、抗ヒスタミン剤、抗菌剤、ビタミン類、香料などが挙げられる。これらは、必要に応じて有効量を配合する。 Furthermore, the adhesive used in the present invention may be blended with a transdermally absorbable drug, if desired. Examples of the drug include analgesic / anti-inflammatory agents, anti-inflammatory agents, antiallergic agents, antihistamines, antibacterial agents, vitamins, and fragrances. These are compounded in effective amounts as necessary.
その他、本発明は、主旨を逸脱しない範囲で当業者の知識に基づき種々なる改良、修正、変更を加えた態様で実施できるものである。 In addition, the present invention can be carried out in a mode in which various improvements, modifications, and changes are added based on the knowledge of those skilled in the art without departing from the spirit of the present invention.
Claims (4)
で表されるポリマー、
下記一般式（２）
で表されるポリマーから選択される１種以上のポリマーである請求項１に記載の医療・健康用テープまたはシート。 The synthetic phospholipid polymer is represented by the following general formula (1)
A polymer represented by
The following general formula (2)
The medical or health tape or sheet according to claim 1, which is one or more polymers selected from polymers represented by the formula:
で表されるポリマー、
下記一般式（２）
で表されるポリマーから選択される１種以上のポリマーを、０．８〜１０重量％の低級アルコールを含有するトルエンに溶解して溶液を得る工程、
該溶液を粘着剤の有機溶剤溶液と混合して混合液を得る工程、
該混合液、または該混合液を有機溶剤で希釈した希釈液、からなる塗布液を基材に塗布し乾燥する工程
を含む医療・健康用テープまたはシートの製造方法。 The following general formula (1)
A polymer represented by
The following general formula (2)
A step of obtaining a solution by dissolving one or more polymers selected from the polymers represented by formula (1) in toluene containing 0.8 to 10% by weight of a lower alcohol;
Mixing the solution with an organic solvent solution of an adhesive to obtain a mixed solution;
A method for producing a medical / health tape or sheet comprising a step of applying a coating solution comprising the mixed solution or a diluted solution obtained by diluting the mixed solution with an organic solvent to a substrate and drying the coating solution.