JP2010010012A - Alkaline battery - Google Patents
Alkaline battery Download PDFInfo
- Publication number
- JP2010010012A JP2010010012A JP2008169813A JP2008169813A JP2010010012A JP 2010010012 A JP2010010012 A JP 2010010012A JP 2008169813 A JP2008169813 A JP 2008169813A JP 2008169813 A JP2008169813 A JP 2008169813A JP 2010010012 A JP2010010012 A JP 2010010012A
- Authority
- JP
- Japan
- Prior art keywords
- zinc alloy
- ppm
- alloy powder
- negative electrode
- battery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、未放電時および過放電時における電池内でのガス発生量が少ないアルカリ電池に関するものである。 The present invention relates to an alkaline battery with a small amount of gas generation in the battery during undischarged and overdischarged.
アルカリ電池の負極に使用される亜鉛合金粉末には、未放電時における内部でのガス発生を防止するために、水素過電圧を上昇させ得るＢｉやＩｎなどの合金元素を含有させることが一般に行われており（例えば、特許文献１）、例えば、亜鉛合金粉末に係る亜鉛合金におけるＢｉの含有量としては、亜鉛合金全量に対して１５０〜３００ｐｐｍ程度とするのが効果的であることが知られている。また、実際に上市されているアルカリ電池においても、負極に水銀を添加しない亜鉛合金粉末を用いる場合には、Ｂｉを１５０ｐｐｍ以上含有する亜鉛合金の粉末を使用することが一般的である。 In general, zinc alloy powder used for the negative electrode of an alkaline battery contains an alloy element such as Bi or In that can increase the hydrogen overvoltage in order to prevent internal gas generation during non-discharge. (For example, Patent Document 1), for example, it is known that the content of Bi in a zinc alloy related to a zinc alloy powder is effectively about 150 to 300 ppm with respect to the total amount of the zinc alloy. Yes. In addition, even in an alkaline battery that is actually on the market, when using a zinc alloy powder that does not add mercury to the negative electrode, it is common to use a zinc alloy powder containing 150 ppm or more of Bi.
ところで、近年では、アルカリ電池の過放電時における内部でのガス発生による電解液の漏出が問題視されている。例えば、放電を終えたアルカリ電池を使用機器から比較的早期に取り出せば特に問題は生じないが、放電を終えた後も長期にわたって使用機器内に放置すると、アルカリ電池が過放電状態となり、その際に内部でガスが発生して、漏液が生じてしまうのである。 By the way, in recent years, leakage of electrolyte due to internal gas generation during overdischarge of alkaline batteries has been regarded as a problem. For example, there is no problem if the discharged alkaline battery is taken out from the equipment used relatively early. However, if the alkaline battery is left in the equipment for a long time after the discharge is finished, the alkaline battery becomes overdischarged. In this case, gas is generated inside and liquid leakage occurs.
前記のような水素過電圧を上昇させ得る合金元素を含む亜鉛合金の粉末を負極に使用する技術では、アルカリ電池の未放電時における内部でのガス発生抑制に関しては一定の効果が認められる一方で、過放電時における内部でのガス発生抑制については、十分な効果が得られない。 In the technique of using a zinc alloy powder containing an alloying element capable of increasing the hydrogen overvoltage as described above for the negative electrode, a certain effect is observed with respect to suppressing gas generation inside when the alkaline battery is not discharged, A sufficient effect cannot be obtained for suppressing gas generation inside during overdischarge.
本発明は、前記事情に鑑みてなされたものであり、その目的は、未放電時および過放電時における内部でのガス発生を抑制し得るアルカリ電池を提供することにある。 This invention is made | formed in view of the said situation, The objective is to provide the alkaline battery which can suppress the gas generation inside at the time of an undischarge and an overdischarge.
前記目的を達成し得た本発明のアルカリ電池（アルカリ一次電池）は、亜鉛合金粉末を含有するゲル状負極、およびアルカリ水溶液からなる電解液を有するアルカリ電池であって、前記亜鉛合金が、Ｂｉを５０〜１２５ｐｐｍ、Ａｌを１００〜２０００ｐｐｍ、並びに、ＣａおよびＭｇの少なくとも一方を合計で１〜５０ｐｐｍ含有することを特徴とするものである。なお、本明細書でいう亜鉛合金粉末に係る亜鉛合金中の各元素の含有量は、質量基準である。 The alkaline battery (alkaline primary battery) of the present invention that has achieved the above object is an alkaline battery having a gelled negative electrode containing zinc alloy powder and an electrolytic solution comprising an alkaline aqueous solution, wherein the zinc alloy contains Bi. Is 50 to 125 ppm, Al is 100 to 2000 ppm, and at least one of Ca and Mg is contained in a total of 1 to 50 ppm. In addition, content of each element in the zinc alloy which concerns on the zinc alloy powder as used in this specification is a mass reference | standard.
本発明によれば、未放電時および過放電時における内部でのガス発生を抑制し得るアルカリ電池を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the alkaline battery which can suppress the gas generation inside at the time of undischarge and overdischarge can be provided.
以下、本発明のアルカリ電池を詳細に説明する。 Hereinafter, the alkaline battery of the present invention will be described in detail.
＜負極＞
本発明のアルカリ電池に係る負極には、亜鉛合金粉末と、電解液と、ゲル化剤とを有するゲル状の負極合剤（ゲル状負極）が使用される。亜鉛合金の粉末中のＺｎ成分が、負極活物質として作用する。
<Negative electrode>
For the negative electrode according to the alkaline battery of the present invention, a gelled negative electrode mixture (gelled negative electrode) having a zinc alloy powder, an electrolytic solution, and a gelling agent is used. The Zn component in the zinc alloy powder acts as a negative electrode active material.
亜鉛合金粉末は、合金元素として、Ｂｉを５０ｐｐｍ以上１２５ｐｐｍ以下、Ａｌを１００ｐｐｍ以上２０００ｐｐｍ以下、ＣａおよびＭｇの少なくとも一方を１ｐｐｍ以上５０ｐｐｍ以下で、それぞれ含有する亜鉛合金により構成されている。本発明のアルカリ電池では、前記の組成を有する亜鉛合金の粉末を負極に用いることにより、未放電時および過放電時における内部でのガス発生を抑制している。 The zinc alloy powder is composed of zinc alloys containing, as alloy elements, Bi of 50 ppm to 125 ppm, Al of 100 ppm to 2000 ppm, and at least one of Ca and Mg of 1 ppm to 50 ppm. In the alkaline battery of the present invention, by using a zinc alloy powder having the above composition for the negative electrode, gas generation inside during undischarged and overdischarge is suppressed.
亜鉛合金粉末を負極に用いたアルカリ電池では、未放電時において、亜鉛合金粉末に係るＺｎ（亜鉛）の腐食によってガスが発生する。前記の通り、従来のアルカリ電池では、例えば、負極に使用する亜鉛合金に、合金元素としてＢｉなどを含有させることで、未放電時における亜鉛合金粉末に係るＺｎの腐食を抑えて、ガス発生を抑制していた。しかしながら、このようなアルカリ電池では、放電終了後に過放電状態となった際に、亜鉛合金粉末において、放電反応に関与せず残存しているＺｎ成分とＢｉの反応によって、ガス発生が促されることが本発明者らの検討により明らかとなった。 In an alkaline battery using zinc alloy powder as a negative electrode, gas is generated due to corrosion of Zn (zinc) related to the zinc alloy powder when not discharged. As described above, in the conventional alkaline battery, for example, by containing Bi or the like as an alloy element in the zinc alloy used for the negative electrode, corrosion of Zn related to the zinc alloy powder at the time of non-discharge is suppressed, and gas generation is generated. It was suppressed. However, in such an alkaline battery, when an overdischarge state occurs after the end of discharge, gas generation is promoted in the zinc alloy powder by the reaction of the remaining Zn component and Bi without participating in the discharge reaction. However, it became clear by examination of the present inventors.
そこで、本発明では、亜鉛合金粉末に係る亜鉛合金中のＢｉ量を制限して過放電時におけるガス発生を抑制した。また、亜鉛合金の合金成分として、Ａｌと、Ｃａおよび／またはＭｇとを特定量で含有させることによって、過放電時のガス発生を更に抑制することに加えて、Ｂｉ量を制限したことに伴って低下する虞のある未放電時のガス発生抑制作用を補い、未放電時においてもガス発生を良好に抑制できるようにした。 Therefore, in the present invention, the amount of Bi in the zinc alloy related to the zinc alloy powder is limited to suppress gas generation during overdischarge. In addition to containing Al and Ca and / or Mg in a specific amount as an alloy component of the zinc alloy, in addition to further suppressing gas generation during overdischarge, the amount of Bi is limited. The gas generation suppression effect at the time of non-discharge, which may decrease, is compensated, and the gas generation can be suppressed well even at the time of non-discharge.
亜鉛合金粉末に係る亜鉛合金中のＢｉ含有量は、過放電時におけるガス発生を抑制する観点から、１２５ｐｐｍ以下であり、１００ｐｐｍ以下であることが好ましい。ただし、亜鉛合金中のＢｉ量が少なすぎると、未放電時におけるガス発生抑制作用が小さくなりすぎる虞があることから、亜鉛合金粉末に係る亜鉛合金中のＢｉ含有量は、５０ｐｐｍ以上であり、７５ｐｐｍ以上であることが好ましい。 The Bi content in the zinc alloy related to the zinc alloy powder is 125 ppm or less and preferably 100 ppm or less from the viewpoint of suppressing gas generation during overdischarge. However, if the amount of Bi in the zinc alloy is too small, there is a possibility that the gas generation suppression action at the time of non-discharge will be too small, so the Bi content in the zinc alloy according to the zinc alloy powder is 50 ppm or more, It is preferable that it is 75 ppm or more.
亜鉛合金粉末に係る亜鉛合金の合金元素としてＡｌを用いることによって、未放電時および過放電時におけるガス発生抑制を達成し得るのは、以下の理由によるものと推測される。亜鉛合金粉末に係る亜鉛合金がＡｌを含有することによって粉末表面の平滑性が向上する。そのため、未反応時における亜鉛合金粉末に係る亜鉛合金中のＺｎ成分の腐食反応が生じ難くなってガス発生が抑制されると考えられる。また、亜鉛合金がＡｌを含有することで、放電に伴って生成する酸化亜鉛の結晶中に存在するＺｎが、Ｚｎよりも一つ価数の高いＡｌで部分的に置換され、前記結晶内に多くの伝導電子が生成し得るようになる。これにより、酸化亜鉛の導電性が高まることから、亜鉛合金粉末に係るＺｎの利用率が向上し、過放電時におけるガス発生の要因となる未反応のＺｎ量を低減することができるため、過放電時におけるガス発生が抑制されると考えられる。 By using Al as the alloy element of the zinc alloy related to the zinc alloy powder, it is presumed that the gas generation suppression during undischarged and overdischarge can be achieved for the following reason. When the zinc alloy related to the zinc alloy powder contains Al, the smoothness of the powder surface is improved. Therefore, it is considered that the corrosion reaction of the Zn component in the zinc alloy related to the zinc alloy powder at the time of unreacted hardly occurs and gas generation is suppressed. In addition, since the zinc alloy contains Al, Zn existing in the zinc oxide crystal generated by the discharge is partially substituted with Al having a single valence higher than Zn, Many conduction electrons can be generated. As a result, the conductivity of zinc oxide is increased, so that the utilization rate of Zn related to the zinc alloy powder can be improved, and the amount of unreacted Zn that causes gas generation during overdischarge can be reduced. It is considered that gas generation during discharge is suppressed.
亜鉛合金粉末に係る亜鉛合金中のＡｌ含有量は、Ａｌを含有させることによる前記の効果（未放電時および過放電時におけるガス発生抑制効果）を確保する観点から、１００ｐｐｍ以上であり、２００ｐｐｍ以上であることが好ましく、５００ｐｐｍ以上であることがより好ましい。ただし、亜鉛合金中のＡｌ量が多すぎると、効果が飽和し、また、亜鉛合金粉末の製造が困難になる傾向にあることから、亜鉛合金粉末に係る亜鉛合金中のＡｌ含有量は、２０００ｐｐｍ以下であり、１５００ｐｐｍ以下であることが好ましく、１２００ｐｐｍ以下であることがより好ましい。 The Al content in the zinc alloy related to the zinc alloy powder is 100 ppm or more and 200 ppm or more from the viewpoint of securing the above-described effect (the effect of suppressing gas generation during undischarge and overdischarge) by containing Al. It is preferable that it is 500 ppm or more. However, if the amount of Al in the zinc alloy is too large, the effect is saturated and the production of the zinc alloy powder tends to be difficult. Therefore, the Al content in the zinc alloy related to the zinc alloy powder is 2000 ppm. Or less, preferably 1500 ppm or less, and more preferably 1200 ppm or less.
また、亜鉛合金粉末に係る亜鉛合金にＣａおよびＭｇの少なくとも一方を含有させることによって、未放電時および過放電時におけるガス発生抑制を達成し得るのは、以下の理由によるものと推測される。前記の通り、亜鉛合金粉末に係る亜鉛合金がＡｌを含有していると、粉末表面の平滑性が向上し、未放電時におけるガス発生が抑制できると考えられるが、亜鉛合金がＡｌと共にＣａおよび／またはＭｇを含有していると、粉末表面の平滑性がより向上しやすくなり、未放電時におけるガス発生が更に良好に抑制できると推測される。また、ＣａおよびＭｇは、Ａｌと同様の機構によって放電に伴って生成する酸化亜鉛の導電性を高め得るため、亜鉛合金粉末に係るＺｎの利用率が向上し、過放電時におけるガス発生が抑制されると考えられる。 Moreover, it is estimated that the gas generation suppression at the time of non-discharge and at the time of overdischarge can be achieved by including at least one of Ca and Mg in the zinc alloy related to the zinc alloy powder for the following reason. As described above, when the zinc alloy related to the zinc alloy powder contains Al, it is considered that the smoothness of the powder surface is improved and gas generation during undischarge can be suppressed. When Mg is contained, the smoothness of the powder surface is more likely to be improved, and it is presumed that the generation of gas during undischarge can be further suppressed. In addition, Ca and Mg can increase the conductivity of zinc oxide generated with discharge by the same mechanism as Al, so the utilization rate of Zn related to zinc alloy powder is improved and gas generation during overdischarge is suppressed. It is thought that it is done.
亜鉛合金粉末に係る亜鉛合金は、ＣａおよびＭｇのいずれか一方のみを含有していてもよく、両方を含有していてもよい。亜鉛合金粉末に係る亜鉛合金中のＣａおよびＭｇの含有量は、これらを含有させることによる前記の効果（未放電時および過放電時におけるガス発生抑制効果）を確保する観点から、両者の合計（ＣａおよびＭｇのいずれか一方のみを含有する場合は、その一方の量。ＣａおよびＭｇの含有量について、以下同じ。）で、１ｐｐｍ以上であり、４ｐｐｍ以上であることが好ましい。ただし、亜鉛合金中のＣａおよびＭｇの量が多すぎると、効果が飽和するばかりか、ＣａまたはＭｇが偏析することにより電池の放電特性が低下する虞があることから、亜鉛合金粉末に係る亜鉛合金中のＣａおよびＭｇの含有量は、両者の合計で、５０ｐｐｍ以下であり、２０ｐｐｍ以下であることが好ましい。 The zinc alloy according to the zinc alloy powder may contain only one of Ca and Mg, or may contain both. The content of Ca and Mg in the zinc alloy related to the zinc alloy powder is the sum of both from the viewpoint of ensuring the above-described effect (the effect of suppressing gas generation during undischarged and overdischarged) due to the inclusion of these. In the case where only one of Ca and Mg is contained, the amount of one of them is the same, and the content of Ca and Mg is 1 ppm or more, and preferably 4 ppm or more. However, if the amount of Ca and Mg in the zinc alloy is too large, not only will the effect be saturated, but the discharge characteristics of the battery may deteriorate due to segregation of Ca or Mg. The total content of Ca and Mg in the alloy is 50 ppm or less, and preferably 20 ppm or less.
なお、亜鉛合金粉末に係る亜鉛合金は、典型的には、前記合金元素以外の部分が、Ｚｎおよび不可避不純物であるが、本発明の効果を損なわない範囲で、他の合金元素を含有していてもよい。 The zinc alloy according to the zinc alloy powder typically contains other alloy elements as long as the portion other than the alloy elements is Zn and inevitable impurities, but does not impair the effects of the present invention. May be.
亜鉛合金に係る前記合金元素以外の合金元素としては、例えばＩｎが挙げられる。Ｉｎを含有させることで、亜鉛合金の水素過電圧をより高め、未放電時におけるガス発生抑制作用を更に向上させることができる。亜鉛合金粉末に係る亜鉛合金中のＩｎの含有量は、１００〜１０００ｐｐｍであることが好ましい。 Examples of alloy elements other than the alloy elements related to the zinc alloy include In. By containing In, the hydrogen overvoltage of the zinc alloy can be further increased, and the gas generation suppressing action when not discharged can be further improved. The content of In in the zinc alloy related to the zinc alloy powder is preferably 100 to 1000 ppm.
また、亜鉛合金粉末に係る亜鉛合金中の亜鉛合金は、９８質量％以上であることが好ましい。 Moreover, it is preferable that the zinc alloy in the zinc alloy which concerns on zinc alloy powder is 98 mass% or more.
負極に係る亜鉛合金粉末は、２００メッシュの篩い目を通過し得るものの割合が、１０質量％以上であることが好ましく、２０質量％以上であることがより好ましい。亜鉛合金粉末が、このように微細な形態を有する場合には、亜鉛合金粉末全体の比表面積が大きくなり、負極での反応を効率よく進めることができるため、電池の負荷特性が良好となる。また、亜鉛合金粉末の表面から中心までの距離が小さくなるため、比較的負荷の小さな放電（軽負荷放電）時においても、Ｚｎの利用率が向上する。そのため、放電終了時において、未反応のＺｎ量（亜鉛合金粉末中のＺｎ成分量）を低減して、過放電時におけるガス発生を更に抑制することができるようになる。 The proportion of the zinc alloy powder relating to the negative electrode that can pass through a 200 mesh sieve is preferably 10% by mass or more, and more preferably 20% by mass or more. When the zinc alloy powder has such a fine form, the specific surface area of the entire zinc alloy powder is increased, and the reaction at the negative electrode can be advanced efficiently, so that the load characteristics of the battery are improved. In addition, since the distance from the surface to the center of the zinc alloy powder is reduced, the utilization factor of Zn is improved even during discharge with a relatively small load (light load discharge). Therefore, at the end of discharge, the amount of unreacted Zn (Zn component amount in the zinc alloy powder) can be reduced to further suppress gas generation during overdischarge.
なお、亜鉛合金粉末における２００メッシュの篩い目を通過し得るものの割合が増加するに従って、亜鉛合金粉末全体の比表面積が増大するが、これにより亜鉛合金粉末と電解液との反応性がより高まるため、亜鉛表面からのガス発生量が増大し、未放電時における内部でのガス発生が大きくなる。また、亜鉛合金粉末中に占める微細な粉末の割合が大きくなると、亜鉛合金粉末全体が嵩高くなって電池製造時の亜鉛合金粉末の取り扱いが困難となる。よって、本発明の電池では、前記の未放電時における内部でのガス発生を抑え、更に、電池製造時の亜鉛合金粉末の取り扱い性を高める観点から、亜鉛合金粉末における２００メッシュの篩い目を通過し得るものの割合は、８０質量％以下であることが好ましく、４０質量％以下であることがより好ましい。 The specific surface area of the entire zinc alloy powder increases as the proportion of the zinc alloy powder that can pass through the 200 mesh sieve increases, but this increases the reactivity between the zinc alloy powder and the electrolyte. In addition, the amount of gas generated from the zinc surface increases, and the generation of gas inside when not discharged increases. Moreover, when the ratio of the fine powder which occupies in a zinc alloy powder becomes large, the whole zinc alloy powder will become bulky and handling of the zinc alloy powder at the time of battery manufacture will become difficult. Therefore, in the battery of the present invention, from the viewpoint of suppressing internal gas generation when not discharged, and further improving the handleability of the zinc alloy powder at the time of battery production, it passes through a 200 mesh sieve in the zinc alloy powder. The ratio of what can be done is preferably 80% by mass or less, and more preferably 40% by mass or less.
更に、２００メッシュの篩い目を通過し得るものの割合が、前記好適値を満足する亜鉛合金粉末を用いることで、未放電時の電解液との反応による腐食に伴うガス発生量をより少なくすることができ、また、均質で流動性が良好な負極合剤を調製することもできる。 Furthermore, by using a zinc alloy powder that can pass through a 200 mesh sieve, the amount of gas generated due to corrosion due to reaction with the electrolyte during non-discharge is reduced. It is also possible to prepare a negative electrode mixture that is homogeneous and has good fluidity.
なお、電池製造時の取り扱い性を考慮すると、負極が有する亜鉛合金粉末は、その最小粒径が７μｍ程度であることが望ましい。また、亜鉛合金粉末は、例えば、その全体が８０メッシュの篩い目を通過し得るものであることが好ましい。 In view of handling at the time of manufacturing the battery, it is desirable that the zinc alloy powder of the negative electrode has a minimum particle size of about 7 μm. Moreover, it is preferable that the zinc alloy powder, for example, as a whole can pass through 80 mesh screens.
更に、本発明に係る負極は、インジウム化合物を含有していることが好ましい。Ａｌ含有量が高い亜鉛合金で構成される亜鉛合金粉末を負極に用いた電池では、例えば軽負荷で放電させた場合、放電途中に導電性の反応生成物（デンドライト）が異常析出し、これが電池缶体と接触して内部短絡を引き起こし、電池の放電時間、すなわち電池の寿命が異常に短くなることがある。 Furthermore, the negative electrode according to the present invention preferably contains an indium compound. In a battery using a zinc alloy powder composed of a zinc alloy having a high Al content for the negative electrode, for example, when discharged at a light load, a conductive reaction product (dendrites) is abnormally precipitated during the discharge, which is the battery. Contact with the can may cause an internal short circuit, and the battery discharge time, that is, the battery life may be shortened abnormally.
しかしながら、負極にインジウム化合物を含有させておくと、インジウム化合物のイオン交換反応により、亜鉛合金粉末の表面にＩｎが偏析し、前記の内部短絡による放電特性の低下を防止することが可能となる。これは、亜鉛合金粉末の表面に偏析したＩｎが、亜鉛合金粉末からのデンドライト生成を抑制するためであると推測される。また、インジウム化合物を負極に含有させておくことで、電池内でのガス発生を更に抑えることもできる。 However, if an indium compound is contained in the negative electrode, In is segregated on the surface of the zinc alloy powder due to an ion exchange reaction of the indium compound, and it becomes possible to prevent the discharge characteristics from being deteriorated due to the internal short circuit. This is presumed to be because In segregated on the surface of the zinc alloy powder suppresses the formation of dendrite from the zinc alloy powder. Moreover, the gas generation in the battery can be further suppressed by containing the indium compound in the negative electrode.
前記のインジウム化合物としては、例えば、酸化インジウム、水酸化インジウムなどが挙げられる。 Examples of the indium compound include indium oxide and indium hydroxide.
本発明のアルカリ電池に係る負極はゲル状負極であり、前記亜鉛合金粉末やインジウム化合物以外に、ゲル化剤および電解液を含有している。 The negative electrode according to the alkaline battery of the present invention is a gelled negative electrode and contains a gelling agent and an electrolytic solution in addition to the zinc alloy powder and the indium compound.
ゲル化剤については特に制限はなく、従来から知られているアルカリ電池に使用されているゲル化剤、例えば、カルボキシメチルセルロース、ポリアクリル酸、ポリアクリル酸などの各種高分子ゲル化剤が使用できる。ゲル状負極中のゲル化剤の含有量は、例えば、１．５〜３質量％であることが好ましい。 The gelling agent is not particularly limited, and various polymer gelling agents such as carboxymethyl cellulose, polyacrylic acid, and polyacrylic acid that are conventionally used in alkaline batteries can be used. . The content of the gelling agent in the gelled negative electrode is preferably 1.5 to 3% by mass, for example.
また、負極に係る電解液としては、特に制限は無く、従来から知られているゲル状負極を有するアルカリ電池に使用されている電解液と同様のもの（例えば、水酸化カリウム、水酸化ナトリウムなどのアルカリ金属の水酸化物の水溶液などのアルカリ水溶液）が使用できるが、電池の放電特性を高める観点からは、水酸化カリウム水溶液を使用することがより好ましい。 Moreover, there is no restriction | limiting in particular as electrolyte solution concerning a negative electrode, The thing similar to the electrolyte solution currently used for the alkaline battery which has a conventionally known gelled negative electrode (For example, potassium hydroxide, sodium hydroxide, etc.) From the viewpoint of improving the discharge characteristics of the battery, it is more preferable to use an aqueous potassium hydroxide solution.
電解液中のアルカリ濃度も特に制限は無く、従来から知られているアルカリ電池と同程度とすればよいが、例えば、電解液に水酸化カリウム水溶液を用いる場合、その水酸化カリウム濃度を、２８〜３８質量％とすることが好ましい。 The alkali concentration in the electrolytic solution is not particularly limited and may be the same as that of a conventionally known alkaline battery. For example, when an aqueous potassium hydroxide solution is used as the electrolytic solution, the potassium hydroxide concentration is 28 It is preferable to set it to -38 mass%.
ゲル状負極は、例えば、亜鉛合金粉末と、予め前記のゲル化剤を用いてゲル状にしておいた電解液とを混合する方法などにより調製できる。前記のインジウム化合物を使用する場合には、例えば、予め亜鉛合金粉末と混合しておき、その後、ゲル状の電解液と混合してもよく、また、亜鉛合金粉末とゲル状の電解液との混合の際に添加しても構わない。更に、これら以外の方法で、ゲル状負極を調製しても構わない。 The gelled negative electrode can be prepared, for example, by a method of mixing a zinc alloy powder and an electrolytic solution that has been previously gelled using the gelling agent. In the case of using the indium compound, for example, it may be previously mixed with zinc alloy powder and then mixed with a gel electrolyte, or the zinc alloy powder and gel electrolyte may be mixed. It may be added during mixing. Furthermore, you may prepare a gelled negative electrode by methods other than these.
なお、ゲル状負極における前記亜鉛合金粉末の含有量は、例えば、６０質量％以上であることが好ましく、６５質量％以上であることがより好ましく、また、７５質量％以下であることが好ましく、７０質量％以下であることがより好ましい。また、負極にインジウム化合物を含有させる場合には、その含有量は、０．００３〜０．０５質量％であることが好ましい。 The content of the zinc alloy powder in the gelled negative electrode is, for example, preferably 60% by mass or more, more preferably 65% by mass or more, and preferably 75% by mass or less. More preferably, it is 70 mass% or less. When the indium compound is contained in the negative electrode, the content is preferably 0.003 to 0.05% by mass.
本発明のアルカリ電池は、前述のゲル状負極を有していればよく、その他の構成・構造については特に制限は無く、従来から知られているアルカリ電池（アルカリ一次電池）で採用されている各構成・構造を適用することができる。 The alkaline battery of the present invention only needs to have the above-mentioned gelled negative electrode, and there are no particular restrictions on the other configuration and structure, and it has been adopted in conventionally known alkaline batteries (alkali primary batteries). Each configuration / structure can be applied.
＜正極＞
本発明のアルカリ電池に係る正極は、例えば、活物質である二酸化マンガン、オキシ水酸化ニッケル、および導電助剤、更には成形のための電解液およびバインダを混合して正極合剤とし、この正極合剤をリング状などに加圧成形することにより形成される。
<Positive electrode>
The positive electrode according to the alkaline battery of the present invention includes, for example, an active material such as manganese dioxide, nickel oxyhydroxide, a conductive additive, and an electrolyte for forming and a binder to form a positive electrode mixture. It is formed by pressing the mixture into a ring shape or the like.
正極活物質は、そのＢＥＴ比表面積が、４０ｍ２／ｇ以上１００ｍ２／ｇ以下であることが好ましい。正極活物質のＢＥＴ比表面積が小さすぎると、成形性は良好であるものの、反応面積が小さくなるために反応効率が悪くなり、電池の負荷特性が低下する虞がある。また、正極活物質のＢＥＴ比表面積が大きすぎると、反応効率は向上するが、かさ密度が低下するために成形性が悪化することがある。正極活物質の成形性を高めて、正極合剤の成形体の強度をより向上させるには、正極活物質のＢＥＴ比表面積は６０ｍ２／ｇ以下であることがより好ましく、また、４５ｍ２／ｇ以上であることがより好ましい。
The positive electrode active material preferably has a BET specific surface area of 40 m 2 / g or more and 100 m 2 / g or less. If the BET specific surface area of the positive electrode active material is too small, the moldability is good, but the reaction area is small and the reaction efficiency is deteriorated, which may reduce the load characteristics of the battery. Moreover, when the BET specific surface area of a positive electrode active material is too large, reaction efficiency will improve, but since a bulk density falls, a moldability may deteriorate. To enhance the moldability of the positive electrode active material, in order to improve the strength of the molded body of the positive electrode mixture, more preferably a BET specific surface area of the positive electrode active material is less than 60
なお、ここでいう正極活物質のＢＥＴ比表面積は、多分子層吸着の理論式であるＢＥＴ式を用いて、表面積を測定、計算したもので、活物質の表面と微細孔の比表面積である。具体的には、窒素吸着法による比表面積測定装置（Ｍｏｕｎｔｅｃｈ社製 Ｍａｃｓｏｒｂ ＨＭ ｍｏｄｅｌｅ−１２０１）を用いて、ＢＥＴ比表面積として得た値である。 Note that the BET specific surface area of the positive electrode active material here is a specific surface area of the surface of the active material and the micropores, which is a surface area measured and calculated using the BET equation, which is a theoretical formula for multi-layer adsorption. . Specifically, it is a value obtained as a BET specific surface area using a specific surface area measurement device (Macsorb HM model-1201 manufactured by Mounttech) using a nitrogen adsorption method.
また、正極活物質として二酸化マンガンを用いる場合、二酸化マンガンはチタンを０．０１〜３．０質量％含有していることが望ましい。この程度の量のチタンを含有する二酸化マンガンでは、比表面積が大きくなって反応効率が向上するため、アルカリ電池の負荷特性をより高めることができる。 Moreover, when using manganese dioxide as a positive electrode active material, it is desirable for manganese dioxide to contain 0.01-3.0 mass% of titanium. With manganese dioxide containing this amount of titanium, the specific surface area is increased and the reaction efficiency is improved, so that the load characteristics of the alkaline battery can be further improved.
正極に係る導電助剤としては、例えば、黒鉛、ケッチェンブラック、アセチレンブラックなどを用いることができる。正極合剤中の導電助剤量は、例えば、正極活物質１００質量部に対して、３〜８．５質量部とすることが好ましい。 For example, graphite, ketjen black, acetylene black, or the like can be used as the conductive assistant for the positive electrode. The amount of the conductive additive in the positive electrode mixture is preferably, for example, 3 to 8.5 parts by mass with respect to 100 parts by mass of the positive electrode active material.
正極に係るバインダとしては、例えば、ポリテトラフルオロエチレン、ポリフッ化ビニリデン、スチレンブタジエンゴムなどを用いることができる。正極合剤中のバインダ量は、例えば、０．１〜１質量％とすることが好ましい。 As the binder for the positive electrode, for example, polytetrafluoroethylene, polyvinylidene fluoride, styrene butadiene rubber, or the like can be used. The amount of the binder in the positive electrode mixture is preferably 0.1 to 1% by mass, for example.
正極に用いる電解液としては、例えば、水酸化カリウム、水酸化ナトリウム、水酸化リチウムなどのアルカリ金属の水酸化物を水に溶解させたアルカリ水溶液や、それに酸化亜鉛などを添加したものなどが用いられるが、後述するように、電池の放電特性を高める観点からは、水酸化カリウム水溶液がより好ましい。電解液中のアルカリ金属の水酸化物の濃度としては、例えば水酸化カリウムの場合、４０〜６０質量％であることが好ましく、また、酸化亜鉛を使用する場合、その濃度は、１．０〜４．０質量％であることが好ましい。 As an electrolytic solution used for the positive electrode, for example, an alkaline aqueous solution in which an alkali metal hydroxide such as potassium hydroxide, sodium hydroxide, or lithium hydroxide is dissolved in water, or a solution in which zinc oxide or the like is added thereto is used. However, as will be described later, an aqueous potassium hydroxide solution is more preferable from the viewpoint of improving the discharge characteristics of the battery. For example, in the case of potassium hydroxide, the concentration of the alkali metal hydroxide in the electrolytic solution is preferably 40 to 60% by mass. When zinc oxide is used, the concentration is 1.0 to It is preferable that it is 4.0 mass%.
＜正極容量に対する負極容量の比＞
前記の通り、過放電時における電池内でのガス発生は、電池の放電が終了した後の負極において、放電反応に関与していない未反応のＺｎ（亜鉛合金粉末に係る亜鉛合金中のＺｎ成分）が存在する場合に起こる。よって、本発明の電池においては、正極容量に対する負極容量の比（負極容量／正極容量）が、１．２５以下であることが好ましく、１．２０以下であることがより好ましく、１．１０以下であることが更に好ましい。このように正極容量に対する負極容量の比を小さくすることで、放電終了時における未反応のＺｎ量を可及的に低減し、過放電時におけるガス発生を、更に抑制することができる。
<Ratio of negative electrode capacity to positive electrode capacity>
As described above, gas generation in the battery at the time of overdischarge is caused by unreacted Zn (Zn component in the zinc alloy related to the zinc alloy powder) that is not involved in the discharge reaction in the negative electrode after the discharge of the battery is completed. ) Occurs. Therefore, in the battery of the present invention, the ratio of the negative electrode capacity to the positive electrode capacity (negative electrode capacity / positive electrode capacity) is preferably 1.25 or less, more preferably 1.20 or less, and 1.10 or less. More preferably. Thus, by reducing the ratio of the negative electrode capacity to the positive electrode capacity, the amount of unreacted Zn at the end of discharge can be reduced as much as possible, and gas generation at the time of overdischarge can be further suppressed.
なお、正極容量に対する負極容量の比が小さすぎると、正極容量と負極容量とのバランスが悪くなって電池の放電容量が低下することがあるため、本発明の電池においては、正極容量に対する負極容量の比が、１．００以上であることが好ましく、１．０５以上であることがより好ましい。 In addition, if the ratio of the negative electrode capacity to the positive electrode capacity is too small, the balance between the positive electrode capacity and the negative electrode capacity is deteriorated and the discharge capacity of the battery may be reduced. The ratio is preferably 1.00 or more, and more preferably 1.05 or more.
本発明の電池における正極容量に対する負極容量の比は、以下のようにして求められる値である。電池組み立て後の正極および負極の活物質の含有量を、正極活物質（二酸化マンガンまたはオキシ水酸化ニッケル）については、その質量と、その中のＭｎ含有率やＮｉ含有率の分析値とから算出し、負極活物質（亜鉛合金中のＺｎ成分）については、ゲル状の負極合剤を回収し、水洗した上で、Ｚｎ含有率を分析して算出する。正極活物質中のＭｎ含有率やＮｉ含有率、負極活物質中のＺｎ含有率は、誘導結合プラズマ（ＩＣＰ）分析により求める。そして、二酸化マンガンの容量を３０８ｍＡｈ／ｇとし、オキシ水酸化ニッケルの容量を２９２ｍＡｈ／ｇとして、前記の正極活物質含有量（二酸化マンガン量やオキシ水酸化ニッケル量）から正極容量を算出し、亜鉛の容量を８２０ｍＡｈ／ｇとして、前記の負極活物質含有量（Ｚｎ量）から負極容量を算出し、正極容量に対する負極容量の比を求める。 The ratio of the negative electrode capacity to the positive electrode capacity in the battery of the present invention is a value determined as follows. The content of the positive and negative electrode active materials after battery assembly is calculated from the mass of the positive electrode active material (manganese dioxide or nickel oxyhydroxide) and the analytical values of the Mn content and Ni content therein. And about a negative electrode active material (Zn component in a zinc alloy), after collect | recovering gel-like negative electrode mixtures and washing with water, it analyzes and calculates Zn content rate. The Mn content and Ni content in the positive electrode active material and the Zn content in the negative electrode active material are determined by inductively coupled plasma (ICP) analysis. Then, the capacity of manganese dioxide is set to 308 mAh / g, the capacity of nickel oxyhydroxide is set to 292 mAh / g, the positive electrode capacity is calculated from the positive electrode active material content (the amount of manganese dioxide and the amount of nickel oxyhydroxide), and zinc The negative electrode capacity is calculated from the negative electrode active material content (Zn amount), and the ratio of the negative electrode capacity to the positive electrode capacity is obtained.
なお、前記の二酸化マンガン、オキシ水酸化ニッケルおよび亜鉛の容量は、「電池便覧 第３版（丸善株式会社）」の第２７頁に記載の表１・４・１「種々の電池活物質の単位電気量当たりの質量および体積」におけるＺｎ、ＭｎＯ２およびＮｉＯＯＨの単位電気量当たりの質量（１．２２０、３．２４４、および３．４２２）の逆数を取り、単位を整えた数値を用いた。 The capacities of manganese dioxide, nickel oxyhydroxide and zinc are shown in Tables 1 and 4 “units of various battery active materials” on page 27 of “Battery Handbook 3rd Edition (Maruzen Co., Ltd.)”. The value obtained by taking the reciprocal of the mass per unit quantity of electricity (1.220, 3.244, and 3.422) of Zn, MnO 2 and NiOOH in “mass and volume per quantity of electricity” was used.
＜電解液＞
正極および負極に使用する以外に電池内に注入するための電解液としては、前記の正極や負極に係る電解液と同様に、例えば、水酸化カリウム、水酸化ナトリウム、水酸化リチウムなどのアルカリ金属の水酸化物の水溶液からなるアルカリ水溶液や、それに酸化亜鉛を添加したものなどを用いることができる。電解液中のアルカリ金属の水酸化物の濃度としては、例えば水酸化カリウムの場合、２８〜３８質量％であることが好ましく、また、酸化亜鉛を使用する場合、その濃度は、１．０〜４．０質量％であることが好ましい。
<Electrolyte>
As an electrolytic solution for injecting into a battery other than for use in the positive electrode and the negative electrode, for example, an alkali metal such as potassium hydroxide, sodium hydroxide, lithium hydroxide, etc., similar to the electrolytic solution related to the positive electrode and the negative electrode. An aqueous alkali solution composed of an aqueous solution of the above-mentioned hydroxide, or a solution in which zinc oxide is added thereto can be used. For example, in the case of potassium hydroxide, the concentration of the alkali metal hydroxide in the electrolytic solution is preferably 28 to 38% by mass. When zinc oxide is used, the concentration is 1.0 to It is preferable that it is 4.0 mass%.
なお、電池の放電特性を高める観点からは、正極用の電解液、負極用の電解液、正極および負極に使用する以外に電池内に注入するための電解液のいずれにおいても、水酸化カリウム水溶液を使用し、電池系内の電解液中における水酸化カリウム濃度が、平均して、好ましくは３８質量％以下、より好ましくは３５質量％以下となるように、前記の各電解液の濃度を調整することが望ましい。 In addition, from the viewpoint of improving the discharge characteristics of the battery, an aqueous potassium hydroxide solution can be used for any of the electrolyte for positive electrode, the electrolyte for negative electrode, and the electrolyte for injecting into the battery other than the positive electrode and negative electrode. And the concentration of each electrolyte solution is adjusted so that the average potassium hydroxide concentration in the electrolyte solution in the battery system is preferably 38% by mass or less, more preferably 35% by mass or less. It is desirable to do.
電池系内の電解液中における水酸化カリウム濃度が高い場合には電解液のイオン伝導性が低く、このような電解液を、例えば前記のように微細な形態の亜鉛合金粉末を有する負極と併用すると、亜鉛合金粉末表面に形成される放電生成物の電気抵抗が高くなると推測される。そのため、電池の短絡時における温度が非常に高くなり、安全性を損なう虞があると共に、亜鉛合金粉末中のＺｎ成分の利用率も低下し、放電終了時において未反応のＺｎ成分量が増大し、過放電時におけるガス発生抑制効果が小さくなる虞がある。 When the potassium hydroxide concentration in the electrolyte solution in the battery system is high, the ionic conductivity of the electrolyte solution is low, and such an electrolyte solution is used in combination with a negative electrode having a zinc alloy powder in a fine form as described above, for example. Then, it is estimated that the electrical resistance of the discharge product formed on the surface of the zinc alloy powder increases. Therefore, the temperature at the time of short-circuiting of the battery becomes very high, which may impair safety, and the utilization rate of the Zn component in the zinc alloy powder also decreases, and the amount of unreacted Zn component increases at the end of discharge. There is a possibility that the effect of suppressing gas generation during overdischarge may be reduced.
そこで、電池系内の電解液中における水酸化カリウム濃度の平均値を前記のように低く設定すれば、電解液の電気抵抗を低くして、抵抗の低い放電生成物を亜鉛合金粉末表面に生成させることが可能となり、電池の短絡時における温度上昇を低減して安全性を高めることができ、また、亜鉛合金粉末に係る亜鉛合金中のＺｎ成分の利用率を更に向上させて、放電終了時における未反応のＺｎ成分量を更に低減することも可能となる。 Therefore, if the average value of the potassium hydroxide concentration in the electrolyte solution in the battery system is set low as described above, the electrical resistance of the electrolyte solution is lowered and a discharge product with low resistance is generated on the surface of the zinc alloy powder. It is possible to increase the safety by reducing the temperature rise at the time of short circuit of the battery, and further improve the utilization rate of the Zn component in the zinc alloy related to the zinc alloy powder, at the end of the discharge It is also possible to further reduce the amount of unreacted Zn component.
ただし、電解液中における水酸化カリウム濃度を低くしすぎると、却って電解液のイオン伝導性が低下する傾向にあるため、電池系内の電解液中における水酸化カリウム濃度は、平均して、好ましくは２８質量％以上、より好ましくは３０質量％以上となるように、正極用の電解液、負極用の電解液、正極および負極に使用する以外に電池内に注入するための電解液の各水酸化カリウム濃度を調整することが望ましい。 However, if the potassium hydroxide concentration in the electrolyte solution is too low, the ionic conductivity of the electrolyte solution tends to decrease. Therefore, the potassium hydroxide concentration in the electrolyte solution in the battery system is preferably averaged. Is 28% by mass or more, more preferably 30% by mass or more, and each water of the electrolyte for pouring into the battery in addition to being used for the positive electrode electrolyte, the negative electrode electrolyte, the positive electrode and the negative electrode. It is desirable to adjust the potassium oxide concentration.
＜セパレータ＞
本発明のアルカリ電池に係るセパレータについては特に制限は無く、例えば、ビニロンとレーヨンを主体とする不織布、ビニロン・レーヨン不織布（ビニロン・レーヨン混抄紙）、ポリアミド不織布、ポリオレフィン・レーヨン不織布、ビニロン紙、ビニロン・リンターパルプ紙、ビニロン・マーセル化パルプ紙などを用いることができる。また、親水処理された微孔性ポリオレフィンフィルム（微孔性ポリエチレンフィルムや微孔性ポリプロピレンフィルムなど）とセロファンフィルムとビニロン・レーヨン混抄紙のような吸液層とを積み重ねたものをセパレータとしてもよい。
<Separator>
The separator for the alkaline battery of the present invention is not particularly limited. For example, a nonwoven fabric mainly composed of vinylon and rayon, a vinylon / rayon nonwoven fabric (vinylon / rayon mixed paper), a polyamide nonwoven fabric, a polyolefin / rayon nonwoven fabric, a vinylon paper, a vinylon. -Linter pulp paper, vinylon mercerized pulp paper, etc. can be used. In addition, a separator in which a hydrophilic microporous polyolefin film (such as a microporous polyethylene film or a microporous polypropylene film), a cellophane film, and a liquid absorbing layer such as vinylon / rayon mixed paper may be used as a separator. .
＜アルカリ電池の構造、およびその他の構成要素＞
本発明のアルカリ電池では、その形状などについては特に制限は無いが、例えば、筒形（円筒形や角筒形など）の形状のものが挙げられる。以下、図面を用いて、本発明の電池の構造を説明する。図１は、本発明のアルカリ電池の一例を示す断面図である。図１のアルカリ電池は、金属製（Ｎｉメッキを施した鉄、ステンレス鋼など）の外装缶１内に、リング状に成形された正極２（正極合剤成形体）が配置されており、その内側にコップ状のセパレータ３が配置され、アルカリ電解液（図示しない）がセパレータ３の内側から注入されている。更にセパレータ３の内側には亜鉛合金粉末を含む負極４（ゲル状の負極合剤）が充填されている。外装缶１における１ｂは正極端子である。外装缶１の開口端部１ａには、金属製（Ｎｉメッキを施した鉄、ステンレス鋼など）の負極端子板７が配されており、樹脂製の封口体６の外周縁部６２を介して前記開口端部１ａが内側に折り曲げられて封口されている。負極端子板７には、金属製（Ｓｎメッキなどを施した真鍮など）の負極集電棒５が、その頭部で溶接されており、負極集電棒５は、封口体６の中央部６１に設けられた透孔６４を通じて負極４内に挿入されている。また、封口時の負極端子板７の変形を防ぎ、かつ封口体６を内側から支える支持手段として、金属ワッシャ９（円板状の金属板）が配置されている。そして、樹脂製の封口体６には、防爆用の薄肉部６３が形成されている。短絡時に電池内においてガスが発生した場合、封口体６の薄肉部６３が優先的に開裂し、生じた裂孔からガスが金属ワッシャ９側に移動する。金属ワッシャ９および負極端子板７にはガス抜き孔が設けられており（図示しない）、電池内のガスは、これらのガス抜き孔を通じて電池外に排出される。樹脂製の封口体６を構成する樹脂としては、例えば、ナイロン６６などが挙げられる。
<Structure of alkaline battery and other components>
In the alkaline battery of the present invention, the shape thereof is not particularly limited. Hereinafter, the structure of the battery of the present invention will be described with reference to the drawings. FIG. 1 is a cross-sectional view showing an example of the alkaline battery of the present invention. The alkaline battery shown in FIG. 1 has a positive electrode 2 (positive electrode mixture molded body) formed in a ring shape in a metal outer casing 1 (Ni-plated iron, stainless steel, etc.). A cup-shaped
図２に、本発明のアルカリ電池の他の例の断面図を示す。図２中、図１と同じ作用を有する要素は同じ符号を付して、重複説明を避ける。図２中、８は、外装缶１と負極端子板７とを絶縁するための絶縁板であり、２０は、発電要素を収納している胴部分である。
FIG. 2 shows a cross-sectional view of another example of the alkaline battery of the present invention. In FIG. 2, elements having the same functions as those in FIG. In FIG. 2, 8 is an insulating plate for insulating the outer can 1 and the negative
図１に示すアルカリ電池では、金属ワッシャ９を使用している関係上、封口部分（図１中、１０）の占める体積が大きくなってしまう。これに対し、この図２の電池のように金属ワッシャをなくし、封口体６を内側から支える支持手段として負極端子板７を利用することで、封口部分１０の占める体積を減少させて発電要素を収容できる胴部分２０の体積を大きくすることができ、正極２および負極４の各合剤の充填量を、図１の電池よりも高めることができる。
In the alkaline battery shown in FIG. 1, since the
本発明のアルカリ電池は、従来から知られているアルカリ電池が用いられている各種用途と同じ用途に適用することができる。 The alkaline battery of the present invention can be applied to the same applications as those in which conventionally known alkaline batteries are used.
以下、実施例に基づいて本発明を詳細に述べる。ただし、下記実施例は本発明を制限するものではない。 Hereinafter, the present invention will be described in detail based on examples. However, the following examples do not limit the present invention.
実施例１
水分を１．６質量％含有する二酸化マンガン、黒鉛、ポリテトラフルオロエチレン粉末および正極合剤調製用のアルカリ電解液（酸化亜鉛を２．９質量％含有する５６質量％水酸化カリウム水溶液）を８７．６：６．７：０．２：５．５の質量比で、５０℃の温度下で混合して正極合剤を調製した。なお、この正極合剤中、二酸化マンガン１００質量部に対して、黒鉛は７．６質量部であった。また、正極合剤が含有する電解液の水酸化カリウム濃度は、二酸化マンガンの含有水分を考慮すると４４．６質量％となった。
Example 1
Manganese dioxide, graphite, polytetrafluoroethylene powder containing 1.6% by mass of water, and an alkaline electrolyte for preparing a positive electrode mixture (56% by mass of potassium hydroxide containing 2.9% by mass of zinc oxide) 87 A positive electrode mixture was prepared by mixing at a mass ratio of .6: 6.7: 0.2: 5.5 at a temperature of 50.degree. In this positive electrode mixture, graphite was 7.6 parts by mass with respect to 100 parts by mass of manganese dioxide. Moreover, the potassium hydroxide concentration of the electrolyte solution contained in the positive electrode mixture was 44.6% by mass in consideration of the moisture content of manganese dioxide.
次に、Ａｌを１０００ｐｐｍ、Ｂｉを１００ｐｐｍ、Ｉｎを５００ｐｐｍ、Ｍｇを５ｐｐｍの割合で含有する亜鉛合金からなる粉末、ポリアクリル酸ソーダ、ポリアクリル酸および負極合剤調製用のアルカリ電解液（酸化亜鉛を２．２質量％含有する３３．５質量％水酸化カリウム水溶液）を３９：０．２：０．２：１８の質量比で混合し、ゲル状の負極合剤を調製した。なお、前記亜鉛合金粉末は、平均粒径が１０９μｍで、８０メッシュの篩い目を全て通過し、かつ２００メッシュの篩い目を通過する亜鉛合金粉末が、全亜鉛合金粉末量に対して２５質量％であって、そのかさ密度は２．６３ｇ／ｃｍ３であった。 Next, a powder composed of a zinc alloy containing 1000 ppm Al, 100 ppm Bi, 500 ppm In, and 5 ppm Mg, sodium acrylate, polyacrylic acid, and an alkaline electrolyte for preparing a negative electrode mixture (zinc oxide) 33.5 mass% potassium hydroxide aqueous solution containing 2.2 mass%) was mixed at a mass ratio of 39: 0.2: 0.2: 18 to prepare a gelled negative electrode mixture. The zinc alloy powder has an average particle size of 109 μm, passes through all 80 mesh screens, and passes through 200 mesh screens, and the zinc alloy powder is 25 mass% with respect to the total zinc alloy powder amount. The bulk density was 2.63 g / cm 3 .
更に、外装缶として、表面に無光沢Ｎｉメッキを施したキルド鋼板製で、図２に示す形状の単３形アルカリ電池用外装缶１を用意した。この外装缶１は、封口部分１０の厚みが０．２５ｍｍで、胴部分２０の厚みが０．１６ｍｍに加工され、また、電池を落下させたときに正極端子１ｂのへこみを防ぐために、正極端子部分の缶厚を胴部分２０より多少厚くしている。この外装缶１を用いて、以下のようにしてアルカリ電池を作製した。
Further, as an outer can, an outer can 1 for an AA alkaline battery made of a killed steel plate having a matte Ni plating on the surface and having the shape shown in FIG. 2 was prepared. The outer can 1 has a sealing portion 10 having a thickness of 0.25 mm and a
前記正極合剤：約１１ｇを、前記外装缶１に挿入してボビン状（中空円筒状）に加圧成形し、内径：９．１ｍｍ、外径：１３．７ｍｍ、高さ：１３．９ｍｍの３個の正極合剤成形体（密度：３．２１ｇ／ｃｍ３）が積み重なった状態とした。次に、外装缶１の開口端から高さ方向において３．５ｍｍの位置にグルーブを施し、外装缶１と封口体６との密着性を向上させるために、このグルーブ位置まで外装缶１の内側にピッチを塗布した。 About 11 g of the positive electrode mixture: inserted into the outer can 1 and press-molded into a bobbin shape (hollow cylindrical shape). The inner diameter is 9.1 mm, the outer diameter is 13.7 mm, and the height is 13.9 mm. Three positive electrode mixture molded bodies (density: 3.21 g / cm 3 ) were stacked. Next, in order to improve the adhesion between the outer can 1 and the sealing body 6 at a position of 3.5 mm in the height direction from the opening end of the outer can 1, the inner side of the outer can 1 up to this groove position. A pitch was applied.
次に、厚みが１００μｍで目付が３０ｇ／ｍ２のアセタール化ビニロンとテンセルからなる不織布を三重に重ねて筒状に巻き、底部になる部分を折り曲げてこの部分を熱融着し、一端が閉じられたコップ状のセパレータ３とした。このセパレータ３を、外装缶１内に挿入された正極１の内側に装填し、注入用のアルカリ電解液（酸化亜鉛を２．２質量％含有する３３．５質量％水酸化カリウム水溶液）１．３５ｇをセパレータの内側に注入し、さらに、前記負極合剤：５．７４ｇをセパレータ３の内側に充填して負極４とした。このとき、電池系内の水分量の合計は正極活物質１ｇ当たり０．２６１ｇで、正極容量に対する負極容量の比は１．１０であった。また、電池系内における電解液の水酸化カリウム濃度は、３４．５質量％となるように調整した。
Next, a nonwoven fabric made of acetalized vinylon having a thickness of 100 μm and a basis weight of 30 g / m 2 and tencel is overlapped in a cylinder, wound into a cylindrical shape, the bottom portion is bent, this portion is heat sealed, and one end is closed The cup-shaped
前記発電要素の充填の後、表面がスズメッキされた真鍮製であり、ナイロン６６製の封口体６と組み合わされた負極集電棒５を、負極４の中央部に差し込み、外装缶１の開口端部１ａの外側からスピニング方式によりかしめることにより、図２に示す単３形アルカリ電池を作製した。ここで、前記負極集電棒５は、打ち抜き・プレス加工により形成された厚みが０．４ｍｍのニッケルメッキ鋼板製の負極端子板７に、あらかじめ溶接により取り付けられたものを用いた。また、外装缶１の開口端と負極端子板７との間には、短絡防止のために絶縁板８を装着した。以上のようにして実施例１の筒形アルカリ電池を作製した。
After filling the power generation element, the negative electrode
実施例２
亜鉛合金粉末を、Ａｌを３００ｐｐｍ、Ｂｉを１００ｐｐｍ、Ｉｎを５００ｐｐｍ、Ｍｇを５ｐｐｍの割合で含有する亜鉛合金からなる粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。なお、実施例２で使用した亜鉛合金粉末は、その平均粒径、２００メッシュの篩い目を通過する粉末の割合、およびかさ密度が、実施例１で使用したものと同じである（後記の実施例３、４、比較例１〜４も同様である。）。
Example 2
A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the zinc alloy powder was changed to a powder composed of a zinc alloy containing 300 ppm Al, 100 ppm Bi, 500 ppm In, and 5 ppm Mg. . In addition, the zinc alloy powder used in Example 2 has the same average particle diameter, the ratio of the powder passing through a 200 mesh sieve, and the bulk density used in Example 1 (implementation described below) The same applies to Examples 3 and 4 and Comparative Examples 1 to 4.)
実施例３
亜鉛合金粉末を、Ａｌを１０００ｐｐｍ、Ｂｉを１００ｐｐｍ、Ｉｎを５００ｐｐｍ、Ｍｇを５０ｐｐｍの割合で含有する亜鉛合金からなる粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。
Example 3
A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the zinc alloy powder was changed to a powder composed of a zinc alloy containing 1000 ppm Al, 100 ppm Bi, 500 ppm In, and 50 ppm Mg. .
実施例４
亜鉛合金粉末を、Ａｌを１０００ｐｐｍ、Ｂｉを１００ｐｐｍ、Ｉｎを５００ｐｐｍ、Ｃａを５ｐｐｍの割合で含有する亜鉛合金からなる粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。
Example 4
A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the zinc alloy powder was changed to a powder composed of a zinc alloy containing 1000 ppm Al, 100 ppm Bi, 500 ppm In, and 5 ppm Ca. .
実施例５
亜鉛合金粉末を、Ａｌを１０００ｐｐｍ、Ｂｉを５０ｐｐｍ、Ｉｎを５００ｐｐｍ、Ｍｇを５ｐｐｍの割合で含有する亜鉛合金からなる粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。
Example 5
A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the zinc alloy powder was changed to a powder composed of a zinc alloy containing 1000 ppm Al, 50 ppm Bi, 500 ppm In, and 5 ppm Mg. .
実施例６
亜鉛合金粉末を、合金元素の組成が実施例１で使用したものと同じであり、平均粒径が５７μｍで、８０メッシュの篩い目を全て通過し、かつ２００メッシュの篩い目を通過する亜鉛合金粉末が、全亜鉛合金粉末量に対して１００質量％の亜鉛合金粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。
Example 6
Zinc alloy powder having the same alloy element composition as used in Example 1, having an average particle size of 57 μm, passing through all 80 mesh screens, and passing through 200 mesh screens A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the powder was changed to 100% by mass of zinc alloy powder with respect to the total amount of zinc alloy powder.
実施例７
亜鉛合金粉末を、合金元素の組成が実施例１で使用したものと同じであり、平均粒径が９０μｍで、８０メッシュの篩い目を全て通過し、かつ２００メッシュの篩い目を通過する亜鉛合金粉末が、全亜鉛合金粉末量に対して５０質量％の亜鉛合金粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。
Example 7
Zinc alloy powder having the same alloy element composition as used in Example 1, having an average particle size of 90 μm, passing through all 80 mesh screens, and passing through 200 mesh screens A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the powder was changed to 50% by mass of zinc alloy powder with respect to the total amount of zinc alloy powder.
実施例８
亜鉛合金粉末を、合金元素の組成が実施例１で使用したものと同じであり、平均粒径が１２６μｍで、８０メッシュの篩い目を全て通過し、かつ２００メッシュの篩い目を通過する亜鉛合金粉末が、全亜鉛合金粉末量に対して５質量％の亜鉛合金粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。
Example 8
Zinc alloy powder having the same alloy element composition as used in Example 1, having an average particle size of 126 μm, passing through all 80 mesh screens, and passing through 200 mesh screens A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the powder was changed to 5 mass% zinc alloy powder with respect to the total amount of zinc alloy powder.
比較例１
亜鉛合金粉末を、Ａｌを３０ｐｐｍ、Ｂｉを１５０ｐｐｍ、Ｉｎを５００ｐｐｍの割合で含有する亜鉛合金からなる粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。
Comparative Example 1
A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the zinc alloy powder was changed to a powder made of a zinc alloy containing 30 ppm Al, 150 ppm Bi, and 500 ppm In.
比較例２
亜鉛合金粉末を、Ａｌを３０ｐｐｍ、Ｂｉを１００ｐｐｍ、Ｉｎを５００ｐｐｍの割合で含有する亜鉛合金からなる粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。
Comparative Example 2
A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the zinc alloy powder was changed to a powder made of a zinc alloy containing 30 ppm Al, 100 ppm Bi, and 500 ppm In.
比較例３
亜鉛合金粉末を、Ａｌを３０ｐｐｍ、Ｂｉを１００ｐｐｍ、Ｉｎを５００ｐｐｍ、Ｍｇを５ｐｐｍの割合で含有する亜鉛合金からなる粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。
Comparative Example 3
A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the zinc alloy powder was changed to a powder made of a zinc alloy containing 30 ppm Al, 100 ppm Bi, 500 ppm In, and 5 ppm Mg. .
比較例４
亜鉛合金粉末を、Ａｌを１０００ｐｐｍ、Ｂｉを１００ｐｐｍ、Ｉｎを５００ｐｐｍの割合で含有する亜鉛合金からなる粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。
Comparative Example 4
A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the zinc alloy powder was changed to a powder made of a zinc alloy containing 1000 ppm Al, 100 ppm Bi, and 500 ppm In.
比較例５
亜鉛合金粉末を、Ａｌを１０００ｐｐｍ、Ｂｉを１５０ｐｐｍ、Ｉｎを５００ｐｐｍ、Ｍｇを５ｐｐｍの割合で含有する亜鉛合金からなる粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。
Comparative Example 5
A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the zinc alloy powder was changed to a powder made of a zinc alloy containing 1000 ppm Al, 150 ppm Bi, 500 ppm In, and 5 ppm Mg. .
比較例６
亜鉛合金粉末を、Ａｌを１０００ｐｐｍ、Ｂｉを３０ｐｐｍ、Ｉｎを５００ｐｐｍ、Ｍｇを５ｐｐｍの割合で含有する亜鉛合金からなる粉末に変更した以外は、実施例１と同様にして筒形アルカリ電池を作製した。
Comparative Example 6
A cylindrical alkaline battery was produced in the same manner as in Example 1 except that the zinc alloy powder was changed to a powder composed of a zinc alloy containing 1000 ppm Al, 30 ppm Bi, 500 ppm In, and 5 ppm Mg. .
実施例１〜８および比較例１〜６の筒形アルカリ電池について、下記のようにして放電特性確認試験およびガス量確認試験を行った。これらの結果を負極の亜鉛合金粉末の構成と共に表１および表２に示す。 About the cylindrical alkaline battery of Examples 1-8 and Comparative Examples 1-6, the discharge characteristic confirmation test and the gas amount confirmation test were done as follows. These results are shown in Tables 1 and 2 together with the structure of the zinc alloy powder of the negative electrode.
＜放電特性確認試験＞
実施例１〜８および比較例１〜６の筒形アルカリ電池を、２０℃でベース放電電流０．６５Ｗとし、３０秒間隔で１．５Ｗのパルス電流が流れた時点の電圧が１．０５Ｖ以下に低下するまでに要するパルス放電の回数を測定した。結果を表１および表２に示すが、表１および表２では、比較例１の電池での結果を１００とした場合の相対値で示している。
<Discharge characteristics confirmation test>
The cylindrical alkaline batteries of Examples 1 to 8 and Comparative Examples 1 to 6 had a base discharge current of 0.65 W at 20 ° C., and the voltage when a 1.5 W pulse current flowed at 30-second intervals was 1.05 V or less The number of pulse discharges required to decrease to a maximum was measured. The results are shown in Tables 1 and 2. In Tables 1 and 2, the results for the battery of Comparative Example 1 are shown as relative values when the result is 100.
＜ガス量確認試験＞
実施例１〜８および比較例１〜６の筒形アルカリ電池（前記の放電特性確認試験を行ったものとは別の電池）を、２０℃、１０Ωで４８時間放電させて過放電状態とし、その後２０℃で１２０時間保持した後の電池内部のガス量を測定した。また、前記のガス量測定を行ったものとは別の電池について、６０℃にて２４０時間保持した後に電池内部のガス量を測定し、未放電のガス量とした。ガス量の測定に当たっては、水中で電池を分解し、電池内のガスを捕集する水上置換法を採用した。また、前記の各ガス量測定は、実施例１〜８および比較例１〜６の電池をそれぞれ５個ずつ用い、これらの結果の平均値を求めた。結果を表１および表２に示すが、表１および表２では、比較例１の電池での結果を１００とした場合の相対値で示している。
<Gas amount confirmation test>
The cylindrical alkaline batteries of Examples 1 to 8 and Comparative Examples 1 to 6 (batteries different from those subjected to the discharge characteristic confirmation test) were discharged at 20 ° C. and 10Ω for 48 hours to be in an overdischarge state, Thereafter, the amount of gas inside the battery after being held at 20 ° C. for 120 hours was measured. Moreover, about the battery different from what performed said gas amount measurement, after hold | maintaining for 240 hours at 60 degreeC, the gas amount inside a battery was measured and it was set as the amount of undischarged gas. In measuring the amount of gas, a water replacement method was adopted in which the battery was disassembled in water and the gas in the battery was collected. Moreover, each said gas amount measurement used each 5 batteries of Examples 1-8 and Comparative Examples 1-6, and calculated | required the average value of these results. The results are shown in Tables 1 and 2. In Tables 1 and 2, the results for the battery of Comparative Example 1 are shown as relative values when the result is 100.
表１から明らかなように、ＭｇまたはＣａを含むとともに、Ｂｉ量を減少させ、Ａｌ量を増加した亜鉛合金粉末を負極に用いた実施例１〜８の筒形アルカリ電池では、未放電時および過放電時におけるガス量が少ない。そのため、実施例１〜８の筒形アルカリ電池では、未放電時および過放電時における電解液の漏出を防止できる。 As is clear from Table 1, in the cylindrical alkaline batteries of Examples 1 to 8 that contain zinc or alloy powder containing Mg or Ca, decreasing the amount of Bi, and increasing the amount of Al for the negative electrode, Less gas during overdischarge. Therefore, in the cylindrical alkaline batteries of Examples 1 to 8, it is possible to prevent leakage of the electrolytic solution during undischarged and overdischarged.
これに対し、表２から明らかなように、Ａｌ量が少なく、ＭｇおよびＣａを含まない亜鉛合金粉末を負極に用いて構成した比較例１、２の筒形アルカリ電池、およびＭｇを含有しているが、Ａｌ量が少ない亜鉛合金粉末を負極に用いて構成した比較例３の筒形アルカリ電池では、ＩｎやＢｉの含有量によらず、実施例１〜５の電池よりも未放電時または過放電時におけるガス量が多い。他方、Ａｌ量は適切であるが、ＭｇおよびＣａを含まない亜鉛合金粉末を負極に用いて構成した比較例４の筒形アルカリ電池では、過放電時におけるガス発生は抑制されているものの、未放電時におけるガス量が多い。また、Ｂｉ量が多い亜鉛合金粉末を負極に用いて構成した比較例５の筒形アルカリ電池では、過放電時におけるガス量が多く、Ｂｉ量が少ない亜鉛合金粉末を負極に用いて構成した比較例６の筒形アルカリ電池では、未放電時におけるガス量が多い。よって、比較例１〜６の電池では、未放電時または過放電時において、電解液の漏出の虞がある。 On the other hand, as is clear from Table 2, the cylindrical alkaline batteries of Comparative Examples 1 and 2 constituted by using a zinc alloy powder containing a small amount of Al and not containing Mg and Ca for the negative electrode, and containing Mg However, in the cylindrical alkaline battery of Comparative Example 3 configured by using the zinc alloy powder with a small amount of Al as the negative electrode, it is not discharged or more than the batteries of Examples 1 to 5 regardless of the contents of In and Bi. Large amount of gas during overdischarge. On the other hand, although the amount of Al is appropriate, in the cylindrical alkaline battery of Comparative Example 4 configured using a zinc alloy powder not containing Mg and Ca as the negative electrode, gas generation during overdischarge was suppressed, but Large amount of gas during discharge. Further, in the cylindrical alkaline battery of Comparative Example 5 configured using the zinc alloy powder with a large amount of Bi as the negative electrode, the comparison was configured using the zinc alloy powder with a large amount of gas during overdischarge and a small amount of Bi as the negative electrode. In the cylindrical alkaline battery of Example 6, the amount of gas when not discharged is large. Therefore, in the batteries of Comparative Examples 1 to 6, there is a possibility that the electrolyte solution leaks when undischarged or overdischarged.
また、２００メッシュの篩い目を通過する微細な亜鉛合金粉末の割合を増加させた実施例６の電池に比べて、微細な亜鉛合金粉末の量を減少させた実施例１〜５、８の電池では、未放電時のガス発生がより良好に抑えられている。 Further, the batteries of Examples 1 to 5 and 8 in which the amount of the fine zinc alloy powder was decreased as compared with the battery of Example 6 in which the ratio of the fine zinc alloy powder passing through the 200 mesh sieve was increased. Then, the gas generation at the time of non-discharge is suppressed more favorably.
なお、実施例１〜５の電池と比較例１〜６の電池とは、負極に使用した亜鉛合金粉末の形態（２００メッシュの篩い目を通過する粉末の割合）が同様であるが、これらの電池では放電特性が同等であり、亜鉛合金粉末の組成を変更しても、従来の電池と同レベルの放電特性を維持できる。 In addition, the batteries of Examples 1 to 5 and the batteries of Comparative Examples 1 to 6 are similar in the form of the zinc alloy powder used in the negative electrode (ratio of the powder passing through the 200 mesh sieve). The battery has the same discharge characteristics, and even if the composition of the zinc alloy powder is changed, the discharge characteristics at the same level as those of the conventional battery can be maintained.
１ 外装缶
２ 正極
３ セパレータ
４ 負極
５ 負極集電棒
６ 樹脂製の封口体
７ 負極端子板
８ 絶縁板
９ 金属ワッシャ
６３ 防爆用の薄肉部
DESCRIPTION OF SYMBOLS 1 Exterior can 2
Claims (6)
前記亜鉛合金が、Ｂｉを５０〜１２５ｐｐｍ、Ａｌを１００〜２０００ｐｐｍ、並びに、ＣａおよびＭｇの少なくとも一方を合計で１〜５０ｐｐｍ含有することを特徴とするアルカリ電池。 An alkaline battery having a gelled negative electrode containing zinc alloy powder and an electrolytic solution comprising an alkaline aqueous solution,
The alkaline alloy characterized in that the zinc alloy contains 50 to 125 ppm Bi, 100 to 2000 ppm Al, and 1 to 50 ppm in total of at least one of Ca and Mg.
The alkaline battery according to any one of claims 1 to 5, wherein the electrolytic solution is a potassium hydroxide aqueous solution, and the concentration of potassium hydroxide of the electrolytic solution in the battery system is 30 to 35% by mass on average.