JP2009051116A - Tire mold and tire manufacturing method - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a tire mold 48 which can be fabricated at a low cost and make a tire whose lopsided wear is inhibited. <P>SOLUTION: This tire mold 48 is equipped with a tread ring 50 having a cavity surface 78 with which a part corresponding with a tread of a green tire comes into contact. In addition, the tread ring 50 is configured of a top ring 66 and a bottom ring 68, and the top ring 66 has an upper contact part 72 which comes into contact with the bottom ring 68. The upper contact part 72 is equipped with many protuberant strips 104 extending in a radial direction. The bottom ring 68 is equipped with a lower contact part 76 which comes into contact with the top ring 66. The lower contact part 76 is equipped with many protuberant strips 112 extending in a radial direction. The protuberant strips 104 of the upper contact part 72 and the protuberant strips 112 of the lower contact part 76 are arranged alternately in the circumference. <P>COPYRIGHT: (C)2009,JPO&INPIT

Description

  The present invention relates to a tire mold and a tire manufacturing method.

  In the tire forming / vulcanizing step, a green tire (also referred to as Raw Cover) obtained by preforming is put into a mold. The green tire is heated while being pressurized in a cavity surrounded by a mold and a bladder. The rubber composition of the green tire flows in the cavity by pressurization and heating. The rubber causes a crosslinking reaction by heating, and a tire is obtained. Molds used in the molding / vulcanizing process are roughly classified into split molds and two-piece molds.

  The split mold includes an arc-shaped tread segment. A ring-shaped cavity surface is formed by arranging a large number of tread segments. In the molding and vulcanization process, when the tire is removed from the split mold, these tread segments are moved radially outward and pulled away from the tread. With this split mold, the tire can be easily taken out.

  In this split mold, the surface of the segment that comes into contact with the adjacent segment is a split surface. A minute gap generated between the dividing surface and another dividing surface adjacent to the dividing surface is a parting line. The parting line extends in the vertical direction on the cavity surface.

  FIG. 4 is a cross-sectional view showing a part of a conventional tire mold 2. The mold 2 in FIG. 4 is a two-piece mold. FIG. 4 also shows the bladder 4 and the green tire 6 in the middle of the molding / vulcanizing process. The left-right direction in FIG. 4 is the radial direction.

  The mold 2 includes a tread ring 8, an upper mold 10, a lower mold 12, an upper bead ring 14, a lower bead ring 16, an upper clamp ring 18, a lower clamp ring 20, and a mold ring 22. The tread ring 8 includes an upper ring 24 and a lower ring 26. In this mold 2, a ring-shaped cavity surface 28 is formed by combining the upper ring 24 and the lower ring 26. In the molding / vulcanizing step, the tread surface of the tire is formed by the portion corresponding to the tread of the green tire 6 coming into contact with the cavity surface 28.

  The upper ring 24 includes a split surface 30 that contacts the lower ring 26. The lower ring 26 includes a split surface 32 that contacts the upper ring 24. A minute gap generated between the dividing surface 30 of the upper ring 24 and the dividing surface 32 of the lower ring 26 is a parting line 34. In this mold 2, the parting line 34 is usually provided at a position corresponding to the equator plane of the tire.

  The upper mold 10 has a ring shape. The upper mold 10 includes a recess 36 into which the upper ring 24 is fitted, and an upper holding portion 38 that contacts the lower mold 12. The upper holding portion 38 is provided with a convex portion 40 protruding downward. The convex portion 40 extends in the circumferential direction.

  The lower mold 12 has a ring shape. The lower mold 12 includes a recess 42 into which the lower ring 26 is fitted, and a lower holding portion 44 that contacts the upper mold 10. The lower holding portion 44 is provided with a convex portion 46 protruding upward. The convex portion 46 extends in the circumferential direction.

  As illustrated, in the mold 2, the convex portion 46 of the lower holding portion 44 is located inside the convex portion 40 of the upper holding portion 38 in the radial direction. The upper mold 10 does not shift in the radial direction with respect to the lower mold 12. For this reason, the upper ring 24 fitted in the recess 36 of the upper mold 10 does not shift in the radial direction with respect to the lower ring 26 fitted in the recess 42 of the lower mold 12. A portion of the mold 2 constituted by the upper holding portion 38 and the lower holding portion 44 is an in-row. Although not shown, the mold 2 is also provided with a dwell on its outer surface from the viewpoint of preventing the deviation.

In the molding and vulcanization process, if a part of the green tire is sandwiched between parting lines, burrs are generated on the tire. This burr affects tire performance. Japanese Patent Application Laid-Open No. 8-216620 discloses a pneumatic tire in which the generation of burrs is suppressed.
JP-A-8-216620

  In the molding and vulcanization process, the rubber composition of the green tire is sandwiched between the parting lines to form burrs. As described above, in the two-piece mold, the parting line formed on the cavity surface is at a position corresponding to the equator surface of the tire. For this reason, in the tire manufactured with this mold, the burr extends along the equator plane. When a vehicle equipped with the tire travels at high speed, uneven wear occurs on the tire. This uneven wear affects tire durability, steering stability, and grip stability.

  As described above, in the split mold, the parting line extends in the vertical direction on the cavity surface. In the tire manufactured by this split mold, the burr extends in the axial direction of the tire. In this tire, the occurrence of uneven wear is suppressed as compared with a tire manufactured by a two-piece mold. This split mold can suppress the occurrence of uneven wear. However, since this split mold has a large number of parts, this split mold has a high manufacturing cost. This split mold affects the production cost of the tire.

  An object of the present invention is to provide a tire mold that can manufacture a tire with low production cost and suppressed occurrence of uneven wear.

The tire manufacturing method according to the present invention includes:
(1) A process for obtaining a green tire by preforming,
(2) The green tire has a tread ring having a cavity surface with which a portion corresponding to the tread of the tire can come into contact, and the tread ring is composed of an upper ring and a lower ring. The upper contact portion includes an upper contact portion that contacts the lower ring, the upper contact portion includes a plurality of protrusions extending in the radial direction, and the lower ring includes a lower contact portion that contacts the upper ring. The lower contact portion includes a plurality of ridges extending in the radial direction, and the ridges of the upper contact portion and the ridges of the lower contact portion can be alternately arranged in the circumferential direction. And (3) a step in which the green tire is pressurized and heated in the mold.

Preferably, in this manufacturing method, the vertical distance A from the tip of the upper ring ridge to the tip of the lower ring ridge, the diameter DC of the cavity surface, and the cavity surface included in the cross section of the tread ring. Of the green tire and the outer diameter DG of the green tire can satisfy the relationship represented by the following formula (I).
DG <DC-2R + (4 (R) ^2- (A) ² ) ^1/2 (I)

  Preferably, in this manufacturing method, the said protruding item | line is provided with the slope which inclines with respect to the circumferential direction. The inclination angle of this slope is 30 ° or more and 60 ° or less.

  The tire mold according to the present invention includes a tread ring having a cavity surface on which a portion corresponding to a tread of a green tire can abut. The tread ring is composed of an upper ring and a lower ring. The upper ring includes an upper contact portion that comes into contact with the lower ring. The upper contact portion includes a large number of ridges extending in the radial direction. The lower ring includes a lower contact portion that comes into contact with the upper ring. The lower contact portion includes a plurality of ridges extending in the radial direction. The ridges of the upper contact portion and the ridges of the lower contact portion can be alternately arranged in the circumferential direction.

  In the tire mold according to the present invention, the tread ring includes an upper ring and a lower ring. This mold is a two-piece mold. The number of parts of this mold is smaller than the number of parts of the split mold having a large number of tread segments. The production cost of this mold is low. Molds with low production costs can contribute to tire production costs. Since the ridges provided on the upper contact portion of the upper ring and the ridges provided on the lower contact portion of the lower ring are alternately arranged in the circumferential direction, the upper ring is arranged in the radial direction with respect to the lower ring. There is no deviation. The upper ring does not shift in the circumferential direction with respect to the lower ring. In order to prevent this shift, the mold does not need to be provided with a member such as an in-row and a dwell. In the tire manufactured with this mold, the occurrence of uneven wear is suppressed. This tire is excellent in durability, steering stability, and grip stability.

  Hereinafter, the present invention will be described in detail based on preferred embodiments with appropriate reference to the drawings.

  FIG. 1 is a cross-sectional view showing a part of a tire mold 48 according to an embodiment of the present invention. FIG. 1 also shows a bladder 4 and a green tire 6 (also referred to as Raw Cover) during the molding / vulcanizing process. The left-right direction in FIG. 1 is the radial direction. This mold 48 is a two-piece mold. The mold 48 is mainly used for manufacturing a tire in which a groove is not provided on the tread surface. The mold 48 includes a tread ring 50, an upper mold 52, a lower mold 54, an upper bead ring 56, a lower bead ring 58, an upper clamp ring 60, a lower clamp ring 62, and a mold ring 64.

  The tread ring 50 has a ring shape. The tread ring 50 is also referred to as OCR (One Casting Ring). The tread ring 50 includes an upper ring 66 and a lower ring 68 located on the lower side of the upper ring 66. In FIG. 1, an alternate long and short dash line CL <b> 1 represents the center line of the tread ring 50.

  The upper ring 66 has a ring shape. The upper ring 66 includes an upper surface 70 and an upper contact portion 72. The upper surface 70 is provided inside the upper ring 66 in the radial direction. The upper surface 70 extends in the circumferential direction. The upper contact portion 72 is provided below the upper ring 66. The upper contact portion 72 contacts the lower ring 68.

  The lower ring 68 has a ring shape. The lower ring 68 includes a lower surface 74 and a lower contact portion 76. The lower surface 74 is provided inside the lower ring 68 in the radial direction. The lower surface 74 extends in the circumferential direction. The lower contact portion 76 is provided on the upper side of the lower ring 68. The lower contact portion 76 contacts the upper ring 66. In the mold 48, when the upper ring 66 is combined with the lower ring 68, a cavity surface 78 composed of the upper surface 70 of the upper ring 66 and the lower surface 74 of the lower ring 68 is formed. In other words, in this mold 48, the tread ring 50 has a ring-shaped cavity surface 78. As shown in the drawing, the portion 80 corresponding to the tread of the green tire 6 can come into contact with the cavity surface 78.

  The upper mold 52 has a ring shape. The upper mold 52 includes a recess 82, an upper dividing surface 84, and a cavity surface 86. The recess 82 extends upward from the lower side of the upper mold 52. The recess 82 extends in the circumferential direction. The upper ring 66 of the tread ring 50 is fitted into the recess 82. The upper dividing surface 84 is located below the upper mold 52. The upper dividing surface 84 contacts the lower mold 54. The cavity surface 86 extends in the circumferential direction. As shown in the figure, a portion 88 a corresponding to one side wall of the green tire 6 can come into contact with the cavity surface 86.

  The lower mold 54 has a ring shape. The lower mold 54 includes a recess 90, a lower dividing surface 92, and a cavity surface 94. The recess 90 extends downward from the upper side of the lower mold 54. The recess 90 extends in the circumferential direction. The lower ring 68 of the tread ring 50 is fitted into the recess 90. The lower dividing surface 92 is located above the lower mold 54. The lower dividing surface 92 abuts on the upper mold 52. The cavity surface 94 extends in the circumferential direction. As shown in the drawing, the cavity surface 94 can abut a portion 88 b corresponding to the other sidewall of the green tire 6.

  The upper bead ring 56 has a ring shape. The upper bead ring 56 is located inside the upper mold 52 in the radial direction. The upper bead ring 56 has a cavity surface 96. A portion 98 a corresponding to one bead of the green tire 6 can come into contact with the cavity surface 96.

  The lower bead ring 58 has a ring shape. The lower bead ring 58 is located on the radially inner side of the lower mold 54. The lower bead ring 58 has a cavity surface 100. A portion 98 b corresponding to the other bead of the green tire 6 can come into contact with the cavity surface 100.

  The mold ring 64 is located inside the upper bead ring 56 in the radial direction. The upper clamp ring 60 is located on the radially inner side of the upper bead ring 56. The upper clamp ring 60 is located below the mold ring 64. One end of the bladder 4 is positioned between the upper clamp ring 60 and the mold ring 64. In the mold 48, one end of the bladder 4 is fixed to the mold 48 by the mold ring 64 and the upper clamp ring 60.

  The lower clamp ring 62 is located above the lower bead ring 58. The other end of the bladder 4 is positioned between the lower clamp ring 62 and the lower bead ring 58. In the mold 48, the other end of the bladder 4 is fixed to the mold 48 by the lower clamp ring 62 and the lower bead ring 58.

  As shown in FIG. 1, in this mold 48, the cavity surface 78 of the tread ring 50, the cavity surface 86 of the upper mold 52, the cavity surface 96 of the upper bead ring 56, the cavity surface 94 of the lower mold 54, and The inner surface constituted by the cavity surface 100 of the lower bead ring 58 is the cavity surface of the mold 48. A space surrounded by the cavity surface of the mold 48 and the outer surface 102 of the bladder 4 is a cavity.

  FIG. 2 is an enlarged side view showing a part of the cavity surface 78 of the tread ring 50 of FIG. FIG. 2 shows a state in which the upper ring 66 and the lower ring 68 are combined. In FIG. 2, the front side of the paper surface is the center side of the mold 48, and the back side of the paper surface is the radially outer side of the mold 48. The left-right direction in FIG. 2 is the circumferential direction. In FIG. 2, the alternate long and short dash line CL <b> 2 is the center line of the cavity surface 78. The center line CL2 corresponds to the equator plane of the tire tread.

  The upper contact portion 72 of the upper ring 66 includes a plurality of ridges 104. These ridges 104 are arranged in the circumferential direction. Although not shown, the ridge 104 extends in the radial direction. The ridge 104 is provided with a pair of inclined surfaces 108 extending upward from the tip 106 so as to expand the skirt. A tip 106 of the ridge 104 is rounded. In the upper contact portion 72, a recess 110 is formed between one protrusion 104 and another protrusion 104 adjacent to the one protrusion 104.

  The lower contact portion 76 of the lower ring 68 includes a large number of ridges 112. These ridges 112 are arranged in the circumferential direction. Although not shown, the ridge 112 extends in the radial direction. The ridge 112 includes a pair of slopes 116 extending downward from the tip 114 so as to expand the bottom. The tip 114 of the ridge 112 is rounded. In the lower contact portion 76, a recess 118 is formed between one ridge 112 and another ridge 112 adjacent to the one ridge 112.

  As described above, on the upper contact portion 72 of the upper ring 66, a large number of ridges 104 extending in the radial direction are arranged in the circumferential direction. A large number of radially extending ridges 112 are arranged in the circumferential direction on the lower contact portion 76 of the lower ring 68. As illustrated, the protrusions 104 of the upper contact portion 72 and the protrusions 112 of the lower contact portion 76 are alternately arranged in the circumferential direction. The ridge 104 of the upper contact portion 72 is fitted into the recess 118 of the lower contact portion 76. The ridge 112 of the lower contact portion 76 is fitted into the recess 110 of the upper contact portion 72. In the mold 48, the upper ring 66 does not shift in the radial direction with respect to the lower ring 68. The upper ring 66 does not shift in the circumferential direction with respect to the lower ring 68. In order to prevent this shift, the mold 48 does not need to be provided with another member such as an in-row and a dwell. In the mold 48, the protrusions 104 and 112 are also provided on the upper divided surface 84 of the upper mold 52 and the lower divided surface 92 of the lower mold 54 from the viewpoint of preventing displacement of the upper ring 66 with respect to the lower ring 68. It may be provided. From the viewpoint of the manufacturing cost of the mold 48, the ridges 104 and 112 may not be provided on the upper divided surface 84 and the lower divided surface 92.

  In the mold 48, a minute gap formed between the upper contact portion 72 and the lower contact portion 76 in the cavity surface 78 of the tread ring 50 is the parting line 120. When a tire is manufactured with the mold 48, if the rubber composition of the green tire 6 enters the parting line 120, burrs are formed in the tire. As shown in FIG. 2, the parting line 120 has a zigzag shape. For this reason, the burrs formed on the tire also have a zigzag shape (not shown). In this tire, the occurrence of uneven wear is suppressed as compared with a tire having a burr manufactured by the conventional two-piece mold 2 and extending along the equator plane. The tire manufactured with this mold 48 is excellent in durability, grip stability, and steering stability.

  When a tire is manufactured by the steady operation of the mold 48, first, the green tire 6 is obtained by preforming. Next, the green tire 6 is put into the opened mold 48. When thrown, the bladder 4 is contracted. As a result, the bladder 4 is positioned inside the green tire 6. The bladder 4 expands by filling with gas. Due to this expansion, the green tire 6 is deformed. This deformation is called shaping. Next, the mold 48 is tightened, and the internal pressure of the bladder 4 is increased. The green tire 6 is sandwiched between the cavity surface of the mold 48 and the outer surface 102 of the bladder 4 and is pressurized. The green tire 6 is heated by heat conduction from the mold 48 and the bladder 4. The rubber composition of the green tire 6 flows by pressurization and heating. The rubber causes a crosslinking reaction by heating, and a tire is obtained.

  As shown in FIG. 2, in this mold 48, the tip 106 of the protrusion 104 of the upper ring 66 is rounded, so there is a gap between the tip 106 and the recess 118 of the lower ring 68. Is formed. In the mold 48, the tip end 114 of the ridge 112 of the lower ring 68 is rounded, so that a gap is formed between the tip 114 and the recess 110 of the upper ring 66. When the tire is manufactured, the gas in the cavity can be effectively discharged through these gaps. With this mold 48, tire air remaining defects can be effectively prevented. The mold 48 can contribute to improving the quality of the tire.

  FIG. 3 is a cross-sectional view showing a state where the green tire 6 is put into the mold 48. In FIG. 3, the lower mold 54, the lower ring 68 of the tread ring 50, and the green tire 6 are shown. The mold 48 shown in FIG. 3 is in an opened state. The left-right direction in FIG. 3 is the radial direction. In FIG. 3, an alternate long and short dash line CL <b> 1 is a center line of the tread ring 50. The point PA is a position corresponding to the equator plane of the tire. This center line CL1 passes through this point PA. The point PB represents the position on the cavity surface 78 of the tip 114 of the ridge 112 provided on the lower ring 68. A two-point difference line LA is an imaginary line representing the tip 106 of the protrusion 104 of the upper ring 66 (not shown), and a point PC represents the position of the tip 106 on the cavity surface 78. A point PD represents a position where the outer diameter of the green tire 6 is maximum.

  The tread of a tire usually has a shape that is convex outward in the radial direction. For this reason, the cavity surface 78 provided in the tread ring 50 also has a shape convex outward in the radial direction. The point PB is located radially inward from the point PA. The mold 48 is configured such that the point PB is located radially outside the point PD. When the green tire 6 is put into the mold 48, the green tire 6 does not contact the lower ring 68 in the portion of the cavity surface 78 from the point PB to the point PC. The green tire 6 is put in without contacting the mold 48. By using this mold 48, the tire can be manufactured stably. Tires manufactured with this mold 48 are of high quality.

  In FIG. 3, a double arrow line A represents the vertical distance from the tip 106 of the ridge 104 of the upper ring 66 (corresponding to the point PC) to the tip 114 of the ridge 112 of the lower ring 68 (corresponding to the point PB). ing. A double arrow line DC represents the diameter of the cavity surface 78 obtained based on the point PA. This diameter DC is the maximum diameter of the cavity surface 78. A double arrow line DR represents the diameter of the cavity surface 78 obtained based on the point PB. The arrow line R represents the radius of curvature of the cavity surface 78 at this point PA. The curvature radius R is determined based on the cavity surface 78 included in the cross section of the tread ring 50. A double arrow line DG represents the outer diameter of the green tire 6 obtained based on the point PD.

In this mold 48, from the viewpoint that the green tire 6 can be loaded without contacting the mold 48, the vertical distance A, the outer diameter DC of the cavity surface 78, the radius of curvature R of the cavity surface 78 and the outside of the green tire 6. The diameter DG can satisfy the relationship represented by the following mathematical formula (I). In other words, the vertical distance A is determined based on the mathematical formula (I). The right side of the mathematical formula (I) is the diameter DR. In the mold 48 having the vertical distance A determined in this way, the diameter DR is larger than the outer diameter DG, so that the green tire 6 can be put in without contacting the mold 48. With this mold 48, tires can be produced stably. Tires manufactured with this mold 48 are of high quality.
DG <DC-2R + (4 (R) ^2- (A) ² ) ^1/2 (I)

  In the mold 48, the vertical distance A is preferably 5 mm or more and 60 mm or less. By setting the distance A to be 5 mm or more, the positional deviation of the upper ring 66 with respect to the lower ring 68 can be effectively prevented. By setting this distance A to (R) 60 mm or less, the influence of the burrs formed on the tire on uneven wear is effectively suppressed.

  As shown in FIG. 2, the slope 108 provided on the protrusion 104 of the upper ring 66 is inclined with respect to the center line CL <b> 2 extending in the circumferential direction. In FIG. 2, the solid line LB represents the inclination direction of one slope 108 of the ridge 104 provided on the upper ring 66. A solid line LC represents the inclination direction of the other slope 108 of the ridge 104. The angle α is an angle formed by the solid line LB with respect to the center line CL2. This angle α is an inclination angle of the one slope 108. The angle β is an angle formed by the solid line LC with respect to the center line CL2. This angle β is the inclination angle of the other slope 108.

  In the mold 48, from the viewpoint of suppressing uneven wear of the manufactured tire, the angle α is preferably 30 ° or more, more preferably 35 ° or more, and particularly preferably 40 ° or more. From the viewpoint of suppressing the mold manufacturing cost and maintaining the rigidity of the ridge 104, the angle α is preferably 60 ° or less, more preferably 55 ° or less, and particularly preferably 50 ° or less.

  In this mold 48, from the viewpoint of suppressing uneven wear of the manufactured tire, the angle β is preferably 30 ° or more, more preferably 35 ° or more, and particularly preferably 40 ° or more. From the viewpoint of suppressing the mold manufacturing cost and maintaining the rigidity of the ridge 104, the angle β is preferably 60 ° or less, more preferably 55 ° or less, and particularly preferably 50 ° or less. From the viewpoint that uneven wear of the manufactured tire is further effectively suppressed, the angle β is preferably the same as the angle α.

  In the mold 48, the slope of the ridge 112 provided on the lower ring 68 facing the slope 108 of the ridge 104 provided on the upper ring 66 from the viewpoint of suppressing generation of unnecessary burrs and uneven wear of the tire. The inclination direction of 116 is preferably the same as the inclination direction of the slope 108 of the upper ring 66. From this viewpoint, the inclination angle of the slope 116 of the lower ring 68 is also preferably 30 ° or more, more preferably 35 ° or more, and particularly preferably 40 ° or more. The inclination angle is preferably 60 ° or less, more preferably 55 ° or less, and particularly preferably 50 ° or less.

  Hereinafter, the effects of the present invention will be clarified by examples. However, the present invention should not be construed in a limited manner based on the description of the examples.

[Example 1]
A pneumatic tire (size = 280 / 680R18) was manufactured using the tire mold of Example 1 having the basic configuration shown in FIG. 1 and the specifications shown in Table 2 below. The mold tread ring includes an upper ring and a lower ring. The ridges provided on the upper ring and the ridges provided on the lower ring have the same shape. The inclination angle of the ridge slope is 45 °. The vertical distance A from the tip of the upper ring ridge to the tip of the lower ring ridge is 20.0 mm. The maximum diameter DC of the cavity surface of this tread ring is 680.0 mm. The radius of curvature R at the position corresponding to the equator plane of the cavity surface is 1000.0 mm. The diameter DR of the cavity surface at the position on the cavity surface of the tip of the ridge provided on the lower ring is 679.9 mm. The outer diameter DG of the green tire put into this mold is 673.0 mm.

[Examples 5 to 8]
A tire was manufactured using a mold having the same configuration as the mold used for manufacturing the tire of Example 1 except that the vertical distance A was as shown in Tables 1 and 2 below.

[Examples 3 and 4 and 9 and 10]
A tire was manufactured using a mold having the same configuration as the mold used for manufacturing the tire of Example 1 except that the slopes of the slopes of the ridges were as shown in Tables 1 and 2 below.

[Example 2]
A tire is manufactured using a mold having the same configuration as the mold used for manufacturing the tire of Example 1 except that the vertical distance A and the slope of the slope of the ridges are as shown in Tables 1 and 2 below. did.

[Comparative Example 1]
It is the conventional mold for tires. This mold is not provided with ridges.

[Evaluation]
The tire manufactured with the prototype mold was mounted on a passenger car (FR car) having a displacement of 3000 cc. The internal pressure of this tire was 200 kPa. The size of the wheel is 18 × 11J. This passenger car was subjected to a running test on an asphalt road surface, and a sensory evaluation was performed by a driver for durability, steering stability and grip stability. After the running test, the appearance of the tire was observed to examine the degree of uneven wear. The results are index values with Comparative Example 1 being 100, and are shown in Tables 1 and 2 below. The higher the score, the better.

  As shown in Tables 1 and 2, the tire manufactured with the tire mold of the example has a higher evaluation than the tire manufactured with the mold of the comparative example. From this evaluation result, the superiority of the present invention is clear.

  The present invention can be applied to various tire molds.

FIG. 1 is a cross-sectional view illustrating a part of a tire mold according to an embodiment of the present invention. FIG. 2 is an enlarged side view showing a part of the cavity surface of the tread ring of FIG. 1. FIG. 3 is a cross-sectional view showing a state where a green tire is put into a mold. FIG. 4 is a cross-sectional view showing a part of a conventional tire mold.

Explanation of symbols

2, 48 ... Mold 4 ... Bladder 6 ... Green tire 8, 50 ... Tread ring 10, 52 ... Upper mold 12, 54 ... Lower mold 14, 56 ... Upper bead ring 16, 58 ... Lower bead ring 18, 60 ... Upper clamp ring 20, 62 ... Lower clamp ring 22, 64 ... Mold ring 24, 66 ... Upper ring 26, 68 .. Lower ring 28, 78, 86, 94, 96, 100 ... Cavity surface 30, 32 ... Dividing surface 34, 120 ... Parting line 36, 42, 82, 90 ... Recess 38 ..Upper holding part 40, 46 ... convex part 44 ... lower holding part 70 ... upper surface 72 ... upper contact part 74 ... lower surface 76 ... lower contact part 80 ... on tread Corresponding part 84 ... Upper divided surface 88a, 88b: portion corresponding to a sidewall 92 ... lower divided surface 98a, 98b ... portion corresponding to a bead 102 ... outer surface 104, 112 ... ridge 106, 114 ... Tip 108, 116 ... Slope 110,118 ... Dent

Claims (4)

A process for obtaining green tires by preforming,
The green tire has a tread ring having a cavity surface on which a portion corresponding to the tread of the tire can contact, and the tread ring is composed of an upper ring and a lower ring, and the upper ring is the lower ring. An upper contact portion that abuts the upper ring, the upper contact portion includes a plurality of ridges extending in the radial direction, and the lower ring includes a lower contact portion that abuts the upper ring. The lower contact portion is provided with a plurality of ridges extending in the radial direction, and the tire mold in which the ridges of the upper contact portion and the ridges of the lower contact portion can be alternately arranged in the circumferential direction is provided. A method for manufacturing a tire, including a step of charging a green tire and a step of pressing and heating the green tire in the mold. Vertical distance A from the tip of the upper ring ridge to the tip of the lower ring ridge, the diameter DC of the cavity surface, the radius of curvature R of the cavity surface included in the cross section of the tread ring, and the green tire The manufacturing method according to claim 1, wherein the outer diameter DG of the material can satisfy the relationship represented by the following mathematical formula (I).
DG <DC-2R + (4 (R) ^2- (A) ² ) ^1/2 (I) The ridge has a slope inclined with respect to the circumferential direction,
The manufacturing method according to claim 1, wherein an inclination angle of the slope is 30 ° or more and 60 ° or less. A tread ring having a cavity surface on which a portion corresponding to a tread of a green tire can abut is provided.
This tread ring is composed of an upper ring and a lower ring,
The upper ring has an upper contact portion that comes into contact with the lower ring,
This upper contact portion is provided with a large number of ridges extending in the radial direction,
The lower ring has a lower contact portion that comes into contact with the upper ring,
This lower contact portion is provided with a number of ridges extending in the radial direction,
A tire mold in which the ridges of the upper contact portion and the ridges of the lower contact portion can be alternately arranged in the circumferential direction.

Images