JP2008000886A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2008000886A5 JP2008000886A5 JP2007158663A JP2007158663A JP2008000886A5 JP 2008000886 A5 JP2008000886 A5 JP 2008000886A5 JP 2007158663 A JP2007158663 A JP 2007158663A JP 2007158663 A JP2007158663 A JP 2007158663A JP 2008000886 A5 JP2008000886 A5 JP 2008000886A5
- Authority
- JP
- Japan
- Prior art keywords
- layer
- cutting tool
- coated cutting
- thickness
- tool insert
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
TiN TiCxNy TiCxOz Al2O3開始 Al2O3
段階 1及び6 2 3 4 5
TiCl4 1.5% 1.4% 2%
N2 38% 38%
CO2 2% 4%
CO 6%
AlCl3 3.2%
H2S − 0.3%
HCl 3.2% 3.2%
H2 残部 残部 残部 残部 残部
CH3CN − 0.6%
圧力 160mbar 60mbar 60mbar 60mbar 70mbar
温度 930℃ 885℃ 1000℃ 1000℃ 1000℃
時間 30分 4.5時間 20分 2分 7時間
段階 1及び6 2 3 4 5
TiCl4 1.5% 1.4% 2%
N2 38% 38%
CO2 2% 4%
CO 6%
AlCl3 3.2%
H2S − 0.3%
HCl 3.2% 3.2%
H2 残部 残部 残部 残部 残部
CH3CN − 0.6%
圧力 160mbar 60mbar 60mbar 60mbar 70mbar
温度 930℃ 885℃ 1000℃ 1000℃ 1000℃
時間 30分 4.5時間 20分 2分 7時間
結果
工具寿命に達するのに要した機械加工のサイクル数
市販インサート 59.5
B) 61
C) 63
工具寿命に達するのに要した機械加工のサイクル数
市販インサート 59.5
B) 61
C) 63
Claims (6)
- 少なくとも1つのすくい面と少なくとも1つの逃げ面とを有し、且つ通常は多角形または円形の本体を備える超硬合金の被覆切削工具インサートであって、
前記被覆切削工具インサートは、4.4−6.6wt%のCoと、4−8.5wt%の立方晶炭化物と、残分のWCと、の組成を有し、且つ0.78−0.92の範囲内のCW比と、立方晶炭化物TiC、TaC及びNbCが枯渇した厚さ10−40μmの表面区域と、を有し、
前記被覆切削工具インサートは、x≧0、y≧0且つx+y=1である少なくとも1つのTiCxNy層を含む厚さ10−25μmの被膜で少なくとも部分的に被覆されており、且つ
α−Al2O3層が少なくとも前記すくい面上の外側層であり、且つ
少なくとも1つの前記すくい面上において、
− 前記TiCxNy層は、3μmから15μmまでの厚さを有し、且つ、50−500MPaの引張応力レベルを有し、
− 前記α−Al2O3層は、3μmから12μmまでの厚さを有し、且つ、I(012)/I(024)≧1.3のXRD回折強度比を有し、且つ少なくともすくい面上の削屑接触区域内における、平均Ra値がMRa<0.12μmを有する最も外側の層であり、且つ
前記少なくとも1つの逃げ面上において、
− 前記TiCxNy層は、500−700MPaの範囲内の引張応力を有し、
− 前記α−Al2O3層は、I(012)/I(024)<1.5のXRD回折強度比を有し、または、
少なくとも1つの前記すくい面と少なくとも1つの前記逃げ面との上において、
− 前記TiCxNy層は、3μmから15μmまでの厚さを有し、且つ50−500MPaの引張応力レベルを有し、
− 前記α−Al2O3層は、3μmから12μmまでの厚さを有し、I(012)/I(024)≧1.3のXRD回折強度比を有し、少なくとも前記すくい面上の前記削屑接触区域内において平均Ra値MRa<0.12μmを有するすくい面上の最も外側の層であり、且つ前記逃げ面上において、前記最も外側の層は、着色された耐熱性塗料または着色PVD層から成る、
ことを特徴とする被覆切削工具インサート。 - 前記TiCxNy層と前記Al2O3層との間に、薄い0.2−2μmのTiCxNyOz結合層を有し、x≧0、z>0、y≧0であることを特徴とする請求項1に記載の被覆切削工具インサート。
- 前記α−Al2O3層は、組織係数TC(012)>1.3を有する012方向の組織を有することを特徴とする請求項1または2に記載の被覆切削工具インサート。
- 前記α−Al2O3層は、組織係数TC(110)>1.5を有する110方向の組織を有することを特徴とする請求項1−3のいずれか1に記載の被覆切削工具インサート。
- 前記被覆は、5μm未満の合計層厚さに、Ti、Nb、Hf、V、Ta、Mo、Zr、Cr、W、及びAlから選択される金属元素を有する金属窒化物、炭化物及び酸化物の少なくとも一つで構成されている追加の層を含むことを特徴とする請求項1−4のいずれか1に記載の被覆切削工具インサート。
- 前記立方晶炭化物が枯渇した前記表面区域は、15μmから35μmまでの厚さを有することを特徴とする請求項1から5のいずれか1に記載の被覆切削工具インサート。