JP2007306890A - Paper sheet for cleansing breast of cow - Google Patents
Paper sheet for cleansing breast of cow Download PDFInfo
- Publication number
- JP2007306890A JP2007306890A JP2006141706A JP2006141706A JP2007306890A JP 2007306890 A JP2007306890 A JP 2007306890A JP 2006141706 A JP2006141706 A JP 2006141706A JP 2006141706 A JP2006141706 A JP 2006141706A JP 2007306890 A JP2007306890 A JP 2007306890A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- wiping
- sheet
- embossed
- breast
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、乳牛の乳房清拭用ペーパー、すなわち、乳牛の搾乳前のプレディッピング後、搾乳後のポストディッピング後に、乳房又は乳頭を清拭するためのペーパーに関する。 The present invention relates to a paper for wiping the dairy cow, that is, a paper for wiping the breast or nipple after pre-dipping before milking and after post-dipping after milking.
酪農家において、乳牛の乳房炎は、乳量及び乳成分（乳質）の低下の原因となり、また治療代負担も生ずるため、その予防が重要とされている。
乳房炎は搾乳時に乳管内へ細菌が侵入して増殖することが一因とされていることから、その防止には搾乳に際して乳牛の搾乳前のプレディッピング（消毒液を乳頭につける）と搾乳終了後のポストディッピング（プレディッピングとは異なる消毒液を乳頭につける）とを行うのが一般的とされている。
ところで、各ディッピングの後には、消毒液等を清拭する作業が行われるが、このような清拭作業は、出願人が知る限り多くの酪農家においては国内２社から販売されている再生古紙を原料とするドライタイプの清拭用ペーパー又は一般的な織布タオルが使用されている。近年では、使い捨てができることから、清拭用ペーパーの需要が高まりつつある。
ここで、乳頭が濡れた状態で搾乳器を取付けると乳頭上で搾乳器が滑ること（業界では、この滑りをライナースリップとも言う）があり、このライナースリップによって乳頭が痛められて乳房炎が主ずることがある。従って、特にプレディッピング後の清拭作業において消毒薬等を確実に清拭することは重要な作業として認知されている。
他方、搾乳前には乳頭刺激（前搾り）を行うのが一般的である。乳頭刺激は、脳下垂体後葉から排乳のためのホルモン（オキシトシン）分泌を促し搾乳効果を向上せしめるために行われ、通常、ホルモンは乳頭刺激から約１分後に分泌されその後５〜６分間程度分泌されるため、効率の良く搾乳を行うべく乳頭刺激からホルモン分泌までの約１分間にプレディッピング、清拭作業、搾乳器の装着までを終了させ、その後５〜６分間搾乳作業を行う。
このように、乳頭刺激から１分間という限られた時間内に、プレディッピング、搾乳器の装着までの作業を行わなければならないため各作業は迅速性が求められる。
そして、各作業のうち必要な消毒時間を要するディッピング作業や、乳房を痛めないように慎重を要する搾乳機の装着時間を確保すべく、特に清拭作業の迅速性が重要となる。 してみると、乳房の清拭用ペーパーにおいては消毒液の確実な清拭と迅速な清拭が求められる。
Mastitis is thought to be caused by bacteria invading into the ducts and multiplying during milking. To prevent this, pre-dipping (milking disinfectant on the nipple) before milking and finishing milking It is common practice to perform post-dipping later (applying a disinfectant different from pre-dipping to the nipple).
By the way, after each dipping, an operation of wiping the disinfectant is performed. As far as the applicant knows, many dairy farmers sell recycled recycled paper sold by two domestic companies. A dry type wiping paper or a general woven towel is used. In recent years, since it can be disposable, the demand for wiping paper is increasing.
Here, if the breast pump is installed with the nipple wet, the breast pump may slip on the nipple (in the industry, this slip is also called liner slip). There is a shift. Accordingly, it is recognized as an important task to surely wipe off the disinfectant and the like particularly in the wiping operation after pre-dipping.
On the other hand, nipple stimulation (pre-squeezing) is generally performed before milking. Nipple stimulation is performed to enhance the milking effect by promoting the secretion of hormones (oxytocin) for lactation from the posterior lobe of the pituitary gland. Normally, hormones are secreted about 1 minute after stimulation of the nipples and about 5-6 minutes thereafter. Since it is secreted, pre-dipping, wiping work, and installation of a milking machine are completed in about 1 minute from nipple stimulation to hormone secretion for efficient milking, and then milking is performed for 5 to 6 minutes.
As described above, since the work up to pre-dipping and the installation of the breast pump must be performed within a limited time of 1 minute after the nipple stimulation, each work is required to be quick.
And in order to ensure the dipping work which requires the required disinfection time among each work | work, and the installation time of the milking machine which needs carefulness so that a breast may not be hurt, especially quickness of a wiping work becomes important. As a result, the wiping paper for breasts requires reliable wiping of the disinfectant and quick wiping.
しかし、従来の乳房清拭用ペーパーは、清拭の迅速性について十分に満足しているとはいえずさらなる改良を要するものであった。
そこで本発明の主たる課題は、搾乳前処理のうちの特に清拭作業の時間を短縮すべく、迅速に清拭作業を行える乳房清拭用ペーパーを提供することにある。
However, conventional breast wiping papers are not fully satisfied with the speed of wiping and require further improvements.
Then, the main subject of this invention is providing the paper for breast wiping which can perform a wiping operation | work rapidly, in order to shorten the time of the wiping operation | work especially in the milking pretreatment.
上記課題を解決した本発明およびその作用効果は次記のとおりである。
＜請求項１記載の発明＞
パルプを主原料とし、
ＪＩＳ Ｐ ８１２４による坪量が１０〜４０ｇ／ｍ2のシートが２枚重ね状態で接合され、
ＪＩＳ Ｌ １０９６ Ｅ法によりソフトネスが、縦５．０〜１１．０ｇ、横３．０〜１０．０ｇ、
ＫＥＳ試験機による曲げ剛性Ｂが、縦０．０１０〜０．０４５ｇ・ｃｍ2／ｃｍ、横０．０１０〜０．０４５ｇ・ｃｍ2／ｃｍであり、かつ、
ＪＡＰＡＮ ＴＡＰＰＩ Ｎｏ．３２−２：２０００に基づいて測定される吸水性が０．１〜１．０秒である、ことを特徴とする乳牛の乳房清拭用ペーパー。
The present invention that has solved the above-described problems and the effects thereof are as follows.
<Invention of
Pulp is the main raw material,
Two sheets having a basis weight of 10 to 40 g / m 2 according to JIS P 8124 are joined in a stacked state,
Softness is 5.0-11.0 g in length, 3.0-10.0 g in width, according to JIS L 1096 E method.
Flexural rigidity by KES tester B is vertical 0.010~0.045g · cm 2 / cm, the lateral 0.010~0.045g · cm 2 / cm, and,
JAPAN TAPPI No. A paper for wiping the dairy cow's breast, wherein the water absorption measured based on 32-2: 2000 is 0.1 to 1.0 seconds.
（作用効果）
本発明のものは、後に実施例で示すように、従来例や市販品のものに比較して、ソフトネスの値が小さく、かつ、曲げ剛性Ｂの値が小さい。ソフトネスは、硬さ又はやわらかさの指標であり、曲げ剛性Ｂは、「値が大きいほど、曲げにくい」ことを表わす。したがって、本発明のものは、柔らかい紙質であり、小さい力でシートを折ったり、曲げたりといったシート外形を容易に変えることができる。特に曲げ剛性Ｂが小さいことは、乳房に対し、その乳房の形に合うようシートがフィットさせることができることを意味し、しかも、柔らかいので、乳房を痛めることもなく、確実に清拭できるのである。
また、本発明のものは、従来例や市販品のものに比較して吸水性が０．１〜１．０秒であり極めて早い。これは消毒液等を迅速に吸収することができることを意味する。
(Function and effect)
As will be shown later in the examples, the present invention has a smaller softness value and a smaller bending rigidity B than conventional and commercially available products. The softness is an index of hardness or softness, and the bending rigidity B represents that “the larger the value, the harder it is to bend”. Therefore, the thing of this invention is soft paper quality, and can change the sheet | seat external shape, such as folding and bending a sheet | seat with small force. In particular, the small bending rigidity B means that the sheet can be fitted to the breast so as to fit the shape of the breast, and since it is soft, it can be reliably wiped without damaging the breast. .
Moreover, the thing of this invention is 0.1 to 1.0 second and a water absorption is very quick compared with the thing of a prior art example or a commercial item. This means that disinfectant etc. can be absorbed rapidly.
＜請求項２記載の発明＞
前記パルプが古紙パルプを含まないものである請求項１記載の乳牛の乳房清拭用ペーパー。
<Invention of
The dairy cow wiping paper according to
（作用効果）
古紙パルプ中には皮膚刺激やアレルギーの原因となる蛍光染料（蛍光増白剤）が含有されていることがある。また、蛍光染料は発癌性物質や環境ホルモン （内分泌攪乱化学物質）であるとの疑いがあり、食品衛生法第６条では食品及び食品に触れる全てのものに蛍光染料を使用することが禁止されている。さらに、古紙パルプに含まれるインキ残留成分であると考えられているビスフェノールＡも環境ホルモンとして認知されており、ごく微量で脳の記憶に関する脳内物質（エストラジオール）の働きを阻害する研究報告がある。
従って、乳房清拭用ペーパーは、乳汁に触れる可能性が高いため、本発明に従って蛍光染料等含有のおそれのある古紙パルプを原料としないのが望ましい。
(Function and effect)
Waste paper pulp may contain fluorescent dyes (fluorescent whitening agents) that cause skin irritation and allergies. In addition, there is a suspicion that fluorescent dyes are carcinogens and environmental hormones (endocrine disrupting chemicals), and Article 6 of the Food Sanitation Law prohibits the use of fluorescent dyes for foods and anything that touches foods. ing. Furthermore, bisphenol A, which is considered to be an ink residual component contained in waste paper pulp, is also recognized as an environmental hormone, and there are research reports that inhibit the action of substances in the brain (estradiol) related to brain memory in a very small amount. .
Therefore, since the wiping paper is highly likely to come into contact with milk, it is desirable not to use waste paper pulp that may contain a fluorescent dye or the like as a raw material according to the present invention.
＜請求項３記載の発明＞
生分解性である請求項１または２記載の乳牛の乳房清拭用ペーパー。
<Invention of
3. The paper for wiping dairy cows according to
（作用効果）
本発明のものは、生分解可能であるので、使用後の清拭用ペーパーは堆肥に混ぜて簡易に処理することができる。ここで、生分解性とは自然界における微生物の関与により低分子化されて分解されることをいう。
(Function and effect)
Since the thing of this invention is biodegradable, the paper for wiping after use can be easily processed by mixing with compost. Here, biodegradability means that the molecule is degraded and degraded due to the involvement of microorganisms in nature.
＜請求項４記載の発明＞
ＫＥＳ試験機による平均曲げヒステリシス幅２ＨＢが、縦０．００５〜０．１５ｇ・ｃｍ／ｃｍ、横０．００５〜０．２０ｇ・ｃｍ／ｃｍである請求項１〜３の何れか１項に記載の乳牛の乳房清拭用ペーパー。
<Invention of Claim 4>
The average bending hysteresis width 2HB by a KES tester is 0.005 to 0.15 g · cm / cm in length and 0.005 to 0.20 g · cm / cm in width. Dairy cow paper cleaning paper.
（作用効果）
平均曲げヒステリシス幅２ＨＢは、「値が大きいほど、回復性（復元性）が悪い」ことを表わす。本発明では、従来例や市販品のものに比較して、平均曲げヒステリシス幅２ＨＢの値が小さい。したがって、清拭時に隈なく清拭でき、またペーパーを取り去るときに、消毒液を残存させることもない。
(Function and effect)
The average bending hysteresis width 2HB indicates that “the larger the value, the worse the recovery (restorability)”. In the present invention, the value of the average bending hysteresis width 2HB is small as compared with the conventional example and those on the market. Therefore, it can be wiped without wrinkles during wiping, and the disinfectant does not remain when the paper is removed.
＜請求項５記載の発明＞
前記シート相互の接合態様が次記（ａ）または（ｂ）である、
（ａ）一方のシートのエンボス凸部の天部と、他方のシートのエンボス凸部の天部とが接着剤により接着される、
（ｂ）一方のシートのエンボス凸部が他方のシートのエンボスの凹部内に嵌り込みかつその嵌り込み域において空間を残して嵌り込むように前記エンボス凸部の天部と前記エンボス凹部の底部とが接着剤により接着される、
請求項１〜４の何れか１項に記載の乳牛の乳房清拭用ペーパー。
<Invention of Claim 5>
The bonding mode between the sheets is the following (a) or (b):
(A) The top of the embossed convex portion of one sheet and the top of the embossed convex portion of the other sheet are bonded with an adhesive.
(B) The top of the embossed convex part and the bottom part of the embossed concave part so that the embossed convex part of one sheet is fitted into the concave part of the embossed part of the other sheet and the space is left in the fitting area. Is bonded by an adhesive,
The paper for the breast cleaning of the dairy cow of any one of Claims 1-4.
（作用効果） (Function and effect)
シート相互の接合態様として、エンボス加工のみの接合でもよいが、接合を確実にならしめ接着剤による接合形態が望ましい。しかも、空間を形成し消毒液の吸収性を高め、嵩高性を得るために、上記のエンボスしたシート相互を接合させるものが特に望ましい。 The sheet may be bonded only by embossing, but it is desirable to use a bonding form with an adhesive that surely bonds the sheet. Moreover, in order to form a space, increase the absorbency of the disinfectant solution, and obtain bulkiness, it is particularly desirable to join the embossed sheets.
以上のとおり、本発明によれば、迅速に乳頭に付着した消毒液を清拭することができる乳房清拭用ペーパーが提供される。 As described above, according to the present invention, there is provided a wiping paper for wiping that can quickly wipe disinfectant adhering to a teat.
以下、本発明を実施するための最良の形態について詳説する。
本発明の乳牛の乳房清拭用ペーパーの坪量（ＪＩＳ Ｐ ８１２４）は、１枚のシートにおいて、１０ｇ／ｍ2〜４０ｇ／ｍ2が望ましい（より望ましくは１７ｇ／ｍ2〜２５ｇ／ｍ2）。１０ｇ／ｍ2未満であるとシート自体が薄くなるため、消毒液の単位面積あたりの吸収量が少なくなり、清拭時に消毒液の吸収が不十分であるとともに、シートが破れたり穴があいたりする恐れがある。４０ｇ／ｍ2を超えると、消毒液の吸収は十分であるものの、全体的にシートの柔軟性が低下し剛度が高まり、乳房に対し、その乳房の形に合うようシートがフィットさせることができにくくなる。なお、最良の形態としては、シートが２枚重ね状態で接合されたものである。
Hereinafter, the best mode for carrying out the present invention will be described in detail.
The basis weight of the breast Qing拭用paper cows of the present invention (JIS P 8124), in one sheet, 10g / m 2 ~40g / m 2 is preferable (more preferably 17g / m 2 ~25g / m 2 ). If it is less than 10 g / m 2 , the sheet itself becomes thin, so the amount of the disinfectant absorbed per unit area decreases, and the disinfectant absorbs insufficiently during wiping, and the sheet breaks or has holes. There is a fear. If it exceeds 40 g / m 2 , the disinfectant solution is sufficiently absorbed, but the overall flexibility of the sheet is reduced and the rigidity is increased, so that the sheet can be fitted to the breast to match the shape of the breast. It becomes difficult. In the best mode, two sheets are joined in a stacked state.
さらに、１枚シート（エンボス未加工。以下特性を示す場合は同様。）基準で、ＪＩＳ Ｌ １０９６ Ｅ法によりソフトネスが、柔軟性確保の観点から、縦５．０〜１１．０ｇ（より望ましくは８．０〜１０．５ｇ）、横３．０〜１０．０ｇ（より望ましくは５．０〜８．０ｇ）とされる。 Further, on the basis of a single sheet (unembossed, the same applies when the following characteristics are shown), softness is compliant with JIS L 1096 E method, from the viewpoint of ensuring flexibility, 5.0 to 11.0 g (more desirable Is 8.0 to 10.5 g) and the width is 3.0 to 10.0 g (more desirably 5.0 to 8.0 g).
他方、ＫＥＳ試験機（カトーテック社製「ＫＥＳＦＢ２−ＡＵＴＯ−Ａ」による曲げ剛性Ｂが、縦０．０１０〜０．０４５ｇ・ｃｍ2／ｃｍ、（より望ましくは０．０１０〜０．３０ｇ・ｃｍ2／ｃｍ）、横０．０１０〜０．０４５ｇ・ｃｍ2／ｃｍ（より望ましくは０．０１０〜０．０２０）ｇ・ｃｍ2／ｃｍが望ましい。この測定方法は、紙や布帛の分野で周知であり、かつ同機の取り扱い説明書に記載のとおりであるので説明を省略する。 On the other hand, the bending rigidity B by KES testing machine (“KESFB2-AUTO-A” manufactured by Kato Tech Co., Ltd. is 0.010 to 0.045 g · cm 2 / cm in length, (more preferably 0.010 to 0.30 g · cm 2 / cm), and a width of 0.010 to 0.045 g · cm 2 / cm (more preferably 0.010 to 0.020) g · cm 2 / cm is desirable.This measuring method is used in the field of paper and fabrics. The description is omitted because it is well known and as described in the instruction manual of the aircraft.
また、ＪＡＰＡＮ ＴＡＰＰＩ Ｎｏ．３２−２：２０００に基づいて測定される吸水性が０．１〜１．０秒（より望ましくは０．１〜０．３秒）である。なお、吸水性の測定方法については後述する。 In addition, JAPAN TAPPI No. The water absorption measured based on 32-2: 2000 is 0.1 to 1.0 seconds (more desirably 0.1 to 0.3 seconds). In addition, the measuring method of water absorption is mentioned later.
さらに、平均曲げヒステリシス幅２ＨＢが、縦０．００５〜０．１５ｇ・ｃｍ／ｃｍ、横０．００５〜０．２０ｇ・ｃｍ／ｃｍであるのが望ましい。 Furthermore, it is desirable that the average bending hysteresis width 2HB is 0.005 to 0.15 g · cm / cm in length and 0.005 to 0.20 g · cm / cm in width.
本発明において、消毒液の清拭性及び吸収性を良好とするために、２枚のシート相互の接合態様が次記（ａ）または（ｂ）であるのが望ましい。
（ａ）一方のシートのエンボス凸部の天部と、他方のシートのエンボス凸部の天部とが接着剤により接着される。
（ｂ）一方のシートのエンボス凸部が他方のシートのエンボスの凹部内に嵌り込みかつその嵌り込み域において空間を残して嵌り込むように前記エンボス凸部の天部と前記エンボス凹部の底部とが接着剤により接着される。
In the present invention, in order to improve the wiping and absorbing properties of the disinfectant, it is desirable that the joining mode of the two sheets is the following (a) or (b).
(A) The top part of the embossed convex part of one sheet and the top part of the embossed convex part of the other sheet are bonded with an adhesive.
(B) The top of the embossed convex part and the bottom part of the embossed concave part so that the embossed convex part of one sheet is fitted into the concave part of the embossed part of the other sheet and the space is left in the fitting area. Are bonded by an adhesive.
（ａ）の形態例について説明すれば、図１に示すように、シート１と２とを２枚重ね状態で接着したもので、その坪量は１０〜４０ｇ／ｍ2とされている。その接着態様は、「Ｔｉｐ ｔｏ Ｔｉｐ」形態としており、一方のシート１のエンボス凸部１Ａの天部と、他方のシート２のエンボス凸部２Ａの天部とが接着剤３により接着したものである。
If the example of (a) is demonstrated, as shown in FIG. 1, the sheet |
（ｂ）の形態例について説明すれば、図２に示すように、一方のシート１のエンボス凸部が他方のシート２のエンボスの凹部内に嵌り込みかつその嵌り込み域において空間を残して嵌り込むように前記エンボス凸部の天部と前記エンボス凹部の底部とが接着剤３により接着したものである。
If the example of (b) is demonstrated, as shown in FIG. 2, the embossing convex part of one sheet |
エンボスの形状は、図示例では裁切四角錐形としてあるが、裁切円錐形や、天部が平面形状で楕円や三角その他多角形などとすることができる。シート相互の接着のために天部は可能な限り平坦であるのが望ましい。天部の面積は０．１〜４０．０ｍｍ2、より好適には０．２５〜４．０ｍｍ2、最も望ましくは０．５〜２．０ｍｍ2である。 The embossed shape is a cut quadrangular pyramid in the illustrated example, but may be a cut conical shape, an ellipse, a triangle or other polygonal shape with a top portion having a planar shape. It is desirable that the top be as flat as possible for bonding the sheets together. Area of the top portion 0.1~40.0mm 2, more preferably 0.25~4.0mm 2, most desirably 0.5 to 2.0 mm 2.
かかる山形のエンボスは図３に図示されているように規則的に多数形成され、エンボスセクションＸ，Ｘ…が形成されている。このエンボスセクションＸ，Ｘ…間に、エンボスが形成されていない、直線状の交差し一辺の長さが１．７３１〜５０．０ｍｍ、好適には１５．０〜５０．０ｍｍで、幅が０．８２４〜２０．０ｍｍ、好適には１．２ｍｍ〜５．０ｍｍの格子状の抜き柄セクションＹが形成されている。抜き柄セクションＹにおいてはシート１，２は接着されていない。
As shown in FIG. 3, a large number of such embossed embosses are regularly formed, and embossed sections X, X... Are formed. No embossing is formed between the embossed sections X, X..., And the length of one side is 1.731 to 50.0 mm, preferably 15.0 to 50.0 mm, and the width is 0. A grid-shaped punched section Y of 824 to 20.0 mm, preferably 1.2 to 5.0 mm is formed. In the punched pattern section Y, the
エンボスセクションＸの面積に対するそのエンボスセクションＸ内の接着剤３による接着部分の総面積は５．０〜３０．０％、好適には９．０〜２５．０％、最も望ましくは１０．０〜１４．５％である。 The total area of the bonded portion by the adhesive 3 in the embossed section X relative to the area of the embossed section X is 5.0 to 30.0%, preferably 9.0 to 25.0%, most preferably 10.0 to 14.5%.
ここで、シート相互の接着剤としては、ＰＶＡ、ＣＭＣ、ＭＣ、デンプンなどを使用できる。 Here, PVA, CMC, MC, starch, etc. can be used as the adhesive between sheets.
接着すべき天部の面積は０．１〜４０．０ｍｍ2、より好適には０．２５〜４．０ｍｍ2、最も望ましくは０．５〜２．０ｍｍ2であるが、天部の面積が過度に小さいとシート相互の接着強度が低下する。天部の面積が過度に大きいと、エンボスによる吸収空間の容積が小さくなり、吸収能力に低下に繋がる。これと関係して、エンボスセクションＸの面積に対するそのエンボスセクションＸ内の接着剤３による接着部分の総面積は５〜３０％、好適には９．０〜２５．０％、最も望ましくは１０．０〜１４．５％であるが、この面積率が小さいと、単位面積当たりの吸収空間の容積を大きくすることができるものの、シート相互の接着強度が低下する。面積率が大きいと、エンボスによる吸収空間の容積が小さくなり、吸収能力に低下に繋がる。 Area of the top portion to be bonded is 0.1~40.0mm 2, more preferably 0.25~4.0mm 2, but most desirably 0.5 to 2.0 mm 2, the area of the top portion If it is too small, the adhesive strength between sheets decreases. When the area of the top is excessively large, the volume of the absorption space due to embossing becomes small, leading to a decrease in absorption capacity. In this connection, the total area of the bonded portion by the adhesive 3 in the embossed section X relative to the area of the embossed section X is 5 to 30%, preferably 9.0 to 25.0%, most preferably 10. Although the area ratio is 0 to 14.5%, if the area ratio is small, the volume of the absorption space per unit area can be increased, but the adhesive strength between sheets decreases. When the area ratio is large, the volume of the absorption space by embossing becomes small, leading to a decrease in absorption capacity.
抜き柄セクションＹは、格子状である限り、正四角形の格子であるほか、長方形の格子や斜め格子形状であってもよい。格子の一辺の長さは１．７３１〜５０．０ｍｍ、好適には１５．０〜５０．０ｍｍで、幅が０．８２４〜２０．０ｍｍ、好適には１．２〜５．０ｍｍが望ましい。この格子長さが過度に短いと、エンボスセクションによる十分な吸収力が得られない。反対に、格子長さが過度に長いと、抜柄セクションによる平面方向への拡散が十分得られない。 As long as the cut-out section Y has a lattice shape, it may be a regular square lattice, a rectangular lattice, or an oblique lattice shape. The length of one side of the grating is 1.731 to 50.0 mm, preferably 15.0 to 50.0 mm, and the width is 0.824 to 20.0 mm, preferably 1.2 to 5.0 mm. If the lattice length is excessively short, sufficient absorption by the embossed section cannot be obtained. On the other hand, if the lattice length is excessively long, sufficient diffusion in the plane direction by the handle section cannot be obtained.
また、格子幅が過度に短いと、抜柄の空間が小さく拡散前に抜き空間が液体により飽和してしまうため、吸収スピードが得られない。反対に、格子幅が過度に長いと、抜柄部のシート自体が貼りつくことで抜柄の空間が維持されず、拡散につながらない。 On the other hand, if the grid width is excessively short, the extraction space is small and the extraction space is saturated with liquid before diffusion, so that the absorption speed cannot be obtained. On the other hand, if the lattice width is excessively long, the pattern space is not maintained because the sheet of the pattern portion sticks, and diffusion does not occur.
抜き柄セクションＹの面積はエンボスセクションＸの面積の１０．０〜５０．０％、特に２０．０〜３０．０％が望ましい。 The area of the punched pattern section Y is preferably 10.0 to 50.0%, particularly 20.0 to 30.0% of the area of the embossed section X.
シート１枚の紙厚は、１３０〜２５０μｍ、好ましくは１５０〜２００μｍとされる。なお、紙厚測定は、ＪＩＳ Ｐ ８１１１の条件下で、尾崎製作所ダイヤルシックネスゲージ「ＰＥＡＣＯＣＫ Ｇ型」を用いて測定する。具体的には、プランジャーと測定台の間にゴミ、チリ等がないことを確認してプランジャーを測定台の上におろし、前記ダイヤルシックネスゲージのメモリを移動させてゼロ点を合わせ、次いで、プランジャーを上げて試料（乳房清拭用ペーパー）を試験台の上におき、プランジャーをゆっくりと下ろしそのときのゲージを読み取る。このとき、プランジャーをのせるだけとする。なお、紙厚は測定を１０回行って得られる平均値とする。
The sheet thickness of one sheet is 130 to 250 μm, preferably 150 to 200 μm. The paper thickness is measured using a OZAKI MFG dial thickness gauge “PEACOCK G type” under the conditions of JIS P8111. Specifically, confirm that there is no dust, dust, etc. between the plunger and the measuring table, lower the plunger on the measuring table, move the memory of the dial thickness gauge to adjust the zero point, and then Then, raise the plunger and place the sample (paper for wiping the breast) on the test table, slowly lower the plunger and read the gauge at that time. At this time, only the plunger is placed. The paper thickness is an average value obtained by performing
さらに、柔軟性の観点から、本発明に係る乳房清拭用ペーパーは、伸び率が１０．０〜 ３０．０％にあることが望まれる。 Furthermore, from the viewpoint of flexibility, the breast cleaning paper according to the present invention is desired to have an elongation of 10.0 to 30.0%.
また、本発明に係る乳房清拭用ペーパーは、吸水量測定試験により測定される吸水量が１５０ｇ／ｍ2以上であることが望まれる。吸水量が１５０ｇ／ｍ2未満であると、消毒液の吸収性が良好でない。望ましくは３５０〜７００ｇ／ｍ2とされる。なお、吸水量測定試験については後述する。 Moreover, it is desirable that the amount of water absorption measured by the water absorption amount measurement test is 150 g / m 2 or more in the paper for breast cleaning according to the present invention. If the water absorption is less than 150 g / m 2 , the absorbency of the disinfectant solution is not good. Desirably, it is 350-700 g / m < 2 >. The water absorption measurement test will be described later.
また、本発明に係る乳房清拭用ペーパーは、ＪＩＳ Ｐ ８１１１に規定される条件下でＪＩＳ Ｐ ８１１３の規定に従って測定される乾燥時の縦方向及び横方向の引張強さが、それぞれ８００〜９００ＣＮ／２５ｍｍおよび２００〜３２０ＣＮ／２５ｍｍであり、かつ縦方向の引張強さが横方向の引張強さの２〜４倍であるのが好ましい。 Further, the breast wiping paper according to the present invention has a tensile strength in the machine direction and the transverse direction of 800 to 900 CN at the time of drying measured under the conditions specified in JIS P 8111 according to the specifications of JIS P 8113. / 25 mm and 200 to 320 CN / 25 mm, and the tensile strength in the longitudinal direction is preferably 2 to 4 times the tensile strength in the transverse direction.
さらに、清拭時にシートが破れたり穴があいたりすることを防止するため、ＪＩＳ Ｐ ８１１３の規定に従って測定される湿潤時の縦方向及び横方向の引張強さが、それぞれ２００〜４５０ＣＮ／２５ｍｍおよび５０〜１５０ＣＮ／２５ｍｍであり、かつ縦方向の引張強さが横方向の引張強さの０．２５〜９．０倍であるのが好ましい。 Furthermore, in order to prevent the sheet from being torn or having a hole during wiping, the tensile strength in the longitudinal direction and the transverse direction when measured according to the provisions of JIS P 8113 is 200 to 450 CN / 25 mm and Preferably, the tensile strength is 50 to 150 CN / 25 mm, and the tensile strength in the longitudinal direction is 0.25 to 9.0 times the tensile strength in the transverse direction.
本発明の乳牛の乳房清拭用ペーパーは、パルプを主原料とする紙シートである。この場合、バージンパルプ１００％が最適である。しかし、全量を古紙パルプとすることもできる。古紙パルプを含ませる場合、４０％以下が特に望ましい。 The milk cleaning paper for dairy cows of the present invention is a paper sheet mainly made of pulp. In this case, 100% virgin pulp is optimal. However, the total amount can also be used paper pulp. When used paper pulp is included, 40% or less is particularly desirable.
本発明に係る乳房清拭用ペーパーでは、公知の原料パルプ、ＮＢＫＰとＬＢＫＰとを任意の割合で配合したものを用いることができるが、特に紙力が不足しがちのときには、ＮＢＫＰ：ＬＢＫＰが１０：０〜５：５、特に７：３〜５：５の比率で配合されたものを推奨する。ＮＢＫＰは、平均繊維長が長く引張り強度が高く、これを高配合とすることによって紙力を増強できる。 In the wiping paper according to the present invention, a known raw material pulp, a blend of NBKP and LBKP at an arbitrary ratio, can be used. : 0 to 5: 5, particularly 7: 3 to 5: 5 is recommended. NBKP has a long average fiber length and a high tensile strength, and the paper strength can be enhanced by using a high blending ratio.
紙力増強のために、原料パルプの一部または全てを叩解して製造することもできる。原料パルプの一部を叩解する場合、ＮＢＫＰ及びＬＢＫＰともに同レベルで叩解するほか、両者を異なるレベルで若しくは一方のみを叩解することもできる。原料パルプの全てを叩解する場合には、ＮＢＫＰ及びＬＢＫＰともに同レベルで叩解するほか、両者を異なるレベルで叩解することもできる。 In order to increase paper strength, some or all of the raw pulp can be beaten and produced. When beating part of the raw pulp, both NBKP and LBKP can be beaten at the same level, or both can be beaten at different levels or only one. When beating all the raw pulp, both NBKP and LBKP can be beaten at the same level, and both can be beaten at different levels.
また、本発明の乳房清拭用ペーパーは生分解性であるのが望ましい。分解性とするにあたっては、例えば、生分解性樹脂繊維を原料パルプに混合せしめて抄紙することができる。生分解性樹脂繊維としては、ポリ乳酸系繊維、ポリブチレンテフタレート系繊維、ポリブチレンサクシネート系繊維等の生分解性繊維が挙げられる。具体例としては、「ラクトロン：カネボウ社開発」、「プラスターチ：クラレ社開発」、「テラマック：ユニチカ社開発」が挙げられる。生分解性樹脂は、一般に酸素含有量が高く、燃焼カロリーが低いため、焼却時に炉を傷めることがなく、また有毒ガスの発生もないという利点ももたらす。 It is also desirable that the breast cleaning paper of the present invention is biodegradable. In making it decomposable, for example, paper can be made by mixing biodegradable resin fibers with raw material pulp. Examples of the biodegradable resin fiber include biodegradable fibers such as polylactic acid fiber, polybutylene terephthalate fiber, and polybutylene succinate fiber. Specific examples include “Lactron: Kanebo Company Development”, “Plastarch: Kuraray Company Development”, and “Teramac: Unitika Company Development”. The biodegradable resin generally has a high oxygen content and a low calorie calorie value, so that it does not damage the furnace at the time of incineration and does not generate toxic gas.
ところで、先の説明からも判るように、本発明で規定する特性は、使用パルプの選定、抄造法、抄紙法、添加剤の選定などによって得ることができる。 By the way, as can be seen from the above description, the characteristics defined in the present invention can be obtained by selection of pulp used, papermaking method, papermaking method, selection of additives, and the like.
なお、本発明の清拭用ペーパーが消毒液は特に限定されるものではないが、現在主に酪農家の間で使用されている「クウォーターメイト」（ヨウ素溶液） （輸入販売元：日本全薬工業、製造元：ウェストアグロ） に特に適する。 The disinfecting solution of the wiping paper of the present invention is not particularly limited. However, “Quarte Mate” (iodine solution) currently used mainly among dairy farmers (Import / Distributor: Nippon Zenyaku) (Industry, manufacturer: West Agro)
以下、本発明を実施例及び比較例によって説明する。比較例は、従来例（先行技術製品としてのＡ社及びＢ社の市販品）である。各測定方法については下記のとおりである。 Hereinafter, the present invention will be described with reference to examples and comparative examples. The comparative example is a conventional example (commercial product of Company A and Company B as a prior art product). Each measuring method is as follows.
（測定条件）
全ての測定は、原則としてＪＩＳ Ｐ ８１１１に規定される条件下で行った。
(Measurement condition)
All measurements were performed under the conditions specified in JIS P 8111 in principle.
（坪量）
紙の坪量は、ＪＩＳ Ｐ ８１２４の規定に準拠して測定した。
(Basis weight)
The basis weight of the paper was measured in accordance with JIS P 8124.
（紙厚）
紙厚は、尾崎製作所ダイヤルシックネスゲージ「ＰＥＡＣＯＣＫ Ｇ型」を用いて測定した。具体的手法については前述のとおりであるので、ここでは詳細を省略する。
(Paper thickness)
The paper thickness was measured using an Ozaki Dial Thickness Gauge “PEACOCK G type”. Since the specific method is as described above, the details are omitted here.
（乾燥時引張強さ）
縦方向および横方向の乾燥時引張強さは、ＪＩＳ Ｐ ８１１３の規定に準拠して測定した。
(Tensile strength when dry)
The tensile strength during drying in the machine direction and the transverse direction was measured in accordance with the provisions of JIS P8113.
（湿潤引張強さ）
縦方向および横方向の湿潤引張強さは、ＪＩＳ Ｐ ８１１３の規定に準拠して測定した。
(Wet tensile strength)
The wet tensile strength in the machine direction and the transverse direction were measured in accordance with the provisions of JIS P 8113.
（伸び率）
試料を５枚重ねて縦方向の幅が２５ｍｍとなるように裁断機を用いて裁断し、次いで、その試料を容量２０ｋｇのロードセル引張試験機（ミネベア株式会社製 ＴＧ−２００Ｎ）を用いてつかみ間隔１００±２ｍｍ、引張速度５０ｍｍ／ｍｉｎで試料が破断する長さを測定し、次式に従って計算した値である。表中の数値は、５回測定した際の平均値である。
伸び率（％）＝［破断時長さ（ｍｍ）−１００（ｍｍ）］÷１００（ｍｍ）
(Growth rate)
Five samples are stacked and cut using a cutting machine so that the vertical width is 25 mm, and then the sample is held using a load cell tensile tester (TG-200N manufactured by Minebea Co., Ltd.) with a capacity of 20 kg. It is a value calculated by measuring the length at which the sample breaks at 100 ± 2 mm and a tensile speed of 50 mm / min, and according to the following equation. The numerical values in the table are average values when measured five times.
Elongation rate (%) = [Length at break (mm) −100 (mm)] ÷ 100 (mm)
（ソフトネス）
ソフトネスは、ハンドルオメータ法（ＪＩＳ Ｌ １０９６ Ｅ法）により測定した。
(Softness)
The softness was measured by a handle ohmmeter method (JIS L 1096 E method).
（吸油量）
本発明の吸油量測定試験は次のように行う。先ず、１００ｍｍ×１００ｍｍの試験片を作成し、吸油前の重量を測定する。また、深さ２０ｍｍのところまでサラダオイルで満たしたバットを用意する。試験片を金網に載せた状態でバット内に浸漬し、試験片全体がサラダオイルに浸った時点で金網を油面から引き上げ、３０秒間放置して余剰サラダオイルを自然落下させる、その後、試験片の吸油後重量を測定し、吸油前後の重量変化（吸収したサラダオイルの重さ）を算出し、さらにこれを１ｍ2あたりに換算した値を吸油量とする。
(Oil absorption)
The oil absorption measurement test of the present invention is performed as follows. First, a test piece of 100 mm × 100 mm is prepared, and the weight before oil absorption is measured. Also, prepare a bat filled with salad oil up to a depth of 20 mm. Immerse the test piece in the vat with the test piece placed on the wire mesh. When the whole test piece is immersed in the salad oil, pull up the wire mesh from the oil level and let it stand for 30 seconds to allow the excess salad oil to fall naturally. The weight after oil absorption is measured, the change in weight before and after oil absorption (weight of absorbed salad oil) is calculated, and the value obtained by converting this per 1 m 2 is taken as the oil absorption amount.
（吸水量）
本発明の吸水量測定試験は次のように行う。先ず、１００ｍｍ×１００ｍｍの試験片を作成し、吸水前の重量を測定する。また、深さ２０ｍｍのところまで水で満たしたバットを用意する。試験片を金網に載せた状態でバット内に浸漬し、試験片全体が水に浸った時点で金網を水面から引き上げ、３０秒間放置して余剰水を自然落下させる、その後、試験片の吸水後重量を測定し、吸水前後の重量変化（吸収した水の重さ）を算出し、さらにこれを１ｍ2あたりに換算した値を吸水量とする。
(Water absorption)
The water absorption measurement test of the present invention is performed as follows. First, a 100 mm × 100 mm test piece is prepared, and the weight before water absorption is measured. In addition, a bat filled with water up to a depth of 20 mm is prepared. The test piece is immersed in the bat with the wire mesh placed, and when the entire test piece is immersed in water, the wire mesh is pulled up from the water surface and left for 30 seconds to allow the excess water to fall naturally. The weight is measured, the change in weight before and after water absorption (the weight of absorbed water) is calculated, and the value obtained by converting this per 1 m 2 is taken as the amount of water absorption.
（吸水性）
吸水性は、ＪＡＰＡＮ ＴＡＰＰＩ Ｎｏ．３２−２：２０００に基づいて測定した。すなわち、直径４０ｍｍ以上の孔を有する支持台に試験片（２枚重ね一組）を支持し、約１０ｍｍの高さから温度２０±１℃の蒸留水１滴（約１ｍＬ）をピペットで前記試験片に滴下する。そして、水滴が試験片に接触したときから、完全に吸収されて反射光が消えるまでの時間を、０．１秒単位で測定する。この試験を５回行い、その平均値を算出して吸水性の値とする。
(Water absorption)
The water absorption is measured by JAPAN TAPPI No. It measured based on 32-2: 2000. That is, a test piece (a set of two sheets) is supported on a support base having a hole having a diameter of 40 mm or more, and one drop (about 1 mL) of distilled water having a temperature of 20 ± 1 ° C. from a height of about 10 mm is pipetted. Drip on a piece. Then, the time from when the water droplet contacts the test piece until it is completely absorbed and the reflected light disappears is measured in units of 0.1 second. This test is performed 5 times, and the average value is calculated as the water absorption value.
（吸薬液性）
吸薬液性は、前記吸水性の測定方法において試験片に滴下する液体を蒸留水から消毒液（クウォーターメイト：日本全薬工業株式会社販売）に代えて測定した。
(Absorbent liquid)
The liquid absorbency was measured by replacing the liquid dropped on the test piece in the water absorption measurement method from distilled water with a disinfectant (Quarte Mate, sold by Nippon Zenyaku Kogyo Co., Ltd.).
（白色度）
白色度は、ＪＩＳ Ｐ ８１２３の規定に準拠して測定した。
(Whiteness)
The whiteness was measured in accordance with JIS P 8123.
（曲げ剛性Ｂ）
曲げ剛性Ｂ、および平均曲げヒステリシス幅２ＨＢは、純曲げ試験機（カトーテック社製「自動化純曲げ試験機 ＫＥＳＦＢ２−ＡＵＴＯ−Ａ」）を使用して測定した。なお曲げ剛性Ｂが大きいほど曲げ難く固い。Ｂ／Ｗは、曲げ剛性Ｂを坪量Ｗで除して算出した。
(Bending rigidity B)
The bending stiffness B and the average bending hysteresis width 2HB were measured using a pure bending tester (“Automated Pure Bending Tester KESFB2-AUTO-A” manufactured by Kato Tech Co., Ltd.). The higher the bending rigidity B, the harder it is to bend. B / W was calculated by dividing the bending stiffness B by the basis weight W.
（清拭性）
実際に酪農家５０名が所有する乳牛に対し、清拭性を試験した。まず、日本全薬工業株式会社が販売する消毒液「クウォーターメイト」を塗布し、実施例及び各比較例のシートで清拭し、その際の使用感を柔らかさ、ソフトさ、消毒液の吸収の速さ、乳房に残る消毒液の残存量の点に主に着目して５段階で判断した。段階５は清拭性にきわめて優れる、４は優れる、３は普通、２は清拭性に難がある、１は清拭性が悪いとした。表中の値は５０名の評価平均値である。
(Wiping properties)
The wiping performance was tested on dairy cows actually owned by 50 dairymen. First, apply the disinfectant “Quarte Mate” sold by Nippon Zenyaku Kogyo Co., Ltd., wipe with the sheets of Examples and Comparative Examples, softness, softness, and absorption of disinfectant Judgment was made in five steps, mainly focusing on the speed of the remaining amount of the disinfectant remaining in the breast. Stage 5 is excellent in wiping property, 4 is excellent, 3 is normal, 2 is difficult to wipe, and 1 is poor wiping property. The values in the table are the average evaluation values of 50 people.
（考察）
本発明に係る実施例のものは迅速かつ確実に清拭できるものであることが判る。また、清拭性の評価についても５０名評価平均で「４．８」であり、比較例１〜２と比較して高い数値となっている。これは、本発明の乳房清拭用ペーパーが、従来例に比較して極めて柔らかくソフトであるにもかかわらず迅速かつ確実な消毒液の吸収がなされるものであることを意味する。
(Discussion)
It turns out that the thing of the Example which concerns on this invention can be wiped quickly and reliably. Moreover, about evaluation of wiping property, it is "4.8" by 50 person evaluation average, and is a high numerical value compared with Comparative Examples 1-2. This means that the wiping paper of the present invention can absorb the disinfectant quickly and reliably despite being extremely soft and soft compared to the conventional example.
本発明は、例えば、乳牛以外の家畜の搾乳時のディッピング作業後に行う清拭作業に利用することもできる。また、ディッピング作業以外に行われる乳牛等の消毒作業時の清拭用にも利用することができる。 This invention can also be utilized for the wiping work performed after the dipping work at the time of milking of livestock other than a cow, for example. Moreover, it can utilize also for the wiping at the time of disinfection operations, such as dairy cows performed other than a dipping operation.
１，２…シート、１Ａ，２Ａ…凸部、２Ｂ…凹部、３…接着剤、Ｘ…エンボスセクション、Ｙ…抜き柄セクション。 1, 2 ... sheet, 1A, 2A ... convex part, 2B ... concave part, 3 ... adhesive, X ... embossed section, Y ... punched section.
Claims (5)
ＪＩＳ Ｐ ８１２４による坪量が１０〜４０ｇ／ｍ2のシートが２枚重ね状態で接合され、
ＪＩＳ Ｌ １０９６ Ｅ法によりソフトネスが、縦５．０〜１１．０ｇ、横３．０〜１０．０ｇ、
ＫＥＳ試験機による曲げ剛性Ｂが、縦０．０１０〜０．０４５ｇ・ｃｍ2／ｃｍ、横０．０１０〜０．０４５ｇ・ｃｍ2／ｃｍであり、かつ、
ＪＡＰＡＮ ＴＡＰＰＩ Ｎｏ．３２−２：２０００に基づいて測定される吸水性が０．１〜１．０秒である、ことを特徴とする乳牛の乳房清拭用ペーパー。 Pulp is the main raw material,
Two sheets having a basis weight of 10 to 40 g / m 2 according to JIS P 8124 are joined in a stacked state,
Softness is 5.0-11.0 g in length, 3.0-10.0 g in width, according to JIS L 1096 E method.
Flexural rigidity by KES tester B is vertical 0.010~0.045g · cm 2 / cm, the lateral 0.010~0.045g · cm 2 / cm, and,
JAPAN TAPPI No. A paper for wiping the dairy cow's breast, wherein the water absorption measured based on 32-2: 2000 is 0.1 to 1.0 seconds.
（ａ）一方のシートのエンボス凸部の天部と、他方のシートのエンボス凸部の天部とが接着剤により接着される、
（ｂ）一方のシートのエンボス凸部が他方のシートのエンボスの凹部内に嵌り込みかつその嵌り込み域において空間を残して嵌り込むように前記エンボス凸部の天部と前記エンボス凹部の底部とが接着剤により接着される、
請求項１〜４の何れか１項に記載の乳牛の乳房清拭用ペーパー。 The bonding mode between the sheets is the following (a) or (b):
(A) The top of the embossed convex portion of one sheet and the top of the embossed convex portion of the other sheet are bonded with an adhesive.
(B) The top of the embossed convex part and the bottom part of the embossed concave part so that the embossed convex part of one sheet is fitted into the concave part of the embossed part of the other sheet and the space is left in the fitting area. Is bonded by an adhesive,
The paper for the breast cleaning of the dairy cow of any one of Claims 1-4.