JP2007231287A - ゾルーゲルアルミナ砥粒及びビトレアス結合研摩材製品 - Google Patents
ゾルーゲルアルミナ砥粒及びビトレアス結合研摩材製品 Download PDFInfo
- Publication number
- JP2007231287A JP2007231287A JP2007101967A JP2007101967A JP2007231287A JP 2007231287 A JP2007231287 A JP 2007231287A JP 2007101967 A JP2007101967 A JP 2007101967A JP 2007101967 A JP2007101967 A JP 2007101967A JP 2007231287 A JP2007231287 A JP 2007231287A
- Authority
- JP
- Japan
- Prior art keywords
- abrasive
- alumina
- coated
- sol
- abrasive grains
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ゾルーゲルアルミナ砥粒において、アルミナ砥粒がセラミック酸化物で被覆され、そして2μm以下の粒径のアルファアルミナ結晶を含むように構成する。
【選択図】なし
Description
この例において、種結晶を入れられたゾルーゲルアルミナ砥粒、950℃の温度で完成されるビトレアス結合剤、ならびに細孔形成剤、潤滑剤および一時的バインダーを含む有機焼去材料、を含むビトレアス結合研磨剤物品の製造が述べられる。2組の試料が同一の配合で調製されたが、本発明により作製された砥石は硝酸コバルト溶液に浸漬された砥粒を含み、ついで本発明により被覆砥粒を与える。
商標「Cerpass−XTL」でSaint−Gobain Industrial Ceramics,Inc.により販売されている砥粒が次のすべての例においてゾルーゲルアルミナ砥粒として使用された。これは少なくとも98%のアルファアルミナを含み、ビッカース硬度約21GPaを有する、種結晶を入れられたゾルーゲルアルミナである。本発明による被覆された砥粒の試料を確保するために、54グリット径の砥粒試料1000gがHobartミキサーに入れられ、硝酸コバルトの溶液が添加された。溶液の量は酸化コバルトとして測定され0.25%の最終砥粒における硝酸コバルト含量を与えるように計算され、このために、添加されるのが必要な硝酸コバルト・6水和物の計算量は4.1gであった。これはpH2.0である水性溶液10gの形態で添加された。明らかなように、被覆するセラミック酸化物前駆体の量は、比較的小さな砥粒は被覆されるべき比較的大きい表面積を増すので、砥石粒径に依存する。たとえば36グリット粒径について、砥粒表面に同一含量の被覆を達成するために、セラミック酸化物前駆体の量は約15%減少されうるが、もしグリット粒径が80であれば、10%増加されるべきである。
グリット粒径36、54および80において、上述のように調製された被覆砥粒のBET表面積は、同一の未処理砥粒と比較された。すべてのグリット粒径において、被覆の結果、測定された表面積が40%までの著しい減少があった。結果は図1に示される。
被覆された砥粒と被覆されていない砥粒の比較試験は、被覆が硬度、静電放出性(electrostatic projectability)、もしくは元素拡散プロフィールに対して、ビトリファイド結合製品の砥粒/結合剤界面にわたって、不利な影響を与えることを示した。アルミナの結晶粒径は0.01〜0.02μmの小さな増加を示した。
次いで、上述のように調製された被覆砥粒はビトレアス結合試験棒の形成においてそのほかは同一である未被覆砥粒に対して比較された。使用された結合剤は約900℃の温度、10時間で完了する低温結合剤であった。被覆されていない砥粒は著しい数の黒点を示した。これらは図2に明瞭に示される。被覆されたものは黒点を何ら示さなかった。表面積の減少との相関は、黒点が砥粒の表面細孔において不完全燃焼された有機材料が集合する結果であるという結論を強く支持する。
この例において、同一の手順が例1に示されるように採用されたが、次の点は差異がある。すなわち、コバルト塩がベーマイトゾルに添加され、そして添加量は、アルミン酸コバルト酸およびアルファアルミナ前駆体を含む層の形態で、酸化コバルトとして測定され、例1に用いられる温度での焼成後にコバルトの質量の1.00%で、砥粒上の堆積をもたらすのに十分な量である。このように製造された砥粒はビトレアス結合研磨材製品を形成するのに要求される延長された焼成スケジュールの後でさえ色彩変化に非常に耐性があった。被覆形成の前後での砥粒表面積の測定は10%を超える表面積の減少を示した。
Claims (8)
- アルミナ砥粒がアルミナ砥粒の質量に基づいて1wt%までのセラミック酸化物で被覆され、そして粒径が2μm以下のアルファアルミナの結晶を含む、被覆されたゾルーゲルアルミナ砥粒。
- アルミナが結晶種を入れられたゾルーゲルアルミナである請求項1記載の被覆された砥粒。
- 被覆が、酸化マグネシウム;二酸化チタン;酸化コバルト;酸化ニッケル;酸化クロム;これらの酸化物の対応するアルミン酸塩;これらの酸化物およびアルミン酸塩の1つ以上とアルファアルミナ前駆体との混合物;ならびにそれらの混合物からなる群より選ばれる請求項1記載の被覆された砥粒。
- BET表面積が被覆されていない砥粒に比べて10〜40%小さい請求項1記載の被覆された砥粒。
- 被覆がアルミン酸コバルトを含む請求項1記載の被覆された砥粒。
- 存在する砥粒が請求項1記載の被覆された砥粒を含むビトレアス結合研摩材製品。
- 存在する砥粒が請求項3記載の被覆された砥粒を含むビトレアス結合研摩材製品。
- 存在する砥粒が請求項5記載の被覆された砥粒を含むビトレアス結合研摩材製品。