JP2007212870A - Method for making lithographic printing plate, and lithographic printing original plate - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a lithographic printing original plate which can be mildly developed at pH 2-10, generates no scum in a developer upon the development, and shows excellent printing durability when made into a lithographic printing plate. <P>SOLUTION: In a method for making a lithographic printing plate, such a lithographic printing original plate having a photosensitive layer containing at least one oil-soluble phthalocyanine compound and a hydrophobic binder polymer whose acid number is ≤0.3 meq/g and a protective layer on a support having a hydrophilic surface is exposed, and the protective layer and an unexposed portion of the photosensitive layer are removed in the presence of a developer of pH 2-10 using an automatic processing machine equipped with a rubbing member. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

  The present invention relates to a method for preparing a lithographic printing plate and a lithographic printing plate precursor used in the method.

In general, a lithographic printing plate has a surface composed of an oleophilic image portion and a hydrophilic non-image portion. In lithographic printing, dampening water and oil-based ink are alternately applied to the plate surface, and the hydrophilic non-image area is dampened with a dampening water receiving area (ink non-receiving area) by utilizing the property that water and oil repel each other. ), After the ink is received only in the oleophilic image area, the ink is transferred to a printing medium such as paper and printed.
In order to produce this lithographic printing plate, a lithographic printing plate precursor (PS plate) in which an oleophilic photosensitive layer (image recording layer) is provided on a hydrophilic support has been widely used. Usually, after exposing the lithographic printing plate precursor through an original image such as a lithographic film, the image recording layer to be an image portion is left, and the other unnecessary image recording layer is removed with an alkaline developer or an organic solvent. The lithographic printing plate is obtained by carrying out plate making by a method in which the surface of the hydrophilic support is exposed by dissolving and removing to form a non-image portion.

In the conventional plate making process of a lithographic printing plate precursor, a step of dissolving and removing unnecessary image recording layers with a developer or the like is necessary after exposure, but simplifies such additional wet processing. This is one of the issues. As one of simplification, it is desired that development can be performed with an aqueous solution close to neutrality or simple water.
In other words, disposal of waste liquid discharged with alkali development processing in recent years due to consideration for the global environment has become a major concern for the entire industry, and alkali (for example, potassium hydroxide) that is the main component of the developer is a major concern. Attention is focused on measures to reduce the burden of waste liquid disposal by development processing that does not rely on a strong alkaline developer having a pH of 10 or more (such as a mild development treatment with a solution of pH 2 to 10) containing a high concentration of such a substance (generally called a strong base). Gathered.

  On the other hand, in recent years, digitization technology that electronically processes, stores, and outputs image information using a computer has become widespread, and various new image output methods corresponding to such digitization technology have been put into practical use. It has come to be. Along with this, digitized image information is carried by high-convergence radiation such as laser light, and the lithographic printing plate precursor is scanned and exposed with that light, directly without using a lithographic film. Computer-to-plate technology for manufacturing is attracting attention. Accordingly, obtaining a lithographic printing plate precursor adapted to such a technique is one of the important technical issues.

  From the background as described above, it is now more strongly desired than ever to adapt both the simplification of the plate making operation and the digitization.

  On the other hand, for example, in Patent Document 1, in an image forming layer of a lithographic printing plate precursor having an image forming layer containing a hydrophobizing precursor, a hydrophilic resin, and a photothermal conversion agent on a hydrophilic support. In addition to the on-press development, it can also be used for printing after exposure by liquid development using water or a suitable aqueous solution as a developer by further containing a compound having an ethylene oxide chain. Has been.

Patent Document 2 contains (i) a hydrophilic support, and (ii) a radical polymerizable ethylenically unsaturated monomer, a radical polymerization initiator and an infrared absorbing dye, and is cured by infrared laser exposure. Moreover, a lithographic printing plate precursor comprising an oleophilic heat-sensitive layer containing 60% by mass or more of water and developable with an aqueous developer having a pH of 2.0 to 10.0 is prepared and exposed imagewise with an infrared laser. A processing method for a lithographic printing plate precursor comprising removing an uncured region of the heat-sensitive layer with an aqueous developer is described.
JP 2002-365789 A US Patent Application Publication No. 2004/0013968

In order to facilitate plate inspection of a lithographic printing plate, it is common to include a plate inspection agent (colorant, dye or pigment) in the photopolymerization layer of the lithographic printing plate precursor. As a plate inspection agent contained in a photopolymerization layer (hereinafter also referred to as photosensitive layer) of a photopolymerization type lithographic printing plate precursor, it exhibits a blue color suitable for plate inspection and absorbs laser light used for image exposure for photopolymerization. Phthalocyanine pigments are used because they have the advantage of not. In order to increase the dispersibility of the phthalocyanine, it is common to coat a polymer or to substitute an acid group, a base, or the like on the pigment surface. However, the lithographic printing plate precursor using the phthalocyanine pigment as described above, when processed with a developer after image exposure, scum is generated in the developer and the developer becomes unstable, or the lithographic printing plate is made. There was a drawback that the printing durability of the plate deteriorated.
The present invention overcomes the above-mentioned drawbacks of the prior art and enables mild development processing at pH 2 to 10 or aqueous solution processing containing a water-soluble polymer, and the development processing may cause residue in the developer. In addition, an object of the present invention is to provide a lithographic printing plate precursor exhibiting excellent printing durability when used as a lithographic printing plate.

  As a result of diligent research, the present inventor was able to achieve the above object by using an oil-soluble phthalocyanine compound as a plate inspection agent contained in the photosensitive layer. That is, the present invention is as follows.

1. A lithographic printing plate precursor having a photosensitive layer containing at least one oil-soluble phthalocyanine compound, a hydrophobic binder polymer having an acid value of 0.3 meq / g or less, and a protective layer on a support having a hydrophilic surface After the exposure, the protective layer and the photosensitive layer in the non-exposed area are removed in the presence of a developer having a pH of 2 to 10 by an automatic processor equipped with a rubbing member. Method.
2. 2. The method of preparing a lithographic printing plate as described in 1 above, wherein a part or all of the photosensitive layer component is contained in a microcapsule or a microgel.
3. 3. The method for preparing a lithographic printing plate as described in 1 or 2 above, wherein the photosensitive layer further contains a chain transfer agent.
4). The method for producing a lithographic printing plate as described in any one of 1 to 3, wherein the chain transfer agent is a thiol compound represented by the following general formula (I).

  In general formula (I), R represents an alkyl group which may have a substituent or an aryl group which may have a substituent, and A represents a 5-membered ring having a carbon atom together with an N = CN moiety. Alternatively, it represents an atomic group that forms a 6-membered heterocycle, and A may further have a substituent.

5). The method for preparing a lithographic printing plate as described in any one of 1 to 4 above, wherein the pH of the developer is from 3 to 8.
6). The method for preparing a lithographic printing plate as described in any one of 1 to 5 above, wherein the developer contains a water-soluble polymer.
7). The method for preparing a lithographic printing plate as described in any one of 1 to 6 above, wherein the lithographic printing plate precursor has an undercoat layer containing a polymer compound having a polymerizable group.
8). A lithographic printing plate precursor having a photosensitive layer containing at least one oil-soluble phthalocyanine compound and a hydrophobic binder polymer having an acid value of 0.3 meq / g or less and a protective layer on a support having a hydrophilic surface. After the laser exposure at a wavelength of 350 to 450 nm, the plate surface is rubbed with a rubbing member in the presence of a developer having a pH of 2 to 10 by an automatic processor equipped with a rubbing member, thereby exposing the protective layer and the non-exposed portion. A lithographic printing plate precursor, wherein the layer can be removed.

When a conventional photopolymerization type lithographic printing plate precursor is processed with a developer after image exposure, the developer becomes unstable due to generation of debris in the developer, and the printing life of the lithographic printing plate that has been made The phthalocyanine pigment was used as the plate inspection agent contained in the photosensitive layer, and this caused a large filler structure to inhibit film crosslinking / polymerization. It is considered that the fountain solution or the like is likely to permeate into the image part or the interface between the image part and the support during the printing of the lithographic printing plate made as a solid matter. On the other hand, since the oil-soluble phthalocyanine compound contained in the photosensitive layer of the lithographic printing plate precursor according to the present invention is not in the form of a pigment, it is suppressed from being precipitated as a solid in the developer, and the film cross-linking / Deterioration of printing durability of lithographic printing plate because polymerization is not hindered and dampening water does not easily penetrate into the image area of the lithographic printing plate and the interface between the image area and the support during printing. It seems that nothing has gone away.
In addition, when the phthalocyanine compound contained in the photosensitive layer is simply in the form of a dye, as in the case of using the pigment form of phthalocyanine, it is deposited as a solid in the developing solution in the development process and generates residue. The oil-soluble phthalocyanine compound of the present invention does not generate residue. This is because phthalocyanine is once dissolved in a developer in a simple dye form, but is usually easily crystallized into a pigment, whereas an oil-soluble phthalocyanine compound is in a stable emulsified state in a developer. As a result, it is considered that no solid precipitates in the developer.

  According to the present invention, mild development processing at pH 2 to 10 is possible, and no debris is generated in the developer by the development processing, and excellent printing durability is obtained when a lithographic printing plate is used. A lithographic printing plate precursor can be provided.

  Hereinafter, the lithographic printing plate precursor used in the lithographic printing plate preparation method of the present invention will be described, and then the lithographic printing plate preparation method will be described.

[Lithographic printing plate precursor]
(Photosensitive layer)
The photosensitive layer of the lithographic printing plate precursor according to the invention contains an oil-soluble phthalocyanine compound and a hydrophobic binder polymer having an acid value of 0.3 meq / g or less as essential components. Furthermore, the photosensitive layer of the present invention preferably contains a sensitizing dye, a polymerization initiator, a polymerizable compound and a chain transfer agent that constitute the photopolymerizable composition.
Below, the oil-soluble phthalocyanine compound, which is the most characteristic component of the present invention, will be described first, and then the other components contained in the photosensitive layer will be described sequentially.

<Oil-soluble phthalocyanine compound>
The phthalocyanine compound contained in the photosensitive layer of the lithographic printing plate precursor according to the present invention is oil-soluble, monomolecular form, non-pigment form, retains the fastness (light resistance, heat resistance) of phthalocyanine itself, and It is not particularly limited as long as it has low absorption at 488 nm and 532 nm which are transmission wavelengths of Ar laser and FDYAG laser suitable for photopolymerization reaction. In addition, said oil solubility shows that it is soluble in organic solvents, such as a ketone, toluene, and Cellsolve.

  Specifically, the oil-soluble phthalocyanine compound means that the amount dissolved in methyl ethyl ketone is 0.1% by mass or more. Such an oil-soluble phthalocyanine compound can be obtained by adding an organic group to a phthalocyanine molecule. Examples of the organic group that can be given in this case include an alkyl group, an alkenyl group, an aromatic ring group, an aralkyl group, a heterocyclic group, and the like, and preferably a long-chain alkyl group, a fluoroalkyl group, a fluoroaryl group, A thiophen-2-yl group, for example, a dodecyl group, a stearyl group, a t-octyl group, a trifluoromethyl group, a pentafluoroethyl group, a pentafluorophenyl group, or the like; Also preferred are those in which carbon atoms in the main chain are substituted with oxygen, sulfur, nitrogen, silicon or the like, such as a polyoxyethylene group. Examples of the oil-soluble phthalocyanine compound as described above include those described in European Patent Publication No. 636644, eXcolor IR-1, IR-2, IR-3, IR-4, manufactured by Nippon Shokubai Co., Ltd. VS-4 etc. are mentioned. The content of the oil-soluble phthalocyanine compound in the photosensitive layer is not particularly limited, but is preferably 0.1 to 1% by mass, more preferably 0.01 to 0.5% by mass, and still more preferably, It is 0.03-0.3 mass%.

<Sensitizing dye>
The photosensitive layer of the present invention can contain a sensitizing dye having absorption corresponding to the wavelength of the exposure light source.
The sensitizing dye used in the present invention is preferably a sensitizing dye having an absorption maximum λ _max at 350 nm to 450 nm and having an oxidation potential in a specific excitation active state.

Examples of preferable sensitizing dyes in the present invention include those belonging to the following compounds and having a maximum absorption λ _max in the wavelength region of 350 to 450 nm.
Polynuclear aromatics (eg, pyrene, perylene, triphenylene), xanthenes (eg, fluorescein, eosin, erythrosine, rhodamine B, rose bengal), cyanines (eg, thiacarbocyanine, oxacarbocyanine), merocyanines ( For example, merocyanine, carbomerocyanine), thiazines (eg, thionine, methylene blue, toluidine blue), acridines (eg, acridine orange, chloroflavin, acriflavine), anthraquinones (eg, anthraquinone), squalium (eg, squalium) ).

  More preferable examples of the sensitizing dye include compounds represented by the following general formulas (II) to (V).

(In the general formula (II), A ₁ represents a sulfur atom or NR ₆ , R ₆ represents an alkyl group or an aryl group, L ₂ represents a basic nucleus of the dye in combination with the adjacent A ₂ and the adjacent carbon atom. R ₇ and R ₈ each independently represent a hydrogen atom or a monovalent nonmetallic atomic group, and R ₇ and R ₈ are bonded to each other to form an acidic nucleus of the dye. W represents an oxygen atom or a sulfur atom.)

  Preferred specific examples of the compound represented by the general formula (II) are shown below.

(In the general formula (III), A ₂ represents a sulfur atom or NR ₁₅ , L ₄ represents a nonmetallic atomic group that forms a basic nucleus of the dye in combination with adjacent A ₂ and a carbon atom, R ₉ , R ₁₀ , R ₁₁ , R ₁₂ , R ₁₃ and R ₁₄ each independently represents a monovalent nonmetallic atomic group, and R ₁₅ represents an alkyl group or an aryl group.)

  Preferable examples of the compound represented by the general formula (III) include the following.

(In general formula (IV), A ₃ and A ₄ each independently represent —S— or —NR ₁₈ or —NR ₁₉ , and R ₁₈ and R ₁₉ each independently represent a substituted or unsubstituted alkyl group, substituted or non-substituted Represents a substituted aryl group, and L ₅ and L ₆ each independently represents a nonmetallic atomic group that forms a basic nucleus of a dye in combination with adjacent A ₃ , A ₄ and adjacent carbon atoms, R ₁₆ , Each R ₁₇ is independently a monovalent nonmetallic atomic group or can be bonded to each other to form an aliphatic or aromatic ring.

  Preferable examples of the compound represented by the general formula (IV) include the following.

(In the general formula (V), R ₂₃ represents an aromatic ring or a hetero ring which may have a substituent, and A ₅ represents an oxygen atom, a sulfur atom or —NR ₂₄ —. R ₂₁ , R ₂₂ and R ₂₄ each independently represents a hydrogen atom or a monovalent nonmetallic atomic group, and R ₂₄ and R ₂₁ , and R ₂₂ and R ₂₄ are bonded together to form an aliphatic or aromatic ring, respectively. Can do.)

  Preferable specific examples of the compound represented by the general formula (V) include those shown below.

  Regarding the sensitizing dye in the present invention, when a lithographic printing plate precursor is used, various chemical modifications for improving the characteristics of the photosensitive layer can be performed. For example, by combining a sensitizing dye and an addition polymerizable compound structure (for example, an acryloyl group or a methacryloyl group) by a method such as a covalent bond, an ionic bond, or a hydrogen bond, the exposure film can be increased in strength or exposed. Unnecessary precipitation suppression of the dye from the subsequent film can be performed.

  Furthermore, when a lithographic printing plate precursor is prepared using the photosensitive composition of the present invention, a hydrophilic site (acid group or polar group such as an ethylene oxide group) is used for the purpose of enhancing the processing suitability to an aqueous developer. Is effective. In addition, for example, a substituent can be appropriately introduced in order to improve the compatibility in the photosensitive layer and to suppress crystal precipitation. For example, in certain types of photosensitive systems, unsaturated bonds such as aryl groups and allyl groups may be very effective in improving compatibility. By introducing an obstacle, crystal precipitation can be remarkably suppressed. In addition, by introducing a phosphonic acid group, an epoxy group, a trialkoxysilyl group, or the like, adhesion to an inorganic substance such as a metal or a metal oxide can be improved. In addition, a method such as polymerization of a sensitizing dye can be used depending on the purpose.

Details of the usage such as which structure of these sensitizing dyes are used, whether they are used alone or in combination of two or more, and how much is added, can be appropriately set according to the performance design of the final photosensitive material. .
For example, the compatibility with the photosensitive composition layer can be enhanced by using two or more sensitizing dyes in combination. In selecting the sensitizing dye, in addition to the photosensitivity, the molar extinction coefficient at the emission wavelength of the light source used is an important factor. By using a dye having a large molar extinction coefficient, the amount of the dye added can be made relatively small, which is economical and advantageous when used for a lithographic printing plate precursor in terms of film physical properties of the photosensitive layer. is there. The photosensitivity of the photosensitive layer, the resolution, and the physical properties of the exposed film are greatly affected by the absorbance at the light source wavelength. Therefore, the addition amount of the sensitizing dye is appropriately selected in consideration of these factors.

  However, for example, for the purpose of curing a thick film having a thickness of 5 μm or more, the degree of curing may be increased by lower absorbance. When used as a lithographic printing plate used in a relatively thin film thickness, the addition amount of the sensitizing dye is such that the absorbance of the photosensitive layer of the present invention is in the range of 0.1 to 1.5, preferably 0.25 to 1. It is preferable to set so as to be in the range. Usually, the amount is preferably 0.05 to 30 parts by mass, more preferably 0.1 to 20 parts by mass, and most preferably 0.2 to 10 parts by mass with respect to 100 parts by mass of the total solid content of the photosensitive layer.

In addition, it is estimated that the sensitizing dye used in the present invention improves the efficiency of electron transfer to the initiator when the oxidation potential and the oxidation potential in the excited state are negatively large, resulting in higher sensitivity. For this reason, the oxidation potential of the specific excited state of the sensitizing dye used in the present invention (for convenience, expressed as E _ox ^* ) is more negative than −1.6, preferably more negative than −1.7. large. Furthermore, E _ox ^* is desirably −1.9 to −2.3, more preferably −2.1 to −2.3.

<Polymerization initiator>
Examples of the polymerization initiator used in the present invention include trihalomethyl compounds, carbonyl compounds, organic peroxides, azo compounds, azide compounds, metallocene compounds, hexaarylbiimidazole compounds, organic boron compounds, disulfone compounds, oxime ester compounds. And onium salt compounds. Among these, at least one selected from the group consisting of hexaarylbiimidazole compounds, onium salts, trihalomethyl compounds, and metallocene compounds is preferable, and hexaarylbiimidazole compounds are particularly preferable. Two or more of the above polymerization initiators can be used in combination as appropriate.

  Examples of the hexaarylbiimidazole polymerization initiator include lophine dimers described in JP-B Nos. 45-37377 and 44-86516, such as 2,2′-bis (o-chlorophenyl) -4,4 ′, 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-bromophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (o, p-dichlorophenyl) ) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-chlorophenyl) -4,4', 5,5'-tetra (m-methoxyphenyl) biimidazole, 2 , 2'-bis (o, o'-dichlorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-nitrophenyl) -4,4', 5,5 ′ − Traphenylbiimidazole, 2,2'-bis (o-methylphenyl) -4,4 ', 5,5'-tetraphenylbiimidazole, 2,2'-bis (o-trifluorophenyl) -4,4 ', 5,5'-tetraphenylbiimidazole and the like.

  The trihalomethyl compound is preferably trihalomethyl-s-triazine, 2,4,6-tris (trichloromethyl) -s-triazine, 2-methoxy-4,6-bis (trichloromethyl) -s-triazine, 2- Trimethyl compounds described in JP-A-58-29803 such as amino-4,6-bis (trichloromethyl) -s-triazine, 2- (P-methoxystyryl) -4,6-bis (trichloromethyl) -s-triazine and the like. Examples thereof include s-triazine derivatives having a halogen-substituted methyl group.

  Examples of the onium salt include onium salts represented by the following general formula (VI).

In general formula (VI), R ¹¹ , R ¹² and R ¹³ may be the same or different and each represents a hydrocarbon group having 20 or less carbon atoms which may have a substituent. Preferable substituents include a halogen atom, a nitro group, an alkyl group having 12 or less carbon atoms, an alkoxy group having 12 or less carbon atoms, or an aryloxy group having 12 or less carbon atoms.
Z ⁻ represents a counter ion selected from the group consisting of halogen ion, perchlorate ion, tetrafluoroborate ion, hexafluorophosphate ion, carboxylate ion, and sulfonate ion, preferably perchlorate ion, hexa Fluorophosphate ions, carboxylate ions, and aryl sulfonate ions.

As the titanocene compound, for example, known compounds described in JP-A Nos. 59-152396 and 61-151197 can be appropriately selected and used.
Specifically, di-cyclopentadienyl-Ti-di-chloride, di-cyclopentadienyl-Ti-bis-phenyl, di-cyclopentadienyl-Ti-bis-2,3,4,5, 6-pentafluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,3,5,6-tetrafluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2, 4,6-trifluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,6-difluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,4-difluoro Phen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,3,4,5,6-pentafluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2, 3, 5, 6 Tetrafluorophen-1-yl, di-methylcyclopentadienyl-Ti-bis-2,4-difluorophen-1-yl, bis (cyclopentadienyl) -bis [2,6-difluoro-3- ( Pyr-1-yl) phenyl] titanium and the like.

  Examples of the carbonyl compound include benzophenone, Michler ketone, 2-methylbenzophenone, 3-methylbenzophenone, 4-methylbenzophenone, 2-chlorobenzophenone, 4-bromobenzophenone, 2-carboxybenzophenone and other benzophenone derivatives, 2,2-dimethoxy- 2-phenylacetophenone, 2,2-diethoxyacetophenone, 1-hydroxycyclohexyl phenyl ketone, α-hydroxy-2-methylphenylpropanone, 1-hydroxy-1-methylethyl- (p-isopropylphenyl) ketone, 1- Hydroxy-1- (p-dodecylphenyl) ketone, 2-methyl- (4 ′-(methylthio) phenyl) -2-morpholino-1-propanone, 1,1,1-trichloromethyl- (p-butylphenyl) Acetophenone derivatives such as ketones, thioxanthone derivatives such as thioxanthone, 2-ethylthioxanthone, 2-isopropylthioxanthone, 2-chlorothioxanthone, 2,4-dimethylthioxanthone, 2,4-diethylthioxanthone, 2,4-diisopropylthioxanthone, p- Examples thereof include benzoic acid ester derivatives such as ethyl dimethylaminobenzoate and ethyl p-diethylaminobenzoate.

Examples of the oxime ester compound include compounds described in JCS Perkin II (1979) 1653-1660), JCSPerkin II (1979) 156-162, Journal of Photopolymer Science and Technology (1995) 202-232, and JP-A 2000-66385. And compounds described in JP-A No. 2000-80068.

The polymerization initiator in the present invention is suitably used alone or in combination of two or more.
The amount of the polymerization initiator used in the photosensitive layer in the present invention is preferably 0.01 to 20% by mass, more preferably 0.1 to 15% by mass, based on the total solid content of the photosensitive layer. More preferably, it is 1.0 mass%-10 mass%.

<Chain transfer agent>
The photosensitive layer of the present invention preferably contains a chain transfer agent. Chain transfer agents contribute to improved sensitivity and storage stability. As the compound that acts as a chain transfer agent, for example, a compound group having SH, PH, SiH, GeH in the molecule is used. These can donate hydrogen to low-activity radical species to generate radicals, or can be oxidized and then deprotonated to generate radicals.

In the photosensitive layer of the present invention, in particular, a thiol compound (for example, 2-mercaptobenzimidazoles) can be preferably used as a chain transfer agent.
Especially, the thiol compound represented by the following general formula (I) is used especially suitably. By using this thiol compound as a chain transfer agent, the problem of odor and sensitivity reduction due to evaporation from the photosensitive layer and diffusion to other layers are avoided, and it has excellent storage stability and high sensitivity and high printing durability. A lithographic printing plate precursor is obtained.

  In general formula (I), R represents an alkyl group which may have a substituent or an aryl group which may have a substituent, and A represents a 5-membered ring having a carbon atom together with an N = CN moiety. Alternatively, it represents an atomic group that forms a 6-membered heterocycle, and A may further have a substituent.

  More preferably, those represented by the following general formula (I-1) or general formula (I-2) are used.

  In general formula (I-1) and formula (I-2), R represents an alkyl group which may have a substituent, or an aryl group which may have a substituent, and X represents a halogen atom or an alkoxyl group. Represents an alkyl group which may have a substituent, or an aryl group which may have a substituent.

  Specific examples of the compound represented by formula (I) are shown below, but the present invention is not limited to these.

  The amount of these chain transfer agents (thiol compounds) used is preferably 0.01 to 20% by mass, more preferably 0.1 to 15% by mass, based on the total solid content of the photosensitive layer. More preferably, it is 1.0-10 mass%.

<Polymerizable compound>
The polymerizable compound used in the photosensitive layer in the present invention is an addition polymerizable compound having at least one ethylenically unsaturated double bond, and is a compound having at least one terminal ethylenically unsaturated bond, preferably two or more. To be elected. Such a compound group is widely known in the industrial field, and can be used without any particular limitation in the present invention. These have chemical forms such as monomers, prepolymers, i.e. dimers, trimers and oligomers, or mixtures thereof and copolymers thereof. Examples of monomers and copolymers thereof include unsaturated carboxylic acids (for example, acrylic acid, methacrylic acid, itaconic acid, crotonic acid, isocrotonic acid, maleic acid, etc.), and esters and amides thereof. In this case, an ester of an unsaturated carboxylic acid and an aliphatic polyhydric alcohol compound, or an amide of an unsaturated carboxylic acid and an aliphatic polyvalent amine compound is used. In addition, an addition reaction product of an unsaturated carboxylic acid ester or amide having a nucleophilic substituent such as a hydroxyl group, amino group or mercapto group with a monofunctional or polyfunctional isocyanate or epoxy, and a monofunctional or polyfunctional compound. A dehydration condensation reaction product with a functional carboxylic acid is also preferably used. Further, an addition reaction product of an unsaturated carboxylic acid ester or amide having an electrophilic substituent such as an epoxy group or an epoxy group with a monofunctional or polyfunctional alcohol, amine or thiol, a halogen group or Also suitable are substitution reaction products of unsaturated carboxylic acid esters or amides having a leaving substituent such as a tosyloxy group with monofunctional or polyfunctional alcohols, amines or thiols. As another example, it is also possible to use a group of compounds substituted with unsaturated phosphonic acid, styrene, vinyl ether or the like instead of the unsaturated carboxylic acid.

  Specific examples of the monomer of an ester of an aliphatic polyhydric alcohol compound and an unsaturated carboxylic acid include acrylic acid esters such as ethylene glycol diacrylate, triethylene glycol diacrylate, 1,3-butanediol diacrylate, and tetramethylene glycol. Diacrylate, propylene glycol diacrylate, neopentyl glycol diacrylate, trimethylolpropane triacrylate, trimethylolpropane tri (acryloyloxypropyl) ether, trimethylolethane triacrylate, hexanediol diacrylate, 1,4-cyclohexanediol diacrylate , Tetraethylene glycol diacrylate, pentaerythritol diacrylate, pentaerythritol triacrylate , Pentaerythritol tetraacrylate, dipentaerythritol diacrylate, dipentaerythritol hexaacrylate, sorbitol triacrylate, sorbitol tetraacrylate, sorbitol pentaacrylate, sorbitol hexaacrylate, tri (acryloyloxyethyl) isocyanurate, isocyanuric acid ethylene oxide (EO) Examples include modified triacrylates and polyester acrylate oligomers.

  Methacrylic acid esters include tetramethylene glycol dimethacrylate, triethylene glycol dimethacrylate, neopentyl glycol dimethacrylate, trimethylolpropane trimethacrylate, trimethylolethane trimethacrylate, ethylene glycol dimethacrylate, 1,3-butanediol dimethacrylate, Hexanediol dimethacrylate, pentaerythritol dimethacrylate, pentaerythritol trimethacrylate, pentaerythritol tetramethacrylate, dipentaerythritol dimethacrylate, dipentaerythritol hexamethacrylate, sorbitol trimethacrylate, sorbitol tetramethacrylate, bis [p- (3-methacryloxy- 2-hydroxypro ) Phenyl] dimethyl methane, bis - [p- (methacryloxyethoxy) phenyl] dimethyl methane.

Itaconic acid esters include ethylene glycol diitaconate, propylene glycol diitaconate, 1,3-butanediol diitaconate, 1,4-butanediol diitaconate, tetramethylene glycol diitaconate, pentaerythritol diitaconate And sorbitol tetritaconate. Examples of crotonic acid esters include ethylene glycol dicrotonate, tetramethylene glycol dicrotonate, pentaerythritol dicrotonate, and sorbitol tetradicrotonate. Examples of isocrotonic acid esters include ethylene glycol diisocrotonate, pentaerythritol diisocrotonate, and sorbitol tetraisocrotonate. Examples of maleic acid esters include ethylene glycol dimaleate, triethylene glycol dimaleate, pentaerythritol dimaleate, and sorbitol tetramaleate.

  Examples of other esters include aliphatic alcohol esters described in JP-B-51-47334 and JP-A-57-196231, JP-A-59-5240, JP-A-59- Those having an aromatic skeleton described in JP-A No. 5241 and JP-A-2-226149 and those containing an amino group described in JP-A-1-165613 are also preferably used. Furthermore, the ester monomers described above can also be used as a mixture.

  Specific examples of amide monomers of aliphatic polyvalent amine compounds and unsaturated carboxylic acids include methylene bis-acrylamide, methylene bis-methacrylamide, 1,6-hexamethylene bis-acrylamide, 1,6-hexamethylene bis. -Methacrylamide, diethylenetriamine trisacrylamide, xylylene bisacrylamide, xylylene bismethacrylamide and the like. Examples of other preferable amide monomers include those having a cyclohexylene structure described in JP-B No. 54-21726.

  Further, urethane-based addition polymerizable compounds produced by using an addition reaction of isocyanate and hydroxyl group are also suitable. Specific examples thereof include, for example, one molecule described in JP-B-48-41708. A vinylurethane compound containing two or more polymerizable vinyl groups in one molecule obtained by adding a vinyl monomer containing a hydroxyl group represented by the following general formula (A) to a polyisocyanate compound having two or more isocyanate groups Etc.

_{CH 2 = C (R 4)} COOCH 2 CH (R 5) OH (A)
(However, R ₄ and R ₅ represent H or CH _3. )

  Also, urethane acrylates such as those described in JP-A-51-37193, JP-B-2-32293, JP-B-2-16765, JP-B-58-49860, JP-B-56- Urethane compounds having an ethylene oxide skeleton described in Japanese Patent No. 17654, Japanese Patent Publication No. 62-39417, and Japanese Patent Publication No. 62-39418 are also suitable. Furthermore, addition polymerizable compounds having an amino structure or a sulfide structure in the molecule described in JP-A-63-277653, JP-A-63-260909, and JP-A-1-105238 are used. Depending on the case, it is possible to obtain a photopolymerizable composition excellent in the photosensitive speed.

Other examples include polyester acrylates, epoxy resins and (meth) acrylic acid as described in JP-A-48-64183, JP-B-49-43191, JP-B-52-30490, and JP-B-52-30490. Mention may be made of polyfunctional acrylates and methacrylates such as reacted epoxy acrylates. In addition, specific unsaturated compounds described in JP-B-46-43946, JP-B-1-40337, JP-B-1-40336, and vinylphosphonic acid-based compounds described in JP-A-2-25493 are also included. Can be mentioned. In some cases, a structure containing a perfluoroalkyl group described in JP-A-61-22048 is preferably used. Furthermore, Journal of Japan Adhesion Association vol. 20, no. 7, pages 300 to 308 (1984) as photocurable monomers and oligomers can also be used.

About these polymerizable compounds, the details of usage such as the structure, single use or combination, addition amount, etc. can be arbitrarily set according to the performance design of the final lithographic printing plate precursor. For example, it is selected from the following viewpoints.
From the viewpoint of sensitivity, a structure having a large unsaturated group content per molecule is preferable, and in many cases, a bifunctional or higher functionality is preferable. Further, in order to increase the strength of the image area, that is, the cured film, those having three or more functionalities are preferable. Further, different functional numbers and different polymerizable groups (for example, acrylic acid ester, methacrylic acid ester, styrenic compound, vinyl ether type). A method of adjusting both sensitivity and strength by using a compound) is also effective.
In addition, the compatibility and dispersibility with other components in the photosensitive layer (for example, binder polymer, polymerization initiator, colorant, etc.), the selection and use method of the polymerizable compound is an important factor. In some cases, the compatibility can be improved by using a low-purity compound or by using two or more kinds in combination. In addition, a specific structure may be selected for the purpose of improving adhesion to a support or a protective layer described later.

  The polymerizable compound is preferably used in the range of 5 to 80% by mass, more preferably 25 to 75% by mass, based on the total solid content of the photosensitive layer. These may be used alone or in combination of two or more. In addition, the usage of the polymerizable compound can be arbitrarily selected from the viewpoint of polymerization inhibition with respect to oxygen, resolution, fogging, refractive index change, surface adhesiveness, etc. The layer construction and coating method such as undercoating and overcoating can also be carried out.

<Hydrophobic binder polymer>
As the hydrophobic binder polymer that can be used in the photosensitive layer of the present invention, a water-insoluble polymer is preferably used. Furthermore, the hydrophobic binder polymer that can be used in the present invention preferably does not substantially contain an acid group such as a carboxyl group, a sulfone group, or a phosphate group. The acid value of the binder polymer (the acid content per gram of the polymer expressed as the number of chemical equivalents) is 0.3 meq / g or less, and more preferably 0.1 meq / g or less.

  That is, the hydrophobic binder polymer that can be used in the present invention is preferably insoluble in water and an aqueous solution of pH 10 or higher, and the solubility of the hydrophobic binder polymer in water and an aqueous solution of pH 10 or higher (polymer concentration at the time of saturated dissolution). However, it is preferable that it is 0.5 mass% or less, More preferably, it is 0.1 mass% or less. By using such a hydrophobic binder polymer, the film strength, water resistance, and inking property of the photosensitive layer are improved, and printing durability is improved. The solubility measuring temperature is a temperature during plate-making development, and is 25 ° C. here.

As the hydrophobic binder polymer, as long as the performance of the lithographic printing plate of the present invention is not impaired, a conventionally known one can be used without limitation within the above range, and a linear organic polymer having a film property is preferable.
As an example of such a hydrophobic binder polymer, a polymer selected from acrylic resin, polyvinyl acetal resin, polyurethane resin, polyamide resin, epoxy resin, methacrylic resin, styrene resin, and polyester resin is preferable. Especially, an acrylic resin is preferable and a (meth) acrylic acid ester copolymer is preferable. More specifically, an alkyl (meth) acrylate or an aralkyl ester and an ester residue (—COOR) of (meth) acrylate ester may have —CH ₂ CH ₂ O— unit or —CH ₂ CH ₂ NH— unit as R. A copolymer with a (meth) acrylic acid ester containing is particularly preferred. The preferable alkyl group of the (meth) acrylic acid alkyl ester is an alkyl group having 1 to 5 carbon atoms, and a methyl group is more preferable. Preferable (meth) acrylic acid aralkyl esters include benzyl (meth) acrylate.

Furthermore, the hydrophobic binder polymer can be provided with a crosslinking property in order to improve the film strength of the image area.
In order to impart crosslinkability to the hydrophobic binder polymer, a crosslinkable functional group such as an ethylenically unsaturated bond may be introduced into the main chain or side chain of the polymer. The crosslinkable functional group may be introduced by copolymerization or may be introduced by a polymer reaction.

  Here, the crosslinkable group is a group that crosslinks the polymer binder in the process of radical polymerization reaction that occurs in the photosensitive layer when the lithographic printing plate precursor is exposed. Although it will not specifically limit if it is a group of such a function, For example, an ethylenically unsaturated bond group, an amino group, an epoxy group etc. are mentioned as a functional group which can be addition-polymerized. Moreover, the functional group which can become a radical by light irradiation may be sufficient, and as such a crosslinkable group, a thiol group, a halogen group, an onium salt structure etc. are mentioned, for example. Especially, an ethylenically unsaturated bond group is preferable and the functional group represented by the following general formula (1)-(3) is especially preferable.

In the general formula (1), R ^{1 to} R ³ each independently represents a monovalent organic group, but R ¹
As preferable examples, a hydrogen atom or an alkyl group which may have a substituent may be mentioned. Among them, a hydrogen atom or a methyl group is preferable because of high radical reactivity. R ² and R ³ are each independently a hydrogen atom, a halogen atom, an amino group, a carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, an optionally substituted alkyl group, or a substituted group. An aryl group that may have a group, an alkoxy group that may have a substituent, an aryloxy group that may have a substituent, an alkylamino group that may have a substituent, and a substituent An arylamino group which may have a substituent, an alkylsulfonyl group which may have a substituent, an arylsulfonyl group which may have a substituent, and the like. Among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, a substituent An alkyl group which may have a substituent and an aryl group which may have a substituent are preferable because of high radical reactivity.

X represents an oxygen atom, a sulfur atom, or N (R ¹² ) —, and R ¹² represents a hydrogen atom or a monovalent organic group. Here, examples of R ¹² include an alkyl group which may have a substituent. Among them, a hydrogen atom, a methyl group, an ethyl group, and an isopropyl group are preferable because of high radical reactivity.

  Here, examples of the substituent that can be introduced include an alkyl group, an alkenyl group, an alkynyl group, an aryl group, an alkoxy group, an aryloxy group, a halogen atom, an amino group, an alkylamino group, an arylamino group, a carboxyl group, an alkoxycarbonyl group, A sulfo group, a nitro group, a cyano group, an amide group, an alkylsulfonyl group, an arylsulfonyl group and the like can be mentioned.

In the general formula (2), R ⁴ to R ⁸ is each independently a monovalent organic group, R ⁴
To R ⁸ is preferably a hydrogen atom, a halogen atom, an amino group, a dialkylamino group, a carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, an alkyl group which may have a substituent, An aryl group which may have a substituent, an alkoxy group which may have a substituent, an aryloxy group which may have a substituent, an alkylamino group which may have a substituent, and a substituent Arylamino group which may have a substituent, an alkylsulfonyl group which may have a substituent, an arylsulfonyl group which may have a substituent, and the like. Among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, a substituent may be mentioned. The alkyl group which may have and the aryl group which may have a substituent are preferable.

Examples of the substituent that can be introduced are the same as those in the general formula (1). Y represents an oxygen atom, a sulfur atom, or N (R ¹² ) —. R ¹² has the same meaning as R ¹² in general formula (1), and preferred examples are also the same.

In the general formula (3), R ⁹ is preferably a hydrogen atom or an alkyl group which may have a substituent. Among them, a hydrogen atom or a methyl group has high radical reactivity. To preferred. R ¹⁰ and R ¹¹ are each independently a hydrogen atom, a halogen atom, an amino group, a dialkylamino group, a carboxyl group, an alkoxycarbonyl group, a sulfo group, a nitro group, a cyano group, or an alkyl group which may have a substituent. An aryl group which may have a substituent, an alkoxy group which may have a substituent, an aryloxy group which may have a substituent, an alkylamino group which may have a substituent, a substituent An arylamino group that may have, an alkylsulfonyl group that may have a substituent, an arylsulfonyl group that may have a substituent, and the like, among them, a hydrogen atom, a carboxyl group, an alkoxycarbonyl group, An alkyl group which may have a substituent and an aryl group which may have a substituent are preferable because of high radical reactivity.

Here, examples of the substituent that can be introduced are the same as those in the general formula (1). Further, Z is an oxygen atom, a sulfur atom, -N (R ¹³⁾ -, or a phenylene group which may have a substituent. Examples of R ¹³ include an alkyl group which may have a substituent. Among them, a methyl group, an ethyl group, and an isopropyl group are preferable because of high radical reactivity.
Among these, (meth) acrylic acid copolymers having a crosslinkable group in the side chain and polyurethane are more preferable.

  Hydrophobic binder polymers having crosslinkability include, for example, free radicals (polymerization initiation radicals or growth radicals in the polymerization process of a polymerizable compound) added to the crosslinkable functional group, and polymerization of polymerizable compounds directly between polymers. Addition polymerization through a chain forms a cross-link between polymer molecules and cures. Alternatively, atoms in the polymer (eg, hydrogen atoms on carbon atoms adjacent to the functional bridging group) are abstracted by free radicals to form polymer radicals that are bonded to each other so that crosslinking between the polymer molecules occurs. Forms and cures.

  The content of the crosslinkable group in the hydrophobic binder polymer (content of unsaturated double bond capable of radical polymerization by iodine titration) is preferably 0.1 to 10.0 mmol, more preferably 1 g per 1 g of the hydrophobic binder polymer. Is 1.0 to 7.0 mmol, most preferably 2.0 to 5.5 mmol.

  Further, it is preferable that the binder polymer is hydrophilic from the viewpoint of improving developability with respect to an aqueous solution, and it is important that the binder polymer is compatible with the polymerizable compound contained in the photosensitive layer from the viewpoint of improving printing durability. Yes, ie lipophilic. From such a viewpoint, in the present invention, it is also effective to copolymerize a hydrophilic group and a lipophilic group in a hydrophobic binder polymer in order to improve developability and printing durability. Examples of the hydrophilic group include a hydroxy group, a carboxylate group, a hydroxyethyl group, an ethyleneoxy group, a hydroxypropyl group, a polyoxyethyl group, a polyoxypropyl group, an amino group, an aminoethyl group, an aminopropyl group, and an ammonium group. And those having a hydrophilic group such as an amide group or a carboxymethyl group.

The hydrophobic binder polymer preferably has a mass average molecular weight of 5,000 or more, more preferably 10,000 to 300,000, and a number average molecular weight of 1,000 or more, preferably 2000 to 250,000. Is more preferable. The polydispersity (mass average molecular weight / number average molecular weight) is preferably 1.1 to 10.
The hydrophobic binder polymer may be any of a random polymer, a block polymer, a graft polymer, and the like, but is preferably a random polymer.

The hydrophobic binder polymer may be used alone or in combination of two or more.
The content of the hydrophobic binder polymer is 5 to 90% by mass, preferably 10 to 70% by mass, and more preferably 10 to 60% by mass with respect to the total solid content of the photosensitive layer. Within this range, good image area strength and image formability can be obtained.

<Microcapsule / Microgel>
In the present invention, several modes can be used as a method for incorporating the photosensitive layer constituents into the photosensitive layer. One is a molecular dispersion type photosensitive layer in which the constituent components are dissolved and applied in an appropriate solvent as described in JP-A-2002-287334, for example. Another aspect is, for example, as described in JP-A-2001-277740 and JP-A-2001-277742, a microcapsule in which all or part of the constituent components are encapsulated in a photosensitive layer. It is a capsule type photosensitive layer. Further, in the microcapsule type photosensitive layer, the constituent component can be contained outside the microcapsule. Here, it is preferable that the microcapsule type photosensitive layer includes a hydrophobic constituent component in the microcapsule and a hydrophilic constituent component outside the microcapsule. As still another embodiment, there may be mentioned an embodiment in which the photosensitive layer contains crosslinked resin particles, that is, microgel. The microgel may contain a part of the constituent component in and / or on the surface thereof. In particular, an embodiment in which a reactive microgel is formed by having a polymerizable compound on the surface thereof is particularly preferable from the viewpoint of image formation sensitivity and printing durability.
In order to obtain better on-press developability, the photosensitive layer is preferably a microcapsule type or microgel type photosensitive layer.

  As a method for microencapsulating or microgelling the photosensitive layer constituent components, known methods can be applied.

  For example, as a method for producing microcapsules, US Pat. No. 2,800,547, US Pat. No. 2,800,498, a method using coacervation, US Pat. No. 3,287,154, Japanese Patent Publication No. 38-19574, The method by the interfacial polymerization method found in US Pat. No. 42-446, the method by the precipitation of polymer found in US Pat. Nos. 3,418,250 and 3,660,304, the isocyanate found in US Pat. No. 3,796,669 Method using polyol wall material, method using isocyanate wall material found in US Pat. No. 3,914,511, urea found in US Pat. Nos. 4,001,140, 4,087,376 and 4,089,802 -Formaldehyde or urea formaldehyde -A method using a resorcinol-based wall forming material, a method using a wall material such as melamine-formaldehyde resin, hydroxycellulose, etc. found in US Pat. No. 4,025,445, Japanese Patent Publication Nos. 36-9163 and 51-9079. In-situ method by monomer polymerization, British Patent No. 930422, US Pat. No. 3,111,407 Spray drying method, British Patent No. 952807, US Pat. No. 9,670,741 Although there is a cooling method, it is not limited to these.

  A preferable microcapsule wall used in the present invention has a three-dimensional cross-linking and has a property of swelling with a solvent. From such a viewpoint, the wall material of the microcapsule is preferably polyurea, polyurethane, polyester, polycarbonate, polyamide, and a mixture thereof, and particularly preferably polyurea and polyurethane. Further, a compound having a crosslinkable functional group such as an ethylenically unsaturated bond capable of introducing a binder polymer may be introduced into the microcapsule wall.

On the other hand, as a method for preparing the microgel, granulation by interfacial polymerization described in JP-B-38-19574 and JP-A-42-446, non-patent document as described in JP-A-5-61214, and the like. Granulation by aqueous dispersion polymerization can be used. However, it is not limited to these methods.
As the method using the interfacial polymerization, the known microcapsule production method described above can be applied.

  Preferred microgels used in the present invention are those granulated by interfacial polymerization and having three-dimensional crosslinking. From such a viewpoint, the material to be used is preferably polyurea, polyurethane, polyester, polycarbonate, polyamide, and a mixture thereof, and polyurea and polyurethane are particularly preferable.

  The average particle size of the microcapsules or microgel is preferably 0.01 to 3.0 μm. 0.05-2.0 micrometers is further more preferable, and 0.10-1.0 micrometer is especially preferable. Within this range, good resolution and stability over time can be obtained.

<Other photosensitive layer components>
The photosensitive layer of the present invention can further contain various additives as required. These will be described below.

<Surfactant>
In the present invention, it is preferable to use a surfactant in the photosensitive layer in order to promote developability and improve the coated surface state. Examples of the surfactant include nonionic surfactants, anionic surfactants, cationic surfactants, amphoteric surfactants, and fluorosurfactants. Surfactant may be used independently and may be used in combination of 2 or more type.

  The nonionic surfactant used for this invention is not specifically limited, A conventionally well-known thing can be used. For example, polyoxyethylene alkyl ethers, polyoxyethylene alkyl phenyl ethers, polyoxyethylene polystyryl phenyl ethers, polyoxyethylene polyoxypropylene alkyl ethers, glycerin fatty acid partial esters, sorbitan fatty acid partial esters, pentaerythritol Fatty acid partial esters, propylene glycol mono fatty acid esters, sucrose fatty acid partial esters, polyoxyethylene sorbitan fatty acid partial esters, polyoxyethylene sorbitol fatty acid partial esters, polyethylene glycol fatty acid esters, polyglycerin fatty acid partial esters, Polyoxyethylenated castor oil, polyoxyethylene glycerin fatty acid partial esters, fatty acid diethanolamides, N N- bis-2-hydroxyalkylamines, polyoxyethylene alkylamines, triethanolamine fatty acid ester, trialkylamine oxide, polyethylene glycol, copolymers of polyethylene glycol and polypropylene glycol.

  The anionic surfactant used in the present invention is not particularly limited, and conventionally known anionic surfactants can be used. For example, fatty acid salts, abietic acid salts, hydroxyalkane sulfonates, alkane sulfonates, dialkyl sulfosuccinate esters, linear alkyl benzene sulfonates, branched alkyl benzene sulfonates, alkyl naphthalene sulfonates, alkyl phenoxy poly Oxyethylene propyl sulfonates, polyoxyethylene alkyl sulfophenyl ether salts, N-methyl-N-oleyl taurine sodium salt, N-alkyl sulfosuccinic acid monoamide disodium salt, petroleum sulfonates, sulfated beef oil, fatty acid alkyl esters Sulfates, alkyl sulfates, polyoxyethylene alkyl ether sulfates, fatty acid monoglyceride sulfates, polyoxyethylene alcohol Ruphenyl ether sulfates, polyoxyethylene styryl phenyl ether sulfates, alkyl phosphates, polyoxyethylene alkyl ether phosphates, polyoxyethylene alkyl phenyl ether phosphates, styrene / maleic anhydride Examples thereof include partial saponification products of polymers, partial saponification products of olefin / maleic anhydride copolymers, and naphthalene sulfonate formalin condensates.

The cationic surfactant used in the present invention is not particularly limited, and conventionally known cationic surfactants can be used. Examples thereof include alkylamine salts, quaternary ammonium salts, polyoxyethylene alkylamine salts, and polyethylene polyamine derivatives.
The amphoteric surfactant used in the present invention is not particularly limited, and conventionally known amphoteric surfactants can be used. Examples thereof include carboxybetaines, aminocarboxylic acids, sulfobetaines, aminosulfuric esters, and imidazolines.

  Of the above surfactants, the term “polyoxyethylene” can be read as “polyoxyalkylene” such as polyoxymethylene, polyoxypropylene, polyoxybutylene, etc. These surfactants can also be used.

More preferable surfactants include fluorine-based surfactants containing a perfluoroalkyl group in the molecule. Examples of such fluorosurfactants include anionic types such as perfluoroalkyl carboxylates, perfluoroalkyl sulfonates, and perfluoroalkyl phosphates; amphoteric types such as perfluoroalkyl betaines; Cation type such as trimethylammonium salt; perfluoroalkylamine oxide, perfluoroalkylethylene oxide adduct, oligomer containing perfluoroalkyl group and hydrophilic group, oligomer containing perfluoroalkyl group and lipophilic group, perfluoroalkyl Nonionic types such as an oligomer containing a group, a hydrophilic group and a lipophilic group, and a urethane containing a perfluoroalkyl group and a lipophilic group. Moreover, the fluorochemical surfactant described in Unexamined-Japanese-Patent No. 62-170950, 62-226143, and 60-168144 is also mentioned suitably.

Surfactant can be used individually or in combination of 2 or more types.
The content of the surfactant is preferably 0.001 to 10% by mass and more preferably 0.01 to 7% by mass with respect to the total solid content of the photosensitive layer.

<Hydrophilic polymer>
In the present invention, a hydrophilic polymer can be contained in order to improve developability and dispersion stability of microcapsules or microgels.
Examples of the hydrophilic polymer include hydroxy group, carboxyl group, carboxylate group, hydroxyethyl group, polyoxyethyl group, hydroxypropyl group, polyoxypropyl group, amino group, aminoethyl group, aminopropyl group, ammonium group, Preferred examples include those having a hydrophilic group such as an amide group, carboxymethyl group, sulfonic acid group, and phosphoric acid group.

  Specific examples include gum arabic, casein, gelatin, starch derivatives, carboxymethylcellulose and its sodium salt, cellulose acetate, sodium alginate, vinyl acetate-maleic acid copolymers, styrene-maleic acid copolymers, polyacrylic acids and their salts, Polymethacrylic acids and their salts, homopolymers and copolymers of hydroxyethyl methacrylate, homopolymers and copolymers of hydroxyethyl acrylate, homopolymers and copolymers of hydroxypropyl methacrylate, homopolymers and copolymers of hydroxypropyl acrylate, homopolymers of hydroxybutyl methacrylate Polymers and copolymers, homopolymers and copolymers of hydroxybutyl acrylate Polyethylene glycols, hydroxypropylene polymers, polyvinyl alcohols, hydrolyzed polyvinyl acetate, polyvinyl formal, polyvinyl butyral, polyvinyl pyrrolidone, acrylamide homopolymers and copolymers having a hydrolysis degree of 60 mol% or more, preferably 80 mol% or more , Homopolymers and polymers of methacrylamide, homopolymers and copolymers of N-methylolacrylamide, polyvinylpyrrolidone, alcohol-soluble nylon, polyether of 2,2-bis- (4-hydroxyphenyl) -propane and epichlorohydrin, etc. Is mentioned.

The hydrophilic polymer preferably has a mass average molecular weight of 5000 or more, more preferably 10,000 to 300,000. The hydrophilic polymer may be any of a random polymer, a block polymer, a graft polymer, and the like.
The content of the hydrophilic polymer in the photosensitive layer is preferably 20% by mass or less, more preferably 10% by mass or less, based on the total solid content of the photosensitive layer.

<Bakeout agent>
In the photosensitive layer of the present invention, a compound that changes color by an acid or a radical can be added in order to form a printout image. As such a compound, various dyes such as diphenylmethane, triphenylmethane, thiazine, oxazine, xanthene, anthraquinone, iminoquinone, azo, and azomethine are effectively used.

Specific examples include brilliant green, ethyl violet, methyl green, crystal violet, basic fuchsin, methyl violet 2B, quinaldine red, rose bengal, methanyl yellow, thymol sulfophthalein, xylenol blue, methyl orange, paramethyl red, Congo Fred, Benzopurpurin 4B, α-Naphthyl Red, Nile Blue 2B, Nile Blue A, Methyl Violet, Malachide Green, Parafukusin, Victoria Pure Blue BOH [manufactured by Hodogaya Chemical Co., Ltd.], Oil Blue # 603 [Orient Chemical Kogyo Co., Ltd.], Oil Pink # 312 [Orient Chemical Co., Ltd.], Oil Red 5B [Orient Chemical Co., Ltd.], Oil Scarlet # 308 [Orient Gaku Kogyo Co., Ltd.], Oil Red OG [Orient Chemical Co., Ltd.], Oil Red RR [Orient Chemical Co., Ltd.], Oil Green # 502 [Orient Chemical Co., Ltd.], Spiron Red BEH Special [made by Hodogaya Chemical Co., Ltd.], m-cresol purple, cresol red, rhodamine B, rhodamine 6G, sulforhodamine B, auramine, 4-p-diethylaminophenyliminonaphthoquinone, 2-carboxyanilino-4-p- Diethylaminophenyliminonaphthoquinone, 2-carboxystearylamino-4-pN, N-bis (hydroxyethyl) amino-phenyliminonaphthoquinone, 1-phenyl-3-methyl-4-p-diethylaminophenylimino-5-pyrazolone, 1-β-naphthyl-4- - dyes and p of diethylamino phenyl imino-5-pyrazolone, p ', p "- hexamethyl triamnotriphenylmethane (leuco crystal violet), and a leuco dye such as Pergascript Blue SRB (manufactured by Ciba-Geigy).

  In addition to the above, a leuco dye known as a material for thermal paper or pressure-sensitive paper is also suitable. Specific examples include crystal violet lactone, malachite green lactone, benzoylleucomethylene blue, 2- (N-phenyl-N-methylamino) -6- (Np-tolyl-N-ethyl) amino-fluorane, 2-anilino. -3-methyl-6- (N-ethyl-p-toluidino) fluorane, 3,6-dimethoxyfluorane, 3- (N, N-diethylamino) -5-methyl-7- (N, N-dibenzylamino) ) -Fluorane, 3- (N-cyclohexyl-N-methylamino) -6-methyl-7-anilinofluorane, 3- (N, N-diethylamino) -6-methyl-7-anilinofluorane, 3 -(N, N-diethylamino) -6-methyl-7-xylidinofluorane, 3- (N, N-diethylamino) -6-methyl-7-chloro Fluorane, 3- (N, N-diethylamino) -6-methoxy-7-aminofluorane, 3- (N, N-diethylamino) -7- (4-chloroanilino) fluorane, 3- (N, N-diethylamino) -7-chlorofluorane, 3- (N, N-diethylamino) -7-benzylaminofluorane, 3- (N, N-diethylamino) -7,8-benzofluorane, 3- (N, N-dibutyl) Amino) -6-methyl-7-anilinofluorane, 3- (N, N-dibutylamino) -6-methyl-7-xylidinofluorane, 3-piperidino-6-methyl-7-anilinofluorane 3-pyrrolidino-6-methyl-7-anilinofluorane, 3,3-bis (1-ethyl-2-methylindol-3-yl) phthalide, 3,3-bis (1-n-butyl- -Methylindol-3-yl) phthalide, 3,3-bis (p-dimethylaminophenyl) -6-dimethylaminophthalide, 3- (4-diethylamino-2-ethoxyphenyl) -3- (1-ethyl- 2-methylindol-3-yl) -4-zaphthalide, 3- (4-diethylaminophenyl) -3- (1-ethyl-2-methylindol-3-yl) phthalide, and the like.

  A suitable addition amount of the dye that changes color by acid or radical is 0.01 to 15% by mass relative to the solid content of the photosensitive layer.

<Polymerization inhibitor>
In order to prevent unnecessary thermal polymerization of the radical polymerizable compound during the production or storage of the photosensitive layer, it is preferable to add a small amount of a thermal polymerization inhibitor to the photosensitive layer of the present invention.
Examples of the thermal polymerization inhibitor include hydroquinone, p-methoxyphenol, di-t-
Butyl-p-cresol, pyrogallol, t-butylcatechol, benzoquinone, 4,4'-thiobis (3-methyl-6-t-butylphenol), 2,2'-methylenebis (4-methyl-6-t-butylphenol) N-nitroso-N-phenylhydroxylamine aluminum salt is preferable.
The addition amount of the thermal polymerization inhibitor is preferably about 0.01 to about 5% by mass with respect to the total solid content of the photosensitive layer.

<Higher fatty acid derivatives, etc.>
In order to prevent polymerization inhibition by oxygen, a higher fatty acid derivative such as behenic acid or behenamide is added to the photosensitive layer of the present invention so that it is unevenly distributed on the surface of the photosensitive layer during the drying process after coating. May be. The amount of the higher fatty acid derivative added is preferably from about 0.1 to about 10% by weight based on the total solid content of the photosensitive layer.

<Plasticizer>
The photosensitive layer of the present invention may contain a plasticizer. Examples of the plasticizer include phthalates such as dimethyl phthalate, diethyl phthalate, dibutyl phthalate, diisobutyl phthalate, dioctyl phthalate, octyl capryl phthalate, dicyclohexyl phthalate, ditridecyl phthalate, butyl benzyl phthalate, diisodecyl phthalate, diallyl phthalate; Glycol esters such as glycol phthalate, ethyl phthalyl ethyl glycolate, methyl phthalyl ethyl glycolate, butyl phthalyl butyl glycolate, triethylene glycol dicaprylate; Phosphate esters such as tricresyl phosphate and triphenyl phosphate Diisobutyl adipate, dioctyl adipate, dimethyl sebacate, dibutyl sebacate, dioct Ruazereto, aliphatic dibasic acid esters such as dibutyl maleate; polyglycidyl methacrylate, triethyl citrate, glycerin triacetyl ester, butyl laurate in. The plasticizer content is preferably about 30% by mass or less based on the total solid content of the photosensitive layer.

<Inorganic fine particles>
The photosensitive layer of the present invention may contain inorganic fine particles in order to improve the cured film strength of the image area. As the inorganic fine particles, for example, silica, alumina, magnesium oxide, titanium oxide, magnesium carbonate, calcium alginate or a mixture thereof can be preferably mentioned. Even if they are not photothermally convertible, they can be used for strengthening the film, enhancing interfacial adhesion by surface roughening, and the like. The inorganic fine particles preferably have an average particle size of 5 nm to 10 μm, and more preferably 0.5 to 3 μm. Within the above range, it is possible to form a non-image portion excellent in hydrophilicity that is stably dispersed in the photosensitive layer, sufficiently retains the film strength of the photosensitive layer, and does not easily cause stains during printing.
The inorganic fine particles as described above can be easily obtained as a commercial product such as a colloidal silica dispersion.
The content of the inorganic fine particles is preferably 20% by mass or less, and more preferably 10% by mass or less, based on the total solid content of the photosensitive layer.

<Low molecular hydrophilic compound>
The photosensitive layer of the present invention can contain a hydrophilic low molecular weight compound for improving developability. Examples of the hydrophilic low-molecular compound include water-soluble organic compounds such as ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol and the like, and ether or ester derivatives thereof, glycerin, Polyhydroxys such as pentaerythritol, organic amines such as triethanolamine and diethanolamine monoethanolamine and salts thereof, organic sulfonic acids such as toluenesulfonic acid and benzenesulfonic acid and salts thereof, organic phosphonic acids such as phenylphosphonic acid and the like Organic carboxylic acids such as salts, tartaric acid, oxalic acid, citric acid, malic acid, lactic acid, gluconic acid, amino acids and their salts, and organic quaternary amines such as tetraethylamine hydrochloride Salt, and the like.

<Co-sensitizer>
The photosensitive layer of the present invention can contain a co-sensitizer. Examples of the co-sensitizer include ethanolamines, N-phenylglycines, N-trimethylsilylmethylanilines, and the like, sulfur-containing compounds in which the nitrogen atoms of the above-described amines are replaced with sulfur atoms and tin atoms, tin-containing compounds, Mention may be made of sulfinates such as sodium arylsulfinate.

<Formation of photosensitive layer>
The photosensitive layer of the present invention is formed by preparing or applying a coating solution by dispersing or dissolving the necessary components described above in a solvent. Solvents used here include ethylene dichloride, cyclohexanone, methyl ethyl ketone, methanol, ethanol, propanol, ethylene glycol monomethyl ether, 1-methoxy-2-propanol, 2-methoxyethyl acetate, 1-methoxy-2-propyl acetate, dimethoxy Examples include ethane, methyl lactate, ethyl lactate, N, N-dimethylacetamide, N, N-dimethylformamide, tetramethylurea, N-methylpyrrolidone, dimethyl sulfoxide, sulfolane, γ-butyllactone, toluene, water, and the like. However, the present invention is not limited to this. These solvents are used alone or in combination. The solid content concentration of the coating solution is preferably 1 to 50% by mass.
The photosensitive layer of the present invention can be formed by preparing a plurality of coating solutions in which the same or different components are dispersed or dissolved in the same or different solvents, and repeatedly applying and drying a plurality of times.

The coating, the photosensitive layer coating amount on the support obtained after drying (solid content) may be varied according to the intended purpose, generally 0.3 to 3.0 g / m ² is preferred. Within this range, good sensitivity and good film properties of the photosensitive layer can be obtained.
Various methods can be used as a coating method. Examples thereof include bar coater coating, spin coating, spray coating, curtain coating, dip coating, air knife coating, blade coating, and roll coating.

(Protective layer)
The lithographic printing plate precursor according to the invention is preferably provided with a protective layer (oxygen blocking layer) on the photosensitive layer in order to block diffusion and penetration of oxygen that hinders the polymerization reaction during exposure. The protective layer used in the present invention preferably has an oxygen permeability A at 25 ° C. and 1 atm of 1.0 ≦ A ≦ 20 (mL / m ² · day). When the oxygen permeability A is extremely low at less than 1.0 (mL / m ² · day), unnecessary polymerization reaction occurs at the time of production and raw storage, and unnecessary fogging and image streaking occur during image exposure. The problem that fatness arises arises. Conversely, when the oxygen permeability A exceeds 20 (mL / m ² · day) and is too high, the sensitivity is lowered. The oxygen permeability A is more preferably in the range of 1.5 ≦ A ≦ 12 (mL / m ² · day), more preferably 2.0 ≦ A ≦ 10.0 (mL / m ² · day). In addition to the oxygen permeability described above, the properties desired for the protective layer further do not substantially inhibit the transmission of light used for exposure, have excellent adhesion to the photosensitive layer, and are easy in the development process after exposure. It is desirable that it can be removed. The device concerning such a protective layer has been conventionally made, and is described in detail in US Pat. No. 3,458,311 and JP-B-55-49729.

As a material that can be used for the protective layer, for example, a water-soluble polymer compound having relatively excellent crystallinity is preferably used. Specifically, polyvinyl alcohol, vinyl alcohol / vinyl phthalate copolymer, vinyl acetate / vinyl are used. Examples include water-soluble polymers such as alcohol / vinyl phthalate copolymer, vinyl acetate / crotonic acid copolymer, polyvinyl pyrrolidone, acidic celluloses, gelatin, gum arabic, polyacrylic acid, and polyacrylamide. Or they can be mixed. Of these, the use of polyvinyl alcohol as the main component gives the best results in terms of basic properties such as oxygen barrier properties and development removability.

  The polyvinyl alcohol used for the protective layer may be partially substituted with an ester, an ether, and an acetal as long as it contains an unsubstituted vinyl alcohol unit for having necessary oxygen barrier properties and water solubility. Similarly, some of them may have other copolymer components. Specific examples of polyvinyl alcohol include those that are hydrolyzed by 71 to 100 mol% and have a polymerization repeating unit in the range of 300 to 2400. Specifically, Kuraray Co., Ltd. PVA-105, PVA-110, PVA-117, PVA-117H, PVA-120, PVA-124, PVA-124H, PVA-CS, PVA-CST, PVA-HC, PVA-203, PVA-204, PVA-205, PVA-210, PVA-217, PVA-220, PVA-224, PVA-217EE, PVA-217E, PVA-220E, PVA-224E, PVA-405, PVA- 420, PVA-613, L-8 and the like, and these can be used alone or in combination. In a preferred embodiment, the content of polyvinyl alcohol in the protective layer is 20 to 95% by mass, and more preferably 30 to 90% by mass.

  Moreover, well-known modified polyvinyl alcohol can also be used preferably. For example, various hydrophilic modification sites such as anion modification sites modified with anions such as carboxyl groups and sulfo groups, cation modification sites modified with cations such as amino groups and ammonium groups, silanol modification sites, and thiol modification sites are randomly selected. Polyvinyl alcohol having various degrees of polymerization, the anion-modified site, the cation-modified site, the silanol-modified site, the thiol-modified site, the alkoxyl-modified site, the sulfide-modified site, and the ester modification of vinyl alcohol and various organic acids. Examples thereof include polyvinyl alcohol having various polymerization degrees having various modified sites such as a site, an ester-modified site of the anion-modified site and alcohols, an epoxy-modified site, and the like.

  As a component used by mixing with polyvinyl alcohol, polyvinyl pyrrolidone or a modified product thereof is preferable from the viewpoint of oxygen barrier properties and development removability, and the content in the protective layer is 3.5 to 80% by mass, preferably 10 to 60%. It is 15 mass%, More preferably, it is 15-30 mass%.

  Components of the protective layer (selection of PVA, use of additives), coating amount, and the like are selected in consideration of fogging, adhesion, and scratch resistance in addition to oxygen barrier properties and development removability. In general, the higher the hydrolysis rate of the PVA used (the higher the content of the unsubstituted vinyl alcohol unit in the protective layer), the thicker the film thickness, the higher the oxygen barrier property, which is advantageous in terms of sensitivity. The molecular weight of the (co) polymer such as polyvinyl alcohol (PVA) can be in the range of 2000 to 10 million, preferably in the range of 20,000 to 3 million.

  As another composition of the protective layer, glycerin, dipropylene glycol and the like can be added in an amount corresponding to several mass% with respect to the (co) polymer to provide flexibility. Anionic surfactants such as sodium acid salts; amphoteric surfactants such as alkylaminocarboxylates and alkylaminodicarboxylates; nonionic surfactants such as polyoxyethylene alkylphenyl ethers to the (co) polymer Mass% can be added.

In addition, adhesion to the image area and scratch resistance are extremely important in handling the plate. That is, when a hydrophilic layer made of a water-soluble polymer is laminated on an oleophilic photosensitive layer, film peeling due to insufficient adhesion tends to occur, and the peeled part causes defects such as poor film hardening due to inhibition of oxygen polymerization. On the other hand, various proposals have been made to improve the adhesion between these two layers. For example, in U.S. Patent Application No. 292,501 and U.S. Patent Application No. 44,563, an acrylic emulsion or a water-insoluble vinyl pyrrolidone-vinyl acetate copolymer is contained in a hydrophilic polymer mainly composed of polyvinyl alcohol. It is described that sufficient adhesiveness can be obtained by mixing 20 to 60% by mass and laminating on a photosensitive layer. Any of these known techniques can be applied to the protective layer in the present invention. Such a coating method of the protective layer is described in detail in, for example, US Pat. No. 3,458,311 and JP-B-55-49729.

Furthermore, the protective layer in the lithographic printing plate precursor according to the invention preferably contains an inorganic stratiform compound for the purpose of improving oxygen barrier properties and photosensitive layer surface protection.
Here, the inorganic layered compound is a particle having a thin flat plate shape. For example, the following general formula A (B, C) _2-5 D ₄ O ₁₀ (OH, F, O) ₂
[However, A is any one of K, Na, and Ca, B and C are any of Fe (II), Fe (III), Mn, Al, Mg, and V, and D is Si or Al. And mica groups such as natural mica and synthetic mica, talc, teniolite, montmorillonite, saponite, hectorite, zirconium phosphate and the like represented by the formula 3MgO.4SiO.H ₂ O.

In the mica group, examples of natural mica include muscovite, soda mica, phlogopite, biotite and sericite. As the synthetic mica, fluorine phlogopite KMg ₃ (AlSi ₃ O ₁₀
) F ₂ , Potassium tetrasilicon mica KMg _2.5 Si ₄ O ₁₀ ) Non-swelling mica such as F ₂ , and Na tetrasilicic mica NaMg _2.5 (Si ₄ O ₁₀ ) F ₂ , Na or Li teniolite (N
_{a, Li) Mg 2 Li (} Si 4 O 10) F 2, montmorillonite of Na or Li hectorite _{(Na, Li) 1/8 Mg 2} /5 Li 1/8 (Si 4 O 10) F 2 , etc. Examples include swelling mica. Synthetic smectite is also useful.

In the present invention, among the inorganic layered compounds, fluorine-based swellable mica, which is a synthetic inorganic layered compound, is particularly useful. That is, this swellable synthetic mica and swellable viscosity minerals such as montmorillonite, saponite, hectorite, bentonite, etc. have a laminated structure composed of unit crystal lattice layers with a thickness of about 10 to 15 mm, Atomic substitution is significantly greater than other viscous minerals. As a result, the lattice layer is deficient in positive charges, and cations such as Na ⁺ , Ca ²⁺ and Mg ²⁺ are adsorbed between the layers in order to compensate for this. The cations present between these layers are called exchangeable cations and exchange with various cations. In particular, when the cation between the layers is Li ⁺ or Na ⁺ , the bond between the layered crystal lattices is weak because the ionic radius is small, and the layer swells greatly with water. If shear is applied in this state, it will easily cleave and form a stable sol in water. Bentonite and swellable synthetic mica have this tendency and are useful in the present invention, and swellable synthetic mica is particularly preferably used.

  As the shape of the inorganic layered compound used in the present invention, from the viewpoint of diffusion control, the smaller the thickness, the better. The plane size is as long as it does not hinder the smoothness of the coated surface or the transmittance of actinic rays. Larger is better. Accordingly, the aspect ratio is 20 or more, preferably 100 or more, particularly preferably 200 or more. The aspect ratio is the ratio of the thickness to the major axis of the particle, and can be measured, for example, from a projected view of the particle by a micrograph. The larger the aspect ratio, the greater the effect that can be obtained.

As for the particle size of the inorganic layered compound used in the present invention, the average major axis is 0.3 to 20 μm,
Preferably it is 0.5-10 micrometers, Most preferably, it is 1-5 micrometers. The average thickness of the particles is 0.1 μm or less, preferably 0.05 μm or less, particularly preferably 0.01 μm or less. For example, among inorganic layered compounds, the size of the swellable synthetic mica that is a representative compound is about 1 to 50 nm in thickness and about 1 to 20 μm in surface size.

  When the inorganic layered compound particles having such a large aspect ratio are contained in the protective layer, the coating film strength is improved, and the permeation of oxygen and moisture can be effectively prevented. Deterioration is prevented, and even when stored for a long time under high-humidity conditions, the storage stability of the planographic printing plate precursor does not deteriorate due to changes in humidity, and the storage stability is excellent.

  It is preferable that content of the inorganic stratiform compound in a protective layer is 5/1-1/100 by mass ratio with respect to the quantity of the binder used for a protective layer. Even when a plurality of types of inorganic layered compounds are used in combination, the total amount of these inorganic layered compounds is preferably the above-described mass ratio.

  Next, an example of a general dispersion method of the inorganic stratiform compound used for the protective layer will be described. First, 5 to 10 parts by mass of the swellable layered compound mentioned above as a preferred inorganic layered compound is added to 100 parts by mass of water, and the mixture is thoroughly swelled and swollen, and then dispersed by a disperser. Examples of the disperser used here include various mills that disperse mechanically by applying a direct force, a high-speed stirring disperser having a large shearing force, and a disperser that provides high-intensity ultrasonic energy. Specifically, ball mill, sand grinder mill, visco mill, colloid mill, homogenizer, tisol bar, polytron, homomixer, homo blender, ketdy mill, jet agitator, capillary emulsifier, liquid siren, electrostrictive ultrasonic generator, An emulsifying device having a Paulman whistle can be used. A dispersion of 5 to 10% by mass of the inorganic stratiform compound dispersed by the above method is highly viscous or gelled and has very good storage stability. When preparing a protective layer coating solution using this dispersion, it is preferably prepared by diluting with water and stirring sufficiently, and then blending with a binder solution.

  In addition to the inorganic layered compound, known additives such as a surfactant for improving the coating property and a water-soluble plasticizer for improving the physical properties of the film can be added to the protective layer coating solution. Examples of the water-soluble plasticizer include propionamide, cyclohexanediol, glycerin, sorbitol and the like. A water-soluble (meth) acrylic polymer can also be added. Furthermore, known additives for improving the adhesion to the photosensitive layer and the temporal stability of the coating solution may be added to the coating solution.

  The protective layer coating solution thus prepared is applied onto the photosensitive layer provided on the support and dried to form a protective layer. The coating solvent can be appropriately selected in relation to the binder, but when a water-soluble polymer is used, it is preferable to use distilled water or purified water. The method for applying the protective layer is not particularly limited, and a known method such as the method described in US Pat. No. 3,458,311 or Japanese Patent Publication No. 55-49729 can be applied. . Specific examples of the protective layer include blade coating, air knife coating, gravure coating, roll coating coating, spray coating, dip coating, and bar coating.

The coating amount of the protective layer is preferably in the range of 0.05 to 10 g / m ^{2 in} terms of the coating amount after drying. When the inorganic layered compound is contained, 0.1 to 0.5 g / The range of m ² is more preferable, and when the inorganic layered compound is not contained, the range of 0.5 to 5 g / m ² is more preferable.

(Support)
The support used in the lithographic printing plate precursor according to the invention is not particularly limited as long as it is a dimensionally stable plate-like hydrophilic support. For example, paper, paper laminated with plastic (eg, polyethylene, polypropylene, polystyrene, etc.), metal plate (eg, aluminum, zinc, copper, etc.), plastic film (eg, cellulose diacetate, cellulose triacetate, cellulose propionate) Cellulose butyrate, cellulose acetate butyrate, cellulose nitrate, polyethylene terephthalate, polyethylene, polystyrene, polypropylene, polycarbonate, polyvinyl acetal, etc.), and paper or plastic films on which the above-mentioned metals are laminated or deposited. Preferable supports include a polyester film and an aluminum plate. Among these, an aluminum plate that has good dimensional stability and is relatively inexpensive is preferable.

  The aluminum plate is a pure aluminum plate, an alloy plate containing aluminum as a main component and containing a trace amount of different elements, or a plastic laminated on a thin film of aluminum or an aluminum alloy. Examples of foreign elements contained in the aluminum alloy include silicon, iron, manganese, copper, magnesium, chromium, zinc, bismuth, nickel, and titanium. The content of foreign elements in the alloy is preferably 10% by mass or less. In the present invention, a pure aluminum plate is preferable, but completely pure aluminum is difficult to manufacture in terms of refining technology, and therefore may contain a slightly different element. The composition of the aluminum plate is not specified, and a publicly known material can be used as appropriate.

  The thickness of the support is preferably from 0.1 to 0.6 mm, more preferably from 0.15 to 0.4 mm, and even more preferably from 0.2 to 0.3 mm.

  Prior to using the aluminum plate, it is preferable to perform a surface treatment such as roughening treatment or anodizing treatment. By the surface treatment, it becomes easy to improve hydrophilicity and secure adhesion between the photosensitive layer and the support. Prior to roughening the aluminum plate, a degreasing treatment with a surfactant, an organic solvent, an alkaline aqueous solution or the like for removing rolling oil on the surface is performed as desired.

The surface roughening treatment of the aluminum plate is performed by various methods. For example, mechanical surface roughening treatment, electrochemical surface roughening treatment (surface roughening treatment for dissolving the surface electrochemically), chemical treatment, etc. Surface roughening treatment (roughening treatment that chemically selectively dissolves the surface).
As a method for the mechanical surface roughening treatment, a known method such as a ball polishing method, a brush polishing method, a blast polishing method, or a buff polishing method can be used.
Examples of the electrochemical surface roughening treatment include a method in which an alternating current or a direct current is used in an electrolytic solution containing an acid such as hydrochloric acid or nitric acid. Another example is a method using a mixed acid as described in JP-A-54-63902.

  The surface-roughened aluminum plate is subjected to an alkali etching treatment using an aqueous solution of potassium hydroxide, sodium hydroxide or the like, if necessary, further neutralized, and if desired, wear resistant. In order to increase the anodic oxidation treatment.

As the electrolyte used for the anodizing treatment of the aluminum plate, various electrolytes that form a porous oxide film can be used. In general, sulfuric acid, hydrochloric acid, oxalic acid, chromic acid or a mixed acid thereof is used. The concentration of these electrolytes is appropriately determined depending on the type of electrolyte.
The conditions for anodizing treatment vary depending on the electrolyte used, and thus cannot be specified in general. In general, however, an electrolyte concentration of 1 to 80% by mass solution, a liquid temperature of 5 to 70 ° C., a current density of 5 to 60 A / d m ² , voltage 1 to 100 V, and electrolysis time 10 seconds to 5 minutes are preferable. The amount of the anodized film formed is preferably from 1.0 to 5.0 g / m ^2, and more preferably 1.5 to 4.0 g / m ^2. Within this range, good printing durability and good scratch resistance of the non-image area of the lithographic printing plate can be obtained.

  As the support used in the present invention, the substrate having the above-mentioned surface treatment and having an anodized film may be used as it is, but for further improvement in adhesion to the upper layer, hydrophilicity, resistance to contamination, heat insulation and the like. If necessary, it contains a micropore enlargement treatment, a micropore sealing treatment, and a hydrophilic compound described in Japanese Patent Application Laid-Open Nos. 2001-253181 and 2001-322365. A surface hydrophilization treatment immersed in an aqueous solution can be selected as appropriate. Of course, these enlargement processing and sealing processing are not limited to those described above, and any conventionally known method can be performed.

Sealing treatment includes vapor sealing, single treatment with zirconic fluoride, treatment with an aqueous solution containing an inorganic fluorine compound such as treatment with sodium fluoride, vapor sealing with addition of lithium chloride, sealing with hot water. Hole processing is also possible.
Of these, sealing treatment with an aqueous solution containing an inorganic fluorine compound, sealing treatment with water vapor, and sealing treatment with hot water are preferable.

  The hydrophilization treatment is described in the specifications of US Pat. Nos. 2,714,066, 3,181,461, 3,280,734, and 3,902,734. There are such alkali metal silicate methods. In this method, the support is immersed in an aqueous solution such as sodium silicate or electrolytically treated. In addition, the treatment with potassium zirconate fluoride described in JP-B 36-22063, U.S. Pat. Nos. 3,276,868, 4,153,461 and 4,689, And a method of treating with polyvinylphosphonic acid as described in the specification of No. 272.

  When using a support having insufficient surface hydrophilicity, such as a polyester film, as the support of the present invention, it is desirable to apply a hydrophilic layer to make the surface hydrophilic. As the hydrophilic layer, at least one element selected from beryllium, magnesium, aluminum, silicon, titanium, boron, germanium, tin, zirconium, iron, vanadium, antimony, and a transition metal described in JP-A-2001-199175 A hydrophilic layer formed by coating a coating solution containing a colloid of oxide or hydroxide, or organic hydrophilicity obtained by crosslinking or pseudo-crosslinking an organic hydrophilic polymer described in JP-A-2002-79772 A hydrophilic layer having a hydrophilic matrix, a hydrophilic layer having an inorganic hydrophilic matrix obtained by sol-gel conversion comprising hydrolysis, condensation reaction of polyalkoxysilane, titanate, zirconate or aluminate, or a metal oxide A hydrophilic layer made of an inorganic thin film having a surface is preferred. Arbitrariness. Among these, a hydrophilic layer formed by applying a coating solution containing a silicon oxide or a hydroxide colloid is preferable.

  Moreover, when using a polyester film etc. as a support body of this invention, it is preferable to provide an antistatic layer in the hydrophilic layer side of a support body, the opposite side, or both sides. In the case where the antistatic layer is provided between the support and the hydrophilic layer, it also contributes to improving the adhesion with the hydrophilic layer. As the antistatic layer, a polymer layer in which metal oxide fine particles or a matting agent are dispersed as described in JP-A-2002-79772 can be used.

The support preferably has a center line average roughness of 0.10 to 1.2 μm. Within this range, good adhesion to the photosensitive layer, good printing durability and good stain resistance can be obtained.
The color density of the support is preferably 0.15 to 0.65 as the reflection density value. Within this range, good image formability by preventing halation during image exposure and good plate inspection after development can be obtained.

(Undercoat layer)
In the lithographic printing plate precursor according to the invention, it is preferable to provide an undercoat layer of a compound containing a polymerizable group on a support. When an undercoat layer is used, the photosensitive layer is provided on the undercoat layer. The undercoat layer reinforces the adhesion between the support and the photosensitive layer in the exposed area, and easily peels the photosensitive layer from the support in the unexposed area, thereby improving the developability.
As the undercoat layer, specifically, a silane coupling agent having an addition-polymerizable ethylenic double bond reactive group described in JP-A-10-282679, JP-A-2-304441. The phosphorus compound etc. which have the ethylenic double bond reactive group of description are mentioned suitably. Particularly preferred compounds include compounds having a polymerizable group such as a methacryl group and an allyl group and a support-adsorptive group such as a sulfonic acid group, a phosphoric acid group and a phosphoric acid ester. A compound having a hydrophilicity-imparting group such as an ethylene oxide group in addition to the polymerizable group and the support-adsorbing group can also be exemplified as a suitable compound.
The coating amount (solid content) of the undercoat layer is preferably from 0.1-100 mg / m ^2, and more preferably 1 to 30 mg / m ^2.

(Back coat layer)
After the surface treatment is performed on the support or after the undercoat layer is formed, a back coat can be provided on the back surface of the support, if necessary. Examples of the back coat include hydrolysis and polycondensation of organic polymer compounds described in JP-A-5-45885, organometallic compounds or inorganic metal compounds described in JP-A-6-35174. A coating layer made of a metal oxide obtained in this manner is preferred. Among them, it is inexpensive to use a silicon alkoxy compound such as Si (OCH ₃ ) ₄ , Si (OC ₂ H ₅ ) ₄ , Si (OC ₃ H ₇ ) ₄ , Si (OC ₄ H ₉ ) _4. It is preferable in terms of easy availability.

[Preparation method of planographic printing plate]
The lithographic printing plate precursor in the present invention is image-exposed with a light source of 350 nm to 450 nm, and then rubbed on the plate surface with a rubbing member in the presence of a developer having a pH of 2 to 10 by an automatic developing machine. The photosensitive layer in the exposed area can be removed at once to form an image on the surface of the aluminum plate support.
That is, after removing the protective layer and the non-exposed portion of the photosensitive layer at once, it can be set on a printing machine and printed immediately.
In addition, such processing in an automatic developing machine has an advantage that it is freed from dealing with the development residue derived from the protective layer and the photosensitive layer that occurs in the case of on-press development.

The developer used in the present invention is an aqueous solution having a pH of 2 to 10. For example, water alone or an aqueous solution containing water as a main component (containing 60% by mass or more of water) is preferable. In particular, an aqueous solution having the same composition as that of a generally known fountain solution, a surfactant (anionic, nonionic, An aqueous solution containing a cationic system or the like, or an aqueous solution containing a water-soluble polymer compound (gum solution) is preferable. In particular, an aqueous solution containing both a surfactant and a water-soluble polymer compound is preferable. The pH of the developer is more preferably 3-8, and even more preferably 4-7.
When an acidic to neutral developer is used, it is preferable to contain either an organic acid or an inorganic acid. By containing an organic acid or an inorganic acid, the developability can be improved during plate making, and the occurrence of stains on the non-image area of the plate-making printing plate can be suppressed.

Examples of the anionic surfactant used in the present invention include fatty acid salts, abietic acid salts, hydroxyalkane sulfonic acid salts, alkane sulfonic acid salts, dialkyl sulfosuccinic acid salts, linear alkyl benzene sulfonic acid salts, branched alkyl benzene sulfonic acid salts, Alkylnaphthalene sulfonates, alkylphenoxy polyoxyethylene propyl sulfonates, polyoxyethylene alkyl sulfophenyl ether salts, N-methyl-N-oleyl taurine sodium, N-alkyl sulfosuccinic acid monoamide disodium salts, petroleum sulfonates , Sulfated castor oil, sulfated beef tallow oil, fatty acid alkyl ester sulfates, alkyl sulfates, polyoxyethylene alkyl ether sulfates, fatty acid compounds Glyceryl sulfate ester salt, polyoxyethylene alkylphenyl ether sulfate ester salt, polyoxyethylene styryl phenyl ether sulfate ester salt, alkyl phosphate ester salt, polyoxyethylene alkyl ether phosphate ester salt, polyoxyethylene alkylphenyl ether phosphate ester salt, styrene -Partial saponifications of maleic anhydride copolymer, partial saponifications of olefin-maleic anhydride copolymer, naphthalene sulfonate formalin condensate and the like. Among these, dialkyl sulfosuccinates, alkyl sulfate esters and alkyl naphthalene sulfonates are particularly preferably used.

  It does not specifically limit as a cationic surfactant used for this invention, A conventionally well-known thing can be used. Examples thereof include alkylamine salts, quaternary ammonium salts, polyoxyethylene alkylamine salts, and polyethylene polyamine derivatives.

Nonionic surfactants used in the present invention include polyethylene glycol type higher alcohol ethylene oxide adduct, alkylphenol ethylene oxide adduct, fatty acid ethylene oxide adduct, polyhydric alcohol fatty acid ester ethylene oxide adduct, higher alkylamine ethylene. Oxide adduct, fatty acid amide ethylene oxide adduct, fat and oil ethylene oxide adduct, polypropylene glycol ethylene oxide adduct, dimethylsiloxane-ethylene oxide block copolymer, dimethylsiloxane- (propylene oxide-ethylene oxide) block copolymer, etc. Alcohol-type glycerol fatty acid ester, pentaerythritol fatty acid ester, sorbitol and sorbita Fatty acid esters of fatty acid esters of sucrose, alkyl ethers of polyhydric alcohols, fatty acid amides of alkanolamines.
These nonionic surfactants may be used alone or in admixture of two or more. In the present invention, ethylene oxide adduct of sorbitol and / or sorbitan fatty acid ester, polypropylene glycol ethylene oxide adduct, dimethylsiloxane-ethylene oxide block copolymer, dimethylsiloxane- (propylene oxide-ethylene oxide) block copolymer, polyhydric alcohol Fatty acid esters are more preferred.

Further, from the viewpoint of stable solubility or turbidity in water, the nonionic surfactant used in the developer of the present invention is HLB (Hydrophile-Lipophile).
The (Balance) value is preferably 6 or more, and more preferably 8 or more. Furthermore, the ratio of the nonionic surfactant contained in the developer is preferably 0.01 to 10% by mass, and more preferably 0.01 to 5% by mass.
Further, acetylene glycol-based and acetylene alcohol-based oxyethylene adducts, fluorine-based and silicone-based surfactants can also be used in the same manner.
As the surfactant used in the developer of the present invention, a nonionic surfactant is particularly suitable from the viewpoint of foam suppression.

  Examples of the water-soluble polymer compound used in the developer of the present invention include soybean polysaccharide, modified starch, gum arabic, dextrin, fibrin derivatives (eg, carboxymethylcellulose, carboxyethylcellulose, methylcellulose, etc.) and modified products thereof, pullulan. , Polyvinyl alcohol and its derivatives, polyvinyl pyrrolidone, polyacrylamide and acrylamide copolymer, vinyl methyl ether / maleic anhydride copolymer, vinyl acetate / maleic anhydride copolymer, styrene / maleic anhydride copolymer, etc. It is done.

A well-known thing can be used for the said soybean polysaccharide, for example, there exists a brand name Soya Five (made by Fuji Oil Co., Ltd.) as a commercial item, and the thing of various grades can be used. What can be preferably used is one in which the viscosity of a 10% by mass aqueous solution is in the range of 10 to 100 mPa / sec.

  As the modified starch, known ones can be used, and starch such as corn, potato, tapioca, rice and wheat is decomposed with acid or enzyme in the range of 5 to 30 glucose residues per molecule, and further in an alkali. It can be made by a method of adding oxypropylene or the like.

Two or more water-soluble polymer compounds can be used in combination. The content of the water-soluble polymer compound in the developer is preferably from 0.1 to 20% by mass, and more preferably from 0.5 to 10% by mass.

  Further, the developer of the present invention may contain an organic solvent. Examples of the organic solvent that can be contained include aliphatic hydrocarbons (hexane, heptane, “Isopar E, H, G” (manufactured by Esso Chemical Co., Ltd.) or gasoline, kerosene, etc.), and aromatic hydrocarbons (toluene). , Xylene, etc.), halogenated hydrocarbons (methylene dichloride, ethylene dichloride, tricrene, monochlorobenzene, etc.) and polar solvents.

  Polar solvents include alcohols (methanol, ethanol, propanol, isopropanol, benzyl alcohol, ethylene glycol monomethyl ether, 2-ethoxyethanol, diethylene glycol monoethyl ether, diethylene glycol monohexyl ether, triethylene glycol monomethyl ether, propylene glycol monoethyl ether , Propylene glycol monomethyl ether, polyethylene glycol monomethyl ether, polypropylene glycol, tetraethylene glycol, ethylene glycol monobutyl ether, ethylene glycol monobenzyl ether, ethylene glycol monophenyl ether, methylphenyl carbinol, n-amyl alcohol, methyl amyl alcohol, etc.) , (Acetone, methyl ethyl ketone, ethyl butyl ketone, methyl isobutyl ketone, cyclohexanone, etc.), esters (ethyl acetate, propyl acetate, butyl acetate, amyl acetate, benzyl acetate, methyl lactate, butyl lactate, ethylene glycol monobutyl acetate, propylene Glycol monomethyl ether acetate, diethylene glycol acetate, diethyl phthalate, butyl levulinate, etc.) and others (triethyl phosphate, tricresyl phosphate, N-phenylethanolamine, N-phenyldiethanolamine, etc.).

  If the organic solvent is insoluble in water, it can be used after being solubilized in water using a surfactant or the like. If the developer contains an organic solvent, safety, ignition, From the viewpoint of property, the concentration of the solvent is preferably less than 40% by mass.

  In addition to the above, the developer of the present invention may contain a preservative, a chelate compound, an antifoaming agent, an organic acid, an inorganic acid, an inorganic salt, and the like.

  Preservatives include phenol or derivatives thereof, formalin, imidazole derivatives, sodium dehydroacetate, 4-isothiazolin-3-one derivatives, benzisothiazolin-3-one, benztriazole derivatives, amiding anidine derivatives, quaternary ammonium salts, pyridine, Derivatives such as quinoline and guanidine, diazine, triazole derivatives, oxazole, oxazine derivatives, nitrobromoalcohol-based 2-bromo-2-nitropropane-1,3diol, 1,1-dibromo-1-nitro-2-ethanol, 1,1-dibromo-1-nitro-2-propanol and the like can be preferably used.

Examples of chelate compounds include ethylenediaminetetraacetic acid, potassium salt thereof, sodium salt thereof; diethylenetriaminepentaacetic acid, potassium salt thereof, sodium salt thereof; triethylenetetraminehexaacetic acid, potassium salt thereof, sodium salt thereof, and hydroxyethylethylenediaminetriacetic acid. Nitrilotriacetic acid, sodium salt; 1-hydroxyethane-1,1-diphosphonic acid, potassium salt, sodium salt; aminotri (methylenephosphonic acid), potassium salt, sodium salt And organic phosphonic acids and phosphonoalkanetricarboxylic acids. Organic amine salts are also effective in place of the sodium and potassium salts of the chelating agents.

As the antifoaming agent, a general silicone-based self-emulsifying type, emulsifying type, nonionic surfactant having a HLB of 5 or less can be used. Silicone defoamers are preferred.
Among them, emulsification dispersion type and solubilization can be used.

  Examples of organic acids include citric acid, acetic acid, succinic acid, malonic acid, salicylic acid, caprylic acid, tartaric acid, malic acid, lactic acid, levulinic acid, p-toluenesulfonic acid, xylenesulfonic acid, phytic acid, and organic phosphonic acid. . The organic acid can also be used in the form of its alkali metal salt or ammonium salt.

  Examples of inorganic acids and inorganic salts include phosphoric acid, metaphosphoric acid, primary ammonium phosphate, secondary ammonium phosphate, primary sodium phosphate, secondary sodium phosphate, primary potassium phosphate, secondary potassium phosphate, Examples include sodium tripolyphosphate, potassium pyrophosphate, sodium hexametaphosphate, magnesium nitrate, sodium nitrate, potassium nitrate, ammonium nitrate, sodium sulfate, potassium sulfate, ammonium sulfate, sodium sulfite, ammonium sulfite, sodium hydrogen sulfate, nickel sulfate and the like.

  The developer described above can be used as a developer and developer replenisher for the exposed negative lithographic printing plate precursor, and is preferably applied to an automatic processor described later. When developing using an automatic processor, the developing solution becomes fatigued according to the amount of processing, so the processing capability may be restored using a replenisher or a fresh developer. This replenishing method is also preferably applied to the lithographic printing plate making method of the present invention.

  The development treatment with an aqueous solution having a pH of 2 to 10 in the present invention can be preferably carried out by an automatic processor equipped with a developer supply means and a rubbing member. As an automatic processor, for example, an automatic processor described in JP-A-2-220061 and JP-A-60-59351, which performs a rubbing process while transporting a lithographic printing plate precursor after image recording, or a cylinder Examples thereof include an automatic processor described in US Pat. Nos. 5,148,746, 5,568,768 and British Patent 2,297,719, which rub the lithographic printing plate precursor after image recording set thereon while rotating a cylinder. Among these, an automatic processor using a rotating brush roll as the rubbing member is particularly preferable.

The rotating brush roll that can be preferably used in the present invention can be appropriately selected in consideration of the difficulty of scratching the image area and the stiffness of the support of the lithographic printing plate precursor. As the rotating brush roll, a known one formed by planting a brush material on a plastic or metal roll can be used. For example, as described in Japanese Patent Application Laid-Open No. 58-159533, Japanese Patent Application Laid-Open No. 3-100554, or Japanese Utility Model Publication No. 62-167253, metal or plastic in which brush materials are implanted in rows. A brush roll can be used in which the groove mold material is radially wound around a plastic or metal roll as a core without a gap.
The brush material includes plastic fibers (for example, polyesters such as polyethylene terephthalate and polybutylene terephthalate, polyamides such as nylon 6.6 and nylon 6.10, polyacrylonitrile, poly (meth) acrylate, etc. Acrylic and polyolefin synthetic fibers such as polypropylene and polystyrene) can be used. For example, the fiber has a hair diameter of 20 to 400 μm and a hair length of 5 to 30 mm. Can be used.
Furthermore, the outer diameter of the rotating brush roll is preferably 30 to 200 mm, and the peripheral speed at the tip of the brush rubbing the plate surface is preferably 0.1 to 5 m / sec.
Moreover, it is preferable to use two or more rotating brush rolls.

  The rotating direction of the rotating brush roll used in the present invention may be the same or opposite to the conveying direction of the planographic printing plate precursor of the present invention. Thus, when two or more rotating brush rolls are used, it is preferable that at least one rotating brush roll rotates in the same direction and at least one rotating brush roll rotates in the opposite direction. This further ensures the removal of the heat sensitive layer in the non-image area. Furthermore, it is also effective to swing the rotating brush roll in the direction of the rotation axis of the brush roll.

  Although the temperature of the developer can be used at any temperature, it is preferably 10 ° C to 50 ° C.

  In the present invention, the lithographic printing plate after the rubbing treatment can be optionally washed with water, dried and desensitized. In the desensitizing treatment, a known desensitizing solution can be used.

  In addition, as the plate-making process of the lithographic printing plate from the lithographic printing plate precursor according to the present invention, the entire surface may be heated before exposure, during exposure, and between exposure and development, if necessary. By such heating, the image forming reaction in the photosensitive layer is promoted, and advantages such as improvement in sensitivity and printing durability and stabilization of sensitivity may occur. Further, for the purpose of improving the image strength and printing durability, it is also effective to subject the developed image to full post heating or full exposure. Usually, the heating before development is preferably performed under a mild condition of 150 ° C. or less. If the temperature is too high, problems such as covering up to the non-image area occur. Very strong conditions are used for heating after development. Usually, it is the range of 200-500 degreeC. If the temperature is low, sufficient image strengthening action cannot be obtained. If the temperature is too high, problems such as deterioration of the support and thermal decomposition of the image area occur.

Prior to the above development processing, the lithographic printing plate precursor is exposed through a transparent original image having a line image, a halftone dot image or the like, or imagewise exposed by laser beam scanning or the like using digital data.
A desirable wavelength of the light source is 350 nm to 450 nm, and specifically, an InGaN semiconductor laser is suitable. The exposure mechanism may be any of an internal drum system, an external drum system, a flat bed system, and the like.

Other exposure light beams that can be used in the present invention include ultrahigh pressure, high pressure, medium pressure, and low pressure mercury lamps, chemical lamps, carbon arc lamps, xenon lamps, metal halide lamps, various visible and ultraviolet laser lamps, fluorescent lamps, and the like. A lamp, a tungsten lamp, sunlight, etc. can also be used.
The following can be used as an available laser light source having a wavelength of 350 nm to 450 nm.
As a gas laser, an Ar ion laser (364 nm, 351 nm, 10 mW to 1 W), a Kr ion laser (356 nm, 351 nm, 10 mW to 1 W), a He—Cd laser (441 nm, 325 nm, 1 mW to 100 mW), and a solid laser as Nd: YAG (YVO ₄ ) and SHG crystal × 2 combinations (355 nm, 5 mW to 1 W), Cr: LiSAF and SHG crystal combination (430 nm, 10 mW), as a semiconductor laser system, KNbO ₃ ring resonator (430 nm, 30 mW), Combination of waveguide type wavelength conversion element and AlGaAs / InGaAs semiconductor (380 nm to 450 nm, 5 mW to 100 mW), combination of waveguide type wavelength conversion element and AlGaInP, AlGaAs semiconductor (300 nm to 350 nm, 5 mW to 100 mW) ), AlGaInN (350 nm to 450 nm, 5 mW
In addition, N ₂ laser (337 nm, pulse 0.1 to 10 mJ), XeF (351 nm, pulse 10 to 250 mJ) as a pulse laser. In particular, an AlGaInN semiconductor laser (commercially available InGaN-based semiconductor laser 400 to 410 nm, 5 to 30 mW) is preferable in terms of wavelength characteristics and cost.

Further, as the lithographic printing plate exposure apparatus of the scanning exposure method, there are an inner drum method, an outer drum method, and a flat bed method as an exposure mechanism, and a light source that can continuously oscillate among the light sources can be preferably used. . Practically, the following exposure apparatus is particularly preferable in terms of the relationship between the photosensitive material sensitivity and the plate making time.
・ Single beam to triple beam exposure equipment that uses one or more gas lasers or solid-state laser light sources so that it becomes a semiconductor laser with a total output of 20 mW or more with an internal drum system. ・ A total output of 20 mW or more with a flat bed system. Multi-beam (1 to 10) exposure equipment that uses one or more semiconductor lasers, gas lasers, or solid-state lasers • Use one or more semiconductor lasers, gas lasers, or solid-state lasers to achieve a total output of 20 mW or more with the external drum system Multi-beam (1 to 9) exposure apparatus ・ Multi-beam (10 or more) exposure apparatus using one or more semiconductor lasers or solid-state lasers so that the total output is 20 mW or more by the external drum system.

In the laser direct-drawing lithographic printing plate as described above, the photosensitive material sensitivity X (J / cm ² ), the photosensitive material exposure area S (cm ² ), the power q (W) of one laser light source, the laser Equation (eq1) is established between the number n and the total exposure time t (s).

  X · S = n · q · t (eq 1)

i) In the case of the internal drum (single beam) system, the laser rotation speed f (radians / s), the sub-scanning length Lx (cm) of the photosensitive material, the resolution Z (dots / cm), and the total exposure time t (s) In general, equation (eq 2) holds.

  f · Z · t = Lx (eq 2)

ii) External drum (multi-beam) system Drum rotation speed F (radians / s), photosensitive material sub-scanning length Lx (cm), resolution Z (dots / cm), total exposure time t (s), number of beams In general, formula (eq 3) is established during (n).

  F.Z.n.t = Lx (eq 3)

iii) Flat head (multi-beam) system Polygon mirror rotation speed H (radians / s), photosensitive material sub-scanning length Lx (cm), resolution Z (dots / cm), total exposure time t (s), Equation (eq 4) is generally established between the number of beams (n).

  F.Z.n.t = Lx (eq 4)

Resolution (2560 dpi) required for the actual printing plate, plate size (A1 / B1, sub-scan length 42 inch), exposure conditions of about 20 sheets / hour and photosensitive characteristics of the planographic printing plate precursor of the present invention (photosensitive wavelength, By substituting (sensitivity: about 0.1 mJ / cm ² ) into the above formula, it is understood that a combination with a multi-beam exposure method using a laser having a total output of 20 mW or more is particularly preferable in the planographic printing plate precursor of the present invention. it can. Further, by combining operability, cost, etc., a combination with an external drum type semiconductor laser multi-beam (10 or more) exposure apparatus is most preferable.

  EXAMPLES Hereinafter, although an Example demonstrates this invention in detail, this invention is not limited to these.

(Production of support)
In order to remove rolling oil on the surface of an aluminum plate (material 1050) having a thickness of 0.3 mm, a degreasing treatment was performed at 50 ° C. for 30 seconds using a 10 mass% sodium aluminate aqueous solution, and then the hair diameter was 0.3 mm. The aluminum surface was grained using three bundle-planted nylon brushes and a pumice-water suspension (specific gravity 1.1 g / cm ³ ) having a median diameter of 25 μm and washed thoroughly with water. This plate was etched by being immersed in a 25 mass% sodium hydroxide aqueous solution at 45 ° C for 9 seconds, washed with water, further immersed in 20 mass% nitric acid at 60 ° C for 20 seconds, and washed with water. At this time, the etching amount of the grained surface was about 3 g / m ² .

Next, an electrochemical roughening treatment was performed continuously using an alternating voltage of 60 Hz. The electrolytic solution at this time was a 1% by mass nitric acid aqueous solution (containing 0.5% by mass of aluminum ions) and a liquid temperature of 50 ° C. The AC power source waveform is electrochemical roughening treatment using a trapezoidal rectangular wave alternating current with a time ratio TP of 0.8 msec until the current value reaches a peak from zero, a duty ratio of 1: 1, and a trapezoidal rectangular wave alternating current. Went. Ferrite was used for the auxiliary anode. The current density was 30 A / dm ² at the peak current value, and 5% of the current flowing from the power source was shunted to the auxiliary anode. The amount of electricity in nitric acid electrolysis was 175 C / dm ² when the aluminum plate was the anode. Then, water washing by spraying was performed.

Next, a 0.5% by mass hydrochloric acid aqueous solution (containing 0.5% by mass of aluminum ions) and an electrolytic solution having a liquid temperature of 50 ° C. and nitric acid electrolysis under the condition of an electric quantity of 50 C / dm ² when the aluminum plate is an anode In the same manner as above, an electrochemical surface roughening treatment was performed, followed by washing with water by spraying. The plate was provided with a direct current anodized film of 2.5 g / m ² at a current density of 15 A / dm ² using 15% by mass sulfuric acid (containing 0.5% by mass of aluminum ions) as an electrolytic solution, then washed with water and dried.
The center line average roughness (Ra) of the support thus obtained was measured using a needle having a diameter of 2 μm and found to be 0.51 μm.

Furthermore, after applying the following undercoat liquid (1) with a bar, it was oven-dried at 80 ° C. for 10 seconds to apply a dry coating amount of 10 mg / m ² , and a support having an undercoat layer used in the following experiments. Produced.

<Undercoat liquid (1)>
・ Undercoat compound (1) 0.012 g
・ Hosmer PE (Unichemical Co., Ltd.) 0.005g
・ Methanol 9.00 g
・ Water 1.00g

[Preparation of lithographic printing plate precursors (1) to (5)]
A photosensitive layer coating solution (1) having the following composition using the sensitizing dyes and polymerization initiators shown in Table 1 was bar-coated on the support provided with the above-mentioned undercoat layer, and then at 70 ° C. for 60 seconds. Oven-dried to form a photosensitive layer having a dry coating amount of 1.2 g / m ² , and a protective layer coating solution (1) having the following composition is formed thereon so that the dry coating amount is 0.75 g / m ^2. After applying using a bar, it was dried at 125 ° C. for 70 seconds to obtain lithographic printing plate precursors (1) to (5).

<Photosensitive layer coating solution (1)>
・ The following binder polymer (1) (average molecular weight 80,000) 0.54 g
・ Polymerizable compound 0.48g
(Dipentaerythritol pentaacrylate, Nippon Kayaku Co., Ltd., SR399E)
-The following sensitizing dye (1) (absorption maximum wavelength; 359 nm) 0.06 g
・ The following polymerization initiator (1) 0.18 g
・ The following chain transfer agent (1) 0.02 g
・ Oil-soluble phthalocyanine Xg shown in Table 1
・ Thermal polymerization inhibitor 0.01g
N-nitrosophenylhydroxylamine aluminum salt ・ The following water-soluble fluorosurfactant (1) 0.001 g
・ Polyoxyethylene-polyoxypropylene condensate 0.04g
(Asahi Denka Kogyo Co., Ltd., Pluronic L44)
・ Tetraethylamine hydrochloride 0.01g
・ 3.5 g of 1-methoxy-2-propanol
・ Methyl ethyl ketone 8.0g

<Protective layer coating solution (1)>
・ The following mica dispersion (1) 13.0 g
Polyvinyl alcohol (saponification degree 98 mol%, polymerization degree 500) 1.3 g
-Sodium 2-ethylhexyl sulfosuccinate 0.2g
・ Poly (vinyl pyrrolidone / vinyl acetate (1/1)) molecular weight 70,000 g
・ Surfactant (Emalex 710, manufactured by Nippon Emulsion Co., Ltd.) 0.05g
・ 133g of water

(Preparation of mica dispersion (1))
To 368 g of water, 32 g of synthetic mica (“Somasif ME-100”: manufactured by Co-op Chemical Co., Ltd., aspect ratio: 1000 or more) is added and dispersed using an homogenizer until the average particle size (laser scattering method) becomes 0.5 μm. A mica dispersion (1) was obtained.

Further, when the oxygen permeability of the protective layer was measured under the same conditions as described above, the oxygen permeability of the protective layer was 2.0 ml / (m ² · day · atom).

[Preparation of comparative planographic printing plate precursor (1 ')]
Instead of oil-soluble phthalocyanine in the photopolymerizable composition, 0.4 g of the following pigment composition was added to prepare a lithographic printing plate precursor (1 ′).

<Pigment composition>
Pigment Blue 15: 6 15 parts by mass Allyl methacrylate / methacrylic acid copolymer 10 parts by mass (copolymerization molar ratio 83/17) Thermal polymerization Cyclohexanone 15 parts by mass Methoxypropyl acetate 20 parts by mass Propylene glycol monomethyl ether 40 parts by mass

[Examples 1 to 5, Comparative Example 1]
(1) Preparation of lithographic printing plate and evaluation of development residue Each of the lithographic printing plate precursors was subjected to imagewise exposure using a 405 nm semiconductor laser having an output of 100 mW while changing the energy density.
Thereafter, the developing solution (1) having the following composition was used, and development processing was carried out with an automatic developing processor having a structure shown in FIG. The pH of the developer was about 5. The automatic developing processor is an automatic processor having two rotating brush rolls. As the rotating brush roll, the first brush roll is made of polybutylene terephthalate fiber (hair diameter: 200 μm, hair length: 17 mm). Using a brush roll with an outer diameter of 90 mm implanted with 200 mm / min in the same direction as the conveying direction (peripheral speed 0.94 m / sec at the tip of the brush), the second brush roll is made of polybutylene terephthalate Using a brush roll having an outer diameter of 60 mm in which fibers (hair diameter: 200 μm, hair length: 17 mm) were implanted, it was rotated 200 times per minute in the direction opposite to the conveying direction (peripheral speed of the brush tip: 0.63 m / sec). . The planographic printing plate precursor was transported at a transport speed of 100 cm / min.
The developer was showered from the spray pipe with a circulation pump and supplied to the plate surface. The tank capacity of the developer was 10 liters.

Developer (1)
・ Water 100g
・ Sodium alkylnaphthalenesulfonate 5g
(Perox NB-L manufactured by Kao Corporation)
・ 1g gum arabic
・ Primary ammonium phosphate 0.05g
・ Citric acid 0.05g
・ Ethylenediaminetetraacetate tetrasodium salt 0.05g

The lithographic printing plate precursor was treated with 20 m ² per day for a total of 200 m ^{2 for} 10 days, and after 10 days, deposits (development residue) in the developing bath were observed.

(2) Evaluation of printing durability The lithographic printing plate obtained after the development described above uses R201 manufactured by Roland as a printing machine, and GEOS-G (N) manufactured by Dainippon Ink & Chemicals, Inc. as the ink. And printed it. The printing portion of the solid image was observed, and the printing durability was examined based on the number of images where the image began to fade. The larger the number, the better the printing durability. The results are shown in Table 2 below.

  From the above results, in the method for preparing a lithographic printing plate using a developer having a pH of 2 to 10, in the comparative example using a pigment-containing lithographic printing plate precursor, precipitation occurs in the developing bath and the printing durability is not good. Whereas it was sufficient, in the example using the lithographic printing plate precursor containing oil-soluble phthalocyanine, it is clear that precipitation in the developing bath does not occur and the printing durability is excellent.

Structure of automatic processor

Explanation of symbols

1: rotating brush roll 2: receiving roll 3: transport roll 4: transport guide plate 5: spray pipe 6: pipeline 7: filter 8: plate supply table 9: plate discharge table 10: developer tank 11: circulation pump 12: plate

Claims (8)

  A lithographic printing plate precursor having a photosensitive layer containing at least one oil-soluble phthalocyanine compound, a hydrophobic binder polymer having an acid value of 0.3 meq / g or less, and a protective layer on a support having a hydrophilic surface After the exposure, the protective layer and the photosensitive layer in the non-exposed area are removed in the presence of a developer having a pH of 2 to 10 by an automatic processor equipped with a rubbing member. Method.   2. The method of preparing a lithographic printing plate according to claim 1, wherein a part or all of the photosensitive layer component is contained in a microcapsule or a microgel.   3. The method for producing a lithographic printing plate according to claim 1, further comprising a chain transfer agent in the photosensitive layer. The method for producing a lithographic printing plate according to any one of claims 1 to 3, wherein the chain transfer agent is a thiol compound represented by the following general formula (I).
(In the general formula (I), R represents an alkyl group which may have a substituent or an aryl group which may have a substituent, and A represents a 5-membered carbon atom together with an N = CN moiety. Represents an atomic group forming a ring or a 6-membered heterocycle, and A may further have a substituent.   The method for preparing a lithographic printing plate according to any one of claims 1 to 4, wherein the pH of the developer is from 3 to 8.   The method for producing a lithographic printing plate according to any one of claims 1 to 5, wherein the developer contains a water-soluble polymer.   The lithographic printing plate precursor according to any one of claims 1 to 6, wherein the lithographic printing plate precursor has an undercoat layer containing a polymer compound having a polymerizable group.   A lithographic printing plate precursor comprising a photosensitive layer containing at least one oil-soluble phthalocyanine compound and a hydrophobic binder polymer having an acid value of 0.3 meq / g or less, and a protective layer on a support having a hydrophilic surface. After the laser exposure at a wavelength of 350 to 450 nm, the plate surface is rubbed with a rubbing member in the presence of a developer having a pH of 2 to 10 by an automatic processor equipped with a rubbing member, thereby exposing the protective layer and the non-exposed portion. A lithographic printing plate precursor, wherein the layer can be removed.