JP2007152756A - Information hiding postcard - Google Patents
Information hiding postcard Download PDFInfo
- Publication number
- JP2007152756A JP2007152756A JP2005351500A JP2005351500A JP2007152756A JP 2007152756 A JP2007152756 A JP 2007152756A JP 2005351500 A JP2005351500 A JP 2005351500A JP 2005351500 A JP2005351500 A JP 2005351500A JP 2007152756 A JP2007152756 A JP 2007152756A
- Authority
- JP
- Japan
- Prior art keywords
- adhesive layer
- postcard
- piece
- rubber latex
- information
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、情報隠蔽葉書に関し、更に詳しくは、弱圧で情報の隠蔽が可能な情報隠蔽葉書に関する。 The present invention relates to an information hiding postcard, and more particularly to an information hiding postcard capable of hiding information with low pressure.
近年、銀行、クレジット会社、官公庁等より個人宛に各個人の預金状況、残高情報、年金情報等を通知する手段として「親展はがき」が使用されている。かかる親展はがきに使用される用紙は、その情報記載面に、感圧接着剤が塗工されており、低い圧力では全く接着しないが、所定圧力以上で圧着すると接着するよう構成されている(特許文献1,2)。
In recent years, “confidential postcards” have been used as means for notifying individual individuals of their deposit status, balance information, pension information, etc. from banks, credit companies, government offices, and the like. The paper used for such confidential postcards is coated with a pressure-sensitive adhesive on its information description surface, and does not adhere at all at low pressures, but is configured to adhere when pressed over a predetermined pressure (patent)
しかし、従来の感圧接着剤は、接着に比較的高い圧力を要するため、接着にはドライシーラー等の圧着装置が必要であり、用途が限られていた。 However, since the conventional pressure-sensitive adhesive requires a relatively high pressure for bonding, a bonding device such as a dry sealer is required for bonding, and its application is limited.
本発明は、大規模な圧着装置を必要とせず、手でこする程度の弱圧でも情報の隠蔽が可能な情報隠蔽葉書を提供することを目的とする。 An object of the present invention is to provide an information concealment postcard which does not require a large-scale crimping apparatus and can conceal information even with a low pressure of rubbing by hand.
すなわち、本発明の情報隠蔽葉書は、情報記入領域を有する葉書片と、前記葉書片の一辺に連接され、少なくとも前記情報記入領域を隠蔽する隠蔽片と、前記隠蔽片の少なくとも前記葉書片と連接された辺と対向する辺に沿って形成された第一接着層と前記葉書片の該第一接着層と対向する位置に形成された第二接着層とからなる接着層と、前記葉書片と前記隠蔽片の少なくとも一方の前記接着層形成領域以外の領域に形成された擬似接着層とを有する情報隠蔽葉書であって、前記接着層が、アクリル変性天然ゴムラテックスと、過酸化物前加硫ラテックスと、合成ゴムラテックスとを含有する感圧接着剤組成物を塗布形成してなる層であることを特徴とする。 That is, the information concealment postcard of the present invention includes a postcard piece having an information entry area, a concealment piece contiguous to one side of the postcard piece and concealing at least the information entry area, and a concatenation piece connected to at least the postcard piece of the concealment piece. An adhesive layer comprising a first adhesive layer formed along a side facing the formed side and a second adhesive layer formed at a position facing the first adhesive layer of the postcard piece; and the postcard piece; An information concealment postcard having a pseudo adhesive layer formed in a region other than the adhesive layer forming region of at least one of the concealing pieces, wherein the adhesive layer comprises an acrylic-modified natural rubber latex and a pre-peroxide vulcanization It is a layer formed by applying and forming a pressure-sensitive adhesive composition containing latex and synthetic rubber latex.
本発明の情報隠蔽葉書の接着層は、弱圧での接着が可能であり、例えば、硬貨、ペン先等を用いて比較的強めに数回こする程度で接着することができる。そのため、接着にドライシーラー等の圧着装置を必要としない。 The adhesive layer of the information hiding postcard of the present invention can be bonded with low pressure, for example, it can be bonded with a relatively strong rubbing several times using a coin, a nib or the like. Therefore, a pressure bonding device such as a dry sealer is not required for bonding.
また、本発明の情報隠蔽葉書の接着層は、通常状態では接着しないため、接着層を剥離紙等で保護する必要がなく、コストダウンを図れる。 Further, since the adhesive layer of the information concealment postcard of the present invention does not adhere in a normal state, it is not necessary to protect the adhesive layer with a release paper or the like, and cost can be reduced.
また、本発明の情報隠蔽葉書の接着層は、一旦接着した後は基材(葉書片、隠蔽片)を破ることなく剥離することはできない。 In addition, the adhesive layer of the information hiding postcard of the present invention cannot be peeled off without tearing the base material (postcard piece, hiding piece) once bonded.
一方、本発明の情報隠蔽葉書の擬似接着層は、一旦接着した後に剥離することが可能であり、その後は、再度加圧しても再び接着することはないが、基材を破ることなく剥離することが可能である。また、接着層を形成する感圧接着剤組成物の接着力を調整した組成物により形成した擬似接着層は、接着層と同様に、剥離紙等で保護する必要がなく、弱圧での接着が可能である。また、透明であり、基材に印刷された文字等を視認できるし、擬似接着層自体が印刷適性を有するため、擬似接着層表面に印刷することも可能である。 On the other hand, the pseudo-adhesion layer of the information concealment postcard of the present invention can be peeled off after being bonded once. After that, it does not adhere again even if it is pressed again, but peels off without breaking the substrate. It is possible. In addition, the pseudo-adhesive layer formed by the composition in which the adhesive force of the pressure-sensitive adhesive composition forming the adhesive layer is adjusted does not need to be protected with release paper or the like as in the case of the adhesive layer. Is possible. Moreover, since it is transparent and the character etc. which were printed on the base material can be visually recognized and the pseudoadhesion layer itself has printability, it is also possible to print on the surface of the pseudoadhesion layer.
以下、本発明の情報隠蔽用紙について、図面を用いて説明する。 Hereinafter, the information hiding paper of the present invention will be described with reference to the drawings.
図1は、本発明の二つ折り葉書の一例を示す図であり、図1(a)は平面図、図1(b)は隠蔽片で情報記入領域を隠蔽している状態を示す斜視図である。 1A and 1B are diagrams showing an example of a two-fold postcard according to the present invention. FIG. 1A is a plan view, and FIG. 1B is a perspective view showing a state where an information entry area is concealed by a concealing piece. is there.
図1において、1は情報記入領域2を有する葉書片、3は葉書片1の一辺に連接され、少なくとも情報記入領域2を隠蔽する隠蔽片、6は擬似接着層、7は折り線であり、接着層は、第一接着層4と第二接着層5からなる。
In FIG. 1, 1 is a postcard piece having an
図1に示す示す様に、第一接着層4は、葉書片1と隠蔽片3が連接された辺(折り線7)と対向する辺に沿って形成されている。第一接着層4の形成位置は、図1に示す位置に限定されないが、隠蔽片3の情報記入領域2と対向する領域以外の領域に形成することが好ましい。第二接着層5は、折り線7にて折り曲げた際に第一接着層4と対向する位置に形成されている。第二接着層5の形成位置は、第一接着層4と対向する位置であればよく、例えば、隠蔽片3の折り線7と直行する辺の長さが葉書片1のそれより長い場合には、葉書片1の裏側に形成すればよい。接着層は通常状態では接着しないため、接着層を剥離紙等で保護する必要はない。
As shown in FIG. 1, the first
擬似接着層6は、隠蔽片3の第一接着層4を形成した領域以外のほぼ全面に形成されている。擬似接着層6の形成位置は、図1に示す位置に限定されず、葉書片1に設けてもよい。接着層を形成する感圧接着剤組成物と同様の組成物で形成した擬似接着層6は、通常状態では接着しないため、擬似接着層6を剥離紙等で保護する必要はない。
The pseudo
本発明の二つ折り葉書は、図1(b)に示す様に、隠蔽片3を折り線7にて折り曲げて情報記入領域2を隠蔽する。そして、擬似接着層6を接着するのに必要な圧力を加えた後、隠蔽片3の接着層に対応する位置を中心に、硬貨、ペン先等を用いて比較的強めに数回こする程度の弱圧を加え、隠蔽片3を葉書片1に接着する。擬似接着層6が、接着層を形成する感圧接着剤組成物と同様の組成物で形成した層である場合には、圧着装置を用いる必要はなく、弱圧で隠蔽片3を葉書片1に接着することができる。
In the two-fold postcard of the present invention, the
隠蔽片3は、剥離することが可能であり、一旦剥離すると再度加圧しても再び接着することはない。しかも、隠蔽片3を剥離する際に、擬似接着層6の部分は、葉書片1及び隠蔽片3を破ることなく、情報記入領域2に記入された情報を視認することができる。一方、接着層の部分は、葉書片1または隠蔽片3を破ることなく剥離することはできず、無理に剥離した場合には、剥離した痕跡が残る程度に葉書片1または隠蔽片3が破れる。従って、郵送中に故意にあるいは誤って、隠蔽片3が剥離されることを防止できる。尚、隠蔽片3を、葉書片1または隠蔽片3自身を破ることなく剥離できるように、予め、切取りミシン目を設けるなどして第一接着層4と第二接着層5が接着した個所を切り離すようにしておいてもよい。
The
接着層は、アクリル変性天然ゴムラテックスと、過酸化物前加硫ラテックスと、合成ゴムラテックスとを含有する感圧接着剤組成物を塗布形成してなる層である。また、擬似接着層6は、アクリル変性天然ゴムラテックスと、過酸化物前加硫ラテックスと、合成ゴムラテックスとを含有する感圧接着剤組成物を塗布形成してなる層であることが好ましく、該感圧接着剤組成物に更にでん粉を含有する感圧接着剤組成物を塗布形成してなる層であることがより好ましい。
The adhesive layer is a layer formed by applying and forming a pressure-sensitive adhesive composition containing an acrylic-modified natural rubber latex, a pre-peroxide vulcanized latex, and a synthetic rubber latex. The
アクリル変性天然ゴムラテックスは、天然ゴムラテックスをアクリル系単量体でグラフとしたラテックスである。アクリル系単量体としては、例えばアクリル酸メチル、アクリル酸n−ブチル、アクリル酸ヘキシル、メタクリル酸メチル等が挙げられ、これらのうちでもメタクリル酸メチルが好ましい。また、グラフト化の度合いは、天然ゴム比5〜50重量%であることが好ましい。 The acrylic modified natural rubber latex is a latex obtained by graphing natural rubber latex with acrylic monomers. Examples of the acrylic monomer include methyl acrylate, n-butyl acrylate, hexyl acrylate, and methyl methacrylate. Among these, methyl methacrylate is preferable. The degree of grafting is preferably 5 to 50% by weight relative to the natural rubber.
過酸化物前加硫ラテックスは、天然ゴムラテックスを過酸化物で前加硫したラテックスである。過酸化物としては、例えばベンゾイルパーオキシド、ジt−ブチルパーオキシジイソプロピルベンゼン、t−ブチルハイドロパーオキシド等が挙げられ、これらのうちでもt−ブチルハイドロオキシドが、反応時のラテックス分散性、安定性に優れていることが知られている。 Peroxide pre-cured latex is a latex obtained by pre-curing natural rubber latex with peroxide. Examples of peroxides include benzoyl peroxide, di-t-butylperoxydiisopropylbenzene, and t-butyl hydroperoxide. Among these, t-butyl hydroxide is latex dispersibility and stability during the reaction. It is known to be excellent in properties.
合成ゴムラテックスとしては、例えば、スチレン−ブタジエンゴムラテックス、アクリロニトリル−ブタジエンゴムラテックス、ブタジエンゴムラテックス、クロロプレンゴムラテックス、ウレタンゴムラテックス等々が挙げられる。 Examples of the synthetic rubber latex include styrene-butadiene rubber latex, acrylonitrile-butadiene rubber latex, butadiene rubber latex, chloroprene rubber latex, urethane rubber latex, and the like.
アクリル変性天然ゴムラテックス(樹脂固形分)と過酸化物前加硫ラテックス(樹脂固形分)の合計量と、合成ゴムラテックス(樹脂固形分)との配合比率(アクリル変性天然ゴムラテックス(樹脂固形分)と過酸化物前加硫ラテックス(樹脂固形分)の合計量:合成ゴムラテックス(樹脂固形分))は、重量比で60:40〜90:10であることが好ましく、より好ましくは70:30〜85:15である。アクリル変性天然ゴムラテックスと過酸化物前加硫ラテックスの合計量がこの範囲より多すぎると(合成ゴムラテックスがこの範囲より少なすぎると)、基材への密着性、剥離時の凝集力が不足する傾向があり、アクリル変性天然ゴムラテックスと過酸化物前加硫ラテックスの合計量がこの範囲より少なすぎると(合成ゴムラテックスがこの範囲より多すぎると)、接着力が低下する傾向がある。 The blending ratio of acrylic modified natural rubber latex (resin solids) and pre-peroxide vulcanized latex (resin solids) to synthetic rubber latex (resin solids) (acrylic modified natural rubber latex (resin solids) ) And pre-peroxide vulcanized latex (resin solid content): the synthetic rubber latex (resin solid content)) is preferably 60:40 to 90:10 by weight, more preferably 70: 30-85: 15. If the total amount of acrylic-modified natural rubber latex and pre-peroxide vulcanized latex is too much above this range (if the synthetic rubber latex is too much below this range), adhesion to the substrate and cohesive force at the time of peeling will be insufficient. If the total amount of the acrylic modified natural rubber latex and the pre-peroxide vulcanized latex is too smaller than this range (if the synthetic rubber latex is more than this range), the adhesive force tends to decrease.
また、アクリル変性天然ゴムラテックス(樹脂固形分)と過酸化物前加硫ラテックス(樹脂固形分)との配合比率(アクリル変性天然ゴムラテックス:過酸化物前加硫ラテックス)は、重量比で10:90〜90:10であることが好ましく、より好ましくは20:80〜30:70であるが、擬似接着層6を形成する場合は80:20〜70:30であることがより好ましい。アクリル変性天然ゴムラテックスがこの範囲より多すぎると(過酸化物前加硫ラテックスがこの範囲より少なすぎると)、接着に要する圧力が高くなる傾向があり、アクリル変性天然ゴムラテックスがこの範囲より少なすぎると(過酸化物前加硫ラテックスがこの範囲より多すぎると)、剥離が困難になる傾向があり、無理に剥離すると基材の破損を生じる可能性がある。
The blending ratio (acrylic modified natural rubber latex: peroxide precured latex) of the acrylic modified natural rubber latex (resin solid content) and the pre-peroxide vulcanized latex (resin solid content) is 10 by weight. Is preferably 90:90:10, more preferably 20: 80-30: 70, but more preferably 80: 20-70: 30 when the
感圧接着剤組成物中のアクリル変性天然ゴムラテックス(樹脂固形分)と過酸化物前加硫ラテックス(樹脂固形分)と合成ゴムラテックス(樹脂固形分)との合計含有量は、好ましくは50〜70重量%、より好ましくは60〜70重量%である。合計含有量が50重量%未満では接着力が低下する傾向があり、70重量%を超えると剥離が困難になる傾向があり、無理に剥離すると基材の破損を生じる可能性がある。 The total content of acrylic-modified natural rubber latex (resin solid content), peroxide pre-vulcanized latex (resin solid content) and synthetic rubber latex (resin solid content) in the pressure-sensitive adhesive composition is preferably 50. It is -70 weight%, More preferably, it is 60-70 weight%. If the total content is less than 50% by weight, the adhesive strength tends to decrease, and if it exceeds 70% by weight, peeling tends to be difficult, and if it is peeled forcibly, the substrate may be damaged.
感圧接着剤組成物は、保存時の接着層または擬似接着層同士の接着を避ける為にアンチブロッキング剤を含有することが好ましい。 The pressure-sensitive adhesive composition preferably contains an anti-blocking agent in order to avoid adhesion between the adhesive layers or pseudo-adhesive layers during storage.
アンチブロッキング剤の含有量は、アクリル変性天然ゴムラテックス(樹脂固形分)と過酸化物前加硫ラテックス(樹脂固形分)と合成ゴムラテックス(樹脂固形分)との合計量100重量部に対し10〜50重量部であることが好ましく、10〜30重量部であることがより好ましい。アンチブロッキング剤の含有量が10重量部未満では保存時に接着層または擬似接着層同士が接着する可能性があり、50重量部を超えると接着力が低下する傾向がある。 The content of the anti-blocking agent is 10 with respect to 100 parts by weight of the total amount of acrylic modified natural rubber latex (resin solid content), pre-peroxide vulcanized latex (resin solid content), and synthetic rubber latex (resin solid content). It is preferably ˜50 parts by weight, and more preferably 10 to 30 parts by weight. If the content of the anti-blocking agent is less than 10 parts by weight, the adhesive layers or pseudo-adhesive layers may adhere to each other during storage, and if it exceeds 50 parts by weight, the adhesive strength tends to decrease.
アンチブロッキング剤としては、例えば、重炭酸カルシウム、軽炭酸カルシウム、タルク、ステアリン酸金属石けん、でん粉、シリカ等が挙げられる。これらのうちでも、接着層または擬似接着層形成後のレーザープリンターによる印刷等に対する耐熱性を向上せしめる為にシリカを含有させることが好ましい。また、擬似接着層6を形成する場合には、でん粉を含有させることが好ましく、その含有量は、好ましくはアンチブロッキング剤中40〜80重量%、より好ましくは50〜70重量%である。接着層6を形成する場合にもでん粉を含有させてもよいが、その含有量はアンチブロッキング剤中40重量%未満とすることが好ましく、より好ましくは20〜30重量%である。
Examples of the anti-blocking agent include calcium bicarbonate, light calcium carbonate, talc, metal stearate soap, starch, silica and the like. Among these, it is preferable to contain silica in order to improve heat resistance against printing by a laser printer after forming the adhesive layer or the pseudo adhesive layer. Moreover, when forming the
感圧接着剤組成物には、塗工適性を維持・向上せしめる為に、界面活性剤、消泡剤、増粘剤等の添加物を添加してもよい。界面活性剤としては、ノニオン界面活性剤とアニオン界面活性剤を併用することが好ましく、ノニオン界面活性剤としては、ポリオキシエチレンラウリルエーテル、ポリオキシエチレンスチレン化フェニルエーテル、ポリオキシエチレンアルキルエーテル等で、HLBが13.0〜19.0のもの、アニオン界面活性剤としては、アルキルベンゼンスルホン酸ナトリウム、高級アルコール硫酸エステルナトリウム、硫酸エステル系等を用いることができる。消泡剤としては非シリコン系消泡剤が接着力に影響をされずに好ましく、0.1〜0.5重量%程度添加することが好ましい。増粘剤はコーターの塗工適性上のため使用され、アクリル系、ポリアクリル酸、PVA、CMC等、セルローズ系増粘剤を用いることができるが、アクリル系増粘剤が粘度の経時変化も少なく好ましい。 In order to maintain and improve the coating suitability, additives such as a surfactant, an antifoaming agent, and a thickener may be added to the pressure-sensitive adhesive composition. As the surfactant, it is preferable to use a nonionic surfactant and an anionic surfactant in combination. Examples of the nonionic surfactant include polyoxyethylene lauryl ether, polyoxyethylene styrenated phenyl ether, and polyoxyethylene alkyl ether. As the anionic surfactant having an HLB of 13.0 to 19.0, sodium alkylbenzene sulfonate, sodium higher alcohol sulfate, sulfate ester or the like can be used. As the antifoaming agent, a non-silicon antifoaming agent is preferable without affecting the adhesive force, and it is preferable to add about 0.1 to 0.5% by weight. Thickeners are used for coater coating suitability, and acrylic, polyacrylic acid, PVA, CMC, etc., cellulose thickeners can be used, but acrylic thickeners also change in viscosity over time. Less preferred.
感圧接着剤組成物は、例えば、アクリル変性天然ゴムラテックスと過酸化物前加硫ラテックスとを配合し、要すれば界面活性剤を添加した後に、合成ゴムラテックスを配合し、要すればアンチブロッキング剤を添加し、更に必要に応じて消泡剤、増粘剤等の添加物を添加して混合することにより製造することができる。アンチブロッキング剤は、分散性をよくするために界面活性剤等の分散媒中に分散させて添加することが好ましい。 The pressure-sensitive adhesive composition is prepared by, for example, blending an acrylic-modified natural rubber latex and a pre-peroxide vulcanized latex, adding a surfactant if necessary, and then blending a synthetic rubber latex, It can be produced by adding a blocking agent and, if necessary, adding additives such as an antifoaming agent and a thickener and mixing them. The antiblocking agent is preferably added after being dispersed in a dispersion medium such as a surfactant in order to improve dispersibility.
擬似接着層6は、他の感圧接着剤組成物を用いて形成してもよいが、手でこする程度の弱圧で接着できる感圧接着剤組成物を用いることが好ましい。その様な感圧接着剤組成物としては、例えば、アクリルエステル樹脂45〜55重量%及びロジンエステル系樹脂10〜20重量%を含有する感圧接着剤組成物等が挙げられる。
The
接着層、擬似接着層6は、感圧接着剤組成物を、グラビアコーター、フレキソ、エアナイフコーター、バーコーターなどの塗布手段により塗布し、乾燥することにより形成できる。感圧接着剤組成物の塗布量は、接着性、剥離性、透明性等の観点より、好ましくは1〜5g/m2(固形分換算)、より好ましくは2〜3g/m2(固形分換算)である。
The adhesive layer and the
葉書片1、隠蔽片3としては、通常の紙の他に、合成紙、あるいはポリエチレン、ポリエチレンテレフタレート、ポリプロピレン、塩化ビニルなどの合成フィルムを用いることもできる。合成フィルムを用いる場合には、マット処理、コロナ処理などの表面処理を施すのが好ましい。
As the
図2は、本発明の部分二つ折り葉書の一例を示す図であり、図2(a)は平面図、図2(b)は隠蔽片で情報記入領域を隠蔽している状態を示す斜視図である。図2において、図1と同様の部材には図1と同一の符号を付し、詳細な説明は省略する。 2 is a diagram showing an example of a partially folded postcard according to the present invention. FIG. 2 (a) is a plan view, and FIG. 2 (b) is a perspective view showing a state where an information entry area is concealed by a concealing piece. It is. 2, the same members as those in FIG. 1 are denoted by the same reference numerals as those in FIG. 1, and detailed description thereof is omitted.
図3、図4は、本発明の部分二つ折り葉書の他の例を示す図であり、図3(a)は平面図、図3(b)は剥離紙で隠蔽片を保護している状態を示す斜視図、図4(a)は剥離紙を切り離した状態を示す平面図、図4(b)は隠蔽片で情報記入領域を隠蔽している状態を示す斜視図である。 3 and 4 are diagrams showing another example of the partially folded postcard of the present invention. FIG. 3 (a) is a plan view, and FIG. 3 (b) is a state in which the concealing piece is protected with release paper. 4A is a plan view showing a state where the release paper is cut off, and FIG. 4B is a perspective view showing a state where the information entry area is concealed by the concealing piece.
図3、図4において、8は剥離紙、9は切り取り線である。尚、図1と同様の部材には図1と同一の符号を付し、詳細な説明は省略する。 3 and 4, 8 is a release paper, and 9 is a cut line. The same members as those in FIG. 1 are denoted by the same reference numerals as those in FIG. 1, and detailed description thereof is omitted.
剥離紙8は、図3(a)に示す様に、隠蔽片3とほぼ同じ形状であり、隠蔽片3の一辺に連接されている。そして、図3(b)に示す様に、剥離紙8を、折り線7’にて折り曲げて、擬似接着層6を保護することができる。情報記入領域2に必要な情報を記入した後、図4(a)に示す様に、剥離紙8を剥がして、切り取り線9にて切り離す。その後、図4(b)に示す様に、隠蔽片3を、折り線7にて折り曲げて葉書片1に接着し、情報記入領域2を隠蔽することができる。
As shown in FIG. 3A, the
図3、図4に示す部分二つ折り葉書は、葉書製造時に、剥離剤を塗工することで剥離紙を形成することができ、擬似接着層6の保護に剥離紙が必要な場合に有用である。
The partially folded postcards shown in FIGS. 3 and 4 are useful when a release paper can be formed by applying a release agent at the time of postcard manufacture, and a release paper is required to protect the pseudo
以下、実施例により本発明を詳細に説明する。 Hereinafter, the present invention will be described in detail by way of examples.
<感圧接着剤組成物の製造>
表1に示す配合で各成分を混合し、ホモコロイドミキサーでよく撹拌して、感圧接着剤組成物を得た。尚、用いたラテックスは以下の通りである。
<Manufacture of pressure-sensitive adhesive composition>
Each component was mixed with the composition shown in Table 1, and stirred well with a homocolloid mixer to obtain a pressure-sensitive adhesive composition. The latex used is as follows.
(1)アクリル変性天然ゴムラテックス
「QY#25MG」(クォー・ユー化成(有)製)、樹脂固形分50wt%
(1) Acrylic-modified natural rubber latex “QY # 25MG” (manufactured by Qu Yu Kasei Co., Ltd.), resin solid content 50 wt%
(2)過酸化物前加硫ラテックス
「QY#055PC」(クォー・ユー化成(有)製)、樹脂固形分55wt%
(2) Pre-peroxide vulcanized latex “QY # 055PC” (manufactured by Qu Yu Kasei Co., Ltd.), resin solid content 55 wt%
(3)合成ゴムラテックス
「DL−620」(旭化成ケミカルズ(株)製)、ハイスチレンタイプ、樹脂固形分50wt%
(3) Synthetic rubber latex “DL-620” (manufactured by Asahi Kasei Chemicals Corporation), high styrene type, resin solid content 50 wt%
<実施例1>
表2に示す感圧接着剤組成物を用いて、図1に示す二つ折り葉書を作成した。すなわち、葉書片1及び隠蔽片3としての上質紙(110kg)に、バーコーターを用いて乾燥重量8〜10g/m2となるように、組成物No.1を塗工し、105℃×1分間熱風乾燥した後、25℃相対湿度50%で1時間放置して、第一接着層4及び第二接着層5を形成した。さらに、隠蔽片3に、バーコーターを用いて乾燥重量8〜10g/m2となるように、組成物No.3を塗工し、105℃×1分間熱風乾燥した後、25℃相対湿度50%で1時間放置して、擬似接着層6を形成した。
<Example 1>
Using the pressure-sensitive adhesive composition shown in Table 2, a bi-fold postcard shown in FIG. 1 was prepared. That is, the composition No. 1 was prepared on a high quality paper (110 kg) as the
得られた二つ折り葉書の隠蔽片3を、折り線7で折り曲げ、500円玉を縦にして14.71Nまでの荷重をかけて第一接着層4及び第二接着層5、擬似接着層6に対応する位置を1回なぞった際に、十分な接着力が得られる最低加重を測定すると共に、剥離速度300mm/minで剥離した際の葉書片1、隠蔽片3の状態を目視で観察した。
The
評価結果を表2に示す。 The evaluation results are shown in Table 2.
<実施例2、比較例1>
表2に示す感圧接着剤組成物を用いた以外は、実施例1と同様にして、図1に示す二つ折り葉書を作成し、評価した。評価結果を表2に示す。
<Example 2, Comparative Example 1>
A bi-fold postcard shown in FIG. 1 was prepared and evaluated in the same manner as in Example 1 except that the pressure-sensitive adhesive composition shown in Table 2 was used. The evaluation results are shown in Table 2.
1 葉書片
2 情報記入領域
3 隠蔽片
4 第一接着層
5 第二接着層
6 擬似接着層
7,7’ 折り線
8 剥離紙
9 切り取り線
1
Claims (9)