JP2007144097A - Golf ball - Google Patents
Golf ball Download PDFInfo
- Publication number
- JP2007144097A JP2007144097A JP2006022757A JP2006022757A JP2007144097A JP 2007144097 A JP2007144097 A JP 2007144097A JP 2006022757 A JP2006022757 A JP 2006022757A JP 2006022757 A JP2006022757 A JP 2006022757A JP 2007144097 A JP2007144097 A JP 2007144097A
- Authority
- JP
- Japan
- Prior art keywords
- golf ball
- cover
- weight
- ball according
- transparent thermoplastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、黄緑色、黄色又はオレンジ色として認識し得る色調に着色されたカバーを有するゴルフボールに関する。 The present invention relates to a golf ball having a cover colored in a color recognizable as yellowish green, yellow or orange.
ゴルフボールの最外層であるカバーは、一般的に白色であるが、カバーが黄色やオレンジ色等に着色されたゴルフボール(カラーボール)も市販されている。この種のカラーボールは、例えば、冬季にプレーする際に特に有効である。すなわち、冬季においてはフィールド上の芝生が枯れて白色を呈するが、カラーボールは、このように白色を呈した芝生上での視認性が白色ボールよりも良好であるからである。 The cover that is the outermost layer of the golf ball is generally white, but golf balls (color balls) in which the cover is colored yellow or orange are also commercially available. This type of color ball is particularly effective when played in winter, for example. That is, in the winter season, the lawn on the field withers and white, but the color ball has better visibility on the white lawn in this way than the white ball.
また、冬季以外であっても、他のプレーヤーと別色のカラーボールを使用することにより、該プレーヤーのボールと識別することが極めて容易となるという利点がある。 In addition, there is an advantage that it is very easy to distinguish from the player's ball by using a color ball of a different color from other players even in the winter season.
しかしながら、カラーボールの需要量はさほど多くはない。この点に関し、特許文献1では、一般的な白色ボールに対して著しく濃厚な色に着色されていることから、白色ボールに慣れたプレーヤーがカラーボールを使用すると、例えば、該プレーヤーがアドレス時に視覚的な違和感を覚えてしまうこと等が理由であると推察して、着色の度合いを小さくすることを提案している。すなわち、特許文献1においては、淡色ボールが開示されている。
However, the demand for color balls is not very large. In this regard, in
しかしながら、特許文献1に開示された淡色ボールは、その名が示す通り着色の度合いが小さいため、目視点からボールまでの距離が長いと、白色ボールと見分けることが容易ではない。すなわち、この淡色ボールには、長距離からの視認性という点では白色ボールと略同等であるため、例えば、冬季にプレーする際に枯れた芝生上の淡色ボールを認識することが容易ではないという懸念がある。
However, the light color ball disclosed in
本発明は、上記した問題を解決するためになされたもので、冬季の枯れた芝生上のみならず、霧、雨等の天候下でプレーする際にも長距離から容易に視認することが可能なゴルフボールを提供することを目的とする。 The present invention has been made to solve the above-described problems, and can be easily viewed from a long distance not only on a dry lawn in winter but also when playing in weather such as fog and rain. An object of the present invention is to provide a golf ball.
前記の目的を達成するために、本発明は、最表面にカバーを有するゴルフボールにおいて、
前記カバーの表面の色調をCIE/L*a*b*表色系で表したとき、明度L*が50以上、色度a*が−20以下又は+20以上、色度b*が+35以上であることを特徴とする。
In order to achieve the above object, the present invention provides a golf ball having a cover on the outermost surface.
When the color tone of the surface of the cover is expressed in the CIE / L * a * b * color system, the lightness L * is 50 or more, the chromaticity a * is −20 or less or +20 or more, and the chromaticity b * is +35 or more. It is characterized by being.
色調が上記のように設定されたカバーを有するゴルフボールは、プレーヤーの目に鮮明な黄緑色、黄色又はオレンジ色として認識される。従って、冬季において、枯れて白色を呈した芝生との区別が容易である。また、霧や雨等の天候下でプレーする際においても、ボールの飛行方向や落下地点を長距離から容易に目視で確認することができる。すなわち、視認性に優れたゴルフボールを得ることができる。 A golf ball having a cover whose color tone is set as described above is recognized as a clear yellow-green, yellow or orange color to the player's eyes. Accordingly, it is easy to distinguish from a lawn that has withered and white in winter. Further, even when playing in weather such as fog or rain, the flight direction and the falling point of the ball can be easily visually confirmed from a long distance. That is, a golf ball having excellent visibility can be obtained.
カバーを上記したように着色するには、透明熱可塑性樹脂又は透明熱可塑性エラストマーの少なくとも一方に1種以上の蛍光染料を添加すればよい。ここで、本発明における「着色」には、呈色した後であっても光を透過することが可能な程度の透明度が残留している場合も含まれるものとする。 In order to color the cover as described above, one or more fluorescent dyes may be added to at least one of the transparent thermoplastic resin or the transparent thermoplastic elastomer. Here, “coloring” in the present invention includes a case in which a degree of transparency that can transmit light remains even after coloring.
この場合、明度L*、色度a*及び色度b*が次式(1)を満足することが好ましい。 In this case, it is preferable that the lightness L * , the chromaticity a *, and the chromaticity b * satisfy the following formula (1).
左辺、すなわち、彩度が明度L*の1.2倍を超えると、呈色が過度に鮮明となる。このため、プレーヤーによっては、打球する際にボールに眩しさを感じることがある。 If the left side, that is, the saturation exceeds 1.2 times the lightness L * , the coloring becomes excessively clear. For this reason, some players may feel dazzling when hitting.
この種の蛍光染料の好適な例としては、ナフタルイミド系蛍光染料、チオキサンテン系蛍光染料、ペリレン系蛍光染料及びチオインジゴ系蛍光染料の群から選択された1種以上を挙げることができる。 Preferable examples of this type of fluorescent dye include one or more selected from the group of naphthalimide fluorescent dyes, thioxanthene fluorescent dyes, perylene fluorescent dyes, and thioindigo fluorescent dyes.
より具体的には、C.I.ソルベントイエロー98又はC.I.ソルベントオレンジ63等の蛍光染料を挙げることができる。カバーは、C.I.ソルベントイエロー98を用いた場合には概ね黄色、明度によっては黄緑色に着色され、一方、C.I.ソルベントオレンジ63を用いた場合にはオレンジ色に着色される。 More specifically, C.I. I. Solvent Yellow 98 or C.I. I. Fluorescent dyes such as Solvent Orange 63 can be mentioned. The cover is C.I. I. When Solvent Yellow 98 is used, it is generally yellow, and depending on the lightness, it is colored yellow-green. I. When Solvent Orange 63 is used, it is colored orange.
なお、透明熱可塑性樹脂又は透明熱可塑性エラストマーの少なくとも一方を100重量部とするとき、前記蛍光染料の好ましい添加割合は、0.005〜3.0重量部である。この場合、カバーが呈色はするものの、光を透過することが可能な程度の半透明となる。本発明においては、上記したように、この状態も「着色」に含まれるものとする。 In addition, when at least one of a transparent thermoplastic resin or a transparent thermoplastic elastomer is 100 weight part, the preferable addition ratio of the said fluorescent dye is 0.005-3.0 weight part. In this case, although the cover is colored, it is translucent to the extent that light can be transmitted. In the present invention, as described above, this state is also included in “coloring”.
ここで、カバーには紫外線吸収剤を添加することが好ましい。これにより、ゴルフボールが優れた耐候性を示すようになる。すなわち、長期間にわたって太陽光に曝される環境下でプレーに使用されても、劣化し難いボールとなる。 Here, it is preferable to add an ultraviolet absorber to the cover. Thereby, the golf ball comes to have excellent weather resistance. That is, even when used for play in an environment exposed to sunlight for a long period of time, the ball is hardly deteriorated.
一般的に、蛍光染料は、340〜400nmの波長域の光、すなわち、紫外線光を吸収して蛍光を発する。従って、紫外線吸収剤としては、340nm未満の波長域で吸収ピークが存在するとともに340〜400nmの波長域で吸収ピークが存在しないものを選定することが好ましい。340〜400nmの波長域に吸収ピークが存在するものであると、前記蛍光が起こり難くなる。このため、プレーヤーには、蛍光による発色が認識され難くなる。 Generally, a fluorescent dye absorbs light in a wavelength range of 340 to 400 nm, that is, ultraviolet light and emits fluorescence. Therefore, it is preferable to select an ultraviolet absorber having an absorption peak in the wavelength range of less than 340 nm and no absorption peak in the wavelength range of 340 to 400 nm. If the absorption peak exists in the wavelength range of 340 to 400 nm, the fluorescence is difficult to occur. For this reason, it becomes difficult for the player to recognize the color developed by fluorescence.
この種の紫外線吸収剤の好適な例としては、シュウ酸アニリド系紫外線吸収剤や、マロン酸エステル系紫外線吸収剤を挙げることができる。 Preferable examples of this type of ultraviolet absorber include oxalic anilide ultraviolet absorbers and malonic ester ultraviolet absorbers.
そして、紫外線吸収剤の割合は、前記透明熱可塑性樹脂又は前記透明熱可塑性エラストマーの少なくとも一方を100重量部としたとき、0.01〜3.0重量部とすることが好ましい。 And it is preferable that the ratio of an ultraviolet absorber shall be 0.01-3.0 weight part when at least one of the said transparent thermoplastic resin or the said transparent thermoplastic elastomer is 100 weight part.
さらに、340〜400nmの波長域に吸収ピークが存在する蛍光染料の好適な例としては、上記したC.I.ソルベントイエロー98又はC.I.ソルベントオレンジ63を挙げることができる。この場合、紫外線吸収剤としては、例えば、340nm未満の波長域である320nmに吸収ピークが存在し、且つ340〜400nmの波長域に吸収ピークが存在しないシュウ酸アニリド誘導体を選定することができる。 Furthermore, as a suitable example of the fluorescent dye having an absorption peak in the wavelength region of 340 to 400 nm, the above-described C.I. I. Solvent Yellow 98 or C.I. I. The solvent orange 63 can be mentioned. In this case, as the ultraviolet absorber, for example, an oxalic acid anilide derivative having an absorption peak at 320 nm that is a wavelength region of less than 340 nm and no absorption peak at a wavelength region of 340 to 400 nm can be selected.
又は、二酸化チタン又は酸化亜鉛の少なくとも一方をカバーに添加するようにしてもよい。この場合においても、ゴルフボールの耐候性を向上させることができる。 Alternatively, at least one of titanium dioxide and zinc oxide may be added to the cover. Even in this case, the weather resistance of the golf ball can be improved.
二酸化チタンの平均粒子径は、10nm〜200nmであることが好ましい。10nm未満であると、耐候性を向上させる効果に乏しい。また、200nmを超えると、カバーが白っぽくなる。一層好ましい平均粒子径は、10〜100nmである。酸化亜鉛を用いる場合も、同様の理由から、平均粒子径が10〜200nmのものであることが好ましく、10〜100nmのものであることが一層好ましい。ここで、本発明においては、樹枝形状粒子の場合、平均短軸径を平均粒子径とする。 The average particle diameter of titanium dioxide is preferably 10 nm to 200 nm. If it is less than 10 nm, the effect of improving the weather resistance is poor. If it exceeds 200 nm, the cover becomes whitish. A more preferable average particle diameter is 10 to 100 nm. Even when zinc oxide is used, for the same reason, the average particle diameter is preferably 10 to 200 nm, and more preferably 10 to 100 nm. Here, in the present invention, in the case of dendritic particles, the average minor axis diameter is defined as the average particle diameter.
透明熱可塑性樹脂又は透明熱可塑性エラストマーの少なくとも一方を100重量部とするとき、二酸化チタン、酸化亜鉛、又はこれらの混合物の好ましい添加割合は、0.01〜1.0重量部である。この場合もカバーが半透明となり、光が透過することが可能となる。 When at least one of the transparent thermoplastic resin or the transparent thermoplastic elastomer is 100 parts by weight, a preferable addition ratio of titanium dioxide, zinc oxide, or a mixture thereof is 0.01 to 1.0 part by weight. In this case as well, the cover is translucent and light can be transmitted.
さらにまた、ヒンダードアミン系光安定剤又はヒンダードフェノール系酸化防止剤の少なくとも一方をカバーに添加することで耐候性を向上させるようにしてもよい。この場合において、カバーを光が透過可能な程度の半透明にするためには、透明熱可塑性樹脂又は透明熱可塑性エラストマーの少なくとも一方を100重量部とするとき、ヒンダードアミン系光安定剤、ヒンダードフェノール系酸化防止剤、又はこれらの混合物を0.01〜2.0重量部の割合で添加することが好ましい。 Furthermore, you may make it improve a weather resistance by adding at least one of a hindered amine light stabilizer or a hindered phenolic antioxidant to a cover. In this case, in order to make the cover translucent enough to transmit light, when at least one of the transparent thermoplastic resin or the transparent thermoplastic elastomer is 100 parts by weight, a hindered amine light stabilizer, a hindered phenol is used. It is preferable to add a system antioxidant or a mixture thereof in a proportion of 0.01 to 2.0 parts by weight.
いずれの場合においても、上記したように構成されたカバーの内側に、非蛍光性の黄色顔料で着色された内層を設けるようにしてもよい。すなわち、本発明によれば、1層のソリッドコアが1層のカバーで被覆されたいわゆるツーピースソリッドゴルフボールのみならず、例えば、上記カバーと内層との2層カバーで複数層のソリッドコアを被覆したマルチピースソリッドゴルフボールを構成することも可能である。 In either case, an inner layer colored with a non-fluorescent yellow pigment may be provided inside the cover configured as described above. That is, according to the present invention, not only a so-called two-piece solid golf ball in which a single layer of solid core is covered with a single layer cover, but also, for example, a multi-layer solid core is covered with a two-layer cover of the cover and the inner layer. It is also possible to construct a multi-piece solid golf ball.
本発明によれば、カバーの明度を所定値以上とし、且つ色度を所定の値以下又は以上に設定するようにしている。このため、鮮明な黄緑色、黄色ないしオレンジ色に着色されたカバーを有するゴルフボールが得られる。 According to the present invention, the brightness of the cover is set to a predetermined value or more, and the chromaticity is set to a predetermined value or less. For this reason, a golf ball having a cover colored in clear yellow-green, yellow or orange is obtained.
このようなゴルフボールは、視認性に優れる。従って、冬季に枯れて白色を呈した芝生と容易に区別することが可能である。また、霧や雨等の天候下でも、飛行方向や落下地点を目視で長距離から容易に判断することができる。 Such a golf ball is excellent in visibility. Therefore, it can be easily distinguished from a lawn that withered in winter and has a white color. Further, even in weather such as fog and rain, the flight direction and the falling point can be easily determined from a long distance visually.
以下、本発明に係るゴルフボールにつき好適な実施の形態を挙げ、添付の図面を参照して詳細に説明する。 Hereinafter, preferred embodiments of the golf ball according to the present invention will be described in detail with reference to the accompanying drawings.
図1は、本実施の形態に係るゴルフボール10の概略全体断面図である。この場合、該ゴルフボール10は、1層のソリッドコア12が1層のカバー14で被覆された、いわゆるツーピースソリッドゴルフボールである。
FIG. 1 is a schematic overall cross-sectional view of a golf ball 10 according to the present embodiment. In this case, the golf ball 10 is a so-called two-piece solid golf ball in which a single-layer
ソリッドコア12の材質としては、従来から存在するツーピースソリッドゴルフボールのソリッドコアと同様のものを選定すればよい。その好適な例としては、ポリブタジエンゴムを基材ゴムとし、α、β−不飽和カルボン酸金属塩であるアクリル酸亜鉛、有機過酸化物であるジクミルパーオキサイド、充填材である酸化亜鉛等を配合したゴム組成物が挙げられる。
As the material of the
一方、カバー14は、アイオノマー樹脂、又は、ポリエステル系熱可塑性エラストマー、ポリアミド系熱可塑性エラストマー、ポリウレタン系熱可塑性エラストマー等の熱可塑性エラストマーの少なくともいずれか一方を含有するカバー用樹脂組成物を主成分とする。すなわち、カバー14は、アイオノマー樹脂又は熱可塑性エラストマーのいずれかを含有するものであってもよいし、アイオノマー樹脂及び熱可塑性エラストマーの混合物を含有するものであってもよい。
On the other hand, the
カバー14の色調は、国際照明委員会(CIE)の規格であるCIE/L*a*b*表色系で表すとき、明度L*が50以上、色度a*が−20以下又は+20以上、色度b*が+35以上に設定される。色度a*が−20以下でカバー14が黄緑色ないし黄色に呈色され、+20以上でオレンジ色に呈色される。ここで、CIE/L*a*b*表色系とは、CIEで規格化された表色系であり、JISにおいてはZ8729として採用されている。また、カバー14における明度L*、色度a*及び色度b*を把握するには、例えば、コニカミノルタ社製の色彩色差計CR−300を用いてボールの表面色を測定すればよい。
The color tone of the
カバー14の明度、色度を上記のように設定することにより、ゴルフボール10は、プレーヤーの目に鮮明な黄緑色、黄色又はオレンジ色として認識される。このため、良好な視認性が確保されるので、例えば、冬季に使用しても、枯れて白色を呈した芝生と容易に区別することができる。また、霧、雨等の天候下でプレーする際にも、長距離から容易に視認することが可能である。
By setting the brightness and chromaticity of the
なお、明度L*が50より小さいと、カバー14の色が暗くなる。また、色度a*が−20より大きいか、又は+20より小さいと、緑方向又は赤方向の色が薄くなる。さらに、色度b*が+35より小さいと黄方向の色が薄くなり、視認性が低下する。明度L*、色度a*、色度b*のより好ましい範囲は、それぞれ、60〜100、−25〜−100(黄緑色ないし黄色)又は+25〜+100(オレンジ色)、+40〜+100である。
If the lightness L * is less than 50, the color of the
カバー14は、黄色として認識し得る色調にすることが特に好ましく、その場合、明度L*を80〜100、色度a*を−25〜−45、色度b*を+85〜+100とすることが好ましい。
It is particularly preferable that the
さらに、L*、a*、b*が次式(1)を満足する関係にあることが好ましい。 Furthermore, it is preferable that L * , a * , and b * have a relationship satisfying the following formula (1).
式(1)における左辺、すなわち、彩度が1.2×L*より大きいと、カバー14が過度に鮮明に呈色される。このため、プレーヤーによっては、打球する際にボールに眩しさを感じることがある。
If the left side in the formula (1), that is, the saturation is larger than 1.2 × L * , the
カバー14の色調を上記したように設定するためには、例えば、アイオノマー樹脂、熱可塑性エラストマー、両者の混合物として透明であるものを選定し、さらに蛍光染料を添加すればよい。
In order to set the color tone of the
この場合、蛍光染料としては、CIE/L*a*b*表色系でカバー14の色調を表すとき、明度L*が50以上、色度a*が−20以下又は+20以上、色度b*が+35以上とするものが選定される。
In this case, as the fluorescent dye, when the color tone of the
この種の蛍光染料の好適な例としては、ナフタルイミド系蛍光染料であるC.I.ソルベントイエロー98が挙げられる。より具体的に例示すれば、クラリアント社製のHostasol Yellow 3G(商品名)等である。また、ナフタルイミド系以外の好適な蛍光染料としては、C.I.ソルベントオレンジ63等のチオキサンテン系蛍光染料や、C.I.バットレッド63等のチオインジゴ系蛍光染料等が例示される。さらに、ペリレン系蛍光染料であってもよい。以上のような蛍光染料は、1種のみを使用するようにしてもよいし、2種以上を混合して使用するようにしてもよい。 Preferable examples of this type of fluorescent dye include naphthalimide-based fluorescent dyes such as C.I. I. Solvent Yellow 98 is exemplified. More specifically, it is Hostsol Yellow 3G (trade name) manufactured by Clariant. Examples of suitable fluorescent dyes other than naphthalimide are C.I. I. Thioxanthene fluorescent dyes such as Solvent Orange 63, C.I. I. Examples thereof include thioindigo fluorescent dyes such as Vat Red 63. Furthermore, a perylene fluorescent dye may be used. The fluorescent dyes as described above may be used alone or in combination of two or more.
蛍光染料の好適な添加量は、カバー用樹脂組成物100重量部に対して0.005〜3.0重量部である。0.005重量部未満であると、彩度が過度に淡くなる。一方、3.0重量部よりも多いと、彩度が過度に濃厚になるとともに退色が生じ易くなる。蛍光染料のより好ましい添加量は、カバー用樹脂組成物100重量部に対して0.01〜2.7重量部、さらに好ましくは0.02〜2.5重量部である。 A suitable addition amount of the fluorescent dye is 0.005 to 3.0 parts by weight with respect to 100 parts by weight of the cover resin composition. If it is less than 0.005 parts by weight, the saturation becomes excessively light. On the other hand, when the amount is more than 3.0 parts by weight, the saturation becomes excessively thick and fading easily occurs. A more preferable addition amount of the fluorescent dye is 0.01 to 2.7 parts by weight, more preferably 0.02 to 2.5 parts by weight with respect to 100 parts by weight of the cover resin composition.
カバー14には、紫外線吸収剤をさらに添加するようにしてもよい。カバー14が紫外線吸収剤を含有するものである場合、ゴルフボール10の耐候性が向上するという利点がある。
An ultraviolet absorber may be further added to the
上記したような蛍光染料は、340〜400nmの波長域の光、すなわち、紫外線光を吸収して蛍光を発するので、紫外線光を吸収する紫外線吸収剤を添加すると、蛍光染料が紫外線光を吸収して蛍光を発することが容易でなくなる。結局、プレーヤーが蛍光による発色を認識することが容易でなくなる。 The fluorescent dye as described above absorbs light in the wavelength range of 340 to 400 nm, that is, ultraviolet light and emits fluorescence. Therefore, when an ultraviolet absorber that absorbs ultraviolet light is added, the fluorescent dye absorbs ultraviolet light. Thus, it becomes difficult to emit fluorescence. Eventually, it becomes difficult for the player to recognize the color developed by the fluorescence.
従って、紫外線吸収剤としては、340nm未満の波長域で吸収ピークが存在するとともに340〜400nmの波長域で吸収ピークが存在しないものを選定することが好ましい。好適な具体例としては、クラリアント社製のSanduvor VSU(商品名)等のシュウ酸アニリド系紫外線吸収剤や、同社製のHostavin PR−25、Hostavin B−CAP(いずれも商品名)等のマロン酸エステル系紫外線吸収剤を挙げることができる。 Therefore, it is preferable to select an ultraviolet absorber having an absorption peak in the wavelength range of less than 340 nm and no absorption peak in the wavelength range of 340 to 400 nm. Preferred specific examples include malonic acids such as oxalic acid anilide-based UV absorbers such as Sanduvor VSU (trade name) manufactured by Clariant, and Hostavin PR-25 and Hostavin B-CAP (both trade names) manufactured by the same company. An ester ultraviolet absorber can be mentioned.
特に、蛍光染料がC.I.ソルベントイエロー98又はC.I.ソルベントオレンジ63である場合、前記したSanduvor VSU等のシュウ酸アニリド誘導体が好適である。なお、シュウ酸アニリド誘導体の吸収ピークは、320nmに存在する。 In particular, the fluorescent dye is C.I. I. Solvent Yellow 98 or C.I. I. In the case of Solvent Orange 63, an oxalic acid anilide derivative such as Sanduvor VSU described above is preferable. The absorption peak of the oxalic acid anilide derivative is present at 320 nm.
この種の紫外線吸収剤の割合は、前記透明熱可塑性樹脂又は前記透明熱可塑性エラストマーの少なくとも一方を100重量部としたとき、0.01〜3.0重量部とすることが好ましい。0.01重量部未満ではゴルフボール10の耐候性を向上させる効果に乏しい。また、3.0重量部を超える割合で添加すると、耐候性が飽和するのでコスト的に不利である。より好ましい添加割合は0.05〜2.5重量部であり、さらに好ましい添加割合は0.1〜2.0重量部である。 The proportion of this type of UV absorber is preferably 0.01 to 3.0 parts by weight when at least one of the transparent thermoplastic resin or the transparent thermoplastic elastomer is 100 parts by weight. If it is less than 0.01 part by weight, the effect of improving the weather resistance of the golf ball 10 is poor. Moreover, when it adds in the ratio exceeding 3.0 weight part, since a weather resistance will be saturated, it is disadvantageous in cost. A more preferable addition ratio is 0.05 to 2.5 parts by weight, and a further preferable addition ratio is 0.1 to 2.0 parts by weight.
又は、カバー14に対し、二酸化チタン、酸化亜鉛、これらの混合物のいずれかを添加するようにしてもよい。この場合においても、ゴルフボール10の耐候性を向上させることができる。
Alternatively, any one of titanium dioxide, zinc oxide, and a mixture thereof may be added to the
ここで、二酸化チタン又は酸化亜鉛としては、平均粒子径が10〜200nmであるものを添加することが好ましい。10nm未満であるものを添加すると、耐候性がさほど向上しない。また、200nmを超えるものを添加するとカバーが白っぽくなる。平均粒子径が10〜100nmであるものが一層好ましい。 Here, it is preferable to add titanium dioxide or zinc oxide having an average particle size of 10 to 200 nm. If a material having a thickness of less than 10 nm is added, the weather resistance is not improved so much. Moreover, when the thing exceeding 200 nm is added, a cover will become whitish. What has an average particle diameter of 10-100 nm is still more preferable.
勿論、混合物を添加する場合には、各々の平均粒子径が、好ましくは10〜200nm、より好ましくは10〜100nmである二酸化チタン及び酸化亜鉛の混合物を使用すればよい。 Of course, when a mixture is added, a mixture of titanium dioxide and zinc oxide having an average particle diameter of preferably 10 to 200 nm, more preferably 10 to 100 nm may be used.
この種の微粒子二酸化チタンとしては、石原産業社製のTTO−55(平均粒子径=30〜50nm)、TTO−51(平均粒子径=10〜30nm)、TTO−D−1(樹枝形状の粒子であり、平均長軸径=200〜300nm、平均短軸径=40〜70nm=平均粒子径)等が例示される。一方、微粒子酸化亜鉛の具体例としては、石原産業社製のFZO−50(平均粒子径=約20nm)、ハクスイテック社製のZINCOX SUPER F−1(平均粒子径=100nm)、ZINCOX SUPER F−2(平均粒子径=65nm)等が挙げられる。 As this kind of fine particle titanium dioxide, TTO-55 (average particle size = 30-50 nm), TTO-51 (average particle size = 10-30 nm), TTO-D-1 (dendritic particles) manufactured by Ishihara Sangyo Co., Ltd. And average major axis diameter = 200 to 300 nm, average minor axis diameter = 40 to 70 nm = average particle diameter) and the like. On the other hand, as specific examples of the fine zinc oxide, FZO-50 (average particle diameter = about 20 nm) manufactured by Ishihara Sangyo Co., Ltd., ZINCOX SUPER F-1 (average particle diameter = 100 nm) manufactured by Hakusui Tech Co., Ltd., ZINCOX SUPER F-2 (Average particle diameter = 65 nm).
二酸化チタン、酸化亜鉛、又はこれらの混合物の添加割合は、透明熱可塑性樹脂又は透明熱可塑性エラストマーの少なくとも一方を100重量部とするとき、0.01〜1.0重量部とすることが好ましい。0.01重量部未満では、ゴルフボール10の耐候性を向上させる効果に乏しい。また、1.0重量部を超えるとカバーが白っぽくなるとともに、耐候性を向上させる効果が飽和するので不経済である。 The addition ratio of titanium dioxide, zinc oxide, or a mixture thereof is preferably 0.01 to 1.0 part by weight when at least one of the transparent thermoplastic resin or the transparent thermoplastic elastomer is 100 parts by weight. If it is less than 0.01 part by weight, the effect of improving the weather resistance of the golf ball 10 is poor. On the other hand, if it exceeds 1.0 part by weight, the cover becomes whitish and the effect of improving the weather resistance is saturated, which is uneconomical.
さらにまた、ヒンダードアミン系光安定剤、ヒンダードフェノール系酸化防止剤、又はこれらの混合物をカバーに添加し、これによりゴルフボール10の耐候性を向上させるようにしてもよい。ヒンダードアミン系光安定剤の具体例としては、チバ・スペシャルティ・ケミカルズ社製のTINUVIN XT 855/FF等が挙げられ、一方、ヒンダードフェノール系酸化防止剤の具体例としては、チバ・スペシャルティ・ケミカルズ社製のIRGANOX 1010、IRGANOX 1076等が挙げられる。 Furthermore, a hindered amine light stabilizer, a hindered phenol antioxidant, or a mixture thereof may be added to the cover, thereby improving the weather resistance of the golf ball 10. Specific examples of hindered amine light stabilizers include TINUVIN XT 855 / FF manufactured by Ciba Specialty Chemicals, while specific examples of hindered phenol antioxidants include Ciba Specialty Chemicals. IRGANOX 1010, IRGANOX 1076, etc. manufactured by the company are mentioned.
この種の光安定剤、酸化防止剤、又は両者の混合物の添加割合は、透明熱可塑性樹脂又は透明熱可塑性エラストマーの少なくとも一方を100重量部とするとき、0.01〜2.0重量部とすることが好ましい。上記と同様、0.01重量部未満ではゴルフボール10の耐候性を向上させる効果に乏しく、2.0重量部を超えると、耐候性を向上させる効果が飽和するので不経済である。 The addition ratio of this type of light stabilizer, antioxidant, or a mixture of both is 0.01 to 2.0 parts by weight when at least one of the transparent thermoplastic resin or the transparent thermoplastic elastomer is 100 parts by weight. It is preferable to do. Similarly to the above, if it is less than 0.01 parts by weight, the effect of improving the weather resistance of the golf ball 10 is poor, and if it exceeds 2.0 parts by weight, the effect of improving the weather resistance is saturated, which is uneconomical.
カバー14には、上記した蛍光染料や紫外線吸収剤、二酸化チタン、酸化亜鉛、酸化防止剤、光安定剤等を同時に添加するようにしてもよい。
The above-described fluorescent dye, ultraviolet absorber, titanium dioxide, zinc oxide, antioxidant, light stabilizer, and the like may be simultaneously added to the
また、カバー14の耐久性を高めるため、該カバー14上にクリアーペイントを塗装するようにしてもよい。クリアーペイントとしては、顔料を含有しないものを使用することができる他、塗膜が十分な透明性を有するのであれば、蛍光顔料、蛍光染料等を含有するものでもよい。
Further, in order to increase the durability of the
上記した実施の形態においては、ツーピースソリッドゴルフボールを例示して説明したが、本発明に係るゴルフボールは、例えば、図2に示すように、1層のソリッドコア20と、内層カバー22及び外層カバー24の2層からなるカバー26を有するスリーピースソリッドゴルフボール28であってもよい。
In the above-described embodiment, the two-piece solid golf ball has been described as an example. However, the golf ball according to the present invention has, for example, a single-layer
この場合、ソリッドコア20は、例えば、上記ソリッドコア12と同様に、ポリブタジエンゴム、アクリル酸亜鉛、ジクミルパーオキサイド、酸化亜鉛等を配合したゴム組成物から形成すればよい。
In this case, the
内層カバー22は、好適には、アイオノマー樹脂又は熱可塑性エラストマーの少なくともいずれか一方を含有するカバー用樹脂組成物を主成分として形成される。この内層カバー22は、従来から存在するスリーピースソリッドゴルフボールにおける内層カバーと同様に透明なものであってもよいし、二酸化チタン等の白色顔料を添加して白色としたものであってもよい。
The
又は、上記カバー14と同様に内層カバー22に対して蛍光染料を添加し、これにより、黄緑色、黄色又はオレンジ色に呈色させるようにしてもよい。勿論、必要に応じ、紫外線吸収剤、酸化防止剤、光安定剤等を添加するようにしてもよく、さらに、蛍光増白剤、着色剤等を添加するようにしてもよい。
Alternatively, a fluorescent dye may be added to the
さらにまた、内層カバー22に対して非蛍光性の黄色顔料を添加し、これにより該内層カバー22を黄色に呈色してもよい。この種の黄色顔料としては、無機顔料、有機顔料、これらの混合物のいずれも使用可能である。勿論、この場合においても、紫外線吸収剤、酸化防止剤、光安定剤、蛍光増白剤、着色剤等を添加するようにしてもよい。
Furthermore, a non-fluorescent yellow pigment may be added to the
そして、無機顔料としては黄色酸化鉄、チタンイエロー等が例示され、有機顔料としてはハンザイエローG、ハンザイエロー10G、ベンジジンイエロー、ベンジジンイエローG等が例示される。 Examples of inorganic pigments include yellow iron oxide and titanium yellow. Examples of organic pigments include Hansa Yellow G, Hansa Yellow 10G, Benzidine Yellow, and Benzidine Yellow G.
このように、本発明では、カバーを2層以上とする場合、カバーを構成する全層を着色する必要は特になく、少なくとも最外層を黄緑色、黄色又はオレンジ色とすればよい。最外層以外のカバー層については、最外層と同様に着色してもよいし、通常の白色にしてもよい。 Thus, in the present invention, when the cover has two or more layers, it is not particularly necessary to color all the layers constituting the cover, and at least the outermost layer may be yellowish green, yellow or orange. The cover layer other than the outermost layer may be colored in the same manner as the outermost layer, or may be white.
この実施形態においては、外層カバー24を上記カバー14と同様に形成し、これにより該外層カバー24を黄緑色、黄色又はオレンジ色に呈色させる。その結果、スリーピースソリッドゴルフボール28が図1に示すゴルフボール10と同様に機能する。外層カバー24上にクリアーペイントを塗装するようにしてもよいことはいうまでもない。
In this embodiment, the
本発明に係るゴルフボールは、以上のツーピースソリッドゴルフボール10やスリーピースソリッドゴルフボール28に限定されるものではなく、1層のソリッドコアと3層以上のカバーから構成されるマルチピースソリッドゴルフボールや、2層以上のソリッドコアと1層以上のカバーから構成されるマルチピースソリッドゴルフボールであってもよい。
The golf ball according to the present invention is not limited to the two-piece solid golf ball 10 and the three-piece
シス−1、4−ポリブタジエンを基材ゴムとし、これにアクリル酸亜鉛、酸化亜鉛、ジクミルパ−オキサイドを混合したゴム組成物でソリッドコア20を作製した。
The
次に、ペルプレンGP−400(東洋紡社製のポリエステル系エラストマーの商品名)と、X−22−2355(信越化学工業社製のシリコーン変性熱可塑性エラストマーの商品名)が重量比で40:60の割合で混合された混合物を、前記ソリッドコア20上に射出成形して内層カバー22を形成した。この内層カバー22は、黄色系色を若干呈した略透明体であった。
Next, the weight ratio of Perprene GP-400 (trade name of a polyester elastomer manufactured by Toyobo Co., Ltd.) and X-22-22355 (trade name of a silicone-modified thermoplastic elastomer manufactured by Shin-Etsu Chemical Co., Ltd.) is 40:60. The mixture mixed at a ratio was injection molded onto the
次に、サーリン8946、サーリン9945、サーリン6120(ともにデュポンポリケミカル社製のアイオノマー樹脂の商品名)の36:36:28の混合物、すなわち、カバー用樹脂組成物に対し、C.I.ソルベントイエロー98であるHostasol Yellow 3G(クラリアント社製の黄色蛍光染料の商品名)、及びシュウ酸アニリド誘導体であるSanduvor VSU(クラリアント社製の紫外線吸収剤の商品名)を添加してカバー原料とした。なお、カバー用樹脂組成物100重量部に対する蛍光染料、紫外線吸収剤の割合は、それぞれ、0.1重量部、0.3重量部とした。 Next, a 36:36:28 mixture of Surlyn 8946, Surlyn 9945, Surlyn 6120 (both trade names of ionomer resins manufactured by DuPont Polychemical Co., Ltd.), that is, C.I. I. Solvent Yellow 98 Hostasol Yellow 3G (trade name of Clariant's yellow fluorescent dye) and Sanduvor VSU (trade name of Clariant's UV absorber) which is an oxalic acid anilide derivative were used as cover materials. . The ratios of the fluorescent dye and the ultraviolet absorber to 100 parts by weight of the cover resin composition were 0.1 parts by weight and 0.3 parts by weight, respectively.
このカバー原料を上記した内層カバー22上に射出成形して外層カバー24を形成し、その後、外層カバー24上にクリアーペイントを塗装してスリーピースソリッドゴルフボール28を得た。これを実施例1とする。
This cover material was injection-molded on the above-described
また、カバー原料に添加している蛍光染料をC.I.ソルベントオレンジ63であるHostasol Red GG(クラリアント社製のオレンジ色蛍光染料の商品名)0.03重量部に変更したことを除いては、実施例1と同様にしてスリーピースソリッドゴルフボール28を作製した。これを実施例2とする。
The fluorescent dye added to the cover material is C.I. I. A three-piece
さらに、以下のようにして別のスリーピースソリッドゴルフボール28を作製した。すなわち、先ず、実施例1に準拠してソリッドコア20を設けた後、サーリン9150、サーリン8150(ともにデュポンポリケミカル社製のアイオノマー樹脂の商品名)が重量比で50:50の混合物に対し、非蛍光性の黄色顔料であるチタンイエロー42−120A(東罐マテリアル・テクノロジー社製の商品名)を0.045重量部、二酸化チタンCR−60−2(石原産業社製の白色顔料の商品名)を0.275重量部添加した添加物からなる内層カバー22を形成した。
Further, another three-piece
次に、サーリン6320、サーリン1855、サーリン1856(いずれもデュポンポリケミカル社製のアイオノマー樹脂の商品名)の60:20:20の混合物(カバー用樹脂組成物)100重量部に対し、ニュクレル1050H(デュポンポリケミカル社製のエチレン−メタクリル酸共重合体の商品名)を2重量部添加するとともに、蛍光染料であるHostasol Yellow 3G、二酸化チタンであるTTO−D−1、酸化亜鉛であるZINCOX SUPER F−1、ヒンダードアミン系光安定剤であるTINUVIN XT 855/FF、ヒンダードフェノール系酸化防止剤であるIRGANOX 1010を、それぞれ、0.1重量部、0.08重量部、0.08重量部、0.08重量部、0.3重量部添加してカバー原料とした。 Next, with respect to 100 parts by weight of a 60:20:20 mixture (resin composition for cover) of Surlyn 6320, Surlyn 1855, Surlyn 1856 (all of which are trade names of ionomer resins manufactured by DuPont Polychemical Co., Ltd.), Nuclerel 1050H ( 2 parts by weight of an ethylene-methacrylic acid copolymer product manufactured by DuPont Polychemical Co., Ltd. was added, and the fluorescent dye Hostasol Yellow 3G, titanium dioxide TTO-D-1, and zinc oxide ZINCOX SUPER F -1, TINUVIN XT 855 / FF which is a hindered amine light stabilizer, and IRGANOX 1010 which is a hindered phenol antioxidant are 0.1 parts by weight, 0.08 parts by weight, 0.08 parts by weight, 0 0.08 parts by weight and 0.3 parts by weight did.
このカバー原料を前記内層カバー22上に射出成形して外層カバー24を形成し、その後、外層カバー24上にクリアーペイントを塗装してスリーピースソリッドゴルフボール28とした。これを実施例3とする。
This cover material was injection molded onto the
比較のため、アイオノマー樹脂100重量部に対し、ZQ−15(ディグロ社製の黄色蛍光顔料の商品名)2.73重量部と二酸化チタンA−220(石原産業社製の白色顔料の商品名)0.07重量部とを添加してカバー原料とした以外は実施例1に準拠して、スリーピースソリッドゴルフボールを作製した。これを比較例1とする。 For comparison, with respect to 100 parts by weight of ionomer resin, 2.73 parts by weight of ZQ-15 (trade name of yellow fluorescent pigment made by Digro) and titanium dioxide A-220 (trade name of white pigment made by Ishihara Sangyo Co., Ltd.) A three-piece solid golf ball was produced according to Example 1 except that 0.07 part by weight was added to obtain a cover raw material. This is referred to as Comparative Example 1.
以上の実施例1〜3、及び比較例1の各スリーピースソリッドゴルフボールにつき、コニカミノルタ社製の色彩色差計CR−300を用いてボール表面の色調を測定し、明度L*、色度a*、色度b*を調べ、さらに、彩度及び1.2×L*を算出した。 For each of the three-piece solid golf balls of Examples 1 to 3 and Comparative Example 1, the color tone of the ball surface was measured using a color difference meter CR-300 manufactured by Konica Minolta Co., Ltd., and the lightness L * and chromaticity a * were measured . The chromaticity b * was examined, and the saturation and 1.2 × L * were calculated.
また、ゴルフボールをグリーン上に載置し、70mm離れた地点から該ゴルフボールが認識し易いか否かを判断して視認性の評価を行った。結果を併せて図2に示す。なお、視認性は、鮮明に見える場合を○、見え難い場合を△とした。この図2から、実施例1〜3のスリーピースソリッドゴルフボール28が比較例1のゴルフボールに比して視認性が良好であることが明らかである。
Further, the golf ball was placed on the green, and visibility was evaluated by judging whether or not the golf ball was easily recognized from a
10…ツーピースソリッドゴルフボール 12、20…ソリッドコア
14、26…カバー 22…内層カバー
24…外層カバー
28…スリーピースソリッドゴルフボール
DESCRIPTION OF SYMBOLS 10 ... Two piece
Claims (18)
前記カバーの表面の色調をCIE/L*a*b*表色系で表したとき、明度L*が50以上、色度a*が−20以下又は+20以上、色度b*が+35以上であることを特徴とするゴルフボール。 In a golf ball having a cover on the outermost surface,
When the color tone of the surface of the cover is expressed in the CIE / L * a * b * color system, the lightness L * is 50 or more, the chromaticity a * is −20 or less or +20 or more, and the chromaticity b * is +35 or more. A golf ball characterized by being.