JP2007084915A - Low density alloy for golf club head - Google Patents
Low density alloy for golf club head Download PDFInfo
- Publication number
- JP2007084915A JP2007084915A JP2006174593A JP2006174593A JP2007084915A JP 2007084915 A JP2007084915 A JP 2007084915A JP 2006174593 A JP2006174593 A JP 2006174593A JP 2006174593 A JP2006174593 A JP 2006174593A JP 2007084915 A JP2007084915 A JP 2007084915A
- Authority
- JP
- Japan
- Prior art keywords
- alloy
- golf club
- titanium
- club head
- aluminum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、ゴルフクラブヘッド用低密度合金に関するもので、チタン、アルミとバナジウムの混合の比例を制御し、さらに選択的にモリブデン、クロム、鉄、シリコンおよび／またはホウ素などの微量の元素を添加することにより、重心の位置を調整すると共に、弾性変形の能力を高めるゴルフクラブヘッド用低密度合金に係るものである。 The present invention relates to a low density alloy for a golf club head, which controls the proportion of mixing titanium, aluminum and vanadium, and selectively adds a trace amount of elements such as molybdenum, chromium, iron, silicon and / or boron. Thus, the present invention relates to a low density alloy for a golf club head that adjusts the position of the center of gravity and enhances the ability of elastic deformation.
従来のゴルフクラブヘッドの構造としては、通常としてステンレスにより製成され、例えばＳＵＳ６３０またはＳＵＳ４３１（アメリカ鋼鉄協会ＡＩＳＩ標準６４０型と４３１型）をもって、さらに精密鋳造法（ロストワックス）により製成される。しかし、上述した材料の密度が比較的大きく、さらに強度が比較的低いため、上述した材料で製成されたヘッドではその壁の厚さは一定の厚さ以上に達しなければならず、それによってヘッドに求められた強度に達することができる。しかし、実際に使用してみると、上記ヘッドの重量が重過ぎないようにヘッドの設計のポイントが要求されることにより、上述した材料により製成されたヘッドの体積を大きく増やすことができず、上記ヘッドのフェース板において比較的よい打球のポイントの範囲も大幅に縮小されるため、打球の失敗の確率も大幅に増えてしまうという問題点があった。 As a conventional golf club head structure, it is usually made of stainless steel, for example, SUS630 or SUS431 (American Steel Association AISI standard 640 type and 431 type) and further made by a precision casting method (lost wax). However, since the density of the above-mentioned material is relatively large and the strength is relatively low, in the head made of the above-mentioned material, the wall thickness must reach a certain thickness or more, thereby The strength required for the head can be reached. However, in actual use, the head design point is required so that the weight of the head is not too heavy, so the volume of the head made of the above-described material cannot be increased greatly. However, since the range of relatively good hitting points on the face plate of the head is greatly reduced, there is a problem in that the probability of hitting a ball is greatly increased.
上述した問題点を解決するべく、業界においてはチタン合金によって製造されたヘッドが研究し開発されてきた。例えば、アメリカ特許第５，５０５，７９５号の「ゴルフクラブの製造方法（Method of manufacturing golf club）」、第５，６４３，１０８号の「ゴルフクラブヘッドの構造およびその製造方法（Structure for golf club head and the method of its manufacture）」、第６，８３２，９６１号の「ウッド型のゴルフクラブヘッド（Wood-type golf club head）」、第６，８８０，２２２号の「ゴルフクラブヘッドの製造方法（Method of manufacturing a golf club head）」および第６，９０５，０６１号の「ゴルフクラブヘッドの製造方法（Method of making a golf club head）」などにおいてＴｉ‐６Ａｌ‐４Ｖのチタン合金（すなわち重量百分率が６％のアルミと４％のバナジウムで、その他はチタン金属である）を採用してゴルフクラブヘッドを製造していたが、チタン合金の密度がステンレスより相対的に低いため、そしてその強度はステンレスと相当になり、さらに相対的に比較的高い弾性変形の能力を現すことができ、ヘッドの重量を増やさないという前提の下でゴルフクラブヘッドの体積の増加を許すことができることにより、ゴルフクラブヘッドにおいて比較的よい打球のポイントの面積を増やすことができるため、打球の成功率を高めることができるようにしたものがある（例えば、特許文献１、２、３、４、５を参照）。
その他に、Ｔｉ‐６Ａｌ‐４Ｖのチタン合金の密度はステンレスより相対的に低くなるため、ゴルフクラブヘッドの部分的な部材に用いられてゴルフクラブヘッドの重心の位置を調整することができ、例えばヘッド本体、フェース板、蓋板または重りなどに用いることができる。また、Ｔｉ‐６Ａｌ‐４Ｖのチタン合金の弾性変形の能力（伸長率）はステンレスより相対的に高くなるため、通常としてその比較的よい弾性変形の能力を利用して打球時において比較的大きい弾性変形の程度を生じさせることができ、さらにゴルフボールがフェース板にぶつかった時に生じた球体の圧縮変形を相対的に減少するのに用いられることにより、打球の応力が抵抗によって吸収される程度を相対的に低くすることができるため、打球応力のエネルギーの損失を避けると共に、打球の距離を増やすことができる。 In addition, since the density of Ti-6Al-4V titanium alloy is relatively lower than that of stainless steel, it can be used as a partial member of the golf club head to adjust the position of the center of gravity of the golf club head. It can be used for a head body, a face plate, a lid plate, a weight, or the like. In addition, since the ability of elastic deformation (elongation rate) of Ti-6Al-4V titanium alloy is relatively higher than that of stainless steel, it is normally relatively large elasticity at the time of hitting using its relatively good elastic deformation ability. The degree of deformation can be generated, and furthermore, it is used to relatively reduce the compressive deformation of the sphere caused when the golf ball hits the face plate, so that the stress of the hit ball is absorbed by the resistance. Since it can be made relatively low, it is possible to avoid the energy loss of the hitting stress and increase the hitting distance.
しかし、ヘッドの体積の大型化と重心調整の自由度を考慮した上、上記チタン合金の密度をさらに改良する必要性があり、そして元の機械強度を保有することにより、上記チタン合金の応用の自由度を高める必要性がある。その他の関係するチタン合金は、以下の表１に示すように、ここでは参考として例に上げる。 However, there is a need to further improve the density of the titanium alloy in consideration of the increase in the volume of the head and the freedom of adjusting the center of gravity, and by maintaining the original mechanical strength, the application of the titanium alloy can be improved. There is a need to increase the degree of freedom. Other related titanium alloys are given here as examples for reference, as shown in Table 1 below.
本発明はこのような問題点に鑑みて発明したものであって、その目的とするところは、チタン‐アルミ‐バナジウム合金には重量百分率が８４％から９４％のチタン、６．５％から９．５％のアルミおよび１．５％以下のバナジウムが含まれ、または選択的にモリブデン、クロム、鉄、シリコンおよび／またはホウ素などの微量の元素を添加することにより、密度が４．４０ｇ／ｃｍ３以下のチタン合金を組成する。上記チタン合金によりゴルフクラブヘッドの全体の重心を調整すると共に、弾性変形の能力を高めることができるため、ヘッドの大型化に役立ち、さらにヘッドの設計の自由度を高めることができるゴルフクラブヘッド用低密度合金を提供しようとするものである。 The present invention was invented in view of these problems, and the object of the present invention is to provide titanium-aluminum-vanadium alloys having titanium in a weight percentage of 84% to 94%, 6.5% to 9%. .5% aluminum and not more than 1.5% vanadium, or by selectively adding trace elements such as molybdenum, chromium, iron, silicon and / or boron, the density is 4.40 g / cm A titanium alloy of 3 or less is composed. For the golf club head, which can adjust the overall center of gravity of the golf club head with the titanium alloy and can increase the elastic deformation capability, which is useful for increasing the size of the head and further increasing the degree of freedom in head design. It is intended to provide a low density alloy.
本発明の第一の目的は、チタン合金のアルミとバナジウムとの比例を調整することにより、密度を低くすると共に、元の機械強度を保有するため、ゴルフクラブヘッドの全体の重心を調整し、さらに弾性変形の能力を高めることができるゴルフクラブヘッド用低密度合金を提供しようとするものである。 The first object of the present invention is to adjust the proportion of the titanium alloy aluminum and vanadium, thereby reducing the density and maintaining the original mechanical strength. It is another object of the present invention to provide a low density alloy for a golf club head that can enhance the ability of elastic deformation.
本発明の第二の目的は、チタン合金のアルミとバナジウムとの比例を調整し、さらに選択的にモリブデン、クロム、鉄、シリコンおよび／またはホウ素などの微量の元素を添加することにより、密度を低くすると共に、元の機械強度を保有するため、ゴルフクラブヘッドの全体の重心を調整し、さらに弾性変形の能力を高めることができるゴルフクラブヘッド用低密度合金を提供しようとするものである。 The second object of the present invention is to adjust the proportion of aluminum and vanadium in the titanium alloy, and further selectively add a trace amount of elements such as molybdenum, chromium, iron, silicon and / or boron to reduce the density. An object of the present invention is to provide a low density alloy for a golf club head capable of adjusting the overall center of gravity of the golf club head and further improving the ability of elastic deformation in order to reduce the original mechanical strength.
上記目的を達成するために、本発明によるゴルフクラブヘッド用低密度合金は、以下のようになるものである。すなわち、
重量百分率が８４％から９４％のチタン、６．５％から９．５％のアルミおよび１．５％以下のバナジウムが含まれることにより、密度が４．４０ｇ／ｃｍ３以下のチタン‐アルミ‐バナジウム合金が組成される。
In order to achieve the above object, a low density alloy for a golf club head according to the present invention is as follows. That is,
Titanium-aluminum with a density of less than 4.40 g / cm 3 by containing titanium with a weight percentage of 84% to 94%, 6.5% to 9.5% aluminum and 1.5% or less vanadium. A vanadium alloy is composed.
本発明によるゴルフクラブヘッド用低密度合金は、上記チタン‐アルミ‐バナジウム合金には他に重量百分率が８％のアルミおよび１％のバナジウムが含まれることもできる。また、上記チタン‐アルミ‐バナジウム合金には他に重量百分率が１．２％以下のモリブデンが含まれることもできる。また、上記チタン‐アルミ‐バナジウム合金には他に重量百分率が１．２％以下のクロムが含まれることもできる。また、上記チタン‐アルミ‐バナジウム合金には他に重量百分率が０．６％以下の鉄が含まれることもできる。また、上記チタン‐アルミ‐バナジウム合金には他に重量百分率が０．６％以下のシリコンが含まれることもできる。また、上記チタン‐アルミ‐バナジウム合金には他に重量百分率が１．０％以下のホウ素が含まれることもできる。また、上記チタン‐アルミ‐バナジウム合金には重量百分率が７．２％から７．８％までのアルミおよび０．０２％から０．０６％までのバナジウムが含まれることもできる。また、上記チタン‐アルミ‐バナジウム合金には他に重量百分率が０．０６％の炭化ホウ素が含まれることもできる。また、上記チタン‐アルミ‐バナジウム合金には重量百分率が１．２％以下のモリブデン、１．２％以下のクロム、０．６％以下の鉄、０．６％以下のシリコンおよび１．０％以下のホウ素が含まれることもできる。 In the low density alloy for golf club heads according to the present invention, the titanium-aluminum-vanadium alloy may further contain aluminum at a weight percentage of 8% and vanadium at 1%. In addition, the titanium-aluminum-vanadium alloy may contain molybdenum having a weight percentage of 1.2% or less. In addition, the titanium-aluminum-vanadium alloy may further contain chromium having a weight percentage of 1.2% or less. In addition, the titanium-aluminum-vanadium alloy may contain iron having a weight percentage of 0.6% or less. In addition, the titanium-aluminum-vanadium alloy may further contain silicon having a weight percentage of 0.6% or less. In addition, the titanium-aluminum-vanadium alloy may further contain boron having a weight percentage of 1.0% or less. The titanium-aluminum-vanadium alloy may also contain aluminum having a weight percentage of 7.2% to 7.8% and vanadium of 0.02% to 0.06%. In addition, the titanium-aluminum-vanadium alloy may further contain boron carbide having a weight percentage of 0.06%. The titanium-aluminum-vanadium alloy has a weight percentage of molybdenum of 1.2% or less, chromium of 1.2% or less, iron of 0.6% or less, silicon of 0.6% or less, and 1.0%. The following boron can also be included.
本発明のゴルフクラブヘッド用低密度合金によれば、チタン合金のアルミとバナジウムとの比例を調整することにより、密度を低くすると共に、元の機械強度を保有するため、ゴルフクラブヘッドの全体の重心を調整し、さらに弾性変形の能力を高めることができるという利点がある。 According to the low density alloy for golf club head of the present invention, by adjusting the proportion of aluminum and vanadium of the titanium alloy, the density is lowered and the original mechanical strength is maintained. There is an advantage that the center of gravity can be adjusted and the ability of elastic deformation can be further enhanced.
本発明のゴルフクラブヘッド用低密度合金によれば、チタン合金のアルミとバナジウムとの比例を調整し、さらに選択的にモリブデン、クロム、鉄、シリコンまたはホウ素などの微量の元素を添加することにより、密度を低くすると共に、元の機械強度を保有するため、ゴルフクラブヘッドの全体の重心を調整し、さらに弾性変形の能力を高めることができるという利点がある。 According to the low density alloy for a golf club head of the present invention, by adjusting the proportion of aluminum and vanadium of the titanium alloy, and further selectively adding a trace amount of element such as molybdenum, chromium, iron, silicon or boron. In addition to reducing the density and maintaining the original mechanical strength, there is an advantage that the overall center of gravity of the golf club head can be adjusted and the ability of elastic deformation can be further increased.
本発明の実施の形態について、以下、図面を参照して説明する。 Embodiments of the present invention will be described below with reference to the drawings.
〔実施例１〕
表２と写真１を参照すると、本発明の実施例１のゴルフクラブヘッド用低密度合金は、チタン金属（密度４．５１ｇ／ｃｍ３）、アルミ金属（密度２．７０ｇ／ｃｍ３）およびバナジウム金属（密度５．７９ｇ／ｃｍ３）を主な合金の成分とし、上記チタン‐アルミ‐バナジウム合金には重量百分率が８４％から９４％のチタン、６．５％から９．５％のアルミおよび１．５％以下のバナジウムが含まれることにより、密度が４．４０ｇ／ｃｍ３以下のチタン合金が組成され、好ましくは選択的にチタン９１％、アルミ８％およびバナジウム１％のチタン‐アルミ‐バナジウム合金（表２に示すＴｉ‐８Ａｌ‐１Ｖ合金）を使用する。従来のＴｉ‐６Ａｌ‐４Ｖの合金と比較してみると、本発明においてはアルミの添加量を相対的に増やすことにより、合金の密度を低くすると共に、強靭性を改良することができるため、必要とする低密度の性質を獲得することができる。バナジウムの添加量を相対的に低くすることにより、合金の機械的性質に影響を及ぼすことなく、鋳造時における流動性を有効に高めると共に、排気の効果を補助することができる。上記チタン‐アルミ‐バナジウム合金は選択的にゴルフクラブヘッドの部材を製造するのに用いられ、例えばヘッド本体、フェース板、蓋板および／または重りなどを製造するのに用いられることができ、好ましくはフェース板を製造するのに用いられる。
[Example 1]
Referring to Table 2 and Photo 1, the low density alloy for golf club heads of Example 1 of the present invention includes titanium metal (density 4.51 g / cm 3 ), aluminum metal (density 2.70 g / cm 3 ), and vanadium. Metal (density 5.79 g / cm 3 ) is the main alloy component, and the titanium-aluminum-vanadium alloy has a weight percentage of 84% to 94% titanium, 6.5% to 9.5% aluminum and By including 1.5% or less vanadium, a titanium alloy having a density of 4.40 g / cm 3 or less is preferably composed of titanium-aluminum, preferably 91% titanium, 8% aluminum, and 1% vanadium. A vanadium alloy (Ti-8Al-1V alloy shown in Table 2) is used. Compared with the conventional Ti-6Al-4V alloy, in the present invention, by relatively increasing the amount of aluminum added, the alloy density can be lowered and the toughness can be improved. The required low density properties can be obtained. By relatively reducing the amount of vanadium added, the fluidity during casting can be effectively increased and the exhaust effect can be assisted without affecting the mechanical properties of the alloy. The titanium-aluminum-vanadium alloy is selectively used for manufacturing a golf club head member, and can be used, for example, for manufacturing a head body, a face plate, a cover plate, and / or a weight. Is used to manufacture face plates.
その他に、Ｔｉ‐６Ａｌ‐１Ｖ合金の密度（４．４０ｇ／ｃｍ３から４．３４ｇ／ｃｍ３）はＴｉ‐６Ａｌ‐４Ｖ合金の密度（４．４２ｇ／ｃｍ３）より相対的に低いため、ゴルフクラブヘッドの部分的な部材に用いられると、ゴルフクラブヘッドの重量を減らすことができ、しかもその機械的性質に大幅に影響を及ぼすことがないため、ゴルフクラブヘッドの重心の位置を調整するのに用いられることができ、例えばヘッド本体、フェース板、蓋板または重りとして用いることができる。 In addition, since the density of Ti-6Al-1V alloy (4.40 g / cm 3 to 4.34 g / cm 3 ) is relatively lower than the density of Ti-6Al-4V alloy (4.42 g / cm 3 ), When used as a partial member of a golf club head, the weight of the golf club head can be reduced and the mechanical properties of the golf club head are not significantly affected, so that the position of the center of gravity of the golf club head is adjusted. For example, it can be used as a head body, a face plate, a lid plate or a weight.
〔実施例２、３、４、５〕
表２を参照すると、本発明の実施例２、３、４、５のゴルフクラブヘッド用低密度合金が掲示される。実施例１と比較してみると、実施例２、３、４、５においては上記Ｔｉ‐６Ａｌ‐１Ｖ合金にはさらに選択的に微量の元素が添加され、例えば重量百分率が１．２％以下のモリブデン、１．２％以下のクロム、０．６％以下の鉄、０．６％以下のシリコンと１％以下のホウ素が添加される。適量なモリブデンを添加することにより、合金から均一に分布された炭化物を析出させることができ、さらに耐熱性を高めることができるため、合金の熔接の熱亀裂を減らし、さらに硬化能力と高温強度を増やすことができる。また、適量なクロムを添加することにより、合金の防錆耐蝕性を高めることができるため、ゴルフクラブヘッドの使用寿命を増やすことができる。また、適量な鉄を添加することにより、良好な塑性を獲得することができる。また、適量なシリコンを添加することにより、溶融金属の流動性を改善することができる。また、ホウ素は高温において組織が安定しており、しかも比較的よい酸化防止の能力、強靭性と塑性を有するため、適量なホウ素を添加することにより、合金の機械的性質を改善することができる。
[Examples 2, 3, 4, 5]
Referring to Table 2, golf club head low density alloys of Examples 2, 3, 4, and 5 of the present invention are posted. When compared with Example 1, in Examples 2, 3, 4, and 5, a small amount of element was further selectively added to the Ti-6Al-1V alloy, for example, the weight percentage was 1.2% or less. Molybdenum, 1.2% or less chromium, 0.6% or less iron, 0.6% or less silicon and 1% or less boron. By adding an appropriate amount of molybdenum, it is possible to precipitate uniformly distributed carbide from the alloy and to further improve the heat resistance, thereby reducing the thermal cracking of the welding of the alloy and further improving the hardening ability and high temperature strength. Can be increased. Further, by adding an appropriate amount of chromium, the rust prevention and corrosion resistance of the alloy can be increased, so that the service life of the golf club head can be increased. In addition, good plasticity can be obtained by adding an appropriate amount of iron. Moreover, the fluidity of the molten metal can be improved by adding an appropriate amount of silicon. In addition, since boron has a stable structure at high temperatures and has relatively good antioxidant ability, toughness and plasticity, the mechanical properties of the alloy can be improved by adding an appropriate amount of boron. .
本発明の実施例２においては、重量百分率が０．２５％から０．５％のモリブデンが添加される。また、本発明の実施例３においては、重量百分率が０．４％から０．６％のクロムが添加される。また、本発明の実施例４においては、重量百分率が０．２％から０．４％の鉄が添加される。また、本発明の実施例５においては、重量百分率が０．２５％から０．３５％のシリコンが添加される。上述した実施例の外に、本発明においては選択的に重量百分率が１．０％以下のホウ素を添加することにより、上記ゴルフクラブヘッドを製成することもできる。本発明の実施例２から実施例５における上記チタン‐アルミ‐バナジウム合金も同様に選択的にゴルフクラブヘッドの部材を製造するのに用いられ、例えばヘッド本体、フェース板、蓋板および／または重りなどを製造するのに用いられることができ、好ましくはフェース板を製造するのに用いられる。 In Example 2 of the present invention, molybdenum with a weight percentage of 0.25% to 0.5% is added. In Example 3 of the present invention, chromium having a weight percentage of 0.4% to 0.6% is added. In Example 4 of the present invention, iron having a weight percentage of 0.2% to 0.4% is added. In Example 5 of the present invention, silicon having a weight percentage of 0.25% to 0.35% is added. In addition to the embodiments described above, in the present invention, the golf club head can be produced by selectively adding boron having a weight percentage of 1.0% or less. The titanium-aluminum-vanadium alloy in the second to fifth embodiments of the present invention is also used to selectively manufacture a golf club head member, for example, a head body, a face plate, a lid plate and / or a weight. Etc., and is preferably used to manufacture a face plate.
このように、上述した実施例１から実施例５においては上記チタン‐アルミ‐バナジウム合金を主な合金の成分とし、さらに選択的にモリブデン、クロム、鉄、シリコンおよび／またはホウ素などの微量の元素を添加することにより、密度がＴｉ‐６Ａｌ‐４Ｖチタン合金より低くかつ伸長率がＴｉ‐６Ａｌ‐４Ｖチタン合金より高いゴルフクラブヘッドが形成される。また、材料そのものの弾性の限度（elastic limit）を超過しないという前提の下で、上記低密度のチタン‐アルミ‐バナジウム合金の伸長率Ｅ％（弾性変形の能力）は高くなる。そのため、その比較的よい弾性変形の能力を利用して打球時において比較的大きい弾性変形の程度を形成することができ、さらに打球の飛距離を高めることができる。また、低密度のＴｉ‐６Ａｌ‐１Ｖ合金を利用することにより、ゴルフクラブヘッドの全体の重量を低くすることができ、さらに上記ゴルフクラブヘッドの部分的な部材に用いられてゴルフクラブヘッドの重心の位置を調整することができ、例えばヘッド本体、蓋板、フェース板または重りなどの部材に用いられることができる。これにより、本発明において上記ゴルフクラブヘッドの重量を増やさないという前提の下で、ゴルフクラブヘッドの体積を大型化にすることにより、ゴルフクラブヘッドにおいて比較的よい打球のポイントの面積を増やすことができるため、打球の成功率を高めることができる。 Thus, in the above-described Examples 1 to 5, the titanium-aluminum-vanadium alloy is used as a main alloy component, and a trace element such as molybdenum, chromium, iron, silicon and / or boron is selectively used. Is added to form a golf club head having a density lower than that of the Ti-6Al-4V titanium alloy and a higher elongation rate than that of the Ti-6Al-4V titanium alloy. Also, the elongation percentage E% (elastic deformation capability) of the low density titanium-aluminum-vanadium alloy is high under the assumption that the elastic limit of the material itself is not exceeded. Therefore, a relatively large degree of elastic deformation can be formed at the time of hitting using the relatively good ability of elastic deformation, and the flight distance of the hitting ball can be further increased. Further, by using a low density Ti-6Al-1V alloy, the overall weight of the golf club head can be reduced, and further, the golf club head can be used as a partial member of the golf club head to provide a center of gravity of the golf club head. For example, it can be used for a member such as a head body, a cover plate, a face plate, or a weight. Thereby, on the premise that the weight of the golf club head is not increased in the present invention, the area of a relatively good hitting point in the golf club head can be increased by increasing the volume of the golf club head. Therefore, the success rate of the hit ball can be increased.
〔実施例６〕
表２、３、４と写真１を参照すると、本発明の実施例６のゴルフクラブヘッドの低密度の合金が掲示される。実施例１、２、３、４、５と比較してみると、実施例６においてはＴｉ‐７．５Ａｌ‐０．０５Ｖ‐０．２Ｓｉ‐０．０６Ｂ４Ｃの低密度の合金が採用されると共に、重量百分率が７．２％から７．８％までのアルミ、０．０２％から０．０６％までのバナジウム、０．２２％のシリコン、０．０６％の炭化ホウ素、０．０６％の鉄、０．０４％の炭素、０．０１％の窒素と０．２１％の酸素が含まれ、その他の比例はチタンである。本発明の実施例６におけるＴｉ‐７．５Ａｌ‐０．０５Ｖ‐０．２Ｓｉ‐０．０６Ｂ４Ｃの低密度の合金は従来のＴｉ‐６Ａｌ‐４Ｖのチタン合金と類似する機械性質を有するが、その４．３２ｇ／ｃｍ３の密度は従来のＴｉ‐６Ａｌ‐４Ｖのチタン合金の密度（４．４２ｇ／ｃｍ３）より低くなる。打撃テスト（打撃速度５５メートル／秒、＃２打撃試験機）おいて、本発明の実施例６におけるＴｉ‐７．５Ａｌ‐０．０５Ｖ‐０．２Ｓｉ‐０．０６Ｂ４Ｃの低密度の合金を鋳造によりフェース板の製成に応用すると、上記フェース板は全て打撃テストの標準を通過することができる。このように、上記Ｔｉ‐７．５Ａｌ‐０．０５Ｖ‐０．２Ｓｉ‐０．０６Ｂ４Ｃの低密度の合金を利用すると、同様にゴルフクラブヘッドの全体の重量を低く抑えることができると共に、上記ゴルフクラブヘッドの部材に応用してゴルフクラブヘッドの重心の位置を調整することができ、例えばヘッド本体、蓋板、フェース板および／または重りなどを製造するのに用いられることができる。このように、本発明においては上記ゴルフクラブヘッドの重量を増やさないとの前提で、上記ゴルフクラブヘッドの体積を大型化にし、上記ゴルフクラブヘッドの比較的よい打球のスポットの面積を増やすことにより、打球の成功率を高めることができる。
Example 6
Referring to Tables 2, 3, 4 and Photo 1, the low density alloy of the golf club head of Example 6 of the present invention is posted. Compared with Examples 1, 2, 3, 4, and 5, in Example 6, a low-density alloy of Ti-7.5Al-0.05V-0.2Si-0.06B 4 C was adopted. And a weight percentage of 7.2% to 7.8% aluminum, 0.02% to 0.06% vanadium, 0.22% silicon, 0.06% boron carbide, 0.06% % Iron, 0.04% carbon, 0.01% nitrogen and 0.21% oxygen, the other proportion being titanium. The Ti-7.5Al-0.05V-0.2Si-0.06B 4 C low density alloy in Example 6 of the present invention has similar mechanical properties to the conventional Ti-6Al-4V titanium alloy. The density of 4.32 g / cm 3 is lower than the density of the conventional Ti-6Al-4V titanium alloy (4.42 g / cm 3 ). Ti-7.5Al-0.05V-0.2Si-0.06B 4 C low-density alloy in Example 6 of the present invention in the impact test (blow rate 55 meters / second, # 2 impact tester) Is applied to the production of face plates by casting, all of the face plates can pass the standard of the impact test. As described above, when the low-density alloy of Ti-7.5Al-0.05V-0.2Si-0.06B 4 C is used, the overall weight of the golf club head can be similarly reduced, The golf club head member can be applied to adjust the position of the center of gravity of the golf club head, and can be used, for example, to manufacture a head body, a cover plate, a face plate, and / or a weight. Thus, in the present invention, on the premise that the weight of the golf club head is not increased, the volume of the golf club head is increased, and the area of a relatively good hitting spot of the golf club head is increased. , Can increase the success rate of the hit ball.
表５を参照すると、本発明のチタン合金において重量百分率が８４％から９４％のチタン、６．５％から９．５％のアルミおよび１．５％以下のバナジウムからなる場合、従来のチタン合金と比較すると、密度を低く下げ、機械性を高め、さらに流動性を高めることができるとの効果を増進することができる。 Referring to Table 5, when the titanium alloy according to the present invention is composed of titanium having a weight percentage of 84% to 94%, 6.5% to 9.5% aluminum, and 1.5% or less of vanadium, the conventional titanium alloy is used. As compared with, the effect of lowering the density, improving the mechanical properties, and further improving the fluidity can be enhanced.
表６参照すると、本発明のチタン合金において他に重量百分率が１．２％以下のモリブデンを添加すると、熱亀裂の防止の効果を増進することができる。また、他に重量百分率が１．２％以下のクロムを添加すると、耐食性の増進との効果を増進することができる。また、他に重量百分率が０．６％以下の鉄を添加すると、塑性の増進との効果を増進することができる。また、他に重量百分率が０．６％以下のシリコンを添加すると、流動性の増進との効果を増進することができる。さらに、他に重量百分率が１．０％以下のホウ素を添加すると、組織の安定との効果を増進することができる。 Referring to Table 6, the addition of molybdenum having a weight percentage of 1.2% or less in the titanium alloy of the present invention can enhance the effect of preventing thermal cracking. In addition, when chromium having a weight percentage of 1.2% or less is added, the effect of improving corrosion resistance can be enhanced. In addition, when iron having a weight percentage of 0.6% or less is added, the effect of the plasticity enhancement can be enhanced. In addition, when silicon having a weight percentage of 0.6% or less is added, the effect of improving fluidity can be enhanced. Furthermore, the addition of boron having a weight percentage of 1.0% or less can enhance the effect of stabilizing the structure.
上述の如く、従来のゴルフクラブヘッドによれば、比較的高密度と比較的低強度を有すると共に、ヘッドの体積を大きく増やすことができないため、比較的よい打球のポイントの範囲は大幅に縮小されてしまうなどの問題点があったが、本発明のゴルフクラブヘッド用低密度合金によれば、低密度の図１に示す本発明のゴルフクラブヘッドのワックスパターンの製造方法によれば、Ｔｉ‐６Ａｌ‐１Ｖ合金を利用することにより、または選択的にモリブデン、クロム、鉄、シリコンおよび／またはホウ素などの微量の元素を添加することにより、密度が４．４０ｇ／ｃｍ３以下のチタン‐アルミ‐バナジウム合金を組成することができるため、ゴルフクラブヘッドの全体の重心を調整すると共に、弾性変形の能力を高めることができ、さらにヘッドの大型化に役立ち、ヘッドの設計の自由度を高めることができる。 As described above, the conventional golf club head has a relatively high density and a relatively low strength and cannot greatly increase the volume of the head, so the range of relatively good hitting points is greatly reduced. However, according to the low density alloy for golf club head of the present invention, according to the method of manufacturing the wax pattern of the golf club head of the present invention shown in FIG. Titanium-aluminum with a density of 4.40 g / cm 3 or less by utilizing 6Al-1V alloy or by selectively adding trace elements such as molybdenum, chromium, iron, silicon and / or boron. Since the vanadium alloy can be composed, the overall center of gravity of the golf club head can be adjusted, and the ability of elastic deformation can be increased. This helps to increase the size of the head and increases the degree of freedom in head design.
本発明は、その精神及び必須の特徴事項から逸脱することなく他のやり方で実施することができる。従って、本明細書に記載した好ましい実施例は例示的なものであり、限定的なものではない。 The present invention may be implemented in other ways without departing from the spirit and essential characteristics thereof. Accordingly, the preferred embodiments described herein are illustrative and not limiting.
Claims (10)