JP2007077754A - Concrete curing sheet - Google Patents

Concrete curing sheet Download PDF

Info

Publication number
JP2007077754A
JP2007077754A JP2005270098A JP2005270098A JP2007077754A JP 2007077754 A JP2007077754 A JP 2007077754A JP 2005270098 A JP2005270098 A JP 2005270098A JP 2005270098 A JP2005270098 A JP 2005270098A JP 2007077754 A JP2007077754 A JP 2007077754A
Authority
JP
Japan
Prior art keywords
concrete
sheet
curing sheet
curing
plastic film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
JP2005270098A
Other languages
Japanese (ja)
Inventor
Hisaaki Kobayashi
久晃 小林
Ikiyuuya Hibino
伊久哉 日比野
Keisuke Naito
恵介 内藤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CCI Corp
Original Assignee
CCI Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CCI Corp filed Critical CCI Corp
Priority to JP2005270098A priority Critical patent/JP2007077754A/en
Publication of JP2007077754A publication Critical patent/JP2007077754A/en
Withdrawn legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a concrete curing sheet of which the installation work can be omitted after removing concrete forms. <P>SOLUTION: This concrete curing sheet is a type which has been provided at a concrete form beforehand. A plastic film 11 or sheet 10 has a water soluble polymer layer 12 on its one surface to prevent the drying of a concrete wall surface after placement. If the surface of the curing sheet is directly decorated, it does not need to be peeled off but can be used as it is as a wall surface material constituting the facing. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

本発明は、水の蒸散を抑制する目的で用いられる基礎コンクリートの養生シートに関するものである。   The present invention relates to a curing sheet for basic concrete used for the purpose of suppressing transpiration of water.

従来、コンクリート基礎は次のように構築される。まず、離型剤を塗った型枠を基礎周りに設置してからコンクリートを打設する。数日後に型枠を外して、コンクリート構造材として、十分な強度及び耐久性を得るために、養生シートを付設して十分な養生を行う。ここで、離型剤を塗るのは硬化後にコンクリートを型枠から剥がし易くするためであり、養生シートを付設するのはコンクリートの乾燥を防ぐためである。しかし、この従来の構築方法では、型枠に離型剤を塗ることと、型枠を外した後に養生シートを付設することの２工程が必要となる。また、通常、コンクリートと養生シートとは完全には密着しておらず、ガムテープなどでシート間をとめているので、風でめくれたり、隙間から、水が蒸散したりして十分強剛にコンクリートを養生できない問題があった。そこで、この工程を１回に簡略化し、かつ養生シートをコンクリート表面に密着させて水の蒸散を防止するために以下のものが提案されている。   Conventionally, a concrete foundation is constructed as follows. First, concrete is placed after a formwork coated with a release agent is installed around the foundation. A few days later, the mold is removed, and a curing sheet is attached to the concrete structure material to obtain sufficient strength and durability. Here, the reason why the release agent is applied is to make it easy to peel the concrete from the mold after curing, and the curing sheet is attached to prevent the concrete from drying. However, this conventional construction method requires two steps of applying a release agent to the mold and attaching a curing sheet after removing the mold. Also, the concrete and the curing sheet are usually not completely in close contact with each other, and the gap between the sheets is secured with gum tape, etc., so that the concrete is sufficiently rigid because it is turned up by the wind or water evaporates from the gap. There was a problem that could not be cured. Therefore, the following has been proposed in order to simplify this process once and prevent the evaporation of water by bringing the curing sheet into close contact with the concrete surface.

例えば、型枠の表面に着脱可能に貼着されるとともに、コンクリート打設面側に向けて拡径化した複数の突起を突出形成した養生シートがある。この養生シートによれば、型面に養生シートを貼着した状態で型枠内部にコンクリートを打設し、コンクリートの固化後に型枠を脱型すればシートの突起がコンクリート表面に食い込んだ状態で残置することができる。そして、養生終了後は、養生シートをコンクリート表面から強制的に引張れば、シートは前記突起を弾性歪曲しつつコンクリート表面から引き剥がすか、或いは突起の根元を切断してシートを撤去することができるという効果を有するものである（特許文献１参照）。   For example, there is a curing sheet that is detachably attached to the surface of a formwork and has a plurality of protrusions that are expanded in diameter toward the concrete casting surface side. According to this curing sheet, when the curing sheet is stuck on the mold surface, concrete is placed inside the mold, and if the mold is removed after the concrete is solidified, the protrusions of the sheet have bite into the concrete surface. Can be left behind. After the curing is completed, if the curing sheet is forcibly pulled from the concrete surface, the sheet may be peeled off from the concrete surface while elastically distorting the protrusion, or the base of the protrusion may be cut and the sheet removed. It has the effect that it can do (refer patent document 1).

しかし、この養生シートは、突起に対応してコンクリート表面に形成された穴は、モルタルなどの充填材による補修処理によって埋める必要があるという問題点があった。
特開平７−１０２７６３号公報 However, this curing sheet has a problem in that holes formed on the concrete surface corresponding to the protrusions need to be filled by a repair process using a filler such as mortar.
JP 7-102763 A

そこで、本発明は、以上の課題を解決するためになされたものであって、その目的とするところは、１）コンクリート打設前に型枠に離型剤を塗っておく、型枠を取り外した後の養生シートを付設する、という二度手間を一回に省略することができ、２）養生シートが風でめくれたりせず、コンクリートと十分密着して水の蒸散を防止して、強剛なコンクリートとすることができる養生シートを提供することにある。   Therefore, the present invention has been made to solve the above-mentioned problems, and the object of the present invention is as follows. 1) A mold release agent is applied to the mold before placing the concrete, and the mold is removed. It is possible to save the time and effort of attaching a curing sheet after the heat treatment at once. 2) The curing sheet does not turn over with the wind, and it adheres well to the concrete to prevent water transpiration, and strong. The object is to provide a curing sheet that can be made of rigid concrete.

以上のような課題を解決するために、本発明のコンクリートの養生シートは、コンクリートの型枠に予め付設して使用する養生シートであり、プラスチックフィルム又はシートの一方表面に水溶性ポリマー層を設けたことを特徴とする。本発明の養生シートに用いられるプラスチックフィルム又はシートは、コンクリート壁面の乾燥を防止するためのものである。従って、最低限水蒸気の透過を防止する程度の気密性を有するものであればよく、プラスチックフィルム又はシートの素材としては前記要件を満たすものであれば限定されない。具体的には、気密性の高さや製品価格の安定性から、ＰＥ、ＰＰ、ＰＥＴ、ＰＶＣ又はナイロン（登録商標）等を用いるとよい。また、使用時の取り扱い性の高さや丈夫さ等を考慮すると、５〜５００μｍの厚さのプラスチックフィルムを使用するとよい。尚、使用するプラスチックフィルム又はシート中には繊維等が混合していても構わない。   In order to solve the problems as described above, the concrete curing sheet of the present invention is a curing sheet that is pre-attached to a concrete mold and provided with a water-soluble polymer layer on one surface of a plastic film or sheet. It is characterized by that. The plastic film or sheet used for the curing sheet of the present invention is for preventing drying of the concrete wall surface. Accordingly, it is sufficient that it has airtightness that prevents water vapor from passing through at least, and the plastic film or sheet material is not limited as long as it satisfies the above requirements. Specifically, PE, PP, PET, PVC, nylon (registered trademark), or the like may be used because of its high airtightness and stable product price. In consideration of the high handling property and durability during use, it is preferable to use a plastic film having a thickness of 5 to 500 μm. It should be noted that fibers or the like may be mixed in the plastic film or sheet to be used.

一方、プラスチックフィルム又はシートの一方表面に設ける水溶性ポリマー層は、打設したコンクリート中に含まれる水分で溶解して、コンクリート中に分散、混合し、コンクリートの乾燥とともに乾固し、その密着力によって該プラスチックフィルム又はシートの硬化したコンクリートへの密着性を確保するようになっている。この水溶性ポリマー層を構成するポリマー成分としては、例えばポリビニルアルコール、ポリビニルエーテル、ポリビニルピロリドン、エチレン−酢酸ビニル共重合体、フェノール樹脂、ポリアクリル酸金属塩などの合成樹脂系ポリマー、澱粉糊、メチルセルロース、ヒドロキシセルロース、エチルヒドロキシエチルセルロース、カルボキシメチルセルロースなどのセルロース系ポリマー、ゼラチンなどのタンパク質系ポリマー等を挙げることができる。中でも取り扱い性、価格、性能の面から、ポリビニルアルコールやエチレン−酢酸ビニル共重合体などが好ましい。この水溶性ポリマー層は、十分な密着性を確保するため、目付量が３〜１００ｇ／ｍ2であることが望ましい。この水溶性ポリマー層は、無孔のシート状のほか、穴あきシート状、ネット状、蜘蛛の巣状、ストライプ状などの形態を採ることができる。 On the other hand, the water-soluble polymer layer provided on one surface of the plastic film or sheet dissolves with the water contained in the cast concrete, disperses and mixes in the concrete, and dries as the concrete dries. Thus, the adhesion of the plastic film or sheet to the hardened concrete is secured. Examples of the polymer component constituting the water-soluble polymer layer include polyvinyl alcohol, polyvinyl ether, polyvinyl pyrrolidone, ethylene-vinyl acetate copolymer, phenolic resin, polyacrylic acid metal salt and other synthetic resin-based polymers, starch paste, and methylcellulose. , Cellulose-based polymers such as hydroxycellulose, ethylhydroxyethylcellulose and carboxymethylcellulose; and protein-based polymers such as gelatin. Of these, polyvinyl alcohol, ethylene-vinyl acetate copolymer and the like are preferable from the viewpoints of handleability, cost, and performance. The water-soluble polymer layer preferably has a basis weight of 3 to 100 g / m 2 in order to ensure sufficient adhesion. The water-soluble polymer layer may take a non-porous sheet shape, a perforated sheet shape, a net shape, a spider web shape, a stripe shape, or the like.

本発明の養生シートの作製方法としては、例えば図８の（ａ）（ｂ）に示すように、プラスチックフィルム又はシート１１の一方面に水で溶解した水溶性ポリマー１２を塗布する方法がある。また、水溶性ポリマーを予め穴あきシート状、ネット状、蜘蛛の巣状に成形しておき、これらの水溶性ポリマーシート１２の一面に水をかけてシート表面の樹脂の一部を溶解させてプラスチックフィルム又はシート１１の一方面に積層した後、乾燥させることで、プラスチックフィルム又はシート１１に水溶性ポリマーシート１２を密着させて養生シート１０を作製する方法などもある。   As a preparation method of the curing sheet of the present invention, for example, as shown in FIGS. 8A and 8B, there is a method in which a water-soluble polymer 12 dissolved in water is applied to one surface of a plastic film or sheet 11. In addition, a water-soluble polymer is previously formed into a perforated sheet, net, or spider web, and water is applied to one surface of these water-soluble polymer sheets 12 to dissolve a part of the resin on the sheet surface. There is also a method of preparing the curing sheet 10 by laminating on one surface of the plastic film or sheet 11 and then drying, thereby bringing the water-soluble polymer sheet 12 into close contact with the plastic film or sheet 11.

本発明の養生シートは、プラスチックフィルム又はシートと水溶性ポリマー層との間に断熱層を設ける形態を採ることもできる。断熱層を設けることによって、暑中下の日射や寒中期の低温などの急激な温度変化による影響を防止することができ、またコンクリートと水の反応効率の向上を図り、より強いコンクリートとすることができるようになる。   The curing sheet of the present invention can take a form in which a heat insulating layer is provided between the plastic film or sheet and the water-soluble polymer layer. By providing a heat insulation layer, it is possible to prevent the effects of sudden temperature changes such as solar radiation under the heat and low temperatures during the cold season, and to improve the reaction efficiency of concrete and water, making it stronger concrete. become able to.

養生シートを型枠に付設する方法としては特に限定されない。例えば、プラスチックフィルム又はシート表面に両面テープを貼りつけたり、接着剤を塗布して付設したりすることができる。両面テープの場合は、粘着層の表面には離型用フィルムが設けてあるので、使用時に離型用フィルムを剥がせば、粘着層が露出して型枠に容易に養生シートを貼着することができるようになるため好適である。勿論、両面テープや接着剤は、表面全体に設けても構わないし、部分的に設けても構わない。また両面テープや接着剤の接着強度は、プラスチックフィルム又はシートがコンクリートに密着する力よりも弱い力で剥がすことができる強度のものを用いれば、型枠を剥がす際にコンクリートに養生シートを残置させることができて都合がよい。   It does not specifically limit as a method of attaching a curing sheet to a formwork. For example, a double-sided tape can be attached to the surface of a plastic film or sheet, or an adhesive can be applied and attached. In the case of double-sided tape, a release film is provided on the surface of the adhesive layer, so if the release film is peeled off during use, the adhesive layer is exposed and the curing sheet is easily attached to the mold. This is preferable. Of course, the double-sided tape and the adhesive may be provided on the entire surface or may be provided partially. Also, if the adhesive strength of the double-sided tape or adhesive is such that the plastic film or sheet can be peeled with a force weaker than the force to adhere to the concrete, the curing sheet is left on the concrete when the formwork is peeled off. It is convenient to be able to.

こうして作製された養生シートは、まず、プラスチックフィルム又はシート側が型枠内面側にくるように型枠に付設して、この型枠をコンクリート基礎等の構造物を形成する場所に設置した後、コンクリートを打設する。そして、コンクリートが硬化した後、前記養生シートのプラスチックフィルム又はシートをコンクリート壁面に密着させた状態、すなわち、水溶性ポリマー層が若干コンクリート内に入り込んで溶融固化して一定の密着力を有した状態のまま、型枠のみを除去する。この状態で養生シートは、コンクリート面を覆うように保護されているので、水分がコンクリート表面から蒸発することはなく、また、断熱材を有する養生シートを用いれば、コンクリートの急激な温度変化を防止でき、水和反応を早めることができ、効果的に養生が促進される。そして、十分に養生がなされたら養生シートを剥がして、コンクリート構造物が完成する。また、養生シートの表面に直接化粧面を設けたり、化粧面を有する化粧シート材を貼りつけたりすることによって、養生シート自体が化粧面とすることができるようにしておけば、養生シートを剥がすことなく、そのまま化粧面を構成する表面部材として使用することができるようになる。   The curing sheet prepared in this way is first attached to the mold so that the plastic film or sheet side is on the inner surface of the mold, and this mold is installed in a place where a structure such as a concrete foundation is formed. To cast. And after the concrete is hardened, the plastic film or sheet of the curing sheet is in close contact with the concrete wall surface, that is, the water-soluble polymer layer is slightly melted and solidified into the concrete and has a certain adhesive force. Remove only the formwork. In this state, the curing sheet is protected so as to cover the concrete surface, so that moisture does not evaporate from the concrete surface, and if a curing sheet having a heat insulating material is used, rapid temperature change of the concrete is prevented. Can accelerate the hydration reaction and effectively promote curing. When the curing is sufficiently performed, the curing sheet is peeled off to complete the concrete structure. In addition, if the curing sheet itself can be made into a decorative surface by providing a decorative surface directly on the surface of the curing sheet or attaching a decorative sheet material having a decorative surface, the curing sheet can be peeled off. However, it can be used as a surface member constituting the decorative surface as it is.

本発明の養生シートによれば、予め型枠に養生シートを付設した状態でコンクリートを打設するので、型枠に離型剤を塗っておく必要がなくなり、型枠を外せば養生シートはコンクリートに付設されることになるので、改めて養生シートを付設するという作業を省略することができる。   According to the curing sheet of the present invention, since the concrete is placed in a state where the curing sheet is previously attached to the mold, it is not necessary to apply a release agent to the mold, and if the mold is removed, the curing sheet becomes concrete. Therefore, the work of attaching a curing sheet anew can be omitted.

また、養生シートは、水溶性ポリマー層を介して全面でコンクリートに密着しているので、風で養生シートがめくれたりすることがない。一方プラスチックフィルム又はシートは水の蒸散を防止するため、十分な水和反応をさせることができて強剛なコンクリートとすることができる。   Moreover, since the curing sheet is in close contact with the concrete through the water-soluble polymer layer, the curing sheet does not turn over due to wind. On the other hand, the plastic film or sheet can be sufficiently hardened to prevent transpiration of water, and can be made to be strong concrete.

以下、本発明を実施するための最良の形態について図１に沿って説明する。図１及び図２は、本発明の実施例１にかかるコンクリートの養生シート１０の断面図を示している。本実施例に係る養生シート１０は、プラスチックフィルム１１と、水溶性ポリマー層１２とからなる。   Hereinafter, the best mode for carrying out the present invention will be described with reference to FIG. 1 and 2 are sectional views of a concrete curing sheet 10 according to Example 1 of the present invention. A curing sheet 10 according to this embodiment includes a plastic film 11 and a water-soluble polymer layer 12.

コンクリートの養生シート１０は、両面テープを部分的に貼りつけて型枠２０に付設して使用される。この養生シートが付設された型枠２０は、コンクリート構造物を作製する所定の位置に取付けられ、型枠２０内部にコンクリートが打設される（図２）。そして、コンクリートの打設に伴い、コンクリート中に含まれる水分で水溶性ポリマー層が溶解して、コンクリート中に分散、混合する。コンクリートの硬化とともに、溶解した水溶性ポリマーも乾固し、その密着力によって該プラスチックフィルム又はシートが硬化したコンクリートへの密着することになる。この段階で、養生シート１０をコンクリートに密着させた状態のまま、すなわち、養生シートをコンクリート表面に残置した状態のままで型枠が外される（図３）。そして、コンクリートが十分に養生し、強度及び耐久性を確保した後、図４に示すように、養生シート１０をコンクリートから剥離して、コンクリート構造物は完成する（図５）。こうして作製されたコンクリート構造物によれば、プラスチックフィルム１１によって水分の蒸散が防止され、水和反応に十分な水分が確保した状態で硬化するため、堅固なコンクリート構造物を構築することができる。   The concrete curing sheet 10 is used by partially attaching a double-sided tape to the formwork 20. The formwork 20 provided with the curing sheet is attached to a predetermined position for producing a concrete structure, and concrete is placed inside the formwork 20 (FIG. 2). As the concrete is placed, the water-soluble polymer layer is dissolved by the water contained in the concrete, and dispersed and mixed in the concrete. As the concrete hardens, the dissolved water-soluble polymer also dries out, and the plastic film or sheet adheres to the hardened concrete by its adhesion. At this stage, the mold is removed with the curing sheet 10 kept in close contact with the concrete, that is, with the curing sheet remaining on the concrete surface (FIG. 3). And after concrete hardens | cures fully and intensity | strength and durability are ensured, as shown in FIG. 4, the curing sheet 10 is peeled from concrete and a concrete structure is completed (FIG. 5). According to the concrete structure produced in this way, the transpiration of moisture is prevented by the plastic film 11 and the resin is cured in a state where sufficient moisture is ensured for the hydration reaction, so that a solid concrete structure can be constructed.

図６は、本発明の実施例２にかかるコンクリートの養生シート１０ａの断面図を示している。実施例２に係るコンクリートの養生シート１０aは、プラスチックフィルム１１ａの水溶性接着剤層１２ａの反対側の表面にタイル状の化粧模様を有する化粧フィルム１３ａを貼り合わせたものである。すなわち、実施例１の養生シート１０ａに対して表面にタイル状の化粧面を設けたものである。それ以外の構成は実施例１と同様である。   FIG. 6: has shown sectional drawing of the curing sheet 10a of the concrete concerning Example 2 of this invention. The concrete curing sheet 10a according to Example 2 is obtained by bonding a decorative film 13a having a tile-like decorative pattern to the surface of the plastic film 11a opposite to the water-soluble adhesive layer 12a. That is, a tile-shaped decorative surface is provided on the surface of the curing sheet 10a of Example 1. Other configurations are the same as those in the first embodiment.

この養生シート１０aは、実施例１と同様にして、型枠を外した後は、コンクリート面に密着させた状態でコンクリート面に付設される。この後、この実施例２における養生シート１０ａによれば、図７に示すようにコンクリート構造物の表面に化粧面を形成することになるので、養生シート１０ａを剥がすことなくそのまま化粧壁面として使用する。なお、図７においては、タイル状の模様にしてあるが、この模様に限定されるものでないことは言うまでもない。   The curing sheet 10a is attached to the concrete surface in a state of being in close contact with the concrete surface after removing the formwork in the same manner as in Example 1. Thereafter, according to the curing sheet 10a in Example 2, a decorative surface is formed on the surface of the concrete structure as shown in FIG. 7, and therefore, the curing sheet 10a is used as it is as a decorative wall surface without peeling off. . In FIG. 7, a tile-shaped pattern is used, but it goes without saying that the pattern is not limited to this pattern.

実施例１に係るコンクリートの養生シートを示す断面図である。1 is a cross-sectional view showing a concrete curing sheet according to Example 1. FIG. 実施例１に係るコンクリートの養生シートを用いて、コンクリート構造物を作製する１工程を示す断面図である。It is sectional drawing which shows 1 process of producing a concrete structure using the concrete curing sheet which concerns on Example 1. FIG. 実施例１に係るコンクリートの養生シートを用いて、コンクリート構造物を作製する１工程を示す断面図である。It is sectional drawing which shows 1 process of producing a concrete structure using the concrete curing sheet which concerns on Example 1. FIG. 実施例１に係るコンクリートの養生シートを用いて、コンクリート構造物を作製する１工程を示す断面図である。It is sectional drawing which shows 1 process of producing a concrete structure using the concrete curing sheet which concerns on Example 1. FIG. 実施例１に係るコンクリートの養生シートを用いて作製されたコンクリート構造物を示す断面図である。It is sectional drawing which shows the concrete structure produced using the concrete curing sheet which concerns on Example 1. FIG. 実施例２に係るコンクリートの養生シートを示す断面図である。It is sectional drawing which shows the curing sheet | seat of the concrete which concerns on Example 2. FIG. 実施例２に係るコンクリートの養生シートによって化粧面が形成されたコンクリート壁面を示す斜視図である。It is a perspective view which shows the concrete wall surface in which the decorative surface was formed with the curing sheet of the concrete which concerns on Example 2. FIG. 本発明の養生シートの作製方法のバリエーションを示す模式図である。It is a schematic diagram which shows the variation of the preparation methods of the curing sheet of this invention.

符号の説明Explanation of symbols

１０ 養生シート
１１ プラスチックフィルム
１２ 水溶性ポリマー層
２０ 型枠
10 Curing sheet 11 Plastic film 12 Water-soluble polymer layer 20 Mold

Claims (6)

型枠に予め付設した後、コンクリートを打設して使用されるコンクリートの養生シートにおいて、
プラスチックフィルム又はシートの一方表面に水溶性ポリマー層を設けたことを特徴とするコンクリートの養生シート。 In the curing sheet of concrete used by placing concrete in advance after being attached to the formwork,
A concrete curing sheet comprising a water-soluble polymer layer on one surface of a plastic film or sheet. 水溶性ポリマー層の目付量が３〜１００ｇ／ｍ2であることを特徴とする請求項１記載のコンクリートの養生シート。 2. The concrete curing sheet according to claim 1, wherein the basis weight of the water-soluble polymer layer is 3 to 100 g / m < 2 >. プラスチックフィルム又はシートは、ＰＥ、ＰＰ、ＰＥＴ、ＰＶＣ又はナイロンからなることを特徴とする請求項１又は２記載のコンクリートの養生シート。 3. The concrete curing sheet according to claim 1, wherein the plastic film or sheet is made of PE, PP, PET, PVC or nylon. プラスチックフィルムの厚みが５〜５００μｍであることを特徴とする請求項１〜３のいずれかに記載のコンクリートの養生シート。 The concrete curing sheet according to any one of claims 1 to 3, wherein the plastic film has a thickness of 5 to 500 µm. プラスチックフィルム又はシートの他方表面に直接化粧面を設け、又は化粧面を形成する化粧用シート材を貼り合わせてなり、コンクリート養生後も剥がすことなく化粧面として使用可能な請求項１〜４のいずれかに記載のコンクリートの養生シート。 Any one of claims 1 to 4, wherein a decorative surface is directly provided on the other surface of the plastic film or sheet, or a decorative sheet material for forming the decorative surface is bonded to each other, and can be used as a decorative surface without being peeled off after curing concrete. Curing sheet for concrete according to crab. 請求項１〜５のいずれかに記載のコンクリートの養生シートを使用してコンクリートを養生する方法であって、
予めプラスチックフィルム又はシートの他方表面側が型枠内面側となるように前記養生シートを付設した型枠を作製する工程、
前記型枠を基礎周りに設置し、型枠内にコンクリートを打設する工程、
コンクリートの打設に伴って前記プラスチックフィルム又はシートの一方表面側の水溶性ポリマー層をコンクリートに密着させる工程、
コンクリートが硬化した後、前記養生シートの一方表面側の水溶性ポリマー層がコンクリート壁面に密着した状態で残置させつつ型枠を除去する工程、
前記コンクリートを養生させる工程、
とからなることを特徴とするコンクリートの養生方法。
A method for curing concrete using the concrete curing sheet according to any one of claims 1 to 5,
A step of producing a mold having the curing sheet attached in advance so that the other surface side of the plastic film or sheet becomes the mold inner surface,
Placing the mold around the foundation and placing concrete in the mold;
A step of closely adhering the water-soluble polymer layer on one surface side of the plastic film or sheet to the concrete as the concrete is placed;
After the concrete is cured, a step of removing the mold while leaving the water-soluble polymer layer on one surface side of the curing sheet in close contact with the concrete wall surface;
Curing the concrete;
A concrete curing method characterized by comprising:
JP2005270098A 2005-09-16 2005-09-16 Concrete curing sheet Withdrawn JP2007077754A (en)