JP2007023235A - Water-based adhesive composition - Google Patents

Water-based adhesive composition Download PDF

Info

Publication number
JP2007023235A
JP2007023235A JP2005211126A JP2005211126A JP2007023235A JP 2007023235 A JP2007023235 A JP 2007023235A JP 2005211126 A JP2005211126 A JP 2005211126A JP 2005211126 A JP2005211126 A JP 2005211126A JP 2007023235 A JP2007023235 A JP 2007023235A
Authority
JP
Japan
Prior art keywords
poly
acrylamide
methyl
water
methoxyethyl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2005211126A
Other languages
Japanese (ja)
Other versions
JP4935011B2 (en
Inventor
Takahiro Okamatsu
隆裕 岡松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yokohama Rubber Co Ltd
Original Assignee
Yokohama Rubber Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yokohama Rubber Co Ltd filed Critical Yokohama Rubber Co Ltd
Priority to JP2005211126A priority Critical patent/JP4935011B2/en
Publication of JP2007023235A publication Critical patent/JP2007023235A/en
Application granted granted Critical
Publication of JP4935011B2 publication Critical patent/JP4935011B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<P>PROBLEM TO BE SOLVED: To obtain a water-based adhesive composition that has excellent compatibility, drying property and adhesiveness to metal materials. <P>SOLUTION: The water-based adhesive composition comprises an aqueous polyurethane resin containing an acrylic temperature-responsive polymer on the surface of resin particle and an acrylic emulsion. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

本発明は、水系接着剤組成物に関し、より詳しくは、水系ポリウレタン樹脂とアクリルエマルジョンとを含有する水系接着剤組成物に関する。   The present invention relates to an aqueous adhesive composition, and more particularly to an aqueous adhesive composition containing an aqueous polyurethane resin and an acrylic emulsion.

溶剤系接着剤を使用する生産ラインにおいて、職場環境の改善や、製品のVOC対策等の観点から、接着剤の無溶剤化の技術が開発されてきている。この無溶剤化の技術としては、水系ポリウレタンエマルジョン(水系ポリウレタン樹脂)を用いることが知られている。
また、この水系ポリウレタン樹脂は、金属材料への密着性(接着性)の観点から、アクリルエマルジョンとブレンドして用いることが知られている。
しかしながら、このブレンド物は、水系ポリウレタン樹脂とアクリルエマルジョンとの相溶性(以下、単に「相溶性」ともいう。)が悪いことから、充分な接着剤皮膜となり得ず、接着性に劣る場合があった。
In production lines using solvent-based adhesives, solvent-free technology for adhesives has been developed from the viewpoint of improving the work environment and taking measures against VOCs in products. As this solvent-free technology, it is known to use an aqueous polyurethane emulsion (aqueous polyurethane resin).
Further, it is known that this water-based polyurethane resin is used by blending with an acrylic emulsion from the viewpoint of adhesion (adhesiveness) to a metal material.
However, since this blend has poor compatibility between the water-based polyurethane resin and the acrylic emulsion (hereinafter, also simply referred to as “compatibility”), it cannot form a sufficient adhesive film and may have poor adhesion. It was.

これに対し、相溶性を改善させる観点から、ウレタンプレポリマーとエチレン性不飽和単量体とを水媒体中で重合させて得られる水系ポリウレタン樹脂や、ポリウレタン系エマルジョンの存在下でエチレン性不飽和モノマーを乳化重合して得られる複合樹脂エマルジョン等が知られている(例えば、特許文献1〜3等参照。)。
また、特許文献4には、「(A)水性ポリウレタンエマルジョンと(B)水性アクリルエマルジョンからなる水性エマルジョン組成物において、(A)/(B)が固形分重量比で2/1〜1/20であり、かつ、
(A)の水性ポリウレタンエマルジョンが、
(イ)有機ポリイソシアネート。
(ロ)低分子ポリオールと、芳香族ポリカルボン酸及び脂肪族ポリカルボン酸から製造されるポリエステルポリオールを含有する高分子ポリオール。
(ハ)多官能ヒドラジド化合物を含有する活性水素基含有化合物。
(ニ)親水性極性基及び活性水素基含有化合物。から製造されるポリマーを含有し、
(B)の水性アクリルエマルジョンが、ケトン基又はアルデヒド基を有する重合性不飽和単量体を含有する重合性不飽和単量体混合物。から製造されるポリマーを含有することを特徴とする水性ポリウレタン−アクリルエマルジョン組成物。」が提案されている。
On the other hand, from the viewpoint of improving the compatibility, ethylenically unsaturated in the presence of an aqueous polyurethane resin obtained by polymerizing a urethane prepolymer and an ethylenically unsaturated monomer in an aqueous medium or a polyurethane emulsion. A composite resin emulsion obtained by emulsion polymerization of monomers is known (for example, see Patent Documents 1 to 3).
Patent Document 4 states that “in an aqueous emulsion composition comprising (A) an aqueous polyurethane emulsion and (B) an aqueous acrylic emulsion, (A) / (B) is 2/1 to 1/20 in weight ratio of solids. And
The aqueous polyurethane emulsion (A) is
(A) Organic polyisocyanate.
(B) A polymer polyol containing a low-molecular polyol and a polyester polyol produced from an aromatic polycarboxylic acid and an aliphatic polycarboxylic acid.
(C) An active hydrogen group-containing compound containing a polyfunctional hydrazide compound.
(D) A hydrophilic polar group and active hydrogen group-containing compound. Containing a polymer produced from
A polymerizable unsaturated monomer mixture in which the aqueous acrylic emulsion of (B) contains a polymerizable unsaturated monomer having a ketone group or an aldehyde group. An aqueous polyurethane-acrylic emulsion composition comprising a polymer produced from Is proposed.

しかしながら、このような水系ポリウレタン樹脂および複合樹脂エマルジョンならびに水性ポリウレタン−アクリルエマルジョン組成物を用いた場合であっても、相溶性は良好となるものの、溶剤系接着剤と同等レベルのライン速度を維持できない、すなわち、乾燥性が劣るため、金属材料との接着性が不十分であるという問題があった。   However, even when such an aqueous polyurethane resin and composite resin emulsion and an aqueous polyurethane-acrylic emulsion composition are used, the compatibility is good, but the line speed equivalent to that of the solvent-based adhesive cannot be maintained. That is, since the drying property is inferior, there is a problem that the adhesion to the metal material is insufficient.

特開平8−165318号公報JP-A-8-165318 特開2001−302714号公報JP 2001-302714 A 特開2004−269700号公報JP 2004-269700 A 特開平10−265735号公報Japanese Patent Laid-Open No. 10-265735

そこで、本発明は、相溶性および乾燥性に優れ、金属材料との接着性も良好な水系接着剤組成物を提供することを課題とする。   Then, this invention makes it a subject to provide the aqueous adhesive composition which is excellent in compatibility and drying property, and has favorable adhesiveness with a metal material.

本発明者は、上記課題を解決するため鋭意検討した結果、樹脂粒子の表面にアクリル系温度応答性ポリマーを有する水系ポリウレタン樹脂と、アクリルエマルジョンとを含有する、水系接着剤組成物が、相溶性および乾燥性に優れ、金属材料との接着性も良好となることを見出し、本発明を完成させた。   As a result of intensive studies to solve the above problems, the present inventors have found that an aqueous adhesive composition containing an aqueous polyurethane resin having an acrylic temperature-responsive polymer on the surface of resin particles and an acrylic emulsion is compatible. And it discovered that it was excellent in drying property and adhesiveness with a metal material, and completed this invention.

即ち、本発明は、下記(1)〜(6)に記載の水系接着剤組成物を提供する。
(1)樹脂粒子表面にアクリル系温度応答性ポリマーを有する水系ポリウレタン樹脂と、アクリルエマルジョンとを含有する、水系接着剤組成物。
(2)上記アクリル系温度応答性ポリマーが、共有結合を介して樹脂粒子表面に存在する、上記(1)に記載の水系接着剤組成物。
(3)上記アクリル系温度応答性ポリマーが、アクリルアミド系ポリマーである、上記(1)または(2)に記載の水系接着剤組成物。
(4)上記アクリルアミド系ポリマーが、ポリ−N−エチルアクリルアミド、ポリ−N−n−プロピルアクリルアミド、ポリ−N−イソプロピルアクリルアミド、ポリ−N−シクロプロピルアクリルアミド、ポリ−N,N−ジエチルアクリルアミド、ポリ−N−メチル−N−エチルアクリルアミド、ポリ−N−メチル−N−n−プロピルアクリルアミド、ポリ−N−メチル−N−イソプロピルアクリルアミド、ポリ−N−アクリロイルピペリジン、ポリ−N−アクリロイルピロリジン、ポリ−N−アクリロイルモルホリン、ポリ−N−メトキシプロピルアクリルアミド、ポリ−N−エトキシプロピルアクリルアミド、ポリ−N−イソプロポキシプロピルアクリルアミド、ポリ−N−エトキシエチルアクリルアミド、ポリ−N−(2,2−ジメトキシエチル)−N−メチルアクリルアミド、ポリ−N−1−メチル−2−メトキシエチルアクリルアミド、ポリ−N−1−メトキシメチルプロピルアクリルアミド、ポリ−N−ジ(2−メトキシエチル)アクリルアミド、ポリ−N−2−メトキシエチル−N−n−プロピルアクリルアミド、ポリ−N−2−メトキシエチル−N−エチルアクリルアミド、ポリ−N−2−メトキシエチル−N−イソプロピルアクリルアミド、ポリ−N−メトキシエトキシプロピルアクリルアミド、ポリ−N−テトラヒドロフルフリルアクリルアミド、ポリ−N−(1,3−ジオキソラン−2−イル)メチルアクリルアミド、ポリ−N−メチル−N−(1,3−ジオキソラン−2−イル)メチルアクリルアミド、ポリ−N−シクロプロピルアクリルアミド、ポリ−N−ピロリジノメチルアクリルアミド、ポリ−N−ピペリジノメチルアクリルアミド、ポリ−N−2−モルホリノエチルアクリレート、ポリ−N−2−モルホリノエトキシエチルアクリレートおよびこれらに対応するメタクリレートからなる群から選択される少なくとも一種である、上記(3)に記載の水系接着剤組成物。
(5)上記水系ポリウレタン樹脂が、
イソシアネート基を2個以上有するポリイソシアネート化合物(A)、水酸基を2個以上有するポリオール化合物(B)、イソシアネート基と反応性を有する基およびイオン性基を有する化合物(C)ならびにイソシアネート基と反応性を有する基を有するエチレン性不飽和単量体(D)を共重合させて生成するウレタンプレポリマーを水媒体中で分散させて得られるウレタンエマルジョンと、
上記アクリル系温度応答性ポリマーを生成するモノマー(E)と、
を共重合させて得られる、上記(1)〜(4)のいずれかに記載の水系接着剤組成物。
(6)上記モノマー(E)が、N−エチルアクリルアミド、N−n−プロピルアクリルアミド、N−イソプロピルアクリルアミド、N−シクロプロピルアクリルアミド、N,N−ジエチルアクリルアミド、N−メチル−N−エチルアクリルアミド、N−メチル−N−n−プロピルアクリルアミド、N−メチル−N−イソプロピルアクリルアミド、N−アクリロイルピペリジン、N−アクリロイルピロリジン、N−アクリロイルモルホリン、N−メトキシプロピルアクリルアミド、N−エトキシプロピルアクリルアミド、N−イソプロポキシプロピルアクリルアミド、N−エトキシエチルアクリルアミド、N−(2,2−ジメトキシエチル)−N−メチルアクリルアミド、N−1−メチル−2−メトキシエチルアクリルアミド、N−1−メトキシメチルプロピルアクリルアミド、N−ジ(2−メトキシエチル)アクリルアミド、N−2−メトキシエチル−N−n−プロピルアクリルアミド、N−2−メトキシエチル−N−エチルアクリルアミド、N−2−メトキシエチル−N−イソプロピルアクリルアミド、N−メトキシエトキシプロピルアクリルアミド、N−テトラヒドロフルフリルアクリルアミド、N−(1,3−ジオキソラン−2−イル)メチルアクリルアミド、N−メチル−N−(1,3−ジオキソラン−2−イル)メチルアクリルアミド、N−シクロプロピルアクリルアミド、N−ピロリジノメチルアクリルアミド、N−ピペリジノメチルアクリルアミド、N−2−モルホリノエチルアクリレート、N−2−モルホリノエトキシエチルアクリレートおよびこれらに対応するメタクリレートからなる群から選択される少なくとも一種であり、
上記ウレタンエマルジョンと、上記モノマー(E)とを、生成するアクリル系温度応答性ポリマーの相転移温度より低い温度で共重合させて得られる、上記(5)に記載の水系接着剤組成物。
That is, this invention provides the aqueous adhesive composition as described in following (1)-(6).
(1) A water-based adhesive composition containing a water-based polyurethane resin having an acrylic temperature-responsive polymer on the surface of resin particles and an acrylic emulsion.
(2) The aqueous adhesive composition according to (1), wherein the acrylic temperature-responsive polymer is present on the surface of the resin particles through a covalent bond.
(3) The aqueous adhesive composition according to (1) or (2) above, wherein the acrylic temperature-responsive polymer is an acrylamide polymer.
(4) The acrylamide polymer is poly-N-ethylacrylamide, poly-Nn-propylacrylamide, poly-N-isopropylacrylamide, poly-N-cyclopropylacrylamide, poly-N, N-diethylacrylamide, poly -N-methyl-N-ethylacrylamide, poly-N-methyl-Nn-propylacrylamide, poly-N-methyl-N-isopropylacrylamide, poly-N-acryloylpiperidine, poly-N-acryloylpyrrolidine, poly- N-acryloylmorpholine, poly-N-methoxypropylacrylamide, poly-N-ethoxypropylacrylamide, poly-N-isopropoxypropylacrylamide, poly-N-ethoxyethylacrylamide, poly-N- (2,2-dimethyl) Xylethyl) -N-methylacrylamide, poly-N-1-methyl-2-methoxyethylacrylamide, poly-N-1-methoxymethylpropylacrylamide, poly-N-di (2-methoxyethyl) acrylamide, poly-N- 2-methoxyethyl-Nn-propylacrylamide, poly-N-2-methoxyethyl-N-ethylacrylamide, poly-N-2-methoxyethyl-N-isopropylacrylamide, poly-N-methoxyethoxypropylacrylamide, poly -N-tetrahydrofurfurylacrylamide, poly-N- (1,3-dioxolan-2-yl) methylacrylamide, poly-N-methyl-N- (1,3-dioxolan-2-yl) methylacrylamide, poly- N-cyclopropylacrylamide, poly Selected from the group consisting of N-pyrrolidinomethylacrylamide, poly-N-piperidinomethylacrylamide, poly-N-2-morpholinoethyl acrylate, poly-N-2-morpholinoethoxyethyl acrylate and the corresponding methacrylates The aqueous adhesive composition according to (3), which is at least one kind.
(5) The water-based polyurethane resin is
Polyisocyanate compound (A) having 2 or more isocyanate groups, polyol compound (B) having 2 or more hydroxyl groups, compound (C) having an isocyanate group-reactive group and an ionic group, and isocyanate group-reactive A urethane emulsion obtained by dispersing a urethane prepolymer produced by copolymerizing an ethylenically unsaturated monomer (D) having a group containing
A monomer (E) for producing the acrylic temperature-responsive polymer;
The aqueous adhesive composition according to any one of the above (1) to (4), which is obtained by copolymerizing
(6) The monomer (E) is N-ethylacrylamide, Nn-propylacrylamide, N-isopropylacrylamide, N-cyclopropylacrylamide, N, N-diethylacrylamide, N-methyl-N-ethylacrylamide, N -Methyl-Nn-propylacrylamide, N-methyl-N-isopropylacrylamide, N-acryloylpiperidine, N-acryloylpyrrolidine, N-acryloylmorpholine, N-methoxypropylacrylamide, N-ethoxypropylacrylamide, N-isopropoxy Propylacrylamide, N-ethoxyethylacrylamide, N- (2,2-dimethoxyethyl) -N-methylacrylamide, N-1-methyl-2-methoxyethylacrylamide, N-1-methoxy Methylpropylacrylamide, N-di (2-methoxyethyl) acrylamide, N-2-methoxyethyl-Nn-propylacrylamide, N-2-methoxyethyl-N-ethylacrylamide, N-2-methoxyethyl-N- Isopropylacrylamide, N-methoxyethoxypropylacrylamide, N-tetrahydrofurfurylacrylamide, N- (1,3-dioxolan-2-yl) methylacrylamide, N-methyl-N- (1,3-dioxolan-2-yl) Methyl acrylamide, N-cyclopropyl acrylamide, N-pyrrolidinomethyl acrylamide, N-piperidinomethyl acrylamide, N-2-morpholinoethyl acrylate, N-2-morpholinoethoxyethyl acrylate and the like It is at least one selected from the group consisting of methacrylate,
The aqueous adhesive composition according to (5), which is obtained by copolymerizing the urethane emulsion and the monomer (E) at a temperature lower than the phase transition temperature of the acrylic temperature-responsive polymer to be produced.

以下に示すように、本発明によれば、相溶性および乾燥性に優れ、金属材料との接着性も良好な水系接着剤組成物を提供することができ、これにより、生産ラインにおける職場環境の改善や、製品のVOC対策を図ることができるため非常に有用である。   As shown below, according to the present invention, it is possible to provide a water-based adhesive composition that is excellent in compatibility and drying properties, and also has good adhesion to a metal material. This is very useful because it can improve and take measures against VOC of products.

本発明の水系接着剤組成物は、樹脂粒子表面にアクリル系温度応答性ポリマーを有する水系ポリウレタン樹脂と、アクリルエマルジョンとを含有する組成物である。
以下、水系ポリウレタン樹脂およびアクリルエマルジョンについて詳述する。
The aqueous adhesive composition of the present invention is a composition containing an aqueous polyurethane resin having an acrylic temperature-responsive polymer on the surface of resin particles and an acrylic emulsion.
Hereinafter, the water-based polyurethane resin and the acrylic emulsion will be described in detail.

[水系ポリウレタン樹脂]
本発明においては、上記水系ポリウレタン樹脂は、樹脂粒子表面にアクリル系温度応答性ポリマーを有する。
上記アクリル系温度応答性ポリマーは、相転移温度を有し、該相転移温度よりも低い温度ではランダムコイル状構造となり水溶性を示し、該相転移温度よりも高い温度では凝集したグロビュール状態となり非水溶性を示す温度応答性を有するポリマーであれば特に限定されず、アクリルアミド系ポリマーであるのが好ましい。
アクリルアミド系ポリマーとしては、具体的には、例えば、ポリ−N−エチルアクリルアミド、ポリ−N−n−プロピルアクリルアミド、ポリ−N−イソプロピルアクリルアミド、ポリ−N−シクロプロピルアクリルアミド、ポリ−N,N−ジエチルアクリルアミド、ポリ−N−メチル−N−エチルアクリルアミド、ポリ−N−メチル−N−n−プロピルアクリルアミド、ポリ−N−メチル−N−イソプロピルアクリルアミド、ポリ−N−アクリロイルピペリジン、ポリ−N−アクリロイルピロリジン、ポリ−N−アクリロイルモルホリン、ポリ−N−メトキシプロピルアクリルアミド、ポリ−N−エトキシプロピルアクリルアミド、ポリ−N−イソプロポキシプロピルアクリルアミド、ポリ−N−エトキシエチルアクリルアミド、ポリ−N−(2,2−ジメトキシエチル)−N−メチルアクリルアミド、ポリ−N−1−メチル−2−メトキシエチルアクリルアミド、ポリ−N−1−メトキシメチルプロピルアクリルアミド、ポリ−N−ジ(2−メトキシエチル)アクリルアミド、ポリ−N−2−メトキシエチル−N−n−プロピルアクリルアミド、ポリ−N−2−メトキシエチル−N−エチルアクリルアミド、ポリ−N−2−メトキシエチル−N−イソプロピルアクリルアミド、ポリ−N−メトキシエトキシプロピルアクリルアミド、ポリ−N−テトラヒドロフルフリルアクリルアミド、ポリ−N−(1,3−ジオキソラン−2−イル)メチルアクリルアミド、ポリ−N−メチル−N−(1,3−ジオキソラン−2−イル)メチルアクリルアミド、ポリ−N−シクロプロピルアクリルアミド、ポリ−N−ピロリジノメチルアクリルアミド、ポリ−N−ピペリジノメチルアクリルアミド、ポリ−N−2−モルホリノエチルアクリレート、ポリ−N−2−モルホリノエトキシエチルアクリレートおよびこれらに対応するメタクリレートならびにこれらの混合物等が挙げられる。
また、上記アクリル系温度応答性ポリマーは、共有結合を介して水系ポリウレタン樹脂の樹脂粒子表面に存在していることが好ましい。
[Water-based polyurethane resin]
In the present invention, the water-based polyurethane resin has an acrylic temperature-responsive polymer on the resin particle surface.
The acrylic temperature-responsive polymer has a phase transition temperature, becomes a random coil-like structure at a temperature lower than the phase transition temperature, exhibits water solubility, and becomes an agglomerated globule state at a temperature higher than the phase transition temperature. The polymer is not particularly limited as long as it is a water-soluble temperature-responsive polymer, and is preferably an acrylamide polymer.
Specific examples of the acrylamide polymer include poly-N-ethylacrylamide, poly-Nn-propylacrylamide, poly-N-isopropylacrylamide, poly-N-cyclopropylacrylamide, poly-N, N- Diethylacrylamide, poly-N-methyl-N-ethylacrylamide, poly-N-methyl-Nn-propylacrylamide, poly-N-methyl-N-isopropylacrylamide, poly-N-acryloylpiperidine, poly-N-acryloyl Pyrrolidine, poly-N-acryloylmorpholine, poly-N-methoxypropyl acrylamide, poly-N-ethoxypropyl acrylamide, poly-N-isopropoxypropyl acrylamide, poly-N-ethoxyethyl acrylamide, poly-N (2,2-dimethoxyethyl) -N-methylacrylamide, poly-N-1-methyl-2-methoxyethylacrylamide, poly-N-1-methoxymethylpropylacrylamide, poly-N-di (2-methoxyethyl) Acrylamide, poly-N-2-methoxyethyl-Nn-propylacrylamide, poly-N-2-methoxyethyl-N-ethylacrylamide, poly-N-2-methoxyethyl-N-isopropylacrylamide, poly-N- Methoxyethoxypropylacrylamide, poly-N-tetrahydrofurfurylacrylamide, poly-N- (1,3-dioxolan-2-yl) methylacrylamide, poly-N-methyl-N- (1,3-dioxolan-2-yl ) Methylacrylamide, poly-N-cyclopropyl acetate Amide, poly-N-pyrrolidinomethyl acrylamide, poly-N-piperidinomethyl acrylamide, poly-N-2-morpholinoethyl acrylate, poly-N-2-morpholinoethoxyethyl acrylate and the corresponding methacrylates and their A mixture etc. are mentioned.
The acrylic temperature-responsive polymer is preferably present on the resin particle surface of the water-based polyurethane resin via a covalent bond.

本発明においては、このようなアクリル系温度応答性ポリマーを樹脂粒子表面に有することによって、得られる水系ポリウレタン樹脂と後述するアクリルエマルジョンとの相溶性が良好なものとなり、また、この水系ポリウレタン樹脂を含有する水系接着剤組成物の乾燥性も良好なものとなる。
これは、水系ポリウレタン樹脂の樹脂粒子表面にアクリル系温度応答性ポリマーを有することによって相溶性が改善され、また、水系ポリウレタン樹脂を含有する水系接着剤組成物を上述した相転移温度よりも低い温度、即ち、含有する水系ポリウレタン樹脂の樹脂粒子表面に存在するアクリル系温度応答性ポリマーが水溶性の状態で塗布し、塗布後においては相転移温度よりも高い温度で乾燥することにより、非水溶性となったアクリル系温度応答性ポリマー同士が、分子間または分子内での疎水性相互作用により凝集して水の放出が促進され、乾燥速度が向上するためであると考えられる。
具体的には、ポリ−N−イソプロピルアクリルアミドおよびポリ−N,N−ジエチルアクリルアミドは、相転移温度が32℃であることから、これらのポリマーを樹脂粒子表面に有する水系ポリウレタン樹脂を含有する水系接着剤組成物を、例えば、室温(25℃)で塗布し、80℃程度の温度で乾燥させることにより、相溶性および乾燥性がいずれも良好となる。
In the present invention, by having such an acrylic temperature-responsive polymer on the surface of the resin particles, the compatibility between the obtained aqueous polyurethane resin and the acrylic emulsion described later becomes good. The drying property of the aqueous adhesive composition to be contained is also good.
This is because the compatibility is improved by having an acrylic temperature-responsive polymer on the surface of the resin particles of the water-based polyurethane resin, and the water-based adhesive composition containing the water-based polyurethane resin is at a temperature lower than the phase transition temperature described above. In other words, water-insoluble water-soluble polyurethane resin containing water-soluble acrylic temperature-responsive polymer is applied in a water-soluble state, and after application is dried at a temperature higher than the phase transition temperature. This is considered to be because the acrylic temperature-responsive polymers thus formed are aggregated by hydrophobic interaction between molecules or within the molecule, and the release of water is promoted to improve the drying rate.
Specifically, since poly-N-isopropylacrylamide and poly-N, N-diethylacrylamide have a phase transition temperature of 32 ° C., an aqueous adhesive containing an aqueous polyurethane resin having these polymers on the resin particle surface. By applying the agent composition at, for example, room temperature (25 ° C.) and drying it at a temperature of about 80 ° C., both compatibility and drying properties are improved.

上記水系ポリウレタン樹脂の重量平均分子量は、10000〜500000であるのが好ましく、50000〜200000であるのがより好ましい。
また、上記水系ポリウレタン樹脂は、固形分質量が30〜60質量%であるのが好ましく、40〜55質量%であるのがより好ましい。
The weight average molecular weight of the water-based polyurethane resin is preferably 10,000 to 500,000, and more preferably 50,000 to 200,000.
The aqueous polyurethane resin preferably has a solid content of 30 to 60% by mass, more preferably 40 to 55% by mass.

上記水系ポリウレタン樹脂の製造方法は特に限定されないが、その具体例としては、イソシアネート基を2個以上有するポリイソシアネート化合物(A)、水酸基を2個以上有するポリオール化合物(B)、イソシアネート基と反応性を有する基およびイオン性基を有する化合物(C)ならびにイソシアネート基と反応性を有する基を有するエチレン性不飽和単量体(D)を共重合させて生成するウレタンプレポリマーを水媒体中で分散させて得られるウレタンエマルジョンと、上記アクリル系温度応答性ポリマーを生成するモノマー(E)と、を共重合させる方法;等が好適に挙げられる。
以下、ポリイソシアネート化合物(A)、ポリオール化合物(B)、化合物(C)、エチレン性不飽和単量体(D)およびこれらを共重合させて得られるウレタンエマルジョン(ウレタンプレポリマー)ならびにモノマー(E)について詳述する。
Although the manufacturing method of the said water-based polyurethane resin is not specifically limited, As the specific example, the polyisocyanate compound (A) which has two or more isocyanate groups, the polyol compound (B) which has two or more hydroxyl groups, and an isocyanate group and reactivity A urethane prepolymer produced by copolymerization of a compound having an ionic group and an ionic group (C) and an ethylenically unsaturated monomer (D) having a group reactive with an isocyanate group in an aqueous medium Preferred examples include a method of copolymerizing a urethane emulsion obtained by polymerization and a monomer (E) that forms the acrylic temperature-responsive polymer.
Hereinafter, a polyisocyanate compound (A), a polyol compound (B), a compound (C), an ethylenically unsaturated monomer (D), a urethane emulsion (urethane prepolymer) and a monomer (E) obtained by copolymerizing them. ) Will be described in detail.

<ポリイソシアネート化合物(A)>
上記ポリイソシアネート化合物(A)は、イソシアネート基を2個以上有するイソシアネート化合物であれば特に限定されず、その具体例としては、トリレンジイソシアネート(TDI)、ジフェニルメタンジイソシアネート(MDI)、1,4−フェニレンジイソシアネート、ポリメチレンポリフェニレンポリイソシアネート、キシリレンジイソシアネート(XDI)、テトラメチルキシリレンジイソシアネート(TMXDI)、トリジンジイソシアネート(TODI)、1,5−ナフタレンジイソシアネート(NDI)、トリフェニルメタントリイソシアネートなどの芳香族ポリイソシアネート;ヘキサメチレンジイソシアネート(HDI)、トリメチルヘキサメチレンジイソシアネート(TMHDI)、リジンジイソシアネート、ノルボルナンジイソシアナートメチル(NBDI)などの脂肪族ポリイソシアネート;トランスシクロヘキサン−1,4−ジイソシアネート、イソホロンジイソシアネート(IPDI)、ビス(イソシアネートメチル)シクロヘキサン(H6XDI)、ジシクロヘキシルメタンジイソシアネート(H12MDI)などの脂環式ポリイソシアネート;上記各ポリイソシアネートのカルボジイミド変性ポリイソシアネート、または、これらのイソシアヌレート変性ポリイソシアネート等が挙げられる。
<Polyisocyanate compound (A)>
The polyisocyanate compound (A) is not particularly limited as long as it is an isocyanate compound having two or more isocyanate groups, and specific examples thereof include tolylene diisocyanate (TDI), diphenylmethane diisocyanate (MDI), 1,4-phenylene. Aromatic poly, such as diisocyanate, polymethylene polyphenylene polyisocyanate, xylylene diisocyanate (XDI), tetramethylxylylene diisocyanate (TMXDI), tolidine diisocyanate (TODI), 1,5-naphthalene diisocyanate (NDI), triphenylmethane triisocyanate Isocyanate; hexamethylene diisocyanate (HDI), trimethylhexamethylene diisocyanate (TMHDI), lysine diisocyanate, nor Aliphatic polyisocyanates such as Luna Nji isocyanatomethyl (NBDI); trans-cyclohexane-1,4-diisocyanate, isophorone diisocyanate (IPDI), bis (isocyanatomethyl) cyclohexane (H 6 XDI), dicyclohexylmethane diisocyanate (H 12 MDI) And alicyclic polyisocyanates such as carbodiimide-modified polyisocyanates of the above polyisocyanates, or isocyanurate-modified polyisocyanates.

これらは、1種単独で用いてもよく、2種以上を併用してもよい。
これらのうち、これらのうち、TDI、IPDI、MDI、HDIであるのが、比較的安価で入手しやすい理由から好ましい。
These may be used alone or in combination of two or more.
Among these, TDI, IPDI, MDI, and HDI are preferable because they are relatively inexpensive and easily available.

<ポリオール化合物(B)>
上記ポリオール化合物(B)は、水酸基を2個以上有するポリオール化合物であれば特に限定されず、その具体例としては、ポリエーテルポリオール、ポリエステルポリオール、その他のポリオール、およびこれらの混合ポリオール等が挙げられる。
<Polyol compound (B)>
The polyol compound (B) is not particularly limited as long as it is a polyol compound having two or more hydroxyl groups, and specific examples thereof include polyether polyols, polyester polyols, other polyols, and mixed polyols thereof. .

ここで、ポリエーテルポリオールとしては、具体的には、例えば、エチレングリコール、ジエチレングリコール、プロピレングリコール、ジプロピレングリコール、グリセリン、1,1,1−トリメチロールプロパン、1,2,5−ヘキサントリオール、1,3−ブタンジオール、1,4−ブタンジオール、ペンタエリスリトールなどの多価アルコールから選ばれる少なくとも1種に、エチレンオキサイド、プロピレンオキサイド、ブチレンオキサイド、ポリオキシテトラメチレンオキサイドなどから選ばれる少なくとも1種を付加させて得られるポリオール等が挙げられる。   Here, as polyether polyol, specifically, for example, ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, glycerin, 1,1,1-trimethylolpropane, 1,2,5-hexanetriol, 1 , 3-butanediol, 1,4-butanediol, at least one selected from polyhydric alcohols such as pentaerythritol, at least one selected from ethylene oxide, propylene oxide, butylene oxide, polyoxytetramethylene oxide, etc. Examples include polyols obtained by addition.

ポリエステルポリオールとしては、具体的には、例えば、エチレングリコール、プロピレングリコール、ブタンジオールペンタンジオール、ヘキサンジオール、グリセリン、1,1,1−トリメチロールプロパン、その他の低分子ポリオールなどから選ばれる少なくとも1種と、グルタル酸、アジピン酸、ピメリン酸、スベリン酸、セバシン酸、ダイマー酸、その他の低分子脂肪族カルボン酸やオリゴマー酸などから選ばれる少なくとも1種との縮合重合体;プロピオンラクトン、バレロラクトンなどの開環重合体;等が挙げられる。   Specific examples of the polyester polyol include at least one selected from ethylene glycol, propylene glycol, butanediol pentanediol, hexanediol, glycerin, 1,1,1-trimethylolpropane, and other low-molecular polyols. And at least one kind selected from glutaric acid, adipic acid, pimelic acid, suberic acid, sebacic acid, dimer acid, other low molecular weight aliphatic carboxylic acids and oligomeric acids; propionlactone, valerolactone, etc. And the like.

その他のポリオールとしては、具体的には、例えば、ポリマーポリオール、ポリカーボネートポリオール;ポリブタジエンポリオール;水素添加されたポリブタジエンポリオール;アクリルポリオール;エチレングリコール、ジエチレングリコール、プロピレングリコール、ジプロピレングリコール、ブタンジオール、ペンタンジオール、ヘキサンジオールなどの低分子ポリオール:等が挙げられる。   Specific examples of other polyols include, for example, polymer polyol, polycarbonate polyol; polybutadiene polyol; hydrogenated polybutadiene polyol; acrylic polyol; ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, butanediol, pentanediol, And low molecular polyols such as hexanediol.

これらは、1種単独で用いてもよく、2種以上を併用してもよい。
これらのうち、重量平均分子量が100〜10000程度であるポリオールが好ましく、500〜5000であるポリオールがより好ましい。重量平均分子量がこの範囲であると、得られるウレタンプレポリマーの硬度および粘度が良好となる。
These may be used alone or in combination of two or more.
Among these, a polyol having a weight average molecular weight of about 100 to 10,000 is preferable, and a polyol having a weight average molecular weight of 500 to 5,000 is more preferable. When the weight average molecular weight is within this range, the hardness and viscosity of the resulting urethane prepolymer are good.

なお、上記で例示した製造方法において、後述する化合物(C)が、イオン性基以外にイソシアネート基と反応性を有する基として水酸基を2個以上有する場合には、ポリオール化合物(B)は必須成分ではなく、所望により用いることができる。   In addition, in the manufacturing method illustrated above, when the compound (C) described later has two or more hydroxyl groups as a group having reactivity with an isocyanate group in addition to the ionic group, the polyol compound (B) is an essential component. Rather, it can be used as desired.

<化合物(C)>
上記化合物(C)は、イソシアネート基と反応性を有する基およびイオン性基を有する化合物であれば特に限定されない。
ここで、イソシアネート基と反応性を有する基としては、具体的には、例えば、水酸基、第1級アミノ基(−NH2)、第2級アミノ基(−NH−)、メルカプト基等が挙げられる。なお、本発明においては、化合物(C)におけるイソシアネート基と反応性を有する基としてカルボキシ基を含まないものとする。
また、イオン性基としては、具体的には、例えば、カルボキシ基、スルホ基などのアニオン性基;第3級アミノ基(≡N)などのカチオン性基;等が挙げられる。
<Compound (C)>
The compound (C) is not particularly limited as long as it is a compound having an isocyanate group-reactive group and an ionic group.
Here, specific examples of the group having reactivity with an isocyanate group include a hydroxyl group, a primary amino group (—NH 2 ), a secondary amino group (—NH—), and a mercapto group. It is done. In the present invention, a carboxy group is not included as a group having reactivity with an isocyanate group in the compound (C).
Specific examples of the ionic group include an anionic group such as a carboxy group and a sulfo group; a cationic group such as a tertiary amino group (≡N);

このような化合物(C)としては、具体的には、例えば、ヒドロキシ酢酸、ヒドロキシプロピオン酸、ヒドロキシ酪酸などの脂肪族モノヒドロキシカルボン酸;ヒドロキシ安息香酸、ヒドロキシエチル安息香酸、ヒドロキシけい皮酸などの芳香族モノヒドロキシカルボン酸;ジメチロールプロピオン酸、ジメチロール酢酸などのジヒドロキシカルボン酸;ヒドロキシベンゼンスルホン酸などのヒドロキシスルホン酸;メルカプト酢酸、メルカプトプロピオン酸、メルカプト安息香酸などのメルカプトカルボン酸;3N−メルカプトエタンスルホン酸などのメルカプトスルホン酸;アミノアジピン酸、アミノ安息香酸などのアミノカルボン酸;アミノベンゼンスルホン酸などのアミノスルホン酸;等が挙げられ、これらを1種単独で用いてもよく、2種以上を併用してもよい。   Specific examples of such compound (C) include aliphatic monohydroxycarboxylic acids such as hydroxyacetic acid, hydroxypropionic acid, and hydroxybutyric acid; hydroxybenzoic acid, hydroxyethylbenzoic acid, hydroxycinnamic acid, and the like. Aromatic monohydroxycarboxylic acid; dihydroxycarboxylic acid such as dimethylolpropionic acid and dimethylolacetic acid; hydroxysulfonic acid such as hydroxybenzenesulfonic acid; mercaptocarboxylic acid such as mercaptoacetic acid, mercaptopropionic acid and mercaptobenzoic acid; 3N-mercaptoethane Mercaptosulfonic acid such as sulfonic acid; aminocarboxylic acid such as aminoadipic acid and aminobenzoic acid; aminosulfonic acid such as aminobenzenesulfonic acid; and the like. These may be used alone. , It may be used in combination of two or more thereof.

<エチレン性不飽和単量体(D)>
上記エチレン性不飽和単量体(D)は、イソシアネート基と反応性を有する基を1個以上有している。
イソシアネート基と反応性を有する基としては、具体的には、例えば、水酸基、第1級アミノ基(−NH2)、第2級アミノ基(−NH−)、メルカプト基、カルボキシ基、アミド基等が挙げられる。
<Ethylenically unsaturated monomer (D)>
The ethylenically unsaturated monomer (D) has one or more groups having reactivity with isocyanate groups.
Specific examples of the group having reactivity with an isocyanate group include, for example, a hydroxyl group, a primary amino group (—NH 2 ), a secondary amino group (—NH—), a mercapto group, a carboxy group, and an amide group. Etc.

このようなエチレン性不飽和単量体(D)としては、具体的には、例えば、アリルアルコール、3−ブテン−1−オール、3−ペンテン−1−オール、4−ペンテン−1−オール、4−ヘキセン−1−オール、5−ヘキセン−1−オール、5−ヘプテン−1−オール、6−ヘプテン−1−オール、6−オクテン−1−オール、7−オクテン−1−オール、7−ノネン−1−オール、8−ノネン−1−オール、2−メチルアリルアルコール、3−メチル−3−ブテン−1−オール、4−メチル−4−ペンテン−1−オール、5−メチル−5−ヘキセン−1−オール、6−メチル−ヘプテン−1−オール、7−メチル−7−オクテン−1−オール、8−メチル−8−ノネン−1−オールなどの脂肪族不飽和アルコール;ヒドロキシスチレン、ヒドロキシエチルスチレン、ヒドロキシプロピルスチレンなどのヒドロキシアルキルスチレン;ビニル安息香酸とジオールとのモノエステル;2−ヒドロキシエチルアクリレート(アクリル酸2−ヒドロキシエチル)、2−ヒドロキシエチルメタクリレート(メタクリル酸2−ヒドロキシエチル)、2−ヒドロキシプロピルアクリレート、2−ヒドロキシプロピルメタクリレートなどのヒドロキシ(メタ)アクリレート;1,4−ブタンジオールモノアクリレート、1,4−ブタンジオールモノメタクリレート、1,6−ヘキサンジオールモノアクリレート、1,6−ヘキサンジオールモノメタクリレート、ポリエチレングリコールモノアクリレート、ポリエチレングリコールモノメタクリレート、ポリプロピレングリコールモノアクリレート、ポリプロピレングリコールモノメタクリレートなどの(メタ)アクリル酸とジオールとのモノエステル;アクリルアミド、3−アクリルアミド−N,N−ジメチルプロピルアミン、2−アクリルアミド−2−メチルプロパンスルホン酸、N−ヒドロキシメチルアクリルアミド、ダイアセトンアクリルアミドなどのアクリルアミド誘導体;メタクリルアミド、3−メタクリルアミド−N,N−ジメチルプロピルアミンなどのメタクリルアミド誘導体;メルカプトスチレン;アミノスチレン;等が挙げられ、これらを、1種単独で用いてもよく、2種以上を併用してもよい。   Specific examples of such an ethylenically unsaturated monomer (D) include allyl alcohol, 3-buten-1-ol, 3-penten-1-ol, 4-penten-1-ol, 4-hexen-1-ol, 5-hexen-1-ol, 5-hepten-1-ol, 6-hepten-1-ol, 6-octen-1-ol, 7-octen-1-ol, 7- Nonen-1-ol, 8-nonen-1-ol, 2-methylallyl alcohol, 3-methyl-3-buten-1-ol, 4-methyl-4-penten-1-ol, 5-methyl-5- Aliphatic unsaturated alcohols such as hexen-1-ol, 6-methyl-hepten-1-ol, 7-methyl-7-octen-1-ol, 8-methyl-8-nonen-1-ol; Hide Hydroxyalkyl styrene such as xylethyl styrene and hydroxypropyl styrene; monoester of vinyl benzoic acid and diol; 2-hydroxyethyl acrylate (2-hydroxyethyl acrylate), 2-hydroxyethyl methacrylate (2-hydroxyethyl methacrylate) Hydroxy (meth) acrylates such as 2-hydroxypropyl acrylate and 2-hydroxypropyl methacrylate; 1,4-butanediol monoacrylate, 1,4-butanediol monomethacrylate, 1,6-hexanediol monoacrylate, 1,6 -Hexanediol monomethacrylate, polyethylene glycol monoacrylate, polyethylene glycol monomethacrylate, polypropylene glycol monoacrylate, Monoester of (meth) acrylic acid and diol such as propylene glycol monomethacrylate; acrylamide, 3-acrylamide-N, N-dimethylpropylamine, 2-acrylamido-2-methylpropanesulfonic acid, N-hydroxymethylacrylamide, Acrylamide derivatives such as diacetone acrylamide; methacrylamide derivatives such as methacrylamide, 3-methacrylamide-N, N-dimethylpropylamine; mercaptostyrene; aminostyrene, etc., and these may be used alone. In addition, two or more kinds may be used in combination.

<ウレタンエマルジョン(ウレタンプレポリマー)>
上記ウレタンエマルジョンは、上述したポリイソシアネート化合物(A)、ポリオール化合物(B)、化合物(C)およびエチレン性不飽和単量体(D)を共重合させてウレタンプレポリマーを得た後に、該ウレタンプレポリマーを水媒体中で分散させて得られる。
<Urethane emulsion (urethane prepolymer)>
The urethane emulsion is obtained by copolymerizing the above-described polyisocyanate compound (A), polyol compound (B), compound (C) and ethylenically unsaturated monomer (D) to obtain a urethane prepolymer. It is obtained by dispersing the prepolymer in an aqueous medium.

ここで、上記共重合には、ポリイソシアネート化合物(A)、ポリオール化合物(B)、化合物(C)およびエチレン性不飽和単量体(D)を同時に(一時に)かくはん等して重合させる態様(第1態様)以外に、例えば、ポリイソシアネート化合物(A)、ポリオール化合物(B)および化合物(C)の共重合により、イオン性基を含有するイソシアネート末端プレポリマーを生成した後に、該プレポリマーにエチレン重合性不飽和単量体(D)を付加させる態様(第2態様)等も含むものである。なお、本発明においては、第1態様であるのが好ましい。   Here, in the copolymerization, the polyisocyanate compound (A), the polyol compound (B), the compound (C) and the ethylenically unsaturated monomer (D) are polymerized by stirring (at the same time) and the like at the same time. In addition to the (first embodiment), for example, an isocyanate-terminated prepolymer containing an ionic group is produced by copolymerization of a polyisocyanate compound (A), a polyol compound (B), and a compound (C), and then the prepolymer A mode (second mode) in which an ethylenically unsaturated monomer (D) is added to the polymer is also included. In the present invention, the first aspect is preferable.

また、上記共重合は、必要に応じて有機錫化合物、有機ビスマス、アミン等のウレタン化触媒の存在下で行うことができ、有機錫化合物の存在下で行うのが好ましい。
有機錫化合物としては、具体的には、例えば、酢酸第一錫、オクタン酸第一錫、ラウリン酸第一錫、オレイン酸第一錫などのカルボン酸第一錫;ジブチル錫アセテート、ジブチル錫ジラウレート、ジブチル錫マレエート、ジブチル錫ジ−2−エチル-ヘキソエート、ジラウリル錫ジアセテート、ジオクチル錫ジアセテートなどのカルボン酸のジアルキル錫塩;水酸化トリメチル錫、水酸化トリブチル錫、水酸化トリオクチル錫などの水酸化トリアルキル錫:酸化ジブチル錫、酸化ジオクチル錫、酸化ジラウリル錫などの酸化ジアルキル錫;二塩化ジブチル錫、二塩化ジオクチル錫などの塩化ジアルキル錫;等が挙げられ、これらを1種単独で用いてもよく、2種以上を併用してもよい。
これらのうち、ジブチル錫ジラウレート、ジブチル錫アセテート、ジブチル錫マレエートであるのが、比較的安価で取り扱いやすい理由から好ましい。
Moreover, the said copolymerization can be performed in presence of urethanization catalysts, such as an organic tin compound, organic bismuth, and an amine as needed, and it is preferable to carry out in presence of an organic tin compound.
Specific examples of the organic tin compound include stannous acetate such as stannous acetate, stannous octoate, stannous laurate and stannous oleate; dibutyltin acetate and dibutyltin dilaurate. Dialkyltin salts of carboxylic acids such as dibutyltin maleate, dibutyltin di-2-ethyl-hexoate, dilauryltin diacetate, dioctyltin diacetate; water such as trimethyltin hydroxide, tributyltin hydroxide, trioctyltin hydroxide Trialkyltin oxide: dialkyltin oxide such as dibutyltin oxide, dioctyltin oxide and dilauryltin oxide; dialkyltin chloride such as dibutyltin dichloride and dioctyltin dichloride; and the like. Or two or more of them may be used in combination.
Of these, dibutyltin dilaurate, dibutyltin acetate, and dibutyltin maleate are preferable because they are relatively inexpensive and easy to handle.

更に、上記共重合は、得られるウレタンプレポリマーのイソシアネート基含有量(NCO%)が0.3〜3%となるように行うのが好ましく、また、ポリイソシアネート化合物(A)、ポリオール化合物(B)、化合物(C)およびエチレン性不飽和単量体(D)の合計質量に対して、ポリイソシアネート化合物(A)を1〜50質量%、ポリオール化合物(B)を30〜90質量%、化合物(C)を0.1〜20質量%、エチレン性不飽和単量体(D)を0.1〜25質量%含有させ、これらを不活性ガス雰囲気下、60〜90℃下で2〜8時間程度かくはんして行うのが好ましい。ここで、NCO%とは、ウレタンプレポリマーの全質量に対するNCO基の質量%を表す。   Further, the copolymerization is preferably carried out so that the isocyanate group content (NCO%) of the resulting urethane prepolymer is 0.3 to 3%. Also, the polyisocyanate compound (A) and the polyol compound (B ), 1 to 50% by mass of the polyisocyanate compound (A), 30 to 90% by mass of the polyol compound (B), and the compound with respect to the total mass of the compound (C) and the ethylenically unsaturated monomer (D). 0.1 to 20% by mass of (C) and 0.1 to 25% by mass of ethylenically unsaturated monomer (D) are contained, and these are contained in an inert gas atmosphere at 60 to 90 ° C. and 2 to 8%. It is preferable to stir for about an hour. Here, NCO% represents mass% of NCO groups with respect to the total mass of the urethane prepolymer.

このような共重合により得られるウレタンプレポリマーの重量平均分子量は、1500〜30000であるのが好ましく、3000〜20000であるのがより好ましい。
また、このようなウレタンプレポリマーとしては、上記で例示した各種のポリイソシアネート化合物(A)、ポリオール化合物(B)、化合物(C)およびエチレン性不飽和単量体(D)を反応させて得られる反応生成物が挙げられ、具体的には、ポリイソシアネート化合物(A)としてトリレンジイソシアネート(TDI)、ポリオール化合物(B)としてペンタンジオール、化合物(C)としてジメチロールブタン酸またはジメチロールプロピオン酸、エチレン性不飽和単量体(D)として2−ヒドロキシエチルメタクリレートまたは2−ヒドロキシエチルアクリレートを用いて反応させて得られるウレタンプレポリマーが好適に例示される。
The weight average molecular weight of the urethane prepolymer obtained by such copolymerization is preferably 1500 to 30000, and more preferably 3000 to 20000.
Such urethane prepolymers are obtained by reacting the various polyisocyanate compounds (A), polyol compounds (B), compounds (C) and ethylenically unsaturated monomers (D) exemplified above. Specifically, tolylene diisocyanate (TDI) is used as the polyisocyanate compound (A), pentanediol is used as the polyol compound (B), and dimethylolbutanoic acid or dimethylolpropionic acid is used as the compound (C). A urethane prepolymer obtained by reacting 2-ethylethyl methacrylate or 2-hydroxyethyl acrylate as the ethylenically unsaturated monomer (D) is preferably exemplified.

一方、共重合により得られたウレタンプレポリマーの水媒体中での分散は、塩基性化合物、必要に応じて添加される粘度調整剤、鎖延長剤の存在下で行われる。この分散により、上記エチレン性不飽和単量体(D)に由来のエチレン性不飽和二重結合を粒子表面に有するウレタンエマルジョンが得られる。
ここで、塩基性化合物は、ウレタンプレポリマーの水性化(中和)のために必要な化合物である。塩基性化合物としては、具体的には、例えば、水酸化ナトリウム、水酸化カリウム、アンモニア、メチルアミン、エチルアミン、プロピルアミン、ブチルアミン、ヘキシルアミン、オクチルアミン、エタノールアミン、プロパノールアミン、ジエタノールアミン、N−メチルジエタノールアミン、ジメチルアミン、ジエチルアミン、トリエチルアミン、N,N−ジメチルエタノールアミン、2−ジメチルアミノ−2−メチル−1−プロパノール、2−アミノ−2−メチル−1−プロパノール、モルホリン等が挙げられ、これらを1種単独で用いてもよく、2種以上を併用してもよい。
また、所望により添加する粘度調整剤としては、水と相溶する有機溶剤が挙げられ、具体的には、酢酸エチル、アセトン、メチルエチルケトン等が好適に例示される。
また、所望により添加する鎖延長剤は、エチレンジアミン、プロピレンジアミン、ヘキサメチレンジアミン、トリエチレンテトラミンなどの脂肪族ジアミン;イソホロンジアミン、ピペラジンなどの脂環式ジアミン;ジフェニルジアミンなど芳香族ジアミン;トリアミン;等が挙げられる。
On the other hand, the urethane prepolymer obtained by copolymerization is dispersed in an aqueous medium in the presence of a basic compound, a viscosity modifier added as necessary, and a chain extender. By this dispersion, a urethane emulsion having an ethylenically unsaturated double bond derived from the ethylenically unsaturated monomer (D) on the particle surface is obtained.
Here, the basic compound is a compound necessary for making the urethane prepolymer aqueous (neutralized). Specific examples of basic compounds include sodium hydroxide, potassium hydroxide, ammonia, methylamine, ethylamine, propylamine, butylamine, hexylamine, octylamine, ethanolamine, propanolamine, diethanolamine, and N-methyl. Examples include diethanolamine, dimethylamine, diethylamine, triethylamine, N, N-dimethylethanolamine, 2-dimethylamino-2-methyl-1-propanol, 2-amino-2-methyl-1-propanol, morpholine, and the like. 1 type may be used independently and 2 or more types may be used together.
Moreover, as a viscosity modifier added if desired, an organic solvent compatible with water can be mentioned, and specifically, ethyl acetate, acetone, methyl ethyl ketone and the like are preferably exemplified.
The chain extender to be added as desired is an aliphatic diamine such as ethylene diamine, propylene diamine, hexamethylene diamine or triethylene tetramine; an alicyclic diamine such as isophorone diamine or piperazine; an aromatic diamine such as diphenyl diamine; Is mentioned.

<モノマー(E)>
上記モノマー(E)は、上記ウレタンエマルジョンまたはウレタンプレポリマーと共重合することができる単量体成分であって、上記アクリル系温度応答性ポリマーを生成するモノマーである。
このようなモノマー(E)としては、具体的には、例えば、N−エチルアクリルアミド、N−n−プロピルアクリルアミド、N−イソプロピルアクリルアミド、N−シクロプロピルアクリルアミド、N,N−ジエチルアクリルアミド、N−メチル−N−エチルアクリルアミド、N−メチル−N−n−プロピルアクリルアミド、N−メチル−N−イソプロピルアクリルアミド、N−アクリロイルピペリジン、N−アクリロイルピロリジン、N−アクリロイルモルホリン、N−メトキシプロピルアクリルアミド、N−エトキシプロピルアクリルアミド、N−イソプロポキシプロピルアクリルアミド、N−エトキシエチルアクリルアミド、N−(2,2−ジメトキシエチル)−N−メチルアクリルアミド、N−1−メチル−2−メトキシエチルアクリルアミド、N−1−メトキシメチルプロピルアクリルアミド、N−ジ(2−メトキシエチル)アクリルアミド、N−2−メトキシエチル−N−n−プロピルアクリルアミド、N−2−メトキシエチル−N−エチルアクリルアミド、N−2−メトキシエチル−N−イソプロピルアクリルアミド、N−メトキシエトキシプロピルアクリルアミド、N−テトラヒドロフルフリルアクリルアミド、N−(1,3−ジオキソラン−2−イル)メチルアクリルアミド、N−メチル−N−(1,3−ジオキソラン−2−イル)メチルアクリルアミド、N−シクロプロピルアクリルアミド、N−ピロリジノメチルアクリルアミド、N−ピペリジノメチルアクリルアミド、N−2−モルホリノエチルアクリレート、N−2−モルホリノエトキシエチルアクリレートおよびこれらに対応するメタクリレートならびにこれらの混合物等が挙げられる。
また、8−アクリロイル−1,4−ジオキサ−8−アザスピロ[4,5]デカンのようなスピロ型化合物も用いることができる。
これらのうち、N−n−プロピルアクリルアミド、N−イソプロピルアクリルアミド、N,N−ジエチルアクリルアミドが、入手が容易である点で好ましい。
<Monomer (E)>
The monomer (E) is a monomer component that can be copolymerized with the urethane emulsion or urethane prepolymer, and is a monomer that forms the acrylic temperature-responsive polymer.
Specific examples of such a monomer (E) include N-ethylacrylamide, Nn-propylacrylamide, N-isopropylacrylamide, N-cyclopropylacrylamide, N, N-diethylacrylamide, and N-methyl. -N-ethylacrylamide, N-methyl-Nn-propylacrylamide, N-methyl-N-isopropylacrylamide, N-acryloylpiperidine, N-acryloylpyrrolidine, N-acryloylmorpholine, N-methoxypropylacrylamide, N-ethoxy Propylacrylamide, N-isopropoxypropylacrylamide, N-ethoxyethylacrylamide, N- (2,2-dimethoxyethyl) -N-methylacrylamide, N-1-methyl-2-methoxyethyl acetate Luamide, N-1-methoxymethylpropylacrylamide, N-di (2-methoxyethyl) acrylamide, N-2-methoxyethyl-Nn-propylacrylamide, N-2-methoxyethyl-N-ethylacrylamide, N- 2-methoxyethyl-N-isopropylacrylamide, N-methoxyethoxypropylacrylamide, N-tetrahydrofurfurylacrylamide, N- (1,3-dioxolan-2-yl) methylacrylamide, N-methyl-N- (1,3 -Dioxolan-2-yl) methylacrylamide, N-cyclopropylacrylamide, N-pyrrolidinomethylacrylamide, N-piperidinomethylacrylamide, N-2-morpholinoethyl acrylate, N-2-morpholinoethoxyethyl acrylate DOO and the corresponding methacrylates and mixtures thereof to these, and the like.
A spiro compound such as 8-acryloyl-1,4-dioxa-8-azaspiro [4,5] decane can also be used.
Of these, Nn-propylacrylamide, N-isopropylacrylamide, and N, N-diethylacrylamide are preferable because they are easily available.

本発明においては、このようなモノマー(E)は、他の単量体、具体的には、アクリル酸、メタクリル酸のような不飽和カルボン酸;メチルアクリレート、エチルアクリレート、n−ブチルアクリレート、tert−ブチルアクリレート、2−エチルヘキシルアクリレート、2−アセトアセトキシエチルアクリレート、2−アセトアセトキシプロピルアクリレート、3−アセトアセトキシプロピルアクリレート、4−シアノアセトアセトキシエチルアクリレート、2−ヒドロキシエチルアクリレート、3−ヒドロキシプロピルアクリレートのようなアクリル酸エステル類および対応するメタクリル酸エステル類;アクリルアミド、N−メチロールアクリルアミド、N−ヒドロキシプロピルアクリルアミドのようなアクリルアミド類及び対応するメタクリルアミド類;N−アクリロイルベンズヒドラジド、N−メタクリロイルベンズヒドラジドのような不飽和ヒドラジド類;アクリロニトリル、メタクリロニトリルのような不飽和ニトリル類;酢酸ビニル、塩化ビニル、スチレン、α−メチルスチレン、N−ビニルイミダゾール、ビニルメチルエーテル、ビニルエチルエーテルのようなビニル化合物類;等を併用することができる。   In the present invention, such a monomer (E) is another monomer, specifically, an unsaturated carboxylic acid such as acrylic acid or methacrylic acid; methyl acrylate, ethyl acrylate, n-butyl acrylate, tert -Butyl acrylate, 2-ethylhexyl acrylate, 2-acetoacetoxyethyl acrylate, 2-acetoacetoxypropyl acrylate, 3-acetoacetoxypropyl acrylate, 4-cyanoacetoacetoxyethyl acrylate, 2-hydroxyethyl acrylate, 3-hydroxypropyl acrylate Acrylic esters and corresponding methacrylic esters such as acrylamide, acrylamides such as N-methylol acrylamide, N-hydroxypropyl acrylamide and the like Methacrylamides; Unsaturated hydrazides such as N-acryloylbenzhydrazide and N-methacryloylbenzhydrazide; Unsaturated nitriles such as acrylonitrile and methacrylonitrile; Vinyl acetate, vinyl chloride, styrene, α-methylstyrene, N -Vinyl compounds such as vinyl imidazole, vinyl methyl ether and vinyl ethyl ether;

上記モノマー(E)と、上記ウレタンエマルジョンとの共重合は、重合開始剤の存在下、得られる本発明の水系ポリウレタン樹脂の樹脂粒子表面に形成するアクリル系温度応答性ポリマーの相転移温度より低い温度、具体的には、使用するモノマーおよび重合開始剤の種類により異なるが、通常5〜50℃の範囲内で選ばれ、より具体的には、例えばモノマー(E)としてN−イソプロピルアクリルアミドやN,N−ジエチルアクリルアミドを用いた場合には32℃よりも低い温度、好ましくは5〜25℃の下で、上記モノマー(E)と上記ウレタンエマルジョンとをかくはんすることにより行われる。
ここで、上記重合開始剤としては、具体的には、例えば、亜硫酸水素ナトリウム、過硫酸アンモニウム、過硫酸カリウム、過酸化水素、過酸化ベンゾイル、t−ブチルハイドロパーオキサイド、クメンハイドロパーオキサイド、p−メタンハイドロパーオキサイド、t−ブチルペロキシ−2−エチルヘキサナート等が挙げられ、これらを1種単独で用いてもよく、2種以上を併用してもよい。
これらのうち、上述したように、相転移温度よりも低い温度で共重合させる必要性、上記モノマー(E)としてN−イソプロピルアクリルアミド、N,N−ジエチルアクリルアミドが好適に用いられる観点から、亜硫酸水素ナトリウム、過硫酸アンモニウムおよび過硫酸カリウムからなる群より選択される少なくとも1種を用いるのが好ましい。
Copolymerization of the monomer (E) and the urethane emulsion is lower than the phase transition temperature of the acrylic temperature-responsive polymer formed on the resin particle surface of the aqueous polyurethane resin of the present invention obtained in the presence of a polymerization initiator. Although it varies depending on the temperature, specifically the type of monomer and polymerization initiator used, it is usually selected within the range of 5 to 50 ° C., and more specifically, for example, N-isopropylacrylamide or N as the monomer (E) , N-diethylacrylamide is used by stirring the monomer (E) and the urethane emulsion at a temperature lower than 32 ° C, preferably 5 to 25 ° C.
Here, as the polymerization initiator, specifically, for example, sodium bisulfite, ammonium persulfate, potassium persulfate, hydrogen peroxide, benzoyl peroxide, t-butyl hydroperoxide, cumene hydroperoxide, p- Examples thereof include methane hydroperoxide and t-butylperoxy-2-ethylhexanate, and these may be used alone or in combination of two or more.
Among these, as described above, from the necessity of copolymerization at a temperature lower than the phase transition temperature, and from the viewpoint that N-isopropylacrylamide and N, N-diethylacrylamide are preferably used as the monomer (E), hydrogen sulfite. It is preferable to use at least one selected from the group consisting of sodium, ammonium persulfate and potassium persulfate.

一方、上記モノマー(E)と、上記ウレタンプレポリマーとの共重合は、上述した塩基性化合物、必要に応じて添加される粘度調整剤および鎖延長剤、ならびに上記重合開始剤の存在下、得られる本発明の水系ポリウレタン樹脂の樹脂粒子表面に形成するアクリル系温度応答性ポリマーの相転移温度より低い温度の下で、上記モノマー(E)と上記ウレタンプレポリマーとをかくはんすることにより行われる。   On the other hand, the copolymerization of the monomer (E) and the urethane prepolymer is obtained in the presence of the basic compound described above, a viscosity modifier and a chain extender added as necessary, and the polymerization initiator. It is carried out by stirring the monomer (E) and the urethane prepolymer under a temperature lower than the phase transition temperature of the acrylic temperature-responsive polymer formed on the resin particle surface of the aqueous polyurethane resin of the present invention.

このような共重合により、上記ウレタンエマルジョンの粒子表面に存する、エチレン性不飽和単量体(D)に由来のエチレン性不飽和二重結合と、上記モノマー(E)またはモノマー(E)の単独重合体の重合性部位(例えば、N−イソプロピルアクリルアミドの場合にはエチレン性不飽和二重結合)とが、共重合により結合し、樹脂粒子表面にアクリル系温度応答性ポリマーを有する水系ポリウレタン樹脂が得られる。
アクリル系温度応答性ポリマーの相転移温度より低い温度で共重合を行うことにより、樹脂粒子表面に存するアクリル系温度応答性ポリマーが水溶性となり、上述したように、得られる本発明の水系ポリウレタン樹脂の塗工性が優れたものとなる。
By such copolymerization, the ethylenically unsaturated double bond derived from the ethylenically unsaturated monomer (D) present on the particle surface of the urethane emulsion and the monomer (E) or the monomer (E) alone A water-based polyurethane resin having an acrylic temperature-responsive polymer on the surface of the resin particle is bonded to the polymerizable portion of the polymer (for example, ethylenically unsaturated double bond in the case of N-isopropylacrylamide) by copolymerization. can get.
By carrying out the copolymerization at a temperature lower than the phase transition temperature of the acrylic temperature-responsive polymer, the acrylic temperature-responsive polymer existing on the surface of the resin particles becomes water-soluble, and as described above, the obtained water-based polyurethane resin of the present invention is obtained. The coating property is excellent.

[アクリルエマルジョン]
本発明においては、上記アクリルエマルジョンは、特に限定されず、従来公知のアクリルエマルジョンを用いることができる。
上記アクリルエマルジョンとしては、例えば、メタクリル酸エステル、アクリル酸エステル、芳香族ビニル単量体、不飽和二トリル、共役ジオレフィン、多官能ビニル単量体、、アミド系単量体、水酸基含有単量体、カプロラクトン付加単量体、アミノ基含有単量体、グリシジル基含有単量体、酸系単量体、ビニル単量体等を、乳化分散剤を用いて重合(乳化重合)して得られる水性エマルジョン等が好適に挙げられる。
[Acrylic emulsion]
In the present invention, the acrylic emulsion is not particularly limited, and a conventionally known acrylic emulsion can be used.
Examples of the acrylic emulsion include methacrylic acid esters, acrylic acid esters, aromatic vinyl monomers, unsaturated nitriles, conjugated diolefins, polyfunctional vinyl monomers, amide monomers, and hydroxyl group-containing monomers. Body, caprolactone addition monomer, amino group-containing monomer, glycidyl group-containing monomer, acid monomer, vinyl monomer, etc., are obtained by polymerization (emulsion polymerization) using an emulsifying dispersant. A water-based emulsion etc. are mentioned suitably.

上記乳化分散剤としては、例えば、ノニオン系、アニオン系、カチオン系の界面活性剤が挙げられ、これらを1種単独で用いてもよく、2種以上を併用してもよい。また、乳化分散剤として、界面活性剤分子中に反応性の二重結合を有する反応性界面活性剤;ポリビニルアルコール、デンプンなどの水溶性高分子;等も用いることができる。これらのうち、水溶性高分子(特に、ポリビニルアルコール)を用いることが好ましい。   Examples of the emulsifying dispersant include nonionic, anionic and cationic surfactants, which may be used alone or in combination of two or more. As the emulsifying dispersant, a reactive surfactant having a reactive double bond in the surfactant molecule; a water-soluble polymer such as polyvinyl alcohol and starch; and the like can also be used. Among these, it is preferable to use a water-soluble polymer (particularly polyvinyl alcohol).

上記メタクリル酸エステルとしては、具体的には、例えば、メタクリル酸メチル、メタクリル酸エチル、メタクリル酸ブチル、メタクリル酸ヘキシル、メタクリル酸シクロヘキシル、メタクリル酸ノニル、メタクリル酸ラウリル、メタクリル酸ラウリル等が挙げられる。
上記アクリル酸エステルとしては、具体的には、例えば、アクリル酸ブチル、アクリル酸ヘキシル、アクリル酸2−エチルヘキシル等が挙げられる。
Specific examples of the methacrylic acid ester include methyl methacrylate, ethyl methacrylate, butyl methacrylate, hexyl methacrylate, cyclohexyl methacrylate, nonyl methacrylate, lauryl methacrylate, and lauryl methacrylate.
Specific examples of the acrylic ester include butyl acrylate, hexyl acrylate, 2-ethylhexyl acrylate, and the like.

上記芳香族ビニル単量体としては、具体的には、例えば、パラメチルスチレン、α−メチルスチレン、パラクロロエチレン、クロルメチレンスチレン、ビニルトルエン等が挙げられる。
上記不飽和二トリルとしては、具体的には、例えば、アクリロニトリル、メタクリルニトリル等が挙げられる。
上記共役ジオレフィンとしては、ブタジエン、具体的には、例えば、イソプレン、クロロプレン等が挙げられる。
上記多官能ビニル単量体としては、具体的には、例えば、ジビニルベンゼン、エチレングリコールジアクリレート、エチレングリコールジメタクリレート、ジエチレングリコールジアクリレート、ジエチレンジグリコールジメタクリレート、メタクリル酸アリル、フタル酸ジアリル、トリメチロールプロパントリアクリレート、グリセリンジアリルエーテル、ポリエチレングリコールジメタクリレート、ポリエチレングリコールジアクリレート等が挙げられる。
Specific examples of the aromatic vinyl monomer include paramethyl styrene, α-methyl styrene, parachloroethylene, chloromethylene styrene, vinyl toluene, and the like.
Specific examples of the unsaturated nitrile include acrylonitrile and methacrylonitrile.
Examples of the conjugated diolefin include butadiene, specifically, isoprene, chloroprene, and the like.
Specific examples of the polyfunctional vinyl monomer include divinylbenzene, ethylene glycol diacrylate, ethylene glycol dimethacrylate, diethylene glycol diacrylate, diethylene diglycol dimethacrylate, allyl methacrylate, diallyl phthalate, and trimethylol. Examples include propane triacrylate, glyceryl diallyl ether, polyethylene glycol dimethacrylate, and polyethylene glycol diacrylate.

上記アミド系単量体としては、具体的には、例えば、アクリルアミド、メタクリルアミド、n−メチロールメタクリルアミド等が挙げられる。
上記水酸基含有単量体としては、具体的には、例えば、β−ヒドロキシエチルアクリレート、β−ヒドロキシメタクリレート等が挙げられる。
上記カプロラクトン付加単量体としては、具体的には、例えば、ダイセル化学製のFA−1、FA−2、FA−3、FM−1などのβ−ヒドロキシエチルアクリレート、β−ヒドロキシメタクリレート等が挙げられる。
上記アミノ基含有単量体としては、具体的には、例えば、ジメチルアミノエチルアクリレート、ジエチルアミノエチルアクリレート等が挙げられる。
グリシジル基含有単量体としては、具体的には、例えば、アクリル酸グリシジル、メタクリル酸ジグリシジル等が挙げられる。
酸系単量体としては、具体的には、例えば、アクリル酸、メタクリル酸、イタコン酸、パラビニル安息香酸等が挙げられる。
ビニル単量体としては、具体的には、例えば、酢酸ビニル、塩化ビニル、塩化ビニリデン等が挙げられる。
Specific examples of the amide monomer include acrylamide, methacrylamide, n-methylol methacrylamide, and the like.
Specific examples of the hydroxyl group-containing monomer include β-hydroxyethyl acrylate, β-hydroxy methacrylate, and the like.
Specific examples of the caprolactone addition monomer include β-hydroxyethyl acrylate and β-hydroxy methacrylate such as FA-1, FA-2, FA-3, and FM-1 manufactured by Daicel Chemical. It is done.
Specific examples of the amino group-containing monomer include dimethylaminoethyl acrylate and diethylaminoethyl acrylate.
Specific examples of the glycidyl group-containing monomer include glycidyl acrylate and diglycidyl methacrylate.
Specific examples of the acid monomer include acrylic acid, methacrylic acid, itaconic acid, paravinyl benzoic acid, and the like.
Specific examples of the vinyl monomer include vinyl acetate, vinyl chloride, and vinylidene chloride.

これらのうち、コスト、取扱い性、物性等の種々の観点から、アクリル酸エステル、メタクリル酸エステルであるのが好ましい。   Of these, acrylic acid esters and methacrylic acid esters are preferable from various viewpoints such as cost, handleability, and physical properties.

上記アクリルエマルジョンの重量平均分子量は、10000〜500000であるのが好ましく、50000〜200000であるのがより好ましい。
また、上記アクリルエマルジョンは、固形分質量が30〜60質量%であるのが好ましく、40〜55質量%であるのがより好ましい。
The weight average molecular weight of the acrylic emulsion is preferably 10,000 to 500,000, and more preferably 50,000 to 200,000.
Moreover, it is preferable that solid content mass is 30-60 mass%, and it is more preferable that the said acrylic emulsion is 40-55 mass%.

本発明においては、上記アクリルエマルジョンとして市販品を用いてもよく、その具体例としては、レジテックス社製のA6001、日本ゼオン社製のLx823等が挙げられる。   In the present invention, commercially available products may be used as the acrylic emulsion, and specific examples thereof include A6001 manufactured by Regex Corporation, Lx823 manufactured by Nippon Zeon Co., Ltd., and the like.

本発明の水系接着剤組成物は、上記水系ポリウレタン樹脂と上記アクリルエマルジョンとを含有するものであり、これらの配合割合は、固形分比(水系ポリウレタン樹脂/アクリルエマルジョン)で、50/50〜80/20であるのが好ましく、60/40〜70/30であるのがより好ましい。   The water-based adhesive composition of the present invention contains the water-based polyurethane resin and the acrylic emulsion, and the blending ratio thereof is 50/50 to 80 in terms of solid content ratio (water-based polyurethane resin / acrylic emulsion). / 20 is preferable, and 60/40 to 70/30 is more preferable.

本発明の水系接着剤組成物は、上記水系ポリウレタン樹脂および上記アクリルエマルジョン以外に、所望により、充填剤、老化防止剤、酸化防止剤、顔料(染料)、可塑剤、揺変性付与剤、紫外線吸収剤、難燃剤、界面活性剤(レベリング剤を含む)、分散剤、接着付与剤、帯電防止剤などの各種添加剤等を含有することができる。   In addition to the aqueous polyurethane resin and the acrylic emulsion, the aqueous adhesive composition of the present invention is optionally filled with a filler, an antioxidant, an antioxidant, a pigment (dye), a plasticizer, a thixotropic agent, and an ultraviolet absorber. Various additives such as an agent, a flame retardant, a surfactant (including a leveling agent), a dispersant, an adhesion-imparting agent, and an antistatic agent can be contained.

充填剤としては、各種形状の有機または無機の充填剤が挙げられる。具体的には、例えば、ヒュームドシリカ、焼成シリカ、沈降シリカ、粉砕シリカ、溶融シリカ;ケイソウ土;酸化鉄、酸化亜鉛、酸化チタン、酸化バリウム、酸化マグネシウム;炭酸カルシウム、炭酸マグネシウム、炭酸亜鉛;ろう石クレー、カオリンクレー、焼成クレー;カーボンブラック;これらの脂肪酸処理物、樹脂酸処理物、ウレタン化合物処理物、脂肪酸エステル処理物;等が挙げられる。   Examples of the filler include organic or inorganic fillers having various shapes. Specifically, for example, fumed silica, calcined silica, precipitated silica, ground silica, fused silica; diatomaceous earth; iron oxide, zinc oxide, titanium oxide, barium oxide, magnesium oxide; calcium carbonate, magnesium carbonate, zinc carbonate; Examples thereof include wax stone clay, kaolin clay, calcined clay; carbon black; these fatty acid treated products, resin acid treated products, urethane compound treated products, fatty acid ester treated products; and the like.

老化防止剤としては、具体的には、例えば、ヒンダードフェノール系等の化合物が挙げられる。
酸化防止剤としては、具体的には、例えば、ブチルヒドロキシトルエン(BHT)、ブチルヒドロキシアニソール(BHA)等が挙げられる。
Specific examples of the anti-aging agent include hindered phenol compounds.
Specific examples of the antioxidant include butylhydroxytoluene (BHT) and butylhydroxyanisole (BHA).

顔料としては、具体的には、例えば、酸化チタン、酸化亜鉛、群青、ベンガラ、リトポン、鉛、カドミウム、鉄、コバルト、アルミニウム、塩酸塩、硫酸塩などの無機顔料;アゾ顔料、フタロシアニン顔料、キナクリドン顔料、キナクリドンキノン顔料、ジオキサジン顔料、アントラピリミジン顔料、アンサンスロン顔料、インダンスロン顔料、フラバンスロン顔料、ペリレン顔料、ペリノン顔料、ジケトピロロピロール顔料、キノナフタロン顔料、アントラキノン顔料、チオインジゴ顔料、ベンズイミダゾロン顔料、イソインドリン顔料、カーボンブラックなどの有機顔料;等が挙げられる。   Specific examples of the pigment include inorganic pigments such as titanium oxide, zinc oxide, ultramarine, bengara, lithopone, lead, cadmium, iron, cobalt, aluminum, hydrochloride, sulfate, etc .; azo pigment, phthalocyanine pigment, quinacridone Pigment, quinacridone quinone pigment, dioxazine pigment, anthrapyrimidine pigment, anthanthrone pigment, indanthrone pigment, flavanthrone pigment, perylene pigment, perinone pigment, diketopyrrolopyrrole pigment, quinonaphthalone pigment, anthraquinone pigment, thioindigo pigment, benzimidazolone And organic pigments such as pigments, isoindoline pigments, and carbon black.

可塑剤としては、具体的には、例えば、ジイソノニルフタレート(DINP);アジピン酸ジオクチル、コハク酸イソデシル;ジエチレングリコールジベンゾエート、ペンタエリスリトールエステル;オレイン酸ブチル、アセチルリシノール酸メチル;リン酸トリクレジル、リン酸トリオクチル;アジピン酸プロピレングリコールポリエステル、アジピン酸ブチレングリコールポリエステル等が挙げられる。これらは、単独で用いてもよく、2種以上を混合して用いてもよい。   Specific examples of the plasticizer include diisononyl phthalate (DINP); dioctyl adipate, isodecyl succinate; diethylene glycol dibenzoate, pentaerythritol ester; butyl oleate, methyl acetylricinoleate; tricresyl phosphate, trioctyl phosphate An adipate propylene glycol polyester, an adipate butylene glycol polyester, and the like. These may be used alone or in combination of two or more.

揺変性付与剤としては、具体的には、例えば、エアロジル(日本エアロジル社製)、ディスパロン(楠本化成社製)等が挙げられる。
接着付与剤としては、具体的には、例えば、テルペン樹脂、フェノール樹脂、テルペン−フェノール樹脂、ロジン樹脂、キシレン樹脂等が挙げられる。
Specific examples of the thixotropic agent include aerosil (manufactured by Nippon Aerosil Co., Ltd.), disparon (manufactured by Enomoto Kasei Co., Ltd.), and the like.
Specific examples of the adhesion-imparting agent include terpene resins, phenol resins, terpene-phenol resins, rosin resins, xylene resins, and the like.

難燃剤としては、具体的には、例えば、クロロアルキルホスフェート、ジメチル・メチルホスホネート、臭素・リン化合物、アンモニウムポリホスフェート、ネオペンチルブロマイド−ポリエーテル、臭素化ポリエーテル等が挙げられる。
帯電防止剤としては、具体的には、例えば、第四級アンモニウム塩;ポリグリコール、エチレンオキサイド誘導体等の親水性化合物等が挙げられる。
Specific examples of the flame retardant include chloroalkyl phosphate, dimethyl / methyl phosphonate, bromine / phosphorus compound, ammonium polyphosphate, neopentyl bromide-polyether, brominated polyether, and the like.
Specific examples of the antistatic agent include quaternary ammonium salts; hydrophilic compounds such as polyglycols and ethylene oxide derivatives.

本発明の水系接着剤組成物の製造方法は、特に限定されないが、上記水系ポリウレタン樹脂および上記アクリルエマルジョンと、所望により添加する各種添加剤とを、混合ミキサー等のかくはん機を用いて十分に混練する方法を用いることができる。   The method for producing the water-based adhesive composition of the present invention is not particularly limited, but the water-based polyurethane resin and the acrylic emulsion and various additives to be added as necessary are sufficiently kneaded using a stirrer such as a mixing mixer. Can be used.

以下、実施例を用いて、本発明について詳細に説明する。ただし、本発明はこれに限定されるものではない。   Hereinafter, the present invention will be described in detail with reference to examples. However, the present invention is not limited to this.

(合成例1および2)
ポリイソシアネート化合物(A1)、ポリオール化合物(B1)、化合物(C1)およびエチレン性不飽和単量体(D1)を、下記表1に示す質量部で、窒素気流下、60℃で3時間反応させ、ウレタンプレポリマーを合成した。
次いで、合成した各ウレタンプレポリマーを単離しない状態で、酢酸エチル(粘度調整剤)に溶解させた後に、水中で、トリエチルアミン(塩基性化合物)およびピペラジン6水和物(鎖延長剤)とともに、10℃で3時間分散させ、ウレタンエマルジョンを調整した。酢酸エチル、水、トリエチルアミンおよびピペラジン6水和物の各質量部ならびに得られた各ウレタンエマルジョンの酢酸エチルを除く固形分(%)を下記表1に示す。
次いで、調整した各ウレタンエマルジョンを単離しない状態で、重合開始剤1および2の存在下、5℃下で16時間モノマー(E1)と反応させ、水系ポリウレタン樹脂1および2を得た。重合開始剤1および2ならびにモノマー(E1)の各質量部を下記表1に示す。
(Synthesis Examples 1 and 2)
The polyisocyanate compound (A1), the polyol compound (B1), the compound (C1) and the ethylenically unsaturated monomer (D1) are reacted at 60 ° C. for 3 hours under a nitrogen stream in the mass parts shown in Table 1 below. A urethane prepolymer was synthesized.
Next, after each synthesized urethane prepolymer is not isolated and dissolved in ethyl acetate (viscosity modifier), in water, with triethylamine (basic compound) and piperazine hexahydrate (chain extender), A urethane emulsion was prepared by dispersing at 10 ° C. for 3 hours. Table 1 below shows each part by mass of ethyl acetate, water, triethylamine, and piperazine hexahydrate and the solid content (%) excluding ethyl acetate of each of the obtained urethane emulsions.
Next, each of the prepared urethane emulsions was reacted with the monomer (E1) at 5 ° C. for 16 hours in the presence of the polymerization initiators 1 and 2 without isolation, to obtain aqueous polyurethane resins 1 and 2. Each mass part of the polymerization initiators 1 and 2 and the monomer (E1) is shown in Table 1 below.

Figure 2007023235
Figure 2007023235

上記表1中の各成分は、以下のものを使用した。
・ポリイソシアネート化合物(A1):TDI(コスモネートTDI100、三井武田ケミカル社製)
・ポリオール化合物(B1):3−メチルペンタンジオール/AA(クラレポリオールP2010、重量平均分子量2000、クラレ社製)
・化合物(C1):ジメチロールブタン酸(日本化成社製)
・エチレン性不飽和単量体(D1):ヒドロキシエチルメタクリレート(HEMA、共栄社化学社製)
・トリエチルアミン(塩基性化合物):関東化学社製
・ピペラジン6水和物(鎖延長剤):日本乳化剤社製
・酢酸エチル(粘度調整剤):関東化学社製
・モノマー(E1):N−イソプロピルアクリルアミド(興人社製)
・重合開始剤1:過硫酸アンモニウム(関東化学社製)
・重合開始剤2:亜硫酸水素ナトリウム(関東化学社製)
The following were used for each component in Table 1 above.
Polyisocyanate compound (A1): TDI (Cosmonate TDI100, manufactured by Mitsui Takeda Chemical Company)
Polyol compound (B1): 3-methylpentanediol / AA (Kuraray polyol P2010, weight average molecular weight 2000, manufactured by Kuraray Co., Ltd.)
Compound (C1): dimethylol butanoic acid (manufactured by Nippon Kasei Co., Ltd.)
Ethylenically unsaturated monomer (D1): hydroxyethyl methacrylate (HEMA, manufactured by Kyoeisha Chemical Co., Ltd.)
Triethylamine (basic compound): manufactured by Kanto Chemical Co., Ltd. Piperazine hexahydrate (chain extender): manufactured by Nippon Emulsifier Co., Ltd. Ethyl acetate (viscosity modifier): manufactured by Kanto Chemical Co., Ltd. Monomer (E1): N-isopropyl Acrylamide (manufactured by Kojinsha)
Polymerization initiator 1: ammonium persulfate (manufactured by Kanto Chemical Co., Inc.)
-Polymerization initiator 2: Sodium hydrogen sulfite (manufactured by Kanto Chemical Co., Inc.)

(実施例1〜3、比較例1〜6および参考例1)
合成例1で得られた水系ポリウレタン樹脂1(固形分:44.6質量%)または合成例2で得られた水系ポリウレタン樹脂2(固形分:44.6質量%)と、アクリルエマルジョン1(A6001、固形分:60.6質量%、レヂテックス社製)とを、下記表2に示す質量部で、窒素気流下、60℃で3時間かくはんし、水系接着剤組成物を調整した。
なお、水系ポリウレタン樹脂1または2と、アクリルエマルジョン1との混合は、いずれの例においても良好であり、相溶性が優れていることが分かった。
(Examples 1 to 3, Comparative Examples 1 to 6 and Reference Example 1)
The aqueous polyurethane resin 1 (solid content: 44.6% by mass) obtained in Synthesis Example 1 or the aqueous polyurethane resin 2 (solid content: 44.6% by mass) obtained in Synthesis Example 2 and acrylic emulsion 1 (A6001) , Solid content: 60.6% by mass, manufactured by Restex Co., Ltd.) was stirred in a nitrogen stream at 60 ° C. for 3 hours under a nitrogen stream to prepare an aqueous adhesive composition.
In addition, it turned out that mixing with the water-based polyurethane resin 1 or 2 and the acrylic emulsion 1 is favorable in any example, and the compatibility is excellent.

得られた各水系接着剤組成物について、以下に示す測定方法により各物性の評価を行った。その結果を下記表2に示す。なお、比較例1および2は、それぞれ水系ポリウレタン樹脂1および水系ポリウレタン樹脂2そのものについて同様の測定を行い、比較例6は、アクリルエマルジョン1そのものについて同様の測定を行い、参考例1として溶剤系の水性ポリウレタン−アクリルエマルジョン接着剤(AU−21、イサム塗料社製)について同様の測定を行った。   About each obtained water-based adhesive composition, each physical property was evaluated with the measuring method shown below. The results are shown in Table 2 below. In Comparative Examples 1 and 2, the same measurement was performed for the water-based polyurethane resin 1 and the water-based polyurethane resin 2 themselves, and in Comparative Example 6, the same measurement was performed for the acrylic emulsion 1 itself. The same measurement was performed for an aqueous polyurethane-acrylic emulsion adhesive (AU-21, manufactured by Isamu Paint Co., Ltd.).

<乾燥性(塗布量100g/m2)>
乾燥性の評価は、得られた各水系接着剤組成物を、JIS H4000に規定の1050材のアルミニウム板(サイズ:10cm×10cm)に塗布量が100g/m2となるように塗布し、20℃、40℃および80℃のそれぞれの温度下(いずれも相対湿度55%)で硬化させ、でのタックフリータイム(分)をJIS A5758に準拠して測定した。
<Drying property (coating amount 100 g / m 2 )>
For evaluation of drying property, each aqueous adhesive composition obtained was applied to an aluminum plate (size: 10 cm × 10 cm) defined in JIS H4000 so that the applied amount was 100 g / m 2. C., 40.degree. C., and 80.degree. C. (each having a relative humidity of 55%) was cured, and the tack free time (minutes) was measured according to JIS A5758.

<金属との接着性(初期接着性)>
金属との接着性の評価をするために、JIS K6256:1999(剛板と加硫ゴムの90度はく離試験)に準じて、以下のはく離試験を行った。
得られた各水系接着剤組成物をアルミニウム板上に塗布し、溶剤系の接着剤での乾燥条件である80℃下30秒間の乾燥を施した後に、組成物の塗布面にポリプロピレンフィルムを圧着させた試験体を作製した。
試験体作成後、直ちに、アルミニウム板とポリプロピレンフィルムとを90度はく離させ、その際の引張強さ(N/25mm)を測定した。
<Adhesion with metal (initial adhesion)>
In order to evaluate the adhesion to metal, the following peel test was performed in accordance with JIS K6256: 1999 (90 degree peel test between rigid plate and vulcanized rubber).
Each aqueous adhesive composition obtained was applied onto an aluminum plate, dried at 80 ° C. for 30 seconds, which is a drying condition with a solvent-based adhesive, and then a polypropylene film was pressure-bonded to the application surface of the composition A test specimen was prepared.
Immediately after the preparation of the test body, the aluminum plate and the polypropylene film were peeled off by 90 degrees, and the tensile strength (N / 25 mm) at that time was measured.

<相溶性(塗布後)>
得られた各水系接着剤組成物をアルミニウム板上に塗布し、80℃下で30秒間乾燥させてフィルム状態とした。その後、フィルム状の接着剤組成物における水系ポリウレタン樹脂1または2と、アクリルエマルジョン1との相分離の有無を目視により確認した。相分離が見られた場合を相溶性(塗布後)に劣るものとして「×」と評価し、相分離が見られなかった場合を相溶性(塗布後)に優れるものとして「○」と評価した。
なお、比較例1、2および6については、相溶性(塗布後)については評価せず、下記表2中においては「−」と記載した。
<Compatibility (after application)>
Each obtained water-based adhesive composition was applied on an aluminum plate and dried at 80 ° C. for 30 seconds to form a film. Thereafter, the presence or absence of phase separation between the aqueous polyurethane resin 1 or 2 and the acrylic emulsion 1 in the film-like adhesive composition was visually confirmed. The case where phase separation was observed was evaluated as “x” as being inferior in compatibility (after application), and the case where phase separation was not observed was evaluated as “◯” as being excellent in compatibility (after application). .
In Comparative Examples 1, 2, and 6, the compatibility (after application) was not evaluated, and in Table 2 below, “−” was written.

Figure 2007023235
Figure 2007023235

上記表2に示す結果より、実施例1〜3の水系接着剤組成物は、その調整時における相溶性のみならず、塗布後における相溶性にも優れ、また、樹脂粒子表面にアクリル系温度応答性ポリマーを有していない水系ポリウレタン樹脂を用いた比較例3〜5ならびに比較例1、2および6の水系接着剤組成物に比べて、乾燥性に優れていることが分かり、更に、金属との接着性についても優れていることが分かった。また、実施例1〜3の水系接着剤組成物は、参考例1に記載の溶剤系接着剤と比較しても、同等以上の乾燥性、接着性および相溶性を有していることが分かった。   From the results shown in Table 2 above, the aqueous adhesive compositions of Examples 1 to 3 are excellent not only in compatibility at the time of adjustment but also in compatibility after application, and the acrylic temperature response on the surface of the resin particles. Compared to the aqueous adhesive compositions of Comparative Examples 3 to 5 and Comparative Examples 1, 2 and 6 using an aqueous polyurethane resin that does not have a water-soluble polymer, it was found that the material was excellent in drying properties, It was also found that the adhesion of the resin was excellent. Moreover, even if compared with the solvent-type adhesive agent of the reference example 1, the water-based adhesive composition of Examples 1 to 3 is found to have equivalent or higher drying properties, adhesiveness, and compatibility. It was.

Claims (6)

樹脂粒子表面にアクリル系温度応答性ポリマーを有する水系ポリウレタン樹脂と、アクリルエマルジョンとを含有する、水系接着剤組成物。   A water-based adhesive composition comprising a water-based polyurethane resin having an acrylic temperature-responsive polymer on the surface of resin particles and an acrylic emulsion. 前記アクリル系温度応答性ポリマーが、共有結合を介して樹脂粒子表面に存在する、請求項1に記載の水系接着剤組成物。   The water-based adhesive composition according to claim 1, wherein the acrylic temperature-responsive polymer is present on the surface of the resin particle through a covalent bond. 前記アクリル系温度応答性ポリマーが、アクリルアミド系ポリマーである、請求項1または2に記載の水系接着剤組成物。   The water-based adhesive composition according to claim 1 or 2, wherein the acrylic temperature-responsive polymer is an acrylamide-based polymer. 前記アクリルアミド系ポリマーが、ポリ−N−エチルアクリルアミド、ポリ−N−n−プロピルアクリルアミド、ポリ−N−イソプロピルアクリルアミド、ポリ−N−シクロプロピルアクリルアミド、ポリ−N,N−ジエチルアクリルアミド、ポリ−N−メチル−N−エチルアクリルアミド、ポリ−N−メチル−N−n−プロピルアクリルアミド、ポリ−N−メチル−N−イソプロピルアクリルアミド、ポリ−N−アクリロイルピペリジン、ポリ−N−アクリロイルピロリジン、ポリ−N−アクリロイルモルホリン、ポリ−N−メトキシプロピルアクリルアミド、ポリ−N−エトキシプロピルアクリルアミド、ポリ−N−イソプロポキシプロピルアクリルアミド、ポリ−N−エトキシエチルアクリルアミド、ポリ−N−(2,2−ジメトキシエチル)−N−メチルアクリルアミド、ポリ−N−1−メチル−2−メトキシエチルアクリルアミド、ポリ−N−1−メトキシメチルプロピルアクリルアミド、ポリ−N−ジ(2−メトキシエチル)アクリルアミド、ポリ−N−2−メトキシエチル−N−n−プロピルアクリルアミド、ポリ−N−2−メトキシエチル−N−エチルアクリルアミド、ポリ−N−2−メトキシエチル−N−イソプロピルアクリルアミド、ポリ−N−メトキシエトキシプロピルアクリルアミド、ポリ−N−テトラヒドロフルフリルアクリルアミド、ポリ−N−(1,3−ジオキソラン−2−イル)メチルアクリルアミド、ポリ−N−メチル−N−(1,3−ジオキソラン−2−イル)メチルアクリルアミド、ポリ−N−シクロプロピルアクリルアミド、ポリ−N−ピロリジノメチルアクリルアミド、ポリ−N−ピペリジノメチルアクリルアミド、ポリ−N−2−モルホリノエチルアクリレート、ポリ−N−2−モルホリノエトキシエチルアクリレートおよびこれらに対応するメタクリレートからなる群から選択される少なくとも一種である、請求項3に記載の水系接着剤組成物。   The acrylamide polymer is poly-N-ethylacrylamide, poly-Nn-propylacrylamide, poly-N-isopropylacrylamide, poly-N-cyclopropylacrylamide, poly-N, N-diethylacrylamide, poly-N- Methyl-N-ethylacrylamide, poly-N-methyl-Nn-propylacrylamide, poly-N-methyl-N-isopropylacrylamide, poly-N-acryloylpiperidine, poly-N-acryloylpyrrolidine, poly-N-acryloyl Morpholine, poly-N-methoxypropyl acrylamide, poly-N-ethoxypropyl acrylamide, poly-N-isopropoxypropyl acrylamide, poly-N-ethoxyethyl acrylamide, poly-N- (2,2-dimethoxy Chill) -N-methylacrylamide, poly-N-1-methyl-2-methoxyethylacrylamide, poly-N-1-methoxymethylpropylacrylamide, poly-N-di (2-methoxyethyl) acrylamide, poly-N- 2-methoxyethyl-Nn-propylacrylamide, poly-N-2-methoxyethyl-N-ethylacrylamide, poly-N-2-methoxyethyl-N-isopropylacrylamide, poly-N-methoxyethoxypropylacrylamide, poly -N-tetrahydrofurfurylacrylamide, poly-N- (1,3-dioxolan-2-yl) methylacrylamide, poly-N-methyl-N- (1,3-dioxolan-2-yl) methylacrylamide, poly- N-cyclopropylacrylamide, poly-N- At least one selected from the group consisting of loridinomethylacrylamide, poly-N-piperidinomethylacrylamide, poly-N-2-morpholinoethyl acrylate, poly-N-2-morpholinoethoxyethyl acrylate, and the corresponding methacrylates The aqueous adhesive composition according to claim 3, wherein 前記水系ポリウレタン樹脂が、
イソシアネート基を2個以上有するポリイソシアネート化合物(A)、水酸基を2個以上有するポリオール化合物(B)、イソシアネート基と反応性を有する基およびイオン性基を有する化合物(C)ならびにイソシアネート基と反応性を有する基を有するエチレン性不飽和単量体(D)を共重合させて生成するウレタンプレポリマーを水媒体中で分散させて得られるウレタンエマルジョンと、
前記アクリル系温度応答性ポリマーを生成するモノマー(E)と、
を共重合させて得られる、請求項1〜4のいずれかに記載の水系接着剤組成物。
The water-based polyurethane resin is
Polyisocyanate compound (A) having 2 or more isocyanate groups, polyol compound (B) having 2 or more hydroxyl groups, compound (C) having an isocyanate group-reactive group and an ionic group, and isocyanate group-reactive A urethane emulsion obtained by dispersing a urethane prepolymer produced by copolymerizing an ethylenically unsaturated monomer (D) having a group containing
A monomer (E) that forms the acrylic temperature-responsive polymer;
The water-based adhesive composition according to any one of claims 1 to 4, which is obtained by copolymerizing.
前記モノマー(E)が、N−エチルアクリルアミド、N−n−プロピルアクリルアミド、N−イソプロピルアクリルアミド、N−シクロプロピルアクリルアミド、N,N−ジエチルアクリルアミド、N−メチル−N−エチルアクリルアミド、N−メチル−N−n−プロピルアクリルアミド、N−メチル−N−イソプロピルアクリルアミド、N−アクリロイルピペリジン、N−アクリロイルピロリジン、N−アクリロイルモルホリン、N−メトキシプロピルアクリルアミド、N−エトキシプロピルアクリルアミド、N−イソプロポキシプロピルアクリルアミド、N−エトキシエチルアクリルアミド、N−(2,2−ジメトキシエチル)−N−メチルアクリルアミド、N−1−メチル−2−メトキシエチルアクリルアミド、N−1−メトキシメチルプロピルアクリルアミド、N−ジ(2−メトキシエチル)アクリルアミド、N−2−メトキシエチル−N−n−プロピルアクリルアミド、N−2−メトキシエチル−N−エチルアクリルアミド、N−2−メトキシエチル−N−イソプロピルアクリルアミド、N−メトキシエトキシプロピルアクリルアミド、N−テトラヒドロフルフリルアクリルアミド、N−(1,3−ジオキソラン−2−イル)メチルアクリルアミド、N−メチル−N−(1,3−ジオキソラン−2−イル)メチルアクリルアミド、N−シクロプロピルアクリルアミド、N−ピロリジノメチルアクリルアミド、N−ピペリジノメチルアクリルアミド、N−2−モルホリノエチルアクリレート、N−2−モルホリノエトキシエチルアクリレートおよびこれらに対応するメタクリレートからなる群から選択される少なくとも一種であり、
前記ウレタンエマルジョンと、前記モノマー(E)とを、生成するアクリル系温度応答性ポリマーの相転移温度より低い温度で共重合させて得られる、請求項5に記載の水系接着剤組成物。
The monomer (E) is N-ethylacrylamide, Nn-propylacrylamide, N-isopropylacrylamide, N-cyclopropylacrylamide, N, N-diethylacrylamide, N-methyl-N-ethylacrylamide, N-methyl- N-n-propylacrylamide, N-methyl-N-isopropylacrylamide, N-acryloylpiperidine, N-acryloylpyrrolidine, N-acryloylmorpholine, N-methoxypropylacrylamide, N-ethoxypropylacrylamide, N-isopropoxypropylacrylamide, N-ethoxyethyl acrylamide, N- (2,2-dimethoxyethyl) -N-methyl acrylamide, N-1-methyl-2-methoxyethyl acrylamide, N-1-methoxymethyl Propylacrylamide, N-di (2-methoxyethyl) acrylamide, N-2-methoxyethyl-Nn-propylacrylamide, N-2-methoxyethyl-N-ethylacrylamide, N-2-methoxyethyl-N-isopropyl Acrylamide, N-methoxyethoxypropylacrylamide, N-tetrahydrofurfurylacrylamide, N- (1,3-dioxolan-2-yl) methylacrylamide, N-methyl-N- (1,3-dioxolan-2-yl) methyl Acrylamide, N-cyclopropyl acrylamide, N-pyrrolidinomethyl acrylamide, N-piperidinomethyl acrylamide, N-2-morpholinoethyl acrylate, N-2-morpholinoethoxyethyl acrylate, and their corresponding methacrylates It is at least one selected from the group consisting of rate,
The water-based adhesive composition according to claim 5, which is obtained by copolymerizing the urethane emulsion and the monomer (E) at a temperature lower than the phase transition temperature of the acrylic temperature-responsive polymer to be produced.
JP2005211126A 2005-07-21 2005-07-21 Water-based adhesive composition Active JP4935011B2 (en)