JP2006321062A - Laser marking paper, label and label sheet - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a laser marking paper for performing laser marking with no limited fixed marking region and a label and a label sheet employing the leaser marking paper thereon. <P>SOLUTION: The label sheet 1, on which a label 11 for a drug container made of a laser marking paper is pasted, comprises a base material 2 containing a dark color base pigment such as carbon black or the like and a front surface coating layer 3 formed on the first surface 13 of the base material and a rear surface layer 7 formed on its second surface 14. The front surface coating layer 3 and the rear surface layer 7 are respectively formed of a bright color base aqueous coating paint containing a sensitizer for laser. On the rear surface side of the rear surface layer 7, a self-adhesive layer 8 is formed, and a releasing paper 9 is releasably stuck to the self-adhesive layer 8. By irradiating laser from the front surface coating layer 3 side, the paint in the region irradiated with the laser of the front surface coating layer 3 evaporates and is flyingly peeled off, resulting in exposing the surface layer of the dark color base base material 2 and a revealing the state, in which dark color base characters or the like are visually recognized. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

  The present invention relates to a laser marking sheet for marking with a laser, a label using the same, and a label sheet.

  Marking the date of manufacture, lot number, etc. of a product on a label, etc., and attaching the label etc. to the product is performed. As a method for marking a label or the like, a method using a laser is known (for example, Patent Document 1).

  Labels are also attached to drug containers such as ampoules and vials to identify the contents, but such labels are coated with an adhesive on the back of a label substrate made of paper or synthetic resin. The surface is printed with information such as drug name and content.

  The information on the label of the medicine container must be hard to disappear and have good visibility. Therefore, a black paint is applied to a predetermined area of the label of the drug container (solid printing), and the black paint is evaporated by a laser to mark the black paint application area.

JP-A-9-277705

  However, according to the above method, it is necessary to perform solid printing for marking in a certain area of the label, and it may be difficult to secure a printing area for solid printing due to display area of the label and design restrictions.

  An object of the present invention is to provide a laser marking sheet for performing laser marking in which a marking area is not limited to a certain area, a label using the same, and a label sheet.

Means for Solving the Problems and Effects of the Invention and Effects of the Invention

The laser marking paper of the present invention for solving the above problems is
A substrate formed by paper containing pigments or dyes;
The first surface of the base material contains a sensitizer for laser, has a light color pigment having a lightness greater than that of the base material pigment or a light color dye having a lightness greater than that of the dye, and is irradiated with laser light. A surface coat layer that is broken and marked.

  By including a laser sensitizer in the surface coat layer, the irradiated portion can be easily destroyed when laser light is irradiated, and marking can be applied. Also, since the pigment is contained in the base material and the surface coat layer has a light-colored pigment having a lightness greater than that of the base material pigment, the characters formed by the marking are visually recognized by the contrast between the surface coat layer and the base material. It's easy to do.

  The base material may contain one or more kinds of acrylic resin, phenol resin, latex adhesive, and petroleum wax. An acrylic resin, a phenol resin, and a latex adhesive function as a binder, and a petroleum wax functions as an additive.

  As the pigment contained in the substrate, a dark pigment may be used. Due to the contrast between the base material and the surface coat layer, characters and the like formed by the marking are easily visible.

  More specifically, for example, carbon black can be used as the pigment contained in the substrate. Since carbon black effectively absorbs far-infrared light and generates heat, the surface coat layer formed on the first surface of the substrate is easily destroyed by laser light.

  The base material may contain a pigment in a region from the first surface to the inside of 10 μm or more. Alternatively, the substrate may contain 5% by weight or more and 90% by weight or less of pigment. By doing in this way, the character etc. which were formed by marking become easier to visually recognize.

  The surface coat layer contains an organic pigment or an inorganic pigment, and an aqueous resin. By containing such a material, it is possible to form a surface coat layer of a light-colored pigment that is broken and marked by being irradiated with laser light.

  The film thickness of the surface coat layer is preferably 10 μm or more and 50 μm or less. By forming in this range, it is possible to form a laser marking sheet that has durability and is easily marked by a laser.

  The sensitizer for laser contains at least one of inorganic metal borate or inorganic metal silicate. By including such a laser sensitizer in the surface coat layer, laser marking can be easily performed.

And the label of this invention contains the adhesion layer in the 2nd surface on the opposite side to the 1st surface of the base material of the said laser marking paper. Such a label has durability and can easily perform laser marking. Furthermore, the label of the present invention is:
It is good also as a structure where the back surface layer which has a light-colored pigment was formed between the base material and the adhesion layer. By comprising in this way, when a label is stuck on a transparent or semi-transparent sticking object, the back side of the label can be seen through the sticking object, but the design is good.

  Furthermore, by forming a label sheet in which the pressure-sensitive adhesive layer of the label is covered with release paper, the label can be easily attached to an object to be applied after laser marking.

  Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 shows a cross-sectional view of a label sheet 1 to which a drug container label 11 which is a laser marking sheet of the present invention is attached. The drug container label 11 includes a base material 2 containing a pigment such as carbon black, a surface coat layer 3 on the first surface 13, and a back layer 7 on the second surface 14. An adhesive layer 8 is formed on the back surface side of the back layer 7, and a release paper 9 is detachably adhered to the adhesive layer 8 to form the label sheet 1.

  As the base material 2, it is desirable to use high-quality colored paper from the viewpoint of durability and color development of laser marking, but the present invention is not limited to this, and plain paper, coated paper, art paper or the like can be used. And the base material 2 contains an inorganic or organic pigment, for example, contains black pigments, such as carbon black. However, the pigment is not limited to carbon black, and is preferably a dark pigment such as cyanine blue, an organic pigment, or milory blue, an inorganic pigment, in order to facilitate visual recognition by laser marking. Alternatively, a dark color dye such as a basic dye having resistance to an alcohol such as ethanol can also be used. Furthermore, the base material 2 may contain an additive such as an acrylic resin, a phenol resin, a binder such as a latex adhesive, and a petroleum wax. By adjusting these blends, the color of characters printed on the label can be adjusted. A pigment such as carbon black absorbs far-infrared light effectively and generates heat due to the contrast between the surface coat layer 3 and the substrate 2, and the surface coat layer 3 is easily destroyed by laser light. The material 2 may be contained in an amount of 5 wt% to 90 wt%.

  The substrate 2 can be impregnated with a pigment such as carbon black using a prewetting method, a float method, a doctor bar method, or the like. Alternatively, a pigment such as carbon black may be contained in the substrate 2 by a coating method such as a knife coater, a comma coater, or a die coater. The thickness of the substrate 2 is not particularly limited, but is desirably impregnated with a pigment such as carbon black at least 10 μm or more from the surface.

  The surface coat layer 3 and the back surface layer 7 are formed of a light-colored aqueous coating paint containing a sensitizer for laser. More specifically, the surface coat layer 3 and the back surface layer 7 include an organic pigment or an inorganic pigment and an aqueous resin. Examples of the organic pigment include a phthalocyanine pigment and an azo pigment. Examples of the inorganic pigment include kaolin and carbon dioxide. Examples of aqueous resins such as titanium and calcium carbonate include emulsion resins. Instead of an organic pigment or an inorganic pigment, a light-colored dye such as a basic dye resistant to alcohol may be included. Further, it contains an adhesive such as starch or synthetic rubber latex, and may contain a sensitizer for laser, a dispersant, a surfactant, petroleum wax or the like as an auxiliary agent.

The laser sensitizer is not particularly limited as long as it is a substance capable of converting laser light into heat. The laser sensitizer is dispersed in the form of particles in the surface coat layer 3 and the back layer 7 or dissolved in a resin. The particle diameter is usually 50 μm or less, and particularly preferably 0.1 to 10 μm. By setting the particle size of the laser sensitizer within this range, the coating can be effectively evaporated and scattered by the laser. The content of the laser sensitizer in the surface coat layer 3 is desirably 3% by weight or more and 50% by weight or less of the surface coat layer 3. If it is 3% by weight or less, the surface coat layer 3 is difficult to be destroyed by the laser, and if it is 50% by weight or more, the color of the surface coat layer 3 is deteriorated and the strength is fragile. A laser having a wavelength in the far infrared region is used, and for example, a CO ₂ laser (wavelength 10.6 μm) can be used. Alternatively, a YAG laser or YVO ₄ laser (wavelength 1.064 μm) may be used. Examples of the laser sensitizer used for a laser having a wavelength in the far infrared region include inorganic borate salts and inorganic silicate salts.

  Specifically, examples of the inorganic borate metal salts include aluminum borate, sodium borate, manganese borate, zinc borate, barium borate, magnesium borate, calcium borate, lithium borate and the like.

  Examples of the inorganic silicate metal salts include kaolin, cordierite, synthetic mica (such as fluorine phlogopite and fluorine tetrasilicon mica), and natural mica (such as mascobite, phlogopite, biotite, and sericite).

  The aqueous coating paint containing the above-described sensitizer for laser is coated on the substrate 2 by a cast coating method using a knife coater, comma coater, die coater, kiss coater, etc., and the surface coat layer 3 and the back layer 7 are formed. It is formed. The surface coat layer 3 is evaporated and scattered by the laser, and the marking visibility is enhanced by the contrast between the exposed black base material 2 and the non-destructive coating layer (surface coat layer 3). It is desirable to have a thickness of

As shown in FIG. 2, the drug container label 1 is marked with a CO ₂ laser or the like. By irradiating a laser from the surface coat layer 3 side, the coating of the region of the surface coat layer 3 irradiated with the laser is evaporated and scattered and peeled off. When the surface layer of the dark base material 2 is exposed, dark characters and the like are visible. Since the surface coat layer 3 contains a sensitizer for laser, the laser energy required to destroy the surface coat layer 3 can be remarkably reduced. Furthermore, since the base material 2 contains a dark pigment such as carbon black, the laser light is absorbed, reflected or scattered, and further heat is generated by the laser light, thereby amplifying the destruction of the surface coat layer 3 and performing high-speed printing. enable. That is, since the surface coat layer 3 contains a laser sensitizer, the surface coat layer 3 is directly destroyed by a laser, reflected from the base material 2 containing a dark pigment such as carbon black, and heat generated by the laser light. Will be destroyed. And this base material 2 uses the contrast with the non-destructive part of the surface coat layer 3 while preventing the transmission of laser light to improve the printing quality, and the printing body with high visibility and excellent printing quality. Can be obtained.

  As shown in FIG. 3, the drug container label 11 marked with laser light can be peeled off from the release paper 9 of the label sheet 1 and used for a drug container 21 such as an ampoule or a vial. The drug container label 11 of the present invention uses a resistant pigment containing carbon black or the like to provide a printed body with high resistance (such as alcohol resistance) and excellent print quality required for a label for drug containers. Obtainable. That is, the label printing is not lost by the chemicals, and it is excellent in friction resistance, moisture resistance, heat resistance, light resistance, and the like. In addition, since laser printing can be performed without solid printing, it is possible to mark the entire label without being restricted by the design of the label.

  Next, the manufacturing process of the drug container label 11 of the present invention will be described. First, an impregnation process and a drying process are demonstrated using FIG. The fine paper used as the substrate 2 is immersed in a liquid tank 31 having a solution 32 containing a pigment such as carbon black, and the fine paper is impregnated with a pigment such as carbon black. In addition, it is advisable to use quality paper that is not coated with silicone or wax. The solution 32 may contain an inorganic pigment, an organic pigment, a phenol resin, a latex adhesive, a petroleum wax, or the like. The coloration of the base material 2 can be adjusted by these formulations. The fine paper (base material 2) immersed in the liquid tank 31 and containing carbon black or the like is subsequently dried by a drying process.

  In addition to the above method, black or dark-colored high-quality paper made of paper made of cellulose fibers mixed with a pigment such as carbon black can be used.

  Then, as shown in FIG. 5, the surface coat layer 3 and the back surface layer 7 are formed by the air knife and roller coating on both surfaces of the base material 2 containing carbon black etc. by a pre-process. And the surface coat layer 3 and the back surface layer 7 are dried by a drying process.

  After the surface coat layer 3 and the back surface layer 7 are formed on the substrate 2, an adhesive layer 8 is formed on the back surface layer 7 side as shown in FIG. Let In this way, the label sheet 1 of the present invention is manufactured.

  Then, as shown in FIG. 7, characters or the like are marked on the drug container label 11 of the label sheet 1 by a laser 51 (see FIG. 2). Subsequently, the label 11 for the medicine container stuck in a peelable state on the release paper 9 of the label sheet 1 is peeled off by turning off the release paper 9 at an acute angle by a peeling device provided with the folding plate 52. Peel from. The peeled drug container label 11 is affixed to the drug container 21 which is a label application object conveyed by the rotation of the labeling disk 53.

  FIG. 8 shows another embodiment of the label sheet. The label sheet 61 has a base material 2 containing carbon black or the like, and a surface coat layer 3 formed on the first surface 13 thereof. An adhesive layer 8 is formed on the second surface 14 of the substrate 2, and a release paper 9 is detachably adhered to the adhesive layer 8. In this embodiment, the back layer 7 is not formed.

  When the back layer 7 is not formed, the manufacturing cost can be reduced. On the other hand, when the coating layer is formed on both surfaces of the substrate 2 as in the above-described embodiment, the adhesive layer 8 can be formed on either surface in the adhesive layer 8 forming step.

  In order to confirm the effect of the present invention, the following printing performance test was conducted. The print reproducibility was evaluated based on whether a label marked with a laser was imaged by an imaging device and whether the label printing could be recognized by the image recognition device. Abrasion resistance was evaluated by applying a load of 500 g to fine paper and rubbing the label 50 times to evaluate the change in the label. As storage stability, moisture resistance, heat resistance and light resistance were evaluated. As for moisture resistance, label change was evaluated after storage for 1 month at 40 ° C. and 95% humidity. For heat resistance, the change in the label was evaluated by storing at 60 ° C. for 72 hours. The light resistance was evaluated by evaluating the change of the label by storing it with light for 80 hours in a fade meter. Tape adhesion was evaluated by attaching cello tape (registered trademark) to the printed surface and removing it. If the print could be recognized well, ◯, if it was recognizable, Δ, if the print was disturbed and difficult to recognize or unrecognizable, x.

  A chemical resistance test was performed on the marked label. Alcohol resistance was evaluated by dripping 99.5% absolute ethanol and 77% disinfecting ethanol for 10 seconds and rubbing 10 times with tissue paper. The evaluation was performed by immersing in 77% ethanol for disinfection for 10 minutes. Human fat resistance was evaluated by rubbing with human fat.

  It was confirmed that the label of the present invention has sufficient durability in any test.

  As described above, since the surface coat layer 3 of the pharmaceutical label of the present invention contains a laser sensitizer, the label can be easily marked. The surface coat layer 3 is evaporated and scattered by the laser, thereby making use of the contrast between the dark-colored base material 2 and the light-colored surface coat layer 3 to provide high visibility and excellent print quality. The font can be obtained. Furthermore, since the surface coat layer 3 is light-colored, it can be printed by printing or the like in addition to laser marking.

Sectional drawing of the label for drug containers of this invention. The figure explaining the printing by a laser. The figure explaining the usage example of the label for medicines. The figure explaining the impregnation of the carbon to a base material. The figure explaining a surface coat layer and a back surface layer. The figure explaining adhesion of an adhesion layer and release paper. The figure explaining peeling of release paper, and sticking of a label. Sectional drawing of the other Example of the label for medicines of this invention.

Explanation of symbols

DESCRIPTION OF SYMBOLS 1 Label sheet 2 Base material 3 Surface coat layer 7 Back surface layer 8 Adhesive layer 9 Release paper 11 Label for drug containers 13 First surface 14 Second surface 21 Drug container 51 Laser

Claims (12)

A substrate formed by paper containing pigments or dyes;
The first surface of the substrate has a light-colored pigment containing a laser sensitizer and having a lightness greater than that of the pigment or a light-colored dye having a lightness greater than that of the dye, and being irradiated with laser light. A laser marking paper comprising a surface coat layer that is broken and marked.   The laser marking paper according to claim 1, wherein the base material contains at least one kind of acrylic resin, phenol resin, latex adhesive, and petroleum wax.   The laser marking paper according to claim 1 or 2, wherein the pigment contained in the base material is a dark pigment.   The laser marking paper according to any one of claims 1 to 3, wherein the pigment contained in the substrate is carbon black.   The laser marking paper according to any one of claims 1 to 4, wherein the base material contains the pigment in an area from the first surface to the inside of 10 µm or more.   The laser marking paper according to any one of claims 1 to 5, wherein the base material contains 5% by weight or more and 90% by weight or less of the pigment.   The laser marking paper according to any one of claims 1 to 6, wherein the surface coat layer includes an organic pigment or an inorganic pigment, and an aqueous resin.   The laser marking paper according to any one of claims 1 to 7, wherein a film thickness of the surface coat layer is 10 µm or more and 50 µm or less.   The laser marking paper according to any one of claims 1 to 8, wherein the laser sensitizer includes at least one of an inorganic borate metal salt or an inorganic silicate metal salt.   The label which contains an adhesion layer in the 2nd surface on the opposite side to the said 1st surface of the said base material of the laser marking paper of any one of Claim 1 thru | or 9.   The label according to claim 10, wherein a back layer having a light color pigment is formed between the substrate and the adhesive layer. The label sheet containing the release paper which covers the said adhesion layer formed in the said 2nd surface of the label of Claim 10 or 11.