JP2006160322A - Easy-peelable film lid for tray - Google Patents
Easy-peelable film lid for tray Download PDFInfo
- Publication number
- JP2006160322A JP2006160322A JP2004355059A JP2004355059A JP2006160322A JP 2006160322 A JP2006160322 A JP 2006160322A JP 2004355059 A JP2004355059 A JP 2004355059A JP 2004355059 A JP2004355059 A JP 2004355059A JP 2006160322 A JP2006160322 A JP 2006160322A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- film
- easy
- tray
- peel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、カレー、ルーなどの保香性を必要とする内容物を収納するポリプロピレン製トレーの開口部を封止するために使用するイージーピール性トレー用フィルム蓋材に関するものである。 The present invention relates to a film cover material for an easy-peeling tray used for sealing an opening of a polypropylene tray for storing contents requiring aroma retaining properties such as curry and roux.
従来、ポリプロピレン製トレーの開口部を封止するために使用するイージーピール（易剥離）性トレー用フィルム蓋材としては、例えば図２に示すように、積層構成が、表面側から順次、表面層（２１０）／押出しラミネーション用ＡＣ剤層（２２０）／中間層（２３０）／ドライラミネーション用接着剤層（２４０）／イージーピールフィルム層（２５０）からなり、表面層（２１０）の積層構成が、表面側から順次、ポリエチレンテレフタレートフィルム層（２１１）／無機酸化物蒸着層（２１２）／保護コート層（２１３）／印刷層（２１４）であり、中間層（２３０）が、ポリエチレンフィルム層であるイージーピール性トレー用フィルム蓋材（２００）が使用されていた。そして、表面層と中間層と間のラミネート強度が弱すぎると、トレーを開封するために、イージーピール性トレー用フィルム蓋材をトレーの開口部に周設するフランジの上面から剥離するときに、表面層と中間層との間でデラミネーション（層間剥離）が発生しやすく、また、表面層と中間層と間のラミネート強度が強すぎると、フィルム裂けを起こしやすいため、押出しラミネート加工時に、表面層と中間層との間のラミネート強度をコントロールして、剥離時の力を分散させるようにしていた。 2. Description of the Related Art Conventionally, as an easy peel (easy peeling) tray cover for an easy-to-peel tray used for sealing an opening of a polypropylene tray, for example, as shown in FIG. (210) / AC layer for extrusion lamination (220) / intermediate layer (230) / adhesive layer for dry lamination (240) / easy peel film layer (250), and the laminated structure of the surface layer (210) is Easy from the surface side: polyethylene terephthalate film layer (211) / inorganic oxide vapor deposition layer (212) / protective coat layer (213) / printing layer (214), and intermediate layer (230) being a polyethylene film layer A film lid for peelable tray (200) has been used. And when the laminate strength between the surface layer and the intermediate layer is too weak, in order to open the tray, when peeling the film cover material for easy peel tray from the upper surface of the flange around the opening of the tray, Delamination (delamination) is likely to occur between the surface layer and the intermediate layer, and if the laminate strength between the surface layer and the intermediate layer is too strong, film tearing is likely to occur. The lamination strength between the layer and the intermediate layer was controlled so that the force at the time of peeling was dispersed.
しかしながら、経時において、イージーピール性トレー用フィルム蓋材とトレーとの接着強度が強くなるため、トレーを開封するときに、イージーピール性トレー用フィルム蓋材の全体が伸びやすくなり、表面層と中間層と間にずれ応力が掛かって、表面層と中間層との間でデラミネーションが発生し、いわゆる二重蓋の不良現象を生じることがあった。 However, since the adhesive strength between the easy-peeling tray film lid and the tray increases with time, the entire easy-peeling film lid becomes easy to stretch when the tray is opened, A shear stress is applied between the layers, and delamination occurs between the surface layer and the intermediate layer, which may cause a so-called double lid defect phenomenon.
本発明は、上述の従来のイージーピール性トレー用フィルム蓋材の問題点を解決したものであり、経時におけるトレーとの接着強度の上昇が比較的に低く、トレー開封時に構成層間のデラミネーションの発生がないイージーピール性トレー用フィルム蓋材を提供するものである。 The present invention solves the above-described problems of the conventional easy-peelable tray film cover material, and the increase in the adhesive strength with the tray over time is relatively low, and the delamination between the constituent layers is prevented when the tray is opened. It is an object of the present invention to provide an easy peel tray film cover material that does not generate.
すなわち、本発明の第１の発明は、積層構成が、表面側から順次、表面層／ドライラミネーション用接着剤層／中間層／ドライラミネーション用接着剤層／イージーピールフィルム層からなり、かつ、表面層の積層構成が、表面側から順次、二軸延伸ポリプロピレンフィルム層／印刷層であり、中間層の積層構成が、表面側から順次、ポリエチレンテレフタレートフィルム層／無機酸化物蒸着層／保護コート層であることを特徴とするイージーピール性トレー用フィルム蓋材である。 That is, in the first invention of the present invention, the laminated structure is composed of the surface layer / the adhesive layer for dry lamination / the intermediate layer / the adhesive layer for dry lamination / the easy peel film layer sequentially from the surface side, and the surface The laminated structure of the layers is biaxially oriented polypropylene film layer / printing layer sequentially from the surface side, and the laminated structure of the intermediate layer is sequentially formed of polyethylene terephthalate film layer / inorganic oxide vapor deposition layer / protective coat layer from the surface side. It is a film cover material for an easy-peeling tray characterized by being.
次に、本発明の第２の発明は、中間層とイージーピールフィルム層との接着強度が、５Ｎ以上であることを特徴とする第１の発明に記載のイージーピール性トレー用フィルム蓋材である。 Next, a second invention of the present invention is an easy peel tray film cover material according to the first invention, characterized in that the adhesive strength between the intermediate layer and the easy peel film layer is 5N or more. is there.
次に、本発明の第３の発明は、イージーピールフィルム層の厚みが、３０μｍ以下であることを特徴とする第１の発明又は第２の発明に記載のイージーピール性トレー用フィル
ム蓋材である。
Next, the third invention of the present invention is the easy-peel tray cover material according to the first invention or the second invention, wherein the easy-peel film layer has a thickness of 30 μm or less. is there.
そして、本発明の第４の発明は、プラスチック製トレーに剥離強度が１０Ｎ以下で接着したことを特徴とする第１の発明乃至第３の発明に記載のイージーピール性トレー用フィルム蓋材である。 According to a fourth aspect of the present invention, there is provided an easy peel tray film cover material according to any one of the first to third aspects, wherein the peel strength is 10 N or less. .
本発明のイージーピール性トレー用フィルム蓋材は、積層構成中の中間層が伸びにくいポリエチレンテレフタレートフィルムを基材とする蒸着フィルムであり、この延びにくい中間層に接着するイージーピールフィルム層の全体も、トレーから剥離するときに、伸びにくくなり、この結果、表面層と中間層と間にずれ応力が発生しにくく、表面層と中間層との間でデラミネーションが発生しにくくなる。また、中間層とイージーピールフィルム層との接着強度を５Ｎ以上にすることで、中間層とイージーピールフィルム層との間でデラミネーションが発生しにくくなる。 The film cover material for easy peelable trays of the present invention is a vapor deposition film based on a polyethylene terephthalate film in which the intermediate layer in the laminated structure is difficult to stretch, and the entire easy peel film layer that adheres to this difficult to extend intermediate layer When peeled from the tray, it becomes difficult to stretch, and as a result, a shift stress is hardly generated between the surface layer and the intermediate layer, and delamination is hardly generated between the surface layer and the intermediate layer. Moreover, delamination becomes difficult to generate | occur | produce between an intermediate | middle layer and an easy peel film layer by making the adhesive strength of an intermediate | middle layer and an easy peel film layer into 5 N or more.
また、トレー開口部フランジに、イージーピール性トレー用フィルム蓋材を熱圧着及び冷却して接着したときに、イージーピール性トレー用フィルム蓋材のイージーピールフィルム層に歪みを発生し、この残留歪みが経時で緩和されると接着強度が上昇する。また、イージーピールフィルム層の構成樹脂間の凝集破壊にともない経時において接着強度が上昇する。本発明のイージーピール性トレー用フィルム蓋材は、イージーピールフィルム層の厚みを３０μｍ以下の薄厚にすることで、イージーピールフィルム層の構成樹脂間の凝集破壊にともなう接着強度の上昇を抑えることができる。 In addition, when the easy-peeling tray film lid is bonded to the tray opening flange by thermocompression bonding and cooling, distortion occurs in the easy-peel film layer of the easy-peeling tray film lid. When is relaxed over time, the adhesive strength increases. In addition, the adhesive strength increases with time due to cohesive failure between the constituent resins of the easy peel film layer. The film cover material for the easy peelable tray of the present invention can suppress an increase in adhesive strength due to cohesive failure between the constituent resins of the easy peel film layer by making the thickness of the easy peel film layer 30 μm or less. it can.
また、本発明のイージーピール性トレー用フィルム蓋材は、プラスチック製トレーに剥離強度が１０Ｎ以下で接着するため、トレーから剥離するときの剥離強度が比較的に弱く、蓋材の構成層間にずれ応力が掛かりずらいため、構成層でデラミネーションして、いわゆる二重蓋の不良現象を生じにくい。 In addition, since the film cover material for easy peelable trays of the present invention adheres to a plastic tray with a peel strength of 10 N or less, the peel strength when peeled from the tray is relatively weak, and the film cover material is displaced between the constituent layers of the cover material. Since stress is difficult to apply, delamination is difficult in the constituent layers, and so-called double lid defect phenomenon is unlikely to occur.
本発明のイージーピール性トレー用フィルム蓋材は、ポリプロピレン製のトレーを密封るために、トレーの開口部に周設するフランジ上面に、ヒートシール法によりイージーピール可能に接着するものである。このイージーピール性トレー用フィルム蓋材（１００）の積層構成は、図１に示すように、表面側から順次、表面層（１１０）／ドライラミネーション用接着剤層（１２０）／中間層（１３０）／ドライラミネーション用接着剤層（１４０）／イージーピールフィルム層（１５０）からなり、表面層（１１０）の積層構成は、表面側から順次、二軸延伸ポリプロピレンフィルム層（１１１）／印刷層（１１２）であり、中間層（１３０）の積層構成は、表面側から順次、ポリエチレンテレフタレートフィルム層（１３１）／無機酸化物蒸着層（１３２）／保護コート層（１３３）であり、中間層（１３０）とイージーピールフィルム層（１５０）との接着強度を５Ｎ以上にし、イージーピールフィルム層の厚みを３０μｍ以下にするものである。そして、トレーを密封した本発明のイージーピール性トレー用フィルム蓋材が、トレーを開封するときに、１０Ｎ以下の剥離強度でフィルム蓋材が剥離可能にトレーにヒートシールするものである。 In order to seal a polypropylene tray, the film cover material for an easy peel tray of the present invention is adhered to the upper surface of a flange provided around the opening of the tray so as to be easily peelable by a heat seal method. As shown in FIG. 1, the laminated structure of the easy peel tray cover (100) is as follows: surface layer (110) / dry lamination adhesive layer (120) / intermediate layer (130) from the surface side. / Dry lamination adhesive layer (140) / Easy peel film layer (150). The surface layer (110) is laminated in the order of the biaxially oriented polypropylene film layer (111) / printing layer (112) from the surface side. The laminated structure of the intermediate layer (130) is polyethylene terephthalate film layer (131) / inorganic oxide vapor deposition layer (132) / protective coat layer (133) sequentially from the surface side, and the intermediate layer (130). The strength of the easy peel film layer (150) is 5N or more, and the thickness of the easy peel film layer is 30 μm or less. . And the film cover material for easy peelable trays of this invention which sealed the tray heat-seals the tray so that the film cover material can be peeled with a peel strength of 10 N or less when the tray is opened.
以下に、本発明の具体的実施例について説明する。 Specific examples of the present invention will be described below.
まず、二軸延伸ポリプロピレンフィルム（二村化学株式会社製 ＦＯＲ ２０μｍ）の片面に、グラビア印刷法で文字及び絵柄を印刷し、次に、この二軸延伸ポリプロピレンフィルムの印刷層側面に、ドライラミネーション用接着剤（大日本インキ化学工業株式会社製 ＬＸ７０３ＶＬ／ＫＲ９０／酢酸エチル＝１５／１／１８）を塗布（ドライ ３．５
〜４．０ｇ／ｍ2 ）し、このドライラミネーション用接着剤層側面に、ポリエチレンテレフタレート層／無機酸化物蒸着層／保護コート層構成の積層フィルム（凸版印刷株式会社製 ＧＬ−ＡＥＨ １２μｍ）のポリエチレンテレフタレート層側をドライラミネーション法で積層し、次に、この積層フィルムの保護コート層側面にドライラミネーション用接着剤（大日本インキ化学工業株式会社製 ＬＸ７０３ＶＬ／ＫＲ９０／酢酸エチル＝１５／１／１８）を塗布（ドライ ３．５〜４．０ｇ／ｍ2 ）し、このドライラミネーション用接着剤塗布層側面に、イージーピールフィルム（ジェイフィルム株式会社製 ＴＨ−１０００ ３０μｍ）をドライラミネーション法で積層して、図１に示す〔上面側〕二軸延伸ポリエチレンテレフタレートフィルム層（１１１）／印刷層（１１２）／ドライラミネーション用接着剤層（１２０）／ポリエチレンテレフタレート層（１３１）／無機酸化物蒸着層（１３２）／保護コート層（１３３）／ドライラミネーション用接着剤層（１４０）／イージーピールフィルム層（１５０）構成の実施例のイージーピール性トレー用フィルム蓋材（１００）を作製した。
First, letters and patterns are printed on one side of a biaxially stretched polypropylene film (FOR 20 μm, manufactured by Nimura Chemical Co., Ltd.) by the gravure printing method, and then dry lamination adhesion is applied to the side of the printed layer of the biaxially stretched polypropylene film. Agent (Dai Nippon Ink Chemical Co., Ltd. LX703VL / KR90 / ethyl acetate = 15/1/18) is applied (dry 3.5
To 4.0 g / m 2 ), and a polyethylene film of a laminated film (GL-AEH 12 μm manufactured by Toppan Printing Co., Ltd.) having a polyethylene terephthalate layer / inorganic oxide vapor deposition layer / protective coat layer structure on the side surface of the adhesive layer for dry lamination. The terephthalate layer side was laminated by a dry lamination method, and then an adhesive for dry lamination (LX703VL / KR90 / ethyl acetate = 15/1/18, manufactured by Dainippon Ink & Chemicals, Inc.) on the side of the protective coating layer of the laminated film. Is applied (dry 3.5-4.0 g / m 2 ), and an easy peel film (TH-1000 30 μm manufactured by J Film Co., Ltd.) is laminated on the side of this dry lamination adhesive coating layer by the dry lamination method. 1 [upper surface side] biaxially stretched polyethylene terephthalate film shown in FIG. Layer (111) / printing layer (112) / adhesive layer for dry lamination (120) / polyethylene terephthalate layer (131) / deposited inorganic oxide layer (132) / protective coating layer (133) / adhesive layer for dry lamination (140) / Easy peel film layer (150) An easy peel tray film lid material (100) according to an example was produced.
次に、従来のイージーピール性トレー用フィルム蓋材の一例である比較例について説明する。 Next, a comparative example which is an example of a conventional film cover material for an easy peel tray will be described.
＜比較例＞
まず、ポリエチレンテレフタレート層／無機酸化物蒸着層／保護コート層構成の積層フィルム（凸版印刷株式会社製 ＧＬ−ＡＥＨ １２μｍ）の保護コート層側面に、グラビア印刷法で文字及び絵柄を印刷し、次に、この印刷層側面に、押出しラミネーション用ＡＣ剤を塗布し、この押出しラミネーション用ＡＣ剤層側面に、押出しラミネーション法でポリエチレン層を積層し、そして、このポリエチレン層側面に、ドライラミネーション用接着剤を塗布し、このドライラミネーション用接着剤塗布層側面に、イージーピールフィルム（ジェイフィルム株式会社製 ＴＨ−１０００ ３０μｍ）をドライラミネーション法で積層して、図２に示すポリエチレンテレフタレートフィルム層（２１１）／無機酸化物蒸着層（２１２）／保護コート層（２１３）／印刷層（２１４）／押出しラミネーション用ＡＣ剤層（２２０）／ポリエチレンフィルム層（２３０）／ドライラミネーション用接着剤層（２４０）／イージーピールフィルム層（２５０）構成の比較例のイージーピール性トレー用フィルム蓋材（２００）を作製した。
<Comparative example>
First, letters and designs are printed by gravure printing on the side of the protective coating layer of a laminated film (GL-AEH 12 μm manufactured by Toppan Printing Co., Ltd.) having a polyethylene terephthalate layer / inorganic oxide vapor deposition layer / protective coating layer configuration, and then An AC agent for extrusion lamination is applied to the side surface of the printing layer, a polyethylene layer is laminated on the side surface of the AC agent layer for extrusion lamination by an extrusion lamination method, and an adhesive for dry lamination is applied to the side surface of the polyethylene layer. An easy peel film (TH-1000 30 μm, manufactured by J Film Co., Ltd.) was laminated on the side of this dry lamination adhesive coating layer by the dry lamination method, and the polyethylene terephthalate film layer (211) / inorganic shown in FIG. Oxide deposition layer (212) / Protective coating layer ( 13) / printing layer (214) / extrusion lamination AC agent layer (220) / polyethylene film layer (230) / dry lamination adhesive layer (240) / easy peel film layer (250) Film tray material (200) for an adhesive tray.
＜評 価＞
まず、実施例のイージーピール性トレー用フィルム蓋材を、ポリプロピレン製のトレーの開口部周縁に設けられてフランジ上面にヒートシール法で各種シール条件でシールしたのち、フィルム蓋材の剥離強度を測定した。シール条件は、温度が１３０℃、１４０℃、１５０℃、１６０℃、１７０℃の５条件で、圧力は１Ｋｇ／ｃｍ2 で、時間は１秒であった。なお、二軸延伸ポリエチレンテレフタレートフィルム層／印刷層の積層フィルムとポリエチレンテレフタレート層／無機酸化物蒸着層／保護コート層の積層フィルムとの間の接着強度は、１．５Ｎで、ポリエチレンテレフタレート層／無機酸化物蒸着層／保護コート層の積層フィルムとイージーピールフィルムとの間の接着強度は、６Ｎであった。測定結果は、図５のシール温度と剥離強度との関係を示すグラフから分かるように、シール温度が高くなるにつれて剥離強度も高くなるが、シール温度が１３０〜１７０℃では、１０Ｎ以下であった。デラミネーションを発生したものはなかった。
<Evaluation>
First, the film cover material for the easy peel tray of the example was provided on the periphery of the opening of the polypropylene tray and sealed on the flange top surface under various sealing conditions by the heat seal method, and then the peel strength of the film cover material was measured. did. The sealing conditions were five conditions of temperatures of 130 ° C., 140 ° C., 150 ° C., 160 ° C., and 170 ° C., the pressure was 1 kg / cm 2 , and the time was 1 second. The adhesive strength between the biaxially stretched polyethylene terephthalate film layer / printed layer laminate film and the polyethylene terephthalate layer / inorganic oxide vapor deposition layer / protective coat layer laminate film is 1.5 N, and the polyethylene terephthalate layer / inorganic The adhesive strength between the oxide vapor deposited layer / protective coat layer laminated film and the easy peel film was 6N. As can be seen from the graph showing the relationship between the seal temperature and the peel strength in FIG. 5, the peel strength increases as the seal temperature increases. However, when the seal temperature is 130 to 170 ° C., it is 10 N or less. . None had delamination.
次に、実施例のイージーピール性トレー用フィルム蓋材と比較例のイージーピール性トレー用フィルム蓋材について、経時におけるシール温度と剥離強度との関係を調べた。シール条件は、温度が１３０℃、１５５℃、１７０℃の３条件で、圧力は１Ｋｇ／ｃｍ2 で、時間は１秒で、冷却条件は、ヒートシール後１秒以内に冷却バーを当てた。また、測定は、初期、１週間後、４週間後に行った。測定結果は、実施例のイージーピール性トレー用フィルム蓋材は、図３のグラフから分かるように、剥離強度は１０Ｎ以下であり、各温
度における剥離強度の上昇も約２Ｎに抑えられていた。一方、比較例のイージーピール性トレー用フィルム蓋材については、図４のグラフから分かるように、剥離強度が１０Ｎを大幅に越えるものもあり、各温度における剥離強度の上昇も４〜６Ｎであった。デラミネーションを発生したものがあった。
Next, the relationship between the sealing temperature and peel strength over time was examined for the easy-peel tray cover for the example and the easy-peel tray cover for the comparative example. The sealing conditions were three conditions of temperatures of 130 ° C., 155 ° C., and 170 ° C., the pressure was 1 kg / cm 2 , the time was 1 second, and the cooling condition was that the cooling bar was applied within 1 second after heat sealing. The measurement was performed initially, after 1 week and after 4 weeks. As can be seen from the graph of FIG. 3, the peel strength of the easy-peelable tray film cover material of the example was 10 N or less, and the increase in peel strength at each temperature was suppressed to about 2 N. On the other hand, as can be seen from the graph of FIG. 4, some of the film covers for the easy peel tray of the comparative example have a peel strength significantly exceeding 10 N, and the increase in peel strength at each temperature was 4 to 6 N. It was. Some had delamination.
１００，２００……イージーピール性トレー用フィルム蓋材
１１０，２１０……表面層
１１１……二軸延伸ポリプロピレンフィルム層
１１２，２１４……印刷層
１２０，１４０，２４０……ドライラミネーション用接着剤層
１３０……中間層
１３１，２１１……ポリエチレンテレフタレートフィルム層
１３２，２１２……無機酸化物蒸着層
１３３，２１３……保護コート層
１５０，２５０……イージーピールフィルム層
２２０……押出しラミネーション用ＡＣ剤層
２３０……中間層，ポリエチレンフィルム層
100, 200... Easy-
Claims (4)