JP2006110760A - Seal rubber cover for tire molding drum - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a seal rubber cover for a tire molding drum excellent in mold releasability, lubricity and airtightness and capable of keeping these properties over a long period of time. <P>SOLUTION: The seal rubber cover 1 for the tire molding drum, which is mounted on the recessed part 9 formed to the surface of the drum segment 3 of the expansible and contractible molding drum 2 to fix a tire bead part 7, is integrally formed into a ring shape from a silicone rubber and the breaking strength of the silicone rubber at a room temperature is set to 6.0-10.0 MPa and the tear strength thereof is set to 20-40 N/mm. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

  The present invention relates to a seal rubber cover for a tire molding drum, and more particularly to a seal rubber cover for a tire molding drum that is excellent in releasability, lubricity and airtightness and can maintain its performance for a long period of time.

  Conventionally, as shown in FIG. 3, a tire molding drum 2 used in a two-stage molding machine for a radial tire has a recess for fitting and engaging the bead portion 7 of the green tire 8 with the surface of the drum segment 3. 9 is provided, and the seal rubber cover 1 is mounted so as to cover the recess 9. For example, the drum segment 3 can be expanded and contracted via a link mechanism 6 when the piston rod 5 of the cylinder 4 expands and contracts. When an internal pressure is applied to inflate the green tire 8, the sealing rubber cover 1 maintains the airtightness.

  Since this seal rubber cover 1 is made of natural rubber, butadiene rubber or the like, it has excellent adhesion to the unvulcanized rubber of the bead portion 7 and good airtightness, but it is difficult to release. When removing the bead part 7 from the drum segment 3, there is a problem that the bead part 7 comes off while being closely attached to the bead part 7.

  For this reason, it has been difficult to achieve close contact by frequently applying a release agent such as zinc stearate to the portion in contact with the bead portion 7 or removing the rubber layer to expose the bare cord.

  However, these methods cannot maintain the releasability for a long time. Also, the number of man-hours for applying the release agent and the quality deterioration due to the adhesion of the release agent to unnecessary parts, the cost increase due to the addition of the code layer There was a problem.

  In the seal rubber cover of FIG. 3, in order to improve the quality by increasing the cushioning property of the part in contact with the bead part 7 and smoothing the movement of the bead part 7 to prevent deformation and cracking, the bead part of the seal rubber cover 1 is improved. It has been proposed that the back side of the seal rubber cover that comes into contact with the base portion 7 is an elastic rubber layer having a predetermined thickness (see Patent Document 1).

Even in this proposal, when natural rubber, butadiene rubber, or the like is used as the material of the seal rubber cover, sufficient releasability and lubricity may not be secured, and further improvement has been demanded.
JP-A-9-123304

  An object of the present invention is to provide a seal rubber cover for a tire molding drum that is excellent in releasability and airtightness and can maintain its performance for a long period of time.

  In order to achieve the above object, a seal rubber cover for a tire molding drum according to the present invention is a seal rubber cover for a tire molding drum that is attached to a recess formed on the surface of a drum segment of a mold drum that can be expanded and contracted to fix a tire bead portion. The seal rubber cover is formed by integrating silicone rubber into a ring shape, and the silicone rubber has a breaking strength at room temperature of 6.0 to 10.0 MPa and a tearing force of 20 to 40 N / mm. is there.

    According to the seal rubber cover for a tire molding drum of the present invention, in the seal rubber cover for a tire molding drum that is attached to a recess formed on the surface of the drum segment of the expandable / contractible molding drum and fixes the tire bead portion, the seal rubber cover is made of silicone. Since it is integrally formed in a ring shape with rubber, an appropriate releasability and lubricity can be imparted to the contact portion with the bead portion, and airtightness can be maintained.

  In addition, since the breaking strength at room temperature of the silicone rubber is 6.0 to 10.0 MPa and the tearing force is 20 to 40 N / mm, even if the bead portion slides on the seal rubber cover, it is not easily worn or damaged. It has excellent durability and can maintain the above effects for a long time.

  As a result, problems such as deterioration in quality due to degradation in quality due to adhesion of the release agent to unnecessary parts, increase in cost due to addition of a cord layer, deformation of the bead due to poor lubrication, etc. Can be avoided.

  Hereinafter, a seal rubber cover for a tire molding drum of the present invention will be described based on the embodiments shown in the drawings. FIG. 1 is a partially cutaway perspective view showing an overall outline of an embodiment of a seal rubber cover 1 for a tire forming drum of the present invention. The seal rubber cover 1 is integrally formed in a ring shape with silicone rubber and has a substantially uniform thickness.

  The seal rubber cover 1 is attached so that the concave portion 1a is fitted to the concave portion 9 of the drum segment of the tire molding drum 2 in a state where the ring is stretched so as to be large, and the state shown in FIG. The drum segment 3 is tightly fixed by force.

  It is preferable to use silicone rubber having an elongation at break of 300% or more for the seal rubber cover 1 because it can be easily attached to the drum segment 3. If the elongation at break is less than 300%, it will be difficult to stretch as the ring is expanded, and it will be difficult to wear, but if it is about 200%, it can be worn, so the elongation at break is the other performance and cost etc. Determine in consideration of

  In addition, since about 200% elongation occurs at the time of mounting, mounting becomes easy if the 200% modulus is lowered. For example, the 200% modulus is preferably in the range of 4.0 MPa to 6.5 MPa.

  For example, the drum segment 3 can be expanded and contracted via the link mechanism 6 when the piston rod 5 of the cylinder 4 expands and contracts. When the belt layer or the tread rubber is pasted and molded, air pressure is applied to the inside of the green tire 8, and the seal rubber cover 1 maintains the airtightness and the green tire 8 is inflated. Slides in the recess 1a of the seal rubber cover so as to rotate.

  The seal rubber cover has appropriate airtightness by using silicone rubber. However, when silicone rubber having a JIS-A hardness of 56 degrees or more and 63 degrees or less is used, a portion in contact with the bead portion 7 becomes a bead portion 7. It is possible to maintain durability while maintaining good airtightness by being deformed along. If the hardness is less than 56 degrees, it is likely to be deformed too much, and the durability may be adversely affected. If the hardness is more than 63 degrees, it is difficult to deform and it is difficult to follow the shape of the bead portion 7 and the airtightness is lowered.

  Usually, the width W of the concave portion 1a of the seal rubber cover is a dimension adapted to a tire having a wide bead portion 7 in order to be compatible with a plurality of tires having different specifications. In the case of molding, the movement of the bead portion 7 in the concave portion 1a of the seal rubber cover becomes larger, and wear and chipping are likely to occur due to sliding.

  However, since this sealing rubber cover 1 uses silicone rubber, the breaking strength at room temperature is 6.0 to 10.0 MPa and the tearing force is 20 to 40 N / mm. It is not easily damaged and has excellent durability. When the green tire 8 is inflated, the bead portion 7 smoothly rotates and slides in the recess 1a of the seal rubber cover for a long period of time. Can be prevented. Here, room temperature is approximately in the range of 10 to 40 ° C.

  The higher the breaking strength is, the more the durability can be improved. However, since it is difficult to obtain and the cost is increased, the range of 6.0 MPa or more and 10.0 MPa or less is preferable in consideration of these. However, if the silicone rubber exceeds 8.5 MPa, it becomes a special specification, which is difficult to obtain and increases the cost. Therefore, as a general-purpose specification, the breaking strength is set to 6.0 MPa or more and 8.5 MPa or less, and the cost of durability is minimized. Costs can be reduced.

  The larger the tearing force, the more the durability can be improved. However, since it is difficult to obtain and the cost is increased, the range of 20 N / mm or more and 40 N / mm or less is preferable in consideration of these. However, if the silicone rubber exceeds 35 N / mm, it will be a special specification, so it will be difficult to obtain and the cost will be high. As a general-purpose specification, it will be 20 N / mm or more and 35 N / mm or less, reducing the durability and minimizing the cost reduction. You can also

  After the green tire 8 is inflated and a belt layer, a tread and the like are pasted and molded, the bead portion 7 is removed from the drum segment 3. However, since the seal rubber cover 1 is made of silicone rubber, it is excellent in releasability. It does not come out of contact with the bead portion 7 from the drum segment 3. There is no need for special man-hours such as application of a release agent as in the prior art or measures such as providing a cord layer to reduce the contact area with the bead portion.

  Moreover, since it is excellent in durability as described above, it is possible to maintain good releasability, lubricity and airtightness over a long period of time.

  As shown in Table 1, a ring-shaped seal rubber cover is integrally manufactured by three types of silicone rubbers having different physical properties (Examples 1 to 3), and a conventional rubber rubber blended rubber blend as a comparative example. One type of seal rubber cover was manufactured, and these were attached to the drum segment of the same type of tire molding drum, and a tire was molded under the same conditions. The shape of the seal rubber cover is the same. Evaluation items are wearability, releasability, and durability.

  The silicone rubber of Example 1 is made of Shin-Etsu Chemical Co., Ltd., product number KE9611U, and the silica used as a filler is wet silica. The silicone rubber of Example 3 is a product number X30-3575U manufactured by the same company, and the silica used as a filler is dry silica.

  Only in the seal rubber cover of the comparative example, the cord layer is arranged in the radial direction at the portion that comes into contact with the bead portion so that the bare cord is exposed to make it difficult to adhere, and the zinc stearate at the portion that comes into contact with the bead portion at the time of tire molding (Release agent) was applied.

  The breaking strength in Table 1 is based on a test using a No. 3 test piece in accordance with JIS K 6251, and the elongation at break is shown in the table as the breaking elongation. The tear strength was tested using a B-type test piece according to JIS K 6252, and the hardness was tested according to JIS K 6253. 200% M in Table 1 indicates a 200% modulus, and is based on a test based on JIS K 6251.

[Removability]
The ease with which the seal rubber cover was attached to the drum segment was relatively evaluated by an operator based on a comparative example. A case where the wearability of the comparative example is better is shown as ○, and a case where the wearability is better than this is shown as ◎.

[Releasability]
The ease of mold release when removing the bead portion from the drum segment was relatively evaluated by an operator based on a comparative example. In the comparative example, the releasability is indicated by ○, and the case where the releasability is better than this is indicated by ◎.

[durability]
Each seal rubber cover was used approximately 500 times a day for molding a tire under the same conditions, and the number of days that can be used without any trouble was shown.

From this result, it was confirmed that the seal rubber cover of the present invention had a release property superior to that of the comparative example and the durability was equal to or higher than that of the comparative example without using a release agent. In addition, it was confirmed that the wearability was improved by setting the elongation at break to a numerically limited range.
In addition, about airtightness, there was no problem about all the sealing rubber covers of Examples 1-3 and a comparative example.

1 is a partially cutaway perspective view showing an overall outline of a seal rubber cover for a tire molding drum of the present invention. It is a longitudinal cross-sectional view which shows the state which has mounted | worn the seal rubber cover of this invention to the drum segment of the tire shaping | molding drum, and fixed the bead part of the green tire. It is a longitudinal cross-sectional view which shows the state which attached the seal rubber cover for conventional tire forming drums to the drum segment of a tire forming drum, and fixed the bead part of the green tire.

Explanation of symbols

1 Seal rubber cover
1a Concave part of seal rubber cover 2 Tire molding drum 3 Drum segment 4 Cylinder 5 Piston rod 6 Link mechanism 7 Bead part
7a Base part of bead part 8 Green tire 9 Recessed part of drum segment

Claims (3)

  In a seal rubber cover for a tire molding drum that is mounted in a recess formed on the surface of a drum segment of an expandable / contractible molding drum and fixes a tire bead portion, the seal rubber cover is integrally formed in a ring shape with silicone rubber, A seal rubber cover for a tire molding drum, wherein the silicone rubber has a breaking strength at room temperature of 6.0 to 10.0 MPa and a tearing force of 20 to 40 N / mm.   The tire rubber drum sealing rubber cover according to claim 1, wherein the silicone rubber has a JIS-A hardness of 56 to 63 degrees.   The seal rubber cover for a tire molding drum according to claim 1 or 2, wherein the elongation at break of the silicone rubber is 300% or more.