JP2006062262A - Inkjet recording sheet - Google Patents

Inkjet recording sheet Download PDF

Info

Publication number
JP2006062262A
JP2006062262A JP2004249144A JP2004249144A JP2006062262A JP 2006062262 A JP2006062262 A JP 2006062262A JP 2004249144 A JP2004249144 A JP 2004249144A JP 2004249144 A JP2004249144 A JP 2004249144A JP 2006062262 A JP2006062262 A JP 2006062262A
Authority
JP
Japan
Prior art keywords
coating agent
recording sheet
ink jet
jet recording
based coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2004249144A
Other languages
Japanese (ja)
Other versions
JP4334443B2 (en
Inventor
Kenichi Sakai
健一 坂井
Yoshihiko Ota
好彦 太田
Fujiyoshi Watanabe
藤義 渡辺
Takashi Hosogai
隆 細貝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hokuetsu Paper Mills Ltd
Original Assignee
Hokuetsu Paper Mills Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hokuetsu Paper Mills Ltd filed Critical Hokuetsu Paper Mills Ltd
Priority to JP2004249144A priority Critical patent/JP4334443B2/en
Publication of JP2006062262A publication Critical patent/JP2006062262A/en
Application granted granted Critical
Publication of JP4334443B2 publication Critical patent/JP4334443B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide an inkjet recording sheet, which has high transparency, is excellent in the image clarity of full color recording, has quick ink drying properties and the small bleeding of an image and can realize a stable operation with neither wrinkle nor recession and further which is excellent in the water resistance of a recording part in an ink jet recording system by an aqueous ink. <P>SOLUTION: In the inkjet recording sheet, in which at least one layered coated layer is provided on at least one side of a highly transparent sheet-like support, a first coated layer, which is just above the support, is a solvent-based coating agent and a second coated layer, which is the outermost layer, is a water based coating agent mainly made of an aqueous urethane resin and a white inorganic pigment and, in addition, includes a cationic polymeric compound under the condition that the white inorganic pigment is a silica having an average particle diameter of 3.0-15.0 μm and the solid content ratio between the aqueous urethane resin and the resin in the water based coating agent is set to be 3.5:1-1:3.5 in order to solve the troubles of this inkjet recording sheet. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

本発明は、インクジェットプリンターやプロッターに使用される記録シートに関するものであり、透明性が高く、とくにＣＡＤ用第二原図用紙として、また、ファンシー用途としてフルカラー出力に適したインクジェット記録シートを提供することに関するものである。   The present invention relates to a recording sheet used for an ink jet printer or a plotter, and provides an ink jet recording sheet having high transparency and particularly suitable for full color output as a second original drawing paper for CAD and fancy use. It is about.

インクジェット記録方式は騒音が少なく、現像や定着等のプロセスを必要とせず、且つ容易にフルカラー記録が行える各種プリンターに利用され、近年急速に普及してきている。   Inkjet recording systems are used in various printers that are low in noise, do not require processes such as development and fixing, and can easily perform full-color recording, and have been rapidly spreading in recent years.

設計製図の分野においては、従来の手書きによる図面の作成からＣＡＤシステムが普及してきた。このＣＡＤシステムの出力機器としてプロッター（プリンタープロッター）の使用が増大している。このプロッターについて記録方式で分類するとペンプロッター、静電プロッター、感熱プロッター、インクジェットプロッターに大別できる。この記録方式の中でもフルカラー化が容易であること、装置の保守が容易であり、なおかつ駆動音及び記録音の発生が非常に低いという利点によりインクジェットプロッターによる記録方式が注目されている。   In the field of design and drafting, CAD systems have become widespread from the creation of drawings by conventional handwriting. The use of a plotter (printer plotter) as an output device of this CAD system is increasing. These plotters can be roughly classified into pen plotters, electrostatic plotters, thermal plotters, and ink jet plotters. Among these recording methods, a recording method using an ink jet plotter has attracted attention because of the advantages that full colorization is easy, the maintenance of the apparatus is easy, and the generation of driving sound and recording sound is very low.

また、クリスマスカード、バースデーカード、各種招待状等のグリーティングカードやペーパークラフト用紙といったいわゆるファンシーペーパーは、従来、予めオフセット印刷等で図柄の印刷を施したカード用紙やペーパークラフト用紙に筆記にてメッセージや模様を直接記入するものが多かった。しかし、近年のパーソナルコンピューター、デジタルカメラ、インクジェットプリンターの急速且つ広範囲な普及により一般家庭でも手軽に写真画像、グラフィックデザイン画像、またはイラスト等をパーソナルコンピューターで独自の処理を行いインクジェットプリンターで印字出力することによってプロ並のメッセージカードやペーパークラフトを手軽に製作することが可能となった。これにより、従来は予めオフセット印刷等を施したいわゆる既製品が使用されていたグリーティングカード等においても、自作による楽しさまたはオリジナリティーを出すため、オフセット印刷等の処理を施していない白紙のカード用紙やペーパークラフト用紙にインクジェットプリンターで写真や模様といった画像を印字し、その上でコメントを自筆するか、または更にコメントをもインクジェットプリンターにて印字するといった場合が増えてきている。   Also, so-called fancy paper such as Christmas cards, birthday cards, greeting cards for various invitations, and paper craft paper, traditionally printed messages and patterns on card paper and paper craft paper that have been printed in advance by offset printing etc. There were many things to fill in directly. However, with the rapid and widespread use of personal computers, digital cameras, and inkjet printers in recent years, photographic images, graphic design images, or illustrations can be easily processed by personal computers and printed out by inkjet printers even in ordinary households. Makes it easy to produce professional message cards and paper craft. As a result, even in greeting cards that have been used so-called off-the-shelf products that have been previously offset printed in advance, blank card paper that has not been subjected to processing such as offset printing or the like to produce fun or originality by yourself Increasingly, an image such as a photograph or a pattern is printed on paper craft paper with an ink jet printer, and a comment is written on the paper, or a comment is further printed with an ink jet printer.

更に最近では、インクジェット記録方式の高速化・高精細化あるいはフルカラー化などの要求による、インクジェット記録装置の性能向上や用途拡大に伴い、インクジェット記録シートに対してもより高度な特性が求められている。   More recently, with the demand for higher speed, higher definition, or full color of the ink jet recording system, the ink jet recording sheet is required to have higher characteristics as the performance of the ink jet recording apparatus is improved and the applications are expanded. .

まず、インクジェット記録シートとしては、画像の印字濃度が高く色調が明るく鮮明であること、インクの吸収が早く印字画像の重なった場合においてもインクが流れ出したり滲んだりしないこと、印字ドットの縦方向や横方向への拡散が必要以上に大きくなく且つ周辺が滑らかでぼやけがないことなど、画像鮮明性に優れていること。その他にも記録後の寸法変化が少なく、カール、波打ち（コックリング）、変形がないこと等が要求される。   First, as an ink jet recording sheet, the image has a high print density and color tone is bright and clear, the ink absorbs quickly and the print image overlaps, and the ink does not flow or bleed. Excellent image clarity such as lateral diffusion is not larger than necessary and the periphery is smooth and free from blur. In addition, there is little change in dimensions after recording, and curling, waving (cockling), no deformation, etc. are required.

また、保存性に関していえば、高湿度条件下などや、印字画像部が水に浸された場合にもインクが流れ出さないように、印字画像の耐水性に優れていることが要求される。   In terms of storability, the printed image is required to have excellent water resistance so that the ink does not flow out even under high humidity conditions or when the printed image portion is immersed in water.

画像のことに関して言えば、インクジェット記録方式でカラー画像を出力する場合、単色のシアン、マゼンタ、イエロー、ブラックの基本４色と、最近ではライトシアン、ライトマゼンタ、ダークイエローの中間色を含む計７色による多階調画像ドットを面順次方式により重ね印字することによって、混色であるレッド、グリーン、ブルー及びその他多数の中間色相と濃度の画像を形成し、天然色銀塩写真に近い画像を形成することができる。   In terms of images, when a color image is output by the ink jet recording method, a total of seven colors including the basic four colors of single color cyan, magenta, yellow, and black, and recently, intermediate colors of light cyan, light magenta, and dark yellow are used. By overprinting multi-tone image dots using the surface sequential method, images of mixed colors such as red, green, blue and many other intermediate hues and densities are formed, and an image close to a natural color silver salt photograph is formed. Can do.

インクジェット記録シートとしては、基本的には上質紙等の普通紙でも記録可能である。しかし、普通紙と呼ばれるインクジェット記録におけるインク受理層を設けていない一般的なカード用紙やペーパークラフト用紙等ではインクジェット記録適性がないため、鮮明且つ見る人を引きつけるような印字画像を得ることはできない。また一般的なこれらの用紙はインクジェット記録におけるインク吸収性が低いため、印字後にインクを乾燥させるため長い乾燥時間を必要とする。無論、設計製図用の高画質な図面用途としても普通紙では不十分であり、高画質であり画像鮮明性に優れているインクジェット記録シートを得るにはシートの表面に塗被層を設け、顔料、バインダー等を最適化したコート紙タイプのインクジェット記録シートが適している。   As the ink jet recording sheet, basically, recording can be performed on plain paper such as high-quality paper. However, general card paper or paper craft paper, which is not provided with an ink receiving layer in ink jet recording called plain paper, is not suitable for ink jet recording, so that a clear and attractive printed image cannot be obtained. In addition, these general papers have low ink absorbability in ink jet recording, and thus require a long drying time to dry the ink after printing. Of course, plain paper is not sufficient for high-quality drawing applications for design and drafting. To obtain an inkjet recording sheet with high image quality and excellent image sharpness, a coating layer is provided on the surface of the sheet, and pigment is used. In addition, a coated paper type ink jet recording sheet with an optimized binder and the like is suitable.

前述したＣＡＤ用第二原図用紙としては、ジアゾコピー用の第二原図である場合や、あるいは内容をチェックする必要のある設計図面やプログラムリストである場合は、記録シートは透明性が高くなければならない。またファンシーペーパー用途としても、招待状等のグリーティングカードやペーパークラフト用紙についても、人目を引きオリジナリティーの高いものとして透明性の高い基材の需要が大きくなってきている。ＣＡＤ用第二原図用紙とファンシーペーパーという全く用途の異なる分野であるが、高透明性が必要であり、インクジェット記録において高画質であり画像鮮明性に優れているものが望まれているという点で要求品質が一致している。   If the above-mentioned second original drawing sheet for CAD is a second original drawing for diazo copy, or a design drawing or program list whose contents need to be checked, the recording sheet must be not highly transparent. Don't be. For fancy paper applications, greeting cards such as invitations and paper craft paper are also attracting attention, and demand for highly transparent base materials is increasing as they are highly eye-catching. Although the second original drawing paper for CAD and fancy paper are completely different fields of use, high transparency is required, and high quality and excellent image sharpness are desired in inkjet recording. The required quality matches.

高透明でありインクジェット記録適性があるということが望まれているが、ＣＡＤ用第二原図用紙とファンシーペーパーとして元来必須とされている下記の品質特性を満足していなければならない。
・ 鉛筆による筆記性及び再筆記性。
・ 消しゴム等による消去性。
・ 朱肉、スタンプ等の捺印性。
・ 引張り、引裂き等の機械的強度。
・ 水、熱、湿、光、ガス等に耐え得る長期保存性。
・ 折り曲げ、折りたたみ性。 Although it is desired to be highly transparent and suitable for ink jet recording, it must satisfy the following quality characteristics that are originally essential for CAD second original drawing paper and fancy paper.
・ Pencil writing and rewriting.
・ Erasability with an eraser.
・ Sealing properties such as vermilion and stamps.
・ Mechanical strength such as pulling and tearing.
-Long-term storage that can withstand water, heat, humidity, light, gas, etc.
-Bending and folding.

ＣＡＤ用第二原図用紙及び透明ファンシーペーパーを得るための透明基材としては従来から、
・ ポリエチレンテレフタレートなどのプラスチックフイルム
・ トレーシングペーパー
・ 合成パルプ混抄紙
・ 油類、可塑剤などを含浸した透明化紙
など種々のものが試みられているがいずれも次のような欠点を有している。 As a transparent base material for obtaining the second original drawing paper for CAD and transparent fancy paper, conventionally,
・ Various types of plastic film such as polyethylene terephthalate ・ Tracing paper ・ Synthetic pulp mixed paper ・ Transparent paper impregnated with oils, plasticizers, etc. have all been tried. Yes.

フィルムベースのインクジェット記録用マットフィルムとしてＣＡＤ用途にも使用され、第二原図適性を兼ね備えたものの例が開示されている（例えば特許文献１参照）。このものは透明性、寸法安定性及び機械的強度には優れているが、折りたたみ性やコスト的に高価になってしまうという難点がある。トレーシングペーパーは折りたたみ性やコストについては問題ないが、寸法安定性、引裂き強度及び耐水性が劣り、特に水系塗工剤を塗工する際には基紙への水分吸収によるボコツキやシワの発生が著しく問題となる。一方、合成パルプ混抄紙は一般に木材パルプと合成パルプとの親和性の悪さに由来する地合ムラや透明度のムラが大きいほか、透明度そのものが低いという欠点がある。また油類、可塑剤等を透明化剤として紙中に含浸した透明化紙では、長期保存中に透明化剤が他へマイグレートし、巻き取りのブロッキングや画像の滲みを生じ、機械的強度も低下するという問題が発生する。また、イソシアネート等の反応性樹脂を含浸させて透明化基材を得るという例も開示されている（例えば特許文献２参照）。しかし、イソシアネート等の反応性樹脂を用いる場合、その反応の度合いを調整することが難しく反応が不完全なまま製品化された場合、経時で反応性樹脂の未反応部分の反応が進み、ボコツキやシワが発生するという可能性がある。   An example of a film-based inkjet recording mat film that is also used for CAD and has the second original drawing suitability is disclosed (for example, see Patent Document 1). This is excellent in transparency, dimensional stability and mechanical strength, but has a drawback that it is expensive in terms of folding property and cost. Tracing paper has no problems in terms of folding and cost, but is inferior in dimensional stability, tear strength, and water resistance, especially when water-based coating agents are applied, it causes unevenness and wrinkles due to moisture absorption in the base paper. Is a significant problem. On the other hand, synthetic pulp-mixed paper generally has the disadvantages of not only large formation unevenness and transparency unevenness due to poor affinity between wood pulp and synthetic pulp, but also low transparency itself. In the case of clarified paper impregnated in paper with oils, plasticizers, etc. as a clarifier, the clarifier migrates to other during long-term storage, resulting in blocking of winding and image blurring, resulting in mechanical strength. The problem that also falls. Moreover, the example of impregnating reactive resins, such as isocyanate, and obtaining a transparent base material is also disclosed (for example, refer patent document 2). However, when a reactive resin such as isocyanate is used, it is difficult to adjust the degree of the reaction, and if the reaction is incomplete, the reaction of the unreacted part of the reactive resin progresses over time. There is a possibility of wrinkles.

上記透明基材の中でも、コストが高いということと元々の透明性が低いという点は、致命的な欠点である。トレーシングペーパーは原料であるパルプを高度に叩解処理しフィブリル化を十分に進め、十分な繊維内及び繊維間結合を持たせることでパルプ内、パルプ間の結合を上げ、固−気界面がなくなるようにし、高い透明性を保っている。原料がパルプであるためコスト的には有利である。しかし、前述したようにトレーシングペーパーは水系塗工剤を塗工する場合、基紙への水分吸収によるボコツキやシワが発生するという問題がある。このボコツキやシワは記録シートとしては重大な欠陥であり、商品としての価値を著しく低下させるものである。一般的にインクジェット記録シートのインク受理層としては白色顔料と水溶性高分子化合物等からなる水系塗工剤が塗工され乾燥することによって得られる場合が多い。しかし、トレーシングペーパーには前述したような問題があるため、直接、水系塗工剤を塗工し、インクジェット記録に適したインク受理層を設けることは出来ない。   Among the transparent substrates, the high cost and the low original transparency are fatal drawbacks. Tracing paper is a highly refined pulverization process of pulp, which is a raw material, and sufficiently promotes fibrillation. By providing sufficient interfiber and interfiber bonds, the bond between pulp and pulp is increased and the solid-gas interface is eliminated. And maintain high transparency. Since the raw material is pulp, it is advantageous in terms of cost. However, as described above, when the tracing paper is coated with an aqueous coating agent, there is a problem that unevenness and wrinkles due to moisture absorption to the base paper occur. Such irregularities and wrinkles are serious defects as a recording sheet and significantly reduce the value as a product. In general, the ink receiving layer of an ink jet recording sheet is often obtained by applying a water-based coating agent comprising a white pigment and a water-soluble polymer compound and drying it. However, since tracing paper has the above-mentioned problems, it is not possible to directly apply an aqueous coating agent and provide an ink receiving layer suitable for ink jet recording.

上記トレーシングペーパーの抱える問題を解決するために様々な開発がなされている（例えば特許文献３参照）。ここでは透明性を保ちながら、インク滲み、インクあふれのない優れたインクジェット適性を有するインクジェット記録用透明紙において、高度に叩解処理を施したパルプを用いて製造された透明紙（トレーシングペーパー）上に、シリカ及びビニルピロリドン重合体を主成分とした塗布液を塗布してなるインクジェット記録透明紙が開示されている。この場合、シリカ及びビニルピロリドン重合体が含まれる塗布液の溶媒が有機溶剤であることから、トレーシングペーパー上に塗布しインクジェット受理層とした場合においても、透明でありながらインクの滲み、あふれがなく、しかも、シワやボコツキの発生しないインクジェット記録透明紙が得られるとある。しかしながら、この場合、トレーシングペーパー上に直接、有機溶剤を溶媒としたシリカを含む塗布液を塗布するため、シリカについては有機溶剤への分散性が良い物に限定される。シリカの有機溶剤への分散性を良くするためには、シリカ表面を有機物処理し疎水性としたものを使用しなければならない。このシリカ自体が疎水性であるため、このシリカを含むインク受理層をトレーシングペーパー上に設けた場合、シワやボコツキは良好であるが水性インクの吸収性についてはインクの重ね合わせである重色部ではインク量が多くなるため十分とはいえず、水に分散する親水性のシリカを使用した水系塗工剤を塗布しインクジェット受理層とした場合と比較すると、インク滲みあふれの度合いが大きかった。また、該公報では、ビニルピロリドン重合体を使用しているが、該重合体は水またはアルコールに可溶な樹脂であり、該公報中の溶媒である有機溶剤をアルコールとした場合、インクジェット受理層中のバインダーとして使用することは出来る。しかし、ビニルピロリドン重合体のインク吸収性能は、ポリビニルアルコールやポリウレタンといった水性高分子化合物と比較すると劣り、インク滲みあふれの度合いが大きかった。また、該公報ではインクジェット記録シートとして重要なインクジェット記録部の耐水性能については全く考慮されていない。このようなインクジェット記録透明紙においても、記録部の耐水性能は必須である。   Various developments have been made to solve the problems of the tracing paper (see, for example, Patent Document 3). Here, on transparent paper (tracing paper) manufactured using highly beaten pulp for inkjet recording transparent paper that has excellent ink jet aptitude without ink bleeding and ink overflow while maintaining transparency In addition, there is disclosed an ink jet recording transparent paper obtained by applying a coating liquid mainly composed of silica and a vinylpyrrolidone polymer. In this case, since the solvent of the coating solution containing silica and the vinyl pyrrolidone polymer is an organic solvent, even when coated on a tracing paper and used as an inkjet receiving layer, the ink bleeds and overflows while being transparent. In addition, there is an ink jet recording transparent paper that is free from wrinkles and unevenness. However, in this case, since a coating liquid containing silica using an organic solvent as a solvent is directly applied on the tracing paper, the silica is limited to those having good dispersibility in the organic solvent. In order to improve the dispersibility of silica in an organic solvent, it is necessary to use a silica surface treated with an organic substance to make it hydrophobic. Since this silica itself is hydrophobic, when an ink receiving layer containing this silica is provided on the tracing paper, wrinkles and unevenness are good, but the absorbability of water-based ink is a heavy color that is a superposition of ink. The amount of ink spilled out was greater than the case where an ink-jet receiving layer was formed by applying a water-based coating agent using hydrophilic silica dispersed in water. . Further, in this publication, a vinylpyrrolidone polymer is used. However, the polymer is a resin that is soluble in water or alcohol. When the organic solvent that is the solvent in the publication is alcohol, the ink jet receiving layer is used. Can be used as a binder inside. However, the ink absorption performance of the vinyl pyrrolidone polymer was inferior to that of an aqueous polymer compound such as polyvinyl alcohol or polyurethane, and the degree of ink bleeding was large. Further, this publication does not consider water resistance performance of an ink jet recording part which is important as an ink jet recording sheet. Even in such an ink jet recording transparent paper, the water resistance of the recording part is essential.

これまで述べたように、インクジェット記録シートにおいて、高透明性とインクジェット記録における高記録性能を両立させることは極めて難しい。しかも、インクジェット記録における用途は拡大しているため、更に厳しい品質性能を要求されている。トレーシングペーパーとしての透明性を損ねることなく、親水性シリカ及び水性高分子化合物を使用した水系塗工剤によって設けられたインクジェット受理層のようにインク量が多い場合でも十分なインク吸収性能を有し、しかもシワやボコツキがない、更にはインクジェット記録部の耐水性能も兼ね備えるといったインクジェット記録シートの開発が望まれていた。トレーシングペーパーを支持体とし、溶剤系塗工剤にてシワやボコツキを抑え、その上に水系塗工剤にてインクジェット適性を持たせるという例も開示されている（特許文献４参照）。しかし、この場合、水系塗工剤層中にカチオンポリマーを含有しないため、インクジェット記録シートの特性として不可欠である記録部の耐水性能がない。そのため、水にさらされた場合に記録部が流れ出し元の記録画像をとどめておくことができない。また、水系塗工剤中に含まれる樹脂がポリビニルアルコールとアクリル樹脂からなり、固形分比が９：１〜８：２とあるが、このようにポリビニルアルコールの比率が多いと、記録部の冴えは良いがインク乾燥性が悪く、被膜自体の耐水性も悪くなってしまう。   As described above, it is extremely difficult to achieve both high transparency and high recording performance in ink jet recording in the ink jet recording sheet. In addition, since applications in inkjet recording are expanding, more stringent quality performance is required. Without sacrificing transparency as a tracing paper, it has sufficient ink absorption performance even when the amount of ink is large, such as an ink-jet receiving layer provided by an aqueous coating agent using hydrophilic silica and an aqueous polymer compound. In addition, there has been a demand for the development of an ink jet recording sheet that is free from wrinkles and irregularities and also has the water resistance of the ink jet recording portion. An example is also disclosed in which a tracing paper is used as a support, wrinkles and unevenness are suppressed with a solvent-based coating agent, and ink-jet suitability is imparted thereon with a water-based coating agent (see Patent Document 4). However, in this case, since the water-based coating agent layer does not contain a cationic polymer, there is no water resistance performance of the recording portion, which is indispensable as a characteristic of the ink jet recording sheet. Therefore, when exposed to water, the recording unit cannot flow out and keep the original recorded image. Further, the resin contained in the water-based coating agent is made of polyvinyl alcohol and acrylic resin, and the solid content ratio is 9: 1 to 8: 2. Is good, but ink drying properties are poor, and the water resistance of the coating itself is also poor.

特開平６−７２０１５号公報JP-A-6-72015 特開平５−２４６１３０号公報JP-A-5-246130 特開２０００−３３５１０１号公報JP 2000-335101 A 特開平９−２６７５５０号公報JP-A-9-267550

本発明の目的は、水性インクによるインクジェット記録方式のプリンター及びプロッターを用いて記録されるインクジェット記録シートにおいて、透明性が高く、フルカラー記録による画像鮮明性に優れ、インク乾燥性が速く、画像の滲みが少なく、シワやボコツキの発生がない安定操業が可能であり、さらにはインクジェット記録部の耐水性にも優れたインクジェット記録シートを提供することにあり、ＣＡＤ用第二原図用紙及びファンシー用透明紙としての両特性を兼ね備えたインクジェット記録シートを提供することにある。   An object of the present invention is an ink jet recording sheet recorded using a printer and a plotter of an ink jet recording system using water-based ink, and has high transparency, excellent image clarity by full color recording, fast ink drying, and image bleeding. In order to provide an ink jet recording sheet that is less likely to cause wrinkles and unevenness, and is excellent in water resistance of the ink jet recording portion, it is intended to provide a second original drawing paper for CAD and a transparent paper for fancy. It is an object to provide an ink jet recording sheet having both characteristics as described above.

本発明者らは、前記の背景技術の問題点を改善するために鋭意研究した結果、透明性の高いシート状支持体、例えばトレーシングペーパーを用い、その少なくとも一方の面に少なくとも１層以上の層構成からなる塗被層を設けたインクジェット記録シートにおいて、該支持体直上層である第１の塗被層が溶剤系塗工剤であり、その塗工量が０．５〜１０ｇ／ｍ2であり、最表層である第２の塗被層が水系塗工剤であり、該水系塗工剤は水性ウレタン樹脂及び白色無機顔料を主体とし、更にはカチオン性高分子化合物を含むこと、該白色無機顔料がコールターカウンター法で測定される平均粒子径３．０〜１５．０μｍのシリカであり、該水系塗工剤に含まれる水性ウレタン樹脂とシリカの固形分比が３．５：１〜１：３．５であることを特徴とするインクジェット記録シートとすることにより、前記課題が解決されることを見出した。 As a result of diligent research to improve the problems of the background art, the present inventors have used a highly transparent sheet-like support, such as tracing paper, and at least one layer on at least one surface thereof. In an ink jet recording sheet provided with a coating layer having a layer structure, the first coating layer, which is a layer immediately above the support, is a solvent-based coating agent, and the coating amount is 0.5 to 10 g / m 2. The second coating layer as the outermost layer is an aqueous coating agent, the aqueous coating agent mainly comprises an aqueous urethane resin and a white inorganic pigment, and further contains a cationic polymer compound, The white inorganic pigment is silica having an average particle diameter of 3.0 to 15.0 μm as measured by a Coulter counter method, and the solid content ratio of the aqueous urethane resin and silica contained in the aqueous coating agent is 3.5: 1 to 1. It is characterized by being 1: 3.5 It has been found that the above-mentioned problems can be solved by using an inkjet recording sheet.

また、上記水系塗工剤に含まれる白色無機顔料がコールターカウンター法で測定される平均粒子径が３．０〜１０．０μｍのシリカであることが好ましく、該水系塗工剤に含まれる水性ウレタン樹脂とシリカの固形分比が３：１〜１：３であることが好ましい。また、カチオン性高分子化合物としては、ポリアミン系樹脂、ジメチルジアリルアンモニウムクロライド系樹脂、エピクロルヒドリン系樹脂、ジシアンジアミド系樹脂、アクリルアミドとジアリルアミン塩酸塩の共重合物の中から選ばれる少なくとも１種類を使用することが好ましい。また、上記溶剤系塗工剤が塩化ビニルと酢酸ビニルの共重合体、ポリ酢酸ビニルから選ばれる少なくとも１種類であり、その塗工量が１〜５ｇ／ｍ2であることが好ましい。以下、塗工量は特に断らない限り、乾燥後の塗工量を示す。更にＪＩＳ Ｐ ８１４９：２０００で測定した不透明度が２０．０％〜６０．０％であることが好ましく、上記溶剤系塗工剤による塗被層及び水系塗工剤による塗被層を支持体の両面に設けることが好ましい。しかも、透明性が高く、コスト的に有利なものとするには支持体としてトレーシングペーパーを使用することが好ましい。 The white inorganic pigment contained in the aqueous coating agent is preferably silica having an average particle size of 3.0 to 10.0 μm as measured by a Coulter counter method, and the aqueous urethane contained in the aqueous coating agent. The solid content ratio of the resin and silica is preferably 3: 1 to 1: 3. The cationic polymer compound should be at least one selected from polyamine resins, dimethyl diallyl ammonium chloride resins, epichlorohydrin resins, dicyandiamide resins, and copolymers of acrylamide and diallylamine hydrochloride. Is preferred. The solvent-based coating agent is at least one selected from a vinyl chloride / vinyl acetate copolymer and polyvinyl acetate, and the coating amount is preferably 1 to 5 g / m 2 . Hereinafter, unless otherwise indicated, the coating amount indicates the coating amount after drying. Further, the opacity measured in accordance with JIS P 8149: 2000 is preferably 20.0% to 60.0%, and the coating layer with the solvent-based coating agent and the coating layer with the aqueous coating agent are formed on the support. It is preferable to provide on both surfaces. Moreover, it is preferable to use tracing paper as a support in order to make it highly transparent and cost-effective.

上記の構成をとることによって、本発明のインクジェット記録シートは、水性インクによるインクジェット記録方式のプリンター及びプロッターを用いて記録されるインクジェット記録シートにおいて、透明性が高く、フルカラー記録による画像鮮明性に優れ、インク乾燥性が速く、画像の滲みが少なく、シワやボコツキの発生がない安定操業が可能であり、更にはインクジェット記録部の耐水性にも優れたものであり、ＣＡＤ用第二原図用紙として、また、ファンシー用透明紙としての両特性を兼ね備えている。
By taking the above configuration, the ink jet recording sheet of the present invention is highly transparent in an ink jet recording sheet recorded using an ink jet recording type printer and plotter using water-based ink, and has excellent image clarity by full color recording. Ink dryness is fast, image bleeding is small, stable operation without wrinkles and blurring is possible, and water resistance of the ink jet recording part is also excellent. Moreover, it has both characteristics as transparent paper for fancy.

本発明はシート状支持体として透明性の高いもの、例えばトレーシングペーパーを用い、該支持体上に少なくとも１層以上の層構成からなる塗被層を設けたインクジェット記録シートにおいて、該支持体直上層である第１の塗被層が、溶剤系塗工剤で塗工される。該第１の塗被層はトレーシングペーパー及び第２の塗被層との接着性が良好で、かつ吸水によるボコツキやシワが発生しないように耐水性を有するものでなくてはならない。第１の塗被層に使用する樹脂としては、有機溶剤への溶解性が良好であり造膜性が良好であるという点から塩化ビニルと酢酸ビニルの共重合体、ポリ酢酸ビニルから選択される少なくとも１種類を使用することが好ましい。第１の塗被層の塗工量としてはトレーシングペーパーと第２の塗被層の接着を確保でき、かつ塗工面の凹凸がない塗工量である０．５〜１０．０ｇ／ｍ2の範囲が有効であり、吸水によるボコツキやシワの発生を防ぐことの出来る耐水性能を得ることが出来る。更に好ましい最適塗工量は１〜５ｇ／ｍ2であり、特に好ましくは２〜４．５ｇ／ｍ２である。０．５ｇ／ｍ２未満の場合は十分な耐水性能が得られずボコツキやシワの発生が認められる。１０．０ｇ／ｍ２を超えた場合は塗工性に悪影響を及ぼし、コーターヘッド部での液ダレや塗工ムラの原因となるし、記録紙の鉛筆筆記性が悪い。しかも、１０．０ｇ／ｍ２を超えた場合はコスト的にも不利である。 The present invention relates to an inkjet recording sheet using a highly transparent sheet-like support, such as tracing paper, and having a coating layer comprising at least one layer structure on the support. The first coating layer, which is the upper layer, is applied with a solvent-based coating agent. The first coating layer must have good adhesion to the tracing paper and the second coating layer, and should have water resistance so that no blur or wrinkle due to water absorption occurs. The resin used for the first coating layer is selected from a copolymer of vinyl chloride and vinyl acetate and polyvinyl acetate from the viewpoints of good solubility in organic solvents and good film-forming properties. It is preferable to use at least one kind. The first coating as the coated amount of the layer can be secured adhesion of tracing paper and the second coating layer, and Ru coating amount der no unevenness of the coated surface 0.5~10.0g / m The range of 2 is effective, and it is possible to obtain water resistance that can prevent the occurrence of unevenness and wrinkles due to water absorption. A more preferable optimum coating amount is 1 to 5 g / m 2 , and particularly preferably 2 to 4.5 g / m 2 . If it is less than 0.5 g / m 2, sufficient water resistance cannot be obtained, and the occurrence of bumps and wrinkles is observed. If it exceeds 10.0 g / m 2 , the coating property will be adversely affected, which may cause dripping and uneven coating at the coater head, and the pencil writing property of the recording paper will be poor. Moreover, if it exceeds 10.0 g / m 2 , it is disadvantageous in terms of cost.

かくして、得られた第１の塗被層上に水性ウレタン樹脂及び白色無機顔料を含む水系塗工剤からなるインク受容層を塗布する。本発明ではＣＡＤ用第二原図用紙及び透明ファンシーペーパー用に使用されるという目的で、塗布乾燥後の透明性が高い水性樹脂が用いられ、水性アクリル樹脂、水性ウレタン樹脂、スチレンアクリル樹脂、ポリビニルアルコール等があげられる。その中でも水性インクによるインクジェット記録が行われた場合、インクの滲みやあふれが発生しない樹脂として、また、被膜の耐水性能が高いという面から考えて、水性ウレタン樹脂が最適である。また、インクの滲みやあふれについては水性ウレタン樹脂だけではインクの吸収性及び乾燥性という意味だけでとらえると不完全である。水性ウレタン樹脂によって得られた高透明性を維持しつつ、更にウレタン樹脂だけの場合よりもインク吸収性及び乾燥性を完全なものにするため、また、ＣＡＤ用第二原図用紙適性も付与させるという目的で平均粒子径（コールターカウンター法で測定）３．０〜１５．０μｍ、好ましくは３．０〜１０μｍの親水性シリカを用いる。他の白色無機顔料としては、クレー、炭酸カルシウム、水酸化アルミニウム、タルク、硫酸バリウム、酸化チタン等があげられる。しかし、これらの白色無機顔料はＣＡＤ用第二原図用紙適性として不可欠である鉛筆筆記性改良には効果はあるが、高い透明性及びインク吸収性を得ることは出来ない。シリカを使用する場合でも、平均粒子径が１５．０μｍを超えるシリカでは、鉛筆筆記時の摩耗度が大きく、さらにインクジェット記録適性においてもインク吸収性が悪化することとなる。平均粒子径が３．０μｍ未満のシリカを使用するとインク吸収性は向上するが透明性が低下することとなる。水性ウレタン樹脂及び平均粒子径３．０〜１５．０μｍのシリカを併用することで透明性を維持したままインクジェット適性をある程度満足するものは得られるが、ＣＡＤ用第二原図用紙及び透明ファンシーペーパーとしての鉛筆筆記性及び透明性を満足させるにはＪＩＳ Ｐ ８１４９：２０００における不透明度が２０％〜６０％の範囲内にあることが好ましい。この不透明度の範囲内においてインクジェット記録適性をも満足させるには、水性ウレタン樹脂とシリカの固形分比を３．５：１〜１：３．５、好ましくは３：１〜１：３の範囲内に収めることで達成できる。この比率範囲よりも水性ウレタン樹脂添加量が多い場合には不透明度が２０％未満となり、透明性は高いがベタツキ感が生じ鉛筆筆記がスムーズに行えず、筆記跡が残る等の問題が発生する。この比率範囲よりもシリカ添加量が多い場合には不透明度が６０％を超えてしまい、ＣＡＤ用第二原図用紙及び透明ファンシーペーパー用途として透明性が足りず、下の図や柄が十分に透けて確認できる状態ではなくなってしまう。   Thus, an ink receiving layer made of an aqueous coating agent containing an aqueous urethane resin and a white inorganic pigment is applied on the obtained first coating layer. In the present invention, a water-based resin having high transparency after coating and drying is used for the purpose of being used for CAD second original paper and transparent fancy paper, and water-based acrylic resin, water-based urethane resin, styrene-acrylic resin, polyvinyl alcohol Etc. Among these, when ink jet recording is performed with water-based ink, water-based urethane resin is most suitable as a resin that does not cause ink bleeding or overflow and from the viewpoint of high water resistance of the coating. Further, ink bleeding and overflow are incomplete when only water-based urethane resin is taken in terms of ink absorbability and drying properties. While maintaining the high transparency obtained by the water-based urethane resin, the ink absorption and drying properties are more complete than in the case of the urethane resin alone, and the second original drawing paper suitability for CAD is also given. For the purpose, hydrophilic silica having an average particle diameter (measured by Coulter counter method) of 3.0 to 15.0 μm, preferably 3.0 to 10 μm is used. Examples of other white inorganic pigments include clay, calcium carbonate, aluminum hydroxide, talc, barium sulfate, and titanium oxide. However, these white inorganic pigments are effective in improving the pencil writing property, which is indispensable as the suitability for the second original drawing paper for CAD, but high transparency and ink absorbability cannot be obtained. Even when silica is used, silica with an average particle diameter exceeding 15.0 μm has a high degree of wear during pencil writing, and further deteriorates ink absorbability in ink jet recording suitability. When silica having an average particle diameter of less than 3.0 μm is used, ink absorbability is improved, but transparency is lowered. By using a water-based urethane resin and silica having an average particle size of 3.0 to 15.0 μm in combination, it is possible to obtain an ink jet aptitude while maintaining transparency. However, as a second original drawing paper for CAD and a transparent fancy paper, In order to satisfy the pencil writability and transparency of JIS P 8149: 2000, the opacity is preferably in the range of 20% to 60%. In order to satisfy ink jet recording suitability within the range of opacity, the solid content ratio of the aqueous urethane resin and silica is in the range of 3.5: 1 to 1: 3.5, preferably 3: 1 to 1: 3. This can be achieved by keeping it inside. When the amount of the aqueous urethane resin added is larger than this ratio range, the opacity is less than 20%, and the transparency is high, but a sticky feeling is generated, and the pencil writing cannot be smoothly performed, and the writing mark remains. . If the amount of silica added is greater than this ratio range, the opacity will exceed 60%, and the transparency of the second original drawing paper for CAD and transparent fancy paper will be insufficient, and the figures and patterns below will be sufficiently transparent. Will not be in a state that can be confirmed.

また、記録部の耐水性もインクジェット記録シートとして欠かすことの出来ない品質要求項目である。記録用水性インク中の染料を定着させることを目的として、水系塗工剤中にカチオン性高分子化合物を含有させることで記録部の耐水性は達成できる。カチオン性高分子化合物としてインクジェット記録部の耐水性向上を目的に作られたものは数多くあるが、その中でどのような化合物を使用するかにノウハウがある。本発明ではカチオン性高分子化合物として、ポリアミン系樹脂、ジメチルジアリルアンモニウムクロライド系樹脂、エピクロルヒドリン系樹脂、ジシアンジアミド系樹脂、アクリルアミドとジアリルアミン塩酸塩の共重合物の中から一つ以上選ばれて使用されることが好ましい。透明性及びインクジェット記録適性を満足しつつ、記録部の耐水性についても良好な物を得るには上記のカチオン性高分子化合物の中から１つ以上選択されることが良い。カチオン性高分子化合物の使用量はシリカ１００重量部当たり１０〜１２０重量部が好ましい。カチオン性高分子化合物の量が１０重量部より少ないと記録部の耐水性が不十分となり、１２０重量部より多いとインクの吸収性が悪くなり、画像の滲みが悪化してしまう。   Further, the water resistance of the recording portion is a quality requirement item that is indispensable as an ink jet recording sheet. For the purpose of fixing the dye in the aqueous recording ink, the water resistance of the recording portion can be achieved by incorporating a cationic polymer compound in the aqueous coating agent. There are many cationic polymer compounds made for the purpose of improving the water resistance of the ink jet recording portion, and there is know-how on which compound to use. In the present invention, as the cationic polymer compound, one or more selected from polyamine resins, dimethyl diallylammonium chloride resins, epichlorohydrin resins, dicyandiamide resins, and copolymers of acrylamide and diallylamine hydrochloride are used. It is preferable. One or more of the above-mentioned cationic polymer compounds may be selected to obtain a recording part with satisfactory water resistance while satisfying transparency and ink jet recording suitability. The amount of the cationic polymer compound used is preferably 10 to 120 parts by weight per 100 parts by weight of silica. When the amount of the cationic polymer compound is less than 10 parts by weight, the water resistance of the recording part is insufficient, and when it is more than 120 parts by weight, the ink absorbability is deteriorated and the bleeding of the image is deteriorated.

これまでに述べた、溶剤系塗工剤による第１の塗被層及びその上に設けられる水系塗工剤による第２の塗被層が片面にのみ設けられる場合でもその効果は発揮されるが、もう一方の面に溶剤系塗工剤による塗被層を設けることで、更に防湿効果が得られボコツキやシワの発生しにくい平らで安定したインクジェット記録シートとなる。また更に両面に水系塗工剤によるインクジェット記録適性を有する塗被層を設けることで、どちらの面にも同じようにインクジェット記録が可能となり、透明性の高い支持体に特有の、どちらがインクジェット記録面かがわからなくなるという問題が発生しなくなる。 Far described, the second coating layer of the first coating layer and an aqueous coating agent provided thereon with a solvent-based coating agent is its effect even when provided only on one side is exhibited By providing a coating layer with a solvent-based coating agent on the other surface, a moisture-proof effect can be obtained, and a flat and stable ink jet recording sheet that is less likely to cause blurs and wrinkles can be obtained. Furthermore, by providing a coating layer having ink jet recording suitability with a water-based coating agent on both sides, it becomes possible to perform ink jet recording on both sides in the same way, which is specific to a highly transparent support, which is the ink jet recording side. The problem of not knowing will not occur.

本発明において、上記特徴を有する支持体直上層である第１の塗被層（溶剤系塗工剤）並びに、最表層である第２の塗被層（水系塗工剤）を設ける方法としては、オフマシンコーターが好ましく。例えば、従来公知のエアーナイフコーター、カーテンコーター、ダイコーター、ブレードコーター、バーコーター、ロッドコーター、ロールコーター、グラビアコーターなどの各種装置をオフマシンで用いることが出来る。塗工後の乾燥方法としてはエアードライヤー、ヤンキードライヤー、ドラムドライヤー等公知の乾燥設備が用いられる。また、キャレンダー処理については表面の平滑性が変化するため鉛筆筆記に影響を及ぼす。しかし、必要があればソフトキャレンダーによる処理を行ってもよい。   In the present invention, as a method of providing the first coating layer (solvent-based coating agent) which is a layer directly above the support having the above characteristics, and the second coating layer (water-based coating agent) which is the outermost layer. An off-machine coater is preferred. For example, various devices such as conventionally known air knife coaters, curtain coaters, die coaters, blade coaters, bar coaters, rod coaters, roll coaters, and gravure coaters can be used off-machine. As a drying method after coating, known drying equipment such as an air dryer, a Yankee dryer, or a drum dryer is used. Moreover, since the smoothness of a surface changes about a calendar process, it affects pencil writing. However, if necessary, processing by a soft calendar may be performed.

本発明によって得られたインクジェット記録シートの坪量としては４０ｇ／ｍ２〜２００ｇ／ｍ２が好ましく、更に、ＣＡＤ用第二原図用紙及び透明ファンシーペーパーの両方の特性を満たすには７０ｇ／ｍ２〜１８０ｇ／ｍ２の坪量が好ましい。 Preferably 40g / m 2 ~200g / m 2 as the basis weight of the ink jet recording sheet obtained by the present invention, further, to meet the characteristics of both the second originals paper and transparent fancy paper for CAD 70 g / m 2 A basis weight of ˜180 g / m 2 is preferred.

以下に実施例を挙げて、本発明を具体的に説明する。無論、本発明はこれらに限定されるものではない。また、例中の部は特に断らない限り、それぞれの重量部を示す。   The present invention will be specifically described below with reference to examples. Of course, the present invention is not limited to these. Moreover, unless otherwise indicated, the part in an example shows each weight part.

基材としてトレーシングペーパー（ＧＮＴ７５、アルジョウィギンズ社製）を使用し、このトレーシングペーパー上に下記に示す組成の塗工液を乾燥後の塗工量が、支持体（基材）直上層である溶剤系塗工剤からなる塗被層（以下、「アンカーコート層」という。）３．５ｇ／ｍ2、最表層である水系塗工剤からなる塗被層（以下、「トップコート層」という。）６．０ｇ／ｍ2となるようにバーコーター法により塗工する。塗工液は順次投入、撹拌して調成する。それぞれの塗工後の乾燥条件については、アンカーコート層が１２５℃で５０秒間で行い、トップコート層は１３０℃で１分間行うことでインクジェット記録シートを得た。この溶剤系塗工剤からなるアンカーコート層成分と、水系塗工剤からなるトップコート層成分について詳しく示す。
〔アンカーコート層成分〕
塩化ビニルと酢酸ビニルとの共重合体（ソルバインＡ、固形分濃度１００％：日信化学工業社製）７部、酢酸ビニル（ビニロールＳ、固形分濃度４７％：昭和高分子社製）３部、メチルエチルケトン３０部とトルエン７０部とした。
〔トップコート層成分〕
水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）２５部、カチオン性高分子化合物としてポリアミン系樹脂（ＤＫ−８５６、固形分濃度５０．０％：星光ＰＭＣ社製）２部、水１３部とし、水性ウレタン樹脂とシリカの固形分比が９：５とした。 Using tracing paper (GNT75, manufactured by Arjo Wiggins Co., Ltd.) as the base material, the coating amount after drying the coating liquid having the composition shown below on this tracing paper is the layer directly above the support (base material). 3.5 g / m 2 of a coating layer made of a solvent-based coating agent (hereinafter referred to as “anchor coat layer”), and a coating layer made of an aqueous coating agent that is the outermost layer (hereinafter referred to as “topcoat layer”) It is applied by a bar coater method so as to be 6.0 g / m 2 . The coating solution is sequentially added and stirred to prepare. About the drying conditions after each coating, the anchor coat layer was performed at 125 ° C. for 50 seconds, and the top coat layer was performed at 130 ° C. for 1 minute to obtain an ink jet recording sheet. An anchor coat layer component composed of this solvent-based coating agent and a top coat layer component composed of an aqueous coating agent will be described in detail.
[Anchor coat layer component]
7 parts of a copolymer of vinyl chloride and vinyl acetate (Solvine A, solid concentration 100%: manufactured by Nissin Chemical Industry Co., Ltd.), 3 parts of vinyl acetate (vinylol S, solid content concentration 47%: manufactured by Showa Polymer Co., Ltd.) 30 parts of methyl ethyl ketone and 70 parts of toluene.
[Topcoat layer component]
60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method measurement average particle size 3.3 μm: manufactured by Mizusawa Chemical Co., Ltd.) 20 parts dispersion) 25 parts, 2 parts of polyamine resin (DK-856, solid concentration 50.0%: made by Seiko PMC) as cationic polymer compound, 13 parts of water, solid urethane resin and silica The split ratio was 9: 5.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）３６部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）４５部、カチオン性高分子化合物としてポリアミン系樹脂（ＤＫ−８５６、固形分濃度５０．０％：星光ＰＭＣ社製）２部、水１７部とし、水性ウレタン樹脂とシリカの固形分比が３：５としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 36 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: Mizusawa Chemical Co., Ltd. 20% dispersion) 45 parts, cationic polymer compound polyamine resin (DK-856, solid content concentration 50.0%: Seiko PMC Co., Ltd.) 2 parts An ink jet recording sheet was obtained in the same manner as in Example 1 except that the water content was 17 parts and the solid content ratio of the aqueous urethane resin and silica was 3: 5.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）１５部、カチオン性高分子化合物としてポリアミン系樹脂（ＤＫ−８５６、固形分濃度５０．０％：星光ＰＭＣ社製）２部、水２３部とし、水性ウレタン樹脂とシリカの固形分比が３：１としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink and Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 15 parts of Mizusawa Chemical Industries 20% dispersion), 2 parts of polyamine resin (DK-856, solid concentration 50.0%: Seiko PMC) as the cationic polymer compound An ink jet recording sheet was obtained in the same manner as in Example 1 except that the water content was 23 parts and the solid content ratio of the aqueous urethane resin and silica was 3: 1.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）２６．６７部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）６０部、カチオン性高分子化合物としてポリアミン系樹脂（ＤＫ−８５６、固形分濃度５０．０％：星光ＰＭＣ社製）２部、水１１．３３部とし、水性ウレタン樹脂とシリカの固形分比が１：３としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 26.67 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter). Counter method measurement average particle size 3.3 μm: Mizusawa Chemical Co., Ltd. 20% dispersion) 60 parts, as a cationic polymer compound polyamine resin (DK-856, solid content concentration 50.0%: manufactured by Seiko PMC) An ink jet recording sheet was obtained in the same manner as in Example 1 except that the amount was 2 parts and water was 11.33 parts, and the solid content ratio of the aqueous urethane resin and silica was 1: 3.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）２５部、カチオン性高分子化合物としてジメチルジアリルアンモニュウムクロライド系樹脂（ＫＲ−８５０、固形分濃度２８．０％：荒川化学工業社製）３．５７部、水１１．４３部とし、水性ウレタン樹脂とシリカの固形分比が９：５としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink and Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 25 parts of a 20% dispersion manufactured by Mizusawa Chemical Co., Ltd., dimethyl diallyl ammonium chloride resin (KR-850, solid concentration 28.0%: Arakawa Chemical Industries, Ltd.) as a cationic polymer compound (Manufactured) An ink jet recording sheet was obtained in the same manner as in Example 1 except that 3.57 parts and 11.43 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 9: 5.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）３６部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）４５部、カチオン性高分子化合物としてジメチルジアリルアンモニウムクロライド系樹脂（ＫＲ−８５０、固形分濃度２８．０％：荒川化学工業社製）３．５７部、水１５．４３部とし、水性ウレタン樹脂とシリカの固形分比が３：５としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 36 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 45 parts of Mizusawa Chemical Co., Ltd. 20% dispersion), dimethyldiallylammonium chloride-based resin (KR-850, solid concentration 28.0%: Arakawa Chemical Industries, Ltd.) as the cationic polymer compound (Manufactured) An ink jet recording sheet was obtained in the same manner as in Example 1 except that 3.57 parts and 15.43 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 3: 5.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）１５部、カチオン性高分子化合物としてジメチルジアリルアンモニウムクロライド系樹脂（ＫＲ−８５０、固形分濃度２８．０％：荒川化学工業社製）３．５７部、水２１．４３部とし、水性ウレタン樹脂とシリカの固形分比が３：１としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink and Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 15 parts of Mizusawa Chemical Co., Ltd. 20% dispersion), dimethyl diallyl ammonium chloride resin (KR-850, solid concentration 28.0%: Arakawa Chemical Industries, Ltd.) as the cationic polymer compound (Manufactured) An ink jet recording sheet was obtained in the same manner as in Example 1 except that 3.57 parts and 21.43 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 3: 1.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）２６．６７部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）６０部、カチオン性高分子化合物としてジメチルジアリルアンモニウムクロライド系樹脂（ＫＲ−８５０、固形分濃度２８．０％：荒川化学工業社製）３．５７部、水９．７６部とし、水性ウレタン樹脂とシリカの固形分比が１：３としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 26.67 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter). Counter method measurement average particle size 3.3 μm: 60 parts of Mizusawa Chemical Co., Ltd. 20% dispersion), dimethyldiallylammonium chloride-based resin (KR-850, solid concentration 28.0%) as a cationic polymer compound: Arakawa Chemical An ink jet recording sheet was obtained in the same manner as in Example 1 except that 3.57 parts (manufactured by Kogyo Co., Ltd.) and 9.76 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 1: 3.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）２５部、カチオン性高分子化合物としてエピクロルヒドリン系樹脂（パピオゲンＰ−１０５、固形分濃度６０．０％：センカ社製）１．６７部、水１３．３３部とし、水性ウレタン樹脂とシリカの固形分比が９：５としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink and Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size: 3.3 μm: 25 parts of a 20% dispersion manufactured by Mizusawa Chemical Co., Ltd., epichlorohydrin-based resin as a cationic polymer compound (papiogen P-105, solid content concentration: 60.0%: manufactured by Senca) An ink jet recording sheet was obtained in the same manner as in Example 1 except that 67 parts and 13.33 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 9: 5.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）３６部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）４５部、カチオン性高分子化合物としてエピクロルヒドリン系樹脂（パピオゲンＰ−１０５、固形分濃度６０．０％：センカ社製）１．６７部、水１７．３３部とし、水性ウレタン樹脂とシリカの固形分比が３：５としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 36 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 45 parts by Mizusawa Chemical Co., Ltd. 20% dispersion), epichlorohydrin resin as a cationic polymer compound (papiogen P-105, solid content concentration 60.0%: manufactured by Senka) An ink jet recording sheet was obtained in the same manner as in Example 1 except that 67 parts and 17.33 parts of water were used and the solid content ratio of the aqueous urethane resin and silica was 3: 5.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）１５部、カチオン性高分子化合物としてエピクロルヒドリン系樹脂（パピオゲンＰ−１０５、固形分濃度６０．０％：センカ社製）１．６７部、水２３．３３部とし、水性ウレタン樹脂とシリカの固形分比が３：１としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink and Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 15 parts of a 20% dispersion manufactured by Mizusawa Chemical Industry Co., Ltd., epichlorohydrin resin as a cationic polymer compound (papiogen P-105, solid content concentration 60.0%: manufactured by Senka) An ink jet recording sheet was obtained in the same manner as in Example 1, except that 67 parts and 23.33 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 3: 1.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）２６．６７部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）６０部、カチオン性高分子化合物としてエピクロルヒドリン系樹脂（パピオゲンＰ−１０５、固形分濃度６０．０％：センカ社製）１．６７部、水１１．６６部とし、水性ウレタン樹脂とシリカの固形分比が１：３としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 26.67 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter). Counter method measurement average particle size 3.3 μm: 60 parts by Mizusawa Chemical Co., Ltd. 20% dispersion), epichlorohydrin resin as a cationic polymer compound (papiogen P-105, solid content concentration 60.0%: manufactured by Senka) An ink jet recording sheet was obtained in the same manner as in Example 1 except that the amount was 1.67 parts and water was 11.66 parts, and the solid content ratio of the aqueous urethane resin to silica was 1: 3.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）２５部、カチオン性高分子化合物としてジシアンジアミド系樹脂（ネオフィックスＦＹ、固形分濃度３７．０％：日華化学社製）２．７部、水１２．３部とし、水性ウレタン樹脂とシリカの固形分比が９：５としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink and Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size: 3.3 μm: 25 parts of a 20% dispersion manufactured by Mizusawa Chemical Co., Ltd., dicyandiamide resin (Neofix FY, solid content concentration: 37.0%: manufactured by Nikka Chemical Co., Ltd.) as a cationic polymer compound 2 An ink jet recording sheet was obtained in the same manner as in Example 1, except that 0.7 part and 12.3 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 9: 5.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）３６部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）４５部、カチオン性高分子化合物としてジシアンジアミド系樹脂（ネオフィックスＦＹ、固形分濃度３７．０％：日華化学社製）２．７部、水１６．３部とし、水性ウレタン樹脂とシリカの固形分比が３：５としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 36 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 45 parts of a 20% dispersion manufactured by Mizusawa Chemical Co., Ltd., dicyandiamide resin (Neofix FY, solid concentration 37.0%: manufactured by Nikka Chemical Co., Ltd.) 2 as a cationic polymer compound An ink jet recording sheet was obtained in the same manner as in Example 1, except that 0.7 part and 16.3 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 3: 5.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）１５部、カチオン性高分子化合物としてジシアンジアミド系樹脂（ネオフィックスＦＹ、固形分濃度３７．０％：日華化学社製）２．７部、水２２．３部とし、水性ウレタン樹脂とシリカの固形分比が３：１としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink and Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 15 parts of a 20% dispersion manufactured by Mizusawa Chemical Co., Ltd., dicyandiamide resin (Neofix FY, solid content concentration 37.0%: manufactured by Nikka Chemical Co., Ltd.) as a cationic polymer compound 2 An ink jet recording sheet was obtained in the same manner as in Example 1, except that 0.7 part and 22.3 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 3: 1.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）２６．６７部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）６０部、カチオン性高分子化合物としてジシアンジアミド系樹脂（ネオフィックスＦＹ、固形分濃度３７．０％：日華化学社製）２．７部、水１０．６３部とし、水性ウレタン樹脂とシリカの固形分比が１：３としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 26.67 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter). Counter method measurement average particle size 3.3 μm: 60 parts of Mizusawa Chemical Co., Ltd. 20% dispersion), dicyandiamide resin (Neofix FY, solid content concentration 37.0%: Nikka Chemical Co., Ltd.) as the cationic polymer compound ) An ink jet recording sheet was obtained in the same manner as in Example 1, except that the amount was 2.7 parts and water was 10.63 parts, and the solid content ratio of the aqueous urethane resin and silica was 1: 3.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）２５部、カチオン性高分子化合物としてアクリルアミドとジアリルアミン塩酸塩の共重合物（スミレ−ズレジン１００１、固形分濃度３０．０％：住友化学工業社製）３．３３部、水１１．６７部とし、水性ウレタン樹脂とシリカの固形分比が９：５としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink and Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 25 parts of Mizusawa Chemical Co., Ltd. 20% dispersion), copolymer of acrylamide and diallylamine hydrochloride as a cationic polymer compound (Smile Resin 1001, solid concentration 30.0%: An ink jet recording sheet was obtained in the same manner as in Example 1 except that 3.33 parts by water (11.67 parts by water) and a solid content ratio of aqueous urethane resin to silica was 9: 5.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）３６部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）４５部、カチオン性高分子化合物としてアクリルアミドとジアリルアミン塩酸塩の共重合物（スミレ−ズレジン１００１、固形分濃度３０．０％：住友化学工業社製）３．３３部、水１５．６７部とし、水性ウレタン樹脂とシリカの固形分比が３：５としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 36 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: Mizusawa Chemical Industries, Ltd. 20% dispersion) 45 parts, copolymer of acrylamide and diallylamine hydrochloride as a cationic polymer compound (Smile Resin 1001, solid concentration 30.0%: (Sumitomo Chemical Co., Ltd.) An ink jet recording sheet was obtained in the same manner as in Example 1, except that 3.33 parts and 15.67 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 3: 5.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）１５部、カチオン性高分子化合物としてアクリルアミドとジアリルアミン塩酸塩の共重合物（スミレ−ズレジン１００１、固形分濃度３０．０％：住友化学工業社製）３．３３部、水２１．６７部とし、水性ウレタン樹脂とシリカの固形分比が３：１としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink and Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 15 parts of a 20% dispersion manufactured by Mizusawa Chemical Industry Co., Ltd. Copolymer of acrylamide and diallylamine hydrochloride as a cationic polymer compound (Violet Resin 1001, solid concentration 30.0%: An ink jet recording sheet was obtained in the same manner as in Example 1 except that 3.33 parts by water (21.67 parts by water) and a solid content ratio of aqueous urethane resin to silica was 3: 1.

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）２６．６７部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）６０部、カチオン性高分子化合物としてアクリルアミドとジアリルアミン塩酸塩の共重合物（スミレ−ズレジン１００１、固形分濃度３０．０％：住友化学工業社製）３．３３部、水１０部とし、水性ウレタン樹脂とシリカの固形分比が１：３としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 26.67 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter). Counter method measurement average particle diameter 3.3 μm: Mizusawa Chemical Co., Ltd. 20% dispersion) 60 parts, copolymer of acrylamide and diallylamine hydrochloride as a cationic polymer compound (Smile Resin 1001, solid concentration 30.0) %: Manufactured by Sumitomo Chemical Co., Ltd.) An inkjet recording sheet was obtained in the same manner as in Example 1 except that 3.33 parts and 10 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 1: 3.

実施例１において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 1.

実施例２において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例２と同じ方法でインクジェット記録シートを得た。   In Example 2, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method measured average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 2.

実施例３において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例３と同じ方法でインクジェット記録シートを得た。   In Example 3, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method measured average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 3.

実施例４において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例４と同じ方法でインクジェット記録シートを得た。   In Example 4, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 4.

実施例５において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例５と同じ方法でインクジェット記録シートを得た。   In Example 5, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 5.

実施例６において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例６と同じ方法でインクジェット記録シートを得た。   In Example 6, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter measurement average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 6.

実施例７において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例７と同じ方法でインクジェット記録シートを得た。   In Example 7, the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 7.

実施例８において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例８と同じ方法でインクジェット記録シートを得た。   In Example 8, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method measurement average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 8.

実施例９において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例９と同じ方法でインクジェット記録シートを得た。   In Example 9, the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 9.

実施例１０において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例１０と同じ方法でインクジェット記録シートを得た。   In Example 10, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method measurement average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 10.

実施例１１において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例１１と同じ方法でインクジェット記録シートを得た。   In Example 11, the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 11.

実施例１２において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例１２と同じ方法でインクジェット記録シートを得た。   In Example 12, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method measured average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 12.

実施例１３において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例１３と同じ方法でインクジェット記録シートを得た。   In Example 13, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 13.

実施例１４において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例１４と同じ方法でインクジェット記録シートを得た。   In Example 14, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 14.

実施例１５において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例１５と同じ方法でインクジェット記録シートを得た。   In Example 15, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method measurement average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 15.

実施例１６において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例１６と同じ方法でインクジェット記録シートを得た。   In Example 16, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 16.

実施例１７において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例１７と同じ方法でインクジェット記録シートを得た。   In Example 17, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method measured average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 17.

実施例１８において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例１８と同じ方法でインクジェット記録シートを得た。   In Example 18, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method measured average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 18.

実施例１９において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例１９と同じ方法でインクジェット記録シートを得た。   In Example 19, except that the silica slurry in [Topcoat layer component] was “Mizukasil P-78D, Coulter counter method measured average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 19.

実施例２０において、〔トップコート層成分〕中のシリカスラリーを、「ミズカシルＰ−７８Ｄ、コールターカウンター法測定平均粒子径８．０μｍ：水澤化学工業社製 ２０％分散液」としたこと以外は実施例２０と同じ方法でインクジェット記録シートを得た。   In Example 20, except that the silica slurry in [Topcoat layer component] was changed to “Mizukasil P-78D, Coulter counter method average particle size 8.0 μm: 20% dispersion manufactured by Mizusawa Chemical Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 20.

実施例１における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   The ink jet recording sheet was obtained by applying and drying the anchor coat layer made of the solvent-based coating agent and the top coat layer made of the water-based coating agent in Example 1 on both surfaces of the support.

実施例２における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 2, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例３における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 3, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例４における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 4, the anchor coat layer composed of a solvent-based coating agent and the top coat layer composed of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例５における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 5, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例６における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 6, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例７における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   The anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent in Example 7 were applied and dried on both sides of the support to obtain an ink jet recording sheet.

実施例８における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 8, the anchor coat layer composed of a solvent-based coating agent and the top coat layer composed of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例９における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   The anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent in Example 9 were applied and dried on both sides of the support to obtain an ink jet recording sheet.

実施例１０における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   The anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent in Example 10 were applied and dried on both sides of the support to obtain an ink jet recording sheet.

実施例１１における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 11, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例１２における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   The anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent in Example 12 were applied and dried on both sides of the support to obtain an ink jet recording sheet.

実施例１３における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 13, the anchor coat layer made of a solvent-based coating agent and the top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例１４における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 14, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例１５における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 15, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例１６における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 16, the anchor coat layer composed of a solvent-based coating agent and the top coat layer composed of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例１７における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 17, an anchor coat layer made of a solvent-based coating agent and a top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例１８における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 18, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例１９における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 19, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例２０における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   The anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent in Example 20 were applied and dried on both sides of the support to obtain an ink jet recording sheet.

実施例２１における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   The anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent in Example 21 were applied and dried on both sides of the support to obtain an ink jet recording sheet.

実施例２２における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 22, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例２３における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 23, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例２４における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 24, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例２５における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 25, the anchor coat layer composed of a solvent-based coating agent and the top coat layer composed of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例２６における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 26, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例２７における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 27, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例２８における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 28, the anchor coat layer composed of a solvent-based coating agent and the top coat layer composed of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例２９における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 29, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例３０における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 30, the anchor coat layer composed of a solvent-based coating agent and the top coat layer composed of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例３１における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 31, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例３２における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 32, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例３３における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 33, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例３４における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 34, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例３５における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 35, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例３６における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 36, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例３７における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 37, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例３８における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 38, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例３９における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 39, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例４０における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。   In Example 40, an anchor coat layer made of a solvent-based coating agent and a top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１Comparative Example 1

実施例１において、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層のどちらも設けずに支持体であるトレーシングペーパー（ＧＮＴ７５、アルジョウィギンズ社製）のみをインクジェット記録シートとした。   In Example 1, only the tracing paper (GNT75, manufactured by Arjo Wiggins Co., Ltd.), which is a support, is inkjet without providing either an anchor coat layer made of a solvent-based coating agent or a top coat layer made of a water-based coating agent. A recording sheet was obtained.

比較例２Comparative Example 2

実施例１において、溶剤系塗工剤からなるアンカーコート層を設け、水系塗工剤からなるトップコート層を設けなかったこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, an ink jet recording sheet was obtained in the same manner as in Example 1 except that an anchor coat layer made of a solvent-based coating agent was provided and a top coat layer made of an aqueous coating agent was not provided.

比較例３Comparative Example 3

実施例１において、溶剤系塗工剤からなるアンカーコート層を設けず、水系塗工剤からなるトップコート層のみ設けたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, an ink jet recording sheet was obtained in the same manner as in Example 1 except that the anchor coat layer made of the solvent-based coating agent was not provided and only the top coat layer made of the water-based coating agent was provided.

比較例４Comparative Example 4

実施例１において、水系塗工剤からなるトップコート層成分中から水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）を除き、水性ウレタン樹脂使用量を０部としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.) was removed from the topcoat layer component consisting of an aqueous coating agent, and the amount of aqueous urethane resin used was 0. An ink jet recording sheet was obtained in the same manner as in Example 1 except that the parts were used.

比較例５Comparative Example 5

実施例１において、水系塗工剤からなるトップコート層成分中からシリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）を除き、シリカ使用量を０部としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, silica slurry (Mizukasil P-78A, Coulter counter method measurement average particle size: 3.3 μm: 20% dispersion manufactured by Mizusawa Chemical Industry Co., Ltd.) was removed from the topcoat layer component composed of an aqueous coating agent. An ink jet recording sheet was obtained in the same manner as in Example 1 except that the amount used was 0 parts.

比較例６Comparative Example 6

実施例１において、水系塗工剤からなるトップコート層成分中からカチオン性高分子化合物を除いたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the inkjet recording sheet was obtained by the same method as Example 1 except having remove | excluded the cationic high molecular compound from the topcoat layer component which consists of a water-system coating agent.

実施例１において、溶剤系塗工剤からなるアンカーコート層の塗工量を０．５ｇ／ｍ２となるようにしたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。 In Example 1, the inkjet recording sheet was obtained by the same method as Example 1 except having made the coating amount of the anchor coat layer which consists of a solvent-type coating agent into 0.5 g / m < 2 >.

実施例２において、溶剤系塗工剤からなるアンカーコート層の塗工量を０．５ｇ／ｍ２となるようにしたこと以外は実施例２と同じ方法でインクジェット記録シートを得た。 In Example 2, an inkjet recording sheet was obtained in the same manner as in Example 2 except that the coating amount of the anchor coat layer made of the solvent-based coating agent was 0.5 g / m 2 .

実施例３において、溶剤系塗工剤からなるアンカーコート層の塗工量を０．５ｇ／ｍ２となるようにしたこと以外は実施例３と同じ方法でインクジェット記録シートを得た。 In Example 3, an inkjet recording sheet was obtained in the same manner as in Example 3 except that the coating amount of the anchor coat layer composed of the solvent-based coating agent was 0.5 g / m 2 .

実施例４において、溶剤系塗工剤からなるアンカーコート層の塗工量を０．５ｇ／ｍ２となるようにしたこと以外は実施例４と同じ方法でインクジェット記録シートを得た。 In Example 4, the inkjet recording sheet was obtained by the same method as Example 4 except having made the coating amount of the anchor coat layer which consists of a solvent-type coating agent into 0.5 g / m < 2 >.

実施例１において、溶剤系塗工剤からなるアンカーコート層の塗工量を６．０ｇ／ｍ２となるようにしたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。 In Example 1, the inkjet recording sheet was obtained by the same method as Example 1 except having made the coating amount of the anchor coat layer which consists of a solvent-type coating agent into 6.0 g / m < 2 >.

実施例２において、溶剤系塗工剤からなるアンカーコート層の塗工量を６．０ｇ／ｍ２となるようにしたこと以外は実施例２と同じ方法でインクジェット記録シートを得た。 In Example 2, an inkjet recording sheet was obtained in the same manner as in Example 2 except that the coating amount of the anchor coat layer made of the solvent-based coating agent was 6.0 g / m 2 .

実施例３において、溶剤系塗工剤からなるアンカーコート層の塗工量を６．０ｇ／ｍ２となるようにしたこと以外は実施例３と同じ方法でインクジェット記録シートを得た。 In Example 3, an inkjet recording sheet was obtained in the same manner as in Example 3 except that the coating amount of the anchor coat layer made of the solvent-based coating agent was 6.0 g / m 2 .

実施例４において、溶剤系塗工剤からなるアンカーコート層の塗工量を６．０ｇ／ｍ２となるようにしたこと以外は実施例４と同じ方法でインクジェット記録シートを得た。 In Example 4, the inkjet recording sheet was obtained by the same method as Example 4 except having made the coating amount of the anchor coat layer which consists of a solvent-type coating agent into 6.0 g / m < 2 >.

比較例７Comparative Example 7

実施例１において、溶剤系塗工剤からなるアンカーコート層の塗工量を１６．０ｇ／ｍ２となるようにしたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。 In Example 1, the inkjet recording sheet was obtained by the same method as Example 1 except having made the coating amount of the anchor coat layer which consists of a solvent-type coating agent into 16.0 g / m < 2 >.

比較例８Comparative Example 8

実施例２において、溶剤系塗工剤からなるアンカーコート層の塗工量を１６．０ｇ／ｍ２となるようにしたこと以外は実施例２と同じ方法でインクジェット記録シートを得た。 In Example 2, an inkjet recording sheet was obtained in the same manner as in Example 2 except that the coating amount of the anchor coat layer made of the solvent-based coating agent was 16.0 g / m 2 .

比較例９Comparative Example 9

実施例３において、溶剤系塗工剤からなるアンカーコート層の塗工量を１６．０ｇ／ｍ２となるようにしたこと以外は実施例３と同じ方法でインクジェット記録シートを得た。 In Example 3, an inkjet recording sheet was obtained in the same manner as in Example 3 except that the coating amount of the anchor coat layer made of the solvent-based coating agent was 16.0 g / m 2 .

比較例１０Comparative Example 10

実施例４において、溶剤系塗工剤からなるアンカーコート層の塗工量を１６．０ｇ／ｍ２となるようにしたこと以外は実施例４と同じ方法でインクジェット記録シートを得た。 In Example 4, the inkjet recording sheet was obtained by the same method as Example 4 except having made the coating amount of the anchor coat layer which consists of a solvent-type coating agent into 16.0 g / m < 2 >.

比較例１１Comparative Example 11

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）１１．３部、カチオン性高分子化合物としてポリアミン系樹脂（ＤＫ−８５６、固形分濃度５０．０％：星光ＰＭＣ社製）２部、水２６．７部とし、水性ウレタン樹脂とシリカの固形分比が４：１としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink and Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle diameter 3.3 μm: Mizusawa Chemical Co., Ltd. 20% dispersion) 11.3 parts, Cationic polymer compound polyamine resin (DK-856, solid content concentration 50.0%: Seiko PMC Co., Ltd.) An ink jet recording sheet was obtained in the same manner as in Example 1 except that 2 parts and 26.7 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 4: 1.

比較例１２Comparative Example 12

実施例１において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）２０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）６０部、カチオン性高分子化合物としてポリアミン系樹脂（ＤＫ−８５６、固形分濃度５０．０％：星光ＰＭＣ社製）２部、水１８部とし、水性ウレタン樹脂とシリカの固形分比が１：４としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。   In Example 1, the [topcoat layer component] was composed of 20 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 60 parts of Mizusawa Chemical Co., Ltd. 20% dispersion), 2 parts of polyamine resin (DK-856, solid concentration 50.0%: Seiko PMC Co., Ltd.) as the cationic polymer compound An ink jet recording sheet was obtained in the same manner as in Example 1, except that the water content was 18 parts and the solid content ratio of the aqueous urethane resin to silica was 1: 4.

比較例１３Comparative Example 13

実施例５において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）１１．３部、カチオン性高分子化合物としてジメチルジアリルアンモニウムクロライド系樹脂（ＫＲ−８５０、固形分濃度２８．０％：荒川化学工業社製）３．５７部、水２５．１３部とし、水性ウレタン樹脂とシリカの固形分比が４：１としたこと以外は実施例５と同じ方法でインクジェット記録シートを得た。 In Example 5, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 11.3 parts of 20% dispersion manufactured by Mizusawa Chemical Co., Ltd., dimethyldiallylammonium chloride-based resin (KR-850, solid content concentration 28.0%: Arakawa Chemical) as the cationic polymer compound An ink jet recording sheet was obtained in the same manner as in Example 5 except that 3.57 parts by industry) and 25.13 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 4: 1.

比較例１４Comparative Example 14

実施例５において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）２０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）６０部、カチオン性高分子化合物としてジメチルジアリルアンモニウムクロライド系樹脂（ＫＲ−８５０、固形分濃度２８．０％：荒川化学工業社製）３．５７部、水１６．４３部とし、水性ウレタン樹脂とシリカの固形分比が１：４としたこと以外は実施例５と同じ方法でインクジェット記録シートを得た。 In Example 5, the [topcoat layer component] was composed of 20 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 60 parts of Mizusawa Chemical Co., Ltd. 20% dispersion), dimethyldiallylammonium chloride-based resin (KR-850, solid concentration 28.0%: Arakawa Chemical Industries, Ltd.) as the cationic polymer compound (Manufactured) An ink jet recording sheet was obtained in the same manner as in Example 5 except that 3.57 parts and 16.43 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 1: 4.

比較例１５Comparative Example 15

実施例９において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）１１．３部、カチオン性高分子化合物としてエピクロルヒドリン系樹脂（パピオゲンＰ−１０５、固形分濃度６０．０％：センカ社製）１．６７部、水２７．０３部とし、水性ウレタン樹脂とシリカの固形分比が４：１としたこと以外は実施例９と同じ方法でインクジェット記録シートを得た。 In Example 9, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (patella coal IJ-50R, solid concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: Mizusawa Chemical Co., Ltd. 20% dispersion) 11.3 parts, as a cationic polymer compound epichlorohydrin resin (papiogen P-105, solid content concentration 60.0%: manufactured by Senka) An ink jet recording sheet was obtained in the same manner as in Example 9 except that 1.67 parts and 27.03 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 4: 1.

比較例１６Comparative Example 16

実施例９において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）２０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）６０部、カチオン性高分子化合物としてエピクロルヒドリン系樹脂（パピオゲンＰ−１０５、固形分濃度６０．０％：センカ社製）１．６７部、水１８．３３部とし、水性ウレタン樹脂とシリカの固形分比が１：４としたこと以外は実施例９と同じ方法でインクジェット記録シートを得た。 In Example 9, the [topcoat layer component] was composed of 20 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 60 parts of Mizusawa Chemical Co., Ltd. 20% dispersion), epichlorohydrin-based resin as a cationic polymer compound (papiogen P-105, solid content concentration 60.0%: manufactured by Senka) An ink jet recording sheet was obtained in the same manner as in Example 9, except that 67 parts and 18.33 parts of water were used and the solid content ratio of the aqueous urethane resin and silica was 1: 4.

比較例１７Comparative Example 17

実施例１３において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）１１．３部、カチオン性高分子化合物としてジシアンジアミド系樹脂（ネオフィックスＦＹ、固形分濃度３７．０％：日華化学社製）２．７部、水２６部とし、水性ウレタン樹脂とシリカの固形分比が４：１としたこと以外は実施例１３と同じ方法でインクジェット記録シートを得た。 In Example 13, the [topcoat layer component] was composed of 60 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 11.3 parts of 20% dispersion manufactured by Mizusawa Chemical Co., Ltd. Dicyandiamide resin (Neofix FY, solid content concentration 37.0%: manufactured by Nikka Chemical Co., Ltd.) as a cationic polymer compound ) An ink jet recording sheet was obtained in the same manner as in Example 13 except that 2.7 parts and 26 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 4: 1.

比較例１８Comparative Example 18

実施例１３において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）２０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）６０部、カチオン性高分子化合物としてジシアンジアミド系樹脂（ネオフィックスＦＹ、固形分濃度３７．０％：日華化学社製）２．７部、水１７．３部とし、水性ウレタン樹脂とシリカの固形分比が１：４としたこと以外は実施例１３と同じ方法でインクジェット記録シートを得た。 In Example 13, the [topcoat layer component] was composed of 20 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 60 parts of Mizusawa Chemical Co., Ltd. 20% dispersion), dicyandiamide resin as a cationic polymer compound (Neofix FY, solid content concentration 37.0%: Nikka Chemical Co., Ltd.) 2 An ink jet recording sheet was obtained in the same manner as in Example 13, except that 0.7 part and 17.3 parts of water were used, and the solid content ratio of the aqueous urethane resin and silica was 1: 4.

比較例１９Comparative Example 19

実施例１７において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）６０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）１１．３部、カチオン性高分子化合物としてアクリルアミドとジアリルアミン塩酸塩の共重合物（スミレ−ズレジン１００１、固形分濃度３０．０％：住友化学工業社製）３．３３部、水２５．３７部とし、水性ウレタン樹脂とシリカの固形分比が４：１としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。 In Example 17, [Topcoat layer component] was composed of 60 parts of a water-based urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 11.3 parts of a 20% dispersion manufactured by Mizusawa Chemical Industry Co., Ltd. Copolymer of acrylamide and diallylamine hydrochloride as a cationic polymer compound (Smile Resin 1001, solid concentration 30.0) %: Manufactured by Sumitomo Chemical Co., Ltd.) 3.33 parts, 25.37 parts of water, and an inkjet recording sheet was obtained in the same manner as in Example 1 except that the solid content ratio of the aqueous urethane resin and silica was 4: 1. It was.

比較例２０Comparative Example 20

実施例１７において、〔トップコート層成分〕を、水性ウレタン樹脂（パテラコールＩＪ−５０Ｒ、固形分濃度１５％：大日本インキ化学工業社製）２０部、シリカスラリー（ミズカシルＰ−７８Ａ、コールターカウンター法測定平均粒子径３．３μｍ：水澤化学工業社製 ２０％分散液）６０部、カチオン性高分子化合物としてアクリルアミドとジアリルアミン塩酸塩の共重合物（スミレ−ズレジン１００１、固形分濃度３０．０％：住友化学工業社製）３．３３部、水１６．６７部とし、水性ウレタン樹脂とシリカの固形分比が１：４としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。 In Example 17, the [topcoat layer component] was composed of 20 parts of an aqueous urethane resin (Pateracol IJ-50R, solid content concentration 15%: manufactured by Dainippon Ink & Chemicals, Inc.), silica slurry (Mizukasil P-78A, Coulter counter method). Measurement average particle size 3.3 μm: 60 parts of Mizusawa Chemical Co., Ltd. 20% dispersion), copolymer of acrylamide and diallylamine hydrochloride as a cationic polymer compound (Violet Resin 1001, solid content concentration 30.0%: (Sumitomo Chemical Co., Ltd.) An ink jet recording sheet was obtained in the same manner as in Example 1 except that 3.33 parts and 16.67 parts of water were used, and the solid content ratio of aqueous urethane resin to silica was 1: 4.

比較例２１Comparative Example 21

実施例１において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。 In Example 1, except that the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 1.

比較例２２Comparative Example 22

実施例２において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例２と同じ方法でインクジェット記録シートを得た。 In Example 2, the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter method measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 2.

比較例２３Comparative Example 23

実施例３において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例３と同じ方法でインクジェット記録シートを得た。 In Example 3, except that the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 3.

比較例２４Comparative Example 24

実施例４において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例４と同じ方法でインクジェット記録シートを得た。 In Example 4, the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 4.

比較例２５Comparative Example 25

実施例５において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例５と同じ方法でインクジェット記録シートを得た。 In Example 5, the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 5.

比較例２６Comparative Example 26

実施例６において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例６と同じ方法でインクジェット記録シートを得た。 In Example 6, except that the silica slurry in [Topcoat layer component] was “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 6.

比較例２７Comparative Example 27

実施例７において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例７と同じ方法でインクジェット記録シートを得た。 In Example 7, the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter method measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 7.

比較例２８Comparative Example 28

実施例８において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例８と同じ方法でインクジェット記録シートを得た。 In Example 8, the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 8.

比較例２９Comparative Example 29

実施例９において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例９と同じ方法でインクジェット記録シートを得た。 In Example 9, the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 9.

比較例３０Comparative Example 30

実施例１０において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例１０と同じ方法でインクジェット記録シートを得た。 In Example 10, except that the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 10.

比較例３１Comparative Example 31

実施例１１において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例１１と同じ方法でインクジェット記録シートを得た。 In Example 11, the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter method measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 11.

比較例３２Comparative Example 32

実施例１２において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例１２と同じ方法でインクジェット記録シートを得た。 In Example 12, the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 12.

比較例３３Comparative Example 33

実施例１３において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例１３と同じ方法でインクジェット記録シートを得た。 In Example 13, the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter measurement average particle diameter 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 13.

比較例３４Comparative Example 34

実施例１４において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例１４と同じ方法でインクジェット記録シートを得た。 In Example 14, the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter method measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 14.

比較例３５Comparative Example 35

実施例１５において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例１５と同じ方法でインクジェット記録シートを得た。 In Example 15, except that the silica slurry in [Topcoat layer component] was “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 15.

比較例３６Comparative Example 36

実施例１６において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例１６と同じ方法でインクジェット記録シートを得た。 In Example 16, except that the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 16.

比較例３７Comparative Example 37

実施例１７において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例１７と同じ方法でインクジェット記録シートを得た。 In Example 17, the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 17.

比較例３８Comparative Example 38

実施例１８において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例１８と同じ方法でインクジェット記録シートを得た。 In Example 18, except that the silica slurry in [Topcoat layer component] was “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 18.

比較例３９Comparative Example 39

実施例１９において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例１９と同じ方法でインクジェット記録シートを得た。 In Example 19, the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter method measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 19.

比較例４０Comparative Example 40

実施例２０において、〔トップコート層成分〕中のシリカスラリーを、「ニップジェルＢＹ−２００、コールターカウンター法測定平均粒子径１．９μｍ：日本シリカ工業社製 ２０％分散液」としたこと以外は実施例２０と同じ方法でインクジェット記録シートを得た。 In Example 20, except that the silica slurry in [Topcoat layer component] was changed to “Nipgel BY-200, Coulter counter measurement average particle size 1.9 μm: 20% dispersion manufactured by Nippon Silica Kogyo Co., Ltd.” An ink jet recording sheet was obtained in the same manner as in Example 20.

比較例４１Comparative Example 41

実施例１において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例１と同じ方法でインクジェット記録シートを得た。 In Example 1, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained in the same manner as in Example 1.

比較例４２Comparative Example 42

実施例２において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例２と同じ方法でインクジェット記録シートを得た。 In Example 2, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter method measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained by the same method as in No. 2.

比較例４３Comparative Example 43

実施例３において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例３と同じ方法でインクジェット記録シートを得た。 In Example 3, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter method measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained in the same manner as in No. 3.

比較例４４Comparative Example 44

実施例４において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例４と同じ方法でインクジェット記録シートを得た。 In Example 4, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter method measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained by the same method as in No. 4.

比較例４５Comparative Example 45

実施例５において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例５と同じ方法でインクジェット記録シートを得た。 In Example 5, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained by the same method as in No. 5.

比較例４６Comparative Example 46

実施例６において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例６と同じ方法でインクジェット記録シートを得た。 In Example 6, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. 6 was used to obtain an ink jet recording sheet.

比較例４７Comparative Example 47

実施例７において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液・」としたこと以外は実施例７と同じ方法でインクジェット記録シートを得た。 In Example 7, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained in the same manner as in Example 7.

比較例４８Comparative Example 48

実施例８において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例８と同じ方法でインクジェット記録シートを得た。 In Example 8, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter method measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained in the same manner as in No. 8.

比較例４９Comparative Example 49

実施例９において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例９と同じ方法でインクジェット記録シートを得た。 In Example 9, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained in the same manner as in Example 9.

比較例５０Comparative Example 50

実施例１０において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例１０と同じ方法でインクジェット記録シートを得た。 In Example 10, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. In the same manner as in No. 10, an ink jet recording sheet was obtained.

比較例５１Comparative Example 51

実施例１１において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例１１と同じ方法でインクジェット記録シートを得た。 In Example 11, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. In the same manner as in No. 11, an ink jet recording sheet was obtained.

比較例５２Comparative Example 52

実施例１２において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例１２と同じ方法でインクジェット記録シートを得た。 In Example 12, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. In the same manner as in No. 12, an ink jet recording sheet was obtained.

比較例５３Comparative Example 53

実施例１３において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例１３と同じ方法でインクジェット記録シートを得た。 In Example 13, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained in the same manner as in Example 13.

比較例５４Comparative Example 54

実施例１４において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例１４と同じ方法でインクジェット記録シートを得た。 In Example 14, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter method measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained in the same manner as in Example 14.

比較例５５Comparative Example 55

実施例１５において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例１５と同じ方法でインクジェット記録シートを得た。 In Example 15, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter method measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An inkjet recording sheet was obtained in the same manner as in Example 15.

比較例５６Comparative Example 56

実施例１６において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例１６と同じ方法でインクジェット記録シートを得た。 In Example 16, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained in the same manner as in No. 16.

比較例５７Comparative Example 57

実施例１７において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例１７と同じ方法でインクジェット記録シートを得た。 In Example 17, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained in the same manner as in No. 17.

比較例５８Comparative Example 58

実施例１８において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例１８と同じ方法でインクジェット記録シートを得た。 In Example 18, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained in the same manner as in No.18.

比較例５９Comparative Example 59

実施例１９において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例１９と同じ方法でインクジェット記録シートを得た。 In Example 19, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained in the same manner as in No. 19.

比較例６０Comparative Example 60

実施例２０において、〔トップコート層成分〕中のシリカスラリーを、「ファインシールＸ−１３、コールターカウンター法測定平均粒子径１６．３μｍ：トクヤマ社製 ２０％分散液」としたこと以外は実施例２０と同じ方法でインクジェット記録シートを得た。 In Example 20, the silica slurry in [Topcoat layer component] was changed to “Fine seal X-13, Coulter counter measurement average particle size 16.3 μm: 20% dispersion manufactured by Tokuyama Corporation”. An ink jet recording sheet was obtained in the same manner as in No. 20.

比較例６１Comparative Example 61

比較例２における、溶剤系塗工剤からなるアンカーコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 2, an anchor coat layer made of a solvent-based coating agent was applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例６２Comparative Example 62

比較例３における、水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 3, the topcoat layer made of an aqueous coating agent was applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例６３Comparative Example 63

比較例４における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 4, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例６４Comparative Example 64

比較例５における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 5, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例６５Comparative Example 65

比較例６における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 6, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例８１における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布乾燥しインクジェット記録シートを得た。 In Example 81, an anchor coat layer made of a solvent-based coating agent and a top coat layer made of a water-based coating agent were applied and dried on both surfaces of the support to obtain an ink jet recording sheet.

実施例８２における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Example 82, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例８３における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Example 83, the anchor coat layer composed of a solvent-based coating agent and the top coat layer composed of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例８４における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Example 84, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例８５における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Example 85, an anchor coat layer made of a solvent-based coating agent and a top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例８６における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Example 86, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例８７における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Example 87, an anchor coat layer made of a solvent-based coating agent and a top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

実施例８８における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Example 88, the anchor coat layer composed of a solvent-based coating agent and the top coat layer composed of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例６６Comparative Example 66

比較例７における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 7, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例６７Comparative Example 67

比較例８における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 8, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例６８Comparative Example 68

比較例９における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 9, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例６９Comparative Example 69

比較例１０における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 10, the anchor coat layer made of a solvent-based coating agent and the top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例７０Comparative Example 70

比較例１１における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 11, the anchor coat layer made of a solvent-based coating agent and the top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例７１Comparative Example 71

比較例１２における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 12, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例７２Comparative Example 72

比較例１３における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 13, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例７３Comparative Example 73

比較例１４における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 14, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例７４Comparative Example 74

比較例１５における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 15, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例７５Comparative Example 75

比較例１６における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 16, an anchor coat layer made of a solvent-based coating agent and a top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例７６Comparative Example 76

比較例１７における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 17, an anchor coat layer made of a solvent-based coating agent and a top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例７７Comparative Example 77

比較例１８における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 18, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例７８Comparative Example 78

比較例１９における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 19, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例７９Comparative Example 79

比較例２０における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 20, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例８０Comparative Example 80

比較例２１における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 21, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例８１Comparative Example 81

比較例２２における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 22, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例８２Comparative Example 82

比較例２３における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 23, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例８３Comparative Example 83

比較例２４における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 24, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例８４Comparative Example 84

比較例２５における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 25, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例８５Comparative Example 85

比較例２６における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 26, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例８６Comparative Example 86

比較例２７における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 27, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例８７Comparative Example 87

比較例２８における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 28, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例８８Comparative Example 88

比較例２９における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 29, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例８９Comparative Example 89

比較例３０における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 30, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例９０Comparative Example 90

比較例３１における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 31, an anchor coat layer made of a solvent-based coating agent and a top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例９１Comparative Example 91

比較例３２における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 32, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例９２Comparative Example 92

比較例３３における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 33, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例９３Comparative Example 93

比較例３４における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 34, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例９４Comparative Example 94

比較例３５における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 35, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例９５Comparative Example 95

比較例３６における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 36, an anchor coat layer made of a solvent-based coating agent and a top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例９６Comparative Example 96

比較例３７における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 37, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例９７Comparative Example 97

比較例３８における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 38, an anchor coat layer made of a solvent-based coating agent and a top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例９８Comparative Example 98

比較例３９における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 39, an anchor coat layer made of a solvent-based coating agent and a top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例９９Comparative Example 99

比較例４０における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 40, an anchor coat layer made of a solvent-based coating agent and a top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１００Comparative Example 100

比較例４１における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 41, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１０１Comparative Example 101

比較例４２における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 42, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１０２Comparative Example 102

比較例４３における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 43, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１０３Comparative Example 103

比較例４４における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 44, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１０４Comparative Example 104

比較例４５における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 45, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１０６Comparative Example 106

比較例４６における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 46, the anchor coat layer made of a solvent-based coating agent and the top coat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１０７Comparative Example 107

比較例４７における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 47, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１０８Comparative Example 108

比較例４８における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 48, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１０９Comparative Example 109

比較例４９における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 49, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１１０Comparative Example 110

比較例５０における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 50, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１１１Comparative Example 111

比較例５１における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 51, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１１２Comparative Example 112

比較例５２における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 52, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１１３Comparative Example 113

比較例５３における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 53, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１１４Comparative Example 114

比較例５４における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 54, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１１５Comparative Example 115

比較例５５における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 55, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１１６Comparative Example 116

比較例５６における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 56, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１１７Comparative Example 117

比較例５７における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 57, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１１８Comparative Example 118

比較例５８における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 58, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１１９Comparative Example 119

比較例５９における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。 In Comparative Example 59, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.

比較例１２０Comparative Example 120

比較例６０における、溶剤系塗工剤からなるアンカーコート層及び水系塗工剤からなるトップコート層を支持体の両面に塗布・乾燥しインクジェット記録シートを得た。

Figure 2006062262
Figure 2006062262
Figure 2006062262
Figure 2006062262
Figure 2006062262
Figure 2006062262
Figure 2006062262
 In Comparative Example 60, the anchor coat layer made of a solvent-based coating agent and the topcoat layer made of a water-based coating agent were applied to both surfaces of the support and dried to obtain an ink jet recording sheet.
Figure 2006062262
Figure 2006062262
Figure 2006062262
Figure 2006062262
Figure 2006062262
Figure 2006062262
Figure 2006062262

上記実施例及び比較例で得られたインクジェット記録シートについての評価を下記の表に示した。評価項目は「不透明度」、「透明性」、「インク乾燥性」、「画像の滲み」、「ボコツキ・シワ」、「鉛筆筆記性」、「印字部耐水性」の７項目とした。各項目の評価方法を説明し評価結果を示すこととする。
「不透明度」…ＪＩＳ Ｐ ８１４９：２０００「紙及び板紙−不透明度試験方法（紙の裏当て）−拡散照明法」に従って測定した値とした。数値は％を表す。
「透明性」…シートの透明性について目視評価した。
・ ：特に透明性が良好。
〇：透明性良好。
・ ：透明性は少しあるように感じるが、下の図や柄が十分に透けて見えず、実用性が劣る。
×：透明性がなく、下の図や柄がほとんど透けて見えず、実用性がない。
「インク乾燥性」…エプソン社製インクジェットプリンターであるＰＭ−９５０Ｃ機を使用し印字を行い、印字部表面のウエット感がなく乾燥状態となるまでに要した時間を目視評価した。
〇：６０秒未満にあり、良好。
・ ：６０〜１２０秒にあり、実用性が劣る。
×：１２０秒を超え、実用性がない。
「画像の滲み」…エプソン社製インクジェットプリンターであるＰＭ−９５０Ｃ機を使用し単色もしくは重色を連続で記録し、隣接する印字部が相互もしくは片方にインクの流れ出しが生じていないかを目視評価した。
〇：滲みのない状態にあり、良好。
・ ：滲みのややある状態にあり、実用性が劣る。
×：滲みの大きい状態にあり、実用性がない。
「ボコツキ・シワ」…塗工乾燥後のシート紙面のボコツキ・シワの程度を目視評価した。
〇：ボコツキ・シワのない状態にあり、良好。
・ ：ボコツキ・シワの若干ある状態にあり、実用性が劣る。
×：ボコツキ・シワのかなりある状態にあり、実用性がない。
「鉛筆筆記性」…三菱鉛筆ユニ（商標登録）０．５ｍｍＨＢを使用して筆記を行い摩耗度、筆記跡及び画線の鮮明性について評価した。
◎：摩耗が問題なく、筆記跡がなく画線も鮮明である状態にあり、非常に良好。
〇：摩耗が殆ど問題なく、筆記跡が殆どなく画線もほぼ鮮明である状態にあり、実用の範囲にある。
・ ：摩耗、筆記跡のいずれかにやや問題があり画線もあまり鮮明ではない状態にあり、実用性が劣る。
×：摩耗、筆記跡のいずれかに著しく問題があり画線が鮮明ではない状態にあり、実用性がない。
「印字部耐水性」…エプソン社製インクジェットプリンターであるＰＭ−９５０Ｃ機を使用し印字を行い、ベタ印字した部分を水に５秒間浸し、濾紙で拭き取り、インクの流れ出しを目視評価した。
〇：インクの流れ出しが目立たず、耐水性が良好である状態にあり、良好。
・ ：インクの流れ出しが二次色で生ずるなど、耐水性がやや悪い状態にあり、実用性が劣る。
×：インクの流れ出しが全般に生じ、耐水性が非常に悪い状態にあり、実用性がない。 Evaluations of the ink jet recording sheets obtained in the above examples and comparative examples are shown in the following table. The evaluation items were seven items of “opacity”, “transparency”, “ink drying property”, “image blur”, “brightness / wrinkle”, “pencil writing property”, and “water resistance of printed portion”. The evaluation method for each item will be explained and the evaluation results will be shown.
“Opacity”: Measured according to JIS P 8149: 2000 “Paper and paperboard—Opacity test method (backing of paper) —diffuse illumination method”. The numerical value represents%.
“Transparency”: The transparency of the sheet was visually evaluated.
・: Transparency is particularly good.
○: Excellent transparency.
・: Although it seems that there is a little transparency, the figure and the pattern below are not sufficiently transparent and practicality is inferior.
X: There is no transparency, the figure and pattern below are hardly seen through, and there is no practicality.
“Ink drying property”: Printing was performed using a PM-950C machine, which is an Epson inkjet printer, and the time required for the printing unit surface to be dry without any wet feeling was visually evaluated.
○: Less than 60 seconds, good.
*: It is in 60 to 120 seconds, and practicality is inferior.
X: It exceeds 120 seconds and is not practical.
"Blur of image": Using a PM-950C machine, an Epson ink jet printer, continuously record a single color or heavy color, and visually evaluate whether adjacent print parts have flowed out of each other or one side. did.
◯: Good without bleeding.
-: Slightly blurred and inferior in practicality.
X: Large blurring and no practicality.
“Unevenness / wrinkle”: The degree of unevenness / wrinkle on the surface of the sheet after coating and drying was visually evaluated.
◯: It is in a state free from bumps and wrinkles and is good.
・: Slightly wrinkled or wrinkled, so practicality is poor.
X: There is a considerable amount of bumpy wrinkles and there is no practicality.
"Pencil writing property": Writing was performed using Mitsubishi Pencil Uni (registered trademark) 0.5 mm HB, and the degree of wear, writing marks, and sharpness of image lines were evaluated.
A: There is no problem with wear, there is no written trace, and the image line is clear, which is very good.
◯: There is almost no problem with wear, there is almost no written trace, the image line is almost clear, and it is in the practical range.
-: There is a slight problem with either wear or handwriting, the image line is not very clear, and the practicality is inferior.
X: There is a significant problem in either wear or writing mark, the image line is not clear, and there is no practicality.
“Water resistance of printed part”: Printing was performed using a PM-950C machine, an Epson inkjet printer, the solid printed part was immersed in water for 5 seconds, wiped with filter paper, and the ink flow was visually evaluated.
◯: The ink flow is inconspicuous and the water resistance is good, which is good.
-: Water is in a slightly poor state, such as ink flowing out in a secondary color, and practicality is inferior.
X: Ink flow generally occurs, the water resistance is very poor, and there is no practicality.

第１表から以下のことが判る：
請求項１の構成要件を満足する実施例１〜８０のインクジェット記録シートは透明性が高く、インク乾燥性が速く、画像の滲みが少なく、シワやボコツキの発生がなく、インクジェット記録部の耐水性も優れたものであり、鉛筆筆記性も優れている。これに対して、溶剤塗工剤および／または水性塗工剤を有していない比較例１〜３（片面塗工）および比較例６１〜６３（両面塗工）の記録シートはインク乾燥性、画像の滲みおよび耐水性（比較例１）、更には鉛筆筆記性も悪い（比較例２および６１）かあるいはボコツキ・シワに問題があり（比較例３および６２）、水性ウレタン樹脂、白色無機顔料またはカチオン性高分子化合物が使用されていない比較例２および６（片面塗工）および比較例６１および６５（両面塗工）の記録シートは耐水性が悪い他に画像の滲み、鉛筆筆記性および／またはインク乾燥性に問題がある場合があり、実用性のないものである。
第１層塗工量が０．５ｇ／ｍ２と比較的に少ない実施例８１〜８４（片面塗工）および実施例８９〜９２（両面塗工）の場合には、ボコツキ・シワが多少発生し、６．０ｇ／ｍ２と比較的に多い実施例８５〜８８（片面塗工）および実施例９３〜９６（両面塗工）の場合には、鉛筆筆記性が実用範囲内であるが、１６．０ｇ／ｍ２と本発明の範囲（０．５〜１０ｇ／ｍ２）を逸脱する比較例７〜１０（片面塗工）および比較例６６〜６９（両面塗工）の場合には鉛筆筆記性が非常に悪い。
水系塗工剤中に含まれる水性ウレタン樹脂とシリカとの比が本発明の範囲（３．５：１〜１：３．５）を逸脱する１：４または４：１の比較例１１〜２０（片面塗工）および比較例７０〜７９（両面塗工）の場合にはインク乾燥性および鉛筆筆記性が不足するかまたは透明性、滲みおよび鉛筆筆記性が不足し、実質的に実用性がない。白色無機顔料のシリカが１．９μmと本発明の範囲（３．０〜１５．０μｍ）に不足する比較例２１〜４０（片面塗工）および比較例８０〜９９（両面塗工）の場合には鉛筆筆記性かまたは透明性が悪く実用性がなく、１６．３μｍと本発明の範囲より多い比較例５１〜６０（片面塗工）および比較例００〜１１９の場合にはインク乾燥性および鉛筆筆記性が悪い他に画像の滲みに問題のある場合が多く、実用に耐えない。
以上から明らかな通り、本発明の実施例によって得られたインクジェット記録シートは、水性インクによるインクジェット記録方式のプリンター及びプロッターを用いて記録されるインクジェット記録シートにおいて、透明性が高く、フルカラー記録による画像鮮明性に優れ、インク乾燥性が速く、画像の滲みが少なく、シワやボコツキの発生がない安定操業が可能であり、更にはインクジェット記録部の耐水性にも優れたものであり、ＣＡＤ用第二原図用紙として、また、ファンシー用透明紙としての両特性を兼ね備えたインクジェット記録シートが得られたと言える。 From Table 1 you can see:
The ink jet recording sheets of Examples 1 to 80 that satisfy the constituent requirements of claim 1 have high transparency, quick ink drying, little bleeding of images, no wrinkles and no blurring, and water resistance of the ink jet recording portion. Is also excellent, and the pencil writing property is also excellent. On the other hand, the recording sheets of Comparative Examples 1 to 3 (single-sided coating) and Comparative Examples 61 to 63 (double-sided coating) that do not have a solvent coating agent and / or an aqueous coating agent have ink drying properties. Image bleeding and water resistance (Comparative Example 1), pencil writing property is also poor (Comparative Examples 2 and 61), or there is a problem of unevenness and wrinkles (Comparative Examples 3 and 62), aqueous urethane resin, white inorganic pigment The recording sheets of Comparative Examples 2 and 6 (single-sided coating) and Comparative Examples 61 and 65 (double-sided coating) in which no cationic polymer compound is used have poor water resistance, image bleeding, pencil writing property and There is a case where there is a problem with the ink drying property, which is not practical.
In the case of Examples 81 to 84 (single-sided coating) and Examples 89 to 92 (double-sided coating) with a relatively small first layer coating amount of 0.5 g / m 2 , some unevenness and wrinkles occur. In the case of Examples 85 to 88 (single-sided coating) and Examples 93 to 96 (double-sided coating) having a relatively large amount of 6.0 g / m 2 , the pencil writing property is within the practical range. pencil in the case of 16.0 g / m 2 and scope of the present invention (0.5 to 10 g / m 2) departing from the Comparative example 7-10 (one side coating) and Comparative example 66 to 69 (both sides coated) Writability is very bad.
Comparative example 11-20 of 1: 4 or 4: 1 in which the ratio of the aqueous urethane resin and silica contained in the aqueous coating agent deviates from the scope of the present invention (3.5: 1 to 1: 3.5). In the case of (single-sided coating) and comparative examples 70 to 79 (double-sided coating), ink drying property and pencil writing property are insufficient, or transparency, bleeding and pencil writing property are insufficient, and practicality is practical. Absent. In the case of Comparative Examples 21 to 40 (single-sided coating) and Comparative Examples 80 to 99 (double-sided coating) where the silica of the white inorganic pigment is 1.9 μm, which is insufficient in the range of the present invention (3.0 to 15.0 μm). Is pencil writing property or poor transparency and impractical, and in the case of Comparative Examples 51 to 60 (single-sided coating) and Comparative Examples 00 to 119, which is 16.3 μm, which is larger than the range of the present invention, ink drying property and pencil In addition to poor writing performance, there are many cases where there is a problem with bleeding of the image, and it is not practical.
As is apparent from the above, the ink jet recording sheet obtained by the example of the present invention is an ink jet recording sheet that is recorded by using an ink jet recording method printer and plotter with water-based ink. Excellent sharpness, fast ink drying, low image bleeding, stable operation with no wrinkles or blurring, and excellent water resistance of the ink jet recording area. It can be said that an ink jet recording sheet having both characteristics as a two-source drawing sheet and a transparent paper for fancy was obtained.

Claims (5)

透明性の高いシート状支持体の少なくとも一方の面に少なくとも１層以上の層構成からなる塗被層を設けたインクジェット記録シートにおいて、該支持体直上層である第１の塗被層が溶剤系塗工剤であり、その塗工量が０．５〜１０ｇ／ｍ2であり、最表層である第２の塗被層が水系塗工剤であり、該水系塗工剤は水性ウレタン樹脂及び白色無機顔料を主体とし、更にはカチオン性高分子化合物を含むこと、該白色無機顔料がコールターカウンター法で測定される平均粒子径３．０〜１５．０μｍのシリカであり、該水系塗工剤に含まれる水性ウレタン樹脂とシリカの固形分比が３．５：１〜１：３．５であることを特徴とするインクジェット記録シート。 In an inkjet recording sheet in which a coating layer having at least one layer structure is provided on at least one surface of a highly transparent sheet-like support, the first coating layer, which is directly above the support, is a solvent-based recording sheet. It is a coating agent, the coating amount is 0.5 to 10 g / m 2 , the second coating layer which is the outermost layer is an aqueous coating agent, and the aqueous coating agent includes an aqueous urethane resin and A white inorganic pigment as a main component, and further containing a cationic polymer compound, and the white inorganic pigment is silica having an average particle size of 3.0 to 15.0 μm as measured by a Coulter counter method, and the aqueous coating agent An ink jet recording sheet, wherein the solid content ratio of the aqueous urethane resin and silica contained in is 3.5: 1 to 1: 3.5. 水系塗工剤に含まれる水性ウレタン樹脂とシリカの固形分比が３：１〜１：３であることを特徴とする請求項１に記載のインクジェット記録シート。 2. The ink jet recording sheet according to claim 1, wherein the solid content ratio of the aqueous urethane resin and silica contained in the aqueous coating agent is 3: 1 to 1: 3. 上記水系塗工剤中に含まれるカチオン性高分子化合物がポリアミン系樹脂、ジメチルジアリルアンモニウムクロライド系樹脂、エピクロルヒドリン系樹脂、ジシアンジアミド系樹脂、アクリルアミドとジアリルアミン塩酸塩の共重合物の中から１つ以上選ばれてなることを特徴とする請求項１または２に記載のインクジェット記録シート。 The cationic polymer compound contained in the aqueous coating agent is selected from one or more of polyamine resins, dimethyl diallyl ammonium chloride resins, epichlorohydrin resins, dicyandiamide resins, and copolymers of acrylamide and diallylamine hydrochloride. The ink jet recording sheet according to claim 1, wherein the ink jet recording sheet is formed. 上記溶剤系塗工剤が塩化ビニルと酢酸ビニルの共重合体、ポリ酢酸ビニルから選ばれる少なくとも１種類を含有し、その塗工量が１〜５ｇ／ｍ2であることを特徴とする請求項１〜３のいずれか一つに記載のインクジェット記録シート。 The solvent-based coating agent contains at least one selected from a copolymer of vinyl chloride and vinyl acetate and polyvinyl acetate, and the coating amount is 1 to 5 g / m 2. The inkjet recording sheet as described in any one of 1-3. ＪＩＳ Ｐ ８１４９：２０００で測定した不透明度が２０．０％〜６０．０％である請求項１〜４のいずれか一つに記載のインクジェット記録シート。 The inkjet recording sheet according to any one of claims 1 to 4, wherein the opacity measured according to JIS P 8149: 2000 is 20.0% to 60.0%.
JP2004249144A 2004-08-27 2004-08-27 Inkjet recording sheet Expired - Fee Related JP4334443B2 (en)