JP2005219216A - Inkjet recording glossy paper - Google Patents
Inkjet recording glossy paper Download PDFInfo
- Publication number
- JP2005219216A JP2005219216A JP2004026476A JP2004026476A JP2005219216A JP 2005219216 A JP2005219216 A JP 2005219216A JP 2004026476 A JP2004026476 A JP 2004026476A JP 2004026476 A JP2004026476 A JP 2004026476A JP 2005219216 A JP2005219216 A JP 2005219216A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- ink
- glossy
- layer
- pulp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、インクジェット記録用光沢紙に関する。特には、古紙パルプを配合した場合であっても、表面光沢が高く、優れた外観を有するインクジェット記録用光沢紙に関する。 The present invention relates to glossy paper for ink jet recording. In particular, the present invention relates to glossy paper for ink-jet recording having a high surface gloss and an excellent appearance even when used paper pulp is blended.
インクジェット記録方式は、インクの液滴を吐出し、記録紙上にインクを付着させることによりドットを形成して記録を行う方式である。近年、インクジェットプリンター、インクジェット記録用紙が技術的に進歩し、印字品質の高い記録が可能になってきている。
近年においては、水性インクを用いたインクジェット記録方式のプリンターの性能が向上し、記録用紙に対しても高吸収性、忠実なドット再現性、耐水性等の特性が要求されるようになってきている。すなわち、良好なインクジェット印字適性の他に、表面光沢が高く、優れた外観を有するインクジェット記録用光沢紙が要求されている。
The ink jet recording method is a method in which ink droplets are ejected and ink is deposited on recording paper to form dots and perform recording. In recent years, ink jet printers and ink jet recording paper have advanced technically, and recording with high print quality has become possible.
In recent years, the performance of ink jet recording printers that use water-based ink has improved, and characteristics such as high absorbency, faithful dot reproducibility, and water resistance have been required for recording paper. Yes. That is, there is a demand for glossy paper for ink-jet recording having a high surface gloss and an excellent appearance in addition to good ink-jet printability.
一方、近年においては、木材資源の節約や紙をリサイクルさせるという観点から、古紙をパルプ原料として用いることが行われている。インクジェット記録用光沢紙は、上述したように、優れた外観を有することが要求されるため、インクジェット記録用光沢紙に古紙パルプを配合することは行われていなかった。 On the other hand, in recent years, waste paper has been used as a pulp raw material from the viewpoint of saving wood resources and recycling paper. As described above, the glossy paper for ink-jet recording is required to have an excellent appearance, and therefore, waste paper pulp has not been added to the glossy paper for ink-jet recording.
特開２０００−１７３８８８号公報には、サイズ剤を添加して脱墨処理を行った脱墨パルプを配合した原料パルプに微細フィブリル化セルロースを添加して抄造する記録用紙の製造方法が開示されている。該公報に開示された製造方法によれば、得られた記録用紙はインクジェット記録に用いることができ、インクジェット記録する際のフェザーリングの発生を防止することができ、インク乾燥性等に優れた記録用紙が得られることが記載されている。しかし、古紙パルプを配合したインクジェット記録用光沢紙において、更に外観を向上させることが望まれている。 Japanese Patent Application Laid-Open No. 2000-173888 discloses a method for producing a recording paper, in which fine fibrillated cellulose is added to a raw material pulp containing a deinked pulp that has been deinked by adding a sizing agent. Yes. According to the manufacturing method disclosed in the publication, the obtained recording paper can be used for ink jet recording, can prevent the occurrence of feathering during ink jet recording, and has excellent ink drying properties. It is described that paper can be obtained. However, it is desired to further improve the appearance of glossy paper for ink-jet recording containing waste paper pulp.
従って、本発明の目的は、原紙に古紙パルプを配合した場合であっても、良好なインクジェット印刷適性を有すると共に、表面光沢が高く、優れた外観を有するインクジェット記録用光沢紙を提供することにある。 Accordingly, an object of the present invention is to provide a glossy paper for ink-jet recording having good ink-jet printability, high surface gloss and excellent appearance even when used paper pulp is blended with the base paper. is there.
本発明者らは、上記目的を達成すべく鋭意検討した結果、古紙パルプを含有してなる原紙の少なくとも一方の面に、塗工層を設け、該塗工層の上にインク受容層を設け、該インク受容層の上に光沢層を設けたインクジェット記録用光沢紙が上記目的を達成し得ることを見出し、本発明を完成させた。 As a result of intensive studies to achieve the above object, the present inventors have provided a coating layer on at least one surface of a base paper containing waste paper pulp, and provided an ink receiving layer on the coating layer. The inventors have found that a glossy paper for ink-jet recording provided with a glossy layer on the ink receiving layer can achieve the above object, and have completed the present invention.
本発明は上記知見に基づいてなされたものであり、全質量中２０質量％以上の古紙パルプを含有してなる原紙の少なくとも一方の面に、無機顔料及びバインダーを含む塗工液を塗布し、乾燥して得られる塗工層が設けられており、該塗工層の上に、少なくとも一層のインク受容層が設けられており、該インク受容層の上に光沢層が設けられ、該光沢層が高光沢の鏡面仕上形成されているインクジェット記録用光沢紙を提供するものである。
上記インクジェット記録用光沢紙は、古紙パルプを配合したものであるが、良好なインクジェット印刷適性を有すると共に、表面光沢が高く、優れた外観を有するものである。
The present invention has been made on the basis of the above knowledge, and a coating liquid containing an inorganic pigment and a binder is applied to at least one surface of a base paper containing 20% by mass or more of waste paper pulp in the total mass, A coating layer obtained by drying is provided, at least one ink receiving layer is provided on the coating layer, a gloss layer is provided on the ink receiving layer, and the gloss layer is provided. Provides a glossy paper for ink-jet recording having a high gloss mirror finish.
The glossy paper for ink-jet recording is a blend of waste paper pulp, and has good ink-jet printability, high surface gloss, and excellent appearance.
上記インクジェット記録用光沢紙においては、無機顔料及びバインダーを含む塗工液の塗布量が、固形分で５〜４０ｇ／ｍ２であることが好ましい。
上記インクジェット記録用光沢紙の光沢層は、ＪＩＳ−Ｐ８１４２に従い測定された６０度白紙光沢度が２５％以上であることが好ましい。
上記インクジェット記録用光沢紙に配合される上記古紙パルプとしては、新聞古紙、雑誌古紙及び段ボール古紙から選択される少なくとも１種を原料とするパルプが挙げられる。
In the glossy paper for ink jet recording, the coating amount of the coating liquid containing an inorganic pigment and a binder is preferably 5 to 40 g / m 2 in terms of solid content.
The glossy layer of the glossy paper for inkjet recording preferably has a 60 ° white paper glossiness of 25% or more measured according to JIS-P8142.
Examples of the used paper pulp to be blended with the glossy paper for ink jet recording include pulps made from at least one selected from newspaper used paper, magazine used paper and cardboard used paper.
本発明のインクジェット記録用光沢紙は、原紙の少なくとも一方の面に、無機顔料及びバインダーを含む塗工液を塗布し、乾燥して得られる塗工層が設けられており、原紙中に夾雑物が含まれていても、その夾雑物が隠蔽されるので、原紙に古紙パルプを配合した場合であっても、優れた外観を有するものである。また、本発明のインクジェット記録用光沢紙は、良好なインクジェット印刷適性を有すると共に、表面光沢の高いものである。 The glossy paper for ink-jet recording of the present invention is provided with a coating layer obtained by applying a coating liquid containing an inorganic pigment and a binder to at least one surface of a base paper and drying the base paper. Even if it is contained, the contaminants are concealed, so that even when used paper pulp is blended with the base paper, it has an excellent appearance. In addition, the glossy paper for ink jet recording of the present invention has good ink jet printability and high surface gloss.
以下、本発明のインクジェット記録用光沢紙について説明する。
本発明のインクジェット記録用光沢紙は、原紙の少なくとも一方の面に、塗工液を塗布し、乾燥して得られる塗工層が設けられており、該塗工層の上に、少なくとも一層のインク受容層が設けられており、該インク受容層の上に光沢層が設けられている。
Hereinafter, the glossy paper for ink jet recording of the present invention will be described.
The glossy paper for ink-jet recording of the present invention is provided with a coating layer obtained by applying a coating liquid on at least one surface of a base paper and drying, and on the coating layer, at least one layer is provided. An ink receiving layer is provided, and a glossy layer is provided on the ink receiving layer.
本発明のインクジェット記録用光沢紙に用いられる原紙は、全質量中２０質量％以上の古紙パルプを含有してなる。古紙パルプ含有量は好ましくは４０〜１００質量％である。原紙中の古紙パルプ含有量が、全質量中２０質量％以上であると、本発明の効果を十分に発揮することができる。 The base paper used for the glossy paper for ink-jet recording of the present invention comprises 20% by mass or more of waste paper pulp in the total mass. The waste paper pulp content is preferably 40 to 100% by mass. The effect of this invention can fully be exhibited as used paper pulp content in a base paper is 20 mass% or more in the total mass.
本発明のインクジェット記録用光沢紙に用いられる原紙に含まれる古紙パルプは、古紙を離解して得られる。古紙を離解して古紙パルプを得る方法に特に制限はなく、従来公知の方法を特に制限なく用いることができる。例えば、パルパーを用いて実施することができる。 The used paper pulp contained in the base paper used for the glossy paper for ink jet recording of the present invention is obtained by disaggregating used paper. There is no restriction | limiting in particular in the method which disaggregates waste paper and obtains waste paper pulp, A conventionally well-known method can be especially used without a restriction | limiting. For example, it can be implemented using a pulper.
原紙中に含まれる古紙パルプとしては、例えば、新聞古紙、雑誌古紙及び段ボール古紙から選択される少なくとも１種を原料とするパルプが挙げられる。その他、チラシ古紙、塗工紙、非塗工紙、地券、カラー印刷された紙、白黒印刷された紙等を用いてもよい。 Examples of the used paper pulp contained in the base paper include pulp made from at least one selected from newspaper used paper, magazine used paper and cardboard used paper. In addition, used leaflet paper, coated paper, non-coated paper, ground paper, color printed paper, black and white printed paper, or the like may be used.
本発明のインクジェット記録用光沢紙に用いられる原紙を製造するために用いられる、古紙パルプ以外のパルプとしては、例えば、広葉樹クラフトパルプ、天然パルプ、合成パルプ等が挙げられる。天然パルプとしては、通常に製紙用に用いられるパルプであればいずれも使用可能である。すなわち、広葉樹晒クラフトパルプ、針葉樹晒クラフトパルプ、広葉樹未晒クラフトパルプ、針葉樹未晒クラフトパルプ、広葉樹亜硫酸パルプ、針葉樹亜硫酸パルプ等が挙げられる。また、木材繊維を含む主原料として、化学的に処理されたパルプ、木材以外の繊維原料であるケナフ、麻、葦等非木材繊維を主原料として化学的に処理されたパルプやチップを機械的にパルプ化したグランドパルプ、木材またはチップに化学薬品を添加しながら機械的にパルプ化したケミグランドパルプ、及びチップを柔らかくなるまで蒸解した後、レファイナー等でパルプ化したセミケミカルパルプ等のバージンパルプ等が挙げられる。 Examples of pulps other than waste paper pulp used for producing the base paper used for the glossy paper for ink jet recording of the present invention include hardwood kraft pulp, natural pulp, and synthetic pulp. Any natural pulp can be used as long as it is usually used for papermaking. That is, examples include hardwood bleached kraft pulp, softwood bleached kraft pulp, hardwood unbleached kraft pulp, softwood unbleached kraft pulp, hardwood sulfite pulp, and conifer sulfite pulp. In addition, chemically treated pulp and non-wood fiber raw materials such as kenaf, hemp, cocoon and other non-wood fibers as the main raw materials are mechanically used as the main raw materials containing wood fibers. Virgin pulp, such as ground pulp, pulp that has been mechanically pulped while adding chemicals to wood or chips, and semi-chemical pulp that has been pulped with a refiner after cooking the chips until soft Etc.
本発明のインクジェット記録用光沢紙に用いられる原紙は、上記パルプを用いて抄紙して製造される。抄紙は、例えば、長網抄紙機、ツインワイヤー抄紙機、オントップ抄紙機、ハイブリッド抄紙機又は丸網抄紙機等の抄紙機を用いて抄紙される。抄紙する際には、パルプに、インクジェット記録用光沢紙を製造する際に通常に用いられる添加剤を添加してもよい。このような添加剤としては、例えばポリアクリルアミド、ポリビニルアルコール系高分子、尿素／ホルマリン樹脂、メラミン／ホルマリン樹脂、澱粉等の紙力増強剤；硫酸バンド等の薬品定着剤、ポリアクリルアミド、アクリルアミド／アミノメチルアクリルアミドの共重合物の塩、カチオン化澱粉、ポリエチレンイミン、ポリエチレンオキサイド、アクリルアミド／アクリル酸ナトリウム共重合物等の濾水性あるいは歩留まり向上剤；ロジンサイズ、アルキルケテンダイマー（ＡＫＤ）、アルケニル無水コハク酸（ＡＳＡ）等のサイズ剤；ポリアミド、ポリアミン、エピクロルヒドリン等の耐水化剤；消泡剤、タルク等の填料；染料；色顔料；抗菌剤；紫外線防止剤；ｐＨ調整剤等が挙げられる。 The base paper used for the glossy paper for ink jet recording of the present invention is produced by making paper using the above pulp. The paper is made using, for example, a paper machine such as a long paper machine, a twin wire paper machine, an on-top paper machine, a hybrid paper machine, or a round paper machine. When making paper, additives commonly used in producing glossy paper for inkjet recording may be added to the pulp. Examples of such additives include polyacrylamide, polyvinyl alcohol polymer, urea / formalin resin, melamine / formalin resin, paper strength enhancer such as starch; chemical fixing agent such as sulfuric acid band, polyacrylamide, acrylamide / amino. Freeness or yield improver such as methyl acrylamide copolymer salt, cationized starch, polyethyleneimine, polyethylene oxide, acrylamide / sodium acrylate copolymer; rosin size, alkyl ketene dimer (AKD), alkenyl succinic anhydride Sizing agents such as (ASA); waterproofing agents such as polyamide, polyamine, epichlorohydrin; fillers such as antifoaming agents and talc; dyes; color pigments; antibacterial agents;
本発明のインクジェット記録用光沢紙において、原紙の少なくとも一方の面に塗布される塗工液に含まれる無機顔料としては、例えば、カオリン、タルク、軽質炭酸カルシウム、炭酸マグネシウム、カ硫酸バリウム、珪酸アルミニウム、珪酸マグネシウム、合成非晶質シリカ、コロイダルシリカ、アルミナ、アルミナとシリカとの複合体、ゼオライト、珪藻土、水酸化マグネシウム、ハイドロキシアパタイト、マイカ、酸化チタン、クレー、酸化亜鉛、チタン酸鉛等が挙げられる。上記無機顔料の中でも、古紙パルプに由来する夾雑物を隠蔽するという観点から、特に好ましいものは酸化チタンである。また、上記無機顔料は、その平均粒径が１００〜５００ｎｍのものが好ましく、２００〜５００ｎｍのものが更に好ましい。また、そのＢＥＴ比表面積は１０〜４０ｍ２／ｇであることが好ましく、１０〜３０ｍ２／ｇであることが更に好ましい。上記無機顔料は単独で用いてもよく、２種以上を混合して用いてもよい。 In the glossy paper for ink-jet recording of the present invention, examples of the inorganic pigment contained in the coating liquid applied to at least one surface of the base paper include kaolin, talc, light calcium carbonate, magnesium carbonate, barium casulfate, and aluminum silicate. , Magnesium silicate, synthetic amorphous silica, colloidal silica, alumina, composite of alumina and silica, zeolite, diatomaceous earth, magnesium hydroxide, hydroxyapatite, mica, titanium oxide, clay, zinc oxide, lead titanate, etc. It is done. Among the inorganic pigments, titanium oxide is particularly preferable from the viewpoint of concealing impurities derived from waste paper pulp. The inorganic pigment preferably has an average particle size of 100 to 500 nm, more preferably 200 to 500 nm. Moreover, it is preferable that the BET specific surface area is 10-40 m < 2 > / g, and it is still more preferable that it is 10-30 m < 2 > / g. The said inorganic pigment may be used independently and may be used in mixture of 2 or more types.
また、塗工液に含まれるバインダーとしては、例えば、ポリビニルアルコール、ポリビニルアセタール、酸化澱粉、エーテル化澱粉、カルボキシメチルセルロース、ヒドロキシエチルセルロース、カゼイン、ゼラチン、大豆タンパク、ポリエチレンイミド系樹脂、ポリアクリル酸またはその共重合体、無水マレイン酸共重合体、アクリルアミド系樹脂、アクリル酸エステル系樹脂、ポリアミド系樹脂、ポリウレタン系樹脂、ポリエステル系樹脂、ポリビニールブチラール系樹脂、アルキッド樹脂、エポキシ系樹脂、エピクロルヒドリン系樹脂、尿素樹脂、メラミン樹脂、スチレンーブタジエン共重合体、メチルメタクリレートーブタジエン共重合体、アクリル酸エステル、メタアクリル酸エステルの重合体または共重合体等のアクリル系重合体ラテックス類、エチレンー酢酸ビニル共重合体等のビニル系重合体ラテックス類の樹脂類等が挙げられる。上記バインダーの中でも、古紙パルプに由来する夾雑物を隠蔽するという観点から、好ましいものはスチレン‐ブタジエン共重合体である。上記バインダーは単独で用いてもよく、２種以上を混合して用いてもよい。 Examples of the binder contained in the coating solution include polyvinyl alcohol, polyvinyl acetal, oxidized starch, etherified starch, carboxymethyl cellulose, hydroxyethyl cellulose, casein, gelatin, soy protein, polyethyleneimide resin, polyacrylic acid or the like. Copolymer, maleic anhydride copolymer, acrylamide resin, acrylate resin, polyamide resin, polyurethane resin, polyester resin, polyvinyl butyral resin, alkyd resin, epoxy resin, epichlorohydrin resin, Acrylic polymerization such as urea resin, melamine resin, styrene-butadiene copolymer, methyl methacrylate-butadiene copolymer, acrylic ester, methacrylic ester polymer or copolymer Latexes, resins, and the like of the vinyl polymer latexes such as ethylene-vinyl acetate copolymer. Among the above binders, a styrene-butadiene copolymer is preferable from the viewpoint of concealing impurities derived from waste paper pulp. The said binder may be used independently and may mix and use 2 or more types.
塗工液中の無機顔料及びバインダーの配合割合は、無機顔料１００質量部に対して、バインダー５〜２０質量部程度が好ましい。バインダーの割合が無機顔料１００質量部に対して５質量部未満であると、塗工層強度が不足する場合があり、一方、２０質量部より多いとインクジェットインク吸収性が損なわれる場合がある。 The blending ratio of the inorganic pigment and binder in the coating liquid is preferably about 5 to 20 parts by mass of the binder with respect to 100 parts by mass of the inorganic pigment. When the proportion of the binder is less than 5 parts by mass with respect to 100 parts by mass of the inorganic pigment, the coating layer strength may be insufficient. On the other hand, when it exceeds 20 parts by mass, the ink-jet ink absorbability may be impaired.
塗工液には必用に応じて、種々の助剤を添加してもよい。助剤としては、例えば、分散剤、保水剤、増粘剤、消泡剤、防腐剤、染料、耐水化剤、蛍光染料、保存剤、紫外線吸収剤、離型剤、潤滑剤及び有機カチオン剤等が挙げられる。
塗工液の塗布方法としては、特に制限はないが、例えばエアーナイフ、ロールコーター、バーコーター、コンマコーター、ブレードコーター等の公知の塗工機を用いて塗工することができる。塗工液の塗工量は固形分換算で、好ましくは５〜４０ｇ／ｍ２であり、更に好ましくは５〜１５ｇ／ｍ２である。塗工液の塗工量が５ｇ／ｍ２未満であると、夾雑物を隠蔽する効果が向上しない場合があり、一方、４０ｇ／ｍ２を超えると塗工層強度が不足する場合がある。
Various auxiliary agents may be added to the coating liquid as necessary. Examples of auxiliary agents include dispersants, water retention agents, thickeners, antifoaming agents, antiseptics, dyes, water resistance agents, fluorescent dyes, preservatives, ultraviolet absorbers, mold release agents, lubricants and organic cation agents. Etc.
Although there is no restriction | limiting in particular as a coating method of a coating liquid, For example, it can coat using well-known coating machines, such as an air knife, a roll coater, a bar coater, a comma coater, a blade coater. The coating amount of the coating liquid in terms of solid content, preferably 5 to 40 g / m 2, more preferably from 5 to 15 g / m 2. When the coating amount of the coating liquid is less than 5 g / m 2 , the effect of concealing impurities may not be improved. On the other hand, when it exceeds 40 g / m 2 , the coating layer strength may be insufficient.
上記塗工液は、通常は水性塗工液として調製される。
塗工液を塗布した後に塗工液を乾燥して、塗工層とするが、この乾燥工程における乾燥方式には特に制限はなく、例えば、赤外線乾燥、熱風乾燥、常温乾燥等が挙げられ、乾燥方式は、適宜選択して用いることができる。
上述のようにして得られる塗工層は、原紙の少なくとも一方の面に設けられるが、両面に設けられていてもよい。
本発明のインクジェット記録用光沢紙は、上述したように、原紙の少なくとも一方の面に塗工層が設けられており、このため、原紙中に含まれる、古紙パルプに由来する夾雑物を隠蔽することが可能となる。
The coating solution is usually prepared as an aqueous coating solution.
After coating the coating liquid, the coating liquid is dried to form a coating layer, but the drying method in this drying process is not particularly limited, and examples include infrared drying, hot air drying, and room temperature drying. The drying method can be appropriately selected and used.
The coating layer obtained as described above is provided on at least one side of the base paper, but may be provided on both sides.
As described above, the glossy paper for ink-jet recording of the present invention is provided with a coating layer on at least one surface of the base paper, and thus conceals the impurities derived from the waste paper pulp contained in the base paper. It becomes possible.
次いで、塗工層の上に設けられるインク受容層について説明する。
インク受容層は、インクを吸収乾燥するための層であり、無機顔料及びバインダーを含んでなる。無機顔料及びバインダーとしては、上記塗工層において説明したものと同様のものが使用可能である。インク受容層に含まれる無機顔料の中でも、インクを吸収乾燥するために好ましいものは、上記の中でも合成非晶質シリカ、コロイダルシリカ、アルミナ である。また、上記無機顔料は、その平均粒径が２．５〜９．０μｍのものが好ましく、４．０〜８．５μｍのものが更に好ましい。また、そのＢＥＴ比表面積は２００〜４００ｍ２／ｇであることが好ましく、２５０〜３５０ｍ２／ｇであることが更に好ましい。上記無機顔料は単独で用いてもよく、２種以上を混合して用いてもよい。
また、インク受容層に含まれるバインダーの中でも、インクを吸収乾燥するために好ましいものはポリビニルアルコール、ポリウレタン系樹脂、エチレン−酢酸ビニル共重合体 である。
Next, the ink receiving layer provided on the coating layer will be described.
The ink receiving layer is a layer for absorbing and drying ink, and includes an inorganic pigment and a binder. As an inorganic pigment and a binder, the thing similar to what was demonstrated in the said coating layer can be used. Among the inorganic pigments contained in the ink receiving layer, synthetic amorphous silica, colloidal silica, and alumina are preferable for absorbing and drying the ink. The inorganic pigment preferably has an average particle size of 2.5 to 9.0 μm, more preferably 4.0 to 8.5 μm. Moreover, it is preferable that the BET specific surface area is 200-400 m < 2 > / g, and it is still more preferable that it is 250-350 m < 2 > / g. The said inorganic pigment may be used independently and may be used in mixture of 2 or more types.
Among binders contained in the ink receiving layer, polyvinyl alcohol, polyurethane resin, and ethylene-vinyl acetate copolymer are preferable for absorbing and drying the ink.
インク受容層は、上記無機顔料及びバインダーを含有する、インク受容層を形成する塗工液を、上記塗工層上に塗布し、乾燥させることによって形成される。インク受容層を形成する塗工液中の無機顔料及びバインダーの配合割合に特に制限はないが、無機顔料及びバインダーの配合割合は、無機顔料１００質量部に対して、バインダー５〜３０質量部程度が好ましい。バインダーの割合が無機顔料１００質量部に対して５質量部未満であると、塗工層強度が不足する場合があり、一方、３０質量部より多いとインクジェットインク吸収性が損なわれる場合がある。
また、インク受容層を形成する塗工液には、必用に応じて、分散剤、保水剤、増粘剤、消泡剤、防腐剤、染料、耐水化剤、蛍光染料、保存剤、紫外線吸収剤、離型剤、潤滑剤及び有機カチオン剤等の助剤を添加してもよい。
The ink receiving layer is formed by applying a coating liquid containing the inorganic pigment and the binder to form the ink receiving layer on the coating layer and drying. The blending ratio of the inorganic pigment and binder in the coating liquid for forming the ink receiving layer is not particularly limited, but the blending ratio of the inorganic pigment and binder is about 5 to 30 parts by weight of the binder with respect to 100 parts by weight of the inorganic pigment. Is preferred. When the proportion of the binder is less than 5 parts by mass with respect to 100 parts by mass of the inorganic pigment, the coating layer strength may be insufficient. On the other hand, when it exceeds 30 parts by mass, the ink-jet ink absorbability may be impaired.
In addition, the coating liquid for forming the ink-receiving layer includes a dispersant, a water retention agent, a thickening agent, an antifoaming agent, a preservative, a dye, a water-resistant agent, a fluorescent dye, a preservative, and an ultraviolet absorber as necessary. Auxiliaries such as agents, mold release agents, lubricants and organic cation agents may be added.
インク受容層を形成する塗工液の塗布方法としては、特に制限はないが、例えばエアーナイフ、ロールコーター、バーコーター、コンマコーター、ブレードコーター等の公知の塗工機を用いて塗工することができる。塗工液の塗工量は固形分換算で、好ましくは５〜２０ｇ／ｍ２である。インク受容層を形成する塗工液の塗工量が５ｇ／ｍ２未満であると、インクジェットインク吸収性が不足する場合があり、一方、２０ｇ／ｍ２を超えると塗工層強度が不足する場合がある。 The application method of the coating liquid for forming the ink receiving layer is not particularly limited, and for example, coating may be performed using a known coating machine such as an air knife, roll coater, bar coater, comma coater, blade coater, etc. Can do. The coating amount of the coating solution is preferably 5 to 20 g / m 2 in terms of solid content. When the coating amount of the coating liquid for forming the ink receiving layer is less than 5 g / m 2 , the ink-jet ink absorbability may be insufficient. On the other hand, when it exceeds 20 g / m 2 , the coating layer strength is insufficient. There is a case.
上記塗工液は、通常は水性塗工液として調製される。
インク受容層を形成する塗工液を塗布した後に塗工液を乾燥して、インク受容層とするが、この乾燥工程における乾燥方式には特に制限はなく、例えば、赤外線乾燥、熱風乾燥、常温乾燥等が挙げられ、乾燥方式は、適宜選択して用いることができる。
上述のようにして得られるインク受容層は、塗工層の上に少なくとも一層設けられる。インク受容層は、２層以上設けられてもよいが、通常は一層のみ設けられる。
The coating solution is usually prepared as an aqueous coating solution.
After applying the coating liquid for forming the ink receiving layer, the coating liquid is dried to form an ink receiving layer. However, there is no particular limitation on the drying method in this drying process, for example, infrared drying, hot air drying, room temperature Drying etc. are mentioned, and the drying method can be appropriately selected and used.
At least one ink receiving layer obtained as described above is provided on the coating layer. Two or more ink receiving layers may be provided, but usually only one layer is provided.
次に、インク受容層の上に設けられる光沢層について説明する。本発明のインクジェット記録用光沢紙に設けられる光沢層は、高光沢の鏡面仕上形成されてなるものである。
光沢層を鏡面仕上形成する方法としては、インク受容層の上に、光沢層用塗工液を塗工して、乾燥させた後に、スーパーカレンダー等によって平滑化処理を施すこともできる。ただし、該塗工層が湿潤状態にある間に加熱された鏡面ドラムに圧接、乾燥して仕上げる方法（ウェットキャスト方式）、又は該塗工層を一旦乾燥した後、再湿潤し、加熱された鏡面ドラムに圧接、乾燥して仕上げる方法（リウェットキャスト方式）が、優れた光沢とインク吸収性とを備えるインクジェット記録用光沢紙を得ることができるため好ましい。加熱された鏡面ドラムに光沢層用塗工液を直接塗工して、該塗工層がある程度湿潤状態にある間にインク受容層に圧接、乾燥して仕上げる方法（プレキャスト方式）であってもよい。
Next, the glossy layer provided on the ink receiving layer will be described. The gloss layer provided on the glossy paper for ink-jet recording of the present invention is formed with a high gloss mirror finish.
As a method for forming the glossy layer with a mirror finish, it is possible to apply a glossy layer coating solution on the ink receiving layer and dry it, followed by a smoothing process using a super calender or the like. However, a method in which the coating layer is pressed against a heated mirror drum while it is in a wet state and dried to finish (wet cast method), or after the coating layer is once dried, it is rewet and heated. A method of finishing by press-contacting and drying on a mirror drum (rewet casting method) is preferable because glossy paper for ink-jet recording having excellent gloss and ink absorbability can be obtained. Even when the glossy layer coating liquid is directly applied to a heated mirror drum, and the ink receiving layer is pressed and dried while the coating layer is in a certain wet state (precast method). Good.
光沢層を形成させるために用いられる、光沢層用塗工液は、無機顔料及びバインダーを含有する。無機顔料及びバインダーとしては、上記塗工層において説明したものと同様のものが使用可能である。光沢層用塗工液に含ませる無機顔料の中で好ましいものは、合成非晶質シリカ、コロイダルシリカ、アルミナである。である。また、上記無機顔料は、その平均粒径が１０〜７０ｎｍのものが好ましく、１０〜５０ｎｍのものが更に好ましい。また、そのＢＥＴ比表面積は１００〜３００ｍ２／ｇであることが好ましく、１００〜２００ｍ２／ｇであることが更に好ましい。上記無機顔料は単独で用いてもよく、２種以上を混合して用いてもよい。 The coating liquid for glossy layer used for forming the glossy layer contains an inorganic pigment and a binder. As an inorganic pigment and a binder, the thing similar to what was demonstrated in the said coating layer can be used. Among the inorganic pigments to be included in the gloss layer coating solution, synthetic amorphous silica, colloidal silica, and alumina are preferable. It is. The inorganic pigment preferably has an average particle size of 10 to 70 nm, more preferably 10 to 50 nm. Moreover, it is preferable that the BET specific surface area is 100-300 m < 2 > / g, and it is still more preferable that it is 100-200 m < 2 > / g. The said inorganic pigment may be used independently and may be used in mixture of 2 or more types.
また、光沢層用塗工液に含ませるバインダーの中で好ましいものはポリビニルアルコール、ポリウレタン系樹脂、エチレン−酢酸ビニル共重合体である。光沢層を形成するための塗工液中の無機顔料及びバインダーの配合割合は、無機顔料１００質量部に対して、バインダー ５〜２０質量部程度が好ましい。バインダーの割合が無機顔料１００質量部に対して５質量部未満であると、塗工層強度が不足する場合があり、一方、２０質量部より多いとインクジェットインク吸収性が不足する場合がある。光沢層用塗工液には、必用に応じて、分散剤、保水剤、増粘剤、消泡剤、防腐剤、染料、耐水化剤、蛍光染料、保存剤、紫外線吸収剤、離型剤、潤滑剤及び有機カチオン剤等の助剤を添加してもよい。 Among the binders to be included in the gloss layer coating liquid, polyvinyl alcohol, polyurethane resin, and ethylene-vinyl acetate copolymer are preferable. The blending ratio of the inorganic pigment and the binder in the coating liquid for forming the gloss layer is preferably about 5 to 20 parts by mass of the binder with respect to 100 parts by mass of the inorganic pigment. When the ratio of the binder is less than 5 parts by mass with respect to 100 parts by mass of the inorganic pigment, the coating layer strength may be insufficient. On the other hand, when it is more than 20 parts by mass, the ink-jet ink absorbability may be insufficient. For the coating liquid for glossy layer, dispersant, water retention agent, thickener, antifoaming agent, preservative, dye, water resistance agent, fluorescent dye, preservative, UV absorber, mold release agent Auxiliaries such as lubricants and organic cation agents may be added.
光沢層用塗工液の塗布方法としては、特に制限はないが、例えばエアーナイフ、ロールコーター、バーコーター、コンマコーター、ブレードコーター等の公知の塗工機を用いて塗工することができる。塗工液の塗工量は固形分換算で、好ましくは５〜１５／ｍ２である。光沢層を形成する塗工液の塗工量が５ｇ／ｍ２未満であると、高光沢度が得られない場合があり、一方、１５ｇ／ｍ２を超えると塗工層強度が不足する場合がある。 The method for applying the coating solution for the gloss layer is not particularly limited, and for example, it can be applied using a known coating machine such as an air knife, roll coater, bar coater, comma coater, blade coater or the like. The coating amount of the coating solution is preferably 5 to 15 / m 2 in terms of solid content. When the coating amount of the coating liquid for forming the gloss layer is less than 5 g / m 2 , high glossiness may not be obtained. On the other hand, when it exceeds 15 g / m 2 , the coating layer strength is insufficient. There is.
本発明のインクジェット記録用光沢紙は、光沢層の、ＪＩＳ−Ｐ８１４２に従い測定された６０度白紙光沢度が、好ましくは２５％以上であり、更に好ましくは３０％以上である。本発明のインクジェット記録用光沢紙は、写真の記録用として用いられるため、ＪＩＳ−Ｐ８１４２に従い測定された６０度白紙光沢度は、２５％未満であると、上記用途として好ましくない場合がある。
本発明のインクジェット記録用光沢紙の光沢層の、ＪＩＳ−Ｐ８１４２に従い測定された６０度白紙光沢度を上記範囲とする方法に特に制限はないが、光沢層を鏡面仕上することによって、光沢度を上記範囲とすることが可能である。
In the glossy paper for ink-jet recording of the present invention, the glossiness of the 60 ° white paper measured in accordance with JIS-P8142 is preferably 25% or more, more preferably 30% or more. Since the glossy paper for inkjet recording of the present invention is used for recording a photograph, if the 60 ° white paper glossiness measured in accordance with JIS-P8142 is less than 25%, it may not be preferable for the above applications.
There is no particular limitation on the method for setting the glossiness of the glossy layer of the glossy paper for ink jet recording of the present invention within the above range to the 60 ° white paper glossiness measured according to JIS-P8142, but the glossiness can be improved by mirror finishing the glossy layer. It is possible to be in the above range.
本発明のインクジェット記録用光沢紙は、原紙の少なくとも一方の面に、無機顔料及びバインダーを含む塗工液を塗布し、乾燥して得られる塗工層が設けられており、原紙中に古紙パルプが含まれ、夾雑物が混入していても、その夾雑物が隠蔽され、優れた外観を有するものとなる。また、本発明のインクジェット記録用光沢紙は光沢層が鏡面仕上形成されており、表面光沢の高いものである。 The glossy paper for ink-jet recording of the present invention is provided with a coating layer obtained by applying a coating liquid containing an inorganic pigment and a binder to at least one surface of a base paper and drying it. Even if impurities are mixed, the impurities are concealed and have an excellent appearance. The glossy paper for ink-jet recording of the present invention has a glossy layer with a mirror finish, and has a high surface gloss.
以下に、実施例を示し、本発明をさらに具体的に説明するが、本発明はこれに限定されるものではない。なお、以下の実施例において、％は、特に断りのない限り質量％を表す。 Hereinafter, the present invention will be described more specifically with reference to examples. However, the present invention is not limited thereto. In the following examples, “%” represents “% by mass” unless otherwise specified.
実施例１
新聞古紙及びチラシ古紙をそれぞれ５０％ずつ配合した古紙をパルパーにて離解、脱墨処理して得た古紙パルプ４０％と、ＬＢＫＰ６０％とを配合してパルプ原料を得た。
上述のようにして得られたパルプ原料１００部に対し、硫酸バンド３部、サイズ剤１０部及びタルク１０部を配合し、長網抄紙機にて抄造、サイズプレスにて紙面に澱粉を塗布し、原紙を得た。
Example 1
A pulp raw material was obtained by blending 40% of waste paper pulp obtained by disaggregating and deinking waste paper containing 50% each of waste newspaper and leaflet waste paper with a pulper, and 60% LBKP.
To 100 parts of the pulp raw material obtained as described above, 3 parts of a sulfuric acid band, 10 parts of a sizing agent and 10 parts of talc are blended, made with a long paper machine, and starch is applied to the paper surface with a size press. I got a base paper.
酸化チタン（チタン工業（株）製、ＫＡ−１０、粒径：４００nm、ＢＥＴ比表面積：１６ｍ２／ｇ）１００部、及びＳＢＲラテックス（日本エイアンドエル（株）製、ＰＡ−９１９０）１５部からなる塗工液をエアナイフコーターを用いて、上述のようにして得られた原紙上に、固形分換算で１５ｇ／ｍ２塗工し、スキャッフドライヤーにて乾燥し、塗工層を設けた。 It consists of 100 parts of titanium oxide (made by Titanium Industry Co., Ltd., KA-10, particle size: 400 nm, BET specific surface area: 16 m 2 / g), and 15 parts of SBR latex (manufactured by Nippon A & L Co., Ltd., PA-9190). The coating liquid was coated on the base paper obtained as described above using an air knife coater at 15 g / m 2 in terms of solid content and dried with a scuff dryer to provide a coating layer.
次いで、シリカ（（株）トクヤマ製、シリカファインシールＸ４５、粒径：４.５μｍ、ＢＥＴ比表面積：３００ｍ２／ｇ）１００部、水酸化ナトリウム１部、ポリビニルアルコール（クラレ（株）製、ＰＶＡ１１７）１５部、及びインク定着剤（住友化学工業（株）製、ＳＲ１００１）５部からなる塗工液をエアナイフコーターを用いて、上述のようにして設けられた塗工層上に固形分換算で１０ｇ／ｍ２塗工し、スキャッフドライヤーにて乾燥し、インク受容層を設けた。 Next, silica (made by Tokuyama Corporation, silica fine seal X45, particle size: 4.5 μm, BET specific surface area: 300 m 2 / g) 100 parts, sodium hydroxide 1 part, polyvinyl alcohol (made by Kuraray Co., Ltd., PVA117) ) 15 parts of an ink fixing agent (manufactured by Sumitomo Chemical Co., Ltd., SR1001) using an air knife coater, the coating liquid consisting of 5 parts is converted into solid content on the coating layer provided as described above. 10 g / m 2 was applied and dried with a scuff dryer to provide an ink receiving layer.
次いで、コロイダルシリカ（日産化学工業（株）製、コロイダルシリカスノーテックスＸＬ、粒径：５０ｎｍ、ＢＥＴ比表面積：１００ｍ２／ｇ）１００部、アクリル樹脂（日本ＮＳＣ（株）製、ＫＥ３５）５部、ポリビニルアルコール（クラレ（株）製、ＰＶＡ１１７）１０部、インク定着剤（昭和高分子（株）製、ポリフィックス７００）５部からなる塗工液をエアナイフコーターを用いて、上述のようにして設けられたインク受容層上に固形分換算で１０ｇ／ｍ２塗工し、スキャッフドライヤーにて乾燥し、次いで乾燥した層を水で再湿潤し、１００℃に加熱したキャストドラムに圧着乾燥させ、高光沢の鏡面仕上を行い、光沢層を形成し、インクジェット記録用光沢紙を得た。 Next, colloidal silica (manufactured by Nissan Chemical Industries, Ltd., colloidal silica snowtex XL, particle size: 50 nm, BET specific surface area: 100 m 2 / g) 100 parts, acrylic resin (manufactured by NSC Japan, KE35) 5 parts The coating liquid consisting of 10 parts of polyvinyl alcohol (manufactured by Kuraray Co., Ltd., PVA117) and 5 parts of ink fixing agent (manufactured by Showa Polymer Co., Ltd., Polyfix 700) was used as described above using an air knife coater. Apply 10 g / m 2 in terms of solid content on the provided ink receiving layer, dry it with a scuff dryer, then re-wet the dried layer with water, press dry on a cast drum heated to 100 ° C A glossy layer was formed by performing a high gloss mirror finish to obtain a glossy paper for ink jet recording.
得られたインクジェット記録用光沢紙について下記評価方法により評価を行った。結果を表１に示す。
（１）６０度白紙光沢度
ＪＩＳ−Ｐ８１４２で規定される方法に従って測定した。
（２）外観試験
ＪＩＳ−Ｐ８２０８で規定される夾雑物測定方法に従って測定した。結果は、インクジェット記録用紙１ｍ２当たりの夾雑物の面積で表した。
The obtained glossy paper for ink jet recording was evaluated by the following evaluation method. The results are shown in Table 1.
(1) 60 degree white paper glossiness It measured according to the method prescribed | regulated by JIS-P8142.
(2) Appearance test It measured according to the foreign substance measuring method prescribed | regulated by JIS-P8208. The results were expressed as the area of impurities per 1 m 2 of inkjet recording paper.
実施例２
原紙パルプを古紙パルプ２０％、及びＬＢＫＰ８０％とした以外は、実施例１と同様に操作を行い、インクジェット記録用光沢紙を得た。得られたインクジェット記録用紙の評価を実施例１と同様にして行った。その結果を表１に示す。
Example 2
Glossy paper for ink-jet recording was obtained in the same manner as in Example 1 except that the base paper pulp was 20% used paper pulp and LBKP 80%. The obtained inkjet recording paper was evaluated in the same manner as in Example 1. The results are shown in Table 1.
実施例３
原紙パルプを古紙パルプ６０％、及びＬＢＫＰ４０％とした以外は、実施例１と同様に操作を行い、インクジェット記録用光沢紙を得た。得られたインクジェット記録用紙の評価を実施例１と同様にして行った。その結果を表１に示す。
Example 3
Glossy paper for inkjet recording was obtained in the same manner as in Example 1 except that the raw paper pulp was changed to 60% used paper pulp and 40% LBKP. The obtained inkjet recording paper was evaluated in the same manner as in Example 1. The results are shown in Table 1.
実施例４
原紙パルプを古紙パルプ８０％、及びＬＢＫＰ２０％とした以外は、実施例１と同様に操作を行い、インクジェット記録用光沢紙を得た。得られたインクジェット記録用紙の評価を実施例１と同様にして行った。その結果を表１に示す。
Example 4
Glossy paper for ink-jet recording was obtained in the same manner as in Example 1 except that the base paper pulp was changed to 80% used paper pulp and 20% LBKP. The obtained inkjet recording paper was evaluated in the same manner as in Example 1. The results are shown in Table 1.
実施例５
原紙パルプを古紙パルプ１００％とした以外は、実施例１と同様に操作を行い、インクジェット記録用光沢紙を得た。得られたインクジェット記録用紙の評価を実施例１と同様にして行った。その結果を表１に示す。
Example 5
A glossy paper for ink-jet recording was obtained in the same manner as in Example 1 except that the raw paper pulp was changed to 100% used paper pulp. The obtained inkjet recording paper was evaluated in the same manner as in Example 1. The results are shown in Table 1.
比較例１
無機顔料及びバインダーを含む塗工層を設けない以外は、実施例１と同様に操作を行い、インクジェット記録用光沢紙を得た。得られたインクジェット記録用紙の評価を実施例１と同様にして行った。その結果を表１に示す。
Comparative Example 1
A glossy paper for ink jet recording was obtained in the same manner as in Example 1 except that a coating layer containing an inorganic pigment and a binder was not provided. The obtained inkjet recording paper was evaluated in the same manner as in Example 1. The results are shown in Table 1.
比較例２
無機顔料及びバインダーを含む塗工層を設けない以外は、実施例５と同様に操作を行い、インクジェット記録用光沢紙を得た。得られたインクジェット記録用紙の評価を実施例１と同様にして行った。その結果を表１に示す。
Comparative Example 2
Glossy paper for ink-jet recording was obtained in the same manner as in Example 5 except that a coating layer containing an inorganic pigment and a binder was not provided. The obtained inkjet recording paper was evaluated in the same manner as in Example 1. The results are shown in Table 1.
表１から明らかなように、実施例１〜実施例５のインクジェット記録用光沢紙は、６０度白紙光沢度が高く、夾雑物が少なく、優れた外観を有するものである。
比較例１及び比較例２のインクジェット記録用光沢紙は、夾雑物が多く見られ、外観に劣るものである。
As can be seen from Table 1, the glossy paper for ink-jet recording of Examples 1 to 5 has a high 60 degree white paper glossiness, little impurities, and an excellent appearance.
The glossy paper for ink-jet recording of Comparative Example 1 and Comparative Example 2 has many impurities and is inferior in appearance.
Claims (4)
該塗工層の上に、少なくとも一層のインク受容層が設けられており、
該インク受容層の上に光沢層が設けられ、該光沢層が高光沢の鏡面仕上形成されているインクジェット記録用光沢紙。 A coating layer obtained by applying and drying a coating liquid containing an inorganic pigment and a binder is provided on at least one surface of a base paper containing 20% by mass or more of waste paper pulp in the total mass,
At least one ink receiving layer is provided on the coating layer,
A glossy paper for ink-jet recording, wherein a glossy layer is provided on the ink receiving layer, and the glossy layer is formed with a high gloss mirror finish.
The glossy paper for ink-jet recording according to any one of claims 1 to 3, wherein the waste paper pulp is a pulp made from at least one selected from newspaper waste paper, magazine waste paper and cardboard waste paper.