JP2005164517A - Composition for producing replica of skin - Google Patents
Composition for producing replica of skin Download PDFInfo
- Publication number
- JP2005164517A JP2005164517A JP2003406909A JP2003406909A JP2005164517A JP 2005164517 A JP2005164517 A JP 2005164517A JP 2003406909 A JP2003406909 A JP 2003406909A JP 2003406909 A JP2003406909 A JP 2003406909A JP 2005164517 A JP2005164517 A JP 2005164517A
- Authority
- JP
- Japan
- Prior art keywords
- composition
- mass
- parts
- polyvinyl
- replica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、皮膚のレプリカ作成に好適な組成物に関し、更に詳細には、その硬化速度及び皮膚立体形状の転写において優れる、皮膚レプリカ作成用の組成物に関する。 The present invention relates to a composition suitable for skin replica creation, and more particularly to a composition for skin replica creation, which is excellent in its curing rate and transfer of skin three-dimensional shape.
皮膚機能を非侵襲的に計測する手段として、高分子を皮膚の形状に即して変形固化させ、形状転写する所謂「レプリカ」を用いて観察を行うことは、非常に有用であり、これを利用した種々の皮膚状態の鑑別法や、化粧料の選択法等が考案されている。（例えば、特許文献１、特許文献２、特許文献３を参照）この「レプリカ」の基本技術は比較的古くから存するが、どの様に忠実に皮膚の立体形状を転写するかが技術的課題であり、当初のプラスチック板の溶剤による一部融解、再固化を利用した方法から、粘ちょう性の被膜形成組成物を固化させる方法に転じたことで大きな飛躍を見た。この様な方法の開発により、手技が極めて容易になり、素人が手軽にレプリカの作成が出来るようになった為である。現在では、販売現場に於けるカウンセリングツールにも使用されるようになっている。この様な状況の中で、かかるレプリカ剤において、課題になっていることは、速やかにカウンセリングなどに生かせるように、作成に要する時間、言い換えれば固化時間を短縮化することであり、その目的から、ポリビニルアルコールを被膜形成剤として用い、膜強度を粉体を含有させることにより補う技術（例えば、特許文献４、特許文献５を参照）、エポキシ樹脂を含む第一剤と、有機アミンを含む第二剤を用時に混合、反応させて用いる方法（例えば、特許文献６を参照）、アクリル酸エチル・メタクリル酸エチルコポリマーを被膜成分に使用する方法（例えば、特許文献７を参照）などが開発されている。しかしこの様な固化時間の短縮は、得られたレプリカ標本において多くの不具合箇所を有するようになるのが常であった。この原因の一つには、固化が早すぎて形状を転写する前に固化してしまうことが存するためであり、もう一つには、固化時に急激な収縮などの現象が起こり、レプリカ用の組成物が皮膚上に残存してしまうことが存するためである。即ち、かかる不具合を生じずに、速やかに固化するレプリカ作成用の組成物の開発が望まれている。 As a means of non-invasively measuring skin function, it is very useful to perform observation using a so-called “replica” in which a polymer is deformed and solidified according to the shape of the skin, and the shape is transferred. Various skin condition discrimination methods, cosmetic selection methods, and the like have been devised. (For example, refer to Patent Document 1, Patent Document 2, and Patent Document 3) The basic technology of this “replica” has existed for a long time, but how to faithfully transfer the three-dimensional shape of the skin is a technical problem. There was a big leap forward by changing from the method using the original melting and re-solidification of the plastic plate to the method of solidifying the viscous film-forming composition. This is because the development of such a method has made the procedure extremely easy and makes it easy for an amateur to create a replica. Nowadays, it is also used for counseling tools at sales sites. In such a situation, the problem with such replica agents is to reduce the time required for preparation, in other words, the solidification time, so that it can be utilized quickly for counseling. , A technology that uses polyvinyl alcohol as a film forming agent and supplements the film strength by containing powder (see, for example, Patent Document 4 and Patent Document 5), a first agent containing an epoxy resin, and a first agent containing an organic amine. A method of mixing and reacting the two agents at the time of use (for example, see Patent Document 6), a method of using an ethyl acrylate / ethyl methacrylate copolymer as a coating component (for example, see Patent Document 7), etc. have been developed. ing. However, such a shortening of the solidification time usually has many defective portions in the obtained replica specimen. One of the reasons is that the solidification is too early and solidifies before transferring the shape. This is because the composition may remain on the skin. That is, it is desired to develop a composition for creating a replica that quickly solidifies without causing such a problem.
一方、部分的にアセチル化されても良いポリビニルアルコールも、ポリビニルピロリドンも、ポリ酢酸ビニルも何れも化粧料用の原料であり、パック化粧料などに使用され、皮膚上の投与においては何ら問題がない。又、この３者を同時に含有する、皮膚のレプリカ作成用の組成物は全く知られておらず、かかる構成の皮膚のレプリカ作成用の組成物が、不具合を生じずに、速やかに固化し、皮膚のレプリカ標本を作製するのに好適なものであることも全く知られていない。 On the other hand, polyvinyl alcohol, polyvinyl pyrrolidone, and polyvinyl acetate, which may be partially acetylated, are raw materials for cosmetics, and are used for pack cosmetics. Absent. Moreover, the composition for skin replica creation containing these three at the same time is not known at all, and the composition for skin replica creation of such a structure quickly solidifies without causing any trouble, It is also not known at all that it is suitable for preparing a skin replica specimen.
本発明は、この様な状況下為されたものであり、不具合を生じずに、速やかに固化するレプリカ作成用の組成物を提供することを課題とする。 The present invention has been made under such circumstances, and an object of the present invention is to provide a composition for producing a replica that quickly solidifies without causing a problem.
かかる状況に鑑みて、本発明者らは、不具合を生じずに、速やかに固化するレプリカ作成用の組成物を求めて、鋭意研究努力を重ねた結果１）部分的にアセチル化されても良いポリビニルアルコールと、２）ポリビニルピロリドンと、３）ポリ酢酸ビニルとを含有する組成物がこの様な特性を備えていることを見出し、発明を完成させるに至った。即ち、本発明は、以下に示す技術に関するものである。
（１）１）部分的にアセチル化されても良いポリビニルアルコールと、２）ポリビニルピロリドンと、３）ポリ酢酸ビニルとを含有することを特徴とする、皮膚のレプリカ作成用の組成物。
（２）前記部分的にアセチル化されても良いポリビニルアルコールが、水酸基の５〜２０％がアセチル化されているものであることを特徴とする、（１）に記載の皮膚のレプリカ作成用の組成物。
（３）前記部分的にアセチル化されても良いポリビニルアルコールと、前記ポリビニルピロリドンと、前記ポリ酢酸ビニルとの混合比において、前記部分的にアセチル化されても良いポリビニルアルコールの含有量が、前記ポリビニルピロリドンの含有量と、前記ポリ酢酸ビニルの含有量との総和に対して、０．５〜１の質量比であることを特徴とする、（１）又は（２）に記載の皮膚のレプリカ作成用の組成物。
（４）前記部分的にアセチル化されても良いポリビニルアルコールと、前記ポリビニルピロリドンと、前記ポリ酢酸ビニルとの混合比において、前記ポリビニルピロリドンの含有量が、前記ポリ酢酸ビニル含有量に対して５〜１０の質量比であることを特徴とする、（１）〜（３）何れか１項に記載の皮膚のレプリカ作成用の組成物。
（５）１）部分的にアセチル化されても良いポリビニルアルコールの含有量と、２）ポリビニルピロリドンの含有量と、３）ポリ酢酸ビニルの含有量との総和が、組成物全量に対して、８〜２０質量％であることを特徴とする、（１）〜（４）何れか１項に記載のレプリカ作成用の組成物。
（６）更に、粉体を２０〜３０質量％含有することを特徴とする、（１）〜（５）何れか１項に記載のレプリカ作成用の組成物。
（７）更に、エタノールを１〜５質量％含有することを特徴とする、（１）〜（６）何れか１項に記載のレプリカ作成用の組成物。
In view of such a situation, the present inventors have sought for a composition for making a replica that quickly solidifies without causing a problem, and as a result of intensive research efforts 1) may be partially acetylated. The inventors have found that a composition containing polyvinyl alcohol, 2) polyvinyl pyrrolidone, and 3) polyvinyl acetate has such properties, and has completed the invention. That is, this invention relates to the technique shown below.
(1) A composition for replicating a skin, comprising 1) polyvinyl alcohol which may be partially acetylated, 2) polyvinylpyrrolidone, and 3) polyvinyl acetate.
(2) The polyvinyl alcohol which may be partially acetylated is characterized in that 5 to 20% of the hydroxyl groups are acetylated. Composition.
(3) In the mixing ratio of the polyvinyl alcohol that may be partially acetylated, the polyvinyl pyrrolidone, and the polyvinyl acetate, the content of the polyvinyl alcohol that may be partially acetylated is The skin replica according to (1) or (2), characterized in that the mass ratio is 0.5 to 1 with respect to the total content of polyvinylpyrrolidone and the content of polyvinyl acetate. Composition for making.
(4) In the mixing ratio of the partially acetylated polyvinyl alcohol, the polyvinyl pyrrolidone, and the polyvinyl acetate, the content of the polyvinyl pyrrolidone is 5 with respect to the polyvinyl acetate content. The composition for skin replica creation according to any one of (1) to (3), wherein the composition is a mass ratio of from 10 to 10.
(5) The sum of 1) the content of polyvinyl alcohol which may be partially acetylated, 2) the content of polyvinylpyrrolidone, and 3) the content of polyvinyl acetate is based on the total amount of the composition. It is 8-20 mass%, The composition for replica creation of any one of (1)-(4) characterized by the above-mentioned.
(6) The composition for replica production according to any one of (1) to (5), further comprising 20 to 30% by mass of powder.
(7) The composition for replica production according to any one of (1) to (6), further comprising 1 to 5% by mass of ethanol.
本発明によれば、不具合を生じずに、速やかに固化するレプリカ作成用の組成物を提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the composition for replica preparation which solidifies rapidly, without producing a malfunction can be provided.
＜１＞本発明の組成物の必須成分である部分的にアセチル化されても良いポリビニルアルコール
本発明の皮膚のレプリカ作成用の組成物は、部分的にアセチル化されても良いポリビニルアルコールを必須成分として含有することを特徴とする。ポリビニルアルコール乃至はその一部の水酸基がアセチル化されたポリビニルアルコールは化粧料の汎用原料のものを使用することが出来る。この内、特に好ましいものは一部の水酸基がアセチル化したポリビニルアルコールであり、該一部の水酸基がアセチル化したポリビニルアルコールとしては、全水酸基の５〜２０％、より好ましくは１０〜１５％がアセチル化されているものが好ましい。この様なポリビニルアルコール乃至はその一部の水酸基がアセチル化されたポリビニルアルコールは、唯一種を含有することも出来るし、二種以上を組み合わせて含有することも出来る。本発明の組成物に於ける、かかるポリビニルアルコール乃至はその一部の水酸基がアセチル化されたポリビニルアルコールの好ましい含有量は、総量で、組成物全量に対して、１〜１０質量％であり、更に好ましくは、３〜８質量％である。この様な水酸基の一部がアセチル化されたポリビニルアルコールとしては、既に市販されているものが存し、それを購入して利用することが出来る。かかる市販品としては、例えば、日本合成株式会社製の「ゴーセノールＥＧ３０」が好ましく例示できる。かかる成分は、他の必須成分である、ポリビニルピロリドンと、ポリ酢酸ビニルとの混合比において、前記部分的にアセチル化されても良いポリビニルアルコールの含有量が、前記ポリビニルピロリドンの含有量と、前記ポリ酢酸ビニルの含有量との総和に対して、０．５〜１、より好ましくは０．６〜０．８の質量比であることが好ましい。この様な量比において、かかる成分は、レプリカ被膜に弾性を付与すると同時に、収縮を抑制する効果を発揮する。
<1> Polyvinyl alcohol which may be partially acetylated which is an essential component of the composition of the present invention The composition for making a replica of the skin of the present invention requires polyvinyl alcohol which may be partially acetylated It is contained as a component. As the polyvinyl alcohol or polyvinyl alcohol in which some of the hydroxyl groups are acetylated, a general-purpose raw material for cosmetics can be used. Among these, particularly preferred is polyvinyl alcohol in which some hydroxyl groups are acetylated, and the polyvinyl alcohol in which some hydroxyl groups are acetylated is 5 to 20%, more preferably 10 to 15% of all hydroxyl groups. Those that are acetylated are preferred. Such polyvinyl alcohol or polyvinyl alcohol in which some of the hydroxyl groups are acetylated may contain only one species or may contain two or more species in combination. In the composition of the present invention, the preferable content of such polyvinyl alcohol or polyvinyl alcohol in which a part of the hydroxyl groups are acetylated is 1 to 10% by mass based on the total amount of the composition, More preferably, it is 3-8 mass%. As such a polyvinyl alcohol in which a part of the hydroxyl group is acetylated, there is a commercially available one, which can be purchased and used. As such a commercial item, for example, “GOHSENOL EG30” manufactured by Nihon Gosei Co., Ltd. can be preferably exemplified. This component is the other essential component, in the mixing ratio of polyvinyl pyrrolidone and polyvinyl acetate, the content of the polyvinyl alcohol which may be partially acetylated, the content of the polyvinyl pyrrolidone, The mass ratio is preferably 0.5 to 1, more preferably 0.6 to 0.8 with respect to the total content of polyvinyl acetate. In such a quantitative ratio, such a component exerts an effect of suppressing shrinkage as well as imparting elasticity to the replica film.
＜２＞本発明の組成物の必須成分であるポリビニルピロリドン
本発明の皮膚のレプリカ作成用の組成物は、ポリビニルピロリドンを必須成分として含有することを特徴とする。本発明の組成物に使用するポリビニルピロリドンとしては、化粧料などで使用されているものであれば、特段の限定無く使用することが出来る。この様なポリビニルピロリドンとしては、既に市販のものが存し、かかる市販品を購入して利用することが出来る。好ましい市販品としては、例えば、ＢＡＳＦ社製の「ルビスコールＫ−９０」などが例示できる。かかる成分は、皮膚から離脱しやすく、速乾性を有する被膜を形成する。本発明の組成物に於ける、かかる成分の好ましい含有量は、５〜１５質量％であり、更に、好ましくは、６〜１０質量％である。又、他の必須成分である、一部の水酸基がアセチル化していても良いポリビニルアルコール、及び、ポリ酢酸ビニルとの関係において、前記部分的にアセチル化されても良いポリビニルアルコールの含有量が、前記ポリビニルピロリドンの含有量と、前記ポリ酢酸ビニルの含有量との総和に対して、０．５〜１、より好ましくは０．６〜０．８の質量比である、前記の条件以外に、前記ポリビニルピロリドンと、前記ポリ酢酸ビニルとの混合比において、前記ポリビニルピロリドンの含有量が、前記ポリ酢酸ビニル含有量に対して５〜１０、より好ましくは６〜８の質量比であることが好ましい。
<2> Polyvinylpyrrolidone as an essential component of the composition of the present invention The composition for replicating skin of the present invention comprises polyvinylpyrrolidone as an essential component. Any polyvinyl pyrrolidone used in the composition of the present invention can be used without particular limitation as long as it is used in cosmetics. Such polyvinyl pyrrolidone already exists on the market, and such a commercial product can be purchased and used. As a preferable commercially available product, for example, “Lubicol K-90” manufactured by BASF can be exemplified. Such components are easily detached from the skin and form a film having quick drying properties. The preferable content of such a component in the composition of the present invention is 5 to 15% by mass, and more preferably 6 to 10% by mass. In addition, in relation to polyvinyl alcohol, which is another essential component, a part of hydroxyl groups may be acetylated, and polyvinyl acetate, the content of polyvinyl alcohol which may be partially acetylated is In addition to the above conditions, which is a mass ratio of 0.5 to 1, more preferably 0.6 to 0.8, based on the total content of the polyvinyl pyrrolidone and the content of the polyvinyl acetate, In the mixing ratio of the polyvinyl pyrrolidone and the polyvinyl acetate, the content of the polyvinyl pyrrolidone is preferably 5 to 10, more preferably 6 to 8 with respect to the polyvinyl acetate content. .
＜３＞本発明の組成物の必須成分であるポリ酢酸ビニル
本発明の皮膚のレプリカ作成用の組成物は、ポリ酢酸ビニルを必須成分として含有することを特徴とする。本発明の組成物に使用するポリ酢酸ビニルとしては、化粧料などで使用されているものであれば、特段の限定無く使用することが出来る。特に好ましいものはポリマーエマルションの形態を取るものである。この様なポリ酢酸ビニルとしては、既に市販のものが存し、かかる市販品を購入して利用することが出来る。好ましい市販品としては、例えば、日信化学工業株式会社製の「ビニブランＧＶ−５６５１」などが例示できる。このものは、ポリ酢酸ビニルを約４０質量％含有するポリマーエマルションである。本発明の組成物に於いて、かかる成分は、水酸基の一部がアセチル化されていても良い、ポリビニルアルコールと、ポリビニルピロリドンとの膜形成時に於ける馴染みを向上させる作用を有する。本発明の組成物に於ける、かかる成分の好ましい含有量は、固形物換算で、組成物全量に対して、０．１〜５質量％であり、０．２〜１質量％である。
<3> Polyvinyl acetate which is an essential component of the composition of the present invention The composition for skin replica production of the present invention is characterized by containing polyvinyl acetate as an essential component. The polyvinyl acetate used in the composition of the present invention can be used without particular limitation as long as it is used in cosmetics and the like. Particularly preferred are those in the form of polymer emulsions. Such polyvinyl acetate already exists on the market, and such a commercial product can be purchased and used. As a preferable commercially available product, for example, “Vinibran GV-5651” manufactured by Nissin Chemical Industry Co., Ltd. can be exemplified. This is a polymer emulsion containing about 40% by weight of polyvinyl acetate. In the composition of the present invention, such a component has an action of improving the familiarity in forming a film of polyvinyl alcohol and polyvinyl pyrrolidone, in which a part of the hydroxyl group may be acetylated. The preferable content of such components in the composition of the present invention is 0.1 to 5% by mass and 0.2 to 1% by mass with respect to the total amount of the composition in terms of solid matter.
＜４＞本発明の皮膚のレプリカ作成用の組成物
本発明の皮膚のレプリカ作成用の組成物は、前記の必須成分である、１）部分的にアセチル化されても良いポリビニルアルコールと、２）ポリビニルピロリドンと、３）ポリ酢酸ビニルとを含有することを特徴とする。これらの成分の総和は、組成物全量に対して、８〜２０質量％であることが好ましく、１０〜１５質量％であることが更に好ましい。本発明の組成物に於いては、かかる成分以外に通常化粧料などで使用される任意の成分を含有することが出来る。この様な任意成分としては、例えば、マカデミアナッツ油、アボガド油、トウモロコシ油、オリーブ油、ナタネ油、ゴマ油、ヒマシ油、サフラワー油、綿実油、ホホバ油、ヤシ油、パーム油、液状ラノリン、硬化ヤシ油、硬化油、モクロウ、硬化ヒマシ油、ミツロウ、キャンデリラロウ、カルナウバロウ、イボタロウ、ラノリン、還元ラノリン、硬質ラノリン、ホホバロウ等のオイル、ワックス類、流動パラフィン、スクワラン、プリスタン、オゾケライト、パラフィン、セレシン、ワセリン、マイクロクリスタリンワックス等の炭化水素類、オレイン酸、イソステアリン酸、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、ベヘン酸、ウンデシレン酸等の高級脂肪酸類、セチルアルコール、ステアリルアルコール、イソステアリルアルコール、ベヘニルアルコール、オクチルドデカノール、ミリスチルアルコール、セトステアリルアルコール等の高級アルコール等、イソオクタン酸セチル、ミリスチン酸イソプロピル、イソステアリン酸ヘキシルデシル、アジピン酸ジイソプロピル、セバチン酸ジ−２−エチルヘキシル、乳酸セチル、リンゴ酸ジイソステアリル、ジ−２−エチルヘキサン酸エチレングリコール、ジカプリン酸ネオペンチルグリコール、ジ−２−ヘプチルウンデカン酸グリセリン、トリ−２−エチルヘキサン酸グリセリン、トリ−２−エチルヘキサン酸トリメチロールプロパン、トリイソステアリン酸トリメチロールプロパン、テトラ−２−エチルヘキサン酸ペンタンエリトリット等の合成エステル油類、ジメチルポリシロキサン、メチルフェニルポリシロキサン、ジフェニルポリシロキサン等の鎖状ポリシロキサン、オクタメチルシクロテトラシロキサン、デカメチルシクロペンタシロキサン、ドデカメチルシクロヘキサンシロキサン等の環状ポリシロキサン、アミノ変性ポリシロキサン、ポリエーテル変性ポリシロキサン、アルキル変性ポリシロキサン、フッ素変性ポリシロキサン等の変性ポリシロキサン等のシリコーン油等の油剤類、脂肪酸セッケン（ラウリン酸ナトリウム、パルミチン酸ナトリウム等）、ラウリル硫酸カリウム、アルキル硫酸トリエタノールアミンエーテル等のアニオン界面活性剤類、塩化ステアリルトリメチルアンモニウム、塩化ベンザルコニウム、ラウリルアミンオキサイド等のカチオン界面活性剤類、イミダゾリン系両性界面活性剤（２−ココイル−２−イミダゾリニウムヒドロキサイド−１−カルボキシエチロキシ２ナトリウム塩等）、ベタイン系界面活性剤（アルキルベタイン、アミドベタイン、スルホベタイン等）、アシルメチルタウリン等の両性界面活性剤類、ソルビタン脂肪酸エステル類（ソルビタンモノステアレート、セスキオレイン酸ソルビタン等）、グリセリン脂肪酸類（モノステアリン酸グリセリン等）、プロピレングリコール脂肪酸エステル類（モノステアリン酸プロピレングリコール等）、硬化ヒマシ油誘導体、グリセリンアルキルエーテル、ＰＯＥソルビタン脂肪酸エステル類（ＰＯＥソルビタンモノオレエート、モノステアリン酸ポリオキエチレンソルビタン等）、ＰＯＥソルビット脂肪酸エステル類（ＰＯＥ−ソルビットモノラウレート等）、ＰＯＥグリセリン脂肪酸エステル類（ＰＯＥ−グリセリンモノイソステアレート等）、ＰＯＥ脂肪酸エステル類（ポリエチレングリコールモノオレート、ＰＯＥジステアレート等）、ＰＯＥアルキルエーテル類（ＰＯＥ２−オクチルドデシルエーテル等）、ＰＯＥアルキルフェニルエーテル類（ＰＯＥノニルフェニルエーテル等）、プルロニック型類、ＰＯＥ・ＰＯＰアルキルエーテル類（ＰＯＥ・ＰＯＰ２−デシルテトラデシルエーテル等）、テトロニック類、ＰＯＥヒマシ油・硬化ヒマシ油誘導体（ＰＯＥヒマシ油、ＰＯＥ硬化ヒマシ油等）、ショ糖脂肪酸エステル、アルキルグルコシド等の非イオン界面活性剤類、ポリエチレングリコール、グリセリン、１，３−ブチレングリコール、エリスリトール、ソルビトール、キシリトール、マルチトール、プロピレングリコール、ジプロピレングリコール、ジグリセリン、イソプレングリコール、１，２−ペンタンジオール、１，２−ヘキシレングリコール、１，２−オクタンジオール等の多価アルコール類、ピロリドンカルボン酸ナトリウム、乳酸、乳酸ナトリウム等の保湿成分類、グアガム、クインスシード、カラギーナン、ガラクタン、アラビアガム、ペクチン、マンナン、デンプン、キサンタンガム、カードラン、メチルセルロース、ヒドロキシエチルセルロース、カルボキシメチルセルロース、メチルヒドロキシプロピルセルロース、コンドロイチン硫酸、デルマタン硫酸、グリコーゲン、ヘパラン硫酸、ヒアルロン酸、ヒアルロン酸ナトリウム、トラガントガム、ケラタン硫酸、コンドロイチン、ムコイチン硫酸、ヒドロキシエチルグアガム、カルボキシメチルグアガム、デキストラン、ケラト硫酸，ローカストビーンガム，サクシノグルカン，カロニン酸，キチン，キトサン、カルボキシメチルキチン、寒天、カルボキシビニルポリマー、ポリアクリル酸ナトリウム、ポリエチレングリコール、ベントナイト等の増粘剤、表面を処理されていても良い、マイカ、タルク、カオリン、合成雲母、炭酸カルシウム、炭酸マグネシウム、無水ケイ酸（シリカ）、酸化アルミニウム、硫酸バリウム等の粉体類、表面を処理されていても良い、ベンガラ、黄酸化鉄、黒酸化鉄、酸化コバルト、群青、紺青、酸化チタン、酸化亜鉛の無機顔料類、表面を処理されていても良い、雲母チタン、魚燐箔、オキシ塩化ビスマス等のパール剤類、レーキ化されていても良い赤色２０２号、赤色２２８号、赤色２２６号、黄色４号、青色４０４号、黄色５号、赤色５０５号、赤色２３０号、赤色２２３号、橙色２０１号、赤色２１３号、黄色２０４号、黄色２０３号、青色１号、緑色２０１号、紫色２０１号、赤色２０４号等の有機色素類、ポリエチレン末、ポリメタクリル酸メチル、ナイロン粉末、オルガノポリシロキサンエラストマー等の有機粉体類、パラアミノ安息香酸系紫外線吸収剤、アントラニル酸系紫外線吸収剤、サリチル酸系紫外線吸収剤、桂皮酸系紫外線吸収剤、ベンゾフェノン系紫外線吸収剤、糖系紫外線吸収剤、２−（２’−ヒドロキシ−５’−ｔ−オクチルフェニル)ベンゾトリアゾール、４−メトキシ−４’−ｔ−ブチルジベンゾイルメタン等の紫外線吸収剤類、エタノール、イソプロパノール等の低級アルコール類、ビタミンＡ又はその誘導体、ビタミンＢ6塩酸塩，ビタミンＢ6トリパルミテート，ビタミンＢ6ジオクタノエート，ビタミンＢ2又はその誘導体，ビタミンＢ12，ビタミンＢ15又はその誘導体等のビタミンＢ類、α−トコフェロール，β−トコフェロール，γ−トコフェロール，ビタミンＥアセテート等のビタミンＥ類、ビタミンＤ類、ビタミンＨ、パントテン酸、パンテチン、ピロロキノリンキノン等のビタミン類などが好ましく例示できる。これらの内、特に好ましいものとしては、表面を処理されていても良い、マイカ、タルク、カオリン、合成雲母、炭酸カルシウム、炭酸マグネシウム、無水ケイ酸（シリカ）、酸化アルミニウム、硫酸バリウム等の粉体類、表面を処理されていても良い、ベンガラ、黄酸化鉄、黒酸化鉄、酸化コバルト、群青、紺青、酸化チタン、酸化亜鉛の無機顔料類等の粉体類が好ましく例示でき、該粉体類の好ましい含有量としては、２０〜３０質量％含有することが例示できる。これらの粉体は、被膜の強度を高め、皮膚表面の立体形状を忠実に写し取り、維持する作用を有する。又、エタノールを含有することも、防腐力を向上させる意味と、乾燥ムラを抑制する意味で好ましい。エタノールの好ましい含有量は、組成物全量に対して、１〜５質量％である。加えて、形成する被膜の、剥離時の崩壊を防ぐ目的で、ポリオキシエチレンポリオキシプロピレンブロックコポリマーや、ポリオキシエチレン脂肪酸グリセリルを０．１〜２質量％含有させることも好ましい。更に、親油性の高い可塑剤として二塩基酸のジエステルを１〜３質量％含有することも好ましい。かかる二塩基酸のジエステルとしては、味ピン酸ジエトキシエチル、コハク酸ジエトキシエチルなどが好ましく例示できる。本発明の組成物は、この様な必須成分と任意成分とを常法に従って処理することにより、製造することが出来る。
<4> Composition for skin replica production of the present invention The composition for skin replica production of the present invention is the essential component described above, 1) polyvinyl alcohol which may be partially acetylated, and 2 It contains polyvinyl pyrrolidone) and 3) polyvinyl acetate. The total sum of these components is preferably 8 to 20% by mass, more preferably 10 to 15% by mass, based on the total amount of the composition. In the composition of this invention, the arbitrary components normally used by cosmetics etc. can be contained besides this component. Such optional ingredients include, for example, macadamia nut oil, avocado oil, corn oil, olive oil, rapeseed oil, sesame oil, castor oil, safflower oil, cottonseed oil, jojoba oil, coconut oil, palm oil, liquid lanolin, hydrogenated coconut oil Oils such as hardened oil, mole, hardened castor oil, beeswax, candelilla wax, carnauba wax, ibotarou, lanolin, reduced lanolin, hard lanolin, jojoba wax, waxes, liquid paraffin, squalane, pristane, ozokerite, paraffin, ceresin, petrolatum , Hydrocarbons such as microcrystalline wax, higher fatty acids such as oleic acid, isostearic acid, lauric acid, myristic acid, palmitic acid, stearic acid, behenic acid, undecylenic acid, cetyl alcohol, stearyl alcohol, isostearyl Alcohol, behenyl alcohol, octyldodecanol, higher alcohol such as myristyl alcohol, cetostearyl alcohol, cetyl isooctanoate, isopropyl myristate, hexyldecyl isostearate, diisopropyl adipate, di-2-ethylhexyl sebacate, cetyl lactate, malic acid Diisostearyl, di-2-ethylhexanoic acid ethylene glycol, dicaprate neopentyl glycol, di-2-heptylundecanoic acid glycerin, tri-2-ethylhexanoic acid glycerin, tri-2-ethylhexanoic acid trimethylolpropane, tri Synthetic ester oils such as trimethylolpropane isostearate and pentane erythritol tetra-2-ethylhexanoate, dimethylpolysiloxane, methylphenylpoly Loxane, linear polysiloxane such as diphenylpolysiloxane, cyclic polysiloxane such as octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, dodecamethylcyclohexanesiloxane, amino-modified polysiloxane, polyether-modified polysiloxane, alkyl-modified polysiloxane, Oil agents such as silicone oil such as modified polysiloxane such as fluorine-modified polysiloxane, anionic surfactants such as fatty acid soap (sodium laurate, sodium palmitate, etc.), potassium lauryl sulfate, triethanolamine ether of alkyl sulfate, chloride Cationic surfactants such as stearyltrimethylammonium, benzalkonium chloride, laurylamine oxide, imidazoline-based amphoteric surfactants (2-cocoyl-2-imida Zolinium hydroxide-1-carboxyethyloxy disodium salt, etc.), betaine surfactants (alkyl betaine, amide betaine, sulfobetaine, etc.), amphoteric surfactants such as acylmethyltaurine, sorbitan fatty acid esters (sorbitan) Monostearate, sorbitan sesquioleate, etc.), glycerin fatty acids (glyceryl monostearate, etc.), propylene glycol fatty acid esters (propylene glycol monostearate, etc.), hardened castor oil derivatives, glycerin alkyl ethers, POE sorbitan fatty acid esters (POE sorbitan monooleate, polyoxyethylene sorbitan monostearate, etc.), POE sorbite fatty acid esters (POE-sorbitol monolaurate, etc.), POE glycerin fatty acid ester Tells (POE-glycerol monoisostearate, etc.), POE fatty acid esters (polyethylene glycol monooleate, POE distearate, etc.), POE alkyl ethers (POE2-octyldodecyl ether, etc.), POE alkyl phenyl ethers (POE nonylphenyl) Ethers, etc.), Pluronic types, POE / POP alkyl ethers (POE / POP2-decyltetradecyl ether, etc.), Tetronics, POE castor oil / hardened castor oil derivatives (POE castor oil, POE hardened castor oil, etc.), Nonionic surfactants such as sucrose fatty acid ester and alkyl glucoside, polyethylene glycol, glycerin, 1,3-butylene glycol, erythritol, sorbitol, xylitol, maltitol, propylene Recall, dipropylene glycol, diglycerin, isoprene glycol, 1,2-pentanediol, 1,2-hexylene glycol, polyhydric alcohols such as 1,2-octanediol, sodium pyrrolidonecarboxylate, lactic acid, sodium lactate, etc. Moisturizing ingredients, guar gum, quince seed, carrageenan, galactan, gum arabic, pectin, mannan, starch, xanthan gum, curdlan, methylcellulose, hydroxyethylcellulose, carboxymethylcellulose, methylhydroxypropylcellulose, chondroitin sulfate, dermatan sulfate, glycogen, heparan Sulfuric acid, hyaluronic acid, sodium hyaluronate, tragacanth gum, keratan sulfate, chondroitin, mucoitin sulfate, hydroxyethyl guar gum, potassium Thickeners such as ruboxymethyl guar gum, dextran, keratosulfuric acid, locust bean gum, succinoglucan, caronic acid, chitin, chitosan, carboxymethylchitin, agar, carboxyvinyl polymer, sodium polyacrylate, polyethylene glycol, bentonite, The surface may be treated, powders such as mica, talc, kaolin, synthetic mica, calcium carbonate, magnesium carbonate, anhydrous silicic acid (silica), aluminum oxide, barium sulfate, etc. may be treated. , Bengala, yellow iron oxide, black iron oxide, cobalt oxide, ultramarine, bitumen, titanium oxide, zinc oxide inorganic pigments, pearls such as titanium mica, fish phosphorus foil, bismuth oxychloride, etc. whose surface may be treated Agents, raked red 202, red 228, red No. 226, Yellow No. 4, Blue No. 404, Yellow No. 5, Red No. 505, Red No. 230, Red No. 223, Orange No. 201, Red No. 213, Yellow No. 204, Yellow No. 203, Blue No. 1, Green No. 201 Organic dyes such as purple 201, red 204, polyethylene powder, polymethyl methacrylate, nylon powder, organic powders such as organopolysiloxane elastomer, paraaminobenzoic acid UV absorber, anthranilic acid UV absorber , Salicylic acid UV absorbers, cinnamic acid UV absorbers, benzophenone UV absorbers, sugar UV absorbers, 2- (2′-hydroxy-5′-t-octylphenyl) benzotriazole, 4-methoxy-4 UV absorbers such as' -t-butyldibenzoylmethane, lower alcohols such as ethanol and isopropanol, vitamins Or a derivative thereof, vitamin B 6 hydrochloride, vitamin B 6 tripalmitate, vitamin B 6 dioctanoate, vitamin B 2 or derivatives thereof, vitamin B 12, vitamin B such as vitamin B 15 or a derivative thereof, alpha-tocopherol, beta -Vitamin E, such as tocopherol, (gamma) -tocopherol, vitamin E acetate, vitamin D, vitamin H, pantothenic acid, panthetin, pyrroloquinoline quinone, etc. can be illustrated preferably. Among these, powders such as mica, talc, kaolin, synthetic mica, calcium carbonate, magnesium carbonate, anhydrous silicic acid (silica), aluminum oxide, barium sulfate, etc. whose surface may be treated are particularly preferable. Preferred examples include powders such as inorganic pigments such as bengara, yellow iron oxide, black iron oxide, cobalt oxide, ultramarine, bitumen, titanium oxide, and zinc oxide whose surface may be treated. Examples of preferable content of the class include 20 to 30% by mass. These powders have the effect of increasing the strength of the coating and faithfully copying and maintaining the three-dimensional shape of the skin surface. Moreover, it is also preferable to contain ethanol from the meaning which improves preservative power, and the meaning which suppresses drying nonuniformity. The preferable content of ethanol is 1 to 5% by mass relative to the total amount of the composition. In addition, it is also preferable to contain 0.1 to 2% by mass of polyoxyethylene polyoxypropylene block copolymer or polyoxyethylene fatty acid glyceryl for the purpose of preventing the coating film to be disintegrated during peeling. Furthermore, it is also preferable to contain 1 to 3% by mass of a dibasic acid diester as a highly lipophilic plasticizer. Preferred examples of such dibasic acid diesters include diethoxyethyl taste pinate and diethoxyethyl succinate. The composition of the present invention can be produced by treating such essential components and optional components according to a conventional method.
以下に、実施例を挙げて、本発明について更に詳細に説明を加えるが、本亜ｈつめいがかかる実施例にのみ、限定を受けないことは言うまでもない。 Hereinafter, the present invention will be described in more detail with reference to examples, but it is needless to say that the present invention is not limited to the examples.
＜実施例１＞
以下に示す処方に従って、本発明の皮膚のレプリカ作成用の組成物１を作成した。即ち、処方成分を、８０℃で良く混練り、混合し、攪拌冷却して、減圧下脱泡して、本発明の皮膚のレプリカ作成用の組成物１を得た。
「ゴーセノールＥＧ３０」 ５ 質量部
１，３−ブタンジオール ２ 質量部
エタノール ５ 質量部
コハク酸ジエトキシエチル ２ 質量部
流動パラフィン ６ 質量部
フェノキシエタノール ０．５質量部
「ルビスコールＫ９０」 ７ 質量部
「ビニブランＧＶ−５６５１」 １ 質量部
カオリン ２０ 質量部
二酸化チタン ５ 質量部
ポリオキシエチレン（２０）セスキステアレート ０．５質量部
ＰＯＥ・ＰＯＰブロックコポリマー １ 質量部
ソルビタンセスキラウレート ０．５質量部
ステアリン酸 ０．１質量部
水 ４４．４質量部
<Example 1>
According to the formulation shown below, a composition 1 for making a skin replica of the present invention was prepared. That is, the formulation components were kneaded well at 80 ° C., mixed, stirred and cooled, and degassed under reduced pressure to obtain the composition 1 for skin replica creation of the present invention.
“Gosenol EG30” 5 parts by mass 1,3-butanediol 2 parts by mass ethanol 5 parts by mass diethoxyethyl succinate 2 parts by mass liquid paraffin 6 parts by mass phenoxyethanol 0.5 parts by mass “Lubicol K90” 7 parts by mass “Vinibrand GV” -5651 "1 part by weight kaolin 20 parts by weight titanium dioxide 5 parts by weight polyoxyethylene (20) sesquistearate 0.5 parts by weight POE / POP block copolymer 1 part by weight sorbitan sesquilaurate 0.5 parts by weight stearic acid 0. 1 part by weight water 44.4 parts by weight
＜参考例１＞
以下に示す処方に従って、参考例の皮膚のレプリカ作成用の参考組成物１を作成した。即ち、処方成分を、８０℃で良く混練り、混合し、攪拌冷却して、減圧下脱泡して、参考例の皮膚のレプリカ作成用の参考組成物１を得た。
「ゴーセノールＥＧ３０」 １２ 質量部
１，３−ブタンジオール ２ 質量部
エタノール ５ 質量部
コハク酸ジエトキシエチル ２ 質量部
流動パラフィン ６ 質量部
フェノキシエタノール ０．５質量部
「ビニブランＧＶ−５６５１」 １ 質量部
カオリン ２０ 質量部
二酸化チタン ５ 質量部
ポリオキシエチレン（２０）セスキステアレート ０．５質量部
ＰＯＥ・ＰＯＰブロックコポリマー １ 質量部
ソルビタンセスキラウレート ０．５質量部
ステアリン酸 ０．１質量部
水 ４４．４質量部
<Reference Example 1>
In accordance with the formulation shown below, Reference Composition 1 for making a skin replica of Reference Example was prepared. That is, the formulation components were well kneaded at 80 ° C., mixed, stirred and cooled, and degassed under reduced pressure to obtain Reference Composition 1 for making a skin replica of Reference Example.
“Gosenol EG30” 12 parts by mass 1,3-butanediol 2 parts by mass ethanol 5 parts by mass diethoxyethyl succinate 2 parts by mass liquid paraffin 6 parts by mass phenoxyethanol 0.5 parts by mass “Viniblanc GV-5651” 1 part by mass kaolin 20 Parts by mass titanium dioxide 5 parts by mass polyoxyethylene (20) sesquistearate 0.5 parts by mass POE / POP block copolymer 1 part by mass sorbitan sesquilaurate 0.5 parts by mass stearic acid 0.1 parts by mass water 44.4 parts by mass Part
＜参考例２＞
以下に示す処方に従って、参考例の皮膚のレプリカ作成用の参考組成物２を作成した。即ち、処方成分を、８０℃で良く混練り、混合し、攪拌冷却して、減圧下脱泡して、参考例の皮膚のレプリカ作成用の参考組成物２を得た。
１，３−ブタンジオール ２ 質量部
エタノール ５ 質量部
コハク酸ジエトキシエチル ２ 質量部
流動パラフィン ６ 質量部
フェノキシエタノール ０．５質量部
「ルビスコールＫ９０」 １２ 質量部
「ビニブランＧＶ−５６５１」 １ 質量部
カオリン ２０ 質量部
二酸化チタン ５ 質量部
ポリオキシエチレン（２０）セスキステアレート ０．５質量部
ＰＯＥ・ＰＯＰブロックコポリマー １ 質量部
ソルビタンセスキラウレート ０．５質量部
ステアリン酸 ０．１質量部
水 ４４．４質量部
<Reference Example 2>
According to the formulation shown below, Reference Composition 2 for making a skin replica of Reference Example was prepared. That is, the formulation components were kneaded well at 80 ° C., mixed, stirred and cooled, and degassed under reduced pressure to obtain Reference Composition 2 for making a skin replica of Reference Example.
1,3-butanediol 2 parts by mass ethanol 5 parts by mass diethoxyethyl succinate 2 parts by mass liquid paraffin 6 parts by mass phenoxyethanol 0.5 parts by mass “Lubicol K90” 12 parts by mass “Vinibran GV-5651” 1 part by mass kaolin 20 parts by mass Titanium dioxide 5 parts by mass polyoxyethylene (20) sesquistearate 0.5 parts by mass POE / POP block copolymer 1 part by mass sorbitan sesquilaurate 0.5 parts by mass stearic acid 0.1 parts by mass water 44.4 Parts by mass
＜参考例３＞
以下に示す処方に従って、参考例の皮膚のレプリカ作成用の参考組成物３を作成した。即ち、処方成分を、８０℃で良く混練り、混合し、攪拌冷却して、減圧下脱泡して、参考例の皮膚のレプリカ作成用の参考組成物３を得た。
「ゴーセノールＥＧ３０」 ６ 質量部
１，３−ブタンジオール ２ 質量部
エタノール ５ 質量部
コハク酸ジエトキシエチル ２ 質量部
流動パラフィン ６ 質量部
フェノキシエタノール ０．５質量部
「ルビスコールＫ９０」 ７ 質量部
カオリン ２０ 質量部
二酸化チタン ５ 質量部
ポリオキシエチレン（２０）セスキステアレート ０．５質量部
ＰＯＥ・ＰＯＰブロックコポリマー １ 質量部
ソルビタンセスキラウレート ０．５質量部
ステアリン酸 ０．１質量部
水 ４４．４質量部
<Reference Example 3>
In accordance with the formulation shown below, Reference Composition 3 for making a skin replica of Reference Example was prepared. That is, the formulation components were well kneaded at 80 ° C., mixed, cooled with stirring, and degassed under reduced pressure to obtain Reference Composition 3 for making a skin replica of Reference Example.
“GOHSENOL EG30” 6 parts by mass 1,3-butanediol 2 parts by mass ethanol 5 parts by mass diethoxyethyl succinate 2 parts by mass liquid paraffin 6 parts by mass phenoxyethanol 0.5 parts by mass “Rubicol K90” 7 parts by mass kaolin 20 parts by mass Parts titanium dioxide 5 parts by weight polyoxyethylene (20) sesquistearate 0.5 parts by weight POE / POP block copolymer 1 part by weight sorbitan sesquilaurate 0.5 parts by weight stearic acid 0.1 parts by weight water 44.4 parts by weight
＜試験例１＞
上記組成物１、比較組成物１、比較組成物２及び比較組成物３を用いて、それぞれ日を変えて、２２名のボランティアの皮膚（顔の頬部）のレプリカを作成し、それを顕微鏡下観察し、標本として不具合な部分が、作成されたレプリカ全体のどれくらいをしめるかを、観察して、グレードＡ：１０％以下、グレードＢ：１０〜４０％、グレードＣ：５０％以上の３つのグレードに分類して、計数した。結果を表１に示す。これより、本発明の組成物はレプリカの作成において、不具合が非常に少ない特質を有していることが判る。
<Test Example 1>
Using composition 1, comparative composition 1, comparative composition 2, and comparative composition 3, each day was changed to make a replica of the skin (facial cheeks) of 22 volunteers. Observe and observe how much of the entire replica created by the defective part of the specimen. Grade A: 10% or less, Grade B: 10-40%, Grade C: 50% or more 3 It was classified into one grade and counted. The results are shown in Table 1. From this, it can be seen that the composition of the present invention has characteristics with very few defects in the production of replicas.
＜実施例２＞
以下に示す処方に従って、本発明の皮膚のレプリカ作成用の組成物２を作成した。即ち、処方成分を、８０℃で良く混練り、混合し、攪拌冷却して、減圧下脱泡して、本発明の皮膚のレプリカ作成用の組成物２を得た。このものも組成物１と同程度の不具合の出現の低さを有していた。
「ゴーセノールＥＧ３０」 ５ 質量部
１，３−ブタンジオール ２ 質量部
エタノール ５ 質量部
コハク酸ジエトキシエチル ２ 質量部
流動パラフィン ６ 質量部
フェノキシエタノール ０．５質量部
「ルビスコールＫ９０」 ７ 質量部
「ビニブランＧＶ−５６５１」 １ 質量部
カオリン ２０ 質量部
二酸化チタン ５ 質量部
ポリオキシエチレン（２０）セスキステアレート ０．５質量部
ポリオキシエチレンヤシ油脂肪酸グリセリル １ 質量部
ソルビタンセスキラウレート ０．５質量部
ステアリン酸 ０．１質量部
水 ４４．４質量部
<Example 2>
According to the formulation shown below, Composition 2 for skin replica creation of the present invention was prepared. That is, the formulation components were kneaded well at 80 ° C., mixed, stirred and cooled, and degassed under reduced pressure to obtain Composition 2 for skin replica production of the present invention. This also had the same low appearance of defects as the composition 1.
“Gosenol EG30” 5 parts by mass 1,3-butanediol 2 parts by mass ethanol 5 parts by mass diethoxyethyl succinate 2 parts by mass liquid paraffin 6 parts by mass phenoxyethanol 0.5 parts by mass “Lubicol K90” 7 parts by mass “Vinibrand GV” -5651 "1 part by weight kaolin 20 parts by weight titanium dioxide 5 parts by weight polyoxyethylene (20) sesquistearate 0.5 parts by weight polyoxyethylene coconut oil fatty acid glyceryl 1 part by weight sorbitan sesquilaurate 0.5 parts by weight stearic acid 0.14 parts by weight water 44.4 parts by weight
＜実施例３＞
以下に示す処方に従って、本発明の皮膚のレプリカ作成用の組成物３を作成した。即ち、処方成分を、８０℃で良く混練り、混合し、攪拌冷却して、減圧下脱泡して、本発明の皮膚のレプリカ作成用の組成物３を得た。このものは、グレード分布では、組成物１と大差がないものの、グレードＡにおける不具合分布が７〜８％の高めに位置するものが、多く、組成物１の方が好ましいものであることが判った。これは、可塑性が低下しているため、離脱時に一部レプリカが破損するためであると推察される。
「ゴーセノールＥＧ３０」 ５ 質量部
１，３−ブタンジオール ２ 質量部
エタノール ５ 質量部
コハク酸ジエトキシエチル ２ 質量部
流動パラフィン ６ 質量部
フェノキシエタノール ０．５質量部
「ルビスコールＫ９０」 ７ 質量部
「ビニブランＧＶ−５６５１」 １ 質量部
カオリン ２０ 質量部
二酸化チタン ５ 質量部
ポリオキシエチレン（２０）セスキステアレート ０．５質量部
ソルビタンセスキラウレート ０．５質量部
ステアリン酸 ０．１質量部
水 ４５．４質量部
<Example 3>
According to the formulation shown below, a composition 3 for making a skin replica of the present invention was prepared. That is, the formulation components were kneaded well at 80 ° C., mixed, stirred and cooled, and defoamed under reduced pressure to obtain a composition 3 for making a skin replica of the present invention. Although there is no significant difference in the grade distribution with respect to the composition 1 in this case, there are many cases where the defect distribution in the grade A is located 7 to 8% higher, and it is found that the composition 1 is preferable. It was. It is presumed that this is because the plasticity is lowered, so that the replica is partially broken at the time of separation.
“Gosenol EG30” 5 parts by mass 1,3-butanediol 2 parts by mass ethanol 5 parts by mass diethoxyethyl succinate 2 parts by mass liquid paraffin 6 parts by mass phenoxyethanol 0.5 parts by mass “Lubicol K90” 7 parts by mass “Vinibrand GV” -5651 "1 part by weight kaolin 20 parts by weight titanium dioxide 5 parts by weight polyoxyethylene (20) sesquistearate 0.5 parts by weight sorbitan sesquilaurate 0.5 parts by weight stearic acid 0.1 parts by weight water 45.4 parts by weight Part
＜実施例４＞
以下に示す処方に従って、本発明の皮膚のレプリカ作成用の組成物４を作成した。即ち、処方成分を、８０℃で良く混練り、混合し、攪拌冷却して、減圧下脱泡して、本発明の皮膚のレプリカ作成用の組成物４を得た。このものは、グレード分布では、組成物１と大差がないものの、グレードＡにおける不具合分布が７〜８％の高めに位置するものが、多く、組成物１の方が好ましいものであることが判った。これは、可塑性が低下しているため、離脱時に一部レプリカが破損するためであると推察される。
「ゴーセノールＥＧ３０」 ５ 質量部
１，３−ブタンジオール ２ 質量部
エタノール ５ 質量部
流動パラフィン ６ 質量部
フェノキシエタノール ０．５質量部
「ルビスコールＫ９０」 ７ 質量部
「ビニブランＧＶ−５６５１」 １ 質量部
カオリン ２０ 質量部
二酸化チタン ５ 質量部
ポリオキシエチレン（２０）セスキステアレート ０．５質量部
ＰＯＥ・ＰＯＰブロックコポリマー １ 質量部
ソルビタンセスキラウレート ０．５質量部
ステアリン酸 ０．１質量部
水 ４６．４質量部
<Example 4>
According to the formulation shown below, composition 4 for skin replica creation of the present invention was prepared. That is, the formulation components were well kneaded at 80 ° C., mixed, stirred and cooled, and degassed under reduced pressure to obtain the composition 4 for skin replica creation of the present invention. Although there is no significant difference in the grade distribution with respect to the composition 1 in this case, there are many cases where the defect distribution in the grade A is located 7 to 8% higher, and it is found that the composition 1 is preferable. It was. It is presumed that this is because the plasticity is lowered, so that the replica is partially broken at the time of separation.
“Gosenol EG30” 5 parts by mass 1,3-butanediol 2 parts by mass ethanol 5 parts by mass liquid paraffin 6 parts by mass phenoxyethanol 0.5 parts by mass “Rubicol K90” 7 parts by mass “Vinibran GV-5651” 1 part by mass kaolin 20 Parts by mass titanium dioxide 5 parts by mass polyoxyethylene (20) sesquistearate 0.5 parts by mass POE / POP block copolymer 1 part by mass sorbitan sesquilaurate 0.5 parts by mass stearic acid 0.1 parts by mass water 46.4 parts by mass Part
本発明は、化粧料選択などのための肌の鑑別のツールに応用できる。 The present invention can be applied to a skin discrimination tool for cosmetics selection and the like.
Claims (7)