JP2005111923A - Decorative film for steel sheet and laminated decorative sheet for steel sheet - Google Patents
Decorative film for steel sheet and laminated decorative sheet for steel sheet Download PDFInfo
- Publication number
- JP2005111923A JP2005111923A JP2003351944A JP2003351944A JP2005111923A JP 2005111923 A JP2005111923 A JP 2005111923A JP 2003351944 A JP2003351944 A JP 2003351944A JP 2003351944 A JP2003351944 A JP 2003351944A JP 2005111923 A JP2005111923 A JP 2005111923A
- Authority
- JP
- Japan
- Prior art keywords
- steel sheet
- laminated
- decorative film
- decorative
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、鋼板用化粧フィルム及び鋼板用積層化粧シートに関する。さらに詳しくは、本発明は、耐湿熱性、エンボス転写性に優れ、熱ラミネート時の層間の密着性、表面エンボスの耐シボ流れ性に優れた鋼板用化粧フィルム及び鋼板用積層化粧シートに関する。 The present invention relates to a decorative film for steel sheet and a laminated decorative sheet for steel sheet. More specifically, the present invention relates to a decorative film for steel sheet and a laminated decorative sheet for steel sheet, which are excellent in moisture and heat resistance and emboss transfer property, and have excellent adhesion between layers at the time of thermal lamination and surface flow resistance of surface embossing.
家庭電気製品、家具調度品、家屋内装材などには、金属板が多量に用いられている。以前は、ロールコーターなどを用いて金属板に塗装し、加熱乾燥したのちにコイルとして巻き取られたプレコート金属板が一般的であった。しかし、塗料の使用に伴う有機溶剤による環境汚染を避けるために、化粧フィルムを金属板に積層したラミネート金属板が普及してきた。
ラミネート金属板用の化粧フィルムとしては、塩化ビニル樹脂フィルムやその積層化粧シートが用いられてきたが、昨今の環境問題などの影響から、ポリオレフィン系化粧フィルムが用いられるようになってきた。しかし、ポリオレフィン系化粧フィルムは、表面硬度が低いためにラミネート金属板に傷がつきやすく、またラミネート金属板を切断したときに糸引き現象がおこり、切断したラミネート金属板を重ねると、化粧フィルムの糸の跡が残るという問題があった。
隠蔽性、表面硬度、耐溶剤性、耐熱性に優れ、カールを生じにくく、金属板との積層が容易である化粧フィルムとして、樹脂成分が、ポリブチレンテレフタレート系樹脂３０〜９０重量％とジカルボン酸成分がテレフタル酸であり、グリコール成分が１,４−シクロヘキサンジメタノールとエチレングリコールである非晶性ポリエステル樹脂１０〜７０重量％からなる化粧フィルムが提案されている（特許文献１）。この化粧フィルムは、表面硬度や耐熱性には優れているが、化粧フィルム同士を積層して積層化粧シートとする際に、加熱ドラムなどを用いた熱ラミネートの際の密着性が悪く、また、表面にエンボス加工をする際のエンボス転写性も不十分であった。
メンブレンプレス成形などの熱加工性が良好であり、耐溶剤性も改良され、従来の塩化ビニル樹脂製化粧シートと同様に扱うことができるポリエステル樹脂製積層化粧シートとして、非晶質ポリエステル樹脂を主成分とする基材フィルム層と、テレフタル酸からなるジカルボン酸成分と、１,４−シクロヘキサンジメタノール２５〜３５モル％とエチレングリコール６５〜７５モル％からなるジオール成分を共重合した非晶質ポリエステル樹脂４０〜９５重量％と、結晶性を有するポリエチレンテレフタレート樹脂又はポリブチレンテレフタレート樹脂５〜６０重量部％からなる保護フィルム層を積層した化粧シートが提案されている（特許文献２）。この積層化粧シートは、成形加工性が良好であり、エンボス加工も可能であるが、単純に塩化ビニル樹脂製積層化粧シートをこのポリエステル樹脂積層化粧シートで置き換えると、耐湿熱性が悪く、フィルムの膨れなどの現象が起こりやすい。そのために、家屋内装材の中でも高温多湿に曝されるユニットバスなどに用いられる鋼板用積層化粧シートには適していない。
また、非配向の結晶性ポリエステル樹脂を主成分として５〜４０重量％の結晶性の低い樹脂層を備えることにより、金属板の上に凹凸模様を形成させた、意匠性を付与したポリエステル樹脂被覆金属板を得ることができると提案されている（特許文献３）。この樹脂フィルムは表面硬度や耐熱性には優れているが、金属板に積層する前のフィルムの状態でエンボス加工すると、結晶性の樹脂を主成分としているために、結晶化により物性が低下するとともに、アフターエンボス転写性、熱ラミネート密着性においても不十分であった。
本発明者らは、先に、ガラス転移温度−３０℃以上２０℃未満の変性ポリエステル樹脂３〜９７重量％、ガラス転移温度２０℃以上５０℃未満のダイマー酸共重合ポリエステル樹脂０〜９４重量％及びガラス転移温度５０℃以上１２０℃未満のポリエステル樹脂３〜９７重量％からなり、特定の流れ値を有する柔軟性ポリエステル化粧シート組成物から、風合が良好であり、施工時にシワやワレが入りにくく、浮きが発生しにくく、欠点部を加熱により容易に修正することができる、壁装材に適した化粧シートが得られることを見いだした（特許文献４）。しかし、この化粧シートも耐湿熱性が若干劣り、フィルムの膨れなどの現象が起こる場合がある。そのために、家屋内装材の中でも高温多湿に曝されるユニットバスなどに用いられる鋼板用化粧フィルム及び鋼板用積層化粧シートには適していない。
As a decorative film for a laminated metal plate, a vinyl chloride resin film or a laminated decorative sheet thereof has been used. However, a polyolefin-based decorative film has come to be used because of recent environmental problems. However, since the polyolefin-based decorative film has a low surface hardness, the laminated metal plate is easily damaged, and when the laminated metal plate is cut, a stringing phenomenon occurs. There was a problem that the mark of the thread remained.
As a decorative film that has excellent concealability, surface hardness, solvent resistance, and heat resistance, does not easily curl, and can be easily laminated with a metal plate, the resin component is 30 to 90% by weight of polybutylene terephthalate resin and dicarboxylic acid. A cosmetic film composed of 10 to 70% by weight of an amorphous polyester resin in which the component is terephthalic acid and the glycol components are 1,4-cyclohexanedimethanol and ethylene glycol has been proposed (Patent Document 1). This decorative film is excellent in surface hardness and heat resistance, but when the decorative films are laminated to form a laminated decorative sheet, the adhesiveness during heat lamination using a heating drum or the like is poor, The emboss transferability when embossing the surface was also insufficient.
Amorphous polyester resin is mainly used as a laminated decorative sheet made of polyester resin that has good heat workability such as membrane press molding, improved solvent resistance, and can be handled in the same way as conventional decorative sheets made of vinyl chloride resin. An amorphous polyester obtained by copolymerizing a base film layer as a component, a dicarboxylic acid component composed of terephthalic acid, a diol component composed of 25-35 mol% 1,4-cyclohexanedimethanol and 65-75 mol% ethylene glycol A decorative sheet in which a protective film layer composed of 40 to 95% by weight of resin and 5 to 60% by weight of polyethylene terephthalate resin or polybutylene terephthalate resin having crystallinity has been proposed (Patent Document 2). This laminated decorative sheet has good molding processability and can be embossed. However, if the laminated decorative sheet made of vinyl chloride resin is simply replaced with this polyester resin laminated decorative sheet, the heat and humidity resistance is poor and the film swells. Such a phenomenon is likely to occur. Therefore, it is not suitable for laminated decorative sheets for steel plates used for unit baths exposed to high temperature and high humidity among interior decorations in homes.
Moreover, the polyester resin coating which provided the design property which formed the uneven | corrugated pattern on the metal plate by providing the resin layer with a low crystallinity of 5 to 40 weight% which has a non-orientation crystalline polyester resin as a main component. It has been proposed that a metal plate can be obtained (Patent Document 3). This resin film is excellent in surface hardness and heat resistance, but when embossed in the state of the film before being laminated on the metal plate, the physical properties are reduced due to crystallization because the main component is a crystalline resin. At the same time, the post-emboss transfer property and the heat laminate adhesiveness were insufficient.
The present inventors previously described a modified polyester resin having a glass transition temperature of −30 ° C. or higher and lower than 20 ° C. in an amount of 3 to 97% by weight, and a dimer acid copolyester resin having a glass transition temperature of 20 ° C. or higher and lower than 50 ° C. in an amount of 0 to 94% by weight. And a flexible polyester decorative sheet composition comprising 3 to 97% by weight of a polyester resin having a glass transition temperature of 50 ° C. or more and less than 120 ° C., having a specific flow value, has a good texture, and has wrinkles and cracks during construction. It has been found that a decorative sheet suitable for a wall covering can be obtained, which is difficult to lift and is less likely to be lifted and whose defect part can be easily corrected by heating (Patent Document 4). However, this decorative sheet is also slightly inferior in heat and moisture resistance, and a phenomenon such as film swelling may occur. Therefore, it is not suitable for a decorative film for a steel sheet and a laminated decorative sheet for a steel sheet used for a unit bath exposed to high temperature and high humidity among interior decorations in a house.
本発明は、耐湿熱性、エンボス転写性に優れ、熱ラミネート加工時の層間の密着性、表面エンボスの耐シボ流れ性に優れた鋼板用化粧フィルム及び鋼板用積層化粧シートを提供することを目的としてなされたものである。 An object of the present invention is to provide a decorative film for a steel sheet and a laminated decorative sheet for a steel sheet, which are excellent in moisture and heat resistance, emboss transferability, adhesion between layers at the time of heat laminating, and excellent surface flow resistance of embossing on the surface. It was made.
本発明者らは、上記の課題を解決すべく鋭意研究を重ねた結果、樹脂成分として(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂を含有し、引張試験における２０％モジュラスが２〜２５ＭＰａであり、ボンデ鋼板にポリウレタン系二液硬化型接着剤を用い、鋼板温度２２０℃、ラミネートロール温度５０℃で圧着して得られるラミネート鋼板を、沸騰水中に３０分間浸漬したのち目視観察する耐沸騰水性試験において、表面に膨れが認められない化粧フィルムは、鋼板用化粧フィルムとして優れた性能を有し、該化粧フィルムを積層して得られる積層化粧シートも、鋼板用積層化粧シートとして優れた性能を有することを見いだし、この知見に基づいて本発明を完成するに至った。
すなわち本発明は、
（１）樹脂成分として、(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂を含有し、引張試験における２０％モジュラスが、２〜２５ＭＰａであり、ボンデ鋼板にポリウレタン系二液硬化型接着剤を用い、鋼板温度２２０℃、ラミネートロール温度５０℃で圧着して得られるラミネート鋼板を、沸騰水中に３０分間浸漬したのち目視観察する耐沸騰水性試験において、表面に膨れが認められないことを特徴とする鋼板用化粧フィルム、
（２）樹脂成分として、(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂３０〜９７重量％と、(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂３〜７０重量％を含有する第１項記載の鋼板用化粧フィルム、
（３）樹脂成分として、(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂４０〜９７重量％と、(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂３〜６０重量％を含有する第１項記載の鋼板用化粧フィルム、
（４）樹脂成分として、(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂３６〜９４重量％、(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂４〜６８重量％及び(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂３〜６０重量％を含有する第１項記載の鋼板用化粧フィルム、
（５）樹脂成分が、(Ｄ)メタクリル酸メチル−ブタジエン−スチレン共重合体（ＭＢＳ）、アクリロニトリル−ブタジエン−スチレン共重合体（ＡＢＳ）、アクリロニトリル−エチレンプロピレンゴム−スチレン共重合体（ＡＥＳ）、アクリロニトリル−アクリル酸エステル−スチレン共重合体（ＡＡＳ）、メタクリル酸エステル／アクリル酸エステルゴムグラフト共重合体、メタクリル酸エステル−アクリロニトリル／アクリル酸エステルゴムグラフト共重合体、熱可塑性ポリエステルエラストマー（ＴＰＥＥ）又は熱可塑性ウレタンエラストマー１〜５０重量％を含有する第１項ないし第４項のいずれかに記載の鋼板用化粧フィルム、
（６）樹脂成分１００重量部に対して、(Ｅ)滑剤０.２〜１０重量部を含有し、カレンダー加工機を用いて製膜してなる第１項ないし第５項のいずれかに記載の鋼板用化粧フィルム、
（７）顔料を含有し、隠蔽率が０.９５以上である第１項ないし第６項のいずれかに記載の鋼板用化粧フィルム、
（８）上面にエンボス加工されてなる第１項ないし第７項のいずれかに記載の鋼板用化粧フィルム、
（９）上面に二液硬化型トップコート又は紫外線硬化型トップコートを有する第７項又は第８項記載の鋼板用化粧フィルム、
（１０）上地が、第１項ないし第６項のいずれかに記載の透明な鋼板用化粧フィルムであり、下地が、第７項記載の鋼板用化粧フィルムであり、上地と下地が積層されてなることを特徴とする鋼板用積層化粧シート、
（１１）上地が、第１項ないし第６項のいずれかに記載の透明な鋼板用化粧フィルムであり、下地が、樹脂成分として、(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂１０〜６０重量％と、(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂４０〜９０重量％を含有する化粧フィルムであり、上地と下地が積層されてなることを特徴とする鋼板用積層化粧シート、
（１２）上地が、二軸延伸ポリエチレンテレフタレートフィルムであり、下地が、第７項記載の鋼板用化粧フィルムであり、上地と下地が積層されてなることを特徴とする鋼板用積層化粧シート、
（１３）上地が、第７項記載の鋼板用化粧フィルムであり、下地が、二軸延伸ポリエチレンテレフタレートフィルムであり、上地と下地が積層されてなることを特徴とする鋼板用積層化粧シート、
（１４）上地が、第１項ないし第６項のいずれかに記載の透明な鋼板用化粧フィルムであり、下地が、樹脂成分として、(Ｆ)ポリトリメチレンテレフタレート系樹脂を含有する化粧フィルムであり、上地と下地が積層されてなることを特徴とする鋼板用化粧シート、
（１５）上地の厚さが１０〜４００μｍであり、下地の厚さが１０〜４００μｍである第１０項ないし第１４項のいずれかに記載の鋼板用積層化粧シート、
（１６）積層した上地の上面若しくは下面又は下地の上面にエンボス加工されてなる第１０項ないし第１５項のいずれかに記載の鋼板用積層化粧シート、及び、
（１７）積層した上地の上面に二液硬化型トップコート又は紫外線硬化型トップコートを有する第１０項ないし第１６項のいずれかに記載の鋼板用積層化粧シート、
を提供するものである。
As a result of intensive studies to solve the above-mentioned problems, the present inventors contain (A) a modified polyethylene terephthalate resin having a glass transition temperature of -10 to 40 ° C. as a resin component, and a 20% modulus in a tensile test. 2-25 MPa, a laminated steel sheet obtained by pressure bonding at a steel sheet temperature of 220 ° C. and a laminating roll temperature of 50 ° C. using a polyurethane-based two-component curable adhesive on a bonde steel sheet, and then visually observed after being immersed in boiling water for 30 minutes In the boiling water resistance test to be observed, the decorative film in which no swelling is observed on the surface has excellent performance as a decorative film for steel sheet, and the laminated decorative sheet obtained by laminating the decorative film is also a laminated decorative sheet for steel sheet As a result, the present invention has been completed based on this finding.
That is, the present invention
(1) As a resin component, it contains (A) a modified polyethylene terephthalate resin having a glass transition temperature of −10 to 40 ° C., and a 20% modulus in a tensile test is 2 to 25 MPa. In a boiling water resistance test in which a laminated steel sheet obtained by pressure bonding using a mold adhesive at a steel plate temperature of 220 ° C. and a laminating roll temperature of 50 ° C. is immersed in boiling water for 30 minutes and then visually observed, no swelling is observed on the surface. A decorative film for steel sheet,
(2) As a resin component, (A) 30 to 97% by weight of a modified polyethylene terephthalate resin having a glass transition temperature of −10 to 40 ° C. and (B) an amorphous polyethylene terephthalate resin 3 having a glass transition temperature of 50 to 120 ° C. The decorative film for steel sheet according to claim 1, containing 70% by weight,
(3) As a resin component, (A) modified polyethylene terephthalate resin 40 to 97% by weight having a glass transition temperature of −10 to 40 ° C. and (C) polybutylene terephthalate resin 3 to 60 having a glass transition temperature of 20 to 50 ° C. The decorative film for steel sheet according to claim 1, which contains wt%,
(4) As resin components, (A) 36 to 94% by weight of a modified polyethylene terephthalate resin having a glass transition temperature of −10 to 40 ° C., and (B) an amorphous polyethylene terephthalate resin 4 to 4 having a glass transition temperature of 50 to 120 ° C. 68% by weight and (C) a decorative film for steel sheet according to item 1, which contains 3 to 60% by weight of a polybutylene terephthalate resin having a glass transition temperature of 20 to 50 ° C.
(5) The resin component is (D) methyl methacrylate-butadiene-styrene copolymer (MBS), acrylonitrile-butadiene-styrene copolymer (ABS), acrylonitrile-ethylenepropylene rubber-styrene copolymer (AES), Acrylonitrile-acrylic ester-styrene copolymer (AAS), methacrylic ester / acrylic ester rubber graft copolymer, methacrylic ester-acrylonitrile / acrylic ester rubber graft copolymer, thermoplastic polyester elastomer (TPEE) or The decorative film for steel sheet according to any one of items 1 to 4, comprising 1 to 50% by weight of a thermoplastic urethane elastomer,
(6) The resin composition according to any one of items 1 to 5, wherein the resin component is contained in an amount of 0.2 to 10 parts by weight with respect to 100 parts by weight of the resin component, and is formed using a calendering machine. Decorative film for steel sheet,
(7) A decorative film for steel sheet according to any one of items 1 to 6, which contains a pigment and has a concealment ratio of 0.95 or more,
(8) The decorative film for steel sheet according to any one of items 1 to 7, wherein the upper surface is embossed,
(9) The decorative film for steel sheet according to item 7 or 8, having a two-component curable topcoat or an ultraviolet curable topcoat on the upper surface,
(10) The top is the transparent steel sheet decorative film according to any one of Items 1 to 6, the base is the steel sheet decorative film according to Item 7, and the top and base are laminated. Laminated decorative sheet for steel sheet, characterized in that
(11) The top is the transparent decorative film for steel sheet according to any one of items 1 to 6, and the base is a resin component. (B) Amorphous having a glass transition temperature of 50 to 120 ° C It is a decorative film containing 10 to 60% by weight of a polyethylene terephthalate resin and (C) 40 to 90% by weight of a polybutylene terephthalate resin having a glass transition temperature of 20 to 50 ° C. Laminated decorative sheet for steel sheet, characterized by
(12) A laminated decorative sheet for steel sheet, wherein the upper layer is a biaxially stretched polyethylene terephthalate film, the lower layer is the decorative film for steel sheet according to item 7, and the upper layer and the lower layer are laminated. ,
(13) A laminated decorative sheet for steel sheet, wherein the upper layer is the decorative film for steel sheet according to item 7, the base is a biaxially stretched polyethylene terephthalate film, and the upper and base are laminated. ,
(14) The decorative film for transparent steel sheet according to any one of items 1 to 6, wherein the base is (F) a polytrimethylene terephthalate resin as a resin component. A decorative sheet for steel sheet, wherein the upper and lower layers are laminated,
(15) The laminated decorative sheet for steel sheet according to any one of items 10 to 14, wherein the upper layer has a thickness of 10 to 400 μm and the lower layer has a thickness of 10 to 400 μm,
(16) The laminated decorative sheet for steel sheet according to any one of items 10 to 15, which is embossed on the upper surface or lower surface of the laminated upper surface or the upper surface of the base material, and
(17) The laminated decorative sheet for steel sheet according to any one of items 10 to 16, having a two-component curable topcoat or an ultraviolet curable topcoat on the upper surface of the laminated upper layer,
Is to provide.
本発明の鋼板用化粧フィルム及び鋼板用積層化粧シートは、耐湿熱性、エンボス転写性が良好であり、熱ラミネート加工時の層間の密着性、表面エンボスの耐シボ流れ性にも優れ、高温多湿の環境においても、安定して使用することができる。 The decorative film for steel sheet and laminated decorative sheet for steel sheet of the present invention have good moisture and heat resistance, emboss transferability, excellent adhesion between layers at the time of heat laminating, and resistance to wrinkle of surface embossing, high temperature and high humidity. It can be used stably even in the environment.
本発明の鋼板用化粧フィルムは、樹脂成分として、(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂を含有し、引張試験における２０％モジュラスが、２〜２５ＭＰａであり、ボンデ鋼板にポリウレタン系二液硬化型接着剤を用い、鋼板温度２２０℃、ラミネートロール温度５０℃で圧着して得られるラミネート鋼板を、沸騰水中に３０分間浸漬したのち目視観察する耐沸騰水性試験において、表面に膨れが認められない鋼板用化粧フィルムである。
本発明に用いる(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂としては、例えば、テレフタル酸、イソフタル酸、ナフタレンジカルボン酸などをジカルボン酸成分とし、エチレングリコール、トリメチレングリコール、テトラメチレングリコール、ポリエチレングリコール、ポリテトラメチレングリコール、ネオペンチルグリコール、シクロヘキサンジメタノール、ビスフェノール化合物のエチレンオキサイド付加物などをグリコール成分として共重合した変性ポリエチレンテレフタレート系樹脂などを挙げることができる。これらの中で、ジカルボン酸成分がテレフタル酸であり、グリコール成分がエチレングリコールとポリテトラメチレングリコールと１,４−シクロヘキサンジメタノールを主体として共重合した変性ポリエチレンテレフタレート系樹脂を特に好適に用いることができる。
The decorative film for steel sheet of the present invention contains (A) a modified polyethylene terephthalate resin having a glass transition temperature of −10 to 40 ° C. as a resin component, and a 20% modulus in a tensile test is 2 to 25 MPa. In a boiling water resistance test in which a laminated steel sheet obtained by pressure bonding at a steel plate temperature of 220 ° C. and a laminating roll temperature of 50 ° C. is immersed in boiling water for 30 minutes and then visually observed. It is a decorative film for steel plates in which no swelling is observed.
Examples of the modified polyethylene terephthalate resin (A) having a glass transition temperature of −10 to 40 ° C. used in the present invention include terephthalic acid, isophthalic acid, naphthalenedicarboxylic acid and the like as dicarboxylic acid components, ethylene glycol, trimethylene glycol, tetra Examples include methylene glycol, polyethylene glycol, polytetramethylene glycol, neopentyl glycol, cyclohexanedimethanol, and a modified polyethylene terephthalate resin copolymerized as a glycol component with an ethylene oxide adduct of a bisphenol compound. Among these, it is particularly preferable to use a modified polyethylene terephthalate resin in which the dicarboxylic acid component is terephthalic acid and the glycol component is mainly copolymerized with ethylene glycol, polytetramethylene glycol, and 1,4-cyclohexanedimethanol. it can.
本発明の鋼板用化粧フィルムは、引張試験における２０％モジュラスが、２〜２５ＭＰａであり、より好ましくは３〜２０ＭＰａである。引張試験における２０％モジュラスは、あらかじめ１ｍｍの厚さにプレスした樹脂シートから、幅１５ｍｍ、長さ１５０ｍｍの試験片を切り取り、標線間距離５０ｍｍの標線を付け、２３±２℃で２４時間状態調節したのち、同じ温度で、つかみ具間距離１００ｍｍで試験片をつかみ、引張速度５０ｍｍ／分で引張試験を行い、伸び２０％のときの引張応力を読み取り、試験片の元の断面積で除して、２０％モジュラスを算出することができる。２０％モジュラスが２ＭＰａ未満であると、フィルムの傷つき性が悪くなるとともに、熱ラミネート加工時に加熱ドラムからの剥離が困難となり、加工性が悪くなるおそれがある。２０％モジュラスが２５ＭＰａを超えると、耐湿熱性が悪くなるおそれがある。 The decorative film for steel sheet of the present invention has a 20% modulus in a tensile test of 2 to 25 MPa, more preferably 3 to 20 MPa. For the 20% modulus in the tensile test, a test piece having a width of 15 mm and a length of 150 mm is cut from a resin sheet that has been previously pressed to a thickness of 1 mm, and a marked line with a distance between marked lines of 50 mm is attached to it at 23 ± 2 ° C. for 24 hours. After adjusting the condition, hold the test piece at the same temperature and the distance between the grips of 100 mm, conduct a tensile test at a tensile speed of 50 mm / min, read the tensile stress when the elongation is 20%, and use the original cross-sectional area of the test piece. By dividing, the 20% modulus can be calculated. If the 20% modulus is less than 2 MPa, the scratching property of the film is deteriorated, and peeling from the heating drum becomes difficult during the heat laminating process, and the workability may be deteriorated. If the 20% modulus exceeds 25 MPa, the heat and humidity resistance may deteriorate.
本発明の鋼板用化粧フィルムは、ボンデ鋼板にポリウレタン系二液硬化型接着剤を用い、鋼板温度２２０℃、ラミネートロール温度５０℃で圧着して得られるラミネート鋼板を、沸騰水中に３０分間浸漬したのち目視観察する耐沸騰水性試験において、表面に膨れが認められない。ボンデ鋼板は、電気亜鉛めっき鋼板にリン酸塩処理を施した鋼板である。ポリウレタン系二液硬化型接着剤は、末端にヒドロキシル基を有する主剤とイソシアネート基を有する硬化剤からなる接着剤であり、例えば、ソニーケミカル(株)のＳＣ６１１などを挙げることができる。ポリウレタン系二液硬化型接着剤を用いて、本発明の鋼板用化粧フィルムを鋼板に積層して得られるラミネート鋼板は、耐湿熱性が良好であり、沸騰水中に３０分間浸漬しても、表面に変化が全く生じない。したがって、本発明の鋼板用化粧フィルム又は鋼板用積層化粧シートを用いて製造されたラミネート鋼板は、ユニットバスなどの高温多湿の環境に曝される用途に好適に用いることができる。耐湿熱性に劣るラミネート鋼板は、沸騰水中に３０分間浸漬すると、表面に膨れが生じたり、剥離しやすくなったりする。このようなラミネート鋼板は、高温多湿の環境における使用には適さない。 The decorative film for steel sheet of the present invention is obtained by immersing a laminated steel sheet obtained by pressure bonding a bonded steel sheet at a steel sheet temperature of 220 ° C. and a laminating roll temperature of 50 ° C. for 30 minutes using a polyurethane-based two-component curable adhesive. Later, in the boiling water resistance test visually observed, no swelling is observed on the surface. The bonde steel sheet is a steel sheet obtained by subjecting an electrogalvanized steel sheet to a phosphate treatment. The polyurethane two-component curable adhesive is an adhesive composed of a main agent having a hydroxyl group at a terminal and a curing agent having an isocyanate group, and examples thereof include SC611 manufactured by Sony Chemical Corporation. A laminated steel sheet obtained by laminating a decorative film for steel sheet of the present invention on a steel sheet using a polyurethane two-component curable adhesive has good heat and humidity resistance, and even if immersed in boiling water for 30 minutes, No change occurs. Therefore, the laminated steel plate manufactured using the decorative film for steel plate or the laminated decorative sheet for steel plate of the present invention can be suitably used for applications exposed to high-temperature and high-humidity environments such as unit baths. When a laminated steel sheet having poor heat-and-moisture resistance is immersed in boiling water for 30 minutes, the surface is swollen or easily peeled off. Such a laminated steel sheet is not suitable for use in a hot and humid environment.
本発明の鋼板用化粧フィルムは、樹脂成分として、(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂３０〜９７重量％と(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂３〜７０重量％を含有することができ、より好ましくは、(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂５５〜８５重量％と(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂１５〜４５重量％を含有することができる。(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂としては、例えば、ジカルボン酸成分がテレフタル酸であり、グリコール成分がエチレングリコール６０モル％以上９０モル％未満と１,４−シクロヘキサンジメタノール１０モル％以上４０モル％未満であるポリエチレンテレフタレート系共重合体、ジカルボン酸成分がテレフタル酸であり、グリコール成分がエチレングリコール１０モル％以上６０モル％未満と１,４−シクロヘキサンジメタノール４０モル％以上９０モル％未満であるポリエチレンテレフタレート系共重合体、さらにジカルボン酸成分がテレフタル酸であり、グリコール成分がエチレングリコール６０〜９０モル％とネオペンチルグリコール又はネオペンチルグリコールとジエチレングリコール１０〜４０モル％であるネオペンチルグリコール共重合ポリエチレンテレフタレート系共重合体などを挙げることができる。樹脂成分として、(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂を含有させることにより、製膜加工性を向上することができる。 The decorative film for steel sheet of the present invention has, as resin components, (A) 30 to 97% by weight of a modified polyethylene terephthalate resin having a glass transition temperature of −10 to 40 ° C. and (B) an amorphous property having a glass transition temperature of 50 to 120 ° C. 3 to 70% by weight of a polyethylene terephthalate resin can be contained, and more preferably, (A) 55 to 85% by weight of a modified polyethylene terephthalate resin having a glass transition temperature of −10 to 40 ° C. and (B) a glass transition temperature of 50. It can contain 15 to 45% by weight of an amorphous polyethylene terephthalate resin at ˜120 ° C. (B) As an amorphous polyethylene terephthalate resin having a glass transition temperature of 50 to 120 ° C., for example, the dicarboxylic acid component is terephthalic acid, and the glycol component is 60 mol% or more and less than 90 mol% of ethylene glycol. Polyethylene terephthalate copolymer of 10 mol% or more and less than 40 mol% of cyclohexane dimethanol, the dicarboxylic acid component is terephthalic acid, and the glycol component is 10 mol% or more and less than 60 mol% of 1,4-cyclohexane dimethanol. Polyethylene terephthalate copolymer of 40 mol% or more and less than 90 mol%, further dicarboxylic acid component is terephthalic acid, glycol component is ethylene glycol 60-90 mol% and neopentyl glycol or neopentyl glycol and diethylene glycol Examples thereof include neopentyl glycol copolymerized polyethylene terephthalate copolymer having 10 to 40 mol%. By incorporating (B) an amorphous polyethylene terephthalate resin having a glass transition temperature of 50 to 120 ° C. as the resin component, film forming processability can be improved.
本発明の鋼板用化粧フィルムは、樹脂成分として、(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂４０〜９７重量％と(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂３〜６０重量％を含有することができ、より好ましくは、(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂５５〜８５重量％と(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂１５〜４５重量％を含有することができる。(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂としては、例えば、ポリブチレンテレフタレート樹脂、ジカルボン酸成分がテレフタル酸とイソフタル酸であり、グリコール成分がテトラメチレングリコールであるポリブチレンテレフタレート系樹脂などを挙げることができる。樹脂成分として、(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂を含有させることにより、耐湿熱性と耐熱性を向上することができる。 The decorative film for steel sheet of the present invention comprises (A) 40 to 97% by weight of a modified polyethylene terephthalate resin having a glass transition temperature of −10 to 40 ° C. and (C) a polybutylene terephthalate having a glass transition temperature of 20 to 50 ° C. 3 to 60% by weight of a resin, more preferably, (A) 55 to 85% by weight of a modified polyethylene terephthalate resin having a glass transition temperature of −10 to 40 ° C. and (C) a glass transition temperature of 20 to 50. The polybutylene terephthalate resin at 15 ° C. can be contained in an amount of 15 to 45 wt%. (C) Polybutylene terephthalate resin having a glass transition temperature of 20 to 50 ° C., for example, polybutylene terephthalate resin, polybutylene terephthalate resin in which the dicarboxylic acid component is terephthalic acid and isophthalic acid, and the glycol component is tetramethylene glycol Examples thereof include resins. By including (C) a polybutylene terephthalate resin having a glass transition temperature of 20 to 50 ° C. as the resin component, it is possible to improve the heat and moisture resistance and heat resistance.
本発明の鋼板用化粧フィルムは、樹脂成分として、(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂３６〜９４重量％、(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂４〜６８重量％及び(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂３〜６０重量％を含有することができ、より好ましくは、(Ａ)ガラス転移温度−１０〜４０℃の変性ポリエチレンテレフタレート系樹脂４０〜６５重量％、(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂１５〜５０重量％及び(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂５〜３５重量％を含有することができる。(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂と(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂を含有させることにより、製膜加工性が良く、しかも耐湿熱性と耐熱性が向上したフィルムをつくることができる。 The decorative film for steel sheet of the present invention has, as a resin component, (A) 36 to 94% by weight of a modified polyethylene terephthalate resin having a glass transition temperature of −10 to 40 ° C. and (B) an amorphous property having a glass transition temperature of 50 to 120 ° C. 4 to 68% by weight of a polyethylene terephthalate resin and (C) 3 to 60% by weight of a polybutylene terephthalate resin having a glass transition temperature of 20 to 50 ° C. can be contained, more preferably (A) a glass transition temperature of −10. 40 to 65% by weight of a modified polyethylene terephthalate resin at -40 ° C, (B) 15 to 50% by weight of an amorphous polyethylene terephthalate resin at a glass transition temperature of 50 to 120 ° C, and (C) a glass transition temperature of 20 to 50 ° C. The polybutylene terephthalate resin can be contained in an amount of 5 to 35% by weight. By including (B) an amorphous polyethylene terephthalate resin having a glass transition temperature of 50 to 120 ° C. and (C) a polybutylene terephthalate resin having a glass transition temperature of 20 to 50 ° C., the film forming processability is good and moisture resistance is improved. Films with improved heat and heat resistance can be produced.
本発明の鋼板用化粧フィルムは、樹脂成分が、(Ｄ)メタクリル酸メチル−ブタジエン−スチレン共重合体（ＭＢＳ）、アクリロニトリル−ブタジエン−スチレン共重合体（ＡＢＳ）、アクリロニトリル−エチレンプロピレンゴム−スチレン共重合体（ＡＥＳ）、アクリロニトリル−アクリル酸エステル−スチレン共重合体（ＡＡＳ）、メタクリル酸エステル／アクリル酸エステルゴムグラフト共重合体、メタクリル酸エステル−アクリロニトリル／アクリル酸エステルゴムグラフト共重合体、熱可塑性ポリエステルエラストマー（ＴＰＥＥ）、熱可塑性ウレタンエラストマーなどのエラストマーを含有することができる。これらのエラストマーの含有量は、１〜５０重量％であることが好ましく、３〜２５重量％であることがより好ましい。これらのエラストマーを含有させることにより、化粧フィルムの低温特性を向上し、低温時におけるワレの発生を防止することができる。 In the decorative film for steel sheet of the present invention, the resin component is (D) methyl methacrylate-butadiene-styrene copolymer (MBS), acrylonitrile-butadiene-styrene copolymer (ABS), acrylonitrile-ethylenepropylene rubber-styrene copolymer. Polymer (AES), acrylonitrile-acrylic ester-styrene copolymer (AAS), methacrylic ester / acrylic ester rubber graft copolymer, methacrylic ester-acrylonitrile / acrylic ester rubber graft copolymer, thermoplastic Elastomers such as polyester elastomer (TPEE) and thermoplastic urethane elastomer can be contained. The content of these elastomers is preferably 1 to 50% by weight, and more preferably 3 to 25% by weight. By containing these elastomers, the low temperature characteristics of the decorative film can be improved, and the occurrence of cracks at low temperatures can be prevented.
本発明の鋼板用化粧フィルムを製造する方法に特に制限はなく、例えば、カレンダー加工機を用いて製膜することができ、あるいは、押出機とＴダイを用いて製膜することもできる。使用するカレンダー加工機に特に制限はなく、例えば、直立型３本ロール、直立型４本ロール、Ｌ型４本ロール、逆Ｌ型４本ロール、Ｚ型ロールなどを挙げることができる。使用する押出機に特に制限はなく、例えば、単軸押出機、同方向回転二軸押出機、異方向回転二軸押出機などを挙げることができる。使用するＴダイに特に制限はなく、例えば、マニホールドダイ、フィッシュテールダイ、コートハンガーダイなどを挙げることができる。
本発明の鋼板用化粧フィルムをカレンダー加工機を用いて製造するとき、樹脂成分１００重量部に対して(Ｆ)滑剤０.２〜１０重量部を含有させることが好ましく、０.５〜５重量部を含有させることがより好ましい。含有させる滑剤に特に制限はなく、例えば、パラフィンワックス、ホリエチレンワックス、ポリプロピレンワックスなどの炭化水素系ワックス、ステアリン酸、ヒドロキシステアリン酸、複合型ステアリン酸、オレイン酸などの脂肪酸系ワックス、ステアリン酸アミド、オキシステアリン酸アミド、オレイン酸アミド、エルシルアミド、リシノール酸アミド、ベヘン酸アミド、メチレンビスステアリン酸アミド、エチレンビスステアリン酸アミドなどの脂肪族アミド系ワックス、ステアリン酸ｎ−ブチル、モンタン酸エステルワックスなどの脂肪族エステル系ワックス、脂肪族金属石けん系ワックス、尿素−ホルムアルデヒドワックスなどを挙げることができる。これらの中で、脂肪族エステル系ワックスは、非晶質ポリエステル樹脂との相溶性が良好であり、樹脂組成物の透明性を損なうことなく、成形性を向上することができるので、特に好適に用いることができる。
There is no restriction | limiting in particular in the method to manufacture the decorative film for steel plates of this invention, For example, it can form into a film using a calendar processing machine, or can also form into a film using an extruder and T-die. There is no restriction | limiting in particular in the calendar processing machine to be used, For example, an upright type 3 roll, an upright type 4 roll, an L type 4 roll, a reverse L type 4 roll, a Z type roll etc. can be mentioned. There is no restriction | limiting in particular in the extruder to be used, For example, a single screw extruder, the same direction rotation twin screw extruder, a different direction rotation twin screw extruder etc. can be mentioned. There is no restriction | limiting in particular in T die to be used, For example, a manifold die, a fish tail die, a coat hanger die, etc. can be mentioned.
When the decorative film for steel sheet of the present invention is produced using a calendar processing machine, it is preferable to contain 0.2 to 10 parts by weight of (F) lubricant with respect to 100 parts by weight of the resin component, and 0.5 to 5 weights. It is more preferable to contain a part. The lubricant to be contained is not particularly limited, and examples thereof include hydrocarbon waxes such as paraffin wax, polyethylene wax and polypropylene wax, stearic acid, hydroxystearic acid, complex stearic acid, fatty acid wax such as oleic acid, and stearamide. , Aliphatic amide waxes such as oxystearic acid amide, oleic acid amide, erucyl amide, ricinoleic acid amide, behenic acid amide, methylene bis stearic acid amide, ethylene bis stearic acid amide, stearic acid n-butyl, montanic acid ester wax, etc. Examples thereof include aliphatic ester waxes, aliphatic metal soap waxes, urea-formaldehyde waxes, and the like. Among these, aliphatic ester waxes are particularly suitable because they have good compatibility with amorphous polyester resins and can improve moldability without impairing the transparency of the resin composition. Can be used.
本発明の鋼板用化粧フィルムは、顔料を含有させて隠蔽性を付与することができる。含有させる顔料に特に制限はなく、例えば、白色顔料としての酸化チタンを配合することにより隠蔽性を付与することができ、あるいは、黒色顔料としてのカーボンブラックを配合することにより隠蔽性を付与することもでき、さらには、白色顔料と他の有色顔料を配合することにより所望の色調と濃度の隠蔽性を付与することもできる。本発明の鋼板用化粧フィルムにおいて、顔料を含有する化粧フィルムの隠蔽率は０.９５以上であることが好ましく、０.９７以上であることがより好ましく、０.９９以上であることがさらに好ましい。隠蔽率が０.９５未満であると、化粧フィルムを鋼板と積層して得られるラミネート鋼板の外観が、基材である鋼板の色調に影響されるおそれがある。化粧フィルムの隠蔽率は、ＪＩＳ Ｋ ５４００ ７.２に準じて測定することができる。視感反射率８０±１の白地と、視感反射率２以下の黒地に塗り分けたアート紙を隠蔽率試験紙とし、隠蔽率試験紙に化粧フィルムを重ねて視感反射率を測定し、黒地の上の化粧フィルムの視感反射率をＢ、白地の上の化粧フィルムの視感反射率をＷとすると、隠蔽率ＨＰは次式により求めることができる。
ＨＰ ＝ Ｂ／Ｗ
視感反射率が０.９８になると、肉眼では白地の上と黒地の上を識別することができない。化粧フィルムを積層する鋼板には、白地と黒地のような極端な色調の差はないので、隠蔽率０.９５以上の鋼板用化粧フィルムにより均一な色調のラミネート鋼板を安定して製造することができる。
The decorative film for steel sheet of the present invention can be provided with a hiding property by containing a pigment. There is no particular limitation on the pigment to be included, for example, concealment can be imparted by blending titanium oxide as a white pigment, or concealment can be imparted by blending carbon black as a black pigment. Furthermore, the desired color tone and density can be concealed by blending a white pigment with another colored pigment. In the decorative film for steel sheet of the present invention, the concealment rate of the decorative film containing a pigment is preferably 0.95 or more, more preferably 0.97 or more, and further preferably 0.99 or more. . If the concealment ratio is less than 0.95, the appearance of the laminated steel sheet obtained by laminating the decorative film with the steel sheet may be affected by the color tone of the steel sheet as the base material. The concealment rate of the decorative film can be measured according to JIS K 5400 7.2. Art paper coated on a white background with a luminous reflectance of 80 ± 1 and a black background with a luminous reflectance of 2 or less was used as a concealment rate test paper, and a decorative film was placed on the concealment rate test paper to measure the luminous reflectance. If the luminous reflectance of the decorative film on the black background is B and the luminous reflectance of the decorative film on the white background is W, the concealment ratio HP can be obtained by the following equation.
HP = B / W
If the luminous reflectance is 0.98, the naked eye cannot distinguish between a white background and a black background. Since there is no extreme color difference between white and black on the steel sheets on which the decorative film is laminated, it is possible to stably produce a laminated steel sheet with a uniform color by using a decorative film for steel sheets with a concealment rate of 0.95 or more. it can.
本発明の鋼板用化粧フィルムには、必要に応じて、エンボス加工を施すことができる。エンボス加工の方法に特に制限はなく、例えば、オンラインで製膜と同時にエンボス加工することができ、あるいは、オフラインでドラム加熱型エンボッサー、マルチシリンダー型エンボッサーなどを用いる、いわゆるアフターエンボス加工をすることもできる。
本発明の鋼板用化粧フィルムは、表面に二液硬化型トップコート又は紫外線硬化型トップコートを有することができる。表面にトップコートを施すことにより、鋼板用化粧フィルムの耐擦傷性を向上し、表面に傷のつきにくい優れた鋼板用化粧フィルムを得ることができる。二液硬化型トップコートは、例えば、ポリオール成分とポリイソシアネート成分からなる二液型ポリウレタン系コーティング剤を塗布して硬化させることにより形成することができる。紫外線硬化型トップコートは、コート層の紫外線硬化波長とは異なる波長帯の特性吸収波長を有し、材料劣化を引き起こす特定の紫外線を吸収する紫外線吸収剤と光安定剤を含む材料を鋼板用化粧フィルムに塗布して、紫外線硬化することにより形成することができる。
The decorative film for steel sheet of the present invention can be embossed as necessary. There is no particular limitation on the embossing method. For example, embossing can be performed at the same time as film formation online, or so-called after embossing using a drum heating embosser, multi-cylinder embosser, etc. can be performed offline. it can.
The decorative film for steel sheet of the present invention can have a two-component curable top coat or an ultraviolet curable top coat on the surface. By applying the top coat to the surface, the scratch resistance of the decorative film for steel sheet can be improved, and an excellent decorative film for steel sheet that is hard to be scratched on the surface can be obtained. The two-component curable topcoat can be formed, for example, by applying and curing a two-component polyurethane coating agent comprising a polyol component and a polyisocyanate component. The UV-curable topcoat has a characteristic absorption wavelength in a wavelength band different from the UV curing wavelength of the coating layer, and a material containing a UV absorber and a light stabilizer that absorbs specific UV light that causes material deterioration It can be formed by applying to a film and curing with ultraviolet light.
本発明の鋼板用積層化粧シートの第一の態様は、上地が、本発明の透明な鋼板用化粧フィルムであり、下地が、顔料を含有し、隠蔽率が０.９５以上である本発明の鋼板用化粧フィルムであり、上地と下地が積層されてなる積層化粧シートである。上地と下地の両方の化粧フィルムを同質の樹脂成分とすることにより、ラミネート性を向上して大きい接着強度を得ることができる。
本発明の鋼板用積層化粧シートの第二の態様は、上地が、本発明の透明な鋼板用化粧フィルムであり、下地が、樹脂成分として、(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂１０〜６０重量％と、(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂４０〜９０重量％を含有する鋼板用化粧フィルムであり、上地と下地が積層されてなる積層化粧シートである。下地に、樹脂成分として、(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂と(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂を含有する化粧フィルムを用いることにより、耐湿熱性と耐熱性を向上することができる。
The first aspect of the laminated decorative sheet for steel sheet of the present invention is the present invention wherein the upper layer is the transparent decorative film for steel sheet of the present invention, the underlayer contains a pigment, and the concealment rate is 0.95 or more. It is a laminated decorative sheet for steel sheets, and is a laminated decorative sheet in which an upper and a base are laminated. By making the decorative film of both the upper and lower layers into the same resin component, the laminating property can be improved and a large adhesive strength can be obtained.
In the second aspect of the laminated decorative sheet for steel sheet of the present invention, the upper is the transparent decorative film for steel sheet of the present invention, and the base is a resin component (B) having a glass transition temperature of 50 to 120 ° C. A decorative film for steel sheet containing 10 to 60% by weight of a crystalline polyethylene terephthalate resin and (C) 40 to 90% by weight of a polybutylene terephthalate resin having a glass transition temperature of 20 to 50 ° C. This is a laminated decorative sheet. For the base, a decorative film containing (B) an amorphous polyethylene terephthalate resin having a glass transition temperature of 50 to 120 ° C. and (C) a polybutylene terephthalate resin having a glass transition temperature of 20 to 50 ° C. is used as the resin component. As a result, heat and moisture resistance and heat resistance can be improved.
本発明の鋼板用積層化粧シートの第三の態様は、上地が、二軸延伸ポリエチレンテレフタレートフィルムであり、下地が、顔料を含有し、隠蔽率が０.９５以上である本発明の鋼板用化粧フィルムであり、上地と下地が積層されてなる積層化粧シートである。二軸延伸ポリエチレンテレフタレートフィルムは、変性ポリエチレンテレフタレート系樹脂フィルムに比べてさらに耐湿熱性が良好であり、また、上地として、二軸延伸ポリエチレンテレフタレートフィルムを積層することにより、表面に傷がつきにくい鋼板用積層化粧シートを得ることができる。
本発明の鋼板用積層化粧シートの第四の態様は、上地が、顔料を含有し、隠蔽率が０.９５以上である本発明の鋼板用化粧フィルムであり、下地が、二軸延伸ポリエチレンテレフタレートフィルムであり、上地と下地が積層されてなる積層化粧シートである。上地に顔料を含有する化粧フィルムを用い、下地に二軸延伸ポリエチレンテレフタレートフィルムを用いることにより、化粧フィルムの伸縮を小さくすることができる。
The third aspect of the laminated decorative sheet for steel sheet of the present invention is for the steel sheet of the present invention in which the top is a biaxially stretched polyethylene terephthalate film, the ground contains a pigment, and the concealment rate is 0.95 or more. It is a decorative film, and is a laminated decorative sheet in which an upper and a base are laminated. Biaxially stretched polyethylene terephthalate film has better heat and moisture resistance compared to modified polyethylene terephthalate resin film, and the upper surface of the steel sheet is not easily damaged by laminating a biaxially stretched polyethylene terephthalate film. A laminated decorative sheet can be obtained.
A fourth aspect of the laminated decorative sheet for steel sheet according to the present invention is the decorative film for steel sheet according to the present invention, wherein the upper layer contains a pigment and the concealment rate is 0.95 or more, and the base is a biaxially stretched polyethylene. It is a terephthalate film, and is a laminated decorative sheet in which an upper and a base are laminated. By using a decorative film containing a pigment on the top and a biaxially stretched polyethylene terephthalate film on the base, the expansion and contraction of the decorative film can be reduced.
本発明の鋼板用積層化粧シートの第五の態様は、上地が、本発明の透明な鋼板用化粧フィルムであり、下地が、樹脂成分として、(Ｆ)ポリトリメチレンテレフタレート系樹脂を含有する化粧フィルムであり、上地と下地が積層されてなる積層化粧シートである。(Ｆ)ポリトリメチレンテレフタレート系樹脂は、例えば、ジカルボン酸成分がテレフタル酸であり、グリコール成分の主成分がトリメチレングリコールであるポリエステル樹脂を挙げることができる。本態様の鋼板用積層化粧シートにおいては、下地に、樹脂成分として、(Ｆ)ポリトリメチレンテレフタレート系樹脂のみを含有する化粧フィルムを用いることができ、あるいは、(Ｆ)ポリトリメチレンテレフタレート系樹脂と(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂を含有する化粧フィルムを用いることもでき、(Ｆ)ポリトリメチレンテレフタレート系樹脂と(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂を含有する化粧フィルムを用いることもでき、さらには、(Ｆ)ポリトリメチレンテレフタレート系樹脂、(Ｂ)ガラス転移温度５０〜１２０℃の非晶性ポリエチレンテレフタレート系樹脂を含有する化粧フィルム及び(Ｃ)ガラス転移温度２０〜５０℃のポリブチレンテレフタレート系樹脂を含有する化粧フィルムを用いることもできる。下地に、樹脂成分として、(Ｆ)ポリトリメチレンテレフタレート系樹脂を含有する化粧フィルムを用いることにより、耐湿熱性と耐熱性を向上することができる。 According to a fifth aspect of the laminated decorative sheet for steel sheet of the present invention, the top is the transparent decorative film for steel sheet of the present invention, and the base contains (F) polytrimethylene terephthalate resin as a resin component. It is a decorative film, and is a laminated decorative sheet in which an upper and a base are laminated. Examples of the (F) polytrimethylene terephthalate resin include a polyester resin in which the dicarboxylic acid component is terephthalic acid and the glycol component is mainly trimethylene glycol. In the laminated decorative sheet for steel sheet of the present embodiment, a decorative film containing only (F) polytrimethylene terephthalate resin as the resin component can be used as the base, or (F) polytrimethylene terephthalate resin. And (B) a decorative film containing an amorphous polyethylene terephthalate resin having a glass transition temperature of 50 to 120 ° C., and (F) a polytrimethylene terephthalate resin and (C) a glass transition temperature of 20 to 50 ° C. A decorative film containing a polybutylene terephthalate resin can be used, and (F) a polytrimethylene terephthalate resin and (B) an amorphous polyethylene terephthalate resin having a glass transition temperature of 50 to 120 ° C. Decorative film and (C) polybutylene terephthalate having a glass transition temperature of 20 to 50 ° C. A decorative film containing a resin can also be used. By using a decorative film containing (F) polytrimethylene terephthalate-based resin as a resin component for the base, it is possible to improve heat and moisture resistance and heat resistance.
本発明の鋼板用積層化粧シートにおいて、上地と下地を積層する方法に特に制限はなく、例えば、熱ラミネート、ドライラミネートなどを挙げることができる。熱ラミネートにおいては、２枚の化粧フィルムを加熱ロールで圧着して貼り合わせ、冷却して鋼板用積層化粧シートとして巻き取ることができる。ドライラミネートにおいては、化粧フィルムの表面に有機溶剤に溶解した接着剤を塗工し、乾燥炉で溶剤を蒸発させて乾燥したのち、他の化粧フィルムと加熱ロールで圧着し、鋼板用積層化粧シートとして巻き取ることができる。必要に応じて、一方又は両方の接着面にあらかじめコロナ放電処理して、接着性を高めることができる。
本発明の鋼板用積層化粧シートの第一の態様、第二の態様、第三の態様、第五の態様において、上地のフィルムの裏面にバックプリント印刷層又は下地の化粧フィルムの積層面に印刷層を有することができる。印刷層を形成する方法に制限はなく、例えば、凸版、平版、凹版、孔版のいずれの版式を用いることもできる。これらの中で、凹版印刷の一種であるグラビア印刷と、凸版印刷の一種であるフレキソ印刷を好適に用いることができる。
本発明の鋼板用積層化粧シートにおいて、上地の厚さは、１０〜４００μｍであることが好ましく、１５〜２００μｍであることがより好ましく、２０〜１００μｍであることがさらに好ましい。上地の厚さが１０μｍ未満であると、破損しやすく、下地との積層が困難になるおそれがある。上地の厚さは４００μｍ以下で鋼板用積層化粧シートとして十分な性能を有し、通常は厚さが４００μｍを超える上地の必要はない。本発明の鋼板用積層化粧シートにおいて、下地の厚さは、１０〜４００μｍであることが好ましく、３０〜３００μｍであることがより好ましく、５０〜２００μｍであることがさらに好ましい。下地の厚さが１０μｍ未満であると、破損しやすく、上地との積層が困難になるおそれがある。下地の厚さは４００μｍ以下で鋼板用積層化粧シートとして十分な性能を有し、通常は厚さが４００μｍを超える下地の必要はない。
In the laminated decorative sheet for steel sheet of the present invention, there is no particular limitation on the method for laminating the upper and the base, and examples thereof include thermal lamination and dry lamination. In thermal lamination, two decorative films can be bonded together by heating rolls, cooled, and wound up as a laminated decorative sheet for steel sheets. In dry laminating, an adhesive dissolved in an organic solvent is applied to the surface of a decorative film, the solvent is evaporated in a drying furnace, and then dried, and then the laminated decorative sheet for steel sheet is pressure-bonded to another decorative film with a heating roll. Can be rolled up as If necessary, one or both of the bonding surfaces can be subjected to corona discharge treatment in advance to enhance the adhesion.
In the first aspect, the second aspect, the third aspect, and the fifth aspect of the laminated decorative sheet for steel sheet of the present invention, on the back surface of the backing film or on the laminated surface of the underlying decorative film. It can have a printing layer. There is no restriction | limiting in the method of forming a printing layer, For example, any plate type of a letterpress, a lithographic plate, an intaglio, and a stencil can also be used. Among these, gravure printing, which is a kind of intaglio printing, and flexographic printing, which is a kind of letterpress printing, can be suitably used.
In the laminated decorative sheet for steel sheet of the present invention, the thickness of the upper layer is preferably 10 to 400 μm, more preferably 15 to 200 μm, and further preferably 20 to 100 μm. If the thickness of the upper layer is less than 10 μm, it is likely to be damaged and it may be difficult to laminate the substrate. The thickness of the upper layer is 400 μm or less, which is sufficient as a laminated decorative sheet for steel sheets, and there is usually no need for an upper layer having a thickness exceeding 400 μm. In the laminated decorative sheet for steel sheet of the present invention, the thickness of the base is preferably 10 to 400 μm, more preferably 30 to 300 μm, and further preferably 50 to 200 μm. If the thickness of the base is less than 10 μm, the base is likely to be damaged and it may be difficult to laminate the base. The thickness of the base is 400 μm or less, which is sufficient as a laminated decorative sheet for steel sheets, and usually there is no need for a base having a thickness exceeding 400 μm.
本発明の鋼板用積層化粧シートには、必要に応じて、積層した上地の上面若しくは下面又は下地の上面にエンボス加工を有することができる。上地の上面にエンボス加工を有する鋼板用積層化粧シートは、上地の鋼板用化粧フィルムの製膜時にオンラインで、又は、製膜後にオフラインでエンボス加工し、エンボス加工を有する面を上面として下地の化粧フィルムと積層することにより製造することができ、あるいは、上地の鋼板用化粧フィルムと下地の化粧フィルムを積層するときにオンラインで、又は、積層後にオフラインでエンボス加工することにより製造することもできる。上地の下面にエンボス加工を有する鋼板用積層化粧シートは、上地の鋼板用化粧フィルムの製膜時にオンラインで、又は、製膜後にオフラインでエンボス加工し、エンボス加工を有する面を下面として下地の化粧フィルムと積層することにより製造することができる。下地の上面にエンボス加工を有する鋼板用積層化粧シートは、下地の化粧フィルムの製膜時にオンラインで、又は、製膜後にオフラインでエンボス加工し、エンボス加工を有する面を上面として上地の化粧フィルムと積層することにより製造することができる。 The laminated decorative sheet for steel sheet of the present invention can have embossing on the upper surface or the lower surface of the laminated upper surface or the upper surface of the underlying material, if necessary. Laminated decorative sheet for steel sheet with embossing on the upper surface of the upper surface is embossed online when forming the decorative film for upper steel sheet or offline after film formation, and the surface with embossing is the upper surface. Can be manufactured by laminating with a decorative film, or by embossing online when laminating a decorative film for a steel sheet and an underlying decorative film, or offline after lamination. You can also. The laminated decorative sheet for steel sheet with embossing on the lower surface of the upper surface is embossed online at the time of film formation of the decorative film for steel sheet of the upper surface or offline after film formation, and the surface having the embossed surface is used as the lower surface. It can manufacture by laminating | stacking with a decorative film. Laminated decorative sheet for steel sheet with embossing on the upper surface of the base is embossed online at the time of forming the base decorative film or offline after film formation, and the upper decorative film with the surface having the embossing as the upper surface It can manufacture by laminating | stacking.
本発明の鋼板用積層化粧シートは、表面に二液硬化型トップコート又は紫外線硬化型トップコートを有することができる。表面にトップコートを施すことにより、鋼板用積層化粧シートの耐擦傷性を向上し、表面に傷のつきにくい優れた鋼板用積層化粧シートを得ることができる。二液硬化型トップコートは、例えば、ポリオール成分とポリイソシアネート成分からなる二液型ポリウレタン系コーティング剤を塗布して硬化させることにより形成することができる。紫外線硬化型トップコートは、コート層の紫外線硬化波長とは異なる波長帯の特性吸収波長を有し、材料劣化を引き起こす特定の紫外線を吸収する紫外線吸収剤と光安定剤を含む材料を鋼板用積層化粧シートに塗布して、紫外線硬化することにより形成することができる。 The laminated decorative sheet for steel sheet of the present invention can have a two-component curable topcoat or an ultraviolet curable topcoat on the surface. By applying a top coat to the surface, the scratch resistance of the laminated decorative sheet for steel sheet can be improved, and an excellent laminated decorative sheet for steel sheet that is hard to be scratched on the surface can be obtained. The two-component curable topcoat can be formed, for example, by applying and curing a two-component polyurethane coating agent comprising a polyol component and a polyisocyanate component. The UV-curable topcoat has a characteristic absorption wavelength in a wavelength band different from the UV-curing wavelength of the coating layer, and is a laminate for steel sheets that includes a UV absorber that absorbs specific UV light that causes material deterioration and a light stabilizer. It can be formed by applying to a decorative sheet and curing with ultraviolet rays.
以下に、実施例を挙げて本発明をさらに詳細に説明するが、本発明はこれらの実施例によりなんら限定されるものではない。
なお、実施例及び比較例において、化粧フィルムと積層化粧シートの評価は、下記の方法により行った。
（１）引張試験（２０％モジュラス）
あらかじめ１ｍｍの厚さにプレスした樹脂シートから、幅１５ｍｍ、長さ１５０ｍｍの試験片を切り取る。試験片の中央部の厚さを測定したのち、標線間距離５０ｍｍの標線を付ける。２３±２℃で２４時間状態調節したのち、同じ温度で、つかみ具間距離１００ｍｍで試験片をつかみ、引張速度５０ｍｍ／分で引張試験を行う。伸び２０％のときの引張応力を読み取り、試験片の元の断面積で除して、２０％モジュラスを算出する。
（２）隠蔽率
ＪＩＳ Ｋ ５４００ ７.２に準じて測定する。
（３）アフターエンボス転写性
加熱ドラム温度が１６０℃のダブリング装置と冷却ドラムの中間に、金属製彫刻ロールと半硬質ゴムで被覆した圧ロールからなるエンボスロールを設置し、梨地柄の砂目模様のエンボス加工を行い、エンボス加工によって得られた化粧フィルム又は積層化粧シートについて、表面性を目視により観察し、下記の基準により判定する。
○：良好
△：やや不良
×：不良
（４）熱ラミネート密着性
温度１６０℃の加熱ドラムを用いて熱圧着により化粧フィルムを積層し、得られた積層化粧シートを両手を使って剥離することを試み、下記の基準により判定する。
○：密着性が良好で、層間で剥離することができない。
×：密着性が低く、層間での剥離が可能である。
（５）耐沸騰水性
厚さ０.３ｍｍのボンデ鋼板に、ポリウレタン系二液硬化型接着剤［ソニーケミカル(株)、ＳＣ６１１］を用い、鋼板温度２２０℃、ラミネートロール温度５０℃で、化粧フィルム又は積層化粧シートを圧着してラミネート鋼板を作製する。得られたラミネート鋼板を沸騰水中に３０分間浸漬したのち、目視により表面の状態を観察し、下記の基準により判定する。
○：表面に変化が全く認められない。
△：表面に軽微な膨れが認められる。
×：表面に膨れが目立ち、剥離しやすくなる。
Hereinafter, the present invention will be described in more detail with reference to examples, but the present invention is not limited to these examples.
In Examples and Comparative Examples, the decorative film and the laminated decorative sheet were evaluated by the following methods.
(1) Tensile test (20% modulus)
A test piece having a width of 15 mm and a length of 150 mm is cut out from a resin sheet pressed to a thickness of 1 mm in advance. After measuring the thickness of the central part of the test piece, a marked line with a distance between marked lines of 50 mm is attached. After conditioning at 23 ± 2 ° C. for 24 hours, the test piece is gripped at the same temperature with a distance between grips of 100 mm, and a tensile test is performed at a tensile speed of 50 mm / min. The tensile stress at 20% elongation is read and divided by the original cross-sectional area of the specimen to calculate the 20% modulus.
(2) Concealment rate Measured according to JIS K 5400 7.2.
(3) After-embossing transferability An embossing roll consisting of a metal engraving roll and a pressure roll covered with semi-rigid rubber is installed between the doubling device with a heating drum temperature of 160 ° C and the cooling drum to create a textured texture. The surface properties of the decorative film or laminated decorative sheet obtained by embossing are visually observed and determined according to the following criteria.
○: Good △: Slightly bad ×: Bad (4) Thermal laminate adhesion Adhesive film is laminated by thermocompression bonding using a heating drum at a temperature of 160 ° C., and the resulting laminated decorative sheet is peeled off using both hands. Attempt and judge according to the following criteria.
○: Adhesiveness is good and peeling between layers is not possible.
X: Adhesiveness is low, and peeling between layers is possible.
(5) Boiling-resistant water Using a polyurethane-based two-component curable adhesive [Sony Chemical Co., Ltd., SC611] to a bonde steel sheet having a thickness of 0.3 mm, a decorative film at a steel sheet temperature of 220 ° C. and a laminating roll temperature of 50 ° C. Alternatively, a laminated steel sheet is produced by pressing a laminated decorative sheet. After immersing the obtained laminated steel sheet in boiling water for 30 minutes, the state of the surface is visually observed and judged according to the following criteria.
○: No change is observed on the surface.
Δ: Slight swelling is observed on the surface.
X: Swelling is conspicuous on the surface and it becomes easy to peel off.
実施例１
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４、テレフタル酸／エチレングリコール／ポリテトラメチレングリコール／１,４−シクロヘキサンジメタノール共重合体、ガラス転移温度１０℃］をＴダイから押し出し、厚さ８０μｍの化粧フィルムを製膜した。この化粧フィルムをオフラインにて、ダブリング装置［(株)川上鉄工所］の加熱ドラムに密着させ、エンボスロールによりエンボス加工を行った。
この１ｍｍ厚樹脂プレスシートの２０％モジュラスは、３.６ＭＰａであった。エンボス転写性は良好であり、又耐沸騰水性試験において、表面に変化は全く認められなかった。
実施例２
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４］７０重量部と(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３、テレフタル酸／エチレングリコール／１,４−シクロヘキサンジメタノール共重合体、ガラス転移温度８１℃］３０重量部を混合し、Ｔダイから押し出し、厚さ８０μｍの化粧フィルムを製膜した。この化粧フィルムをオフラインにて、ダブリング装置の加熱ドラムに密着させ、エンボスロールによりエンボス加工を行った。
この１ｍｍ厚樹脂プレスシートの２０％モジュラスは、１１ＭＰａであった。エンボス転写性は良好であり、又耐沸騰水性試験において、表面に変化は全く認められなかった。
実施例３
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４］５０重量部、(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３］３０重量部及び(Ｃ１)ポリブチレンテレフタレート系樹脂［ポリプラススチック(株)、ジュラネックス５００ＬＰ、イソフタル酸共重合ポリブチレンテレフタレート系樹脂、ガラス転移温度２２℃］２０重量部を混合し、Ｔダイから押し出し、厚さ６０μｍの化粧フィルムを製膜した。この化粧フィルムをオフラインにて、ダブリング装置の加熱ドラムに密着させ、エンボスロールによりエンボス加工を行った。
この１ｍｍ厚樹脂プレスシートの２０％モジュラスは、１８ＭＰａであった。エンボス転写性は良好であり、又耐沸騰水性試験において、表面に変化は全く認められなかった。
実施例４
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４］５０重量部、(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３］４０重量部及び(Ｄ１)メタクリル酸メチル−ブタジエン−スチレン共重合体［鐘淵化学工業(株)、カネエースＢ−３１］１０重量部を混合し、Ｔダイから押し出し、厚さ１００μｍの化粧フィルムを製膜した。この化粧フィルムをオフラインにて、ダブリング装置の加熱ドラムに密着させ、エンボスロールによりエンボス加工を行った。
この１ｍｍ厚樹脂プレスシートの２０％モジュラスは、１５ＭＰａであった。エンボス転写性は良好であり、又耐沸騰水性試験において、表面に変化は全く認められなかった。
実施例５
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４］６０重量部、(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３］３５重量部、(Ｄ１)メタクリル酸メチル−ブタジエン−スチレン共重合体［鐘淵化学工業(株)、カネエースＢ−３１］５重量部及び(Ｅ)モンタン酸エステルワックス［クラリアントジャパン(株)、リコワックスＯＰ、カルシウムけん化モンタン酸エステルワックス］２重量部をバンバリミキサーで混練し、逆Ｌ型カレンダーを用いて、厚さ７０μｍの化粧フィルムを製膜した。この化粧フィルムをオフラインにて、ダブリング装置の加熱ドラムに密着させ、エンボスロールによりエンボス加工を行った。
この１ｍｍ厚樹脂プレスシートの２０％モジュラスは、１０ＭＰａであった。エンボス転写性は良好であり、又耐沸騰水性試験において、表面に変化は全く認められなかった。
実施例６
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４］４５重量部、(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３］３５重量部、(Ｃ１)ポリブチレンテレフタレート系樹脂［ポリプラススチック(株)、ジュラネックス５００ＬＰ］１０重量部、(Ｄ１)メタクリル酸メチル−ブタジエン−スチレン共重合体［鐘淵化学工業(株)、カネエースＢ−３１］１０重量部、(Ｅ)モンタン酸エステルワックス［クラリアントジャパン(株)、リコワックスＯＰ］２重量部及び着色剤［住化カラー(株)、ＥＰＭ７Ａ１４４１、白色マスターバッチ］３０重量部をバンバリミキサーで混練し、逆Ｌ型カレンダーを用いて、厚さ１００μｍの化粧フィルムを製膜した。この化粧フィルムの隠蔽率は、０.９９９であった。この化粧フィルムをオフラインにて、ダブリング装置の加熱ドラムに密着させ、エンボスロールによりエンボス加工を行った。
この１ｍｍ厚樹脂プレスシートの２０％モジュラスは、１６ＭＰａであった。エンボス転写性は良好であり、又耐沸騰水性試験において、表面に変化は全く認められなかった。
Example 1
(A) Modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124, terephthalic acid / ethylene glycol / polytetramethylene glycol / 1,4-cyclohexanedimethanol copolymer, glass transition temperature 10 ° C.] extruded from a T-die A decorative film having a thickness of 80 μm was formed. This decorative film was brought into close contact with a heating drum of a doubling apparatus [Kawakami Iron Works Co., Ltd.] and embossed with an embossing roll.
The 20% modulus of this 1 mm thick resin press sheet was 3.6 MPa. The emboss transferability was good, and no change was observed on the surface in the boiling water resistance test.
Example 2
(A) 70 parts by weight of modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124] and (B1) amorphous polyethylene terephthalate resin [Eastman Chemical Japan Co., Ltd., PETG6763, terephthalic acid / ethylene glycol / 1, 30 parts by weight of 4-cyclohexanedimethanol copolymer, glass transition temperature 81 ° C.] was mixed and extruded from a T die to form a decorative film having a thickness of 80 μm. This decorative film was brought into close contact with a heating drum of a doubling apparatus offline and embossed with an embossing roll.
The 20% modulus of this 1 mm thick resin press sheet was 11 MPa. The emboss transferability was good, and no change was observed on the surface in the boiling water resistance test.
Example 3
(A) Modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124] 50 parts by weight, (B1) Amorphous polyethylene terephthalate resin [Eastman Chemical Japan Co., Ltd., PETG6763] 30 parts by weight and (C1) Poly 20 parts by weight of butylene terephthalate resin [Polyplastic Co., Ltd., DURANEX 500LP, isophthalic acid copolymerized polybutylene terephthalate resin, glass transition temperature 22 ° C.] mixed, extruded from a T-die, and a 60 μm thick decorative film Was formed. This decorative film was brought into close contact with a heating drum of a doubling apparatus offline and embossed with an embossing roll.
The 20% modulus of this 1 mm thick resin press sheet was 18 MPa. The emboss transferability was good, and no change was observed on the surface in the boiling water resistance test.
Example 4
(A) Modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124] 50 parts by weight, (B1) Amorphous polyethylene terephthalate resin [Eastman Chemical Japan Co., Ltd., PETG6763] 40 parts by weight and (D1) Methacryl 10 parts by weight of an acid methyl-butadiene-styrene copolymer [Kanebuchi Chemical Industry Co., Ltd., Kane Ace B-31] was mixed and extruded from a T-die to form a decorative film having a thickness of 100 μm. This decorative film was brought into close contact with a heating drum of a doubling apparatus offline and embossed with an embossing roll.
The 20% modulus of this 1 mm thick resin press sheet was 15 MPa. The emboss transferability was good, and no change was observed on the surface in the boiling water resistance test.
Example 5
(A) Modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124] 60 parts by weight, (B1) Amorphous polyethylene terephthalate resin [Eastman Chemical Japan Co., Ltd., PETG6763] 35 parts by weight, (D1) Methacryl Methyl acid-butadiene-styrene copolymer [Kanebuchi Chemical Industry Co., Ltd., Kane Ace B-31] 5 parts by weight and (E) Montanate ester wax [Clariant Japan Co., Ltd., Lycowax OP, calcium saponified montanate ester Wax] 2 parts by weight was kneaded with a Banbury mixer, and a decorative film having a thickness of 70 μm was formed using an inverted L-type calendar. This decorative film was brought into close contact with a heating drum of a doubling apparatus offline and embossed with an embossing roll.
The 20% modulus of this 1 mm thick resin press sheet was 10 MPa. The emboss transferability was good, and no change was observed on the surface in the boiling water resistance test.
Example 6
(A) 45 parts by weight of modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124], (B1) 35 parts by weight of amorphous polyethylene terephthalate resin [Eastman Chemical Japan Ltd., PETG6763], (C1) Poly 10 parts by weight of butylene terephthalate resin [Polyplastic Co., Ltd., DURANEX 500LP], (D1) methyl methacrylate-butadiene-styrene copolymer [Kanebuchi Chemical Industry Co., Ltd., Kane Ace B-31] 10 parts by weight , (E) 2 parts by weight of montanic acid ester wax [Clariant Japan Co., Ltd., Ricowax OP] and 30 parts by weight of colorant [Sumika Color Co., Ltd., EPM7A1441, white masterbatch] A decorative film having a thickness of 100 μm was formed using an L-shaped calendar. The concealment rate of this decorative film was 0.999. This decorative film was brought into close contact with a heating drum of a doubling apparatus offline and embossed with an embossing roll.
The 20% modulus of this 1 mm thick resin press sheet was 16 MPa. The emboss transferability was good, and no change was observed on the surface in the boiling water resistance test.
実施例７
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４］５５重量部、(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３］３０重量部、(Ｃ１)ポリブチレンテレフタレート系樹脂［ポリプラススチック(株)、ジュラネックス５００ＬＰ］１０重量部、(Ｄ１)メタクリル酸メチル−ブタジエン−スチレン共重合体［鐘淵化学工業(株)、カネエースＢ−３１］５重量部、(Ｅ)モンタン酸エステルワックス［クラリアントジャパン(株)、リコワックスＯＰ］２重量部及び着色剤［住化カラー(株)、ＥＰＭ７Ａ１４４１、白色マスターバッチ］３０重量部をバンバリミキサーで混練し、逆Ｌ型カレンダーを用いて、厚さ９０μｍの下地化粧フィルムを製膜した。この下地化粧フィルムの隠蔽率は０.９９８であり、１ｍｍ厚樹脂プレスシートの２０％モジュラスは１７ＭＰａであった。
実施例５で得られた透明の化粧フィルムを上地として繰り出し、ダブリング装置［(株)川上鉄工所］の加熱ドラムに密着させ、上記の下地化粧フィルムを繰り出して加熱ドラム上の上地と圧着して積層し、エンボスロールによりエンボス加工を行った。
その積層化粧シートのエンボス転写性は良好であり、熱ラミネートにおいて、密着性は良好であった。耐沸騰水性試験において、表面に変化は全く認められなかった。
実施例８
(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３］４０重量部、(Ｃ２)ポリブチレンテレフタレート樹脂［東レ(株)、トレコン１２００Ｓ、ガラス転移温度４０℃］６０重量部及び着色剤［住化カラー(株)、ＥＰＭ７Ａ１４４１］３０重量部を混合し、Ｔダイから押し出し、厚さ８０μｍの下地化粧フィルムを製膜した。この下地化粧フィルムの隠蔽率は０.９９８であり、１ｍｍ厚樹脂プレスシートの２０％モジュラスは２１ＭＰａであった。
実施例７と同様にして、実施例５で得られた透明の化粧フィルムを上地とし、ダブリング装置とエンボスロールを用い、上記の下地化粧フィルムと圧着して積層し、エンボス加工を行った。
その積層化粧シートのエンボス転写性は良好であり、熱ラミネートにおいて、密着性は良好であった。耐沸騰水性試験において、表面に変化は全く認められなかった。
実施例９
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４］５５重量部、(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３］３５重量部、(Ｄ２)メタクリル酸エステル／アクリル酸エステルゴムグラフト共重合体［鐘淵化学工業(株)、カネエースＦＭ２１］１０重量部及び着色剤［住化カラー(株)、ＥＰＭ７Ａ１４４１］３０重量部を混合し、Ｔダイから押し出し、厚さ９０μｍの下地化粧フィルムを製膜した。この下地化粧フィルムの隠蔽率は０.９９８であり、１ｍｍ厚樹脂プレスシートの２０％モジュラスは１７ＭＰａであった。
この化粧フィルムに、厚さ２５μｍの二軸延伸ポリエチレンテレフタレートフィルム［東洋紡績(株)、Ｅ５１３１］を上地とし、ドライラミネーションにより積層し、積層化粧シートを得た。この積層化粧シートは、耐沸騰水性試験において、表面に変化は全く認められなかった。
実施例１０
(Ｂ２)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＣＴＧ５４４５、１,４−シクロヘキサンジメタノール共重合ポリエチレンテレフタレート系樹脂、ガラス転移温度８１℃］６０重量部、(Ｆ)ポリトリメチレンテレフタレート系樹脂［旭化成(株)、１０Ｎ００、ガラス転移温度４７℃］４０重量部及び着色剤［住化カラー(株)、ＥＰＭ７Ａ１４４１］３０重量部を混合し、Ｔダイから押し出し、厚さ１００μｍの下地化粧フィルムを製膜した。この下地化粧フィルムの隠蔽率は０.９９９であり、１ｍｍ厚樹脂プレスシートの２０％モジュラスは２４ＭＰａであった。
実施例７と同様にして、実施例５で得られた透明の化粧フィルムを上地とし、ダブリング装置とエンボスロールを用い、上記の下地化粧フィルムと圧着して積層し、エンボス加工を行った。
その積層化粧シートのエンボス転写性は良好であり、熱ラミネートにおいて、密着性は良好であった。耐沸騰水性試験において、表面に変化は全く認められなかった。
実施例１１
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４］５５重量部、(Ｂ３)非晶性ポリエチレンテレフタレート系樹脂［東洋紡績(株)、ＳＲ１７３ＣＡ］１０重量部、(Ｃ１)ポリブチレンテレフタレート系樹脂［ポリプラススチック(株)、ジュラネックス５００ＬＰ］３０重量部、(Ｄ１)メタクリル酸メチル−ブタジエン−スチレン共重合体［鐘淵化学工業(株)、カネエースＢ−３１］５重量部、(Ｅ)モンタン酸エステルワックス［クラリアントジャパン(株)、リコワックスＯＰ］２重量部及び着色剤［住化カラー(株)、ＥＰＭ７Ａ１４４１、白色マスターバッチ］３０重量部をバンバリミキサーで混練し、逆Ｌ型カレンダーを用いて、厚さ９０μｍの下地化粧フィルムを製膜した。この下地化粧フィルムの隠蔽率は０.９９８であり、１ｍｍ厚樹脂プレスシートの２０％モジュラスは１９ＭＰａであった。
実施例７と同様にして、実施例５で得られた透明の化粧フィルムを上地とし、ダブリング装置とエンボスロールを用い、上記の下地化粧フィルムと圧着して積層し、エンボス加工を行った。
その積層化粧シートのエンボス転写性は良好であり、熱ラミネートにおいて、密着性は良好であった。
さらに、積層化粧シートの表面に、ウレタンアクリレート系紫外線硬化型塗料［(株)ニッコー化学研究所、Ｔ−ＵＶ−１］を塗布し、硬化させることにより、トップコートを形成した。
このトップコートを有する積層化粧シートは、耐沸騰水性試験において、表面に変化は全く認められなかった。
Example 7
(A) 55 parts by weight of modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124], (B1) 30 parts by weight of amorphous polyethylene terephthalate resin [Eastman Chemical Japan, PETG6763], (C1) Poly 10 parts by weight of a butylene terephthalate resin [Polyplastic Co., Ltd., DURANEX 500LP], (D1) 5 parts by weight of a methyl methacrylate-butadiene-styrene copolymer [Kanebuchi Chemical Industry Co., Ltd., Kane Ace B-31] , (E) 2 parts by weight of montanic acid ester wax [Clariant Japan Co., Ltd., Ricowax OP] and 30 parts by weight of colorant [Sumika Color Co., Ltd., EPM7A1441, white masterbatch] A base decorative film having a thickness of 90 μm was formed using an L-type calendar. The concealment rate of this base decorative film was 0.998, and the 20% modulus of the 1 mm-thick resin press sheet was 17 MPa.
The transparent decorative film obtained in Example 5 is fed out as an upper layer and brought into close contact with the heating drum of a doubling apparatus [Kawakami Iron Works Co., Ltd.]. And embossing with an embossing roll.
The embossed transfer property of the laminated decorative sheet was good, and the adhesiveness was good in the heat lamination. In the boiling water resistance test, no change was observed on the surface.
Example 8
(B1) 40 parts by weight of amorphous polyethylene terephthalate resin [Eastman Chemical Japan Co., Ltd., PETG6763], (C2) 60 parts by weight of polybutylene terephthalate resin [Toray Industries, Inc., Toraycon 1200S, glass transition temperature 40 ° C.] And 30 parts by weight of a colorant [Sumika Color Co., Ltd., EPM7A1441] were mixed and extruded from a T-die to form a base decorative film having a thickness of 80 μm. The concealment rate of this base decorative film was 0.998, and the 20% modulus of the 1 mm thick resin press sheet was 21 MPa.
In the same manner as in Example 7, the transparent decorative film obtained in Example 5 was used as the top, and a doubling device and an embossing roll were used to pressure-bond and laminate the above base decorative film, and embossing was performed.
The embossed transfer property of the laminated decorative sheet was good, and the adhesiveness was good in the heat lamination. In the boiling water resistance test, no change was observed on the surface.
Example 9
(A) 55 parts by weight of modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124], (B1) 35 parts by weight of amorphous polyethylene terephthalate resin [Eastman Chemical Japan Co., Ltd., PETG6763], (D2) methacryl 10 parts by weight of an acid ester / acrylic acid ester rubber graft copolymer [Kanebuchi Chemical Industry Co., Ltd., Kane Ace FM21] and 30 parts by weight of a colorant [Suika Color Co., Ltd., EPM7A1441] are mixed and extruded from a T-die. A base decorative film having a thickness of 90 μm was formed. The concealment rate of this base decorative film was 0.998, and the 20% modulus of the 1 mm-thick resin press sheet was 17 MPa.
On this decorative film, a biaxially stretched polyethylene terephthalate film [Toyobo Co., Ltd., E5131] having a thickness of 25 μm was laminated and dry laminated to obtain a laminated decorative sheet. In this laminated decorative sheet, no change was observed on the surface in the boiling water resistance test.
Example 10
(B2) Amorphous polyethylene terephthalate resin [Eastman Chemical Japan Co., Ltd., PCTG5445, 1,4-cyclohexanedimethanol copolymerized polyethylene terephthalate resin, glass transition temperature 81 ° C.] 60 parts by weight, (F) Polytri 40 parts by weight of methylene terephthalate resin [Asahi Kasei Co., Ltd., 10N00, glass transition temperature 47 ° C.] and 30 parts by weight of colorant [Sumika Color Co., Ltd., EPM7A1441] were mixed and extruded from a T-die, with a thickness of 100 μm. A base decorative film was formed. The concealment rate of this base decorative film was 0.999, and the 20% modulus of the 1 mm-thick resin press sheet was 24 MPa.
In the same manner as in Example 7, the transparent decorative film obtained in Example 5 was used as the top, and a doubling device and an embossing roll were used to pressure-bond and laminate the above base decorative film, and embossing was performed.
The embossed transfer property of the laminated decorative sheet was good, and the adhesiveness was good in the heat lamination. In the boiling water resistance test, no change was observed on the surface.
Example 11
(A) 55 parts by weight of modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124], (B3) 10 parts by weight of amorphous polyethylene terephthalate resin [Toyobo Co., Ltd., SR173CA], (C1) polybutylene terephthalate -Based resin [Polyplastic Co., Ltd., DURANEX 500LP] 30 parts by weight, (D1) Methyl methacrylate-butadiene-styrene copolymer [Kanekuma Chemical Co., Ltd., Kane Ace B-31] 5 parts by weight, ( E) 2 parts by weight of montanic acid ester wax [Clariant Japan Co., Ltd., Ricowax OP] and 30 parts by weight of colorant [Sumika Color Co., Ltd., EPM7A1441, white masterbatch] were kneaded with a Banbury mixer, and inverted L type Using a calender, a base decorative film having a thickness of 90 μm was formed. The concealment rate of this base decorative film was 0.998, and the 20% modulus of the 1 mm-thick resin press sheet was 19 MPa.
In the same manner as in Example 7, the transparent decorative film obtained in Example 5 was used as the top, and a doubling device and an embossing roll were used to pressure-bond and laminate the above base decorative film, and embossing was performed.
The embossed transfer property of the laminated decorative sheet was good, and the adhesiveness was good in the heat lamination.
Further, a top coat was formed by applying and curing a urethane acrylate ultraviolet curable paint [Nikko Chemical Laboratory, T-UV-1] on the surface of the laminated decorative sheet.
In the laminated decorative sheet having this top coat, no change was observed on the surface in the boiling water resistance test.
比較例１
(Ｃ２)ポリブチレンテレフタレート樹脂［東レ(株)、トレコン１２００Ｓ、ガラス転移温度４０℃］をＴダイから押し出し、厚さ１００μｍの化粧フィルムを製膜した。この化粧フィルムをオフラインにて、ダブリング装置［(株)川上鉄工所］の加熱ドラムに密着させ、エンボスロールによりエンボス加工を行った。
この１ｍｍ厚樹脂プレスシートの２０％モジュラスは、２１ＭＰａであった。エンボス転写性は、不良であった。又耐沸騰水性試験において、表面に変化は全く認められなかった。
比較例２
(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３］９０重量部、(Ｃ１)ポリブチレンテレフタレート系樹脂［ポリプラススチック(株)、ジュラネックス５００ＬＰ］１０重量部及び(Ｅ)モンタン酸エステルワックス［クラリアントジャパン(株)、リコワックスＯＰ］２重量部をバンバリミキサーで混練し、逆Ｌ型カレンダーを用いて、厚さ８０μｍの化粧フィルムを製膜した。この化粧フィルムをオフラインにて、ダブリング装置の加熱ドラムに密着させ、エンボスロールによりエンボス加工を行った。
この１ｍｍ厚樹脂プレスシートの２０％モジュラスは、２８ＭＰａであった。エンボス転写性は良好であった。又耐沸騰水性試験において、表面に膨れが目立ち、剥離しやすくなった。
比較例３
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４］１５重量部、(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３］８０重量部、(Ｃ１)ポリブチレンテレフタレート系樹脂［ポリプラススチック(株)、ジュラネックス５００ＬＰ］５重量部、(Ｅ)モンタン酸エステルワックス［クラリアントジャパン(株)、リコワックスＯＰ］２重量部及び着色剤［住化カラー(株)、ＥＰＭ７Ａ１４４１、白色マスターバッチ］３０重量部をバンバリミキサーで混練し、逆Ｌ型カレンダーを用いて、厚さ９０μｍの化粧フィルムを製膜した。この化粧フィルムの隠蔽率は、０.９９９であった。この化粧フィルムをオフラインにて、ダブリング装置の加熱ドラムに密着させ、エンボスロールによりエンボス加工を行った。
この１ｍｍ厚樹脂プレスシートの２０％モジュラスは、２７ＭＰａであった。エンボス転写性は良好であった。又耐沸騰水性試験において、表面に膨れが目立ち、剥離しやすくなった。
Comparative Example 1
(C2) Polybutylene terephthalate resin [Toray Industries, Inc., Toraycon 1200S, glass transition temperature 40 ° C.] was extruded from a T-die to form a decorative film having a thickness of 100 μm. This decorative film was brought into close contact with a heating drum of a doubling apparatus [Kawakami Iron Works Co., Ltd.] and embossed with an embossing roll.
The 20% modulus of this 1 mm thick resin press sheet was 21 MPa. The emboss transferability was poor. In the boiling water resistance test, no change was observed on the surface.
Comparative Example 2
(B1) 90 parts by weight of amorphous polyethylene terephthalate resin [Eastman Chemical Japan Co., Ltd., PETG6763], (C1) 10 parts by weight of polybutylene terephthalate resin [Polyplastic Co., Ltd., DURANEX 500LP] E) 2 parts by weight of a montanic acid ester wax [Clariant Japan Co., Ltd., Ricowax OP] was kneaded with a Banbury mixer, and a decorative film having a thickness of 80 μm was formed using an inverted L-type calendar. This decorative film was brought into close contact with a heating drum of a doubling apparatus offline and embossed with an embossing roll.
The 20% modulus of this 1 mm thick resin press sheet was 28 MPa. The emboss transferability was good. Further, in the boiling water resistance test, swelling was conspicuous on the surface and it was easy to peel off.
Comparative Example 3
(A) Modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124] 15 parts by weight, (B1) Amorphous polyethylene terephthalate resin [Eastman Chemical Japan, PETG6763] 80 parts by weight, (C1) Poly 5 parts by weight of butylene terephthalate resin [Polyplastic Co., Ltd., DURANEX 500LP], 2 parts by weight of (E) montanic acid ester wax [Clariant Japan Co., Ltd., Lycowax OP] and a colorant [Suika Color Co., Ltd. ), EPM7A1441, white masterbatch] 30 parts by weight were kneaded with a Banbury mixer, and a decorative film having a thickness of 90 μm was formed using an inverted L-type calendar. The concealment rate of this decorative film was 0.999. This decorative film was brought into close contact with a heating drum of a doubling apparatus offline and embossed with an embossing roll.
The 20% modulus of this 1 mm thick resin press sheet was 27 MPa. The emboss transferability was good. Further, in the boiling water resistance test, swelling was conspicuous on the surface and it was easy to peel off.
比較例４
比較例１と同様にして、(Ｃ２)ポリブチレンテレフタレート樹脂［東レ(株)、トレコン１２００Ｓ、ガラス転移温度４０℃］を用いて、厚さ７０μｍの上地化粧フィルムを製膜した。
(Ｃ２)ポリブチレンテレフタレート樹脂［東レ(株)、トレコン１２００Ｓ、ガラス転移温度４０℃］１００重量部、(Ｅ)モンタン酸エステルワックス［クラリアントジャパン(株)、リコワックスＯＰ］２重量部及び着色剤［住化カラー(株)、ＥＰＭ７Ａ１４４１、白色マスターバッチ］３０重量部をバンバリミキサーで混練し、逆Ｌ型カレンダーを用いて、厚さ８０μｍの下地化粧フィルムを製膜した。この下地化粧フィルムの隠蔽率は０.９９８であり、１ｍｍ厚樹脂プレスシートの２０％モジュラスは２１ＭＰａであった。
上地化粧フィルムを繰り出し、ダブリング装置［(株)川上鉄工所］の加熱ドラムに密着させ、下地化粧フィルムを繰り出して加熱ドラム上の上地と圧着して積層し、エンボスロールによりエンボス加工を行った。
その積層化粧シートのエンボス転写性は、不良であり、熱ラミネートにおいて、密着性が低く、層間での剥離が可能であった。耐沸騰水性試験において、表面に変化は全く認められなかった。
比較例５
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４］２０重量部、(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３］３０重量部、(Ｃ１)ポリブチレンテレフタレート系樹脂［ポリプラススチック(株)、ジュラネックス５００ＬＰ］５０重量部及び着色剤［住化カラー(株)、ＥＰＭ７Ａ１４４１］３０重量部を混合し、Ｔダイから押し出し、厚さ９０μｍの下地化粧フィルムを製膜した。この下地化粧フィルムの隠蔽率は０.９９９であり、１ｍｍ厚樹脂プレスシートの２０％モジュラスは２０ＭＰａであった。
比較例４と同様にして、比較例１で得られた透明の化粧フィルムを上地とし、ダブリング装置とエンボスロールを用い、上記の下地化粧フィルムと圧着して積層し、エンボス加工を行った。
その積層化粧シートのエンボス転写性は、不良であり、熱ラミネートにおいて、密着性が低く、層間での剥離が可能であった。耐沸騰水性試験において、表面に変化は全く認められなかった。
比較例６
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４］５０重量部、(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３］４０重量部、(Ｃ１)ポリブチレンテレフタレート系樹脂［ポリプラススチック(株)、ジュラネックス５００ＬＰ］１０重量部、(Ｅ)モンタン酸エステルワックス［クラリアントジャパン(株)、リコワックスＯＰ］２重量部及び着色剤［住化カラー(株)、ＥＰＭ７Ａ１４４１］３０重量部をバンバリミキサーで混練し、逆Ｌ型カレンダーを用いて、厚さ１００μｍの下地化粧フィルムを製膜した。この下地化粧フィルムの隠蔽率は０.９９９であり、１ｍｍ厚樹脂プレスシートの２０％モジュラスは１８ＭＰａであった。
比較例４と同様にして、比較例２で得られた透明の化粧フィルムを上地とし、ダブリング装置とエンボスロールを用い、上記の下地化粧フィルムと圧着して積層し、エンボス加工を行った。
その積層化粧シートのエンボス転写性は良好であり、熱ラミネートにおいて、密着性は良好であった。耐沸騰水性試験において、表面に膨れが目立ち、剥離しやすくなった。
比較例７
(Ａ)変性ポリエチレンテレフタレート系樹脂［三菱レイヨン(株)、ＤＮ１２４］５重量部、(Ｂ１)非晶性ポリエチレンテレフタレート系樹脂［イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３］９０重量部、(Ｃ１)ポリブチレンテレフタレート系樹脂［ポリプラススチック(株)、ジュラネックス５００ＬＰ］５重量部、(Ｅ)モンタン酸エステルワックス［クラリアントジャパン(株)、リコワックスＯＰ］２重量部及び着色剤［住化カラー(株)、ＥＰＭ７Ａ１４４１］３０重量部をバンバリミキサーで混練し、逆Ｌ型カレンダーを用いて、厚さ７０μｍの下地化粧フィルムを製膜した。この下地化粧フィルムの隠蔽率は０.９９８であり、１ｍｍ厚樹脂プレスシートの２０％モジュラスは２７ＭＰａであった。
比較例４と同様にして、実施例５で得られた透明の化粧フィルムを上地とし、ダブリング装置とエンボスロールを用い、上記の下地化粧フィルムと圧着して積層し、エンボス加工を行った。
その積層化粧シートのエンボス転写性は良好であり、熱ラミネートにおいて、密着性は良好であった。
さらに、積層化粧シートの表面に、ポリウレタン系二液硬化型塗料［ザ インンテック(株)、ＮＨＷＰ］を塗布し、硬化させることにより、トップコートを形成した。
このトップコートを有する積層化粧シートは、耐沸騰水性試験において、表面に膨れが目立ち、剥離しやすくなった。
Comparative Example 4
In the same manner as in Comparative Example 1, an upper decorative film having a thickness of 70 μm was formed using (C2) polybutylene terephthalate resin [Toray Industries, Inc., Toraycon 1200S, glass transition temperature 40 ° C.].
(C2) 100 parts by weight of polybutylene terephthalate resin [Toray Industries, Inc., Toraycon 1200S, glass transition temperature 40 ° C.], (E) 2 parts by weight of montanic acid ester wax [Clariant Japan Co., Ltd., Ricowax OP], and colorant [Sumika Color Co., Ltd., EPM7A1441, white masterbatch] 30 parts by weight were kneaded with a Banbury mixer, and a base decorative film having a thickness of 80 μm was formed using an inverted L-type calendar. The concealment rate of this base decorative film was 0.998, and the 20% modulus of the 1 mm thick resin press sheet was 21 MPa.
Roll out the upper decorative film, adhere it to the heating drum of the doubling machine [Kawakami Iron Works Co., Ltd.], pay out the base decorative film, press and laminate the upper decorative film on the heating drum, and emboss it with an embossing roll. It was.
The embossed transferability of the laminated decorative sheet was poor, and in heat lamination, the adhesiveness was low, and peeling between layers was possible. In the boiling water resistance test, no change was observed on the surface.
Comparative Example 5
(A) Modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124] 20 parts by weight, (B1) Amorphous polyethylene terephthalate resin [Eastman Chemical Japan Co., Ltd., PETG6763] 30 parts by weight, (C1) Poly 50 parts by weight of butylene terephthalate resin [Polyplastic Co., Ltd., DURANEX 500LP] and 30 parts by weight of colorant [Sumika Color Co., Ltd., EPM7A1441] are mixed, extruded from a T-die, and a base makeup having a thickness of 90 μm A film was formed. The concealment rate of this base decorative film was 0.999, and the 20% modulus of the 1 mm thick resin press sheet was 20 MPa.
In the same manner as in Comparative Example 4, the transparent decorative film obtained in Comparative Example 1 was used as the top, and a doubling device and an embossing roll were used to press-bond and laminate the above-mentioned base decorative film, and embossing was performed.
The embossed transferability of the laminated decorative sheet was poor, and in heat lamination, the adhesiveness was low, and peeling between layers was possible. In the boiling water resistance test, no change was observed on the surface.
Comparative Example 6
(A) Modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124] 50 parts by weight, (B1) Amorphous polyethylene terephthalate resin [Eastman Chemical Japan Co., Ltd., PETG6763] 40 parts by weight, (C1) Poly 10 parts by weight of butylene terephthalate resin [Polyplastic Co., Ltd., DURANEX 500LP], 2 parts by weight of (E) montanic acid ester wax [Clariant Japan Co., Ltd., Lycowax OP] and a colorant [Suika Color Co., Ltd. ), EPM7A1441] 30 parts by weight were kneaded with a Banbury mixer, and a base decorative film having a thickness of 100 μm was formed using an inverted L-type calendar. The concealment rate of this base decorative film was 0.999, and the 20% modulus of the 1 mm thick resin press sheet was 18 MPa.
In the same manner as in Comparative Example 4, the transparent decorative film obtained in Comparative Example 2 was used as the top, using a doubling device and an embossing roll, and pressure-bonded to the base decorative film and laminated, and embossed.
The embossed transfer property of the laminated decorative sheet was good, and the adhesiveness was good in the heat lamination. In the boiling water resistance test, blisters were conspicuous on the surface and it was easy to peel off.
Comparative Example 7
(A) Modified polyethylene terephthalate resin [Mitsubishi Rayon Co., Ltd., DN124] 5 parts by weight, (B1) Amorphous polyethylene terephthalate resin [Eastman Chemical Japan Co., Ltd., PETG6763] 90 parts by weight, (C1) Poly 5 parts by weight of butylene terephthalate resin [Polyplastic Co., Ltd., DURANEX 500LP], 2 parts by weight of (E) montanic acid ester wax [Clariant Japan Co., Ltd., Lycowax OP] and a colorant [Suika Color Co., Ltd. ), EPM7A1441] 30 parts by weight were kneaded with a Banbury mixer, and a base decorative film having a thickness of 70 μm was formed using an inverted L-type calendar. The concealment rate of this base decorative film was 0.998, and the 20% modulus of the 1 mm-thick resin press sheet was 27 MPa.
In the same manner as in Comparative Example 4, the transparent decorative film obtained in Example 5 was used as the top, and a doubling device and an embossing roll were used to press-bond and laminate the above-mentioned base decorative film, followed by embossing.
The embossed transfer property of the laminated decorative sheet was good, and the adhesiveness was good in the heat lamination.
Furthermore, a top coat was formed by applying and curing a polyurethane two-component curable paint [Zynetech Co., Ltd., NHWP] on the surface of the laminated decorative sheet.
The laminated decorative sheet having this top coat was conspicuous on the surface in the boiling water resistance test, and was easily peeled off.
実施例１〜１１の配合組成と構成を第１表に、その評価結果を第２表に示し、比較例１〜７の配合組成と構成を第３表に、その評価結果を第４表に示す。ただし、表中、各成分は、下記の略号により表す。
(Ａ)変性ＰＥＴ系：変性ポリエチレンテレフタレート系樹脂、三菱レイヨン(株)、ＤＮ１２４、テレフタル酸／エチレングリコール／ポリテトラメチレングリコール／１,４−シクロヘキサンジメタノール共重合体、ガラス転移温度１０℃。
(Ｂ１)非晶性ＰＥＴ系：非晶性ポリエチレンテレフタレート系樹脂、イーストマン ケミカル ジャパン(株)、ＰＥＴＧ６７６３、テレフタル酸／エチレングリコール／１,４−シクロヘキサンジメタノール共重合体、ガラス転移温度８１℃。
(Ｂ２)非晶性ＰＥＴ系：非晶性ポリエチレンテレフタレート系樹脂、イーストマン ケミカル ジャパン(株)、ＰＣＴＧ５４４５、１,４−シクロヘキサンジメタノール共重合ポリエチレンテレフタレート系樹脂、ガラス転移温度８１℃。
(Ｂ３)非晶性ＰＥＴ系：非晶性ポリエチレンテレフタレート系樹脂、東洋紡績(株)、ＳＲ１７３ＣＡ、ネオペンチルグリコール共重合ポリエチレンテレフタレート系樹脂、ガラス転移温度７９℃。
(Ｃ１)ＰＢＴ系：ポリブチレンテレフタレート系樹脂、ポリプラススチック(株)、ジュラネックス５００ＬＰ、イソフタル酸共重合ポリブチレンテレフタレート系樹脂、ガラス転移温度２２℃。
(Ｃ２)ＰＢＴ：ポリブチレンテレフタレート樹脂、東レ(株)、トレコン１２００Ｓ、ガラス転移温度４０℃。
(Ｄ１)ＭＢＳ：メタクリル酸メチル−ブタジエン−スチレン共重合体、鐘淵化学工業(株)、カネエースＢ−３１。
(Ｄ２)ＦＭ２１：メタクリル酸エステル／アクリル酸エステルゴムグラフト共重合体、鐘淵化学工業(株)、カネエースＦＭ２１。
(Ｅ)滑剤：モンタン酸エステルワックス、クラリアントジャパン(株)、リコワックスＯＰ、カルシウムけん化モンタン酸エステルワックス。
(Ｆ)ＰＴＴ系：ポリトリメチレンテレフタレート系樹脂、旭化成(株)、１０Ｎ００、ガラス転移温度４７℃。
着色剤：住化カラー(株)、ＥＰＭ７Ａ１４４１、白色マスターバッチ。
The compounding compositions and configurations of Examples 1 to 11 are shown in Table 1, the evaluation results are shown in Table 2, the compounding compositions and configurations of Comparative Examples 1 to 7 are shown in Table 3, and the evaluation results are shown in Table 4. Show. However, each component is represented by the following abbreviations in the table.
(A) Modified PET series: Modified polyethylene terephthalate series resin, Mitsubishi Rayon Co., Ltd., DN124, terephthalic acid / ethylene glycol / polytetramethylene glycol / 1,4-cyclohexanedimethanol copolymer, glass transition temperature 10 ° C.
(B1) Amorphous PET: Amorphous polyethylene terephthalate resin, Eastman Chemical Japan, PETG6763, terephthalic acid / ethylene glycol / 1,4-cyclohexanedimethanol copolymer, glass transition temperature 81 ° C.
(B2) Amorphous PET system: Amorphous polyethylene terephthalate resin, Eastman Chemical Japan, PCTG5445, 1,4-cyclohexanedimethanol copolymerized polyethylene terephthalate resin, glass transition temperature 81 ° C.
(B3) Amorphous PET: Amorphous polyethylene terephthalate resin, Toyobo Co., Ltd., SR173CA, neopentyl glycol copolymer polyethylene terephthalate resin, glass transition temperature 79 ° C.
(C1) PBT type: polybutylene terephthalate resin, Polyplastic Co., Ltd., DURANEX 500LP, isophthalic acid copolymerized polybutylene terephthalate resin, glass transition temperature 22 ° C.
(C2) PBT: polybutylene terephthalate resin, Toray Industries, Inc., Toraycon 1200S, glass transition temperature 40 ° C.
(D1) MBS: Methyl methacrylate-butadiene-styrene copolymer, Kaneka Chemical Co., Ltd., Kane Ace B-31.
(D2) FM21: Methacrylate / Acrylate rubber graft copolymer, Kaneka Chemical Co., Ltd., Kane Ace FM21.
(E) Lubricant: Montanate ester wax, Clariant Japan Co., Ltd., Ricowax OP, calcium saponified montanate ester wax.
(F) PTT series: Polytrimethylene terephthalate series resin, Asahi Kasei Corporation, 10N00, glass transition temperature 47 ° C.
Colorant: Sumika Color Co., Ltd., EPM7A1441, white masterbatch.
樹脂成分として、(Ａ)ガラス転移温度１０℃の変性ポリエチレンテレフタレート系樹脂を含有し、２０％モジュラスが３.６ＭＰａである実施例１の化粧フィルム、(Ａ)ガラス転移温度１０℃の変性ポリエチレンテレフタレート系樹脂と(Ｂ１)ガラス転移温度８１℃の非晶性ポリエチレンテレフタレート系樹脂を含有し、２０％モジュラスが１１ＭＰａである実施例２の化粧フィルム、(Ａ)ガラス転移温度１０℃の変性ポリエチレンテレフタレート系樹脂、(Ｂ１)ガラス転移温度８１℃の非晶性ポリエチレンテレフタレート系樹脂及び(Ｃ１)ガラス転移温度２２℃のポリブチレンテレフタレート系樹脂を含有し、２０％モジュラスが１８ＭＰａである実施例３の化粧フィルム、(Ａ)ガラス転移温度１０℃の変性ポリエチレンテレフタレート系樹脂、(Ｂ１)ガラス転移温度８１℃の非晶性ポリエチレンテレフタレート系樹脂及び(Ｄ１)メタクリル酸メチル−ブタジエン−スチレン共重合体を含有し、２０％モジュラスが１５ＭＰａである実施例４の化粧フィルム、(Ａ)ガラス転移温度１０℃の変性ポリエチレンテレフタレート系樹脂、(Ｂ１)ガラス転移温度８１℃の非晶性ポリエチレンテレフタレート系樹脂及び(Ｄ１)メタクリル酸メチル−ブタジエン−スチレン共重合体を含有し、２０％モジュラスが１０ＭＰａである実施例５の化粧フィルム、(Ａ)ガラス転移温度１０℃の変性ポリエチレンテレフタレート系樹脂、(Ｂ１)ガラス転移温度８１℃の非晶性ポリエチレンテレフタレート系樹脂、(Ｃ１)ガラス転移温度２２℃のポリブチレンテレフタレート系樹脂及び(Ｄ１)メタクリル酸メチル−ブタジエン−スチレン共重合体を含有し、２０％モジュラスが１６ＭＰａである着色剤を配合した実施例６の化粧フィルムは、いずれもエンボス転写性が良好であり、耐沸騰水性も優れている。
同様な樹脂成分を含有し、２０％モジュラスが１７〜１９ＭＰａである化粧フィルムを下地とし、実施例５の化粧フィルムを上地として積層した実施例７と実施例１１の積層化粧シート、上地が実施例５の化粧フィルムであり、下地の化粧フィルムが樹脂成分として(Ｂ１)ガラス転移温度８１℃の非晶性ポリエチレンテレフタレート系樹脂４０重量％と(Ｃ２)ガラス転移温度４０℃のポリブチレンテレフタレート樹脂６０重量％を含有する実施例８の積層化粧シート、上地が実施例５の化粧フィルムであり、下地の化粧フィルムが樹脂成分として(Ｂ２)ガラス転移温度が８１℃である非晶性ポリエチレンテレフタレート系樹脂６０重量％と(Ｆ)ガラス転移温度４７℃のポリトリメチレンテレフタレート系樹脂４０重量％を含有する実施例１０の積層化粧シートは、いずれもエンボス転写性が良好であり、耐沸騰水性も優れ、熱ラミネートによる上地と下地の密着性も良好である。又同様な樹脂成分を含有し、２０％モジュラスが１７ＭＰａである化粧フィルムを下地とし、二軸延伸ポリエチレンテレフタレートフィルムを上地としてドライラミネーションにより積層した実施例９の積層化粧シートは、耐沸騰水性に優れている。
これに対して、樹脂成分として(Ｃ２)ガラス転移温度４０℃のポリブチレンテレフタレート樹脂のみを含有し、２０％モジュラスが２１ＭＰａである比較例１の化粧フィルムは、エンボス転写性が不良である。樹脂成分として(Ｂ１)ガラス転移温度８１℃の非晶性ポリエチレンテレフタレート系樹脂と(Ｃ１)ガラス転移温度２２℃のポリブチレンテレフタレート系樹脂を含有し、２０％モジュラスが２８ＭＰａである比較例２の化粧フィルム、(Ａ)ガラス転移温度１０℃の変性ポリエチレンテレフタレート系樹脂、(Ｂ１)ガラス転移温度８１℃の非晶性ポリエチレンテレフタレート系樹脂及び(Ｃ１)ガラス転移温度２２℃のポリブチレンテレフタレート系樹脂を含有するが、(Ａ)成分の含有量が少なく、２０％モジュラスが２７ＭＰａである比較例３の化粧フィルムは、耐沸騰水性が不良である。
比較例１と同じ樹脂組成の化粧フィルムを積層した比較例４の積層化粧シート、比較例１の化粧フィルムを積層した比較例５の積層化粧シートは、エンボス転写性が不良であり、熱ラミネート密着性も低い。比較例２の化粧フィルムを積層した比較例６の積層化粧シートは、耐沸騰水性が不良である。実施例５の化粧フィルムを積層し、二液硬化型のトップコートを施しても、下地の化粧フィルムの樹脂成分の(Ａ)ガラス転移温度１０℃の変性ポリエチレンテレフタレート系樹脂の含有量が少ない比較例７の積層化粧シートは、耐沸騰水性が不良である。
As a resin component, (A) a decorative polyethylene terephthalate resin having a glass transition temperature of 10 ° C. and containing 20% modulus of 3.6 MPa, (A) a modified polyethylene terephthalate having a glass transition temperature of 10 ° C. (B1) A decorative film of Example 2 containing an amorphous polyethylene terephthalate resin having a glass transition temperature of 81 ° C. and a 20% modulus of 11 MPa, and (A) a modified polyethylene terephthalate system having a glass transition temperature of 10 ° C. A decorative film of Example 3 containing a resin, (B1) an amorphous polyethylene terephthalate resin having a glass transition temperature of 81 ° C., and (C1) a polybutylene terephthalate resin having a glass transition temperature of 22 ° C. and having a 20% modulus of 18 MPa. (A) a modified polyethylene terephthalate resin having a glass transition temperature of 10 ° C., B1) A decorative film of Example 4 containing an amorphous polyethylene terephthalate resin having a glass transition temperature of 81 ° C. and (D1) a methyl methacrylate-butadiene-styrene copolymer and having a 20% modulus of 15 MPa, (A) It contains a modified polyethylene terephthalate resin having a glass transition temperature of 10 ° C., (B1) an amorphous polyethylene terephthalate resin having a glass transition temperature of 81 ° C., and (D1) a methyl methacrylate-butadiene-styrene copolymer. The decorative film of Example 5 having a pressure of 10 MPa, (A) a modified polyethylene terephthalate resin having a glass transition temperature of 10 ° C., (B1) an amorphous polyethylene terephthalate resin having a glass transition temperature of 81 ° C., and (C1) a glass transition temperature of 22 ° C. Polybutylene terephthalate resin and (D1) methyl methacrylate-butyl Diene - containing styrene copolymer, decorative film of Example 6 20% modulus was blended colorant is 16MPa are both good embossing characteristics, is excellent boiling water resistance.
A laminated decorative sheet of Example 7 and Example 11 in which the decorative film containing the same resin component and having a 20% modulus of 17 to 19 MPa as a base and the decorative film of Example 5 as a base is laminated. It is a decorative film of Example 5, and the base decorative film is a resin component (B1) 40% by weight of an amorphous polyethylene terephthalate resin having a glass transition temperature of 81 ° C. and (C2) a polybutylene terephthalate resin having a glass transition temperature of 40 ° C. A laminated decorative sheet of Example 8 containing 60% by weight, the top is the decorative film of Example 5, and the base decorative film is a resin component (B2) Amorphous polyethylene terephthalate having a glass transition temperature of 81 ° C. Example 10 containing 60% by weight of a resin and 40% by weight of (F) a polytrimethylene terephthalate resin having a glass transition temperature of 47 ° C. Layer decorative sheet are both good embossing characteristics, boiling water resistance excellent adhesion to the upper base and the underlying by heat lamination is good. Also, the laminated decorative sheet of Example 9 containing a similar resin component and having a 20% modulus of 17 MPa as a base and a biaxially stretched polyethylene terephthalate film as a base and laminated by dry lamination is resistant to boiling water. Are better.
On the other hand, the decorative film of Comparative Example 1 containing only (C2) a polybutylene terephthalate resin having a glass transition temperature of 40 ° C. as a resin component and having a 20% modulus of 21 MPa has poor emboss transferability. The makeup of Comparative Example 2 containing (B1) an amorphous polyethylene terephthalate resin having a glass transition temperature of 81 ° C. and (C1) a polybutylene terephthalate resin having a glass transition temperature of 22 ° C. as the resin component, and having a 20% modulus of 28 MPa. Film, (A) modified polyethylene terephthalate resin having a glass transition temperature of 10 ° C, (B1) amorphous polyethylene terephthalate resin having a glass transition temperature of 81 ° C, and (C1) a polybutylene terephthalate resin having a glass transition temperature of 22 ° C However, the decorative film of Comparative Example 3 in which the content of the component (A) is small and the 20% modulus is 27 MPa has poor boiling water resistance.
The laminated decorative sheet of Comparative Example 4 in which a decorative film having the same resin composition as that of Comparative Example 1 was laminated and the laminated decorative sheet of Comparative Example 5 in which the decorative film of Comparative Example 1 was laminated had poor emboss transferability and were heat laminated. The nature is also low. The laminated decorative sheet of Comparative Example 6 in which the decorative film of Comparative Example 2 is laminated has poor boiling water resistance. Comparison in which the content of the modified polyethylene terephthalate resin having a glass transition temperature of 10 ° C. as the resin component of the base decorative film is low even when the decorative film of Example 5 is laminated and a two-component curable topcoat is applied. The laminated decorative sheet of Example 7 has poor boiling water resistance.
本発明の鋼板用化粧フィルム及び鋼板用積層化粧シートは、耐湿熱性とエンボス転写性に優れ、熱ラミメネート時の層間の密着性、表面エンボスの耐シボ流れ性に優れるので、ラミネート鋼板に加工して、家庭電気製品、家具調度品、家屋内装材などとして好適に用いることができる。 The decorative film for steel sheet and laminated decorative sheet for steel sheet of the present invention are excellent in moisture and heat resistance and emboss transfer property, and are excellent in adhesion between layers at the time of thermal lamination and surface flow resistance of surface embossing. It can be suitably used as household electrical appliances, furniture furnishings, indoor interior materials, and the like.
Claims (17)
The laminated decorative sheet for steel sheet according to any one of claims 10 to 16, wherein the laminated upper sheet has a two-component curable top coat or an ultraviolet curable top coat.