JP2004331149A

JP2004331149A - Lid for use of tray-like container

Info

Publication number: JP2004331149A
Application number: JP2003128732A
Authority: JP
Inventors: Eishin Miyake; 英信三宅; Atsushi Tsujii; 篤辻井; Koichi Shiozaki; 浩一塩崎; Hirofumi Kawai; 広文河合; Yasuhiko Sei; 康彦静
Original assignee: Toppan Printing Co Ltd
Current assignee: Toppan Inc
Priority date: 2003-05-07
Filing date: 2003-05-07
Publication date: 2004-11-25
Anticipated expiration: 2023-05-07
Also published as: JP4196723B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide a lid for use of a tray-like container with which an adhesion strength between a base material and an intermediate layer is stabilized and the adhesion strength between the base material and the intermediate layer does not become unstable due to the extrusion temperature of molten polyethylene. <P>SOLUTION: The tray-like container (20) includes a bottom wall (21), a peripheral wall (22) standing on the periphery thereof, and an upper opening (23), and includes a flange (24) horizontally extending outward from the upper end rim of the peripheral wall. The lid (10) for use of the tray-like container covers the upper opening of the container (20) and is heat-sealed with the flange. The lid is constituted of a composite film (10) consisting of the base material (11), a print layer (12), the intermediate layer (13) and a sealant layer (14) sequentially from the outside of the container. A linear low-density polyethylene resin is used respectively in the intermediate layer (13) and in a layer (141) positioned at a region facing the intermediate layer of the sealant layer (14). <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

【０００１】
【発明の属する技術分野】
本発明は、カレー、シチューなどの固型ルー等を収納するトレー状容器の開口部を覆いフランジ部と熱封緘されるトレー状容器用蓋材に関し、特には、ガスバリア性を有し、かつ、容器から容易に開封が可能ないわゆるイージーピール性を有するトレー状容器用蓋材に関する。
【０００２】
【従来の技術】
従来、底壁とその周縁に立設された周壁と上部開口を備え、該周壁の上端縁より外方に水平方向に延出されたフランジ部を備えたポリプロピレン樹脂、ポリエチレン樹脂等のポリオレフィン系樹脂を主体とするトレー状容器に、カレー、シチュー等の固型ルーを収納して、上部開口を基材フィルム／イージーピールフィルム等の複合フィルムからなる蓋材で密封シールしたトレー状容器包装体が提案されている。
【０００３】
しかしながら、この種の蓋材は、複合フィルムからトレー状容器に適合した大きさの蓋材に打ち抜く際、フィルムのカット性が悪い場合には蓋材の端面がギザギザになり易く、この状態でトレー状容器と密封シールした場合、開封する際にカット部分のギザギザがノック効果となり材質破壊されてしまい、蓋材がトレー状容器からきれいに剥離できないという問題があった。
【０００４】
この問題を解決するための方法として、例えば、開封時に、界面剥離によりイージーピールし、同時に基材から破れが走って蓋材が破れそうになると、中間層の部分が層間剥離して、蓋材の破れを防止するようにしたものがある（例えば、特許文献１、特許文献２）。
【０００５】
【特許文献１】
特開２００１−３１５８３３号公報
【特許文献２】
特開２００１−３１５８３６号公報
【０００６】
ところが、この発明においては、基材層であるアルミナを蒸着したポリエチレンテレフタレートフィルムと中間層である溶融ポリエチレンとの間の接着強度を安定化させることが困難である、溶融ポリエチレンの押し出し温度により基材と中間層の接着強度が不安定になる等の問題がある。
【０００７】
【発明が解決しようとする課題】
本発明は、基材に蒸着プラスチックフィルム、シーラント層にイージーピールフィルムを使用して、ポリエチレンテレフタレートフィルム・アルミナ蒸着層／インキ層／線状低密度ポリエチレン樹脂／シーラント層（線状低密度ポリエチレン樹脂／ポリプロピレン樹脂用イージーピール層）構成からなる複合フィルムを蓋材に使用したトレー状容器用蓋材に関する以上のような問題点を解決するためになされたもので、基材と中間層との接着強度を安定化させ、また、溶融ポリエチレンの押し出し温度により基材と中間層の接着強度が不安定にならないようにしたトレー状容器用蓋材を提供することを課題とする。
【０００８】
【課題を解決するための手段】
本発明の請求項１の発明は、底壁とその周縁に立設された周壁と上部開口を備え、該周壁の上端縁より外方に水平方向に延出されたフランジ部を備えたトレー状容器の、前記上部開口を覆いフランジ部と熱封緘されるトレー状容器用蓋材において、前記蓋材が、容器外側から、基材／印刷層／中間層／シーラント層の層構成からなる複合フィルムで構成されており、前記中間層と、シーラント層の中間層と対向する部位に位置する層とに、それぞれ線状低密度ポリエチレン樹脂が使用されていることを特徴とする、トレー状容器用蓋材である。
【０００９】
このように請求項１記載の発明によれば、中間層と、シーラント層の中間層と対向する部位に位置する層とに、それぞれ線状低密度ポリエチレン樹脂を使用しているので、蓋材のフランジ部に対する接着強度が強くなっても蓋材の剥離時に蓋材が材質破壊することがない。
【００１０】
また、請求項２の発明は、請求項１の発明において、前記中間層の線状低密度ポリエチレン樹脂の厚さが２０〜３０μｍであることを特徴とする、トレー状容器用蓋材である。
【００１１】
このように請求項２記載の発明によれば、中間層の線状低密度ポリエチレン樹脂の厚さを２０〜３０μｍとしたので、開封時に蓋材が破れることがない。
【００１２】
また、請求項３の発明は、請求項１又は２の発明において、前記シーラント層の中間層と対向する部位に位置する層の線状低密度ポリエチレン樹脂の厚さが２０〜３０μｍであることを特徴とする、請求項１又は２記載のトレー状容器用蓋材である。
【００１３】
このように請求項３記載の発明によれば、シーラント層であるイージーピールフィルムの中間層と対向する部位に位置する層の線状低密度ポリエチレン樹脂の厚さを２０〜３０μｍとしたので、安定した接着強度と蓋材の開封時の材質破壊，特に、エッジ切れ防止の効果が高い。
【００１４】
【発明の実施の形態】
本発明のトレー状容器用蓋材を一実施形態に基づいて以下に詳細に説明する。本発明のトレー状容器用蓋材は、例えば、図１、図２に示すように、底壁（２１）とその周縁に立設された周壁（２２）と上部開口（２３）を備え、該周壁の上端縁より外方に水平方向に延出されたフランジ部（２４）を備えたトレー状容器（２０）の、上部開口を覆いフランジ部と熱封緘されるトレー状容器用蓋材（１０）である。
【００１５】
蓋材（１０）は、容器外側から、基材（１１）／印刷層（１２）／中間層（１３）／シーラント層（１４）、からなる複合フィルム（１０）から構成されている。
そして、中間層（１３）と、シーラント層（１４）の中間層と対向して位置する部位の層（１４１）とに、それぞれ線状低密度ポリエチレン樹脂が使用されているものである。
【００１６】
基材（１１）としては、ポリエチレンテレフタレートフィルム、ポリプロピレンフィルム、ポリアミドフィルム等のプラスチックフィルム、アルミニウム箔、紙の単体又はこれらの２以上の複合材料が好ましく使用できる。
【００１７】
アルミニウムや酸化アルミニウム、酸化ケイ素などの薄膜を上記のプラスチックフィルムに物理蒸着あるいは化学蒸着などの蒸着法により設けた蒸着プラスチックフィルムも使用可能である。
特に、一軸ないし二軸延伸されたポリエチレンテレフタレートフィルム上に、酸化アルミニウムや酸化ケイ素などの無機化合物の薄膜を設けたものが好ましく使用できる。
これらの材質を適宜に選択することにより、目的および用途に応じて強度、ガスバリア性、耐熱性や防湿性を付与させることが可能である。
【００１８】
印刷層（１２）は、一般的には、基材（１１）の裏面に設けられるものであり、基材（１１）にグラビア法などの公知の印刷手法により、適宜のデザインの絵柄や文字により印刷層（１２）を形成させる。
【００１９】
中間層（１３）は印刷層を設けた基材（１１）と後記するイージーピールフィルムからなるシーラント層（１４）を接着させる層で、線状低密度ポリエチレン樹脂が好ましく使用できる。
中間層（１３）に線状低密度ポリエチレン樹脂を使用することにより、蓋材をトレー状容器のフランジ部から剥がす際、材質破壊を起こさずに剥がすことができる。
線状低密度ポリエチレン樹脂は、破壊しづらく、伸び易いという強靱性を必要とするため、好ましくは炭素数が６のＣ_６、炭素数が８のＣ_８の線状低密度ポリエチレン樹脂が良く、密度は０．９１０〜０．９２０ｇ／ｃｍ^３が良い。
【００２０】
シーラント層（１４）は、蓋材の最内層に位置する層で、トレー状容器（２０）のフランジ部（２４）と熱封緘性を有する樹脂であり、かつ、イージーピール性を必要とする。
このような条件を満たすものとして、多層構成のイージーピールフィルムがある。具体的には、例えば、〔外層〕線状低密度ポリエチレン樹脂（２０μｍ）／ポリプロピレン樹脂と線状低密度ポリエチレン樹脂のブレンド層（１０μｍ）／ポリオレフィン系イージーピール性樹脂「ＶＭＸ」（１０μｍ）（ジェイフィルム株式会社製）〔内層〕構成からなるイージーピールフィルム（厚さ４０μｍ）が好ましく使用できる。
【００２１】
多層構成のイージーピールフィルムに使用する線状低密度ポリエチレン樹脂も中間層に使用する線状低密度ポリエチレン樹脂と同様に、好ましくは炭素数が６のＣ_６、炭素数が８のＣ_８の線状低密度ポリエチレン樹脂が良く、密度は０．９１０〜０．９２０ｇ／ｃｍ^３が良い。
【００２２】
印刷層（１２）を設けた基材（１１）とシーラント層（１４）とは、一般的には、溶融ポリエチレン樹脂等を中間層として、該中間層（１３）を介して、例えば、押し出しラミネート法により貼り合わせることができる。
その際、基材（印刷層）にアンカーコート剤を塗布して押し出しラミネートすることにより、基材と中間層との間の接着強度をより強固なものとすることができる。
【００２３】
【実施例】
以下実施例により本発明を詳細に説明する。
〈実験；１〉
基材（１１）として、表面に酸化アルミニウムの薄膜を蒸着法により４００ｎｍ程度の厚さに設けた延伸ポリエチレンテレフタレートフィルム（厚さ１６μｍ）を用意した。
このフィルムの蒸着薄膜層の上にグラビア印刷法により印刷層（１２）を設けた。
【００２４】
別にシーラント層（１４）として、〔外層〕線状低密度ポリエチレン樹脂（２０μｍ）／ポリプロピレン樹脂と線状低密度ポリエチレン樹脂のブレンド層（１０μｍ）／ポリオレフィン系イージーピール性樹脂ＶＭＸ）（１０μｍ）〔内層〕構成からなる多層構成のイージーピールフィルム（ジェイフィルム株式会社製）を用意した。
【００２５】
基材の印刷層（１２）とシーラント層（１４）の線状低密度ポリエチレン樹脂（１４１）面とを対向させて、線状低密度ポリエチレン樹脂を介在させ、溶融押し出しラミネート法により貼り合わせ（線状低密度ポリエチレン樹脂の厚さは２０μｍ）、酸化アルミニウムの薄膜が形成された延伸ポリエチレンテレフタレートフィルム（厚さ１６μｍ）（１１）／印刷層（１２）／線状低密度ポリエチレン樹脂（厚さ２０μｍ）（１３）／線状低密度ポリエチレン樹脂（２０μｍ）／ポリプロピレン樹脂と線状低密度ポリエチレン樹脂のブレンド層（１０μｍ）／シーラント（１０μｍ）（１４）構成からなる複合フィルムを作製した。
【００２６】
なお、この際、アンカーコート剤として、２液水性型ポリウレエタン系アンカーコート剤であるチタボンドＴ−１８５（日本曹達株式会社製）を印刷層（１２）の上にグラビア印刷法により塗布し、中間層（１３）となる溶融線状低密度ポリエチレン樹脂と印刷層（１２）の間の接着補強剤とした。そして、グラビア版の版深度を代えることにより、基材（１１）と中間層（１３）の接着強度が１〜４Ｎ／１５ｍｍとなるものを実施例１のトレー状容器用蓋材として作製し、また、接着強度が４〜６Ｎ／１５ｍｍとなるものを実施例２のトレー状容器用蓋材として作製し、接着強度が１Ｎ／１５ｍｍ以下となるものを比較例１のトレー状容器用蓋材とて作製した。
【００２７】
〈実験；２〉
中間層となる樹脂として線状低密度ポリエチレン樹脂（２０μｍ）の代わりに低密度ポリエチレン樹脂（１５μｍ）を用いた以外は実験１と同じ基材、印刷層、シーラント層を用いて、酸化アルミニウムの薄膜が形成された延伸ポリエチレンテレフタレートフィルム（厚さ１６μｍ）（１１）／印刷層（１２）／低密度ポリエチレン樹脂（厚さ１５μｍ）（１３）／線状低密度ポリエチレン樹脂（２０μｍ）／ポリプロピレン樹脂と線状低密度ポリエチレン樹脂のブレンド層（１０μｍ）／シーラント（１０μｍ）（１４）構成からなる複合フィルムを作製した。
【００２８】
なお、この際、実験１で用いたと同じアンカーコート剤を印刷層（１２）の上にグラビア印刷法により塗布し、中間層（１３）となる溶融線状低密度ポリエチレン樹脂と印刷層（１２）の間の接着補強剤とした。そして、グラビア版の版深度を代えることにより、基材（１１）と中間層（１３）の接着強度が１〜４Ｎ／１５ｍｍとなるものを比較例２のトレー状容器用蓋材として作製し、また、接着強度が４〜６Ｎ／１５ｍｍとなるものを比較例３のトレー状容器用蓋材として作製し、接着強度が１Ｎ／１５ｍｍ以下となるものを比較例４のトレー状容器用蓋材とて作製した。
【００２９】
このようにして作製した実施例２種類、比較例４種類、合計６種類のトレー状容器用蓋材をポリプロピレン樹脂製のフランジ部を有するトレー状容器に被せて温度；１４５°Ｃ、圧力；０．２ＭＰａ、時間；１秒の条件で熱シール後、蓋材をカット性の悪い刃で切断面がギザギザを作った状態でカットし、蓋材の開封性を以下の条件でチェック、観察した。その結果を表１に示す。
開封性の検査方法‥蓋材の先端を手で摘んでトレー状容器のフランジから剥がす。その際、中間層の樹脂とシーラント層の内面樹脂との間から材質破壊せずに、きれいにイージーピールするものを剥離良好（○）とし、材質破壊したり、二重袋になるものを不良（×）とした。
【００３０】
【表１】

【００３１】
このように、多層のイージーピールフィルムの内層に線状低密度ポリエチレン樹脂層を設け、中間層の樹脂も線状低密度ポリエチレン樹脂を使用することにより、蓋材の切断面にギザギザがあったとしてもきれいにイージーピールすることができ、接着強度が上がっても材質破壊することがない（実験１）。
【００３２】
【発明の効果】
上記のように、本発明のトレー状容器用蓋材を用いることにより、安定した接着強度が維持でき、且つ、強靱な線状低密度ポリエチレン樹脂を設けることで二重袋や材質破壊等の開封不良をなくすことができる。
【図面の簡単な説明】
【図１】本発明のトレー状容器用蓋材をトレー状容器に被せて熱封緘した状態の一実施例を示す、部分断面説明図である。
【図２】本発明のトレー状容器用蓋材の層構成の一実施例を示す、断面説明図である。
【符号の説明】
１０‥‥蓋材、複合フィルム
１１‥‥基材
１２‥‥印刷層
１３‥‥中間層
１４‥‥シーラント層
１４１‥‥シーラント層の中間層に対向する部位に位置する層
２０‥‥トレー状容器
２１‥‥底壁
２２‥‥周壁
２３‥‥上部開口
２４‥‥フランジ部[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a tray-like container lid material that covers the opening of a tray-like container for storing a solid roux or the like such as curry and stew, and is heat-sealed with a flange portion, and in particular, has gas barrier properties, and The present invention relates to a lid material for a tray-shaped container having a so-called easy-peeling property, which can be easily opened from the container.
[0002]
[Prior art]
Conventionally, a polyolefin resin such as a polypropylene resin or a polyethylene resin having a bottom wall and a peripheral wall and an upper opening erected on the peripheral edge thereof, and a flange portion extending horizontally outward from an upper edge of the peripheral wall. In a tray-shaped container mainly composed of a tray, a tray-shaped container package containing a solid roux such as curry and stew, and sealing the upper opening with a lid made of a composite film such as a base film / easy peel film is sealed. Proposed.
[0003]
However, when punching a lid material of this type from a composite film into a lid material of a size suitable for a tray-shaped container, if the cutability of the film is poor, the end surface of the lid material is likely to be jagged. When the container is hermetically sealed with the container, there is a problem that the jagged portion of the cut portion is knocked when the container is opened, and the material is destroyed, so that the lid material cannot be peeled off from the tray container.
[0004]
As a method for solving this problem, for example, at the time of opening, easy peeling due to interfacial peeling, and at the same time, when the lid material is about to be torn due to tearing from the base material, the intermediate layer portion is delaminated and the lid material There is a device that prevents the breakage of an image (for example, Patent Documents 1 and 2).
[0005]
[Patent Document 1]
JP 2001-315833 A [Patent Document 2]
JP 2001-315836 A
However, in the present invention, it is difficult to stabilize the adhesive strength between a polyethylene terephthalate film on which alumina is deposited as a base material layer and molten polyethylene as an intermediate layer. However, there is a problem that the adhesive strength of the intermediate layer becomes unstable.
[0007]
[Problems to be solved by the invention]
The present invention uses a polyethylene terephthalate film / alumina vapor deposited layer / ink layer / linear low density polyethylene resin / sealant layer (linear low density polyethylene resin / This was made to solve the above-mentioned problems with the lid material for tray-shaped containers using a composite film consisting of an easy peel layer for polypropylene resin) as the lid material, and the adhesive strength between the base material and the intermediate layer It is another object of the present invention to provide a lid material for a tray-shaped container, which stabilizes the adhesiveness of the molten polyethylene and prevents the adhesive strength between the base material and the intermediate layer from becoming unstable due to the extrusion temperature of the molten polyethylene.
[0008]
[Means for Solving the Problems]
According to a first aspect of the present invention, there is provided a tray having a bottom wall, a peripheral wall erected on the peripheral edge thereof, and an upper opening, and a flange portion extending horizontally outward from an upper edge of the peripheral wall. In a lid material for a tray-shaped container which covers the upper opening of the container and is heat-sealed with a flange portion, the lid material has a layer structure of a base material / printing layer / intermediate layer / sealant layer from the outside of the container. Wherein the intermediate layer and a layer of the sealant layer located at a portion facing the intermediate layer are each made of a linear low-density polyethylene resin, wherein a lid for a tray-shaped container is provided. Material.
[0009]
As described above, according to the first aspect of the invention, since the linear low-density polyethylene resin is used for each of the intermediate layer and the layer of the sealant layer facing the intermediate layer, Even when the adhesive strength to the flange portion is increased, the material of the lid material does not break when the lid material is peeled off.
[0010]
A second aspect of the present invention is the lid material for a tray-shaped container according to the first aspect of the present invention, wherein the thickness of the linear low-density polyethylene resin of the intermediate layer is 20 to 30 μm.
[0011]
Thus, according to the second aspect of the present invention, the thickness of the linear low-density polyethylene resin of the intermediate layer is set to 20 to 30 μm, so that the lid material is not broken at the time of opening.
[0012]
According to a third aspect of the present invention, in the first or second aspect of the invention, the thickness of the linear low-density polyethylene resin of the layer located at a portion facing the intermediate layer of the sealant layer is 20 to 30 μm. The lid material for a tray-shaped container according to claim 1 or 2, which is characterized by the following.
[0013]
As described above, according to the third aspect of the present invention, the thickness of the linear low-density polyethylene resin of the layer located at the portion facing the intermediate layer of the easy peel film as the sealant layer is set to 20 to 30 μm. The adhesive strength and the effect of breaking the material at the time of opening the lid material, particularly, the effect of preventing edge breakage are high.
[0014]
BEST MODE FOR CARRYING OUT THE INVENTION
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The lid material for a tray-shaped container of the present invention will be described in detail below based on one embodiment. The lid material for a tray-shaped container of the present invention includes, for example, as shown in FIGS. 1 and 2, a bottom wall (21), a peripheral wall (22) erected on the periphery thereof, and an upper opening (23). A tray-shaped container lid (10) having a flange (24) extending horizontally outward from the upper edge of the peripheral wall and covering the upper opening of the tray-shaped container (20) and being thermally sealed with the flange. ).
[0015]
The lid member (10) is composed of a composite film (10) composed of a substrate (11) / printed layer (12) / intermediate layer (13) / sealant layer (14) from the outside of the container.
The intermediate low-density polyethylene resin is used for each of the intermediate layer (13) and the layer (141) of the sealant layer (14) which is located opposite to the intermediate layer.
[0016]
As the base material (11), a plastic film such as a polyethylene terephthalate film, a polypropylene film, or a polyamide film, an aluminum foil, a simple substance of paper, or a composite material of two or more of these can be preferably used.
[0017]
A vapor-deposited plastic film in which a thin film of aluminum, aluminum oxide, silicon oxide, or the like is provided on the above plastic film by a vapor deposition method such as physical vapor deposition or chemical vapor deposition can also be used.
In particular, a film obtained by providing a thin film of an inorganic compound such as aluminum oxide or silicon oxide on a uniaxially or biaxially stretched polyethylene terephthalate film can be preferably used.
By appropriately selecting these materials, it is possible to impart strength, gas barrier properties, heat resistance and moisture resistance according to the purpose and application.
[0018]
The printing layer (12) is generally provided on the back surface of the base material (11), and is formed on the base material (11) by a well-known printing technique such as a gravure method using a picture or a character of an appropriate design. A printing layer (12) is formed.
[0019]
The intermediate layer (13) is a layer for adhering a base material (11) provided with a printing layer and a sealant layer (14) made of an easy peel film described later, and a linear low density polyethylene resin can be preferably used.
By using the linear low-density polyethylene resin for the intermediate layer (13), when the lid material is peeled off from the flange portion of the tray-shaped container, the lid material can be peeled off without causing material destruction.
The linear low density polyethylene resin, hard to destroy, requires a toughness of easy elongation, preferably good linear low density polyethylene resin of C ₈ of C _6, carbon atoms 8 6 carbon atoms, The density is preferably 0.910 to 0.920 g / cm ³ .
[0020]
The sealant layer (14) is a resin located at the innermost layer of the lid material, is a resin having heat sealing properties with the flange portion (24) of the tray-like container (20), and requires easy peelability.
An example of a film that satisfies such conditions is an easy-peel film having a multilayer structure. Specifically, for example, [outer layer] linear low-density polyethylene resin (20 μm) / blend layer of polypropylene resin and linear low-density polyethylene resin (10 μm) / polyolefin-based easy-peel resin “VMX” (10 μm) (J) An easy-peel film (thickness: 40 μm) having a [inner layer] configuration can be preferably used.
[0021]
Similarly to the linear low-density polyethylene resin used for the intermediate layer, the linear low-density polyethylene resin used for the easy-peel film having a multilayer structure is preferably a C ₆ wire having ₆ carbon atoms and a C ₈ wire having 8 carbon atoms. A low-density polyethylene resin is preferable, and the density is preferably 0.910 to 0.920 g / cm ³ .
[0022]
The base material (11) provided with the printing layer (12) and the sealant layer (14) are generally formed, for example, by extrusion lamination using the molten polyethylene resin or the like as an intermediate layer via the intermediate layer (13). It can be bonded by a method.
At that time, the adhesive strength between the base material and the intermediate layer can be further increased by applying the anchor coat agent to the base material (printing layer) and performing extrusion lamination.
[0023]
【Example】
Hereinafter, the present invention will be described in detail with reference to examples.
<Experiment;1>
As the base material (11), a stretched polyethylene terephthalate film (16 μm in thickness) having a thin film of aluminum oxide provided on the surface to a thickness of about 400 nm by a vapor deposition method was prepared.
A printing layer (12) was provided on the vapor-deposited thin film layer of this film by a gravure printing method.
[0024]
Separately, as the sealant layer (14), [outer layer] linear low-density polyethylene resin (20 μm) / blend layer of polypropylene resin and linear low-density polyethylene resin (10 μm) / polyolefin-based easy-peel resin VMX (10 μm) [inner layer An easy peel film (manufactured by J-Film Co., Ltd.) having a multilayer structure having the following structure was prepared.
[0025]
The printed layer (12) of the base material and the surface of the linear low-density polyethylene resin (141) of the sealant layer (14) are opposed to each other, and the linear low-density polyethylene resin is interposed therebetween and bonded by a melt extrusion lamination method (line Low-density polyethylene resin is 20 μm in thickness), stretched polyethylene terephthalate film (16 μm in thickness) on which a thin film of aluminum oxide is formed (11) / printing layer (12) / linear low-density polyethylene resin (20 μm in thickness) (13) / A composite film having a linear low density polyethylene resin (20 μm) / blended layer of a polypropylene resin and a linear low density polyethylene resin (10 μm) / sealant (10 μm) (14) was prepared.
[0026]
In this case, as an anchor coating agent, Titabond T-185 (manufactured by Nippon Soda Co., Ltd.), which is a two-pack aqueous polyurethane-based anchor coating agent, was applied onto the printing layer (12) by a gravure printing method. It was used as an adhesion reinforcing agent between the molten linear low-density polyethylene resin (13) and the printed layer (12). Then, by changing the plate depth of the gravure plate, a material having an adhesive strength between the base material (11) and the intermediate layer (13) of 1 to 4 N / 15 mm was produced as the lid material for the tray-shaped container of Example 1, In addition, a material having an adhesive strength of 4 to 6 N / 15 mm was prepared as the tray-shaped container lid material of Example 2, and a material having an adhesive strength of 1 N / 15 mm or less was used as the tray-shaped container lid material of Comparative Example 1. Produced.
[0027]
<Experiment;2>
An aluminum oxide thin film using the same base material, printing layer, and sealant layer as in Experiment 1 except that the low-density polyethylene resin (15 μm) was used instead of the linear low-density polyethylene resin (20 μm) as the resin for the intermediate layer. Stretched polyethylene terephthalate film on which is formed (thickness 16 μm) (11) / printing layer (12) / low density polyethylene resin (thickness 15 μm) (13) / linear low density polyethylene resin (20 μm) / polypropylene resin and wire A composite film composed of a blend layer (10 μm) / sealant (10 μm) (14) of a low-density polyethylene resin was prepared.
[0028]
At this time, the same anchor coating agent as that used in Experiment 1 was applied onto the printing layer (12) by a gravure printing method, and a molten linear low-density polyethylene resin serving as the intermediate layer (13) and the printing layer (12) were used. And an adhesive reinforcement between the two. Then, by changing the plate depth of the gravure plate, a material having an adhesive strength of the substrate (11) and the intermediate layer (13) of 1 to 4 N / 15 mm was produced as a lid material for a tray-shaped container of Comparative Example 2, In addition, a material having an adhesive strength of 4 to 6 N / 15 mm was prepared as a tray-shaped container lid material of Comparative Example 3, and a material having an adhesive strength of 1 N / 15 mm or less was manufactured as the tray-shaped container lid material of Comparative Example 4. Produced.
[0029]
A total of six kinds of lids for tray-shaped containers, two kinds of examples and four kinds of comparative examples thus produced, were put on a tray-shaped container having a flange portion made of polypropylene resin, and the temperature was 145 ° C., the pressure was 0; After heat sealing under the conditions of .2 MPa and a time of 1 second, the lid material was cut in a state where the cut surface was jagged with a blade having poor cutting properties, and the openability of the lid material was checked and observed under the following conditions. Table 1 shows the results.
Opening inspection method (1) Pick up the tip of the lid material by hand and peel off from the flange of the tray-shaped container. At this time, the material that easily and easily peels without destruction of the material between the resin of the intermediate layer and the inner surface resin of the sealant layer is regarded as good peeling (（), and the material that is destroyed or becomes a double bag is defective ( X).
[0030]
[Table 1]

[0031]
Thus, by providing a linear low-density polyethylene resin layer in the inner layer of the multilayer easy-peel film, and also by using a linear low-density polyethylene resin for the resin of the intermediate layer, assuming that the cut surface of the lid material was jagged. Can easily and easily peel, and the material is not destroyed even if the adhesive strength is increased (Experiment 1).
[0032]
【The invention's effect】
As described above, by using the lid material for a tray-shaped container of the present invention, stable adhesive strength can be maintained, and by providing a tough linear low-density polyethylene resin, double bags or material breakage can be opened. Defects can be eliminated.
[Brief description of the drawings]
FIG. 1 is an explanatory partial cross-sectional view showing one embodiment of a state in which a lid material for a tray-shaped container of the present invention is covered on a tray-shaped container and heat sealed.
FIG. 2 is an explanatory cross-sectional view showing one embodiment of the layer structure of the lid material for a tray-shaped container of the present invention.
[Explanation of symbols]
10 cover material, composite film 11 base material 12 printing layer 13 intermediate layer 14 sealant layer 141 layer located at a position facing the intermediate layer of sealant layer 20 tray-shaped container 21 ‥‥ Bottom wall 22 ‥‥ Peripheral wall 23 ‥‥ Top opening 24 ‥‥ Flange

Claims

A tray-shaped container having a bottom wall, a peripheral wall erected on a peripheral edge thereof, and an upper opening, and a flange-shaped container having a flange portion extending horizontally outward from an upper edge of the peripheral wall; And a lid material for a tray-shaped container that is heat-sealed,
The lid material is composed of a composite film having a layer structure of a base material / printing layer / intermediate layer / sealant layer from the outside of the container, and is located at a position facing the intermediate layer and the intermediate layer of the sealant layer. A lid material for a tray-shaped container, wherein a linear low-density polyethylene resin is used for each of the layers.

The lid material for a tray-like container according to claim 1, wherein the thickness of the linear low-density polyethylene resin of the intermediate layer is 20 to 30 µm.

The lid material for a tray-shaped container according to claim 1 or 2, wherein the thickness of the linear low-density polyethylene resin of a layer located at a portion facing the intermediate layer of the sealant layer is 20 to 30 µm.