JP2004315658A

JP2004315658A - Biaxially oriented polystyrene-based resin adhesive tape or adhesive label

Info

Publication number: JP2004315658A
Application number: JP2003111571A
Authority: JP
Inventors: Koichi Yasugata; 公一安形; Yoshiyuki Tatsuki; 芳幸田附
Original assignee: Asahi Kasei Life and Living Corp
Current assignee: Asahi Kasei Corp
Priority date: 2003-04-16
Filing date: 2003-04-16
Publication date: 2004-11-11
Anticipated expiration: 2023-04-16
Also published as: JP4397620B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide a biaxially oriented polystyrene-based resin adhesive tape or label, especially having properties suitable for a design-displaying tape or label for a container, a case or the like, a tape for fixing a bag and a container, or binding a food, and a stationery tape by improving properties of being easily torn by hand, and properties of being torn straightly. <P>SOLUTION: The biaxially oriented polystyrene-based resin adhesive tape or adhesive label is obtained by using a biaxially oriented film comprising a polystyrene resin as a base material, and has 0.5-4.5 N tear load in the transverse direction of the adhesive tape or the adhesive label, 2.0-8.5 tensile elongation at break in the machine direction, ≥0.7 MPa stress of heat shrinkage at 110°C in the machine direction, and 1.0-4.0 ratio of the heat shrinkages in the machine and transverse directions. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

【０００１】
【発明の属する技術分野】
本発明は、ポリスチレン系樹脂からなるニ軸延伸フィルムを基材とするポリスチレン系樹脂粘着テープまたは粘着ラベルに関する。さらに詳しくは、袋、容器、食品等の表示や密封、固定、封函、結束及び文具等に好適に使用される手切れ性、カット時の直進性に優れる粘着テープまたは粘着ラベル関する。
【０００２】
【従来の技術】
袋、容器、ケース、食品等の意匠表示や、封函用などにプラスチック製のテープ、ラベルが従来から使用されている。これら袋、容器、ケース等には、ポリエチレンテレフタレート、ポリプロピレン、ポリエチレン、ポリスチレンなどのプラスチックが多用されており、またテープ、ラベルの素材も、同様にポリエチレンテレフタレート、ポリプロピレン、ポリ塩化ビニル、セロハン、ポリスチレンなどが一般に知られている。これら素材のテープのうちポリエチレンテレフタレートやポリプロピレン、ポリ塩化ビニル、セロハン製のテープは、手切れ性が悪いため、無機粒子の混合やエンボス加工、テープに傷を入れる、延伸加工方法を工夫するなどの方法で手切れ性を改良することも検討されている。
【０００３】
ところで、近年、高齢化社会になりつつあり、より手切れ性の良いテープが求められ、また製品安全の観点から、刃を用いないで簡単に子供や高齢者でも切れるテープが求められている。
そして、袋や容器等がより簡単に開封できる粘着テープ、ラベルが求められている。
特に、袋の簡易な密封方法として、バッグシーラー用テープを用いて、バッグシーラーで密封される袋や、スーパーマーケットなどのバックヤードでサラダを透明容器に詰め、該容器の本体と蓋を粘着テープで留めたり、調味料を蓋に粘着テープで留めたり、長ねぎ等の食品を粘着テープで結束するなど、粘着テープの使用例が増えてきている。
【０００４】
これらのテープは、強度の観点からポリエチレンテレフタレート製、ポリプロピレン製、セロハン製が多く用いられている。
これらのテープは手切れ性が悪く、手切れ性付与に関し、特開昭５１−１６３４６号公報には、側縁、端縁部に切り込み、裂傷などの傷痕を付与したテープが開示されており、特開平１１−５９５６号公報には、端縁部から離れた内側に傷痕を設けたテープが開示され、特開平５−５９３３４号公報には、両端部に引き裂き開始点を設けるテープが開示されている。
【０００５】
さらに、特開昭５１−３４２７１号公報には、特定の配向性による横引き裂き性を向上したフィルムが提案されている。
特開平５−２８７２４３号公報には、無延伸合成樹脂フィルムと二軸延伸合成樹脂フィルムとの積層フィルムに粘着剤層を設けることで、爪で押さえることにより切断できるテープが開示されている。
また、粘着テープをより剥がしやすくするため、特開平５−１３２０７２号公報には、粘着剤を基材表面全面に施さないテープが開示されている。
【０００６】
ポリスチレン系樹脂フィルムを基材とした粘着テープ、粘着ラベルに関しては、特開昭５８−１８９２８２号公報で開示されるように脆さを改善する方法として低密度ポリエチレンを積層する方法、特開平３−１３１６７７号公報には、耐溶剤性に劣るポリスチレンに対し、特定の溶剤を用いた離型剤層が開示されている。
しかしながら、上記の粘着テープ、粘着ラベルは、高齢者や子供が容易に手で切れるほどの手切れ性は有していない。またカット時の直進性の改良に必要な技術的開示もないものである。
【０００７】
手切れ性付与に関し、テープの何れかの部位に傷痕を施す特開昭５１−１６３４６号公報、特開平１１−５９５６号公報では、傷痕によって初期の切れ性は向上するものの、基材フィルムの強度の影響が全くなくなるものではなく、テープの全幅に渡って、高齢者や子供が簡単に手で切れる程の手切れ性に優れた粘着テープではない。また、カット時の直進性も基材フィルムの影響が強く反映されるため、直進性が悪い。
【０００８】
特開平５−５９３３４号公報においても同様である。
特開昭５１−３４２７１号公報には、特定の配向性を持たせるよう延伸操作を規定しているが、延伸操作だけでは、充分な手切れ性は得られていない。
特開平５−２８７２４３号公報には、積層フィルムが提案されているが、二軸延伸フィルムの強度の影響を受け、手切れ性が不充分である。
特開平５−１３２０７２号公報は、テープを容器等に貼った後、剥がしやすいようにしたものであり、易開封用テープとして有用なものであるが、テープ自身の幅が狭いために、粘着力を維持するために粘着部分がある程度必要であり、剥がせる部分（粘着剤がない部分）が少なく、高齢者等には扱いにくいものであった。
【０００９】
ポリスチレンを基材とする粘着テープは、手切れ性が比較的良好であるが、脆い欠点を有し、特開昭５８−１８９２８２号公報で開示されるように低密度ポリエチレンを積層する方法が開示されているが、手切れ性を悪化させてしまう問題がある。同様に、特開平３−１３１６７７号公報には、特定の溶剤を用いて、脆さを改善する方法が開示されおり、脆さは改善されるが、手切れ性が向上するわけではない。
このように、従来のテープ類は、高齢者や子供が簡単に手で切れる程の手切れ性を有すものはなく、かつ直進カット性も付与されている粘着テープ類を供給することは非常に難しいのが現状である。
【００１０】
【特許文献１】
特開昭５１−１６３４６号公報
【特許文献２】
特開平１１−５９５６号公報
【特許文献３】
特開平５−５９３３４号公報
【特許文献４】
特開昭５１−３４２７１号公報
【特許文献５】
特開平５−２８７２４３号公報
【特許文献６】
特開平５−１３２０７２号公報
【特許文献７】
特開昭５８−１８９２８２号公報
【特許文献８】
特開平３−１３１６７７号公報
【００１１】
【発明が解決しようとする課題】
テープの手切れ性、手切れ時の直進カット性またはラベルのラベラーによるカット時の直進カット性を付与し、特に袋、容器、ケース、食品等の密封、封緘、固定や結束に好適な性能を有する二軸延伸ポリスチレン系樹脂粘着テープまたは粘着ラベルを提供することを目的とする。
【００１２】
【課題を解決するための手段】
本発明者等は、前記課題を解決するため、紫外線照射について鋭意研究した結果、基材フィルムに所定量の紫外線を照射することで、縦方向の延伸配向性が維持でき、同時に縦方向の引張破断伸度を最小限にすることができることを見出し、本発明を完成するに至った。
すなわち、縦方向の延伸配向性が維持されることから、ディスペンサー等で粘着テープを引き出す時に破断する問題がなく、同時に縦方向の引張破断伸度を小さくできることから、横方向に簡単に手で切れるよになり、かつカット時の直進性が改善されることを見出したのである。
好ましくは、基材である二軸延伸ポリスチレン系樹脂フィルムに、紫外線照射の積算光量が３００〜５０００ｍＪ／ｃｍ^２となるように照射することで、縦方向の延伸配向性が維持でき、かつ縦方向の引張破断伸度を小さくできることを見出したものである。
【００１３】
すなわち本発明は、下記の通りである。
（１）二軸延伸ポリスチレン系樹脂からなる基材フィルムの少なくとも片面に粘着剤層を設けた粘着テープまたは粘着ラベルであって、該粘着テープまたは粘着ラベルの横方向の剪断荷重が０．５〜４．５Ｎ、縦方向の引張破断伸度が２．０〜８．５％、縦方向の１１０℃における熱収縮応力が０．７ＭＰａ以上であり、且つ縦と横方向の該熱収縮応力比が１．０〜４．０であることを特徴とする二軸延伸ポリスチレン系樹脂粘着テープまたは粘着ラベル。
【００１４】
（２）基材フィルムが、積算光量が３００〜５０００ｍＪ／ｃｍ^２の紫外線照射を施していることを特徴とする請求項１記載の二軸延伸ポリスチレン系樹脂粘着テープまたは粘着ラベル。
本発明の上記の構成によれば、粘着テープを容易に手で切ることやラベルを被接着物に貼るラベラーでの直進カット性に優れる。また、袋、容器の密封、封緘、固定用テープ、食品の結束用テープとした場合は、袋や容器を開ける際に、食品の束を解す際に、テープを引き剥がすことなく、テープを手で切断し開封することが可能になる。
【００１５】
【発明の実施の形態】
以下、本発明について、特にその好ましい態様を中心に、詳細に説明する。
本発明のポリスチレン系樹脂粘着テープまたは粘着ラベルの基材となる二軸延伸ポリスチレン系樹脂フィルム（粘着加工等の加工前のフィルム）は、下記の如く選定できる。
基材フィルムとしては、縦方向の１１０℃における熱収縮応力（以下「ＯＲＳ」と記す）が０．９ＭＰａ以上であり、縦方向の引張破断伸度が、２．５％以上である基材フィルムが望ましい。
【００１６】
本発明における紫外線照射の好ましい処理条件は、基材となるフィルムのＯＲＳ及び縦方向の引張破断伸度で決定される。紫外線照射の積算光量は、好ましくは３００〜５０００ｍＪ／ｃｍ^２、より好ましくは４００ｍＪ／ｃｍ^２〜４０００ｍＪ／ｃｍ^２、さらに好ましくは、５００〜３０００ｍＪ／ｃｍ^２である。積算光量が５０００ｍＪ／ｃｍ^２を超えると、縦方向の延伸配向性が維持できない場合がある。また、複数回に渡って紫外線を照射する場合においても、積算光量の合計が５０００ｍＪ／ｃｍ^２を超えると、同様に縦方向の延伸配向性が維持できない場合がある。
【００１７】
一回の紫外線照射における積算光量は、３０００ｍＪ／ｃｍ^２以下であることが望ましい。これは、紫外線の光源による発熱が大きく、二軸延伸ポリスチレン系樹脂フィルムが収縮しやすくなるためである。
積算光量が３００ｍＪ／ｃｍ^２未満では、縦方向の引張破断伸度が低下しにくい。
例えば、引張破断伸度が大きな基材フィルムにあっては、積算光量を高くして、本発明で開示する粘着テープ、ラベルとしての縦方向の引張破断伸度を２．０〜８．５％にする照射条件を選定する。
【００１８】
逆に、引張破断伸度の小さな基材フィルムに対しては、積算光量を小さくすることで、本発明で開示する粘着テープ、ラベルが得られる。
なお、粘着剤の種類や塗工量によって、縦方向の引張破断伸度が変化する場合があるので、粘着テープ、粘着ラベルとして、引張破断伸度が２．０〜８．５％になるように、積算光量を調整する必要がある。
また、紫外線照射処理を施さないで、本発明で開示するような粘着テープ、ラベルが得られる二軸延伸ポリスチレン系樹脂フィルムは、得られにくい。
【００１９】
これは、ポリスチレン系樹脂が非結晶性樹脂であることから、フィルム化には延伸操作が不可欠であり、この延伸操作等の工程中で破断等の問題が発生しないためには、好ましくはＯＲＳが０．９ＭＰａ以上であり、同様に粘着加工等の二次加工に際しても、０．７ＭＰａ以上が好ましい。このように二次加工できる二軸延伸ポリスチレン系樹脂フィルムは、より高い配向性を有することが好ましく、縦方向の引張破断伸度も９％以上が好ましい。
【００２０】
一方で、ポリスチレン樹脂にスチレン−ブタジエンの共重合体ゴム成分をゴム成分として、０．５ｗｔ％〜１５ｗｔ％含有した二軸延伸ポリスチレン系樹脂フィルムがあり、これは、該ゴム成分の含有により、低延伸配向性であって、ＯＲＳが０．７ＭＰａ未満で二次加工適性の悪いフィルムであり、粘着テープ、ラベル用基材フィルムとしては適さない。
本発明でＯＲＳを規定している理由は、ゴム成分を含有した基材フィルムと含有しない基材フィルムの引張弾性率に大差はないが、ＯＲＳで比較すると差があり、基材フィルムの延伸配向性を評価し、かつ加工適性を判断する上で重要な指標であることから採用したものである。
【００２１】
本発明に好適に採用できる基材フィルムとしては、旭化成株式会社製のＯＰＳ（登録商標）フィルムＧＭグレード、ＤｏｗＣｈｅｍｉｃａｌ社製のＴＲＹＣＩＴＥ（商品名）グレード等が挙げられる。
本発明における粘着テープ、ラベルの横方向の剪断荷重は、０．５〜４．５Ｎである。好ましくは、０．７〜４．０Ｎである。剪断荷重が０．５Ｎ未満では、横方向に裂けやすくなり、例えば、長ねぎを複数本結束して輸送した場合に、輸送途中でテープが破断してしまうなどの問題が発生する。
【００２２】
横方向の剪断荷重が４．５Ｎを超えると、高齢者や子供が手でテープを切れなくなる。
縦方向の引張破断伸度は、２．０％〜８．５％である。好ましくは、２．５％〜７．０％である。２．０％未満では、テープ加工中に裂ける問題が発生し、８．５％を超えると直進カット性に劣る。
縦方向の１１０℃における熱収縮応力は、０．７ＭＰａ以上、好ましくは０．９ＭＰａ以上である。ＯＲＳが０．７ＭＰａ未満では、テープ加工中に破断するか裂ける問題が発生する。
【００２３】
また、該ＯＲＳの縦横比（縦方向のＯＲＳ／横方向のＯＲＳ）は、１．０〜４．０、好ましくは１．０〜３．５である。縦横比が１．０未満及び４．０を超えると、テープを幅方向に手で切った時、幅方向の途中から斜めにカットされ、幅方向の直進カット性が劣る。
また、縦方向のＯＲＳが０．７ＭＰａ未満で、ＯＲＳの縦横比が、１．０〜４．０の場合でも直進カット性が悪い。これは、縦方向の延伸配向性が高く維持されていないと、幅方向への直線的亀裂伝播性が低下すると考えられる。すなわち、延伸配向により分子鎖が縦方向に整列し、幅方向に手で切り始めたときに発生した亀裂は、縦方向に配列した分子鎖末端を横切って亀裂が幅方向に直線的に伝播するものと推定される。
【００２４】
次に本発明の好ましい製造方法について、以下に記載する。
本発明の二軸延伸ポリスチレン系樹脂粘着テープまたは粘着ラベルの基材となる二軸延伸ポリスチレンフィルムは、前述の如く、旭化成株式会社等から入手できる。
また、本発明の粘着テープ、粘着ラベルの基材となるフィルムは、少なくとも片面コロナ処理が施されていることが好ましい。コロナ処理レベルは、フィルムのブロッキングを防ぐ観点よりフィルムの表面張力が６０ｍＮ／ｍ未満が好ましく、より好ましくは５５ｍＮ／ｍ未満、さらに好ましくは５０ｍＮ／ｍ未満である。下限は粘着剤、離型剤、印刷インキ等の塗布膜の均一性とフィルムとの密着強度向上の観点より、４０ｍＮ／ｍ以上が好ましい。
【００２５】
基材フィルムの厚さは、テープ、ラベルとして必要な強度を確保するため５μｍ以上が好ましく、手切れ性、直進カット性の観点より１００μｍ以下が好ましい。より好ましくは、１５〜７５μｍ、さらに好ましくは、２５〜６０μｍである。
本発明の二軸延伸ポリスチレン系樹脂粘着テープまたは粘着ラベルは、基材フィルムに紫外線の照射を行うことが好ましい。紫外線照射は、粘着剤塗工前等の基材フィルムに照射しても良く、粘着剤塗工等の加工中、加工後、若しくはスリット中に照射しても良い。紫外線照射は公知の装置・方法、例えば、光源として高圧水銀ランプ、若しくはメタルハライドランプを用いて照射し、３６５ｎｍの紫外線における積算光量が３００〜５０００ｍＪ／ｃｍ^２になるように紫外線ランプの出力や基材フィルムの速度を選定することが好ましい。照射は複数回に分けて実施することも可能である。
【００２６】
下述の如く、紫外線照射型の離型剤やインキ等を用いた場合においては、離型剤やインキ等の硬化に要した積算光量も、本発明で開示する合計積算光量に含まれる。例えば、紫外線照射型の２色印刷を施す場合に、１色当たり１２０ｍＪ／ｃｍ^２の積算光量で硬化した場合には、合計２４０ｍＪ／ｃｍ^２となり、本発明で開示する粘着テープ、粘着ラベルを得るには、少なくとも６０ｍＪ／ｃｍ^２の積算光量を前もって照射しておくか、後工程で照射することが好ましい。
【００２７】
本発明で開示するように、紫外線照射により、二軸延伸ポリスチレン系樹脂フィルムは、縦方向のＯＲＳがほぼ維持され、縦方向の引張破断伸度が大幅に低下し、手切れ性、直進カット性に優れる粘着テープ・ラベルが得られる。
本発明の二軸延伸ポリスチレン系樹脂粘着テープまたは粘着ラベルは、基材フィルムの少なくとも片面に公知の方法で粘着加工したものである。またテープとして使用する場合は、片面に粘着加工し、その反対面に離型剤加工したものが好ましい。更に、任意の面に印刷を行ったものでも良い。
【００２８】
テープの製造方法の好ましい一例は、上述の基材フィルムを必要により少なくとも片面をコロナ処理し、ダイレクトグラビアコーター、オフセットグラビアコーター、エアーナイフコーター、バーコーター等の方法でコロナ処理面に離型剤を塗布した後、反対面にグラビア印刷機、凸版印刷機、フレキソ印刷機、スクリーン印刷機等で任意のデザインを印刷した後粘着剤を塗布する方法である。また必要によっては印刷前にコロナ処理を施したり、アンカーコート剤を塗布しても良い。アンカーコート剤は離型剤と同様、公知のコーターで塗布することができる。印刷は行わなくても良く、用途によっては離型剤を塗布しなくても良い。
【００２９】
他のテープ製造方法の一例は、上述の基材フィルムを必要により少なくとも片面をコロナ処理（より好ましくは両面コロナ処理）し、フィルムの片面に粘着剤をセパレーターより転写させ貼付、タック紙を作成した後、反対面をグラビア印刷機、凸版印刷機、フレキソ印刷、スクリーン印刷機等で任意のデザインを印刷した後、ダイレクトグラビアコーター、オフセットグラビアコーター、エアーナイフコーター、バーコーター等の方法で離型剤を塗布する方法である。また必要によっては印刷前にコロナ処理を施したり、アンカーコート剤を塗布しても良い。
【００３０】
また、ラベルの製造方法の一例は、上述の基材フィルムを必要により少なくとも片面をコロナ処理（より好ましくは両面コロナ処理）し、フィルムの片面に粘着剤をセパレーターより転写させながらタック紙を作成し巻き取った後、粘着剤の反対面に任意のデザインをグラビア印刷機、凸版印刷機、フレキソ印刷機、スクリーン印刷機等で印刷、型抜き機により任意の形状にフィルムを型抜きし、ラベルを製造する方法である。また必要によっては印刷前にコロナ処理を施したり、アンカーコート剤を塗布しても良い。
【００３１】
この他、本発明のテープ、ラベルの加工方法に制限はなく、上記以外の公知の方法で行うことも可能である。
本発明の二軸延伸ポリスチレン系樹脂粘着テープまたは粘着ラベルにおいて、粘着剤は、粘着剤主ポリマーと粘着付与剤および架橋剤等の添加剤等からなる公知のもので、ホットメルト系粘着剤、エマルジョン型の粘着剤、紫外線重合型粘着剤、溶剤系粘着剤など従来から使用されている粘着剤を使用できるが、環境対策の観点より、好ましくはホットメルト系粘着剤、エマルジョン型の粘着剤、紫外線照射型粘着剤などである。
【００３２】
同様に離型剤についても公知の離型剤が使用可能であり、一般の離型剤としてはシリコーン樹脂が好ましい。シリコーン樹脂としては、熱、紫外線、電子線等による硬化反応型シリコーン樹脂が好ましく、より好ましくは紫外線硬化反応型シリコーン樹脂である。シリコーン樹脂は溶剤型、エマルジョン型、無溶剤型いずれも使用可能であるが、環境適性を考慮した場合、エマルジョン型や無溶剤型が好ましい。
【００３３】
印刷インキも同様に印刷方法にあわせて公知のインキを使用することができる。この場合、石油系の有機溶剤を使用していないもの（水溶性インキ、大豆インキ等）を選定するのが好ましい。
以下、本発明の二軸延伸ポリスチレン系樹脂粘着テープまたは粘着ラベルについて、実施例に基づいて具体的に説明する。
なお、各物性値及び評価は、下記の測定方法及び評価方法で行った。
【００３４】
（１）剪断荷重
図１および図２に示すように、２ｍｍ間隔で平行に置いた旭化成株式会社製ＯＰＳシート（登録商標）グレード＃７７００（巾１５ｍｍ、厚み０．１３ｍｍ）に対し、その直行方向に剪断荷重を測定する粘着テープまたは粘着ラベル（巾１５ｍｍ）を貼付ける。更にその上に、ＯＰＳシート（登録商標）と平行方向にセロハンテープを貼付け、凹型状の剪断荷重測定用サンプルを得る。剪断荷重測定時のサンプルの状態を図３に示す。剪断荷重の測定は、図１において左右にあるＯＰＳシート（登録商標）の上部分を、それぞれインストロン型引張試験機の上下チャック部分にはさみ込みんだ後、３００ｍｍ／ｍｉｎの速度で引張試験することにより行ない、粘着テープまたはラベルが破断した際の最大荷重を剪断荷重として求めた。
【００３５】
（２）縦方向の引張破断伸度
ＡＳＴＭＤ−８８２に準拠して測定した。
（３）１１０℃における熱収縮応力及び応力比
ＡＳＴＭＤ−１５０４に準拠して測定した（１１０℃のシリコーン油中でのピーク応力）。
【００３６】
（４）紫外線照射及び積算光量
アイグラフィック株式会社製型式ＵＳ０５−０３００１（商品名）を用いて紫外線照射を行った。紫外線照射の光源は、出力１２０Ｗ／ｃｍのメタルハライドランプを用いた。
積算光量は、同社製の積算光量測定装置型式ＵＶＰＦ−３６（商品名）を用いて測定した。
波長が３６５ｎｍである紫外線の積算光量は、コンベアー速度により調整した。例えば、１０００ｍＪ／ｃｍ^２の積算光量は、コンベアー速度を０．７ｍ／ｍｉｎとして、紫外線照射した。また、コンベアー速度が５ｍ／ｍｉｎの時は１４０ｍＪ／ｃｍ^２であった。
【００３７】
（５）手切れ性
５歳の男児５人、女児５人の計１０人のモニターにより、１５ｍｍ幅のテープを任意の長さ引き出し、容易に手で切れるかどうかを１０回づつ行った。結果を以下の基準で評価した。○以上が合格レベルである。
◎：全てのモニターが８回以上容易に手で切ることができる。
○：８回以上容易に手で切ることができるモニターは８人以下、且つ残りのモニターは６回以上容易に手で切れことができる。
△：３人以上のモニターは６回以上容易に手で切ることができるが、４回以下しか容易に引裂くことができないモニターが１人以上いる。
×：５回以上容易に引裂くことができたモニターが４人以下である。
【００３８】
（６）手切れ直進性
手切れ性試験において容易に手切れできたテープの切断辺の平均長さを測定し、以下の基準で評価した。
◎：切断辺長さ／テープ巾が、１．２以下
○：切断辺長さ／テープ巾が、１．２より大きく１．３未満
△：切断辺長さ／テープ巾が、１．３以上１．４未満
×：切断辺長さ／テープ巾が、１．４以上
【００３９】
【実施例１】
旭化成株式会社製ＯＰＳ（登録商標）フィルムＧＭグレードの片面コロナ処理済み（４５ｍＮ／ｍ）、フィルム厚み４０μｍを基材フィルムとして選択した。このフィルムの物性は、表１に記載した。
この基材フィルムをＡ４版にカットし、４ｍｍ厚のＡ４版のアクリル板に基材フィルムをテープで四隅を固定し、前述の装置を用いて、積算光量が１０００ｍＪ／ｃｍ^２になるようコンベアー速度を調整して紫外線照射を行った。
紫外線照射後の物性を表１に記載した。
基材フィルムのコロナ処理面に離型剤としてＥ．Ｉ．Ｄｕｐｏｎｔ社製ＱＵＩＬＯＮ（商品名）のシリコーンアルコール溶液をメイヤバーで塗布、乾燥し、反対面にホットメルト粘着剤をＴダイを用いて、Ａ４版サンプル上に流延し、平均２５μｍの厚みで塗布しテープ原反を作成した後、６０ｍｍ幅に切りテープを得た。
テープの評価結果を表１に記載した。
【００４０】
【実施例２〜３及び比較例１〜２】
積算光量を変えた以外は実施例１と同様に実施し、結果を表１に示した。
ここで、比較例１のテープは、手切れ性が悪いため、手切れ直進性の評価はできなかった。また、比較例２のテープは非常に脆く、剪断荷重の測定ができず、且つテープとしての手切れ性及び直進カット性の評価ができなかった。
【００４１】
【実施例４】
基材フィルムとして、２５μｍ厚のＧＭグレードを用いた以外は、実施例１と同様に実施した。
【００４２】
【比較例３】
基材フィルムとして、大石産業株式会社製ＧＬグレードフィルム厚み２５μｍを用い、片面のコロナ処理を行い４５ｍＮ／ｍの表面張力としたのち、実施例１と同様に実施し、結果を表１に記載した。
直進カット性が悪く、ラベラーでの切断には不適なものであった。
なお、該基材フィルムは、ゴム成分を５．１ｗｔ％含有していた。
【００４３】
【表１】

【００４４】
【発明の効果】
本発明の二軸延伸ポリスチレン系樹脂粘着テープまたは粘着ラベルは、縦方向性の延伸配向性に優れ、ディスペンサーによるテープ引出し時の破断がなく使用できる。手切れ性に優れることから、高齢者や子供でも容易にカットでき、特に、袋、容器、ケース、食品等の表示用や密封、固定、封緘、結束や文具等に好適に使用される手切れ性や直進カット性に優れる粘着テープ及び粘着ラベルを得ることができる。
【図面の簡単な説明】
【図１】剪断荷重測定用サンプルを示す上面模式図。
【図２】剪断荷重測定用サンプルを示す断面模式図。
【図３】剪断荷重測定前の測定用サンプルの状態を示す斜視模式図。
【符号の説明】
１ＯＰＳシート（登録商標）旭化成株式会社製グレード＃７７００
２ＯＰＳシート（登録商標）旭化成株式会社製グレード＃７７００
３セロハンテープ日東電工包装システム株式会社製（１５ｍｍ巾）
４粘着テープまたは粘着ラベルのサンプル（１５ｍｍ巾）[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a polystyrene resin pressure-sensitive adhesive tape or label using a biaxially stretched film made of a polystyrene resin as a base material. More specifically, the present invention relates to an adhesive tape or an adhesive label having excellent hand-cutting properties and excellent straightness at the time of cutting, which are suitably used for displaying, sealing, fixing, sealing, bundling and stationery of bags, containers, foods and the like.
[0002]
[Prior art]
2. Description of the Related Art Plastic tapes and labels have been conventionally used for design indications of bags, containers, cases, foods, etc., and for sealing. Plastics such as polyethylene terephthalate, polypropylene, polyethylene, and polystyrene are frequently used for these bags, containers, cases, and the like, and tapes and labels are also made of polyethylene terephthalate, polypropylene, polyvinyl chloride, cellophane, polystyrene, and the like. Is generally known. Among the tapes made of these materials, tapes made of polyethylene terephthalate, polypropylene, polyvinyl chloride, and cellophane have poor hand-cutting properties, so mixing and embossing of inorganic particles, scratching the tape, devising a stretching method, etc. Improving hand-cutting properties by a method is also being considered.
[0003]
By the way, in recent years, with the aging society, tapes with better hand-cutting properties have been demanded, and from the viewpoint of product safety, tapes that can be easily cut by children and elderly people without using a blade have been demanded.
Further, there is a need for an adhesive tape and a label that allow a bag or a container to be more easily opened.
In particular, as a simple bag sealing method, using a bag sealer tape, the salad is packed in a transparent container in a bag sealed with a bag sealer or in a backyard such as a supermarket, and the main body and lid of the container are sealed with adhesive tape. The use of pressure-sensitive adhesive tapes has been increasing, such as fastening, seasonings to lids with pressure-sensitive adhesive tapes, and binding foods such as green onions with pressure-sensitive adhesive tapes.
[0004]
These tapes are often made of polyethylene terephthalate, polypropylene, or cellophane from the viewpoint of strength.
These tapes have poor hand-cutting properties, and regarding the provision of hand-cutting properties, JP-A-51-16346 discloses a tape provided with a cut such as a side edge or an edge and a scar such as a tear. Japanese Patent Application Laid-Open No. H11-5956 discloses a tape provided with a scar on the inside away from the edge, and Japanese Patent Application Laid-Open No. H5-59334 discloses a tape having a tear start point at both ends. I have.
[0005]
Furthermore, Japanese Patent Application Laid-Open No. S51-34271 proposes a film having improved lateral tearability due to a specific orientation.
JP-A-5-287243 discloses a tape which can be cut by pressing with a nail by providing an adhesive layer on a laminated film of a non-stretched synthetic resin film and a biaxially stretched synthetic resin film.
Further, in order to make the pressure-sensitive adhesive tape easier to peel off, Japanese Patent Application Laid-Open No. H5-132072 discloses a tape in which a pressure-sensitive adhesive is not applied to the entire surface of a substrate.
[0006]
With respect to pressure-sensitive adhesive tapes and labels using a polystyrene resin film as a base material, as disclosed in JP-A-58-189282, as a method for improving brittleness, a method of laminating low-density polyethylene, JP 131677 discloses a release agent layer using a specific solvent for polystyrene having poor solvent resistance.
However, the above-mentioned pressure-sensitive adhesive tapes and pressure-sensitive adhesive labels do not have such hand-cutting properties that elderly people and children can easily cut by hand. Further, there is no technical disclosure necessary for improving the straightness at the time of cutting.
[0007]
Japanese Patent Application Laid-Open Nos. 51-16346 and 11-5956, in which a scratch is applied to any part of the tape with respect to the hand-cutting property, the initial cutting property is improved by the scar, but the strength of the base film is improved. Is not completely eliminated, and the adhesive tape is not so easy to cut by the hand that the elderly and children can easily cut it over the entire width of the tape. In addition, the straightness at the time of cutting is also strongly reflected by the influence of the base film, so that the straightness is poor.
[0008]
The same applies to JP-A-5-59334.
Japanese Patent Application Laid-Open No. 51-34271 specifies a stretching operation so as to have a specific orientation, but sufficient hand-cutting properties cannot be obtained only by the stretching operation.
Japanese Patent Application Laid-Open No. Hei 5-287243 proposes a laminated film, but the hand-cutting property is insufficient due to the influence of the strength of the biaxially stretched film.
Japanese Patent Application Laid-Open No. Hei 5-132207 discloses a tape that is easily peeled off after being attached to a container or the like, and is useful as an easy-opening tape. In order to maintain the adhesiveness, a certain amount of adhesive part is necessary, and there are few parts that can be peeled off (parts without adhesive), making it difficult for elderly people to handle.
[0009]
Adhesive tapes based on polystyrene have relatively good hand-cutting properties, but have brittle defects, and a method of laminating low-density polyethylene as disclosed in JP-A-58-189282 is disclosed. However, there is a problem that the hand cutting property is deteriorated. Similarly, Japanese Patent Application Laid-Open No. 3-131677 discloses a method for improving brittleness by using a specific solvent, and the brittleness is improved, but the hand-cutting property is not improved.
As described above, none of the conventional tapes has such a sharpness that the elderly or children can easily cut it by hand, and it is very difficult to supply adhesive tapes that have a straight cut property. It is difficult at present.
[0010]
[Patent Document 1]
JP-A-51-16346 [Patent Document 2]
Japanese Patent Application Laid-Open No. 11-5956 [Patent Document 3]
JP-A-5-59334 [Patent Document 4]
JP-A-51-34271 [Patent Document 5]
JP-A-5-287243 [Patent Document 6]
JP-A-5-132072 [Patent Document 7]
JP-A-58-189282 [Patent Document 8]
JP-A-3-131677
[Problems to be solved by the invention]
The tape has the ability to be cut by hand, cut straight by hand when cut, or cut straight by label labeler.Especially suitable for sealing, sealing, fixing and bundling bags, containers, cases, foods, etc. It is an object of the present invention to provide a biaxially stretched polystyrene resin adhesive tape or adhesive label having the same.
[0012]
[Means for Solving the Problems]
The present inventors have conducted intensive studies on ultraviolet irradiation in order to solve the above-mentioned problems, and as a result, by irradiating a predetermined amount of ultraviolet rays to the base film, the longitudinal stretching orientation can be maintained, and at the same time, the longitudinal tensile strength can be maintained. They have found that the elongation at break can be minimized, and have completed the present invention.
That is, since the stretching orientation in the longitudinal direction is maintained, there is no problem of breaking when the adhesive tape is pulled out with a dispenser or the like, and at the same time, the tensile elongation at break in the longitudinal direction can be reduced, so that it can be easily cut by hand in the transverse direction. It has been found that it has improved and the straightness at the time of cutting has been improved.
Preferably, the biaxially stretched polystyrene resin film as the base material is irradiated so that the integrated amount of ultraviolet irradiation is 300 to 5000 mJ / cm ² , whereby the stretch orientation in the longitudinal direction can be maintained and the longitudinal direction can be maintained. It has been found that the tensile elongation at break can be reduced.
[0013]
That is, the present invention is as follows.
(1) An adhesive tape or an adhesive label provided with an adhesive layer on at least one surface of a base film made of a biaxially stretched polystyrene-based resin, wherein the adhesive tape or the adhesive label has a lateral shear load of 0.5 to 0.5. 4.5N, the tensile elongation at break in the longitudinal direction is 2.0 to 8.5%, the heat shrinkage stress at 110 ° C. in the longitudinal direction is 0.7 MPa or more, and the heat shrinkage stress ratio in the longitudinal and transverse directions is A biaxially oriented polystyrene-based resin adhesive tape or adhesive label, which has a molecular weight of 1.0 to 4.0.
[0014]
(2) base film, biaxially oriented polystyrene resin pressure-sensitive adhesive tape or adhesive label according to claim 1, wherein the integrated light quantity, characterized in that it subjected to ultraviolet irradiation 300~5000mJ / cm ^2.
ADVANTAGE OF THE INVENTION According to the said structure of this invention, it is easy to cut an adhesive tape by hand easily, and it is excellent in the straight cutting property in the labeler which sticks a label to an adherend. In the case of tapes for sealing, sealing and fixing bags and containers, and tapes for bundling food, when unpacking the bags when opening the bag or container, remove the tape by hand without peeling off the tape. Can be cut and opened.
[0015]
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, the present invention will be described in detail with particular emphasis on preferred embodiments.
The biaxially stretched polystyrene resin film (the film before processing such as adhesive processing) serving as the base material of the polystyrene resin pressure-sensitive adhesive tape or pressure-sensitive adhesive label of the present invention can be selected as follows.
As the base film, a base film having a longitudinal heat shrinkage stress at 110 ° C. (hereinafter referred to as “ORS”) of 0.9 MPa or more and a tensile elongation at break of 2.5% or more in the longitudinal direction. Is desirable.
[0016]
The preferable treatment conditions of the ultraviolet irradiation in the present invention are determined by the ORS of the film as the base material and the tensile elongation at break in the longitudinal direction. Integrated light quantity of ultraviolet irradiation is preferably 300~5000mJ / cm ^2, more preferably ^{^{400mJ / cm 2 ~4000mJ / cm 2}} , more preferably a 500~3000mJ / cm ^2. When the cumulative light amount exceeds 5000 mJ / cm ² , the stretch orientation in the longitudinal direction may not be maintained. In addition, even in the case of irradiating ultraviolet rays a plurality of times, if the total integrated light amount exceeds 5000 mJ / cm ² , similarly, the stretch orientation in the longitudinal direction may not be maintained.
[0017]
It is desirable that the integrated light quantity in one ultraviolet irradiation is 3000 mJ / cm ² or less. This is because the heat generated by the ultraviolet light source is large, and the biaxially stretched polystyrene resin film tends to shrink.
If the integrated light quantity is less than 300 mJ / cm ² , the tensile elongation at break in the longitudinal direction is unlikely to decrease.
For example, in the case of a base film having a large tensile breaking elongation, the integrated light amount is increased so that the longitudinal elongation at break in the longitudinal direction as an adhesive tape or label disclosed in the present invention is 2.0 to 8.5%. Select the irradiation conditions for
[0018]
Conversely, for a base film having a small tensile elongation at break, the pressure-sensitive adhesive tape or label disclosed in the present invention can be obtained by reducing the integrated light amount.
In addition, since the tensile elongation at break in the longitudinal direction may change depending on the type of the adhesive and the amount of coating, the elongation at break may be 2.0 to 8.5% as an adhesive tape or an adhesive label. In addition, it is necessary to adjust the integrated light quantity.
Further, it is difficult to obtain a biaxially stretched polystyrene-based resin film from which an adhesive tape and a label as disclosed in the present invention can be obtained without performing an ultraviolet irradiation treatment.
[0019]
This is because a polystyrene-based resin is an amorphous resin, a stretching operation is indispensable for forming a film, and in order to prevent a problem such as breakage during the stretching operation or the like, preferably ORS is used. The pressure is 0.9 MPa or more, and is also preferably 0.7 MPa or more also in secondary processing such as adhesive processing. The biaxially stretched polystyrene-based resin film that can be subjected to secondary processing as described above preferably has higher orientation, and the tensile elongation at break in the longitudinal direction is preferably 9% or more.
[0020]
On the other hand, there is a biaxially stretched polystyrene-based resin film containing 0.5% to 15% by weight of a polystyrene resin containing a styrene-butadiene copolymer rubber component as a rubber component. The film is stretch-oriented and has an ORS of less than 0.7 MPa and is not suitable for secondary processing, and is not suitable as an adhesive tape or a base film for labels.
The reason for defining the ORS in the present invention is that there is no significant difference in the tensile modulus between the base film containing the rubber component and the base film not containing the rubber component, but there is a difference when compared with the ORS, and the stretching orientation of the base film is different. It is adopted because it is an important index in evaluating the formability and determining the suitability for processing.
[0021]
Examples of the base film that can be suitably used in the present invention include OPS (registered trademark) film GM grade manufactured by Asahi Kasei Corporation and TRYCITE (trade name) grade manufactured by Dow Chemical Company.
The lateral shear load of the pressure-sensitive adhesive tape or label in the present invention is 0.5 to 4.5 N. Preferably, it is 0.7 to 4.0N. If the shearing load is less than 0.5 N, it tends to tear in the lateral direction. For example, when a plurality of onions are bound and transported, a problem such as breakage of the tape during transport occurs.
[0022]
When the lateral shear load exceeds 4.5N, the elderly and children cannot cut the tape by hand.
The tensile elongation at break in the machine direction is 2.0% to 8.5%. Preferably, it is 2.5% to 7.0%. If it is less than 2.0%, a problem of tearing during tape processing occurs, and if it exceeds 8.5%, the straight cutting property is poor.
The heat shrinkage stress at 110 ° C. in the longitudinal direction is 0.7 MPa or more, preferably 0.9 MPa or more. If the ORS is less than 0.7 MPa, a problem of breakage or tearing during tape processing occurs.
[0023]
The aspect ratio (ORS in the vertical direction / ORS in the horizontal direction) of the ORS is 1.0 to 4.0, preferably 1.0 to 3.5. When the aspect ratio is less than 1.0 and exceeds 4.0, when the tape is cut in the width direction by hand, the tape is cut obliquely from the middle in the width direction, and the straight-line cutability in the width direction is inferior.
Further, even when the ORS in the vertical direction is less than 0.7 MPa and the aspect ratio of the ORS is 1.0 to 4.0, the straight-moving cut property is poor. This is thought to be because the linear crack propagation in the width direction decreases if the stretching orientation in the longitudinal direction is not maintained high. That is, the cracks generated when the molecular chains are aligned in the vertical direction by the stretch orientation and started to be cut by hand in the width direction, the cracks propagate linearly in the width direction across the ends of the molecular chains arranged in the vertical direction. It is presumed that.
[0024]
Next, a preferred production method of the present invention will be described below.
As described above, the biaxially oriented polystyrene film used as the base material of the biaxially oriented polystyrene resin adhesive tape or adhesive label of the present invention can be obtained from Asahi Kasei Corporation or the like.
Moreover, it is preferable that the film used as the base material of the pressure-sensitive adhesive tape and the pressure-sensitive adhesive label of the present invention has been subjected to at least one-sided corona treatment. The corona treatment level is preferably such that the surface tension of the film is less than 60 mN / m, more preferably less than 55 mN / m, and still more preferably less than 50 mN / m from the viewpoint of preventing blocking of the film. The lower limit is preferably 40 mN / m or more from the viewpoint of uniformity of a coating film of a pressure-sensitive adhesive, a release agent, a printing ink, and the like and improvement in adhesion strength to the film.
[0025]
The thickness of the base film is preferably 5 μm or more in order to secure the necessary strength as a tape or label, and is preferably 100 μm or less from the viewpoint of hand cutting and straight cutting. More preferably, it is 15 to 75 μm, further preferably 25 to 60 μm.
In the biaxially oriented polystyrene resin pressure-sensitive adhesive tape or pressure-sensitive adhesive label of the present invention, it is preferable to irradiate the base film with ultraviolet rays. The ultraviolet irradiation may be performed on the base film before the application of the adhesive or the like, or may be performed during, after the processing of the application of the adhesive or in the slit. Ultraviolet irradiation is performed using a known apparatus or method, for example, using a high-pressure mercury lamp or a metal halide lamp as a light source. The output of the ultraviolet lamp or the base material is adjusted so that the integrated amount of light at 365 nm ultraviolet light becomes 300 to 5000 mJ / cm ^2. It is preferred to select the speed of the film. Irradiation can be performed in a plurality of times.
[0026]
As described below, when an ultraviolet irradiation type release agent, ink, or the like is used, the integrated light amount required for curing the release agent, the ink, or the like is also included in the total integrated light amount disclosed in the present invention. For example, when performing ultraviolet irradiation type two-color printing, when curing is performed with an integrated light amount of 120 mJ / cm ² per color, the total amount is 240 mJ / cm ² , and the adhesive tape and the adhesive label disclosed in the present invention are obtained. In this case, it is preferable to irradiate at least an integrated light amount of at least 60 mJ / cm ² in advance, or to irradiate it in a later step.
[0027]
As disclosed in the present invention, the biaxially stretched polystyrene-based resin film is almost maintained in the longitudinal direction by irradiation with ultraviolet light, the tensile elongation at break in the longitudinal direction is greatly reduced, and the hand-cutting property and the straight cutting property are reduced. This gives an adhesive tape / label with excellent properties.
The pressure-sensitive adhesive tape or label of the biaxially oriented polystyrene resin of the present invention is obtained by subjecting at least one surface of a substrate film to pressure-sensitive adhesive processing by a known method. When used as a tape, it is preferable that one surface is subjected to adhesive processing and the other surface is subjected to a release agent processing. Further, an image printed on an arbitrary surface may be used.
[0028]
A preferred example of a method for producing a tape is to perform a corona treatment on at least one surface of the above-described base film as necessary, and apply a release agent to the corona-treated surface by a method such as a direct gravure coater, an offset gravure coater, an air knife coater, or a bar coater. After applying, an arbitrary design is printed on the opposite surface with a gravure printing machine, letterpress printing machine, flexographic printing machine, screen printing machine or the like, and then an adhesive is applied. If necessary, a corona treatment may be performed before printing, or an anchor coating agent may be applied. The anchor coat agent can be applied with a known coater, like the release agent. Printing need not be performed, and a release agent may not be applied depending on the application.
[0029]
An example of another tape manufacturing method is that the above-described base film is subjected to corona treatment (more preferably, double-sided corona treatment) on at least one side as required, and an adhesive is transferred from a separator to one side of the film, and is attached to form a tack paper. After printing any design on the other side with a gravure printing machine, letterpress printing machine, flexographic printing, screen printing machine, etc., release agent by direct gravure coater, offset gravure coater, air knife coater, bar coater etc. Is applied. If necessary, a corona treatment may be performed before printing, or an anchor coating agent may be applied.
[0030]
One example of a label manufacturing method is to form a tack sheet while corona-treating at least one surface of the above-described base film as needed (more preferably, double-sided corona treatment), and transferring an adhesive to one surface of the film from a separator. After winding, print the desired design on the opposite side of the adhesive with a gravure printing machine, letterpress printing machine, flexographic printing machine, screen printing machine, etc. It is a manufacturing method. If necessary, a corona treatment may be performed before printing, or an anchor coating agent may be applied.
[0031]
In addition, the method for processing the tape and label of the present invention is not limited, and the method can be performed by a known method other than the above.
In the biaxially oriented polystyrene resin pressure-sensitive adhesive tape or pressure-sensitive adhesive label of the present invention, the pressure-sensitive adhesive is a known material comprising a pressure-sensitive adhesive main polymer and additives such as a tackifier and a cross-linking agent, and a hot-melt pressure-sensitive adhesive, an emulsion. Pressure-sensitive adhesives, UV-polymerizable pressure-sensitive adhesives, conventionally used pressure-sensitive adhesives such as solvent-based pressure-sensitive adhesives can be used, but from the viewpoint of environmental measures, preferably hot-melt-type pressure-sensitive adhesives, emulsion-type pressure-sensitive adhesives, ultraviolet light Irradiation adhesives and the like.
[0032]
Similarly, a known release agent can be used as the release agent, and a silicone resin is preferable as a general release agent. As the silicone resin, a silicone resin cured by heat, ultraviolet rays, an electron beam or the like is preferable, and a silicone resin cured by ultraviolet rays is more preferable. As the silicone resin, any of a solvent type, an emulsion type and a non-solvent type can be used, but in consideration of environmental suitability, an emulsion type or a solventless type is preferable.
[0033]
As the printing ink, a known ink can be used in accordance with the printing method. In this case, it is preferable to select one that does not use a petroleum organic solvent (such as a water-soluble ink or a soy ink).
Hereinafter, the biaxially oriented polystyrene resin adhesive tape or adhesive label of the present invention will be specifically described based on examples.
In addition, each physical property value and evaluation were performed by the following measurement methods and evaluation methods.
[0034]
(1) Shear load As shown in FIGS. 1 and 2, the direction perpendicular to the OPS sheet (registered trademark) grade # 7700 (15 mm width, 0.13 mm thickness) manufactured by Asahi Kasei Corporation placed in parallel at 2 mm intervals. A pressure-sensitive adhesive tape or a pressure-sensitive label (15 mm in width) for measuring a shear load is attached to the device. Furthermore, a cellophane tape is stuck thereon in a direction parallel to the OPS sheet (registered trademark) to obtain a concave-shaped sample for measuring a shear load. FIG. 3 shows the state of the sample at the time of measuring the shear load. For the measurement of the shear load, the upper portions of the OPS sheet (registered trademark) on the left and right in FIG. 1 are respectively inserted into upper and lower chuck portions of an Instron type tensile tester, and then a tensile test is performed at a speed of 300 mm / min. The maximum load when the pressure-sensitive adhesive tape or label broke was determined as the shear load.
[0035]
(2) Tensile elongation at break in the longitudinal direction was measured in accordance with ASTM D-882.
(3) Heat shrinkage stress at 110 ° C. and stress ratio Measured according to ASTM D-1504 (peak stress in silicone oil at 110 ° C.).
[0036]
(4) Ultraviolet irradiation and integrated light amount Ultraviolet irradiation was performed using Model US05-03001 (trade name) manufactured by Eye Graphic Co., Ltd. As a light source for ultraviolet irradiation, a metal halide lamp having an output of 120 W / cm was used.
The integrated light amount was measured using an integrated light amount measurement device model UVPF-36 (trade name) manufactured by the company.
The integrated amount of ultraviolet light having a wavelength of 365 nm was adjusted by the conveyor speed. For example, with the integrated light quantity of 1000 mJ / cm ² , ultraviolet irradiation was performed at a conveyor speed of 0.7 m / min. When the conveyor speed was 5 m / min, it was 140 mJ / cm ² .
[0037]
(5) Hand-cutting property Using a monitor of 5 boys and 5 girls of 5 years old, a total of 10 monitors pulled out a tape of 15 mm width to an arbitrary length and performed 10 times whether or not it could be easily cut by hand. The results were evaluated according to the following criteria. ○ The above is the pass level.
A: All monitors can be easily cut by hand eight times or more.
：: 8 or less monitors can be easily cut by hand more than 8 times, and the remaining monitors can be cut by hand more than 6 times easily.
B: Three or more monitors can be easily cut by hand six times or more, but one or more monitors can be easily torn only four times or less.
X: The number of monitors that could be easily torn 5 or more times was 4 or less.
[0038]
(6) Hand cutting straightness The average length of the cut side of the tape which could be easily cut in the hand cutting test was measured and evaluated according to the following criteria.
◎: Cut side length / tape width is 1.2 or less ：: Cut side length / tape width is larger than 1.2 and less than 1.3 △: Cut side length / tape width is 1.3 or more Less than 1.4 ×: Cut side length / tape width is 1.4 or more.
Embodiment 1
Asahi Kasei Corporation OPS (registered trademark) film A GM grade single-sided corona treated (45 mN / m) and a film thickness of 40 μm were selected as the base film. The physical properties of this film are shown in Table 1.
The base film is cut into A4 size plates, and the four corners of the base film are fixed to a 4 mm thick A4 size acrylic plate with tape, and the conveyor speed is set to 1000 mJ / cm ² using the above-described apparatus. Was adjusted to perform ultraviolet irradiation.
Table 1 shows the physical properties after ultraviolet irradiation.
E. as a release agent on the corona-treated surface of the substrate film I. A silicone alcohol solution of QUIILON (trade name) manufactured by Dupont Co. was applied with a Mayer bar, dried, and a hot-melt adhesive was cast on the opposite surface using a T-die on an A4 size sample, and applied with an average thickness of 25 μm. After preparing the raw tape, the tape was cut into a width of 60 mm to obtain a tape.
Table 1 shows the evaluation results of the tape.
[0040]
Examples 2-3 and Comparative Examples 1-2
The procedure was performed in the same manner as in Example 1 except that the integrated light amount was changed, and the results are shown in Table 1.
Here, the tape of Comparative Example 1 was poor in hand-cutting property, so that the hand-cut straightness could not be evaluated. Further, the tape of Comparative Example 2 was very brittle, the shear load could not be measured, and the hand-cutting property and straight-cutting property of the tape could not be evaluated.
[0041]
Embodiment 4
The same operation as in Example 1 was performed except that a 25 μm-thick GM grade was used as the base film.
[0042]
[Comparative Example 3]
As a base film, a GL grade film thickness of 25 μm manufactured by Oishi Sangyo Co., Ltd. was used, and a corona treatment was performed on one side to give a surface tension of 45 mN / m. Then, the same operation as in Example 1 was performed. .
The straight cutting property was poor, and was unsuitable for cutting with a labeler.
The base film contained 5.1 wt% of a rubber component.
[0043]
[Table 1]

[0044]
【The invention's effect】
The biaxially stretched polystyrene resin pressure-sensitive adhesive tape or pressure-sensitive adhesive label of the present invention has excellent longitudinal stretch orientation and can be used without breakage when the tape is pulled out by a dispenser. It is easy to cut, even for elderly people and children, because of its excellent hand-cutting properties. The adhesive tape and the adhesive label which are excellent in the property and the straight cutting property can be obtained.
[Brief description of the drawings]
FIG. 1 is a schematic top view showing a sample for measuring a shear load.
FIG. 2 is a schematic cross-sectional view showing a sample for measuring a shear load.
FIG. 3 is a schematic perspective view showing a state of a measurement sample before a shear load measurement.
[Explanation of symbols]
1 OPS sheet (registered trademark) grade # 7700 manufactured by Asahi Kasei Corporation
2 OPS sheet (registered trademark) grade # 7700 manufactured by Asahi Kasei Corporation
3 Cellophane tape manufactured by Nitto Denko Packaging System Co., Ltd. (15mm width)
4 Sample of adhesive tape or label (15mm width)

Claims

An adhesive tape or an adhesive label provided with an adhesive layer on at least one surface of a base film made of a biaxially oriented polystyrene resin, wherein the adhesive tape or the adhesive label has a shear load of 0.5 to 4.5 N in a lateral direction. The tensile elongation at break in the machine direction is 2.0 to 8.5%, the heat shrinkage stress at 110 ° C. in the machine direction is 0.7 MPa or more, and the heat shrinkage stress ratio in the machine direction is 1.0. A biaxially stretched polystyrene resin adhesive tape or adhesive label, wherein

Base film, biaxially oriented polystyrene resin pressure-sensitive adhesive tape or adhesive label according to claim 1, wherein the integrated quantity of light is characterized in that it is subjected to ultraviolet irradiation 300~5000mJ / cm ^2.