JP2004295012A - Photosensitive composition - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a photosensitive composition which is suitable for a lithographic printing original plate having high sensitivity to the oscillation wavelength of an inexpensive short wave semiconductor laser, and which uses a new photoinitiation system having high sensitivity in a wide wavelength region from 350 nm to 450 nm, excellent plate wear and favorable handling property in a bright room. <P>SOLUTION: The photosensitive composition contains: (i) a sensitizing dye expressed by general formula (1), Dye-L-M; (ii) an activator compound which induces a chemical change by the interaction with light absorption of the sensitizing dye to generate at least one species of radicals, acids and bases; and (iii) a compound which irreversibly changes its physical or chemical characteristics by at least one species of the radicals, acids and bases. In formula (1), Dye represents a sensitizing dye skeleton, L a divalent organic group linking Dye and M, and M an acceptor group having a lower reduction potential than the excitation oxidation potential of Dye. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

【００１６】
（Ａは置換基を有しても良い芳香族環またはヘテロ環を表し、Ｘ、Ｙは酸素原子、硫黄原子または−Ｎ（Ｒ_１）−を表す。Ｒ_１、Ｒ_２、Ｒ_３、Ｒ_４、Ｒ_５、Ｒ_６、Ｒ_７、Ｒ_８、Ｒ_９、Ｒ_１０、Ｒ_１１、Ｒ_１２、Ｒ_１３は、それぞれ独立に、水素原子または、一価の非金属原子団であり、ＡとＲ_１、Ｒ_２、Ｒ_３、Ｒ_６、Ｒ_１３は、それぞれ互いに、脂肪族性または芳香族性の環を形成するために結合することができる。但し、Ａ、Ｒ_１、Ｒ_２、Ｒ_３、Ｒ_４、Ｒ_５、Ｒ_６、Ｒ_７、Ｒ_８、Ｒ_９、Ｒ_１０、Ｒ_１１、Ｒ_１２、Ｒ_１３の少なくとも１つは、下記部分構造（５）に示す１価の有機残基を表す。下記部分構造中、Ｌは一般式（２）、一般式（３）または一般式（４）で表される構造とＭを連結する２価の有機基を表し、Ｍはアンモニウム基、ピリジニウム基、スルホニウム基またはホスホニウム基を表す。）
【００１７】
【化４】

【００１８】
本発明の感光性組成物（以下、光重合性組成物とも称する）は、効果を得る上で（ｉ）の一般式（１）で表される増感色素は、一般式（２）で表される増感色素、一般式（３）で表される増感色素及び一般式（４）で表される増感色素から選択される少なくとも１種であることが好ましい。
本発明の感光性組成物を用いる平版印刷版用原版は、４５０ｎｍより短波長のレーザー光源を用いた走査露光に十分な感度を有し、明るいセーフライト下でも取り扱い可能で、かつ耐刷性、汚れ性に優れた平版印刷版を与える。
【００１９】
【発明の実施の形態】
本発明の実施の形態について詳細に説明する。
〔Ａ．光開始系〕
本発明の光開始系は（ｉ）特定構造を有する、一般式（１）で表される増感色素と、（ｉｉ）増感色素の光吸収により生じる電子励起状態との相互作用により化学変化を起こし、ラジカル、酸および塩基のうちの少なくともいずれか１種を生成する活性剤化合物とからなる。
【００２０】
本発明の増感色素（ｉ）の特徴の１つは、３００ｎｍから４５０ｎｍ域に特に優れた吸収特性を有することにある。さらに（ｉ）は、種々の活性剤の分解を効率良く引き起こし、非常に高い感光性を示す。一般に、増感色素／活性剤からなる光開始系の増感機構は▲１▼増感色素の電子励起状態から活性剤への電子移動反応に基づく、活性剤の還元的分解、▲２▼活性剤から増感色素の電子励起状態への電子移動に基づく、活性剤の酸化的分解、▲３▼増感色素の電子励起状態から活性剤へのエネルギー移動に基づく、活性剤の電子励起状態からの分解、といった経路が知られるが、本発明の増感色素は、これら何れのタイプの増感反応をも優れた効率で引き起こすことがわかった。
【００２１】
本発明者らは、高感度を得るためには増感色素が、式（１）で表される増感色素、すなわち増感色素が光吸収した後の励起酸化電位よりも低い還元電位を有するアクセプター基を有する増感色素であることが非常に重要であることを見出した。その作用機構は明らかではないが、増感色素が光吸収により生じる電子励起状態からアクセプターに電子及び／又はエネルギーが移動し、続いてアクセプターから活性剤へ電子及び／又はエネルギーが移動することで活性剤が分解する反応機構をとるため、増感色素と活性剤の２分子反応で生じる活性剤から増感色素への電子及び／又はエネルギーの移動による失活過程が抑制されることが、活性剤分解にいたる後続反応の効率化に有効に作用していることが考えられる。また、本発明の増感色素は高強度の発光（ケイ光および／またはりん光）スペクトルを示すことから、１つの可能性としては、本発明の増感色素は励起寿命が比較的長いことが、活性剤との反応効率化に作用している可能性もある。
【００２２】
（Ａ１）増感色素
本発明に用いられる増感色素は下記一般式（１）で表されるものである。
【００２３】
Ｄｙｅ−Ｌ−Ｍ （１）
【００２４】
（式中Ｄｙｅは、増感色素骨格を表し、ＬはＤｙｅとＭを連結する２価の有機基を表し、ＭはＤｙｅ励起酸化電位よりも低い還元電位を有するアクセプター基を表す。）
【００２５】
一般式（１）について説明する。Ｄｙｅは増感色素骨格を表す。好ましい増感色素骨格は、以下に示す構造が挙げられる。
【００２６】
［増感色素］
本発明の光重合性組成物の１成分となり得る増感色素骨格としては、分光増感色素、光源の光を吸収して光重合開始剤と相互作用する染料あるいは顔料が挙げられる。
好ましい増感色素骨格としては多核芳香族類（例えば、ピレン、ペリレン、トリフェニレン）
キサンテン類（例えば、フルオレッセイン、エオシン、エリスロシン、ローダミンＢ、ローズベンガル
メロシアニン類（例えば、メロシアニン、カルボメロシアニン）
チアジン類（例えば、チオニン、メチレンブルー、トルイジンブルー）
アクリジン類（例えば、アクリジンオレンジ、クロロフラビン、アクリフラビン）
【００２７】
アントラキノン類（例えば、アントラキノン）
スクアリウム類（例えば、スクアリウム）
等が挙げられる。より好ましい分光増感色素又は染料の例としては特公平３７−１３０３４号記載のスチリル系色素、例えば、
【００２８】
【化５】

【００２９】
特開昭６４−５６７６７号記載のアントラキノン類、例えば
【００３０】
【化６】

【００３１】
特開平２−１７１４号記載のベンゾキサンテン染料。特開平２−２２６１４８号及び特開平２−２２６１４９号記載のアクリジン類、例えば、
【００３２】
【化７】

【００３３】
特開平２−６３０５３号記載のベンゾフラン色素、例えば
【００３４】
【化８】

【００３５】
特開平２−８５８５８号、特開平２−２１６１５４号の共役ケトン色素、例えば
【００３６】
【化９】

【００３７】
特開昭５７−１０６０５号記載の色素。特公平２−３０３２１号記載のアゾシンナミリデン誘導体、例えば、
【００３８】
【化１０】

【００３９】
特開昭６２−３１８４４号、特開昭６２−３１８４８号、特開昭６２−１４３０４３号記載のキサンテン系色素、例えば、
【００４０】
【化１１】

【００４１】
特公昭５９−２８３２５号記載のアミノスチリルケトン、例えば
【００４２】
【化１２】

【００４３】
特公昭６１−９６２１号記載の以下の一般式〔６〕〜〔１３〕で表されるメロシアニン色素、例えば、
【００４４】
【化１３】

【００４５】
一般式〔８〕〜〔１３〕において、Ｘ^８は水素原子、アルキル基、置換アルキル基、アルコキシ基、アリール基、置換アリール基、アリールオキシ基、アラルキル基又はハロゲン原子を表わす。一般式〔７〕においてＰｈはフェニル基を表わす。一般式〔６〕〜〔１３〕において、Ｒ^４８、Ｒ^４９およびＲ^５０はそれぞれアルキル基、置換アルキル基、アルケニル基、アリール基、置換アリール基又はアラルキル基を表わし、互いに等しくても異なってもよい。特開平２−１７９６４３号記載の以下の一般式〔１４〕〜〔１６〕で表わされる色素、例えば
【００４６】
【化１４】

【００４７】
Ａ：酸素原子、イオウ原子、セレン原子、テルル原子、アルキル又はアリール置換された窒素原子またはジアルキル置換された炭素原子を表わす。
Ｙ^３：水素原子、アルキル基、置換アルキル基、アリール基、置換アリール基、アラルキル基、アシル基、または置換アルコキシカルボニル基を表わす。
Ｒ^５１、Ｒ^５２：水素原子、炭素数１〜１８のアルキル基、もしくは置換基として、Ｒ^５３Ｏ−、
【００４８】
【化１５】

【００４９】
−（ＣＨ_２ＣＨ_２Ｏ）ｗ−Ｒ^５３、ハロゲン原子（Ｆ、Ｃｌ、Ｂｒ、Ｉ）を有する炭素数１〜１８の置換アルキル基を表す。但し、Ｒ^５３は水素原子又は炭素数１〜１０のアルキル基を表わし、Ｂは、ジアルキルアミノ基、水酸基、アシルオキシ基、ハロゲン原子、ニトロ基を表わす。ｗは０〜４の整数、ｘは１〜２０の整数を表わす。特開平２−２４４０５０号記載の以下の一般式〔１７〕で表されるメロシアニン色素、例えば、
【００５０】
【化１６】

【００５１】
（式中Ｒ^５４およびＲ^５５は各々独立して水素原子、アルキル基、置換アルキル基、アルコキシカルボニル基、アリール基、置換アリール基またはアラルキル基を表わす。Ａ^２は酸素原子、イオウ原子、セレン原子、テルル原子、アルキルないしはアリール置換された窒素原子、またはジアルキル置換された炭素原子を表わす。Ｘ^９は含窒素ヘテロ五員環を形成するのに必要な非金属原子群を表わす。Ｙ^４は置換フェニル基、無置換ないし置換された多核芳香環、または無置換ないしは置換されたヘテロ芳香環を表わす。Ｚ^３は水素原子、アルキル基、置換アルキル基、アリール基、置換アリール基、アラルキル基、アルコキシ基、アルキルチオ基、アリールチオ基、置換アミノ基、アシル基、またはアルコキシカルボニル基を表わし、Ｙ^４と互いに結合して環を形成していてもよい。好ましい具体例としては
【００５２】
【化１７】

【００５３】
特公昭５９−２８３２６号記載の以下の一般式〔１８〕で表されるメロシアニン色素、例えば、
【００５４】
【化１８】

【００５５】
上式において、Ｒ^５６およびＲ^５７はそれぞれ水素原子、アルキル基、置換アルキル基、アリール基、置換アリール基またはアラルキル基を表わし、それらは互いに等しくても異ってもよい。Ｘ^１０はハメット（Ｈａｍｍｅｔｔ）のシグマ（σ）値が−０．９から＋０．５までの範囲内の置換基を表わす。特開昭５９−８９３０３号記載の以下の一般式〔１９〕で表されるメロシアニン色素、例えば、
【００５６】
【化１９】

【００５７】
（式中Ｒ^５８およびＲ^５９は各々独立して水素原子、アルキル基、置換アルキル基、アリール基、置換アリール基またはアラルキル基を表わす。Ｘ^１１はハメット（Ｈａｍｍｅｔｔ）のシグマ（σ）値が−０．９から＋０．５までの範囲内の置換基を表わす。Ｙ^５は水素原子、アルキル基、置換アルキル基、アリール基、置換アリール基、アラルキル基、アシル基またはアルコキシカルボニル基を表わす。）好ましい具体例としては、
【００５８】
【化２０】

【００５９】
特開平８−１２９２５７号記載の以下の一般式〔２０〕で表されるメロシアニン色素、例えば
【００６０】
【化２１】

【００６１】
（式中、Ｒ^６０、Ｒ^６１、Ｒ^６２、Ｒ^６３、Ｒ^６８、Ｒ^６９、Ｒ^７０、Ｒ^７１はそれぞれ独立して、水素原子、ハロゲン原子、アルキル基、置換アルキル基、アリール基、置換アリール基、ヒドロキシル基、置換オキシ基、メルカプト基、置換チオ基、アミノ基、置換アミノ基、置換カルボニル基、スルホ基、スルホナト基、置換スルフィニル基、置換スルホニル基、ホスフォノ基、置換ホスフォノ基、ホスフォナト基、置換ホスフォナト基、シアノ基、ニトロ基を表すか、もしくは、Ｒ^６０とＲ^６１、Ｒ^６１とＲ^６２、Ｒ^６２とＲ^６３、Ｒ^６８とＲ^６９、Ｒ^６９とＲ^７０、Ｒ^７０とＲ^７１が互いに結合して脂肪族又は芳香族環を形成していても良く、Ｒ^６４は水素原子、アルキル基、置換アルキル基、アリール基、又は置換アリール基を表し、Ｒ^６５は置換、又は無置換のアルケニルアルキル基、又は置換もしくは無置換のアルキニルアルキル基を表し、Ｒ^６６、Ｒ^６７はそれぞれ独立して、水素原子、ハロゲン原子、アルキル基、置換アルキル基、アリール基、置換アリール基、置換カルボニル基を表す）好ましい具体例としては
【００６２】
【化２２】

【００６３】
特開平８−３３４８９７号記載の以下の一般式〔２１〕で表されるベンゾピラン系色素、例えば
【００６４】
【化２３】

【００６５】
（式中、Ｒ^７２〜Ｒ^７５は互いに独立して、水素原子、ハロゲン原子、アルキル基、アリール基、水酸基、アルコキシ基又はアミノ基を表す。またＲ^７２〜Ｒ^７５はそれらが各々結合できる炭素原子と共に非金属原子から成る環を形成していても良い。Ｒ^７６は水素原子、アルキル基、アリール基、ヘテロ芳香族基、シアノ基、アルコキシ基、カルボキシ基又はアルケニル基を表す。Ｒ^７７はＲ^７６で表される基または−Ｚ−Ｒ^７６であり、Ｚはカルボニル基、スルホニル基、スルフィニル基またはアリーレンジカルボニル基を表す。またＲ^７６及びＲ^７７は共に非金属原子から成る環を形成しても良い。ＡはＯ原子、Ｓ原子、ＮＨまたは置換基を有するＮ原子を表す。ＢはＯ原子、または＝Ｃ（Ｇ１）（Ｇ２）の基を表す。Ｇ１、Ｇ２は同一でも異なっていても良く、水素原子、シアノ基、アルコキシカルボニル基、アリールオキシカルボニル基、アシル基、アリールカルボニル基、アルキルチオ基、アリールチオ基、アルキルスルホニル基、アリールスルホニル基、又はフルオロスルホニル基を表す。但し、Ｇ１、Ｇ２は同時に水素原子となることはない。またＧ１及びＧ２は炭素原子と共に非金属原子からなる環を形成していても良い）等を挙げることができる。
【００６６】
さらに好ましい増感色素骨格としては、下記一般式（２）、一般式（３）および一般式（４）で表される増感色素骨格が挙げられる。
【００６７】
【化２４】

【００６８】
（Ａは置換基を有しても良い芳香族環またはヘテロ環を表し、Ｘ、Ｙは酸素原子、硫黄原子または−Ｎ（Ｒ_１）−を表す。Ｒ_１、Ｒ_２、Ｒ_３、Ｒ_４、Ｒ_５、Ｒ_６、Ｒ_７、Ｒ_８、Ｒ_９、Ｒ_１０、Ｒ_１１、Ｒ_１２、Ｒ_１３は、それぞれ独立に、水素原子または、一価の非金属原子団であり、ＡとＲ_１、Ｒ_２、Ｒ_３、Ｒ_６、Ｒ_１３は、それぞれ互いに、脂肪族性または芳香族性の環を形成するために結合することができる。但し、Ａ、Ｒ_１、Ｒ_２、Ｒ_３、Ｒ_４、Ｒ_５、Ｒ_６、Ｒ_７、Ｒ_８、Ｒ_９、Ｒ_１０、Ｒ_１１、Ｒ_１２、Ｒ_１３の少なくとも１つは、下記部分構造（５）に示す１価の有機残基を表す。下記部分構造中、Ｌは一般式（２）、一般式（３）または一般式（４）で表される構造とＭを連結する２価の有機基を表し、Ｍはアンモニウム基、ピリジニウム基、スルホニウム基またはホスホニウム基を表す。）
【００６９】
【化２５】

【００７０】
Ｒ_１、Ｒ_２、Ｒ_３、Ｒ_４、Ｒ_５、Ｒ_６、Ｒ_７、Ｒ_８、Ｒ_９、Ｒ_１０、Ｒ_１１、Ｒ_１２、Ｒ_１３の好ましい具体例について述べる。好ましいアルキル基の例としては、炭素原子数が１から２０までの直鎖状、分岐状、および環状のアルキル基を挙げることができ、その具体例としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、ヘキサデシル基、オクタデシル基、エイコシル基、イソプロピル基、イソブチル基、ｓ−ブチル基、ｔ−ブチル基、イソペンチル基、ネオペンチル基、１−メチルブチル基、イソヘキシル基、２−エチルヘキシル基、２−メチルヘキシル基、シクロヘキシル基、シクロペンチル基、２−ノルボルニル基を挙げることができる。これらの中では、炭素原子数１から１２までの直鎖状、炭素原子数３から１２までの分岐状、ならびに炭素原子数５から１０までの環状のアルキル基がより好ましい。
【００７１】
置換アルキル基の置換基としては、水素を除く一価の非金属原子団が用いられ、好ましい例としては、ハロゲン原子（−Ｆ、−Ｂｒ、−Ｃｌ、−Ｉ）、ヒドロキシル基、アルコキシ基、アリーロキシ基、メルカプト基、アルキルチオ基、アリールチオ基、アルキルジチオ基、アリールジチオ基、アミノ基、Ｎ−アルキルアミノ基、Ｎ，Ｎ−ジアルキルアミノ基、Ｎ−アリールアミノ基、Ｎ，Ｎ−ジアリールアミノ基、Ｎ−アルキル−Ｎ−アリールアミノ基、アシルオキシ基、カルバモイルオキシ基、Ｎ−アルキルカルバモイルオキシ基、Ｎ−アリールカルバモイルオキシ基、Ｎ，Ｎ−ジアルキルカルバモイルオキシ基、Ｎ，Ｎ−ジアリールカルバモイルオキシ基、Ｎ−アルキル−Ｎ−アリールカルバモイルオキシ基、アルキルスルホキシ基、アリールスルホキシ基、アシルチオ基、アシルアミノ基、Ｎ−アルキルアシルアミノ基、Ｎ−アリールアシルアミノ基、ウレイド基、Ｎ′−アルキルウレイド基、Ｎ′，Ｎ′−ジアルキルウレイド基、
【００７２】
Ｎ′−アリールウレイド基、Ｎ′，Ｎ′−ジアリールウレイド基、Ｎ′−アルキル−Ｎ′−アリールウレイド基、Ｎ−アルキルウレイド基、Ｎ−アリールウレイド基、Ｎ′−アルキル−Ｎ−アルキルウレイド基、Ｎ′−アルキル−Ｎ−アリールウレイド基、Ｎ′，Ｎ′−ジアルキル−Ｎ−アルキルウレイド基、Ｎ′，Ｎ′−ジアルキル−Ｎ−アリールウレイド基、Ｎ′−アリール−Ｎ−アルキルウレイド基、Ｎ′−アリール−Ｎ−アリールウレイド基、Ｎ′，Ｎ′−ジアリール−Ｎ−アルキルウレイド基、Ｎ′，Ｎ′−ジアリール−Ｎ−アリールウレイド基、Ｎ′−アルキル−Ｎ′−アリール−Ｎ−アルキルウレイド基、Ｎ′−アルキル−Ｎ′−アリール−Ｎ−アリールウレイド基、アルコキシカルボニルアミノ基、アリーロキシカルボニルアミノ基、Ｎ−アルキル−Ｎ−アルコキシカルボニルアミノ基、Ｎ−アルキル−Ｎ−アリーロキシカルボニルアミノ基、Ｎ−アリール−Ｎ−アルコキシカルボニルアミノ基、Ｎ−アリール−Ｎ−アリーロキシカルボニルアミノ基、ホルミル基、アシル基、カルボキシル基、
【００７３】
アルコキシカルボニル基、アリーロキシカルボニル基、カルバモイル基、Ｎ−アルキルカルバモイル基、Ｎ，Ｎ−ジアルキルカルバモイル基、Ｎ−アリールカルバモイル基、Ｎ，Ｎ−ジアリールカルバモイル基、Ｎ−アルキル−Ｎ−アリールカルバモイル基、アルキルスルフィニル基、アリールスルフィニル基、アルキルスルホニル基、アリールスルホニル基、スルホ基（−ＳＯ_３Ｈ）及びその共役塩基基（以下、スルホナト基と称す）、アルコキシスルホニル基、アリーロキシスルホニル基、スルフィナモイル基、Ｎ−アルキルスルフィナモイル基、Ｎ，Ｎ−ジアルキルスルフィナモイル基、Ｎ−アリールスルフィナモイル基、Ｎ，Ｎ−ジアリールスルフィナモイル基、Ｎ−アルキル−Ｎ−アリールスルフィナモイル基、スルファモイル基、Ｎ−アルキルスルファモイル基、Ｎ，Ｎ−ジアルキルスルファモイル基、Ｎ−アリールスルファモイル基、Ｎ，Ｎ−ジアリールスルファモイル基、Ｎ−アルキル−Ｎ−アリールスルファモイル基、ホスフォノ基（−ＰＯ_３Ｈ_２）及びその共役塩基基（以下、ホスフォナト基と称す）、
【００７４】
ジアルキルホスフォノ基（−ＰＯ_３（ａｌｋｙｌ）_２）、ジアリールホスフォノ基（−ＰＯ_３（ａｒｙｌ）_２）、アルキルアリールホスフォノ基（−ＰＯ_３（ａｌｋｙｌ）（ａｒｙｌ））、モノアルキルホスフォノ基（−ＰＯ_３Ｈ（ａｌｋｙｌ））及びその共役塩基基（以後、アルキルホスフォナト基と称す）、モノアリールホスフォノ基（−ＰＯ_３Ｈ（ａｒｙｌ））及びその共役塩基基（以後、アリールホスフォナト基と称す）、ホスフォノオキシ基（−ＯＰＯ_３Ｈ_２）及びその共役塩基基（以後、ホスフォナトオキシ基と称す）、ジアルキルホスフォノオキシ基（−ＯＰＯ_３（ａｌｋｙｌ）_２）、ジアリールホスフォノオキシ基（−ＯＰＯ_３（ａｒｙｌ）_２）、アルキルアリールホスフォノオキシ基（−ＯＰＯ_３（ａｌｋｙｌ）（ａｒｙｌ））、モノアルキルホスフォノオキシ基（−ＯＰＯ_３Ｈ（ａｌｋｙｌ））及びその共役塩基基（以後、アルキルホスフォナトオキシ基と称す）、モノアリールホスフォノオキシ基（−ＯＰＯ_３Ｈ（ａｒｙｌ））及びその共役塩基基（以後、アリールフォスホナトオキシ基と称す）、シアノ基、ニトロ基、アリール基、ヘテロアリール基、アルケニル基、アルキニル基が挙げられる。
【００７５】
これらの置換基における、アルキル基の具体例としては、前述のアルキル基が挙げられ、アリール基の具体例としては、フェニル基、ビフェニル基、ナフチル基、トリル基、キシリル基、メシチル基、クメニル基、クロロフェニル基、ブロモフェニル基、クロロメチルフェニル基、ヒドロキシフェニル基、メトキシフェニル基、エトキシフェニル基、フェノキシフェニル基、アセトキシフェニル基、ベンゾイロキシフェニル基、メチルチオフェニル基、フェニルチオフェニル基、メチルアミノフェニル基、ジメチルアミノフェニル基、アセチルアミノフェニル基、カルボキシフェニル基、メトキシカルボニルフェニル基、エトキシフェニルカルボニル基、フェノキシカルボニルフェニル基、Ｎ−フェニルカルバモイルフェニル基、フェニル基、シアノフェニル基、スルホフェニル基、スルホナトフェニル基、ホスフォノフェニル基、ホスフォナトフェニル基等を挙げることができる。
【００７６】
ヘテロアリール基としては、窒素、酸素、硫黄原子の少なくとも一つを含有する単環、もしくは多環芳香族環が用いられ、特に好ましいヘテロアリール基の例としては、例えば、チオフェン、チアスレン、フラン、ピラン、イソベンゾフラン、クロメン、キサンテン、フェノキサジン、ピロール、ピラゾール、イソチアゾール、イソオキサゾール、ピラジン、ピリミジン、ピリダジン、インドリジン、イソインドリジン、インドイール、インダゾール、プリン、キノリジン、イソキノリン、フタラジン、ナフチリジン、キナゾリン、シノリン、プテリジン、カルバゾール、カルボリン、フェナンスリン、アクリジン、ペリミジン、フェナンスロリン、フタラジン、フェナルザジン、フェノキサジン、フラザン、フェノキサジンや等があげられ、これらは、さらにベンゾ縮環しても良く、また置換基を有していても良い。
【００７７】
また、アルケニル基の例としては、ビニル基、１−プロペニル基、１−ブテニル基、シンナミル基、２−クロロ−１−エテニル基、等が挙げられ、アルキニル基の例としては、エチニル基、１−プロピニル基、１−ブチニル基、トリメチルシリルエチニル基等が挙げられる。アシル基（Ｇ_１ＣＯ−）におけるＧ_１としては、水素、ならびに上記のアルキル基、アリール基を挙げることができる。これら置換基の内、更により好ましいものとしてはハロゲン原子（−Ｆ、−Ｂｒ、−Ｃｌ、−Ｉ）、アルコキシ基、アリーロキシ基、、アルキルチオ基、アリールチオ基、Ｎ−アルキルアミノ基、Ｎ，Ｎ−ジアルキルアミノ基、アシルオキシ基、Ｎ−アルキルカルバモイルオキシ基、Ｎ−アリールカルバモイルオキシ基、アシルアミノ基、ホルミル基、アシル基、カルボキシル基、アルコキシカルボニル基、アリーロキシカルボニル基、カルバモイル基、Ｎ−アルキルカルバモイル基、Ｎ，Ｎ−ジアルキルカルバモイル基、Ｎ−アリールカルバモイル基、Ｎ−アルキル−Ｎ−アリールカルバモイル基、スルホ基、スルホナト基、スルファモイル基、Ｎ−アルキルスルファモイル基、Ｎ，Ｎ−ジアルキルスルファモイル基、Ｎ−アリールスルファモイル基、Ｎ−アルキル−Ｎ−アリールスルファモイル基、ホスフォノ基、ホスフォナト基、ジアルキルホスフォノ基、ジアリールホスフォノ基、モノアルキルホスフォノ基、アルキルホスフォナト基、モノアリールホスフォノ基、アリールホスフォナト基、ホスフォノオキシ基、ホスフォナトオキシ基、アリール基、アルケニル基が挙げられる。
【００７８】
一方、置換アルキル基におけるアルキレン基としては前述の炭素数１から２０までのアルキル基上の水素原子のいずれか１つを除し、２価の有機残基としたものを挙げることができ、好ましくは炭素原子数１から１２までの直鎖状、炭素原子数３から１２までの分岐状ならびに炭素原子数５から１０までの環状のアルキレン基を挙げることができる。
【００７９】
該置換基とアルキレン基を組み合わせる事により得られるＲ_１〜Ｒ_１３として好ましい置換アルキル基の、具体例としては、クロロメチル基、ブロモメチル基、２−クロロエチル基、トリフルオロメチル基、メトキシメチル基、メトキシエトキシエチル基、アリルオキシメチル基、フェノキシメチル基、メチルチオメチル基、トリルチオメチル基、エチルアミノエチル基、ジエチルアミノプロピル基、モルホリノプロピル基、アセチルオキシメチル基、ベンゾイルオキシメチル基、Ｎ−シクロヘキシルカルバモイルオキシエチル基、Ｎ−フェニルカルバモイルオキシエチル基、アセチルアミノエチル基、Ｎ−メチルベンゾイルアミノプロピル基、２−オキソエチル基、２−オキソプロピル基、カルボキシプロピル基、メトキシカルボニルエチル基、アリルオキシカルボニルブチル基、クロロフェノキシカルボニルメチル基、カルバモイルメチル基、Ｎ−メチルカルバモイルエチル基、Ｎ，Ｎ−ジプロピルカルバモイルメチル基、Ｎ−（メトキシフェニル）カルバモイルエチル基、Ｎ−メチル−Ｎ−（スルホフェニル）カルバモイルメチル基、
【００８０】
スルホブチル基、スルホナトブチル基、スルファモイルブチル基、Ｎ−エチルスルファモイルメチル基、Ｎ，Ｎ−ジプロピルスルファモイルプロピル基、Ｎ−トリルスルファモイルプロピル基、Ｎ−メチル−Ｎ−（ホスフォノフェニル）スルファモイルオクチル基、ホスフォノブチル基、ホスフォナトヘキシル基、ジエチルホスフォノブチル基、ジフェニルホスフォノプロピル基、メチルホスフォノブチル基、メチルホスフォナトブチル基、トリルホスフォノヘキシル基、トリルホスフォナトヘキシル基、ホスフォノオキシプロピル基、ホスフォナトオキシブチル基、ベンジル基、フェネチル基、α−メチルベンジル基、１−メチル−１−フェニルエチル基、ｐ−メチルベンジル基、シンナミル基、アリル基、１−プロペニルメチル基、２−ブテニル基、２−メチルアリル基、２−メチルプロペニルメチル基、２−プロピニル基、２−ブチニル基、３−ブチニル基、等を挙げることができる。
【００８１】
Ｒ_１、Ｒ_２、Ｒ_３、Ｒ_４、Ｒ_５、Ｒ_６、Ｒ_７、Ｒ_８、Ｒ_９、Ｒ_１０、Ｒ_１１、Ｒ_１２およびＲ_１３として好ましいアリール基の具体例としては、１個から３個のベンゼン環が縮合環を形成したもの、ベンゼン環と５員不飽和環が縮合環を形成したものを挙げることができ、具体例としては、フェニル基、ナフチル基、アントリル基、フェナントリル基、インデニル基、アセナフテニル基、フルオレニル基、を挙げることができ、これらのなかでは、フェニル基、ナフチル基がより好ましい。
【００８２】
Ｒ_１、Ｒ_２、Ｒ_３、Ｒ_４、Ｒ_５、Ｒ_６、Ｒ_７、Ｒ_８、Ｒ_９、Ｒ_１０、Ｒ_１１、Ｒ_１２およびＲ_１３として好ましい置換アリール基の具体例としては、前述のアリール基の環形成炭素原子上に置換基として、水素を除く一価の非金属原子団を有するものが用いられる。好ましい置換基の例としては前述のアルキル基、置換アルキル基、ならびに、先に置換アルキル基における置換基として示したものを挙げることができる。この様な、置換アリール基の好ましい具体例としては、ビフェニル基、トリル基、キシリル基、メシチル基、クメニル基、クロロフェニル基、ブロモフェニル基、フルオロフェニル基、クロロメチルフェニル基、トリフルオロメチルフェニル基、ヒドロキシフェニル基、メトキシフェニル基、メトキシエトキシフェニル基、アリルオキシフェニル基、フェノキシフェニル基、メチルチオフェニル基、トリルチオフェニル基、エチルアミノフェニル基、ジエチルアミノフェニル基、モルホリノフェニル基、アセチルオキシフェニル基、ベンゾイルオキシフェニル基、Ｎ−シクロヘキシルカルバモイルオキシフェニル基、Ｎ−フェニルカルバモイルオキシフェニル基、
【００８３】
アセチルアミノフェニル基、Ｎ−メチルベンゾイルアミノフェニル基、カルボキシフェニル基、メトキシカルボニルフェニル基、アリルオキシカルボニルフェニル基、クロロフェノキシカルボニルフェニル基、カルバモイルフェニル基、Ｎ−メチルカルバモイルフェニル基、Ｎ，Ｎ−ジプロピルカルバモイルフェニル基、Ｎ−（メトキシフェニル）カルバモイルフェニル基、Ｎ−メチル−Ｎ−（スルホフェニル）カルバモイルフェニル基、スルホフェニル基、スルホナトフェニル基、スルファモイルフェニル基、Ｎ−エチルスルファモイルフェニル基、Ｎ，Ｎ−ジプロピルスルファモイルフェニル基、Ｎ−トリルスルファモイルフェニル基、Ｎ−メチル−Ｎ−（ホスフォノフェニル）スルファモイルフェニル基、ホスフォノフェニル基、ホスフォナトフェニル基、ジエチルホスフォノフェニル基、ジフェニルホスフォノフェニル基、メチルホスフォノフェニル基、メチルホスフォナトフェニル基、トリルホスフォノフェニル基、トリルホスフォナトフェニル基、アリル基、１−プロペニルメチル基、２−ブテニル基、２−メチルアリルフェニル基、２−メチルプロペニルフェニル基、２−プロピニルフェニル基、２−ブチニルフェニル基、３−ブチニルフェニル基、等を挙げることができる。
【００８４】
次に、一般式（２）〜（４）におけるＡについて説明する。Ａは置換基を有しても良い芳香族環またはヘテロ環をあらわし、置換基を有しても良い芳香族環またはヘテロ環の具体例としては、一般式（２）〜（４）中のＲ_１〜Ｒ_１３で記載したものと同様のものが挙げられる。
【００８５】
本発明の一般式であらわされる増感色素は、上に示したような酸性核や、活性メチレン基を有する酸性核と、置換、もしくは非置換の、芳香族環またはヘテロ環との縮合反応によって得られるが、これらは特公昭５９−２８３２９を参照して合成することができる。
【００８６】
次にＬについて説明する。Ｌは、増感色素骨格とアクセプター基Ｍとを連結する２価の有機基を表す。Ｌで表される２価の有機基としては、例えばアルキレン基、フェニレン基、ナフチレン基、等が挙げられる。上記２価の有機基はさらに置換基を有していてもよく、導入可能な置換基としては、例えば、アルキル基、アリール基、アルコキシ基、アシルオキシ基、ハロゲン原子、ヒドロキシ基、アミノ基、シアノ基、ニトロ基、等が挙げられる。また、Ｌはヘテロ原子を有していてもよい。ヘテロ原子を有する連結基の具体例としては、以下の部分構造を有するものが挙げられる。
【００８７】
【化２６】

【００８８】
ここで、「以下の部分構造を有する」とは、連結基、あるいは末端基としてのＬが上記部分構造を少なくとも１つ有することを意味し、上記部分構造を複数有するものであってもよい。従って、Ｌは、上記部分構造自体であってもよく、さらにこれらを複数個連結した基、或いは、上記部分構造と他の炭化水素基等をとを連結した基等であってもよい。特に好ましいＬの具体例としては、以下に示す構造が挙げられる。
【００８９】
【化２７】

【００９０】
次にアクセプター基Ｍについて説明する。Ｍは、増感色素の光吸収により生じる励起酸化電位よりも低い還元電位を有するアクセプター基を表す。好ましいアクセプター基としては、アンモニウム基またはピリジニウム基またはスルホニウム基またはホスホニウム基が挙げられる。アクセプター基の好ましい具体例を以下に示すが、本発明は、これに限定されるものではない。
【００９１】
【化２８】

【００９２】
特に好ましいアクセプター基としては、アンモニウム基、ピリジニウム基が挙げられ、さらに好ましい例としてはピリジニウム基が挙げられる。
【００９３】
次に対アニオンＸ⁻の好ましい例について説明する。
Ｘ⁻の好ましい例としては、ハロゲン化物イオン（Ｆ⁻、Ｃｌ⁻、Ｂｒ⁻、Ｉ⁻）、スルホン酸イオン、有機ホウ素アニオン、過塩素酸イオン（ＣｌＯ_４ ⁻）ならびに下記一般式（ａ）または（ｂ）で表されるアニオンが挙げられる。
【００９４】
ＭＸ_ｒ （ａ）
ＭＸ_ｒ−１（ＯＨ） （ｂ）
【００９５】
（式中、Ｍは、ホウ素原子、リン原子、砒素原子、またはアンチモン原子を表し、Ｘは、ハロゲン原子を表し、ｒは４〜６の整数を表す。）
【００９６】
スルホン酸イオンの好ましい例としては、メタンスルホン酸イオン、ベンゼンスルホン酸イオン、ｐ−トルエンスルホン酸イオン（ＴｓＯ⁻）、ｐ−スチレンスルホン酸イオン、β−ナフトキノン−４−スルホン酸イオン、アントラキノン−１，５−ジスルホン酸イオン、アントラキノン−１，８−ジスルホン酸イオン、アントラキノン−１−スルホン酸イオン、アントラキノン−２−スルホン酸イオン、キノリン−８−スルホン酸イオン、ヒドロキノンスルホン酸イオン、１，５−ナフタレンジスルホン酸イオン、１−ナフタレンスルホン酸イオン、２−ナフタレンスルホン酸イオン、２−アミノ−１−ナフタレンスルホン酸イオン、２−ナフトール−６−スルホン酸イオン、ジブチルナフタレンスルホン酸イオン、ナフタレン−１，３，６−トリスルホン酸イオン、ｍ−ベンゼンジスルホン酸イオン、ｐ−フェノールスルホン酸イオン、ドデシルベンゼンスルホン酸イオン、２−ヒドロキシ−４−メトキシベンゾフェノン−５−スルホン酸イオン、４−アセチルベンゼンスルホン酸イオン、４−ニトロトルエン−２−スルホン酸イオン、ｏ−ベンズアルデヒドスルホン酸イオン、ジフェニルアミン−４−スルホン酸イオン、ベンズアルデヒド−２，４−ジスルホン酸イオン、メシチレンスルホン酸イオン、トリフルオロメタンスルホン酸イオン、クロロスルホン酸イオン、フルオロスルホン酸イオン、９，１０−ジメトキシアントラセン−２−スルホン酸イオン等が挙げられる。
【００９７】
一般式（１）で表される化合物は、先述の増感色素骨格と、２価の有機基Ｌと、アクセプター基Ｍとを順次組み合わせることで構成できる。以下に一般式（１）で表される化合物の好ましい具体例（Ｄ１）〜（Ｄ４９）を示すが、本発明はこれに限定されるものではない。
【００９８】
【化２９】

【００９９】
【化３０】

【０１００】
【化３１】

【０１０１】
【化３２】

【０１０２】
【化３３】

【０１０３】
本発明の一般式（１）で表される増感色素は、Ｆ．Ｍ．ヘイマーら著、「ザ・シアニン・ダイズ・アンド・リレィテッド・コンパウンズ」（Ｆ．Ｍ．Ｈａｍｅｒ ｅｔ ａｌ．， ”Ｔｈｅ Ｃｙａｎｉｎｅ Ｄｙｅｓ ａｎｄ Ｒｅｌａｔｅｄ Ｃｏｍｐｏｕｎｄｓ ”） 第５１１〜６１１頁（１９６４年）に記載された方法、ＫＡＩ ＡＲＮＥ ＪＥＮＳＥＮ およびＬＡＲＳ ＨＥＮＲＩＫＳＥＮらがＡＣＴＡ ＣＨＥＭＩＣＡ ＳＣＡＮＤＩＮＡＶＩＣＡ ２２巻１１０７〜１１２８頁（１９６８年）に記載した方法などを参照して合成することができる。
【０１０４】
本発明の増感色素に関しては、さらに、感光層の特性を改良するための様々な化学修飾を行うことも可能である。例えば、増感色素と、付加重合性化合物構造（例えば、アクリロイル基やメタクリロイル基）とを、共有結合、イオン結合、水素結合等の方法により結合させることで、露光膜の高強度化や、露光後の膜からの色素の不要な析出抑制を行うことができる。また、増感色素と後述の活性剤化合物のラジカル、酸または塩基の発生パート等との結合により、特に開始系の濃度の低い状態での感光性を著しく高めることができる。さらに、本発明の感光層の好ましい使用様態である、（アルカリ）水系現像液への処理適性を高める目的に対しては、親水性部位（カルボキシル基並びにそのエステル、スルホン酸基並びにそのエステル、エチレンオキサイド基等の酸基もしくは極性基）の導入が有効である。特にエステル型の親水性基は、感光層中では比較的疎水的構造を有するため相溶性に優れ、かつ、現像液中では、加水分解により酸基を生成し、親水性が増大するという特徴を有する。その他、例えば、感光層中での相溶性向上、結晶析出抑制のために適宜置換基を導入することができる。例えば、ある種の感光系では、アリール基やアリル基等の不飽和結合が相溶性向上に非常に有効である場合があり、また、分岐アルキル構造導入等の方法により、色素π平面間の立体障害を導入することで、結晶析出が著しく抑制できる。また、ホスホン酸基やエポキシ基、トリアルコキシシリル基等の導入により、金属や金属酸化物等の無機物への密着性を向上させることができる。そのほか、目的に応じ、増感色素のポリマー化等の方法も利用できる。
【０１０５】
これらの増感色素のどの構造を用いるか、単独で使用するか２種以上併用するか、添加量はどうか、といった使用法の詳細は、最終的な感材の性能設計にあわせて適宜設定できる。例えば、増感色素を２種以上併用することで、感光層への相溶性を高めることができる。増感色素の選択は、感光性の他、使用する光源の発光波長でのモル吸光係数が重要な因子である。モル吸光係数の大きな色素を使用することにより、色素の添加量は比較的少なくできるので、経済的であり、かつ感光層の膜物性の点からも有利である。感光層の感光性、解像度や、露光膜の物性は光源波長での吸光度に大きな影響を受けるので、これらを考慮して増感色素の添加量を適宜選択する。例えば、吸光度が０．１以下の低い領域では感度が低下する。また、ハレーションの影響により低解像度となる。但し、例えば５μｍ以上の厚い膜を硬化させる目的に対しては、このような低い吸光度の方がかえって硬化度を上げられる場合もある。また、吸光度が３以上のような高い領域では、感光層表面で大部分の光が吸収され、より内部での硬化が阻害され、例えば印刷版として使用した場合には膜強度、基板密着性の不十分なものとなる。比較的薄い膜厚で使用する平版印刷版としての使用に際しては、増感色素の添加量は、感光層の吸光度が０．１から１．５の範囲、好ましくは０．２５から１の範囲となるように設定するのが好ましい。平版印刷版として利用する場合には、これは、通常、感光層成分１００重量部に対し、０．０５〜３０重量部、好ましくは０．１〜２０重量部、さらに好ましくは０．２〜１０重量部の範囲である。
【０１０６】
（Ａ２）活性剤化合物
本発明における光開始系の第２の必須成分である、活性剤について説明する。本発明における活性剤は増感色素の電子励起状態との相互作用を経て、化学変化を生じ、ラジカル、酸および塩基のうちの少なくともいずれか１種を生成する化合物である。以下、このようにして生じたラジカル、酸、塩基を単に活性種と呼ぶ。これらの化合物が存在しない場合や、活性剤のみを単独で用いた場合には、実用上十分な感度が得られないが、前記、増感色素と、活性化合物を併用する一つの態様として、これらを、適切な化学的方法（増感色素と、活性剤化合物との化学結合による連結等）によって単一の化合物として利用することも可能である。このような技術思想は、例えば、特許第２７２０１９５号公報に開示されている。
【０１０７】
通常これらの、活性剤の多くは、次の、▲１▼から▲３▼の初期化学プロセスを経て、活性種を生成するものと考えられる。即ち、▲１▼増感色素の電子励起状態から活性剤への電子移動反応に基づく、活性剤の還元的分解、▲２▼活性剤から増感色素の電子励起状態への電子移動に基づく、活性剤の酸化的分解、▲３▼増感色素の電子励起状態から活性剤へのエネルギー移動に基づく、活性剤の電子励起状態からの分解、である。個々の、活性剤化合物が▲１▼から▲３▼のどのタイプに属するかに関しては、曖昧な場合も多いが、本発明における、増感色素の大きな特徴は、これら、何れのタイプの活性剤と組み合わせても非常に高い増感効果を示すことにある。
【０１０８】
具体的な活性剤化合物は当業者間で公知のものを制限なく使用でき、具体的には、例えば、 Ｂｒｕｃｅ Ｍ． Ｍｏｎｒｏｅら著、Ｃｈｅｍｉｃａｌ Ｒｅｖｕｅ，９３，４３５（１９９３）．やＲ．Ｓ．Ｄａｖｉｄｓｏｎ著、Ｊｏｕｒｎａｌ ｏｆ Ｐｈｏｔｏｃｈｅｍｉｓｔｒｙ ａｎｄ ｂｉｏｌｏｇｙ
Ａ：Ｃｈｅｍｉｓｔｒｙ，７３．８１（１９９３）．Ｊ．Ｐ．Ｆａｕｓｓｉｅｒ”Ｐｈｏｔｏｉｎｉｔｉａｔｅｄ Ｐｏｌｙｍｅｒｉｚａｔｉｏｎ−Ｔｈｅｏｒｙ ａｎｄ Ａｐｐｌｉｃａｔｉｏｎｓ” ：Ｒａｐｒａ Ｒｅｖｉｅｗ ｖｏｌ．９，Ｒｅｐｏｒｔ，Ｒａｐｒａ Ｔｅｃｈｎｏｌｏｇｙ（１９９８）．Ｍ．Ｔｓｕｎｏｏｋａ ｅｔ ａｌ．，Ｐｒｏｇ．Ｐｏｌｙｍ．Ｓｃｉ．，２１，１（１９９６）．に多く、記載されている。また、前記▲１▼、▲２▼の機能を有する他の化合物群としては、さらに、Ｆ． Ｄ．Ｓａｅｖａ，Ｔｏｐｉｃｓ ｉｎ Ｃｕｒｒｅｎｔ Ｃｈｅｍｉｓｔｒｙ，１５６，５９（１９９０）．Ｇ． Ｇ． Ｍａｓｌａｋ，Ｔｏｐｉｃｓ ｉｎ Ｃｕｒｒｅｎｔ Ｃｈｅｍｉｓｔｒｙ，１６８，１（１９９３）．Ｈ． Ｂ．Ｓｈｕｓｔｅｒ ｅｔ ａｌ，ＪＡＣＳ，１１２，６３２９（１９９０）．Ｉ． Ｄ．Ｆ．Ｅａｔｏｎ ｅｔ ａｌ，ＪＡＣＳ，１０２，３２９８（１９８０）． 等に記載されているような、酸化的もしくは還元的に結合解裂を生じる化合物群も知られる。
【０１０９】
以下、好ましい活性剤の具体例に関し、（ａ）還元されて結合解裂を起こし活性種を生成するもの、（ｂ）酸化されて結合解裂を起こし活性種を生成しうるもの、（ｃ）その他のものに分類して説明するが、個々の化合物がこれらのどれに属するかに関しては通説がない場合も多く、本発明はこれらの反応機構に関する記述に制限を受けるものではない。
【０１１０】
（ａ）還元されて結合解裂を起こし活性種を生成するもの。
炭素−ハロゲン結合を有する化合物：還元的に炭素−ハロゲン結合が解裂し、活性種を発生すると考えられる（例えば、Ｐｏｌｙｍｅｒ Ｐｒｅｐｒｉｎｔｓ，Ｊｐｎ．，４１（３）５４２（１９９２）．に記載れている）。活性種としては、ラジカル、酸を発生しうる。具体的には、例えば、ハロメチル−ｓ−トリアジン類の他、Ｍ．Ｐ．Ｈｕｔｔ，Ｅ．Ｆ．ＥｌｓｌａｇｅｒおよびＬ．Ｍ．Ｍｅｒｂｅｌ著Ｊｏｕｒｎａｌ ｏｆ Ｈｅｔｅｒｏｃｙｃｌｉｃ ｃｈｅｍｉｓｔｒｙ，７，５１１（１９７０）．に記載される合成方法により当業者が容易に合成しうるハロメチルオキサジアゾール類、また、ドイツ特許２６４１１００号，同３３３３４５０号，同３０２１５９０号、同３０２１５９９号に記載される化合物等が好適に使用できる。
【０１１１】
窒素−窒素結合もしくは、含窒素ヘテロ環−含窒素ヘテロ環結合を有する化合物：還元的に結合解裂を起こす（例えば、Ｊ．Ｐｙｓ．Ｃｈｅｍ．，９６，２０７（１９９２）．に記載されている）。具体的にはヘキサアリールビイミダゾール類等が好適に使用される。生成する活性種はロフィンラジカルであり、必要に応じ水素供与体との併用で、ラジカル連鎖反応を開始するほか、ロフィンラジカルによる酸化反応を用いた画像形成も知られる（Ｊ．Ｉｍａｇｉｎｇ Ｓｃｉ．，３０，２１５（１９８６）．に記載される）。
【０１１２】
酸素−酸素結合を有する化合物：還元的に酸素−酸素結合が解裂し、活性ラジカルを発生すると考えられる（例えば、Ｐｏｌｙｍ．Ａｄｖ．Ｔｅｃｈｎｏｌ．，１，２８７（１９９０）．に記載されている）。具体的には、例えば、有機過酸化物類等が好適に使用される。活性種としてラジカルを発生しうる。
【０１１３】
オニウム化合物：還元的に炭素−ヘテロ結合や、酸素−窒素結合が解裂し、活性種を発生すると考えられる（例えば、Ｊ．Ｐｈｏｔｏｐｏｌｙｍ．Ｓｃｉ．Ｔｅｃｈｎｏｌ．，３，１４９（１９９０）．に記載されている）。具体的には例えば、欧州特許１０４１４３号，米国特許４８３７１２４号，特開平２−１５０８４８号，特開平２−９６５１４号に記載されるヨードニウム塩類、欧州特許３７０６９３号，同２３３５６７号，同２９７４４３号，同２９７４４２号，同２７９２１０号，同４２２５７０号，米国特許３９０２１４４号，同４９３３３７７号，同４７６００１３号，同４７３４４４４号，同２８３３８２７号に記載されるスルホニウム塩類、ジアゾニウム塩類（置換基を有しても良いベンゼンジアゾニウム等）、ジアゾニウム塩樹脂類（ジアゾジフェニルアミンのホルムアルデヒド樹脂等）、Ｎ−アルコキシピリジニウム塩類等（例えば、ＵＳＰ４，７４３，５２８号、特開昭６３−１３８３４５号、特開昭６３−１４２３４５号、特開昭６３−１４２３４６号、特公昭４６−４２３６３号等に記載されるもので、具体的には１−メトキシ−４−フェニルピリジニウム テトラフルオロボレート等）、さらには特公昭５２−１４７２７７号、同５２−１４２７８号，同５２−１４２７９号記載の化合物が好適に使用される。活性種としてラジカルや酸を生成する。
【０１１４】
活性エステル類：スルホン酸やカルボン酸のニトロベンジルエステル類、スルホン酸やカルボン酸とＮ−ヒドロキシ化合物（Ｎ−ヒドロキシフタルイミドやオキシム等）とのエステル類、ピロガロールのスルホン酸エステル類、ナフトキノンジアジド−４−スルホン酸エステル類等は還元的に分解しうる。活性種としては、ラジカル、酸、を発生しうる。具体的な、スルホン酸エステル類の例としては、欧州特許０２９０７５０号、同０４６０８３号，同１５６１５３号，同２７１８５１号、同０３８８３４３号，米国特許３９０１７１０号，同４１８１５３１号，特開昭６０−１９８５３８号，特開昭５３−１３３０２２号に記載されるニトロベンズルエステル化合物、欧州特許０１９９６７２，同８４５１５号，同１９９６７２，同０４４１１５号，同０１０１１２２号，米国特許４６１８５６４，同４３７１６０５号，同４４３１７７４号、特開昭６４−１８１４３号，特開平２−２４５７５６号，特開平４−３６５０４８号記載のイミノスルホネート化合物、特公昭６２−６２２３号、特公昭６３−１４３４０号，特開昭５９−１７４８３１号に記載される化合物等が挙げられ、さらに、例えば下記に示すような化合物が挙げられる。
【０１１５】
【化３４】

【０１１６】
（式中、Ａｒは置換されても良い芳香族基、脂肪族基を表す。）
また、活性種として塩基を生成することも可能であり、例えば下記のような化合物群が知られる。
【０１１７】
フェロセン、鉄アレーン錯体類：還元的に活性ラジカルを生成しうる。具体的には例えば、特開平１−３０４４５３号、特開平１−１５２１０９号に開示されている。
【０１１８】
【化３５】

【０１１９】
（式中Ｒは置換されても良い脂肪族基、芳香族基を表す。）
ジスルホン類：還元的にＳ−Ｓ結合解裂を起こし酸を発生しうる。例えば特開昭６１−１６６５４４号に記載されるようなジフェニルジスルホン類が知られる。
【０１２０】
（ｂ）酸化されて結合解裂を起こし活性種を生成するもの。
アルキルアート錯体：酸化的に炭素−ヘテロ結合が解裂し、活性ラジカルを生成すると考えられる（例えば、Ｊ．Ａｍ．Ｃｈｅｍ．Ｓｏｃ．，１１２，６３２９（１９９０）．に記載される）。具体的には例えば、トリアリールアルキルボレート類が好適に使用される。
【０１２１】
アルキルアミン化合物：酸化により窒素に隣接した炭素上のＣ−Ｘ結合が解裂し、活性ラジカルを生成するものと考えられる（例えば、Ｊ．Ａｍ．Ｃｈｅｍ．Ｓｏｃ．，１１６，４２１１（１９９４）．に記載される）。Ｘとしては、水素原子、カルボキシル基、トリメチルシリル基、ベンジル基等が好適である。具体的には、例えば、エタノールアミン類、Ｎ−フェニルグリシン類、Ｎ−トリメチルシリルメチルアニリン類等が挙げられる。
【０１２２】
含硫黄、含錫化合物：上述のアミン類の窒素原子を硫黄原子、錫原子に置き換えたものが、同様の作用により活性ラジカルを生成しうる。また、Ｓ−Ｓ結合を有する化合物もＳ−Ｓ解裂による増感が知られる。
【０１２３】
α−置換メチルカルボニル化合物：酸化により、カルボニル−α炭素間の結合解裂により、活性ラジカルを生成しうる。また、カルボニルをオキシムエーテルに変換したものも同様の作用を示す。具体的には、２−アルキル−１−［４−（アルキルチオ）フェニル］−２−モルフォリノプロノン−１類、並びに、これらと、ヒドロキシアミン類とを反応したのち、Ｎ−ＯＨをエーテル化したオキシムエーテル類を挙げることができる。
【０１２４】
スルフィン酸塩類：還元的に活性ラジカルを生成しうる。具体的は、アリールスルフィン酸ナトリウム等を挙げることができる。
【０１２５】
（ｃ）その他
増感機構は明確ではないが、活性剤として機能しうるものも多い。チタノセン等の有機金属化合物や芳香族ケトン、アシルフォスフィン、ビスアシルフォスフィン類等が挙げられ、活性種としては、ラジカル、酸を発生しうる。
【０１２６】
以下、本発明に使用される活性剤化合物の内、感度や安定性に特に優れる好ましい化合物群を具体的に例示する。
【０１２７】
（１）ハロメチルトリアジン類
下記一般式［Ｉ］で表される化合物が挙げられる。特にラジカル発生、酸発生能に優れる。
【０１２８】
【化３６】

【０１２９】
式［Ｉ］中、Ｘはハロゲン原子を表す。Ｙ^１は−ＣＸ_３、−ＮＨ_２、−ＮＨＲ^１’、−ＮＲ^１’_２、−ＯＲ^１’を表す。ここでＲ^１’はアルキル基、置換アルキル基、アリール基、置換アリール基を表す。またＲ^１’は−ＣＸ_３、アルキル基、置換アルキル基、アリール基、置換アリール基、置換アルケニル基を表す。
【０１３０】
このような化合物の具体例としては、例えば、若林ら著、Ｂｕｌｌ． Ｃｈｅｍ． Ｓｏｃ． Ｊａｐａｎ， ４２，２９２４（１９６９）記載の化合物、例えば、２−フェニル−４，６−ビス（トリクロルメチル）−Ｓ−トリアジン、２−（ｐ−クロルフェニル）−４，６−ビス（トリクロルメチル）−Ｓ−トリアジン、２−（ｐ−トリル）−４，６−ビス（トリクロルメチル）−Ｓ−トリアジン、２−（ｐ−メトキシフェニル）−４，６−ビス（トリクロルメチル）−Ｓ−トリアジン、２−（２’，４’−ジクロルフェニル）−４，６−ビス（トリクロルメチル）−Ｓ−トリアジン、２，４，６−トリス（トリクロルメチル）−Ｓ−トリアジン、２−メチル−４，６−ビス（トリクロルメチル）−Ｓ−トリアジン、２−ｎ−ノニル−４，６−ビス（トリクロルメチル）−Ｓ−トリアジン、２−（α，α，β−トリクロルエチル）−４，６−ビス（トリクロルメチル）−Ｓ−トリアジン等が挙げられる。その他、英国特許第１３８８４９２ 号明細書記載の化合物、例えば、２−スチリル−４，６−ビス（トリクロルメチル）−Ｓ−トリアジン、２−（ｐ−メチルスチリル）−４，６−ビス（トリクロルメチル）−Ｓ−トリアジン、２−（ｐ−メトキシスチリル）−４，６−ビス（トリクロルメチル）−Ｓ−トリアジン、２−（ｐ−メトキシスチリル）−４−アミノ−６−トリクロルメチル−Ｓ−トリアジン等、特開昭５３−１３３４２８号記載の化合物、例えば、２−（４−メトキシ−ナフト−１−イル）−４，６−ビス−トリクロルメチル−Ｓ−トリアジン、２−（４−エトキシ−ナフト−１−イル）−４，６−ビス−トリクロルメチル−Ｓ−トリアジン、２−〔４−（２−エトキシエチル）−ナフト−１−イル〕−４，６−ビス−トリクロルメチル−Ｓ−トリアジン、２−（４，７−ジメトキシ−ナフト−１−イル〕−４，６−ビス−トリクロルメチル−Ｓ−トリアジン、２−（アセナフト−５−イル）−４，６−ビス−トリクロルメチル−Ｓ−トリアジン等、独国特許第３３３７０２４ 号明細書記載の化合物、例えば下記の化合物を挙げることができる。
【０１３１】
【化３７】

【０１３２】
【化３８】

【０１３３】
また、Ｆ． Ｃ． Ｓｃｈａｅｆｅｒ等による Ｊ． Ｏｒｇ． Ｃｈｅｍ．，２９，１５２７（１９６４）記載の化合物、例えば２−メチル−４，６−ビス（トリブロムメチル）−Ｓ−トリアジン、２，４，６−トリス（トリブロムメチル）−Ｓ−トリアジン、２，４，６−トリス（ジブロムメチル）−Ｓ−トリアジン、２−アミノ−４−メチル−６−トリブロムメチル−Ｓ−トリアジン、２−メトキシ−４−メチル−６−トリクロルメチル−Ｓ−トリアジン等を挙げることができる。
【０１３４】
さらに特開昭６２−５８２４１号記載の化合物、例えば下記の化合物を挙げることができる。
【０１３５】
【化３９】

【０１３６】
【化４０】

【０１３７】
更に特開平５−２８１７２８号記載の化合物、例えば下記の化合物を挙げることができる。
【０１３８】
【化４１】

【０１３９】
（２）チタノセン類
活性剤として特に好適に用いられる、チタノセン化合物は、前記した増感色素との共存下で光照射した場合、活性種を発生し得るチタノセン化合物であればいずれであってもよく、例えば、特開昭５９−１５２３９６号、特開昭６１−１５１１９７号、特開昭６３−４１４８３号、特開昭６３−４１４８４号、特開平２−２４９号、特開平２−２９１号、特開平３−２７３９３号、特開平３−１２４０３号、特開平６−４１１７０号公報に記載されている公知の化合物を適宜に選択して用いることができる。
【０１４０】
さらに具体的には、ジ−シクロペンタジエニル−Ｔｉ−ジ−クロライド、ジ−シクロペンタジエニル−Ｔｉ−ビス−フェニル、ジ−シクロペンタジエニル−Ｔｉ−ビス−２，３，４，５，６−ペンタフルオロフェニ−１−イル、ジ−シクロペンタジエニル−Ｔｉ−ビス−２，３，５，６−テトラフルオロフェニ−１−イル、ジ−シクロペンタジエニル−Ｔｉ−ビス−２，４，６−トリフルオロフェニ−１−イル、ジ−シクロペンタジエニル−Ｔｉ−ビス−２，６−ジフルオロフエニ−１−イル、ジ−シクロペンタジエニル−Ｔｉ−ビス−２，４−ジフルオロフエニ−１−イル、ジ−メチルシクロペンタジエニル−Ｔｉ−ビス−２，３，４，５，６−ペンタフルオロフエニ−１−イル、ジ−メチルシクロペンタジエニル−Ｔｉ−ビス−２，３，５，６−テトラフルオロフエニ−１−イル、ジ−メチルシクロペンタジエニル−Ｔｉ−ビス−２，４−ジフルオロフエニ−１−イル、ビス（シクロペンタジエニル）−ビス（２，６−ジフルオロ−３−（ピル−１−イル）フェニル）チタニウム等を挙げることができる。
【０１４１】
（３）ボレート塩化合物
下記一般式［ＩＩ］で表されるボレート塩類はラジカル発生能に優れる。
【０１４２】
【化４２】

【０１４３】
一般式［ＩＩ］中、Ｒ^５１、Ｒ^５２、Ｒ^５３およびＲ^５４は互いに同一でも異なっていてもよく、各々置換もしくは無置換のアルキル基、置換もしくは無置換のアリール基、置換もしくは無置換のアルケニル基、置換もしくは無置換のアルキニル基、または置換もしくは無置換の複素環基を示し、Ｒ^５１、Ｒ^５２、Ｒ^５３およびＲ^５４はその２個以上の基が結合して環状構造を形成してもよい。ただし、Ｒ^５１、Ｒ^５２、Ｒ^５３およびＲ^５４のうち、少なくとも１つは置換または無置換のアルキル基である。Ｚ^＋はアルカリ金属カチオンまたは第４級アンモニウムカチオンを示す。
【０１４４】
上記Ｒ^５１〜Ｒ^５４のアルキル基としては、直鎖、分枝、環状のものが含まれ、炭素原子数１〜１８のものが好ましい。具体的にはメチル、エチル、プロピル、イソプロピル、ブチル、ペンチル、ヘキシル、オクチル、ステアリル、シクロブチル、シクロペンチル、シクロヘキシルなどが含まれる。また置換アルキル基としては、上記のようなアルキル基に、ハロゲン原子（例えば−Ｃｌ、−Ｂｒなど）、シアノ基、ニトロ基、アリール基（好ましくはフェニル基）、ヒドロキシ基、下記の基、
【０１４５】
【化４３】

【０１４６】
（ここでＲ^５５、Ｒ^５６は独立して水素原子、炭素数１〜１４のアルキル基、またはアリール基を示す。）、−ＣＯＯＲ^５７（ここでＲ^５７は水素原子、炭素数１〜１４のアルキル基、またはアリール基を示す。）、−ＣＯＯＲ^５８または−ＯＲ^５９（ここでＲ^５８は炭素数１〜１４のアルキル基、またはアリール基を示す。）を置換基として有するものが含まれる。
【０１４７】
上記Ｒ^５１〜Ｒ^５４のアリール基としては、フェニル基、ナフチル基などの１〜３環のアリール基が含まれ、置換アリール基としては、上記のようなアリール基に前述の置換アルキル基の置換基、または炭素数１〜１４のアルキル基を有するものが含まれる。
【０１４８】
上記Ｒ^５１〜Ｒ^５４のアルケニル基としては、炭素数２〜１８の直鎖、分枝、環状のものが含まれ、置換アルケニル基の置換基としては、前記の置換アルキル基の置換基として挙げたものが含まれる。
【０１４９】
上記Ｒ^５１〜Ｒ^５４のアルキニル基としては、炭素数２〜２８の直鎖または分枝のものが含まれ、置換アルキニル基の置換基としては、前記置換アルキル基の置換基として挙げたものが含まれる。
【０１５０】
また、上記Ｒ^５１〜Ｒ^５４の複素環基としてはＮ、ＳおよびＯの少なくとも１つを含む５員環以上、好ましくは５〜７員環の複素環基が挙げられ、この複素環基には縮合環が含まれていてもよい。さらに置換基として前述の置換アリール基の置換基として挙げたものを有していてもよい。
【０１５１】
一般式［ＩＩ］で示される化合物例としては具体的には米国特許第３５６７４５３号、同４３４３８９１号、ヨーロッパ特許第１０９７７２号、同１０９７７３号に記載されている化合物および以下に示すものが挙げられる。
【０１５２】
【化４４】

【０１５３】
（４）ヘキサアリールビイミダゾール類
安定性に優れ、高感度なラジカル発生が可能である。具体的には、２，２’−ビス（ｏ−クロロフェニル）−４，４’，５，５’−テトラフェニルビイミダゾール、２，２’−ビス（ｏ−ブロモフェニル）−４，４’，５，５’−テトラフェニルビイミダゾール、２，２’−ビス（ｏ，ｐ−ジクロロフェニル）−４，４’，５，５’−テトラフェニルビイミダゾール、２，２’−ビス（ｏ−クロロフェニル）−４，４’，５，５’−テトラ（ｍ−メトキシフェニル）ビイミダゾール、２，２’−ビス（ｏ，ｏ’−ジクロロフェニル）−４，４’，５，５’−テトラフェニルビイミダゾール、２，２’−ビス（ｏ−ニトロフェニル）−４，４’，５，５’−テトラフェニルビイミダゾール、２，２’−ビス（ｏ−メチルフェニル）−４，４’，５，５’−テトラフェニルビイミダゾール、２，２’−ビス（ｏ−トリフルオロメチルフェニル）−４，４’，５，５’−テトラフェニルビイミダゾール等が挙げられる。
【０１５４】
（５）オニウム塩化合物
周期律表の１５（５Ｂ）、１６（６Ｂ）、１７（７Ｂ）族元素、具体的にはＮ、Ｐ、Ａｓ、Ｓｂ、Ｂｉ、Ｏ、Ｓ、Ｓｅ、Ｔｅ、Ｉのオニウム化合物は感度に優れた活性剤である。特にヨードニウム塩やスルホニウム塩、とりわけ、ジアリールヨードニウム、トリアリールスルホニウム塩化合物は感度と保存安定性の両方の観点で極めて優れている。酸、および／またはラジカルの発生が可能であり、これらは目的に応じて、使用条件を適宜選択することで使い分けることができる。具体的には以下の化合物が挙げられる。
【０１５５】
【化４５】

【０１５６】
【化４６】

【０１５７】
【化４７】

【０１５８】
【化４８】

【０１５９】
（６）有機過酸化物
有機過酸化物型の活性剤を用いる場合、活性種としてラジカルの発生を非常に高感度で行うことができる。
【０１６０】
「有機過酸化物」としては分子中に酸素−酸素結合を１個以上有する有機化合物のほとんど全てが含まれるが、その例としては、例えばメチルエチルケトンパーオキサイド、シクロヘキサノンパーオキサイド、３，３，５−トリメチルシクロヘキサノンパーオキサイド、メチルシクロヘキサノンパーオキサイド、アセチルアセトンパーオキサイド、１，１−ビス（ｔ−ブチルパーオキシ）−３，３，５−トリメチルシクロヘキサン、１，１−ビス（ｔ−ブチルパーオキシ）シクロヘキサン、２，２−ビス（ｔ−ブチルパーオキシ）ブタン、ｔ−ブチルハイドロパーオキサイド、クメンハイドロパーオキサイド、ジイソプロピルベンゼンハイドロパーオキサイド、パラメタンハイドロパーオキサイド、２，５−ジメチルヘキサン−２，５−ジハイドロパーオキサイド、１，１，３，３−テトラメチルブチルハイドロパーオキサイド、ジ−ｔ−ブチルパーオキサイド、ｔ−ブチルクミルパーオキサイド、ジクミルパーオキサイド、ビス（ｔ−ブチルパーオキシイソプロピル）ベンゼン、２，５−ジメチル−２，５−ジ（ｔ−ブチルパーオキシ）ヘキサン、２，５−ジメチル−２，５−ジ（ｔ−ブチルパーオキシ）ヘキシン−３、アセチルパーオキサイド、イソブチリルパーオキサイド、オクタノイルパーオキサイド、デカノイルパーオキサイド、ラウロイルパーオキサイド、３，５，５−トリメチルヘキサノイルパーオキサイド、過酸化こはく酸、過酸化ベンゾイル、２，４−ジクロロベンゾイルパーオキサイド、メタ−トルオイルパーオキサイド、ジイソプロピルパーオキシジカーボネート、ジ−２−エチルヘキシルパーオキシジカーボネート、ジ−２−エトキシエチルパーオキシジカーボネート、ジメトキシイソプロピルパーオキシカーボネート、ジ（３−メチル−３−メトキシブチル）パーオキシジカーボネート、ｔ−ブチルパーオキシアセテート、ｔ−ブチルパーオキシピバレート、ｔ−ブチルパーオキシネオデカノエート、ｔ−ブチルパーオキシオクタノエート、ｔ−ブチルパーオキシ−３，５，５−トリメチルヘキサノエート、ｔ−ブチルパーオキシラウレート、ｔ−ブチルパーオキシベンゾエート、ジ−ｔ−ブチルパーオキシイソフタレート、２，５−ジメチル−２，５−ジ（ベンゾイルパーオキシ）ヘキサン、ｔ−ブチル過酸化マレイン酸、ｔ−ブチルパーオキシイソプロピルカーボネート、３，３’，４，４’−テトラ−（ｔ−ブチルパーオキシカルボニル）ベンゾフェノン、３，３’，４，４’−テトラ−（ｔ−アミルパーオキシカルボニル）ベンゾフェノン、３，３’，４，４’−テトラ（ｔ−ヘキシルパーオキシカルボニル）ベンゾフェノン、３，３’，４，４’−テトラ（ｔ−オクチルパーオキシカルボニル）ベンゾフェノン、３，３’，４，４’−テトラ（クミルパーオキシカルボニル）ベンゾフェノン、３，３’，４，４’−テトラ（ｐ−イソプロピルクミルパーオキシカルボニル）ベンゾフェノン、カルボニルジ（ｔ−ブチルパーオキシ二水素二フタレート）、カルボニルジ（ｔ−ヘキシルパーオキシ二水素二フタレート）等がある。
【０１６１】
これらの中で、３，３’，４，４’−テトラ−（ｔ−ブチルパーオキシカルボニル）ベンゾフェノン、３，３’，４，４’−テトラ−（ｔ−アミルパーオキシカルボニル）ベンゾフェノン、３，３’，４，４’−テトラ（ｔ−ヘキシルパーオキシカルボニル）ベンゾフェノン、３，３’，４，４’−テトラ（ｔ−オクチルパーオキシカルボニル）ベンゾフェノン、３，３’，４，４’−テトラ（クミルパーオキシカルボニル）ベンゾフェノン、３，３’，４，４’−テトラ（ｐ−イソプロピルクミルパーオキシカルボニル）ベンゾフェノン、ジ−ｔ−ブチルジパーオキシイソフタレートなどの過酸化エステル系が好ましい。
【０１６２】
以上述べた活性剤に関しても、先の増感色素と同様、さらに、感光層の特性を改良するための様々な化学修飾を行うことも可能である。例えば、増感色素や、付加重合性不飽和化合物その他の活性剤パートとの結合、親水性部位の導入、相溶性向上、結晶析出抑制のための置換基導入、密着性を向上させる置換基導入、ポリマー化等の方法が利用できる。
【０１６３】
これらの活性剤化合物の使用法に関しても、先述の増感色素同様、感材の性能設計により適宜、任意に設定できる。例えば、２種以上併用することで、感光層への相溶性を高めることができる。活性剤化合物の使用量は通常多い方が感光性の点で有利であり、感光層成分１００重量部に対し、０．５〜８０重量部、好ましくは１〜５０重量部の範囲で用いることで十分な感光性が得られる。一方、例えばチタノセン化合物のように、活性剤自身が可視光に吸収を持つような場合、黄色灯、白色灯下での使用に際しては、５００ｎｍ付近の光によるカブリ性の点から活性剤の使用量は少ないことが好ましいが、本発明の増感色素との組み合わせにより活性剤化合物の使用量は６重量部以下、さらに１．９重量部以下、さらには１．４重量部以下にまで下げても十分な感光性を得ることができる。
【０１６４】
〔Ｂ．成分（ｉｉｉ）〕
本発明における第３の必須成分（ｉｉｉ）は上述の光開始系の光反応により生じた、活性種の作用により、その物理的または化学的特性が不可逆的に変化する化合物であり、成分（ｉｉｉ）は、このような性質を有するものであれば特に制限なく任意のものを使用でき、例えば、上述の開始系に挙げた化合物自身がそのような性質を有する場合も多い。光開始系から生成したラジカル、酸、および／または塩基により、変化する成分（ｉｉｉ）の特性としては、例えば、吸収スペクトル（色）、化学構造、分極率等の分子的な物性や、溶解性、強度、屈折率、流動性、粘着性、等の材料的な物性の変化を含む。
【０１６５】
例えば、成分（ｉｉｉ）として、ｐＨ指示薬のように、ｐＨによって吸収スペクトルの変化する化合物を用い、開始系から酸または塩基を発生させれば、露光部のみの色味をかえることができるが、このような組成物は画像形成材料として有用である。同様に、（ｉｉｉ）として、酸化・還元や求核付加反応により吸収スペクトルが変化する化合物を用いた場合、開始系から生成するラジカルによる酸化、還元等を引き起こし画像形成が可能である。そのような例は例えば、Ｊ．Ａｍ．Ｃｈｅｍ．Ｓｏｃ．，１０８，１２８（１９８６）、Ｊ．Ｉｍａｇｉｎｇ．Ｓｃｉ．，３０，２１５（１９８６）、Ｉｓｒａｅｌ．Ｊ．Ｃｈｅｍ．，２５，２６４（１９８６）、に開示されている。
【０１６６】
また、（ｉｉｉ）として付加重合または、重縮合可能な化合物を用い、開始系と組み合わせることにより、光硬化性樹脂、あるいはネガ型フォトポリマーを形成可能である。
【０１６７】
（ｉｉｉ）としては、ラジカル重合性化合物（エチレン性不飽和結合を有する化合物等）やカチオン重合性化合物（エポキシ化合物、ビニルエーテル化合物、メチロール化合物等）、アニオン重合性化合物（エポキシ化合物等）が用いられ、そのような例は、例えば、フォトポリマー懇話会編、フォトポリマーハンドブック、工業調査会（１９８９）や、高分子，４５，７８６（１９９６）．等に記載される。また、（ｉｉｉ）としてチオール化合物を用い、光ラジカル発生系と組み合わせた組成物も良く知られる。
【０１６８】
（ｉｉｉ）として酸分解性の化合物を用い、光酸発生剤と組み合わせることも有用である。例えば、側鎖や、主鎖が酸で分解する高分子を用い、光により溶解性や親疎水性等を変化させる材料は光分解型感光性樹脂、ポジ型フォトポリマーとして広く実用されている。そのような具体例は、例えば、ＡＣＳ．Ｓｙｍｐ．Ｓｅｒ．２４２，１１（１９８４）．、特開昭６０−３６２５号、ＵＳＰ−５１０２７７１号，同５２０６３１７号，同５２１２０４７号，特開平４−２６８５０号，特開平３−１９２１７３１号，特開昭６０−１０２４７号，特開昭６２−４０４５０号等が挙げられる。
【０１６９】
以下には本発明の目的の一つである、高感度な平版印刷版を得る目的に対し特に優れた成分（ｉｉｉ）である、付加重合可能な化合物に関しより詳しく述べる。
【０１７０】
（Ｂ−１）付加重合性化合物
本発明に使用される好ましい成分（ｉｉｉ）である、少なくとも一個のエチレン性不飽和二重結合を有する付加重合性化合物は、末端エチレン性不飽和結合を少なくとも１個、好ましくは２個以上有する化合物から選ばれる。このような化合物群は当該産業分野において広く知られるものであり、本発明においてはこれらを特に限定なく用いることができる。これらは、例えばモノマー、プレポリマー、すなわち２量体、３量体およびオリゴマー、またはそれらの混合物ならびにそれらの共重合体などの化学的形態をもつ。モノマーおよびその共重合体の例としては、不飽和カルボン酸（例えば、アクリル酸、メタクリル酸、イタコン酸、クロトン酸、イソクロトン酸、マレイン酸など）や、そのエステル類、アミド類が挙げられ、好ましくは、不飽和カルボン酸と脂肪族多価アルコール化合物とのエステル、不飽和カルボン酸と脂肪族多価アミン化合物とのアミド類が用いられる。また、ヒドロキシル基や、アミノ基、メルカプト基等の求核性置換基を有する不飽和カルボン酸エステル、アミド類と単官能もしくは多官能イソシアネート類、エポキシ類との付加反応物、単官能もしくは、多官能のカルボン酸との脱水縮合反応物等も好適に使用される。また、イソシアナト基や、エポキシ基、等の親電子性置換基を有する、不飽和カルボン酸エステル、アミド類と単官能もしくは多官能のアルコール類、アミン類、チオール類との付加反応物、ハロゲン基や、トシルオキシ基、等の脱離性置換基を有する、不飽和カルボン酸エステル、アミド類と単官能もしくは多官能のアルコール類、アミン類、チオール類との置換反応物も好適である。また、別の例として、上記の不飽和カルボン酸の代わりに、不飽和ホスホン酸、スチレン、ビニルエーテル等に置き換えた化合物群を使用することも可能である。
【０１７１】
脂肪族多価アルコール化合物と不飽和カルボン酸とのエステルのモノマーの具体例としては、アクリル酸エステルとして、エチレングリコールジアクリレート、トリエチレングリコールジアクリレート、１，３−ブタンジオールジアクリレート、テトラメチレングリコールジアクリレート、プロピレングリコールジアクリレート、ネオペンチルグリコールジアクリレート、トリメチロールプロパントリアクリレート、トリメチロールプロパントリ（アクリロイルオキシプロピル）エーテル、トリメチロールエタントリアクリレート、ヘキサンジオールジアクリレート、１，４−シクロヘキサンジオールジアクリレート、テトラエチレングリコールジアクリレート、ペンタエリスリトールジアクリレート、ペンタエリスリトールトリアクリレート、ペンタエリスリトールテトラアクリレート、ジペンタエリスリトールジアクリレート、ジペンタエリスリトールヘキサアクリレート、ソルビトールトリアクリレート、ソルビトールテトラアクリレート、ソルビトールペンタアクリレート、ソルビトールヘキサアクリレート、トリ（アクリロイルオキシエチル）イソシアヌレート、ポリエステルアクリレートオリゴマー等がある。
【０１７２】
メタクリル酸エステルとしては、テトラメチレングリコールジメタクリレート、トリエチレングリコールジメタクリレート、ネオペンチルグリコールジメタクリレート、トリメチロールプロパントリメタクリレート、トリメチロールエタントリメタクリレート、エチレングリコールジメタクリレート、１，３−ブタンジオールジメタクリレート、ヘキサンジオールジメタクリレート、ペンタエリスリトールジメタクリレート、ペンタエリスリトールトリメタクリレート、ペンタエリスリトールテトラメタクリレート、ジペンタエリスリトールジメタクリレート、ジペンタエリスリトールヘキサメタクリレート、ソルビトールトリメタクリレート、ソルビトールテトラメタクリレート、ビス〔ｐ−（３−メタクリルオキシ−２−ヒドロキシプロポキシ）フェニル〕ジメチルメタン、ビス−〔ｐ−（メタクリルオキシエトキシ）フェニル〕ジメチルメタン等がある。
【０１７３】
イタコン酸エステルとしては、エチレングリコールジイタコネート、プロピレングリコールジイタコネート、１，３−ブタンジオールジイタコネート、１，４−ブタンジオールジイタコネート、テトラメチレングリコールジイタコネート、ペンタエリスリトールジイタコネート、ソルビトールテトライタコネート等がある。
【０１７４】
クロトン酸エステルとしては、エチレングリコールジクロトネート、テトラメチレングリコールジクロトネート、ペンタエリスリトールジクロトネート、ソルビトールテトラジクロトネート等がある。
【０１７５】
イソクロトン酸エステルとしては、エチレングリコールジイソクロトネート、ペンタエリスリトールジイソクロトネート、ソルビトールテトライソクロトネート等がある。
【０１７６】
マレイン酸エステルとしては、エチレングリコールジマレート、トリエチレングリコールジマレート、ペンタエリスリトールジマレート、ソルビトールテトラマレート等がある。
【０１７７】
その他のエステルの例として、例えば、特公昭４６−２７９２６号、特公昭５１−４７３３４号、特開昭５７−１９６２３１号記載の脂肪族アルコール系エステル類や、特開昭５９−５２４０号、特開昭５９−５２４１号、特開平２−２２６１４９号記載の芳香族系骨格を有するもの、特開平１−１６５６１３号記載のアミノ基を含有するもの等も好適に用いられる。
【０１７８】
さらに、前述のエステルモノマーは混合物としても使用することができる。
【０１７９】
また、脂肪族多価アミン化合物と不飽和カルボン酸とのアミドのモノマーの具体例としては、メチレンビス−アクリルアミド、メチレンビス−メタクリルアミド、１，６−ヘキサメチレンビス−アクリルアミド、１，６−ヘキサメチレンビス−メタクリルアミド、ジエチレントリアミントリスアクリルアミド、キシリレンビスアクリルアミド、キシリレンビスメタクリルアミド等がある。
【０１８０】
その他の好ましいアミド系モノマーの例としては、特公昭５４−２１７２６号記載のシクロへキシレン構造を有すものを挙げることができる。
【０１８１】
また、イソシアネートと水酸基の付加反応を用いて製造されるウレタン系付加重合性化合物も好適であり、そのような具体例としては、例えば、特公昭４８−４１７０８号公報中に記載されている１分子に２個以上のイソシアネート基を有するポリイソシアネート化合物に、下記一般式（ＩＩＩ）で示される水酸基を含有するビニルモノマーを付加させた１分子中に２個以上の重合性ビニル基を含有するビニルウレタン化合物等が挙げられる。
【０１８２】
ＣＨ_２＝Ｃ（Ｒ）ＣＯＯＣＨ_２ＣＨ（Ｒ’）ＯＨ （ＩＩＩ）
【０１８３】
（ただし、ＲおよびＲ’はＨあるいはＣＨ_３を示す。）
【０１８４】
また、特開昭５１−３７１９３号、特公平２−３２２９３号、特公平２−１６７６５号に記載されているようなウレタンアクリレート類や、特公昭５８−４９８６０号、特公昭５６−１７６５４号、特公昭６２−３９４１７号、特公昭６２−３９４１８号記載のエチレンオキサイド系骨格を有するウレタン化合物類も好適である。
【０１８５】
さらに、特開昭６３−２７７６５３号、特開昭６３−２６０９０９号、特開平１−１０５２３８号に記載される、分子内にアミノ構造やスルフィド構造を有する付加重合性化合物類を用いることによっては、非常に感光スピードに優れた光重合性組成物を得ることができる。
【０１８６】
その他の例としては、特開昭４８−６４１８３号、特公昭４９−４３１９１号、特公昭５２−３０４９０号、各公報に記載されているようなポリエステルアクリレート類、エポキシ樹脂と（メタ）アクリル酸を反応させたエポキシアクリレート類等の多官能のアクリレートやメタクリレートを挙げることができる。また、特公昭４６−４３９４６号、特公平１−４０３３７号、特公平１−４０３３６号記載の特定の不飽和化合物や、特開平２−２５４９３号記載のビニルホスホン酸系化合物等も挙げることができる。また、ある場合には、特開昭６１−２２０４８号記載のペルフルオロアルキル基を含有する構造が好適に使用される。さらに日本接着協会誌 ｖｏｌ． ２０、Ｎｏ． ７、３００〜３０８ページ（１９８４年）に光硬化性モノマーおよびオリゴマーとして紹介されているものも使用することができる。
【０１８７】
これらの、付加重合性化合物について、どのような構造を用いるか、単独で使用するか併用するか、添加量はどうかといった、使用方法の詳細は、最終的な感材の性能設計にあわせて、任意に設定できる。例えば次のような観点から選択される。感光スピードの点では１分子あたりの不飽和基含量が多い構造が好ましく、多くの場合、２官能以上が好ましい。また、画像部すなわち硬化膜の強度を高くするためには、３官能以上のものが良く、さらに、異なる官能数・異なる重合性基（例えばアクリル酸エステル、メタクリル酸エステル、スチレン系化合物、ビニルエーテル系化合物）のものを併用することで、感光性と、強度を両方を調節する方法も有効である。大きな分子量の化合物や、疎水性の高い化合物は感光スピードや、膜強度に優れる反面、現像スピードや現像液中での析出といった点で好ましく無い場合がある。また、感光層中の他の成分（例えばバインダーポリマー、開始剤、着色剤等）との相溶性、分散性に対しても、付加重合化合物の選択・使用法は重要な要因であり、例えば、低純度化合物の使用や、２種以上の併用により相溶性を向上させることがある。また、支持体、オーバーコート層等の密着性を向上させる目的で特定の構造を選択することもあり得る。感光層中の付加重合性化合物の配合比に関しては、多い方が感度的に有利であるが、多すぎる場合には、好ましく無い相分離が生じたり、感光層の粘着性による製造工程上の問題（例えば、感材成分の転写、粘着に由来する製造不良）や、現像液からの析出が生じる等の問題を生じうる。これらの観点から、好ましい配合比は、多くの場合、組成物全成分に対して５〜８０重量％、好ましくは２５〜７５重量％である。また、これらは単独で用いても２種以上併用してもよい。そのほか、付加重合性化合物の使用法は、酸素に対する重合阻害の大小、解像度、かぶり性、屈折率変化、表面粘着性等の観点から適切な構造、配合、添加量を任意に選択でき、さらに場合によっては下塗り、上塗りといった層構成・塗布方法も実施しうる。
【０１８８】
〔バインダーポリマー〕
本発明の好ましい実施形態である、平版印刷版への適用に際しては、感光性組成物にさらにバインダーポリマーを使用することが好ましい。バインダーとしては線状有機高分子重合体を含有させることが好ましい。このような「線状有機高分子重合体」としては、どれを使用しても構わない。好ましくは水現像あるいは弱アルカリ水現像を可能とする水あるいは弱アルカリ水可溶性または膨潤性である線状有機高分子重合体が選択される。線状有機高分子重合体は、組成物の皮膜形成剤としてだけでなく、水、弱アルカリ水あるいは有機溶剤現像剤としての用途に応じて選択使用される。例えば、水可溶性有機高分子重合体を用いると水現像が可能になる。このような線状有機高分子重合体としては、側鎖にカルボン酸基を有する付加重合体、例えば特開昭５９−４４６１５号、特公昭５４−３４３２７号、特公昭５８−１２５７７号、特公昭５４−２５９５７号、特開昭５４−９２７２３号、特開昭５９−５３８３６号、特開昭５９−７１０４８号に記載されているもの、すなわち、メタクリル酸共重合体、アクリル酸共重合体、イタコン酸共重合体、クロトン酸共重合体、マレイン酸共重合体、部分エステル化マレイン酸共重合体等がある。また同様に側鎖にカルボン酸基を有する酸性セルロース誘導体がある。この他に水酸基を有する付加重合体に環状酸無水物を付加させたものなどが有用である。
【０１８９】
特にこれらの中で〔ベンジル（メタ）アクリレート／（メタ）アクリル酸／必要に応じてその他の付加重合性ビニルモノマー〕共重合体および〔アリル（メタ）アクリレート／（メタ）アクリル酸／必要に応じてその他の付加重合性ビニルモノマー〕共重合体は、膜強度、感度、現像性のバランスに優れており、好適である。
【０１９０】
また、特公平７−１２００４号、特公平７−１２００４１号、特公平７−１２００４２号、特公平８−１２４２４号、特開昭６３−２８７９４４号、特開昭６３−２８７９４７号、特開平１−２７１７４１号、特願平１０−１１６２３２号明細書等に記載される、酸基を含有するウレタン系バインダーポリマーは、非常に、強度に優れるので、耐刷性・低露光適性の点で有利である。
【０１９１】
また、特開平１１−１７１９０７号公報記載のアミド基を有するバインダーは優れた現像性と膜強度を併せもち、好適である。
【０１９２】
さらにこの他に水溶性線状有機高分子として、ポリビニルピロリドンやポリエチレンオキサイド等が有用である。また硬化皮膜の強度を上げるためにアルコール可溶性ナイロンや２，２−ビス−（４−ヒドロキシフェニル）−プロパンとエピクロロヒドリンのポリエーテル等も有用である。これらの線状有機高分子重合体は全組成物中に任意な量を混和させることができる。しかし９０重量％を超える場合には形成される画像強度等の点で好ましい結果を与えない。好ましくは３０〜８５重量％である。また光重合可能なエチレン性不飽和二重結合を有する化合物と線状有機高分子重合体は、重量比で１／９〜７／３の範囲とするのが好ましい。好ましい実施様態においてバインダーポリマーは実質的に水不要でアルカリに可溶なものが用いられる。そうすることで、現像液として、環境上好ましくない有機溶剤を用いないかもしくは非常に少ない使用量に制限できる。このような使用法においてはバインダーポリマーの酸価（ポリマー１ｇ当たりの酸含率を化学等量数で表したもの）と分子量は画像強度と現像性の観点から適宜選択される。好ましい酸価は、０．４〜３．０ｍｅｑ／ｇであり、好ましい分子量は重量平均分子量で３０００から５０万の範囲であり、より好ましくは、酸価が０．６〜２．０、分子量が１万から３０万の範囲である。
【０１９３】
〔Ｃ．その他の成分〕
本発明の感光性組成物には、さらにその用途、製造方法等に適したその他の成分を適宜添加することができる。以下、好ましい添加剤に関し例示する。
【０１９４】
（Ｃ１）共増感剤
ある種の添加剤（以後、共増感剤という）を用いることで、感度をさらに向上させることができる。これらの作用機構は明確ではないが、多くは次のような化学プロセスに基づくものと考えられる。即ち、先述の開始系の光吸収により開始される光反応と、それに引き続く付加重合反応の過程で生じる様々な中間活性種（ラジカル、過酸化物、酸化剤、還元剤等）と、共増感剤が反応し、新たな活性ラジカルを生成するものと推定される。これらは、大きくは、（ａ）還元されて活性ラジカルを生成しうるもの、（ｂ）酸化されて活性ラジカルを生成しうるもの、（ｃ）活性の低いラジカルと反応し、より活性の高いラジカルに変換するか、もしくは連鎖移動剤として作用するものに分類できるが、個々の化合物がこれらのどれに属するかに関しては、通説がない場合も多い。
【０１９５】
（ａ）還元されて活性ラジカルを生成する化合物
炭素−ハロゲン結合を有する化合物：還元的に炭素−ハロゲン結合が解裂し、活性ラジカルを発生すると考えられる。具体的には、例えば、トリハロメチル−ｓ−トリアジン類や、トリハロメチルオキサジアゾール類等が好適に使用できる。
【０１９６】
窒素−窒素結合を有する化合物：還元的に窒素−窒素結合が解裂し、活性ラジカルを発生すると考えられる。具体的にはヘキサアリールビイミダゾール類等が好適に使用される。
【０１９７】
酸素−酸素結合を有する化合物：還元的に酸素−酸素結合が解裂し、活性ラジカルを発生すると考えられる。具体的には、例えば、有機過酸化物類等が好適に使用される。
【０１９８】
オニウム化合物：還元的に炭素−ヘテロ結合や、酸素−窒素結合が解裂し、活性ラジカルを発生すると考えられる。具体的には例えば、ジアリールヨードニウム塩類、トリアリールスルホニウム塩類、Ｎ−アルコキシピリジニウム（アジニウム）塩類等が好適に使用される。
フェロセン、鉄アレーン錯体類：還元的に活性ラジカルを生成しうる。
【０１９９】
（ｂ）酸化されて活性ラジカルを生成する化合物
アルキルアート錯体：酸化的に炭素−ヘテロ結合が解裂し、活性ラジカルを生成すると考えられる。具体的には例えば、トリアリールアルキルボレート類が好適に使用される。
【０２００】
アルキルアミン化合物：酸化により窒素に隣接した炭素上のＣ−Ｘ結合が解裂し、活性ラジカルを生成するものと考えられる。Ｘとしては、水素原子、カルボキシル基、トリメチルシリル基、ベンジル基等が好適である。具体的には、例えば、エタノールアミン類、Ｎ−フェニルグリシン類、Ｎ−トリメチルシリルメチルアニリン類等が挙げられる。
【０２０１】
含硫黄、含錫化合物：上述のアミン類の窒素原子を硫黄原子、錫原子に置き換えたものが、同様の作用により活性ラジカルを生成しうる。また、Ｓ−Ｓ結合を有する化合物もＳ−Ｓ解裂による増感が知られる。
【０２０２】
α−置換メチルカルボニル化合物：酸化により、カルボニル−α炭素間の結合解裂により、活性ラジカルを生成しうる。また、カルボニルをオキシムエーテルに変換したものも同様の作用を示す。具体的には、２−アルキル−１−［４−（アルキルチオ）フェニル］−２−モルフォリノプロノン−１類、並びに、これらと、ヒドロキシアミン類とを反応したのち、Ｎ−ＯＨをエーテル化したオキシムエーテル類を挙げることができる。
【０２０３】
スルフィン酸塩類：還元的に活性ラジカルを生成しうる。具体的は、アリールスルフィン酸ナトリウム等を挙げることができる。
【０２０４】
ｃ）ラジカルと反応し高活性ラジカルに変換、もしくは連鎖移動剤として作用する化合物：例えば、分子内にＳＨ、ＰＨ、ＳｉＨ、ＧｅＨを有する化合物群が用いられる。これらは、低活性のラジカル種に水素供与して、ラジカルを生成するか、もしくは、酸化された後、脱プロトンすることによりラジカルを生成しうる。具体的には、例えば、２−メルカプトベンズイミダゾール類等が挙げられる。
【０２０５】
これらの共増感剤のより具体的な例は、例えば、特開平９−２３６９１３号公報中に、感度向上を目的とした添加剤として、多く記載されている。以下に、その一部を例示するが、本発明はこれらに限定されるものはない。−ＴＭＳはトリメチルシリル基である。
【０２０６】
【化４９】

【０２０７】
これらの共増感剤に関しても、先の増感色素と同様、さらに、感光層の特性を改良するための様々な化学修飾を行うことも可能である。例えば、増感色素や活性剤、付加重合性不飽和化合物その他のパートとの結合、親水性部位の導入、相溶性向上、結晶析出抑制のための置換基導入、密着性を向上させる置換基導入、ポリマー化等の方法が利用できる。
【０２０８】
これらの共増感剤は、単独でまたは２種以上併用して用いることができる。使用量はエチレン性不飽和二重結合を有する化合物１００重量部に対し０．０５〜１００重量部、好ましくは１〜８０重量部、さらに好ましくは３〜５０重量部の範囲が適当である。
【０２０９】
（Ｃ２）重合禁止剤
また、本発明においては以上の基本成分の他に感光性組成物の製造中あるいは保存中において重合可能なエチレン性不飽和二重結合を有する化合物の不要な熱重合を阻止するために少量の熱重合防止剤を添加することが望ましい。適当な熱重合防止剤としてはハイドロキノン、ｐ−メトキシフェノール、ジ−ｔ−ブチル−ｐ−クレゾール、ピロガロール、ｔ−ブチルカテコール、ベンゾキノン、４，４’−チオビス（３−メチル−６−ｔ−ブチルフェノール）、２，２’−メチレンビス（４−メチル−６−ｔ−ブチルフェノール）、Ｎ−ニトロソフェニルヒドロキシアミン第一セリウム塩等が挙げられる。熱重合防止剤の添加量は、全組成物の重量に対して約０．０１重量％〜約５重量％が好ましい。また必要に応じて、酸素による重合阻害を防止するためにベヘン酸やベヘン酸アミドのような高級脂肪酸誘導体等を添加して、塗布後の乾燥の過程で感光層の表面に偏在させてもよい。高級脂肪酸誘導体の添加量は、全組成物の約０．５重量％〜約１０重量％が好ましい。
【０２１０】
（Ｃ３）着色剤等
さらに、感光層の着色を目的として染料もしくは顔料を添加してもよい。これにより、印刷版としての、製版後の視認性や、画像濃度測定機適性といったいわゆる検版性を向上させることができる。着色剤としては、多くの染料は光重合系感光層の感度の低下を生じるので、着色剤としては、特に顔料の使用が好ましい。具体例としては例えばフタロシアニン系顔料、アゾ系顔料、カーボンブラック、酸化チタンなどの顔料、エチルバイオレット、クリスタルバイオレット、アゾ系染料、アントラキノン系染料、シアニン系染料などの染料がある。染料および顔料の添加量は全組成物の約０．５重量％〜約５重量％が好ましい。
【０２１１】
（Ｃ４）その他の添加剤
さらに、硬化皮膜の物性を改良するために無機充填剤や、その他可塑剤、感光層表面のインク着肉性を向上させうる感脂化剤等の公知の添加剤を加えてもよい。
【０２１２】
可塑剤としては例えばジオクチルフタレート、ジドデシルフタレート、トリエチレングリコールジカプリレート、ジメチルグリコールフタレート、トリクレジルホスフェート、ジオクチルアジペート、ジブチルセバケート、トリアセチルグリセリン等があり、結合剤を使用した場合、エチレン性不飽和二重結合を有する化合物と結合剤との合計重量に対し１０重量％以下添加することができる。
【０２１３】
また、後述する膜強度（耐刷性）向上を目的とした、現像後の加熱・露光の効果を強化するための、ＵＶ開始剤や、熱架橋剤等の添加もできる。
【０２１４】
その他、感光層と支持体との密着性向上や、未露光感光層の現像除去性を高めるための添加剤、中間層を設けることを可能である。例えば、ジアゾニウム構造を有する化合物や、ホスホン化合物、等、基板と比較的強い相互作用を有する化合物の添加や下塗りにより、密着性が向上し、耐刷性を高めることが可能であり、一方ポリアクリル酸や、ポリスルホン酸のような親水性ポリマーの添加や下塗りにより、非画像部の現像性が向上し、汚れ性の向上が可能となる。
【０２１５】
本発明の光重合性組成物を支持体上に塗布する際には種々の有機溶剤に溶かして使用に供される。ここで使用する溶媒としては、アセトン、メチルエチルケトン、シクロヘキサン、酢酸エチル、エチレンジクロライド、テトラヒドロフラン、トルエン、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、エチレングリコールジメチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、アセチルアセトン、シクロヘキサノン、ジアセトンアルコール、エチレングリコールモノメチルエーテルアセテート、エチレングリコールエチルエーテルアセテート、エチレングリコールモノイソプロピルエーテル、エチレングリコールモノブチルエーテルアセテート、３−メトキシプロパノール、メトキシメトキシエタノール、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールジメチルエーテル、ジエチレングリコールジエチルエーテル、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、３−メトキシプロピルアセテート、Ｎ，Ｎ−ジメチルホルムアミド、ジメチルスルホキシド、γ−ブチロラクトン、乳酸メチル、乳酸エチルなどがある。これらの溶媒は、単独あるいは混合して使用することができる。そして、塗布溶液中の固形分の濃度は、２〜５０重量％が適当である。
【０２１６】
感光層の支持体被覆量は、主に、感光層の感度、現像性、露光膜の強度・耐刷性に影響しうるもので、用途に応じ適宜選択することが望ましい。被覆量が少なすぎる場合には、耐刷性が十分でなくなる。一方多すぎる場合には、感度が下がり、露光に時間がかかる上、現像処理にもより長い時間を要するため好ましくない。本発明の主要な目的である走査露光用平版印刷版としては、その被覆量は乾燥後の重量で約０．１ｇ／ｍ^２〜約１０ｇ／ｍ^２の範囲が適当である。より好ましくは０．５〜５ｇ／ｍ^２である。
【０２１７】
〔支持体〕
本発明の主要な目的の一つである、平版印刷版を得るには上記感光層を、表面が親水性の支持体上に設けることが望ましい。親水性の支持体としては、従来公知の、平版印刷版に使用される親水性支持体を限定無く使用することができる。使用される支持体は寸度的に安定な板状物であることが好ましく、例えば、紙、プラスチック（例えば、ポリエチレン、ポリプロピレン、ポリスチレン等）がラミネートされた紙、金属板（例えば、アルミニウム、亜鉛、銅等）、プラスチックフィルム（例えば、二酢酸セルロース、三酢酸セルロース、プロピオン酸セルロース、酪酸セルロース、酢酸酪酸セルロース、硝酸セルロース、ポリエチレンテレフタレート、ポリエチレン、ポリスチレン、ポリプロピレン、ポリカーボネート、ポリビニルアセタール等）、上記のような金属がラミネートもしくは蒸着された紙もしくはプラスチックフィルム等が含まれ、これらの表面に対し、必要に応じ親水性の付与や、強度向上、等の目的で適切な公知の物理的、化学的処理を施しても良い。
【０２１８】
特に、好ましい支持体としては、紙、ポリエステルフィルムまたはアルミニウム板が挙げられ、その中でも寸法安定性がよく、比較的安価であり、必要に応じた表面処理により親水性や強度に優れた表面を提供できるアルミニウム板は特に好ましい。また、特公昭４８−１８３２７号に記載されているようなポリエチレンテレフタレートフィルム上にアルミニウムシートが結合された複合体シートも好ましい。
【０２１９】
好適なアルミニウム板は、純アルミニウム板およびアルミニウムを主成分とし、微量の異元素を含む合金板であり、更にはアルミニウムがラミネートまたは蒸着されたプラスチックフィルムでもよい。アルミニウム合金に含まれる異元素には、ケイ素、鉄、マンガン、銅、マグネシウム、クロム、亜鉛、ビスマス、ニッケル、チタン等がある。合金中の異元素の含有量は高々１０重量％以下である。本発明において特に好適なアルミニウムは、純アルミニウムであるが、完全に純粋なアルミニウムは精錬技術上製造が困難であるので、僅かに異元素を含有するものでもよい。このように本発明に適用されるアルミニウム板は、その組成が特定されるものではなく、従来より公知公用の素材のアルミニウム板を適宜に利用することができる。本発明で用いられるアルミニウム板の厚みはおよそ０．１ｍｍ〜０．６ｍｍ程度、好ましくは０．１５ｍｍ〜０．４ｍｍ、特に好ましくは０．２ｍｍ〜０．３ｍｍである。
【０２２０】
また金属、特にアルミニウムの表面を有する支持体の場合には、粗面化（砂目立て）処理、珪酸ソーダ、弗化ジルコニウム酸カリウム、燐酸塩等の水溶液への浸漬処理、あるいは陽極酸化処理などの表面処理がなされていることが好ましい。
【０２２１】
アルミニウム板の表面の粗面化処理は、種々の方法により行われるが、例えば、機械的に粗面化する方法、電気化学的に表面を溶解粗面化する方法および化学的に表面を選択溶解させる方法により行われる。機械的方法としては、ボール研磨法、ブラシ研磨法、ブラスト研磨法、バフ研磨法等の公知の方法を用いることができる。また、電気化学的な粗面化法としては塩酸、硝酸等の電解液中で交流または直流により行う方法がある。また、特開昭５４−６３９０２号に開示されているように両者を組み合わせた方法も利用することができる。また、アルミニウム板を粗面化するに先立ち、所望により、表面の圧延油を除去するために、例えば、界面活性剤、有機溶剤またはアルカリ性水溶液等による脱脂処理が行われる。
【０２２２】
さらに、粗面化したのちに珪酸ナトリウム水溶液に浸漬処理されたアルミニウム板が好ましく使用できる。特公昭４７−５１２５号に記載されているようにアルミニウム板を陽極酸化処理したのちに、アルカリ金属珪酸塩の水溶液に浸漬処理したものが好適に使用される。陽極酸化処理は、例えば、燐酸、クロム酸、硫酸、硼酸等の無機酸、もしくは蓚酸、スルファミン酸等の有機酸またはそれらの塩の水溶液または非水溶液の単独または二種以上を組み合わせた電解液中でアルミニウム板を陽極として電流を流すことにより実施される。
【０２２３】
また、米国特許第３６５８６６２号に記載されているようなシリケート電着も有効である。
【０２２４】
さらに、特公昭４６−２７４８１号、特開昭５２−５８６０２号、特開昭５２−３０５０３号に開示されているような電解グレインを施した支持体と、上記陽極酸化処理および珪酸ソーダ処理を組合せた表面処理も有用である。
【０２２５】
また、特開昭５６−２８８９３号に開示されているような機械的粗面化、化学的エッチング、電解グレイン、陽極酸化処理さらに珪酸ソーダ処理を順に行ったものも好適である。
【０２２６】
さらに、これらの処理を行った後に、水溶性の樹脂、例えばポリビニルホスホン酸、スルホン酸基を側鎖に有する重合体および共重合体、ポリアクリル酸、水溶性金属塩（例えば硼酸亜鉛）もしくは、黄色染料、アミン塩等を下塗りしたものも好適である。
【０２２７】
さらに特開平７−１５４９８３号公報に開示されているようなラジカルによって付加反応を起こし得る官能基を共有結合させたゾル−ゲル処理基板も好適に用いられる。
【０２２８】
その他好ましい例として、任意の支持体上に表面層として耐水性の親水性層を設けたものも挙げることができる。このような表面層としては例えばＵＳ３０５５２９５号や、特開昭５６−１３１６８号記載の無機顔料と結着剤とからなる層、特開平９−８０７４４記載の親水性膨潤層、特表平８−５０７７２７記載の酸化チタン、ポリビニルアルコール、珪酸類からなるゾルゲル膜等を挙げることができる。
【０２２９】
これらの親水化処理は、支持体の表面を親水性とするために施される以外に、その上に設けられる光重合性組成物の有害な反応を防ぐため、かつ感光層の密着性の向上等のために施されるものである。
【０２３０】
〔保護層〕
本発明の望ましい様態である、走査露光用平版印刷版においては、通常、露光を大気中で行うため、光重合性組成物の層の上に、さらに、保護層を設けることが好ましい。保護層は、感光層中で露光により生じる画像形成反応を阻害する大気中に存在する酸素や、塩基性物質等の低分子化合物の感光層への混入を防止し、大気中での露光を可能とする。従って、このような保護層に望まれる特性は、酸素等の低分子化合物の透過性が低いことであり、さらに、露光に用いる光の透過は実質阻害せず、感光層との密着性に優れ、かつ、露光後の現像工程で容易に除去できることが望ましい。このような、保護層に関する工夫が従来よりなされており、米国特許第３、４５８、３１１号、特開昭５５−４９７２９号に詳しく記載されている。保護層に使用できる材料としては例えば、比較的、結晶性に優れた水溶性高分子化合物を用いることがよく、具体的には、ポリビニルアルコール、ポリビニルピロリドン、酸性セルロース類、ゼラチン、アラビアゴム、ポリアクリル酸などのような水溶性ポリマーが知られているが、これらの内、ポリビニルアルコールを主成分として用いることが、酸素遮断性、現像除去性といった基本特性的にもっとも良好な結果を与える。
【０２３１】
保護層に使用するポリビニルアルコールは、必要な酸素遮断性と水溶性を有するための、未置換ビニルアルコール単位を含有する限り、一部がエステル、エーテル、およびアセタールで置換されていても良い。また、同様に一部が他の共重合成分を有していても良い。ポリビニルアルコールの具体例としては７１〜１００モル％加水分解され、分子量が重量平均分子量で３００から２４００の範囲のものを挙げることができる。具体的には、株式会社クラレ製のＰＶＡ−１０５、ＰＶＡ−１１０、ＰＶＡ−１１７、ＰＶＡ−１１７Ｈ、ＰＶＡ−１２０、ＰＶＡ−１２４、ＰＶＡ−１２４Ｈ、ＰＶＡ−ＣＳ、ＰＶＡ−ＣＳＴ、ＰＶＡ−ＨＣ、ＰＶＡ−２０３、ＰＶＡ−２０４、ＰＶＡ−２０５、ＰＶＡ−２１０、ＰＶＡ−２１７、ＰＶＡ−２２０、ＰＶＡ−２２４、ＰＶＡ−２１７ＥＥ、ＰＶＡ−２１７Ｅ、ＰＶＡ−２２０Ｅ、ＰＶＡ−２２４Ｅ、ＰＶＡ−４０５、ＰＶＡ−４２０、ＰＶＡ−６１３、Ｌ−８等が挙げられる。
【０２３２】
保護層の成分（ＰＶＡの選択、添加剤の使用）、塗布量等は、酸素遮断性・現像除去性の他、カブリ性や密着性・耐傷性を考慮して選択される。一般には使用するＰＶＡの加水分解率が高い程（保護層中の未置換ビニルアルコール単位含率が高い程）、膜厚が厚い程酸素遮断性が高くなり、感度の点で有利である。しかしながら、極端に酸素遮断性を高めると、製造時・生保存時に不要な重合反応が生じたり、また画像露光時に、不要なカブリ、画線の太りが生じたりという問題を生じる。また、画像部との密着性や、耐傷性も版の取り扱い上極めて重要である。即ち、水溶性ポリマーからなる親水性の層を親油性の重合層に積層すると、接着力不足による膜剥離が発生しやすく、剥離部分が酸素の重合阻害により膜硬化不良などの欠陥を引き起こす。これに対し、これら２層間の接着性を改良すべく種々の提案がなされている。例えば米国特許第２９２５０１号、米国特許第４４５６３号には、主にポリビニルアルコールからなる親水性ポリマー中に、アクリル系エマルジョンまたは水不溶性ビニルピロリドン−ビニルアセテート共重合体などを２０〜６０重量％混合し、重合層の上に積層することにより、十分な接着性が得られることが記載されている。本発明における保護層に対しては、これらの公知の技術をいずれも適用することができる。このような保護層の塗布方法については、例えば米国特許第３，４５８，３１１号、特開昭５５−４９７２９号に詳しく記載されている。
【０２３３】
さらに、保護層に他の機能を付与することもできる。例えば、露光に使う、３５０ｎｍから４５０ｎｍの光の透過性に優れ、かつ５００ｎｍ以上の光を効率良く吸収しうる、着色剤（水溶性染料等）の添加により、感度低下を起こすことなく、セーフライト適性をさらに高めることができる。
【０２３４】
本発明の光重合性組成物を用いた感光材料を画像形成材料として使用する際には、通常、画像露光したのち、現像液で感光層の未露光部を除去し、画像を得る。これらの光重合性組成物を平版印刷版の作成に使用する際の好ましい現像液としては、特公昭５７−７４２７号に記載されているような現像液が挙げられ、ケイ酸ナトリウム、ケイ酸カリウム、水酸化ナトリウム、水酸化カリウム、水酸化リチウム、第三リン酸ナトリウム、第二リン酸ナトリウム、第三リン酸アンモニウム、第二リン酸アンモニウム、メタケイ酸ナトリウム、重炭酸ナトリウム、アンモニア水などのような無機アルカリ剤やモノエタノールアミンまたはジエタノールアミンなどのような有機アルカリ剤の水溶液が適当である。このようなアルカリ溶液の濃度が０．１〜１０重量％、好ましくは０．５〜５重量％になるように添加される。
【０２３５】
また、このようなアルカリ性水溶液には、必要に応じて界面活性剤やベンジルアルコール、２−フェノキシエタノール、２−ブトキシエタノールのような有機溶媒を少量含むことができる。例えば、米国特許第３３７５１７１号および同第３６１５４８０号に記載されているものを挙げることができる。
【０２３６】
さらに、特開昭５０−２６６０１号、同５８−５４３４１号、特公昭５６−３９４６４号、同５６−４２８６０号の各公報に記載されている現像液も優れている。
【０２３７】
特に好ましい現像液としては、特開２００２−２０２６１６号公報に記載の、下記式で表される非イオン性化合物を含有し、ｐＨが１１．５〜１２．８であり、かつ３〜３０ｍＳ／ｃｍの電導度を有する現像液が挙げられる。
【０２３８】
Ａ−Ｗ （ＩＶ）
【０２３９】
式中、ＡはＡ−ＨのｌｏｇＰが１．５以上の疎水性有機基を表し、ＷはＷ−ＨのｌｏｇＰが１．０未満の非イオン性の親水性有機基を表す。
ｌｏｇＰとは、Ｃ．Ｈａｎｓｃｈ，Ａ．Ｌｅｏ，“Ｓｕｂｓｔｉｔｕｅｎｔ Ｃｏｎｓｔａｎｔｓ ｆｏｒ Ｃｏｒｒｅｌａｔｉｏｎ Ａｎａｌｙｓｉｓ ｉｎ Ｃｈｅｍｉｓｔｒｙ ａｎｄ Ｂｉｏｌｏｇｙ”，Ｊ．Ｗｉｌｅ＆Ｓｏｎｓ，１９７９． 記載の疎水性パラメータとして一般的に使用されるものであり、目的とする分子（Ａ−Ｈ及びＷ−Ｈ）のオクタノール／水２層系に対して、各層に分配される割合から算出した平衡濃度比Ｐの対数として定義される。
ここでは、式（ＩＶ）中のＡ，Ｗの各基を特定する指標として使用しており、Ａ，Ｗ各有機基に便宜的に水素原子結合させた、Ａ−Ｈ、Ｗ−Ｈ構造に対して、Ａ．Ｋ．Ｇｈｏｓｅ、ｅｔ．ａｌ．Ｊ． Ｃｏｍｐｕｔ．Ｃｈｅｍ． ９，８０（１９８８）．記載の方法に基づき、既知データより計算し、求めたものである。
【０２４０】
具体的には、構造としては、有機基Ａ、Ｗは互いに異なり、上述のｌｏｇＰを満足する、一価の有機残基を表す。より好ましくは、互いに同一または異なり、水素原子、ハロゲン原子、置換基を有していても良く、かつ、不飽和結合を含んでいても良い炭化水素基、ヘテロ環基、ヒドロキシル基、置換オキシ基、メルカプト基、置換チオ基、アミノ基、置換アミノ基、置換カルボニル基、カルボキシラート基、スルホ基、スルホナト基、置換スルフィニル基、置換スルホニル基、ホスホノ基、置換ホスホノ基、ホスホナト基、置換ホスホナト基 、シアノ基、ニトロ基を表す。
【０２４１】
上記置換基を有していてもよく、かつ、不飽和結合を含んでいても良い炭化水素基としては、アルキル基、置換アルキル基、アリール基、置換アリール基、アルケニル基、置換アルケニル基、アルキニル基及び置換アルキニル基があげられる。
【０２４２】
アルキル基としては炭素原子数が１から２０までの直鎖状、分岐状、または環状のアルキル基を挙げることができ、その具体例としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、ヘキサデシル基、オクタデシル基、エイコシル基、イソプロピル基、イソブチル基、ｓ−ブチル基、ｔ−ブチル基、イソペンチル基、ネオペンチル基、１−メチルブチル基、イソヘキシル基、２−エチルヘキシル基、２−メチルヘキシル基、シクロヘキシル基、シクロペンチル基、２−ノルボルニル基を挙げることができる。これらの中では、炭素原子数１から１２までの直鎖状、炭素原子数３から１２までの分岐状、ならびに炭素原子数５から１０までの環状のアルキル基がより好ましい。
【０２４３】
置換アルキル基は置換基とアルキレン基との結合により構成され、置換基としては、水素を除く一価の非金属原子団が用いられ、好ましい例としては、ハロゲン原子（−Ｆ、−Ｂｒ、−Ｃｌ、−Ｉ）、ヒドロキシル基、アルコキシ基、アリーロキシ基、メルカプト基、アルキルチオ基、アリールチオ基、アルキルジチオ基、アリールジチオ基、アミノ基、Ｎ−アルキルアミノ基、Ｎ，Ｎ−ジアルキルアミノ基、Ｎ−アリールアミノ基、Ｎ，Ｎ−ジアリールアミノ基、Ｎ−アルキル−Ｎ−アリールアミノ基、アシルオキシ基、カルバモイルオキシ基、Ｎ−アルキルカルバモイルオキシ基、Ｎ−アリールカルバモイルオキシ基、Ｎ，Ｎ−ジアルキルカルバモイルオキシ基、Ｎ，Ｎ−ジアリールカルバモイルオキシ基、Ｎ−アルキル−Ｎ−アリールカルバモイルオキシ基、アルキルスルホキシ基、アリールスルホキシ基、アシルチオ基、
【０２４４】
アシルアミノ基、Ｎ−アルキルアシルアミノ基、Ｎ−アリールアシルアミノ基、ウレイド基、Ｎ′−アルキルウレイド基、Ｎ′，Ｎ′−ジアルキルウレイド基、Ｎ′−アリールウレイド基、Ｎ′，Ｎ′−ジアリールウレイド基、Ｎ′−アルキル−Ｎ′−アリールウレイド基、Ｎ−アルキルウレイド基、Ｎ−アリールウレイド基、Ｎ′−アルキル−Ｎ−アルキルウレイド基、Ｎ′−アルキル−Ｎ−アリールウレイド基、Ｎ′，Ｎ′−ジアルキル−Ｎ−アルキルウレイド基、Ｎ′，Ｎ′−ジアルキル−Ｎ−アリールウレイド基、Ｎ′−アリール−Ｎ−アルキルウレイド基、Ｎ′−アリール−Ｎ−アリールウレイド基、Ｎ′，Ｎ′−ジアリール−Ｎ−アルキルウレイド基、Ｎ′，Ｎ′−ジアリール−Ｎ−アリールウレイド基、Ｎ′−アルキル−Ｎ′−アリール−Ｎ−アルキルウレイド基、Ｎ′−アルキル−Ｎ′−アリール−Ｎ−アリールウレイド基、
【０２４５】
アルコキシカルボニルアミノ基、アリーロキシカルボニルアミノ基、Ｎ−アルキル−Ｎ−アルコキシカルボニルアミノ基、Ｎ−アルキル−Ｎ−アリーロキシカルボニルアミノ基、Ｎ−アリール−Ｎ−アルコキシカルボニルアミノ基、Ｎ−アリール−Ｎ−アリーロキシカルボニルアミノ基、ホルミル基、アシル基、カルボキシル基及びその共役塩基基（以下、カルボキシラートと称す）、アルコキシカルボニル基、アリーロキシカルボニル基、カルバモイル基、Ｎ−アルキルカルバモイル基、Ｎ，Ｎ−ジアルキルカルバモイル基、Ｎ−アリールカルバモイル基、Ｎ，Ｎ−ジアリールカルバモイル基、Ｎ−アルキル−Ｎ−アリールカルバモイル基、アルキルスルフィニル基、アリールスルフィニル基、アルキルスルホニル基、
【０２４６】
アリールスルホニル基、スルホ基（−ＳＯ_３Ｈ）及びその共役塩基基（以下、スルホナト基と称す）、アルコキシスルホニル基、アリーロキシスルホニル基、スルフィナモイル基、Ｎ−アルキルスルフィナモイル基、Ｎ，Ｎ−ジアルキルスルフィナモイル基、Ｎ−アリールスルフィナモイル基、Ｎ，Ｎ−ジアリールスルフィナモイル基、Ｎ−アルキル−Ｎ−アリールスルフィナモイル基、スルファモイル基、Ｎ−アルキルスルファモイル基、Ｎ，Ｎ−ジアルキルスルファモイル基、Ｎ−アリールスルファモイル基、Ｎ，Ｎ−ジアリールスルファモイル基、Ｎ−アルキル−Ｎ−アリールスルファモイル基、
【０２４７】
Ｎ−アシルスルファモイル基及びその共役塩基基、Ｎ−アルキルスルホニルスルファモイル基（−ＳＯ_２ＮＨＳＯ_２（ａｌｋｙｌ））及びその共役塩基基、Ｎ−アリールスルホニルスルファモイル基（−ＳＯ_２ＮＨＳＯ_２（ａｌｌｙｌ））及びその共役塩基基、Ｎ−アルキルスルホニルカルバモイル基（−ＣＯＮＨＳＯ_２（ａｌｋｙｌ））及びその共役塩基基、Ｎ−アリールスルホニルカルバモイル基（−ＣＯＮＨＳＯ_２（ａｌｌｙｌ））及びその共役塩基基、アルコキシシリル基（−Ｓｉ（Ｏａｌｋｙｌ）_３）、アリーロキシシリル基（−Ｓｉ（Ｏａｌｌｙｌ）_３）、ヒドロキシシリル基（−Ｓｉ（ＯＨ）_３）及びその共役塩基基、
【０２４８】
ホスホノ基（−ＰＯ_３Ｈ_２）及びその共役塩基基（以下、ホスホナト基と称す）、ジアルキルホスホノ基（−ＰＯ_３（ａｌｋｙｌ）_２）、ジアリールホスホノ基（−ＰＯ_３（ａｒｙｌ）_２）、アルキルアリールホスホノ基（−ＰＯ_３（ａｌｋｙｌ）（ａｒｙｌ））、モノアルキルホスホノ基（−ＰＯ_３Ｈ（ａｌｋｙｌ））及びその共役塩基基（以後、アルキルホスホナト基と称す）、モノアリールホスホノ基（−ＰＯ_３Ｈ（ａｒｙｌ））及びその共役塩基基（以後、アリールホスホナト基と称す）、ホスホノオキシ基（−ＯＰＯ_３Ｈ_２）及びその共役塩基基（以後、ホスホナトオキシ基と称す）、ジアルキルホスホノオキシ基（−ＯＰＯ_３（ａｌｋｙｌ）_２）、ジアリールホスホノオキシ基（−ＯＰＯ_３（ａｒｙｌ）_２）、アルキルアリールホスホノオキシ基（−ＯＰＯ_３（ａｌｋｙｌ）（ａｒｙｌ））、モノアルキルホスホノオキシ基（−ＯＰＯ_３Ｈ（ａｌｋｙｌ））及びその共役塩基基（以後、アルキルホスホナトオキシ基と称す）、モノアリールホスホノオキシ基（−ＯＰＯ_３Ｈ（ａｒｙｌ））及びその共役塩基基（以後、アリールホスホナトオキシ基と称す）、シアノ基、ニトロ基、アリール基、アルケニル基、アルキニル基が挙げられる。
【０２４９】
これらの置換基における、アルキル基の具体例としては、前述のアルキル基が挙げられ、アリール基の具体例としては、フェニル基、ビフェニル基、ナフチル基、トリル基、キシリル基、メシチル基、クメニル基、フルオロフェニル基、クロロフェニル基、ブロモフェニル基、クロロメチルフェニル基、ヒドロキシフェニル基、メトキシフェニル基、エトキシフェニル基、フェノキシフェニル基、アセトキシフェニル基、ベンゾイロキシフェニル基、メチルチオフェニル基、フェニルチオフェニル基、メチルアミノフェニル基、ジメチルアミノフェニル基、アセチルアミノフェニル基、カルボキシフェニル基、メトキシカルボニルフェニル基、エトキシカルボニルフェニル基、フェノキシカルボニルフェニル基、Ｎ−フェニルカルバモイルフェニル基、フェニル基、ニトロフェニル基、シアノフェニル基、スルホフェニル基、スルホナトフェニル基、ホスホノフェニル基、ホスホナトフェニル基などを挙げることができる。また、アルケニル基の例としては、ビニル基、１−プロペニル基、１−ブテニル基、シンナミル基、２−クロロ−１−エテニル基等が挙げられ、アルキニル基の例としては、エチニル基、１−プロピニル基、１−ブチニル基、トリメチルシリルエチニル基、フェニルエチニル基等が挙げられる。
【０２５０】
上述のアシル基（Ｒ^４ＣＯ−）としては、Ｒ^４が水素原子及び上記のアルキル基、アリール基、アルケニル基、アルキニル基を挙げることができる。一方、置換アルキル基におけるアルキレン基としては、前述の炭素数１から２０までのアルキル基上の水素原子のいずれか１つを除し、２価の有機残基としたものを挙げることができ、好ましくは炭素原子数１から１２までの直鎖状、炭素原子数３から１２までの分岐状ならびに炭素原子数５から１０までの環状のアルキレン基を挙げることができる。好ましい置換アルキル基の具体例としては、クロロメチル基、ブロモメチル基、２−クロロエチル基、トリフルオロメチル基、メトキシメチル基、メトキシエトキシエチル基、アリルオキシメチル基、フェノキシメチル基、メチルチオメチル基、トリルチオメチル基、エチルアミノエチル基、ジエチルアミノプロピル基、モルホリノプロピル基、アセチルオキシメチル基、ベンゾイルオキシメチル基、Ｎ−シクロヘキシルカルバモイルオキシエチル基、Ｎ−フェニルカルバモイルオキシエチル基、アセチルアミノエチル基、Ｎ−メチルベンゾイルアミノプロピル基、２−オキソエチル基、２−オキソプロピル基、カルボキシプロピル基、メトキシカルボニルエチル基、メトキシカルボニルメチル基、メトキシカルボニルブチル基、エトキシカルボニルメチル基、ブトキシカルボニルメチル基、アリルオキシカルボニルメチル基、ベンジルオキシカルボニルメチル基、メトキシカルボニルフェニルメチル基、トリクロロメチルカルボニルメチル基、アリルオキシカルボニルブチル基、クロロフェノキシカルボニルメチル基、カルバモイルメチル基、Ｎ−メチルカルバモイルエチル基、Ｎ，Ｎ−ジプロピルカルバモイルメチル基、Ｎ−（メトキシフェニル）カルバモイルエチル基、Ｎ−メチル−Ｎ−（スルホフェニル）カルバモイルメチル基、スルホプロピル基、スルホブチル基、スルホナトブチル基、スルファモイルブチル基、Ｎ−エチルスルファモイルメチル基、Ｎ，Ｎ−ジプロピルスルファモイルプロピル基、Ｎ−トリルスルファモイルプロピル基、Ｎ−メチル−Ｎ−（ホスホノフェニル）スルファモイルオクチル基、
【０２５１】
【化５０】

【０２５２】
ホスホノブチル基、ホスホナトヘキシル基、ジエチルホスホノブチル基、ジフェニルホスホノプロピル基、メチルホスホノブチル基、メチルホスホナトブチル基、トリルホスホノヘキシル基、トリルホスホナトヘキシル基、ホスホノオキシプロピル基、ホスホナトオキシブチル基、ベンジル基、フェネチル基、α−メチルベンジル基、１−メチル−１−フェニルエチル基、ｐ−メチルベンジル基、シンナミル基、アリル基、１−プロペニルメチル基、２−ブテニル基、２−メチルアリル基、２−メチルプロペニルメチル基、２−プロピニル基、２−ブチニル基、３−ブチニル基、等を挙げることができる。
【０２５３】
アリール基としては１個から３個のベンゼン環が縮合環を形成したもの、ベンゼン環と５員不飽和環が縮合環を形成したものを挙げることができ、具体例としては、フェニル基、ナフチル基、アントリル基、フェナントリル基、インデニル基、アセナブテニル基、フルオレニル基等を挙げることができ、これらのなかでは、フェニル基、ナフチル基がより好ましい。
【０２５４】
置換アリール基は、置換基がアリール基に結合したものであり、前述のアリール基の環形成炭素原子上に置換基として、水素を除く一価の非金属原子団を有するものが用いられる。好ましい置換基の例としては前述のアルキル基、置換アルキル基、ならびに、先に置換アルキル基における置換基として示したものを挙げることができる。これらの、置換アリール基の好ましい具体例としては、ビフェニル基、トリル基、キシリル基、メシチル基、クメニル基、クロロフェニル基、ブロモフェニル基、フルオロフェニル基、クロロメチルフェニル基、トリフルオロメチルフェニル基、ヒドロキシフェニル基、メトキシフェニル基、メトキシエトキシフェニル基、アリルオキシフェニル基、フェノキシフェニル基、メチルチオフェニル基、トリルチオフェニル基、フェニルチオフェニル基、エチルアミノフェニル基、ジエチルアミノフェニル基、モルホリノフェニル基、アセチルオキシフェニル基、ベンゾイルオキシフェニル基、Ｎ−シクロヘキシルカルバモイルオキシフェニル基、Ｎ−フェニルカルバモイルオキシフェニル基、アセチルアミノフェニル基、Ｎ−メチルベンゾイルアミノフェニル基、カルボキシフェニル基、メトキシカルボニルフェニル基、アリルオキシカルボニルフェニル基、クロロフェノキシカルボニルフェニル基、カルバモイルフェニル基、Ｎ−メチルカルバモイルフェニル基、Ｎ，Ｎ−ジプロピルカルバモイルフェニル基、Ｎ−（メトキシフェニル）カルバモイルフェニル基、Ｎ−メチル−Ｎ−（スルホフェニル）カルバモイルフェニル基、
【０２５５】
スルホフェニル基、スルホナトフェニル基、スルファモイルフェニル基、Ｎ−エチルスルファモイルフェニル基、Ｎ，Ｎ−ジプロピルスルファモイルフェニル基、Ｎ−トリルスルファモイルフェニル基、Ｎ−メチル−Ｎ−（ホスホノフェニル）スルファモイルフェニル基、ホスホノフェニル基、ホスホナトフェニル基、ジエチルホスホノフェニル基、ジフェニルホスホノフェニル基、メチルホスホノフェニル基、メチルホスホナトフェニル基、トリルホスホノフェニル基、トリルホスホナトフェニル基、アリル基、１−プロペニルメチル基、２−ブテニル基、２−メチルアリルフェニル基、２−メチルプロペニルフェニル基、２−プロピニルフェニル基、２−ブチニルフェニル基、３−ブチニルフェニル基等を挙げることができる。
【０２５６】
アルケニル基としては、上述のものを挙げることができる。置換アルケニル基は、置換基がアルケニル基の水素原子と置き換わり結合したものであり、この置換基としては、上述の置換アルキル基における置換基が用いられ、一方アルケニル基は上述のアルケニル基を用いることができる。好ましい置換アルケニル基の例としては
【０２５７】
【化５１】

【０２５８】
等を挙げることができる。アルキニル基としては、上述のものを挙げることができる。置換アルキニル基は、置換基がアルキニル基の水素原子と置き換わり、結合したものであり、この置換基としては、上述の置換アルキル基における置換基が用いられ、一方アルキニル基は上述のアルキニル基を用いることができる。
【０２５９】
ヘテロ環基とは、ヘテロ環上の水素を１つ除した一価の基及びこの一価の基からさらに水素を１つ除し、上述の置換アルキル基における置換基が結合してできた一価の基（置換ヘテロ環基）である。好ましいヘテロ環の例としては、
【０２６０】
【化５２】

【０２６１】
【化５３】

【０２６２】
等を挙げることができる。
置換オキシ基（Ｒ^５Ｏ−）としては、Ｒ^５が水素を除く一価の非金属原子団であるものを用いることができる。好ましい置換オキシ基としては、アルコキシ基、アリーロキシ基、アシルオキシ基、カルバモイルオキシ基、Ｎ−アルキルカルバモイルオキシ基、Ｎ−アリールカルバモイルオキシ基、Ｎ，Ｎ−ジアルキルカルバモイルオキシ基、Ｎ，Ｎ−ジアリールカルバモイルオキシ基、Ｎ−アルキル−Ｎ−アリールカルバモイルオキシ基、アルキルスルホキシ基、アリールスルホキシ基、ホスホノオキシ基、ホスホナトオキシ基等を挙げることができる。これらにおけるアルキル基、ならびにアリール基としては前述のアルキル基、置換アルキル基ならびに、アリール基、置換アリール基として示したものを挙げることができる。
【０２６３】
また、アシルオキシ基におけるアシル基（Ｒ^６ＣＯ−）としては、Ｒ^６が、前述のアルキル基、置換アルキル基、アリール基ならびに置換アリール基のものを挙げることができる。これらの置換基の中では、アルコキシ基、アリーロキシ基、アシルオキシ基、アリールスルホキシ基等がより好ましい。好ましい置換オキシ基の具体例としては、メトキシ基、エトキシ基、プロピルオキシ基、イソプロピルオキシ基、ブチルオキシ基、ペンチルオキシ基、ヘキシルオキシ基、ドデシルオキシ基、ベンジルオキシ基、アリルオキシ基、フェネチルオキシ基、カルボキシエチルオキシ基、メトキシカルボニルエチルオキシ基、エトキシカルボニルエチルオキシ基、メトキシエトキシ基、フェノキシエトキシ基、メトキシエトキシエトキシ基、エトキシエトキシエトキシ基、モルホリノエトキシ基、モルホリノプロピルオキシ基、アリロキシエトキシエトキシ基、フェノキシ基、トリルオキシ基、キシリルオキシ基、メシチルオキシ基、クメニルオキシ基、メトキシフェニルオキシ基、エトキシフェニルオキシ基、クロロフェニルオキシ基、ブロモフェニルオキシ基、アセチルオキシ基、ベンゾイルオキシ基、ナフチルオキシ基、フェニルスルホニルオキシ基、ホスホノオキシ基、ホスホナトオキシ等が挙げられる。
【０２６４】
置換チオ基（Ｒ^７Ｓ−）としてはＲ^７が水素を除く一価の非金属原子団のものを使用できる。好ましい置換チオ基の例としては、アルキルチオ基、アリールチオ基、アルキルジチオ基、アリールジチオ基、アシルチオ基を挙げることができる。これらにおけるアルキル基、アリール基としては前述のアルキル基、置換アルキル基、ならびにアリール基、置換アリール基として示したものを挙げることができ、アシルチオ基におけるアシル基（Ｒ^６ＣＯ−）のＲ^６は前述のとおりである。これらの中ではアルキルチオ基、ならびにアリールチオ基がより好ましい。好ましい置換チオ基の具体例としては、メチルチオ基、エチルチオ基、フェニルチオ基、エトキシエチルチオ基、カルボキシエチルチオ基、メトキシカルボニルチオ基等が挙げられる。
【０２６５】
置換アミノ基（Ｒ^８ＮＨ−，（Ｒ^９）（Ｒ^１０）Ｎ−）としては、Ｒ^８，Ｒ^９，Ｒ^１０が水素を除く一価の非金属原子団のものを使用できる。置換アミノ基の好ましい例としては、Ｎ−アルキルアミノ基、Ｎ，Ｎ−ジアルキルアミノ基、Ｎ−アリールアミノ基、Ｎ，Ｎ−ジアリールアミノ基、Ｎ−アルキル−Ｎ−アリールアミノ基、アシルアミノ基、Ｎ−アルキルアシルアミノ基、Ｎ−アリールアシルアミノ基、ウレイド基、Ｎ′−アルキルウレイド基、Ｎ′，Ｎ′−ジアルキルウレイド基、Ｎ′−アリールウレイド基、Ｎ′，Ｎ′−ジアリールウレイド基、Ｎ′−アルキル−Ｎ′−アリールウレイド基、Ｎ−アルキルウレイド基、Ｎ−アリールウレイド基、Ｎ′−アルキル−Ｎ−アルキルウレイド基、Ｎ′−アルキル−Ｎ−アリールウレイド基、Ｎ′，Ｎ′−ジアルキル−Ｎ−アルキルウレイド基、Ｎ′，Ｎ′−ジアルキル−Ｎ−アリールウレイド基、Ｎ′−アリール−Ｎ−アルキルウレイド基、Ｎ′−アリール−Ｎ−アリールウレイド基、Ｎ′，Ｎ′−ジアリール−Ｎ−アルキルウレイド基、Ｎ′，Ｎ′−ジアリール−Ｎ−アリールウレイド基、Ｎ′−アルキル−Ｎ′−アリール−Ｎ−アルキルウレイド基、Ｎ′−アルキル−Ｎ′−アリール−Ｎ−アリールウレイド基、アルコキシカルボニルアミノ基、アリーロキシカルボニルアミノ基、Ｎ−アルキル−Ｎ−アルコキシカルボニルアミノ基、Ｎ−アルキル−Ｎ−アリーロキシカルボニルアミノ基、Ｎ−アリール−Ｎ−アルコキシカルボニルアミノ基、Ｎ−アリール−Ｎ−アリーロキシカルボニルアミノ基が挙げられる。これらにおけるアルキル基、アリール基としては前述のアルキル基、置換アルキル基、ならびにアリール基、置換アリール基として示したものを挙げることができ、アシルアミノ基、Ｎ−アルキルアシルアミノ基、Ｎ−アリールアシルアミノ基におけるアシル基（Ｒ^６ＣＯ−）のＲ^６は前述のとおりである。これらの内、より好ましいものとしては、Ｎ−アルキルアミノ基、Ｎ，Ｎ−ジアルキルアミノ基、Ｎ−アリールアミノ基、アシルアミノ基等が挙げられる。好ましい置換アミノ基の具体例としては、メチルアミノ基、エチルアミノ基、ジエチルアミノ基、モルホリノ基、ピペリジノ基、ピロリジノ基、フェニルアミノ基、ベンゾイルアミノ基、アセチルアミノ基等が挙げられる。
【０２６６】
置換カルボニル基（Ｒ^１１−ＣＯ−）としては、Ｒ^１１が一価の非金属原子団のものを使用できる。置換カルボニル基の好ましい例としては、ホルミル基、アシル基、カルボキシル基、アルコキシカルボニル基、アリーロキシカルボニル基、カルバモイル基、Ｎ−アルキルカルバモイル基、Ｎ，Ｎ−ジアルキルカルバモイル基、Ｎ−アリールカルバモイル基、Ｎ，Ｎ−ジアリールカルバモイル基、Ｎ−アルキル−Ｎ−アリールカルバモイル基等が挙げられる。これらにおけるアルキル基、アリール基としては前述のアルキル基、置換アルキル基、ならびにアリール基、置換アリール基として示したものを挙げることができる。これらの内、より好ましい置換基としては、ホルミル基、アシル基、カルボキシル基、アルコキシカルボニル基、アリーロキシカルボニル基、カルバモイル基、Ｎ−アルキルカルバモイル基、Ｎ，Ｎ−ジアルキルカルバモイル基、Ｎ−アリールカルバモイル基等が挙げられ、更により好ましいものとしては、ホルミル基、アシル基、アルコキシカルボニル基ならびにアリーロキシカルボニル基が挙げられる。好ましい置換基の具体例としては、ホルミル基、アセチル基、ベンゾイル基、カルボキシル基、メトキシカルボニル基、アリルオキシカルボニル基、Ｎ−メチルカルバモイル基、Ｎ−フェニルカルバモイル基、Ｎ，Ｎ−ジエチルカルバモイル基、モルホリノカルボニル基等が挙げられる。
【０２６７】
置換スルフィニル基（Ｒ^１２−ＳＯ−）としてはＲ^１２が一価の非金属原子団のものを使用できる。好ましい例としては、アルキルスルフィニル基、アリールスルフィニル基、スルフィナモイル基、Ｎ−アルキルスルフィナモイル基、Ｎ，Ｎ−ジアルキルスルフィナモイル基、Ｎ−アリールスルフィナモイル基、Ｎ，Ｎ−ジアリールスルフィナモイル基、Ｎ−アルキル−Ｎ−アリールスルフィナモイル基が挙げられる。これらにおけるアルキル基、アリール基としては、前述のアルキル基、置換アルキル基、ならびにアリール基、置換アリール基として示したものを挙げることができる。これらの内、より好ましい例としてはアルキルスルフィニル基、アリールスルフィニル基等が挙げられる。このような置換スルフィニル基の具体例としては、へキシルスルフィニル基、ベンジルスルフィニル基、トリルスルフィニル基等が挙げられる。
【０２６８】
置換スルホニル基（Ｒ^１３−ＳＯ_２−）としては、Ｒ^１３が一価の非金属原子団のものを使用できる。より好ましい例としては、アルキルスルホニル基、アリールスルホニル基を挙げることができる。これらにおけるアルキル基、アリール基としては前述のアルキル基、置換アルキル基、ならびにアリール基、置換アリール基として示したものを挙げることができる。このような、置換スルホニル基の具体例としては、ブチルスルホニル基、クロロフェニルスルホニル基等が挙げられる。
【０２６９】
スルホナト基（−ＳＯ_３−）は前述のとおり、スルホ基（−ＳＯ_３Ｈ）の共役塩基陰イオン基を意味し、通常は対陽イオンと共に使用されるのが好ましい。このような対陽イオンとしては、一般に知られるもの、すなわち、種々のオニウム類（アンモニウム類、スルホニウム類、ホスホニウム類、ヨードニウム類、アジニウム類等）、ならびに金属イオン類（Ｎａ^＋、Ｋ^＋、Ｃａ^２＋、Ｚｎ^２＋等）が挙げられる。
【０２７０】
カルボキシラート基（−ＣＯ_２−）は前述のとおり、カルボキシル基（ＣＯ_２Ｈ）の共役塩基陰イオン基を意味し、通常は対陽イオンと共に使用されるのが好ましい。このような対陽イオンとしては、一般に知られるもの、すなわち、種々のオニウム類（アンモニウム類、スルホニウム類、ホスホニウム類、ヨードニウム類、アジニウム類等）、ならびに金属イオン類（Ｎａ^＋、Ｋ^＋、Ｃａ^２＋、Ｚｎ^２＋等）が挙げられる。
【０２７１】
置換ホスホノ基とはホスホノ基上の水酸基の一つもしくは二つが他の有機オキソ基によって置換されたものを意味し、好ましい例としては、前述のジアルキルホスホノ基、ジアリールホスホノ基、アルキルアリールホスホノ基、モノアルキルホスホノ基、モノアリールホスホノ基が挙げられる。これらの中ではジアルキルホスホノ基、ならびにジアリールホスホノ基がより好ましい。このような具体例としては、ジエチルホスホノ基、ジブチルホスホノ基、ジフェニルホスホノ基等が挙げられる。
【０２７２】
ホスホナト基（−ＰＯ_３ ^２−、−ＰＯ_３Ｈ⁻）とは前述のとおり、ホスホノ基（−ＰＯ_３Ｈ_２）の、酸第一解離もしくは、酸第二解離に由来する共役塩基陰イオン基を意味する。通常は対陽イオンと共に使用されるのが好ましい。このような対陽イオンとしては、一般に知られるもの、すなわち、種々のオニウム類（アンモニウム類、スルホニウム類、ホスホニウム類、ヨードニウム類：アジニウム類、等）、ならびに金属イオン類（Ｎａ^＋、Ｋ^＋、Ｃａ^２＋、Ｚｎ^２＋等）が挙げられる。
【０２７３】
置換ホスホナト基とは前述の置換ホスホノ基の内、水酸基を一つ有機オキソ基に置換したものの共役塩基陰イオン基であり、具体例としては、前述のモノアルキルホスホノ基（−ＰＯ_３Ｈ（ａｌｋｙｌ））、モノアリールホスホノ基（−ＰＯ_３Ｈ（ａｒｙｌ））の共役塩基を挙げることができる。通常は対陽イオンと共に使用されるのが好ましい。このような対陽イオンとしては、一般に知られるもの、すなわち、種々のオニウム類（アンモニウム類、スルホニウム類、ホスホニウム類、ヨードニウム類、アジニウム類、等）、ならびに金属イオン類（Ｎａ^＋、Ｋ^＋、Ｃａ^２＋、Ｚｎ^２＋等）が挙げられる。
【０２７４】
前記式（ＩＶ）中、Ａ及びＷの各構造は、より好ましくは、Ａが芳香族を含
有する有機基、Ｗがポリオキシアルキレン基を含有する非イオン性の有機基である。
【０２７５】
なお、Ａ−ＨおよびＷ−Ｈの具体例を以下に示す。
【０２７６】
【化５４】

【０２７７】
【化５５】

【０２７８】
また、前記一般式（ＩＶ）の非イオン性化合物の具体例を以下に示す。
【０２７９】
【化５６】

【０２８０】
【化５７】

【０２８１】
【化５８】

【０２８２】
前記式（ＩＶ）の非イオン性化合物として、さらに好ましいものとしては、
下記式（ＩＶ−Ａ）または（ＩＶ−Ｂ）で示されるものである。
【０２８３】
【化５９】

【０２８４】
上記式中、Ｒ_１０、Ｒ_２０は、Ｈまたは炭素数１〜１００の炭化水素基であり、ｎ、ｍは０〜１００の整数（ただし、ｎ及びｍは同時に０ではない）である。炭化水素基としては、アルキル基、アリール基、アラルキル基等が挙げられ、さらにこれらの炭化水素基がエーテル結合、エステル結合またはアミド結合で結合したものも含む。
より好ましいＲ_１０、Ｒ_２０としては、Ｈまたは炭素数１〜１００の直鎖または分岐鎖アルキル基が挙げられる。また、Ｒ_１０、Ｒ_２０は基：Ｒ_３０−Ｘ−（Ｒ_３０は炭素数１〜１００の直鎖または分岐鎖アルキル基であり、Ｘは−Ｏ−、−ＯＣＯ−、−ＣＯＯ−、−ＮＨＣＯ−、または−ＣＯＮＨ−を表す）を表してもよい。
更に好ましくはＲ_１０、Ｒ_２０は水素原子、炭素数１〜１０の直鎖または分岐鎖アルキル基または基：Ｒ_３０−Ｘ−（Ｒ_３０は炭素数１〜１０の直鎖または分岐鎖アルキル基であり、Ｘは−Ｏ−、−ＯＣＯ−、−ＣＯＯ−、−ＮＨＣＯ−、または−ＣＯＮＨ−）である。
【０２８５】
一般式（ＩＶ−Ａ）で表される化合物としては、ポリオキシエチレンフェニルエーテル、ポリオキシエチレンメチルフェニルエーテル、ポリオキシエチレンオクチルフェニルエーテル、ポリオキシエチレンノニルフェニルエーテル等が挙げられる。
一般式（ＩＶ−Ｂ）で表される化合物としては、ポリオキシエチレンナフチルエーテル、ポリオキシエチレンメチルナフチルエーテル、ポリオキシエチレンオクチルナフチルエーテル、ポリオキシエチレンノニルナフチルエーテル等が挙げられる。
【０２８６】
前記一般式（ＩＶ−Ａ）および（ＩＶ−Ｂ）の化合物において、ポリオキシエチレン鎖の繰り返し単位数は、好ましくは３〜５０、より好ましくは５〜３０である。ポリオキシプロピレン鎖の繰り返し単位数は、好ましくは０〜１０、より好ましくは０〜５である。ポリオキシエチレン部とポリオキシプロピレン部はランダムでもブロックの共重合体でもよい。
前記一般式（ＩＶ−Ａ）および（ＩＶ−Ｂ）で示されるノニオン芳香族エーテル系活性剤は、単独または２種類以上を組み合わせて使用される。
【０２８７】
本発明において、前記一般式（ＩＶ）で示される非イオン性化合物は、現像液中０．１〜１５質量％、好ましくは１．０〜８．０質量％添加することが効果的である。
ここで添加量が０．１質量％以上であると、現像性低下および感光層成分の溶解性が向上し、１５質量％以下であると、印刷版の耐刷性が低下しない。
【０２８８】
その他、本発明の平版印刷版用原版の製版プロセスとしては、必要に応じ、露光前、露光中、露光から現像までの間に、全面を加熱しても良い。このような加熱により、感光層中の画像形成反応が促進され、感度や耐刷性の向上や、感度の安定化といった利点が生じ得る。さらに、画像強度・耐刷性の向上を目的として、現像後の画像に対し、全面後加熱もしくは、全面露光を行うことも有効である。通常現像前の加熱は１５０℃以下の穏和な条件で行うことが好ましい。１５０℃以下であると、非画像部にかぶりの問題が生じない。現像後の加熱には非常に強い条件を利用する。通常は２００〜５００℃の範囲である。２００℃以上であると十分な画像強化作用が得られ、５００℃以下の場合には支持体の劣化、画像部の熱分解といった問題が生じない。
【０２８９】
本発明による走査露光平版印刷版の露光方法は、公知の方法を制限なく用いることができる。望ましい、光源の波長は３５０ｎｍから４５０ｎｍであり、具体的にはＩｎＧａＮ系半導体レーザが好適である。露光機構は、内面ドラム方式、外面ドラム方式、フラットベッド方式等の何れでも良い。また、本発明の感光層成分は、高い水溶性のものを使用することで、中性の水や弱アルカリ水に可溶とすることもできるが、このような構成の平版印刷版は印刷機上に装填後、機上で露光−現像といった方式を行うこともできる。
【０２９０】
３５０〜４５０ｎｍの入手可能なレーザー光源としては以下のものを利用することができる。
【０２９１】
ガスレーザーとして、Ａｒイオンレーザー（３６４ｎｍ、３５１ｎｍ、１０ｍＷ〜１Ｗ）、Ｋｒイオンレーザー（３５６ｎｍ、３５１ｎｍ、１０ｍＷ〜１Ｗ）、Ｈｅ−Ｃｄレーザー（４４１ｎｍ、３２５ｎｍ、１ｍＷ〜１００ｍＷ）、
固体レーザーとして、Ｎｄ：ＹＡＧ（ＹＶＯ_４）とＳＨＧ結晶×２回の組み合わせ（３５５ｎｍ、５ｍＷ〜１Ｗ）、Ｃｒ：ＬｉＳＡＦとＳＨＧ結晶の組み合わせ（４３０ｎｍ、１０ｍＷ）、
半導体レーザー系として、ＫＮｂＯ_３リング共振器（４３０ｎｍ、３０ｍＷ）、導波型波長変換素子とＡｌＧａＡｓ、ＩｎＧａＡｓ半導体の組み合わせ（３８０ｎｍ〜４５０ｎｍ、５ｍＷ〜１００ｍＷ）、導波型波長変換素子とＡｌＧａＩｎＰ、ＡｌＧａＡｓ半導体の組み合わせ（３００ｎｍ〜３５０ｎｍ、５ｍＷ〜１００ｍＷ）、ＡｌＧａＩｎＮ（３５０ｎｍ〜４５０ｎｍ、５ｍＷ〜３０ｍＷ）
その他、パルスレーザーとしてＮ_２レーザー（３３７ｎｍ、パルス０．１〜１０ｍＪ）、ＸｅＦ（３５１ｎｍ、パルス１０〜２５０ｍＪ）
【０２９２】
特にこの中でＡｌＧａＩｎＮ半導体レーザー（市販ＩｎＧａＮ系半導体レーザー４００〜４１０ｎｍ、５〜３０ｍＷ）が波長特性、コストの面で好適である。
【０２９３】
また走査露光方式の平版印刷版露光装置としては、露光機構として内面ドラム方式、外面ドラム方式、フラットベッド方式があり、光源としては上記光源の中でパルスレーザー以外のもの全てを利用することができる。現実的には感材感度と製版時間の関係で、以下の露光装置が特に好ましい。
【０２９４】
・内面ドラム方式でガスレーザーあるいは固体レーザー光源を１つ使用するシングルビーム露光装置
・フラットベッド方式で半導体レーザーを多数（１０個以上）使用したマルチビームの露光装置
・外面ドラム方式で半導体レーザーを多数（１０個以上）使用したマルチビームの露光装置
【０２９５】
以上のようなレーザー直描型の平版印刷版においては、一般に感材感度Ｘ（Ｊ／ｃｍ^２）、感材の露光面積Ｓ（ｃｍ^２）、レーザー光源１個のパワーｑ（Ｗ）、レーザー本数ｎ、全露光時間ｔ（ｓ）との間に式（ｅｑ１）が成立する。
Ｘ・Ｓ＝ｎ・ｑ・ｔ − （ｅｑ１）
【０２９６】
ｉ）内面ドラム（シングルビーム）方式の場合
レーザー回転数ｆ（ラジアン／ｓ）、感材の副走査長Ｌｘ（ｃｍ）、解像度Ｚ（ドット／ｃｍ）、全露光時間ｔ（ｓ）の間には一般的に式（ｅｑ２）が成立する。
ｆ・Ｚ・ｔ＝Ｌｘ − （ｅｑ２）
ｉｉ）外面ドラム（マルチビーム）方式の場合
ドラム回転数Ｆ（ラジアン／ｓ）、感材の副走査長Ｌｘ（ｃｍ）、解像度Ｚ（ドット／ｃｍ）、全露光時間ｔ（ｓ）、ビーム数（ｎ）の間には一般的に式（ｅｑ３）が成立する。
Ｆ・Ｚ・ｎ・ｔ＝Ｌｘ − （ｅｑ３）
ｉｉｉ）フラットベッド（マルチビーム）方式の場合
ポリゴンミラーの回転数Ｈ（ラジアン／ｓ）、感材の副走査長Ｌｘ（ｃｍ）、解像度Ｚ（ドット／ｃｍ）、全露光時間ｔ（ｓ）、ビーム数（ｎ）の間には一般的に式（ｅｑ４）が成立する。
Ｈ・Ｚ・ｎ・ｔ＝Ｌｘ − （ｅｑ４）
【０２９７】
実際の印刷版に要求される解像度（２５６０ｄｐｉ）、版サイズ（Ａ１／Ｂ１、副走査長４２ｉｎｃｈ）、２０枚／１時間程度の露光条件と本発明の感光性組成物の感光特性（感光波長、感度：約０．１ｍＪ／ｃｍ^２）を上記式に代入することで、本発明の感材においては半導体レーザーのマルチビーム露光方式との組み合わせがより好ましいことが理解できる。さらに操作性、コスト等を掛け合わせることにより外面ドラム方式の半導体レーザーマルチビーム露光装置との組み合わせが最も好ましいことになる。
【０２９８】
また、本発明による光重合性組成物に対するその他の露光光線としては、超高圧、高圧、中圧、低圧の各水銀灯、ケミカルランプ、カーボンアーク灯、キセノン灯、メタルハライド灯、可視および紫外の各種レーザーランプ、蛍光灯、タングステン灯、太陽光等も使用できる。また、本発明による光重合性組成物の用途としては走査露光用平版印刷版の他、広く、光硬化樹脂の用途として知られるものに制限なく適用できる。例えば、必要に応じカチオン重合性化合物と併用した液状の光重合性組成物に適用することで、高感度な光造形用材料が得られる。また、光重合にともなう、屈折率の変化を利用し、ホログラム材料とすることもできる。光重合に伴う、表面の粘着性の変化を利用して様々な転写材料（剥離感材、トナー現像感材等）にも応用できる。マイクロカプセルの光硬化にも適用できる。フォトレジスト等の電子材料製造、インクや塗料、接着剤等の光硬化樹脂材料にも応用できる。
【０２９９】
【実施例】
以下、実施例によって本発明を説明するが、本発明はこれらの実施例に限定されるものではない。
（合成例）Ｄ５の合成
ジフェニルアミノベンゾアルデヒド３５ｇ、ピペリジン２．０ｇをメタノール５００ｍｌに溶解させた後、１時間還流しながら攪拌した。次に３−エチル−２−チオキソ−４−オキサゾリジオン２０ｇを加え４時間還流しながら攪拌した。反応終了後、室温まで放冷すると、黄色結晶が析出した。析出した結晶を濾過し、メタノール１０００ｍｌに加え１時間攪拌した。結晶を濾過、乾燥することで下記化合物（Ｄ５’）を４８ｇ得た（収率９１％）。^１Ｈ−ＮＭＲにより同定を行った。
【０３００】
【化６０】

次に硝酸銀１．７ｇをアセトニトリル２０ｍｌに溶解させた後、上記Ｄ５’で表される色素前駆体２．０ｇを加え０．５時間攪拌した。次に、３−ブロモ−１−プロピルアミン ３．２ｇを滴下し３０分攪拌後、トリエチルアミン２．５ｇを滴下し、さらに１．５時間攪拌した。反応終了後、アセトンを３０ｍｌ加え、析出した銀塩をセライトを用いて濾別、濾液を水 ２００ｍｌに投入した。析出した結晶を濾取後、メタノール中でリスラリーし、下記化合物（Ｄ５”）を２．３ｇ得た（収率９３％）。^１Ｈ−ＮＭＲにより同定を行った。
【０３０１】
【化６１】

次に、アセトン３０ｍｌに、上記Ｄ５”で表される化合物０．５ｇと４−ｔ−ブチルピリジン０．１７ｇを溶解させた後、６０℃に加熱し、８時間攪拌した。反応終了後、アセトンを減圧溜去し、得られた反応物をメタノール６０ｍｌと水５０ｍｌに溶解させ、さらにメタノール６０ｍｌと水５０ｍｌに溶解させたＫＰＦ_６を混合し、析出してきたＤ５の粗生成物を濾過し、メタノールでリスラリーすることで下記化合物（Ｄ５）を０．５３ｇ得た（２ステップ収率７５％）。^１Ｈ−ＮＭＲにより同定を行った。
【化６２】

【０３０２】
〔実施例１〜１７、比較例１〜６〕
（支持体の調製）
厚さ０．３ｍｍのアルミニウム板を１０重量％水酸化ナトリウムに６０℃で２５秒間浸漬してエッチングした後、流水で水洗後２０重量％硝酸で中和洗浄し、次いで水洗した。これを正弦波の交番波形電流を用いて１重量％硝酸水溶液中で３００クーロン／ｄｍ^２の陽極時電気量で電解粗面化処理を行った。引き続いて１重量％水酸化ナトリウム水溶液中に４０℃で５秒間浸漬後３０重量％の硫酸水溶液中に浸漬し、６０℃で４０秒間デスマット処理した後、２０重量％硫酸水溶液中、電流密度２Ａ／ｄｍ^２において、陽極酸化皮膜の厚さが２．７ｇ／ｍ^２になるように、２分間陽極酸化処理した。その表面粗さを測定したところ、０．３μｍ （ＪＩＳＢ０６０１によるＲａ表示）であった。
【０３０３】
このように処理された基板の裏面に下記のゾル−ゲル反応液をバーコーターで塗布し１００℃で１分間乾燥し、乾燥後の塗布量が７０ｍｇ／ｍ^２のバックコート層を設けた支持体を作成した。
【０３０４】
ゾル−ゲル反応液
テトラエチルシリケート ５０重量部
水 ２０重量部
メタノール １５重量部
リン酸 ０．０５重量部
【０３０５】
上記成分を混合、撹拌すると約５分で発熱が開始した。６０分間反応させた後、以下に示す液を加えることによりバックコート塗布液を調製した。
【０３０６】

【０３０７】
（感光層の調製）
このように処理されたアルミニウム板上に、下記組成の光重合性組成物を乾燥塗布量が１．０〜２．０ｇ／ｍ^２となるように塗布し、８０℃２分間乾燥させ感光層を形成させた。
【０３０８】

【０３０９】
（保護層の調製）
この感光層上にポリビニルアルコール（ケン化度９８モル％、重合度５５０）の３重量％の水溶液を乾燥塗布重量が２ｇ／ｍ^２となるように塗布し、１００℃で２分間乾燥した。
【０３１０】
（感度の評価）
このように得られた感材上に、富士写真フイルム（株）製の富士ステップガイド（△Ｄ＝０．１５で不連続的に透過光学濃度が変化するグレースケール）を密着させ、光学フィルターを通したキセノンランプにより既知の露光エネルギーとなるように露光を行った。その後、下記組成の現像液に２５℃、１０秒間浸漬し、現像を行い、画像が完全に除去される最高の段数を読み、その露光エネルギー量を求め、感度を算出した（単位、ｍＪ／ｃｍ^２）。エネルギー量が小さい程、高感度である。短波半導体レーザへの露光適性を見積もる目的で、光学フィルターとしてケンコーＢＰ−４０を用い、４００ｎｍのモノクロミックな光で露光を行った。結果を表１に示す。
【０３１１】

【０３１２】
【化６３】

【０３１３】
【表１】

【０３１４】
表１から明らかなように、本発明の開始系を用いた実施例１〜１７は実用上十分な高感度を示す。本発明の開始系を用いない比較例１〜５との比較により、本発明の開始系は増感色素と活性剤の併用によって高感度を発現しうることが明らかである。さらに、実施例１〜５からは本発明の活性剤は、その増感機構によらず広い範囲のものが適用できることがわかる。さらに、実施例１１と比較例６との比較により、本発明の増感色素が、高感度を示す構造上の特徴が、増感色素の励起酸化電位より低い還元電位を有するアクセプター構造にあることが示唆されるが、これは予期し得ぬ発見であった。
【０３１５】
〔実施例１８〜２６、比較例７〕
以下の手順で平版印刷版を作製し、印刷性能を評価した。結果を表２に示す。
【０３１６】
「支持体の前処理」
厚さ０．３ｍｍの材質１Ｓのアルミニウム板を８号ナイロンブラシと８００メッシュのパミストンの水懸濁液を用い、その表面を砂目立てした後、よく水で洗浄した。１０重量％水酸化ナトリウムに７０℃で６０秒間浸漬してエッチングした後、流水で水洗後２０重量％硝酸で中和洗浄し、次いで水洗した。これをＶ_Ａ＝１２．７Ｖの条件で、正弦波の交番波形電流を用いて１重量％硝酸水溶液中で３００クーロン／ｄｍ^２の陽極時電気量で電解粗面化処理を行った。その表面粗さを測定したところ、０．４５μｍ （ＪＩＳ Ｂ０６０１によるＲａ表示）であった。
【０３１７】
「支持体表面の親水化処理」
上記の支持体を、３号ケイ酸ソーダ（ＳｉＯ_２＝２８〜３０％、Ｎａ_２Ｏ＝９〜１０％、Ｆｅ＝０．０２％以下）の２．５重量％、ｐＨ＝１１．２、７０℃の水溶液に１３秒浸漬し、続いて水洗した。表面の蛍光Ｘ線分析により求めた、Ｓｉ元素量から、表面シリケート量は１０ｍｇ／ｍ^２と求められた。
【０３１８】
「中間層の塗設」
上記の親水化支持体表面上に、フェニルホスホン酸の塗布量が２０ｍｇ／ｍ^２となるようにように、下記の（Ａ）の組成の塗布液を調製し、ホイラーにて１８０ｒｐｍの条件で塗布後、８０℃で３０秒間乾燥させた。
【０３１９】
（中間層塗布液Ａ）
フェニルホスホン酸 ０．０７ｇ〜１．４ｇ
メタノール ２００ｇ
【０３２０】
「感光層の塗設」
上記中間層を設けた支持体上に、下記組成の感光液を調製し、塗布量が１．０〜２．０ｇ／ｍ^２になるように、ホイラーで塗布し、１００℃で１分間乾燥させた。
【０３２１】
（感光液）

【０３２２】
「保護層の塗設」
この感光層上にポリビニルアルコール（ケン化度９８モル％、重合度５５０）の３重量％の水溶液を乾燥塗布重量が２ｇ／ｍ^２となるように塗布し、１００℃で２分間乾燥した。
【０３２３】
「平版印刷版用原版の露光」
上記のようにして得られた平版印刷版用原版を、光源として４００ｎｍの単色光を用い、版面露光エネルギー密度２００μＪ／ｃｍ^２となるように露光パワーを調節し、ベタ画像露光および１７５線／インチ、１％刻みで１から９９％となる網点画像露光を行った。
【０３２４】
「現像／製版」
富士写真フイルム（株）製自動現像機ＬＰ−８５０に所定の現像液（表２中に記載）と富士写真フイルム（株）製フィニッシャーＦＰ−２Ｗをそれぞれ仕込み現像液温度３０℃、現像時間１８秒の条件で露光済みの版を現像／製版し、平版印刷版を得た。
【０３２５】
「耐刷性試験」
印刷機としてローランド社製Ｒ２０１を使用し、インキとして大日本インキ社製ＧＥＯＳ−Ｇ（Ｎ）を使用した。ベタ画像部の印刷物を観察し、画像がかすれはじめた枚数によって耐刷性を調べた。数字が多いほど耐刷性が良い。
【０３２６】
「網点耐刷性強制試験」
印刷機としてローランド社製Ｒ２０１を使用し、インキとして大日本インキ社製ＧＥＯＳ−Ｇ（Ｎ）を使用した。印刷開始から５０００枚目に富士写真フイルム（株）製ＰＳプレートクリーナーＣＬ−２を印刷用スポンジにしみこませ、網点部を拭き、版面のインキを洗浄した。その後、１０，０００枚印刷を行い、印刷物における網点の版飛びの有無を目視で観察した。
【０３２７】
「汚れ性試験」
印刷機としてローランド社製Ｒ２０１を使用し、インキとして大日本インキ社製ＧＥＯＳ−Ｇ（Ｓ）を使用した。非画像部（未露光部）の印刷物を観察し、汚れ性を評価した。
【０３２８】
（表２中の付加重合性化合物）
（Ｍ−１）
ペンタエルスリトールテトラアクリレート
（新中村化学工業（株）製；ＮＫエステルＡ−ＴＭＭＴ）
（Ｍ−２）
グリセリンジメタクリレートヘキサメチレンジイソシアネートウレタンプレポリマー
（共栄社化学（株）製；ＵＡ１０１Ｈ）
【０３２９】
（表２中のバインダーポリマー）
（Ｂ−１）
アリルメタクリレート／メタクリル酸／Ｎ−イソプロピルアクリルアミド（共重合モル比６６／１３／２１）
ＮａＯＨ滴定により求めた実測酸価１．１８ｍｅｑ／ｇ
ＧＰＣ測定より求めた重量平均分子量１２．５万
【０３３０】
（Ｂ−２）
アリルメタクリレート／メタクリル酸共重合体（共重合モル比８２／１８）
ＮａＯＨ滴定により求めた実測酸価１．５８ｍｅｑ／ｇ
ＧＰＣ測定より求めた重量平均分子量１３．０万
【０３３１】
（Ｂ−３）
下記ジイソシアネートとジオールの縮重合物であるポリウレタン樹脂
４、４’−ジフェニルメタンジイソイソシネート（ＭＤＩ）
ヘキサメチレンジイソシアネート（ＨＭＤＩ）
ポリプロピレングリコール、重量平均分子量１０００（ＰＰＧ１０００）
２、２−ビス（ヒドロキシメチル）プロピオニックアシッド（ＤＭＰＡ）
テトラエチレングリコール（ＴＥＧ）
共重合モル比（ＭＤＩ／ＨＭＤＩ／ＰＰＧ１０００／ＤＭＰＡ／ＴＥＧ）４０／１０／１１／２７／１２
ＮａＯＨ滴定により求めた実測酸価１．０７ｍｅｑ／ｇ
ＧＰＣ測定より求めた重量平均分子量４．３万
【０３３２】
（表２中の現像液）
（ＤＶ−１）
下記組成からなるｐＨ１０の水溶液
モノエタノールアミン ０．１ 重量部
トリエタノールアミン １．５ 重量部
下記式２の化合物 ４．０ 重量部
下記式３の化合物 ２．５ 重量部
下記式４の化合物 ０．２ 重量部
水 ９１．７ 重量部
【０３３３】
（ＤＶ−２）
下記組成からなるｐＨ１０の水溶液
炭酸水素ナトリウム １．２ 重量部
炭酸ナトリウム ０．８ 重量部
下記式２の化合物 ３．０ 重量部
下記式３の化合物 ２．０ 重量部
下記式４の化合物 ０．２ 重量部
水 ９２．８ 重量部
【０３３４】
（ＤＶ−３）
下記組成からなるｐＨ１３の水溶液
１Ｋケイ酸カリウム ３．０ 重量部
水酸化カリウム １．５ 重量部
下記式４の化合物 ０．２ 重量部
水 ９５．３ 重量部
【０３３５】
【化６４】

【０３３６】
（ここでＲはＨまたはＣ_４Ｈ_９であり、ｎは約４（平均値）である。）
【０３３７】

【０３３８】
【表２】

【０３３９】
表２から明らかなように、本発明による平版印刷版は走査露光により高い生産性をもって製版可能な条件、即ち、非常に低エネルギーの露光条件によっても、優れた平版印刷版を提供する。一方、本発明の開始系を用いない、比較例７では、実用可能な平版印刷版は得られなかった。
【０３４０】
〔実施例２７〕
開始系を下記のような組成に変え、光重合層の膜厚を１．５ｇ／ｍ^２に変えた以外は実施例１〜１７と同様に、平版印刷版用原版を調製した。
開始系 Ｄ２４ ０．１２ｇ
活性剤 Ａ−１ ０．０８ｇ
共増感剤 Ｃ−２ ０．２ｇ
【０３４１】
得られた平版印刷版用原版に対し、４００ｎｍの単色光を用い、露光エネルギー密度０．２５ｍＪ／ｃｍ^２となる条件で、走査露光を行った。次に、版を１００℃で、１０秒間加熱後、先述の現像処理を実施した。
【０３４２】
視認性に優れた、青色の画像を有する平版印刷版が得られた。得られた版を用い、ハイデルベルグ社ＫＯＲ−Ｄ機を用い、オフセット印刷を実施したところ、画像濃度、汚れ性に優れた印刷物を５万枚以上得ることができた。
【０３４３】
〔実施例２８〕
実施例２７の版を露光前に黄色灯下に１時間さらした後、全く同様に製版・印刷を実施した。実施例２７と全く同様の良好な結果が得られた。
【０３４４】
〔実施例２９〕
実施例２８の版を、湿度６５％、４５℃の強制保存条件下で３日間保存後、実施例２７と同様に、製版・印刷を実施した。実施例２７と同様の良好な結果が得られた。
【０３４５】
〔実施例３０〕
ＰＥＴフイルム上に下記組成からなる感光層を塗布量２．０ｇ／ｍ^２となるように塗設した。
【０３４６】
（感光層全固形分中の含有量）
バインダー樹脂（ポリメチルメタクリレート） ９３．８ｗｔ％
増感色素 Ｄ４０ １．２ｗｔ％
活性剤 Ａ−６ ５．０ｗｔ％
酸消色染料（ビクトリアピュアブルーのナフタレンスルホン酸塩）２．０ｗｔ％
【０３４７】
得られた青色の感材を、メタルハライドランプにて、３０秒間露光を行った。青色が完全に消色し、淡黄色の透明フイルムに変化した。このように、本開始系は酸発生剤としても機能する。
【０３４８】
〔実施例３１〕
活性剤をＡ−７に変えた以外は実施例３０と同様の操作を行った。実施例３０と同様の色素の光消色が認められた。
【０３４９】
〔実施例３２〕
活性剤をＡ−８に変えた以外は実施例３１と同様の操作を行った。色素の光消色が認められた。
【０３５０】
〔実施例３３〕
ＰＥＴフイルム上に下記組成からなる感光層を塗布量２．０ｇ／ｍ^２となるように塗設した。
【０３５１】
（感光層全固形分中の含有量）
バインダー樹脂（ポリメチルメタクリレート） ９０ｗｔ％
増感色素 Ｄ３８ ２．０ｗｔ％
活性剤 Ａ−９ ８．０ｗｔ％
【０３５２】
得られた感材表面上の膜面ｐＨを測定したところ、５．６を示した。次に感材をキセノンランプで５分間露光後、膜面ｐＨを測定したところ、９．５を示した。このように、本開始系は光塩基発生能を有する。
【０３５３】
〔実施例３４〕
ＰＥＴフイルム上に下記組成からなる感光層を塗布量２．０ｇ／ｍ^２となるように塗設した。
【０３５４】
（感光層全固形分中の含有量）
バインダー樹脂（ポリメチルメタクリレート） ９１．５ｗｔ％
増感色素 Ｄ３０ １．５ｗｔ％
活性剤 Ａ−６ ５．０ｗｔ％
酸化発色染料（ロイコクリスタルバイオレット） ２．０ｗｔ％
【０３５５】
得られた淡黄色透明の感材を、メタルハライドランプにて、３０秒間露光を行った。鮮やかな青色に発色した。これは、本開始系のラジカル生成によるロイコ色素の酸化発色と考えられる。式１〜４以外の実施例および比較例中の化合物の構造は以下のとおりである。
【０３５６】
【化６５】

【０３５７】
【化６６】

【０３５８】
（ここで、Ｔｓはトシル基を、Ｔｆはトリフルオロメタンスルホン酸を表す。）
【０３５９】
【発明の効果】
本発明の感光性組成物を適用した平版印刷版用原版はＩｎＧａＮのような短波長の半導体レーザによる走査露光に適した十分な感度を有し、かつ耐刷性・汚れ性・安定性に優れた平版印刷版を与える。また、該走査露光用平版印刷版用原版は黄色灯下でのカブリが著しく改良されており、版を取り扱う作業性が大幅に改善することができる。また、本発明の光開始系は感度に優れ、ラジカル、酸、塩基を発生可能である。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a novel photoinitiating system, in particular, a photosensitive composition containing a photoinitiating system having high sensitivity, excellent printing durability, and excellent stability. The present invention also particularly relates to a photopolymerizable composition that is excellent as a material for a lithographic printing plate precursor capable of making a plate by scanning exposure based on a digital signal.
[0002]
[Prior art]
Conventionally, as a lithographic printing plate, a PS plate having a configuration in which a lipophilic photosensitive resin layer is provided on a hydrophilic support is widely used. As a plate making method, mask exposure (surface exposure) is usually performed through a lithographic film. After exposure), the desired printing plate was obtained by dissolving and removing the non-image area.
[0003]
In recent years, digitization techniques for electronically processing, storing, and outputting image information using a computer have become widespread, and various new image output methods corresponding to the technique have come into practical use. As a result, computer-to-plate (CTP) technology that scans highly directional light such as laser light in accordance with digitized image information and directly manufactures a printing plate without using a lith film is desired. Obtaining an adapted printing plate precursor is an important technical issue.
[0004]
As one of the methods for obtaining such a lithographic printing plate capable of scanning exposure, an ink-receptive photosensitive resin layer (hereinafter referred to as a photosensitive layer) provided on a hydrophilic support has been excellent in photosensitive speed. A configuration using a photopolymerization composition has been proposed and is already on the market. The original plate having such a configuration has a desirable printing plate and printing performance such that the development processing is simple, and further, the resolution, the inking property, the printing durability, and the stain resistance are excellent.
[0005]
The photopolymerizable composition basically comprises an ethylenically unsaturated compound, a photopolymerization initiating system, and a binder resin. Image formation is performed by the photoinitiating system absorbing light and generating active radicals. It causes addition polymerization and causes insolubilization of the photosensitive layer. Most of the conventional proposals for photopolymerizable compositions capable of scanning exposure disclose the use of photoinitiating systems with excellent photosensitivity, see, for example, Bruce M. et al. Monroe et al., Chemical Review, 93, 435 (1993). And R. S. By Davidson, Journal of Photochemistry and biology A: Chemistry, 73.81 (1993). Many are described.
[0006]
For the conventional CTP system using a photopolymerizable composition comprising these starting systems and a long-wavelength visible light source such as an Ar laser (488 nm) or an FD-YAG laser (532 nm) as the light source, production of the plate making process In order to improve the performance, it is desired to write at higher speed, but the purpose is not achieved because the output of the light source is not sufficiently high and the sensitivity of the photosensitive material is not sufficiently high.
[0007]
On the other hand, in recent years, for example, a semiconductor laser using an InGaN-based material and capable of continuous oscillation in a 350 nm to 450 nm region has become a practical stage. The scanning exposure system using these short-wave light sources has an advantage that an economical system can be constructed while having a sufficient output because a semiconductor laser can be manufactured at a low cost because of its structure. Furthermore, a light-sensitive material having a short photosensitive area capable of working under a brighter safelight can be used as compared with a system using a conventional FD-YAG or Ar laser.
[0008]
However, no photoinitiation system having a sufficient sensitivity for scanning exposure in a short wavelength region of 350 nm to 450 nm is known to date.
[0009]
Furthermore, obtaining a highly sensitive photoinitiating system is a technique that is still widely desired in the imaging field (see, for example, Patent Document 1, Non-Patent Documents 1 and 2). A photoinitiating system consisting of a sensitizing dye and an activator can generate an acid and a base in addition to the above active radicals depending on the choice of the activator. For example, image formation such as stereolithography, holography, and color hard copy It is used in the field of manufacturing electronic materials such as photoresists, and photocurable resin materials such as inks, paints and adhesives. In these industrial fields, in order to efficiently cause the decomposition of the active agent, it is desired in the present industrial field to find a sensitizing dye excellent in light absorption and sensitizing ability.
[0010]
[Patent Document 1]
JP 2000-258910 A
[Non-Patent Document 1]
J. et al. P. Fausier “Photoinitiated Polymerization—Theory and Applications”: Rapra Review vol. 9, Report, Rapra Technology (1998)
[Non-Patent Document 2]
M.M. Tsunooka et al. , Prog. Polym. Sci. , 21, 1 (1996)
[0011]
[Problems to be solved by the invention]
An object of the present invention is to obtain a lithographic printing plate for scanning exposure that is excellent in workability and economy and is compatible with a CTP system, and is a lithographic plate that is highly sensitive to the oscillation wavelength of an inexpensive short-wave semiconductor laser. Photosensitivity using a novel photoinitiating system suitable for printing plate masters, etc., having high sensitivity to a wide range of wavelengths from 300 nm to 450 nm, excellent printing durability, and good light room handling It is to provide a composition.
[0012]
[Means for Solving the Problems]
As a result of intensive studies to achieve the above object, the present inventors have found that a novel photoinitiating system comprising a sensitizing dye having a specific structure and an activator gives particularly high photosensitivity, The present invention has been achieved.
That is, the photosensitive composition of the present invention is as follows.
(1) (i) A chemical change is caused by the interaction between a sensitizing dye represented by the following general formula (1) and (ii) an electronically excited state generated by light absorption of the sensitizing dye, thereby generating radicals, acids and bases. And (iii) a compound whose physical or chemical properties are irreversibly changed by at least one of radicals, acids and bases. A photosensitive composition.
[0013]
Dye-LM (1)
[0014]
(In the formula, Dye represents a sensitizing dye skeleton, L represents a divalent organic group linking Dye and M, and M represents an acceptor group having a reduction potential lower than the Dye excitation oxidation potential.)
[0015]
The preferred embodiments of the present invention are listed below.
(2) The acceptor group of the sensitizing dye represented by the general formula (1) described in (1) is an ammonium group, a pyridinium group, a sulfonium group, or a phosphonium group, Photosensitive composition.
(3) (i) At least selected from a sensitizing dye represented by the following general formula (2), a sensitizing dye represented by the general formula (3), and a sensitizing dye represented by the general formula (4) (Ii) an activator compound that undergoes a chemical change by interaction with an electronically excited state generated by light absorption of a sensitizing dye and generates at least one of a radical, an acid, and a base; iii) A photosensitive composition containing a compound whose physical or chemical properties are irreversibly changed by at least one of radicals, acids and bases.
[Chemical 3]

[0016]
(A represents an aromatic ring or a hetero ring which may have a substituent, and X and Y are an oxygen atom, a sulfur atom or -N (R₁)-. R₁, R₂, R₃, R₄, R₅, R₆, R₇, R₈, R₉, R₁₀, R₁₁, R₁₂, R₁₃Are each independently a hydrogen atom or a monovalent nonmetallic atomic group, and A and R₁, R₂, R₃, R₆, R₁₃Can be linked together to form an aliphatic or aromatic ring, respectively. However, A, R₁, R₂, R₃, R₄, R₅, R₆, R₇, R₈, R₉, R₁₀, R₁₁, R₁₂, R₁₃At least one of represents a monovalent organic residue shown in the following partial structure (5). In the following partial structure, L represents a divalent organic group that connects M to the structure represented by the general formula (2), the general formula (3), or the general formula (4), and M represents an ammonium group, a pyridinium group, Represents a sulfonium group or a phosphonium group. )
[0017]
[Formula 4]

[0018]
In order to obtain the effect of the photosensitive composition of the present invention (hereinafter also referred to as a photopolymerizable composition), the sensitizing dye represented by the general formula (1) of (i) is represented by the general formula (2). It is preferable that the sensitizing dye is at least one selected from the sensitizing dye represented by the general formula (3) and the sensitizing dye represented by the general formula (4).
The lithographic printing plate precursor using the photosensitive composition of the present invention has sufficient sensitivity for scanning exposure using a laser light source having a wavelength shorter than 450 nm, can be handled even under a bright safelight, and has printing durability. Gives a lithographic printing plate with excellent stain resistance.
[0019]
DETAILED DESCRIPTION OF THE INVENTION
Embodiments of the present invention will be described in detail.
[A. (Photo initiation system)
The photoinitiating system of the present invention is chemically changed by the interaction between (i) a sensitizing dye having a specific structure represented by the general formula (1) and (ii) an electronically excited state caused by light absorption of the sensitizing dye. And an activator compound that generates at least one of radicals, acids, and bases.
[0020]
One of the characteristics of the sensitizing dye (i) of the present invention is that it has particularly excellent absorption characteristics in the region of 300 nm to 450 nm. Further, (i) efficiently causes degradation of various active agents and exhibits very high photosensitivity. In general, the sensitizing mechanism of a photoinitiating system consisting of a sensitizing dye / active agent is (1) reductive decomposition of the active agent based on the electron transfer reaction from the electronically excited state of the sensitizing dye to the active agent, and (2) activity. Oxidative decomposition of the active agent based on the electron transfer from the sensitizing dye to the electronically excited state of the sensitizing dye, and (3) from the electronically excited state of the active agent based on the energy transfer from the electronically excited state of the sensitizing dye to the active agent. The sensitizing dye of the present invention has been found to cause any of these types of sensitizing reactions with excellent efficiency.
[0021]
In order to obtain high sensitivity, the present inventors have a sensitizing dye having a reduction potential lower than the excitation oxidation potential after the sensitizing dye represented by the formula (1), that is, the sensitizing dye absorbs light. It was found that a sensitizing dye having an acceptor group is very important. The mechanism of action is not clear, but the sensitizing dye is activated by the transfer of electrons and / or energy from the electronically excited state caused by light absorption to the acceptor, and then the electron and / or energy transferred from the acceptor to the activator. Since the reaction mechanism of the agent is decomposed, it is possible that the deactivation process due to the transfer of electrons and / or energy from the activator to the sensitizer dye caused by the bimolecular reaction of the sensitizing dye and the activator is suppressed. It is thought that it is effective in improving the efficiency of subsequent reactions leading to decomposition. In addition, since the sensitizing dye of the present invention exhibits a high-intensity emission (fluorescence and / or phosphorescence) spectrum, one possibility is that the sensitizing dye of the present invention has a relatively long excitation lifetime. There is also a possibility that it is acting on the reaction efficiency with the active agent.
[0022]
(A1) Sensitizing dye
The sensitizing dye used in the present invention is represented by the following general formula (1).
[0023]
Dye-LM (1)
[0024]
(In the formula, Dye represents a sensitizing dye skeleton, L represents a divalent organic group linking Dye and M, and M represents an acceptor group having a reduction potential lower than the Dye excitation oxidation potential.)
[0025]
The general formula (1) will be described. Dye represents a sensitizing dye skeleton. Preferred sensitizing dye skeletons include the following structures.
[0026]
[Sensitizing dye]
Examples of the sensitizing dye skeleton that can be one component of the photopolymerizable composition of the present invention include a spectral sensitizing dye and a dye or pigment that absorbs light from a light source and interacts with a photopolymerization initiator.
Preferred sensitizing dye skeletons are polynuclear aromatics (eg, pyrene, perylene, triphenylene).
Xanthenes (eg fluorescein, eosin, erythrosin, rhodamine B, rose bengal)
Merocyanines (eg, merocyanine, carbomerocyanine)
Thiazines (eg thionine, methylene blue, toluidine blue)
Acridines (eg, acridine orange, chloroflavin, acriflavine)
[0027]
Anthraquinones (eg, anthraquinones)
Squariums (eg, squalium)
Etc. Examples of more preferable spectral sensitizing dyes or dyes are styryl dyes described in JP-B-37-13034, for example,
[0028]
[Chemical formula 5]

[0029]
Anthraquinones described in JP-A No. 64-56767, for example
[0030]
[Chemical 6]

[0031]
Benzoxanthene dyes described in JP-A-2-1714. Acridines described in JP-A-2-226148 and JP-A-2-226149, for example,
[0032]
[Chemical 7]

[0033]
Benzofuran dyes described in JP-A-2-63053, for example
[0034]
[Chemical 8]

[0035]
Conjugated ketone dyes disclosed in JP-A-2-85858 and JP-A-2-216154, for example
[0036]
[Chemical 9]

[0037]
A dye described in JP-A-57-10605. Azocinnamylidene derivatives described in JP-B-2-30321, for example,
[0038]
Embedded image

[0039]
Xanthene dyes described in JP-A-62-31844, JP-A-62-31848, JP-A-62-143043, for example,
[0040]
Embedded image

[0041]
Aminostyryl ketones described in JP-B-59-28325, such as
[0042]
Embedded image

[0043]
Merocyanine dyes represented by the following general formulas [6] to [13] described in JP-B 61-9621, for example,
[0044]
Embedded image

[0045]
In the general formulas [8] to [13], X⁸Represents a hydrogen atom, an alkyl group, a substituted alkyl group, an alkoxy group, an aryl group, a substituted aryl group, an aryloxy group, an aralkyl group or a halogen atom. In the general formula [7], Ph represents a phenyl group. In the general formulas [6] to [13], R⁴⁸, R⁴⁹And R⁵⁰Each represents an alkyl group, a substituted alkyl group, an alkenyl group, an aryl group, a substituted aryl group or an aralkyl group, which may be the same or different. Dyes represented by the following general formulas [14] to [16] described in JP-A-2-17943, for example,
[0046]
Embedded image

[0047]
A: represents an oxygen atom, a sulfur atom, a selenium atom, a tellurium atom, an alkyl or aryl-substituted nitrogen atom or a dialkyl-substituted carbon atom.
Y³: Represents a hydrogen atom, an alkyl group, a substituted alkyl group, an aryl group, a substituted aryl group, an aralkyl group, an acyl group, or a substituted alkoxycarbonyl group.
R⁵¹, R⁵²: As a hydrogen atom, an alkyl group having 1 to 18 carbon atoms, or a substituent, R⁵³O-,
[0048]
Embedded image

[0049]
-(CH₂CH₂O) w-R⁵³Represents a substituted alkyl group having 1 to 18 carbon atoms having a halogen atom (F, Cl, Br, I). However, R⁵³Represents a hydrogen atom or an alkyl group having 1 to 10 carbon atoms, and B represents a dialkylamino group, a hydroxyl group, an acyloxy group, a halogen atom, or a nitro group. w represents an integer of 0 to 4, and x represents an integer of 1 to 20. Merocyanine dyes represented by the following general formula [17] described in JP-A-2-244050, for example,
[0050]
Embedded image

[0051]
(Where R⁵⁴And R⁵⁵Each independently represents a hydrogen atom, an alkyl group, a substituted alkyl group, an alkoxycarbonyl group, an aryl group, a substituted aryl group or an aralkyl group. A²Represents an oxygen atom, a sulfur atom, a selenium atom, a tellurium atom, an alkyl or aryl-substituted nitrogen atom, or a dialkyl-substituted carbon atom. X⁹Represents a group of nonmetallic atoms necessary to form a nitrogen-containing hetero five-membered ring. Y⁴Represents a substituted phenyl group, an unsubstituted or substituted polynuclear aromatic ring, or an unsubstituted or substituted heteroaromatic ring. Z³Represents a hydrogen atom, an alkyl group, a substituted alkyl group, an aryl group, a substituted aryl group, an aralkyl group, an alkoxy group, an alkylthio group, an arylthio group, a substituted amino group, an acyl group, or an alkoxycarbonyl group;⁴And may be bonded to each other to form a ring. Preferred examples are
[0052]
Embedded image

[0053]
Merocyanine dyes represented by the following general formula [18] described in JP-B-59-28326, for example,
[0054]
Embedded image

[0055]
In the above formula, R⁵⁶And R⁵⁷Each represents a hydrogen atom, an alkyl group, a substituted alkyl group, an aryl group, a substituted aryl group or an aralkyl group, which may be the same or different from each other. X¹⁰Represents a substituent having a Hammett's sigma (σ) value in the range of −0.9 to +0.5. Merocyanine dyes represented by the following general formula [19] described in JP-A-59-89303, for example,
[0056]
Embedded image

[0057]
(Where R⁵⁸And R⁵⁹Each independently represents a hydrogen atom, an alkyl group, a substituted alkyl group, an aryl group, a substituted aryl group or an aralkyl group. X¹¹Represents a substituent having a Hammett's sigma (σ) value in the range of −0.9 to +0.5. Y⁵Represents a hydrogen atom, an alkyl group, a substituted alkyl group, an aryl group, a substituted aryl group, an aralkyl group, an acyl group or an alkoxycarbonyl group. ) Preferred examples include
[0058]
Embedded image

[0059]
Merocyanine dyes represented by the following general formula [20] described in JP-A-8-129257, for example
[0060]
Embedded image

[0061]
(Wherein R⁶⁰, R⁶¹, R⁶², R⁶³, R⁶⁸, R⁶⁹, R⁷⁰, R⁷¹Are each independently a hydrogen atom, halogen atom, alkyl group, substituted alkyl group, aryl group, substituted aryl group, hydroxyl group, substituted oxy group, mercapto group, substituted thio group, amino group, substituted amino group, substituted carbonyl group , Sulfo group, sulfonate group, substituted sulfinyl group, substituted sulfonyl group, phosphono group, substituted phosphono group, phosphonate group, substituted phosphonate group, cyano group, nitro group, or R⁶⁰And R⁶¹, R⁶¹And R⁶², R⁶²And R⁶³, R⁶⁸And R⁶⁹, R⁶⁹And R⁷⁰, R⁷⁰And R⁷¹May be bonded to each other to form an aliphatic or aromatic ring, and R⁶⁴Represents a hydrogen atom, an alkyl group, a substituted alkyl group, an aryl group, or a substituted aryl group, and R⁶⁵Represents a substituted or unsubstituted alkenylalkyl group, or a substituted or unsubstituted alkynylalkyl group, R⁶⁶, R⁶⁷Each independently represents a hydrogen atom, a halogen atom, an alkyl group, a substituted alkyl group, an aryl group, a substituted aryl group, or a substituted carbonyl group).
[0062]
Embedded image

[0063]
A benzopyran dye represented by the following general formula [21] described in JP-A-8-334897, for example,
[0064]
Embedded image

[0065]
(Wherein R⁷²~ R⁷⁵Independently denote a hydrogen atom, a halogen atom, an alkyl group, an aryl group, a hydroxyl group, an alkoxy group or an amino group. Also R⁷²~ R⁷⁵May form a ring composed of nonmetallic atoms together with carbon atoms to which they can be bonded. R⁷⁶Represents a hydrogen atom, an alkyl group, an aryl group, a heteroaromatic group, a cyano group, an alkoxy group, a carboxy group or an alkenyl group. R⁷⁷Is R⁷⁶Or a group represented by -ZR⁷⁶And Z represents a carbonyl group, a sulfonyl group, a sulfinyl group or an arylene carbonyl group. Also R⁷⁶And R⁷⁷Both may form a ring composed of nonmetallic atoms. A represents an O atom, an S atom, NH, or an N atom having a substituent. B represents an O atom or a group of = C (G1) (G2). G1 and G2 may be the same or different, and may be a hydrogen atom, a cyano group, an alkoxycarbonyl group, an aryloxycarbonyl group, an acyl group, an arylcarbonyl group, an alkylthio group, an arylthio group, an alkylsulfonyl group, an arylsulfonyl group, or fluoro. Represents a sulfonyl group. However, G1 and G2 do not become hydrogen atoms at the same time. G1 and G2 may form a ring composed of a nonmetallic atom together with a carbon atom).
[0066]
More preferable sensitizing dye skeletons include sensitizing dye skeletons represented by the following general formula (2), general formula (3), and general formula (4).
[0067]
Embedded image

[0068]
(A represents an aromatic ring or a hetero ring which may have a substituent, and X and Y are an oxygen atom, a sulfur atom or -N (R₁)-. R₁, R₂, R₃, R₄, R₅, R₆, R₇, R₈, R₉, R₁₀, R₁₁, R₁₂, R₁₃Are each independently a hydrogen atom or a monovalent nonmetallic atomic group, and A and R₁, R₂, R₃, R₆, R₁₃Can be linked together to form an aliphatic or aromatic ring, respectively. However, A, R₁, R₂, R₃, R₄, R₅, R₆, R₇, R₈, R₉, R₁₀, R₁₁, R₁₂, R₁₃At least one of represents a monovalent organic residue shown in the following partial structure (5). In the following partial structure, L represents a divalent organic group that connects M to the structure represented by the general formula (2), the general formula (3), or the general formula (4), and M represents an ammonium group, a pyridinium group, Represents a sulfonium group or a phosphonium group. )
[0069]
Embedded image

[0070]
R₁, R₂, R₃, R₄, R₅, R₆, R₇, R₈, R₉, R₁₀, R₁₁, R₁₂, R₁₃A preferred specific example will be described. Examples of preferable alkyl groups include linear, branched, and cyclic alkyl groups having 1 to 20 carbon atoms. Specific examples thereof include a methyl group, an ethyl group, a propyl group, Butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, hexadecyl, octadecyl, eicosyl, isopropyl, isobutyl, s-butyl, Examples thereof include t-butyl group, isopentyl group, neopentyl group, 1-methylbutyl group, isohexyl group, 2-ethylhexyl group, 2-methylhexyl group, cyclohexyl group, cyclopentyl group and 2-norbornyl group. Of these, linear alkyl groups having 1 to 12 carbon atoms, branched alkyl groups having 3 to 12 carbon atoms, and cyclic alkyl groups having 5 to 10 carbon atoms are more preferable.
[0071]
As the substituent of the substituted alkyl group, a monovalent nonmetallic atomic group excluding hydrogen is used, and preferred examples include a halogen atom (—F, —Br, —Cl, —I), a hydroxyl group, an alkoxy group, Aryloxy group, mercapto group, alkylthio group, arylthio group, alkyldithio group, aryldithio group, amino group, N-alkylamino group, N, N-dialkylamino group, N-arylamino group, N, N-diarylamino group N-alkyl-N-arylamino group, acyloxy group, carbamoyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamoyloxy group, N, N-dialkylcarbamoyloxy group, N, N-diarylcarbamoyloxy group, N-alkyl-N-arylcarbamoyloxy group, alkylsulfoxy group, Reel sulphoxide group, an acylthio group, an acylamino group, N- alkylacylamino group, N- arylacylamino group, a ureido group, N'- alkylureido group, N ', N'- dialkyl ureido group,
[0072]
N'-arylureido group, N ', N'-diarylureido group, N'-alkyl-N'-arylureido group, N-alkylureido group, N-arylureido group, N'-alkyl-N-alkylureido Group, N′-alkyl-N-arylureido group, N ′, N′-dialkyl-N-alkylureido group, N ′, N′-dialkyl-N-arylureido group, N′-aryl-N-alkylureido group Group, N′-aryl-N-arylureido group, N ′, N′-diaryl-N-alkylureido group, N ′, N′-diaryl-N-arylureido group, N′-alkyl-N′-aryl -N-alkylureido group, N'-alkyl-N'-aryl-N-arylureido group, alkoxycarbonylamino group, aryloxycarbonyl Mino group, N-alkyl-N-alkoxycarbonylamino group, N-alkyl-N-aryloxycarbonylamino group, N-aryl-N-alkoxycarbonylamino group, N-aryl-N-aryloxycarbonylamino group, formyl Group, acyl group, carboxyl group,
[0073]
Alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N, N-diarylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, Alkylsulfinyl group, arylsulfinyl group, alkylsulfonyl group, arylsulfonyl group, sulfo group (-SO₃H) and conjugated base groups thereof (hereinafter referred to as sulfonate groups), alkoxysulfonyl groups, aryloxysulfonyl groups, sulfinamoyl groups, N-alkylsulfinamoyl groups, N, N-dialkylsulfinamoyl groups, N-aryls Rufinamoyl group, N, N-diarylsulfinamoyl group, N-alkyl-N-arylsulfinamoyl group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfamoyl group, N-aryl Sulfamoyl group, N, N-diarylsulfamoyl group, N-alkyl-N-arylsulfamoyl group, phosphono group (—PO₃H₂) And conjugated base groups thereof (hereinafter referred to as phosphonate groups),
[0074]
Dialkylphosphono group (-PO₃(Alkyl)₂), Diarylphosphono group (—PO₃(Aryl)₂), An alkylarylphosphono group (—PO₃(Alkyl) (aryl)), monoalkylphosphono group (—PO₃H (alkyl)) and its conjugate base group (hereinafter referred to as alkyl phosphonate group), monoaryl phosphono group (—PO₃H (aryl)) and its conjugate base group (hereinafter referred to as aryl phosphonate group), phosphonooxy group (-OPO₃H₂) And conjugated base groups thereof (hereinafter referred to as phosphonatooxy groups), dialkylphosphonooxy groups (—OPO)₃(Alkyl)₂), Diarylphosphonooxy group (-OPO₃(Aryl)₂), An alkylarylphosphonooxy group (—OPO₃(Alkyl) (aryl)), monoalkylphosphonooxy group (—OPO₃H (alkyl)) and its conjugate base group (hereinafter referred to as alkylphosphonatooxy group), monoarylphosphonooxy group (—OPO)₃H (aryl)) and its conjugated base group (hereinafter referred to as arylphosphonatooxy group), cyano group, nitro group, aryl group, heteroaryl group, alkenyl group and alkynyl group.
[0075]
Specific examples of the alkyl group in these substituents include the above-described alkyl groups, and specific examples of the aryl group include a phenyl group, a biphenyl group, a naphthyl group, a tolyl group, a xylyl group, a mesityl group, and a cumenyl group. , Chlorophenyl group, bromophenyl group, chloromethylphenyl group, hydroxyphenyl group, methoxyphenyl group, ethoxyphenyl group, phenoxyphenyl group, acetoxyphenyl group, benzoyloxyphenyl group, methylthiophenyl group, phenylthiophenyl group, methylamino Phenyl group, dimethylaminophenyl group, acetylaminophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, ethoxyphenylcarbonyl group, phenoxycarbonylphenyl group, N-phenylcarbamoylphenyl group, phenyl group Cyanophenyl group, sulfophenyl group, sulfonatophenyl group, phosphonophenyl phenyl group, phosphonophenyl phenyl group and the like.
[0076]
As the heteroaryl group, a monocyclic or polycyclic aromatic ring containing at least one of nitrogen, oxygen and sulfur atoms is used. Examples of particularly preferred heteroaryl groups include thiophene, thiathrene, furan, Pyran, isobenzofuran, chromene, xanthene, phenoxazine, pyrrole, pyrazole, isothiazole, isoxazole, pyrazine, pyrimidine, pyridazine, indolizine, isoindolizine, indoyl, indazole, purine, quinolidine, isoquinoline, phthalazine, naphthyridine, Quinazoline, cinolin, pteridine, carbazole, carboline, phenanthrine, acridine, perimidine, phenanthrolin, phthalazine, phenazazine, phenoxazine, furazane, phenoxazine, etc. It further may be benzo-fused or may have a substituent.
[0077]
Examples of alkenyl groups include vinyl, 1-propenyl, 1-butenyl, cinnamyl, 2-chloro-1-ethenyl, etc. Examples of alkynyl include ethynyl, 1 -Propynyl group, 1-butynyl group, trimethylsilylethynyl group and the like. Acyl group (G₁G in CO-)₁Examples thereof include hydrogen, and the above alkyl groups and aryl groups. Among these substituents, even more preferred are halogen atoms (—F, —Br, —Cl, —I), alkoxy groups, aryloxy groups, alkylthio groups, arylthio groups, N-alkylamino groups, N, N -Dialkylamino group, acyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamoyloxy group, acylamino group, formyl group, acyl group, carboxyl group, alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group Group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, sulfo group, sulfonate group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfa group Moyl group, N-aryl sulf Moyl group, N-alkyl-N-arylsulfamoyl group, phosphono group, phosphonate group, dialkyl phosphono group, diaryl phosphono group, monoalkyl phosphono group, alkyl phosphonate group, monoaryl phosphono group, aryl phosphine group Examples include an onato group, a phosphonooxy group, a phosphonateoxy group, an aryl group, and an alkenyl group.
[0078]
On the other hand, examples of the alkylene group in the substituted alkyl group include divalent organic residues obtained by removing any one of the hydrogen atoms on the alkyl group having 1 to 20 carbon atoms. Can include linear alkylene groups having 1 to 12 carbon atoms, branched chains having 3 to 12 carbon atoms, and cyclic alkylene groups having 5 to 10 carbon atoms.
[0079]
R obtained by combining the substituent and an alkylene group₁~ R₁₃Specific examples of preferred substituted alkyl groups include chloromethyl group, bromomethyl group, 2-chloroethyl group, trifluoromethyl group, methoxymethyl group, methoxyethoxyethyl group, allyloxymethyl group, phenoxymethyl group, methylthiomethyl group. , Tolylthiomethyl group, ethylaminoethyl group, diethylaminopropyl group, morpholinopropyl group, acetyloxymethyl group, benzoyloxymethyl group, N-cyclohexylcarbamoyloxyethyl group, N-phenylcarbamoyloxyethyl group, acetylaminoethyl group, N-methylbenzoylaminopropyl group, 2-oxoethyl group, 2-oxopropyl group, carboxypropyl group, methoxycarbonylethyl group, allyloxycarbonylbutyl group, chlorophenoxycarbonyl Butyl group, a carbamoylmethyl group, N- methylcarbamoyl ethyl, N, N- dipropylcarbamoylmethyl group, N- (methoxyphenyl) carbamoyl ethyl group, N- methyl -N- (sulfophenyl) carbamoylmethyl group,
[0080]
Sulfobutyl group, sulfonatobutyl group, sulfamoylbutyl group, N-ethylsulfamoylmethyl group, N, N-dipropylsulfamoylpropyl group, N-tolylsulfamoylpropyl group, N-methyl-N- (phosphono Phenyl) sulfamoyloctyl group, phosphonobutyl group, phosphonatohexyl group, diethylphosphonobutyl group, diphenylphosphonopropyl group, methylphosphonobutyl group, methylphosphonatobutyl group, tolylphosphonohexyl group, tolylphosphine group Onatohexyl group, phosphonooxypropyl group, phosphonatoxybutyl group, benzyl group, phenethyl group, α-methylbenzyl group, 1-methyl-1-phenylethyl group, p-methylbenzyl group, cinnamyl group, allyl group, 1-propenylmethyl group, 2- Thenyl group, 2-methylallyl group, 2-methyl propenyl methyl group, 2-propynyl group, 2-butynyl, 3-butynyl, and the like.
[0081]
R₁, R₂, R₃, R₄, R₅, R₆, R₇, R₈, R₉, R₁₀, R₁₁, R₁₂And R₁₃Specific examples of preferred aryl groups include those in which 1 to 3 benzene rings form a condensed ring, and those in which a benzene ring and a 5-membered unsaturated ring form a condensed ring. Includes a phenyl group, a naphthyl group, an anthryl group, a phenanthryl group, an indenyl group, an acenaphthenyl group, and a fluorenyl group, and among these, a phenyl group and a naphthyl group are more preferable.
[0082]
R₁, R₂, R₃, R₄, R₅, R₆, R₇, R₈, R₉, R₁₀, R₁₁, R₁₂And R₁₃Specific examples of the preferred substituted aryl group include those having a monovalent nonmetallic atomic group excluding hydrogen as a substituent on the ring-forming carbon atom of the aryl group described above. Examples of preferred substituents include the alkyl groups, substituted alkyl groups, and those previously shown as substituents in the substituted alkyl group. Preferred examples of such a substituted aryl group include biphenyl group, tolyl group, xylyl group, mesityl group, cumenyl group, chlorophenyl group, bromophenyl group, fluorophenyl group, chloromethylphenyl group, trifluoromethylphenyl group. Hydroxyphenyl group, methoxyphenyl group, methoxyethoxyphenyl group, allyloxyphenyl group, phenoxyphenyl group, methylthiophenyl group, tolylthiophenyl group, ethylaminophenyl group, diethylaminophenyl group, morpholinophenyl group, acetyloxyphenyl group, Benzoyloxyphenyl group, N-cyclohexylcarbamoyloxyphenyl group, N-phenylcarbamoyloxyphenyl group,
[0083]
Acetylaminophenyl group, N-methylbenzoylaminophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, allyloxycarbonylphenyl group, chlorophenoxycarbonylphenyl group, carbamoylphenyl group, N-methylcarbamoylphenyl group, N, N-di Propylcarbamoylphenyl group, N- (methoxyphenyl) carbamoylphenyl group, N-methyl-N- (sulfophenyl) carbamoylphenyl group, sulfophenyl group, sulfonatophenyl group, sulfamoylphenyl group, N-ethylsulfamoyl Phenyl group, N, N-dipropylsulfamoylphenyl group, N-tolylsulfamoylphenyl group, N-methyl-N- (phosphonophenyl) sulfamoylphenyl group, phosphonophenyl group, phos Onatophenyl group, diethylphosphonophenyl group, diphenylphosphonophenyl group, methylphosphonophenyl group, methylphosphonatophenyl group, tolylphosphonophenyl group, tolylphosphonatophenyl group, allyl group, 1-propenylmethyl group, 2 -Butenyl group, 2-methylallylphenyl group, 2-methylpropenylphenyl group, 2-propynylphenyl group, 2-butynylphenyl group, 3-butynylphenyl group and the like can be mentioned.
[0084]
Next, A in the general formulas (2) to (4) will be described. A represents an aromatic ring or a hetero ring which may have a substituent, and specific examples of the aromatic ring or hetero ring which may have a substituent include those in the general formulas (2) to (4). R₁~ R₁₃The thing similar to what was described in (5) is mentioned.
[0085]
The sensitizing dye represented by the general formula of the present invention is formed by a condensation reaction between an acidic nucleus as shown above, an acidic nucleus having an active methylene group, and a substituted or unsubstituted aromatic ring or heterocyclic ring. Although these are obtained, these can be synthesized with reference to Japanese Patent Publication No. 59-28329.
[0086]
Next, L will be described. L represents a divalent organic group that connects the sensitizing dye skeleton and the acceptor group M. Examples of the divalent organic group represented by L include an alkylene group, a phenylene group, and a naphthylene group. The divalent organic group may further have a substituent. Examples of the substituent that can be introduced include an alkyl group, an aryl group, an alkoxy group, an acyloxy group, a halogen atom, a hydroxy group, an amino group, and a cyano group. Group, nitro group, and the like. L may have a hetero atom. Specific examples of the linking group having a hetero atom include those having the following partial structures.
[0087]
Embedded image

[0088]
Here, “having the following partial structure” means that L as a linking group or terminal group has at least one of the partial structures, and may have a plurality of the partial structures. Therefore, L may be the partial structure itself, and may be a group in which a plurality of these are connected, or a group in which the partial structure is connected to another hydrocarbon group or the like. Specific examples of particularly preferable L include the structures shown below.
[0089]
Embedded image

[0090]
Next, the acceptor group M will be described. M represents an acceptor group having a reduction potential lower than the excitation oxidation potential generated by light absorption of the sensitizing dye. Preferred acceptor groups include ammonium groups, pyridinium groups, sulfonium groups, or phosphonium groups. Although the preferable specific example of an acceptor group is shown below, this invention is not limited to this.
[0091]
Embedded image

[0092]
Particularly preferred acceptor groups include an ammonium group and a pyridinium group, and more preferred examples include a pyridinium group.
[0093]
Next, counter anion X⁻A preferred example of will be described.
X⁻As a preferable example, a halide ion (F⁻, Cl⁻, Br⁻, I⁻), Sulfonate ion, organoboron anion, perchlorate ion (ClO)₄ ⁻) And anions represented by the following general formula (a) or (b).
[0094]
MX_r                      (A)
MX_r-1(OH) (b)
[0095]
(In the formula, M represents a boron atom, a phosphorus atom, an arsenic atom, or an antimony atom, X represents a halogen atom, and r represents an integer of 4 to 6.)
[0096]
Preferred examples of the sulfonate ion include methanesulfonate ion, benzenesulfonate ion, p-toluenesulfonate ion (TsO⁻), P-styrenesulfonic acid ion, β-naphthoquinone-4-sulfonic acid ion, anthraquinone-1,5-disulfonic acid ion, anthraquinone-1,8-disulfonic acid ion, anthraquinone-1-sulfonic acid ion, anthraquinone-2 -Sulfonic acid ion, quinoline-8-sulfonic acid ion, hydroquinonesulfonic acid ion, 1,5-naphthalenedisulfonic acid ion, 1-naphthalenesulfonic acid ion, 2-naphthalenesulfonic acid ion, 2-amino-1-naphthalenesulfonic acid Ion, 2-naphthol-6-sulfonate ion, dibutylnaphthalenesulfonate ion, naphthalene-1,3,6-trisulfonate ion, m-benzenedisulfonate ion, p-phenolsulfonate ion, dodecylbenzenesulfonate ion 2 Hydroxy-4-methoxybenzophenone-5-sulfonic acid ion, 4-acetylbenzenesulfonic acid ion, 4-nitrotoluene-2-sulfonic acid ion, o-benzaldehyde sulfonic acid ion, diphenylamine-4-sulfonic acid ion, benzaldehyde-2, Examples include 4-disulfonic acid ion, mesitylenesulfonic acid ion, trifluoromethanesulfonic acid ion, chlorosulfonic acid ion, fluorosulfonic acid ion, 9,10-dimethoxyanthracene-2-sulfonic acid ion, and the like.
[0097]
The compound represented by the general formula (1) can be constituted by sequentially combining the above-described sensitizing dye skeleton, the divalent organic group L, and the acceptor group M. Preferred specific examples (D1) to (D49) of the compound represented by the general formula (1) are shown below, but the present invention is not limited thereto.
[0098]
Embedded image

[0099]
Embedded image

[0100]
Embedded image

[0101]
Embedded image

[0102]
Embedded image

[0103]
The sensitizing dye represented by the general formula (1) of the present invention is F.I. M.M. The method described in Hammer et al., “The Cyanine Soybean and Relieved Compounds” (FM Hamer et al., “The Cyanine Dyes and Related Compounds”), pages 511-611 (1964). , KAI ARNE JENSEN and LARS HENRIKSEN et al. Can be synthesized with reference to the method described in ACTA CHEMICA SCANDINAVICA 22: 1107-1128 (1968).
[0104]
The sensitizing dye of the present invention can be further subjected to various chemical modifications for improving the characteristics of the photosensitive layer. For example, sensitizing dye and addition polymerizable compound structure (for example, acryloyl group or methacryloyl group) are bonded by a method such as covalent bond, ionic bond, hydrogen bond, etc. Unnecessary precipitation suppression of the dye from the subsequent film can be performed. Further, the photosensitivity in a state where the concentration of the starting system is low can be remarkably enhanced by the combination of the sensitizing dye and the radical, acid or base generation part of the activator compound described later. Furthermore, for the purpose of improving the processing suitability to (alkaline) aqueous developers, which is a preferred mode of use of the photosensitive layer of the present invention, hydrophilic sites (carboxyl groups and esters thereof, sulfonic acid groups and esters thereof, ethylene Introduction of an acid group or a polar group such as an oxide group is effective. In particular, ester-type hydrophilic groups have a relatively hydrophobic structure in the photosensitive layer, so that they have excellent compatibility, and in the developer, acid groups are generated by hydrolysis, resulting in increased hydrophilicity. Have. In addition, for example, a substituent can be appropriately introduced in order to improve compatibility in the photosensitive layer and to suppress crystal precipitation. For example, in certain types of photosensitive systems, unsaturated bonds such as aryl groups and allyl groups may be very effective in improving compatibility. By introducing an obstacle, crystal precipitation can be remarkably suppressed. Further, by introducing a phosphonic acid group, an epoxy group, a trialkoxysilyl group, or the like, adhesion to an inorganic substance such as a metal or a metal oxide can be improved. In addition, a method such as polymerization of a sensitizing dye can be used depending on the purpose.
[0105]
Details of the usage such as which structure of these sensitizing dyes are used, whether they are used alone or in combination of two or more, and how much is added, can be appropriately set according to the performance design of the final photosensitive material. . For example, the compatibility with the photosensitive layer can be increased by using two or more sensitizing dyes in combination. In selecting the sensitizing dye, in addition to the photosensitivity, the molar extinction coefficient at the emission wavelength of the light source used is an important factor. By using a dye having a large molar extinction coefficient, the amount of the dye added can be made relatively small, which is economical and advantageous from the viewpoint of film properties of the photosensitive layer. Since the photosensitivity and resolution of the photosensitive layer and the physical properties of the exposure film are greatly affected by the absorbance at the light source wavelength, the addition amount of the sensitizing dye is appropriately selected in consideration of these factors. For example, the sensitivity decreases in a low region where the absorbance is 0.1 or less. Also, the resolution becomes low due to the influence of halation. However, for the purpose of curing a thick film of, for example, 5 μm or more, there is a case where such a low absorbance can be increased instead. In the region where the absorbance is 3 or more, most of the light is absorbed on the surface of the photosensitive layer, and the internal curing is inhibited. For example, when used as a printing plate, the film strength and the substrate adhesion are poor. It will be insufficient. When used as a lithographic printing plate used in a relatively thin film thickness, the amount of sensitizing dye added is such that the absorbance of the photosensitive layer is in the range of 0.1 to 1.5, preferably in the range of 0.25 to 1. It is preferable to set so that When used as a lithographic printing plate, this is usually 0.05 to 30 parts by weight, preferably 0.1 to 20 parts by weight, more preferably 0.2 to 10 parts by weight per 100 parts by weight of the photosensitive layer component. The range is parts by weight.
[0106]
(A2) Activator compound
The activator, which is the second essential component of the photoinitiating system in the present invention, will be described. The activator in the present invention is a compound that undergoes a chemical change through interaction with the electronically excited state of the sensitizing dye to generate at least one of radicals, acids, and bases. Hereinafter, radicals, acids, and bases generated in this way are simply referred to as active species. When these compounds are not present, or when only the active agent is used alone, a practically sufficient sensitivity cannot be obtained. However, as one aspect of using the sensitizing dye and the active compound in combination, Can be used as a single compound by an appropriate chemical method (eg, linking a sensitizing dye and an activator compound by chemical bonding). Such a technical idea is disclosed in, for example, Japanese Patent No. 2720195.
[0107]
Usually, many of these activators are considered to generate active species through the following initial chemical processes (1) to (3). (1) Reductive decomposition of the activator based on the electron transfer reaction from the electronically excited state of the sensitizing dye to the active agent, (2) Based on the electron transfer from the active agent to the electronically excited state of the sensitizing dye, Oxidative decomposition of the active agent, and (3) decomposition of the active agent from the electronically excited state based on energy transfer from the electronically excited state of the sensitizing dye to the active agent. There are many cases where the individual activator compounds belong to (1) to (3), but there are many vague cases. The major characteristic of the sensitizing dye in the present invention is any type of these activators. Even in combination, it has a very high sensitizing effect.
[0108]
Specific activator compounds known to those skilled in the art can be used without limitation, and specific examples include, for example, Bruce M. et al. Monroe et al., Chemical Review, 93, 435 (1993). And R. S. By Davidson, Journal of Photochemistry and biology
A: Chemistry, 73.81 (1993). J. et al. P. Faussier “Photoinitiated Polymerization—Theory and Applications”: Rapra Review vol. 9, Report, Rapra Technology (1998). M.M. Tsunooka et al. , Prog. Polym. Sci. , 21, 1 (1996). Many are described. In addition, as other compound groups having the functions (1) and (2), F.I. D. Saeva, Topics in Current Chemistry, 156, 59 (1990). G. G. Maslak, Topics in Current Chemistry, 168, 1 (1993). H. B. Shuster et al, JACS, 112, 6329 (1990). I. D. F. Eaton et al, JACS, 102, 3298 (1980). A group of compounds that cause oxidative or reductive bond cleavage is also known, as described in the above.
[0109]
Hereinafter, with respect to specific examples of preferred active agents, (a) those that are reduced to cause bond cleavage to generate active species, (b) those that can be oxidized to cause bond cleavage to generate active species, (c) Although it will be described as being classified into the others, there are many cases where there is no general explanation as to which of the individual compounds belongs, and the present invention is not limited to the description of these reaction mechanisms.
[0110]
(A) Those that are reduced to cause bond cleavage and generate active species.
Compound having a carbon-halogen bond: It is considered that a carbon-halogen bond is reductively cleaved to generate an active species (for example, described in Polymer Preprints, Jpn., 41 (3) 542 (1992). ). As the active species, radicals and acids can be generated. Specifically, for example, in addition to halomethyl-s-triazines, M.M. P. Hutt, E .; F. Elslager and L.L. M.M. Journal of Heterocyclic Chemistry by Merbel, 7, 511 (1970). Halomethyl oxadiazoles that can be easily synthesized by those skilled in the art by the synthesis method described in JP-A No. 2641100, JP-A No. 3333450, JP-A No. 3021590, and No. 3021599 are preferably used. it can.
[0111]
Compounds having a nitrogen-nitrogen bond or nitrogen-containing heterocycle-nitrogen-containing heterocycle bond: reductive bond cleavage (for example, as described in J. Pys. Chem., 96, 207 (1992). ). Specifically, hexaarylbiimidazoles and the like are preferably used. The generated active species is a lophine radical, and in combination with a hydrogen donor as necessary, a radical chain reaction is initiated, and image formation using an oxidation reaction with a lophine radical is also known (J. Imaging Sci., 30). 215 (1986)).
[0112]
Compound having oxygen-oxygen bond: It is considered that the oxygen-oxygen bond is reductively cleaved to generate an active radical (for example, described in Polym. Adv. Technol., 1,287 (1990)). . Specifically, for example, organic peroxides are preferably used. A radical can be generated as an active species.
[0113]
Onium compound: It is considered that a carbon-hetero bond or an oxygen-nitrogen bond is reductively cleaved to generate an active species (for example, described in J. Photopolym. Sci. Technol., 3, 149 (1990). ing). Specifically, for example, iodonium salts described in European Patent No. 104143, U.S. Pat. No. 4,837,124, Japanese Patent Laid-Open No. 2-150848, and Japanese Patent Laid-Open No. 2-96514, European Patent Nos. 370693, 233567, 297443, 293442, 279210, 422570, U.S. Pat. Nos. 3,902,144, 4,933,377, 4,760013, 4,734,344 and 2,833,827, sulfonium salts and diazonium salts (which may have a substituent) Diazonium, etc.), diazonium salt resins (formaldehyde resin of diazodiphenylamine, etc.), N-alkoxypyridinium salts, etc. (eg, USP 4,743,528, JP-A 63-138345, JP-A 63-142345, Kaisho 63 142346, Japanese Patent Publication No. 46-42363, etc., specifically 1-methoxy-4-phenylpyridinium tetrafluoroborate, etc.), and further, Japanese Patent Publication Nos. 52-147277, 52-14278, The compounds described in No. 52-14279 are preferably used. Generates radicals and acids as active species.
[0114]
Active esters: nitrobenzyl esters of sulfonic acid and carboxylic acid, esters of sulfonic acid and carboxylic acid and N-hydroxy compounds (N-hydroxyphthalimide, oxime, etc.), sulfonate esters of pyrogallol, naphthoquinone diazide-4 -Sulfonates can be reductively decomposed. As the active species, radicals and acids can be generated. Specific examples of the sulfonic acid esters include European Patent Nos. 0290750, 046083, 156153, 271851, 0388343, U.S. Pat. Nos. 3,901,710 and 4,181,531, JP-A-60-198538. Nitrobenzle ester compounds described in JP-A-53-133022, European Patents 0196672, 84515, 199672, 044115, 0101122, US Pat. Nos. 4,618,564, 4371605, and 4431774, The iminosulfonate compounds described in JP-A No. 64-18143, JP-A-2-245756, JP-A-4-365048, JP-B-62-2223, JP-B-63-14340, JP-A-59-174831 Compounds, etc. For example compounds may be mentioned below.
[0115]
Embedded image

[0116]
(In the formula, Ar represents an optionally substituted aromatic group or aliphatic group.)
Moreover, it is also possible to produce | generate a base as an active species, for example, the following compound groups are known.
[0117]
Ferrocene and iron arene complexes: An active radical can be reductively generated. Specifically, for example, they are disclosed in JP-A-1-304453 and JP-A-1-152109.
[0118]
Embedded image

[0119]
(In the formula, R represents an aliphatic group or an aromatic group which may be substituted.)
Disulfones: Reducing S—S bond reductively and generating an acid. For example, diphenyl disulfones as described in JP-A No. 61-166544 are known.
[0120]
(B) Those that are oxidized to cause bond cleavage and generate active species.
Alkylate complex: It is considered that a carbon-hetero bond is oxidatively cleaved to generate an active radical (for example, as described in J. Am. Chem. Soc., 112, 6329 (1990)). Specifically, for example, triarylalkyl borates are preferably used.
[0121]
Alkylamine compound: It is considered that the C—X bond on carbon adjacent to nitrogen is cleaved by oxidation to generate an active radical (for example, J. Am. Chem. Soc., 116, 4211 (1994). As described in). X is preferably a hydrogen atom, a carboxyl group, a trimethylsilyl group, a benzyl group or the like. Specific examples include ethanolamines, N-phenylglycines, N-trimethylsilylmethylanilines, and the like.
[0122]
Sulfur-containing and tin-containing compounds: Compounds in which the nitrogen atoms of the above-described amines are replaced with sulfur atoms and tin atoms can generate active radicals by the same action. Further, a compound having an SS bond is also known to be sensitized by SS cleavage.
[0123]
α-Substituted methylcarbonyl compound: An active radical can be generated by oxidative cleavage of the carbonyl-α carbon bond. Moreover, what converted carbonyl into the oxime ether also shows the same effect | action. Specifically, 2-alkyl-1- [4- (alkylthio) phenyl] -2-morpholinopronone-1 and these and a hydroxylamine were reacted, and then N—OH was etherified. Mention may be made of oxime ethers.
[0124]
Sulfinic acid salts: An active radical can be reductively generated. Specific examples include sodium arylsulfinate.
[0125]
(C) Other
Although the sensitization mechanism is not clear, many can function as an activator. Examples thereof include organometallic compounds such as titanocene, aromatic ketones, acylphosphine, and bisacylphosphine. Active species can generate radicals and acids.
[0126]
Hereinafter, among the activator compounds used in the present invention, preferred compounds particularly excellent in sensitivity and stability are specifically exemplified.
[0127]
(1) Halomethyltriazines
Examples include compounds represented by the following general formula [I]. In particular, it excels in radical generation and acid generation ability.
[0128]
Embedded image

[0129]
In the formula [I], X represents a halogen atom. Y¹Is -CX₃, -NH₂, -NHR¹', -NR¹’₂, -OR¹Represents'. Where R¹'Represents an alkyl group, a substituted alkyl group, an aryl group, or a substituted aryl group. Also R¹'-CX₃Represents an alkyl group, a substituted alkyl group, an aryl group, a substituted aryl group, or a substituted alkenyl group.
[0130]
Specific examples of such compounds include, for example, Wakabayashi et al., Bull. Chem. Soc. Japan, 42, 2924 (1969), for example, 2-phenyl-4,6-bis (trichloromethyl) -S-triazine, 2- (p-chlorophenyl) -4,6-bis (trichloromethyl) -S-triazine, 2- (p-tolyl) -4,6-bis (trichloromethyl) -S-triazine, 2- (p-methoxyphenyl) -4,6-bis (trichloromethyl) -S-triazine, 2- (2 ′, 4′-dichlorophenyl) -4,6-bis (trichloromethyl) -S-triazine, 2,4,6-tris (trichloromethyl) -S-triazine, 2-methyl-4, 6-bis (trichloromethyl) -S-triazine, 2-n-nonyl-4,6-bis (trichloromethyl) -S-triazine, 2- (α, α, β-trichloroethyl) -4, - bis (trichloromethyl) -S- triazine. In addition, compounds described in GB 1388492, for example, 2-styryl-4,6-bis (trichloromethyl) -S-triazine, 2- (p-methylstyryl) -4,6-bis (trichloromethyl) ) -S-triazine, 2- (p-methoxystyryl) -4,6-bis (trichloromethyl) -S-triazine, 2- (p-methoxystyryl) -4-amino-6-trichloromethyl-S-triazine Compounds described in JP-A-53-133428, such as 2- (4-methoxy-naphth-1-yl) -4,6-bis-trichloromethyl-S-triazine, 2- (4-ethoxy-naphtho) -1-yl) -4,6-bis-trichloromethyl-S-triazine, 2- [4- (2-ethoxyethyl) -naphth-1-yl] -4,6-bis-trick Rumethyl-S-triazine, 2- (4,7-dimethoxy-naphth-1-yl) -4,6-bis-trichloromethyl-S-triazine, 2- (acenaphtho-5-yl) -4,6-bis Examples include compounds described in German Patent No. 3337024, such as -trichloromethyl-S-triazine, and the like.
[0131]
Embedded image

[0132]
Embedded image

[0133]
F.F. C. By Schaefer et al. Org. Chem. 29, 1527 (1964), such as 2-methyl-4,6-bis (tribromomethyl) -S-triazine, 2,4,6-tris (tribromomethyl) -S-triazine, 2, 4,6-tris (dibromomethyl) -S-triazine, 2-amino-4-methyl-6-tribromomethyl-S-triazine, 2-methoxy-4-methyl-6-trichloromethyl-S-triazine, etc. be able to.
[0134]
Further, compounds described in JP-A No. 62-58241, for example, the following compounds can be mentioned.
[0135]
Embedded image

[0136]
Embedded image

[0137]
Further, compounds described in JP-A-5-281728, for example, the following compounds can be mentioned.
[0138]
Embedded image

[0139]
(2) Titanocenes
The titanocene compound that is particularly preferably used as the activator may be any titanocene compound that can generate an active species when irradiated with light in the presence of the above-described sensitizing dye. JP 59-152396, JP 61-151197, JP 63-41483, JP 63-41484, JP 2-249, JP 2-291, JP 3-27393 Known compounds described in JP-A-3-12403 and JP-A-6-41170 can be appropriately selected and used.
[0140]
More specifically, di-cyclopentadienyl-Ti-di-chloride, di-cyclopentadienyl-Ti-bis-phenyl, di-cyclopentadienyl-Ti-bis-2,3,4,5 , 6-pentafluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,3,5,6-tetrafluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2 , 4,6-trifluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,6-difluorophen-1-yl, di-cyclopentadienyl-Ti-bis-2,4 -Difluorophenyl-1-yl, di-methylcyclopentadienyl-Ti-bis-2,3,4,5,6-pentafluorophen-1-yl, di-methylcyclopentadienyl-Ti- Bis-2, 3, , 6-tetrafluorophenyl-1-yl, di-methylcyclopentadienyl-Ti-bis-2,4-difluorophen-1-yl, bis (cyclopentadienyl) -bis (2,6- And difluoro-3- (pyr-1-yl) phenyl) titanium.
[0141]
(3) Borate salt compound
Borate salts represented by the following general formula [II] are excellent in radical generating ability.
[0142]
Embedded image

[0143]
In general formula [II], R⁵¹, R⁵², R⁵³And R⁵⁴May be the same as or different from each other, and each represents a substituted or unsubstituted alkyl group, a substituted or unsubstituted aryl group, a substituted or unsubstituted alkenyl group, a substituted or unsubstituted alkynyl group, or a substituted or unsubstituted heterocyclic group. Represents a cyclic group, R⁵¹, R⁵², R⁵³And R⁵⁴The two or more groups may combine to form a cyclic structure. However, R⁵¹, R⁵², R⁵³And R⁵⁴Of these, at least one is a substituted or unsubstituted alkyl group. Z⁺Represents an alkali metal cation or a quaternary ammonium cation.
[0144]
R above⁵¹~ R⁵⁴Examples of the alkyl group include linear, branched, and cyclic groups, and those having 1 to 18 carbon atoms are preferable. Specifically, methyl, ethyl, propyl, isopropyl, butyl, pentyl, hexyl, octyl, stearyl, cyclobutyl, cyclopentyl, cyclohexyl and the like are included. Examples of the substituted alkyl group include the above alkyl groups, halogen atoms (for example, -Cl, -Br, etc.), cyano groups, nitro groups, aryl groups (preferably phenyl groups), hydroxy groups, the following groups,
[0145]
Embedded image

[0146]
(Where R⁵⁵, R⁵⁶Independently represents a hydrogen atom, an alkyl group having 1 to 14 carbon atoms, or an aryl group. ), -COOR⁵⁷(Where R⁵⁷Represents a hydrogen atom, an alkyl group having 1 to 14 carbon atoms, or an aryl group. ), -COOR⁵⁸Or -OR⁵⁹(Where R⁵⁸Represents an alkyl group having 1 to 14 carbon atoms or an aryl group. ) As a substituent.
[0147]
R above⁵¹~ R⁵⁴Examples of the aryl group include 1 to 3 ring aryl groups such as a phenyl group and a naphthyl group, and the substituted aryl group includes a substituent of the above-described substituted alkyl group or a carbon number of 1 as described above. Those having ˜14 alkyl groups are included.
[0148]
R above⁵¹~ R⁵⁴Examples of the alkenyl group include straight-chain, branched, and cyclic groups having 2 to 18 carbon atoms, and examples of the substituent of the substituted alkenyl group include those listed above as the substituents of the substituted alkyl group.
[0149]
R above⁵¹~ R⁵⁴Examples of the alkynyl group include linear or branched groups having 2 to 28 carbon atoms, and examples of the substituent of the substituted alkynyl group include those exemplified as the substituent of the substituted alkyl group.
[0150]
In addition, the above R⁵¹~ R⁵⁴Examples of the heterocyclic group include a 5- or more-membered heterocyclic group containing at least one of N, S and O, preferably a 5- to 7-membered heterocyclic group, and this heterocyclic group includes a condensed ring. Also good. Furthermore, you may have what was mentioned as a substituent of the above-mentioned substituted aryl group as a substituent.
[0151]
Specific examples of the compound represented by the general formula [II] include compounds described in U.S. Pat. Nos. 3,567,453 and 4,434,891, European Patent Nos. 109772 and 109773, and those shown below.
[0152]
Embedded image

[0153]
(4) Hexaarylbiimidazoles
Excellent stability and highly sensitive radical generation is possible. Specifically, 2,2′-bis (o-chlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o-bromophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o, p-dichlorophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o-chlorophenyl) -4,4 ', 5,5'-tetra (m-methoxyphenyl) biimidazole, 2,2'-bis (o, o'-dichlorophenyl) -4,4', 5,5'-tetraphenylbiimidazole 2,2′-bis (o-nitrophenyl) -4,4 ′, 5,5′-tetraphenylbiimidazole, 2,2′-bis (o-methylphenyl) -4,4 ′, 5,5 '-Tetraphenylbiimidazole, 2, 2' Bis (o-trifluoromethylphenyl) -4,4 ', 5,5'-tetraphenyl biimidazole.
[0154]
(5) Onium salt compounds
15 (5B), 16 (6B), and 17 (7B) group elements of the periodic table, specifically, onium compounds of N, P, As, Sb, Bi, O, S, Se, Te, and I are sensitive. It is an excellent activator. In particular, iodonium salts and sulfonium salts, particularly diaryl iodonium and triaryl sulfonium salt compounds, are extremely excellent in terms of both sensitivity and storage stability. Acids and / or radicals can be generated, and these can be used properly by appropriately selecting the use conditions according to the purpose. Specific examples include the following compounds.
[0155]
Embedded image

[0156]
Embedded image

[0157]
Embedded image

[0158]
Embedded image

[0159]
(6) Organic peroxide
When an organic peroxide type activator is used, radical generation as an active species can be performed with very high sensitivity.
[0160]
“Organic peroxide” includes almost all organic compounds having one or more oxygen-oxygen bonds in the molecule. Examples thereof include methyl ethyl ketone peroxide, cyclohexanone peroxide, 3,3,5- Trimethylcyclohexanone peroxide, methylcyclohexanone peroxide, acetylacetone peroxide, 1,1-bis (t-butylperoxy) -3,3,5-trimethylcyclohexane, 1,1-bis (t-butylperoxy) cyclohexane, 2,2-bis (t-butylperoxy) butane, t-butyl hydroperoxide, cumene hydroperoxide, diisopropylbenzene hydroperoxide, parameterone hydroperoxide, 2,5-dimethylhexane-2,5-diha Dropper oxide, 1,1,3,3-tetramethylbutyl hydroperoxide, di-t-butyl peroxide, t-butylcumyl peroxide, dicumyl peroxide, bis (t-butylperoxyisopropyl) benzene, 2,5-dimethyl-2,5-di (t-butylperoxy) hexane, 2,5-dimethyl-2,5-di (t-butylperoxy) hexyne-3, acetyl peroxide, isobutyryl peroxide , Octanoyl peroxide, decanoyl peroxide, lauroyl peroxide, 3,5,5-trimethylhexanoyl peroxide, succinic peroxide, benzoyl peroxide, 2,4-dichlorobenzoyl peroxide, meta-toluoyl peroxide Oxide, diisopropyl peroxydicarbo , Di-2-ethylhexyl peroxydicarbonate, di-2-ethoxyethyl peroxydicarbonate, dimethoxyisopropyl peroxycarbonate, di (3-methyl-3-methoxybutyl) peroxydicarbonate, t-butyl percarbonate Oxyacetate, t-butylperoxypivalate, t-butylperoxyneodecanoate, t-butylperoxyoctanoate, t-butylperoxy-3,5,5-trimethylhexanoate, t-butyl Peroxylaurate, t-butylperoxybenzoate, di-t-butylperoxyisophthalate, 2,5-dimethyl-2,5-di (benzoylperoxy) hexane, t-butylmaleic acid, t- Butyl peroxyisopropyl carbonate, 3,3 ', 4,4 '-Tetra- (t-butylperoxycarbonyl) benzophenone, 3,3', 4,4'-tetra- (t-amylperoxycarbonyl) benzophenone, 3,3 ', 4,4'-tetra (t- (Hexylperoxycarbonyl) benzophenone, 3,3 ′, 4,4′-tetra (t-octylperoxycarbonyl) benzophenone, 3,3 ′, 4,4′-tetra (cumylperoxycarbonyl) benzophenone, 3,3 Examples include ', 4,4'-tetra (p-isopropylcumylperoxycarbonyl) benzophenone, carbonyldi (t-butylperoxydihydrogen diphthalate), and carbonyldi (t-hexylperoxydihydrogendiphthalate).
[0161]
Among these, 3,3 ′, 4,4′-tetra- (t-butylperoxycarbonyl) benzophenone, 3,3 ′, 4,4′-tetra- (t-amylperoxycarbonyl) benzophenone, 3 , 3 ′, 4,4′-tetra (t-hexylperoxycarbonyl) benzophenone, 3,3 ′, 4,4′-tetra (t-octylperoxycarbonyl) benzophenone, 3,3 ′, 4,4 ′ Peroxide esters such as tetra (cumylperoxycarbonyl) benzophenone, 3,3 ′, 4,4′-tetra (p-isopropylcumylperoxycarbonyl) benzophenone, di-t-butyldiperoxyisophthalate are preferred. .
[0162]
As with the sensitizing dyes described above, various chemical modifications for improving the characteristics of the photosensitive layer can also be carried out with respect to the activator described above. For example, bonding with sensitizing dyes, addition polymerizable unsaturated compounds and other active agent parts, introduction of hydrophilic sites, compatibility improvement, introduction of substituents to suppress crystal precipitation, introduction of substituents to improve adhesion A method such as polymerization can be used.
[0163]
The use method of these activator compounds can be arbitrarily set as appropriate depending on the performance design of the light-sensitive material as in the case of the sensitizing dye described above. For example, the compatibility with the photosensitive layer can be enhanced by using two or more kinds in combination. A larger amount of the activator compound is usually advantageous in terms of photosensitivity, and is used in an amount of 0.5 to 80 parts by weight, preferably 1 to 50 parts by weight, based on 100 parts by weight of the photosensitive layer component. Sufficient photosensitivity can be obtained. On the other hand, when the active agent itself absorbs visible light, such as a titanocene compound, the amount of the active agent used from the viewpoint of fogging by light near 500 nm when used under a yellow or white light. However, the amount of the activator compound used in combination with the sensitizing dye of the present invention may be 6 parts by weight or less, further 1.9 parts by weight or less, and even 1.4 parts by weight or less. Sufficient photosensitivity can be obtained.
[0164]
[B. Ingredient (iii)]
The third essential component (iii) in the present invention is a compound whose physical or chemical properties are irreversibly changed by the action of the active species generated by the photoreaction of the above-described photoinitiating system, and the component (iii) ) Can be used without particular limitation as long as it has such properties. For example, the compounds listed in the above-mentioned initiation system themselves often have such properties. The properties of the component (iii) that changes due to radicals, acids, and / or bases generated from the photoinitiating system include, for example, molecular properties such as absorption spectrum (color), chemical structure, polarizability, and solubility. Changes in material properties such as strength, refractive index, fluidity, and adhesiveness.
[0165]
For example, as a component (iii), if a compound whose absorption spectrum changes with pH, such as a pH indicator, is used and an acid or base is generated from the initiation system, the color of only the exposed area can be changed. Such a composition is useful as an image forming material. Similarly, when a compound whose absorption spectrum is changed by oxidation / reduction or nucleophilic addition reaction is used as (iii), it is possible to form an image by causing oxidation or reduction by radicals generated from the initiation system. Such examples are described, for example, in J. Org. Am. Chem. Soc. 108, 128 (1986); Imaging. Sci. , 30, 215 (1986), Israel. J. et al. Chem. 25, 264 (1986).
[0166]
Moreover, a photocurable resin or a negative photopolymer can be formed by using a compound capable of addition polymerization or polycondensation as (iii) and combining with a starting system.
[0167]
As (iii), a radical polymerizable compound (such as a compound having an ethylenically unsaturated bond), a cationic polymerizable compound (such as an epoxy compound, a vinyl ether compound, or a methylol compound) or an anion polymerizable compound (such as an epoxy compound) is used. Such examples are described in, for example, Photopolymer Social Meeting, Photopolymer Handbook, Industrial Research Committee (1989), Polymers, 45,786 (1996). Etc. are described. Further, a composition using a thiol compound as (iii) and combined with a photo radical generating system is also well known.
[0168]
It is also useful to use an acid-decomposable compound as (iii) and combine it with a photoacid generator. For example, a material that uses a polymer whose side chain or main chain is decomposed by an acid and changes its solubility or hydrophilicity / hydrophobicity by light is widely used as a photodegradable photosensitive resin or a positive photopolymer. Such a specific example is, for example, ACS. Symp. Ser. 242, 11 (1984). JP-A-60-3625, USP-5102771, JP-A-5206317, JP-A-512047, JP-A-4-26850, JP-A-3-1921731, JP-A-60-10247, JP-A-62-245050. Issue.
[0169]
Hereinafter, the addition-polymerizable compound, which is a component (iii) particularly excellent for the purpose of obtaining a highly sensitive lithographic printing plate, which is one of the objects of the present invention, will be described in more detail.
[0170]
(B-1) Addition polymerizable compound
The addition polymerizable compound having at least one ethylenically unsaturated double bond, which is a preferred component (iii) used in the present invention, is a compound having at least one terminal ethylenically unsaturated bond, preferably two or more. Chosen from. Such compound groups are widely known in the industrial field, and these can be used without any particular limitation in the present invention. These have chemical forms such as monomers, prepolymers, i.e. dimers, trimers and oligomers, or mixtures thereof and copolymers thereof. Examples of monomers and copolymers thereof include unsaturated carboxylic acids (for example, acrylic acid, methacrylic acid, itaconic acid, crotonic acid, isocrotonic acid, maleic acid, etc.), and esters and amides thereof. In this case, an ester of an unsaturated carboxylic acid and an aliphatic polyhydric alcohol compound, or an amide of an unsaturated carboxylic acid and an aliphatic polyvalent amine compound is used. In addition, unsaturated carboxylic acid ester having a nucleophilic substituent such as hydroxyl group, amino group, mercapto group, amide and monofunctional or polyfunctional isocyanate, addition reaction product of epoxy, monofunctional or polyfunctional A dehydration condensation reaction product with a functional carboxylic acid is also preferably used. In addition, an unsaturated carboxylic acid ester having an electrophilic substituent such as an isocyanato group or an epoxy group, an addition reaction product of an amide with a monofunctional or polyfunctional alcohol, an amine or a thiol, a halogen group Also suitable are substitution reaction products of unsaturated carboxylic acid esters, amides with monofunctional or polyfunctional alcohols, amines, and thiols having a leaving substituent such as a tosyloxy group. As another example, it is also possible to use a group of compounds substituted with unsaturated phosphonic acid, styrene, vinyl ether or the like instead of the unsaturated carboxylic acid.
[0171]
Specific examples of the monomer of an ester of an aliphatic polyhydric alcohol compound and an unsaturated carboxylic acid include acrylic acid esters such as ethylene glycol diacrylate, triethylene glycol diacrylate, 1,3-butanediol diacrylate, and tetramethylene glycol. Diacrylate, propylene glycol diacrylate, neopentyl glycol diacrylate, trimethylolpropane triacrylate, trimethylolpropane tri (acryloyloxypropyl) ether, trimethylolethane triacrylate, hexanediol diacrylate, 1,4-cyclohexanediol diacrylate , Tetraethylene glycol diacrylate, pentaerythritol diacrylate, pentaerythritol triacrylate , Pentaerythritol tetraacrylate, dipentaerythritol diacrylate, dipentaerythritol hexaacrylate, sorbitol triacrylate, sorbitol tetraacrylate, sorbitol pentaacrylate, sorbitol hexaacrylate, tri (acryloyloxyethyl) isocyanurate, polyester acrylate oligomer.
[0172]
Methacrylic acid esters include tetramethylene glycol dimethacrylate, triethylene glycol dimethacrylate, neopentyl glycol dimethacrylate, trimethylolpropane trimethacrylate, trimethylolethane trimethacrylate, ethylene glycol dimethacrylate, 1,3-butanediol dimethacrylate, Hexanediol dimethacrylate, pentaerythritol dimethacrylate, pentaerythritol trimethacrylate, pentaerythritol tetramethacrylate, dipentaerythritol dimethacrylate, dipentaerythritol hexamethacrylate, sorbitol trimethacrylate, sorbitol tetramethacrylate, bis [p- (3-methacryloxy- 2-hydroxypro ) Phenyl] dimethyl methane, bis - [p- (methacryloxyethoxy) phenyl] dimethyl methane.
[0173]
Itaconic acid esters include ethylene glycol diitaconate, propylene glycol diitaconate, 1,3-butanediol diitaconate, 1,4-butanediol diitaconate, tetramethylene glycol diitaconate, pentaerythritol diitaconate And sorbitol tetritaconate.
[0174]
Examples of crotonic acid esters include ethylene glycol dicrotonate, tetramethylene glycol dicrotonate, pentaerythritol dicrotonate, and sorbitol tetradicrotonate.
[0175]
Examples of isocrotonic acid esters include ethylene glycol diisocrotonate, pentaerythritol diisocrotonate, and sorbitol tetraisocrotonate.
[0176]
Examples of maleic acid esters include ethylene glycol dimaleate, triethylene glycol dimaleate, pentaerythritol dimaleate, and sorbitol tetramaleate.
[0177]
Examples of other esters include aliphatic alcohol esters described in JP-B-46-27926, JP-B-51-47334, JP-A-57-196231, JP-A-59-5240, JP Those having an aromatic skeleton described in JP-A-59-5241 and JP-A-2-226149, those containing an amino group described in JP-A-1-165613, and the like are also preferably used.
[0178]
Furthermore, the ester monomers described above can also be used as a mixture.
[0179]
Specific examples of amide monomers of aliphatic polyvalent amine compounds and unsaturated carboxylic acids include methylene bis-acrylamide, methylene bis-methacrylamide, 1,6-hexamethylene bis-acrylamide, 1,6-hexamethylene bis. -Methacrylamide, diethylenetriamine trisacrylamide, xylylene bisacrylamide, xylylene bismethacrylamide and the like.
[0180]
Examples of other preferable amide monomers include those having a cyclohexylene structure described in JP-B No. 54-21726.
[0181]
In addition, urethane-based addition polymerizable compounds produced by using an addition reaction of isocyanate and hydroxyl group are also suitable, and specific examples thereof include, for example, one molecule described in JP-B-48-41708. A vinyl urethane containing two or more polymerizable vinyl groups in one molecule obtained by adding a vinyl monomer containing a hydroxyl group represented by the following general formula (III) to a polyisocyanate compound having two or more isocyanate groups. Compounds and the like.
[0182]
CH₂= C (R) COOCH₂CH (R ') OH (III)
[0183]
(However, R and R 'are H or CH.₃Indicates. )
[0184]
Also, urethane acrylates such as those described in JP-A-51-37193, JP-B-2-32293, and JP-B-2-16765, JP-B-58-49860, JP-B-56-17654, Urethane compounds having an ethylene oxide skeleton described in JP-B-62-39417 and JP-B-62-39418 are also suitable.
[0185]
Further, by using addition polymerizable compounds having an amino structure or a sulfide structure in the molecule described in JP-A-63-277653, JP-A-63-260909, and JP-A-1-105238, It is possible to obtain a photopolymerizable composition excellent in the photosensitive speed.
[0186]
Other examples include polyester acrylates, epoxy resins and (meth) acrylic acid as described in JP-A-48-64183, JP-B-49-43191, JP-B-52-30490, and JP-A-52-30490. Mention may be made of polyfunctional acrylates and methacrylates such as reacted epoxy acrylates. Further, specific unsaturated compounds described in JP-B-46-43946, JP-B-1-40337 and JP-B-1-40336, vinylphosphonic acid compounds described in JP-A-2-25493, and the like can also be mentioned. . In some cases, a structure containing a perfluoroalkyl group described in JP-A-61-22048 is preferably used. Furthermore, Journal of Japan Adhesion Association vol. 20, no. 7, pages 300 to 308 (1984), which are introduced as photocurable monomers and oligomers, can also be used.
[0187]
For these addition-polymerizable compounds, details of how to use, such as what type of structure to use, whether to use alone or in combination, how much is added, etc., according to the performance design of the final photosensitive material, Can be set arbitrarily. For example, it is selected from the following viewpoints. From the viewpoint of photosensitive speed, a structure having a high unsaturated group content per molecule is preferable, and in many cases, a bifunctional or higher functionality is preferable. Further, in order to increase the strength of the image portion, that is, the cured film, those having three or more functionalities are preferable, and furthermore, different functional numbers and different polymerizable groups (for example, acrylic acid ester, methacrylic acid ester, styrenic compound, vinyl ether type). A method of adjusting both photosensitivity and strength by using the compound) together is also effective. A compound having a large molecular weight or a compound having a high hydrophobicity is not preferable in terms of development speed and precipitation in a developing solution, although it is excellent in photosensitive speed and film strength. In addition, the selection and use method of the addition polymerization compound is also an important factor for the compatibility and dispersibility with other components in the photosensitive layer (for example, binder polymer, initiator, colorant, etc.). The compatibility may be improved by using a low-purity compound or using two or more kinds in combination. In addition, a specific structure may be selected for the purpose of improving the adhesion of the support, overcoat layer and the like. Regarding the compounding ratio of the addition polymerizable compound in the photosensitive layer, a larger amount is more advantageous in terms of sensitivity, but if it is too much, an undesirable phase separation occurs or a problem in the production process due to the adhesiveness of the photosensitive layer. For example, problems such as transfer of photosensitive material components and manufacturing defects due to adhesion, and precipitation from a developer may occur. From these viewpoints, the preferred blending ratio is often 5 to 80% by weight, preferably 25 to 75% by weight, based on the total components of the composition. These may be used alone or in combination of two or more. In addition, the use method of the addition polymerizable compound can be arbitrarily selected from the viewpoint of polymerization inhibition with respect to oxygen, resolution, fogging, refractive index change, surface adhesiveness, etc. Depending on the case, a layer configuration and coating method such as undercoating and overcoating can be performed.
[0188]
[Binder polymer]
In application to a lithographic printing plate, which is a preferred embodiment of the present invention, it is preferable to further use a binder polymer in the photosensitive composition. The binder preferably contains a linear organic high molecular polymer. Any such “linear organic polymer” may be used. Preferably, a linear organic high molecular weight polymer that is soluble in water or weakly alkaline water or swellable that enables water development or weak alkaline water development is selected. The linear organic high molecular polymer is selected and used not only as a film-forming agent for the composition but also according to its use as water, weak alkaline water or an organic solvent developer. For example, when a water-soluble organic polymer is used, water development is possible. Examples of such linear organic high molecular polymers include addition polymers having a carboxylic acid group in the side chain, such as JP 59-44615, JP-B 54-34327, JP-B 58-12777, and JP-B. 54-25957, JP-A-54-92723, JP-A-59-53836, JP-A-59-71048, ie, methacrylic acid copolymer, acrylic acid copolymer, itacon Examples include acid copolymers, crotonic acid copolymers, maleic acid copolymers, and partially esterified maleic acid copolymers. Similarly, there is an acidic cellulose derivative having a carboxylic acid group in the side chain. In addition, those obtained by adding a cyclic acid anhydride to an addition polymer having a hydroxyl group are useful.
[0189]
Among these, [benzyl (meth) acrylate / (meth) acrylic acid / other addition polymerizable vinyl monomers as required] copolymer and [allyl (meth) acrylate / (meth) acrylic acid / as required Other addition-polymerizable vinyl monomers] are preferred because they are excellent in the balance of film strength, sensitivity and developability.
[0190]
In addition, Japanese Patent Publication No. 7-2004, Japanese Patent Publication No. 7-120041, Japanese Patent Publication No. 7-120042, Japanese Patent Publication No. 8-12424, Japanese Patent Laid-Open No. 63-287944, Japanese Patent Laid-Open No. 63-287947, Japanese Patent Laid-Open No. The urethane-based binder polymer containing an acid group described in Japanese Patent No. 271741 and Japanese Patent Application No. 10-116232 is very excellent in strength, and is advantageous in terms of printing durability and low exposure suitability. .
[0191]
A binder having an amide group described in JP-A No. 11-171907 is suitable because it has excellent developability and film strength.
[0192]
In addition, polyvinyl pyrrolidone, polyethylene oxide, and the like are useful as the water-soluble linear organic polymer. In order to increase the strength of the cured film, alcohol-soluble nylon, polyether of 2,2-bis- (4-hydroxyphenyl) -propane and epichlorohydrin, and the like are also useful. These linear organic high molecular polymers can be mixed in an arbitrary amount in the entire composition. However, when it exceeds 90% by weight, a favorable result is not given in terms of the strength of the formed image. Preferably it is 30 to 85% by weight. The weight ratio of the compound having a photopolymerizable ethylenically unsaturated double bond and the linear organic polymer is preferably 1/9 to 7/3. In a preferred embodiment, a binder polymer that does not require water and is soluble in alkali is used. By doing so, an organic solvent that is not environmentally preferable is not used as the developer, or the amount can be limited to a very small amount. In such a method of use, the acid value of the binder polymer (the acid content per gram of polymer expressed as a chemical equivalent number) and the molecular weight are appropriately selected from the viewpoint of image strength and developability. The preferred acid value is 0.4 to 3.0 meq / g, and the preferred molecular weight is in the range of 3000 to 500,000 in terms of weight average molecular weight, more preferably the acid value is 0.6 to 2.0 and the molecular weight is It is in the range of 10,000 to 300,000.
[0193]
[C. Other ingredients
To the photosensitive composition of the present invention, other components suitable for its use and production method can be added as appropriate. Hereinafter, preferred additives will be exemplified.
[0194]
(C1) Co-sensitizer
Sensitivity can be further improved by using a certain additive (hereinafter referred to as a co-sensitizer). These mechanisms of action are not clear, but many are thought to be based on the following chemical processes. That is, co-sensitization with a variety of intermediate active species (radicals, peroxides, oxidizing agents, reducing agents, etc.) generated in the course of the photoreaction initiated by light absorption of the initiation system described above and the subsequent addition polymerization reaction. It is presumed that the agent reacts to generate new active radicals. These can be broadly divided into (a) those that can be reduced to generate active radicals, (b) those that can be oxidized to generate active radicals, and (c) radicals that are more active by reacting with less active radicals. Can be categorized as those that act as chain transfer agents, but there is often no generality as to which of these individual compounds belong.
[0195]
(A) Compound that is reduced to produce an active radical
Compound having carbon-halogen bond: It is considered that the carbon-halogen bond is reductively cleaved to generate an active radical. Specifically, for example, trihalomethyl-s-triazines and trihalomethyloxadiazoles can be preferably used.
[0196]
Compound having nitrogen-nitrogen bond: It is considered that the nitrogen-nitrogen bond is reductively cleaved to generate an active radical. Specifically, hexaarylbiimidazoles and the like are preferably used.
[0197]
Compound having oxygen-oxygen bond: It is considered that the oxygen-oxygen bond is reductively cleaved to generate an active radical. Specifically, for example, organic peroxides are preferably used.
[0198]
Onium compounds: It is considered that carbon-hetero bonds and oxygen-nitrogen bonds are reductively cleaved to generate active radicals. Specifically, for example, diaryliodonium salts, triarylsulfonium salts, N-alkoxypyridinium (azinium) salts and the like are preferably used.
Ferrocene and iron arene complexes: An active radical can be reductively generated.
[0199]
(B) Compounds that are oxidized to produce active radicals
Alkylate complex: It is considered that an active radical is generated by oxidative cleavage of a carbon-hetero bond. Specifically, for example, triarylalkyl borates are preferably used.
[0200]
Alkylamine compound: It is considered that the C—X bond on carbon adjacent to nitrogen is cleaved by oxidation to generate an active radical. X is preferably a hydrogen atom, a carboxyl group, a trimethylsilyl group, a benzyl group or the like. Specific examples include ethanolamines, N-phenylglycines, N-trimethylsilylmethylanilines, and the like.
[0201]
Sulfur-containing and tin-containing compounds: Compounds in which the nitrogen atoms of the above-described amines are replaced with sulfur atoms and tin atoms can generate active radicals by the same action. Further, a compound having an SS bond is also known to be sensitized by SS cleavage.
[0202]
α-Substituted methylcarbonyl compound: An active radical can be generated by oxidative cleavage of the carbonyl-α carbon bond. Moreover, what converted carbonyl into the oxime ether also shows the same effect | action. Specifically, 2-alkyl-1- [4- (alkylthio) phenyl] -2-morpholinopronone-1 and these and a hydroxylamine were reacted, and then N—OH was etherified. Mention may be made of oxime ethers.
[0203]
Sulfinic acid salts: An active radical can be reductively generated. Specific examples include sodium arylsulfinate.
[0204]
c) Compounds that react with radicals to convert into highly active radicals or act as chain transfer agents: For example, a group of compounds having SH, PH, SiH, GeH in the molecule is used. These can donate hydrogen to low-activity radical species to generate radicals, or can be oxidized and then deprotonated to generate radicals. Specifically, 2-mercaptobenzimidazoles etc. are mentioned, for example.
[0205]
Many more specific examples of these co-sensitizers are described, for example, in JP-A-9-236913 as additives for the purpose of improving sensitivity. Some examples are shown below, but the present invention is not limited thereto. -TMS is a trimethylsilyl group.
[0206]
Embedded image

[0207]
These co-sensitizers can also be subjected to various chemical modifications for improving the characteristics of the photosensitive layer as in the case of the above sensitizing dye. For example, bonding with sensitizing dyes and activators, addition polymerizable unsaturated compounds and other parts, introduction of hydrophilic sites, compatibility improvement, introduction of substituents to suppress crystal precipitation, introduction of substituents to improve adhesion A method such as polymerization can be used.
[0208]
These co-sensitizers can be used alone or in combination of two or more. The amount used is 0.05 to 100 parts by weight, preferably 1 to 80 parts by weight, and more preferably 3 to 50 parts by weight with respect to 100 parts by weight of the compound having an ethylenically unsaturated double bond.
[0209]
(C2) Polymerization inhibitor
In the present invention, in addition to the above basic components, a small amount of heat is used to prevent unnecessary thermal polymerization of a compound having an ethylenically unsaturated double bond that can be polymerized during production or storage of the photosensitive composition. It is desirable to add a polymerization inhibitor. Suitable thermal polymerization inhibitors include hydroquinone, p-methoxyphenol, di-t-butyl-p-cresol, pyrogallol, t-butylcatechol, benzoquinone, 4,4'-thiobis (3-methyl-6-t-butylphenol ), 2,2′-methylenebis (4-methyl-6-tert-butylphenol), N-nitrosophenylhydroxyamine primary cerium salt and the like. The addition amount of the thermal polymerization inhibitor is preferably about 0.01% by weight to about 5% by weight with respect to the weight of the total composition. If necessary, a higher fatty acid derivative such as behenic acid or behenic acid amide may be added to prevent polymerization inhibition due to oxygen, and it may be unevenly distributed on the surface of the photosensitive layer in the course of drying after coating. . The amount of the higher fatty acid derivative added is preferably from about 0.5% to about 10% by weight of the total composition.
[0210]
(C3) Colorant, etc.
Further, a dye or pigment may be added for the purpose of coloring the photosensitive layer. Thereby, so-called plate inspection properties such as visibility after plate making and suitability for an image density measuring machine as a printing plate can be improved. As the colorant, many dyes cause a decrease in the sensitivity of the photopolymerization type photosensitive layer. Therefore, it is particularly preferable to use a pigment as the colorant. Specific examples include pigments such as phthalocyanine pigments, azo pigments, carbon black and titanium oxide, and dyes such as ethyl violet, crystal violet, azo dyes, anthraquinone dyes, and cyanine dyes. The amount of dye and pigment added is preferably about 0.5% to about 5% by weight of the total composition.
[0211]
(C4) Other additives
Furthermore, in order to improve the physical properties of the cured film, known additives such as inorganic fillers, other plasticizers, and oil-sensitizing agents that can improve the ink inking property on the surface of the photosensitive layer may be added.
[0212]
Examples of plasticizers include dioctyl phthalate, didodecyl phthalate, triethylene glycol dicaprylate, dimethyl glycol phthalate, tricresyl phosphate, dioctyl adipate, dibutyl sebacate, and triacetyl glycerin. 10% by weight or less based on the total weight of the compound having a polymerizable unsaturated double bond and the binder can be added.
[0213]
Further, for the purpose of improving the film strength (printing durability), which will be described later, a UV initiator, a thermal crosslinking agent, or the like can be added to enhance the effect of heating and exposure after development.
[0214]
In addition, it is possible to provide an additive and an intermediate layer for improving the adhesion between the photosensitive layer and the support, and improving the development removability of the unexposed photosensitive layer. For example, by adding or undercoating a compound having a relatively strong interaction with the substrate, such as a compound having a diazonium structure or a phosphone compound, adhesion can be improved and printing durability can be increased. By adding or undercoating a hydrophilic polymer such as acid or polysulfonic acid, the developability of the non-image area is improved, and the stain resistance can be improved.
[0215]
When the photopolymerizable composition of the present invention is applied on a support, it is dissolved in various organic solvents and used. Solvents used here include acetone, methyl ethyl ketone, cyclohexane, ethyl acetate, ethylene dichloride, tetrahydrofuran, toluene, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol dimethyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether, Acetylacetone, cyclohexanone, diacetone alcohol, ethylene glycol monomethyl ether acetate, ethylene glycol ethyl ether acetate, ethylene glycol monoisopropyl ether, ethylene glycol monobutyl ether acetate, 3-methoxypropanol, methoxymethoxyethanol, diethylene glycol monomethyl ether, Ethylene glycol monoethyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, 3-methoxypropyl acetate, N, N-dimethylformamide, dimethyl sulfoxide, γ-butyrolactone, methyl lactate, lactic acid There are ethyl and the like. These solvents can be used alone or in combination. The solid content in the coating solution is suitably 2 to 50% by weight.
[0216]
The coating amount of the support of the photosensitive layer mainly affects the sensitivity of the photosensitive layer, the developability, the strength and the printing durability of the exposed film, and is preferably selected appropriately depending on the application. When the coating amount is too small, the printing durability is not sufficient. On the other hand, if the amount is too large, the sensitivity is lowered, it takes time for exposure, and a longer time is required for development processing, which is not preferable. The lithographic printing plate for scanning exposure, which is the main object of the present invention, has a coating amount of about 0.1 g / m by weight after drying.²~ About 10g / m²The range of is appropriate. More preferably 0.5 to 5 g / m²It is.
[0217]
[Support]
In order to obtain a lithographic printing plate, which is one of the main objects of the present invention, it is desirable to provide the photosensitive layer on a support having a hydrophilic surface. As the hydrophilic support, a conventionally known hydrophilic support for use in a lithographic printing plate can be used without limitation. The support used is preferably a dimensionally stable plate, for example, paper, paper laminated with plastic (eg, polyethylene, polypropylene, polystyrene, etc.), metal plate (eg, aluminum, zinc). , Copper, etc.), plastic films (eg, cellulose diacetate, cellulose triacetate, cellulose propionate, cellulose butyrate, cellulose acetate butyrate, cellulose nitrate, polyethylene terephthalate, polyethylene, polystyrene, polypropylene, polycarbonate, polyvinyl acetal, etc.), Such as paper or plastic film laminated or vapor-deposited with metal, and known physical and chemical treatments suitable for the purpose of imparting hydrophilicity and improving the strength as necessary. May be applied.
[0218]
In particular, preferred supports include paper, polyester film or aluminum plate, among which dimensional stability is good, relatively inexpensive, and a surface with excellent hydrophilicity and strength is provided by surface treatment as needed. An aluminum plate which can be used is particularly preferred. A composite sheet in which an aluminum sheet is bonded on a polyethylene terephthalate film as described in Japanese Patent Publication No. 48-18327 is also preferable.
[0219]
A suitable aluminum plate is a pure aluminum plate or an alloy plate containing aluminum as a main component and containing a trace amount of foreign elements, and may be a plastic film on which aluminum is laminated or vapor-deposited. Examples of foreign elements contained in the aluminum alloy include silicon, iron, manganese, copper, magnesium, chromium, zinc, bismuth, nickel, and titanium. The content of foreign elements in the alloy is at most 10% by weight. Particularly suitable aluminum in the present invention is pure aluminum, but completely pure aluminum is difficult to produce in the refining technique, and may contain slightly different elements. Thus, the composition of the aluminum plate applied to the present invention is not specified, and an aluminum plate made of a publicly known material can be appropriately used. The thickness of the aluminum plate used in the present invention is about 0.1 mm to 0.6 mm, preferably 0.15 mm to 0.4 mm, and particularly preferably 0.2 mm to 0.3 mm.
[0220]
In the case of a support having a surface of metal, particularly aluminum, roughening (graining) treatment, immersion treatment in an aqueous solution of sodium silicate, potassium fluoride zirconate, phosphate, etc., or anodic oxidation treatment, etc. It is preferable that surface treatment is performed.
[0221]
The surface roughening treatment of the aluminum plate is performed by various methods. For example, a method of mechanically roughening, a method of electrochemically dissolving and roughening a surface, and a method of selectively dissolving a surface chemically. This is done by the method of As the mechanical method, a known method such as a ball polishing method, a brush polishing method, a blast polishing method, or a buff polishing method can be used. In addition, as an electrochemical surface roughening method, there is a method of performing alternating current or direct current in an electrolytic solution such as hydrochloric acid or nitric acid. Further, as disclosed in JP-A-54-63902, a method in which both are combined can also be used. Further, prior to roughening the aluminum plate, for example, a degreasing treatment with a surfactant, an organic solvent, an alkaline aqueous solution, or the like is performed in order to remove rolling oil on the surface, if desired.
[0222]
Furthermore, an aluminum plate that has been roughened and then immersed in an aqueous sodium silicate solution can be preferably used. As described in Japanese Examined Patent Publication No. 47-5125, an aluminum plate which has been anodized and then immersed in an aqueous solution of an alkali metal silicate is preferably used. The anodizing treatment is carried out in an electrolytic solution in which an inorganic acid such as phosphoric acid, chromic acid, sulfuric acid or boric acid, or an organic acid such as oxalic acid or sulfamic acid, or a salt solution thereof, or a combination of two or more thereof, is used. This is carried out by passing an electric current using the aluminum plate as an anode.
[0223]
Silicate electrodeposition as described in US Pat. No. 3,658,662 is also effective.
[0224]
Further, a combination of a support with electrolytic grain as disclosed in JP-B-46-27481, JP-A-52-58602, JP-A-52-30503, and the above-described anodizing treatment and sodium silicate treatment is combined. Surface treatment is also useful.
[0225]
Further, those obtained by performing mechanical surface roughening, chemical etching, electrolytic graining, anodizing treatment, and sodium silicate treatment in this order as disclosed in JP-A-56-28893 are also suitable.
[0226]
Furthermore, after performing these treatments, water-soluble resins such as polyvinylphosphonic acid, polymers and copolymers having sulfonic acid groups in the side chain, polyacrylic acid, water-soluble metal salts (for example, zinc borate) or Those having a primer such as a yellow dye or an amine salt are also suitable.
[0227]
Further, a sol-gel treated substrate in which a functional group capable of causing an addition reaction by a radical as disclosed in JP-A-7-154983 is covalently used.
[0228]
Other preferred examples include those in which a water-resistant hydrophilic layer is provided as a surface layer on an arbitrary support. Examples of such a surface layer include a layer made of an inorganic pigment and a binder described in US Pat. No. 3,055,295 and JP-A-56-13168, a hydrophilic swelling layer described in JP-A-9-80744, and JP-A-8-507727. Examples thereof include sol-gel films made of the described titanium oxide, polyvinyl alcohol, and silicic acids.
[0229]
These hydrophilic treatments are performed to make the surface of the support hydrophilic, in order to prevent harmful reaction of the photopolymerizable composition provided thereon, and to improve the adhesion of the photosensitive layer. It is given for the purpose.
[0230]
[Protective layer]
In the lithographic printing plate for scanning exposure, which is a desirable mode of the present invention, it is usually preferable to provide a protective layer on the layer of the photopolymerizable composition in order to perform exposure in the air. Protective layer prevents exposure to oxygen and low molecular weight compounds such as basic substances in the atmosphere that hinder the image formation reaction caused by exposure in the photosensitive layer, allowing exposure in the atmosphere And Therefore, the properties desired for such a protective layer are low permeability of low-molecular compounds such as oxygen, and further, transmission of light used for exposure is not substantially inhibited and adhesion to the photosensitive layer is excellent. And it is desirable that it can be easily removed in the development step after exposure. Such a device for the protective layer has been conventionally devised, which is described in detail in US Pat. No. 3,458,311 and JP-A-55-49729. As a material that can be used for the protective layer, for example, a water-soluble polymer compound that is relatively excellent in crystallinity is preferably used. Specifically, polyvinyl alcohol, polyvinyl pyrrolidone, acidic celluloses, gelatin, gum arabic, Water-soluble polymers such as acrylic acid are known, but among these, the use of polyvinyl alcohol as a main component gives the best results in terms of basic properties such as oxygen barrier properties and development removability.
[0231]
The polyvinyl alcohol used for the protective layer may be partially substituted with an ester, an ether, and an acetal as long as it contains an unsubstituted vinyl alcohol unit for having necessary oxygen barrier properties and water solubility. Similarly, some of them may have other copolymer components. Specific examples of polyvinyl alcohol include those having a hydrolysis rate of 71 to 100 mol% and a molecular weight in the range of 300 to 2400 in terms of weight average molecular weight. Specifically, Kuraray Co., Ltd. PVA-105, PVA-110, PVA-117, PVA-117H, PVA-120, PVA-124, PVA-124H, PVA-CS, PVA-CST, PVA-HC, PVA-203, PVA-204, PVA-205, PVA-210, PVA-217, PVA-220, PVA-224, PVA-217EE, PVA-217E, PVA-220E, PVA-224E, PVA-405, PVA- 420, PVA-613, L-8 and the like.
[0232]
Components of the protective layer (selection of PVA, use of additives), coating amount, and the like are selected in consideration of fogging, adhesion, and scratch resistance in addition to oxygen barrier properties and development removability. In general, the higher the hydrolysis rate of the PVA used (the higher the content of the unsubstituted vinyl alcohol unit in the protective layer), the thicker the film thickness, the higher the oxygen barrier property, which is advantageous in terms of sensitivity. However, when the oxygen barrier property is extremely increased, there arises a problem that unnecessary polymerization reaction occurs during production and raw storage, and unnecessary fogging and image line thickening occur during image exposure. In addition, adhesion to the image area and scratch resistance are extremely important in handling the plate. That is, when a hydrophilic layer made of a water-soluble polymer is laminated on an oleophilic polymer layer, film peeling due to insufficient adhesion tends to occur, and the peeled part causes defects such as poor film hardening due to inhibition of oxygen polymerization. On the other hand, various proposals have been made to improve the adhesion between these two layers. For example, in U.S. Pat. Nos. 292501 and 44563, 20-60 wt% of an acrylic emulsion or a water-insoluble vinylpyrrolidone-vinyl acetate copolymer is mixed in a hydrophilic polymer mainly composed of polyvinyl alcohol. It is described that sufficient adhesion can be obtained by laminating on a polymerized layer. Any of these known techniques can be applied to the protective layer in the present invention. Such a coating method of the protective layer is described in detail in, for example, US Pat. No. 3,458,311 and JP-A-55-49729.
[0233]
Furthermore, other functions can be imparted to the protective layer. For example, by adding a colorant (such as a water-soluble dye) that is excellent in the transmission of light from 350 nm to 450 nm and that can absorb light of 500 nm or more, which is used for exposure, it is safe light without causing a decrease in sensitivity. Suitability can be further enhanced.
[0234]
When a photosensitive material using the photopolymerizable composition of the present invention is used as an image forming material, usually, after image exposure, an unexposed portion of the photosensitive layer is removed with a developer to obtain an image. Preferred developers when using these photopolymerizable compositions in the preparation of lithographic printing plates include those described in JP-B-57-7427, such as sodium silicate and potassium silicate. , Sodium hydroxide, potassium hydroxide, lithium hydroxide, tribasic sodium phosphate, dibasic sodium phosphate, tribasic ammonium phosphate, dibasic ammonium phosphate, sodium metasilicate, sodium bicarbonate, aqueous ammonia etc. An inorganic alkaline agent and an aqueous solution of an organic alkaline agent such as monoethanolamine or diethanolamine are suitable. Such an alkaline solution is added so that the concentration is 0.1 to 10% by weight, preferably 0.5 to 5% by weight.
[0235]
Such an alkaline aqueous solution may contain a small amount of a surfactant, an organic solvent such as benzyl alcohol, 2-phenoxyethanol, and 2-butoxyethanol as necessary. Examples thereof include those described in US Pat. Nos. 3,375,171 and 3,615,480.
[0236]
Further, the developers described in JP-A-50-26601, 58-54341, JP-B-56-39464, and 56-42860 are also excellent.
[0237]
As a particularly preferred developer, a nonionic compound represented by the following formula described in JP-A No. 2002-202616 is contained, the pH is 11.5 to 12.8, and 3 to 30 mS / cm. And a developer having the following conductivity.
[0238]
A-W (IV)
[0239]
In the formula, A represents a hydrophobic organic group having a log P of AH of 1.5 or more, and W represents a nonionic hydrophilic organic group having a log P of W-H of less than 1.0.
logP is C.I. Hansch, A.M. Leo, “Substituent Constants for Correlation Analysis in Chemistry and Biology”, J. Am. Wille & Sons, 1979. Equilibrium that is generally used as the described hydrophobicity parameter and calculated from the proportion distributed to each layer for the octanol / water bilayer system of the target molecule (AH and WH). It is defined as the logarithm of the concentration ratio P.
Here, it uses as a parameter | index which identifies each group of A and W in Formula (IV), and it has an AH and WH structure conveniently hydrogen-bonded to each organic group of A and W. In contrast, A. K. Gose, et. al. J. et al. Comput. Chem. 9, 80 (1988). Based on the described method, it is calculated from known data.
[0240]
Specifically, as the structure, the organic groups A and W are different from each other, and represent a monovalent organic residue that satisfies the above-mentioned logP. More preferably, they are the same or different from each other and may have a hydrogen atom, a halogen atom, a substituent, and may contain an unsaturated bond, a heterocyclic group, a hydroxyl group, a substituted oxy group. , Mercapto group, substituted thio group, amino group, substituted amino group, substituted carbonyl group, carboxylate group, sulfo group, sulfonate group, substituted sulfinyl group, substituted sulfonyl group, phosphono group, substituted phosphono group, phosphonato group, substituted phosphonate group Represents a cyano group or a nitro group.
[0241]
Examples of the hydrocarbon group which may have the above substituent and may contain an unsaturated bond include an alkyl group, a substituted alkyl group, an aryl group, a substituted aryl group, an alkenyl group, a substituted alkenyl group, and an alkynyl group. Groups and substituted alkynyl groups.
[0242]
Examples of the alkyl group include linear, branched, or cyclic alkyl groups having 1 to 20 carbon atoms. Specific examples thereof include a methyl group, an ethyl group, a propyl group, a butyl group, and pentyl. Group, hexyl group, heptyl group, octyl group, nonyl group, decyl group, undecyl group, dodecyl group, tridecyl group, hexadecyl group, octadecyl group, eicosyl group, isopropyl group, isobutyl group, s-butyl group, t-butyl group , Isopentyl group, neopentyl group, 1-methylbutyl group, isohexyl group, 2-ethylhexyl group, 2-methylhexyl group, cyclohexyl group, cyclopentyl group and 2-norbornyl group. Of these, linear alkyl groups having 1 to 12 carbon atoms, branched alkyl groups having 3 to 12 carbon atoms, and cyclic alkyl groups having 5 to 10 carbon atoms are more preferable.
[0243]
The substituted alkyl group is composed of a bond between a substituent and an alkylene group. As the substituent, a monovalent non-metallic atomic group other than hydrogen is used. Preferred examples include halogen atoms (—F, —Br, — Cl, -I), hydroxyl group, alkoxy group, aryloxy group, mercapto group, alkylthio group, arylthio group, alkyldithio group, aryldithio group, amino group, N-alkylamino group, N, N-dialkylamino group, N -Arylamino group, N, N-diarylamino group, N-alkyl-N-arylamino group, acyloxy group, carbamoyloxy group, N-alkylcarbamoyloxy group, N-arylcarbamoyloxy group, N, N-dialkylcarbamoyl Oxy group, N, N-diarylcarbamoyloxy group, N-alkyl-N-aryl Rubamoiruokishi group, alkyl sulfoxy group, aryl sulfoxy group, an acylthio group,
[0244]
Acylamino group, N-alkylacylamino group, N-arylacylamino group, ureido group, N'-alkylureido group, N ', N'-dialkylureido group, N'-arylureido group, N', N'- Diarylureido group, N'-alkyl-N'-arylureido group, N-alkylureido group, N-arylureido group, N'-alkyl-N-alkylureido group, N'-alkyl-N-arylureido group, N ′, N′-dialkyl-N-alkylureido group, N ′, N′-dialkyl-N-arylureido group, N′-aryl-N-alkylureido group, N′-aryl-N-arylureido group, N ′, N′-diaryl-N-alkylureido group, N ′, N′-diaryl-N-arylureido group, N′-alkyl-N ′ Aryl -N- alkylureido group, N'- alkyl -N'- aryl -N- arylureido group,
[0245]
Alkoxycarbonylamino group, aryloxycarbonylamino group, N-alkyl-N-alkoxycarbonylamino group, N-alkyl-N-aryloxycarbonylamino group, N-aryl-N-alkoxycarbonylamino group, N-aryl-N -Aryloxycarbonylamino group, formyl group, acyl group, carboxyl group and its conjugate base group (hereinafter referred to as carboxylate), alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group, N, N -Dialkylcarbamoyl group, N-arylcarbamoyl group, N, N-diarylcarbamoyl group, N-alkyl-N-arylcarbamoyl group, alkylsulfinyl group, arylsulfinyl group, alkylsulfonyl group,
[0246]
Arylsulfonyl group, sulfo group (-SO₃H) and conjugated base groups thereof (hereinafter referred to as sulfonate groups), alkoxysulfonyl groups, aryloxysulfonyl groups, sulfinamoyl groups, N-alkylsulfinamoyl groups, N, N-dialkylsulfinamoyl groups, N-aryls Rufinamoyl group, N, N-diarylsulfinamoyl group, N-alkyl-N-arylsulfinamoyl group, sulfamoyl group, N-alkylsulfamoyl group, N, N-dialkylsulfamoyl group, N-aryl Sulfamoyl group, N, N-diarylsulfamoyl group, N-alkyl-N-arylsulfamoyl group,
[0247]
N-acylsulfamoyl group and its conjugate base group, N-alkylsulfonylsulfamoyl group (—SO₂NHSO₂(Alkyl)) and its conjugate base group, N-arylsulfonylsulfamoyl group (-SO₂NHSO₂(Allyl)) and its conjugate base group, N-alkylsulfonylcarbamoyl group (—CONHSO₂(Alkyl)) and its conjugate base group, N-arylsulfonylcarbamoyl group (—CONHSO)₂(Allyl)) and its conjugate base group, alkoxysilyl group (-Si (Oalkyl))₃), Aryloxysilyl group (-Si (Oallyl))₃), Hydroxysilyl group (-Si (OH)₃) And its conjugate base group,
[0248]
Phosphono group (-PO₃H₂) And conjugated base groups thereof (hereinafter referred to as phosphonate groups), dialkylphosphono groups (—PO₃(Alkyl)₂), Diarylphosphono group (—PO₃(Aryl)₂), An alkylarylphosphono group (—PO₃(Alkyl) (aryl)), monoalkylphosphono group (—PO₃H (alkyl)) and its conjugate base group (hereinafter referred to as alkylphosphonate group), monoarylphosphono group (—PO₃H (aryl)) and its conjugate base group (hereinafter referred to as arylphosphonate group), phosphonooxy group (-OPO₃H₂) And conjugated base groups thereof (hereinafter referred to as phosphonatoxy groups), dialkylphosphonooxy groups (—OPO)₃(Alkyl)₂), Diarylphosphonooxy group (-OPO₃(Aryl)₂), An alkylarylphosphonooxy group (—OPO₃(Alkyl) (aryl)), monoalkylphosphonooxy group (—OPO₃H (alkyl)) and its conjugate base group (hereinafter referred to as alkylphosphonatoxy group), monoarylphosphonooxy group (—OPO)₃H (aryl)) and its conjugate base group (hereinafter referred to as arylphosphonatoxy group), cyano group, nitro group, aryl group, alkenyl group, alkynyl group.
[0249]
Specific examples of the alkyl group in these substituents include the above-described alkyl groups, and specific examples of the aryl group include a phenyl group, a biphenyl group, a naphthyl group, a tolyl group, a xylyl group, a mesityl group, and a cumenyl group. , Fluorophenyl group, chlorophenyl group, bromophenyl group, chloromethylphenyl group, hydroxyphenyl group, methoxyphenyl group, ethoxyphenyl group, phenoxyphenyl group, acetoxyphenyl group, benzoyloxyphenyl group, methylthiophenyl group, phenylthiophenyl Group, methylaminophenyl group, dimethylaminophenyl group, acetylaminophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, ethoxycarbonylphenyl group, phenoxycarbonylphenyl group, N-phenylcarbamoyl group Group, a phenyl group, nitrophenyl group, cyanophenyl group, sulfophenyl group, sulfonatophenyl group, phosphonophenyl group, and the like phosphonium Hona preparative phenyl group. Examples of the alkenyl group include vinyl group, 1-propenyl group, 1-butenyl group, cinnamyl group, 2-chloro-1-ethenyl group and the like. Examples of alkynyl group include ethynyl group, 1- Examples include propynyl group, 1-butynyl group, trimethylsilylethynyl group, phenylethynyl group and the like.
[0250]
The acyl group (R⁴CO-) is R⁴Can include a hydrogen atom and the above alkyl, aryl, alkenyl, and alkynyl groups. On the other hand, examples of the alkylene group in the substituted alkyl group include a divalent organic residue obtained by removing any one of the hydrogen atoms on the alkyl group having 1 to 20 carbon atoms. Preferred examples include linear alkylene groups having 1 to 12 carbon atoms, branched alkylene groups having 3 to 12 carbon atoms, and cyclic alkylene groups having 5 to 10 carbon atoms. Specific examples of preferred substituted alkyl groups include chloromethyl, bromomethyl, 2-chloroethyl, trifluoromethyl, methoxymethyl, methoxyethoxyethyl, allyloxymethyl, phenoxymethyl, methylthiomethyl, Ruthiomethyl group, ethylaminoethyl group, diethylaminopropyl group, morpholinopropyl group, acetyloxymethyl group, benzoyloxymethyl group, N-cyclohexylcarbamoyloxyethyl group, N-phenylcarbamoyloxyethyl group, acetylaminoethyl group, N- Methylbenzoylaminopropyl group, 2-oxoethyl group, 2-oxopropyl group, carboxypropyl group, methoxycarbonylethyl group, methoxycarbonylmethyl group, methoxycarbonylbutyl group, ethoxycarbonyl Bonylmethyl group, butoxycarbonylmethyl group, allyloxycarbonylmethyl group, benzyloxycarbonylmethyl group, methoxycarbonylphenylmethyl group, trichloromethylcarbonylmethyl group, allyloxycarbonylbutyl group, chlorophenoxycarbonylmethyl group, carbamoylmethyl group, N- Methylcarbamoylethyl group, N, N-dipropylcarbamoylmethyl group, N- (methoxyphenyl) carbamoylethyl group, N-methyl-N- (sulfophenyl) carbamoylmethyl group, sulfopropyl group, sulfobutyl group, sulfonatobutyl group, sulfur Famoylbutyl group, N-ethylsulfamoylmethyl group, N, N-dipropylsulfamoylpropyl group, N-tolylsulfamoylpropyl group, N-methyl-N- (phosphono Eniru) sulfamoyl-octyl group,
[0251]
Embedded image

[0252]
Phosphonobutyl group, phosphonatohexyl group, diethylphosphonobutyl group, diphenylphosphonopropyl group, methylphosphonobutyl group, methylphosphonatobutyl group, tolylphosphonohexyl group, tolylphosphonatohexyl group, phosphonooxypropyl group, Phosphonatooxybutyl group, benzyl group, phenethyl group, α-methylbenzyl group, 1-methyl-1-phenylethyl group, p-methylbenzyl group, cinnamyl group, allyl group, 1-propenylmethyl group, 2-butenyl group , 2-methylallyl group, 2-methylpropenylmethyl group, 2-propynyl group, 2-butynyl group, 3-butynyl group, and the like.
[0253]
Examples of the aryl group include those in which 1 to 3 benzene rings form a condensed ring, and those in which a benzene ring and a 5-membered unsaturated ring form a condensed ring. Specific examples include a phenyl group, naphthyl A group, an anthryl group, a phenanthryl group, an indenyl group, an acenaphthenyl group, a fluorenyl group, and the like. Among these, a phenyl group and a naphthyl group are more preferable.
[0254]
The substituted aryl group is a group in which the substituent is bonded to the aryl group, and those having a monovalent non-metallic atomic group excluding hydrogen as a substituent on the ring-forming carbon atom of the aryl group described above are used. Examples of preferred substituents include the alkyl groups, substituted alkyl groups, and those previously shown as substituents in the substituted alkyl group. Preferred examples of these substituted aryl groups include biphenyl group, tolyl group, xylyl group, mesityl group, cumenyl group, chlorophenyl group, bromophenyl group, fluorophenyl group, chloromethylphenyl group, trifluoromethylphenyl group, Hydroxyphenyl, methoxyphenyl, methoxyethoxyphenyl, allyloxyphenyl, phenoxyphenyl, methylthiophenyl, tolylthiophenyl, phenylthiophenyl, ethylaminophenyl, diethylaminophenyl, morpholinophenyl, acetyl Oxyphenyl group, benzoyloxyphenyl group, N-cyclohexylcarbamoyloxyphenyl group, N-phenylcarbamoyloxyphenyl group, acetylaminophenyl group, N-methylbenzoyl Minophenyl group, carboxyphenyl group, methoxycarbonylphenyl group, allyloxycarbonylphenyl group, chlorophenoxycarbonylphenyl group, carbamoylphenyl group, N-methylcarbamoylphenyl group, N, N-dipropylcarbamoylphenyl group, N- (methoxyphenyl) ) Carbamoylphenyl group, N-methyl-N- (sulfophenyl) carbamoylphenyl group,
[0255]
Sulfophenyl group, sulfonatophenyl group, sulfamoylphenyl group, N-ethylsulfamoylphenyl group, N, N-dipropylsulfamoylphenyl group, N-tolylsulfamoylphenyl group, N-methyl-N- (Phosphonophenyl) sulfamoylphenyl group, phosphonophenyl group, phosphonatophenyl group, diethylphosphonophenyl group, diphenylphosphonophenyl group, methylphosphonophenyl group, methylphosphonatophenyl group, tolylphosphonophenyl group , Tolylphosphonatophenyl group, allyl group, 1-propenylmethyl group, 2-butenyl group, 2-methylallylphenyl group, 2-methylpropenylphenyl group, 2-propynylphenyl group, 2-butynylphenyl group, 3- A butynylphenyl group etc. can be mentioned.
[0256]
Examples of the alkenyl group include those described above. The substituted alkenyl group is a group in which the substituent is replaced and bonded to a hydrogen atom of the alkenyl group, and as the substituent, the substituent in the above-mentioned substituted alkyl group is used, while the alkenyl group uses the above-mentioned alkenyl group. Can do. Examples of preferred substituted alkenyl groups include
[0257]
Embedded image

[0258]
Etc. Examples of the alkynyl group include those described above. The substituted alkynyl group is a group in which the substituent is replaced with a hydrogen atom of the alkynyl group, and the substituent in the above-described substituted alkyl group is used as this substituent, while the alkynyl group uses the above-described alkynyl group. be able to.
[0259]
The heterocyclic group is a monovalent group obtained by removing one hydrogen on the heterocyclic ring and a group formed by bonding one substituent to the above-mentioned substituted alkyl group by further removing one hydrogen from the monovalent group. It is a valent group (substituted heterocyclic group). Examples of preferred heterocycles include
[0260]
Embedded image

[0261]
Embedded image

[0262]
Etc.
Substituted oxy group (R⁵As O-), R⁵In which is a monovalent non-metallic atomic group excluding hydrogen can be used. Preferred examples of the substituted oxy group include an alkoxy group, an aryloxy group, an acyloxy group, a carbamoyloxy group, an N-alkylcarbamoyloxy group, an N-arylcarbamoyloxy group, an N, N-dialkylcarbamoyloxy group, and an N, N-diarylcarbamoyloxy group. Groups, N-alkyl-N-arylcarbamoyloxy groups, alkylsulfoxy groups, arylsulfoxy groups, phosphonooxy groups, phosphonatoxy groups, and the like. Examples of the alkyl group and aryl group in these include the alkyl groups, substituted alkyl groups, aryl groups, and substituted aryl groups described above.
[0263]
In addition, an acyl group (R⁶CO-) is R⁶Can include those of the aforementioned alkyl group, substituted alkyl group, aryl group and substituted aryl group. Of these substituents, an alkoxy group, an aryloxy group, an acyloxy group, an arylsulfoxy group, and the like are more preferable. Specific examples of preferred substituted oxy groups include methoxy, ethoxy, propyloxy, isopropyloxy, butyloxy, pentyloxy, hexyloxy, dodecyloxy, benzyloxy, allyloxy, phenethyloxy, Carboxyethyloxy group, methoxycarbonylethyloxy group, ethoxycarbonylethyloxy group, methoxyethoxy group, phenoxyethoxy group, methoxyethoxyethoxy group, ethoxyethoxyethoxy group, morpholinoethoxy group, morpholinopropyloxy group, allyloxyethoxyethoxy group, Phenoxy, tolyloxy, xylyloxy, mesityloxy, cumenyloxy, methoxyphenyloxy, ethoxyphenyloxy, chlorophenyloxy, bromo Niruokishi group, acetyloxy group, benzoyloxy group, naphthyloxy group, a phenylsulfonyloxy group, a phosphonooxy group, phosphonatoxy and the like.
[0264]
Substituted thio group (R⁷R for S-)⁷Can be a monovalent nonmetallic atomic group excluding hydrogen. Examples of preferred substituted thio groups include alkylthio groups, arylthio groups, alkyldithio groups, aryldithio groups, and acylthio groups. Examples of the alkyl group and aryl group in these include the alkyl groups, substituted alkyl groups, aryl groups, and substituted aryl groups described above. The acyl group (R⁶CO-) R⁶Is as described above. Among these, an alkylthio group and an arylthio group are more preferable. Specific examples of preferable substituted thio groups include a methylthio group, an ethylthio group, a phenylthio group, an ethoxyethylthio group, a carboxyethylthio group, and a methoxycarbonylthio group.
[0265]
Substituted amino group (R⁸NH-, (R⁹) (R¹⁰) N-) includes R⁸, R⁹, R¹⁰Can be a monovalent nonmetallic atomic group excluding hydrogen. Preferred examples of the substituted amino group include an N-alkylamino group, an N, N-dialkylamino group, an N-arylamino group, an N, N-diarylamino group, an N-alkyl-N-arylamino group, an acylamino group, N-alkylacylamino group, N-arylacylamino group, ureido group, N′-alkylureido group, N ′, N′-dialkylureido group, N′-arylureido group, N ′, N′-diarylureido group N'-alkyl-N'-arylureido group, N-alkylureido group, N-arylureido group, N'-alkyl-N-alkylureido group, N'-alkyl-N-arylureido group, N ', N′-dialkyl-N-alkylureido group, N ′, N′-dialkyl-N-arylureido group, N′-aryl-N-alkyl Ureido group, N'-aryl-N-arylureido group, N ', N'-diaryl-N-alkylureido group, N', N'-diaryl-N-arylureido group, N'-alkyl-N'- Aryl-N-alkylureido group, N′-alkyl-N′-aryl-N-arylureido group, alkoxycarbonylamino group, aryloxycarbonylamino group, N-alkyl-N-alkoxycarbonylamino group, N-alkyl- N-aryloxycarbonylamino group, N-aryl-N-alkoxycarbonylamino group, N-aryl-N-aryloxycarbonylamino group can be mentioned. Examples of the alkyl group and aryl group include those described above as the alkyl group, substituted alkyl group, aryl group, and substituted aryl group, such as acylamino group, N-alkylacylamino group, and N-arylacylamino. An acyl group (R⁶CO-) R⁶Is as described above. Of these, more preferred are N-alkylamino group, N, N-dialkylamino group, N-arylamino group, acylamino group and the like. Specific examples of preferred substituted amino groups include methylamino group, ethylamino group, diethylamino group, morpholino group, piperidino group, pyrrolidino group, phenylamino group, benzoylamino group, acetylamino group and the like.
[0266]
Substituted carbonyl group (R¹¹-CO-) includes R¹¹Can be a monovalent non-metallic atomic group. Preferred examples of the substituted carbonyl group include formyl group, acyl group, carboxyl group, alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group, N, N-diarylcarbamoyl group, N-alkyl-N-arylcarbamoyl group and the like can be mentioned. Examples of the alkyl group and aryl group in these include those described above as the alkyl group, substituted alkyl group, aryl group, and substituted aryl group. Among these, more preferred substituents are formyl group, acyl group, carboxyl group, alkoxycarbonyl group, aryloxycarbonyl group, carbamoyl group, N-alkylcarbamoyl group, N, N-dialkylcarbamoyl group, N-arylcarbamoyl group. Groups, etc., and even more preferred are formyl group, acyl group, alkoxycarbonyl group and aryloxycarbonyl group. Specific examples of preferred substituents include formyl group, acetyl group, benzoyl group, carboxyl group, methoxycarbonyl group, allyloxycarbonyl group, N-methylcarbamoyl group, N-phenylcarbamoyl group, N, N-diethylcarbamoyl group, Examples thereof include a morpholinocarbonyl group.
[0267]
Substituted sulfinyl group (R¹²-SO-) is R¹²Can be a monovalent non-metallic atomic group. Preferable examples include alkylsulfinyl group, arylsulfinyl group, sulfinamoyl group, N-alkylsulfinamoyl group, N, N-dialkylsulfinamoyl group, N-arylsulfinamoyl group, N, N-diarylsulfinamoyl. Group, N-alkyl-N-arylsulfinamoyl group. Examples of the alkyl group and aryl group in these include those described above as the alkyl group, substituted alkyl group, aryl group, and substituted aryl group. Of these, more preferred examples include an alkylsulfinyl group and an arylsulfinyl group. Specific examples of such a substituted sulfinyl group include a hexylsulfinyl group, a benzylsulfinyl group, and a tolylsulfinyl group.
[0268]
Substituted sulfonyl group (R¹³-SO₂-) As R¹³Can be a monovalent non-metallic atomic group. More preferable examples include an alkylsulfonyl group and an arylsulfonyl group. Examples of the alkyl group and aryl group in these include those described above as the alkyl group, substituted alkyl group, aryl group, and substituted aryl group. Specific examples of such a substituted sulfonyl group include a butylsulfonyl group and a chlorophenylsulfonyl group.
[0269]
Sulfonato group (-SO₃As described above,-) represents a sulfo group (-SO₃H) means a conjugated base anionic group, usually preferably used together with a counter cation. Such counter cations include those generally known, that is, various oniums (ammoniums, sulfoniums, phosphoniums, iodoniums, aziniums, etc.), and metal ions (Na⁺, K⁺, Ca²⁺, Zn²⁺Etc.).
[0270]
Carboxylate group (-CO₂-) Is a carboxyl group (CO₂H) means a conjugated base anionic group, usually preferably used together with a counter cation. Such counter cations include those generally known, that is, various oniums (ammoniums, sulfoniums, phosphoniums, iodoniums, aziniums, etc.), and metal ions (Na⁺, K⁺, Ca²⁺, Zn²⁺Etc.).
[0271]
The substituted phosphono group means a group in which one or two hydroxyl groups on the phosphono group are substituted with other organic oxo groups, and preferred examples thereof include the above-mentioned dialkylphosphono group, diarylphosphono group, alkylarylphospho group. Group, monoalkylphosphono group and monoarylphosphono group. Of these, dialkylphosphono groups and diarylphosphono groups are more preferred. Specific examples thereof include a diethyl phosphono group, a dibutyl phosphono group, a diphenyl phosphono group, and the like.
[0272]
Phosphonato group (-PO₃ ^2-, -PO₃H⁻) Is a phosphono group (—PO as described above).₃H₂), A conjugate base anion group derived from acid first dissociation or acid second dissociation. Usually, it is preferable to use it with a counter cation. Examples of such counter cations include those generally known, that is, various oniums (ammoniums, sulfoniums, phosphoniums, iodoniums: aziniums, etc.), and metal ions (Na⁺, K⁺, Ca²⁺, Zn²⁺Etc.).
[0273]
The substituted phosphonato group is a conjugated base anion group obtained by substituting one organic oxo group in the above-mentioned substituted phosphono group. As a specific example, the monoalkylphosphono group (—PO₃H (alkyl)), monoarylphosphono group (—PO₃H (aryl)) conjugate base. Usually, it is preferable to use it with a counter cation. Such counter cations include those generally known, that is, various oniums (ammoniums, sulfoniums, phosphoniums, iodoniums, aziniums, etc.), and metal ions (Na⁺, K⁺, Ca²⁺, Zn²⁺Etc.).
[0274]
In the formula (IV), the structures of A and W are more preferably that A contains an aromatic group.
And an organic group having W is a nonionic organic group containing a polyoxyalkylene group.
[0275]
Specific examples of AH and WH are shown below.
[0276]
Embedded image

[0277]
Embedded image

[0278]
Specific examples of the nonionic compound of the general formula (IV) are shown below.
[0279]
Embedded image

[0280]
Embedded image

[0281]
Embedded image

[0282]
As the nonionic compound of the formula (IV), more preferred are:
It is shown by the following formula (IV-A) or (IV-B).
[0283]
Embedded image

[0284]
In the above formula, R₁₀, R₂₀Is H or a hydrocarbon group having 1 to 100 carbon atoms, and n and m are integers of 0 to 100 (however, n and m are not 0 at the same time). Examples of the hydrocarbon group include an alkyl group, an aryl group, an aralkyl group and the like, and further include those in which these hydrocarbon groups are bonded by an ether bond, an ester bond or an amide bond.
More preferred R₁₀, R₂₀As, H or a C1-C100 linear or branched alkyl group is mentioned. R₁₀, R₂₀Is a group: R₃₀-X- (R₃₀Represents a linear or branched alkyl group having 1 to 100 carbon atoms, and X represents —O—, —OCO—, —COO—, —NHCO—, or —CONH—.
More preferably R₁₀, R₂₀Is a hydrogen atom, a linear or branched alkyl group having 1 to 10 carbon atoms or a group: R₃₀-X- (R₃₀Is a linear or branched alkyl group having 1 to 10 carbon atoms, and X is —O—, —OCO—, —COO—, —NHCO—, or —CONH—.
[0285]
Examples of the compound represented by the general formula (IV-A) include polyoxyethylene phenyl ether, polyoxyethylene methyl phenyl ether, polyoxyethylene octyl phenyl ether, polyoxyethylene nonyl phenyl ether, and the like.
Examples of the compound represented by the general formula (IV-B) include polyoxyethylene naphthyl ether, polyoxyethylene methyl naphthyl ether, polyoxyethylene octyl naphthyl ether, polyoxyethylene nonyl naphthyl ether, and the like.
[0286]
In the compounds of the general formulas (IV-A) and (IV-B), the number of repeating units of the polyoxyethylene chain is preferably 3 to 50, more preferably 5 to 30. The number of repeating units of the polyoxypropylene chain is preferably 0 to 10, more preferably 0 to 5. The polyoxyethylene part and the polyoxypropylene part may be random or block copolymers.
The nonionic aromatic ether activators represented by the general formulas (IV-A) and (IV-B) are used alone or in combination of two or more.
[0287]
In the present invention, it is effective to add the nonionic compound represented by the general formula (IV) in the developer in an amount of 0.1 to 15% by mass, preferably 1.0 to 8.0% by mass.
Here, when the addition amount is 0.1% by mass or more, the developability is lowered and the solubility of the photosensitive layer components is improved, and when it is 15% by mass or less, the printing durability of the printing plate is not reduced.
[0288]
In addition, as the plate making process of the lithographic printing plate precursor according to the present invention, the entire surface may be heated before exposure, during exposure, and between exposure and development, if necessary. By such heating, an image forming reaction in the photosensitive layer is promoted, and advantages such as improvement in sensitivity and printing durability and stabilization of sensitivity may occur. Further, for the purpose of improving the image strength and printing durability, it is also effective to carry out whole surface post-heating or whole surface exposure on the developed image. Usually, heating before development is preferably performed under mild conditions of 150 ° C. or less. When the temperature is 150 ° C. or lower, the problem of fogging does not occur in the non-image area. Very strong conditions are used for heating after development. Usually, it is the range of 200-500 degreeC. When the temperature is 200 ° C. or higher, sufficient image strengthening action can be obtained. When the temperature is 500 ° C. or lower, problems such as deterioration of the support and thermal decomposition of the image portion do not occur.
[0289]
As a method for exposing a scanning exposure lithographic printing plate according to the present invention, a known method can be used without limitation. Desirably, the wavelength of the light source is 350 nm to 450 nm, and specifically, an InGaN-based semiconductor laser is suitable. The exposure mechanism may be any of an internal drum system, an external drum system, a flat bed system, and the like. In addition, the photosensitive layer component of the present invention can be made soluble in neutral water or weak alkaline water by using a high water-soluble component. After loading on top, a system such as exposure-development can be performed on the machine.
[0290]
As an available laser light source of 350 to 450 nm, the following can be used.
[0291]
As a gas laser, Ar ion laser (364 nm, 351 nm, 10 mW to 1 W), Kr ion laser (356 nm, 351 nm, 10 mW to 1 W), He—Cd laser (441 nm, 325 nm, 1 mW to 100 mW),
As a solid state laser, Nd: YAG (YVO₄) And SHG crystal x 2 combinations (355 nm, 5 mW to 1 W), Cr: LiSAF and SHG crystal combination (430 nm, 10 mW),
As a semiconductor laser system, KNbO₃Ring resonator (430 nm, 30 mW), combination of waveguide wavelength conversion element and AlGaAs, InGaAs semiconductor (380 nm to 450 nm, 5 mW to 100 mW), combination of waveguide wavelength conversion element, AlGaInP, AlGaAs semiconductor (300 nm to 350 nm, 5 mW to 100 mW), AlGaInN (350 nm to 450 nm, 5 mW to 30 mW)
In addition, N as a pulse laser₂Laser (337 nm, pulse 0.1 to 10 mJ), XeF (351 nm, pulse 10 to 250 mJ)
[0292]
In particular, an AlGaInN semiconductor laser (commercially available InGaN-based semiconductor laser 400 to 410 nm, 5 to 30 mW) is preferable in terms of wavelength characteristics and cost.
[0293]
Further, as the lithographic printing plate exposure apparatus of the scanning exposure method, there are an inner drum method, an outer drum method, and a flat bed method as an exposure mechanism, and all of the light sources other than the pulse laser can be used as the light source. . Practically, the following exposure apparatus is particularly preferable in terms of the relationship between the photosensitive material sensitivity and the plate making time.
[0294]
・ Single beam exposure system that uses one gas laser or solid-state laser light source with internal drum system
・ Multi-beam exposure system that uses many (10 or more) semiconductor lasers in a flatbed system
・ Multi-beam exposure system that uses many (10 or more) semiconductor lasers with an external drum system
[0295]
In the laser direct-drawing lithographic printing plate as described above, the photosensitive material sensitivity X (J / cm) is generally used.²), Exposure area S (cm²), The equation (eq1) is established among the power q (W) of one laser light source, the number n of lasers, and the total exposure time t (s).
X · S = n · q · t − (eq1)
[0296]
i) Internal drum (single beam) system
Equation (eq2) is generally established among the laser rotation speed f (radians / s), the sub-scanning length Lx (cm) of the photosensitive material, the resolution Z (dots / cm), and the total exposure time t (s). .
f · Z · t = Lx − (eq2)
ii) External drum (multi-beam) system
A general formula among drum rotation speed F (radians / s), photosensitive material sub-scanning length Lx (cm), resolution Z (dots / cm), total exposure time t (s), and number of beams (n) (Eq3) is established.
F · Z · n · t = Lx − (eq3)
iii) In case of flat bed (multi-beam) system
It is common among the rotation speed H (radian / s) of the polygon mirror, the sub-scanning length Lx (cm) of the photosensitive material, the resolution Z (dot / cm), the total exposure time t (s), and the number of beams (n). Equation (eq4) is established.
H · Z · n · t = Lx − (eq4)
[0297]
Resolution required for an actual printing plate (2560 dpi), plate size (A1 / B1, sub-scan length 42 inch), exposure conditions of about 20 sheets / hour and photosensitive characteristics of the photosensitive composition of the present invention (photosensitive wavelength, Sensitivity: about 0.1mJ / cm²) Is substituted into the above formula, it can be understood that a combination with a semiconductor laser multi-beam exposure method is more preferable in the photosensitive material of the present invention. Further, by combining operability, cost, etc., a combination with an external drum type semiconductor laser multi-beam exposure apparatus is most preferable.
[0298]
In addition, other exposure light rays for the photopolymerizable composition according to the present invention include ultrahigh pressure, high pressure, medium pressure, and low pressure mercury lamps, chemical lamps, carbon arc lamps, xenon lamps, metal halide lamps, and various visible and ultraviolet lasers. A lamp, a fluorescent lamp, a tungsten lamp, sunlight, etc. can also be used. Moreover, as a use of the photopolymerizable composition by this invention, besides the planographic printing plate for scanning exposure, it can apply without limitation to what is widely known as a use of photocurable resin. For example, a highly sensitive optical modeling material can be obtained by applying to a liquid photopolymerizable composition used in combination with a cationic polymerizable compound as necessary. Further, a hologram material can be obtained by utilizing a change in refractive index accompanying photopolymerization. It can be applied to various transfer materials (peeling sensitive material, toner developing sensitive material, etc.) by utilizing the change in surface adhesiveness accompanying photopolymerization. It can also be applied to photocuring of microcapsules. It can also be applied to the production of electronic materials such as photoresists, and photocurable resin materials such as inks, paints, and adhesives.
[0299]
【Example】
EXAMPLES Hereinafter, although an Example demonstrates this invention, this invention is not limited to these Examples.
(Synthesis Example) Synthesis of D5
After 35 g of diphenylaminobenzaldehyde and 2.0 g of piperidine were dissolved in 500 ml of methanol, the mixture was stirred for 1 hour while refluxing. Next, 20 g of 3-ethyl-2-thioxo-4-oxazolidione was added and stirred for 4 hours under reflux. After completion of the reaction, the mixture was allowed to cool to room temperature, whereby yellow crystals were precipitated. The precipitated crystals were filtered, added to 1000 ml of methanol, and stirred for 1 hour. The crystals were filtered and dried to obtain 48 g of the following compound (D5 ′) (yield 91%).¹Identification was performed by 1 H-NMR.
[0300]
Embedded image

Next, after 1.7 g of silver nitrate was dissolved in 20 ml of acetonitrile, 2.0 g of the dye precursor represented by D5 ′ was added and stirred for 0.5 hour. Next, 3.2 g of 3-bromo-1-propylamine was added dropwise and stirred for 30 minutes, then 2.5 g of triethylamine was added dropwise, and the mixture was further stirred for 1.5 hours. After completion of the reaction, 30 ml of acetone was added, the precipitated silver salt was filtered off using celite, and the filtrate was poured into 200 ml of water. The precipitated crystals were collected by filtration and reslurried in methanol to obtain 2.3 g of the following compound (D5 ″) (yield 93%).¹Identification was performed by 1 H-NMR.
[0301]
Embedded image

Next, after dissolving 0.5 g of the compound represented by D5 ″ and 0.17 g of 4-t-butylpyridine in 30 ml of acetone, the mixture was heated to 60 ° C. and stirred for 8 hours. The KPF was dissolved in 60 ml of methanol and 50 ml of water, and further dissolved in 60 ml of methanol and 50 ml of water.₆Were filtered, and the precipitated crude product of D5 was filtered and reslurried with methanol to obtain 0.53 g of the following compound (D5) (2-step yield 75%).¹Identification was performed by 1 H-NMR.
Embedded image

[0302]
[Examples 1-17, Comparative Examples 1-6]
(Preparation of support)
An aluminum plate having a thickness of 0.3 mm was etched by being immersed in 10 wt% sodium hydroxide at 60 ° C. for 25 seconds, washed with running water, neutralized with 20 wt% nitric acid, and then washed with water. This was changed to 300 coulomb / dm in a 1% by weight aqueous nitric acid solution using a sinusoidal alternating current.²Electrolytic surface roughening treatment was performed with the amount of electricity at the time of anode. Subsequently, after dipping in a 1% by weight aqueous sodium hydroxide solution at 40 ° C. for 5 seconds and then in a 30% by weight sulfuric acid aqueous solution and desmutting at 60 ° C. for 40 seconds, the current density in a 20% by weight sulfuric acid aqueous solution was 2A / current density. dm²The thickness of the anodized film is 2.7 g / m²Then, anodization was performed for 2 minutes. When the surface roughness was measured, it was 0.3 μm (Ra indication according to JISB0601).
[0303]
The following sol-gel reaction solution was applied to the back surface of the substrate thus treated with a bar coater and dried at 100 ° C. for 1 minute, and the coating amount after drying was 70 mg / m.²A support having a back coat layer was prepared.
[0304]
Sol-gel reaction solution
50 parts by weight of tetraethyl silicate
20 parts by weight of water
15 parts by weight of methanol
0.05 parts by weight of phosphoric acid
[0305]
When the above components were mixed and stirred, heat generation started in about 5 minutes. After reacting for 60 minutes, a backcoat coating solution was prepared by adding the following solution.
[0306]

[0307]
(Preparation of photosensitive layer)
On the aluminum plate thus treated, the photopolymerizable composition having the following composition was dried at a coating amount of 1.0 to 2.0 g / m.²And a photosensitive layer was formed by drying at 80 ° C. for 2 minutes.
[0308]

[0309]
(Preparation of protective layer)
A 3 wt% aqueous solution of polyvinyl alcohol (saponification degree 98 mol%, polymerization degree 550) was dried on the photosensitive layer at a dry coating weight of 2 g / m 2.²And then dried at 100 ° C. for 2 minutes.
[0310]
(Evaluation of sensitivity)
A Fuji step guide manufactured by Fuji Photo Film Co., Ltd. (gray scale whose transmission optical density changes discontinuously at ΔD = 0.15) is adhered to the photosensitive material thus obtained, and an optical filter is attached. The exposure was performed with a passed xenon lamp so as to obtain a known exposure energy. Thereafter, the film was immersed in a developer having the following composition at 25 ° C. for 10 seconds, developed, the maximum number of steps at which the image was completely removed was read, the exposure energy amount was determined, and the sensitivity was calculated (unit, mJ / cm).²). The smaller the amount of energy, the higher the sensitivity. For the purpose of estimating the suitability of exposure to a short-wave semiconductor laser, Kenko BP-40 was used as an optical filter, and exposure was performed with 400 nm monochromic light. The results are shown in Table 1.
[0311]

[0312]
Embedded image

[0313]
[Table 1]

[0314]
As is apparent from Table 1, Examples 1 to 17 using the initiation system of the present invention show practically sufficient sensitivity. From comparison with Comparative Examples 1 to 5 that do not use the initiation system of the present invention, it is clear that the initiation system of the present invention can express high sensitivity by the combined use of a sensitizing dye and an activator. Furthermore, Examples 1 to 5 show that a wide range of activators of the present invention can be applied regardless of the sensitization mechanism. Furthermore, as a result of comparison between Example 11 and Comparative Example 6, the sensitizing dye of the present invention has a high structural sensitivity in the acceptor structure having a reduction potential lower than the excitation oxidation potential of the sensitizing dye. This is an unexpected discovery.
[0315]
[Examples 18 to 26, Comparative Example 7]
A lithographic printing plate was prepared according to the following procedure, and the printing performance was evaluated. The results are shown in Table 2.
[0316]
"Pretreatment of support"
An aluminum plate of material 1S having a thickness of 0.3 mm was used with a No. 8 nylon brush and an aqueous suspension of 800 mesh Pamiston, the surface of which was grained, and then thoroughly washed with water. Etching was performed by immersing in 10% by weight sodium hydroxide at 70 ° C. for 60 seconds, washing with running water, neutralizing and washing with 20% by weight nitric acid, and then washing with water. This is V_A= 12.7 V, 300 coulomb / dm in 1 wt% nitric acid aqueous solution using a sinusoidal alternating waveform current²Electrolytic surface roughening treatment was performed with the amount of electricity at the time of anode. When the surface roughness was measured, it was 0.45 μm (Ra indication according to JIS B0601).
[0317]
"Hydrophilic treatment of the support surface"
The above-mentioned support is made of No. 3 sodium silicate (SiO₂= 28-30%, Na₂O = 9-10%, Fe = 0.02% or less) was immersed in an aqueous solution of 2.5% by weight, pH = 11.2, 70 ° C. for 13 seconds, followed by washing with water. From the amount of Si element obtained by surface fluorescent X-ray analysis, the amount of surface silicate is 10 mg / m.²I was asked.
[0318]
"Coating the middle layer"
A coating amount of phenylphosphonic acid is 20 mg / m on the hydrophilic support surface.²A coating solution having the following composition (A) was prepared so as to be, and after being applied with a wheeler under the condition of 180 rpm, it was dried at 80 ° C. for 30 seconds.
[0319]
(Intermediate layer coating solution A)
Phenylphosphonic acid 0.07g ~ 1.4g
Methanol 200g
[0320]
"Coating of photosensitive layer"
On the support provided with the intermediate layer, a photosensitive solution having the following composition was prepared, and the coating amount was 1.0 to 2.0 g / m.²Then, it was applied with a wheeler and dried at 100 ° C. for 1 minute.
[0321]
(Photosensitive solution)

[0322]
"Coating of protective layer"
A 3 wt% aqueous solution of polyvinyl alcohol (saponification degree 98 mol%, polymerization degree 550) was dried on the photosensitive layer at a dry coating weight of 2 g / m 2.²And then dried at 100 ° C. for 2 minutes.
[0323]
"Exposure of lithographic printing plate precursor"
The lithographic printing plate precursor obtained as described above was subjected to 400 nm monochromatic light as a light source, and a plate surface exposure energy density of 200 μJ / cm.²The exposure power was adjusted so that a solid image exposure and a halftone dot image exposure of 175 lines / inch from 1 to 99% in 1% increments were performed.
[0324]
"Development / plate making"
A predetermined developer (described in Table 2) and a finisher FP-2W manufactured by Fuji Photo Film Co., Ltd. were loaded into an automatic processor LP-850 manufactured by Fuji Photo Film Co., Ltd., respectively, and the developer temperature was 30 ° C. and the development time was 18 seconds. The exposed plate was developed / engraved under the following conditions to obtain a lithographic printing plate.
[0325]
"Print durability test"
R201 manufactured by Roland was used as the printing machine, and GEOS-G (N) manufactured by Dainippon Ink was used as the ink. The printed matter in the solid image portion was observed, and the printing durability was examined based on the number of sheets on which the image began to fade. The higher the number, the better the printing durability.
[0326]
"Forced dot printing test"
R201 manufactured by Roland was used as the printing machine, and GEOS-G (N) manufactured by Dainippon Ink was used as the ink. On the 5000th sheet from the start of printing, PS plate cleaner CL-2 manufactured by Fuji Photo Film Co., Ltd. was soaked in a printing sponge, the halftone dots were wiped, and the ink on the printing plate was washed. Thereafter, 10,000 sheets were printed, and the presence or absence of halftone dots in the printed matter was visually observed.
[0327]
"Dirty test"
R201 manufactured by Roland was used as the printing machine, and GEOS-G (S) manufactured by Dainippon Ink was used as the ink. The printed matter in the non-image area (unexposed area) was observed to evaluate the stain property.
[0328]
(Addition polymerizable compound in Table 2)
(M-1)
Pentaerythritol tetraacrylate
(Shin Nakamura Chemical Co., Ltd .; NK Ester A-TMMT)
(M-2)
Glycerin dimethacrylate hexamethylene diisocyanate urethane prepolymer
(Kyoeisha Chemical Co., Ltd .; UA101H)
[0329]
(Binder polymer in Table 2)
(B-1)
Allyl methacrylate / methacrylic acid / N-isopropylacrylamide (copolymerization molar ratio 66/13/21)
Measured acid value obtained by NaOH titration 1.18 meq / g
Weight average molecular weight determined by GPC measurement 125,000
[0330]
(B-2)
Allyl methacrylate / methacrylic acid copolymer (copolymerization molar ratio 82/18)
Measured acid value obtained by NaOH titration 1.58 meq / g
Weight average molecular weight determined by GPC measurement: 13 million
[0331]
(B-3)
Polyurethane resin that is a condensation polymer of the following diisocyanates and diols
4,4'-diphenylmethane diisoisocyanate (MDI)
Hexamethylene diisocyanate (HMDI)
Polypropylene glycol, weight average molecular weight 1000 (PPG1000)
2,2-bis (hydroxymethyl) propionic acid (DMPA)
Tetraethylene glycol (TEG)
Copolymerization molar ratio (MDI / HMDI / PPG1000 / DMPA / TEG) 40/10/11/27/12
Measured acid value obtained by NaOH titration 1.07 meq / g
Weight average molecular weight determined by GPC measurement 43,000
[0332]
(Developer in Table 2)
(DV-1)
PH 10 aqueous solution having the following composition
Monoethanolamine 0.1 parts by weight
1.5 parts by weight of triethanolamine
Compound of formula 2 below 4.0 parts by weight
Compound of formula 3 below 2.5 parts by weight
Compound of the following formula 4 0.2 parts by weight
91.7 parts by weight of water
[0333]
(DV-2)
PH 10 aqueous solution having the following composition
Sodium bicarbonate 1.2 parts by weight
Sodium carbonate 0.8 parts by weight
Compound of formula 2 below 3.0 parts by weight
Compound of formula 3 below 2.0 parts by weight
Compound of the following formula 4 0.2 parts by weight
92.8 parts by weight of water
[0334]
(DV-3)
PH 13 aqueous solution having the following composition
1K potassium silicate 3.0 parts by weight
Potassium hydroxide 1.5 parts by weight
Compound of the following formula 4 0.2 parts by weight
95.3 parts by weight of water
[0335]
Embedded image

[0336]
(Where R is H or C₄H₉And n is about 4 (average value). )
[0337]

[0338]
[Table 2]

[0339]
As is apparent from Table 2, the lithographic printing plate according to the present invention provides an excellent lithographic printing plate even under conditions capable of making a plate with high productivity by scanning exposure, that is, under very low energy exposure conditions. On the other hand, no practical lithographic printing plate was obtained in Comparative Example 7 which did not use the initiation system of the present invention.
[0340]
Example 27
The starting system is changed to the following composition, and the film thickness of the photopolymerization layer is 1.5 g / m.²A lithographic printing plate precursor was prepared in the same manner as in Examples 1 to 17 except that
Starting system D24 0.12g
Activator A-1 0.08g
Cosensitizer C-2 0.2g
[0341]
For the obtained lithographic printing plate precursor, monochromatic light of 400 nm was used, and the exposure energy density was 0.25 mJ / cm.²Scanning exposure was performed under the following conditions. Next, the plate was heated at 100 ° C. for 10 seconds and then subjected to the development processing described above.
[0342]
A lithographic printing plate having a blue image with excellent visibility was obtained. When offset printing was carried out using the obtained plate and a Heidelberg KOR-D machine, 50,000 sheets or more of printed matter excellent in image density and stain resistance could be obtained.
[0343]
Example 28
The plate of Example 27 was exposed to a yellow lamp for 1 hour before exposure, and plate making and printing were carried out in the same manner. Good results exactly the same as in Example 27 were obtained.
[0344]
Example 29
The plate of Example 28 was stored for 3 days under a forced storage condition of 65% humidity and 45 ° C., and then plate-making and printing were performed in the same manner as in Example 27. Good results similar to those of Example 27 were obtained.
[0345]
Example 30
A photosensitive layer having the following composition is applied on a PET film at a coating amount of 2.0 g / m²It was coated so that
[0346]
(Content in the total solid content of the photosensitive layer)
Binder resin (polymethyl methacrylate) 93.8wt%
Sensitizing dye D40 1.2wt%
Activator A-6 5.0 wt%
Acid decoloring dye (Victoria Pure Blue naphthalene sulfonate) 2.0wt%
[0347]
The obtained blue sensitive material was exposed for 30 seconds with a metal halide lamp. The blue color disappeared completely and changed to a pale yellow transparent film. Thus, the present initiation system also functions as an acid generator.
[0348]
Example 31
The same operation as in Example 30 was performed except that the activator was changed to A-7. The same photodecoloration of the dye as in Example 30 was observed.
[0349]
[Example 32]
The same operation as in Example 31 was performed except that the activator was changed to A-8. Photodecoloration of the dye was observed.
[0350]
Example 33
A photosensitive layer having the following composition is applied on a PET film at a coating amount of 2.0 g / m²It was coated so that
[0351]
(Content in the total solid content of the photosensitive layer)
Binder resin (polymethyl methacrylate) 90wt%
Sensitizing dye D38 2.0wt%
Activator A-9 8.0 wt%
[0352]
When the film surface pH on the surface of the obtained photosensitive material was measured, it was 5.6. Next, the photosensitive material was exposed to a xenon lamp for 5 minutes, and the pH of the film surface was measured to find 9.5. Thus, this initiation system has the ability to generate a photobase.
[0353]
Example 34
A photosensitive layer having the following composition is applied on a PET film at a coating amount of 2.0 g / m²It was coated so that
[0354]
(Content in the total solid content of the photosensitive layer)
Binder resin (polymethyl methacrylate) 91.5wt%
Sensitizing dye D30 1.5wt%
Activator A-6 5.0 wt%
Oxidative coloring dye (leuco crystal violet) 2.0wt%
[0355]
The obtained light yellow transparent sensitive material was exposed for 30 seconds with a metal halide lamp. It developed a bright blue color. This is considered to be oxidative coloring of the leuco dye by radical generation of the present initiation system. The structures of the compounds in Examples and Comparative Examples other than Formulas 1 to 4 are as follows.
[0356]
Embedded image

[0357]
Embedded image

[0358]
(Here, Ts represents a tosyl group, and Tf represents trifluoromethanesulfonic acid.)
[0359]
【The invention's effect】
The lithographic printing plate precursor to which the photosensitive composition of the present invention is applied has sufficient sensitivity suitable for scanning exposure by a semiconductor laser having a short wavelength such as InGaN, and is excellent in printing durability, stain resistance and stability. Give a lithographic printing plate. In addition, the lithographic printing plate precursor for scanning exposure has significantly improved fogging under a yellow light, and the workability of handling the plate can be greatly improved. The photoinitiating system of the present invention is excellent in sensitivity and can generate radicals, acids, and bases.

Claims (3)

(I) A chemical change is caused by the interaction between the sensitizing dye represented by the following general formula (1) and (ii) the light absorption of the sensitizing dye, and at least one of radicals, acids and bases And (iii) a photosensitive composition containing a compound whose physical or chemical properties are irreversibly changed by at least one of radicals, acids and bases.
Dye-LM (1)
(In the formula, Dye represents a sensitizing dye skeleton, L represents a divalent organic group linking Dye and M, and M represents an acceptor group having a reduction potential lower than the Dye excitation oxidation potential.) The photosensitive composition according to claim 1, wherein the acceptor group of the sensitizing dye represented by the general formula (1) is an ammonium group, a pyridinium group, a sulfonium group, or a phosphonium group. (I) at least one selected from a sensitizing dye represented by the following general formula (2), a sensitizing dye represented by the general formula (3), and a sensitizing dye represented by the general formula (4); (Ii) an activator compound that undergoes a chemical change by interaction with the light absorption of the sensitizing dye to produce at least one of a radical, an acid and a base; and (iii) a radical, an acid and a base A photosensitive composition comprising a compound whose physical or chemical properties are irreversibly changed by at least one of them.

(A represents an aromatic ring or a hetero ring which may have a substituent, and X and Y represent an oxygen atom, a sulfur atom or -N (R ₁ )-. R ₁ , R ₂ , R ₃ , R ₄ , R ₅ , R ₆ , R ₇ , R ₈ , R ₉ , R ₁₀ , R ₁₁ , R ₁₂ , R ₁₃ are each independently a hydrogen atom or a monovalent nonmetallic atomic group, R ₁ , R ₂ , R ₃ , R ₆ , R ₁₃ can be bonded to each other to form an aliphatic or aromatic ring provided that A, R ₁ , R ₂ , R ₃ , R ₄ , R ₅ , R ₆ , R ₇ , R ₈ , R ₉ , R ₁₀ , R ₁₁ , R ₁₂ , R ₁₃ are at least one monovalent organic residue represented by the partial structure (5) below. In the following partial structure, L connects M to the structure represented by the general formula (2), the general formula (3), or the general formula (4). Represents a divalent organic group, and M represents an ammonium group, a pyridinium group, a sulfonium group, or a phosphonium group.)