JP2004291537A

JP2004291537A - Decorative sheet

Info

Publication number: JP2004291537A
Application number: JP2003089837A
Authority: JP
Inventors: Nobuo Kawabe; 伸夫川邊; Yasuhiro Takeda; 康浩竹田
Original assignee: Daiken Trade and Industry Co Ltd
Current assignee: Daiken Trade and Industry Co Ltd
Priority date: 2003-03-28
Filing date: 2003-03-28
Publication date: 2004-10-21

Abstract

<P>PROBLEM TO BE SOLVED: To provide a decorative sheet ensured in moisture permeability and enhanced in water resistance without bringing about an increase in costs. <P>SOLUTION: The decorative sheet is obtained by forming a coating film 2 having both of air permeability and water resistance on the surface of a mineral fiberboard 1 comprising mineral fibers, an inorganic filler, a binder and a B-type silica gel as a moisture absorbing and discharging material. The coating film 2 comprises vehicle, pigment, and the B-type silica gel as an air permeable material. By this constitution, the moisture absorbing and discharging capacity or physical adsorbing function for formaldehyde, VOC, a malodor or the like of the mineral fiberboard 1 being a base material can be prevented from being damaged, the decorative sheet can be wiped by water, and the physical adsorbing function for formaldehyde, VOC, a malodor or the like and a moisture absorbing and discharging capacity can be applied to the decorative sheet. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

【０００１】
【発明の属する技術分野】
本発明は、内装材として用いられる化粧板に関し、特に水拭き可能で水廻り用に好適な化粧板に関する技術分野に属する。
【０００２】
【従来の技術】
従来より、この種水拭き可能な化粧板として、例えば特許文献１に示されているように、ロックウール（岩綿）からなる基材の表面に耐水性の塗装を施したものが知られている。このものでは、内部に水が浸み込まないので、水拭きが可能であり、水廻りの化粧板に用いることができる。
【０００３】
【特許文献１】
特開昭５７―１１３０６３号公報
【０００４】
【発明が解決しようとする課題】
しかしながら、上記従来の特許文献１のものでは、反面、耐水性の塗膜により透湿性が悪くなるので、ロックウール本来の吸放湿性やホルムアルデヒド吸着機能等が阻害される難がある。
【０００５】
上記ロックウールの基材自体に耐湿性を付与するために、結合剤として耐水性に優れたフェノール樹脂やメラミン樹脂を用いることが考えられるが、そうすると、一般的に使用される澱粉に比べて高価となり、必要な強度を発現するためにはコストアップとするのは避けられない。
【０００６】
本発明の目的は、上記した化粧板の構成に所定の改良を加えることで、基材自体に耐湿性を付与する場合の如きコストアップを招くことなく、透湿性が確保されかつ耐水性をも有する化粧板が得られるようにすることにある。
【０００７】
【課題を解決するための手段】
上記の目的を達成すべく、この発明では、化粧板の基材に吸放湿材を含有させ、その基材表面に通気性及び耐水性の両方を有する塗料を塗布するようにした。
【０００８】
具体的には、請求項１の発明の化粧板では、鉱物質繊維、無機充填材、結合剤及び吸放湿材からなる基材としての鉱物質繊維板の表面に、耐水性のあるビヒクルと、顔料と、通気性材とからなりかつ通気性及び耐水性の両方を有する塗料が塗布された塗膜が形成されていることを特徴とする。
【０００９】
上記の構成によると、化粧板の基材としての鉱物質繊維板に吸放湿材が含まれているので、この吸放湿材が基材の結合剤よりも選択的に湿気を多く吸着するようになり、基材の湿気による強度低下や寸法変化（例えば天井材として使用したときの垂れ下がり現象等）を防止することができる。また、基材の結合材として、メラミン樹脂やフェノール樹脂等のような高価な耐湿性結合剤を用いずに、澱粉等の安価な結合剤を用いることができるので、十分な強度を発現するためのコストアップを招くこともない。
【００１０】
また、化粧板の基材たる鉱物質繊維板に吸放湿材が用いられているので、高湿環境になるのを防止することができ、水廻り部分で問題になる結露やカビの繁殖を抑えることができる。
【００１１】
さらに、鉱物質繊維板の表面に、耐水性のあるビヒクル、顔料及び通気性材からなり通気性と耐水性との両方を有する塗料が塗布されて塗膜が形成されているので、化粧板表面の水拭きができると同時に、その塗膜中に分散した通気性材が湿気やガスを透過させかつ自ら吸放湿するようになる。このことで、基材としての鉱物質繊維板の吸放湿性能やホルムアルデヒド、ＶＯＣ、臭気等の物理吸着機能が阻害されることはなく、よって、水拭きができるとともに、ホルムアルデヒド、ＶＯＣ、臭気等の吸着機能と吸放湿性とを併せ持った化粧板が得られる。
【００１２】
請求項２の発明では、上記吸放湿材及び／又は通気性材はＢ型シリカゲルとする。このＢ型シリカゲルは、常態では放湿しないＡ型シリカゲルと異なり、常態において吸放湿するので、上記吸放湿材及び／又は通気性材として特に好ましい。
【００１３】
【発明の実施の形態】
以下、本発明の実施形態を図面に基づいて詳細に説明する。以下の好ましい実施形態の説明は、本質的に例示に過ぎず、本発明、その適用物或いはその用途を制限することを意図するものでは全くない。
【００１４】
図１は本発明の実施形態に係る化粧板Ａを示し、この化粧板Ａは室内の天井材や壁材等として用いられる。１は基材としての鉱物質繊維板であって、この鉱物質繊維板１の表面に塗料が塗布されて塗膜２が形成されている。
【００１５】
上記鉱物質繊維板１は、ロックウール等の鉱物質繊維と、パーライトやベントナイト等の無機充填材と、澱粉や故紙パルプ等の結合剤（バインダ）と、吸放湿材としてのＢ型シリカゲルとからなる。例えば、これらの材料をスラリーとして成板した後、脱水、成型及び乾燥することで得られる。
【００１６】
上記吸放湿材としてのＢ型シリカゲルは、Ａ型シリカゲルと異なり、常態において吸放湿するので、上記吸放湿材として特に好ましい。Ａ型シリカゲルは低湿度においても吸湿性に優れているが、常態では放湿しない。
【００１７】
すなわち、シリカゲルはＪＩＳでＡ型とＢ型とに大別され、両者は構造による違いである。Ａ型シリカゲルは一般的な乾燥剤として用いられているもので、微細な構造となっていて表面積が大きく、水分子と化学吸着によって結合する。一方、Ｂ型シリカゲルはあまり微細ではないために、表面積も小さく、化学吸着よりも構造間での毛細管現象による物理吸着により水分子と結合する。従って、図２に示すように、Ａ型シリカゲルでは、一度吸着した水分子は強制的に加熱しないと脱着しないが、Ｂ型シリカゲルでは、低湿度条件にすると除放していくので、呼吸作用があるといわれており、本実施形態では、このＢ型シリカゲルが用いられる。
【００１８】
尚、Ｂ型シリカゲル以外の他の吸放湿材を用いることもできる。その場合、使用する吸放湿材としては、水分を選択的に吸着し易い親水性のものが好ましく、さらには寸法変化の殆どない無機系の材料が好ましい。無機系でも吸湿により膨潤する粘度鉱物は好ましくない。
【００１９】
上記塗膜２は、ビヒクルと、顔料と、それ自体に通気性を持つ通気性材としてのＢ型シリカゲルとからなるもので、通気性と耐水性との両方を併せ持っている。尚、Ｂ型シリカゲル以外の通気性材を用いることもできる。
【００２０】
したがって、この実施形態に係る化粧板Ａにおいては、その基材としての鉱物質繊維板１に吸放湿材としてのＢ型シリカゲルが含まれているので、このＢ型シリカゲルが基材の結合剤よりも選択的に湿気を吸着するようになり、基材の湿気による強度低下や寸法変化を防止することができる。この強度低下や寸法変化としては、化粧板Ａを例えば天井材として使用したときの垂れ下がり現象がある。この垂れ下がり現象は、基材の結合剤として使用されている澱粉が湿気により糊化して結合力が低下するためであるが、この実施形態のようにＢ型シリカゲルが添加されていると、そのＢ型シリカゲルの方が澱粉（結合剤）に比べ選択的に多く湿気を吸着するようになるので、天井材として使用したときの垂れ下がり現象が防止される。
【００２１】
また、鉱物質繊維板１（基材）の結合材として、メラミン樹脂やフェノール樹脂等のような高価な耐湿性結合剤を用いると、十分な強度を発現するためにはコストアップするが、安価な澱粉等の結合剤を用いることが可能となるので、コストアップを招くことはない。
【００２２】
また、化粧板Ａの基材たる鉱物質繊維板１に吸放湿材が用いられているので、高湿環境に陥るのを防止して、水廻り部分で問題になる結露やカビの繁殖を抑えることができる。
【００２３】
さらに、鉱物質繊維板１の表面に、耐水性のあるビヒクル、顔料及び通気性材からなる通気性の塗料が塗布されて塗膜２が形成されているので、化粧板Ａ表面の水拭きができると同時に、その塗膜２中に分散した通気性材としての多孔質のＢ型シリカゲルが湿気やガスを透過させかつ自ら吸放湿するようになる。このことで、基材としての鉱物質繊維板１の吸放湿性能やホルムアルデヒド、ＶＯＣ、臭気等の物理吸着機能が阻害されるのを防ぐことができる。よって、化粧板Ａは水拭きができ、しかもホルムアルデヒド、ＶＯＣ、臭気等の吸着機能と吸放湿性とを併せ持つものとなる。
【００２４】
【実施例】
次に、具体的に実施した実施例について説明する。
【００２５】
（実施例１）
鉱物質繊維板からなる基材は、主成分としてのロックウールと、無機充填材としてのパーライト及びベントナイトと、バインダとしての澱粉及び故紙パルプと、吸放湿材料としてのＢ型シリカゲルとを材料とした。このＢ型シリカゲルの粒径は３０〜５００μｍである。これら材料を水に均一に分散混練してスラリーとし、通常の鉱物質繊維板の製造方法である湿式抄造にて成板し、減圧脱水、プレス成形し、さらに乾燥したものを基材とした。
【００２６】
次いで、上記基材の表面を下塗り塗料及び上塗り塗料により塗装した。下塗り塗料は、体質顔料として炭酸カルシウムを３０ｗｔ％と、白色顔料として酸化チタンを１５ｗｔ％と、艶消し顔料としてシリカを９ｗｔ％と、バインダとして酢酸ビニル樹脂を１６ｗｔ％と、助剤として分散剤、防カビ剤、消泡剤及び増粘剤を計１ｗｔ％と、ホルムアルデヒド吸着剤としてアミン類のアセチルアセトアミノアミン（Ｒ−ＣＯＮＨＮＨ_２）を２．５ｗｔ％と、通気性材としてＢ型シリカゲルを３ｗｔ％とに、残部の水を加えて撹拌したものである（尚、この下塗り塗料については、ある程度通気性があるので、通気性材を添加しなくても使用できる）。
【００２７】
一方、上塗り塗料は、バインダとしてアクリル樹脂を７０ｗｔ％と、顔料として発色顔料を３ｗｔ％と、撥水剤を４ｗｔ％と、その他の助剤として分散剤、防カビ剤、消泡剤及びブロッキング防止剤を計２ｗｔ％と、通気性材としてＢ型シリカゲルを３ｗｔ％とに、残部の水を加えて塗料化したものである。そして、これら下塗り塗料及び上塗り塗料を耐水性透湿性塗料とした。
【００２８】
上記塗料中のＢ型シリカゲルの粒径は７５μｍ以下、換言すれば下塗り塗料及び上塗り塗料の各々による塗膜厚さ以下である。尚、上記ホルムアルデヒド吸着剤としてのアセチルアセトアミノアミンは、下塗り塗料に代えて上塗り塗料に添加してもよいと考えられる。
【００２９】
そして、上記下塗り塗料を上記基材表面に１５０〜２５０ｇ／ｍ^２の割合で塗布して乾燥させた後、その上に上記上塗り塗料を５０〜１５０ｇ／ｍ^２の割合で塗布して乾燥したものを試験片（サンプル）とした。
【００３０】
（比較例１）
比較例１は、上記実施例において、Ｂ型シリカゲル（吸放湿材）を含まない通常の鉱物質繊維板を基材として使用したものであり、塗料としては、Ｂ型シリカゲルが添加されていなくて通気性が低く耐水性のみに優れた塗料（実施例の塗料においてＢ型シリカゲルの添加を省いたもの）を使用したものである。その他の構成は実施例と同じである。
【００３１】
（比較例２）
比較例２は、基材の結合剤として耐水性のあるメラミンを添加し、塗料としては、比較例１と同様に、Ｂ型シリカゲルが添加されていなくて通気性が低くかつ耐水性に優れた塗料を使用したものである。
【００３２】
以上の実施例、比較例１及び比較例２についての組成を下記の表１に示す。
【００３３】
【表１】

【００３４】
上記実施例、比較例１及び比較例２に対し、▲１▼吸放湿性能、▲２▼ホルムアルデヒド吸着性能、▲３▼曲げ強度、及び▲４▼耐サグ性能（垂れ下がり性能）を試験により評価した。
【００３５】
▲１▼ 吸放湿性能
試験片の木口及び裏面をアルミテープにてマスキングし、２５℃５０％ＲＨ条件下で２４時間以上養生した。この養生後、雰囲気を２５℃９０％ＲＨに変更し、試験片の吸湿量を重量変化により測定した。２４時間の経過後、再び２５℃５０％ＲＨに戻し、放湿量を測定した。その結果を図３に示す。この図３によれば、実施例は比較例１及び比較例２の３倍以上の吸放湿量が得られている。すなわち、基材にＢ型シリカゲルを含まずかつ通気性の低い塗料を塗布した比較例１及び比較例２は、吸放湿性に劣っているのに対し、基材及び塗料にＢ型シリカゲルを含んだ実施例では、その吸放湿性が優れていることが判る。
【００３６】
▲２▼ ホルムアルデヒド吸着性能
１０ｃｍ角の試験片の木口及び裏面をアルミテープにてマスキングして、４０Ｌアクリルデシケータに設置し、このデシケータにホルムアルデヒドガスを０．５０ｐｐｍになるよう注入した。ガス注入から経時時間毎にデシケータ内の空気をサンプリングし、ＡＨＭＴ比色法によりホルムアルデヒド濃度を測定した。このような測定を常態（５５％ＲＨ）で行い、その測定結果を図４に示す。
【００３７】
この図４によれば、ホルムアルデヒドの吸着性能は、比較例１及び比較例２に比べ実施例の方が、残存率が低いので遥かに大きくなっていることが判る。比較例１及び比較例２は通気性の低い塗料を塗布しているので、ホルムアルデヒドの基材への物理吸着及び下塗り塗料の吸着剤への化学吸着が十分に行われず、ホルムアルデヒド吸着性能が劣っているのに対し、実施例では、ホルムアルデヒドの基材への物理吸着及び下塗り塗料の吸着剤への化学吸着が有効に行われている。
【００３８】
▲３▼ 曲げ強度
実施例、比較例１及び比較例２について、ＪＩＳＡ５９０５に従って曲げ強度（耐湿強度を含む）を測定した。養生は常態（２５℃５０％ＲＨ）及び増湿時（４０℃９０％ＲＨ）の各々で２４時間以上行った。その結果を表２に示す。
【００３９】
【表２】

【００４０】
この表２によれば、比較例２は基材に耐水性結合剤を添加しているので、増湿時の強度が最も高い。結合材として澱粉を使用している実施例は、水分によって強度が低下しているものの、基材中のＢ型シリカゲルが澱粉に対し湿気を選択的に多く吸着するので、比較例２に比べその約１割程度の減少に留まっている。尚、比較例１は実施例のような効果がないので、比較例２の約４割程度まで減少している。
【００４１】
これらの結果から、表面に耐水性塗料を塗布しても、裏面や木口からの湿気の浸入で基材の強度が低下することが判る。
▲４▼ 耐サグ性能（垂れ下がり性能）
図５に示す専用治具１０を用いて垂れ下がりの変位を測定した。この治具１０は、板状の基部１１と、この基部１１の長さ方向両端に起立状に立設された所定高さ（基準高さ）の支持部１２，１２とからなるもので、この治具１０上に試験片Ｔを長さ方向両端部が支持部１２，１２に支持されるように載置し、基部１１の長さ方向中央の上面から試験片Ｔの長さ方向中央部下面までの高さを垂れ下がり寸法ｈとした。試験片Ｔの幅は２５．４ｍｍ、長さは３００ｍｍであり、治具１０の両支持部１２，１２間の間隔、つまり試験片Ｔのスパンｓはｓ＝２８０ｍｍであった。
【００４２】
そして、試験片Ｔを２５℃５０％にて２４時間以上養生し、その後、２５℃９０％ＲＨ、３０℃９０％ＲＨ、４０℃９０％ＲＨに順に変更しながら、２４時間後の試験片Ｔが自重により垂れ下がるときの垂れ下がり寸法ｈの変位を測定した。この垂れ下がり寸法の測定結果を図６に示す。また、寸法変化の割合（％）を表３に示す。
【００４３】
【表３】

【００４４】
図６に示されている垂れ下がり寸法は、基本的に上記曲げ強度と同じ現象を示している。
【００４５】
また、表３に示されている寸法変化についてみると、実施例では、基材中、寸法変化の少ない吸放湿材（シリカゲル）が選択的に湿気を吸着するので、澱粉や故紙パルプのように膨張し易いものが湿気を吸い難くなっている。これに対し、比較例１では、これらのものがそのまま湿気を吸って膨張している。比較例２では、耐水性結合剤によって寸法変化が抑えられている。
【００４６】
以上の結果から、本発明によれば、基材としての鉱物質繊維板の吸放湿性能やホルムアルデヒド、ＶＯＣ、臭気等の物理吸着機能を確保し、水拭きが可能でしかもホルムアルデヒド、ＶＯＣ、臭気等の吸着機能と吸放湿性とを併せ持った化粧板が得られることが判る。
【００４７】
【発明の効果】
以上説明したように、請求項１の発明の化粧板によると、鉱物質繊維、無機充填材、結合剤及び吸放湿材からなる鉱物質繊維板の表面に、ビヒクルと、顔料と、通気性材とからなりかつ通気性及び耐水性を有する塗膜を形成したことにより、基材の結合材としてメラミン樹脂やフェノール樹脂等のような高価な耐湿性結合剤を用いた場合のようにコストアップすることなく、基材としての鉱物質繊維板の吸放湿性能やホルムアルデヒド、ＶＯＣ、臭気等の物理吸着機能を確保して、水拭きが可能でしかもホルムアルデヒド、ＶＯＣ、臭気等の吸着機能と吸放湿性とを併せ持った化粧板が得られる。
【００４８】
請求項２の発明によると、吸放湿材及び／又は通気性材を常態において吸放湿するＢ型シリカゲルとしたことにより、好ましい吸放湿材及び／又はが容易に得られる。
【図面の簡単な説明】
【図１】本発明の実施形態に係る化粧板の断面図である。
【図２】Ｂ型シリカゲルの吸湿性能をＡ型シリカゲルと比較して示す特性図である。
【図３】吸放湿性能を示す図である。
【図４】ホルムアルデヒド吸着性能を示す図である。
【図５】耐サグ性能のために治具を用いて試験片の垂れ下がり寸法の変位を測定する状態を示す図である。
【図６】耐サグ性能を示す図である。
【符号の説明】
Ａ化粧板
１鉱物質繊維板
２塗膜[0001]
TECHNICAL FIELD OF THE INVENTION
TECHNICAL FIELD The present invention relates to a decorative panel used as an interior material, and particularly to a technical field of a decorative panel that can be wiped with water and is suitable for use around water.
[0002]
[Prior art]
Conventionally, as this kind of decorative panel that can be wiped with water, for example, as shown in Patent Literature 1, a decorative panel in which water-resistant coating is applied to the surface of a base material made of rock wool (rock wool) has been known. I have. In this case, since water does not permeate into the inside, it can be wiped with water and can be used as a decorative board around water.
[0003]
[Patent Document 1]
JP-A-57-113063
[Problems to be solved by the invention]
However, in the case of the above-mentioned conventional patent document 1, on the other hand, since the moisture permeability is deteriorated by the water-resistant coating film, it is difficult to impair the original moisture absorption / release properties of rock wool and the formaldehyde adsorption function.
[0005]
In order to impart moisture resistance to the rock wool base material itself, it is conceivable to use a phenol resin or a melamine resin having excellent water resistance as a binder, but in such a case, it is more expensive than commonly used starch. Therefore, it is inevitable to increase the cost in order to develop the required strength.
[0006]
An object of the present invention is to provide a predetermined improvement to the configuration of the decorative board described above, thereby ensuring moisture permeability and ensuring water resistance without incurring an increase in cost as in the case of imparting moisture resistance to the substrate itself. The purpose of the present invention is to provide a decorative plate having the same.
[0007]
[Means for Solving the Problems]
In order to achieve the above object, in the present invention, a moisture absorbing / releasing material is contained in a base material of a decorative board, and a paint having both air permeability and water resistance is applied to the surface of the base material.
[0008]
Specifically, in the decorative board according to the first aspect of the present invention, the surface of the mineral fiber board as a base material composed of mineral fibers, an inorganic filler, a binder, and a moisture absorbing and releasing material is provided with a water-resistant vehicle. And a coating film formed of a pigment and a gas-permeable material and coated with a paint having both gas permeability and water resistance.
[0009]
According to the above configuration, since the mineral fiber board as the base material of the decorative board contains the moisture absorbing / releasing material, the moisture absorbing / releasing material selectively absorbs more moisture than the binder of the substrate. As a result, it is possible to prevent a decrease in strength and a dimensional change (for example, a sagging phenomenon when used as a ceiling material) due to moisture of the base material. In addition, as an inexpensive binder such as starch can be used without using an expensive moisture-resistant binder such as a melamine resin or a phenol resin as a binder of the base material, in order to exhibit sufficient strength. Cost does not increase.
[0010]
In addition, since a moisture absorbing and releasing material is used for the mineral fiber board, which is the base material of the decorative board, it is possible to prevent a high humidity environment, and to prevent condensation and mold propagation that may be a problem in the water area. Can be suppressed.
[0011]
Further, since a paint made of a water-resistant vehicle, a pigment and a breathable material and having both air permeability and water resistance is applied to the surface of the mineral fiber board to form a coating film, the decorative board surface At the same time, the air-permeable material dispersed in the coating film allows moisture and gas to permeate and absorbs and releases moisture by itself. As a result, the moisture absorption / desorption performance of the mineral fiber board as a base material and the physical adsorption function of formaldehyde, VOC, odor, etc. are not hindered, so that water can be wiped and formaldehyde, VOC, odor, etc. A decorative board having both an adsorption function and a moisture absorption / release property can be obtained.
[0012]
In the invention of claim 2, the moisture absorbing / releasing material and / or the gas permeable material is B-type silica gel. Since the B-type silica gel absorbs and releases moisture in a normal state unlike the A-type silica gel which does not release moisture in a normal state, it is particularly preferable as the above-mentioned moisture absorbing and releasing material and / or a gas-permeable material.
[0013]
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, embodiments of the present invention will be described in detail with reference to the drawings. The following description of preferred embodiments is merely exemplary in nature and is in no way intended to limit the invention, its applications, or its uses.
[0014]
FIG. 1 shows a decorative panel A according to an embodiment of the present invention, and the decorative panel A is used as a ceiling material or wall material in a room. Reference numeral 1 denotes a mineral fiber board as a base material, and a paint is applied to the surface of the mineral fiber board 1 to form a coating film 2.
[0015]
The mineral fiber board 1 includes mineral fibers such as rock wool, inorganic fillers such as pearlite and bentonite, a binder (binder) such as starch and waste paper pulp, and B-type silica gel as a moisture absorbing and releasing material. Consists of For example, it is obtained by forming these materials as a slurry, dehydrating, molding and drying.
[0016]
Unlike the A-type silica gel, the B-type silica gel as the above-mentioned moisture absorbing and releasing material absorbs and releases moisture in a normal state, and is therefore particularly preferable as the above-mentioned moisture absorbing and releasing material. A-type silica gel is excellent in hygroscopicity even at low humidity, but does not release moisture under normal conditions.
[0017]
That is, silica gel is roughly classified into A type and B type according to JIS, and both are different depending on the structure. A-type silica gel is used as a general drying agent, has a fine structure and a large surface area, and is bonded to water molecules by chemical adsorption. On the other hand, since B-type silica gel is not very fine, it has a small surface area and binds to water molecules by physical adsorption by capillary action between structures rather than chemical adsorption. Therefore, as shown in FIG. 2, the water molecules once adsorbed by the A-type silica gel do not desorb unless forcedly heated, whereas the B-type silica gel releases under low-humidity conditions, and thus has a respiratory action. In this embodiment, the B-type silica gel is used.
[0018]
In addition, other moisture absorbing / releasing materials other than the B-type silica gel can be used. In this case, as the moisture absorbing / releasing material to be used, a hydrophilic material which can easily adsorb moisture selectively is preferable, and furthermore, an inorganic material having almost no dimensional change is preferable. Viscous minerals that swell due to moisture absorption are also undesirable in inorganic systems.
[0019]
The coating film 2 is composed of a vehicle, a pigment, and B-type silica gel as a gas-permeable material having gas permeability by itself, and has both gas permeability and water resistance. In addition, a gas-permeable material other than B-type silica gel can be used.
[0020]
Therefore, in the decorative board A according to this embodiment, since the mineral fiberboard 1 as the base material contains B-type silica gel as the moisture absorbing and releasing material, the B-type silica gel is used as the binder of the base material. Moisture is more selectively adsorbed than the above, and it is possible to prevent a decrease in strength and a change in dimensions of the base material due to moisture. As the strength decrease and the dimensional change, there is a sagging phenomenon when the decorative board A is used as a ceiling material, for example. This sagging phenomenon is because starch used as a binder of the base material is gelatinized by moisture to lower the bonding strength. However, when B-type silica gel is added as in this embodiment, the B Since the type silica gel selectively absorbs more moisture than the starch (binder), the sagging phenomenon when used as a ceiling material is prevented.
[0021]
When an expensive moisture-resistant binder such as a melamine resin or a phenol resin is used as a binder for the mineral fiber board 1 (substrate), the cost increases in order to exhibit sufficient strength, but the cost is low. Since it becomes possible to use a binder such as natural starch, the cost does not increase.
[0022]
In addition, since the moisture absorbing / releasing material is used for the mineral fiber board 1 as a base material of the decorative board A, it is possible to prevent falling into a high-humidity environment, and to prevent dew condensation and mold propagation which are problematic in the water area. Can be suppressed.
[0023]
Further, a water-resistant vehicle, a breathable paint composed of a pigment and a breathable material is applied to the surface of the mineral fiber board 1 to form the coating film 2, so that the surface of the decorative board A can be wiped with water. At the same time, the porous B-type silica gel as a gas-permeable material dispersed in the coating film 2 allows moisture and gas to permeate and absorbs and releases moisture by itself. Accordingly, it is possible to prevent the moisture absorption / desorption performance of the mineral fiber board 1 as a base material and the physical adsorption function of formaldehyde, VOC, odor and the like from being hindered. Therefore, the decorative plate A can be wiped with water, and has both a function of adsorbing formaldehyde, VOC, odor and the like, and a property of absorbing and releasing moisture.
[0024]
【Example】
Next, a specific embodiment will be described.
[0025]
(Example 1)
The base material made of mineral fiberboard is made of rock wool as a main component, perlite and bentonite as inorganic fillers, starch and waste paper pulp as a binder, and B-type silica gel as a moisture absorbing and releasing material. did. The particle size of the B-type silica gel is 30 to 500 μm. These materials were uniformly dispersed and kneaded in water to form a slurry, which was formed by wet papermaking, which is a usual method for producing a mineral fiber board, dewatered under reduced pressure, press-formed, and further dried to obtain a base material.
[0026]
Next, the surface of the base material was coated with an undercoat and an overcoat. The undercoat paint is composed of 30% by weight of calcium carbonate as an extender pigment, 15% by weight of titanium oxide as a white pigment, 9% by weight of silica as a matting pigment, 16% by weight of vinyl acetate resin as a binder, and a dispersant as an auxiliary agent. A total of 1% by weight of a fungicide, a defoamer and a thickener, 2.5% by weight of acetylacetaminoamine (R-CONHNH ₂ ) as an amine as a formaldehyde adsorbent, and 3% by weight of B-type silica gel as a gas permeable material. % And the rest of the water was added and stirred. (Note that this undercoating material has some air permeability, and can be used without adding a gas permeable material.)
[0027]
On the other hand, the top coat paint contains 70% by weight of an acrylic resin as a binder, 3% by weight of a coloring pigment as a pigment, 4% by weight of a water repellent, and other dispersants, a fungicide, a defoamer, and an anti-blocking agent. The composition was made into a paint by adding 2 wt% of the agent in total and 3 wt% of B-type silica gel as a breathable material, and adding the remaining water. Then, the undercoating paint and the topcoating paint were used as water-resistant and moisture-permeable paints.
[0028]
The particle size of the B-type silica gel in the paint is not more than 75 μm, in other words, not more than the thickness of each of the undercoat and the overcoat. It is considered that acetylacetaminoamine as the above-mentioned formaldehyde adsorbent may be added to the top coat instead of the undercoat.
[0029]
Then, the undercoat paint is applied to the substrate surface at a rate of 150 to 250 g / m ² and dried, and then the top coat is applied at a rate of 50 to 150 g / m ² and dried. Was used as a test piece (sample).
[0030]
(Comparative Example 1)
Comparative Example 1 uses a normal mineral fiber board containing no B-type silica gel (moisture absorbing / desorbing material) as a base material in the above-described example, and no B-type silica gel was added as a coating material. A coating material having low air permeability and excellent water resistance only (the coating material of the example without addition of B-type silica gel) is used. Other configurations are the same as those of the embodiment.
[0031]
(Comparative Example 2)
In Comparative Example 2, water-resistant melamine was added as a binder for the base material, and as the coating material, as in Comparative Example 1, B-type silica gel was not added, and the air permeability was low and the water resistance was excellent. It uses paint.
[0032]
The compositions of the above Examples, Comparative Examples 1 and 2 are shown in Table 1 below.
[0033]
[Table 1]

[0034]
The above Examples, Comparative Examples 1 and 2, were evaluated by tests for (1) moisture absorption / desorption performance, (2) formaldehyde adsorption performance, (3) bending strength, and (4) sag resistance performance (hanging performance). did.
[0035]
{Circle around (1)} The mouth and the back of the test piece for moisture absorption / release performance were masked with an aluminum tape and cured at 25 ° C. and 50% RH for 24 hours or more. After this curing, the atmosphere was changed to 25 ° C. and 90% RH, and the amount of moisture absorption of the test piece was measured by weight change. After 24 hours, the temperature was returned to 25 ° C. and 50% RH again, and the amount of released moisture was measured. The result is shown in FIG. According to FIG. 3, in the example, the amount of moisture absorption / release is three times or more that of the comparative examples 1 and 2. That is, Comparative Examples 1 and 2 in which the base material was not coated with B-type silica gel and coated with a low-permeability coating material were inferior in moisture absorption / release properties, whereas the base material and the coating material included B-type silica gel. However, in the examples, it can be seen that the moisture absorption / release properties are excellent.
[0036]
{Circle around (2)} The test piece having a formaldehyde adsorption performance of 10 cm square was masked with an aluminum tape at the mouth and the back of the test piece, placed in a 40 L acrylic desiccator, and a formaldehyde gas was injected into the desiccator so as to be 0.50 ppm. The air in the desiccator was sampled every time elapsed from the gas injection, and the formaldehyde concentration was measured by the AHMT colorimetric method. Such a measurement is performed in a normal state (55% RH), and the measurement result is shown in FIG.
[0037]
According to FIG. 4, it can be seen that the adsorption performance of formaldehyde is much higher in the example than in the comparative example 1 and the comparative example 2 because the residual ratio is lower. In Comparative Example 1 and Comparative Example 2, a coating material having low air permeability was applied, so that the physical adsorption of formaldehyde to the base material and the chemical adsorption to the adsorbent of the undercoat coating material were not sufficiently performed, and the formaldehyde adsorption performance was poor. In contrast, in the examples, the physical adsorption of formaldehyde to the base material and the chemical adsorption of the undercoat paint to the adsorbent are effectively performed.
[0038]
{Circle around (3)} Flexural strength The flexural strength (including the moisture resistance) of the examples, comparative examples 1 and 2 was measured in accordance with JIS A 5905. Curing was performed for 24 hours or more in each of a normal state (25 ° C., 50% RH) and a humidified state (40 ° C., 90% RH). Table 2 shows the results.
[0039]
[Table 2]

[0040]
According to Table 2, Comparative Example 2 has the highest strength when humidified because the water-resistant binder is added to the substrate. In the example using starch as the binder, although the strength is reduced by moisture, the B-type silica gel in the base material selectively adsorbs a large amount of moisture to the starch. It has been reduced by about 10%. In addition, since the comparative example 1 does not have the effect of the embodiment, it is reduced to about 40% of the comparative example 2.
[0041]
From these results, it can be seen that even when the water-resistant paint is applied to the front surface, the strength of the base material is reduced due to the infiltration of moisture from the back surface or the tip of the wood.
(4) Anti-sag performance (hanging performance)
The hanging displacement was measured using the dedicated jig 10 shown in FIG. The jig 10 includes a plate-shaped base portion 11 and

support portions

12, 12 of a predetermined height (reference height) erected at both ends in the longitudinal direction of the base portion 11. The test piece T is placed on the jig 10 such that both ends in the longitudinal direction are supported by the supporting

portions

12, 12, and the lower surface of the test piece T in the longitudinal direction central portion from the upper surface at the center in the longitudinal direction of the base 11. The height up to this point was defined as a hanging dimension h. The width of the test piece T was 25.4 mm and the length was 300 mm, and the interval between the

support portions

12 and 12 of the jig 10, that is, the span s of the test piece T was s = 280 mm.
[0042]
Then, the test piece T is cured at 25 ° C. and 50% for 24 hours or more. After that, the test piece T after 24 hours is sequentially changed to 25 ° C. 90% RH, 30 ° C. 90% RH, and 40 ° C. 90% RH. Was measured by measuring the displacement of the sagging dimension h when sagging due to its own weight. FIG. 6 shows the measurement result of the sag dimension. Table 3 shows the dimensional change ratio (%).
[0043]
[Table 3]

[0044]
The sagging dimension shown in FIG. 6 basically shows the same phenomenon as the above bending strength.
[0045]
In addition, looking at the dimensional change shown in Table 3, in the examples, the moisture absorbing / releasing material (silica gel) having a small dimensional change in the base material selectively adsorbs moisture, so that it is similar to starch or waste paper pulp. Something that easily expands is less likely to absorb moisture. On the other hand, in Comparative Example 1, these materials expand as they absorb moisture. In Comparative Example 2, the dimensional change was suppressed by the water-resistant binder.
[0046]
From the above results, according to the present invention, the moisture absorption / desorption performance and the physical adsorption function of formaldehyde, VOC, odor and the like of the mineral fiber board as the base material are ensured, water can be wiped, and formaldehyde, VOC, odor It can be seen that a decorative board having both the adsorption function of the above and the moisture absorption / release properties can be obtained.
[0047]
【The invention's effect】
As described above, according to the decorative board of the first aspect of the present invention, the vehicle, the pigment, and the air permeable material are provided on the surface of the mineral fiber board made of the mineral fiber, the inorganic filler, the binder, and the moisture absorbent. By forming a coating film consisting of a material and having breathability and water resistance, the cost increases as when an expensive moisture-resistant binder such as melamine resin or phenol resin is used as the binder for the base material. The water absorption and release performance of formaldehyde, VOC, odor, etc. is ensured by securing the moisture absorption / desorption performance of the mineral fiber board as a base material and the physical adsorption function of formaldehyde, VOC, odor, etc., and the absorption function of formaldehyde, VOC, odor, etc. A decorative plate having both moisture release properties can be obtained.
[0048]
According to the second aspect of the present invention, by using the B-type silica gel which absorbs and releases moisture in a normal state, the preferred absorbent and / or breathable material can be easily obtained.
[Brief description of the drawings]
FIG. 1 is a sectional view of a decorative board according to an embodiment of the present invention.
FIG. 2 is a characteristic diagram showing the moisture absorption performance of B-type silica gel in comparison with A-type silica gel.
FIG. 3 is a diagram showing moisture absorption / release performance.
FIG. 4 is a graph showing formaldehyde adsorption performance.
FIG. 5 is a diagram showing a state in which a displacement of a sag dimension of a test piece is measured using a jig for sag resistance performance.
FIG. 6 is a graph showing sag resistance.
[Explanation of symbols]
A decorative board 1 mineral fiber board 2 coating film

Claims

On the surface of mineral fiber board as a base material composed of mineral fiber, inorganic filler, binder and moisture absorbing and releasing material,
A decorative board comprising a water-resistant vehicle, a pigment, and a gas-permeable material, and a coating film formed with a coating material having both gas-permeability and water-resistance.

The decorative board according to claim 1,
A decorative plate, wherein the moisture absorbing / releasing material and / or the breathable material is B-type silica gel.