JP2004182968A - Cycloolefin copolymer formed by ring-opening polymerization, process for producing the same, and optical material - Google Patents
Cycloolefin copolymer formed by ring-opening polymerization, process for producing the same, and optical material Download PDFInfo
- Publication number
- JP2004182968A JP2004182968A JP2003143161A JP2003143161A JP2004182968A JP 2004182968 A JP2004182968 A JP 2004182968A JP 2003143161 A JP2003143161 A JP 2003143161A JP 2003143161 A JP2003143161 A JP 2003143161A JP 2004182968 A JP2004182968 A JP 2004182968A
- Authority
- JP
- Japan
- Prior art keywords
- group
- ring
- general formula
- cyclic olefin
- opening copolymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】
【発明の属する技術分野】
本発明は、環状オレフィン系開環共重合体およびその製造方法並びに光学材料に関し、更に詳しくは、透明性等の光学特性に優れ、他素材との親和性が高くて接着性や印刷性等の後加工性が良好で、他の素材との親和性と低吸水(湿)性とのバランスに優れ、しかも、耐熱性および機械的強度に優れた環状オレフィン系開環共重合体およびその製造方法並びに光学材料に関する。
【0002】
【従来の技術】
近年、電子機器類の軽量化、小型・高密度化の要請に伴い、従来無機ガラスが用いられていたレンズ、バックライト、導光板、液晶基板などの光学部品や液晶表示素子部品の分野において、無機ガラスから光学的に透明な樹脂への代替が進められている。また、透明樹脂をシート、フィルムまたは薄膜などの形態で用いられることが多くなっている。
光学材料用の透明樹脂としては、従来、ポリアクリレート、ポリカーボネートなどが広く用いられている。然るに、無機ガラス代替用の透明樹脂においては、透明性以外に、耐熱性、耐吸湿性、接着・密着性、破壊強度などの特性の向上が求められている。
そして、このような要求に応えるため、光学材料として、環状オレフィン重合体が使用され始めている。
【0003】
例えば、透明性、耐熱性の優れた環状オレフィン重合体としては、ビシクロ[2.2.1]ヘプト−2−エン(ノルボルネン)を代表とする環状オレフィン化合物の付加重合体が提案されている(例えば、特許文献1、特許文献2、特許文献3および特許文献4参照。)。
しかしながら、これらの環状オレフィン系付加重合体は、300℃を超えるガラス転移温度を示すため、非常に高い耐熱性を有するものであるが、その反面、射出成形、押し出し成形などの熱溶融成形が困難である、などの問題がある。
【0004】
また、環状オレフィン系化合物の重合体としては、環状オレフィン系化合物と、エチレンなどの非環状オレフィン化合物との付加共重合体が知られている(例えば特許文献5、特許文献6および非特許文献1参照。)。そして、これらの環状オレフィン系付加共重合体を得るための重合触媒としては、メタロセンなどのジルコニウム、チタン、バナジウムを含む触媒系が知られている。
しかしながら、これらの触媒系は、エステル基やアルコキシシリル基などの極性基を含む単量体に対してはほとんど重合能を示さないため、得られる共重合体に接着性などの機能を付与したり、加水分解性シリル基などの架橋基を導入することが困難である。さらに、上記環状オレフィン系付加共重合体は、エチレン連鎖の結晶化などによって、透明性が低いものとなることがあり、光学材料として用いるには必ずしも好適なものではない。
【0005】
また、レンズや光ディスク等を製造するための光学材料に有用な環状オレフィン系重合体としては、環状オレフィン系化合物の開環(共)重合体もしくはその水素添加物が提案されている(例えば、特許文献7、特許文献8、特許文献9、特許文献10、特許文献11および特許文献12参照。)。これらの環状オレフィン系開環(共)重合体もしくはその水素添加物は、耐熱性に優れ、吸水(湿)性が低く、透明性等の光学特性にも優れ、さらに射出成形等の成形性にも優れたものである。然るに、このような環状オレフィン系開環(共)重合体もしくはその水素添加物は、極性基を有しないために他の素材との親和性が低く、例えば、接着、印刷あるいは蒸着等の後加工性に問題がある。
そして、斯かる問題を解決すべく、環状オレフィン系開環(共)重合体もしくはその水素添加物として、分子内に極性基を導入したものが提案されている(例えば、特許文献13、特許文献14参照。)。これらの環状オレフィン系開環(共)重合体もしくはその水素添加物は、耐熱性や光学特性に優れ、さらに射出成形等の成形性にも優れるばかりでなく、極性基を有しない環状オレフィン系開環(共)重合体もしくはその水素添加物と比較して、他の素材との親和性に優れるために、接着等の後加工性も優れたものである。然るに、このような環状オレフィン系開環(共)重合体もしくはその水素添加物は、機械的強度が低いため、シートやフィルム等の薄肉成形品としたときに問題が生じることがある。
【0006】
一方、ジシクロペンタジエン(別名:トリシクロ[5.2.1.02,6 ]デカ−3,8−ジエン)は、上記の環状オレフィン系重合体を得るための単量体の合成において、出発原料として工業的に広く用いられている化合物である。
然るに、ジシクロペンタジエン(以下、「DCP」ともいう。)それ自体を、環状オレフィン系重合体を得るための単量体として用いる場合には、DCPがその分子内にオレフィン性二重結合を2個有するため、ゲル状物や分岐を有するポリマーが生成することがあるため、環状オレフィン系重合体を工業的に製造するための原料としてDCPを用いる場合には、当該環状オレフィン系重合体の製造に支障が生じることがある、という問題がある。
そこで、複数のオレフィン性二重結合が存在することに起因する問題を解決するため、DCPにおけるノルボルネン環の二重結合が水素化され、5員環の二重結合のみが残存するトリシクロ[5.2.1.02,6 ]デカ−3−エンを開環(共)重合してなる開環(共)重合体およびその水素添加物が提案されている(例えば特許文献15参照。)。
しかしながら、このような開環(共)重合体は、トリシクロ[5.2.1.02,6 ]デカ−3−エンにおける5員環が開環したものであり、その水素添加物は、メチレン基の三連鎖を構造単位に含むものであるため、ガラス転移温度が比較的低いものしか得ることができない、という問題がある。
【0007】
また、DCPには、エキソ(exo)体およびエンド(endo)体の二種の立体異性体が存在するが、いずれの開環重合体の水素添加物においても、そのガラス転移温度はそれぞれ97℃、66℃であって100℃未満であるため、耐熱性を要求される材料に用いることは困難である(例えば非特許文献2参照。)。さらに、DCPに由来する構造単位の割合が70重量%以上である開環(共)重合体の水素添加物であって、用いられるDCPにおけるエンド体の割合が50%以上であるものが提案され、このような開環(共)重合体の水素添加物によれば、耐衝撃性などの機械的強度が改良される効果があるとされている(例えば、特許文献16参照。)。然るに、これらの開環(共)重合体のガラス転移温度はいずれも120℃以下であり、高い耐熱性が要求される材料として満足する性能を有するものではない。
【0008】
【特許文献1】
特開平4−63807号公報
【特許文献2】
特開平8−198919号公報
【特許文献3】
特表平9−508649号公報
【特許文献4】
特表平11−505880号公報
【特許文献5】
特開昭61−292601号公報
【特許文献6】
米国特許第2,883,372号明細書
【特許文献7】
特開昭63−21878号公報
【特許文献8】
特開平1−138257号公報
【特許文献9】
特開平1−168725号公報
【特許文献10】
特開平2−102221号公報
【特許文献11】
特開平2−133413号公報
【特許文献12】
特開平4−170425号公報
【特許文献13】
特開昭50−111200号公報
【特許文献14】
特開平1−132626号公報
【特許文献15】
特開平7−196779号公報
【特許文献16】
特開平11−130846号公報
【非特許文献1】
「マクロモレクラー ヘミー,マクロモレキュラー シンポジア(Die Makromolekulare Chemie,Macromolecular Symposia)」,(スイス),ヒューティッヒ アンド ヴェプフ フェアラーク,バーゼル(Huthig & Wepf Verlag,Basel),1991年,第47巻,p.83
【非特許文献2】
「ポリマージャーナル(Polymer Journal)」,(日本),社団法人高分子学会,1995年12月,第27巻,第12号,p.1167
【0009】
【発明が解決しようとする課題】
本発明は、以上のような事情に基づいてなされたものであって、その第1の目的は、透明性等の光学特性に優れ、他素材との親和性が高くて接着性や印刷性等の後加工性が良好であり、他素材との親和性と低吸水(湿)性とのバランスに優れ、しかも、優れた耐熱性および機械的強度を有する環状オレフィン系開環共重合体を提供することにある。
本発明の第2の目的は、上記の環状オレフィン系開環共重合体を有利に製造することができる方法を提供することにある。
本発明の第3の目的は、上記の環状オレフィン系開環共重合体よりなる光学材料を提供することにある。
【0010】
【課題を解決するための手段】
本発明の環状オレフィン系開環共重合体は、下記一般式(1−1)、下記一般式(1−2)若しくは下記一般式(1−3)で表される構造単位(A)と、下記一般式(2)で表される構造単位(B)とを、モル換算で10:90〜70:30となる割合で含有してなる環状オレフィン系開環共重合体または水素添加された環状オレフィン系開環共重合体であって、当該構造単位(A)を得るための単量体は、エンド体の割合が80モル%以上のものであり、ガラス転移温度が120〜250℃であることを特徴とする。
【0011】
【化5】
【0012】
〔一般式(1−1)〜一般式(1−3)において、R1〜R13は、それぞれ独立に水素原子、ハロゲン原子、または炭素数1〜4のアルキル基およびハロゲン化アルキル基から選ばれた基を示し、X1 〜X3 は、エチレン基またはビニレン基を示す。〕
【0013】
【化6】
【0014】
〔一般式(2)において、mは1または2であり、X4 はエチレン基またはビニレン基を示し、R14〜R17は、それぞれ独立に、水素原子、ハロゲン原子、炭素数1〜20のアルキル基、シクロアルキル基、アリール基、アルケニル基、ハロゲン化炭化水素基、R14若しくはR15とR16若しくはR17とが結合して形成されるアルキレン基、−(CH2 )k Zで表される基、またはR14若しくはR15とR16若しくはR17とが結合して形成される−(CH2 )k −C(O)O−で表される基を示し、R14〜R17のうち少なくとも1つは−(CH2 )k Zで表される基または−(CH2 )k −C(O)O−で表される基である。ここで、kは0〜3の整数であり、Zは、−C(O)O−R18または−OC(O)−R19で表される基を示し、R18およびR19は、炭素数1〜10の炭化水素基またはハロゲン化炭化水素基を示す。〕
【0015】
本発明の環状オレフィン系開環共重合体においては、上記一般式(1−1)、上記一般式(1−2)若しくは上記一般式(1−3)で表される構造単位(A)を得るための単量体は、下記一般式(3−1)、下記一般式(3−2)若しくは下記一般式(3−3)で表されるトリシクロモノオレフィン化合物よりなり、当該トリシクロモノオレフィン化合物におけるエンド体の割合が80モル%以上のものであることが好ましい。
【0016】
【化7】
【0017】
〔一般式(3−1)〜一般式(3−3)において、R1〜R13は、それぞれ独立に水素原子、ハロゲン原子、または炭素数1〜4のアルキル基およびハロゲン化アルキル基から選ばれた基を示す。〕
【0018】
また、本発明の環状オレフィン系開環共重合体においては、加水分解性シリル基またはオキセタニル基を側鎖に有する環状オレフィン系化合物に由来する構造単位(C)を全構造単位の0.1〜30モル%となる割合で含有していてもよい。
また、本発明の環状オレフィン系開環共重合体においては、前記加水分解性シリル基またはオキセタニル基によって架橋されていてもよい。
また、本発明の環状オレフィン系開環共重合体においては、構造単位(A)の少なくとも一部が、トリシクロ[5.2.1.02,6 ]デカ−8−エンに由来する構造単位であることが好ましい。
【0019】
本発明の環状オレフィン系開環共重合体の製造方法は、上記一般式(3−1)、上記一般式(3−2)若しくは上記一般式(3−3)で表されるトリシクロモノオレフィン化合物よりなり、当該トリシクロモノオレフィン化合物におけるエンド体の割合が80モル%以上である単量体と、下記一般式(4)で表される単量体とがモル換算で10:90〜70:30となる割合で含有されてなる単量体組成物を、開環共重合処理する工程を有することを特徴とする。
【0020】
【化8】
【0021】
〔一般式(4)において、mは1または2であり、R14〜R17は、それぞれ独立に、水素原子、ハロゲン原子、炭素数1〜20のアルキル基、シクロアルキル基、アリール基、アルケニル基、ハロゲン化炭化水素基、R14若しくはR15とR16若しくはR17とが結合して形成されるアルキレン基、−(CH2 )k Zで表される基、またはR14若しくはR15とR16若しくはR17とが結合して形成される−(CH2 )k −C(O)O−で表される基を示し、R14〜R17のうち少なくとも1つは−(CH2 )k Zで表される基または−(CH2 )k −C(O)O−で表される基である。ここで、kは0〜3の整数であり、Zは、−C(O)O−R18または−OC(O)−R19で表される基を示し、R18およびR19は、炭素数1〜10の炭化水素基またはハロゲン化炭化水素基を示す。〕
【0022】
本発明の環状オレフィン系開環共重合体の製造方法においては、前記単量体組成物を開環共重合処理した後、水素添加することが好ましい。
【0023】
本発明の光学材料は、上記の環状オレフィン系開環共重合体を含有してなることを特徴とする。
【0024】
【発明の実施の形態】
以下、本発明の実施の形態について詳細に説明する。
本発明の環状オレフィン系開環共重合体は、上記一般式(1−1)、上記一般式(1−2)若しくは上記一般式(1−3)で表される構造単位(A)(以下、単に「構造単位(A)」ともいう。)と、上記一般式(2)で表される構造単位(B)(以下、単に「構造単位(B)」ともいう。)とよりなるものである。
【0025】
本発明の環状オレフィン系開環共重合体における構造単位(A)を得るための単量体としては、上記一般式(3−1)、上記一般式(3−2)若しくは上記一般式(3−3)で表されるトリシクロモノオレフィン化合物よりなり、当該トリシクロモノオレフィン化合物におけるエンド体の割合が80モル%以上であるもの(以下、「特定単量体(A)」という。)が好ましく用いられる。
このような特定単量体(A)としては、公知の方法を適宜用いて合成されたものを使用することができ、その合成法としては特に限定されるものではないが、一般にはシクロペンタジエン(以下、「CPD」ともいう。)またはDCPと、目的とする特定単量体(A)に応じて選択された単環状モノオレフィン類、例えばシクロペンテンやシクロヘキセンとのディールス−アルダー(Diels−Alder)反応による合成法が利用される。
かかるディールス−アルダー反応は、窒素、アルゴンなどの不活性気体の雰囲気下で行うことが好ましく、反応溶媒は、特に必要とされる場合を除き、用いなくてもよい。反応温度は、高ければ高いほど反応速度が高くなるが、エンド体生成の選択性が低下することが多く、このような観点から、通常、150〜250℃、好ましくは170〜230℃の範囲内で実施される。
【0026】
反応に供されるCPDまたはDCPと単環状モノオレフィンとは、任意の割合で用いることができるが、エンド体生成の選択性などの観点から、単環状モノオレフィンをCPDまたはDCPに対して3〜50当量過剰に用いることが好ましい。また、反応原料の添加方法としては、反応原料の全部を1回で反応系に供給する方法、CPDまたはDCP、および単環状モノオレフィンの少なくとも一方を2回以上に分割して反応系に供給する方法、CPDまたはDCP、および単環状モノオレフィンの少なくとも一方を反応系に連続的に供給する方法のいずれであってもよい。
このようにして得られる生成物は、蒸留などの公知の方法によって、分離、精製した後、本発明の環状オレフィン系開環共重合体を得るための特定単量体(A)として供される。
【0027】
特定単量体(A)において、エンド体の割合が80モル%以上であることが必要であり、好ましくは90モル%以上、さらに好ましくは95モル%以上である。特定単量体(A)におけるエンド体の割合が80モル%未満である場合には、得られる開環共重合体水素化物の機械強度が不十分なものとなる。
ここで、特定単量体(A)におけるエンド体とエキソ体との割合は、ガスクロマトグラフィー分析によって測定することができる。
【0028】
特定単量体(A)の具体例としては、
トリシクロ[5.2.1.02,6 ]デカ−8−エン、
3−メチルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
4−メチルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
3,4−ジメチルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
3,5−ジメチルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
3,4,5−トリメチルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
3−エチルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
4−エチルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
3,4−ジエチルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
3,5−ジエチルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
3−メチル−5−エチルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
3−イソプロピルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
4−イソプロピルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
3,4−ジイソプロピルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
3,5−ジイソプロピルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
3−メチル−5−イソプロピルトリシクロ[5.2.1.02,6 ]デカ−8−エン、
3−クロロトリシクロ[5.2.1.02,6 ]デカ−8−エン、
などのトリシクロ[5.2.1.02,6 ]デセン類、
【0029】
トリシクロ[6.2.1.02,7 ]ウンデカ−3−エン、
3−メチルトリシクロ[6.2.1.02,7 ]ウンデカ−3−エン、
4−メチルトリシクロ[6.2.1.02,7 ]ウンデカ−3−エン、
3,4−ジメチルトリシクロ[6.2.1.02,7 ]ウンデカ−3−エン、
3,5−ジメチルトリシクロ[6.2.1.02,7 ]ウンデカ−3−エン、
3,4,5,6−テトラメチルトリシクロ[6.2.1.02,7 ]ウンデカ−3−エン、
3−エチルトリシクロ[6.2.1.02,7 ]ウンデカ−3−エン、
4−エチルトリシクロ[6.2.1.02,7 ]ウンデカ−3−エン、
などのトリシクロ[6.2.1.02,7 ]ウンデセン類、
【0030】
トリシクロ[8.2.1.02,9 ]トリデカ−11−エン、
3−メチルトリシクロ[8.2.1.02,9 ]トリデカ−11−エン、
4−メチルトリシクロ[8.2.1.02,9 ]トリデカ−11−エン、
5−メチルトリシクロ[8.2.1.02,9 ]トリデカ−11−エン、
などのトリシクロ[8.2.1.02,9 ]トリデセン類
などが挙げられるが、これらに限定されるものではない。
これらの化合物は、1種単独でまたは2種以上を組み合わせて特定単量体(A)として用いることができる。
【0031】
これらの中でも、トリシクロ[5.2.1.02,6 ]デカ−8−エン、トリシクロ[6.2.1.02,7 ]ウンデカ−3−エン、トリシクロ[8.2.1.02,9 ]トリデカ−11−エンが好ましく、特に、トリシクロ[5.2.1.02,6 ]デカ−8−エンは入手しやすいため好ましく用いられる。
【0032】
以上のように、本発明の環状オレフィン系開環共重合体における構造単位(A)は、上記の特定単量体(A)を開環共重合する方法によって得ることができるが、これ以外の方法としては、例えば、トリシクロ[5.2.1.02,6 ]デカ−3,8−ジエン(ジシクロペンタジエン)などのトリシクロジオレフィン類を開環共重合し、しかる後、側鎖の環状オレフィン性不飽和結合を水素添加する方法によっても得ることができる。かかる方法を適用する場合には、側鎖の環状オレフィン性不飽和結合が開環重合中に反応してゲル状物や分岐を有するポリマーが生成することがあるので、このような副反応が起きないように重合条件を適宜調整することが好ましい。
【0033】
本発明においては、構造単位(B)を得るための単量体として、上記一般式(4)で表される単量体(以下、「特定単量体(B)」という。)が用いられる。
【0034】
特定単量体(B)の具体例としては、
8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン、
8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン、
8−メチル−8−エトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン、
8−メチル−8−ブトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン、
8−メチル−8−シクロヘキシルオキシカルボニルテトラシクロ[4.4.0.12,5.17,10]ドデカ−3−エン、
8−トリフロロエチルオキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン、
8−アセトキシオキシテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン、
8−メチル−8−アセトキシオキシテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン、
11−メチル−11−メトキシカルボニルヘキサシクロ[6.6.1.13,5 .02,7 .09,14.110,13 ]ヘプタデカ−4−エン、
11−メトキシカルボニルヘキサシクロ[6.6.1.13,6 .02,7 .09,14.110,13 ]ヘプタデカ−4−エン、
などが挙げられるが、これらに限定されるものではない。
これらの化合物は、1種単独でまたは2種以上を組み合わせて特定単量体(B)として用いることができる。
これらの中でも、mが1であるテトラシクロドデセン類が好ましく、8−メトキシカルボニル−テトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン、8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エンがより好ましい。
【0035】
本発明の環状オレフィン系開環共重合体における構造単位(A)と構造単位(B)との割合は、モル換算で構造単位(A):構造単位(B)が10:90〜70:30、好ましくは20:80〜65:35とされ、これにより、接着性または密着性と低吸水(湿)性とのバランスが良好で、かつ、耐熱性および機械強度に優れた、光学材料に好適な環状オレフィン系開環共重合体が得られる。
構造単位(A)の割合が過小である場合には、当該環状オレフィン系開環共重合体は、その機械強度が低いものとなることがある。一方、構造単位(A)の割合が過大である場合には、当該環状オレフィン系開環共重合体は、その接着性または密着性が低いものとなると共に、ガラス転移温度が低いものとなって耐熱性が低いものとなることがある。
【0036】
また、本発明の環状オレフィン系開環共重合体においては、全構造単位における構造単位(A)および構造単位(B)の合計の割合が50モル%以上であることが好ましく、より好ましくは70モル%以上、さらに好ましくは80モル%以上である。構造単位(A)および構造単位(B)の合計の割合が50モル%未満である場合には、耐熱性、透明性や複屈折性等の光学特性、吸水(湿)性、他素材との親和性などの特性について、良好なバランスを得ることが困難になり、いずれかの特性が実用に適さないものとなることがある。
【0037】
本発明の環状オレフィン系開環共重合体においては、上記構造単位(A)および上記構造単位(B)に加えて、さらに加水分解性シリル基またはオキセタニル基を側鎖に有する環状オレフィン系化合物(以下、「特定単量体(C)」という。)に由来する構造単位(C)を含有させることができる。ここで、加水分解性シリル基としては、下記一般式(5−1)または下記一般式(5−2)で表される基を挙げることができる。
【0038】
【化9】
【0039】
〔一般式(5−1)および一般式(5−2)において、R20およびR21は、それぞれ独立に、水素原子または炭素数が1〜20の炭化水素基を示し、R22〜R25は、それぞれ独立に、炭素数が1〜10のアルキル基、アリール基、アルコキシ基、アリロキシ基およびハロゲン原子から選ばれた置換基を示し、nは0〜5の整数を示す。また、Yは、炭素数が2〜20の脂肪族ジオール、脂環族ジオールまたは芳香族ジオールの炭化水素残基を示す。〕
【0040】
このような構造単位(C)を含有してなる環状オレフィン系開環共重合体は、光酸発生剤、熱酸発生剤、加水分解により有機酸または無機酸が発生する化合物、スズ、アルミニウム、ジルコニウム、チタンなどの金属と、有機酸若しくはβ−ジケトンとの塩、またはこれらの金属のアルコキシド若しくはフェノキシドなどによって、側鎖の加水分解性シリル基またはオキセタニル基を架橋することができ、これにより、耐薬品性、耐溶剤性、耐熱性、機械的強度が改良された環状オレフィン系開環共重合体を得ることができる。
【0041】
特定単量体(C)の具体例としては、以下の化合物を例示することができるが、本発明はこれらに限定されるものではない。
加水分解性シリル基を有する環状オレフィン系化合物の具体例としては、
5−トリメトキシシリルビシクロ[2.2.1]ヘプト−2−エン、
5−トリエトキシシリルビシクロ[2.2.1]ヘプト−2−エン、
5−メチルジメトキシシリルビシクロ[2.2.1]ヘプト−2−エン、
5−メチルジエトキシシリルビシクロ[2.2.1]ヘプト−2−エン、
5−トリクロロシリルビシクロ[2.2.1]ヘプト−2−エン、
5−メチルジクロロシリルビシクロ[2.2.1]ヘプト−2−エン、
5−[1’,4’,4’−トリメチル−2’,6’−ジオキサ−1’−シラシクロヘキシル]ビシクロ[2.2.1]ヘプト−2−エン、
8−トリエトキシシリル−テトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン、
8−メチルジエトキシシリル−テトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エンなどを挙げることができる。
【0042】
オキセタニル基を有する環状オレフィン系化合物の具体例としては、
2−[(3−オキセタニル)メトキシ]ビシクロ[2.2.1]ヘプト−5−エン、
2−[(3−エチル−3−オキセタニル)メトキシ]ビシクロ[2.2.1]ヘプト−2−エン、
2−[(3−オキセタニル)メトキシメチル]ビシクロ[2.2.1]ヘプト−5−エン、
2−[(3−エチル−3−オキセタニル)メトキシメチル]ビシクロ[2.2.1]ヘプト−2−エン、
8−[(3−エチル−3−オキセタニル)メトキシメチル]テトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン、
ビシクロ[2.2.1]ヘプト−5−エン−2−カルボン酸(3−エチル−3−オキセタニル)メチル、
2−メチルビシクロ[2.2.1]ヘプト−5−エン−2−カルボン酸(3−エチル−3−オキセタニル)メチルなどを挙げることができる。
これらの化合物は、1種単独または2種以上を組み合わせて特定単量体(C)として用いることができる。
【0043】
本発明の環状オレフィン系開環共重合体において、構造単位(C)を含有する場合には、その割合が全構造単位の0.1〜30モル%であることが好ましく、より好ましくは1〜20モル%である。この割合が0.1モル%未満である場合には、架橋が充分に行われず、そのため、得られる環状オレフィン系開環共重合体は、耐溶媒性、耐薬品性、機械的強度の改良が不充分なものとなる。一方、この割合が30モル%を超える場合には、得られる環状オレフィン系開環共重合体の吸水性が増大し、さらに成形体とされたときの強靭性が低下することがある。
【0044】
また、本発明の環状オレフィン系開環共重合体においては、構造単位(A)、構造単位(B)および必要に応じて導入される構造単位(C)に加えて、これらの構造単位以外のノルボルネン系化合物(以下、「特定単量体(D)」という。)に由来する構造単位(D)を全構造単位の30モル%以下となる割合で含有させることができる。
特定単量体(D)の具体例としては、ビシクロ[2.2.1]ヘプト−2−エン(ノルボルネン)、5−メチルビシクロ[2.2.1]ヘプト−2−エンや5−ヘキシルビシクロ[2.2.1]ヘプト−2−エンなどのアルキル置換ノルボルネン、5−トリフルオロメチルビシクロ[2.2.1]ヘプト−2−エンなどのハロゲン化アルキル置換ノルボルネン、5−フェニルビシクロ[2.2.1]ヘプト−2−エンなどのアリール置換ノルボルネン、5−フェニルメチルビシクロ[2.2.1]ヘプト−2−エンなどアラルキル置換ノルボルネン、テトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン、8−エチルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エンなどのテトラシクロドデセン類を挙げることができる。このような化合物を共重合することにより、得られる環状オレフィン系開環共重合体のガラス転移温度や加工性を調節したり、柔軟性を付与したりすることができる。
【0045】
本発明の環状オレフィン系開環共重合体のガラス転移温度は、120〜250℃であり、好ましくは120〜180℃、さらに好ましくは130〜170℃である。このガラス転移温度が120℃未満である場合には、当該環状オレフィン系開環共重合体の耐熱性が低く、一方、このガラス転移温度が250℃を超える場合には、当該環状オレフィン系開環共重合体は、射出成形や押し出し成形などの熱溶融成形における加工性が低いものとなるばかりでなく、熱溶融成形において、高い成形温度が必要となるため、環状オレフィン系開環共重合体が熱劣化しやすく、得られる成型品が脆くなったり着色したりすることがあるため、好ましくない。
【0046】
本発明の環状オレフィン系開環共重合体は、120℃でゲル・パーミエションクロマトグラフィーにより測定されるポリスチレン換算の数平均分子量(Mn)が、好ましくは5,000〜300,000、より好ましくは10,000〜100,000、特に好ましくは20,000〜70,000であり、同重量平均分子量(Mw)が、好ましくは20,000〜700,000、より好ましくは40,000〜400,000、特に好ましくは50,000〜200,000である。
上記数平均分子量が5,000未満である場合または上記重量平均分子量が20,000未満である場合には、当該環状オレフィン系開環共重合体をフィルム、薄膜またはシートとしたときに、その破壊強度および伸びが小さくて割れやすくなることが多い。一方、上記数平均分子量が300,000を超える場合または重量平均分子量が700,000を超える場合には、当該環状オレフィン系開環共重合体は溶融粘度および溶液粘度が高いものとなり、成形加工における取扱いが困難となることがあり好ましくない。
ここで、環状オレフィン系開環共重合体の分子量は、重合触媒の量、分子量調節剤の添加量、共重合体への転化率および重合温度を変更することによって調節することができる。
【0047】
本発明の環状オレフィン系開環共重合体は、特定単量体(A)と、特定単量体(B)と、必要に応じて用いられる特定単量体(C)および/または特定単量体(D)とが含有されてなる単量体組成物を開環共重合処理することにより、あるいは上記単量体組成物を開環共重合処理した後、得られる生成物に水素添加することにより製造される。
ここで、単量体組成物における特定単量体(A)と特定単量体(B)との割合は、モル換算で特定単量体(A):特定単量体(B)が10:90〜70:30、好ましくは20:80〜65:35とされ、これにより、接着性または密着性と低吸水(湿)性とのバランスが良好で、かつ、耐熱性および機械強度に優れた、光学材料に好適な環状オレフィン系開環共重合体が得られる。
【0048】
開環共重合処理に用いられる重合触媒としては、単成分系触媒または多成分系触媒が用いられる。
(1)単成分系触媒としては、
ビスシクロペンタジエニル−3,3−ジメチルチタナシクロブタン、ビスシクロペンタジエニル−3−t−ブチルチタナシクロブタン、または
W(OR26)2 (=NAr)(=CH(C(CH3 ) 2 R27)、
Mo(OR28)2 (=NAr)(=CH(C(CH3 )2 R29)、
W(Br)2 (OCH2 (t−Bu))2 (=CH(t−Bu))、
W(CO)4 (=C(OMe)(CH2 CH2 CH=CH2 )、
RuCl2 [PPh3 ]2 (=CHCO2 Et)、
RuCl2 [PCy3 ]2 (=CHCH=CPh2 )、
RuCl2 [PCy3 ]2 (=CHPh)、
Ta(OAr)3 (=CH(t−Bu))、若しくは
Ta(SAr’)3 (=CH(t−Bu))
〔ここで、R26〜R29は、炭化水素基あるいはハロゲン化炭化水素基を示し、ArおよびAr’は芳香族置換基を示す。〕で表される化合物を用いることができる。
【0049】
(2)多成分系触媒としては、(i)成分:タングステン、モリブデン、レニウム、チタンおよびハフニウムの化合物から選ばれた少なくとも1種と、(ii)成分:周期表IA、IIA、IIB、IIIA、IVAあるいはIVB族元素の化合物であって、当該元素−炭素結合または当該元素−水素結合を有するものから選ばれた少なくとも1種とを組み合わせてなるものを好適に用いることができ、必要に応じて、(ii) 成分:添加剤(活性向上剤)をさらに組み合わせたものであってもよい。
(i)成分として適当なタングステン、モリブデン、レニウム、チタンまたはハフニウムの化合物としては、これらのハロゲン化物、オキシハロゲン化物、アルコキシド、フェノキシド、カルボン酸塩、β−ジケトン化合物、スルフォン酸塩、リン酸塩、亜リン酸塩、カルボニル錯体、アセトニトリル錯体、シクロペンタジエニル錯体、インデニル錯体、ヒドリド錯体、およびそれらの誘導体などが挙げられ、これらは単独でまたは2種以上を組み合わせて用いることができるが、タングステンおよびモリブデンの化合物としては、特にアルコキシド、フェノキシド、ハロゲン化物、オキシハロゲン化物が高い重合活性を示すことから好ましく用いられる。
【0050】
(i)成分として用いられる化合物の具体例としては、WCl6 、WCl5 、WCl4 、WBr6 、WBr4 、WOCl4 、WOBr4 、W(OC6 H5 )6 、WCl4 (OCH2 CH2 Cl)2 、WCl2 (OC6 H5 )4 、WOCl2 〔OC6 H3 −2,6−(i−Pr)2 〕2 、WO(OC6 H3 −2,6−Me2 )4 、MoCl5 、MoCl3 、Mo(OC2 H5 )5 、MoO2 (acac)2 、Mo(CO)5 (C5 H5 N)、WCl6 ・(C5 H5 N)、ReOCl3 、Re(CO)5 Cl、TiCl4 、HfCl4 、ZrCl4 、(η5 −C5 H5 )2 TiCl2 、(η5 −C9 H7 )2 TiCl2 などが挙げられる。これらは、1種単独でまたは2種以上を組み合わせて用いることができる。
【0051】
(ii)成分として用いられる化合物の具体例として、例えば、メチルリチウム、エチルリチウム、ブチルリチウム、フェニルリチウム、シクロペンタジエニルリチウムなどの有機リチウム類、シクロペンタジエニルナトリウムなどの有機ナトリウム類、ジメチルマグネシウム、ジエチルマグネシウム、ジブチルマグネシウム、ハロゲン化エチルマグネシウム、ハロゲン化ブチルマグネシウムなどの有機マグネシウム類、トリアルキルアルミニウム、ジアルキルアルミニウムハライド、アルキルアルミニウムジハライド、アルキルアルミニウムセスキハライド、水素化ジアルキルアルミニウム、アルキルアルミノキサンなどの有機アルミニウム類、ジアルキル亜鉛などの有機亜鉛類、テトラアルキルスズ、テトラフェニルスズなどの有機スズ類、水素化リチウム、水素化リチウムアルミニウム、水素化ナトリウム、水素化ホウ素ナトリウム、水素化アルミニウムなどの金属水素化物類などを使用することができる。
(ii)成分は、(i)成分に対して金属原子に換算したモル比で好ましくは1〜100倍、より好ましくは2〜30倍の範囲で用いられる。
【0052】
(iii)成分の活性向上剤は、開環共重合の活性をより向上させるために必要に応じて用いられ、その具体例としては、水、酸素、アセトアルデヒド、アセトアルデヒドジエチルアセタール、エチレンオキシド、エピクロルヒドリン、N−ニトロソジメチルアニリン、テトラブチルアンモニウムクロライド、N−ニトロソジフェニルアミン、三臭化アルミニウムなどを挙げることができる。
(iii)成分の使用割合は、特に限定されるものではなく、その種類により 適宜選択されるが、通常、(i)成分に対して、モル比で0.005〜10倍、好ましくは0.01〜2倍の範囲で用いられる。
【0053】
開環共重合処理に用いられる溶媒としては、ペンタン、ノルマルヘキサン、ノルマルヘプタン、ブタン、2−メチルブタンなどの脂肪族炭化水素、シクロヘキサン、シクロペンタン、メチルシクロペンタンなどの脂環式炭化水素、トルエン、ベンゼン、キシレン、メシチレンなどの芳香族炭化水素、ジクロロメタン、1,2−ジクロロエタン、1,2−ジクロロエチレン、クロロベンゼン、o−ジクロロベンゼンなどのハロゲン化炭化水素、酢酸エチル、酢酸ブチル、γ−ブチロラクトン、ニトロメタンなどの極性溶媒が挙げられ、これらは1種単独でまたは2種以上を組み合わせて用いることができる。また、溶媒の使用量は単量体に対して重量比で1〜20倍の範囲であることが好ましい。
【0054】
開環共重合処理の具体的な方法の一例について説明すると、窒素またはアルゴン雰囲気下で、反応容器に、溶媒と、必須の単量体である特定単量体(A)および特定単量体(B)、並びに任意の単量体である特定単量体(C)および/または特定単量体(D)からなる単量体成分と、必要に応じて用いられる分子量調節剤とを仕込み、この重合系を−20℃から100℃の範囲の温度に設定する。次いで、この重合系に重合触媒を添加して−20℃から120℃の範囲で重合を行う。
以上において、分子量調節剤としては、エチレン、プロピレン、1−ブテン、1−ヘキセン、1−オクテンなどのα−オレフィン、ビニルエーテル、チオビニルエーテル、酢酸ビニルなどを用いることができる。
また、重合触媒の添加量は、当該重合触媒における遷移金属原子1グラム原子当たり単量体成分が100〜100,000モルとなる量であることが好ましい。
また、重合方式はバッチ式であっても連続式であってもよい。
また、特定単量体(A)または特定単量体(B)、さらに必要に応じて使用される特定単量体(C)または特定単量体(D)のいずれかを反応容器に供給して重合を開始し、重合処理中に、その他の単量体を反応容器に段階的にまたは連続的に供給することにより、構造単位の各々の割合が傾斜的に変化した状態または各構造単位がブロック状に偏在した状態の環状オレフィン系開環共重合体を得ることもできる。
また、重合反応の停止は、水、アルコール、有機酸、炭酸ガス、アルデヒド化合物、ケトン化合物などから選ばれた化合物により行われる。
【0055】
重合反応が終了した後、必要に応じて、重合反応混合物に対して重合触媒残さの分離・除去処理を行ってもよい。かかる分離・除去処理の方法としては、公知の方法を適宜用いることができる。例えば、重合反応混合物に塩酸、硝酸、硫酸などの無機酸や、マレイン酸、フマル酸などの有機酸を添加し、その後、水やアルコールの溶液で洗浄する方法などが挙げられる。また、重合触媒残さは、珪藻土、アルミナ、シリカ、活性炭などの吸着剤に吸着させることによって、或いはフィルターなどによるろ過処理を行うことによって、除去することもできる。
そして、重合体溶液をメタノール、エタノール、イソプロパノールなどのアルコール類やその他の貧溶媒を用いて凝固し、減圧および/または加熱乾燥することにより、目的とする環状オレフィン系開環共重合体が得られる。この工程では、重合体溶液に残存する未反応モノマーも除去される。
【0056】
本発明の環状オレフィン系開環共重合体は、必ずしも水素添加されていることは必要ではなく、その用途に応じて上記開環重合によって得られた開環共重合体をそのまま使用することもできるが、加熱着色や熱劣化が抑制されて優れた熱安定性が得られる点で、分子中のオレフィン性不飽和結合が水素添加されていることが好ましい。
【0057】
分子中のオレフィン性不飽和結合を水素添加するための水素化反応は、開環重合が終了した後、その共重合体溶液を使用して行ってもよく、触媒残さや未反応の単量体を除去処理した後に、開環共重合体を適宜の溶媒に溶解することによって調製された共重合体溶液を使用して行ってもよい。
水素化反応は、通常、水素圧が1.0〜15MPa、温度が50〜200℃の条件で行われる。水素化触媒としては、シリカ、アルミナ、ゼオライト、ケイソウ土、マグネシア、カーボン、炭酸カルシウムなどから選ばれた担体にパラジウム、白金、プラチナ、ロジウム、イリジウム、ルテニウム、ニッケルから選ばれた金属が担持された不均一系触媒、あるいはオクタン酸ニッケル/トリエチルアルミニウム、ナフテン酸ニッケル/トリエチルアルミニウム、オクタン酸コバルト/トリエチルアルミニウム、オクタン酸コバルト/n−ブチルリチウム、ビスシクロペンタジエニルチタニウムジクロライド/ジエチルアルミニウムクロライド、酢酸パラジウム/トリエチルアルミニウム、トリス(トリフェニルホスフィン)クロロロジウム、トリス(トリフェニルホスフィン)ヒドリド・カルボニル・クロロ・ルテニウム、トリス(トリトリルホスフィン)ヒドリド・カルボニル・クロロ・ルテニウム、トリス(トリキシリルホスフィン)ヒドリド・カルボニル・クロロ・ルテニウム、トリス(トリシクロヘキシルホスフィン)ヒドリド・カルボニル・クロロルテニウム、トリス(トリフェニルホスフィン)ジヒドロ・カルボニル・ルテニウム、ビス(トリフェニルホスフィン)ジクロロルテニウムなどの均一系触媒が好適に用いられる。
水素化触媒は、通常、開環共重合体に対し、遷移金属原子換算で10〜1000ppmの範囲で使用される。
【0058】
水素添加された開環共重合体は、分子中のオレフィン性不飽和結合の水素化率が高いほど優れた熱安定性を有するものとなる。その結果、脱溶媒工程、ペレット化工程、製品の成形加工工程などにおいて、加熱による熱劣化や酸素による劣化などを抑制することができる。
水素化率は、通常、95%以上、好ましくは99%以上、さらに好ましくは99.5%以上である。水素化率が95%未満の場合には、当該水素添加開環共重合体は、耐熱劣化性が不十分となることがある。
【0059】
本発明の環状オレフィン系開環共重合体には、公知の酸化防止剤、例えば、2,6−ジ−t−ブチル,4−メチルフェノール、4,4’−チオビス−(6−t−ブチル−3−メチルフェノール)、1,1’−ビス(4−ヒドロキシフェニル)シクロヘキサン、2,2’−メチレンビス(4−エチル−6−t−ブチルフェノール)、2,5−ジ−t−ブチルヒドロキノン、ペンタエリスリチル−テトラキス[3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネートなどのフェノール系あるいはヒドロキノン系酸化防止剤を添加することができる。さらに、トリス(4−メトキシ−3,5−ジフェニル)ホスファイト、トリス(ノニルフェニル)ホスファイト、トリス(2,4−ジ−t−ブチルフェニル)ホスファイト、ビス(2,6−ジ−t−ブチル−4−メチルフェニル)ペンタエリストールジホスファイト、ビス(2,4−ジ−t−ブチルフェニル)ペンタエリスリトールジホスファイトなどのリン系酸化防止剤を配合することにより、酸化安定性を向上させることができる。
これら化合物の中では、TGA(熱重量分析)における5%重量減少で測定される分解温度が250℃以上となるものが好ましい。また、これら酸化防止剤の使用量は、本発明の環状オレフィン系開環共重合体100重量部に対して0.05〜5.0重量部であることが好ましい。
【0060】
本発明の環状オレフィン系開環共重合体において、構造単位(C)を有するものは、当該構造単位(C)における加水分解性シリル基またはオキセタニル基を架橋してなる架橋体とすることができる。
【0061】
構造単位(C)が加水分解性シリル基を有するものである場合において、当該共重合体の架橋方法としては、例えば、
(a)加水分解により酸を発生する化合物、または
(b)g線、h線、i線、等の紫外線、遠紫外線、X線、電子線等の活性光線の照射、あるいは熱により、強ブレンステッド酸、あるいはルイス酸を発生する化合物、
を共重合体に配合し、所定の操作により発生する酸によって起こる加水分解/縮合反応により、当該シリル基間を架橋する方法が挙げられる。
上記(a)の化合物の具体例としては、有機亜リン酸エステル化合物、有機スルフィン酸エステル、カルボン酸のt−ブチルエステル、カルボン酸のヘミアセタールエステルなどが挙げられる。
上記(b)の化合物としては、種々のジアゾニウム塩、アンモニウム塩、ヨードニウム塩、スルホニウム塩、ホスホニウム塩、アルソニウム塩、オキソニウム塩などのオニウム塩、ハロゲン含有オキサジアゾール化合物、ハロゲン含有トリアジン化合物、ハロゲン含有アセトフェノン化合物、ハロゲン含有ベンゾフェノン化合物などの特定のハロゲン化有機化合物、キノンジアジド化合物、α,α−ビス(スルホニル)ジアゾメタン化合物、α−カルボニル−α−スルホニル−ジアゾメタン化合物、スルホニル化合物、有機酸エステル化合物、有機酸アミド化合物、有機酸イミド化合物などが挙げられる。
【0062】
構造単位(C)がオキセタニル基を有するものである場合において、当該共重合体の架橋方法としては、例えば、
上記(b)の化合物を配合し、発生する酸によって起こるオキセタニル基の開環カチオン重合反応によって架橋する方法が挙げられる。上記(b)の化合物として、光により酸を発生する化合物を用いる場合には、室温で架橋可能であるため、より好ましい。
【0063】
上記(a)の化合物または上記(b)の化合物は、環状オレフィン系開環共重合体100重量部に対して0.05〜20重量部、好ましくは0.2〜10重量部となる割合で用いられる。
【0064】
本発明の環状オレフィン系開環共重合体においては、炭化水素溶媒あるいはハロゲン化炭化水素溶媒から選ばれた当該共重合体を溶解し得る溶媒に、当該共重合体を溶解させることにより、共重合体溶液を調製し、この共重合体溶液を、スチールベルトやポリエステルなどのキャリアーフィルムなどの上にキャスティングし、その後、乾燥処理する溶剤キャスト法(溶液流延法)によって、フィルム状あるいはシート状にて成形することができる。また、射出成形法、圧縮成型法、Tダイによる押出成形法などによって、ペレット状、フィルム状、シート状、またはその他の形状に成形することができる。
【0065】
本発明の環状オレフィン系開環共重合体は、その他の熱可塑性樹脂、例えば本発明の環状オレフィン系開環共重合体以外の環状オレフィン系(共)重合体(例えば環状オレフィン系付加重合体、水素化された開環重合体)や、芳香族環あるいは脂環式炭化水素構造を有する石油樹脂類、水素化されたスチレン系樹脂などとブレンドすることにより、透明性を保持しつつ、軟化温度、複屈折などが調節された樹脂組成物として得ることもできる。
【0066】
本発明の環状オレフィン系開環共重合体は、優れた光学透明性、耐熱性、接着・密着性、低吸水性、機械強度を有するため、導光板、偏光フィルム、表面保護フィルム、光拡散フィルム、位相差フィルム、透明導電性フィルム、反射防止フィルム、OHPフィルム、光ディスク、光ファイバー、レンズ、プリズムなどの光学部品や、光学部品のコーティング材などの光学材料として極めて有用であり、さらには半導体封止剤などの電子部品材料、コーティング剤、接着剤さらに医療機器、各種容器、バインダーなどとして有用である。
【0067】
【実施例】
以下、本発明の具体的な実施例について説明するが、本発明はこれらの実施例に限定されるものではない。また、以下の実施例において、重量平均分子量、数平均分子量、全光線透過率、ガラス転移温度、吸水率、接着・密着性、引張強度および伸びは下記の方法で測定した。
【0068】
(1)重量平均分子量および数平均分子量:
東ソ−(株)製のHタイプカラムが装着された、ウオターズ(WATERS)社製の150C型ゲルパーミエ−ションクロマトグラフィー(GPC)装置により、o−ジクロロベンゼンを溶媒として用い、120℃の条件で、試料の標準ポリスチレン換算の重量平均分子量および数平均分子量を測定した。
(2)全光線透過率:
ASTM−D1003に準拠し、厚みが120μmの試験片を作製し、その全光線透過率を測定した。
(3)ガラス転移温度:
動的粘弾性のTanδ(=貯蔵弾性率E’と損失弾性率E”との比E”/E’)のピーク温度により、試料のガラス転移温度を測定した。動的粘弾性の測定はレオバイブロンDDV−01FP(オリエンテック製)を用い、測定周波数が10Hz、昇温速度が4℃/分、加振モードが単一波形、加振振幅が2.5μmのものを用いて得られるTanδの温度分散のピーク温度で求めた。
(4)吸水率:
厚みが120μmの試験片を作製し、ASTM−D570に準拠し、この試験片を23℃の水中に24時間浸漬させた後、試験片の重量変化より吸水率を測定した。
(5)接着性・密着性:
10cm×10cmの試験片を作製し、この試験片にアルミニウムを蒸着し、形成された蒸着膜に、カッターナイフにより、縦方向および横方向にそれぞれ1mm間隔で碁盤目状に切り込みを入れることにより、互いに分離された1mm×1mmの寸法のブロックを100個(10個×10個)形成し、セロハンテープによって蒸着膜の剥離試験を行い、全ブロック(100個)中における剥離したブロックの数を測定した。
(6)引張強度および伸び
JIS K7113に準拠し、引張り速度3mm/分の条件で試験の引張強度および伸びを測定した。
【0069】
〈実施例1〉
300ミリリットルのガラス製耐圧ビン内に、窒素雰囲気下で、溶媒としてトルエン80ミリリットル、特定単量体(A)としてエンド体とエキソ体とのモル比が95:5であるトリシクロ[5.2.1.02,6 ]デカ−8−エン51ミリモル、特定単量体(B)として8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン119ミリモル、および分子量調節剤として1−ヘキセン42.5ミリモルを仕込み、さらに重合触媒としてトリエチルアルミニウム0.119ミリモルおよび六塩化タングステンのメタノール変性物[メタノール/タングステン=3(モル/モル)]0.017ミリモルをこの順で加えた。そして、80℃で2時間の条件で特定単量体(A)および特定単量体(B)の開環重合を行い、その後、メタノールによって重合反応を停止した。単量体の開環共重合体への転化率は97%であった。
次いで、得られた反応溶液に水660ミリリットルおよび乳酸47.5ミリモルを加えて攪拌した後、静置することにより、水相と反応溶液相とに分離した。その後、触媒成分の反応物を含む水相を除去し、反応溶液を3リットルのイソプロパノールに加えて生成物を凝固させて回収することにより、未反応の単量体を除去し、回収した生成物を、真空下に50℃で15時間乾燥処理することにより、環状オレフィン系開環共重合体を得た。得られた環状オレフィン系開環共重合体を「開環共重合体A」とする。
この開環共重合体Aのベンゼン−d6 中における270MHz、 1H−NMRスペクトルより、トリシクロ[5.2.1.02,6 ]デカ−8−エンに由来する構造単位(A)の割合が32モル%(21.5重量%)、8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エンに由来する構造単位(B)の割合が68モル%(78.5重量%)と定量された(メトキシカルボニル基に基づく3.2〜3.6ppmの吸収と、二重結合に隣接する水素に基づく5.4〜5.8ppmの吸収との比から算出した。)。開環共重合体Aの 1H−NMRスペクトルを図1に示し、赤外吸収スペクトルを図2に示す。
【0070】
500ミリリットルのステンレス製耐圧反応器中に、得られた開環共重合体A15gをトルエン200gに溶解させた溶液と、カルボニルクロロヒドリドトリス(トリフェニルホスフィン)ルテニウム[RuHCl(CO)(PPh3 )3 ]をルテニウム原子換算で70ppm加え、水素圧10MPa、165℃、4時間の条件で水素化反応を行った。得られた反応溶液を乳酸水溶液によって脱触媒処理した後、イソプロピルアルコールによって凝固させることにより、水素添加された環状オレフィン系開環共重合体を得た。得られた水素添加開環状オレフィン系開環共重合体を「開環共重合体AH」とする。
この開環共重合体AHの1H−NMRスペクトルを測定し、メトキシカルボニル基に基づく3.2〜3.6ppmの吸収ピークと、開環共重合体AHにおける水素化されずに残留した二重結合に隣接する水素に基づく5.4〜5.8ppmの吸収ピークとの相対比から水素化率を算出したところ、99.7%であった。開環共重合体AHの 1H−NMRスペクトル図を図3に示し、赤外吸収スペクトル図を図4に示す。また、開環共重合体AHのポリスチレン換算の数平均分子量(Mn)は20,000、重量平均分子量(Mw)は75,000、Mw/Mnは3.7であった。
【0071】
開環共重合体AH10gをテトラヒドロフラン35.5gに溶解し、得られた共重合体溶液に、酸化防止剤としてペンタエリスリチルテトラキス[3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネート]およびトリス(2,4−ジ−t−ブチルフェニル)ホスファイトを、開環共重合体AH100重量部に対してそれぞれ0.5重量部となる割合で添加した。この共重合体溶液を用い、溶剤キャスト法によって、厚みが120μmのフィルムを作製した。得られたフィルムの残留溶媒は0.5重量%であった。このフィルムから試験片を作製し、各物性の評価を行った。その結果を表1に示す。
【0072】
〈実施例2〉
特定単量体(A)としてエンド体とエキソ体とのモル比が95:5であるトリシクロ[5.2.1.02,6 ]デカ−8−エン75ミリモル、特定単量体(B)として8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン95ミリモルを用いたこと以外は、実施例1と同様にして環状オレフィン系開環共重合体を調製し(得られた環状オレフィン系開環共重合体を「開環共重合体B」とする。)、水素化された環状オレフィン系開環共重合体を調製した(得られた水素添加環状オレフィン系開環共重合体を「開環共重合体BH」とする。)。単量体の開環共重合体への転化率は90%であり、開環共重合体BHの水素化率は99.8%であった。開環共重合体BHの 1H−NMRスペクトル図を図5に示す。
また、開環共重合体Bにおけるトリシクロ[5.2.1.02,6 ]デカ−8−エンに由来する構造単位の割合は45モル%(32.3重量%)、8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エンに由来する構造単位の割合は55モル%(67.7重量%)であった。また、開環共重合体BHの数平均分子量(Mn)は73,000、重量平均分子量(Mw)は168,000、Mw/Mnは2.3であった。
また、開環共重合体BHについて、実施例1と同様にして試験片を作製し、各物性の評価を行った。その結果を表1に示す。
【0073】
〈実施例3〉
特定単量体(A)としてエンド体とエキソ体とのモル比が99:1であるトリシクロ[5.2.1.02,6 ]デカ−8−エンを用いたこと以外は、実施例1と同様して環状オレフィン系開環共重合体を調製し(得られた環状オレフィン系開環共重合体を「開環共重合体C」とする。)、水素化された環状オレフィン系開環共重合体を調製した(得られた水素添加環状オレフィン系開環共重合体を「開環共重合体CH」とする。)。単量体の開環共重合体への転化率は94%であり、開環共重合体CHの水素化率は99.7%であった。
また、開環共重合体Cにおけるトリシクロ[5.2.1.02,6 ]デカ−8−エンに由来する構造単位の割合は32モル%(21.5重量%)、8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エンに由来する構造単位の割合は68モル%(78.5重量%)であった。また、開環共重合体CHの数平均分子量(Mn)は74,000、重量平均分子量(Mw)は151,000、Mw/Mnは2.0であった。
また、開環共重合体CHについて、実施例1と同様にして試験片を作製し、各物性の評価を行った。その結果を表1に示す。
【0074】
〈実施例4〉
特定単量体(A)としてエンド体とエキソ体とのモル比が99:1であるトリシクロ[5.2.1.02,6 ]デカ−8−エン45ミリモル、特定単量体(B)として8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン100.5ミリモルを用いると共に、特定単量体(C)として5−トリエトキシシリルビシクロ[2.2.1]ヘプト−2−エン5ミリモルを用い、更に、水素添加反応における処理温度を125℃に変更したこと以外は、実施例1と同様にして環状オレフィン系開環共重合体を調製し(得られた環状オレフィン系開環共重合体を「開環共重合体D」とする。)、水素化された環状オレフィン系開環共重合体を調製した(得られた水素添加環状オレフィン系開環共重合体を「開環共重合体DH」とする。)。単量体の開環共重合体への転化率は93%であり、開環共重合体DHの水素化率は99.7%であった。開環共重合体DHの 1H−NMRスペクトル図を図6に示す。
また、開環共重合体Dにおけるトリシクロ[5.2.1.02,6 ]デカ−8−エンに由来する構造単位の割合は32モル%(21.3重量%)、8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エンに由来する構造単位の割合は65モル%(74.9重量%)、5−トリエトキシシリルビシクロ[2.2.1]ヘプト−2−エンに由来の構造単位の割合は3モル%(3.8重量%)であった。
また、開環共重合体DHの数平均分子量(Mn)は69,000、重量平均分子量(Mw)は162,000、Mw/Mnは2.3であった。
【0075】
開環共重合体DH10gをテトラヒドロフラン35.5gに溶解し、得られた共重合体溶液に、酸化防止剤としてペンタエリスリチルテトラキス[3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネート]およびトリス(2,4−ジ−t−ブチルフェニル)ホスファイトを、開環共重合体DH100重量部に対してそれぞれ0.5重量部となる割合で添加し、さらに架橋剤の亜リン酸ジブチルを開環共重合体DH100重量部に対して0.7重量部となる割合で添加した。この共重合体溶液を用い、溶剤キャスト法によって、厚みが120μmのフィルムを作製し、このフィルムに対して120℃の水蒸気を2時間接触させることにより、架橋処理を行った。架橋処理されたフィルムから試験片を作製し、各物性の評価を行った。その結果を表1に示す。
また、上記架橋処理されたフィルムから作製した試験片を、開環共重合体DHに対して良溶媒であるテトラヒドロフラン、トルエンおよび塩化メチレンに浸漬したところ、当該試験片はこれらの溶媒に対して不溶であり、架橋によって耐溶剤性が向上したことが確認された。
【0076】
〈実施例5〉
特定単量体(A)としてエンド体とエキソ体とのモル比が95:5であるトリシクロ[5.2.1.02,6 ]デカ−8−エン105ミリモル、特定単量体(B)として8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エン65ミリモルを用いたこと以外は、実施例1と同様にして環状オレフィン系開環共重合体を調製し(得られた環状オレフィン系開環共重合体を「開環共重合体E」とする。)、水素化された環状オレフィン系開環共重合体を調製した(得られた水素添加環状オレフィン系開環共重合体を「開環共重合体EH」とする。)。単量体の開環共重合体への転化率は88%であり、開環共重合体EHの水素化率は99.8%であった。開環共重合体EHの 1H−NMRスペクトル図を図7に示す。
また、開環共重合体Eにおけるトリシクロ[5.2.1.02,6 ]デカ−8−エンに由来する構造単位の割合は62モル%(48.5重量%)、8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エンに由来する構造単位の割合は38モル%(51.5重量%)であった。また、開環共重合体EHの数平均分子量(Mn)は69,000、重量平均分子量(Mw)は158,000、Mw/Mnは2.3であった。
また、開環共重合体EHについて、実施例1と同様にして試験片を作製し、各物性の評価を行った。その結果を表1に示す。
【0077】
〈比較例1〉
開環重合に供される単量体として、8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エンのみを170ミリモルを用いたこと以外は、実施例1と同様して環状オレフィン系開環重合体を調製し(得られた環状オレフィン系開環重合体を「開環重合体F」とする。)、水素化された環状オレフィン系開環重合体を調製した(得られた水素添加環状オレフィン系開環重合体を「開環重合体FH」とする。)。単量体の開環重合体への転化率は100%であり、開環重合体FHの水素化率は99.8%であった。
また、開環重合体FHの数平均分子量(Mn)は20,000、重量平均分子量(Mw)は73,000、Mw/Mnは3.7であった。
また、開環重合体FHについて、実施例1と同様にして試験片を作製し、各物性の評価を行った。その結果を表1に示す。
【0078】
〈比較例2〉
エンド体とエキソ体とのモル比が95:5であるトリシクロ[5.2.1.02,6 ]デカ−8−エンの代わりにエンド体とエキソ体とのモル比が10:90であるトリシクロ[5.2.1.02,6 ]デカ−8−エンを用いたこと以外は、実施例1と同様して環状オレフィン系開環共重合体を調製し(得られた環状オレフィン系開環共重合体を「開環共重合体G」とする。)、水素化された環状オレフィン系開環共重合体を調製した(得られた水素添加環状オレフィン系開環重合体を「開環共重合体GH」とする。)。単量体の開環共重合体への転化率は98%であり、開環共重合体GHの水素化率は99.8%であった。
また、開環共重合体GHの数平均分子量(Mn)は75,000、重量平均分子量(Mw)は165,000、Mw/Mnは2.2であった。
また、開環共重合体GHについて、実施例1と同様にして試験片を作製し、各物性の評価を行った。その結果を表1に示す。
【0079】
〈比較例3〉
8−メチル−8−メトキシカルボニルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エンの代わりに8−エチルテトラシクロ[4.4.0.12,5 .17,10]ドデカ−3−エンを用いたこと以外は、実施例1と同様して環状オレフィン系開環共重合体を調製し(得られた環状オレフィン系開環共重合体を「開環共重合体H」とする。)、水素化された環状オレフィン系開環共重合体を調製した(得られた水素添加環状オレフィン系開環共重合体を「開環共重合体HH」とする。)。単量体の開環共重合体への転化率は99%であり、開環共重合体HHの水素化率は99.8%であった。
また、開環共重合体HHの数平均分子量(Mn)は21,000、重量平均分子量(Mw)は69,000、Mw/Mnは3.3であった。
また、開環共重合体HHについて、テトラヒドロフランの代わりにシクロヘキサンを用いたこと以外は実施例1と同様にして試験片を作製し、各物性の評価を行った。その結果を表1に示す。
【0080】
【表1】
【0081】
表1から明らかなように、実施例1〜実施例5に係る環状オレフィン系開環共重合体(開環共重合体AH〜開環共重合体EH)は、全光線透過率が高く、ガラス転移温度が高く、吸水率が低く、金属に対する密着性または接着性が高く、機械的強度が高いものであることが確認された。
これに対して、比較例1に係る環状オレフィン系開環重合体(開環重合体FH)は、実施例に係る開環共重合体に比較して吸水率が高く、強度が低いものであり、比較例2に係る環状オレフィン系開環共重合体(開環共重合体GH)は、実施例に係る開環共重合体に比較して強度が低いものであり、比較例3に係る環状オレフィン系開環共重合体(開環共重合体HH)は、実施例に係る開環共重合体に比較して密着性・接着性が低いものであった。
【0082】
【発明の効果】
本発明の環状オレフィン系開環共重合体は、エンド体の割合が80%以上である特定のトリシクロモノオレフィン類に由来する構造単位と、エステル基を有する特定のテトラシクロドデセン類に由来する構造単位とを含有してなるため、透明性等の光学特性に優れ、吸水(湿)性が低く、他素材との親和性が高くて接着性や印刷性等の後加工性が良好であり、しかも、優れた耐熱性および機械的強度を有するものである。
本発明の製造方法によれば、上記の環状オレフィン系開環共重合体を有利に製造することができる。
本発明の環状オレフィン系開環共重合体は、このような特性を有するため、光学部品や、光学部品のコーティング材などの光学材料として極めて有用であり、さらには半導体封止剤などの電子部品材料、コーティング剤、接着剤さらに医療機器、各種容器、バインダーなどとして有用である。
【図面の簡単な説明】
【図1】実施例1で得られた開環共重合体Aの 1H−NMRスペクトル図である。
【図2】実施例1で得られた開環共重合体Aの赤外吸収スペクトル図である。
【図3】実施例1で得られた開環共重合体AHの 1H−NMRスペクトル図である。
【図4】実施例1で得られた開環共重合体AHの赤外吸収スペクトル図である。
【図5】実施例2で得られた開環共重合体BHの 1H−NMRスペクトル図である。
【図6】実施例4で得られた開環共重合体DHの 1H−NMRスペクトル図である。
【図7】実施例5で得られた開環共重合体EHの 1H−NMRスペクトル図である。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a cyclic olefin-based ring-opening copolymer, a method for producing the same, and an optical material, and more specifically, excellent optical properties such as transparency, high affinity with other materials, adhesiveness, printability, etc. Cyclic olefin ring-opening copolymer having good post-processability, excellent balance between affinity with other materials and low water absorption (humidity), excellent heat resistance and mechanical strength, and method for producing the same And an optical material.
[0002]
[Prior art]
In recent years, with the demand for weight reduction, miniaturization and high density of electronic devices, in the field of optical parts and liquid crystal display element parts such as lenses, backlights, light guide plates, liquid crystal substrates, etc., which conventionally used inorganic glass Substitutions from inorganic glass to optically transparent resins are underway. In addition, a transparent resin is often used in the form of a sheet, a film, or a thin film.
Conventionally, polyacrylate, polycarbonate, and the like have been widely used as transparent resins for optical materials. However, in the transparent resin for substituting inorganic glass, in addition to transparency, improvement in characteristics such as heat resistance, moisture absorption resistance, adhesion / adhesion, and breaking strength is required.
In order to meet such demands, cyclic olefin polymers have begun to be used as optical materials.
[0003]
For example, as a cyclic olefin polymer excellent in transparency and heat resistance, an addition polymer of a cyclic olefin compound represented by bicyclo [2.2.1] hept-2-ene (norbornene) has been proposed ( (For example, see
However, these cyclic olefin based addition polymers exhibit a glass transition temperature exceeding 300 ° C. and therefore have very high heat resistance, but on the other hand, it is difficult to perform hot melt molding such as injection molding and extrusion molding. There is a problem such as.
[0004]
Further, as a polymer of a cyclic olefin compound, an addition copolymer of a cyclic olefin compound and an acyclic olefin compound such as ethylene is known (for example,
However, since these catalyst systems show little polymerization ability for monomers containing polar groups such as ester groups and alkoxysilyl groups, functions such as adhesion can be imparted to the resulting copolymer. It is difficult to introduce a crosslinking group such as a hydrolyzable silyl group. Furthermore, the cyclic olefin-based addition copolymer may become low in transparency due to crystallization of an ethylene chain and is not necessarily suitable for use as an optical material.
[0005]
In addition, as a cyclic olefin polymer useful as an optical material for producing a lens, an optical disk, or the like, a ring-opening (co) polymer of a cyclic olefin compound or a hydrogenated product thereof has been proposed (for example, patents). (Ref. Literature 7, Patent Literature 8,
And in order to solve such a problem, what introduce | transduced the polar group in the molecule | numerator is proposed as a cyclic olefin type ring-opening (co) polymer or its hydrogenated substance (for example,
[0006]
On the other hand, dicyclopentadiene (also known as: tricyclo [5.2.1.0 2,6 Deca-3,8-diene) is a compound that is widely used industrially as a starting material in the synthesis of monomers for obtaining the above cyclic olefin polymers.
However, when dicyclopentadiene (hereinafter also referred to as “DCP”) itself is used as a monomer for obtaining a cyclic olefin polymer, DCP has 2 olefinic double bonds in its molecule. In order to produce a polymer having a gel-like substance or a branch because it has an individual, when DCP is used as a raw material for industrial production of a cyclic olefin polymer, the production of the cyclic olefin polymer There is a problem that may cause trouble.
Therefore, in order to solve the problem caused by the presence of a plurality of olefinic double bonds, tricyclo [5. 2.1.0 2,6 A ring-opening (co) polymer obtained by ring-opening (co) polymerization of deca-3-ene and a hydrogenated product thereof have been proposed (for example, see Patent Document 15).
However, such ring-opening (co) polymers are tricyclo [5.2.1.0]. 2,6 Since the 5-membered ring in deca-3-ene is opened, and the hydrogenated product contains three chains of methylene groups in the structural unit, only those having a relatively low glass transition temperature can be obtained. There is a problem.
[0007]
DCP has two stereoisomers, an exo form and an endo form, and the glass transition temperature of each hydrogenated product of the ring-opening polymer is 97 ° C., respectively. Since it is 66 ° C. and lower than 100 ° C., it is difficult to use it for a material that requires heat resistance (see, for example, Non-Patent Document 2). Furthermore, a hydrogenated product of a ring-opening (co) polymer in which the proportion of structural units derived from DCP is 70% by weight or more, and a proportion in which the proportion of endo-forms in the DCP used is 50% or more is proposed. According to the hydrogenated product of such a ring-opening (co) polymer, it is said that there is an effect of improving mechanical strength such as impact resistance (see, for example, Patent Document 16). However, the glass transition temperatures of these ring-opening (co) polymers are all 120 ° C. or lower, and do not have satisfactory performance as materials requiring high heat resistance.
[0008]
[Patent Document 1]
JP-A-4-63807
[Patent Document 2]
JP-A-8-198919
[Patent Document 3]
Japanese National Patent Publication No. 9-508649
[Patent Document 4]
Japanese National Patent Publication No. 11-505880
[Patent Document 5]
JP 61-292601 A
[Patent Document 6]
US Pat. No. 2,883,372
[Patent Document 7]
Japanese Unexamined Patent Publication No. 63-21878
[Patent Document 8]
JP-A-1-138257
[Patent Document 9]
JP-A-1-168725
[Patent Document 10]
Japanese Patent Laid-Open No. 2-102221
[Patent Document 11]
JP-A-2-133413
[Patent Document 12]
Japanese Patent Laid-Open No. 4-170425
[Patent Document 13]
JP 50-111200 A
[Patent Document 14]
JP-A-1-132626
[Patent Document 15]
Japanese Patent Laid-Open No. 7-19679
[Patent Document 16]
JP-A-11-130846
[Non-Patent Document 1]
“Macromolecular Hemmy, Macromolecular Symposia” (Switzerland), Hutig and Wepff Fairlark, Basel (Hutig & Wepf Ver. 91, B. B. 91 p. 83
[Non-Patent Document 2]
“Polymer Journal” (Japan), Polymer Society of Japan, December 1995, Vol. 27, No. 12, p. 1167
[0009]
[Problems to be solved by the invention]
The present invention has been made on the basis of the circumstances as described above, and its first object is excellent in optical properties such as transparency, high affinity with other materials, adhesiveness, printability, etc. Providing a cyclic olefin ring-opening copolymer with good post-processability, excellent balance between affinity with other materials and low water absorption (wet), and excellent heat resistance and mechanical strength There is to do.
The second object of the present invention is to provide a method capable of advantageously producing the above cyclic olefin ring-opening copolymer.
The third object of the present invention is to provide an optical material comprising the above cyclic olefin-based ring-opening copolymer.
[0010]
[Means for Solving the Problems]
The cyclic olefin-based ring-opening copolymer of the present invention includes a structural unit (A) represented by the following general formula (1-1), the following general formula (1-2) or the following general formula (1-3); Cyclic olefin-based ring-opening copolymer or hydrogenated cyclic containing the structural unit (B) represented by the following general formula (2) in a molar ratio of 10:90 to 70:30 The monomer for obtaining the structural unit (A), which is an olefin-based ring-opening copolymer, has an end-body ratio of 80 mol% or more, and has a glass transition temperature of 120 to 250 ° C. It is characterized by that.
[0011]
[Chemical formula 5]
[0012]
[In General Formula (1-1) to General Formula (1-3), R 1 ~ R 13 Each independently represents a hydrogen atom, a halogen atom, or a group selected from an alkyl group having 1 to 4 carbon atoms and a halogenated alkyl group; 1 ~ X 3 Represents an ethylene group or a vinylene group. ]
[0013]
[Chemical 6]
[0014]
[In General Formula (2), m is 1 or 2, and X 4 Represents an ethylene group or vinylene group, R 14 ~ R 17 Each independently represents a hydrogen atom, a halogen atom, an alkyl group having 1 to 20 carbon atoms, a cycloalkyl group, an aryl group, an alkenyl group, a halogenated hydrocarbon group, R 14 Or R 15 And R 16 Or R 17 And an alkylene group formed by bonding with-(CH 2 ) k A group represented by Z, or R 14 Or R 15 And R 16 Or R 17 -(CH 2 ) k -C (O) O- represents a group represented by R 14 ~ R 17 At least one of which is-(CH 2 ) k A group represented by Z or-(CH 2 ) k It is a group represented by —C (O) O—. Here, k is an integer of 0 to 3, and Z is —C (O) O—R. 18 Or -OC (O) -R 19 R represents a group represented by R 18 And R 19 Represents a hydrocarbon group having 1 to 10 carbon atoms or a halogenated hydrocarbon group. ]
[0015]
In the cyclic olefin ring-opening copolymer of the present invention, the structural unit (A) represented by the general formula (1-1), the general formula (1-2) or the general formula (1-3) is used. The monomer for obtaining consists of the tricyclomonoolefin compound represented by the following general formula (3-1), the following general formula (3-2), or the following general formula (3-3), It is preferable that the ratio of the endo form in an olefin compound is 80 mol% or more.
[0016]
[Chemical 7]
[0017]
[In General Formula (3-1) to General Formula (3-3), R 1 ~ R 13 Each independently represents a hydrogen atom, a halogen atom, or a group selected from an alkyl group having 1 to 4 carbon atoms and a halogenated alkyl group. ]
[0018]
Further, in the cyclic olefin ring-opening copolymer of the present invention, the structural unit (C) derived from the cyclic olefin compound having a hydrolyzable silyl group or oxetanyl group in the side chain is 0.1 to 0.1 of all structural units. You may contain in the ratio used as 30 mol%.
Moreover, in the cyclic olefin type ring-opening copolymer of the present invention, it may be cross-linked by the hydrolyzable silyl group or oxetanyl group.
In the cyclic olefin ring-opening copolymer of the present invention, at least a part of the structural unit (A) is tricyclo [5.2.1.0]. 2,6 It is preferably a structural unit derived from deca-8-ene.
[0019]
The production method of the cyclic olefin ring-opening copolymer of the present invention is a tricyclomonoolefin represented by the general formula (3-1), the general formula (3-2) or the general formula (3-3). A monomer composed of a compound and having a proportion of an endo form in the tricyclomonoolefin compound of 80 mol% or more and a monomer represented by the following general formula (4) are 10:90 to 70 in terms of mole. : It has the process of carrying out the ring-opening copolymerization process of the monomer composition formed by the ratio used as 30.
[0020]
[Chemical 8]
[0021]
[In General Formula (4), m is 1 or 2, and R 14 ~ R 17 Each independently represents a hydrogen atom, a halogen atom, an alkyl group having 1 to 20 carbon atoms, a cycloalkyl group, an aryl group, an alkenyl group, a halogenated hydrocarbon group, R 14 Or R 15 And R 16 Or R 17 And an alkylene group formed by bonding with-(CH 2 ) k A group represented by Z, or R 14 Or R 15 And R 16 Or R 17 -(CH 2 ) k -C (O) O- represents a group represented by R 14 ~ R 17 At least one of which is-(CH 2 ) k A group represented by Z or-(CH 2 ) k It is a group represented by —C (O) O—. Here, k is an integer of 0 to 3, and Z is —C (O) O—R. 18 Or -OC (O) -R 19 R represents a group represented by R 18 And R 19 Represents a hydrocarbon group having 1 to 10 carbon atoms or a halogenated hydrocarbon group. ]
[0022]
In the method for producing a cyclic olefin-based ring-opening copolymer of the present invention, it is preferable to hydrogenate the monomer composition after the ring-opening copolymerization treatment.
[0023]
The optical material of the present invention is characterized by containing the above cyclic olefin ring-opening copolymer.
[0024]
DETAILED DESCRIPTION OF THE INVENTION
Hereinafter, embodiments of the present invention will be described in detail.
The cyclic olefin ring-opening copolymer of the present invention is a structural unit (A) represented by the general formula (1-1), the general formula (1-2) or the general formula (1-3) , Also simply “structural unit (A)”) and the structural unit (B) represented by the general formula (2) (hereinafter also simply referred to as “structural unit (B)”). is there.
[0025]
As the monomer for obtaining the structural unit (A) in the cyclic olefin ring-opening copolymer of the present invention, the above general formula (3-1), the above general formula (3-2) or the above general formula (3) -3), and the ratio of the endo form in the tricyclomonoolefin compound is 80 mol% or more (hereinafter referred to as “specific monomer (A)”). Preferably used.
As such a specific monomer (A), those synthesized by appropriately using known methods can be used, and the synthesis method is not particularly limited, but in general, cyclopentadiene ( Hereinafter, also referred to as “CPD”) or DCP and a Diels-Alder reaction of monocyclic monoolefins selected according to the target specific monomer (A), for example, cyclopentene or cyclohexene. The synthesis method is used.
Such Diels-Alder reaction is preferably carried out in an atmosphere of an inert gas such as nitrogen or argon, and a reaction solvent may not be used unless particularly required. The higher the reaction temperature, the higher the reaction rate, but the selectivity for endo-form formation often decreases. From this point of view, it is usually within the range of 150 to 250 ° C, preferably 170 to 230 ° C. Will be implemented.
[0026]
CPD or DCP to be subjected to the reaction and the monocyclic monoolefin can be used in an arbitrary ratio, but from the viewpoint of the selectivity of endo-form formation, the monocyclic monoolefin is 3 to 3 with respect to CPD or DCP. It is preferable to use an excess of 50 equivalents. In addition, as a method for adding the reaction raw material, a method in which all of the reaction raw material is supplied to the reaction system at once, at least one of CPD or DCP and a monocyclic monoolefin is divided into two or more times and supplied to the reaction system Any of the method, CPD or DCP, and a method of continuously supplying at least one of monocyclic monoolefins to the reaction system may be used.
The product thus obtained is separated and purified by a known method such as distillation, and then provided as a specific monomer (A) for obtaining the cyclic olefin ring-opening copolymer of the present invention. .
[0027]
In the specific monomer (A), the proportion of the endo form needs to be 80 mol% or more, preferably 90 mol% or more, more preferably 95 mol% or more. When the proportion of the endo isomer in the specific monomer (A) is less than 80 mol%, the mechanical strength of the obtained ring-opening copolymer hydride becomes insufficient.
Here, the ratio of the endo isomer and the exo isomer in the specific monomer (A) can be measured by gas chromatography analysis.
[0028]
As a specific example of the specific monomer (A),
Tricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3-methyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
4-methyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3,4-dimethyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3,5-dimethyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3,4,5-trimethyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3-ethyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
4-ethyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3,4-diethyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3,5-diethyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3-methyl-5-ethyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3-Isopropyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
4-Isopropyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3,4-diisopropyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3,5-diisopropyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3-Methyl-5-isopropyltricyclo [5.2.1.0 2,6 ] Dec-8-ene,
3-chlorotricyclo [5.2.1.0 2,6 ] Dec-8-ene,
Tricyclo [5.2.1.0 2,6 ] Decenes,
[0029]
Tricyclo [6.2.1.0 2,7 ] Undec-3-ene,
3-methyltricyclo [6.2.1.0 2,7 ] Undec-3-ene,
4-methyltricyclo [6.2.1.0 2,7 ] Undec-3-ene,
3,4-dimethyltricyclo [6.2.1.0 2,7 ] Undec-3-ene,
3,5-dimethyltricyclo [6.2.1.0 2,7 ] Undec-3-ene,
3,4,5,6-tetramethyltricyclo [6.2.1.0 2,7 ] Undec-3-ene,
3-ethyltricyclo [6.2.1.0 2,7 ] Undec-3-ene,
4-ethyltricyclo [6.2.1.0 2,7 ] Undec-3-ene,
Such as tricyclo [6.2.1.0 2,7 ] Undecenes,
[0030]
Tricyclo [8.2.1.0 2,9 ] Trideca-11-ene,
3-methyltricyclo [8.2.1.0 2,9 ] Trideca-11-ene,
4-methyltricyclo [8.2.1.0 2,9 ] Trideca-11-ene,
5-methyltricyclo [8.2.1.0 2,9 ] Trideca-11-ene,
Tricyclo [8.2.1.0 2,9 ] Tridecenes
However, it is not limited to these.
These compounds can be used as the specific monomer (A) singly or in combination of two or more.
[0031]
Among these, tricyclo [5.2.1.0 2,6 ] Dec-8-ene, tricyclo [6.2.1.0 2,7 ] Undec-3-ene, tricyclo [8.2.1.0] 2,9 ] Tridec-11-ene is preferred, especially tricyclo [5.2.1.0]. 2,6 Deca-8-ene is preferably used because it is easily available.
[0032]
As described above, the structural unit (A) in the cyclic olefin-based ring-opening copolymer of the present invention can be obtained by a method of ring-opening copolymerization of the specific monomer (A). As a method, for example, tricyclo [5.2.1.0 2,6 It can also be obtained by ring-opening copolymerization of tricyclodiolefins such as deca-3,8-diene (dicyclopentadiene) and then hydrogenating the side chain cyclic olefinic unsaturated bonds. When such a method is applied, the side chain cyclic olefinically unsaturated bond may react during ring-opening polymerization to produce a gel-like or branched polymer. It is preferable to adjust the polymerization conditions as appropriate so as not to occur.
[0033]
In the present invention, a monomer represented by the general formula (4) (hereinafter referred to as “specific monomer (B)”) is used as a monomer for obtaining the structural unit (B). .
[0034]
As a specific example of the specific monomer (B),
8-Methoxycarbonyltetracyclo [4.4.0.1 2,5 . 1 7, 10 ] Dodec-3-ene,
8-Methyl-8-methoxycarbonyltetracyclo [4.4.0.1 2,5 . 1 7, 10 ] Dodec-3-ene,
8-Methyl-8-ethoxycarbonyltetracyclo [4.4.0.1 2,5 . 1 7, 10 ] Dodec-3-ene,
8-Methyl-8-butoxycarbonyltetracyclo [4.4.0.1 2,5 . 1 7, 10 ] Dodec-3-ene,
8-Methyl-8-cyclohexyloxycarbonyltetracyclo [4.4.0.1 2,5 . 1 7, 10 ] Dodec-3-ene,
8-trifluoroethyloxycarbonyltetracyclo [4.4.0.1 2,5 . 1 7, 10 ] Dodec-3-ene,
8-acetoxyoxytetracyclo [4.4.0.1 2,5 . 1 7, 10 ] Dodec-3-ene,
8-Methyl-8-acetoxyoxytetracyclo [4.4.0.1 2,5 . 1 7, 10 ] Dodec-3-ene,
11-methyl-11-methoxycarbonylhexacyclo [6.6.1.1 3, 5 . 0 2,7 . 0 9,14 . 1 10, 13 ] Heptadeca-4-ene,
11-methoxycarbonylhexacyclo [6.6.1.1 3, 6 . 0 2,7 . 0 9,14 . 1 10, 13 ] Heptadeca-4-ene,
However, it is not limited to these.
These compounds can be used as a specific monomer (B) individually by 1 type or in combination of 2 or more types.
Among these, tetracyclododecenes in which m is 1 are preferable, and 8-methoxycarbonyl-tetracyclo [4.4.0.1]. 2,5 . 1 7, 10 ] Dodec-3-ene, 8-methyl-8-methoxycarbonyltetracyclo [4.4.0.1] 2,5 . 1 7, 10 ] Dodec-3-ene is more preferred.
[0035]
The ratio of the structural unit (A) and the structural unit (B) in the cyclic olefin-based ring-opening copolymer of the present invention is such that the structural unit (A): the structural unit (B) is 10:90 to 70:30 in terms of mole. , Preferably 20:80 to 65:35, which is suitable for an optical material having a good balance between adhesiveness or adhesion and low water absorption (humidity) and excellent heat resistance and mechanical strength. A cyclic olefin-based ring-opening copolymer is obtained.
When the proportion of the structural unit (A) is too small, the cyclic olefin ring-opening copolymer may have a low mechanical strength. On the other hand, when the proportion of the structural unit (A) is excessive, the cyclic olefin-based ring-opening copolymer has low adhesiveness or adhesiveness and low glass transition temperature. The heat resistance may be low.
[0036]
In the cyclic olefin ring-opening copolymer of the present invention, the total ratio of the structural unit (A) and the structural unit (B) in all the structural units is preferably 50 mol% or more, more preferably 70. It is more than mol%, more preferably more than 80 mol%. When the total proportion of the structural unit (A) and the structural unit (B) is less than 50 mol%, the heat characteristics, optical properties such as transparency and birefringence, water absorption (humidity), and other materials Regarding characteristics such as affinity, it becomes difficult to obtain a good balance, and any of the characteristics may become unsuitable for practical use.
[0037]
In the cyclic olefin ring-opening copolymer of the present invention, in addition to the structural unit (A) and the structural unit (B), a cyclic olefin compound having a hydrolyzable silyl group or oxetanyl group in the side chain ( Hereinafter, the structural unit (C) derived from “specific monomer (C)”) can be contained. Here, examples of the hydrolyzable silyl group include groups represented by the following general formula (5-1) or the following general formula (5-2).
[0038]
[Chemical 9]
[0039]
[In General Formula (5-1) and General Formula (5-2), R 20 And R 21 Each independently represents a hydrogen atom or a hydrocarbon group having 1 to 20 carbon atoms; 22 ~ R 25 Each independently represents a substituent selected from an alkyl group having 1 to 10 carbon atoms, an aryl group, an alkoxy group, an allyloxy group and a halogen atom, and n represents an integer of 0 to 5. Y represents a hydrocarbon residue of an aliphatic diol, alicyclic diol or aromatic diol having 2 to 20 carbon atoms. ]
[0040]
The cyclic olefin ring-opening copolymer containing such a structural unit (C) includes a photoacid generator, a thermal acid generator, a compound that generates an organic acid or an inorganic acid by hydrolysis, tin, aluminum, A side chain hydrolyzable silyl group or oxetanyl group can be cross-linked by a salt of a metal such as zirconium or titanium with an organic acid or a β-diketone, or an alkoxide or phenoxide of these metals. A cyclic olefin-based ring-opening copolymer having improved chemical resistance, solvent resistance, heat resistance and mechanical strength can be obtained.
[0041]
Specific examples of the specific monomer (C) include the following compounds, but the present invention is not limited thereto.
As a specific example of a cyclic olefin compound having a hydrolyzable silyl group,
5-trimethoxysilylbicyclo [2.2.1] hept-2-ene,
5-triethoxysilylbicyclo [2.2.1] hept-2-ene,
5-methyldimethoxysilylbicyclo [2.2.1] hept-2-ene,
5-methyldiethoxysilylbicyclo [2.2.1] hept-2-ene,
5-trichlorosilylbicyclo [2.2.1] hept-2-ene,
5-methyldichlorosilylbicyclo [2.2.1] hept-2-ene,
5- [1 ′, 4 ′, 4′-trimethyl-2 ′, 6′-dioxa-1′-silacyclohexyl] bicyclo [2.2.1] hept-2-ene,
8-triethoxysilyl-tetracyclo [4.4.0.1 2,5 . 1 7, 10 ] Dodec-3-ene,
8-Methyldiethoxysilyl-tetracyclo [4.4.0.1 2,5 . 1 7, 10 And dodeca-3-ene.
[0042]
As a specific example of the cyclic olefin compound having an oxetanyl group,
2-[(3-oxetanyl) methoxy] bicyclo [2.2.1] hept-5-ene,
2-[(3-ethyl-3-oxetanyl) methoxy] bicyclo [2.2.1] hept-2-ene,
2-[(3-oxetanyl) methoxymethyl] bicyclo [2.2.1] hept-5-ene,
2-[(3-ethyl-3-oxetanyl) methoxymethyl] bicyclo [2.2.1] hept-2-ene,
8-[(3-Ethyl-3-oxetanyl) methoxymethyl] tetracyclo [4.4.0.1 2,5 . 1 7, 10 ] Dodec-3-ene,
Bicyclo [2.2.1] hept-5-ene-2-carboxylic acid (3-ethyl-3-oxetanyl) methyl,
And 2-methylbicyclo [2.2.1] hept-5-ene-2-carboxylic acid (3-ethyl-3-oxetanyl) methyl.
These compounds can be used as the specific monomer (C) alone or in combination of two or more.
[0043]
In the cyclic olefin ring-opening copolymer of the present invention, when the structural unit (C) is contained, the proportion thereof is preferably 0.1 to 30 mol% of the total structural units, more preferably 1 to 20 mol%. When this proportion is less than 0.1 mol%, crosslinking is not sufficiently performed, and thus the obtained cyclic olefin-based ring-opening copolymer has improved solvent resistance, chemical resistance, and mechanical strength. It will be insufficient. On the other hand, when this ratio exceeds 30 mol%, the water absorption of the obtained cyclic olefin-based ring-opening copolymer increases, and the toughness when formed into a molded product may be lowered.
[0044]
In addition, in the cyclic olefin-based ring-opening copolymer of the present invention, in addition to the structural unit (A), the structural unit (B) and the structural unit (C) introduced as necessary, other than these structural units A structural unit (D) derived from a norbornene-based compound (hereinafter referred to as “specific monomer (D)”) can be contained in a proportion of 30 mol% or less of all structural units.
Specific examples of the specific monomer (D) include bicyclo [2.2.1] hept-2-ene (norbornene), 5-methylbicyclo [2.2.1] hept-2-ene and 5-hexyl. Alkyl-substituted norbornene such as bicyclo [2.2.1] hept-2-ene, halogenated alkyl-substituted norbornene such as 5-trifluoromethylbicyclo [2.2.1] hept-2-ene, 5-phenylbicyclo [ 2.2.1] aryl-substituted norbornene such as hept-2-ene, aralkyl-substituted norbornene such as 5-phenylmethylbicyclo [2.2.1] hept-2-ene, tetracyclo [4.4.0.1 2,5 . 1 7, 10 ] Dodec-3-ene, 8-ethyltetracyclo [4.4.0.1] 2,5 . 1 7, 10 And tetracyclododecenes such as dodec-3-ene. By copolymerizing such a compound, the glass transition temperature and processability of the resulting cyclic olefin-based ring-opening copolymer can be adjusted, or flexibility can be imparted.
[0045]
The glass transition temperature of the cyclic olefin ring-opening copolymer of the present invention is 120 to 250 ° C, preferably 120 to 180 ° C, more preferably 130 to 170 ° C. When the glass transition temperature is less than 120 ° C., the heat resistance of the cyclic olefin ring-opening copolymer is low. On the other hand, when the glass transition temperature exceeds 250 ° C., the cyclic olefin ring-opening copolymer is low. Copolymers not only have low processability in hot melt molding such as injection molding and extrusion molding, but also require high molding temperatures in hot melt molding, so cyclic olefin ring-opening copolymers are It is not preferable because it easily deteriorates by heat and the resulting molded product may become brittle or colored.
[0046]
The cyclic olefin-based ring-opening copolymer of the present invention has a polystyrene-equivalent number average molecular weight (Mn) measured by gel permeation chromatography at 120 ° C., preferably 5,000 to 300,000, more preferably. Is 10,000 to 100,000, particularly preferably 20,000 to 70,000, and the same weight average molecular weight (Mw) is preferably 20,000 to 700,000, more preferably 40,000 to 400, 000, particularly preferably 50,000 to 200,000.
When the number average molecular weight is less than 5,000 or the weight average molecular weight is less than 20,000, when the cyclic olefin-based ring-opening copolymer is used as a film, thin film or sheet, its destruction In many cases, the strength and elongation are small, and it is easy to break. On the other hand, when the number average molecular weight exceeds 300,000 or the weight average molecular weight exceeds 700,000, the cyclic olefin-based ring-opening copolymer has a high melt viscosity and solution viscosity. Since handling may become difficult, it is not preferable.
Here, the molecular weight of the cyclic olefin-based ring-opening copolymer can be adjusted by changing the amount of the polymerization catalyst, the addition amount of the molecular weight regulator, the conversion rate to the copolymer, and the polymerization temperature.
[0047]
The cyclic olefin ring-opening copolymer of the present invention comprises a specific monomer (A), a specific monomer (B), a specific monomer (C) and / or a specific monomer used as necessary. Hydrogenating the product obtained by subjecting the monomer composition containing the product (D) to ring-opening copolymerization treatment or after subjecting the monomer composition to ring-opening copolymerization treatment Manufactured by.
Here, the ratio of the specific monomer (A) and the specific monomer (B) in the monomer composition is 10: specific monomer (A): specific monomer (B) in terms of mole. 90-70: 30, preferably 20: 80-65: 35, which provides a good balance between adhesion or adhesion and low water absorption (wet), and excellent heat resistance and mechanical strength. Thus, a cyclic olefin-based ring-opening copolymer suitable for an optical material can be obtained.
[0048]
As the polymerization catalyst used for the ring-opening copolymerization treatment, a single component catalyst or a multicomponent catalyst is used.
(1) As a single component catalyst,
Biscyclopentadienyl-3,3-dimethyl titanacyclobutane, biscyclopentadienyl-3-t-butyl titanacyclobutane, or
W (OR 26 ) 2 (= NAr) (= CH (C (CH 3 ) 2 R 27 ),
Mo (OR 28 ) 2 (= NAr) (= CH (C (CH 3 ) 2 R 29 ),
W (Br) 2 (OCH 2 (T-Bu)) 2 (= CH (t-Bu)),
W (CO) 4 (= C (OMe) (CH 2 CH 2 CH = CH 2 ),
RuCl 2 [PPh 3 ] 2 (= CHCO 2 Et),
RuCl 2 [PCy 3 ] 2 (= CHCH = CPh 2 ),
RuCl 2 [PCy 3 ] 2 (= CHPh),
Ta (OAr) 3 (= CH (t−Bu)), or
Ta (SAr ') 3 (= CH (t-Bu))
[Where R 26 ~ R 29 Represents a hydrocarbon group or a halogenated hydrocarbon group, and Ar and Ar ′ represent an aromatic substituent. The compound represented by this can be used.
[0049]
(2) As the multi-component catalyst, (i) component: at least one selected from compounds of tungsten, molybdenum, rhenium, titanium and hafnium; and (ii) component: periodic table IA, IIA, IIB, IIIA, A compound of an IVA or IVB group element that is combined with at least one selected from those having the element-carbon bond or the element-hydrogen bond can be suitably used. , (Ii) Component: A combination of additives (activity improvers) may be used.
(I) As compounds of tungsten, molybdenum, rhenium, titanium or hafnium suitable as component, these halides, oxyhalides, alkoxides, phenoxides, carboxylates, β-diketone compounds, sulfonates, phosphates , Phosphites, carbonyl complexes, acetonitrile complexes, cyclopentadienyl complexes, indenyl complexes, hydride complexes, and derivatives thereof, which can be used alone or in combination of two or more. As the compounds of tungsten and molybdenum, alkoxides, phenoxides, halides, and oxyhalides are particularly preferably used because they exhibit high polymerization activity.
[0050]
Specific examples of compounds used as component (i) include WCl 6 , WCl 5 , WCl 4 , WBr 6 , WBr 4 , WOCl 4 , WOBr 4 , W (OC 6 H 5 ) 6 , WCl 4 (OCH 2 CH 2 Cl) 2 , WCl 2 (OC 6 H 5 ) 4 , WOCl 2 [OC 6 H 3 -2,6- (i-Pr) 2 ] 2 , WO (OC 6 H 3 -2,6-Me 2 ) 4 , MoCl 5 , MoCl 3 , Mo (OC 2 H 5 ) 5 , MoO 2 (Acac) 2 , Mo (CO) 5 (C 5 H 5 N), WCl 6 ・ (C 5 H 5 N), ReOCl 3 , Re (CO) 5 Cl, TiCl 4 , HfCl 4 , ZrCl 4 , (Η 5 -C 5 H 5 ) 2 TiCl 2 , (Η 5 -C 9 H 7 ) 2 TiCl 2 Etc. These can be used individually by 1 type or in combination of 2 or more types.
[0051]
Specific examples of the compound used as the component (ii) include, for example, organic lithiums such as methyl lithium, ethyl lithium, butyl lithium, phenyl lithium, cyclopentadienyl lithium, organic sodiums such as cyclopentadienyl sodium, dimethyl Organic magnesium such as magnesium, diethylmagnesium, dibutylmagnesium, halogenated ethylmagnesium, halogenated butylmagnesium, trialkylaluminum, dialkylaluminum halide, alkylaluminum dihalide, alkylaluminum sesquihalide, dialkylaluminum hydride, alkylaluminoxane, etc. Organoaluminum, organozinc such as dialkylzinc, organotin such as tetraalkyltin and tetraphenyltin , It may be used lithium hydride, lithium aluminum hydride, sodium hydride, sodium borohydride, and metal hydrides such as aluminum hydride.
The component (ii) is preferably used in the range of 1 to 100 times, more preferably 2 to 30 times in terms of a molar ratio converted to a metal atom with respect to the component (i).
[0052]
(Iii) The activity improver of the component is used as necessary to further improve the activity of ring-opening copolymerization, and specific examples thereof include water, oxygen, acetaldehyde, acetaldehyde diethyl acetal, ethylene oxide, epichlorohydrin, N -Nitrosodimethylaniline, tetrabutylammonium chloride, N-nitrosodiphenylamine, aluminum tribromide and the like.
The ratio of the component (iii) used is not particularly limited and is appropriately selected depending on the kind thereof. Usually, the molar ratio is 0.005 to 10 times, preferably 0. It is used in the range of 01 to 2 times.
[0053]
Solvents used for the ring-opening copolymerization treatment include aliphatic hydrocarbons such as pentane, normal hexane, normal heptane, butane, and 2-methylbutane, alicyclic hydrocarbons such as cyclohexane, cyclopentane, and methylcyclopentane, toluene, Aromatic hydrocarbons such as benzene, xylene, mesitylene, halogenated hydrocarbons such as dichloromethane, 1,2-dichloroethane, 1,2-dichloroethylene, chlorobenzene, o-dichlorobenzene, ethyl acetate, butyl acetate, γ-butyrolactone, nitromethane The polar solvent of these etc. is mentioned, These can be used individually by 1 type or in combination of 2 or more types. Moreover, it is preferable that the usage-amount of a solvent is the range of 1-20 times by weight ratio with respect to a monomer.
[0054]
An example of a specific method of ring-opening copolymerization will be described. In a nitrogen or argon atmosphere, a solvent, a specific monomer (A) that is an essential monomer, and a specific monomer ( B), a monomer component consisting of a specific monomer (C) and / or a specific monomer (D), which is an optional monomer, and a molecular weight regulator used as necessary, The polymerization system is set to a temperature in the range of -20 ° C to 100 ° C. Next, a polymerization catalyst is added to this polymerization system, and polymerization is carried out in the range of -20 ° C to 120 ° C.
In the above, α-olefin such as ethylene, propylene, 1-butene, 1-hexene and 1-octene, vinyl ether, thiovinyl ether, vinyl acetate, and the like can be used as the molecular weight regulator.
Moreover, it is preferable that the addition amount of a polymerization catalyst is the quantity from which a monomer component will be 100-100,000 mol per gram atom of transition metal atoms in the said polymerization catalyst.
The polymerization method may be a batch method or a continuous method.
In addition, either the specific monomer (A) or the specific monomer (B), or the specific monomer (C) or the specific monomer (D) used as necessary is supplied to the reaction vessel. The polymerization is started, and during the polymerization process, by supplying other monomers stepwise or continuously to the reaction vessel, the proportion of each structural unit is changed in a gradient or each structural unit is It is also possible to obtain a cyclic olefin-based ring-opening copolymer that is unevenly distributed in a block shape.
The polymerization reaction is stopped by a compound selected from water, alcohol, organic acid, carbon dioxide gas, aldehyde compound, ketone compound and the like.
[0055]
After completion of the polymerization reaction, a polymerization catalyst residue may be separated and removed from the polymerization reaction mixture as necessary. As the separation / removal treatment method, a known method can be used as appropriate. For example, there may be mentioned a method of adding an inorganic acid such as hydrochloric acid, nitric acid or sulfuric acid, or an organic acid such as maleic acid or fumaric acid to the polymerization reaction mixture, and then washing with a solution of water or alcohol. The polymerization catalyst residue can also be removed by adsorbing it on an adsorbent such as diatomaceous earth, alumina, silica, activated carbon, or by performing a filtration treatment with a filter or the like.
The polymer solution is coagulated with alcohols such as methanol, ethanol, isopropanol and other poor solvents, and the desired cyclic olefin ring-opening copolymer is obtained by drying under reduced pressure and / or heat. . In this step, unreacted monomers remaining in the polymer solution are also removed.
[0056]
The cyclic olefin-based ring-opening copolymer of the present invention does not necessarily need to be hydrogenated, and the ring-opening copolymer obtained by the ring-opening polymerization can be used as it is depending on its use. However, it is preferable that the olefinic unsaturated bond in the molecule is hydrogenated in that heat coloring and thermal deterioration are suppressed and excellent thermal stability is obtained.
[0057]
The hydrogenation reaction for hydrogenating the olefinically unsaturated bond in the molecule may be carried out using the copolymer solution after the completion of the ring-opening polymerization. After the removal treatment, a copolymer solution prepared by dissolving the ring-opening copolymer in an appropriate solvent may be used.
The hydrogenation reaction is usually performed under conditions of a hydrogen pressure of 1.0 to 15 MPa and a temperature of 50 to 200 ° C. As a hydrogenation catalyst, a metal selected from palladium, platinum, platinum, rhodium, iridium, ruthenium, and nickel was supported on a carrier selected from silica, alumina, zeolite, diatomaceous earth, magnesia, carbon, calcium carbonate, and the like. Heterogeneous catalysts, or nickel octoate / triethylaluminum, nickel naphthenate / triethylaluminum, cobalt octoate / triethylaluminum, cobalt octoate / n-butyllithium, biscyclopentadienyltitanium dichloride / diethylaluminum chloride, palladium acetate / Triethylaluminum, tris (triphenylphosphine) chlororhodium, tris (triphenylphosphine) hydridocarbonyl chlororuthenium, tris (tri Rylphosphine) hydrido carbonyl chloro ruthenium, tris (trixyl phosphine) hydrido carbonyl chloro ruthenium, tris (tricyclohexylphosphine) hydrido carbonyl chlororuthenium, tris (triphenylphosphine) dihydro carbonyl ruthenium, A homogeneous catalyst such as bis (triphenylphosphine) dichlororuthenium is preferably used.
The hydrogenation catalyst is usually used in the range of 10 to 1000 ppm in terms of transition metal atoms with respect to the ring-opening copolymer.
[0058]
The hydrogenated ring-opening copolymer has excellent thermal stability as the hydrogenation rate of the olefinically unsaturated bond in the molecule increases. As a result, heat deterioration due to heating, deterioration due to oxygen, and the like can be suppressed in a solvent removal process, a pelletizing process, a product forming process, and the like.
The hydrogenation rate is usually 95% or more, preferably 99% or more, more preferably 99.5% or more. When the hydrogenation rate is less than 95%, the hydrogenated ring-opening copolymer may have insufficient heat deterioration resistance.
[0059]
Examples of the cyclic olefin-based ring-opening copolymer of the present invention include known antioxidants such as 2,6-di-t-butyl, 4-methylphenol, 4,4′-thiobis- (6-t-butyl). -3-methylphenol), 1,1′-bis (4-hydroxyphenyl) cyclohexane, 2,2′-methylenebis (4-ethyl-6-tert-butylphenol), 2,5-di-tert-butylhydroquinone, A phenolic or hydroquinone antioxidant such as pentaerythrityl-tetrakis [3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate can be added. Further, tris (4-methoxy-3,5-diphenyl) phosphite, tris (nonylphenyl) phosphite, tris (2,4-di-t-butylphenyl) phosphite, bis (2,6-di-t -By adding phosphorus antioxidants such as -butyl-4-methylphenyl) pentaerythritol diphosphite and bis (2,4-di-t-butylphenyl) pentaerythritol diphosphite, oxidation stability is improved. Can be improved.
Among these compounds, those having a decomposition temperature of 250 ° C. or higher measured by 5% weight loss in TGA (thermogravimetric analysis) are preferable. Moreover, it is preferable that the usage-amount of these antioxidant is 0.05-5.0 weight part with respect to 100 weight part of cyclic olefin type | system | group ring-opening copolymers of this invention.
[0060]
In the cyclic olefin ring-opening copolymer of the present invention, the one having the structural unit (C) can be a crosslinked product obtained by crosslinking the hydrolyzable silyl group or oxetanyl group in the structural unit (C). .
[0061]
In the case where the structural unit (C) has a hydrolyzable silyl group, as a crosslinking method of the copolymer, for example,
(A) a compound that generates an acid by hydrolysis, or
(B) a compound that generates strong Bronsted acid or Lewis acid by irradiation with actinic rays such as ultraviolet rays, far ultraviolet rays, X rays, electron beams, etc., such as g rays, h rays, i rays, or heat;
Can be blended in the copolymer, and the silyl groups can be crosslinked by a hydrolysis / condensation reaction caused by an acid generated by a predetermined operation.
Specific examples of the compound (a) include organic phosphite compounds, organic sulfinic acid esters, carboxylic acid t-butyl esters, carboxylic acid hemiacetal esters, and the like.
Examples of the compound (b) include various diazonium salts, ammonium salts, iodonium salts, sulfonium salts, phosphonium salts, arsonium salts, onium salts such as oxonium salts, halogen-containing oxadiazole compounds, halogen-containing triazine compounds, and halogen-containing compounds. Specific halogenated organic compounds such as acetophenone compounds, halogen-containing benzophenone compounds, quinonediazide compounds, α, α-bis (sulfonyl) diazomethane compounds, α-carbonyl-α-sulfonyl-diazomethane compounds, sulfonyl compounds, organic acid ester compounds, organic Examples include acid amide compounds and organic acid imide compounds.
[0062]
In the case where the structural unit (C) has an oxetanyl group, as a method for crosslinking the copolymer, for example,
The method of mix | blending the compound of the said (b), and bridge | crosslinking by the ring-opening cationic polymerization reaction of the oxetanyl group caused by the acid to generate | occur | produce is mentioned. When a compound that generates an acid by light is used as the compound (b), it is more preferable because it can be crosslinked at room temperature.
[0063]
The compound (a) or the compound (b) is 0.05 to 20 parts by weight, preferably 0.2 to 10 parts by weight, based on 100 parts by weight of the cyclic olefin ring-opening copolymer. Used.
[0064]
In the cyclic olefin-based ring-opening copolymer of the present invention, the copolymer is dissolved in a solvent capable of dissolving the copolymer selected from a hydrocarbon solvent or a halogenated hydrocarbon solvent. A coalescence solution is prepared, and this copolymer solution is cast on a carrier film such as a steel belt or polyester, and then dried into a film or sheet by a solvent casting method (solution casting method). Can be molded. Further, it can be formed into a pellet shape, a film shape, a sheet shape, or other shapes by an injection molding method, a compression molding method, an extrusion molding method using a T die, or the like.
[0065]
The cyclic olefin-based ring-opening copolymer of the present invention is a thermoplastic resin, for example, a cyclic olefin-based (co) polymer other than the cyclic olefin-based ring-opening copolymer of the present invention (for example, a cyclic olefin-based addition polymer, Hydrogenated ring-opening polymer), petroleum resins having an aromatic or alicyclic hydrocarbon structure, and hydrogenated styrenic resins to maintain transparency while maintaining softening temperature Also, it can be obtained as a resin composition with controlled birefringence.
[0066]
Since the cyclic olefin-based ring-opening copolymer of the present invention has excellent optical transparency, heat resistance, adhesion / adhesion, low water absorption, and mechanical strength, a light guide plate, a polarizing film, a surface protective film, a light diffusion film , Phase difference film, transparent conductive film, antireflection film, OHP film, optical component such as optical disc, optical fiber, lens, prism, etc., and extremely useful as optical materials such as coating material for optical components, and semiconductor encapsulation It is useful as an electronic component material such as an agent, a coating agent, an adhesive, a medical device, various containers, and a binder.
[0067]
【Example】
Specific examples of the present invention will be described below, but the present invention is not limited to these examples. In the following examples, the weight average molecular weight, number average molecular weight, total light transmittance, glass transition temperature, water absorption, adhesion / adhesion, tensile strength and elongation were measured by the following methods.
[0068]
(1) Weight average molecular weight and number average molecular weight:
Using a 150C-type gel permeation chromatography (GPC) apparatus manufactured by WATERS equipped with an H-type column manufactured by Tosoh Corporation, using o-dichlorobenzene as a solvent at 120 ° C. The weight average molecular weight and number average molecular weight of the sample in terms of standard polystyrene were measured.
(2) Total light transmittance:
Based on ASTM-D1003, a test piece having a thickness of 120 μm was prepared, and the total light transmittance was measured.
(3) Glass transition temperature:
The glass transition temperature of the sample was measured by the peak temperature of Tan δ of dynamic viscoelasticity (= ratio E ″ / E ′ of storage elastic modulus E ′ and loss elastic modulus E ″). Measurement of dynamic viscoelasticity using Leo Vibron DDV-01FP (manufactured by Orientec), measuring frequency 10Hz,
(4) Water absorption rate:
A test piece having a thickness of 120 μm was prepared, and the test piece was immersed in water at 23 ° C. for 24 hours in accordance with ASTM-D570, and then the water absorption was measured from the change in weight of the test piece.
(5) Adhesiveness / adhesion:
A test piece of 10 cm × 10 cm was prepared, aluminum was vapor-deposited on this test piece, and the formed deposited film was cut into a grid pattern at intervals of 1 mm in the vertical and horizontal directions by a cutter knife, 100 blocks (10 x 10) with dimensions of 1 mm x 1 mm separated from each other were formed, and the peel-off test of the deposited film was performed using cellophane tape, and the number of peeled blocks in all blocks (100) was measured. did.
(6) Tensile strength and elongation
Based on JIS K7113, the tensile strength and elongation of the test were measured under the condition of a tensile speed of 3 mm / min.
[0069]
<Example 1>
In a 300 ml glass pressure-resistant bottle, under a nitrogen atmosphere, 80 ml of toluene as a solvent, and tricyclo [5.2. 1.0 2,6 ] Deca-8-ene 51 mmol, 8-methyl-8-methoxycarbonyltetracyclo [4.4.0.1 as the specific monomer (B) 2,5 . 1 7, 10 119 mmol of dodec-3-ene, 42.5 mmol of 1-hexene as a molecular weight regulator, 0.119 mmol of triethylaluminum as a polymerization catalyst and methanol-modified product of tungsten hexachloride [methanol / tungsten = 3 (mol / Mol)] 0.017 mmol was added in this order. Then, ring-opening polymerization of the specific monomer (A) and the specific monomer (B) was performed at 80 ° C. for 2 hours, and then the polymerization reaction was stopped with methanol. The conversion rate of the monomer to the ring-opening copolymer was 97%.
Next, 660 ml of water and 47.5 mmol of lactic acid were added to the obtained reaction solution and stirred, and then allowed to stand to separate into an aqueous phase and a reaction solution phase. Thereafter, the aqueous phase containing the reaction product of the catalyst component is removed, and the reaction solution is added to 3 liters of isopropanol to solidify and recover the product, thereby removing the unreacted monomer and recovering the recovered product. Was dried at 50 ° C. for 15 hours under vacuum to obtain a cyclic olefin ring-opening copolymer. The obtained cyclic olefin-based ring-opening copolymer is referred to as “ring-opening copolymer A”.
Benzene-d of this ring-opening copolymer A 6 270MHz in, 1 From the 1 H-NMR spectrum, tricyclo [5.2.1.0 2,6 The proportion of the structural unit (A) derived from deca-8-ene is 32 mol% (21.5 wt%), 8-methyl-8-methoxycarbonyltetracyclo [4.4.0.1]. 2,5 . 1 7, 10 The proportion of the structural unit (B) derived from dodec-3-ene was determined to be 68 mol% (78.5 wt%) (3.2 to 3.6 ppm absorption based on the methoxycarbonyl group, double Calculated from the ratio to 5.4-5.8 ppm absorption based on hydrogen adjacent to the bond). Of the ring-opening copolymer A 1 The H-NMR spectrum is shown in FIG. 1, and the infrared absorption spectrum is shown in FIG.
[0070]
In a 500 ml stainless steel pressure-resistant reactor, a solution of 15 g of the obtained ring-opening copolymer A dissolved in 200 g of toluene, carbonylchlorohydridotris (triphenylphosphine) ruthenium [RuHCl (CO) (PPh 3 ) 3 ] Was added in an amount of 70 ppm in terms of ruthenium atoms, and a hydrogenation reaction was carried out under conditions of a hydrogen pressure of 10 MPa and 165 ° C. for 4 hours. The resulting reaction solution was decatalyzed with an aqueous lactic acid solution and then coagulated with isopropyl alcohol to obtain a hydrogenated cyclic olefin ring-opening copolymer. The obtained hydrogenated cyclic olefin-based ring-opening copolymer is referred to as “ring-opening copolymer AH”.
This ring-opening copolymer AH 1 The H-NMR spectrum was measured, and the absorption peak of 3.2 to 3.6 ppm based on the methoxycarbonyl group and the hydrogen adjacent to the double bond remaining unhydrogenated in the ring-opening copolymer AH5. It was 99.7% when hydrogenation rate was computed from the relative ratio with the absorption peak of 4-5.8 ppm. Of the ring-opening copolymer AH 1 An H-NMR spectrum is shown in FIG. 3, and an infrared absorption spectrum is shown in FIG. The ring-opening copolymer AH had a polystyrene-equivalent number average molecular weight (Mn) of 20,000, a weight average molecular weight (Mw) of 75,000, and Mw / Mn of 3.7.
[0071]
10 g of ring-opening copolymer AH was dissolved in 35.5 g of tetrahydrofuran, and pentaerythrityl tetrakis [3- (3,5-di-t-butyl-4-hydroxyphenyl) was added as an antioxidant to the resulting copolymer solution. ) Propionate] and tris (2,4-di-t-butylphenyl) phosphite were added at a ratio of 0.5 parts by weight per 100 parts by weight of the ring-opening copolymer AH. Using this copolymer solution, a film having a thickness of 120 μm was produced by a solvent casting method. The residual solvent of the obtained film was 0.5% by weight. A test piece was prepared from this film and evaluated for each physical property. The results are shown in Table 1.
[0072]
<Example 2>
Tricyclo [5.2.1.0] wherein the specific monomer (A) has a molar ratio of endo-isomer to exo-isomer of 95: 5. 2,6 Deca-8-ene 75 mmol, 8-methyl-8-methoxycarbonyltetracyclo [4.4.0.1 as the specific monomer (B) 2,5 . 1 7, 10 A cyclic olefin-based ring-opening copolymer was prepared in the same manner as in Example 1 except that 95 mmol of dodec-3-ene was used (the obtained cyclic olefin-based ring-opening copolymer was “ring-opening copolymer”). And a hydrogenated cyclic olefin ring-opening copolymer was prepared (the resulting hydrogenated cyclic olefin ring-opening copolymer is referred to as “ring-opening copolymer BH”). ). The conversion rate of the monomer to the ring-opening copolymer was 90%, and the hydrogenation rate of the ring-opening copolymer BH was 99.8%. Of the ring-opening copolymer BH 1 The H-NMR spectrum is shown in FIG.
In addition, tricyclo [5.2.1.0] in the ring-opening copolymer B. 2,6 The proportion of structural units derived from deca-8-ene was 45 mol% (32.3% by weight), 8-methyl-8-methoxycarbonyltetracyclo [4.4.0.1. 2,5 . 1 7, 10 The proportion of structural units derived from dodec-3-ene was 55 mol% (67.7 wt%). The ring-opening copolymer BH had a number average molecular weight (Mn) of 73,000, a weight average molecular weight (Mw) of 168,000, and Mw / Mn of 2.3.
Moreover, about the ring-opening copolymer BH, the test piece was produced similarly to Example 1 and each physical property was evaluated. The results are shown in Table 1.
[0073]
<Example 3>
Tricyclo [5.2.1.0] wherein the specific monomer (A) has a molar ratio of endo-isomer to exo-isomer of 99: 1. 2,6 A cyclic olefin ring-opening copolymer was prepared in the same manner as in Example 1 except that deca-8-ene was used (the resulting cyclic olefin ring-opening copolymer was referred to as “ring-opening copolymer”). C ”), a hydrogenated cyclic olefin-based ring-opening copolymer was prepared (the resulting hydrogenated cyclic olefin-based ring-opening copolymer is referred to as“ ring-opening copolymer CH ”). The conversion rate of the monomer to the ring-opening copolymer was 94%, and the hydrogenation rate of the ring-opening copolymer CH was 99.7%.
In addition, tricyclo [5.2.1.0] in the ring-opening copolymer C. 2,6 The proportion of structural units derived from deca-8-ene was 32 mol% (21.5 wt%), 8-methyl-8-methoxycarbonyltetracyclo [4.4.0.1. 2,5 . 1 7, 10 The proportion of structural units derived from dodec-3-ene was 68 mol% (78.5 wt%). The number average molecular weight (Mn) of the ring-opening copolymer CH was 74,000, the weight average molecular weight (Mw) was 151,000, and Mw / Mn was 2.0.
Moreover, about the ring-opening copolymer CH, the test piece was produced similarly to Example 1 and each physical property was evaluated. The results are shown in Table 1.
[0074]
<Example 4>
Tricyclo [5.2.1.0] wherein the specific monomer (A) has a molar ratio of endo-isomer to exo-isomer of 99: 1. 2,6 ] Deca-8-ene 45 mmol, 8-methyl-8-methoxycarbonyltetracyclo [4.4.0.1 as the specific monomer (B) 2,5 . 1 7, 10 ] While using 100.5 mmol of dodec-3-ene and 5 mmol of 5-triethoxysilylbicyclo [2.2.1] hept-2-ene as the specific monomer (C), further hydrogenation reaction A cyclic olefin ring-opening copolymer was prepared in the same manner as in Example 1 except that the treatment temperature was changed to 125 ° C. (the obtained cyclic olefin ring-opening copolymer was referred to as “ring-opening copolymer”). D ”), and a hydrogenated cyclic olefin ring-opening copolymer was prepared (the resulting hydrogenated cyclic olefin ring-opening copolymer is referred to as“ ring-opening copolymer DH ”). The conversion rate of the monomer to the ring-opening copolymer was 93%, and the hydrogenation rate of the ring-opening copolymer DH was 99.7%. Of the ring-opening copolymer DH 1 The H-NMR spectrum is shown in FIG.
In addition, tricyclo [5.2.1.0] in the ring-opening copolymer D. 2,6 The proportion of structural units derived from deca-8-ene was 32 mol% (21.3% by weight), 8-methyl-8-methoxycarbonyltetracyclo [4.4.0.1. 2,5 . 1 7, 10 The proportion of structural units derived from dodec-3-ene is 65 mol% (74.9 wt%), the proportion of structural units derived from 5-triethoxysilylbicyclo [2.2.1] hept-2-ene Was 3 mol% (3.8 wt%).
The number average molecular weight (Mn) of the ring-opening copolymer DH was 69,000, the weight average molecular weight (Mw) was 162,000, and Mw / Mn was 2.3.
[0075]
10 g of ring-opening copolymer DH was dissolved in 35.5 g of tetrahydrofuran, and pentaerythrityltetrakis [3- (3,5-di-t-butyl-4-hydroxyphenyl) was added as an antioxidant to the resulting copolymer solution. ) Propionate] and tris (2,4-di-t-butylphenyl) phosphite are added at a ratio of 0.5 parts by weight to 100 parts by weight of the ring-opening copolymer DH, respectively. Dibutyl phosphate was added at a ratio of 0.7 parts by weight with respect to 100 parts by weight of the ring-opening copolymer DH. Using this copolymer solution, a film having a thickness of 120 μm was produced by a solvent casting method, and a cross-linking treatment was performed by contacting the film with water vapor at 120 ° C. for 2 hours. A test piece was prepared from the crosslinked film, and each physical property was evaluated. The results are shown in Table 1.
In addition, when a test piece prepared from the above crosslinked film was immersed in tetrahydrofuran, toluene and methylene chloride, which are good solvents, for the ring-opening copolymer DH, the test piece was insoluble in these solvents. It was confirmed that the solvent resistance was improved by crosslinking.
[0076]
<Example 5>
Tricyclo [5.2.1.0] wherein the specific monomer (A) has a molar ratio of endo-isomer to exo-isomer of 95: 5. 2,6 Deca-8-ene 105 mmol, 8-methyl-8-methoxycarbonyltetracyclo [4.4.0.1 as the specific monomer (B) 2,5 . 1 7, 10 A cyclic olefin-based ring-opening copolymer was prepared in the same manner as in Example 1 except that 65 mmol of dodec-3-ene was used (the obtained cyclic olefin-based ring-opening copolymer was “ring-opening copolymer”). And a hydrogenated cyclic olefin ring-opening copolymer was prepared (the resulting hydrogenated cyclic olefin ring-opening copolymer is referred to as "ring-opening copolymer EH"). ). The conversion rate of the monomer to the ring-opening copolymer was 88%, and the hydrogenation rate of the ring-opening copolymer EH was 99.8%. Of the ring-opening copolymer EH 1 The H-NMR spectrum is shown in FIG.
Further, tricyclo [5.2.1.0] in the ring-opening copolymer E is used. 2,6 The proportion of structural units derived from deca-8-ene is 62 mol% (48.5 wt%), 8-methyl-8-methoxycarbonyltetracyclo [4.4.0.1. 2,5 . 1 7, 10 The proportion of structural units derived from dodec-3-ene was 38 mol% (51.5 wt%). The ring-opening copolymer EH had a number average molecular weight (Mn) of 69,000, a weight average molecular weight (Mw) of 158,000, and Mw / Mn of 2.3.
Moreover, about the ring-opening copolymer EH, the test piece was produced similarly to Example 1, and each physical property was evaluated. The results are shown in Table 1.
[0077]
<Comparative example 1>
As a monomer used for ring-opening polymerization, 8-methyl-8-methoxycarbonyltetracyclo [4.4.0.1]. 2,5 . 1 7, 10 A cyclic olefin ring-opening polymer was prepared in the same manner as in Example 1 except that 170 mmol of dodec-3-ene alone was used. A hydrogenated cyclic olefin ring-opening polymer was prepared (the resulting hydrogenated cyclic olefin ring-opening polymer is referred to as “ring-opening polymer FH”). The conversion rate of the monomer to the ring-opening polymer was 100%, and the hydrogenation rate of the ring-opening polymer FH was 99.8%.
The number average molecular weight (Mn) of the ring-opening polymer FH was 20,000, the weight average molecular weight (Mw) was 73,000, and Mw / Mn was 3.7.
Moreover, about the ring-opening polymer FH, the test piece was produced similarly to Example 1, and each physical property was evaluated. The results are shown in Table 1.
[0078]
<Comparative example 2>
Tricyclo [5.2.1.0] in which the molar ratio of endo form to exo form is 95: 5. 2,6 ] Tricyclo [5.2.1.0] in which the molar ratio of endo to exo instead of deca-8-ene is 10:90 2,6 A cyclic olefin ring-opening copolymer was prepared in the same manner as in Example 1 except that deca-8-ene was used (the resulting cyclic olefin ring-opening copolymer was referred to as “ring-opening copolymer”). G ”)) and a hydrogenated cyclic olefin-based ring-opening copolymer was prepared (the resulting hydrogenated cyclic olefin-based ring-opening polymer is referred to as“ ring-opening copolymer GH ”). The conversion rate of the monomer to the ring-opening copolymer was 98%, and the hydrogenation rate of the ring-opening copolymer GH was 99.8%.
The ring-opening copolymer GH had a number average molecular weight (Mn) of 75,000, a weight average molecular weight (Mw) of 165,000, and Mw / Mn of 2.2.
Moreover, about the ring-opening copolymer GH, the test piece was produced similarly to Example 1 and each physical property was evaluated. The results are shown in Table 1.
[0079]
<Comparative Example 3>
8-Methyl-8-methoxycarbonyltetracyclo [4.4.0.1 2,5 . 1 7, 10 ] 8-ethyltetracyclo [4.4.0.1 instead of dodec-3-ene] 2,5 . 1 7, 10 A cyclic olefin ring-opening copolymer was prepared in the same manner as in Example 1 except that dodec-3-ene was used (the obtained cyclic olefin ring-opening copolymer was referred to as “ring-opening copolymer”). H ”.), A hydrogenated cyclic olefin-based ring-opening copolymer was prepared (the resulting hydrogenated cyclic olefin-based ring-opening copolymer is referred to as“ ring-opening copolymer HH ”). The conversion rate of the monomer to the ring-opening copolymer was 99%, and the hydrogenation rate of the ring-opening copolymer HH was 99.8%.
The number average molecular weight (Mn) of the ring-opening copolymer HH was 21,000, the weight average molecular weight (Mw) was 69,000, and Mw / Mn was 3.3.
Moreover, about the ring-opening copolymer HH, the test piece was produced similarly to Example 1 except having used cyclohexane instead of tetrahydrofuran, and each physical property was evaluated. The results are shown in Table 1.
[0080]
[Table 1]
[0081]
As is clear from Table 1, the cyclic olefin ring-opening copolymers (ring-opening copolymer AH to ring-opening copolymer EH) according to Examples 1 to 5 have a high total light transmittance and are made of glass. It was confirmed that the transition temperature was high, the water absorption was low, the adhesion or adhesion to metal was high, and the mechanical strength was high.
On the other hand, the cyclic olefin ring-opening polymer according to Comparative Example 1 (ring-opening polymer FH) has a higher water absorption and lower strength than the ring-opening copolymer according to the example. The cyclic olefin-based ring-opening copolymer according to Comparative Example 2 (ring-opening copolymer GH) is lower in strength than the ring-opening copolymer according to Example, and the cyclic according to Comparative Example 3 The olefin ring-opening copolymer (ring-opening copolymer HH) had lower adhesion and adhesiveness than the ring-opening copolymers according to the examples.
[0082]
【The invention's effect】
The cyclic olefin-based ring-opening copolymer of the present invention is derived from a specific tricyclododecene having a structural unit derived from a specific tricyclomonoolefin having an end-body ratio of 80% or more and an ester group. It has excellent optical properties such as transparency, low water absorption (humidity), high affinity with other materials, and good post-processability such as adhesion and printability. In addition, it has excellent heat resistance and mechanical strength.
According to the production method of the present invention, the above cyclic olefin-based ring-opening copolymer can be advantageously produced.
Since the cyclic olefin-based ring-opening copolymer of the present invention has such characteristics, it is extremely useful as an optical material such as an optical component or a coating material for the optical component, and further an electronic component such as a semiconductor sealing agent. It is useful as a material, coating agent, adhesive, medical equipment, various containers, binders, and the like.
[Brief description of the drawings]
FIG. 1 shows the ring-opening copolymer A obtained in Example 1. 1 It is a H-NMR spectrum figure.
2 is an infrared absorption spectrum diagram of the ring-opening copolymer A obtained in Example 1. FIG.
FIG. 3 shows the ring-opening copolymer AH obtained in Example 1. 1 It is a H-NMR spectrum figure.
4 is an infrared absorption spectrum diagram of the ring-opening copolymer AH obtained in Example 1. FIG.
FIG. 5 shows the ring-opening copolymer BH obtained in Example 2. 1 It is a H-NMR spectrum figure.
FIG. 6 shows the ring-opening copolymer DH obtained in Example 4. 1 It is a H-NMR spectrum figure.
FIG. 7 shows the ring-opening copolymer EH obtained in Example 5. 1 It is a H-NMR spectrum figure.
Claims (8)
当該構造単位(A)を得るための単量体は、エンド体の割合が80モル%以上のものであり、ガラス転移温度が120〜250℃であることを特徴とする環状オレフィン系開環共重合体。
The monomer for obtaining the structural unit (A) is a cyclic olefin-based ring-opening copolymer characterized in that the proportion of endo-form is 80 mol% or more and the glass transition temperature is 120 to 250 ° C. Polymer.