JP2003252665A - Powdery quick setting agent for shotcrete and method for working shotcrete using it - Google Patents
Powdery quick setting agent for shotcrete and method for working shotcrete using itInfo
- Publication number
- JP2003252665A JP2003252665A JP2002091409A JP2002091409A JP2003252665A JP 2003252665 A JP2003252665 A JP 2003252665A JP 2002091409 A JP2002091409 A JP 2002091409A JP 2002091409 A JP2002091409 A JP 2002091409A JP 2003252665 A JP2003252665 A JP 2003252665A
- Authority
- JP
- Japan
- Prior art keywords
- quick
- setting
- shotcrete
- setting agent
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、粉体急結剤を用い
る吹付けコンクリートの施工方法に関し、特に、粉塵低
減効果、急結性及び急結剤の圧送性に優れた吹付けコン
クリートの施工方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for constructing shotcrete using a powder quick-setting admixture, and in particular, the construction of shotcrete excellent in dust reduction effect, quick-setting property and pumpability of quick-setting admixture. Regarding the method.
【０００２】[0002]
【従来の技術及び発明が解決しようとする課題】掘削さ
れたトンネルや地下空間の建設工事では、露出面にコン
クリートを吹付けてライニングし、該露出面の崩落を防
止する方法が広く実施されている。2. Description of the Related Art In the construction work of excavated tunnels and underground spaces, a method of spraying concrete on the exposed surface and lining it to prevent the exposed surface from collapsing is widely practiced. There is.
【０００３】コンクリート吹付け工法としては、湿式工
法と乾式工法が知られている。湿式工法では、未硬化の
ベースコンクリートを輸送パイプを通して圧送し、先端
の吹付けノズルから吹出し、掘削された露出面にコンク
リートを吹付けてライニングする。また、ベースコンク
リートだけでは、急結性が得られないので、急結剤を圧
送途中で添加混合している。また、乾式工法では、骨
材、セメント及び粉体急結剤を輸送パイプを通して圧送
し、先端の吹付けノズルから吹出し、別に圧送された水
と共に、掘削された露出面に吹付けてライニングする。As a concrete spraying method, a wet method and a dry method are known. In the wet method, uncured base concrete is pressure-fed through a transport pipe, blown out from a spray nozzle at the tip, and concrete is sprayed on the excavated exposed surface for lining. Further, since the quick setting property cannot be obtained only by the base concrete, the quick setting agent is added and mixed during the pressure feeding. Further, in the dry method, aggregate, cement, and powder quick-setting admixture are pressure-fed through a transport pipe, blown out from a spray nozzle at the tip, and sprayed on the excavated exposed surface together with water that has been separately pressure-fed for lining.
【０００４】従来から、急結剤としては、カルシウムア
ルミネート系鉱物、カルシウムサルホアルミネート系鉱
物やカルシウムナトリウムアルミネート系鉱物を主成分
とした粉体急結剤と、アルミン酸塩、炭酸アルカリや硫
酸アルミニウム等の水溶液を主成分とした液体急結剤が
あることが知られている。粉体急結剤を使用した吹付け
工法では、液体急結剤を使用した場合に比べて、急結性
に優れている、という利点がある。一方で、急結剤が粉
体であるため、充分混合されずに残った急結剤粉体が粉
塵として発生するため、粉塵発生量が多くなるという欠
点がある。これに対し、液体急結剤を使用した吹付け工
法では、粉体急結剤を使用した場合に比べて粉塵が少な
い、という利点がある。これは、急結剤が液体であるた
め、急結剤からの粉塵発生がほとんど無いためと考えら
れる。一方で、液体急結剤を使用した場合は、粉体急結
剤を使用した場合に比べて急結性に劣るため、トンネル
の天端（天井）部分に吹付けた場合の付着が悪い、厚吹
きした場合（コンクリートの吹付け厚さが厚い場合）、
吹付けコンクリートが自重により崩落する等の、欠点を
有していた。Conventionally, as a quick-setting agent, a powdered quick-setting agent mainly containing calcium aluminate-based minerals, calcium sulfaluminate-based minerals and calcium sodium aluminate-based minerals, aluminates, alkali carbonates and It is known that there is a liquid quick-setting agent containing an aqueous solution of aluminum sulfate or the like as a main component. The spraying method using the powder quick-setting admixture has an advantage that the quick-setting property is superior to the case where the liquid quick-setting admixture is used. On the other hand, since the quick-setting agent is a powder, the quick-setting agent powder that is left without being sufficiently mixed is generated as dust, which has a drawback that the amount of dust generated increases. On the other hand, the spraying method using the liquid quick-setting admixture has an advantage that the amount of dust is less than that in the case where the powder quick-setting admixture is used. It is considered that this is because the quick-setting admixture is a liquid, so that almost no dust is generated from the quick-setting admixture. On the other hand, when the liquid quick-setting agent is used, the quick-setting property is inferior to the case where the powder quick-setting agent is used, so the adhesion is poor when sprayed on the top (ceiling) part of the tunnel. When spraying thickly (when the spraying thickness of concrete is thick),
There was a defect that the shotcrete collapsed due to its own weight.
【０００５】そこで、本発明では、良好な急結性を有
し、かつ、粉塵発生量の少ない吹付けコンクリート用粉
体急結剤及びそれを用いた吹付けコンクリート施工方法
を提供することを目的とするものである。Therefore, the present invention has an object to provide a powder quick-setting admixture for spraying concrete which has a good quick-setting property and produces a small amount of dust, and a spraying concrete construction method using the same. It is what
【０００６】[0006]
【課題を解決するための手段】本発明者は、上記の課題
を解決すべく鋭意研究した結果、特定の液状物質を配合
すれば、粉塵発生が低減するとともに急結性及び急結剤
供給装置での圧送性にも優れた粉体急結剤が得られるこ
とを見出し、本発明を完成させた。As a result of intensive studies to solve the above-mentioned problems, the present inventor has found that when a specific liquid substance is blended, the generation of dust is reduced and the quick-setting and quick-setting agent supply device is reduced. The present invention has been completed by finding that a powder quick-setting admixture excellent in pressure-feeding property can be obtained.
【０００７】即ち、本発明は、アルキレングリコール、
ポリアルキレングリコール、低級アルコールのアルキレ
ンオキサイド付加物、流動パラフィン及び油乳化剤混合
物の群から選ばれる１種又は２種以上の液状物質を含有
することを特徴とする吹付けコンクリート用粉体急結剤
を提供するものである。また、本発明は、当該吹付けコ
ンクリート用粉体急結剤を用いることを特徴とする、吹
付けコンクリートの施工方法を提供するものである。That is, the present invention provides an alkylene glycol,
A powder quick-setting admixture for shotcrete containing one or more liquid substances selected from the group of polyalkylene glycol, alkylene oxide adduct of lower alcohol, liquid paraffin and oil emulsifier mixture. It is provided. The present invention also provides a method for constructing shotcrete, characterized by using the powdered quick-setting admixture for shotcrete.
【０００８】[0008]
【発明の実施の形態】以下、本発明についてさらに詳し
く説明する。本発明の吹付けコンクリート用急結剤は、
粉体急結剤中に、単独では液体である液状物質を粉体と
しての性状を損なわない量含有させることを特徴とする
ものである。当該液状物質を粉体急結剤に含有させるこ
とにより、粉体急結剤の微粉部分が凝集して粒子径が大
きくなり、空気中に飛散しても直ぐに落下するようにな
るため、未混合急結剤が空気中に飛散しても粉塵となり
にくく、粉塵発生量を低減することができる。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in more detail below. The quick setting agent for shotcrete of the present invention is
The present invention is characterized in that a liquid substance which is a liquid alone is contained in the powder quick-setting admixture in an amount that does not impair the properties of the powder. By including the liquid substance in the powder quick-setting admixture, the fine powder part of the powder quick-setting admixture agglomerates to increase the particle size, and even if it scatters in the air, it immediately falls, so it is not mixed. Even if the quick-setting agent scatters in the air, it hardly becomes dust, and the amount of dust generation can be reduced.
【０００９】本発明において用いられる液状物質は、流
動性を有する物質又は混合物であって、融点が２０℃以
下のものが好ましい。The liquid substance used in the present invention is preferably a substance or mixture having fluidity and having a melting point of 20 ° C. or lower.
【００１０】アルキレングリコールとしては、炭素数２
〜５のアルキレングリコールが好ましく、例えばエチレ
ングリコール、プロピレングリコール、トリメチルグリ
コール、ブチレングリコール、１，４−ブタンジオー
ル、１，５−ペンタンジオール等が挙げられる。The alkylene glycol has 2 carbon atoms.
Alkylene glycol of 5 to 5 are preferable, and examples thereof include ethylene glycol, propylene glycol, trimethyl glycol, butylene glycol, 1,4-butanediol, and 1,5-pentanediol.
【００１１】ポリアルキレングリコールとしては、炭素
数２〜４のアルキレングリコール単位を有するものが好
ましく、例えば、ポリエチレングリコール、ポリプロピ
レングリコール、ポリオキシエチレンポリオキシプロピ
レングリコール、ポリブチレングリコール等が挙げられ
る。当該ポリアルキレングリコールのうち、融点２０℃
以下のもの、特に分子量６００以下のものが好ましい。
また、特に、ジエチレングリコールが好ましい。The polyalkylene glycol preferably has an alkylene glycol unit having 2 to 4 carbon atoms, and examples thereof include polyethylene glycol, polypropylene glycol, polyoxyethylene polyoxypropylene glycol and polybutylene glycol. Of the polyalkylene glycol, melting point 20 ° C
The following, especially those having a molecular weight of 600 or less are preferable.
Further, diethylene glycol is particularly preferable.
【００１２】低級アルコールのアルキレンオキサイド付
加物としては、炭素数１〜５の低級アルコールに炭素数
２〜４のアルキレンオキサイドを付加したものであっ
て、平均付加モル数が１〜３０であるものが挙げられ、
特に分子量が１０００以下であるものが好ましい。The alkylene oxide adduct of a lower alcohol is a lower alcohol having a carbon number of 1 to 5 to which an alkylene oxide having a carbon number of 2 to 4 is added, and the average addition mole number is 1 to 30. Named
Particularly, those having a molecular weight of 1,000 or less are preferable.
【００１３】流動パラフィンは、粘度が４０℃で１０〜
８０mm2／ｓであるのが好ましい。Liquid paraffin has a viscosity of 10 to 10 at 40 ° C.
It is preferably 80 mm 2 / s.
【００１４】油乳化剤混合物としては、鉱油、植物油、
動物油及び合成油から選ばれる油と乳化剤との混合物が
挙げられる。鉱油としては各種石油類、植物油としては
大豆油、ヒマシ油、オリーブ油等、動物油としては魚
油、鯨油等が挙げられ、油としては鉱油が好ましい。乳
化剤としては、非イオン性界面活性剤、アニオン性界面
活性剤が好ましく、特に、非イオン性界面活性剤が好ま
しい。非イオン性界面活性剤としては、ポリオキシエチ
レン高級アルキルエーテル、ポリオキシエチレン高級脂
肪酸エステル、ポリプロピレングリコール・エチレンオ
キサイド付加物（分子量１０００以上）、油脂のエチレ
ンオキサイド付加油等が挙げられる。特にＨＬＢ（例え
ば、Griffin式）が８〜１８であるのが好ましい。油と
乳化剤の混合重量比は、油／乳化剤が１０／１〜１／１
０、更に９／１〜１／９であるのが好ましい。The oil emulsifier mixture includes mineral oil, vegetable oil,
Mention may be made of mixtures of oils and emulsifiers selected from animal oils and synthetic oils. Mineral oils include various petroleums, vegetable oils include soybean oil, castor oil, olive oil, and the like, animal oils include fish oil, whale oil, and the like, with mineral oils being preferred. As the emulsifier, nonionic surfactants and anionic surfactants are preferable, and nonionic surfactants are particularly preferable. Examples of nonionic surfactants include polyoxyethylene higher alkyl ethers, polyoxyethylene higher fatty acid esters, polypropylene glycol / ethylene oxide adducts (molecular weight of 1000 or more), and ethylene oxide addition oils of fats and oils. In particular, it is preferable that the HLB (for example, Griffin type) is 8 to 18. The mixing weight ratio of oil and emulsifier is 10/1 to 1/1 of oil / emulsifier.
It is preferably 0, more preferably 9/1 to 1/9.
【００１５】これらの液状物質のうち、ジエチレングリ
コール、トリエチレングリコール、エチルアルコールの
プロピレンオキサイド付加物、流動パラフィン、鉱油と
乳化剤（特にポリオキシエチレンアルキルエーテル）と
の混合物が好ましい。Among these liquid substances, diethylene glycol, triethylene glycol, a propylene oxide adduct of ethyl alcohol, liquid paraffin, a mixture of mineral oil and an emulsifier (particularly polyoxyethylene alkyl ether) is preferable.
【００１６】本発明において用いられる、液状物質は、
水の含有率が１重量％未満のもの、特に水を含有しない
ものが好ましい。液状物質中の水の含有率が１重量％以
上であると、急結剤の長期安定性、つまり長期間保存し
た粉体急結剤の急結性が大きく低下するので好ましくな
い。The liquid substance used in the present invention is
Those having a water content of less than 1% by weight, particularly those containing no water are preferable. When the content of water in the liquid substance is 1% by weight or more, the long-term stability of the quick-setting agent, that is, the quick-setting property of the powder quick-setting agent stored for a long period of time is greatly reduced, which is not preferable.
【００１７】本発明の粉体急結剤中の液状物質含有量
は、粉塵発生低減効果、急結性及び急結剤供給装置での
圧送性の点から１〜１２重量％、更に１〜１０重量％が
好ましい。液状物質の含有量が、１重量％未満である
と、粉塵低減効果が大きく低下するので、好ましくな
い。また、含有量が１２重量％を超えた場合、通常用い
られている粉体急結剤供給装置での圧送が困難となるた
め好ましくない。さらに１５重量％以上になると急結剤
の一部が塊状となり、圧送されてくるコンクリートとの
混合性及び急結性が低下するので、更に好ましくない。
液状物質の含有量が１〜１２重量％の範囲では急結性が
ほとんど低下せず、また、常用の粉体急結剤供給装置で
粉体急結剤を圧送する場合、圧送性がほとんど変化しな
いので好ましい。The content of the liquid substance in the powder quick-setting admixture of the present invention is from 1 to 12% by weight, and further from 1 to 10 from the viewpoint of the dust generation reducing effect, the quick-setting property and the pressure-feeding property in the quick-coupling agent supply device. Weight percent is preferred. When the content of the liquid substance is less than 1% by weight, the dust reduction effect is significantly reduced, which is not preferable. On the other hand, if the content exceeds 12% by weight, it becomes difficult to carry out pressure feeding by a powder quick-setting admixture supplying device which is usually used, which is not preferable. Further, if the content is 15% by weight or more, a part of the quick-setting agent becomes a lump, and the mixing property with the concrete fed under pressure and the quick-setting property are deteriorated.
When the content of the liquid substance is in the range of 1 to 12% by weight, the quick-setting property hardly deteriorates, and when the powder quick-setting agent is pressure-fed by a conventional powder quick-setting agent supply device, the pressure-feeding property hardly changes. It is preferable because it does not.
【００１８】本発明において、粉体急結剤は、特に限定
するものではなく、カルシウムアルミネート系急結剤、
カルシウムサルホアルミネート系急結剤、カルシウムナ
トリウムアルミネート系急結剤、炭酸アルカリ金属塩、
粉末状アルミン酸ナトリウム等のいずれの粉体急結剤も
用いることができ、急結性能及び硬化後のコンクリート
の性状から、カルシウムアルミネート系急結剤、カルシ
ウムサルホアルミネート系急結剤又はカルシウムナトリ
ウムアルミネート系急結剤が好ましい。また、一般の吹
付けコンクリート用の急結剤、高強度型コンクリート用
の急結剤のいずれも用いることができる。In the present invention, the powder quick-setting agent is not particularly limited, and a calcium aluminate-based quick-setting agent,
Calcium sulphoaluminate type quick-setting agent, calcium sodium aluminate type quick-setting agent, alkali metal carbonate,
Any powder quick-setting agent such as powdered sodium aluminate can be used, and calcium-aluminate-based quick-setting agent, calcium-sulfaluminate-based quick-setting agent or calcium can be used depending on the quick-setting performance and the properties of concrete after hardening. A sodium aluminate type quick-setting agent is preferred. Further, both a general quick-setting agent for shotcrete and a quick-setting agent for high strength concrete can be used.
【００１９】本発明において、液状物質を粉体急結剤へ
含有させる方法としては、ミキサー内で、粉体急結剤の
構成材料の混合時に噴霧添加することが好ましい。噴霧
ではなく、液状物質を滴下又は流下させた場合、液状物
質と粉末の混合が不充分となりやすく、噴霧した場合に
比べて液体と粉末の混合により多くのエネルギーを要
し、混合が不充分となった場合には粉塵低減効果が低下
するため好ましくない。また、液状物質は粉体急結剤の
全構成材料の混合時に噴霧添加するのが、粉塵低減効果
及び急結性能の点から好ましい。In the present invention, as a method of incorporating the liquid substance into the powder quick-setting admixture, it is preferable to add it by spraying in the mixer at the time of mixing the constituent materials of the powder quick-setting admixture. When the liquid substance is dropped or allowed to flow down instead of being sprayed, the liquid substance and the powder are likely to be insufficiently mixed, and more energy is required to mix the liquid and the powder as compared with the case of being sprayed, and the mixing is insufficient. If this happens, the dust reduction effect will decrease, which is not preferable. In addition, it is preferable to add the liquid substance by spraying at the time of mixing all the constituent materials of the powder quick-setting agent, from the viewpoints of dust reduction effect and quick-setting performance.
【００２０】本発明でいうコンクリートとは、少なくと
もセメント、水及び骨材を混合したものをいい、一般の
コンクリート、高強度型コンクリート（大断面トンネル
の吹付け用）等のコンクリートのほかにモルタルを含む
ものである。また、通常コンクリートに用いられてい
る、減水剤、高性能減水剤、ＡＥ減水剤、流動化剤等の
分散剤、炭素繊維、アラミド繊維、有機繊維、金属ファ
イバー等の繊維（ファイバー）、収縮低減剤、急硬材や
遅延剤等の凝結時間調整剤、膨張材、防錆剤、防凍剤、
着色材、水和熱抑制剤、増粘剤、保水剤、防水剤、発泡
剤、起泡剤、消泡剤、アルカリ骨材反応抑制剤、フィラ
ー、ＡＥ剤、水中不分離性混和剤等の混和剤や混和材等
を１種又は２種以上を用いることもできる。The concrete referred to in the present invention means a mixture of at least cement, water and aggregate. In addition to concrete such as general concrete and high strength concrete (for spraying large section tunnels), mortar is also used. It includes. In addition, water-reducing agents, high-performance water-reducing agents, AE water-reducing agents, dispersants such as superplasticizers, carbon fibers, aramid fibers, organic fibers, metal fibers and other fibers that are commonly used in concrete, and shrinkage reduction. Agent, setting agent for setting time such as quick hardening material and retarder, swelling material, rust preventive, antifreeze,
Colorants, heat of hydration inhibitors, thickeners, water retention agents, waterproofing agents, foaming agents, foaming agents, defoaming agents, alkaline aggregate reaction inhibitors, fillers, AE agents, water inseparable admixtures, etc. It is also possible to use one kind or two or more kinds of admixtures and admixtures.
【００２１】セメントとしては、普通、早強、中庸熱、
低熱ポルトランドセメント等のポルトランドセメント
や、高炉セメント、フライアッシュセメント等の混合セ
メントを使用することができる。また、前記セメントの
一部を石灰石粉末やシリカヒュームで置換したセメント
や、前記セメントに石膏、凝結時間調整剤等の各種混和
材（剤）を添加したセメントも使用することができる。As cement, normal strength, early strength, moderate heat,
Portland cements such as low heat Portland cements and mixed cements such as blast furnace cements and fly ash cements can be used. Further, a cement obtained by substituting a part of the cement with limestone powder or silica fume, or a cement obtained by adding various admixtures (agents) such as gypsum and a setting time adjusting agent to the cement can also be used.
【００２２】高性能減水剤としては、アルキルアリルス
ルホン酸系、ナフタレンスルホン酸系、メラミンスルホ
ン酸系、ポリカルボン酸系等の高性能減水剤（高性能Ａ
Ｅ減水剤も含む）を用いることが出来、コンクリートの
強度を高める場合に用いたほうが良い。高性能減水剤
（高性能ＡＥ減水剤）としては、液状又は粉末状どちら
でも使用可能である。As the high performance water reducing agent, a high performance water reducing agent such as alkylallyl sulfonic acid type, naphthalene sulfonic acid type, melamine sulfonic acid type, polycarboxylic acid type (high performance A
E water reducing agent is also included), and it is better to use it when increasing the strength of concrete. As the high-performance water reducing agent (high-performance AE water reducing agent), either liquid or powder form can be used.
【００２３】骨材としては、川砂、海砂、山砂、砕砂、
川砂利、海砂利、山砂利、砕石、スラグ骨材等が挙げら
れ、これらの混合物を用いてもよい。As the aggregate, river sand, sea sand, mountain sand, crushed sand,
Examples thereof include river gravel, sea gravel, mountain gravel, crushed stone, and slag aggregate, and a mixture thereof may be used.
【００２４】ベースコンクリートの調製方法は、特に限
定するものではなく、生コン工場や工事現場に設置した
慣用のミキサーで混合すれば良い。The method for preparing the base concrete is not particularly limited, and it may be mixed with a conventional mixer installed in a ready-mixed concrete factory or a construction site.
【００２５】また、吹付けコンクリートの施工方法につ
いては、従来より行われている湿式工法、乾式工法、Ｓ
ＥＣ工法を任意に適用することができる。吹付け装置、
及び、急結剤添加装置も、粉体急結剤用として従来より
用いられている装置を任意に適用することができる。Regarding the construction method of shotcrete, the conventional wet method, dry method, S
The EC method can be applied arbitrarily. Spraying device,
Also, as the quick-setting agent adding apparatus, any apparatus conventionally used for powder quick-setting agents can be arbitrarily applied.
【００２６】[0026]
【実施例】以下、実施例により本発明を説明する。
１．使用材料
セメント；普通ポルトランドセメント（太平洋セメント
（株）製）
高性能減水剤；ポリカルボン酸系高性能減水剤「NT-100
0HX2」（（株）エヌエムビー製）
細骨材；北九州市小倉南区産砕砂（比重：2.69）：長崎
県壱岐郡郷ノ浦沖合海砂（比重：2.59）＝３：７（重量
比）混合品
粗骨材；北九州市門司区鹿喰産砕石（比重：2.80）
水；水道水
粉体急結剤；
（１）：カルシウムアルミネート系急結剤「ショットマ
スター」（太平洋マテリアル（株）製、一般の吹付けコ
ンクリート用）
（２）：カルシウムアルミネート系急結剤「ショットマ
スターＨ」（太平洋マテリアル（株）製、高強度型吹付
けコンクリート用）
急結剤添加用の液状物質；
ａ：ジエチレングリコール（水の含有率0.0重量％、以
下同じ）
ｂ：ジエチレングリコール（1.0重量％）
ｃ：トリエチレングリコール（0.0重量％）
ｄ：エチルアルコールのプロピレンオキサイド付加物
（平均分子量：200）（0.0重量％）
ｅ：流動パラフィン（40℃、粘度70mm2／ｓ）（0.0重量
％）
ｆ：鉱油（ナフテン系炭化水素を主成分とする自動車潤
滑油）90重量％／乳化剤（ポリオキシエチレンドデシル
エーテル）10重量％（0.0重量％）
ｇ：ａ50重量％／ｆ50重量％EXAMPLES The present invention will be described below with reference to examples. 1. Materials used Cement: Ordinary Portland cement (manufactured by Taiheiyo Cement Co., Ltd.) High performance water reducing agent: Polycarboxylic acid high performance water reducing agent "NT-100"
0HX2 "(manufactured by NMB Co., Ltd.) Fine aggregate; crushed sand from Kokuraminami-ku, Kitakyushu City (specific gravity: 2.69): Offshore sea sand from Gonoura, Iki-gun, Nagasaki (specific gravity: 2.59) = 3: 7 (weight ratio) Aggregate: Crushed stone from Kakuro, Moji-ku, Kitakyushu City (Specific gravity: 2.80) Water; Tap water powder quick-setting agent; (1): Calcium aluminate quick-setting agent "Shotmaster" (manufactured by Taiheiyo Material Co. Ltd. (2): Calcium aluminate type quick setting agent "Shotmaster H" (for Taiheiyo Material Co., Ltd., high strength type spraying concrete) Liquid substance for adding quick setting agent; a: Diethylene glycol (Water content 0.0% by weight, same below) b: Diethylene glycol (1.0% by weight) c: Triethylene glycol (0.0% by weight) d: Propylene oxide adduct of ethyl alcohol (average molecular weight: 200) (0.0% by weight) %) E: Liquid paraffin (40 ° C., viscosity 70 mm 2 / s) (0.0% by weight) f: Mineral oil (automotive lubricating oil whose main component is naphthene hydrocarbon) 90% by weight / emulsifier (polyoxyethylene dodecyl ether) ) 10% by weight (0.0% by weight) g: a50% by weight / f50% by weight
【００２７】２．粉体急結剤の製造方法
ミキサー内で、急結剤の全構成材料に上記液体を噴霧し
ながら混合した。2. Method for producing powder quick-setting admixture In a mixer, all the constituent materials of the quick-setting admixture were mixed while spraying the above liquid.
【００２８】３．急結剤・粉塵量はコンクリートを用い
て、模擬トンネルにおいて評価した。ベースコンクリー
トの配合を表１、液体添加剤の種類・添加量及び粉体急
結剤の種類・添加量等を表２に示す。ベースコンクリー
トの混練は、２軸強制練りミキサー（２．５m3）を用い
て、一般の吹付けコンクリートは４５秒、高強度型では
６０秒間混練した。3. The amount of quick-setting agent and the amount of dust were evaluated in a simulated tunnel using concrete. Table 1 shows the composition of the base concrete, and Table 2 shows the type and amount of the liquid additive and the type and amount of the powder quick setting agent. The base concrete was kneaded using a biaxial forced kneading mixer (2.5 m 3 ) for 45 seconds for general sprayed concrete and 60 seconds for high strength type concrete.
【００２９】[0029]
【表１】 [Table 1]
【００３０】[0030]
【表２】 [Table 2]
【００３１】表１のベースコンクリートに表２に示す種
類および量の粉体急結剤を添加し、シートで閉鎖し無風
状態とした模擬トンネル内で吹付けを行い、トンネル吹
付け面の正面で距離７ｍ位置での粉塵量を測定した。な
お、吹付け速度及び１回の吹付け時間は１０m3／hr×１
０分間とした。吹付け装置として、スギウエエンジニア
リング（株）製スイングエースを、急結剤の供給装置と
して太平洋マテリアル（株）製Ｔ−クリートを用いた。The type and amount of the powder quick-setting admixture shown in Table 2 was added to the base concrete shown in Table 1, and spraying was performed in a simulated tunnel which was closed with a sheet and kept in a windless state. The dust amount was measured at a distance of 7 m. The spraying speed and one spraying time are 10 m 3 / hr x 1
It was set to 0 minutes. Swing Ace manufactured by Sugiue Engineering Co., Ltd. was used as the spraying device, and T-cleat manufactured by Taiheiyo Material Co., Ltd. was used as the device for supplying the quick-setting agent.
【００３２】上記吹付けコンクリートに対して以下の
１）〜３）の特性を測定した。
１）急結性；吹付け直後のコンクリートの状態を指蝕に
より調べ、握り潰せない場合を○、握り潰せる場合を×
とした。
２）粉塵量；粉塵濃度計を用いて、前述の測定条件に
て、模擬トンネル内の粉塵濃度を測定した。
３）急結剤供給装置での圧送性；吹付け時の急結剤使用
量を測定し、所定の添加率（表２）での吹付けが可能で
あった場合を○、所定の添加率での吹付けができなかっ
た場合を×とした。それらの結果を表３に示す。The properties 1) to 3) below were measured for the above shotcrete. 1) Quick setting property: The condition of concrete immediately after spraying is examined by finger erosion, and ○ indicates that it cannot be crushed, and × indicates that it can be crushed.
And 2) Dust amount: Using a dust concentration meter, the dust concentration in the simulated tunnel was measured under the above measurement conditions. 3) Pressurizing property with the quick-setting agent supply device: The amount of the quick-setting agent used at the time of spraying was measured, and ○ when the spraying at the predetermined addition rate (Table 2) was possible, the predetermined addition rate The case where the spraying was not possible was marked with x. The results are shown in Table 3.
【００３３】[0033]
【表３】 [Table 3]
【００３４】表３から明らかなように、本発明における
急結剤を使用した場合、充分な急結性及び圧送性を維持
したまま、粉塵量を大幅に下げることができた（実施例
１〜１１）。一方、粉体急結剤中に前記液状物質を含ん
でいないものは、粉塵量の発生量が多かった（比較例１
〜２）。As is clear from Table 3, when the quick-setting admixture of the present invention was used, the amount of dust could be significantly reduced while maintaining sufficient quick-setting property and pumping property (Examples 1 to 1). 11). On the other hand, those in which the liquid substance was not contained in the powder quick-setting admixture produced a large amount of dust (Comparative Example 1).
~ 2).
【００３５】[0035]
【発明の効果】吹付け工法において、特定の液状物質を
含有する粉体急結剤を用いることによって、吹付けコン
クリートの急結性及び急結剤の圧送性を変化させること
なく、粉塵発生量を低減することができる。EFFECTS OF THE INVENTION In the spraying method, by using a powder quick-setting admixture containing a specific liquid substance, the amount of dust generated can be changed without changing the quick-setting property of sprayed concrete and the pumping property of the quick-setting admixture. Can be reduced.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） // Ｃ０４Ｂ 103:12 Ｃ０４Ｂ 103:12 103:40 103:40 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) // C04B 103: 12 C04B 103: 12 103: 40 103: 40
Claims (3)
グリコール、低級アルコールのアルキレンオキサイド付
加物、流動パラフィン及び油乳化剤混合物の群から選ば
れる１種又は２種以上の液状物質を含有することを特徴
とする吹付けコンクリート用粉体急結剤。1. A spray comprising one or more liquid substances selected from the group of alkylene glycol, polyalkylene glycol, alkylene oxide adduct of lower alcohol, liquid paraffin and oil emulsifier mixture. Powder quick setting agent for concrete.
る請求項１記載の吹付けコンクリート用粉体急結剤。2. The powder quick-setting admixture for shotcrete according to claim 1, wherein the content of the liquid substance is 1 to 12% by weight.
ト用粉体急結剤を用いることを特徴とする吹付けコンク
リートの施工方法。3. A method for constructing shotcrete using the powdered quick-setting admixture for shotcrete according to claim 1 or 2.