JP2003231352A - Ink-jet recording paper - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide ink-jet recording paper which is excellent in glossiness and an ink-jet recording aptitude and especially prevents damages (traveling trace, spur trace) to the surface of the paper by a feed roll installed in the conveyance section in an ink-jet printer from standing out. <P>SOLUTION: In the ink-jet recording paper, at least one recording layer containing amorphous silica, zeolite and/or aluminum oxide, and an adhesive resin is formed on a paper support at least 135.6 mJ in internal bond strength (Tappi UM403), containing pulp and baked kaolin 0.5-5 μm in average particle size and 5-50 m<SP>2</SP>/g in specific surface area and/or amorphous silica 1-50 μm in average particle size and 50-300 m<SP>2</SP>/g in specific surface area. A gloss layer at least 30% in 75 degree glossiness (JIS Z8741) containing the polymer at least 40°C is glass transition temperature of an ethylenically unsaturated monomer and colloidal silica is formed on the recording layer. <P>COPYRIGHT: (C)2003,JPO

Description

Detailed Description of the Invention

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink jet recording paper having excellent gloss and ink jet recording suitability, and in particular, damage to the paper surface (running traces, spur traces) caused by a paper feed roll installed in a conveyance section of an ink jet printer. The present invention relates to an inconspicuous inkjet recording paper.

[0002]

2. Description of the Related Art Recording by an inkjet printer is
It is used in various fields due to its low noise, high-speed recording, and easy multicoloring. As the ink jet recording paper, high-quality paper designed so as to have high ink absorbability, coated paper having a surface coated with a porous pigment, and the like are applied. For example, Japanese Unexamined Patent Publication (Kokai) No. 62-158084 discloses a method for producing ink jet recording paper having high ink absorbency and high color development using fine particle synthetic silica. However, since all of these papers are mainly so-called matte ink jet recording papers with low surface gloss, it is impossible to obtain photographic full color recording. Therefore, in recent years, an inkjet recording paper having a high surface gloss and an excellent appearance has been demanded.

Generally, as a paper having a high surface gloss, a coated paper having a glossy surface coated with a plate-like pigment and, if necessary, a calendar treatment, or a wet coating layer having a mirror surface is used. There is known a so-called cast coated paper obtained by copying the mirror surface of the heating drum surface by pressure bonding and drying. This cast coated paper has high surface gloss and better surface smoothness compared to super calendered ordinary coated paper,
Since it has an excellent printing effect, it is mainly used for high-grade printed matter and the like, but when it is used for ink jet recording paper, it has various problems. That is, generally, a conventional cast coated paper is disclosed in US Pat.
No. 6 (Patent Document 1). A film-forming substance such as an adhesive in the pigment composition forming the coating layer gives a high gloss by copying the mirror surface of the cast coater. On the other hand, the presence of this film-forming substance causes the coating layer to lose its porosity, resulting in a problem that ink absorption during ink jet recording is extremely reduced. In order to improve the ink absorbability, it is important to make the cast coating layer porous so that the ink can be easily absorbed. For that purpose, it is necessary to reduce the film forming property. Reducing the amount of membranous material results in lower white paper gloss. As described above, it was extremely difficult to satisfy both the surface gloss of the cast coated paper and the suitability for inkjet recording at the same time.

As a method for solving the above problems, a glass transition point of 40 ° C. or higher obtained by polymerizing a monomer having an ethylenically unsaturated bond on a base paper provided with an undercoating layer containing a pigment and an adhesive as main components. A coating liquid having a copolymer composition as a main component is applied to form a coating layer for casting, and the coating layer for casting is pressed and dried on a mirror surface drum heated while the coating layer is in a wet state. By finishing,
The present inventors have found that a cast paper for inkjet recording having both excellent gloss and ink absorbency can be obtained, and proposed it as JP-A-7-89220 (Patent Document 2).
By the above-mentioned technology, a recording sheet having excellent surface gloss and ink jet recording suitability has been obtained. However, a recording sheet having excellent surface gloss, specifically, 75 ° glossiness (JIS Z8741) of the surface is 30% or more. In the case of a recording sheet, there is a problem in that damage to the surface of the paper (hereinafter referred to as spur trace) due to spurs of the gears of the paper feed roll, which is installed in the transport section of the inkjet printer, is visually noticeable. In particular, in recent years, due to the high definition of printers, it has become possible to obtain photographic images, but in this case, in order to improve the transport accuracy of the printer, the number of spurs such as gears attached to the transport roll after printing is increased. Tend to increase,
The current situation is that spur marks are becoming more noticeable.

[0005]

[Patent Document 1] US Pat. No. 5,275,846

[Patent Document 2] JP-A-7-89220

[0006]

The printed recording medium is conveyed from the printing surface side while being pressed by, for example, a metal gear (spur). The printed part swells with the ink, and the spur hits the softened part of the recording material, leaving a mark. The present invention solves such problems, and provides an inkjet recording paper excellent in inkjet recording suitability such as gloss and print density, ink absorbency, and recording image quality.

[0007]

An ink jet recording paper of the present invention comprises a paper support and a paper support formed on the paper support.
An inkjet recording paper having at least one recording layer containing a pigment selected from amorphous silica, zeolite, and aluminum oxide and an adhesive resin, and a gloss layer formed on the recording layer, (1) The paper support contains pulp, and further, calcined kaolin having an average particle size of 0.5 to ⁵ μm and a specific surface area of 5 to 50 m ² / g, or an average particle size of 1 to 50 μm and 50 to 50 μm. 300 m ²
1 to 15% by weight of amorphous silica having a specific surface area of / g
Of the above-mentioned paper support,
The internal bond strength measured according to M403 is 135.
Polymer composition of 6 mJ (100 × 10 ⁻³ ft-lb) or more, (2) the gloss layer is obtained by polymerizing a monomer having an ethylenically unsaturated bond, and has a glass transition point of 40 ° C. or more. And a colloidal silica pigment having an average particle size of 0.01 to 5 μm, and (3) the recording side surface of the recording paper has a 75 ° gloss value of 30% measured according to JIS Z 8741. The above is the feature.

In the ink jet recording paper of the present invention, the internal bond strength of the paper support is 135.6 mJ (10
0 × 10 ^-3 ft-lb) or more 406.8 mJ (300 × 10 ^-3)
ft-lb) or less is preferable. In the inkjet recording paper of the present invention, the gloss layer is coated on the paper support with a coating liquid containing the resin and colloidal silica, and is dried while the coating layer is in a wet state. After rewetting, the wet coating layer is preferably formed by press-contact drying with a heated mirror surface drum. In the inkjet recording paper of the present invention, the freeness (CSF) of the pulp contained in the paper support is 30.
It is preferably 0 to 450 ml.

[0009]

BEST MODE FOR CARRYING OUT THE INVENTION The base paper used as the paper support in the present invention contains pulp such as wood as a main component, and the Z-axis strength of the paper support, that is, the internal bond strength, is 135.6 mJ.
It is characterized by being (100 × 10 ⁻³ ft-lb) or more. Z-axis strength is 203.4 mJ (150 × 10 ^-3 ft-lb)
The above is more preferable. The Z-axis strength is obtained by measuring the average energy required to separate the paper into two layers, and the specific measuring method is shown in TappiUM403. The upper limit is not specified, but 406.8 mJ (3
If it exceeds 00 × 10 ⁻³ ft-lb), the effect is saturated, and print blurring, cockling, curling and the like may be deteriorated. As a result of repeated studies to reduce the spur mark, the present inventors have found that there is a correlation between the Z-axis strength of the base paper and the level of the spur mark. That is, the surface 75 ° gloss (JIS
In the ink jet recording paper with Z8741) of 30% or more, it was revealed that the higher the Z-axis strength of the base paper, the less the occurrence of spur marks. The reason for this is considered to be that when ink-jet recording, the base paper swells and becomes flexible due to the ink, and spatter marks are easily attached to the printed part. However, when the base paper has high Z-axis strength, It is presumed that the bond is strong and the ink does not easily swell even if it penetrates.

The pulp used as the main component of the base paper is chemical pulp such as LBKP or NBKP, GP, TM.
Examples include mechanical pulp such as P and waste paper pulp such as DIP. Generally, the lower the pulp freeness (CSF), the higher the Z-axis strength of the base paper. However, if the freeness (CSF) is too low (for example, less than 300 ml), cockling (unevenness due to swelling of the printed portion) after printing is deteriorated, and drainage is further reduced, which impairs operability in the papermaking process. In addition, it may be difficult to control the curl of the manufactured base paper. Further, since the air permeability of the base paper is lowered, it becomes difficult for the water to escape when the coating is carried out by the cast method, and the paper becomes rough and the operability is remarkably lowered.

JISP-812 of pulp used for base paper
Freeness (CSF) defined in 1 is 300 to 45
0 ml is preferred. The freeness is more preferably 350 to 440 ml. The reason for this is presumed that when the pulp freeness is 450 ml or less, the softening and fibrillation of the pulp progresses to strengthen the fiber-fiber bond of the base paper and make it difficult for the ink to permeate and swell. . However, if the freeness is less than 300 ml, cockling after printing (unevenness due to partial swelling of the printed part) deteriorates, and drainage decreases, which may impair operability in the papermaking process. It may be difficult to control the curl of the formed base paper. Further, since the air permeability of the base paper is lowered, when the coating is carried out by the cast method, it is difficult for the water to escape, and the paper may be rough or the operability may be significantly lowered.

Freeness can be adjusted by beating. Beating has a function of softening and fibrillating pulp fibers by mechanical means (to loosen the pulp surface and the inside to make fine fibers) and increase the bond between pulp fibers of paper. Generally, a beater, a Jordan, a conical refiner, a drum refiner, a disc refiner, or other beating apparatus is used. Freeness is adjusted by the energy required for processing in the beater. Generally, the more the beating energy is applied, the lower the freeness (CSF) is.

In addition to pulp, pigments (fillers), adhesives, sizing agents, fixing agents, retention aids, cationizing agents, paper strength enhancers, dyes, optical brighteners, etc. are appropriately used as raw paper materials. To be done. Amorphous silica and calcined kaolin are used as pigments, and these are blended for the purpose of imparting opacity, preventing backing of ink, imparting ink absorbability, and the like. That is, amorphous silica and calcined kaolin are effective for the purpose of imparting ink absorbency. Especially as amorphous silica, the average particle size is 1 to 50 μm and the specific surface area is 50 to 30.
0m ² / g, calcined kaolin has an average particle size of 0.5
-5 μm and a specific surface area of 5-50 m ² / g are used.

However, in the base paper for a support of the ink jet recording paper of the present invention, if the blending amount of the pigment is too large, the interlaminar strength tends to decrease. On the other hand, when the amount of the pigment blended is small, the interlayer strength tends to improve, the swelling of the base paper due to the ink is suppressed, and spur marks are less likely to form,
Since the ink absorbability may decrease, printing blurring or unevenness may occur, and ink strike-through (show-through) may become noticeable, so it is necessary to make an appropriate adjustment. When the pigment is silica or calcined kaolin, the content thereof is 1 to 15% by weight, preferably 2 to 8% by weight, as a content with respect to the base paper (paper support), for the reasons described above. The pigment content relative to the base paper can be determined by measuring the ash content of the base paper. The base paper can be coated and impregnated with starch, polyvinyl alcohol, a cationic resin, or the like by a size press or the like to improve the surface strength or adjust the penetration of the coating layer.
Further, it is preferable to smooth the surface of the base paper with a calendar or the like because the coating layer can be uniformly formed.

The swelling of the base paper can be suppressed by suppressing the ink penetration by blending a sizing agent or the like into the base paper or providing a barrier layer on the surface of the base paper. The absorption capacity is likely to decrease, the ink is likely to bleed, and uneven density is likely to occur, resulting in poor image quality. The sizing degree is preferably about 1 to 100 seconds, more preferably about 2 to 50 seconds, based on 100 g / m ² of paper. As described above, generally, the lower the freeness (CSF) of pulp and the smaller the amount of the internally added pigment, the higher the Z-axis strength of the base paper tends to be. Further, the Z-axis strength is increased by blending the paper strength enhancer.
Examples of the paper strength enhancer include starch, cationized starch, vegetable gum, polyacrylamide resin, polyamide epichlorohydrin resin and the like. Further, when the surface of the raw paper is subjected to size press treatment with a polymer such as starch or polyvinyl alcohol, the interlaminar strength tends to increase due to the impregnation of the material.

The recording layer provided on the base paper will be described. The recording layer contains a pigment and an adhesive. On the recording layer itself,
A glossing treatment may be performed by casting finish, super calendar treatment, or the like, but a glossy layer containing a resin and a pigment as a main component may be provided on the recording layer.
As the pigment to be contained in the recording layer, amorphous silica (including colloidal silica), zeolite and aluminum oxide may be used alone or in combination of two or more kinds.

Amorphous silica, zeolite and aluminum oxide are excellent in ink absorbency, and it is particularly preferable to contain amorphous silica as the main component of the pigment. As the amorphous silica, synthetic amorphous silica is preferable. Synthetic amorphous silica is roughly classified into a wet method and a dry method depending on the production method. The wet method can be obtained by using sodium silicate as a raw material to neutralize with an acid to precipitate silica, and is further divided into a precipitation method and a gelation method. Further, the dry method uses silicon tetrachloride as a raw material, hydrogen,
It is obtained by burning with oxygen to precipitate silica.
It is usually called white carbon, and is known as silicic acid anhydride, silicic acid hydrate, and the like. The average secondary particle size of the synthetic amorphous silica is preferably about 0.5 to 20 μm. Further, for the purpose of absorbing ink, it is desirable that the oil absorption amount and the BET type specific surface area are high, but if it is too high, the viscosity of the coating composition may be too high, and the oil absorption amount is generally 10
0 ~ 400ml / 100g, BET specific surface area is 1
It is preferably about 00 to 500 m ² .

Examples of the adhesive include proteins such as casein, soybean protein and synthetic protein, and various starches such as starch and oxidized starch,
Polyvinyl alcohol, cellulose derivatives such as carboxymethyl cellulose and methyl cellulose, styrene-butadiene copolymer, methyl methacrylate-butadiene copolymer conjugated diene polymer latex, acrylic polymer latex, ethylene-vinyl acetate copolymer vinyl, etc. Conventionally known adhesives which are generally used for coated papers such as polymer latex are used alone or in combination. The amount of the adhesive compounded is not particularly limited, but is adjusted to 1 to 100 parts by weight, more preferably 2 to 50 parts by weight, relative to 100 parts by weight of the pigment. If the amount of the adhesive is small, the strength of the recording layer may be weakened, the surface may be easily scratched, and powder may drop. On the other hand, if the amount of the adhesive is large, the ink absorbency is lowered, and the desired inkjet recording suitability may not be obtained.

The recording layer may contain a cationic compound for the purpose of fixing the dye component in the ink, increasing the print density and imparting print water resistance. Examples of the cationic compound include cationic resins and low molecular weight cationic compounds (for example, cationic surfactants). A cationic resin is preferable from the viewpoint of the effect of improving the print density, and it can be used as a water-soluble resin or an emulsion. Further, it can be used as a cationic organic pigment in which a cationic resin is insolubilized by a means such as crosslinking to give a particulate form. Such a cationic pigment has a functional group (hydroxyl group, carboxyl group, amino group, acetoacetyl group, etc.) that reacts with a polyfunctional monomer to form a crosslinked resin when polymerizing a cationic resin. A cross-linking resin is added to the cation resin as necessary, and the cross-linking resin is formed by means of heat, radiation or the like. Cationic compounds, especially cationic resins, may also serve as adhesives.

The following can be exemplified as the cationic resin. Specifically, 1) polyalkylene polyamines such as polyethylene polyamine and polypropylene polyamine or derivatives thereof, 2) acrylic resin having secondary amine group, tertiary amine group or quaternary ammonium group, 3)
Polyvinylamine, polyvinylamidines, 4) dicyan-based cationic resin typified by dicyandiamide-formalin polycondensate, 5) polyamine-based cationic resin typified by dicyandiamide-diethylenetriamine polycondensate, 6) epichlorohydrin-dimethylamine addition polymer , 7) Dimethyldiallylammonium chloride-S
0 ₂ copolymer, 8) diallylamine salt -S0 ₂ copolymer, 9) dimethyldiallylammonium chloride polymer, 10) polymers of allylamine salts, 11) dialkylaminoethyl (meth) acrylate quaternary salt polymer, 1
2) Cationic compounds such as acrylamide-diallylamine salt copolymer. The cationic compound is 1 to 10 with respect to 100 parts by weight of the pigment.
It can be used in an amount of 0 part by weight, more preferably 5 to 50 parts by weight. If the blending amount is small, it is difficult to obtain the effect of improving the print density, and if the blending amount is large, the print density is decreased,
Image blurring may occur.

In addition, various auxiliaries such as a dispersant, a thickener, an antifoaming agent, a colorant, an antistatic agent and a preservative used in the production of general coated paper are appropriately added. A recording layer composition composed of the above materials generally has a solid content concentration of 5 to 5.
Adjusted to about 65% by weight, basis weight of about 20-400 g / m
1 to 50 g / m ² by dry weight on about ^two substrates, and more preferably a blade coater so that the order of 2 to 20 g / m ^2, an air knife coater, roll coater, brush coater, champflex coater, a bar coater Coating and drying are carried out by various publicly known coating devices such as a gravure coater. Further, if necessary, smoothing treatment such as super calendering and brushing can be performed after the recording layer is dried.

Next, a gloss layer is further provided on the recording layer containing the above-mentioned pigment and adhesive as the main components. This glossy layer is configured to contain a resin and, if necessary, a pigment. It is preferable that the gloss layer is porous or liquid-permeable so that the ink can quickly pass therethrough as long as the gloss is not hindered. In order to do this, it is advisable to add a pigment or select a drying condition such that the resin is not completely formed into a film within a range that does not reduce the gloss. When a pigment is added to the gloss layer, colloidal silica, which is excellent in terms of gloss, transparency and ink absorbability, is used, and its average particle size is 0.01
˜5 μm, preferably 0.05 to 1 μm.
If the particle size is less than 0.01 μm, the effect of improving ink absorbency is poor, and if it exceeds 5 μm, gloss and print density may decrease.

When colloidal silica is used, the gloss layer is excellent in ink absorbency and transparency. Therefore, when a cationic compound is blended in the gloss layer, the ink dye is efficiently fixed to the gloss layer to improve the transparency of the gloss layer. Together, they tend to produce very good print density.

As the resin of the gloss layer, a polymer resin obtained by polymerizing a monomer having an ethylenically unsaturated bond is used. Examples of the polymer composition obtained by polymerizing a monomer having an ethylenically unsaturated bond (hereinafter referred to as an ethylenic monomer) include methyl acrylate, ethyl acrylate, butyl acrylate, 2 ethylhexyl acrylate, lauryl acrylate, 2-hydroxyethyl acrylate, Alkyl group such as glycidyl acrylate having 1 to 18 carbon atoms, alkyl methacrylate such as methyl methacrylate, ethyl methacrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate, glycidyl methacrylate having 1 to 18 carbon atoms Methacrylic acid ester, styrene, α
-Methylstyrene, vinyltoluene, acrylonitrile, vinyl chloride, vinylidene chloride, vinyl acetate, vinyl propionate, acrylamide, N-methylolacrylamide, ethylene, butadiene, acrylic acid, methacrylic acid and other heavy monomers obtained by polymerization An example is coalescence.

The polymer may be a copolymer in which two or more kinds of ethylenic monomers are used in combination, if necessary, and may be a substituted derivative of these polymers or copolymers. Further, the above-mentioned ethylenic monomer is polymerized in the presence of colloidal silica, and Si—O—R (R:
(Polymer component) A functional group capable of reacting with colloidal silica such as SiOH group is introduced into the complex or the above-mentioned polymer or copolymer, and then reacted with the colloidal silica to form a complex. It is also possible to use it as it is. When this composite is used, it tends to have excellent gloss and ink absorbability, and when the casting method described below is used, it also tends to have excellent releasability from the cast drum. Although the composite particles are not particularly limited, for example, the average particle size is about 30 to 150 nm.

The above (co) polymer composition preferably has a glass transition point of 40 ° C. or higher, and 50 to 100 ° C.
Is more desirable. If the glass transition point is low, film formation will proceed excessively during drying, and the porosity of the surface will decrease, which may result in a decrease in the ink absorption rate. Also, the drying temperature is important, and if the drying temperature is too high, the film formation proceeds too much, and the surface porosity decreases, resulting in a decrease in the ink absorption rate. Conversely, if the drying temperature is too low, the gloss is poor. And the productivity will decrease. As a method of providing the glossy layer, a coating liquid containing a resin and, if necessary, a pigment as a main component may be applied onto the recording layer, and a smoothing treatment may be performed with a super calendar or the like. However, it is preferable to apply a coating liquid composed mainly of a resin and, if necessary, a pigment as a main component, and then press-contact and dry the heated mirror surface drum while the coating layer is in a wet state to finish. Method (wet cast method), or method in which the coating layer is once dried and re-wetted, then pressed against a heated mirror surface drum and dried (rewet cast method)
However, it is preferable because an inkjet recording paper having both excellent gloss and ink absorbency can be obtained. The temperature of the heated mirror drum is, for example, 50 to 150 ° C., preferably 70.
~ 120 ° C.

Further, a heated mirror drum is directly coated with a coating liquid containing a resin and optionally a pigment, and the recording layer is formed while the coating layer is in a wet state to some extent. It is also possible to adopt a method (precast method) of finishing by pressing and drying a base material provided in advance. Furthermore, a coating liquid containing a resin and, if necessary, a pigment is applied onto a smooth film or sheet, and the coating layer or the recording layer surface to be laminated is in a wet state to some extent. In the meantime, it is also possible to employ a method (film transfer method) in which a smooth film or sheet is pressed and dried on a base material and then peeled off to finish. In the coating composition for the gloss layer, pigments, defoaming agents, colorants, antistatic agents used for general printing coated paper and inkjet paper are used to adjust whiteness, viscosity, fluidity, etc. Various auxiliaries such as agents, preservatives and dispersants, and thickeners are appropriately added. In addition, it is possible to add a cationic resin to the ink to fix the ink dye to the gloss layer.

When the above-mentioned gloss layer coating liquid is coated on the recording layer, a blade coater, an air knife coater,
Various known coating devices such as roll coater, brush coater, champlex coater, bar coater and gravure coater can be used. After that, preferably, as described above, while the coating layer is in a wet state, or after once dried and re-wetted, it is pressed against a heated mirror surface drum and dried to perform cast finishing. In this case, the coating amount of the gloss layer coating liquid is 0.2 to 30 g / m ² , preferably 1 to 10 g / m ² in terms of dry solid content. Where 0.2 g / m
^If it is less than ² , the gloss may not be sufficient, and 30 g / m
^If it exceeds ² , the ink drying property may be deteriorated or the recording density may be lowered. After providing the glossy layer, smoothing treatment can be further performed by a super calendar or the like.

According to the present invention, a recording material having excellent glossiness can be obtained, but the recording surface has a 75 ° glossiness (JIS Z).
8741) is 30% or more, which makes it possible to obtain excellent image quality and photographic-quality high-quality recording. The glossiness is preferably 40% or more, more preferably 65% or more. There is no particular upper limit, but it is 95%, for example.

[0030]

The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to these examples.
Unless otherwise specified, parts and% in the examples represent parts by weight and% by weight, respectively. Examples 1 to 9, Comparative Examples 1 and 2, 100 parts of hardwood kraft pulp, calcined kaolin (average particle size 1 μm, specific surface area 18 m ² / g, Ansilex; Engelhard Mineral Co., Ltd.) 0 to 30 parts, commercially available sizing agent. A base paper having a basis weight of 100 g / m ² was made into a paper by a base paper prescription consisting of 2 parts, starch (tapioca) 0.75 part, wet paper strengthening agent 0.5 part, and sulfuric acid band 1.5 parts. Pulp fleenase (CSF: used in each Example and Comparative Example)
JISP-8121) is shown in Table 1. The calcined kaolin was blended so that the ash content would be the value shown in Table 1. Next, as a pigment, amorphous silica (specific surface area 340 m ² /
g, average secondary particle diameter 4.5 μm, trade name; Fineseal X-45, manufactured by Tokuyama Corporation, 100 parts, silyl-modified polyvinyl alcohol (R1130: manufactured by Kuraray Co., Ltd.) 25 parts as an adhesive, cation 5 parts of dicyandiamide-based resin (Neofix E-117; Nichika Kagaku Co., Ltd.) as a cationic resin, and cationic acrylamide-based resin (SUMIRETS RESIN SR1001; Sumitomo Chemical Co., Ltd.)
15 parts) and 0.5 part of sodium polyphosphate as a dispersant were added to prepare a recording layer coating solution having a solid content concentration of 18%. This recording layer coating liquid was applied to one side of the above-mentioned base paper by an air knife coater so as to have a dry weight of 6 g / m ² and dried.

On the other hand, styrene-2 having a glass transition point of 75 ° C.
100 parts of a complex of methylhexyl acrylate copolymer and colloidal silica (copolymer and colloidal silica weight ratio: 50:50, composite particle size 80 nm), alkyl vinyl ether / maleic acid derivative copolymerization as thickening / dispersing agent A coating liquid for a glossy layer having a solid content of 25% was prepared, which was composed of 5 parts of coalescence and 2 parts of lecithin as a release agent. This gloss layer coating liquid is applied onto the above recording layer using a roll coater, and immediately thereafter, it is pressed against a mirror surface drum having a surface temperature of 80 ° C., dried, and then released from the recording layer, thereby producing a gloss type inkjet recording sheet. Got The coating amount of the gloss layer at this time was 6 g / m ² in terms of solid content weight.

Example 10 100 parts of hardwood kraft pulp (freeness CSF; 4
20 ml), amorphous synthetic silica (average secondary particle size 10 μ)
m, specific surface area 190 m ² / g, Tokusil GUN; made by Tokuyama) 4 parts, commercial size 0.2 parts, starch (tapioca) 0.75 parts, wet paper strength enhancer 0.5 part, sulfuric acid band 1.5 100 g / m ² basis weight based on the base paper prescription
The base paper of was made into paper. The ash content at this time was 3%. A recording layer and a gloss layer were provided in the same manner as in Examples 1 to 9 except that this base paper was used.

Comparative Example 3 Amorphous silica (average particle size 4.5 μm, trade name; Fineseal X-45, manufactured by Tokuyama Corp.) was used as a pigment.
00 parts, 25 parts of silyl-modified polyvinyl alcohol (R1130: manufactured by Kuraray Co., Ltd.) as an adhesive, and dicyandiamide resin (Neofix E as a cationic resin.
-117; 5 parts by Nichika Kagaku Co., Ltd., and a cationic acrylamide resin (Smilet's resin SR100)
1; Sumitomo Chemical Co., Ltd.) and 15 parts of sodium polyphosphate as a dispersant were added to prepare a recording layer coating solution having a solid content concentration of 18%. This recording layer coating liquid was used in Example 5
8 g / dry weight on one side of the same base paper as used in
An ink jet recording paper was obtained by coating with an air knife coater and drying so as to obtain m ² . No gloss layer is provided.

Comparative Example 4 The same base paper as that used in Example 5 was used as it was. Comparative Example 5 Commercially available gloss type inkjet recording film (H
G101: manufactured by Canon Inc. was used.

The ink jet recording suitability, white paper gloss and print storability of the thus obtained ink jet recording paper are summarized in Table 1. The above evaluation was carried out by the following method. [Z-axis strength, internal bond strength] Sisalkraft-SCOTT INTERNAL BOND TESTER MODEL-
Measured with B (TAPPI UM403). [Inkjet recording suitability] Printing was performed using an inkjet printer PM700C (manufactured by Seiko Epson Corp.). (Uniformity of Solid Printed Area) Printing unevenness (dark and light unevenness) of a solid printed area of two colors of cyan ink and magenta ink was visually evaluated. ◯: A good level with almost no printing unevenness. Δ: The printing unevenness is slightly conspicuous, which is a problem in practical use. X: Printing unevenness is noticeable.

(Bleeding of Ink) Solid printing of cyan ink and magenta ink was printed by bringing the boundaries into contact with each other, and the bleeding at the boundaries was evaluated. ○: Almost no bleeding is observed. ○-: Bleeding is slightly observed, but there is no practical problem. X: Bleeding is noticeable, which is a practical problem. (Dryability of ink) Cyan ink and magenta ink
The dryness of the ink was evaluated for the solid print portion of the color mixture. ◯: No stain at all even if touched with a finger immediately after printing. X: Soiled when touched with a finger immediately after printing. (Water resistance of printing) Characters were printed with black, cyan, magenta, and yellow inks, respectively, and 3 drops of water were dropped on the printed portion with a spid, and after 1 minute, the degree of printing bleeding was visually evaluated. A: Almost no change in printing. X: Printing is disturbed.

(Printing Density After Inkjet Recording) The printing density of a solid black printed portion was measured with Macbeth RD-914. (Spur Scratch) Solid printing of two colors of cyan ink and magenta ink was printed on the entire surface of an A4 size recording sheet, and the spur trace was visually evaluated. ◎: Almost no spur mark is seen. ○: Spur traces are slightly visible. ○-: Spur marks are slightly conspicuous, but there is no problem in practical use. Δ: Spur marks are slightly conspicuous, which is a practical problem. ×: The spur mark is tight.

[Cockling] Solid printing of a mixture of two colors of cyan ink and magenta ink was performed on the entire surface of an A4 size recording sheet, and cockling (wrinkles after printing) was visually evaluated. ○: Cockling is not noticeable. ○-: Cockling is slightly conspicuous, but is at a practically acceptable level. [White paper gloss] 75 of white paper according to JIS-P8142
° Gloss was measured.

[0039]

[Table 1]

[0040]

As is clear from the results of Table 1, the ink jet recording paper of the present invention was excellent in gloss and ink jet recording suitability and had no spur trace.

   ─────────────────────────────────────────────────── ─── Continued front page    (72) Inventor Masahiro Morie             Made by Oji 1-10-6 Shinonome, Koto-ku, Tokyo             Paper Co., Ltd. Shinonome Research Center (72) Inventor Masami Kubota             Made by Oji 1-10-6 Shinonome, Koto-ku, Tokyo             Paper Co., Ltd. Shinonome Research Center F-term (reference) 2C056 EA04 EA13 FC06                 2H086 BA01 BA13 BA21 BA32 BA33                       BA36 BA41 BA45

Claims (4)

[Claims] 1. A paper support, and at least one recording layer formed on the paper support and containing a pigment selected from amorphous silica, zeolite, and aluminum oxide and an adhesive resin. An inkjet recording paper having a gloss layer formed on a recording layer, wherein (1) the paper support contains pulp, and further 0.5
The average particle diameter and 5 to 50 m 1 to 15 weight amorphous silica having a specific surface area of calcined kaolin, or 1~50μm average particle diameter and 50 to 300 m ² / g of a specific surface area of ² / g of ~5μm %, And the internal bond strength of the paper support, measured according to Tappi UM403, is 135.6 mJ (100 × 10 ⁻³ ft-lb) or more, and (2) the gloss The layer comprises a polymer composition obtained by polymerizing a monomer having an ethylenically unsaturated bond and having a glass transition point of 40 ° C. or higher, and a colloidal silica pigment having an average particle size of 0.01 to 5 μm, (3) JIS Z on the recording side surface of the recording sheet
An inkjet recording paper having a 75 ° gloss value of 30% or more measured according to 8741. 2. The internal bond strength of the paper support is 135.
6mJ (100 × 10 ^-3ft-lb) or more 406.8mJ (30
0x10^-3ft-lb) or less.
Cudget recording paper. 3. The gloss layer is coated on the paper support with a coating liquid containing the resin and colloidal silica, and is dried and rewetted once while the coating layer is in a wet state. The inkjet recording paper according to claim 1, which is formed by pressing and drying the wet coating layer on a heated mirror surface drum. 4. The freeness (CSF) of the pulp contained in the paper support is 300 to 450 ml.
3. The inkjet recording sheet according to any one of 3 above.