JP2003171587A - Radiation-curable ink for forming peelable layer and sheet obtained by using the same - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a radiation-curable ink for forming a peelable layer which exhibits excellent suitability for a printing ink, can easily form a peelable layer exhibiting high peeling performances on a prescribed necessary part of a substrate by radiation-cure after applied by means of offset printing or the like and permits printing such as ink-jet ink printing, electrostatic printing and the like, writing, sealing and the like on the formed peelable layer, and a sheet obtained using the same which permits secondary entry or additional entry for secondary use. <P>SOLUTION: The radiation-curable ink for forming a peelable layer comprises a vehicle mainly composed of a radiation-curable component and a powder of a peelable substance incorporated therewith. <P>COPYRIGHT: (C)2003,JPO

Description

Detailed Description of the Invention

[0001]

TECHNICAL FIELD The present invention relates to a radiation-curable release layer forming ink and a sheet using the same.

[0002]

2. Description of the Related Art Conventionally, a sheet having a release layer in which a release agent is applied to a substrate has been widely used as a recording sheet for release paper, adhesive paper tape, delivery slips, etc., and a silicone release agent for forming the release layer. Water-based inks (including emulsion type) and UV-curable inks such as fluorinated release agents, alkyl pendant release agents, and long-chain alkyl release agents are used. However, since a sheet having such a release layer cannot be printed by inkjet ink, electrostatic printing or the like, writing, marking, etc., it is discarded as dust without being used secondarily. Linerless labels without release paper have also been commercialized, but printing was done in advance and secondary entry and additional entry were not possible.

[0003]

SUMMARY OF THE INVENTION The first object of the present invention is to solve the problems of the prior art, and since it is excellent in printing ink suitability, a base material is required by offset printing without using a special coating device. A release layer-forming ink capable of easily forming a release layer having a high release property at a predetermined location (partial printing or spot printing is possible), and an inkjet ink printing or electrostatic printing is performed on the formed release layer. It is an object of the present invention to provide a radiation-curable release layer forming ink capable of printing such as printing, writing, and marking. A second object of the present invention is to provide a sheet having a release layer formed using this radiation-curable release layer forming ink.

[0004]

Means for Solving the Problems As a result of intensive studies to solve the above-mentioned problems, the present inventors have used a vehicle mainly containing a radiation-curable component, and blended a peelable substance powder with this vehicle. They have found that the problem can be solved by using a radiation-curable release layer forming ink, and completed the present invention.

That is, the radiation-curable release layer-forming ink according to claim 1 of the present invention is characterized in that a release agent powder is mixed with a vehicle containing a radiation-curable component as a main component. Ink for forming a curable release layer.

The radiation-curable release layer forming ink according to claim 2 of the present invention is the ink according to claim 1, wherein the release material powder is added to 100 parts by mass of a vehicle containing a radiation-curable component as a main component. It is characterized by containing 10 to 80 parts by mass.

The sheet according to claim 3 of the present invention is a release layer formed by using the ink for forming a radiation-curable release layer according to claim 1 or 2 on a predetermined portion of at least one surface of a substrate. It is characterized by having.

The radiation-curable release layer-forming ink of the present invention has excellent suitability for printing inks, so that it is applied by offset printing or the like without using a special coating device, and then is irradiated with radiation to be cured to form a substrate. It is possible to easily form a peeling layer having high peeling performance at a required predetermined position of (the partial printing or spot printing is possible), and printing such as inkjet ink printing or electrostatic printing on the formed peeling layer, Writing,
You can stamp it.

Since the sheet of the present invention has a release layer formed by using the radiation-curable release layer forming ink of the present invention on a predetermined portion of at least one surface of the substrate, the sheet has low cost and high release performance. In addition, since the release layer is excellent in printability such as ink jet ink printing and electrostatic printing, writing property, imprintability, etc., secondary entry and additional entry are possible,
Secondary use is possible.

[0010]

BEST MODE FOR CARRYING OUT THE INVENTION It is essential to use a vehicle mainly containing a radiation-curable component for the radiation-curable release layer forming ink of the present invention, and a releasable substance powder is blended with this vehicle. Is prepared.

The radiation-curable component used in the present invention is ultraviolet light,
There is no particular limitation as long as it is a component that can be cured by radiation such as electron beams, X-rays, β-rays, and γ-rays, and among these, UV-curable and / or electron-beam curable types can be preferably used.

The energy of ultraviolet rays used for ultraviolet curing (free radical polymerization, cationic polymerization) is 3 to 6 eV.
It is necessary to add a photoinitiator or sensitizer to accelerate the photochemical reaction, and it takes several seconds or more to complete the curing, whereas it is generally used for electron beam curing (free radical polymerization). Even if the energy of the electron beam is low, the energy is large at about 150 to 300 KeV, the reaction initiation mechanism is slightly different, and the polymerization / crosslinking reaction is initiated at the same time as irradiation. Therefore, these initiators and sensitizers are added. Curing is complete in a fraction of a second or less, with no need. In the present invention, it is preferable to use one of the above-mentioned characteristics of the ultraviolet curable type and the electron beam curable type, or to use both in combination, depending on the purpose.

The radiation curing component used in the present invention includes
Any known photopolymerizable monomer and / or photopolymerizable oligomer can be arbitrarily selected and used. Examples of such a photopolymerizable monomer include unsaturated carboxylic acids such as acrylic acid and methacrylic acid or esters thereof, such as alkyl-, cycloalkyl-, halogenated alkyl-, alkoxyalkyl-, hydroxyalkyl-, aminoalkyl-. , Tetrahydrofurfuryl-, allyl-, glycidyl-, benzyl-, phenoxy-acrylates and methacrylates, alkylene glycols, polyoxyalkylene glycol mono- or diacrylates and methacrylates, trimethylolpropane triacrylate and methacrylates, pentaerythritol tetraacrylate and Acrylamide mono- or di-substituted with acrylamide, methacrylamide or its derivatives such as methacrylate, for example with alkyl or hydroxyalkyl groups. Amides and methacrylamides, diacetone acrylamides and methacrylamides, N, N'-alkylenebisacrylamides and methacrylamides, allyl compounds such as allyl alcohol, allyl isocyanate, diallyl phthalate, triallyl isocyanurate, maleic acid, maleic anhydride. , Fumaric acid or its esters such as alkyl, alkyl halides, alkoxyalkyl mono or dimaleates and fumarate, and other unsaturated compounds such as styrene, vinyltoluene, divinylbenzene, N-vinylcarbazole, N-vinylpyrrolidone, etc. Used.

For applications where curing shrinkage is an obstacle, for example, isobornyl acrylate or methacrylate, norbornyl acrylate or methacrylate, dicyclopentenoxyethyl acrylate or methacrylate, dicyclopentenoxypropyl acrylate or Acrylate or methacrylic acid ester of diethylene glycol dicyclopentenyl monoether such as methacrylate, polyoxyethylene or polypropylene glycol dicyclopentenyl monoether acrylic acid ester or methacrylic acid ester, such as dicyclopentenyl cinnamate, dicyclopentenoxy Ethyl cinnamate, dicyclopentenoxyethyl monofumarate or difumarate such as 3,9-bis (1,1
-Bismethyl-2-oxyethyl) -spiro [5,5]
Undecane, 3,9-bis (1,1-bismethyl-2-
Oxyethyl) -2,4,8,10-tetraoxaspiro [5,5] undecane, 3,9-bis (2-oxyethyl) -spiro [5,5] undecane, 3,9-bis (2-oxyethyl) Mono-, diacrylate or mono-, dimethacrylate such as -2,4,8,10-tetraoxaspiro [5,5] undecane, or mono-, ethylene oxide or propylene oxide addition polymer of these spiroglycols, Diacrylate, mono- or dimethacrylate, or methyl ether of the monoacrylate or methacrylate, 1-azabicyclo [2,2,2] -3-octenyl acrylate or methacrylate, bicyclo [2,2,1] -5 -Heptene-2,3-dicarboxyl monoallyl ester, such as dicyclopenta Enyl acrylate or methacrylate, it can be used a photopolymerizable monomer, such as dicyclopentadienyl oxyethyl acrylate or methacrylate, dihydrodicyclopentadienyl acrylate or methacrylate. These photopolymerizable monomers may be used alone or in combination of two or more.

Examples of the photopolymerizable oligomer include acrylic acid esters of epoxy resins such as diglycidyl ether diacrylate of bisphenol A, reaction products of epoxy resins with acrylic acid and methyltetrahydrophthalic anhydride, and epoxy resins with 2-hydroxy. Epoxy resin prepolymers such as reaction products with ethyl acrylate, reaction products with diglycidyl ether of epoxy resin and diallylamine, ring-opening copolymerized esters of glycidyl diacrylate and phthalic anhydride, methacrylic acid dimers Unsaturated polyester prepolymers such as esters of carboxylic acid and polyol, polyesters obtained from acrylic acid, phthalic anhydride and propylene oxide, reaction products of polyethylene glycol, maleic anhydride and glycidyl methacrylate, etc. , A reaction product of polyvinyl alcohol and N-methylolacrylamide, a polyvinyl alcohol-based prepolymer such as one obtained by esterifying polyvinyl alcohol with succinic anhydride and then adding glycidyl methacrylate, and pyromellitic dianhydride. A polyamide prepolymer such as a prepolymer obtained by reacting a diallyl esterified product with p, p'-diaminodiphenyl, a reaction product of an ethylene-maleic anhydride copolymer and allylamine, methyl vinyl ether-maleic anhydride A reaction product of an acid copolymer and 2-hydroxyethyl acrylate, a polyacrylic acid such as a product obtained by further reacting it with glycidyl methacrylate, or a maleic acid copolymer-based prepolymer, etc. Linked alkylene segments, or saturated polyester segment or both, and the like urethane prepolymer having an acryloyl group or a methacryloyl group at both ends. It is suitable that these photopolymerizable oligomers have a weight average molecular weight of about 2,000 to 30,000.

The photopolymerization initiator used in the present invention includes a thermal decomposition type radical polymerization initiator such as a peroxide or an azo compound which is decomposed by heat to generate a radical [eg, benzoyl peroxide, azobisisobutyronitrile]. , Cumene hydroperoxide, tert-butyl hydroperoxide, persulfates (potassium salts, ammonium salts), redox-based catalysts that increase the rate of radical generation by adding a reducing agent, etc. Benzoin alkyl ethers such as benzoin ethyl ether, benzoin-n-propyl ether, benzoin-isopropyl ether, benzoin isobutyl ether, 2,2-dimethoxy-2-phenylacetophenone, benzophenone, benzyl, diacetyl, diphenyl sulfide, ether Singh, thionine, 9,10-anthraquinone, 2-ethyl-9,10-anthraquinone. These photopolymerization initiators may be used alone or in combination of two or more. The content thereof is preferably selected in the range of 5 to 15 parts by mass per 100 parts by mass of the radiation curing component.

The peelable substance powder used in the present invention is not particularly limited. Specific examples of the peelable substance powder used in the present invention include fine powders such as tetrafluoroethylene resin such as KT-300M, KT-400H, and KTL.
-450, KTL-8F, KTL-4N, KTL-50
0F, KTL-350, KTL-610, KTL-8N
(Manufactured by Kitamura Co., Ltd.), a trefil F powder that is made into a powder while highly blending various silicone polymers with an inorganic carrier.
-201, F-202, F-204, F-250, F-
300 (manufactured by Toray Dow Corning Silicone Co., Ltd.), trefil R-900, R-902A, R-910 (manufactured by Toray Dow Corning Silicone Co., Ltd.), which is a fine powder of silicone resin, spherical or non-spherical Trefill E-500, E-505C, E-506, which are silicone rubber elastic bodies that are ultrafine particles in a fixed shape
C, E-600, E-601, E-604, E-850
(Manufactured by Toray Dow Corning Silicone Co., Ltd.) and the like. These may be used alone or in combination of two or more.

The amount of the peelable substance powder used in the present invention is not particularly limited, but 10 to 80 parts by mass, preferably 20 to 70 parts by mass of the peelable substance powder relative to 100 parts by mass of the vehicle. It is desirable to add the compound in an amount of, preferably 40 to 60 parts by weight. If it is less than 10 parts by mass, the releasability may not be improved, and if it exceeds 80 parts by mass, the suitability for printing ink may be deteriorated, and printing, writing, marking, etc. may not be possible.

The radiation-curable release layer-forming ink of the present invention further comprises, if desired, additional components commonly used,
For example, a reactive diluent, a tackifier, a viscosity modifier, an antioxidant, a pH modifier, an antifoaming agent, various stabilizers, a colorant, a lubricant, a sensitizer and the like can be contained.

The radiation-curable release layer-forming ink of the present invention is applied to a predetermined portion of at least one surface of a substrate by a coating means such as a gravure coater, a flexo coater, an air knife coater, and a bar coater, and is irradiated with radiation. Then, the sheet of the present invention having a release layer can be easily formed by curing.

As the base material used in the present invention, in addition to ordinary paper, synthetic paper, or synthetic film of polyethylene, polyethylene terephthalate having transparency, polypropylene, vinyl chloride or the like can be used. When using these synthetic films, it is preferable to subject the surface of the base material to a surface treatment such as a mat treatment or a corona treatment. The coating amount on the substrate surface is not particularly limited, but is, for example, 0.5 to 30 g / m ² , preferably 3 to 20 g / m ² ,
It is more preferably 5 to 15 g / m ² .

As the ink jet ink used in the present invention, for example, JP-A-7-228808,
The one described in JP-A 7-228809 can be used. In particular, at least one anionic dye selected from the group consisting of anthraquinone, benzoquinone, naphthoxyquinone, xanthene, triphenylmethane, quinoline, indigoid, azine, oxazine, thiazine and methine dyes. Ink is preferably used. Specific examples of these are described in JP-A-7-2288.
This is illustrated in paragraph No. 0015 of Japanese Patent Publication No. 09-09. As a medium used in this ink, a mixed solvent of water and a water-soluble organic solvent can be used. In addition to this, a pH adjusting agent, a viscosity adjusting agent, a surface tension adjusting agent and the like can be contained.

FIG. 1 is an explanatory view for explaining an embodiment of the seat of the present invention. In FIG. 1, the sheet 1 of the present invention
The release layer-forming ink of the present invention is used to form the release layer 3 at a predetermined position on the upper surface of the substrate 2.

FIG. 2 is an explanatory view for explaining an application example of the seat of the present invention shown in FIG. In the application example shown in FIG. 2, the sheet 1 of the present invention shown in FIG. 1 is used as a release paper, on which a label 5 having an adhesive layer 4 on the lower surface is laminated via the adhesive layer 4. ing. When the label 5 is used, the sheet 1 of the present invention is peeled off, and the label 5 is attached to another adherend via the adhesive layer 4.

FIG. 3 is an explanatory view showing another application example of the sheet of the present invention, which is re-adhesive / re-peelable adhesive to the left end portion of the lower surface of the sheet 1 of the present invention with the immersion preventive treatment layer 6 interposed therebetween. It has an agent layer 4. Then, the immersion-proof layer 6 and the adhesive layer 4 are the sheet 1
It may be provided on the entire lower surface of the.

FIG. 4 is a perspective view showing an application example of the sheet 1 of the present invention shown in FIG. 3, in which the sheet 1 having characters 7 and entry fields 8 printed with a printing ink on the release layer 3 is provided. Are stacked in plural.

FIG. 5 is a sectional view taken along line VV of the message memo shown in FIG. A plurality of sheets 1 each having a peeling layer 3 on the upper surface and further having an adhesive layer 4 which can be re-adhered and re-peeled on the left end portion of the lower surface via an immersion treatment layer 6 are sequentially laminated. And is integrated on the mount 9. The sheet 1 can be peeled off one by one and peeled off, and can be used for application to other adherends.

FIG. 6 is an explanatory view showing an example in which the sheet of the present invention is used for a delivery slip. The delivery slip 10 is, in order from the bottom, a sheet 1 of the present invention, an adhesive layer 4, an offset-printed white printed layer 11, a 3-4 color offset-printed design printed layer 12, and a protective layer for the design printed layer 12. The medium layer 13, the adhesive layer 4, and the sheet 1A of the present invention in which the release layer 3 is formed on the lower surface of the thermal paper 2A. At the time of use, the sheet 1 of the present invention on the lower surface is peeled off, the delivery slip 10 is attached to a corrugated cardboard, and the sheet 1A of the present invention on the upper surface is peeled off. When the sheet 1A of the present invention is peeled off, the characters and illustrations on which the design printing of the design printing layer 12 is printed are visible with the white printing of the white printing layer 11 as the background.

[0029]

The present invention will be described in more detail with reference to the following examples and comparative examples, but the present invention is not limited to these examples. (Example 1) 45 parts by mass of N-methoxymethylacrylamide (manufactured by Nitto Unitech Co., Ltd.) was mixed with 47 parts by mass of polyethylene glycol dimethacrylate (manufactured by Sartomer Co., Ltd.), and a photopolymerization initiator (trade name: VICURE55) was further added.
(Manufactured by Akzo Nobel) >>. 100 parts by mass of the obtained vehicle liquid, spherical silicone powder as a peelable substance powder <Product name: Trefil E-500
(Manufactured by Toray Dow Corning Silicone Co., Ltd.)> 45 parts by mass. To improve the printability, trimethylolpropane triacrylate (Toa Gosei Co., Ltd.) 10
After adding parts by mass, kneading was performed using a three-roll mill to prepare the radiation-curable release layer forming ink of the present invention. 2 g of the obtained radiation-curable release layer-forming ink of the present invention was applied on a high-quality paper (70 kg continuous amount) using a resin relief printing plate.
The printability was evaluated by performing offset printing so as to be / m ^2, and the sheet of the present invention having a release layer was prepared by irradiating with ultraviolet rays to cure. The peeling force of the obtained release layer of the sheet of the present invention was measured by the following peeling force measuring method. Apart from this, the following methods were also used to evaluate the writability, printability, and imprintability. The measurement results are summarized in Table 1.

(Peeling Force Measuring Method) First, a paper adhesive tape (width: 25 mm) is placed on the release layer surface, and a 2 kg roller (width: 50 mm) is reciprocated once to apply the tape. After leaving the sample with the paper adhesive tape attached for 1 hour in an atmosphere of a temperature of 23 ° C and a humidity of 50%, a small tabletop material testing machine A
Using GS-50A (manufactured by Shimadzu Corporation), the peeling force is measured by peeling at 180 degrees.

(Evaluation method of writability and evaluation criteria)
The peeling layer surface was evaluated by writing the alphabet with a pencil of hardness F, a line marker, and a water-based ink (fountain pen), as well as printing with an inkjet printer and marking (shachihata). . Evaluation Criteria: ◯: No blurring or cissing is written. Δ: Some blurring or cissing is generated after writing, but this is not a practical problem. ×: Writing blurring and cissing occurred, and it could not be used.

(Example 2) Table 1 shows the results of evaluation performed in the same manner as in Example 1 except that N-methoxymethylacrylamide used in Example 1 was changed to N-ethoxymethylacrylamide (manufactured by Nitto Unitech Co., Ltd.). Show.

(Example 3) The spherical silicone powder used in Example 1 was used as a trade name: Trefil E-600.
(Manufactured by Toray Dow Corning Silicone Co., Ltd.)> Was evaluated in the same manner as in Example 1. The evaluation results are shown in Table 1.

(Example 4) Evaluation was performed in the same manner as in Example 1 except that the spherical silicone powder used in Example 1 was changed to tetrafluoroethylene resin powder <trade name: KTL-500F (manufactured by Kitamura)>. I went. Table 1 shows the evaluation results
Shown in.

(Example 5) Evaluation was made in the same manner as in Example 1 except that the spherical silicone powder used in Example 1 was changed to tetrafluoroethylene resin powder <trade name: KTL-4N (manufactured by Kitamura)>. I went. The evaluation results are shown in Table 1.

Example 6 The kneading amount of the spherical silicone powder used in Example 1 was changed to 20 parts by mass, and 4 was newly added.
Fluorinated ethylene resin powder <Product name: KTL-500
F (manufactured by Kitamura Co.)> Was kneaded in the same manner as in Example 1 except that 15 parts by mass were kneaded. The evaluation results are shown in Table 1.

(Comparative Example 1) The foam fine paper used in Example 1 was evaluated in the same manner as in Example 1. The evaluation results are shown in Table 1.

Comparative Example 2 75 parts by mass of rosin-modified phenolic resin varnish and 14 parts by mass of linseed oil varnish were mixed,
7 parts by mass of wood wax (baltimic acid glyceride) and 4 parts by mass of a drier were mixed. To the resulting varnish, 35 parts by mass of a spherical releasable substance powder <trade name: Trefil E-600 (manufactured by Toray Dow Corning Silicone Co., Ltd.)> Was added, and a three-roll mill was used for exfoliation for comparison. A layer forming ink was prepared. The ink thus obtained was subjected to offset printing on a high-quality paper of 70 kg continuous amount of foam using a resin relief printing plate so as to have a printability of ² g / m ² , and the printability was evaluated, and a comparative sheet having a release layer was prepared. Table 1 shows the results of evaluating the release layer of the obtained comparative sheet in the same manner as in Example 1.

(Comparative Example 3) Table 1 shows the results of evaluation performed in the same manner as in Example 1 using a release paper containing silicone oil for comparison.

[0040]

[Table 1]

The release layer-forming inks of Examples 1 to 6 are excellent in printability, and it can be seen from Table 1 that they have an appropriate amount of release force and are excellent in release performance. At the time of peeling, the peelable substance powder does not separate to the paper adhesive tape side and the peeling layer does not peel off. It is also excellent in writing, printing and marking. On the other hand, since the comparative sheet of Comparative Example 1 is the high-quality paper itself, it can be sufficiently predicted from Table 1 that the peeling force is too large and the peeling performance is inferior and the paper peeling occurs. The release layer-forming ink for comparison of Comparative Example 2 is inferior in writability and printability, and has an excessively large peeling force and inferior peeling performance. The sheet for comparison of Comparative Example 3 is inferior in writability, printability, imprintability, and peeling performance.

[0042]

The radiation-curable release layer-forming ink according to the first aspect of the present invention is an ink in which a release material powder is mixed with a vehicle containing a radiation-curable component as a main component. Since it has excellent ink suitability, it can be applied by offset printing without using a special coating device and then cured by irradiation with radiation to easily form a release layer with high release performance at the required predetermined locations on the substrate. It has a remarkable effect that it can be formed (partial printing or spot printing is possible), and printing such as ink jet ink printing or electrostatic printing, writing, and marking can be performed on the formed release layer.

The radiation-curable release layer-forming ink according to claim 2 of the present invention is the ink according to claim 1 in which 100 parts by mass of a vehicle containing a radiation-curable component as a main component is used as a release material powder. Since 10 to 80 parts by mass are blended, the same effects as those of the ink according to the first aspect are exerted, the suitability for printing ink is more excellent, and further the releasability and the printability are surely improved.

The sheet according to claim 3 of the present invention is a release layer formed by using the radiation-curable release layer forming ink according to claim 1 or 2 on a predetermined portion of at least one surface of a substrate. Since it has low cost and high peeling performance, the peeling layer is excellent in printability such as inkjet ink printing and electrostatic printing, writing property, and imprinting property, and secondary entry and additional entry are possible. Therefore, it has a remarkable effect that it can be used secondarily.

[Brief description of drawings]

FIG. 1 is an explanatory diagram illustrating an embodiment of a seat of the present invention.

FIG. 2 is an explanatory diagram for explaining an application example of the sheet of the present invention shown in FIG.

FIG. 3 is an explanatory diagram showing another application example of the seat of the present invention.

FIG. 4 is an explanatory diagram for explaining an application example of the sheet of the present invention shown in FIG.

5 is a cross-sectional view taken along the line VV of the message memo shown in FIG.

FIG. 6 is an explanatory diagram showing an example in which the sheet of the present invention is used for a delivery slip.

[Explanation of symbols]

1, 1A Sheet of the present invention 2, 2A base material 3 Release layer 4 Adhesive layer 5 labels 7 characters 8 entry fields 9 mounts 10 home delivery slips 11 White printing layer 12 Design printing layer 13 medium layer

   ─────────────────────────────────────────────────── ─── Continued front page    (72) Inventor Kazuo Nishito             3-1-1, Ashihara-dori, Hyogo-ku, Kobe-shi, Hyogo               Bando Chemical Co., Ltd. Central Research Laboratory (72) Inventor Akio Sasaki             1-6 Surugadai Kanda, Chiyoda-ku, Tokyo             Toppan Forms Co., Ltd. (72) Inventor Akira Hirasawa             1-6 Surugadai Kanda, Chiyoda-ku, Tokyo             Toppan Forms Co., Ltd. F-term (reference) 2H086 BA01 BA15 BA36                 4F100 AB11 AK01A AK18 AK25                       AK26 AT00B BA02 BA07                       CA02A CA30 DE01A DG10                       GB90 JB14A JL00 JL14A                       YY00A                 4J038 CD122 DL032 EA012 FA011                       FA061 FA081 FA091 FA111                       FA191 FA201 FA231 FA251                       FA261 FA271 KA20 NA10                       PA17                 4J039 AD01 AD04 AD06 AD21 AE05                       AE06 AE07 AE08 AE11 AF03                       BE27 BE33 EA04 EA06 EA48                       GA02

Claims (3)

[Claims] 1. An ink for forming a radiation-curable release layer, characterized in that a release material powder is mixed with a vehicle containing a radiation-curable component as a main component. 2. The peelable substance powders 10 to 80 relative to 100 parts by mass of a vehicle containing a radiation-curable component as a main component.
The radiation-curable release layer forming ink according to claim 1, wherein the ink is mixed in an amount of part by mass. 3. A sheet having a release layer formed using the radiation-curable release layer-forming ink according to claim 1 or 2 on a predetermined portion of at least one surface of a base material.