JP2003145028A - Inspection method of coating condition of hot melt adhesive - Google Patents
Inspection method of coating condition of hot melt adhesiveInfo
- Publication number
- JP2003145028A JP2003145028A JP2001340831A JP2001340831A JP2003145028A JP 2003145028 A JP2003145028 A JP 2003145028A JP 2001340831 A JP2001340831 A JP 2001340831A JP 2001340831 A JP2001340831 A JP 2001340831A JP 2003145028 A JP2003145028 A JP 2003145028A
- Authority
- JP
- Japan
- Prior art keywords
- melt adhesive
- hot melt
- adherend
- hot
- inspection method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、ホットメルト接着
剤の塗布状態の検査方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for inspecting a coated state of a hot melt adhesive.
【０００２】[0002]
【従来の技術】例えば使い捨ておむつや生理用ナプキン
などの衛生用物品を製造する際に、これらを構成する各
種材料（各種被着体）同士を接着するためにホットメル
ト接着剤が広く利用されている。ここで、ホットメルト
接着剤は接着箇所の被着体の種類や特性、接着部分に要
求される接着力などに応じて点状、面状、線状などの任
意の形状で一方の被着体の所定位置に塗布され、他方の
被着体の所定位置と貼り合わせられている。2. Description of the Related Art In the production of sanitary articles such as disposable diapers and sanitary napkins, for example, hot melt adhesives have been widely used for adhering various materials (adhesives) constituting them. There is. Here, the hot-melt adhesive is an arbitrary shape such as a dot, a surface, or a line depending on the type and characteristics of the adherend to be adhered and the adhesive strength required for the adhered part. Is applied to a predetermined position of and is bonded to a predetermined position of the other adherend.
【０００３】これら衛生用物品は高速で連続生産される
ので、ホットメルト接着剤の塗布機として一般的に用い
られるホットメルトアプリケータを長時間連続運転して
ホットメルト接着剤を塗布している。しかし、ホットメ
ルトアプリケーターを長時間連続運転するとノズルが詰
まりやすく、いったんノズルが詰まり始めるとホットメ
ルト接着剤を塗布すべき箇所に所定の形状で塗布できな
かったり、所定量のホットメルト接着剤を塗布できない
という問題点が発生する。Since these sanitary articles are continuously produced at a high speed, a hot melt applicator generally used as a hot melt adhesive applicator is continuously operated for a long time to apply the hot melt adhesive. However, if the hot melt applicator is operated continuously for a long time, the nozzles are likely to become clogged, and once the nozzles become clogged, it is not possible to apply the hot melt adhesive in the prescribed shape or to apply the prescribed amount of hot melt adhesive. There is a problem that it cannot be done.
【０００４】そのため定期的にノズルを清掃したり、ノ
ズルの交換を行っているが、ノズルの清掃時期や交換時
期の見極めは、製造されてくる衛生用物品を定期的に抜
きとり、手にとってホットメルト接着剤がきちんと少な
くとも一方の被着体に塗布され、他方の被着体にしっか
り接着しているか否かを観察することにより行ってい
る。For this reason, the nozzles are regularly cleaned and the nozzles are replaced. However, when determining the cleaning time or replacement time of the nozzles, the sanitary articles to be manufactured are pulled out periodically and hot to the hand. This is done by observing whether or not the melt adhesive is properly applied to at least one adherend and is firmly adhered to the other adherend.
【０００５】ところが、衛生用物品では各種被着体やホ
ットメルト接着剤を白色や無色にすることが多く、ま
た、生産ラインは高速で走行していることが多いので、
これらを短時間で観察するのは容易ではなく、ホットメ
ルト接着剤の塗布状態を短時間のうちに的確に把握する
ことは困難であるという問題点がある。However, in hygiene articles, various adherends and hot-melt adhesives are often white or colorless, and the production line often runs at high speed.
It is not easy to observe these in a short time, and it is difficult to accurately grasp the application state of the hot melt adhesive in a short time.
【０００６】[0006]
【発明が解決しようとする課題】本発明の目的は、上記
問題点に鑑み、被着体やホットメルト接着剤が白色や無
色である場合でも、また、高速で走行中の生産ラインに
おいても、ホットメルト接着剤の塗布状態を短時間のう
ちに的確に把握することができるホットメルト接着剤の
塗布状態の検査方法を提供することにある。In view of the above problems, an object of the present invention is to provide an adherend or a hot-melt adhesive which is white or colorless, and also in a production line which is running at a high speed. It is an object of the present invention to provide a method for inspecting the application state of a hot melt adhesive, which can accurately grasp the application state of the hot melt adhesive in a short time.
【０００７】[0007]
【課題を解決するための手段】本発明のホットメルト接
着剤の塗布状態の検査方法（以下、単に「検査方法」と
略記する）は、蛍光成分を含有するホットメルト接着剤
を少なくとも一方の被着体に塗布した後に、または、蛍
光成分を含有するホットメルト接着剤が塗布された少な
くとも一方の被着体を他方の被着体と接着した後に、該
ホットメルト接着剤に紫外線を照射して、該ホットメル
ト接着剤が発する蛍光を観察することを特徴とする。A method for inspecting a coating state of a hot melt adhesive of the present invention (hereinafter, simply referred to as "inspection method") comprises a hot melt adhesive containing a fluorescent component on at least one side. After applying to the adherend, or after adhering at least one adherend coated with a hot melt adhesive containing a fluorescent component and the other adherend, the hot melt adhesive is irradiated with ultraviolet rays. And observing fluorescence emitted by the hot melt adhesive.
【０００８】一般に、特に衛生用物品に用いられるホッ
トメルト接着剤としては、スチレン−共役ジエン−スチ
レンブロック共重合体などの合成ゴム（合成エラストマ
ー）やポリオレフィン系樹脂などの合成樹脂を主成分と
するホットメルト接着剤が汎用されており、これら主成
分に対して、必要に応じて、例えば、粘着性付与樹脂、
プロセスオイル（可塑化オイル）、軟化剤（可塑剤）、
酸化防止剤（老化防止剤）、熱安定剤、光安定剤、紫外
線吸収剤、着色剤、充填剤等の添加剤が添加されてい
る。In general, hot melt adhesives used particularly for hygiene articles are mainly composed of synthetic rubber (synthetic elastomer) such as styrene-conjugated diene-styrene block copolymer or synthetic resin such as polyolefin resin. Hot melt adhesives are widely used, and for these main components, if necessary, for example, tackifying resin,
Process oil (plasticizing oil), softener (plasticizer),
Additives such as antioxidants (anti-aging agents), heat stabilizers, light stabilizers, UV absorbers, colorants, and fillers are added.
【０００９】上記粘着性付与樹脂、プロセスオイル、軟
化剤等のなかには、それ自体が蛍光物質であったり蛍光
成分を含有するものがあるので、ホットメルト接着剤が
蛍光を発することがある。しかし、ホットメルト接着剤
が強い蛍光を発すると衛生用物品の汚れを認識しにくく
するという観点から、ホットメルト接着剤の蛍光発光は
好ましくないものとされており、上記原料由来の蛍光発
光を防止するために、紫外線吸収剤を添加して通常の環
境下ではホットメルト接着剤が強い蛍光を発することが
ないようにされている。Some of the above tackifying resins, process oils, softening agents, etc., are fluorescent substances themselves or contain fluorescent components, so that the hot melt adhesive may emit fluorescence. However, when the hot-melt adhesive emits strong fluorescence, it becomes difficult to recognize stains on hygiene articles, and the fluorescent emission of the hot-melt adhesive is considered unfavorable. Therefore, an ultraviolet absorber is added so that the hot melt adhesive does not emit strong fluorescence under a normal environment.
【００１０】ところで、本発明者は、紫外線吸収剤を含
有し蛍光発光を防止したホットメルト接着剤であって
も、紫外線の照射強度（照度）を強くすればごく僅かで
はあってもホットメルト接着剤が蛍光を発するものと考
え、蛍光成分を含有するホットメルト接着剤を少なくと
も一方の被着体に塗布した後に、または、蛍光成分を含
有するホットメルト接着剤が塗布された少なくとも一方
の被着体を他方の被着体と接着した後に、上記ホットメ
ルト接着剤に紫外線を照射して、ホットメルト接着剤が
発する蛍光を観察することにより、ホットメルト接着剤
の塗布状態を簡便かつ迅速に検査することができると考
え本発明を完成するに至った。By the way, the inventor of the present invention has found that even a hot melt adhesive containing an ultraviolet absorber and preventing fluorescence emission can be hot melt bonded even if the irradiation intensity (illuminance) of ultraviolet light is increased, although it is very small. It is considered that the agent emits fluorescence, and after applying a hot melt adhesive containing a fluorescent component to at least one adherend, or at least one deposition applied with a hot melt adhesive containing a fluorescent component. After bonding the body to the other adherend, irradiate the hot melt adhesive with ultraviolet light and observe the fluorescence emitted by the hot melt adhesive to easily and quickly inspect the application state of the hot melt adhesive. It was thought that it was possible to complete the present invention.
【００１１】本発明の検査方法が適用されるホットメル
ト接着剤は、特に限定されるものではなく、蛍光成分を
含有するものであれば如何なるホットメルト接着剤であ
っても良いが、なかでも衛生用物品に用いられるホット
メルト接着剤が特に相応しい。The hot melt adhesive to which the inspection method of the present invention is applied is not particularly limited and may be any hot melt adhesive as long as it contains a fluorescent component. Hot melt adhesives used in consumer articles are particularly suitable.
【００１２】衛生用物品に汎用されているホットメルト
接着剤としては、例えば、Ａ−Ｂ−Ａ型ブロック共重合
体やＡ−Ｂ型ブロック共重合体などのゴム状のブロック
共重合体や、ポリオレフィン系樹脂などの合成樹脂を主
成分とし、この主成分に対して、必要に応じて、例え
ば、粘着性付与樹脂、プロセスオイル、軟化剤、酸化防
止剤等の添加剤が添加されてなるホットメルト接着剤が
挙げられる。Examples of hot melt adhesives generally used for hygiene articles include rubber-like block copolymers such as ABA type block copolymers and AB type block copolymers, Hot with a synthetic resin such as a polyolefin resin as the main component, and additives such as tackifying resin, process oil, softening agent, antioxidant, etc. added to the main component, if necessary. Melt adhesives may be mentioned.
【００１３】上記Ａ−Ｂ−Ａ型ブロック共重合体および
Ａ−Ｂ型ブロック共重合体において、Ａはビニル芳香族
化合物重合体ブロックを示し、Ｂは共役ジエン重合体ブ
ロックを示す。In the ABA type block copolymer and the AB type block copolymer, A represents a vinyl aromatic compound polymer block and B represents a conjugated diene polymer block.
【００１４】上記Ａ−Ｂ−Ａ型ブロック共重合体として
は、例えば、スチレン−ブタジエン−スチレンブロック
共重合体（ＳＢＳ）、スチレン−イソプレン−スチレン
ブロック共重合体（ＳＩＳ）、これらの共役ジエン部分
が水素添加されて得られるスチレン−エチレン−ブチレ
ン−スチレンブロック共重合体（ＳＥＢＳ）やスチレン
−エチレン−プロピレン−スチレンブロック共重合体
（ＳＥＰＳ）等が挙げられる。また、Ａ−Ｂ型ブロック
共重合体としては、例えば、スチレン−ブタジエンブロ
ック共重合体（ＳＢ）、スチレン−イソプレンブロック
共重合体（ＳＩ）、これらの共役ジエン部分が水素添加
されて得られるスチレン−エチレン−ブチレンブロック
共重合体（ＳＥＢ）やスチレン−エチレン−プロピレン
ブロック共重合体（ＳＥＰ）等が挙げられる。Examples of the ABA type block copolymer include styrene-butadiene-styrene block copolymer (SBS), styrene-isoprene-styrene block copolymer (SIS), and conjugated diene moieties thereof. Examples thereof include styrene-ethylene-butylene-styrene block copolymer (SEBS) and styrene-ethylene-propylene-styrene block copolymer (SEPS) obtained by hydrogenating Examples of the AB type block copolymer include styrene-butadiene block copolymer (SB), styrene-isoprene block copolymer (SI), and styrene obtained by hydrogenating a conjugated diene portion of these. Examples thereof include ethylene-butylene block copolymer (SEB) and styrene-ethylene-propylene block copolymer (SEP).
【００１５】また、上記ポリオレフィン系樹脂として
は、例えば、ポリエチレン、ポリプロピレン、エチレン
とエチレン以外のα−オレフィンとの共重合体、エチレ
ンと酢酸ビニルとのエチレンを主体とする共重合体、プ
ロピレンとプロピレン以外のα−オレフィンとの共重合
体等が挙げられる。Examples of the polyolefin resin include polyethylene, polypropylene, copolymers of ethylene and α-olefins other than ethylene, copolymers of ethylene and vinyl acetate mainly composed of ethylene, and propylene and propylene. Other examples include copolymers with α-olefins.
【００１６】粘着性付与樹脂としては、例えば、ロジ
ン、ロジンエステル、二量化ロジン、重合ロジン、不均
化ロジンおよびこれらの水素添加物などのロジン系樹
脂、テルペン樹脂、テルペンフェノール樹脂およびこれ
らの水素添加物などのテルペン系樹脂、Ｃ５系石油樹
脂、Ｃ９系石油樹脂およびこれらの水素添加物などの石
油系樹脂、フェノール改質炭化水素系樹脂、キシレン系
樹脂、クマロンインデン系樹脂等が挙げられる。Examples of the tackifying resin include rosin resins such as rosin, rosin ester, dimerized rosin, polymerized rosin, disproportionated rosin and hydrogenated products thereof, terpene resins, terpene phenol resins and hydrogens thereof. Examples include terpene-based resins such as additives, C5-based petroleum resins, C9-based petroleum resins and petroleum-based resins such as hydrogenated products thereof, phenol-modified hydrocarbon-based resins, xylene-based resins, and coumarone-indene-based resins. .
【００１７】プロセスオイルや軟化剤としては、例え
ば、液状ポリブテン、液状ポリプロピレン、石油ワック
ス、パラフィンワックス、微結晶ワックス、合成ワック
ス、ポリエチレングリース、水素化動物脂肪油、魚脂肪
油、植物脂肪油、鉱油、ナフチオン、パラフィン鉱油な
どの炭化水素油等が挙げられる。Examples of process oils and softeners include liquid polybutene, liquid polypropylene, petroleum wax, paraffin wax, microcrystalline wax, synthetic wax, polyethylene grease, hydrogenated animal fat oil, fish fat oil, vegetable fat oil, mineral oil. , Hydrocarbon oils such as naphthion and paraffin mineral oil.
【００１８】酸化防止剤としては、例えば、ヒンダード
フェノール系酸化防止剤やヒンダードアミン系酸化防止
剤等が挙げられる。Examples of the antioxidants include hindered phenol antioxidants and hindered amine antioxidants.
【００１９】一般に、蛍光を発光しやすい物質（化合
物）としては、例えば、分子中に不飽和二重結合を有す
るものや芳香族成分を含有するものが挙げられる。In general, examples of substances (compounds) that easily emit fluorescence include those having an unsaturated double bond in the molecule and those containing an aromatic component.
【００２０】従って、本発明で用いられるホットメルト
接着剤は、ホットメルト接着剤を構成する上記各成分の
なかでも、分子中に不飽和二重結合を有する成分、換言
すれば、未水添もしくは部分水添の成分や、分子中に芳
香族成分を含有する成分を用いることが好ましい。Therefore, the hot-melt adhesive used in the present invention is a component having an unsaturated double bond in the molecule among the above-mentioned components constituting the hot-melt adhesive, in other words, unhydrogenated or It is preferable to use a partially hydrogenated component or a component containing an aromatic component in the molecule.
【００２１】具体的には、例えば、未水添もしくは部分
水添の上記ブロック共重合体を主成分とし、この主成分
に対して、分子中に芳香族成分を含有する未水添もしく
は部分水添の上記粘着性付与樹脂、プロセスオイル、軟
化剤等が添加されてなるホットメルト接着剤が好まし
い。但し、未水添もしくは部分水添の成分は、得られる
ホットメルト接着剤の耐候性や熱安定性等を阻害するこ
とがあるので、所望の蛍光発光性と耐候性や熱安定性等
とのバランスを考慮した上で、その種類や添加量を選定
することが好ましい。Specifically, for example, the above-mentioned unhydrogenated or partially hydrogenated block copolymer is used as a main component, and an unhydrogenated or partially hydrogenated compound containing an aromatic component in the molecule is added to the main component. A hot melt adhesive obtained by adding the above tackifying resin, process oil, softening agent and the like is preferable. However, since unhydrogenated or partially hydrogenated components may impair the weather resistance and thermal stability of the obtained hot-melt adhesive, the desired fluorescence and weather resistance and thermal stability It is preferable to select the type and the addition amount after considering the balance.
【００２２】本発明で用いられるホットメルト接着剤
は、優れた蛍光発光性を発現させるという観点から、紫
外線吸収剤が含有されていないことが好ましいが、前記
理由により紫外線吸収剤を含有させる場合には、紫外線
吸収剤の含有量はホットメルト接着剤中の４重量％以下
であることが好ましい。ホットメルト接着剤中における
紫外線吸収剤の含有量が４重量％を超えると、紫外線の
照度を著しく高めてもホットメルト接着剤が蛍光を発光
しなくなることがある。The hot melt adhesive used in the present invention preferably contains no ultraviolet absorber from the viewpoint of exhibiting excellent fluorescence emission properties. However, when the ultraviolet absorber is contained for the above reason. It is preferable that the content of the ultraviolet absorber is 4% by weight or less in the hot melt adhesive. When the content of the ultraviolet absorber in the hot melt adhesive exceeds 4% by weight, the hot melt adhesive may not emit fluorescence even if the illuminance of ultraviolet rays is significantly increased.
【００２３】本発明で用いられるホットメルト接着剤の
製造方法は、特別なものではなく、加熱装置を備えた攪
拌混練機を用いて、ホットメルト接着剤を構成する各成
分の各所定量を加熱溶融し、均一に攪拌混練することに
より、所望のホットメルト接着剤を得ることができる。The method for producing the hot-melt adhesive used in the present invention is not special, and a predetermined amount of each component constituting the hot-melt adhesive is heated and melted by using a stirring and kneading machine equipped with a heating device. Then, the desired hot melt adhesive can be obtained by uniformly stirring and kneading.
【００２４】上記ホットメルト接着剤の形状は、特に限
定されるものではなく、例えば、ブロック状、ペレット
状、台形状、短冊状、球状、ロープ状等のいずれの形状
であっても良い。The shape of the hot melt adhesive is not particularly limited, and may be any shape such as block, pellet, trapezoid, strip, sphere, and rope.
【００２５】上記ホットメルト接着剤の塗布方法は、特
に限定されるものではなく、例えば、ビード塗布機、ス
パイラルスプレー機、カーテンスプレー機、スロットス
プレー機、コーティング塗布機等の公知の塗布機を用い
て、常法により、少なくとも一方の被着体の所定の箇所
に所定の塗布量となるように塗布すれば良い。また、上
記塗布の形状も、特に限定されるものではなく、例え
ば、全面塗布であっても良いし、ドット状、ビード状、
スパイラル状等の部分塗布であっても良い。The method of applying the hot melt adhesive is not particularly limited, and for example, a known coating machine such as a bead coating machine, a spiral spraying machine, a curtain spraying machine, a slot spraying machine or a coating coating machine is used. Then, it may be applied by a conventional method to a predetermined location on at least one of the adherends so as to have a predetermined coating amount. Further, the shape of the coating is not particularly limited, and may be, for example, a blanket coating, a dot shape, a bead shape,
Partial coating in a spiral shape or the like may be used.
【００２６】本発明の検査方法においては、上述したホ
ットメルト接着剤を少なくとも一方の被着体に塗布した
後に、または、上述したホットメルト接着剤が塗布され
た少なくとも一方の被着体を他方の被着体と接着した後
に、上記ホットメルト接着剤に紫外線を照射して、ホッ
トメルト接着剤が発する蛍光を観察することにより、ホ
ットメルト接着剤の塗布状態を把握する。In the inspection method of the present invention, after applying the above-mentioned hot-melt adhesive to at least one adherend, or after applying at least one adherend to which the above-mentioned hot-melt adhesive is applied to the other adherend. After adhering to the adherend, the hot melt adhesive is irradiated with ultraviolet rays and the fluorescence emitted by the hot melt adhesive is observed to grasp the application state of the hot melt adhesive.
【００２７】上記紫外線の照射源としては、好ましくは
波長３６５ｎｍ前後の光を中心とする紫外線を照射しう
るものであれば如何なる照射源であっても良く、特に限
定されるものではないが、例えば、蛍光ランプ、高圧水
銀灯、超高圧水銀灯、メタルハライドランプ、ケミカル
ランプ、キセノンランプ等が挙げられる。これらの照射
源は、単独で用いられても良いし、２種類以上が併用さ
れても良い。また、これらの照射源は、生産ライン中に
単数設置されていても良いし、複数設置されていても良
い。The UV irradiation source may be any irradiation source, as long as it can irradiate UV rays having a wavelength of about 365 nm as a center, and is not particularly limited, but for example, , Fluorescent lamps, high pressure mercury lamps, ultra high pressure mercury lamps, metal halide lamps, chemical lamps, xenon lamps and the like. These irradiation sources may be used alone or in combination of two or more. Moreover, these irradiation sources may be installed singly or plurally in the production line.
【００２８】上記紫外線は、少なくとも一方の被着体に
塗布されたホットメルト接着剤に対して直接的に照射し
ても良いし、または、ホットメルト接着剤が塗布された
少なくとも一方の被着体を他方の被着体と接着した後
に、好ましくは透明もしくは半透明な被着体を通して、
ホットメルト接着剤に対して間接的に照射しても良い。
特に衛生用物品においては、例えばポリエチレンフィル
ムなどの白色半透明もしくは無色半透明な被着体が用い
られるので、上記間接的な照射も可能である。The above-mentioned ultraviolet rays may be directly applied to the hot melt adhesive applied to at least one adherend, or at least one adherend applied with the hot melt adhesive. After being bonded to the other adherend, preferably through a transparent or translucent adherend,
The hot melt adhesive may be indirectly irradiated.
Particularly in hygiene articles, since a white translucent or colorless translucent adherend such as a polyethylene film is used, the above indirect irradiation is also possible.
【００２９】ホットメルト接着剤に対する紫外線の照度
は、特に限定されるものではなく、ホットメルト接着剤
の有する蛍光発光性に対応して適宜決定されれば良く、
例えば、ホットメルト接着剤の蛍光発光性が小さい場合
には、紫外線の照度を高めれば良い。The illuminance of ultraviolet rays on the hot melt adhesive is not particularly limited and may be appropriately determined in accordance with the fluorescence emission property of the hot melt adhesive.
For example, when the hot-melt adhesive has a low fluorescence emission property, the illuminance of ultraviolet rays may be increased.
【００３０】紫外線を照射されたホットメルト接着剤が
発する蛍光の観察方法は、特に限定されるものではな
く、目視で観察しても良いし、画像処理等の機械を用い
て観察しても良いが、高速で走行中の生産ライン上で観
察する場合には、画像処理等の機械を用いて観察する方
が好ましい。The method of observing the fluorescence emitted from the hot melt adhesive irradiated with ultraviolet rays is not particularly limited and may be visually observed or may be observed using a machine such as image processing. However, when observing on a production line running at high speed, it is preferable to observe using a machine such as image processing.
【００３１】[0031]
【作用】本発明の検査方法は、蛍光成分を含有するホッ
トメルト接着剤を少なくとも一方の被着体に塗布した後
に、または、蛍光成分を含有するホットメルト接着剤が
塗布された少なくとも一方の被着体を他方の被着体と接
着した後に、上記ホットメルト接着剤に紫外線を照射し
て、ホットメルト接着剤が発する蛍光を観察するので、
被着体やホットメルト接着剤が白色や無色である場合で
も、また、高速で走行中の生産ラインにおいても、ホッ
トメルト接着剤の塗布状態を短時間のうちに的確に把握
することができる。In the inspection method of the present invention, the hot melt adhesive containing the fluorescent component is applied to at least one adherend, or the hot melt adhesive containing the fluorescent component is applied to at least one of the adherends. After adhering the adherend to the other adherend, irradiating the hot melt adhesive with ultraviolet rays and observing the fluorescence emitted by the hot melt adhesive,
Even when the adherend or the hot-melt adhesive is white or colorless, or even on a production line running at a high speed, the applied state of the hot-melt adhesive can be accurately grasped in a short time.
【００３２】また、紫外線吸収剤の含有量が０〜４重量
％のホットメルト接着剤を用いることにより、上記特性
はより顕著なものとなる。By using a hot melt adhesive containing 0 to 4% by weight of the ultraviolet absorber, the above characteristics become more remarkable.
【００３３】[0033]
【発明の実施の形態】本発明をさらに詳しく説明するた
め以下に実施例を挙げるが、本発明はこれら実施例のみ
に限定されるものではない。なお、実施例中の「部」は
「重量部」を意味する。BEST MODE FOR CARRYING OUT THE INVENTION The following examples are given to illustrate the present invention in more detail, but the present invention is not limited to these examples. In addition, "part" in an Example means a "weight part."
【００３４】（実施例１）ＳＥＢＳ（商品名「クレイト
ンＧ１６５２」、クレイトンポリマージャパン社製）２
５部、水添Ｃ９系石油樹脂（商品名「アルコンＰ１０
０」、荒川化学工業社製）５５部、芳香族成分を含有し
ないプロセスオイル（商品名「ダイアナプロセスオイル
ＰＷ−９０」、出光興産社製）２０部およびヒンダード
フェノール系酸化防止剤（商品名「イルガノックス１０
１０」、チバスペシャルティケミカルズ社製）１部を均
一に溶融混練して、ホットメルト接着剤を作製した。(Example 1) SEBS (trade name "Clayton G1652", manufactured by Clayton Polymer Japan) 2
5 parts, hydrogenated C9 petroleum resin (trade name "Arcon P10
0 ", Arakawa Chemical Industry Co., Ltd.) 55 parts, aromatic component-free process oil (Brand name" Diana Process Oil PW-90 ", Idemitsu Kosan Co., Ltd.) 20 parts and hindered phenolic antioxidant (Brand name) "Irganox 10
10 ", manufactured by Ciba Specialty Chemicals Co., Ltd.) was uniformly melted and kneaded to prepare a hot melt adhesive.
【００３５】（実施例２）ＳＢＳ（商品名「アサプレン
Ｔ−４３８」、旭化成工業社製）２５部、水添Ｃ９系石
油樹脂（商品名「アルコンＭ１００」、荒川化学工業社
製）５５部、芳香族成分を６．２重量％含有するプロセ
スオイル（商品名「ダイアナフレシアＮ９０」、出光興
産社製）２０部およびヒンダードフェノール系酸化防止
剤「イルガノックス１０１０」１部を均一に溶融混練し
て、ホットメルト接着剤を作製した。(Example 2) SBS (trade name "Asaprene T-438", manufactured by Asahi Kasei Kogyo Co., Ltd.) 25 parts, hydrogenated C9 petroleum resin (trade name "Alcon M100", manufactured by Arakawa Chemical Industry Co., Ltd.) 55 parts, 20 parts of process oil (trade name "Diana Fresia N90", manufactured by Idemitsu Kosan Co., Ltd.) containing 6.2% by weight of an aromatic component and 1 part of hindered phenolic antioxidant "Irganox 1010" are uniformly melt-kneaded. To produce a hot melt adhesive.
【００３６】（実施例３）ＳＢＳ「アサプレンＴ−４３
８」２５部、水添Ｃ９系石油樹脂「アルコンＭ１００」
３５部、未水添Ｃ９系石油樹脂（商品名「ハイレジンＲ
Ｓ−９」、東邦化学社製）２０部、芳香族成分を含有し
ないプロセスオイル「ダイアナプロセスオイルＰＷ−９
０」２０部およびヒンダードフェノール系酸化防止剤
「イルガノックス１０１０」１部を均一に溶融混練し
て、ホットメルト接着剤を作製した。(Example 3) SBS "Asaprene T-43"
8 "25 parts, hydrogenated C9 petroleum resin" Alcon M100 "
35 parts, unhydrogenated C9 petroleum resin (trade name "High Resin R
S-9 ", manufactured by Toho Chemical Co., Ltd.) 20 parts, process oil containing no aromatic component" Diana Process Oil PW-9 "
20 parts of 0 "and 1 part of the hindered phenolic antioxidant" Irganox 1010 "were uniformly melt-kneaded to prepare a hot melt adhesive.
【００３７】（実施例４）ＳＢＳ「アサプレンＴ−４３
８」２５部、水添Ｃ９系石油樹脂「アルコンＭ１００」
５５部、芳香族成分を６．２重量％含有するプロセスオ
イル「ダイアナフレシアＮ９０」２０部、ヒンダードフ
ェノール系酸化防止剤「イルガノックス１０１０」１部
およびベンゾトリアゾール系紫外線吸収剤（商品名「チ
ヌビンＰ」、チバスペシャルティケミカルズ社製）０．
１部を均一に溶融混練して、ホットメルト接着剤を作製
した。Example 4 SBS "Asaprene T-43"
8 "25 parts, hydrogenated C9 petroleum resin" Alcon M100 "
55 parts, 20 parts of process oil "Diana Fresia N90" containing 6.2% by weight of aromatic components, 1 part of hindered phenolic antioxidant "Irganox 1010" and benzotriazole ultraviolet absorber (trade name "Tinuvin P ", manufactured by Ciba Specialty Chemicals) 0.
One part was melt-kneaded uniformly to prepare a hot melt adhesive.
【００３８】（比較例１）ＳＥＢＳ「クレイトンＧ１６
５２」２５部、水添Ｃ９系石油樹脂「アルコンＰ１０
０」５５部、芳香族成分を含有しないプロセスオイル
「ダイアナプロセスオイルＰＷ−９０」２０部、ヒンダ
ードフェノール系酸化防止剤「イルガノックス１０１
０」１部およびベンゾトリアゾール系紫外線吸収剤「チ
ヌビンＰ」５部を均一に溶融混練して、ホットメルト接
着剤を作製した。(Comparative Example 1) SEBS "Kraton G16"
52 "25 parts, hydrogenated C9 petroleum resin" Alcon P10 "
0 "55 parts, process oil containing no aromatic component" Diana Process Oil PW-90 "20 parts, hindered phenolic antioxidant" Irganox 101 "
1 part of 0 "and 5 parts of benzotriazole-based ultraviolet absorber" Tinuvin P "were uniformly melt-kneaded to prepare a hot melt adhesive.
【００３９】実施例１〜実施例４および比較例１で得ら
れたホットメルト接着剤の蛍光発光性を以下の方法で評
価した。その結果は表１に示すとおりであった。The fluorescent emission properties of the hot melt adhesives obtained in Examples 1 to 4 and Comparative Example 1 were evaluated by the following method. The results are shown in Table 1.
【００４０】蛍光発光性：使い捨ておむつに使用される
不織布およびポリエチレンフィルムを被着体として用
い、ホットメルト接着剤を塗布量が１０ｇ／ｍ2 となる
ようにポリエチレンフィルムにコーティング塗布し、直
ちに不織布を貼り合わせた。次いで、接着部に紫外線を
照度１５０μＷ／ｃｍ2 および１５００μＷ／ｃｍ2 の
２条件で照射し、ホットメルト接着剤が発する蛍光を目
視で観察して、下記判定基準によりホットメルト接着剤
の蛍光発光性を評価した。なお、紫外線の照度測定は、
商品名「ＵＶ ＲＡＤＩＯＭＥＴＥＲ ＵＶＲ−２」
（トプコン社製）を用いて、３６５ｎｍの波長で行っ
た。
〔判定基準〕
○‥‥蛍光が十分に確認され、ホットメルト接着剤の塗
布状態も鮮明に把握できた。
△‥‥蛍光が確認され、ホットメルト接着剤の塗布状態
もやや不鮮明ではあったが把握できた。
×‥‥蛍光が確認されず、ホットメルト接着剤の塗布状
態も把握できなかった。Fluorescent property: Using a non-woven fabric and polyethylene film used in disposable diapers as adherends, a hot-melt adhesive was coated on the polyethylene film so that the coating amount was 10 g / m 2, and the non-woven fabric was immediately applied. Pasted together Then, an ultraviolet ray to the adhesive portion irradiated with two conditions illuminance 150μW / cm 2 and 1500μW / cm 2, by observing the fluorescence hot melt adhesive emits visually fluorescing of the hot melt adhesive according to the following criteria Was evaluated. In addition, the illuminance measurement of ultraviolet rays,
Product name "UV RADIOMETER UVR-2"
(Manufactured by Topcon) was used at a wavelength of 365 nm. [Judgment Criteria] ◯: Fluorescence was sufficiently confirmed, and the application state of the hot melt adhesive could be clearly grasped. B: Fluorescence was confirmed, and the application state of the hot melt adhesive was somewhat unclear, but it was understood. ×: No fluorescence was confirmed, and the application state of the hot melt adhesive could not be grasped.
【００４１】[0041]
【表１】 [Table 1]
【００４２】表１から明らかなように、本発明による実
施例１〜実施例４の検査方法では、いずれもホットメル
ト接着剤が優れた蛍光発光性を発現した。これに対し、
紫外線吸収剤の含有量が４重量％を超えていたホットメ
ルト接着剤を用いた比較例１の検査方法では、紫外線の
照度が１５００μＷ／ｃｍ2 の場合でも、ホットメルト
接着剤は全く蛍光発光性を発現しなかった。As is clear from Table 1, in all the inspection methods of Examples 1 to 4 according to the present invention, the hot melt adhesives exhibited excellent fluorescence emission properties. In contrast,
In the inspection method of Comparative Example 1 using the hot-melt adhesive whose content of the ultraviolet absorber exceeded 4% by weight, even when the illuminance of ultraviolet rays was 1500 μW / cm 2 , the hot-melt adhesive was completely fluorescent. Was not expressed.
【００４３】[0043]
【発明の効果】以上述べたように、本発明のホットメル
ト接着剤の塗布状態の検査方法は、被着体やホットメル
ト接着剤が白色や無色である場合でも、また、高速で走
行中の生産ラインにおいても、ホットメルト接着剤の塗
布状態を短時間のうちに的確に把握することができるの
で、各種工業用途、特に使い捨ておむつや生理用ナプキ
ンなどの衛生用物品を製造する際のホットメルト接着剤
の塗布状態のインラインにおける簡便かつ迅速な検査方
法として好適に用いられる。As described above, the method for inspecting the application state of the hot melt adhesive according to the present invention is effective even when the adherend or the hot melt adhesive is white or colorless and is running at a high speed. Even on the production line, it is possible to accurately grasp the application state of the hot melt adhesive in a short time, so it is possible to use hot melt for various industrial applications, especially for manufacturing hygienic articles such as disposable diapers and sanitary napkins. It is preferably used as an in-line simple and quick inspection method of the adhesive application state.
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2G051 AA90 AC22 BA01 BA05 DA06 EA12 4D075 BB46Z BB99Z CA47 CB09 DA04 DA31 DC30 EA07 EA35 EC47 4J040 BA182 BA202 DA001 DA022 DK012 DM011 DN032 DN072 EB082 HB02 HB03 HB40 JB01 KA26 KA29 NA02 ─────────────────────────────────────────────────── ─── Continued front page F term (reference) 2G051 AA90 AC22 BA01 BA05 DA06 EA12 4D075 BB46Z BB99Z CA47 CB09 DA04 DA31 DC30 EA07 EA35 EC47 4J040 BA182 BA202 DA001 DA022 DK012 DM011 DN032 DN072 EB082 HB02 HB03 HB40 JB01 KA26 KA29 NA02
Claims (2)
を少なくとも一方の被着体に塗布した後に、または、蛍
光成分を含有するホットメルト接着剤が塗布された少な
くとも一方の被着体を他方の被着体と接着した後に、上
記ホットメルト接着剤に紫外線を照射して、ホットメル
ト接着剤が発する蛍光を観察することを特徴とするホッ
トメルト接着剤の塗布状態の検査方法。1. After applying a hot melt adhesive containing a fluorescent component to at least one adherend, or applying at least one adherend coated with a hot melt adhesive containing a fluorescent component to the other. A method for inspecting the application state of a hot melt adhesive, which comprises irradiating the hot melt adhesive with ultraviolet rays after gluing it to an adherend and observing fluorescence emitted from the hot melt adhesive.
〜４重量％を含有するホットメルト接着剤であることを
特徴とする請求項１に記載のホットメルト接着剤の塗布
状態の検査方法。2. The hot melt adhesive is an ultraviolet absorber 0
The method for inspecting the application state of a hot melt adhesive according to claim 1, which is a hot melt adhesive containing -4% by weight.